US 8,973,806 B2Grant

Fine grained Ni-based alloys for resistance to stress corrosion cracking and methods for their design

Issue Date:2015-03-10

•12 Claims

•13 Drawing Sheets

Abstract

A class of nickel based alloys having a fine grain structure resistant to stress corrosion cracking, and methods of alloy design to produce further alloys within the class are presented. The alloys act as suitable welding materials in similar applications to that of Alloy 622. The fine-grained structure of these novel alloys may also be advantageous for other reasons as well such as wear, impact, abrasion, corrosion, etc. These alloys have similar phases to Alloy 622 in that they are composed primarily of austenitic nickel, however the phase morphology is a much finer grained structure opposed to the long dendritic grains common to Alloy 622 when it is subject to cooling rates from a liquid state inherent to the welding process.

Metadata

Assignee

Scoperta, Inc.

Inventor

Justin Lee Cheney

Application Information

Application Number:US 14/136,235

Filing Date:2013-12-20

Priority Date:2011-03-23

Art Unit:1735

Classifications

IPC:

B23K31/02B23K35/22B23K35/34C23C4/06B22F5/12B22F7/08B23K35/02B23K35/30C22C1/02C22C19/03C22C19/05C22F1/10

Patent Drawings (13 sheets)

Description

Incorporation by Reference to Any Priority Applications

[0001] Any and all application for which foreign or domestic priority claim is identified in the Application Data Sheet as filed with the present application are hereby incorporated by reference under 37 CFR 1.57.

Technical Field

[0002] The present invention relates generally to corrosion resistant alloys typically used in cladding operations to protect steel surfaces in power generation, chemical processing, oil and gas, and other industries.

Description of the Related Art

[0003] In corrosion prone environments, nickel-based alloys are frequently employed as weld overlays. Austenitic nickel is the desired phase for corrosion performance and thermal expansion compatibility with mild steel. While the current offering of Alloy 622 or similar high Cr and Mo Ni-based alloys offer good corrosion protection, they commonly fail in applications subject to thermal fluctuations, such as boiler tubes. Such thermal fluctuations induce stress corrosion cracking in Alloy 622 or similar alloys along the grain boundaries, which commonly extend from the surface of a weld bead down to the weld/substrate interface. Along this path there is no resistance to crack propagation, and it is a common failure mechanism in applications under thermal cycling.

[0004] Dilution of the weld bead with the underlying steel is also a factor which must be minimized if the corrosive performance of the weld overlay is to be maintained. The presence of iron in the weld metal reduces corrosion performance with increasing concentration. In practice, weld parameters are closely controlled and the weld is deposited in the vertical position so that dilution is minimized below a certain level, such as 10-15% whereas typical weld overlay conditions will create 30% dilution. A competing interest towards minimizing dilution is increasing productivity. Increased amperage and wire feed rates allow the material to be deposited faster and thus enable the cladding to be performed in a minimal time.

Brief Summary of the Embodiments of the Invention

[0005] The present invention is directed toward a class of alloys having a fine grain structure resistant to stress corrosion cracking, and methods of alloy design to produce further alloys within the class. The purpose of these alloys are to act as suitable welding materials in similar applications to that of Alloy 622. The fine-grained structure of these novel alloys may also be advantageous for other reasons as well such as wear, impact, abrasion, corrosion, etc. These alloys have similar phases to Alloy 622 in that they are composed primarily of austenitic nickel, however the phase morphology is a much finer grained structure opposed to the long dendritic grains common to Alloy 622 when it is subject to cooling rates from a liquid state inherent to the welding process. In one embodiment, the fine grained structure of the alloy class presented here offer improved stress corrosion cracking resistance because there is no path of easy crack propagation as there is in typical Alloy 622 or similar alloys. In another embodiment, the alloys are manufactured into a form of cored wire which allows for improved productivity and minimal dilution. These alloys may be employed in corrosion protection of boiler tubes in power generation plants or a wide variety of other potential applications.

[0006] In one embodiment, a composition of matter is presented, comprising a balance of nickel; between approximately 20.5 and 30 wt. % chromium; between approximately 5.5 and 18.5 wt. % molybdenum; between 0 and approximately 1.75 wt. % boron; between 0 and approximately 3.5 wt. % silicon; between 0 and approximately 5 wt. % titanium; between 0 and approximately 17 wt. % niobium; and between 0 and approximately 15 wt. % tin. In a further embodiment, the composition comprises a balance of nickel; between approximately 25 and 30 wt. % chromium; between approximately 5.5 and 15.5 wt. % molybdenum; between approximately 0.3 and 1.6 wt. % boron; and between 0 and approximately 3.5 wt. % silicon; but does not include titanium, niobium, or tin except as impurities. In a still further embodiment, the composition comprises a balance of nickel; between approximately 26 and 29 wt. % chromium; between approximately 10 and 15.5 wt. % molybdenum; between approximately 0.4 and 1.2 wt. % boron; and between approximately 1 and 3 wt. % silicon.

[0007] In a further embodiment, the composition of matter is in the form of a cored welding wire. The composition is present in the aggregate combination of the sheath and the core powder materials. The weld bead formed using the welding wire is an alloy having the composition, along with some inevitable dilution caused by the substrate. In particular, the sheath may be an alloy also having a composition in the above ranges, but with a melting temperature less than the final weld bead. During welding, the sheath is melted and carries the powder components to the substrate to form a weld pool. The powder components diffuse with the melted sheath to form a liquid weld pool. Because the weld pool has a higher melting temperature than the sheath, the weld pool cools rapidly, limiting dilution by the substrate and forming a fine-grained structure.

