US 8,313,719 B2Grant

Method of making active materials for use in secondary electrochemical cells

Issue Date:2012-11-20

•15 Claims

•21 Drawing Sheets

Abstract

The present invention provides for the preparation of an “optimized” VPO₄phase or V—P—O/C precursor. The VPO₄precursor is an amorphous or nanocrystalline powder. The V—P—O/C precursor is amorphous in nature and contains finely divided and dispersed carbon. Throughout the specification it is understood that the VPO₄precursor and the V—P—O/C precursor materials can be used interchangeably to produce the final vanadium phosphates, with the V—P—O/C precursor material being the preferred precursor. The precursors can subsequently be used to make vanadium based electroactive materials and use of such precursor materials offers significant advantages over other processes known for preparing vanadium phosphate compounds.

Metadata

Assignee

Valence Technology, Inc.

Inventors

Jeremy Barker
Aiden Bryan
Paul Burns
Richard Gover

Application Information

Application Number:US 13/106,196

Filing Date:2011-05-12

Priority Date:2005-03-28

Art Unit:1736

Classifications

IPC:

C01B25/00

Patent Drawings (21 sheets)

Description

FIELD OF THE INVENTION

[0001] This application is a continuation of U.S. patent application Ser. No. 11/682,339 filed Mar. 6, 2007 now abandoned which is a continuation-in-part of U.S. patent application Ser. No. 11/277,746 filed Mar. 28, 2006, which claims priority from U.S. provisional patent application 60/729,932 filed Oct. 25, 2005, which claims priority from U.S. provisional patent application 60/666,132 filed Mar. 28, 2005.

[0002] The present invention relates to the novel preparation of a nanocrystalline VPO₄precursor and in another embodiment to an amorphous V—P—O/C precursor (or V—P—O-carbon composite material/precursor). The invention further relates to the use of this VPO₄precursor or V—P—O/C precursor in methods for making vanadium phosphate compounds. Such methods for making vanadium phosphates are beneficial in that the methods proceed at faster reaction rates and at lower temperatures then known methods for making vanadium phosphates. Such precursors also produce a purer product. The vanadium phosphate compounds so prepared are electroactive and are useful in making electrochemical cells.

BACKGROUND OF THE INVENTION

[0003] A battery pack consists of one or more electrochemical cells or batteries, wherein each cell typically includes a positive electrode, a negative electrode, and an electrolyte or other material for facilitating movement of ionic charge carriers between the negative electrode and positive electrode. As the cell is charged, cations migrate from the positive electrode to the electrolyte and, concurrently, from the electrolyte to the negative electrode. During discharge, cations migrate from the negative electrode to the electrolyte and, concurrently, from the electrolyte to the positive electrode.

[0004] By way of example and generally speaking, lithium ion batteries are prepared from one or more lithium ion electrochemical cells containing electrochemically active (electroactive) materials. Such cells typically include, at least, a negative electrode, a positive electrode, and an electrolyte for facilitating movement of ionic charge carriers between the negative and positive electrode. As the cell is charged, lithium ions are transferred from the positive electrode to the electrolyte and, concurrently from the electrolyte to the negative electrode. During discharge, the lithium ions are transferred from the negative electrode to the electrolyte and, concurrently from the electrolyte back to the positive electrode. Thus with each charge/discharge cycle the lithium ions are transported between the electrodes. Such lithium ion batteries are called rechargeable lithium ion batteries or rocking chair batteries.

[0005] The electrodes of such batteries generally include an electroactive material having a crystal lattice structure or framework from which ions, such as lithium ions, can be extracted and subsequently reinserted and/or from which ions such as lithium ions can be inserted or intercalated and subsequently extracted. Recently a class of transition metal phosphates and mixed metal phosphates have been developed, which have such a crystal lattice structure. These transition metal phosphates are insertion based compounds and allow great flexibility in the design of lithium ion batteries.

[0006] A class of such materials is disclosed in U.S. Pat. No. 6,528,033 B1 (Barker et al.). The compounds therein are of the general formula Li_aMI_bMII_c(PO₄)_dwherein MI and MII are the same or different. MI is a metal selected from the group consisting of Fe, Co, Ni, Mn, Cu, V, Sn, Cr and mixtures thereof. MII is optionally present, but when present is a metal selected from the group consisting of Mg, Ca, Zn, Sr, Pb, Cd, Sn, Ba, Be and mixtures thereof. More specific examples of such compounds include compounds wherein MI is vanadium and more specifically includes Li₃V₂(PO₄)₃. U.S. Pat. No. 6,645,452 B1 (Barker et al.) further discloses electroactive vanadium phosphates such as LiVPO₄F and LiV_0.9Al_o.1PO₄F.

[0007] Although these compounds find use as electrochemically active materials these materials are not always economical to produce. Thus it would be beneficial to have a process for preparing such intercalation materials at lower temperatures and with faster reaction kinetics. The inventors of the present invention have now found a method for preparing a novel VPO₄precursor and a novel V—P—O/C precursor and processes employing such precursors to produce vanadium phosphate compounds more economically and efficiently.

SUMMARY OF THE INVENTION

[0008] The present invention provides for the preparation of an “optimized” VPO₄phase or V—P—O/C precursor. The VPO₄precursor is an amorphous or nanocrystalline powder. The V—P—O/C precursor is amorphous in nature and contains finely divided and dispersed carbon. Throughout the specification it is understood that the VPO₄precursor and the V—P—O/C precursor materials can be used interchangeably to produce the final vanadium phosphates, with the V—P—O/C precursor material being the preferred precursor. The precursors can subsequently be used to make vanadium based electroactive materials and use of such precursor materials offers significant advantages over other processes known for preparing vanadium phosphate compounds. .

BRIEF DESCRIPTION OF THE DRAWINGS

[0009] FIG. 1 is a schematic cross-sectional diagram illustrating the structure of a non-aqueous electrolyte cylindrical electrochemical cell of the present invention.

[0010] FIG. 2 is a representative X-ray pattern for a sample of an amorphous V—P—O/C sample prepared at 700° C. for 4 hours as in Example 1.

[0011] FIG. 3 is an X-ray powder pattern for a sample of LiVPO₄F for a product prepared according to Example 2.

[0012] FIG. 4 is observed, difference and calculated plot obtained from Rietveld analysis of an optimized sample of LiVPO₄F prepared in Example 2.

[0013] FIG. 5 shows a schematic representation of the structure of LiVPO₄F projected down the c-axis.

[0014] FIG. 6 shows the first cycle current data for a Li/LiVPO₄F cell made with the LiVPO₄F prepared in Example 2.

[0015] FIG. 7 shows a representative X-ray powder patterns for LiV_1-xAl_xPO₄F made by the process according to Example 3.

[0016] FIG. 8 shows the unit cell volume versus Al content for LiV_1-xAl_xPO₄F made by the process according to Example 3.

