US 7,674,715 B2Grant

Method for forming tungsten materials during vapor deposition processes

Issue Date:2010-03-09

•25 Claims

•11 Drawing Sheets

Abstract

In one embodiment, a method for forming a tungsten material on a substrate surface is provide which includes positioning a substrate within a deposition chamber, heating the substrate to a deposition temperature, and exposing the substrate sequentially to diborane and a tungsten precursor gas to form a tungsten nucleation layer on the substrate during an atomic layer deposition (ALD) process. The method further provides exposing the substrate to a deposition gas comprising hydrogen gas and the tungsten precursor gas to form a tungsten bulk layer over the tungsten nucleation layer during a chemical vapor deposition (CVD) process. Examples are provided which include ALD and CVD processes that may be conducted in the same deposition chamber or in different deposition chambers.

Metadata

Assignee

Applied Materials, Inc.

Inventors

Moris Kori
Alfred W. Mak
Jeong Soo Byun
Lawrence Chung-Lai Lei
Hua Chung
Ashok Sinha
Ming Xi

Application Information

Application Number:US 12/335,983

Filing Date:2008-12-16

Priority Date:2000-06-28

Art Unit:2891

Classifications

IPC:

H01L21/44

Patent Drawings (11 sheets)

Description

Cross-Reference to Related Applications

[0001] This application is a continuation of U.S. Ser. No. 11/766,121 (APPM/004714.C8), filed Jun. 21, 2007, and issued as U.S. Pat. No. 7,465,666, which is a continuation of U.S. Ser. No. 11/468,156 (APPM/004714.C6), filed Aug. 29, 2006, and issued as U.S. Pat. No. 7,235,486, which is a continuation of U.S. Ser. No. 11/338,565 (APPM/004714.C4), filed Jan. 24, 2006, and issued as U.S. Pat. No. 7,115,494, which is a continuation of U.S. Ser. No. 10/951,354 (APPM/004714.C3), filed Sep. 29, 2004, and issued as U.S. Pat. No. 7,033,922, which is a continuation of U.S. Ser. No. 09/625,336 (APPM/004714.D1), filed Jul. 25, 2000, and issued as U.S. Pat. No. 6,855,368, which is a divisional of U.S. Ser. No. 09/605,593 (APPM/004714), filed Jun. 28, 2000, and issued as U.S. Pat. No. 6,551,929, which are herein incorporated by reference in their entirety.

Background of the Invention

[0002] 1. Field of the Invention

[0003] This invention relates to the processing of semiconductor substrates. More particularly, this invention relates to improvements in the process of depositing refractory metal layers on semiconductor substrates.

[0004] 2. Description of the Related Art

[0005] The semiconductor processing industry continues to strive for larger production yields while increasing the uniformity of layers deposited on substrates having increasing larger surface areas. These same factors in combination with new materials also provide higher integration of circuits per unit area of the substrate. As circuit integration increases, the need for greater uniformity and process control regarding layer thickness rises. As a result, various technologies have been developed to deposit layers on substrates in a cost-effective manner, while maintaining control over the characteristics of the layer. Chemical vapor deposition (CVD) is one of the most common deposition processes employed for depositing layers on a substrate. CVD is a flux-dependent deposition technique that requires precise control of the substrate temperature and precursors introduced into the processing chamber in order to produce a desired layer of uniform thickness. These requirements become more critical as substrate size increases, creating a need for more complexity in chamber design and gas flow technique to maintain adequate uniformity.

[0006] A variant of CVD that demonstrates superior step coverage, compared to CVD, is atomic layer deposition (ALD). ALD is based upon atomic layer epitaxy (ALE) that was originally employed to fabricate electroluminescent displays. ALD employs chemisorption to deposit a saturated monolayer of reactive precursor molecules on a substrate surface. This is achieved by alternatingly pulsing an appropriate reactive precursor into a deposition chamber. Each injection of a reactive precursor is separated by an inert gas purge to provide a new atomic layer additive to previous deposited layers to form a uniform layer on the substrate. The cycle is repeated to form the layer to a desired thickness. A drawback with ALD techniques is that the deposition rate is much lower than typical CVD techniques by at least one order of magnitude.

[0007] Employing the aforementioned deposition techniques it is seen that formation of a layer at a high deposition rate while providing adequate step coverage are conflicting characteristics often necessitating sacrificing one to obtain the other. This has been prevalent when depositing refractory metal layers to cover gaps or vias during formation of contacts that interconnect adjacent metallic layers separated by a dielectric layer. Historically, CVD techniques have been employed to deposit conductive material in order to inexpensively and quickly form contacts. Due to the increasing integration of semiconductor circuitry, tungsten has been used based upon the superior step coverage of tungsten. As a result, deposition of tungsten employing CVD techniques enjoys wide application in semiconductor processing due to the high throughput of the process.

[0008] Depositing tungsten in this manner, however, is attendant with several disadvantages. For example, blanket deposition of a tungsten layer on a semiconductor wafer is time-consuming at temperatures below 400° C. The deposition rate of tungsten may be improved by increasing the deposition temperature to, e.g., about 500° C. to about 550° C. Temperatures in this range may compromise the structural and operational integrity of the underlying portions of the integrated circuit being formed. Tungsten has also frustrated photolithography steps during the manufacturing process by providing a relatively rough surface having a reflectivity of 20% or less than that of a silicon substrate. Finally, tungsten has proven difficult to deposit uniformly. This has been shown by variance in tungsten layers' thickness of greater than 1%, which frustrates control of the resistivity of the layer. Several prior attempts to overcome the aforementioned drawbacks have been attempted.

[0009] For example, in U.S. Pat. No. 5,028,565, which is assigned to the assignee of the present invention, a method is disclosed to improve, inter alia, uniformity of tungsten layers by varying the deposition chemistry. The method includes, in pertinent part, formation of a nucleation layer over an intermediate barrier layer before depositing the tungsten layer via bulk deposition. The nucleation layer is formed from a gaseous mixture of tungsten hexafluoride, hydrogen, silane and argon. The nucleation layer is described as providing a layer of growth sites to promote uniform deposition of a tungsten layer. The benefits provided by the nucleation layer are described as being dependent upon the barrier layer present. For example, were the barrier layer formed from titanium nitride, the tungsten layer's thickness uniformity is improved as much as 15%. The benefits provided by the nucleation layer are not substantial if the barrier layer is formed from sputtered tungsten or sputtered titanium tungsten.

[0010] A need exists, therefore, to provide techniques to improve the characteristics of refractory metal layers deposited on semiconductor substrates.

Summary of the Invention

[0011] A method and system reduces the resistance of contacts of refractory metal layers by controlling the presence of fluorine contained therein. The present invention is based upon the discovery that when employing ALD techniques to form refractory metal layers on a substrate, the carrier gas employed impacts the presence of fluorine in the resulting layer. As a result, the method features chemisorbing onto the substrate alternating monolayers of a first compound and a second compound, with the second compound having fluorine atoms associated therewith, with each of the first and second compounds being introduced into the processing chamber along with a carrier gas; and controlling a quantity of the fluorine atoms associated with the monolayer of the second compound as a function of the carrier gas. Specifically, it was found that by introducing the first and second compounds employing H₂as a carrier gas, the amount of fluorine present in the resulting refractory metal layer was substantially reduced, compared to employing either nitrogen (N₂) or argon as a carrier gas.

[0012] To that end, the system includes a processing chamber, having a holder, disposed therein to support the substrate. A gas delivery system and a pressure control system are in fluid communication with the processing chamber. A temperature control system is in thermal communication therewith. A controller is in electrical communication with gas delivery system, temperature control system, and the pressure control system. A memory is in data communication with the controller. The memory comprises a computer-readable medium having a computer-readable program embodied therein. The computer-readable program includes instructions for controlling the operation of the processing chamber.

Brief Description of the Drawings

[0013] FIG. 1 is a perspective view of a semiconductor processing system in accordance with the present invention;

[0014] FIG. 2 is a detailed view of the processing chambers shown above in FIG. 1;

[0015] FIG. 3 is a schematic view showing deposition of a first molecule onto a substrate during ALD;

[0016] FIG. 4 is a schematic view showing deposition of second molecule onto a substrate during ALD to form a refractory metal layer;

[0017] FIG. 5 is a graphical representation showing the concentration of gases introduced into the processing chamber shown above in FIG. 2, and the time in which the gases are present in the processing chamber, in accordance with the present invention;

[0018] FIG. 6 is a graphical representation showing the relationship between the number of ALD cycles and the thickness of a layer formed on a substrate employing ALD, in accordance with the present invention;

[0019] FIG. 7 is a graphical representation showing the relationship between the number of ALD cycles and the resistivity of a layer formed on a substrate employing ALD, in accordance with the present invention;

[0020] FIG. 8 is a graphical representation showing the relationship between the deposition rate of a layer formed on a substrate employing ALD and the temperature of the substrate;

[0021] FIG. 9 is a graphical representation showing the relationship between the resistivity of a layer formed on a substrate employing ALD and the temperature of the substrate, in accordance with the present invention;

[0022] FIG. 10 is a cross-sectional view of a patterned substrate having a nucleation layer formed thereon employing ALD, in accordance with the present invention;

[0023] FIG. 11 is a partial cross-sectional view of the substrate, shown above in FIG. 10, with a refractory metal layer formed atop of the nucleation layer employing CVD, in accordance with the present invention;

[0024] FIG. 12 is a graphical representation showing the concentration of gases shown above in FIG. 5 in accordance with a first alternate embodiment of the present invention;

[0025] FIG. 13 is a graphical representation showing the concentration of gases shown above in FIG. 5 in accordance with a second alternate embodiment of the present invention;

[0026] FIG. 14 is a graphical representation showing the fluorine content versus depth of a refractory metal layer formed on a substrate employing ALD either Ar or N₂being a carrier gas; and

[0027] FIG. 15 is a graphical representation showing the fluorine content versus depth of a refractory metal layer formed on a substrate employing ALD with H₂being a carrier gas.

Detailed Description of the Invention

[0028] Referring to FIG. 1, an exemplary wafer processing system includes two or more processing chambers 12 and 14 disposed in a common work area 16 surrounded by a wall 18. The processing chambers 12 and 14 are in data communication with a controller 22 that is connected to one or more monitors, shown as 24 and 26. The monitors typically display common information concerning the process associated with the processing chambers 12 and 14. One of the monitors 26 is mounted to the wall 18, with the remaining monitor 24 being disposed in the work area 16. Operational control of the processing chambers 12 and 14 may be achieved use of a light pen, associated with one of the monitors 24 and 26, to communicate with the controller 22. For example, light pen 28 is associated with monitor 24 and facilitates communication with the controller 22 through monitor 24. Light pen 29 facilitates communication with the controller 22 through monitor 26.