Brief Description of the Drawings

[0008] The present invention, in accordance with one or more various embodiments, is described in detail with reference to the following figures. The drawings are provided for purposes of illustration only and merely depict typical or example embodiments of the invention. These drawings are provided to facilitate the reader's understanding of the invention and shall not be considered limiting of the breadth, scope, or applicability of the invention. It should be noted that for clarity and ease of illustration these drawings are not necessarily made to scale.

[0009] FIG. 1 illustrates a modeling diagram developed using compositional ranges of chromium, nickel, and molybdenum.

[0010] FIG. 2A illustrates a coarse grained dendritic microstructure typical of Alloy 622 type weld overlays used in boiler tube corrosion protection.

[0011] FIG. 2B is an optical micrograph, at the same scale as FIG. 2A, illustrating the fine grained microstructure of typical embodiments of the invention, specifically NiBalCr27.35Mo10.71Fe0.23 Si2.71B1.17 (in wt. %) produced in ingot form.

[0012] FIG. 3A illustrates a weld trial using the stringer bead technique.

[0013] FIG. 3B illustrates a weld trial using the oscillation technique.

[0014] FIG. 4A is a commercially available Alloy 622.

[0015] FIG. 4B illustrates an embodiment of the present invention, alloy Ni_BalCr_27.35Mo_10.71Fe_0.23Si_2.71B_1.17.

[0016] FIG. 5 is an optical micrograph (500×) of an embodiment of the invention, alloy Ni_BalCr_28.86Mo_15.17Fe_0.14Si_1.13B_0.47, welded on to flat steel plate showing image analysis used to determine grain size.

[0017] FIG. 6 is a zoom-in of FIG. 5, showing detail of the 63 μm grain.

[0018] FIGS. 7A and 7B are optical micrographs of Alloy 622 welded with GMAW technique.

[0019] FIG. 8 is an x-ray diffraction spectrum of welded Ni_BalCr_28.86Mo_15.17Fe_0.14Si_1.13B_0.47showing a phase structure of entirely austenitic nickel, the desired phase for corrosion performance and thermal expansion compatibility with mild steel.

[0020] FIG. 9 is a schematic detailing the manufacture and welding process of a cored wire.

[0021] The figures are not intended to be exhaustive or to limit the invention to the precise form disclosed. It should be understood that the invention can be practiced with modification and alteration, and that the invention be limited only by the claims and the equivalents thereof.

Detailed Description of the Embodiments of the Invention

[0022] The present invention is directed toward a class of alloys having a fine grain structure resistant to stress corrosion cracking, and methods of alloy design to produce further alloys within the class. The purpose of these alloys are to act as suitable welding materials in similar applications to that of Alloy 622. The fine-grained structure of these novel alloys may also be advantageous for other reasons as well such as wear, impact, abrasion, corrosion, etc. These alloys have similar phases to Alloy 622 in that they are composed primarily of austenitic nickel, however the phase morphology is a much finer grained structure opposed to the long dendritic grains common to Alloy 622 when it is subject to cooling rates from a liquid state inherent to the welding process. In one embodiment, the fine grained structure of the alloy class presented here offer improved stress corrosion cracking resistance because there is no path of easy crack propagation as there is in typical Alloy 622 or similar alloys. In another embodiment, the alloys are manufactured into a form of cored wire which allows for improved productivity and minimal dilution. These alloys may be employed in corrosion protection of boiler tubes in power generation plants or a wide variety of other potential applications. As used herein the term “fine grain structure” refers to alloys having grain lengths that are less than 150 μm.

[0023] In one embodiment, a method of designing fine grained weld materials comprises using theoretical liquidus temperature calculations to design for alloy chemistries located on or near deep eutectics, thus insuring a fine grained alloy microstructure under cooling rates common to the welding process, 5000 K/s or less. Predicted liquidus temperatures of various experimental compositional ranges may be developed using computer modeling. FIG. 1 illustrates a modeling diagram developed using compositional ranges of chromium, nickel, and molybdenum. Compositions having the lowest predicted melting temperature will typically have finer grain size. In the illustrated modeling diagram, the compositions 101 shown in red have the lowest melting temperatures. In the described embodiment, the method further comprises establishing constraints where certain elements are restricted to minimum values and given this constraint, the alloy with the lowest melting temperature is selected. In the illustrated compositions, desired corrosion performance requires at least 6 at. % molybdenum. Accordingly, in the illustrated embodiment, alloys having low melting temperatures under these constraint 102, are investigated further. Such further investigations, in some embodiments, may comprise production of alloy ingots for property testing and welding wires for application testing. In the illustrated embodiment, a minimum amount of Cr may also be employed as a constraint, for example 20 wt. %.

[0024] FIG. 2 illustrates a comparison between grain structures in commercial alloys and embodiments of the invention. FIG. 2A illustrates a coarse grained dendritic microstructure typical of Alloy 622 type weld overlays used in boiler tube corrosion protection. This example is 27% Cr, 11% Mo, balance Ni (in weight percent) produced in ingot form. As can be seen, single grains are greater than several millimeters in length. FIG. 2B is an optical micrograph, at the same scale as FIG. 2A, illustrating the fine grained microstructure of typical embodiments of the invention, specifically Ni_BalCr_27.35Mo_10.71Fe_0.23Si_2.71B_1.17(in wt. %) produced in ingot form.