[0017] FIG. 9 shows a comparison of the electrochemical response of

[0018] Li/LiVPO₄F, Li/LiAl_0.25V_0.75PO₄F and Li/LiAl_0.5V_0.5PO₄F cells made by the process of Example 3.

[0019] FIG. 10 shows a representative X-ray powder pattern for LiVP₂O₇made by the process of Example 5.

[0020] FIG. 11 shows the observed, difference and calculated plots obtained for a sample of LiVP₂O₇made by the process of Example 5.

[0021] FIG. 12 shows a schematic representation of the structure of LiVP₂O₇made by the process of Example 5.

[0022] FIG. 13 shows a first cycle constant current data for a Li/LiVP₂O₇cell.

[0023] FIG. 14 shows EVS data for a representative Li/LiVP₂O₇cell cycled between 2.5-4.7 V. Left: EVS Voltage profile. Right: EVS Differential Capacity Profile.

[0024] FIG. 15 shows EVS data for a representative graphite//LiVP₂O₇lithium ion cell cycled between 2.5-4.6 V. The data shown is for the tenth cycle. Left: EVS Voltage Profile. Right EVS Differential Capacity Profile.

[0025] FIG. 16 shows the life cycle data collected for LiVP₂O₇//graphite cell.

[0026] FIG. 17 shows X-ray patterns for samples of LiV_i-xAl_xPO₄F prepared according to the process of Example 10.

[0027] FIG. 18 shows the electrochemical results for samples of LiV_1-xAl_xP₂O₇prepared according to Example 10.

[0028] FIG. 19 shows a comparison of a sample of LVP prepared using conventional known methods and prepared using the VPO₄process according to Example 11.

[0029] FIG. 20 shows the EVS electrochemical response for LVP sample prepared according to Example 11

[0030] FIG. 21 shows the X-ray powder pattern for the sample of Na₃V₂(PO₄)₂F₃prepared according to the method of Example 12.

DETAILED DESCRIPTION OF THE INVENTION

[0031] Specific benefits and embodiments of the present invention are apparent from the detailed description set forth herein below. It should be understood, however, that the detailed description and specific examples, while indicating embodiments among those preferred, are intended for purposes of illustration only and are not intended to limit the scope of the invention.

[0032] The following is a list of some of the definitions of various terms used herein:

[0033] As used herein “battery” refers to a device comprising one or more electrochemical cells for the production of electricity. Each electrochemical cell comprises an anode, a cathode and an electrolyte.

[0034] As used herein the terms “anode” and “cathode” refer to the electrodes at which oxidation and reduction occur, respectively, during battery discharge. During charging of the battery, the sites of oxidation and reduction are reversed.

[0035] As used herein the terms “nominal formula” or “nominal general formula” refer to the fact that the relative proportion of atomic species may vary slightly on the order of 2 percent to 5 percent, or more typically, 1 percent to 3 percent.

[0036] As used herein the words “preferred” and “preferably” refer to embodiments of the invention that afford certain benefits under certain circumstances. Further the recitation of one or more preferred embodiments are not useful and is not intended to exclude other embodiments from the scope of the invention.

[0037] Referring to FIG. 1, a secondary electrochemical cell 10 having an electrode active material described herein below as nominal general formula (I), is illustrated. The cell 10 includes a spirally coiled or wound electrode assembly 12 enclosed in a sealed container, preferably a rigid cylindrical casing 14. The electrode assembly 12 includes: a positive electrode 16 consisting of, among other things, an electrode active material described herein below; a counter negative electrode 18; and a separator 20 interposed between the first and second electrodes 16, 18. The separator 20 is preferably an electrically insulating, ionically conductive microporous film, and composed of a polymeric material selected from the group consisting of polyethylene, polyethylene oxide, polyacrylonitrile and polyvinylidene fluoride, polymethyl methacrylate, polysiloxane, copolymers thereof, and admixtures thereof.

[0038] Each electrode 16, 18 includes a current collector 22 and 24, respectively, for providing electrical communication between the electrodes 16, 18 and an external load. Each current collector 22, 24 is a foil or grid of an electrically conductive metal such as iron, copper, aluminum, titanium, nickel, stainless steel, or the like, having a thickness of between 5 μm and 100 μm, preferably 5 μm and 20 μm. Optionally, the current collector may be treated with an oxide-removing agent such as a mild acid and the like, and coated with an electrically conductive coating for inhibiting the formation of electrically insulating oxides on the surface of the current collector 22, 24. Examples of suitable coatings include polymeric materials comprising a homogenously dispersed electrically conductive material (e.g. carbon), such polymeric materials including: acrylics including acrylic acid and methacrylic acids and esters, including poly (ethylene-co-acrylic acid); vinylic materials including poly(vinyl acetate) and poly(vinylidene fluoride-co-hexafluoropropylene); polyesters including poly(adipic acid-co-ethylene glycol); polyurethanes; fluoroelastomers; and mixtures thereof.

[0039] The positive electrode 16 further includes a positive electrode film 26 formed on at least one side of the positive electrode current collector 22, preferably both sides of the positive electrode current collector 22, each film 26 having a thickness of between 10 μm and 150 μm, preferably between 25 μm an 125 μm, in order to realize the optimal capacity for the cell 10. The positive electrode film 26 is preferably composed of between 80% and 99% by weight of an electrode active material described herein below as general formula (I), between 1% and 10% by weight binder, and between 1% and 10% by weight electrically conductive agent.

[0040] Suitable binders include: polyacrylic acid; carboxymethylcellulose; diacetylcellulose; hydroxypropylcellulose; polyethylene; polypropylene; ethylene-propylene-diene copolymer; polytetrafluoroethylene; polyvinylidene fluoride; styrene-butadiene rubber; tetrafluoroethylene-hexafluoropropylene copolymer; polyvinyl alcohol; polyvinyl chloride; polyvinyl pyrrolidone; tetrafluoroethylene-perfluoroalkylvinyl ether copolymer; vinylidene fluoride-hexafluoropropylene copolymer; vinylidene fluoride-chlorotrifluoroethylene copolymer; ethylenetetrafluoroethylene copolymer; polychlorotrifluoroethylene; vinylidene fluoride-pentafluoropropylene copolymer; propylene-tetrafluoroethylene copolymer; ethylene-chlorotrifluoroethylene copolymer; vinylidene fluoride-hexafluoropropylene-tetrafluoroethylene copolymer; vinylidene fluoride-perfluoromethylvinyl ether-tetrafluoroethylene copolymer; ethylene-acrylic acid copolymer; ethylene-methacrylic acid copolymer; ethylene-methyl acrylate copolymer; ethylene-methyl methacrylate copolymer; styrene-butadiene rubber; fluorinated rubber; polybutadiene; and admixtures thereof. Of these materials, most preferred are polyvinylidene fluoride and polytetrafluoroethylene.