[0029] Referring both to FIGS. 1 and 2, each of the processing chambers 12 and 14 includes a housing 30 having a base wall 32, a cover 34, disposed opposite to the base wall 32, and a sidewall 36, extending therebetween. The housing 30 defines a chamber 37, and a pedestal 38 is disposed within the processing chamber 37 to support a substrate 42, such as a semiconductor wafer. The pedestal 38 may be mounted to move between the cover 34 and the base wall 32, using a displacement mechanism (not shown). Supplies of processing gases 39a, 39b, and 39c are in fluid communication with the processing chamber 37 via a showerhead 40. Regulation of the flow of gases from the supplies 39a, 39b and 39c is effectuated via flow valves 41.

[0030] Depending on the specific process, the substrate 42 may be heated to a desired temperature prior to layer deposition via a heater embedded within the pedestal 38. For example, the pedestal 38 may be resistively heated by applying an electric current from an AC power supply 43 to the heater element 44. The wafer 40 is, in turn, heated by the pedestal 38, and can be maintained within a desired process temperature range of, for example, about 20° C. to about 750° C. A temperature sensor 46, such as a thermocouple, is also embedded in the wafer support pedestal 38 to monitor the temperature of the pedestal 38 in a conventional manner. For example, the measured temperature may used in a feedback loop to control the electrical current applied to the heater element 44 by the power supply 43, such that the wafer temperature can be maintained or controlled at a desired temperature which is suitable for the particular process application. The pedestal 38 is optionally heated using radiant heat (not shown). A vacuum pump 48 is used to evacuate the processing chamber 37 and to help maintain the proper gas flows and pressure inside the processing chamber 37.

[0031] Referring to FIGS. 1 and 3, one or both of the processing chambers 12 and 14, discussed above may operate to deposit refractory metal layers on the substrate employing ALD techniques. Depending on the specific stage of processing, the refractory metal layer may be deposited on the material from which the substrate 42 is fabricated, e.g., SiO₂. The refractory metal layer may also be deposited on a layer previously formed on the substrate 42, e.g., titanium, titanium nitride and the like.

[0032] ALD proceeds by chemisorption. The initial surface of the substrate 42 presents an active ligand to the process region. A batch of a first processing gas, in this case Aa_x, results in a layer of “A” being deposited on the substrate 42 having a surface of ligand “a” exposed to the processing chamber 37. Thereafter, a purge gas enters the processing chamber 37 to purge the gas Aa_x. After purging gas Aa_xfrom the processing chamber 37, a second batch of processing gas, Bb_y, is introduced into the processing chamber 37. The a ligand present on the substrate surface reacts with the “b” ligand and “B” atom on the, releasing molecules ab and Ba, that move away from the substrate 42 and are subsequently pumped from the processing chamber 37. In this manner, a surface comprising a monolayer of A atoms remains upon the substrate 42 and exposed to the processing chamber 37, shown in FIG. 4. The process proceeds cycle after cycle, until the desired thickness is achieved.

[0033] Referring to both FIGS. 2 and 5, although any type of processing gas may be employed, in the present example, the processing gas Aa_xis WF₆and the processing gas Bb_yis B₂H₆. Two purge gases were employed: Ar and N₂. Each of the processing gases is flowed into the processing chamber 37 with a carrier gas, which in this example were one of the purge gases: WF₆is introduced with Ar and B₂H₆is introduced with N₂. It should be understood, however, that the purge gas may differ from the carrier gas, discussed more fully below. One cycle of the ALD technique in accordance with the present invention includes flowing the purge gas, N₂, into the processing chamber 37 during time t₁, which is approximately five seconds before B₂H₆is flowed into the processing chamber 37. During time t₂, the processing gas B₂H₆is flowed into the processing chamber 37 for approximately five seconds, along with a carrier gas, which in this example is N₂. After five seconds have lapsed, the flow of B₂H₆terminates and the flow of N₂continues during time t₃for an additional five seconds, purging the processing chamber of B₂H₆. During time t₄, the processing chamber 37 is pumped so as to remove all gases. The pumping process lasts approximately thirty seconds. After pumping of the process chamber 37, the carrier gas Ar is introduced for approximately five seconds during time t₅, after which time the process gas WF₆is introduced into the processing chamber 37 for about five seconds, along with the carrier gas Ar during time t₆. The flow of the processing gas WF₆into the processing chamber 37 is terminated approximately five seconds after it commenced. After the flow of WF₆into the processing chamber 37 terminates, the flow of Ar continues for five additional seconds, during time t₇. Thereafter, the processing chamber 37 is pumped so as to remove all gases therein, during time t₈. As before, the pumping process lasts approximately thirty seconds, thereby concluding one cycle of the ALD technique in accordance with the present invention.

[0034] The benefits of employing ALD are manifold, including flux-independence of layer formation that provides uniformity of deposition independent of the size of a substrate. For example, the measured difference of the layer uniformity and thickness measured between of 200 mm substrate and a 32 mm substrate deposited in the same chamber is negligible. This is due to the self-limiting characteristics of chemisorption. Further, the chemisorption characteristics contribute to near-perfect step coverage over complex topography.

[0035] In addition, the thickness of the layer A, shown in FIG. 4, may be easily controlled while minimizing the resistance of the same by employing ALD. With reference to FIG. 6 it is seen the slope of line 50 that the thickness of the tungsten layer A is proportional to the number of cycles employed to form the same. The resistivity of the tungsten layer, however, is relatively independent of the thickness of the layer, as shown by the slope of line 52 in FIG. 7. Thus, employing ALD, the thickness of a refractory metal layer may be easily controlled as a function of the cycling of the process gases introduced into the processing chamber with a negligible effect on the resistivity.

[0036] Referring to FIG. 8, control of the deposition rate was found to be dependent upon the temperature of the substrate 42. As shown by the slope of line 54, increasing the temperature of the substrate 42 increased the deposition rate of the tungsten layer A. For example, at point 56, the deposition rate is shown to be approximately 2 Å/cycle at 250° C. However at point 58 the deposition rate is approximately 5 Å/cycle at a temperature of 450° C. The resistivity of the tungsten layer, however, is virtually independent of the layer thickness, as shown by the slope of curve 59, shown in FIG. 9. As a result, the deposition rate of the tungsten layer may be controlled as a function of temperature without comprising the resistivity of the same. However, it is preferred to perform many processing steps at temperatures well below 450° C.

[0037] To that end, a bifurcated deposition process may be practiced in which nucleation of the refractory metal layer occurs in a different chamber than the formation of the remaining portion of the refractory metal layer. Specifically, in the present example, nucleation of a tungsten layer occurs in chamber 12 employing the ALD techniques discussed above, with the substrate 42 being heated in the range of 200° C. to 400° C., and the processing chamber 37 being pressurized in the range of 1 to 10 Torr. A nucleation layer 60 of approximately 12 to 20 nm is formed on a patterned substrate 42, shown in FIG. 10. As shown, the substrate 42 includes a barrier layer 61 and a patterned layer having a plurality of vias 63. The nucleation layer is formed adjacent to the patterned layer covering the vias 63. As shown, forming the nucleation layer 60 employing ALD techniques provides 100% step coverage. To decrease the time required to form a complete layer of tungsten, a bulk deposition of tungsten onto the nucleation layer 60 occurs using CVD techniques, while the substrate 42 is disposed in processing chamber 14, shown in FIG. 1. The bulk deposition may be performed using recipes well known in the art. In this manner, a tungsten layer 65 providing a complete plug fill is achieved on the patterned layer with vias having aspect ratios of approximately 6:1, shown in FIG. 11.

[0038] As mentioned above, in an alternate embodiment of the present invention, the carrier gas may differ from the purge gas, as shown in FIG. 12. The purge gas, which is introduced at time intervals t₁, t₃, t₅and t₇comprises of Ar. The carrier gas, which is introduced at time intervals t₂and t₆, comprises of N₂. Thus, at time interval t₂the gases introduced into the processing chamber include a mixture of B₂H₆and N₂, and a time interval t₆, the gas mixture includes WF₆and N₂. The pump process during time intervals t₄and t₈is identical to the pump process discussed above with respect to FIG. 5. In yet another embodiment, shown in FIG. 13, the carrier gas during time intervals t₂and t₆comprises H₂, with the purge gas introduced at time intervals t₁, t₃, t₅and t₇comprising of Ar. The pump processes at time intervals t₄and t₈are as discussed above. As a result, at time interval t₂the gas mixture introduced into the processing chamber 37 consists of B₂H₆and H₂, and WF₆and H₂, at time interval t₆.

[0039] An advantage realized by employing the H₂carrier gas is that the stability of the tungsten layer A may be improved. Specifically, by comparing curve 66 in FIG. 14 with the curve 68 in FIG. 15, it is seen that the concentration of fluorine in the nucleation layer 60 is much less when H₂is employed as the carrier gas, as compared with use of N₂or Ar as a carrier gas. Specifically, the apex and nadir of curve 66 show that the fluorine concentration reaches levels in excess of 1×10²¹atoms per cubic centimeter and only as low as just below 1×10¹⁹atoms per cubic centimeter. Curve 68, however, shows that the fluorine concentration is well below 1×10²¹atoms per cubic centimeter at the apex and well below 1×10¹⁷atoms per cubic centimeter at the nadir. Thus, employing H₂as the carrier gas provides a much more stable film, i.e., the probability of fluorine diffusing into the substrate, or adjacent layer is reduced. This also reduces the resistance of the refractory metal layer by avoiding the formation of a metal fluoride that may result from the increased fluorine concentration. Thus, the stability of the nucleation layer, as well as the resistivity of the same, may be controlled as a function of the carrier gas employed. This is also true when a refractory metal layer is deposited entirely employing ALD techniques, i.e., without using other deposition techniques, such as CVD.

[0040] Referring again to FIG. 2, the process for depositing the tungsten layer may be controlled using a computer program product that is executed by the controller 22. To that end, the controller 22 includes a central processing unit (CPU) 70, a volatile memory, such as a random access memory (RAM) 72 and permanent storage media, such as a floppy disk drive for use with a floppy diskette, or hard disk drive 74. The computer program code can be written in any conventional computer readable programming language; for example, 68000 assembly language, C, C++, Pascal, FORTRAN, and the like. Suitable program code is entered into a single file, or multiple files, using a conventional text editor and stored or embodied in a computer-readable medium, such as the hard disk drive 74. If the entered code text is in a high level language, the code is compiled and the resultant compiler code is then linked with an object code of precompiled WINDOWS® library routines. To execute the linked and compiled object code the system user invokes the object code, causing the CPU 70 to load the code in RAM 72. The CPU 70 then reads and executes the code to perform the tasks identified in the program.

[0041] Although the invention has been described in terms of specific embodiments, one skilled in the art will recognize that various changes to the reaction conditions, i.e., temperature, pressure, film thickness and the like can be substituted and are meant to be included herein. In addition, other refractory metals may be deposited, in addition to tungsten, and other deposition techniques may be employed in lieu of CVD. For example, physical vapor deposition (PVD) techniques, or a combination of both CVD and PVD techniques may be employed. Therefore, the scope of the invention should not be based upon the foregoing description. Rather, the scope of the invention should be determined based upon the claims recited herein, including the full scope of equivalents thereof.