[0025] FIG. 3 illustrates weld trials using alloys Ni_BalCr_27.35Mo_10.71Fe_0.23Si_2.71B_1.17(301) and Ni_BalCr_28.86Mo_15.17Fe_0.14S_1.13B_0.47(302). FIG. 3A illustrates a weld trial using the stringer bead technique on alloy #301 and FIG. 3B illustrates a weld trial using the oscillation technique on alloys #301 and #302.

[0026] FIG. 4 illustrates optical micrographs (500×) comparing commercially available alloys and an embodiment of the current invention. FIG. 4A is a commercially available Alloy 622. FIG. 4B illustrates an embodiment of the present invention, alloy Ni_BalCr_27.35Mo_10.71Fe_0.23Si_2.71B_1.17. Alloy 622 posses grain much larger than 100 μm extending across the entire field of view (>150 μm in total height). Alloy Ni_BalCr_27.35Mo_10.71Fe_0.23Si_2.71B_1.17possesses a fine grain structure with lengths 100 μm or less. Both alloys were processed using the conventional gas metal arc welding (GMAW) technique, a process which completely melts the alloy and allows a cooling rate slower than 5000 K/s.

[0027] FIG. 5 is an optical micrograph (500×) of an embodiment of the invention, alloy Ni_BalCr_28.86Mo_15.17Fe_0.14Si_1.13B_0.47, welded on to flat steel plate showing image analysis used to determine grain size. Grain sizes between 36 μm and 63 μm are highlighted.

[0028] FIG. 6 is a zoom-in of FIG. 5, showing detail of the 63 μm grain. The minimum dimension of the grain (501) which is 4.5 μm and the maximum dimension of the grain (502) which is 63 μm. For the purposes of this disclosure the maximum dimension of the grain is the characteristic length of the grain. Grain length is critical to the stress corrosion cracking behavior of the material.

[0029] FIGS. 7A and 7B are optical micrographs of Alloy 622 welded with GMAW technique. FIG. 7A is a 500× image showing detailed grains which extend out of field of view and cannot be accurately measured along their maximum level at this magnification. FIG. 7B is a 50× image showing the full length of grains in Alloy 622 at 1250 μm or greater.

[0030] FIG. 8 is an x-ray diffraction spectrum of welded Ni_BalCr_28.86Mo_15.17Fe_0.14Si_1.13B_0.47showing a phase structure of entirely austenitic nickel, the desired phase for corrosion performance and thermal expansion compatibility with mild steel.

[0031] FIG. 9 is a schematic depicting the welding process involving a cored wire manufactured using the disclosed techniques. Powder feedstock (902) is inserted into a metallic sheath material (901). During the welding process, the sheath and powder feedstock are melted and alloyed together in the arc (903) and deposited as a weld pool (904) on the substrate (905). In some embodiments, the melting temperature of the sheath material is controlled such that it is below the melting temperature of the weld pool.

[0032]

TABLE 1

List of alloy compositions
Alloy	Form	Ni	Cr	Mo	Fe	C	B	Si	Ti	Nb	Sn	alpha	T

1	Ingot	53.6	26.33	11.04	0	0	0	4.9	0	0	4.14	1.39	1361
2	Ingot	45.38	26.92	12.25	0	0	0	3.71	0	0	11.74	1.35	1361
3	Ingot	44.13	23.09	16.39	0	0	0	2.74	1.56	12.09	0	1.39	1479
4	Ingot	41.32	22.44	18.48	0	0	0	3.73	4.77	9.25	0	1.34	1521
5	Ingot	58.58	27	10.12	0	0	1.2	3.11	0	0	0	1.31	1497
6	Ingot	55.62	29.48	10.1	0	0	1.63	3.17	0	0	0	1.27	1560
7	Ingot	47.49	29.32	10.68	0	0	1.15	2.98	0	0	8.39	1.26	1518
8	Ingot	39.39	20.58	7.7	0	0	0.33	0.85	0	16.83	14.33	1.30	1497
9	Ingot	55.36	26.6	13.8	0	0	1.18	3.06	0	0	0	1.29	1542
10	Ingot	56.8	28.75	10.14	0	0	1.2	3.11	0	0	0	1.32	1489
11	Ingot	59.9	27.38	9.47	0	0	1.19	2.05	0	0	0	1.37	1429
12	Ingot	55.73	27.84	13.23	0	0	1.17	2.03	0	0	0	1.36	1470
13	Ingot	56.47	27.32	12.41	0	0	0.78	3.03	0	0	0	1.38	1425
14	Ingot	60.63	28.35	7.13	0	0	0.79	3.09	0	0	0	1.40	1381
15	Ingot	58.18	27.26	11.79	0	0	0.77	2	0	0	0	1.36	1442
16	Ingot	59.27	26.68	12.7	0	0	0.37	0.97	0	0	0	1.26	1551
A	Wire	57.83	27.35	10.71	0.23	0	1.17	2.71	0	0	0	N/A	N/A
B	Wire	54.23	28.86	15.17	0.14	0	0.47	1.13	0	0	0	N/A	N/A
C	Wire	59.2	26.7	12.7	0	0	0.4	1	0	0	0	N/A	N/A
D	Wire	67.86	25.78	5.65	0	0.02	0.69	0	0	0	0	N/A	N/A