[0041] Suitable electrically conductive agents include: natural graphite (e.g. flaky graphite, and the like); manufactured graphite; carbon blacks such as acetylene black, Ketzen black, channel black, furnace black, lamp black, thermal black, and the like; conductive fibers such as carbon fibers and metallic fibers; metal powders such as carbon fluoride, copper, nickel, and the like; and organic conductive materials such as polyphenylene derivatives.

[0042] The negative electrode 18 is formed of a negative electrode film 28 formed on at least one side of the negative electrode current collector 24, preferably both sides of the negative electrode current collector 24. The negative electrode film 28 is composed of between 80% and 95% of an intercalation material, between 2% and 10% by weight binder, and (optionally) between 1% and 10% by weight of an electrically conductive agent.

[0043] Intercalation materials suitable herein include: transition metal oxides, metal chalcogenides, carbons (e.g. graphite), and mixtures thereof capable of intercalating the alkali metal-ions present in the electrolyte in the electrochemical cell's nascent state.

[0044] In one embodiment, the intercalation material is selected from the group consisting of crystalline graphite and amorphous graphite, and mixtures thereof, each such graphite having one or more of the following properties: a lattice interplane (002) d-value (d₍₀₀₂₎) obtained by X-ray diffraction of between 3.35 Å to 3.34 Å, inclusive (3.35 Å≦d₍₀₀₂₎≦3.34 Å), preferably 3.354 Å to 3.370 Å, inclusive (3.354 Å≦d₍₀₀₂₎≦3.370 Å; a crystallite size (L_c) in the c-axis direction obtained by X-ray diffraction of at least 200 Å, inclusive (L_c≧200 Å), preferably between 200 Å and 1,000 Å, inclusive (200 Å≦L_c≦1,000 Å); an average particle diameter (P_d) of between 1 μm to 30 μm, inclusive (1 μm≦P_d≦30 μm); a specific surface (SA) area of between 0.5 m²/g to 50 m²/g, inclusive (0.5 m²/g≦SA≦50 m²/g); and a true density (ρ) of between 1.9 g/cm³to 2.25 g/cm³, inclusive (1.9 g/cm³≦ρ≦2.25 g/cm³).

[0045] Referring again to FIG. 1, to ensure that the electrodes 16, 18 do not come into electrical contact with one another, in the event the electrodes 16, 18 become offset during the winding operation during manufacture, the separator 20 “overhangs” or extends a width “a” beyond each edge of the negative electrode 18. In one embodiment, 50 μm≦a≦2,000 μm. To ensure alkali metal does not plate on the edges of the negative electrode 18 during charging, the negative electrode 18 “overhangs” or extends a width “b” beyond each edge of the positive electrode 16. In one embodiment, 50 μm≦b≦2,000 μm.

[0046] The cylindrical casing 14 includes a cylindrical body member 30 having a closed end 32 in electrical communication with the negative electrode 18 via a negative electrode lead 34, and an open end defined by crimped edge 36. In operation, the cylindrical body member 30, and more particularly the closed end 32, is electrically conductive and provides electrical communication between the negative electrode 18 and an external load (not illustrated). An insulating member 38 is interposed between the spirally coiled or wound electrode assembly 12 and the closed end 32.

[0047] A positive terminal subassembly 40 in electrical communication with the positive electrode 16 via a positive electrode lead 42 provides electrical communication between the positive electrode 16 and the external load (not illustrated). Preferably, the positive terminal subassembly 40 is adapted to sever electrical communication between the positive electrode 16 and an external load/charging device in the event of an overcharge condition (e.g. by way of positive temperature coefficient (PTC) element), elevated temperature and/or in the event of excess gas generation within the cylindrical casing 14. Suitable positive terminal assemblies 40 are disclosed in U.S. Pat. No. 6,632,572 to Iwaizono, et al., issued Oct. 14, 2003; and U.S. Pat. No. 6,667,132 to Okochi, et al., issued Dec. 23, 2003. A gasket member 42 sealingly engages the upper portion of the cylindrical body member 30 to the positive terminal subassembly 40.

[0048] A non-aqueous electrolyte (not shown) is provided for transferring ionic charge carriers between the positive electrode 16 and the negative electrode 18 during charge and discharge of the electrochemical cell 10. The electrolyte includes a non-aqueous solvent and an alkali metal salt dissolved therein capable of forming a stable SEI layer on the negative electrode (most preferably, a lithium salt). In the electrochemical cell's nascent state (namely, before the cell undergoes cycling), the non-aqueous electrolyte contains one or more metal-ion charge carriers.

[0049] Suitable solvents include: a cyclic carbonate such as ethylene carbonate, propylene carbonate, butylene carbonate or vinylene carbonate; a non-cyclic carbonate such as dimethyl carbonate, diethyl carbonate, ethyl methyl carbonate or dipropyl carbonate; an aliphatic carboxylic acid ester such as methyl formate, methyl acetate, methyl propionate or ethyl propionate; a .gamma.-lactone such as y-butyrolactone; a non-cyclic ether such as 1,2-dimethoxyethane, 1,2-diethoxyethane or ethoxymethoxyethane; a cyclic ether such as tetrahydrofuran or 2-methyltetrahydrofuran; an organic aprotic solvent such as dimethylsulfoxide, 1,3-dioxolane, formamide, acetamide, dimethylformamide, dioxolane, acetonitrile, propylnitrile, nitromethane, ethyl monoglyme, phospheric acid triester, trimethoxymethane, a dioxolane derivative, sulfolane, methylsulfolane, 1,3-dimethyl-2-imidazolidinone, 3-methyl-2-oxazolidinone a propylene carbonate derivative, a tetrahydrofuran derivative, ethyl ether, 1,3-propanesultone, anisole, dimethylsulfoxide and N-methylpyrrolidone; and mixtures thereof. A mixture of a cyclic carbonate and a non-cyclic carbonate or a mixture of a cyclic carbonate, a non-cyclic carbonate and an aliphatic carboxylic acid ester, are preferred.

[0050] Suitable alkali metal salts, particularly lithium salts, include: LiClO₄; LiBF₄; LiPF₆; LiAlCl₄; LiSbF₆; LiSCN; LiCF₃SO₃; LiCF₃CO₂; Li(CF₃SO₂)₂; LiAsF₆; LiN(CF₃SO//2)₂; LiB₁₀Cl₁₀; a lithium lower aliphatic carboxylate; LiCl; LiBr; LiI; a chloroboran of lithium; lithium tetraphenylborate; lithium imides; LiBOB (lithium bis(oxalate)borate) and mixtures thereof. Preferably, the electrolyte contains at least LiPF₆.