Claims

What is claimed is:

1. A method for forming a tungsten material on a substrate surface, comprising:

heating a substrate within a deposition chamber;

exposing the substrate sequentially to a first processing gas comprising a tungsten precursor and a second processing gas comprising diborane to form a tungsten nucleation layer on the substrate during an atomic layer deposition process, wherein the tungsten nucleation layer comprises a fluorine concentration of about 1×10²¹atoms/cm³or less; and

depositing a tungsten bulk layer over the tungsten nucleation layer during a chemical vapor deposition process.

2. The method of claim 1, wherein the fluorine concentration is about 1×10¹⁹atoms/cm³or less.

3. The method of claim 2, wherein the fluorine concentration is about 1×10¹⁷atoms/cm³or less.

4. The method of claim 1, wherein the first processing gas further comprises hydrogen gas.

5. The method of claim 1, wherein the first processing gas further comprises nitrogen gas.

6. The method of claim 5, wherein the tungsten precursor is tungsten hexafluoride.

7. The method of claim 1, wherein the second processing gas further comprises hydrogen gas.

8. The method of claim 1, wherein the second processing gas further comprises nitrogen gas.

9. The method of claim 1, wherein the tungsten nucleation layer is formed having a thickness within a range from about 10 Å to about 100 Å.

10. The method of claim 1, wherein the tungsten nucleation layer is formed having a thickness within a range from about 12 nm to about 20 nm.

11. The method of claim 1, wherein the deposition chamber is a first deposition station within a deposition system containing multiple stations surrounded by a wall.

12. The method of claim 11, further comprising:

moving the substrate from the first deposition station to a second deposition station subsequent the atomic layer deposition process and prior to the chemical vapor deposition process; and

forming the tungsten bulk layer within the second deposition station.

13. The method of claim 1, wherein the substrate is heated to a temperature within a range from about 200° C. to about 400° C., and the deposition chamber is pressurized to a pressure within a range from about 1 Torr to about 10 Torr during the atomic layer deposition process.

14. The method of claim 1, further comprising exposing the substrate to an initiation gas prior to the atomic layer deposition process, wherein the initiation gas comprises nitrogen or argon.

15. The method of claim 14, wherein the substrate is exposed to the initiation gas for about 5 seconds.

16. A method for forming a tungsten material on a substrate surface, comprising:

heating a substrate within a deposition chamber;

exposing the substrate sequentially to a first processing gas and a second processing gas to form a tungsten nucleation layer on the substrate during an atomic layer deposition process, wherein the first processing gas comprises a tungsten precursor and a carrier gas and the second processing gas comprises a reagent and hydrogen gas; and

depositing a tungsten bulk layer over the tungsten nucleation layer during a chemical vapor deposition process.

17. The method of claim 16, wherein the tungsten nucleation layer comprises a fluorine concentration of about 1×10¹⁹atoms/cm³or less.

18. The method of claim 17, wherein the fluorine concentration is about 1×10¹⁷atoms/cm³or less.

19. The method of claim 18, wherein the reagent is diborane.

20. The method of claim 18, wherein the first processing gas comprises a hydrogen carrier gas.

21. The method of claim 16, wherein the first processing gas comprises a nitrogen carrier gas.

22. The method of claim 21, wherein the tungsten precursor is tungsten hexafluoride.

23. The method of claim 16, wherein the deposition chamber is a first deposition station within a deposition system containing multiple stations surrounded by a wall.

24. The method of claim 23, further comprising:

moving the substrate from the first deposition station to a second deposition station subsequent the atomic layer deposition process and prior to the chemical vapor deposition process; and

forming the tungsten bulk layer within the second deposition station.

25. A method for forming a tungsten material on a substrate surface, comprising:

heating a substrate within a deposition chamber;

exposing the substrate sequentially to a first processing gas and a second processing gas to form a tungsten nucleation layer on the substrate during an atomic layer deposition process, wherein the first processing gas comprises tungsten hexafluoride and a carrier gas and the second processing gas comprises diborane and hydrogen gas; and

depositing a tungsten bulk layer over the tungsten nucleation layer during a chemical vapor deposition process.

Patent Citations (736)