[0033] Table 1 is a list of alloys compositions in weight percent and corresponding melting temperatures, T (in Kelvin), produced and evaluated as embodiments of the present invention. Alloys 1-16 were produced in ingot form. These alloys were evaluated, and based on those results, the alloys A, B, C, and D were manufactured in the form of welding wire. It should be noted that the compositions of A, B, C, and D could not be made to replicate any of Alloy 1-16 due to manufacturing variations and restrictions. The alloys fall within the compositional range: Ni_balCr_20.5-30Mo_5.5-18.5B_0-1.75Si_0-5Ti_0-5Nb_0-17Sn_0-15, measured in weight percent. Some embodiments of the invention may fall within the compositional range: Ni_balCr_25-30Mo_5.5-15.5B_0.3-1.6Si_0-3.5, measured in weight percent. Still further embodiments may fall within the compositional range: Ni_balCr_26-29Mo_10-15.5B_0.4-1.2Si_1-3, measured in weight percent. As understood in the art, any composition may have certain impurities. Impurities common in embodiments of the invention include Fe, Nb, and C.

[0034] One embodiment of the invention comprises a nickel-based alloy possessing phase morphologies on the order of 150 microns or less in the longest dimension when cooled from a liquid state at 5000 K/s or less. In a further embodiment the microstructure is primarily 90% or greater formed of austenitic nickel. In a still further embodiment, the microstructure contains silicide, boride, carbide, aluminide, or nitride precipitates. In one embodiment, the Nickel-based alloy comprises one or a combination of Cr or Mo. In a second embodiment, the alloy further comprises one or a combination of Si or B. In a third embodiment, the alloy comprises one or a combination of N, O, Mg, Ca, Ti, Mn, Fe, Co, Cu, Zn, Nb, Ag, Sn, or W. In a fourth embodiment of the invention, the alloy is given by the formula (in weight percent) Ni_100-a-b-c-dCr_aMo_bSi_cB_dFe_ewhere a=20 to 32, b=4 to 20, c=0 to 6, d=0 to 6, e=0 to 5.

[0035] In a fifth embodiment of the invention, the alloy comprises one or a mixture of the following compositions: Ni_BalCr_27.35Mo_10.71Fe_0.23Si_2.71B_1.17(Alloy A); Ni_BalCr_28.86Mo_15.17Fe_0.14Si_1.13B_0.47(Alloy B); Ni_BalCr_26.7Mo_12.7Si_1.0B_0.4(Alloy C); Ni_BalCr_25.78Mo_5.65B_0.69C_0.02(Alloy D). In various embodiments, the alloy may be in the form of a welding wire, whether solid, flux-cored, or metal-cored. The alloys may be used as a weld overlay coating for corrosion protection. The alloys may be deposited using welding techniques such as the gas metal arc weld technique or thermal spray techniques such as twin wire arc spray. The alloys may be used to product boiler tubes and related assemblies in power generation plants. In some embodiments, these alloys achieving higher deposition rates via the various welding (gas metal arc weld or other) and thermal spray techniques (twin wire arc spray or other) because of their lower melting temperatures.

[0036] Another embodiment of this invention corresponds to the manufacture of cored welding wire to minimized dilution under conditions of high productivity.

[0037] FIG. 9 illustrates the manufacture of a cored wire that involves a sheath material 901 which is wrapped into a cylinder and filled with a powder 902, whereas the melting and alloying between both the sheath and powder material in the arc 903 results in the desired alloy. Cored wire is used primarily for its ability to deliver higher current densities and thus higher levels of productivity. Typically, the cored wire is manufactured using common alloys. In the case of Ni—Cr—Mo alloys, pure nickel or nickel-chromium alloy strip is used to form the sheath material 901, and the powder 902 contains an elevated molybdenum content. When the sheath and powder materials are melted and combined 903 in a spray during the welding process, the desired Ni—Cr—Mo alloy content is deposited in the weld bead 904. It is inherent although undesirable in this process for some of the substrate material 905 to dilute the weld bead composition. Accordingly, the weld bead 904 will comprise a weld component having a composition falling with one of the disclosed compositional ranges and a substrate dilution component having a composition similar to that of the substrate material 905.

[0038] In further embodiments, the cored wire may comprise a sheath 901 formed of a first alloy falling within one of the compositional ranges disclosed herein and the powder material 902 may comprise powder material components such that the weld bead formed forms a second alloy falling within one of the compositional ranges disclosed herein. For example, a first alloy for the sheath 901 and a second alloy for the weld bead 904 may be selected such that the different in the melting temperatures between the two alloys is at least 50° C., or preferably at least 100° C. For example, alloys 1 or 2 from Table 1 may be used as sheaths for welding wires with appropriate powder cores to form alloys 7 or 8, respectively. Of course, any sheath and final weld composition may be utilized. The upward shift in melting temperature of the weld pool as the powder alloys with the sheath will cause the bead to solidify rapidly effectively lowering the dilution further and allowing for highly controlled welding—for example, in the vertical position. In addition to the processing advantages created by the disclosed manufacturing techniques, this example will also contain the fine-grain structure designed to prevent stress corrosion cracking in the weld

[0039] In this particular embodiment, the cored wire is manufactured in such a way that the melting temperature of the sheath material is lower (>50° C.) than the melting temperature of the final composition in the weld bead. Design of such an article of manufacture can be achieved with thermodynamic modeling techniques such as those shown in FIG. 1. A cored wire, which has a sheath material of lower melting temperature than the final composition of the weld bead, allows for increased productivity and decreased dilution.

