US 8,801,960 B2Grant
Lithium-containing complex oxide, non-aqueous secondary battery using the lithium-containing complex oxide, and method for producing the lithium-containing complex oxide
Issue Date:2014-08-12
•19 Claims
•7 Drawing Sheets
Abstract
Because of the composition represented by General Formula: Li1+x+αNi(1−x−y+δ)/2Mn(1−x−y−δ)/2MyO2 (where 0≦x≦0.05, −0.05≦x+α≦0.05, 0≦y≦0.4; −0.1≦δ≦0.1 (when 0≦y≦0.2) or −0.24≦δ≦0.24 (when 0.2<y≦0.4); and M is at least one element selected from the group consisting of Ti, Cr, Fe, Co, Cu, Zn, Al, Ge and Sn), a high-density lithium-containing complex oxide with high stability of a layered crystal structure and excellent reversibility of charging/discharging can be provided, and a high-capacity non-aqueous secondary battery excellent in durability is realized by using such an oxide for a positive electrode.
Metadata
Assignee
- Hitachi Maxell, Ltd.
Inventors
- Atsushi Ueda
- Kazutaka Uchitomi
- Shigeo Aoyama
Application Information
Application Number:US 12/023,704
Filing Date:2008-01-31
Priority Date:2000-11-16
Art Unit:1736
Classifications
IPC:
H01M4/48H01M4/50H01M4/52
Patent Drawings (7 sheets)
Description
Cross-Reference to Related Applications
[0001] This application is a divisional application of U.S. patent application Ser. No. 10/181,163 filed on Jul. 16, 2002, now U.S. Pat. No. 7,351,500, which is a National Stage Application of PCT Application No. PCT/JP01/09967 filed on Nov. 14, 2001, which claims priority to Japanese Patent Application Nos. 2001-282767, filed on Sep. 18, 2001, and 2000-350307, filed on Nov. 16, 2000.
Technical Field
[0002] The present invention relates to a lithium-containing complex oxide that can be used as a material for a positive electrode of a non-aqueous secondary battery, a non-aqueous secondary battery using the lithium-containing complex oxide, and a method for producing the lithium-containing complex oxide.
Background Art
[0003] In recent years, along with the development of portable electronic equipment such as mobile phones and notebook computers, and the commercialization of electric automobiles, there is an increasing demand for a miniaturized and lightweight secondary battery with a high capacity. At present, as a secondary battery with a high capacity satisfying this demand, a non-aqueous secondary battery such as a lithium secondary battery using LiCoO2 for a positive electrode and a carbon material for a negative electrode is being commercialized. Such a lithium secondary battery has a high energy density, and can be miniaturized and reduced in weight, so that it has been paid attention to as a power source of portable electronic equipment.
[0004] LiCoO2 used as a material for a positive electrode of the lithium secondary battery is easy to produce and handle, so that it is often used as a preferable active material. However, LiCoO2 is produced using cobalt, which is rare metal, as a material. Therefore, it is conceivable that a material shortage will become serious in the future. Furthermore, the price of cobalt itself is high and fluctuates greatly, so that it is desired to develop a material for a positive electrode that can be supplied stably at a low cost.
[0005] In view of the above, materials of a lithium-manganese oxide type are expected to be a prospective substitute for LiCoO2 as a material for a positive electrode of a lithium secondary battery. Among them, lithium-manganese oxides with a Spinel structure, such as Li2Mn4O9, Li4Mn5O12, and LiMn2O4, are being investigated. In particular, LiMn2O4 can be charged/discharged in a potential range in the vicinity of 4 V against Li metal. The use of LiMn2O4 is disclosed in at least the following (JP 6 (1994)-76824 A, JP 7 (1995)-73883 A, JP 7 (1995)-230802 A, JP 7 (1995)-245106 A, etc.).
[0006] The theoretical discharge capacity of LiCoO2 is 274 mAh/g. However, when deep charging/discharging is conducted, LiCoO2 is changed in phase to influence a cycle life. Therefore, in an actual lithium secondary battery, the practical discharge capacity falls in a range of 125 to 140 mAh/g.
[0007] In contrast, the theoretical discharge capacity of LiMn2O4 is 148 mAh/g. However, LiMn2O4 also is changed in phase during charging/discharging in the same way as in LiCoO2. Furthermore, in the case of using a carbon material as a negative active material, since the irreversible capacity of the carbon material is large, the discharge capacity that can be used in the case where LiMn2O4 is used actually for a battery is decreased to about 90 to 105 mAh/g. As is apparent from this, when LiMn2O4 is used as a positive active material, the battery capacity cannot be increased compared with the case where LiCoO2 is used as a positive active material.
[0008] Furthermore, the true density of LiCoO2 is 4.9 to 5.1 g/cm3, whereas the true density of LiMn2O4 is very low (i.e., 4.0 to 4.2 g/cm3). Therefore, considering the filing property as a positive active material, LiMn2O4 is more disadvantageous in terms of the capacity.
[0009] Furthermore, in a lithium secondary battery using LiMn2O4 as a positive active material, the structure of LiMn2O4 itself is unstable during charging/discharging. Therefore, there is a problem that the cycle characteristics of the LiMn2O4 type battery are worse than those of the LiCoO2 type battery.
[0010] In order to solve the above-mentioned problem, it also is considered that a layered lithium-manganese oxide of LiMnO2 or the like having a structure different from that of LiMn2O4 is used as a material for a positive electrode. However, as a result of the detailed study of this oxide by the inventors of the present invention, it was found that the properties such as the structure and characteristics are changed remarkably due to the composition of a compound, in particular, the presence of elements constituting the oxide other than Li and Mn, the kind thereof, and the ratio of quantity thereof, and the process in which the oxide is formed.
[0011] For example, in the case where the average valence of Mn approaches 3 due to the fluctuation of the composition of Spinel type lithium-manganese oxide (LiMn2O4), the crystal structure of the above-mentioned oxide is strained to cause a phase change from the Spinel structure of a cubic to a tetragonal, whereby LiMnO2 is formed. The phase change from the cubic to the tetragonal occurs along with charging/discharging in a potential range in the vicinity of 3 V with respect to lithium. Therefore, the lithium secondary battery using the Spinel type lithium-manganese oxide (LiMn2O4) as a material for a positive electrode cannot be used in the same way as in the above-mentioned lithium secondary battery that is charged/discharged at a voltage in the vicinity of 4 V.
[0012] Furthermore, in the case where the structure molar ratio (Li/Mn) is 1, due to the Jahn-Teller effect of trivalent Mn, the crystal structure of LiMnO2 exhibits an orthorhombic system.
[0013] This compound (LiMnO2) can be charged/discharged electrochemically at a Li quantity ratio of 0 to 1.0, which results in a discharge capacity of about 285 mAh/g in terms of theory. However, as the ratio of tetravalent Mn is increased during initial charging, a phase transition to a Spinel structure occurs. Therefore, the initial charge/discharge curve and the second and subsequent charge/discharge curves exhibit different shapes. In addition, the discharge capacity in the case where discharging is terminated at a voltage of 3.5 V or more is decreased remarkably from a theoretical value. Furthermore, the structure is changed with the movement of Mn during charging/discharging. Therefore, cycle durability is insufficient, and rapid charging/discharging cannot be conducted.
[0014] Therefore, in order to commercialize a layered lithium-manganese oxide such as LiMnO2, it is required to solve the problems involved in stabilization of a crystal structure, an increase in capacity due to the enhancement of reversibility of charging/discharging, and durability during a charge/discharge cycle.
Disclosure of Invention
[0015] The present invention, in one aspect, provides a lithium-containing complex oxide that has a stable structure, is excellent in reversibility of charging/discharging and durability during a charge/discharge cycle, and has a high energy density per volume, and to provide a non-aqueous secondary battery using the lithium-containing complex oxide for a positive electrode, which is excellent in durability such as cycle characteristics.
[0016] More specifically, a lithium-containing complex oxide of the present invention includes a composition represented by General Formula: Li1+x+αNi(1−x−y+δ/2Mn(1−x−y−δ)/2MyO2 (where 0≦x≦0.05, −0.05≦x+α≦0.05, 0≦y≦0.4; −0.1≦δ≦0.1 (when 0≦y≦0.2) or −0.24≦δ≦0.24 (when 0.2<y≦0.4); and M is at least one element selected from the group consisting of Ti, Cr, Fe, Co, Cu, Zn, Al, Ge and Sn).