Patent	Date	Inventor	Cited By
US4058430(A)	1977-11-01	Suntola et al.	Applicant
US4389973(A)	1983-06-01	Suntola et al.	Applicant
US4413022(A)	1983-11-01	Suntola et al.	Applicant
US4486487(A)	1984-12-01	Skarp et al.	Applicant
US4767494(A)	1988-08-01	Kobayashi et al.	Applicant
US4806321(A)	1989-02-01	Nishizawa et al.	Applicant
US4813846(A)	1989-03-01	Helms et al.	Applicant
US4829022(A)	1989-05-01	Kobayashi et al.	Applicant
US4834831(A)	1989-05-01	Nishizawa et al.	Applicant
US4838983(A)	1989-06-01	Schumaker et al.	Applicant
US4838993(A)	1989-06-01	Aoki et al.	Applicant
US4840921(A)	1989-06-01	Matsumoto et al.	Applicant
US4845049(A)	1989-07-01	Sunakawa et al.	Applicant
US4859625(A)	1989-08-01	Matsumoto et al.	Applicant
US4859627(A)	1989-08-01	Sunakawa et al.	Applicant
US4861417(A)	1989-08-01	Mochizuki et al.	Applicant
US4876218(A)	1989-10-01	Pessa et al.	Applicant
US4917556(A)	1990-04-01	Stark et al.	Applicant
US4927670(A)	1990-05-01	Erbil	Applicant
US4931132(A)	1990-06-01	Aspnes et al.	Applicant
US4951601(A)	1990-08-01	Maydan et al.	Applicant
US4960720(A)	1990-10-01	Shimbo et al.	Applicant
US4975252(A)	1990-12-01	Nishizawa et al.	Applicant
US4993357(A)	1991-02-01	Scholz et al.	Applicant
US5000113(A)	1991-03-01	Wang et al.	Applicant
US5013683(A)	1991-05-01	Petroff et al.	Applicant
US5028565(A)	1991-07-01	Chang et al.	Applicant
US5082798(A)	1992-01-01	Arimoto et al.	Applicant
US5085885(A)	1992-02-01	Foley et al.	Applicant
US5091320(A)	1992-02-01	Aspnes et al.	Applicant
US5130269(A)	1992-07-01	Kitahara et al.	Applicant
US5166092(A)	1992-11-01	Mochizuki et al.	Applicant
US5173474(A)	1992-12-01	Connell et al.	Applicant
US5186718(A)	1993-02-01	Tepman et al.	Applicant
US5205077(A)	1993-04-01	Wittstock et al.	Applicant
US5225366(A)	1993-07-01	Yoder	Applicant
US5234561(A)	1993-08-01	Randhawa et al.	Applicant
US5246536(A)	1993-09-01	Nishizawa et al.	Applicant
US5250148(A)	1993-10-01	Nishizawa et al.	Applicant
US5254207(A)	1993-10-01	Nishizawa et al.	Applicant
US5256244(A)	1993-10-01	Ackerman	Applicant
US5259881(A)	1993-11-01	Edwards et al.	Applicant
US5270247(A)	1993-12-01	Sakuma et al.	Applicant
US5278435(A)	1994-01-01	Van Hove et al.	Applicant
US5281274(A)	1994-01-01	Yoder	Applicant
US5286296(A)	1994-02-01	Sato et al.	Applicant
US5290748(A)	1994-03-01	Knuuttila et al.	Applicant
US5294286(A)	1994-03-01	Nishizawa et al.	Applicant
US5296403(A)	1994-03-01	Nishizawa et al.	Applicant
US5300186(A)	1994-04-01	Kitahara et al.	Applicant
US5306666(A)	1994-04-01	Izumi et al.	Applicant
US5311055(A)	1994-05-01	Goodman et al.	Applicant
US5316615(A)	1994-05-01	Copel et al.	Applicant
US5316793(A)	1994-05-01	Wallace et al.	Applicant
US5330610(A)	1994-07-01	Eres et al.	Applicant
US5336324(A)	1994-08-01	Stall et al.	Applicant
US5338389(A)	1994-08-01	Nishizawa et al.	Applicant
US5348911(A)	1994-09-01	Jurgensen et al.	Applicant
US5374570(A)	1994-12-01	Nasu et al.	Applicant
US5395791(A)	1995-03-01	Cheng et al.	Applicant
US5438952(A)	1995-08-01	Otsuka et al.	Applicant
US5439876(A)	1995-08-01	Graf et al.	Applicant
US5441703(A)	1995-08-01	Jurgensen et al.	Applicant
US5443033(A)	1995-08-01	Nishizawa et al.	Applicant
US5443647(A)	1995-08-01	Aucoin et al.	Applicant
US5455072(A)	1995-10-01	Bension et al.	Applicant
US5458084(A)	1995-10-01	Thorne et al.	Applicant
US5469806(A)	1995-11-01	Mochizuki et al.	Applicant
US5480818(A)	1996-01-01	Matsumoto et al.	Applicant
US5483919(A)	1996-01-01	Yokoyama et al.	Applicant
US5484664(A)	1996-01-01	Kitahara et al.	Applicant
US5503875(A)	1996-04-01	Imai et al.	Applicant
US5521126(A)	1996-05-01	Okamura et al.	Applicant
US5526244(A)	1996-06-01	Bishop	Applicant
US5527733(A)	1996-06-01	Nishizawa et al.	Applicant
US5532511(A)	1996-07-01	Nishizawa et al.	Applicant
US5540783(A)	1996-07-01	Eres et al.	Applicant
US5580380(A)	1996-12-01	Liu et al.	Applicant
US5601651(A)	1997-02-01	Watabe et al.	Applicant
US5609689(A)	1997-03-01	Kato et al.	Applicant
US5616181(A)	1997-04-01	Yamamoto et al.	Applicant
US5637530(A)	1997-06-01	Gaines et al.	Applicant
US5641984(A)	1997-06-01	Aftergut et al.	Applicant
US5644128(A)	1997-07-01	Wollnik et al.	Applicant
US5667592(A)	1997-09-01	Boitnott et al.	Applicant
US5674786(A)	1997-10-01	Turner et al.	Applicant
US5693139(A)	1997-12-01	Nishizawa et al.	Applicant
US5695564(A)	1997-12-01	Imahashi et al.	Applicant
US5705224(A)	1998-01-01	Murota et al.	Applicant
US5707880(A)	1998-01-01	Aftergut et al.	Applicant
US5711811(A)	1998-01-01	Suntola et al.	Applicant
US5730801(A)	1998-03-01	Tepman et al.	Applicant
US5730802(A)	1998-03-01	Ishizumi et al.	Applicant
US5747113(A)	1998-05-01	Tsai	Applicant
US5749974(A)	1998-05-01	Habuka et al.	Applicant
US5788447(A)	1998-08-01	Yonemitsu et al.	Applicant
US5788799(A)	1998-08-01	Steger et al.	Applicant
US5796116(A)	1998-08-01	Nakata et al.	Applicant
US5801634(A)	1998-09-01	Young et al.	Applicant
US5804488(A)	1998-09-01	Shih et al.	Applicant
US5807792(A)	1998-09-01	Ilg et al.	Applicant
US5830270(A)	1998-11-01	McKee et al.	Applicant
US5834372(A)	1998-11-01	Lee et al.	Applicant
US5835677(A)	1998-11-01	Li et al.	Applicant
US5851849(A)	1998-12-01	Comizzoli et al.	Applicant
US5855675(A)	1999-01-01	Doering et al.	Applicant
US5855680(A)	1999-01-01	Soininen et al.	Applicant
US5856219(A)	1999-01-01	Naito et al.	Applicant
US5858102(A)	1999-01-01	Tsai	Applicant
US5866213(A)	1999-02-01	Foster et al.	Applicant
US5866795(A)	1999-02-01	Wang et al.	Applicant
US5879459(A)	1999-03-01	Gadgil et al.	Applicant
US5882165(A)	1999-03-01	Maydan et al.	Applicant
US5882413(A)	1999-03-01	Beaulieu et al.	Applicant
US5904565(A)	1999-05-01	Nguyen et al.	Applicant
US5916365(A)	1999-06-01	Sherman	Applicant
US5923056(A)	1999-07-01	Lee et al.	Applicant
US5923985(A)	1999-07-01	Aoki et al.	Applicant
US5925574(A)	1999-07-01	Aoki et al.	Applicant
US5928389(A)	1999-07-01	Jevtic	Applicant
US5942040(A)	1999-08-01	Kim et al.	Applicant
US5947710(A)	1999-09-01	Cooper et al.	Applicant
US5972430(A)	1999-10-01	DiMeo, Jr. et al.	Applicant
US6001420(A)	1999-12-01	Mosely et al.	Applicant
US6001669(A)	1999-12-01	Gaines et al.	Applicant
US6015590(A)	2000-01-01	Suntola et al.	Applicant
US6015917(A)	2000-01-01	Bhandari et al.	Applicant
US6025627(A)	2000-02-01	Forbes et al.	Applicant
US6036773(A)	2000-03-01	Wang et al.	Applicant
US6042652(A)	2000-03-01	Hyun et al.	Applicant
US6043177(A)	2000-03-01	Falconer et al.	Applicant
US6051286(A)	2000-04-01	Zhao et al.	Applicant
US6062798(A)	2000-05-01	Muka	Applicant
US6071808(A)	2000-06-01	Merchant et al.	Applicant
US6084302(A)	2000-07-01	Sandhu	Applicant
US6086677(A)	2000-07-01	Umotoy et al.	Applicant
US6099904(A)	2000-08-01	Mak et al.	Applicant
US6110556(A)	2000-08-01	Bang et al.	Applicant
US6113977(A)	2000-09-01	Soininen et al.	Applicant
US6117244(A)	2000-09-01	Bang et al.	Applicant
US6124158(A)	2000-09-01	Dautartas et al.	Applicant
US6130147(A)	2000-10-01	Major et al.	Applicant
US6139700(A)	2000-10-01	Kang et al.	Applicant
US6140237(A)	2000-10-01	Chan et al.	Applicant
US6140238(A)	2000-10-01	Kitch	Applicant
US6143659(A)	2000-11-01	Leem et al.	Applicant
US6144060(A)	2000-11-01	Park et al.	Applicant
US6156382(A)	2000-12-01	Rajagopalan et al.	Applicant
US6158446(A)	2000-12-01	Mohindra et al.	Applicant
US6162715(A)	2000-12-01	Mak et al.	Applicant
US6174377(B1)	2001-01-01	Doering et al.	Applicant
US6174809(B1)	2001-01-01	Kang et al.	Applicant
US6197683(B1)	2001-03-01	Kang et al.	Applicant
US6200893(B1)	2001-03-01	Sneh	Applicant
US6203613(B1)	2001-03-01	Gates et al.	Applicant
US6206967(B1)	2001-03-01	Mak et al.	Applicant
US6207302(B1)	2001-03-01	Sugiura et al.	Applicant
US6207487(B1)	2001-03-01	Kim et al.	Applicant
US6218298(B1)	2001-04-01	Hoinkis	Applicant
US6248605(B1)	2001-06-01	Harkonen et al.	Applicant
US6251190(B1)	2001-06-01	Mak et al.	Applicant
US6270572(B1)	2001-08-01	Kim et al.	Applicant
US6271148(B1)	2001-08-01	Kao et al.	Applicant
US6274484(B1)	2001-08-01	Tsai et al.	Applicant
US6284646(B1)	2001-09-01	Leem et al.	Applicant
US6287965(B1)	2001-09-01	Kang et al.	Applicant
US6291876(B1)	2001-09-01	Stumborg et al.	Applicant
US6305314(B1)	2001-10-01	Sneh et al.	Applicant
US6306098(B1)	2001-10-01	Orr et al.	Applicant
US6306216(B1)	2001-10-01	Kim et al.	Applicant
US6309713(B1)	2001-10-01	Mak et al.	Applicant
US6326297(B1)	2001-12-01	Vijayendran	Applicant
US6333260(B1)	2001-12-01	Kwon et al.	Applicant