[0051] One embodiment of the invention involves the production of a nanocrystalline and/or amorphous VPO₄. This material can be used a precursor for preparing various vanadium based products. This material is very reactive and allows for the preparation of various vanadium based products at low temperatures and with very fast kinetics. Additionally this VPO₄is useful as a precursor of vanadium based products in that other processes for making the vanadium based products may cause production of unwanted impurity phases, such as V₂O₃, in the vanadium based products.

[0052] In another embodiment the invention involves the production of a amorphous V—P—O/C precursor with no “definite” composition (see FIG. 2). This V—P—O/C precursor has the correct ratio of V and PO₄to make the final product (e.g. LiVPO₄F), is close to X-ray amorphous (see FIG. 2) and it contains finely divided and dispersed carbon. This material can be used a precursor for preparing various vanadium based products. This material is very reactive and allows for the preparation of various vanadium based products at low temperatures and with very fast kinetics. Additionally this V—P—O/C precursor is useful as a precursor of vanadium based products in that other processes for making the vanadium based products may cause production of unwanted impurity phases, such as V₂O₃, in the vanadium based products.

[0053] It is understood that the VPO₄and V—P—O/C precursor materials can be used interchangeably in the reactions described herein. The V—P—O/C precursor is the preferred precursor. Thus where it is stated that VPO₄is used the V—P—O/C precursor could alternately be used and vice versa. Alternatively, either precursor may be referred to as a vanadium phosphate precursor.

[0054] The vanadium phosphate precursor is made for example by mixing vanadium pentoxide (V₂O₅), ammonium hydrogen phosphate [(NH₄)₂HPO₄or (NH₄)H₂PO₄] and a source of carbon, such as Enasco carbon. The mixture is then milled and/or micronized (i.e. some form of high energy mixing/homogenizing), pelletized and heated at a temperature in the range from about 400° C. to about 900° C. Preferably the milled mixture is heated in the temperature range from about 500° C. to about 800° C. and more preferably from about 600° C. to about 750° C. The mixture is heated from about 30 minutes to about 16 hours and more preferably from about 1 to about 8 hours.

[0055] The amorphous V—P—O/C precursors may be produced at temperatures from 300-800° C. and more preferably at about 600° C. Reaction of these preferred amorphous V—P—O/C precursors with appropriate alkali metal compounds result in improved vanadium phosphate products which can be produced at lower temperatures than when using the crystalline VPO₄precursors.

[0056] The reaction proceeds according to the following equations:
0.5 V₂O₅+(NH₄)₂HPO₄+carbon→VPO₄+2NH₃+1.5 H₂O+CO
or
0.5 V₂O₅+(NH₄)H₂PO₄+carbon→VPO₄+NH₃+1.5 H₂O.

[0057] Alternatively other vanadium containing compounds such as V₂O₃, VO₂, NH₄VO₃and the like can be used in the place of the V₂O₅. If lithium products are the desired end products LiVO₃and the like may also be employed in place of the V₂O₃. Likewise, alternatively other phosphate sources such as P₂O₅, H₃PO₄and the like can be used in place of the ammonium phosphate starting materials.

[0058] In one aspect, the source of carbon is provided by elemental carbon, preferably in particulate form such as graphites, amorphous carbon, carbon blacks and the like. In another aspect, the source of carbon may also be provided by an organic precursor material, or by a mixture of elemental carbon and organic precursor material. The organic precursor material will also be referred to in this application as an organic material. The organic material or organic precursor material is one that is capable of forming a decomposition product that contains carbon. The carbon is formed in situ.

[0059] Alternatively or in addition, the source of carbon may be provided by an organic material. The organic material is characterized as containing carbon and at least one other element, preferably hydrogen. The organic material generally forms a decomposition product, referred to herein as a carbonaceous material, upon heating under the conditions of the reaction.

[0060] The organic precursor material may be any organic material capable of undergoing pyrolysis or carbonization, or any other decomposition process that leads to a carbonaceous material rich in carbon. Such precursors include in general any organic material, i.e., compounds characterized by containing carbon and at least one other element. Although the organic material may be a perhalo compound containing essentially no carbon-hydrogen bonds, typically the organic materials contain carbon and hydrogen. Other elements, such as without limitation, halogens, oxygen, nitrogen, phosphorus, and sulfur, may be present in the organic material, as long as they do not significantly interfere with the decomposition process. One example of a preferred organic material is coke, which contains mostly carbon and hydrogen. Other precursors include, without limitation, organic hydrocarbons, alcohols, esters, ketones, aldehydes, carboxylic acids, sulfonates, and ethers. Preferred precursors include the above species containing aromatic rings, especially the aromatic hydrocarbons such as tars, pitches, and other petroleum products or fractions. As used here, hydrocarbon refers to an organic compound made up of carbon and hydrogen, and containing no significant amounts of other elements. Hydrocarbons may contain impurities having some heteroatoms. Such impurities might result, for example, from partial oxidation of a hydrocarbon or incomplete separation of a hydrocarbon from a reaction mixture or natural source such as petroleum.

[0061] Other organic precursor materials include sugars and other carbohydrates, including derivatives and polymers. Examples of polymers include, without limitation, starch, cellulose, and their ether or ester derivatives. Other derivatives include, without limitation, the partially reduced and partially oxidized carbohydrates discussed below. On heating, carbohydrates readily decompose to form carbon and water. The term carbohydrates as used here encompasses the D-, L-, and DL-forms, as well as mixtures, and includes material from natural or synthetic sources.

[0062] In one sense as used in the invention, carbohydrates are organic materials that can be written with molecular formula (C)_m(H₂O)_n, where m and n are integers. For simple hexose or pentose sugars, m and n are equal to each other. Non-limiting examples of hexoses of formula C₆H₁₂O₆include allose, altose, glucose, mannose, gulose, inose, galactose, talose, sorbose, tagatose, and fructose. Pentoses of formula C₅H₁₀O₅are represented by, without limitation, ribose, arabinose, and xylose. Tetroses include erythrose and threose, while glyceric aldehyde is a triose. Other carbohydrates include the two-ring sugars (di-saccharides) of general formula C₁₂H₂₂O₁₁. Examples include, without limitation, sucrose, maltose, lactose, trehalose, gentiobiose, cellobiose, and melibiose. Three-ring (trisaccharides such as raffinose) and higher oligomeric and polymer carbohydrates may also be used. Non-limiting examples include starch and cellulose. As noted above, the carbohydrates readily decompose to carbon and water when heated to a sufficiently high temperature. The water of decomposition tends to turn to steam under the reaction conditions and volatilize.

[0063] It will be appreciated that other materials will also tend to readily decompose to H₂O and a material very rich in carbon. Such materials are also intended to be included in the term “carbohydrate” as used in the invention. Such materials include slightly reduced carbohydrates such as, without limitation, glycerol, sorbitol, mannitol, iditol, dulcitol, talitol, arabitol, xylitol, and adonitol, as well as “slightly oxidized” carbohydrates such as, without limitation, gluconic, mannonic, glucuronic, galacturonic, mannuronic, saccharic, manosaccharic, ido-saccharic, mucic, talo-mucic, and allo-mucic acids. The formula of the slightly oxidized and the slightly reduced carbohydrates is similar to that of the carbohydrates.