[0017] Furthermore, a method for producing a lithium-containing complex oxide having a composition represented by General Formula: Li1+x+αNi(1−x−y+δ/2Mn(1−x−y−δ)/2MyO2 (where 0≦x≦0.05, −0.05≦x+α≦0.05, 0≦y≦0.4; −0.1≦δ≦0.1 (when 0≦y≦0.2) or −0.24≦δ≦0.24 (when 0.2<y≦0.4); and M is at least one element selected from the group consisting of Ti, Cr, Fe, Co, Cu, Zn, Al, Ge and Sn) is characterized by sintering a complex compound containing at least Ni and Mn as constituent elements and a Li compound.
[0018] Furthermore, a non-aqueous secondary battery of the present invention includes a positive electrode made of a positive active material, a negative electrode made of a negative active material, and a non-aqueous electrolyte, wherein the positive active material is a lithium-containing complex oxide having a composition represented by General Formula: Li1+x+αNi(1−x−y+δ/2Mn(1−x−y−δ)/2MyO2 (where 0≦x≦0.05, −0.05≦x+α≦0.05, 0≦y≦0.4; −0.1≦δ≦0.1 (when 0≦y≦0.2) or −0.24≦δ≦0.24 (when 0.2<y≦0.4); and M is at least one element selected from the group consisting of Ti, Cr, Fe, Co, Cu, Zn, Al, Ge and Sn).
Brief Description of Drawings
[0019] FIG. 1 is a view showing an X-ray diffraction pattern of a lithium-containing complex oxide synthesized in Example 1 according to the present invention.
[0020] FIG. 2 is a view showing an X-ray diffraction pattern of a lithium-containing complex oxide synthesized in Example 8 according to the present invention.
[0021] FIG. 3 is a view showing an X-ray diffraction pattern of a lithium-containing complex oxide synthesized in Example 9 according to the present invention.
[0022] FIG. 4 is a view showing an X-ray diffraction pattern of a lithium-containing complex oxide synthesized in Comparative Example 4 according to the present invention.
[0023] FIG. 5 is a view showing an X-ray diffraction pattern of a lithium-containing complex oxide synthesized in Comparative Example 5 according to the present invention.
[0024] FIG. 6 is a view showing discharge curves of positive electrodes of batteries using, for positive electrodes, the lithium-containing complex oxides synthesized in Examples 1, 6, and 8 according to the present invention, and Comparative Examples 1 and 2.
Best Mode for Carrying Out the Invention
[0025] Hereinafter, the present invention will be described in more detail by way of embodiments. The lithium-containing complex oxide of the present invention is a complex oxide in a very limited composition range based on a composition containing at least Ni and Mn as constituent elements, in which the quantity ratio between Ni and Mn is 1:1, represented by General Formula: Li1+x+αNi(1−x−y+δ)/2Mn(1−x−y−δ)/2MyO2 (where 0≦x≦0.05, −0.05≦x+α≦0.05, 0≦y≦0.4; −0.1≦δ≦0.1 (when 0≦y≦0.2) or −0.24≦δ≦0.24 (when 0.2≦y≦0.4); and M is at least one element selected from the group consisting of Ti, Cr, Fe, Co, Cu, Zn, Al, Ge and Sn).
[0026] According to the present invention, the reason why a lithium-containing complex oxide only in the limited composition range is selected is as follows. In a lithium-manganese oxide, as described above, when the ratio of trivalent Mn is increased, the crystal structure is strained due to the Jahn-Teller effect, and the potential of charging/discharging is lowered. Therefore, it is required to set the valence of Mn to be close to 4. However, as the ratio of tetravalent Mn is increased, a phase transition to a Spinel structure is likely to occur, which necessitates stabilization of the crystal structure.
[0027] The inventors of the present invention considered that, in order to solve the above-mentioned problems, it is effective to increase the average valence of Mn by allowing an excess amount of Li to be contained in LiMnO2 or to substitute an element (e.g., Co, Ni, etc.) capable of stably constituting a layered lithium-containing complex oxide for Mn of LiMnO2, and studied the quantity ratio of Li, the kind of substituent elements, and the quantity ratio thereof in detail.
[0028] Consequently, the following was found: in a composition range based on the composition represented by General Formula LiNi1/2Mn1/2O2 in which the quantity ratio between Ni and Mn is ½:½ (i.e., 1:1), Li is substituted for Ni and Mn by x/2, respectively, the quantity ratio between Ni and Mn is shifted from ½:½ by δ/2 and −δ/2, respectively, the quantity ratio of Li has a width of α, and an element M (where M is at least one element selected from the group consisting of Ti, Cr, Fe, Co, Cu, Zn, Al, Ge and Sn) is substituted for Ni and Ma by y/2, respectively; that is, in a composition range represented by General Formula: Li1+x+αNi(1−x−y+δ)/2Mn(1−x−y−δ)/2MyO2 (where 0≦x≦0.05, −0.05≦x+α≦0.05, 0≦y≦0.4; −0.1≦δ≦0.1 (when 0≦y≦0.2) or −0.24≦δ≦0.24 (when 0.2<y≦0.4); and M is at least one element selected from the group consisting of Ti, Cr, Fe, Co, Cu, Zn, Al, Ge and Sn), a lithium-containing complex oxide whose layered crystal structure is stabilized and which is excellent in reversibility of charging/discharging and durability during a charging/discharging cycle in a potential range in the vicinity of 4 V can be obtained. The following also was found: particularly, in the case of y>0, i.e., in the case where the element M is added, a lithium-containing complex oxide having more excellent characteristics can be obtained.
[0029] This is considered to be caused by the following: the average valence of Mn in the lithium-containing complex oxide has a value in the vicinity of 4 (about 3.3 to 4); and movement of Mn in the crystal is suppressed in the course of doping of Li and removal of Li during charging/discharging. According to the present invention, as the valence of Mn, a value measured by an X-ray absorption spectrometer was used.
[0030] Furthermore, as described above, when the lithium-containing complex oxide containing at least Ni and Mn as constituent elements, having a stable layered structure and being excellent in reversibility of charging/discharging and durability during a charging/discharging cycle, is subjected to an X-ray diffraction measurement using a CuKα-ray, diffraction peaks corresponding to those of (003) and (104) of LiNiO2 are present at a diffraction angle 2θ in the vicinity of 18° and 44°, one for each, and in a range of 63° to 66°, two diffraction peaks corresponding to those of (108) and (110) are present. Thus, it was found that the above-mentioned lithium-containing complex oxide is a single-phase complex oxide having the same characteristics as those of LiNiO2.
[0031] The diffraction pattern was studied in more detail. Consequently, the following also was found: assuming that the areas of the diffraction peaks in the vicinity of 18° and 44° (i.e., accumulated intensity) are I18 and I44, the ratio I44/I18 is 0.9<I44/I18≦1.2 (when 0≦y≦0.2) or 0.7≦I44/I18≦1 (when 0.2<y≦0.4), and the difference θa between diffraction angles (2θ) of two diffraction peaks in the above-mentioned range of 63° to 66° is 0.3°≦θa≦0.6° (when 0≦y≦0.2) or 0.55°≦θa≦0.75° (when 0.2<y≦0.4).
[0032] The lithium-containing complex oxide having such a charging/discharging curve can be charged/discharged in a voltage range in the vicinity of 4 V in the same way as in LiMn2O4 having a Spinel structure, and can be substituted for LiCoO2 that is a conventional positive active material.
[0033] It also was found that the lithium-containing complex oxide having the above-mentioned composition has a large true density (i.e., 4.55 to 4.95 g/cm3) and a high volume energy density. The true density of the lithium-containing complex oxide containing Mn in a predetermined range is varied largely depending upon the composition thereof. However, its structure is stabilized and a single phase is likely to be formed in the above-mentioned narrow composition range. Therefore, the above-mentioned lithium-containing complex oxide is considered to have a large true density close to that of LiCoO2. Particularly in the case of a composition dose to a stoichiometric ratio, the true density becomes a large value, and in −0.015≦x+α≦0.015, a high-density complex oxide of about 4.7 g/cm3 or more is obtained.
[0034] Furthermore, as described above, the lithium-containing complex oxide of the present invention is based on the composition in which the quantity ratio between Ni and Mn is 1:1 as in LiNi1/2Mn1/2O2. However, the composition was studied in more detail, the following was found: a lithium-containing complex oxide having particularly excellent characteristics can be obtained in the vicinity of the composition where the quantity ratio of Ni, Mn and M is 1:1:1 (i.e., the composition represented by General Formula: LiNi1/3Mn1/3M1/3O2 where y=⅓).