US6335280(B1)	2002-01-01	van der Jeugd	Applicant
US6342277(B1)	2002-01-01	Sherman	Applicant
US6348376(B2)	2002-02-01	Lim et al.	Applicant
US6355561(B1)	2002-03-01	Sandhu et al.	Applicant
US6358829(B2)	2002-03-01	Yoon et al.	Applicant
US6368954(B1)	2002-04-01	Lopatin et al.	Applicant
US6369430(B1)	2002-04-01	Adetutu et al.	Applicant
US6372598(B2)	2002-04-01	Kang et al.	Applicant
US6379748(B1)	2002-04-01	Bhandari et al.	Applicant
US6391785(B1)	2002-05-01	Satta et al.	Applicant
US6399491(B2)	2002-06-01	Jeon et al.	Applicant
US6416577(B1)	2002-07-01	Suntoloa et al.	Applicant
US6416822(B1)	2002-07-01	Chiang et al.	Applicant
US6420189(B1)	2002-07-01	Lopatin	Applicant
US6423619(B1)	2002-07-01	Grant et al.	Applicant
US6428859(B1)	2002-08-01	Chiang et al.	Applicant
US6447933(B1)	2002-09-01	Wang et al.	Applicant
US6451119(B2)	2002-09-01	Sneh et al.	Applicant
US6451695(B2)	2002-09-01	Sneh	Applicant
US6458701(B1)	2002-10-01	Chae et al.	Applicant
US6468924(B2)	2002-10-01	Lee et al.	Applicant
US6475276(B1)	2002-11-01	Elers et al.	Applicant
US6475910(B1)	2002-11-01	Sneh	Applicant
US6478872(B1)	2002-11-01	Chae et al.	Applicant
US6482262(B1)	2002-11-01	Elers et al.	Applicant
US6482733(B2)	2002-11-01	Raaijmakers et al.	Applicant
US6482740(B2)	2002-11-01	Soininen et al.	Applicant
US6498091(B1)	2002-12-01	Chen et al.	Applicant
US6511539(B1)	2003-01-01	Raaijmakers et al.	Applicant
US6524952(B1)	2003-02-01	Srinivas et al.	Applicant
US6534395(B2)	2003-03-01	Werkhoven et al.	Applicant
US6534404(B1)	2003-03-01	Danek et al.	Applicant
US6548424(B2)	2003-04-01	Putkonen et al.	Applicant
US6551929(B1)	2003-04-01	Kori et al.	Applicant
US6569501(B2)	2003-05-01	Chiang et al.	Applicant
US6585823(B1)	2003-07-01	Van Wijck et al.	Applicant
US6593484(B2)	2003-07-01	Yasuhara et al.	Applicant
US6596602(B2)	2003-07-01	Iizuka et al.	Applicant
US6596643(B2)	2003-07-01	Chen et al.	Applicant
US6599572(B2)	2003-07-01	Saanila et al.	Applicant
US6607976(B2)	2003-08-01	Chen et al.	Applicant
US6607977(B1)	2003-08-01	Rozbicki et al.	Applicant
US6620723(B1)	2003-09-01	Byun et al.	Applicant
US6627268(B1)	2003-09-01	Fair et al.	Applicant
US6630201(B2)	2003-10-01	Chiang et al.	Applicant
US6632279(B1)	2003-10-01	Ritala et al.	Applicant
US6635965(B1)	2003-10-01	Lee et al.	Applicant
US6660126(B2)	2003-12-01	Nguyen et al.	Applicant
US6660622(B2)	2003-12-01	Chen et al.	Applicant
US6686271(B2)	2004-02-01	Raaijmakers et al.	Applicant
US6713373(B1)	2004-03-01	Omstead	Applicant
US6718126(B2)	2004-04-01	Lei	Applicant
US6720027(B2)	2004-04-01	Yang et al.	Applicant
US6720260(B1)	2004-04-01	Fair et al.	Applicant
US6740585(B2)	2004-05-01	Yoon et al.	Applicant
US6764940(B1)	2004-07-01	Rozbicki et al.	Applicant
US6772072(B2)	2004-08-01	Ganguli et al.	Applicant
US6773507(B2)	2004-08-01	Jallepally et al.	Applicant
US6777352(B2)	2004-08-01	Tepman et al.	Applicant
US6784096(B2)	2004-08-01	Chen et al.	Applicant
US6790773(B1)	2004-09-01	Drewery et al.	Applicant
US6797340(B2)	2004-09-01	Fang et al.	Applicant
US6797608(B1)	2004-09-01	Lin	Applicant
US6797642(B1)	2004-09-01	Chu et al.	Applicant
US6800173(B2)	2004-10-01	Chiang et al.	Applicant
US6803272(B1)	2004-10-01	Halliyal et al.	Applicant
US6809026(B2)	2004-10-01	Yoon et al.	Applicant
US6815285(B2)	2004-11-01	Choi et al.	Applicant
US6821563(B2)	2004-11-01	Yudovsky	Applicant
US6821889(B2)	2004-11-01	Elers et al.	Applicant
US6827978(B2)	2004-12-01	Yoon et al.	Applicant
US6831004(B2)	2004-12-01	Byun et al.	Applicant
US6833161(B2)	2004-12-01	Wang et al.	Applicant
US6838125(B2)	2005-01-01	Chung et al.	Applicant
US6846516(B2)	2005-01-01	Yang et al.	Applicant
US6849545(B2)	2005-02-01	Mak et al.	Applicant
US6855368(B1)	2005-02-01	Kori et al.	Applicant
US6875271(B2)	2005-04-01	Glenn et al.	Applicant
US6878402(B2)	2005-04-01	Chiang et al.	Applicant
US6893915(B2)	2005-05-01	Park et al.	Applicant
US6905541(B2)	2005-06-01	Chen et al.	Applicant
US6905737(B2)	2005-06-01	Verplancken et al.	Applicant
US6911391(B2)	2005-06-01	Yang et al.	Applicant
US6915592(B2)	2005-07-01	Guenther	Applicant
US6916398(B2)	2005-07-01	Chen et al.	Applicant
US6932871(B2)	2005-08-01	Chang et al.	Applicant
US6936538(B2)	2005-08-01	Byun	Applicant
US6936906(B2)	2005-08-01	Chung et al.	Applicant
US6939801(B2)	2005-09-01	Chung et al.	Applicant
US6939804(B2)	2005-09-01	Lai et al.	Applicant
US6951804(B2)	2005-10-01	Seutter et al.	Applicant
US6953742(B2)	2005-10-01	Chen et al.	Applicant
US6955211(B2)	2005-10-01	Ku et al.	Applicant
US6958174(B1)	2005-10-01	Klaus et al.	Applicant
US6958296(B2)	2005-10-01	Chen et al.	Applicant
US6972267(B2)	2005-12-01	Cao et al.	Applicant
US6974771(B2)	2005-12-01	Chen et al.	Applicant
US6998014(B2)	2006-02-01	Chen et al.	Applicant
US7005372(B2)	2006-02-01	Levy et al.	Applicant
US7026238(B2)	2006-04-01	Xi et al.	Applicant
US7033922(B2)	2006-04-01	Kori et al.	Applicant
US7041335(B2)	2006-05-01	Chung	Applicant
US7049226(B2)	2006-05-01	Chung et al.	Applicant
US7081271(B2)	2006-07-01	Chung et al.	Applicant
US7094680(B2)	2006-08-01	Seutter et al.	Applicant
US7094685(B2)	2006-08-01	Yang et al.	Applicant
US7101795(B1)	2006-09-01	Xi et al.	Applicant
US7115494(B2)	2006-10-01	Sinha et al.	Applicant
US7115499(B2)	2006-10-01	Wang et al.	Applicant
US7141494(B2)	2006-11-01	Lee et al.	Applicant
US7186385(B2)	2007-03-01	Ganguli et al.	Applicant
US7204886(B2)	2007-04-01	Chen et al.	Applicant
US7208413(B2)	2007-04-01	Byun et al.	Applicant
US7211144(B2)	2007-05-01	Lu et al.	Applicant
US7211508(B2)	2007-05-01	Chung et al.	Applicant
US7220673(B2)	2007-05-01	Xi et al.	Applicant
US7235486(B2)	2007-06-01	Kori et al.	Applicant
US7465666(B2)	2008-12-01	Kori et al.	Applicant
US2001/0000866(A1)	2001-05-01	Sneh et al.	Applicant
US2001/0002280(A1)	2001-05-01	Sneh	Applicant
US2001/0009140(A1)	2001-07-01	Bondestam et al.	Applicant
US2001/0009695(A1)	2001-07-01	Saanila et al.	Applicant
US2001/0011526(A1)	2001-08-01	Doering et al.	Applicant
US2001/0024387(A1)	2001-09-01	Raaijmakers et al.	Applicant
US2001/0025979(A1)	2001-10-01	Kim et al.	Applicant
US2001/0028924(A1)	2001-10-01	Sherman	Applicant
US2001/0029094(A1)	2001-10-01	Mee-Young et al.	Applicant
US2001/0031562(A1)	2001-10-01	Raaijmakers et al.	Applicant
US2001/0034123(A1)	2001-10-01	Jeon et al.	Applicant
US2001/0041250(A1)	2001-11-01	Werkhoven et al.	Applicant
US2001/0042799(A1)	2001-11-01	Kim et al.	Applicant
US2001/0050039(A1)	2001-12-01	Park	Applicant
US2001/0054730(A1)	2001-12-01	Kim et al.	Applicant
US2001/0054769(A1)	2001-12-01	Raaijmakers et al.	Applicant
US2002/0000598(A1)	2002-01-01	Kang et al.	Applicant
US2002/0004293(A1)	2002-01-01	Soininen et al.	Applicant
US2002/0007790(A1)	2002-01-01	Park	Applicant
US2002/0009544(A1)	2002-01-01	McFeely et al.	Applicant
US2002/0019121(A1)	2002-02-01	Pyo	Applicant
US2002/0020869(A1)	2002-02-01	Park et al.	Applicant
US2002/0021544(A1)	2002-02-01	Cho et al.	Applicant
US2002/0031618(A1)	2002-03-01	Sherman	Applicant
US2002/0037630(A1)	2002-03-01	Agarwal et al.	Applicant
US2002/0041931(A1)	2002-04-01	Suntola et al.	Applicant
US2002/0048635(A1)	2002-04-01	Kim et al.	Applicant
US2002/0048880(A1)	2002-04-01	Lee	Applicant
US2002/0052097(A1)	2002-05-01	Park	Applicant
US2002/0055235(A1)	2002-05-01	Agarwal et al.	Applicant
US2002/0060363(A1)	2002-05-01	Xi et al.	Applicant
US2002/0061612(A1)	2002-05-01	Sandhu et al.	Applicant
US2002/0066411(A1)	2002-06-01	Chiang et al.	Applicant
US2002/0068458(A1)	2002-06-01	Chiang et al.	Applicant
US2002/0073924(A1)	2002-06-01	Chiang et al.	Applicant
US2002/0074588(A1)	2002-06-01	Lee	Applicant
US2002/0076481(A1)	2002-06-01	Chiang et al.	Applicant
US2002/0076507(A1)	2002-06-01	Chiang et al.	Applicant
US2002/0076508(A1)	2002-06-01	Chiang et al.	Applicant
US2002/0076837(A1)	2002-06-01	Hujanen et al.	Applicant
US2002/0081844(A1)	2002-06-01	Jeon et al.	Applicant
US2002/0086111(A1)	2002-07-01	Byun et al.	Applicant
US2002/0086507(A1)	2002-07-01	Park et al.	Applicant
US2002/0090829(A1)	2002-07-01	Sandhu et al.	Applicant
US2002/0094689(A1)	2002-07-01	Park	Applicant
US2002/0098627(A1)	2002-07-01	Pomarede et al.	Applicant
US2002/0104481(A1)	2002-08-01	Chiang et al.	Applicant
US2002/0105088(A1)	2002-08-01	Yang et al.	Applicant
US2002/0106536(A1)	2002-08-01	Lee et al.	Applicant
US2002/0106846(A1)	2002-08-01	Seutter et al.	Applicant
US2002/0109168(A1)	2002-08-01	Kim et al.	Applicant