[0040] It is well known to those in the field that increased welding power, typically achieved through increasing the amperage, results in higher material deposition rates and a higher level of dilution. Thus, in operations such as boiler cladding where minimizing dilution is a critical concern, productivity must be sacrificed. In a cored wire system the sheath carries the current in the welding process and dictates the current density. Sheath materials of higher melting temperature require more power to melt.

[0041] In the disclosed embodiment, a relatively low power level is required to weld the low melting temperature sheath material. During the welding process the powder combines with the molten sheath material forming a molten weld pool of a final desired composition. The alloying of the powder with the molten sheath effectively raises the melting temperature of the final weld bead composition causing the weld pool to solidify rapidly.

[0042] The relatively low power input limits the dilution experienced in the welding process because less heat is input into the substrate. Sheath materials with very low melting temperatures allow the productivity to be increased while simultaneously lowering the dilution. The rapid solidification of the weld pool is also advantageous in that it prevents the weld pool from dripping down the substrate surface in vertical welding operations.

Example 1

[0043] Manufacture of Wire of Alloy 9, using a sheath material composed of Alloy 11. Alloy 11 has a calculated melting temperature of 1429 K (1155° C.) roughly 200° C. below the melting temperature of Inconel 622 (Tm—1351-1387° C.) and 200° C.-300° C. below the melting temperature of pure Nickel and Ni—Cr alloys Tm=1345-1455° C.). The melting temperature of Inconel 622 is relevant as that is a common feedstock used in solid wire cladding. The melting temperature of pure Nickel and Ni—Cr alloys is relevant in that it is the sheath material used in the manufacture of Ni—Cr—Mo cored wires. Thus, the Alloy 11 sheath requires less heat input during the welding process and will provide the advantage of lower process dilution and higher productivity over the other conventional solutions (solid Inconel 622 wire, cored wire of Ni or Ni—Cr sheath). The powder feedstock in this manufacturing example is a mixture of Ni—Cr, Ni—Mo, Ni—B, Ni—Si, B, and Si powder components such that when alloyed together with the sheath composed of Alloy 11 will form a weld bead with the composition of Alloy 9. The melting temperature of Alloy 9 is 1542 K (1267° C.), roughly 100° C. above the melting temperature of the sheath material. The upward shift in melting temperature of the weld pool as the powder alloys with the sheath will cause the bead to solidify rapidly effectively lowering the dilution further and allowing for highly controlled welding in the vertical position. In addition to the processing advantages created by the disclosed manufacturing techniques, this example will also contain the fine-grain structure designed to prevent stress corrosion cracking in the weld.

[0044] Although the invention is described above in terms of various exemplary embodiments and implementations, it should be understood that the various features, aspects and functionality described in one or more of the individual embodiments are not limited in their applicability to the particular embodiment with which they are described, but instead can be applied, alone or in various combinations, to one or more of the other embodiments of the invention, whether or not such embodiments are described and whether or not such features are presented as being a part of a described embodiment. Thus, the breadth and scope of the present invention should not be limited by any of the above-described exemplary embodiments.

[0045] Terms and phrases used in this document, and variations thereof, unless otherwise expressly stated, should be construed as open ended as opposed to limiting. As examples of the foregoing: the term “including” should be read as meaning “including, without limitation” or the like; the term “example” is used to provide exemplary instances of the item in discussion, not an exhaustive or limiting list thereof; the terms “a” or “an” should be read as meaning “at least one,” “one or more” or the like; and adjectives such as “conventional,” “traditional,” “normal,” “standard,” “known” and terms of similar meaning should not be construed as limiting the item described to a given time period or to an item available as of a given time, but instead should be read to encompass conventional, traditional, normal, or standard technologies that may be available or known now or at any time in the future. Likewise, where this document refers to technologies that would be apparent or known to one of ordinary skill in the art, such technologies encompass those apparent or known to the skilled artisan now or at any time in the future.

[0046] The presence of broadening words and phrases such as “one or more,” “at least,” “but not limited to” or other like phrases in some instances shall not be read to mean that the narrower case is intended or required in instances where such broadening phrases may be absent. Additionally, the various embodiments set forth herein are described in terms of exemplary block diagrams, flow charts and other illustrations. As will become apparent to one of ordinary skill in the art after reading this document, the illustrated embodiments and their various alternatives can be implemented without confinement to the illustrated examples. For example, block diagrams and their accompanying description should not be construed as mandating a particular architecture or configuration.

Claims

Certificate of Correction present

The claims shown below may not include correction changes. Use the corrected PDF for authoritative text.

The invention claimed is:

1. A method, comprising:

welding a substrate to form a weld bead using a cored welding wire, the cored welding wire comprising a sheath comprising nickel and having a sheath melting temperature and a powder core disposed within the sheath;

wherein the weld bead has a weld melting temperature at least 50° C. greater than the sheath melting temperature; and

wherein during welding the sheath and powder core are melted to form a welding pool, wherein the welding pool is applied to the substrate to form the weld bead, the welding pool comprising a substrate dilution component and a weld component.

2. The method of claim 1, wherein the weld component comprises:

a balance of nickel;

between approximately 20.5 and 30 wt. % chromium;

between approximately 5.5 and 18.5 wt. % molybdenum;

between 0 and approximately 1.75 wt. % boron;

between 0 and approximately 3.5 wt. % silicon;

between 0 and approximately 17 wt. % niobium; and

between 0 and approximately 15 wt. % tin.