[0035] In the above-mentioned General Formula: Li1+x+αNi(1−x−y+δ)/2Mn(1−x−y−δ)/2MyO2 (where M is at least one element selected from the group consisting of Ti, Cr, Fe, Co, Cu, Zn, Al, Ge and Sn), in the composition range of 0≦y≦0.2, only a small shift (δ/2) in quantity ratio between Ni and Mn can be permitted, whereas in the composition range of 0.2<y≦0.4, the stability of the crystal structure becomes higher, and a single phase is likely to be formed. As a result, even if a shift in quantity ratio between Ni and Mn is increased, an intended lithium-containing complex oxide can be obtained. Therefore, in the above-mentioned General Formula, when 0≦y≦0.2, the range of δ becomes narrow (i.e., −0.1≦δ≦0.1), whereas when 0.2<y≦0.4, the range of δ becomes wide (i.e., −0.24≦δ≦0.24).
[0036] Furthermore, in the composition range of 0.2<y≦0.4, the true density becomes larger than that of the compound in the composition range of 0≦y≦0.2. Therefore, it also was clarified that such a material is suitable for a higher capacity. More specifically, a compound with a stoichiometric composition has a true density of about 4.75 to 4.95 g/cm3 in the composition range of 0.2<y≦0.4, whereas it has a true density of about 4.55 to 4.74 g/cm3 in the composition range of 0≦y≦0.2.
[0037] Herein, the reason why the upper limit value of y is set to be 0.4 is that when the composition at y>0.4, i.e., the substitution amount by the element M becomes larger than 0.4, a heterogeneous phase is likely to be formed in an intended complex oxide, impairing the stability of the compound.
[0038] The use of a compound in a very wide composition range containing a composition range of the lithium-containing complex oxide of the present invention as a material for a positive electrode of a non-aqueous secondary battery has already been disclosed in JP 3064655 B, JP 9 (1997)-199127 A, JP 10 (1998)-69910 A, JP 2000-294242 A, and the like. However, none of them discloses that a lithium-containing complex oxide having particularly excellent characteristics is obtained in a limited composition range where the quantity ratio between Ni and Mn is in the vicinity of 1:1 as disclosed by the present invention. Thus, the present invention would not have been obvious over these prior arts.
[0039] In the above-mentioned lithium-containing complex oxide, it is very difficult to obtain a single phase only by mixing a Li compound, a Mn compound, a Ni compound, and the like, followed by sintering.
[0040] The reason for this is considered as follows: since the diffusion speed of Ni, Mn and the like in a solid is low, it is difficult to allow them to be diffused uniformly in a synthesis reaction, so that they are not distributed uniformly in a generated oxide.
[0041] The inventors of the present invention also studied a method for synthesizing the above-mentioned oxide in detail, and consequently, found that a single phase of the lithium-containing complex oxide of the present invention can be synthesized relatively easily by sintering a complex compound containing at least Ni and Mn as constituent elements and a Li compound. More specifically, a complex compound of constituent elements such as Ni and Mn is synthesized previously, and the resultant compound is sintered together with a Li compound, whereby the metal element is distributed uniformly during the reaction of formation of the oxide, and hence, the formation of a single phase can be simplified. Needless to say, the method for synthesizing the lithium-containing complex oxide of the present invention is not limited to the above method. However, the physical properties (i.e., the structure stability, reversibility of charging/discharging, true density, and the like) of a complex oxide to be generated are considered to be varied largely depending upon which synthesis process is used.
[0042] Herein, as the complex compound containing at least Ni and Mn as constituent elements, for example, a coprecipitated compound containing at least Ni and Mn, a hydrothermally synthesized compound containing at least Ni and Mn, a mechanically synthesized compound containing at least Ni and Mn, and compounds obtained by heat-treating these compounds may be used. An oxide or a hydroxide of Ni and Mn such as Ni0.5Mn0.5(OH)2, NiMn2O4, and Ni0.5Mn0.5OOH can be used preferably. In the case of synthesizing a lithium-containing complex oxide containing M as a constituent element (M is at least one element selected from the group consisting of Ti, Cr, Fe, Co, Cu, Zn, Al, Ge and Sn), an intended oxide can be obtained by mixing a complex compound containing at least Ni and Mn, a Li compound, and a compound containing M, followed by sintering. If possible, it is preferable to use a complex oxide containing M in addition to Ni and Mn from the beginning. The quantity ratio of Ni, Mn and M in the above-mentioned complex compound should be selected appropriately in accordance with the composition of an intended lithium-containing complex oxide.
[0043] As the Li compound, various lithium salts can be used. Examples of the lithium salts include lithium hydroxide.monohydrate, lithium nitrate, lithium carbonate, lithium acetate, lithium bromide, lithium chloride, lithium citrate, lithium fluoride, lithium iodide, lithium lactate, lithium oxalate, lithium phosphate, lithium pyruvate, lithium sulfate, lithium oxide, and the like. Among them, lithium hydroxide.monohydrate is used most preferably because it does not generate gas that adversely affects an environment, such as carbon dioxide, nitrogen oxide, and sulfur oxide.
[0044] The complex compound containing at least Ni and Mn as constituent elements and the Li compound are mixed in a ratio substantially in accordance with the composition of an intended lithium-containing complex oxide. For example, the mixture is sintered in an atmosphere containing oxygen at 700° C. to 1100° C. for 1 to 24 hours, whereby a lithium-containing complex oxide of the present invention can be synthesized.
[0045] Regarding the heat treatment for the above-mentioned sintering, it is preferable that the mixture is once heated to a temperature (about 250° C. to 850° C.) lower than a sintering temperature instead of being heated to a predetermined temperature directly, pre-heated at the temperature, and further heated to a sintering temperature so as to effect a reaction. The reason for this is as follows: in the generation process of the lithium-containing complex oxide of the present invention, the reaction between the Li compound and the complex compound containing at least Ni and Mn as constituent elements is effected in stages, and the lithium-containing complex oxide is generated finally via an intermediate product. More specifically, in the case where the mixture is heated to a sintering temperature directly, the Li compound and the complex compound containing at least Ni and Mn as constituent elements are reacted partially up to the final stage, and the lithium-containing complex oxide thus generated may hinder the reaction of an unreacted substance and impair the uniformity of the composition. Furthermore, in order to shorten a time required for a reaction process and obtain a homogeneous lithium-containing complex oxide, it is effective to conduct heating in stages. The time for pre-heating is not particularly limited; however, it should be conducted generally for about 0.5 to 30 hours.
[0046] Furthermore, in the process of sintering the mixture of the Li compound and the complex compound containing at least Ni and Mn as constituent elements, a mixture obtained in a dry state may be used as it is. However, it is preferable that the mixture is dispersed in a solvent such as ethanol to form a slurry, and mixed in a planet type ball mill for about 30 to 60 minutes, followed by drying. This is because the homogeneity of the lithium-containing complex oxide to be synthesized is enhanced further.
[0047] The above-mentioned heat treatment should be conducted in an atmosphere containing oxygen, i.e., in the air, in an environment of a mixture of inert gas (e.g., argon, helium, nitrogen, etc.) and oxygen gas, or in oxygen gas. The ratio of the oxygen in the environment preferably is set at 10% or more by volume.
[0048] The flow rate of the above-mentioned gas is preferably 1 dm3/min. per 100 g of the mixture, more preferably 1 to 5 dm3/min. In the case where the gas flow rate is small, i.e., in the case where the gas flow speed is low, a reaction is effected non-uniformly, whereby an impurity such as Mn2O3 and Li2MnO3 is likely to be generated.
[0049] By using the lithium-containing complex oxide of the present invention obtained by the above-mentioned method as a positive active material, a non-aqueous secondary battery is produced, for example, as follows.
[0050] As a positive electrode, a positive electrode mixture is used as it is, which is obtained by adding, if required, a conductive assistant such as scaly graphite and acetylene black and a binder such as polytetrafluoroethylene and vinylidene polyfluoride to the above-mentioned lithium-containing complex oxide. Alternatively, a substrate that also functions as a charge collector is coated with or impregnated with the positive electrode mixture, whereby the positive electrode mixture is used under the condition of being integrated with the substrate. Examples of the substrate include a net of metal such as aluminum, stainless steel, titanium and copper; punching metal, expanded metal, foamed metal, metal foil, and the like.
[0051] As a positive active material, the above-mentioned lithium-containing complex oxide may be used by itself. In addition, the above-mentioned lithium-containing complex oxide may be mixed with another active material, or the lithium-containing complex oxide may be used as a complex with another active material. For example, the electron conductivity of the above-mentioned lithium-containing complex oxide is inferior to that of the lithium-containing cobalt oxide such as LiCoO2. Therefore, a voltage drop is likely to be increased during discharging of a large current or at the end of discharging. However, by using a lithium-containing cobalt oxide excellent in electron conductivity mixed with the lithium-containing complex oxide, the voltage drop can be suppressed, whereby discharge characteristics can be enhanced. As the lithium-containing cobalt oxide, not only LiCoO2 but also a compound such as LiCo1−tNitO2 obtained by substituting another element (e.g., Ni) for a part of Co of LiCoO2 can be used. In this case, if the ratio of the lithium-containing cobalt oxide is increased too much, durability such as high-temperature storage characteristics is likely to be decreased. Therefore, it is required that the ratio of the lithium-containing cobalt oxide is set to be 50% or less by mass, based on the entire active material.