US2002/0115886(A1)	2002-08-01	Yasuhara et al.	Applicant
US2002/0117399(A1)	2002-08-01	Chen et al.	Applicant
US2002/0121241(A1)	2002-09-01	Nguyen et al.	Applicant
US2002/0121342(A1)	2002-09-01	Nguyen et al.	Applicant
US2002/0121697(A1)	2002-09-01	Marsh	Applicant
US2002/0135071(A1)	2002-09-01	Kang et al.	Applicant
US2002/0144655(A1)	2002-10-01	Chiang et al.	Applicant
US2002/0144657(A1)	2002-10-01	Chiang et al.	Applicant
US2002/0146511(A1)	2002-10-01	Chiang et al.	Applicant
US2002/0155722(A1)	2002-10-01	Satta et al.	Applicant
US2002/0162506(A1)	2002-11-01	Sneh et al.	Applicant
US2002/0164421(A1)	2002-11-01	Chiang et al.	Applicant
US2002/0164423(A1)	2002-11-01	Chiang et al.	Applicant
US2002/0177282(A1)	2002-11-01	Song	Applicant
US2002/0182320(A1)	2002-12-01	Leskela et al.	Applicant
US2002/0187256(A1)	2002-12-01	Elers et al.	Applicant
US2002/0187631(A1)	2002-12-01	Kim et al.	Applicant
US2002/0197402(A1)	2002-12-01	Chiang et al.	Applicant
US2002/0197863(A1)	2002-12-01	Mak et al.	Applicant
US2003/0013300(A1)	2003-01-01	Byun	Applicant
US2003/0013320(A1)	2003-01-01	Kim et al.	Applicant
US2003/0017697(A1)	2003-01-01	Choi et al.	Applicant
US2003/0022487(A1)	2003-01-01	Yoon et al.	Applicant
US2003/0022507(A1)	2003-01-01	Chen et al.	Applicant
US2003/0029715(A1)	2003-02-01	Yu et al.	Applicant
US2003/0031807(A1)	2003-02-01	Elers et al.	Applicant
US2003/0032281(A1)	2003-02-01	Werkhoven et al.	Applicant
US2003/0038369(A1)	2003-02-01	Layadi et al.	Applicant
US2003/0042630(A1)	2003-03-01	Babcoke et al.	Applicant
US2003/0049931(A1)	2003-03-01	Byun et al.	Applicant
US2003/0049942(A1)	2003-03-01	Haukka et al.	Applicant
US2003/0053799(A1)	2003-03-01	Lei	Applicant
US2003/0054631(A1)	2003-03-01	Raaijmakers et al.	Applicant
US2003/0057526(A1)	2003-03-01	Chung et al.	Applicant
US2003/0057527(A1)	2003-03-01	Chung et al.	Applicant
US2003/0059538(A1)	2003-03-01	Chung et al.	Applicant
US2003/0072884(A1)	2003-04-01	Zhang et al.	Applicant
US2003/0072975(A1)	2003-04-01	Shero et al.	Applicant
US2003/0079686(A1)	2003-05-01	Chen et al.	Applicant
US2003/0082296(A1)	2003-05-01	Elers et al.	Applicant
US2003/0082300(A1)	2003-05-01	Todd et al.	Applicant
US2003/0082301(A1)	2003-05-01	Chen et al.	Applicant
US2003/0082307(A1)	2003-05-01	Chung et al.	Applicant
US2003/0087520(A1)	2003-05-01	Chen et al.	Applicant
US2003/0089308(A1)	2003-05-01	Raaijmakers	Applicant
US2003/0101927(A1)	2003-06-01	Raaijmakers	Applicant
US2003/0104126(A1)	2003-06-01	Fang et al.	Applicant
US2003/0106490(A1)	2003-06-01	Jallepally et al.	Applicant
US2003/0108674(A1)	2003-06-01	Chung et al.	Applicant
US2003/0113187(A1)	2003-06-01	Lei et al.	Applicant
US2003/0116087(A1)	2003-06-01	Nguyen et al.	Applicant
US2003/0121608(A1)	2003-07-01	Chen et al.	Applicant
US2003/0123216(A1)	2003-07-01	Yoon et al.	Applicant
US2003/0124262(A1)	2003-07-01	Chen et al.	Applicant
US2003/0127043(A1)	2003-07-01	Lu et al.	Applicant
US2003/0129826(A1)	2003-07-01	Werkhoven et al.	Applicant
US2003/0134508(A1)	2003-07-01	Raaijmakers et al.	Applicant
US2003/0143328(A1)	2003-07-01	Chen et al.	Applicant
US2003/0143839(A1)	2003-07-01	Raaijmakers et al.	Applicant
US2003/0143841(A1)	2003-07-01	Yang et al.	Applicant
US2003/0153177(A1)	2003-08-01	Tepman et al.	Applicant
US2003/0153181(A1)	2003-08-01	Yoon et al.	Applicant
US2003/0157760(A1)	2003-08-01	Xi et al.	Applicant
US2003/0161952(A1)	2003-08-01	Wang et al.	Applicant
US2003/0165615(A1)	2003-09-01	Aaltonen et al.	Applicant
US2003/0168750(A1)	2003-09-01	Basceri et al.	Applicant
US2003/0173586(A1)	2003-09-01	Moriwaki et al.	Applicant
US2003/0181035(A1)	2003-09-01	Yoon et al.	Applicant
US2003/0186495(A1)	2003-10-01	Saanila et al.	Applicant
US2003/0190423(A1)	2003-10-01	Yang et al.	Applicant
US2003/0190497(A1)	2003-10-01	Yang et al.	Applicant
US2003/0190804(A1)	2003-10-01	Glenn et al.	Applicant
US2003/0194493(A1)	2003-10-01	Chang et al.	Applicant
US2003/0194825(A1)	2003-10-01	Law et al.	Applicant
US2003/0194858(A1)	2003-10-01	Lee et al.	Applicant
US2003/0203616(A1)	2003-10-01	Chung et al.	Applicant
US2003/0205729(A1)	2003-11-01	Basceri et al.	Applicant
US2003/0213987(A1)	2003-11-01	Basceri et al.	Applicant
US2003/0219942(A1)	2003-11-01	Choi et al.	Applicant
US2003/0224217(A1)	2003-12-01	Byun et al.	Applicant
US2003/0224578(A1)	2003-12-01	Chung et al.	Applicant
US2003/0224600(A1)	2003-12-01	Cao et al.	Applicant
US2003/0232497(A1)	2003-12-01	Xi et al.	Applicant
US2004/0005749(A1)	2004-01-01	Choi et al.	Applicant
US2004/0009307(A1)	2004-01-01	Koh et al.	Applicant
US2004/0009336(A1)	2004-01-01	Marcadal et al.	Applicant
US2004/0011504(A1)	2004-01-01	Ku et al.	Applicant
US2004/0013577(A1)	2004-01-01	Ganguli et al.	Applicant
US2004/0013803(A1)	2004-01-01	Chung et al.	Applicant
US2004/0014315(A1)	2004-01-01	Lai et al.	Applicant
US2004/0014320(A1)	2004-01-01	Chen et al.	Applicant
US2004/0015300(A1)	2004-01-01	Ganguli et al.	Applicant
US2004/0018304(A1)	2004-01-01	Chung et al.	Applicant
US2004/0018723(A1)	2004-01-01	Byun et al.	Applicant
US2004/0018747(A1)	2004-01-01	Lee et al.	Applicant
US2004/0025370(A1)	2004-02-01	Guenther	Applicant
US2004/0033698(A1)	2004-02-01	Lee et al.	Applicant
US2004/0041320(A1)	2004-03-01	Hodumi	Applicant
US2004/0043630(A1)	2004-03-01	Vaartstra et al.	Applicant
US2004/0046197(A1)	2004-03-01	Basceri et al.	Applicant
US2004/0048461(A1)	2004-03-01	Chen et al.	Applicant
US2004/0065255(A1)	2004-04-01	Yang et al.	Applicant
US2004/0067641(A1)	2004-04-01	Yudovsky	Applicant
US2004/0071897(A1)	2004-04-01	Verplancken et al.	Applicant
US2004/0077183(A1)	2004-04-01	Chung	Applicant
US2004/0105934(A1)	2004-06-01	Chang et al.	Applicant
US2004/0144311(A1)	2004-07-01	Chen et al.	Applicant
US2004/0170403(A1)	2004-09-01	Lei	Applicant
US2004/0187304(A1)	2004-09-01	Chen et al.	Applicant
US2004/0197492(A1)	2004-10-01	Chen et al.	Applicant
US2004/0202786(A1)	2004-10-01	Wongsenakhum et al.	Applicant
US2004/0209460(A1)	2004-10-01	Xi et al.	Applicant
US2004/0209465(A1)	2004-10-01	Xi et al.	Applicant
US2004/0211665(A1)	2004-10-01	Yoon et al.	Applicant
US2004/0214354(A1)	2004-10-01	Marsh et al.	Applicant
US2004/0219784(A1)	2004-11-01	Kang et al.	Applicant
US2004/0224506(A1)	2004-11-01	Choi et al.	Applicant
US2004/0235285(A1)	2004-11-01	Kang et al.	Applicant
US2004/0241321(A1)	2004-12-01	Ganguli et al.	Applicant
US2004/0247788(A1)	2004-12-01	Fang et al.	Applicant
US2004/0256351(A1)	2004-12-01	Chung et al.	Applicant
US2004/0266175(A1)	2004-12-01	Chen et al.	Applicant
US2005/0006799(A1)	2005-01-01	Gregg et al.	Applicant
US2005/0008779(A1)	2005-01-01	Yang et al.	Applicant
US2005/0009325(A1)	2005-01-01	Chung et al.	Applicant
US2005/0031786(A1)	2005-02-01	Lee et al.	Applicant
US2005/0059240(A1)	2005-03-01	Choi et al.	Applicant
US2005/0059241(A1)	2005-03-01	Kori et al.	Applicant
US2005/0064098(A1)	2005-03-01	Elers et al.	Applicant
US2005/0074968(A1)	2005-04-01	Chen et al.	Applicant
US2005/0104142(A1)	2005-05-01	Narayanan et al.	Applicant
US2005/0106865(A1)	2005-05-01	Chung et al.	Applicant
US2005/0118804(A1)	2005-06-01	Byun et al.	Applicant
US2005/0139948(A1)	2005-06-01	Chung et al.	Applicant
US2005/0164487(A1)	2005-07-01	Seutter et al.	Applicant
US2005/0173068(A1)	2005-08-01	Chen et al.	Applicant
US2005/0176240(A1)	2005-08-01	Wang et al.	Applicant
US2005/0189072(A1)	2005-09-01	Chen et al.	Applicant
US2005/0208763(A1)	2005-09-01	Byun	Applicant
US2005/0220998(A1)	2005-10-01	Chang et al.	Applicant
US2005/0252449(A1)	2005-11-01	Nguyen et al.	Applicant
US2005/0255690(A1)	2005-11-01	Chen et al.	Applicant
US2005/0257735(A1)	2005-11-01	Guenther	Applicant
US2005/0260357(A1)	2005-11-01	Olsen et al.	Applicant
US2005/0266682(A1)	2005-12-01	Chen et al.	Applicant
US2005/0271812(A1)	2005-12-01	Myo et al.	Applicant
US2005/0271813(A1)	2005-12-01	Kher et al.	Applicant
US2005/0271814(A1)	2005-12-01	Chang et al.	Applicant
US2005/0277290(A1)	2005-12-01	Yang et al.	Applicant
US2005/0287807(A1)	2005-12-01	Lai et al.	Applicant
US2006/0009034(A1)	2006-01-01	Lai et al.	Applicant
US2006/0019033(A1)	2006-01-01	Muthukrishnan et al.	Applicant
US2006/0019494(A1)	2006-01-01	Cao et al.	Applicant
US2006/0019495(A1)	2006-01-01	Marcadal et al.	Applicant
US2006/0030148(A1)	2006-02-01	Seutter et al.	Applicant
US2006/0035025(A1)	2006-02-01	Verplancken et al.	Applicant
US2006/0040052(A1)	2006-02-01	Fang et al.	Applicant
US2006/0057843(A1)	2006-03-01	Chen et al.	Applicant