3. The method of claim 2, wherein the sheath comprises:

a balance of nickel;

between approximately 20.5 and 30 wt. % chromium;

between approximately 5.5 and 18.5 wt. % molybdenum;

between 0 and approximately 1.75 wt. % boron;

between 0 and approximately 3.5 wt. % silicon;

between 0 and approximately 5 wt. % titanium;

between 0 and approximately 17 wt. % niobium; and

between 0 and approximately 15 wt. % tin.

4. The method of claim 1, wherein the substrate comprises a boiler tube.

5. The method of claim 1, wherein the weld bead is part of a weld overlay.

6. A method of applying a coating to a substrate comprising:

providing a metal cored welding wire containing an outer sheath formed from an alloy of a certain melting temperature and an inner powder comprising one or more metal alloy compositions; and

welding the metal cored welding wire onto a substrate to form an alloy coating, wherein the sheath and powder of the metal cored wire are melted together during welding;

wherein the alloy coating has a melting temperature at least 5020 C. greater than a melting temperature of the outer sheath;

wherein welding the metal cored welding wire onto a substrate comprises forming a welding pool, the welding pool comprising a substrate dilution component and a weld component.

7. The method of claim 6, wherein the alloy coating has a melting temperature at least 100° C. greater than the melting temperature of the alloy sheath.

8. The method of claim 6, wherein the metal cored wire comprises a nickel-based sheath and a powder core.

9. The method of claim 6, wherein the weld component comprises:

a balance of nickel;

between approximately 20.5 wt. % and 30 wt. % chromium;

between approximately 5.5 wt. % and 18.5 wt. % molybdenum;

between approximately 0 wt. % and 1.75 wt. % boron;

between approximately 0 wt. % and 3.5 wt. % silicon;

between approximately 0 wt. % and 5 wt. % titanium;

between approximately 0 wt. % and 17 wt. % niobium; and

between approximately 0 wt. % and 15 wt. % tin.

10. A method of applying a coating to a substrate Comprising:

providing a metal cored welding wire containing an outer sheath formed from an alloy of a certain melting temperature and an inner powder comprising one or more metal alloy compositions; and

welding the metal cored welding wire onto a substrate to form an alloy coating, wherein the sheath and powder of the metal cored wire are melted together during welding;

wherein the alloy coating has a melting temperature at least 50° C. greater than a melting temperature of the outer sheath;

wherein welding the metal cored welding wire onto a substrate comprises forming a welding pool, the welding pool comprising a substrate dilution component and a weld component, the weld component comprising in weight percent a mixture of one or more of the following:

Ni_balCr_27.35Mo_10.71Fe_0.23Si_2.71B_1.17;

Ni_balCr_28.86Mo_15.17Fe_0.14Si_1.13B_0.47;

Ni_balCr_26.7Mo_12.7Si_1.0B_0.4; and

Ni_balCr_25.78Mo_5.65B_0.69C_0.02.

11. The method of claim 6, whereas the sheath alloy component of the cored wire comprises:

nickel;

between approximately 20.5 wt. % and 30 wt. % chromium;

between approximately 5.5 wt. % and 18.5 wt. % molybdenum;

between approximately 0 wt. % and 1.75 wt. % boron;

between approximately 0 wt. % and 3.5 wt. % silicon;

between approximately 0 wt. % and 5 wt. % titanium;

between approximately 0 wt. % and 17 wt. % niobium; and

between approximately 0 wt. % and 15 wt. % tin.

12. A method of applying a coating to a substrate comprising:

providing a metal cored welding wire containing an outer sheath formed from an alloy of a certain melting temperature and an inner powder comprising one or more metal alloy compositions; and

welding the metal cored welding wire onto a substrate to form an alloy coating, wherein the sheath and powder of the metal cored wire are melted together during welding;

wherein the alloy coating has a melting temperature at least 50° C. greater than a melting temperature of the outer sheath;

wherein the sheath alloy component of the cored wire comprises in weight percent a mixture of one or more of the following:

Ni_balCr_27.35Mo _10.71Fe_0.23Si_2.71B_1.17;

Ni_balCr_28.86Mo_15.17Fe_0.14Si_1.13B_0.47;

Ni_balCr_26.7Mo_12.7Si_1.0B_0.4; and

Ni_balCr_25.78Mo_5.65B_0.69C_0.02.

Patent Citations (84)