[0052] Furthermore, as a negative active material to be opposed to the positive electrode, lithium or a lithium-containing compound generally is used. Examples of the lithium-containing compound include a lithium alloy such as a Li—Al alloy, a Li—Pb alloy, a Li—In alloy and a Li—Ga alloy; elements capable of forming an alloy with lithium such as Si, Sn, and a Mg—Si alloy; and an alloy mainly containing these elements. Furthermore, a carbon material such as graphite and fibrous carbon, a lithium-containing complex nitride, and the like can be used in addition to an oxide material such as a Sn oxide and a Si oxide. Furthermore, the above-mentioned plurality of materials may be combined, and a complex of a carbon material and Si also is used preferably. The same method as that of the positive electrode also applies to the production of the negative electrode.
[0053] Although varied depending upon the kind of a negative active material, the ratio between the positive and negative active materials generally is set as (mass of a positive active material)/(mass of a negative active material)=1.5 to 3.5, whereby the characteristics of the lithium-containing complex oxide can be utilized. In the case of using, as a negative active material, elements capable of forming an alloy with lithium, an alloy mainly containing these elements, a lithium-containing complex nitride, or a complex of these materials with another component such as a carbon material, the capacity of the negative electrode becomes too large at the above-mentioned ratio. Therefore, it is desirable to set (mass of a positive active material)/(mass of a negative active material) to be 4 to 7.
[0054] Examples of a non-aqueous electrolyte in the non-aqueous secondary battery of the present invention include an organic solvent type liquid electrolyte in which an electrolyte is dissolved in an organic solvent (i.e., an electrolytic solution), a polymer electrolyte in which the electrolytic solution is held in a polymer, and the like. Although there is no particular limit to an organic solvent contained in the electrolytic solution or the polymer electrolyte, it is preferable that the organic solvent contains a chain ester in terms of the load characteristics. Examples of the chain ester include chain carbonate such as dimethyl carbonate, diethyl carbonate and ethyl methyl carbonate; ethyl acetate; and methyl propionate. These chain esters may be used alone or in combination. Particularly, in order to enhance low-temperature characteristics, it is preferable that the above-mentioned chain ester occupies 50% by volume of the entire organic solvent. It is particularly preferable that the chain ester occupies 65% by volume or more of the entire organic solvent.
[0055] The organic solvent preferably is composed of the above-mentioned chain ester mixed with another ester having a high dielectric constant (30 or more), so as to enhance a discharge capacity, instead of being composed of only the above-mentioned chain ester. Examples of such an ester include cyclic carbonate such as ethylene carbonate, propylene carbonate, butylene carbonate and vinylene carbonate, γ-butylolactone, ethylene glycol sulfite, and the like. In particular, an ester with a cyclic structure such as ethylene carbonate and propylene carbonate is more preferable.
[0056] An ester with such a high dielectric constant is contained preferably in an amount of 10% by volume, more preferably 20% by volume, based on the entire organic solvent, in terms of the discharge capacity. Furthermore, in terms of the load characteristics, the ester is contained preferably in an amount of 40% by volume or less, more preferably 30% by volume or less.
[0057] Furthermore, examples of the solvent that can be used other than the ester having a high dielectric constant include 1,2-dimethoxyethane, 1,3-dioxolane, tetrahydrofuran, 2-methyl-tetrahydrofuran, diethylether, and the like. In addition, an amineimide type organic solvent, a sulfur-containing or fluorine-containing organic solvent, and the like can be used.
[0058] As an electrolyte to be dissolved in the organic solvent, for example, LiClO4, LiPF6, LiBF4, LiAsF6, LiSbF6, LiCF3SO3, LiC4F9SO3, LiCF3CO2, Li2C2F4(SO3)2, LiN(CF3SO2)2, LiC(CF3SO2)3, LiCnF2n+1SO3 (n≧2), and the like are used alone or in combination. Among them, LiPF6, LiC4F9SO3, and the like that allow satisfactory charge/discharge characteristics to be obtained are used preferably. Although there is no particular limit to the concentration of the electrolyte in the electrolytic solution, the concentration is preferably about 0.3 to 1.7 mol/dm3, more preferably about 0.4 to 1.5 mol/dm3.
[0059] Furthermore, for the purpose of enhancing the safety and storage characteristics of a battery, an aromatic compound may be contained in a non-aqueous electrolytic solution. As the aromatic compound, benzenes having an alkyl group such as cydohexylbenzene and t-butylbenzene, biphenyl, or fluorobenzenes are used preferably
[0060] It is preferable that a separator has sufficient strength and is capable of holding a large quantity of electrolytic solution. In view of this, a microporous film made of polypropylene, polyethylene, polyolefin such as a copolymer of propylene and ethylene, a nonwoven fabric, and the like with a thickness of 5 to 50 μm are used preferably. Particularly, in the case of using a thin separator (5 to 20 μm), battery characteristics such as a charge/discharge cycle and high-temperature storage are likely to be degraded. However, since the lithium-containing complex oxide of the present invention is excellent in safety, even if such a thin separator is used, a battery is allowed to function with stability.
[0061] Hereinafter, the present invention will be described by way of examples. The present invention is not limited to the examples.
Example 1
[0062] Ammonium water with its pH adjusted to about 12 by addition of sodium hydroxide was placed in a reaction container. While strongly stirring the ammonium water, a mixed aqueous solution containing nickel sulfate and manganese nitrate in an amount of 1 mol/dm3, respectively, and 25% by mass of ammonium water were dropped onto the reaction container at 46 cm3/min. and 3.3 cm3/min., respectively, by using a metering pump, whereby a coprecipitated compound of Ni and Mn was generated. At this time, a sodium hydroxide aqueous solution with a concentration of 3.2 mol/dm3 also was dropped simultaneously so that the temperature of the reaction solution was kept at 50° C. and the pH thereof was kept at about 12. Furthermore, the reaction was effected while nitrogen gas was purged at a rate of 1 dm3/min. so that the atmosphere of the reaction solution became inactive.
[0063] The product thus obtained was washed with water, filtered and dried to obtain a hydride containing Ni and Mn in a ratio of 1:1. Then, 0.2 mol of the hydride and 0.198 mol of LiOH.H2O were obtained, and the mixture was dispersed in ethanol to form a slurry. Thereafter, the slurry was mixed in a planet type ball mil for 40 minutes, and dried at room temperature to prepare a mixture. Then, the mixture was placed in a crucible made of alumina, and heated to 800° C. at an air flow of 1 dm3/min. The mixture was kept at that temperature for 2 hours, whereby preheating was conducted. The temperature was raised further to 1000° C., and the mixture was sintered for 12 hours, whereby a lithium-containing complex oxide was synthesized. The prepared compound was ground in a mortar and stored as powder in a desicator.
[0064] The above-mentioned oxide powder was measured for a composition by an atomic absorption spectrometer, revealing that the composition was represented by Li0.99Ni0.5Mn0.5O2. Furthermore, in order to analyze the state of the above-mentioned compound, X-ray absorption spectroscopy (XAS) of Mn was conducted, using BL4 beam port of superconducting small radiation source “Aurora” (produced by Sumitomo Electric Industries, Ltd.) at SR center of Ritsumeikan University. The data thus obtained was analyzed with analysis software “REX” (produced by Rigaku Denki), based on the Literature (Journal of the Electrochemical Society, 146 P2799-2809 (1999)). In order to determine the valence of Mn of the above-mentioned compound, as reference samples, MnO2 and LiNi0.5Mn1.5O4 (both of them are reference samples as compounds having Mn of which average valence is 4), LiMn2O4 (reference sample as a compound having Mn of which average valence is 3.5), LiMnO2 and Mn2O3 (both of them are reference samples as compounds having Mn of which average valence is 3), and MnO (reference sample as a compound having Mn of which average valence is 2) were used. A regression line representing the relationship between the K absorption edge position of n of each reference sample and the valence of Mn was obtained. As a result, the K absorption edge position of MnO2 was substantially the same as that of LiNi0.5Mn1.5O4. Therefore, the average valence of Mn of the above-mentioned compound was determined to be about 4.
[0065] Regarding Ni, it was not possible to obtain a compound appropriate as a reference sample having Ni with a valence of 3 or more, so that its exact valence was not obtained. However, the K absorption edge position of the reference sample having Ni was substantially the same as that of NiO and LiNi0.5Mn1.5O4 that are compounds having Ni of which average valence is 2. Therefore, it was assumed that the average valence of Ni of the above-mentioned compound is about 2.