[0064] A preferred carbohydrate is sucrose. Under the reaction conditions, sucrose melts at about 150-180° C. The liquid melt tends to distribute itself among the starting materials. At temperatures above about 450° C., sucrose and other carbohydrates decompose to form carbon and water. The as-decomposed carbon powder is in the form of fresh amorphous fine particles with high surface area and high reactivity.

[0065] The organic precursor material may also be an organic polymer. Organic polymers include without limitation, polyolefins such as polyethylene and polypropylene, butadiene polymers, isoprene polymers, vinyl alcohol polymers, furfuryl alcohol polymers, styrene polymers including polystyrene, polystyrene-polybutadiene and the like, divinylbenzene polymers, naphthalene polymers, phenol condensation products including those obtained by reaction with aldehyde, polyacrylonitrile, polyvinyl acetate, as well as cellulose starch and esters and ethers thereof described above.

[0066] In some embodiments, the organic precursor material is a solid available in particulate form. Particulate materials may be combined with the other particulate starting materials and reacted by heating according to the methods described above.

[0067] In other embodiments, the organic precursor material may be a liquid. In such cases, the liquid precursor material is combined with the other particulate starting materials to form a mixture. The mixture is heated, whereupon the organic material forms a carbonaceous material in situ. The liquid precursor materials may also advantageously serve or function as a binder in the starting material mixture as noted above.

[0068] In an alternative embodiment of the invention the vanadium phosphate precursor is made for example by mixing vanadium pentoxide (V₂O₅), ammonium hydrogen phosphate [(NH₄)₂HPO₄or (NH₄)H₂PO₄]. The mixture is then milled and/or micronized (i.e. some form of high energy mixing/homogenizing), pelletized and heated at a temperature in the range from about 400° C. to about 900° C. in the presence of reducing gas or gases. Non-limiting examples or reducing gases include hydrogen, methane, ammonia and carbon monoxide. The reducing atmosphere may be provided as pure reducing gas, or as mixtures of reducing gas with other gases. Non-limiting examples of reducing atmosphere mixtures include hydrogen-argon, hydrogen-nitrogen, carbon monoxide-hydrogen, carbon monoxide-argon, and the like. The reducing gas may but need not be provided in molar excess. The reducing gas may be used in partial pressures from about 0.01 atmosphere up to super-atmospheric, depending on such factors as the size of the sample, the volume of the heating chamber, and the excess of gas, if any, required for the reaction

[0069] In an alternate embodiment the reaction is carried out in a reducing atmosphere in the presence of a reductant. Such reductant includes, without limitation carbon and organic precursor materials as discussed above. Such reducing atmosphere, includes without limitation, the reducing gases and mixtures thereof discussed above.

[0070] In one embodiment of the invention the vanadium phosphate precursor is mixed with an alkali metal containing compound and optionally with another metal containing compound to produce alkali metal vanadium phosphate compounds. By way of example alkali metal containing compounds include NaF, LiF, LiH₂PO₄, NaOH, Na₂CO₃, Li₃PO₄and the like and mixtures thereof. If the desired end product is a fluorophosphate (e.g. NaVPO₄F, LiVPO₄F) suitable precursors can include NH₄F and the like together with an appropriate alkali ion salt. Preferred alkali metal containing compounds are compounds containing Na or Li and the more preferred alkali metal containing compounds contain Li. The optional metal containing compounds are compounds containing a metal ion selected from the group consisting of Al, Ti, Cr, Fe Mn, Mo, Nb and the like. Examples of such metal containing compounds include for example AlPO₄,

[0071] Fe₂O₃, Mn₂O₃, Fe₃O₄, FeO, MnO₂, MnO, CrPO₄, FePO₄MnPO₄, aluminum hydroxide, aluminum oxide, aluminum carbonate, Cr₂O₃, Nb₂O₅and the like.

[0072] The vanadium phosphate precursors are then reacted with an appropriate alkali metal according to, for example the following reactions:
3 LiH₂PO₄+2 VPO₄→Li₃V₂(PO₄)₃+3H₂O
or
VPO₄+LiF→LiVPO₄F
or
3 NaF+2 VPO₄→Na₃V₂(PO₄)₂F₃.

[0073] The alkali metal compound is a compound of lithium, sodium, or potassium. The alkali metal compound serves as a source of alkali metal ion in particulate form. Preferred alkali metal compounds are sodium compounds and lithium compounds. Examples of compounds include, without limitation, carbonates, metal oxides, hydroxides, sulfates, aluminates, phosphates and silicates. Examples of lithium compounds thus include, without limitation, lithium carbonates, lithium metal oxides, lithium mixed metal oxides, lithium hydroxides, lithium aluminates, and lithium silicates, while analogous sodium compounds are also preferred. A preferred lithium compound is lithium carbonate. Sodium carbonate and sodium hydroxide are preferred sodium compounds.

[0074] Typically the VPO₄precursor, alkali metal containing compound and optional other metal containing compound are milled and then pelletized. The mixture is then heated at a temperature from about 500° C. to about 900° C. More preferably the mixture is heated from about 500° C. to about 800° C. and most preferably from about 600° C. to about 750° C. The mixture is heated for about 30 minutes to about 16 hours and more preferably from about 1 to about 8 hours.

[0075] The reaction produces electrode active compounds represented by the nominal general formula (I):
A_aV_1-xM_x(PO₄)_dZ_f. (I)
wherein A is selected from the group consisting of Li, Na, K and mixtures thereof;

[0076] a is greater than 0.1 and less than or equal to 3;
[0077] x is zero or less than 1;
[0078] d is greater than 0 and less than or equal to 3
[0079] M is a metal selected from the group consisting of Al, Ti, Cr, Fe, Mn, Mo, Nb and mixtures thereof;
[0080] Z is F, Cl, or OH:
[0081] and f is greater than or equal to 0 but less than or equal to 3.

[0082] Examples of such compounds include but are not limited to LiVPO₄, LiV_1-xAl_xPO₄F, Na_xVPO₄F_x, Li_0.1Na_0.9VPO₄F, NaVPO₄F, NaVPO₄OH, NaVPO₄F, Li₃V₂(PO₄)₃, LiV_0.75Al_0.25PO₄F, LiV_0.5Al_0.5PO₄F, Na_1.2VPO₄F_1.2and Na₃V₂(PO₄)₂F₃, and the like.