Patent	Date	Inventor	Cited By
US2043952(A)	1936-06-01	Ffield	Applicant
US2156306(A)	1939-05-01	Rapatz	Applicant
US2936229(A)	1960-05-01	Shepard	Applicant
US3024137(A)	1962-03-01	Witherell	Applicant
US3181970(A)	1965-05-01	Witherell et al.	Applicant
US3448241(A)	1969-06-01	Penson et al.	Examiner
US3554792(A)	1971-01-01	Johnson	Applicant
US3650734(A)	1972-03-01	Kantor et al.	Applicant
US3843359(A)	1974-10-01	Fiene et al.	Applicant
US3859060(A)	1975-01-01	Eiselstein et al.	Applicant
US3975612(A)	1976-08-01	Nakazaki et al.	Applicant
US4010309(A)	1977-03-01	Peterson	Applicant
US4017339(A)	1977-04-01	Okuda et al.	Applicant
US4042383(A)	1977-08-01	Petersen et al.	Applicant
US4415530(A)	1983-11-01	Hunt	Applicant
US4639576(A)	1987-01-01	Shoemaker et al.	Applicant
US4762681(A)	1988-08-01	Tassen et al.	Applicant
US4981644(A)	1991-01-01	Chang	Applicant
US5306358(A)	1994-04-01	Lai et al.	Applicant
US5375759(A)	1994-12-01	Hiraishi et al.	Applicant
US5618451(A)	1997-04-01	Ni	Applicant
US5861605(A)	1999-01-01	Ogawa et al.	Examiner
US5935350(A)	1999-08-01	Raghu et al.	Applicant
US6210635(B1)	2001-04-01	Jackson et al.	Applicant
US6441334(B1)	2002-08-01	Aida et al.	Applicant
US6608286(B2)	2003-08-01	Jiang	Applicant
US6702906(B2)	2004-03-01	Ogawa et al.	Applicant
US6750430(B2)	2004-06-01	Kelly	Examiner
US7361411(B2)	2008-04-01	Daemen et al.	Applicant
US7491910(B2)	2009-02-01	Kapoor et al.	Applicant
US7569286(B2)	2009-08-01	Daemen et al.	Applicant
US7776451(B2)	2010-08-01	Jiang et al.	Applicant
US7935198(B2)	2011-05-01	Branagan et al.	Applicant
US8153935(B2)	2012-04-01	Jang et al.	Applicant
US8187725(B2)	2012-05-01	Kiser et al.	Applicant
US8562759(B2)	2013-10-01	Cheney et al.	Applicant
US8562760(B2)	2013-10-01	Cheney et al.	Applicant
US8640941(B2)	2014-02-01	Cheney	Applicant
US8647449(B2)	2014-02-01	Cheney et al.	Applicant
US2002/0148533(A1)	2002-10-01	Kim et al.	Examiner
US2004/0062677(A1)	2004-04-01	Chabenat et al.	Applicant
US2004/0079742(A1)	2004-04-01	Kelly	Examiner
US2004/0115086(A1)	2004-06-01	Chabenat et al.	Applicant
US2006/0191606(A1)	2006-08-01	Ogawa et al.	Applicant
US2007/0029295(A1)	2007-02-01	Branagan	Applicant
US2007/0090167(A1)	2007-04-01	Arjakine et al.	Applicant
US2007/0284018(A1)	2007-12-01	Hamano et al.	Applicant
US2008/0031769(A1)	2008-02-01	Yeh	Applicant
US2008/0093352(A1)	2008-04-01	Jang et al.	Examiner
US2008/0149397(A1)	2008-06-01	Overstreet	Applicant
US2008/0241580(A1)	2008-10-01	Kiser et al.	Examiner
US2009/0017328(A1)	2009-01-01	Katoh et al.	Applicant
US2009/0258250(A1)	2009-10-01	Daemen et al.	Applicant
US2009/0285715(A1)	2009-11-01	Arjakine et al.	Applicant
US2010/0009089(A1)	2010-01-01	Junod et al.	Applicant
US2010/0044348(A1)	2010-02-01	Buchmann	Applicant
US2010/0101780(A1)	2010-04-01	Ballew et al.	Applicant
US2010/0166594(A1)	2010-07-01	Hirata et al.	Applicant
US2010/0189588(A1)	2010-07-01	Kawatsu et al.	Applicant
US2011/0064963(A1)	2011-03-01	Cheney et al.	Applicant
US2011/0100720(A1)	2011-05-01	Branagan et al.	Applicant
US2011/0139761(A1)	2011-06-01	Sugahara et al.	Examiner
US2011/0171485(A1)	2011-07-01	Kawamoto et al.	Examiner
US2012/0055903(A1)	2012-03-01	Izutani et al.	Examiner
US2012/0156020(A1)	2012-06-01	Kottilingam et al.	Applicant
US2012/0160363(A1)	2012-06-01	Jin et al.	Applicant
US2012/0288400(A1)	2012-11-01	Hirata et al.	Applicant
CN102686762	2012-09-01		Applicant
DE2754437	1979-07-01		Applicant
DE3320513(A)	1983-12-01		Examiner
EP365884	1990-05-01		Applicant
EP1338663	2003-08-01		Applicant
EP2305415	2003-08-01		Applicant
JP58-132393(A)	1982-01-01		Examiner
JP60-133996(A)	1985-07-01		Applicant
JP3-133593(A)	1991-06-01		Applicant
WO2006/086350	2006-08-01		Applicant
WO2011/035193	2011-03-01		Applicant
WO2011/071054	2011-06-01		Applicant
WO2011/158706	2011-12-01		Applicant
WO/2012/037339	2012-03-01		Applicant
WO/2012/129505	2012-09-01		Applicant
WO2013/101561	2013-07-01		Applicant
WO/2013/133944	2013-09-01		Applicant

Non-Patent Literature (15)