Example 2
[0066] First, 0.198 mol of hydroxide containing Ni and n in a ratio of 1:1, synthesized in the same way as in Example 1 and 0.202 mol of LiOH.H2O were obtained, and a lithium-containing complex oxide represented by Li1.01Ni0.495Mn0.495O2 was synthesized in the same way as in Example 1.
Example 3
[0067] First, 0.196 mol of hydroxide containing Ni and Mn in a ratio of 1:1, synthesized in the same way as in Example 1 and 0.204 mol of LiOH.H2O were obtained, and a lithium-containing complex oxide represented by Li1.02Ni0.49Mn0.49O2 was synthesized in the same way as in Example 1.
Example 4
[0068] First, 0.194 mol of hydroxide containing Ni and Mn in a ratio of 1:1, synthesized in the same way as in Example 1 and 0.206 mol of LiOH.H2O were obtained, and a lithium-containing complex oxide represented by Li1.03Ni0.485Mn0.485O2 was synthesized in the same way as in Example 1.
Example 5
[0069] First, 0.192 mol of hydroxide containing Ni and Mn in a ratio of 1:1, synthesized in the same way as in Example 1 and 0.208 mol of LiOH. H2O were obtained, and a lithium-containing complex oxide represented by Li1.04Ni0.48Mn0.48O2 was synthesized in the same way as in Example 1.
Example 6
[0070] First, 0.19 mol of hydroxide containing Ni and Mn in a ratio of 1:1, synthesized in the same way as in Example 1 and 0.21 mol of LiOH.H2O were obtained, and a lithium-containing complex oxide represented by Li1.05Ni0.475Mn0.475O2 was synthesized in the same way as in Example 1.
Example 7
[0071] A hydroxide containing Ni, Mn and Co in a ratio of 4.5:4.5:1 was synthesized in the same way as in Example 1, except that a mixed aqueous solution containing nickel sulfate, manganese nitrate and cobalt sulfate in a ratio of 0.9 mol/dm3, 0.9 mol/dm3 and 0.2 mol/dm3, respectively, was dropped. A lithium-containing complex oxide represented by Li0.99Ni0.45Mn0.45Co0.1O2 was synthesized in the same way as in Example 1.
Example 8
[0072] A lithium-containing complex oxide represented by Li0.99Ni0.375Mn0.375Co0.25O2 was synthesized in the same way as in Example 1, except that a mixed aqueous solution containing nickel sulfate, manganese nitrate and cobalt sulfate in a ratio of 0.75 mol/dm3, 0.75 mol/dm8 and 0.5 mol/dm3, respectively, was dropped.
Example 9
[0073] A lithium-containing complex oxide represented by Li0.99Ni0.34Mn0.33Co0.33O2 was synthesized in the same way as in Example 1, except that a mixed aqueous solution containing nickel sulfate, manganese nitrate and cobalt sulfate in a ratio of 0.67 mol/dm3, 0.66 mol/dm3 and 0.66 mol/dm3, respectively, was dropped.
Example 10
[0074] A lithium-containing complex oxide represented by Li0.99Ni0.3Mn0.3Co0.4O2 was synthesized in the same way as in Example 1, except that a mixed aqueous solution containing nickel sulfate, manganese nitrate and cobalt sulfate in a ratio of 0.6 mol/dm3, 0.6 mol/dm3 and 0.8 mol/dm3, respectively, was dropped.
Comparative Example 1
[0075] First, 0.2 mol of LiOH.H2O and 0.2 mol of MnOOH were obtained and mixed in a planet type ball mil for 30 min. to obtain a mixture. The mixture was placed in a crucible made of alumina. The mixture was sintered at 450° C. for 10 hours at a nitrogen stream of 1 dm3/min, whereby orthorhombic lithium-manganese oxide represented by LiMnO0 was synthesized.
Comparative Example 2
[0076] 0.18 mol of hydroxide containing Ni and Mn in a ratio of 1:1 synthesized in the same way as in Example 1 and 0.22 mol of LiOH.H2O were obtained, and a lithium-containing complex oxide represented by Li1.1Ni0.45Mn0.45O2 was synthesized in the same way as in Example 1.
Comparative Example 3
[0077] A lithium-containing complex oxide represented by Li0.99Ni0.25Mn0.25Co0.5O2 was synthesized in the same way as in Example 1, except that a mixed aqueous solution containing nickel sulfate, manganese nitrate and cobalt sulfate in an amount of 0.5 mol/dm3, 0.5 mol/dm3 and 1 mol/dm3, respectively, was dropped.
Comparative Example 4
[0078] A lithium-containing complex oxide represented by Li0.99Ni0.2Mn0.2Co0.6O2 was synthesized in the same way as in Example 1, except that a mixed aqueous solution containing nickel sulfate, manganese nitrate and cobalt sulfate in an amount of 0.4 mol/dm3, 0.4 mol/dm3 and 1.2 mol/dm3, respectively, was dropped.
Comparative Example 5
[0079] A lithium-containing complex oxide represented by Li0.99Ni0.25Mn0.75O2 was synthesized in the same way as in Example 1, except that a mixed aqueous solution containing nickel sulfate and manganese nitrate in an amount of 0.5 mol/dm3 and 1.5 mol/dm3, respectively, was dropped.
Comparative Example 6
[0080] A lithium-containing complex oxide represented by Li0.99Ni0.6Mn0.3Co0.1O2 was synthesized in the same way as in Example 7, except that the ratio between nickel sulfate and manganese nitrate is 1.2 mol/dm3 and 0.6 mol/dm3, respectively. More specifically, the lithium-containing complex oxide in Comparative Example 6 is different from Example 7 only in an amount ratio between Ni and Mn.
Reference Example
[0081] First, 0.2 mol of LiOH.H2O and 0.1 mol of Ni(OH)2, and 0.1 mol of MnOOH were obtained and mixed in a planet type ball mill for 30 minutes to obtain a mixture. The mixture was placed in a crucible made of alumina, and sintered in the air at 800° C. for 10 hours, whereby a lithium-containing complex oxide represented by LiNi0.5Mn0.5O2 was synthesized.
[0082] Table 1 shows the list of the respective lithium-containing complex oxides synthesized in Examples 1 to 10, Comparative Examples 1 to 6, and Reference Example.
[0083]
| TABLE 1 | |||||
|---|---|---|---|---|---|
| Composition [Li1+x+αNi(1−x−y+δ)/2Mn(1−x−y−δ)/2MyO2] | |||||
| x | x + α | y | δ | ||
| Example 1 | Li0.99Ni0.5Mn0.5O2 | 0 | −0.01 | 0 | 0 |
| Example 2 | Li1.01Ni0.495Mn0.495O2 | 0.01 | 0.01 | 0 | 0 |
| Example 3 | Li1.02Ni0.49Mn0.49O2 | 0.02 | 0.02 | 0 | 0 |
| Example 4 | Li1.03Ni0.485Mn0.485O2 | 0.03 | 0.03 | 0 | 0 |
| Example 5 | Li1.04Ni0.48Mn0.48O2 | 0.04 | 0.04 | 0 | 0 |
| Example 6 | Li1.05Ni0.475Mn0.475O2 | 0.05 | 0.05 | 0 | 0 |
| Example 7 | Li0.99Ni0.45Mn0.45Co0.1O2 | 0 | −0.01 | 0.1 | 0 |
| Example 8 | Li0.99Ni0.375Mn0.375Co0.25O2 | 0 | −0.01 | 0.25 | 0 |
| Example 9 | Li0.99Ni0.34Mn0.33Co0.33O2 | 0 | −0.01 | 0.33 | 0.01 |
| Example 10 | Li0.99Ni0.3Mn0.3Co0.4O2 | 0 | −0.01 | 0.4 | 0 |
| Comparative | LiMnO2 | 0 | 0 | 0 | −1 |
| Example 1 | |||||
| Comparative | Li1.1Ni0.45Mn0.45O2 | 0.1 | 0.1 | 0 | 0 |
| Example 2 | |||||
| Comparative | Li0.99Ni0.25Mn0.25Co0.5O2 | 0 | −0.01 | 0.5 | 0 |
| Example 3 | |||||
| Comparative | Li0.99Ni0.2Mn0.2Co0.6O2 | 0 | −0.01 | 0.6 | 0 |
| Example 4 | |||||
| Comparative | Li0.99Ni0.25Mn0.75O2 | 0 | −0.01 | 0 | −0.5 |
| Example 5 | |||||
| Comparative | Li0.99Ni0.6Mn0.3Co0.1O2 | 0 | −0.01 | 0.1 | 0.3 |
| Example 6 | |||||
| Reference | LiNi0.5Mn0.5O2 | 0 | 0 | 0 | 0 |
| Example | |||||
[0084] The above-mentioned lithium-containing complex oxides in Examples 1 to 10 of the present invention, Comparative Examples 1 to 6, and Reference Example were subjected to X-ray diffraction measurement using a CuKα line. The lithium-containing complex oxides in Examples 1 to 10 of the present invention, Comparative Examples 2 to 6, and Reference Example exhibited X-ray diffraction patterns similar to that of LiNiO2 having a layered structure, whereas a peak representing the generation of a heterogeneous phase was recognized in the X-ray diffraction patterns in Comparative Examples 3 to 5 and Reference Example. Furthermore, the X-ray diffraction pattern in Comparative Example 1 is an orthorhombic pattern different from that of LiNiO2. In Examples 1 to 10 of the present invention, and Comparative Examples 2 and 6, a peak caused by the generation of a heterogeneous phase was not recognized. More specifically, there was one diffraction peak where a diffraction angle 2θ was in the vicinity of 18°, there was one diffraction peak where a diffraction angle 2θ was in the vicinity of 44°, and there were two diffraction peaks where the diffraction angle 2θ was present in the vicinity of 63° to 66°. Thus, the obtained oxide was recognized to be a single phase of the lithium-containing complex oxide having a structure similar to that of LiNiO2. Ea the diffraction peak where the diffraction angle 2θ was present in a range of 63° to 66°, a peak by a Kα2 line also was recognized adjacent to a peak by a Kα1 line of Cu. According to the present invention, as the diffraction peak where the diffraction angle 2θ was present in a range of 63° to 66°, only a peak by the Kα1 line is considered.