US2006/0062917(A1)	2006-03-01	Muthukrishnan et al.	Applicant
US2006/0075966(A1)	2006-04-01	Chen et al.	Applicant
US2006/0128132(A1)	2006-06-01	Sinha et al.	Applicant
US2006/0128150(A1)	2006-06-01	Gandikota et al.	Applicant
US2006/0148253(A1)	2006-07-01	Chung et al.	Applicant
US2006/0153973(A1)	2006-07-01	Chang et al.	Applicant
US2006/0153995(A1)	2006-07-01	Narwankar et al.	Applicant
US2006/0156979(A1)	2006-07-01	Thakur et al.	Applicant
US2006/0199372(A1)	2006-09-01	Chung et al.	Applicant
US2006/0216928(A1)	2006-09-01	Chung et al.	Applicant
US2006/0257295(A1)	2006-11-01	Chen et al.	Applicant
US2006/0264031(A1)	2006-11-01	Xi et al.	Applicant
US2006/0276020(A1)	2006-12-01	Yoon et al.	Applicant
US2006/0292864(A1)	2006-12-01	Yang et al.	Applicant
US2006/0292874(A1)	2006-12-01	Kori et al.	Applicant
US2007/0003698(A1)	2007-01-01	Chen et al.	Applicant
US2007/0009658(A1)	2007-01-01	Yoo et al.	Applicant
US2007/0018244(A1)	2007-01-01	Hung et al.	Applicant
US2007/0020890(A1)	2007-01-01	Thakur et al.	Applicant
US2007/0020924(A1)	2007-01-01	Wang et al.	Applicant
US2007/0026147(A1)	2007-02-01	Chen et al.	Applicant
US2007/0067609(A1)	2007-03-01	Chen et al.	Applicant
US2007/0099415(A1)	2007-05-01	Chen et al.	Applicant
US2007/0119370(A1)	2007-05-01	Ma et al.	Applicant
US2007/0119371(A1)	2007-05-01	Ma et al.	Applicant
US2007/0128862(A1)	2007-06-01	Ma et al.	Applicant
US2007/0128863(A1)	2007-06-01	Ma et al.	Applicant
US2007/0128864(A1)	2007-06-01	Ma et al.	Applicant
DE19627017	1997-01-01		Applicant
DE19820147	1999-07-01		Applicant
EP344352	1989-12-01		Applicant
EP429270	1991-05-01		Applicant
EP442490	1991-08-01		Applicant
EP799641	1997-10-01		Applicant
EP1167569	2002-01-01		Applicant
FR2626110	1989-07-01		Applicant
FR2692597	1993-12-01		Applicant
GB2355727	2001-05-01		Applicant
JP58098917	1983-06-01		Applicant
JP58100419	1983-06-01		Applicant
JP60065712	1985-04-01		Applicant
JP61035847	1986-02-01		Applicant
JP61069508	1986-04-01		Applicant
JP61210623	1986-09-01		Applicant
JP62091495	1987-04-01		Applicant
JP62141717	1987-06-01		Applicant
JP62167297	1987-07-01		Applicant
JP62171999	1987-07-01		Applicant
JP62232919	1987-10-01		Applicant
JP63062313	1988-03-01		Applicant
JP63085098	1988-04-01		Applicant
JP63090833	1988-04-01		Applicant
JP63222420	1988-09-01		Applicant
JP63222421	1988-09-01		Applicant
JP63227007	1988-09-01		Applicant
JP63252420	1988-10-01		Applicant
JP63266814	1988-11-01		Applicant
JP64009895	1989-01-01		Applicant
JP64009896	1989-01-01		Applicant
JP64009897	1989-01-01		Applicant
JP64037832	1989-02-01		Applicant
JP64082615	1989-03-01		Applicant
JP64082617	1989-03-01		Applicant
JP64082671	1989-03-01		Applicant
JP64082676	1989-03-01		Applicant
JP1103982	1989-04-01		Applicant
JP1103996	1989-04-01		Applicant
JP64090524	1989-04-01		Applicant
JP1117017	1989-05-01		Applicant
JP1143221	1989-06-01		Applicant
JP1143233	1989-06-01		Applicant
JP1154511	1989-06-01		Applicant
JP1236657	1989-09-01		Applicant
JP1245512	1989-09-01		Applicant
JP1264218	1989-10-01		Applicant
JP1270593	1989-10-01		Applicant
JP1272108	1989-10-01		Applicant
JP1290221	1989-11-01		Applicant
JP1290222	1989-11-01		Applicant
JP1296673	1989-11-01		Applicant
JP1303770	1989-12-01		Applicant
JP1305894	1989-12-01		Applicant
JP1313927	1989-12-01		Applicant
JP2012814	1990-01-01		Applicant
JP2014513	1990-01-01		Applicant
JP2017634	1990-01-01		Applicant
JP2063115	1990-03-01		Applicant
JP2074029	1990-03-01		Applicant
JP2074587	1990-03-01		Applicant
JP2106822	1990-04-01		Applicant
JP2129913	1990-05-01		Applicant
JP2162717	1990-06-01		Applicant
JP2172895	1990-07-01		Applicant
JP2196092	1990-08-01		Applicant
JP2203517	1990-08-01		Applicant
JP2230690	1990-09-01		Applicant
JP2230722	1990-09-01		Applicant
JP2246161	1990-10-01		Applicant
JP2264491	1990-10-01		Applicant
JP2283084	1990-11-01		Applicant
JP2304916	1990-12-01		Applicant
JP3019211	1991-01-01		Applicant
JP3022569	1991-01-01		Applicant
JP3023294	1991-01-01		Applicant
JP3023299	1991-01-01		Applicant
JP3044967	1991-02-01		Applicant
JP3048421	1991-03-01		Applicant
JP3070124	1991-03-01		Applicant
JP3185716	1991-08-01		Applicant
JP3208885	1991-09-01		Applicant
JP3234025	1991-10-01		Applicant
JP3286522	1991-12-01		Applicant
JP3286531	1991-12-01		Applicant
JP4031391	1992-02-01		Applicant
JP4031396	1992-02-01		Applicant
JP4100292	1992-04-01		Applicant
JP4111418	1992-04-01		Applicant
JP4132214	1992-05-01		Applicant
JP4132681	1992-05-01		Applicant
JP4151822	1992-05-01		Applicant
JP4162418	1992-06-01		Applicant
JP4175299	1992-06-01		Applicant
JP4186824	1992-07-01		Applicant
JP4212411	1992-08-01		Applicant
JP4260696	1992-09-01		Applicant
JP4273120	1992-09-01		Applicant
JP4285167	1992-10-01		Applicant
JP4291916	1992-10-01		Applicant
JP4325500	1992-11-01		Applicant
JP4328874	1992-11-01		Applicant
JP5029228	1993-02-01		Applicant
JP5047665	1993-02-01		Applicant
JP5047666	1993-02-01		Applicant
JP5047668	1993-02-01		Applicant
JP5074717	1993-03-01		Applicant
JP5074724	1993-03-01		Applicant
JP5102189	1993-04-01		Applicant
JP5160152	1993-06-01		Applicant
JP5175143	1993-07-01		Applicant
JP5175145	1993-07-01		Applicant
JP5182906	1993-07-01		Applicant
JP5186295	1993-07-01		Applicant
JP5206036	1993-08-01		Applicant
JP5234899	1993-09-01		Applicant
JP5235047	1993-09-01		Applicant
JP5251339	1993-09-01		Applicant
JP5270997	1993-10-01		Applicant
JP5283336	1993-10-01		Applicant
JP5291152	1993-11-01		Applicant
JP5304334	1993-11-01		Applicant
JP5343327	1993-12-01		Applicant
JP5343685	1993-12-01		Applicant
JP6045606	1994-02-01		Applicant
JP6132236	1994-05-01		Applicant
JP6177381	1994-06-01		Applicant
JP6196809	1994-07-01		Applicant
JP6222388	1994-08-01		Applicant
JP6224138	1994-08-01		Applicant
JP6230421	1994-08-01		Applicant
JP6252057	1994-09-01		Applicant
JP6291048	1994-10-01		Applicant
JP7070752	1995-03-01		Applicant
JP7086269	1995-03-01		Applicant
JP7300649	1995-11-01		Applicant
JP8181076	1996-07-01		Applicant
JP8245291	1996-09-01		Applicant
JP8264530	1996-10-01		Applicant
JP9260786	1997-10-01		Applicant
JP9293681	1997-11-01		Applicant
JP10188840	1998-07-01		Applicant
JP10190128	1998-07-01		Applicant
JP10308283	1998-11-01		Applicant
JP11269652	1999-10-01		Applicant
JP2000031387	2000-01-01		Applicant
JP2000058777	2000-02-01		Applicant
JP2000068072	2000-03-01		Applicant
JP2000087029	2000-03-01		Applicant
JP2000138094	2000-05-01		Applicant
JP2000218445	2000-08-01		Applicant
JP2000319772	2000-11-01		Applicant
JP2000340883	2000-12-01		Applicant
JP2000353666	2000-12-01		Applicant
JP2001020075	2001-01-01		Applicant
JP2001062244	2001-03-01		Applicant
JP2001111000	2001-04-01		Applicant
JP2001152339	2001-06-01		Applicant
JP2001172767	2001-06-01		Applicant
JP2001189312	2001-07-01		Applicant
JP2001217206	2001-08-01		Applicant
JP2001220287	2001-08-01		Applicant
JP2001220294	2001-08-01		Applicant
JP2001240972	2001-09-01		Applicant
JP2001254181	2001-09-01		Applicant
JP2001284042	2001-10-01		Applicant
JP2001303251	2001-10-01		Applicant
JP2001328900	2001-11-01		Applicant
JP2000178735	2008-06-01		Applicant
WO-9002216	1990-03-01		Applicant
WO-9110510	1991-07-01		Applicant
WO-9302111	1993-02-01		Applicant
WO-9617107	1996-06-01		Applicant
WO-9618756	1996-06-01		Applicant
WO-9806889	1998-02-01		Applicant
WO-9851838	1998-11-01		Applicant
WO-9901595	1999-01-01		Applicant
WO-9913504	1999-03-01		Applicant
WO-9929924	1999-06-01		Applicant
WO-9941423	1999-08-01		Applicant
WO-9965064	1999-12-01		Applicant
WO-0011721	2000-03-01		Applicant
WO-0015865	2000-03-01		Applicant
WO-0015881	2000-03-01		Applicant
WO-0016377	2000-03-01		Applicant
WO-0054320	2000-09-01		Applicant
WO-0063957	2000-10-01		Applicant
WO-0079019	2000-12-01		Applicant
WO-0079576	2000-12-01		Applicant
WO-0115220	2001-03-01		Applicant
WO-0117692	2001-03-01		Applicant
WO-0127346	2001-04-01		Applicant
WO-0127347	2001-04-01		Applicant
WO-0129280	2001-04-01		Applicant
WO-0129891	2001-04-01		Applicant
WO-0129893	2001-04-01		Applicant
WO-0136702	2001-05-01		Applicant
WO-0140541	2001-06-01		Applicant
WO-0166832	2001-09-01		Applicant
WO-0201628	2002-01-01		Applicant
WO-0208485	2002-01-01		Applicant
WO-0243115	2002-05-01		Applicant
WO-0245167	2002-06-01		Applicant
WO-0245871	2002-06-01		Applicant
WO-0246489	2002-06-01		Applicant
WO-02067319	2002-08-01		Applicant
WO-2004106584	2004-12-01		Applicant
WO-2005027211	2005-03-01		Applicant