[0083] In another embodiment of the invention the reaction produces electrode active compounds represented by the nominal general formula (I):
A_aV_1-xM_xP₂O₇ (I)
wherein A is selected from the group consisting of Li, Na, K and mixtures thereof;

[0084] a is greater than 0.1 and less than or equal to 3;
[0085] x is greater than or equal 0 and less than 1; and
[0086] M is a metal selected from the group consisting of Al, Ti, Cr, Cr, Fe, Mn, Mo, Nb and mixtures thereof. An example of such electrode active material includes, but is not limited to LiVP₂O₇.

[0087] The electrode active materials described herein are in their nascent or as-synthesized state, prior to undergoing cycling in an electrochemical cell. The components of the electrode active material are selected so as to maintain electroneutrality of the electrode active material. The stoichiometric values of one or more elements of the composition may take on non-integer values.

[0088] In all embodiments described herein, moiety Z (when provided) is selected from the group consisting of OH (hydroxyl), a halogen, or mixtures thereof. In one embodiment, Z is selected from the group consisting of OH, F (Fluorine), Cl (Chlorine), and mixtures thereof. In another embodiment, Z is OH. In another embodiment, Z is F, or a mixture of F with OH or Cl.

[0089] Typically for electrochemical testing, composite electrodes were fabricated using 84-wt % active material, 6-wt % Super P (conductive carbon) and 10-wt % PVdf-H FP co-polymer (Elf Atochem) binder. The electrolyte comprised a 1M LiPF₆solution in ethylene carbonate/dimethyl carbonate (2:1 by weight) while a dried glass fiber filter (Whatman, Grade GF/A) was used as the electrode separator. A commercially available crystalline graphite or lithium metal foil were used as the anode active material. High-resolution electrochemical measurements were performed using the Electrochemical Voltage Spectroscopy (EVS) technique. (J. Barker, Electrochim. Acta, 40, 1603 (1995)). EVS is a voltage step method, which provides a high resolution approximation to the open circuit voltage curve for the electrochemical system under investigation. Cycling tests of the hybrid-ion cells were performed using a commercial battery cycler (Maccor Inc., Tulsa, Okla., USA).

[0090] The following non-limiting examples illustrate the compositions and methods of the present invention.

EXAMPLE 1

Preparation of VPO4

[0091] VPO₄was prepared according to the following reaction:
½V₂O₅+(NH₄)₂HPO₄+1.0 C→VPO₄+2 NH₃+3/2 H₂O+CO
9.1 g V₂O₅, 13.2 g of (NH₄)₂HPO₄and 1.32 g of carbon (10% mass excess) were used. Carbon was added to the reaction mixture so that the V⁵⁺ in the V₂O₅was reduced to V³⁺ in the product which is an example of carbothermal reduction. The excess carbon in the product helps act as a conducting agent in the vanadium phosphate electroactive materials produced therefrom, which improves the electrochemical properties of such electroactive materials.

[0092] It has been found that it is necessary to use a homogenous starting material. This can be achieved using high energy milling methods, which can include ball milling and micronizing. The sample prepared herein were prepared using McCrone micronizers to obtain the starting materials.

[0093] The VPO₄materials prepared herein were prepared at a number of different temperatures in the range from about 650° C. to about 900° C. The samples prepared at higher temperatures contained V₂O₃as an impurity. Such materials would be unsuitable as precursors since V₂O₃is known to be detrimental to the electrochemical performance in Li ion cells. It has been found that preparing these materials at low temperatures, typically about 700° C. for about 4 to about 16 hours under a flowing argon atmosphere can be used effectively for the preparation of a number of precursor materials. The precursor materials on removal from the furnace range from dark brown to black in color. The color is dependent on the amount of carbon added in the initial reaction mixture.

[0094] FIG. 2 is a typical X-ray powder pattern obtained for a sample of V—P—O/C precursor made at 700° for 4 hours. The powder pattern of these materials prepared at low temperature generally have a “featureless” powder pattern, which can be interpreted as being due to either the material being amorphous or that the obtained crystallites are very small nanoparticles.

EXAMPLE 2

Preparation of LiVPO4F using VPO4

[0095] LiVPO₄was prepared according to the following reaction:
LiF+VPO₄→LiVPO₄F
The LiF (2.6 g) and VPO₄(1.46 g) were mixed and micronized. The amount of LiF added is dependent on the amount of residual carbon present in the VPO₄. The stoichiometric amount of LiF is added based on the above reaction. An allowance can be made for the amount of residual carbon left over from the V—P—O/C synthesis. This is normally about 3 weight percent. The mixture was then heated in the temperature range of about 600° to about 700° C. for up to about 1 hour. At temperatures in excess of 700° C., it is believed that VF₃sublimation occurs which leads to the formation of Li₃V₂(PO₄)₃(LVP-nasicon).

[0096] FIG. 3 shows an example of a powder pattern obtained for a sample of LiVPO₄F. Refinement of the XRD data for the LiVPO₄F samples was carried out using the Rietveld method. H. M. Rietveld, J. Appl. Crystallograph, 2, (1969) 65. R. A. Young in “The Rietveld Method”, Chapter 1, Oxford Science Publications. A. C. Larsen and R. B. Von Dreele, Los Alamos Laboratory Report, NO-LA-U-86-746 (1987). The X-ray data can be satisfactorily refined using a structural model based on either Tavorite, LiFePO₄OH (U.S. Pat. No. 6,387,568 Barker et al.) or Amblygonite, LiAlPO₄F (Groat et al, American Mineralogist, 88, 195 (2003). The X-ray data for the LiVPO₄F samples derived from the optimized synthesis conditions for this process favor the Amblygonite structural model as the most likely structure of this model. (Such optimized conditions being V—P—O/C prepared at 700° C., followed by reaction with LiF at 700° C. to produce LiVPO₄).

[0097] FIG. 4 shows the fit obtained for the LiVPO₄F sample using the Rietveld analysis. The refined cell parameters are given as space group P-1: a=5.16727(13) Å, b=5.30590(13) Å, c=7.28964(19) Å, α=108.9108(14)°, β=107.2137(13)°, γ=98.4002(16)° and cell volume=174.007(8) Å³; with fitting statistics being R_wp11.08%, R_p=8.05% and x=2.352.

[0098] FIG. 5 shows a schematic representation (along the c axis) of the LiVPO₄F based on the Amblygonite structural model. The LiVPO₄F structure comprises a three dimensional framework being built from [PO₄] tetrahedral and [VO₄F₂] octahedral with the oxygen atoms shared between the PO₄and VO₄F₂. This model predicts the presence of two distinct crystallographic sites for alkali ions which explains the electrochemical lithium extraction behavior exhibited by this material.

[0099] An electrode is made with 84% of the active material, 6% of Super P conductive carbon, and 10% poly vinylidene difluoride. A cell with that electrode as cathode and lithium anode is constructed with an electrolyte comprising 1 M LiPF₆dissolved in 2:1 by weight mixture of ethylene carbonate:dimethyl carbonate.