[0085] Among the above diffraction patterns, the X-ray diffraction patterns in Examples 1, 8, 9, Comparative Example 4 and 5 are illustrated in FIGS. 1 to 5 .
[0086] Table 2 shows values obtained by measuring the ratio (I44/I18) between the accumulated intensities I18 and I44 of the diffraction peaks in the vicinity of 18° and 44°, and the difference θa in diffraction angle between two diffraction peaks in a range of 63° to 66°. The lithium-containing complex oxide in Comparative Example 1 is different from that of the present invention in crystal structure. In the lithium-containing complex oxides in Comparative Examples 3 to 5 and Reference Example, at least three diffraction peaks were present in a range of 63° to 66° due to the generation of a heterogeneous phase. Therefore, Table 2 does not describe the data of these compounds.
[0087]
| TABLE 2 | |||
|---|---|---|---|
| X-ray diffraction measurement | |||
| Ratio of | |||
| accumulated | |||
| intensity | Difference in | ||
| (I44/I18) | diffraction angle 2θ (°) | ||
| Example 1 | 1.13 | 0.313 | |
| Example 2 | 1.14 | 0.348 | |
| Example 3 | 1.10 | 0.390 | |
| Example 4 | 1.11 | 0.435 | |
| Example 5 | 1.08 | 0.510 | |
| Example 6 | 1.06 | 0.555 | |
| Example 7 | 1.04 | 0.553 | |
| Example 8 | 0.88 | 0.672 | |
| Example 9 | 0.83 | 0.700 | |
| Example 10 | 0.77 | 0.617 | |
| Comparative | 0.99 | 0.625 | |
| Example 2 | |||
| Comparative | 0.83 | 0.600 | |
| Example 6 | |||
[0088] In the lithium-containing complex oxides in Examples 1 to 7 where 0≦y≦0.2, the accumulated intensity ratio I44/I18 was in a range of 0.9 to 1.2, and the diffraction angle difference θa was in a range of 0.3° to 0.6°. Furthermore, in Examples 8 to 10 where 0.2<y≦0.4, I44/I18 was in a range of 0.7 to 1, and θa was in a range of 0.55° to 0.75°. On the other hand, in Comparative Examples 2 and 6 where the composition was out of the range of the present invention, I44/I18 or θa deviated from the above range. In Comparative Examples 3 to 5 and Reference Example, at least three diffraction peaks were present in a range of 63° to 66°.
[0089] Next, the lithium-containing complex oxides in Examples 1 to 10 of the present invention, Comparative Examples 1 to 6, and Reference Example were measured for the true density, using a true density measurement apparatus. Table 3 shows the results. The measurement error was −0.03 g/cm3 at maximum.
[0090]
| TABLE 3 | ||
|---|---|---|
| True density (g/cm3) | ||
| Example 1 | 4.74 | |
| Example 2 | 4.72 | |
| Example 3 | 4.68 | |
| Example 4 | 4.65 | |
| Example 5 | 4.62 | |
| Example 6 | 4.57 | |
| Example 7 | 4.75 | |
| Example 8 | 4.76 | |
| Example 9 | 4.80 | |
| Example 10 | 4.82 | |
| Comparative Example 1 | 4.20 | |
| Comparative Example 2 | 4.38 | |
| Comparative Example 3 | 4.83 | |
| Comparative Example 4 | 4.90 | |
| Comparative Example 5 | 4.46 | |
| Comparative Example 6 | 4.65 | |
| Reference Example | 4.61 | |
[0091] In the lithium-containing complex oxides in Examples 1 to 10 of the present invention, the true density was 4.57 to 4.82 g/cm3. Particularly, in Examples 1, 2, and 7 to 10 where the oxide had substantially a stoichiometric composition (i.e., −0.015≦x+α≦0.015), the true density had a large value (i.e., 4.7 g/cm3 or more). Among them, in Examples 8 to 10 where a substitution amount y of the element M was 0.2<y≦0.4, the largest true density (i.e., 4.76 g/cm3 or more) was obtained.
[0092] On the other hand, in Comparative Example 1 using a conventional orthorhombic complex oxide, and Comparative Example 2 where the oxide had a composition remarkably shifted from the stoichiometric composition, the true density had a small value (i.e., 4.5 g/cm3 or less). In Comparative Examples 5 and 6 where the ratio between Ni and Mn was out of the range of the present invention, irrespective of whether the oxide had substantially a stoichiometric composition, the true density was decreased, compared with Examples 1, 2, and 7 to 10 of the present invention. Furthermore, the lithium-containing complex oxide in Reference Example had poor homogeneity due to the generation of a heterogeneous phase or the remaining unreacted substance. Therefore, the true density in Reference Example was decreased, compared with the lithium-containing complex oxide in Example 1.
[0093] Herein, the true densities of the lithium-containing complex oxides in Comparative examples 3 and 4 were higher than those of the examples of the present invention. This is not because complex oxides with the true density shown in Table 3 were obtained as a single phase, but because about 5.1 g/cm3 of LiCoO2 was generated as a heterogeneous phase.
[0094] Next, the lithium-containing complex oxides in Examples 1 to 10 of the present invention and Comparative Examples 1 and 2 were measured for discharge capacity by the following method.
[0095] First, 250 parts by mass of N-methyl-2-pyrrolidone were added to 20 parts by mass of polyvinylidene fluoride as a binder, and the mixture was heated to 60° C. to dissolve polyvinylidene fluoride in N-methyl-2-pyrrolidone, whereby a binder solution was prepared. The above-mentioned lithium-containing complex oxide was added in an amount of 450 parts by mass as a positive active material to the binder solution. Furthermore, 5 parts by mass of carbon black and 25 parts by mass of graphite were added, as a conductive assistant, to the resultant mixture, followed by stirring to prepare a coating in the form of a slurry. The coating thus obtained was applied to both surfaces of an aluminum foil (thickness: 20 μm) uniformly, and dried. Thereafter, the aluminum foil with the coating applied thereto was subjected to pressure forming by a roller press. The resultant aluminum foil was cut to a band-shaped positive electrode (483 mm×54 mm) having an average thickness of 190 μm.
[0096] A separator made of a microporous polyethylene film (thickness: 25 μm) was placed between the positive electrode produced as described above and a negative electrode made of a lithium foil. A non-aqueous solution was used as an electrolyte, in which LiPF6 was dissolved in a concentration of 1.0 mol/dm3 in a mixed solvent containing ethylene carbonate and ethyl methyl carbonate in a volume ratio of 1:3. A reference electrode of lithium was placed. Thus, a battery for evaluating the discharge capacity of the positive electrode was assembled.
[0097] The above battery was charged to 4.3 V at a current density with respective to the area of the positive electrode of 0.2 mA/cm2, and discharged to 3.1 V at the same current density, whereby the discharge capacity was measured. Table 4 shows values obtained by converting the measured discharge capacities into values per unit mass (mAh/g) and per unit volume (mAh/cm3) of the positive active material. FIG. 6 shows discharge curves of the positive electrodes of the batteries using the lithium-containing complex oxides in Examples 1, 6, 8, and Comparative Examples 1 and 2.