Non-Patent Literature (60)

Ashtiani, et al. “Pulsed Nucleation Layer of Tungsten Nitride Barrier Film and its Application in DRAM and Logic Manufacturing,” SEMI Technical Symposium: Innovations in Semiconductor Manufacturing (STS: ISM), SEMICON Korea 2006, Semiconductor Equipment and Materials International, pp. 1-6.Applicant
Bader, et al. “Integrated Processing Equipment,” Solid State Technology, Cowan Pub., vol. 33, No. 5 (May 1, 1990), pp. 149-154.Applicant
Bedair “Atomic Layer Epitaxy Deposition Processes,” J. Vac. Sci. Techol. 12(1) (Jan./Feb. 1994).Applicant
Cameron, et al. “Atomic Layer Deposition of SiO2 and TiO2 in Alumina Tubular Membranes,” Langmuir, vol. 16, No. 19, American Chemical Society, 2000 pp. 7435-7444.Applicant
Choi, et al. “Stability of TiB2 as a Diffusion Barrier on Silicon,” J. Electrochem. Soc. 138(10) (Oct. 1991), pp. 3062-3067.Applicant
Choi, et al. “The Effect of Annealing on Resistivity of Low Pressure Chemical Vapor Deposited Titanium Diboride,” J. Appl. Phys. 69(11) (Jun. 1, 1991), pp. 7853-7861.Applicant
Clark-Phelps, et al. “Engineered Tantalum Aluminate and Hafnium Aluminate ALD Films for Ultrathin Dielectric Films with Improved Electrical and Thermal Properties,” Mat. Res. Soc. Symp. Proc. vol. 670 (2001).Applicant
Derbyshire “Applications of Integrated Processing,” Solid State Technology, US, Cowan Pub., vol. 37, No. 12 (Dec. 1, 1994), pp. 45-47.Applicant
Eisenbraum, et al. “Atomic Layer Deposition (ALD) of Tantalum-based materials for zero thickness copper barrier applications,” Proceedings of the IEEE 2001 International Interconnect Technology Conference (Cat. No. 01EX461) 2001.Applicant
Elam, et al. “Nucleation and Growth During Tungsten Atomic Layer Deposition on SiO2 Surfaces,” Thin Solid Films, 386, (2001), pp. 41-52.Applicant
Elers, et al. “NbCl5 As a Precursor in Atomic Layer Epitaxy,” Appl. Surf. Sci., vol. 82/83 (1994), pp. 468-474.Applicant
George, et al. “Atomic Layer Controlled Deposition of SiO2 and Al2O3 Using ABAB . . . Binary Reaction Sequence Chemistry,” Appl. Surf. Sci., vol. 82/83 (1994), pp. 460-467.Applicant
George, et al. “Surface Chemistry for Atomic Layer Growth,” J. Phys. Chem. 1996, 100, 13121-13131.Applicant
Goswami, et al. Transition Metals Show Promise as Copper Barriers, Semiconductor International, ATMI, San Jose—May 1, 2004, Semiconductor International, pp. 1-7.Applicant
Hong, et al. “Characteristics of PAALD-TaN thin films derived from TAIMATA precursor for copper metallization”, Internconnect Technology Conference, 2004. Proceedings of the IEEE 2004 International, Jun. 7-9, 2004, pp. 9-11.Applicant
Hultman, et al. “Review of the Thermal and Mechanical Stability of TiN-based Thin Films,” Zeitschnft Fur Metallkunde, 90(10) (Oct. 1999), pp. 803-813.Applicant
Hwang, et al. “Nanometer-Size α-PbO2-type TiO2 in Garnet: A Thermobarometer for Ultrahigh-Pressure Metamorphism,” Science Vo. 288 (Apr. 14, 2000).Applicant
IBM Tech. Disc. Bull. “Knowledge-Based Dynamic Scheduler in Distributed Computer Control,” (Jun. 1990), pp. 80-84.Applicant
IBM Tech. Disc. Bull. “Multiprocessor and Multitasking Architecture for Tool Control of the Advanced via Inspection Tools,” (May 1992), pp. 190-191.Applicant
Kim, et al. “Atomic Layer Deposition of Low Resistivity and High-Density Tungsten Nitride Thin Film Using B2H6, WF6 and NH3,” Electrochem. Solid-State Lett., vol. 9, Issue 3, (2006), pp. C54-C57.Applicant
Kitigawa, et al. “Hydrogen-mediated Low Temperature Epitaxy of Si in Plasma-enhanced Chemical Vapor Deposition,” Applied Surface Science (2000), pp. 30-34.Applicant
Klaus, et al. “Atomic Layer Deposition of SiO2 Using Catalyzed and Uncatalyzed Self-Limiting Surface Reactions,” Surface Review and Letters, vol. 6, Nos. 3 & 4 (1999) 435-448.Applicant
Klaus, et al. “Atomic Layer Deposition of Tungsten using Sequential Surface Chemistry with a Sacrificial Stripping Reaction,” Thin Solid Films 360 (2000), pp. 145-153. (Accepted Nov. 16, 1999).Applicant
Klaus, et al. “Atomically Controlled Growth of Tungsten and Tungsten Nitride Using Sequential Surface Reactions,” Applied Surface Science, 162-163 (2000), pp. 479-491.Applicant
Kukli, et al. “Atomic Layer Epitaxy Growth of Tantalum Oxide Thin Films from Ta(OC2H5)5 and H2O,” Journal of the Electrochemical Society, vol. 142, No. 5, May 1995; p. 1670-5.Applicant
Kukli, et al. “In situ Study of Atomic Layer Epitaxy Growth of Tantalum Oxide Thin Films From Ta(OC2H5)5 and H2O,” Applied Surface Science, vol. 112, Mar. 1997, p. 236-42.Applicant
Kukli, et al. “Properties of {Nb1-xTax}2O5 Solid Solutions and {Nb1-xTax}2O5-ZrO2 Nanolaminates Grown by Atomic Layer Epitaxy,” 1997; p. 785-93.Applicant
Kukli, et al. “Properties of Ta2O5-Based Dielectric Nanolaminates Deposited by Atomic Layer Epitaxy,” Journal of the Electrochemical Society, vol. 144, No. 1, Jan. 1997; p. 300-6.Applicant
Kukli, et al. “Tailoring the Dielectric Properties of HfO2-Ta2-O5 Nanolaminates,” Applied Physics Letters, vol. 68, No. 26, Jun. 24, 1996; p. 3737-9.Applicant
Lee, “The Preparation of Titanium-Based Thin Film by CVD Using Titanium Chlorides as Precursors,” Chemical Vapor Deposition, 5(2) (Mar. 1999), pp. 69-73.Applicant
Lee, et al. “Pulsed Nucleation for Ultra-High Aspect Ratio Tungsten Plugfill,” Materials Research Society, 2002, pp. 649-653.Applicant
Martensson, et al. “Atomic Layer Epitaxy of Copper on Tantalum,” Chemical Vapor Deposition, 3(1) (Feb. 1, 1997), pp. 45-50.Applicant
Martensson, et al. “Atomic Layer Epitaxy of Copper, Growth & Selectivity in the Cu (II)-2,2.6,6-Tetramethyl-3, 5-Heptanedion ATE/H2 Process,” J. Electrochem. Soc.,145(8) (Aug. 1998), pp. 2926-2931.Applicant
Martensson, et al. “Use of Atomic Layer Epitaxy for Fabrication of Si/TiN/Cu Structures,” J. Vac. Sci. & Tech. B, vol. 17, No. 5, (Sept. 1999) pp. 2122-2128.Applicant
Maydan “Cluster Tools for Fabrication of Advanced Devices,” Jap. J. of Applied Physics, Extended Abstracts, 22nd Conference Solid State Devices and Materials (1990), pp. 849-852.Applicant
McGeachin “Synthesis and Properties of Some β-diketimines Derived From Acetylacetone, and Their Metal Complexes,” Canadian J. of Chemistry, vol. 46 (1968), pp. 1903-1912.Applicant
Min, et al. “Atomic Layer Deposition of TiN Thin Films by Sequential Introduction of Ti Precursor and NH3,” Mat. Res. Soc. Symp. Proc. vol. 514 (1998).Applicant
Min, et al. “Chemical Vapor Deposition of Ti-Si-N Films with Alternating Source Supply,” Mat., Res. Soc. Symp. Proc., vol. 564 (Apr. 5, 1999), pp. 207-210.Applicant
Min, et al. “Metal-organic Atomic-layer Deposition of Titanium-silicon-nitride films,” Applied Physics Letters, vol. 75, No. 11 (Sep. 13, 1999).Applicant
Niinisto, et al. “Synthesis of Oxide Thin Films and Overlayers by Atomic Layer Epitaxy for Advanced Applications,” Materials Science and Engineering B41 (1996) 23-29.Applicant
Ohba, et al. “Thermal Decomposition of Methylhydrazine and Deposition Properties of CVD TiN Thin Films,” Conference Proceedings, Advanced Metallization for ULSI Applications in 1993 (1994), pp. 143-149.Applicant
Park, et al. “Performance improvement of MOSFET with HfO2Al2O3 laminate gate dielectric and CVD-TaN metal gate deposited by TAIMATA”, Electron Devices Meeting, 2003. IEDM '03 Techinical Digest. IEEE International Dec. 8-10, 2003, pp. 13.6.1-13.6.4.Applicant
Proceedings of the ICEEE 1998 International Interconnect Technology Conference—San Francisco, California, Jun. 1-3, 1998.Applicant
Ritala, et al. “Atomic Force Microscopy Study of Titanium Dioxide Thin Films Grown by Atomic Layer Epitaxy,” Thin Solid Films, vol. 228, No. 1-2 (May 15, 1993), pp. 32-35.Applicant
Ritala, et al. “Atomic Layer Epitaxy Growth of TiN Thin Films From TiI4 and NH3,” J. Electrochem. Soc., vol. 145, No. 8 (Aug. 1998) pp. 2914-2920.Applicant
Ritala, et al. “Atomic Layer Epitaxy Growth of TiN Thin Films,” J. Electrochem. Soc., 142(8) (Aug. 1995), pp. 2731-2737.Applicant
Ritala, et al. “Effects of Intermediate Zinc Pulses on Properties of TiN and NbN Films by Atomic Layer Epitaxy,” Applied Surface Science, vol. 120, No. 3-4, (Dec. 1997), pp. 199-212.Applicant
Ritala, et al. “Growth of Titanium Dioxide Thin Films by Atomic Layer Epitaxy,” Thin Solid Films, vol. 225, No. 1-2 (Mar. 25, 1993) pp. 288-295.Applicant
Ritala, et al. “Perfectly Conformal TiN and Al2O3 Films Deposited by Atomic Layer Deposition,” Chemical Vapor Deposition, Jan. 1999, 5, No. 1, pp. 6-9.Applicant
Ritala, et al. “Surface Roughness Reduction in Atomic Layer Epitaxy Growth of Titanium Dioxide Thin Films,” Thin Solid-Films, vol. 249, No. 2 (Sept. 15, 1994), pp. 155-162.Applicant
Rossnagel, et al. “Plasma-enhanced Atomic Layer Deposition of Ta and Ti for Interconnect Diffusion Barriers,” J. Vacuum Sci. & Tech. B., vol. 18, No. 4 (Jul. 2000), pp. 2016-2020.Applicant
Scheper, et al. “Low-temperature Deposition of Titanium Nitride Films From Dialkylhydrazine-based Precursors,” Materials Science in Semiconductor Processing 2(1999), pp. 149-157.Applicant
Shenai, et al. “Correlation of vapor pressure equation and film properties with trimethylindium purity for the MOVPE grown III-V compounds,” Journal of Crystal Growth 248 (2003) pp. 91-98.Applicant
Solanki, et al. “Atomic Layer Deposition of Copper Seed Layers,” Electrochemical and Solid State Letters, 3(10) (2000), pp. 479-480.Applicant
Suzuki, et al. “A 0.2-μm Contact Filing by 450° C.-hydrazine-reduced TiN film With Low Resistivity,” IEDM 92-979, pp. 11.8.1-11.8.3.Applicant
Suzuki, et al. “LPCVD-TiN Using Hydrazine and TiCl4,” VMIC Conference (Jun. 8-9, 1993), pp. 418-423.Applicant
Wise, et al. “Diethyldiethoxysilane as a New Precursor for SiO2 Growth on Silicon”, Mat. Res. Soc. Symp. Proc., vol. 334 (1994), pp. 37-43.Applicant
Yamaga, et al. “Atomic Layer Epitaxy of ZnS by a New Gas Supplying System in a Low-pressure Metalorganic Vapor Phase Epitaxy,” J. of Crystal Growth 117 (1992), pp. 152-155.Applicant
Yamaguchi, et al. “Atomic-layer Chemical-Vapor-Deposition of Silicon Dioxide Films With Extremely Low Hydrogen Content,” Appl. Surf. Sci., vol. 130-132 (1998), pp. 202-207.Applicant
Yang, et al. “Atomic Layer Deposition of Tungsten Film from WF6/B2H6: Nucleation Layer for Advanced Semiconductor Devices,” Conference Proceedings ULSI XVII (2002), Materials Research Society, pp. 655-660.Applicant

Abstract