[0100] FIG. 6 shows the first cycle constant current data obtained for the cell built using the sample of LiVPO₄F. A slight inflection is seen in the data during the charge process, which is related to preferential depopulation of one of the Li sites within the structure. No such feature is observed during the discharge process, indicating that during reinsertion of the Li neither of the sites is preferred. This observation is clearly supported by the observation of two peaks in the differential capacity plot obtained during EVS measurement. Long term cycling of this material shows good electrochemical properties.

EXAMPLE 3

[0101] An electrode active material comprising LiV_1-xAl_xPO₄F was made according to the following reaction scheme:
(1-x)VPO₄+x AlPO₄+LiF→LiV_1-xAl_xPO₄F

[0102] The LiF, VPO₄and AlPO₄were mixed and micronized in the required amounts. If for example x=0.2
0.8 VPO₄+0.2 AlPO₄+LiF→LiV_0.8Al_0.2PO₄F
Then 1.167 g of VPO₄were mixed with 0.244 g AlPO₄and 0.259 g LiF. The mixture was then heated in the temperature range 600-700° C. for up to 1 hour.

[0103] An electrode is made with 84% of the active material, 6% of Super P conductive carbon, and 10% poly vinylidene difluoride. A cell with that electrode as cathode and a lithium anode is constructed with an electrolyte comprising 1 M LiPF₆dissolved in 2:1 by weight mixture of ethylene carbonate:dimethyl carbonate.

[0104] FIG. 7 shows the X-ray powder patterns for samples of LiV_1-xAl_xPO₄F. The results shown in FIG. 7 show that high quality samples can be prepared relatively easily.

[0105] FIG. 8 is a plot of Al content versus unit cell volume, obtained from Rietveld analysis of several samples. The plot clearly shows a linear relationship between Al content and the unit cell volume which is consistent with Vegards law, i.e. formation of a solid solution series between the V and Al.

[0106] Varying the amount of Al in a sample makes it possible to vary the operating voltage of the sample. FIG. 9 shows a comparison of the electrochemical response of samples containing varying amounts of Al. Addition of more Al to a sample has the effect of reducing the overvoltage (i.e. voltage polarization) and is thought to be related to the increase in substitutionial disorder of the material. The addition of Al on the V sites upsets the ordering (V-V-etc) of the transition metal. This will affect the resultant voltage characteristics to some extent. However, as Al is electrochemically inactive it has the effect of reducing the overall capacity of the material. Life cycling data suggests that the Al doped samples have a lower fade rate then observed with LiVPO₄F.

EXAMPLE 4

[0107] An electrode active material comprising Na_1.2VPO₄F_1.2was made as follows. In a first step, a metal phosphate was made by carbothermal reduction of a metal oxide, here exemplified by vanadium pentoxide. The overall reaction scheme of the carbothermal reduction is as follows.
0.5V₂O₅+NH₄H₂PO₄+C→VPO₄+NH₃+1.5H₂O+CO
9.1 grams of V₂O₅, 11.5 grams of NH₄H₂PO₄and 1.2 grams of carbon (10% excess) are used. The precursors were premixed using a mortar and pestle and then pelletized. The pellet was transferred to an oven equipped with a flowing argon atmosphere. The sample was heated at a ramp rate of 2° per minute to an ultimate temperature of 300° C. and maintained at this temperature for three hours. The sample was cooled to room temperature, removed from the oven, recovered, re-mixed and repelletized. The pellet is transferred to a furnace with an argon atmosphere. The sample is heated at a ramp rate of 2° per minute to an ultimate temperature 750° C. and maintained at this temperature for 8 hours.

[0108] In a second step, the vanadium phosphate made in the first step was reacted with an alkali metal halide, exemplified by sodium fluoride, according to the following reaction scheme.
xNaF+VPO₄→Na_xVPO₄F_x
14.6 grams of VPO₄and 4.2 grams of NaF were used. The precursors are pre-mixed using a mortar and pestle and then pelletized. The pellet was transferred to an oven equipped with a flowing argon atmosphere. The sample was heated at a ramp rate of 2° per minute to an ultimate temperature of 750° C. and maintained at this temperature for an hour. The sample was cooled and removed from the furnace.

[0109] To make Na_1.2VPO₄F_1.2, the reaction is repeated with a 20% mass excess of sodium fluoride over the previous reaction. The precursors were pre-mixed using a mortar and pestle and pelletized as before. The sample was heated to an ultimate temperature of 700° C. and maintained at this temperature for 15 minutes. The sample was cooled and removed from the oven. There is only a small weight loss during reaction, indicating almost full incorporation of the NaF. To make an active material of formula Na_1.5VPO₄F_1.5the reaction is repeated with an approximate 50% mass excess of sodium fluoride over the first reaction. The sample is heated at 700° C. for 15 minutes, cooled, and removed from the oven.

[0110] An electrode is made with 84% of the active material, 6% of Super P conductive carbon, and 10% poly vinylidene difluoride. A cell with that electrode as cathode and lithium foil as anode is constructed with an electrolyte comprising 1 M LiPF₆dissolved in 2:1 by weight mixture of ethylene carbonate:dimethyl carbonate.

EXAMPLE 5

[0111] An electrode active material comprising LiVP₂O₇was made according to the following reaction scheme.
LiH₂PO₄+VPO₄→LiVP₂O₇+H₂O
LiH₂PO₄(10.39 g) and VPO₄(14.59 g) were used. The precursors were mixed using a mortar and pestle and then pelletized. The pellet was transferred to an oven equipped with a flowing argon atmosphere. The sample was heated at a ramp rate of 2° per minute to an ultimate temperature of 750° C. and maintained at this temperature for an hour. It has been found that this material can be prepared in temperatures ranging from about 650° C. to about 850° C. The sample is cooled and removed from the furnace.

[0112] An electrode is made with 84% of the active material, 6% of Super P conductive carbon, and 10% poly vinylidene difluoride. A cell with that electrode as cathode and carbon intercalation anode is constructed with an electrolyte comprising 1 M LiPF₆dissolved in 2:1 by weight mixture of ethylene carbonate:dimethyl carbonate.

[0113] FIG. 10 is a representative X-ray powder pattern for LiVP₂O₇. The structure of this material has been examined using the Rietveld method using the model presented by Rousse. Rousse et al., Int. J. Inorg. Mat., 3, 881 (2001). The obtained fit is presented in FIG. 11. The refined unit cell lattice parameters are: a=4.8211(2) Å, b=8.1283(3) Å, c=6.9404(3) Å, α=90°, β=108.949(2)°, γ=90°, volume=257.24(2) Å³with R_wp=12.97%, R_p=9.23% and x²=1.30.

[0114] The structure of LiVP₂O₇can be described as a 3-D framework of corner sharing VO₆octahedra and P₂O₇groups. This framework arrangement provides tunnels in which Li ions are coordinated tetrahedrally, as shown in FIG. 12.