Branagan, et al.: Developing extreme hardness (>15GPa) in iron based nanocomosites, Composites Part A: Applied Science and Manufacturing, Elsevier Science Publishers B.V., Amsterdam, NL, vol. 33, No. 6, Jun. 1, 2002, pp. 855-859.Applicant
Canadian Office Action, re CA Application No. 2,774,546, dated Nov. 14, 2013.Applicant
Cheney, et al.: “Development of quaternary Fe-based bulk metallic glasses,” Materials Science and Engineering, vol. 492, No. 1-2, Sep. 25, 2008, pp. 230-235.Applicant
Chinese First Office Action, App. No. 201080051858.0, Issued May 24, 2013.Applicant
International Preliminary Report on Patentability and Written Opinion re PCT Application No. PCT/US2010/049381, mailed Mar. 29, 2012.Applicant
International Search Report re PCT Application No. PCT/US2010/049381, dated Nov. 5, 2010.Applicant
International Search Report re PCT Application No. PCT/US2011/051746, dated Jun. 6, 2012.Applicant
International Preliminary Report on Patentability and Written Opinion re PCT Application No. PCT/US2011/051746, mailed Mar. 28, 2013.Applicant
International Search Report and Written Opinion re PCT Application No. PCT/US2013/025982, mailed May 29, 2013.Applicant
International Search Report re PCT Application No. PCT/US2012/030365, dated Jul. 10, 2012.Applicant
International Preliminary Report on Patentability and Written Opinion re PCT Application No. PCT/US2012/030365, mailed Oct. 3, 2013.Applicant
International Search Report and Written Opinion re PCT Application No. PCT/US2012/070398, mailed Apr. 12, 2013.Applicant
International Search Report and Written Opinion re PCT Application No. PCT/US2013/64391, mailed Dec. 16, 2013.Applicant
Khalifa, et al.: “Effect of Mo—Fe substitution on glass forming ability, thermal stability, and hardness of Fe—C—B—Mo—Cr—W bulk amorphous allows,” Materials Science and Engineering, vol. 490, No. 1-2, Aug. 25, 2008, pp. 221-228.Applicant
Tillack, et al.: “Selection of Nickel, Nickel—Copper, Nickel—Cromium, and Nickel—Chromium—Iron Allows”, AMS Handbook, Welding, Brazing and Soldering, vol. 6,Dec. 1, 1993 pp. 586-592, XP008097120, p. 589.Applicant

Abstract

Description

Incorporation by Reference to Any Priority Applications

Technical Field

Description of the Related Art

Brief Summary of the Embodiments of the Invention

Brief Description of the Drawings

[0009] FIG. 1 illustrates a modeling diagram developed using compositional ranges of chromium, nickel, and molybdenum.

[0010] FIG. 2A illustrates a coarse grained dendritic microstructure typical of Alloy 622 type weld overlays used in boiler tube corrosion protection.

[0012] FIG. 3A illustrates a weld trial using the stringer bead technique.

[0013] FIG. 3B illustrates a weld trial using the oscillation technique.

[0014] FIG. 4A is a commercially available Alloy 622.

[0015] FIG. 4B illustrates an embodiment of the present invention, alloy Ni_BalCr_27.35Mo_10.71Fe_0.23Si_2.71B_1.17.

[0017] FIG. 6 is a zoom-in of FIG. 5, showing detail of the 63 μm grain.

[0018] FIGS. 7A and 7B are optical micrographs of Alloy 622 welded with GMAW technique.

[0020] FIG. 9 is a schematic detailing the manufacture and welding process of a cored wire.

Detailed Description of the Embodiments of the Invention

[0032]

TABLE 1

List of alloy compositions
Alloy	Form	Ni	Cr	Mo	Fe	C	B	Si	Ti	Nb	Sn	alpha	T

1	Ingot	53.6	26.33	11.04	0	0	0	4.9	0	0	4.14	1.39	1361
2	Ingot	45.38	26.92	12.25	0	0	0	3.71	0	0	11.74	1.35	1361
3	Ingot	44.13	23.09	16.39	0	0	0	2.74	1.56	12.09	0	1.39	1479
4	Ingot	41.32	22.44	18.48	0	0	0	3.73	4.77	9.25	0	1.34	1521
5	Ingot	58.58	27	10.12	0	0	1.2	3.11	0	0	0	1.31	1497
6	Ingot	55.62	29.48	10.1	0	0	1.63	3.17	0	0	0	1.27	1560
7	Ingot	47.49	29.32	10.68	0	0	1.15	2.98	0	0	8.39	1.26	1518
8	Ingot	39.39	20.58	7.7	0	0	0.33	0.85	0	16.83	14.33	1.30	1497
9	Ingot	55.36	26.6	13.8	0	0	1.18	3.06	0	0	0	1.29	1542
10	Ingot	56.8	28.75	10.14	0	0	1.2	3.11	0	0	0	1.32	1489
11	Ingot	59.9	27.38	9.47	0	0	1.19	2.05	0	0	0	1.37	1429
12	Ingot	55.73	27.84	13.23	0	0	1.17	2.03	0	0	0	1.36	1470
13	Ingot	56.47	27.32	12.41	0	0	0.78	3.03	0	0	0	1.38	1425
14	Ingot	60.63	28.35	7.13	0	0	0.79	3.09	0	0	0	1.40	1381
15	Ingot	58.18	27.26	11.79	0	0	0.77	2	0	0	0	1.36	1442
16	Ingot	59.27	26.68	12.7	0	0	0.37	0.97	0	0	0	1.26	1551
A	Wire	57.83	27.35	10.71	0.23	0	1.17	2.71	0	0	0	N/A	N/A
B	Wire	54.23	28.86	15.17	0.14	0	0.47	1.13	0	0	0	N/A	N/A
C	Wire	59.2	26.7	12.7	0	0	0.4	1	0	0	0	N/A	N/A
D	Wire	67.86	25.78	5.65	0	0.02	0.69	0	0	0	0	N/A	N/A