[0098]
| TABLE 4 | |||
|---|---|---|---|
| Discharge capacity | |||
| Positive active material | (mAh/g) | (mAh/cm3) | |
| Example 1 | 148 | 702 | |
| Example 2 | 145 | 684 | |
| Example 3 | 143 | 669 | |
| Example 4 | 141 | 656 | |
| Example 5 | 139 | 642 | |
| Example 6 | 136 | 622 | |
| Example 7 | 150 | 713 | |
| Example 8 | 152 | 724 | |
| Example 9 | 153 | 734 | |
| Example 10 | 153 | 737 | |
| Comparative Example 1 | 70 | 294 | |
| Comparative Example 2 | 112 | 491 | |
[0099] The lithium-containing complex oxides in Examples 1 to 10 of the present invention are capable of being operated at a high discharge potential of 3.5 V or more, and exhibited a large discharge capacity (i.e., 136 to 153 mAh/g). In contrast, the lithium-containing complex oxides in Comparative Examples 1 and 2 had a discharge capacity of 130 mAh/g or less, and had a true density smaller than those of the present invention. Therefore, when converted to a discharge capacity per unit volume, the difference in discharge capacity between the oxides of the present invention and those in Comparative Examples 1 and 2 became more conspicuous.
[0100] Furthermore, in order to evaluate the characteristics of the above-mentioned lithium-containing complex oxides as a non-aqueous secondary battery, a non-aqueous secondary battery was produced in the following structure.
Example 11
[0101] By using the lithium-containing complex oxides in Examples 1 and 9 independently as a positive active material, non-aqueous secondary batteries were produced. A positive electrode was obtained by coating an aluminum foil substrate with a paste produced by mixing 92 parts by mass of the positive active material, 4.5 parts by mass of artificial graphite, 0.5 parts by mass of carbon black, and 3 parts by mass of polyvinylidene fluoride, followed by drying and pressure-forming.
[0102] A negative electrode was obtained by coating a copper foil substrate with a paste produced by mixing 92 parts by mass of artificial graphite, 3 parts by mass of low-crystalline carbon, and 5 parts by mass of polyvinylidene fluoride.
[0103] The above-mentioned positive electrode and negative electrode were wound via a separator made of a microporous polyethylene film (thickness: 16 μm). As an electrolyte, a mixed solvent containing ethylene carbonate and ethyl methyl carbonate (volume ratio: 1:2) with LiPF6 dissolved in a concentration of 1.2 mol/dm3 was used. Thus, a cylindrical non-aqueous secondary battery with a capacity of 600 mAh was produced. The mass ratio between the positive active material and the negative active material [(mass of the positive active material)/(mass of the negative active material)] was set at 1.9.
Example 12
[0104] A non-aqueous secondary battery was produced in the same way as in Example 11, except that 70% by mass of the lithium-containing complex oxide in Example 1 and 30% by mass of LiCoO2 were mixed as a positive active material.
Comparative Example 7
[0105] A non-aqueous secondary battery was produced in the same way as in Example 11, except that the lithium-containing complex oxide in Comparative Example 6, LiCoO2 and LiNi0.8Co0.2O2 used for a commercially available non-aqueous secondary battery were used independently as a positive active material.
[0106] The non-aqueous secondary batteries in Examples 11 and 12, and Comparative Example 7 were evaluated for cycle characteristics and high-temperature storage characteristics. The cycle characteristics were evaluated based on the ratio (capacity retention ratio (%)) of a discharge capacity after 100 cycles with respect to a discharge capacity in an initial stage of the cycle when charging/discharging was conducted at a current value of 1C (600 mA). The high-temperature storage characteristics were evaluated based on the change in discharge capacity before and after storage when the batteries were retained at 60° C. for 20 days. More specifically, the high-temperature storage characteristics were evaluated based on the ratio (capacity retention ratio (%)) of a discharge capacity after storage with respect to a discharge capacity before storage, obtained by comparing the discharge capacities when charging/discharging was conducted at a current value of 1C before and after storage. Table 5 shows the results of the evaluation of these characteristics.
[0107]
| TABLE 5 | |||
|---|---|---|---|
| Capacity retention ratio (%) | |||
| Positive active | Cycle | High-temperature | |
| Battery | material | characteristics | storage characteristics |
| Example 11 | Example 1 | 96 | 97 |
| Example 9 | 98 | 98 | |
| Example 12 | Example 1 + | 94 | 96 |
| LiCoO2 | |||
| Comparative | Comparative | 92 | 87 |
| Example 7 | Example 6 | ||
| LiCoO2 | 88 | 91 | |
| LiNi0.8Co0.2O2 | 93 | 90 | |
[0108] The non-aqueous secondary batteries in Examples 11 and 12 using the lithium complex oxide of the present invention as a positive active material exhibited excellent cycle characteristics and high-temperature storage characteristics, irrespective of using a thin separator (thickness: 16 μm). On the other hand, the non-aqueous secondary battery in Comparative Example 6 in which the composition was out of the range of the present invention and the non-aqueous secondary battery in Comparative Example 7 using LiCoO2 or LiNi0.8Co0.2O2 used in a commercially available non-aqueous secondary battery as a positive active material exhibited cycle characteristics and high-temperature storage characteristics that were less excellent than those of the present invention.
[0109] Furthermore, the batteries in Examples 11 and 12 were discharged at a current value of 2C (1200 mA) so as to check the characteristics thereof dung discharge at a large current. As a result, the discharge capacity of the battery in Example 11 was 525 mAh, whereas that of the battery in Example 12 was 573 mAh. Thus, remarkable enhancement of the characteristics was recognized. This is because a lithium-containing cobalt oxide was mixed in the lithium-containing complex oxide of the present invention.
Example 13
[0110] Furthermore, a non-aqueous secondary battery was produced by using a complex of Si and a carbon material as a negative active material. Si powder and artificial graphite were mixed in a planet type ball mill to form a complex, and the resultant complex was sifted to obtain a negative active material. As a positive active material, the lithium-containing complex oxide in Example 1 was used. Thus, a non-aqueous secondary battery was produced in the same way as in Example 11, except that the above-mentioned active materials were used. The mass ratio between the positive active material and the negative active material was set at 6.6. In this battery, the mass ratio of the positive active material was increased due to the use of a high-capacity material as the negative active material. Therefore, the discharge capacity was increased by about 7% with the same size as that in Example 11.
[0111] The above-mentioned non-aqueous secondary battery was measured for a discharge capacity at a discharge current of 2C to obtain 605 mAh. Thus, the battery had excellent characteristics even during discharge at a large current. This is because the load on the positive active material during discharge was reduced due to the increased mass ratio of the positive active material, resulting in a decrease in a voltage drop.
Industrial Applicability
[0112] As described above, according to the present invention, because of the composition represented by General Formula: Li1+x+αNi(1−x−y+δ)/2Mn(1−x−y−δ)/2MyO2 (where 0≦x≦0.05, −0.05≦x+α≦0.05, 0≦y≦0.4; −0.1≦δ≦0.1 (when 0≦y≦0.2) or −0.24≦δ≦0.24 (when 0.2<y≦0.4); and M is at least one element selected from the group consisting of Ti, Cr, Fe, Co, Cu, Zn, Al, Ge and Sn), a high-density lithium-containing complex oxide with high stability of a crystal structure and satisfactory reversibility of charging/discharging can be provided.
[0113] Furthermore, due to the use of the above-mentioned lithium-containing complex oxide as a positive active material, a non-aqueous secondary battery with a high capacity excellent in durability can be provided. The above-mentioned lithium-containing complex oxide contains Mn, which is rich in resource and less expensive, as one of main components. Therefore, such an oxide is suitable for mass-production, and can contribute to the reduction in cost.
Claims
The invention claimed is:
1. A method for producing a lithium-containing complex oxide, comprising:
coprecipitating a complex compound containing at least Ni and Mn as constituent elements in an inactive atmosphere;
mixing the complex compound and a compound of Li at a predetermined ratio; and
sintering the mixture at a sintering temperature of about 700° C. to 1100° C. in an atmosphere containing oxygen, thereby forming a complex oxide with a layered crystal structure,
wherein the lithium-containing complex oxide further contains a substituent element M,
wherein the substituent element M contains Co, and assuming that a total quantity of Ni, Mn, and the substituent element M is 1-x, and a quantity ratio of the substituent element M is y, x satisfies 0≦x≦0.05, y satisfies 0.1<y≦0.4, and a quantity ratio of Co is 0.1 or more,
wherein a composition of the complex compound containing at least Ni and Mn as constituent elements is adjusted so that a difference δ in a quantity ratio between Ni and Mn constituting the lithium-containing complex oxide satisfies −0.1≦δ≦0.1, and
wherein an average valence of Mn constituting the lithium-containing complex oxide is set to be about 3.3 to 4.
2. The method for producing a lithium-containing complex oxide according to claim 1, wherein, for mixing the complex compound containing at least Ni and Mn as constituent elements and the compound of Li at a predetermined ratio, the complex compound and the compound of Li are dispersed in a solvent to form a slurry.
3. A method for producing a lithium-containing complex oxide according to claim 1, wherein an average valence of Mn is about 4.
4. The method for producing a lithium-containing complex oxide according to claim 1, wherein an average valence of Mn is about 4 and an average valence of Ni is about 2.
5. The method for producing a lithium-containing complex oxide according to claim 1, wherein the complex compound is one selected from an oxide and a hydroxide.
6. The method for producing a lithium-containing complex oxide according to claim 1, wherein the lithium-containing complex oxide has a composition represented by General Formula Li1+x+αNi(1−x−y+δ)/2Mn(1−x−y−δ)/2MyO2 where 0≦x≦0.05, −0.05≦x+α≦0.05, 0<y≦0.2, −0.1≦δ≦0.1; M is at least one element containing Co, and a quantity ratio of Co is 0.1 or more.
7. The method for producing a lithium-containing complex oxide according to claim 1, wherein pre-heating is conducted at a temperature lower than the sintering temperature before the sintering.
8. The method for producing a lithium-containing complex oxide according to claim 7, wherein a temperature during the pre-heating is about 250° C. to 850° C.
9. The method for producing a lithium-containing complex oxide according to claim 1, wherein a quantity ratio among Ni, Mn, and the substituent element M in the lithium-containing complex oxide is 1:1:1.
10. The method for producing a lithium-containing complex oxide according to claim 1, wherein y=⅓.
11. The method for producing a lithium-containing complex oxide according to claim 1, wherein, in an x-ray diffraction measurement of the lithium-containing complex oxide using a CuKα-ray, two diffraction peaks are present at a diffraction angle 2θ in a range of 63° to 66°.
12. The method for producing a lithium-containing complex oxide according to claim 6, wherein the substituent element M in the General Formula is at least one element containing at least Co, selected from the group consisting of Ti, Cr, Fe, Co, Cu, Zn, Al, Ge, and Sn.
13. A method for producing a lithium-containing complex oxide, comprising:
coprecipitating a complex compound containing at least Ni and Mn as constituent elements in an inactive atmosphere;
mixing the complex compound and a compound of Li at a predetermined ratio; and
sintering the mixture at a sintering temperature of about 700° C. to 1100° C. in an atmosphere containing oxygen, thereby forming a complex oxide with a layered crystal structure,
wherein the lithium-containing complex oxide further contains a substituent element M,
wherein the substituent element M contains Co, and assuming that a total quantity of Ni, Mn, and the substituent element M is 1-x and a quantity ratio of the substituent element M is y, x satisfies 0≦x≦0.05, and y satisfies 0.2<y≦0.4,
wherein a composition of the complex compound containing at least Ni and Mn as constituent elements is adjusted so that a difference δ in a quantity ratio between Ni and Mn constituting the lithium-containing complex oxide satisfies −0.24≦δ≦0.24, and
wherein an average valence of Mn constituting the lithium-containing complex oxide is set to be about 3.3 to 4.
14. The method for producing a lithium-containing complex oxide according to claim 13, wherein the lithium-containing complex oxide has a composition represented by General Formula Li1+x+αNi(1−x−y+δ)/2Mn(1−x−y−δ)/2MyO2 where 0≦x≦0.05, −0.05≦x+α≦0.05, 0.2<y≦0.4, −0.24≦δ≦0.24; M is at least one element containing Co.
15. The method for producing a lithium-containing complex oxide according to claim 14, wherein the substituent element M in the General Formula is at least one element containing at least Co selected from the group consisting of Ti, Cr, Fe, Co, Cu, Zn, Al, Ge, and Sn.
16. The method for producing a lithium-containing complex oxide according to claim 13, wherein an average valence of Mn is about 4.
17. The method for producing a lithium-containing complex oxide according to claim 13, wherein an average valence of Mn is about 4 and an average valence of Ni is about 2.
18. The method for producing a lithium-containing complex oxide according to claim 13, wherein y=⅓.
19. The method for producing a lithium-containing complex oxide according to claim 13, wherein, in an x-ray diffraction measurement of the lithium-containing complex oxide using a CuKα-ray, two diffraction peaks are present at a diffraction angle 2θ in a range of 63° to 66°.
Patent Citations (25)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US5626635(A) | 1997-05-01 | Yamaura et al. | Examiner |
| US5707756(A) | 1998-01-01 | Inoue et al. | Applicant |
| US5718989(A) | 1998-02-01 | Aoki et al. | Examiner |
| US6040090(A) | 2000-03-01 | Sunagawa et al. | Applicant |
| US6551744(B1) | 2003-04-01 | Ohzuku et al. | Examiner |
| US6660432(B2) | 2003-12-01 | Paulsen et al. | Examiner |
| US6964828(B2) | 2005-11-01 | Lu et al. | Examiner |
| US2001/0028874(A1) | 2001-10-01 | Cho et al. | Examiner |
| US2002/0053663(A1) | 2002-05-01 | Ito et al. | Examiner |
| CN1097526(A) | 1995-01-01 | Applicant | |
| EP782206 | 1997-07-01 | Applicant | |
| EP918041 | 1999-05-01 | Applicant | |
| EP1443575Al | 2004-08-01 | Applicant | |
| JP5-242891 | 1993-09-01 | Applicant | |
| JP6-044973(A) | 1994-02-01 | Applicant | |
| JP6044973 | 1994-02-01 | Examiner | |
| JP10-172570(A) | 1998-06-01 | Applicant | |
| JP10199525 | 1998-07-01 | Applicant | |
| JP10289731(A) | 1998-10-01 | Applicant | |
| JP10-294100 | 1998-11-01 | Applicant | |
| JP10316431 | 1998-12-01 | Examiner | |
| JP11-307094 | 1999-11-01 | Examiner | |
| JP11307094 | 1999-11-01 | Applicant | |
| JP2000133262(A) | 2000-05-01 | Applicant | |
| JP2000-223122 | 2000-08-01 | Examiner |
Non-Patent Literature (16)
- Lu et al, “Layered Li[NixCo1-2xMnx]O2 Cathode materials for Lithium-Ion Batteries,” Electrochemical and Solid State Letters, 2001, 4(12), A200-A203; Oct. 5, 2001.Examiner
- Partial Translation of JP Publication No. 11-307094 published Nov. 5, 1999 (2 pages).Applicant
- Rossen, E. et al., Structure and Electrochemistry of LixMnyNi1-yO2; Solid State Ionics 57, pp. 311-318 (1992).Applicant
- Neudecker, B.J., et al. Lithium Manganese Nickel Oxides Lix(MnyNi1-y)2-xO2; Synthesis and Characterization of Thin Films and Bulk Phases; J. Electrochem. Soc., vol. 145, No. 12, Dec. 1998, pp. 4148-4159.Applicant
- European Communication issued in Application No. 01 982 785.6 dated Jun. 26, 2009 (7 pages).Applicant
- Patent Abstracts of Japan and machine translation, publication No. 10199525, published Jul. 31, 1998 (23 pages).Applicant
- Liu, Z. et al. “Synthesis and characterization of LiNi1-x-yCoxMny02 as the cathode materials of secondary lithium batteries” Journal of Power Sources, Elsevier, Amsterdam, NL vol. 81-82, Sep. 1999 (4 pages).Applicant
- Patent Abstracts of Japan and machine translation, publication No. 05242891, published Sep. 21, 1993 (17 pages).Applicant
- Patent Abstracts of Japan and machine translation, publication No. 10316431, published Dec. 2, 1998 (28 pages).Applicant
- Patent Abstracts of Japan and machine translation, publication No. 10-294100 published Nov. 4, 1998 (21 pages).Applicant
- Supplementary European Search Report issued in EP Application No. 01982785 dated Aug. 25, 2008 (8 pages).Applicant
- Patent Abstracts of Japan and machine translation, publication No. 11-307094 published Nov. 5, 1999 (23 pages).Applicant
- Office Action issued in Japanese Application No. 2007-323614 dated Feb. 3, 2011 (9 pages).Applicant
- Office Action issued in Chinese Application No. 201010223465.5 dated Apr. 25, 2011 (3 pages).Applicant
- Office Action issued in European Application No. 01982785.6 dated Sep. 3, 2010 (7 pages).Applicant
- Office Action in corresponding European Application No. 01982785.6 mailed Jan. 30, 2013 (9 pages).Applicant