[0115] Previous studies by Uebou and Wurm have shown that this material has relatively poor electrochemical properties, with discharge capacities in the region of 50 mAh/g observed at a very low rate (typically a very low rate). Uebou et al., Solid State Ionics, 148, 323, (2002). Wurm et al., Chem. Mater., 14, 2701, (2002). The present inventors have found that by producing a composite of this diphosphate and a high surface area carbon, there is a noticeable improvement in the electrochemical properties. The properties are shown in FIG. 13.

[0116] The data in FIG. 13 shows a discharge capacity in the region of about 68 MAh/g. Taking into account the residual carbon this discharge capacity has a value closer to about 71 mAh/g. Although this would appear to be only a modest improvement over that reported by Uebou and Wum, these experiments were performed at a rate in the region of C/15. It is believed that some of the irreversibility is due to the upper voltage limit used in this experiment.

[0117] FIG. 14 shows the results of an EVS experiment performed using voltage limits of 2.5 to 4.7 volts (versus Li). The reversible specific capacity for LiVP₂O₇is 93 mAh/g. It was noted however, that the capacity increased slowly over the first ten cycles, reaching 101 mAh/g after the tenth cycle. Examination of the differential capacity versus cell voltage plot shows that this system works with relatively low polarization. The differential capacity plot shows some evidence of decomposition at voltages greater than approximately 4.35 volts.

[0118] Similarly, good results have been obtained in Li ion cells, with EVS results after 10 cycles shown in FIG. 15. It can be seen therefrom that there is a decrease in observed cell polarization. FIG. 16 shows the results of life cycle experiments performed with this material.

EXAMPLE 6

[0119] An electrode active material comprising Li_0.1Na_0.9VPO₄F was made according to the following reaction scheme.
xLiF+(1-x)NaF+VPO₄→Li_xNa_1-xVPO₄F
As an alternative to using alkali fluorides, a reaction between VPO₄and NH₄F and a mixture of Li₂CO₃and Na₂CO₃may also be used.

[0120] To make Li_0.1Na_0.9VPO₄F, 1.459 grams VPO₄, 0.026 grams of LiF, and 0.378 grams of NaF were premixed, pelletized, placed in an oven and heated to an ultimate temperature of 700° C. The temperature is maintained for fifty minutes after which the sample is cooled to room temperature and removed from the oven. To make Li_0.95Na_0.05VPO₄F, 1.459 grams of VPO₄, 0.246 grams of LiF, and 0.021 grams of NaF are mixed together and heated in an oven as in the previous step. An electrode is made with 84% of the active material, 6% of Super P conductive carbon, and 10% poly vinylidene difluoride. A cell with that electrode as cathode and carbon intercalation anode is constructed with an electrolyte comprising 1 M LiPF₆dissolved in 2:1 by weight mixture of ethylene carbonate:dimethyl carbonate.

EXAMPLE 7

[0121] An electrode active material comprising NaVPO₄F is made hydrothermally according to the following reaction scheme.
NaF+VPO₄→NaVPO₄F

[0122] 1.49 grams of VPO₄and 1.42 grams of NaF are premixed with approximately 20 milliliters of deionized water, transferred and sealed in a Parr Model 4744 acid digestion bomb, which is a Teflon lined stainless steel hydrothermal reaction vessel. The bomb is placed in an oven and heated at a ramp rate of 5° per minute to an ultimate temperature of 250° C. to create an internal pressure and maintained at this temperature for forty-eight hours. The sample is slowly cooled to room temperature and removed from the furnace for analysis. The product sample is washed repeatedly with deionized water to remove unreacted impurities. Then the sample is dried in an oven equipped with argon gas flow at 250° C. for one hour. An electrode is made with 84% of the active material, 6% of Super P conductive carbon, and 10% poly vinylidene difluoride. A cell with that electrode as cathode and carbon intercalation anode is constructed with an electrolyte comprising 1 M LiPF₆dissolved in 2:1 by weight mixture of ethylene carbonate:dimethyl carbonate.

EXAMPLE 8

[0123] An electrode active material of formula NaVPO₄OH is made according to the following reaction scheme.
NaOH+VPO₄→NaVPO₄OH

[0124] In this Example, the reaction of the Example 7 is repeated, except that an appropriate molar amount of sodium hydroxide is used instead of sodium fluoride. The reaction is carried out hydrothermally as in Example 7. The hydroxyl group is incorporated into the active material at the relatively low temperature of reaction. An electrode is made with 84% of the active material, 6% of Super P conductive carbon, and 10% poly vinylidene difluoride. A cell with that electrode as cathode and carbon intercalation anode is constructed with an electrolyte comprising 1 M LiPF₆dissolved in 2:1 by weight mixture of ethylene carbonate:dimethyl carbonate.

EXAMPLE 9

[0125] An electrode active material comprising NaVPO₄F is made according to the following reaction scheme.
0.5Na₂CO₃+NH₄F+VPO₄→NaVPO₄F+NH₃+0.500O₂+0.5H₂O

[0126] 1.23 grams of VPO₄, 0.31 grams of NH₄F, and 0.45 grams Na₂CO₃are premixed with approximately 20 milliliters of deionized water and transferred and sealed in a Parr Model 4744 acid digestion bomb, which is a Teflon lined stainless steel reaction vessel. The bomb is placed in an oven and heated to an ultimate temperature of 250° 0 and maintained at this temperature for forty-eight hours. The sample is cooled to room temperature and removed for analysis. The sample is washed repeatedly with the deionized water to remove unreacted impurities and thereafter is dried in an argon atmosphere at 250° C. for an hour. An electrode is made with 84% of the active material, 6% of Super P conductive carbon, and 10% poly vinylidene difluoride. A cell with that electrode as cathode and carbon intercalation anode is constructed with an electrolyte comprising 1 M LiPF₆dissolved in 2:1 by weight mixture of ethylene carbonate:dimethyl carbonate.

EXAMPLE 10

[0127] Electrode active materials comprising compounds of the formula LiV_1-xAl_xPO₄were made according to the following reaction scheme:
(1-x) VPO₄+x AlPO₄+LiH₂PO₄→LiV_1-xAl_xP₂O₇+H₂O

[0128] The precursors were mixed using a mortar and pestle and then pelletized. The pellet was transferred to an oven equipped with a flowing argon atmosphere. The samples were heated at a ramp rate of 2° per minute to an ultimate temperature of about 650° C. to about 850° C. and maintained at these temperatures for about 4 to about 8 hours. The sample is cooled and removed from the furnace. An electrode is made with 84% of the active material, 6% of Super P conductive carbon, and 10% polyvinylidene difluoride. A cell with that electrode as cathode and lithium anode is constructed with an electrolyte comprising 1M LiPF₆dissolved in 2:1 by weight ethylene carbonate to dimethyl carbonate is constructed and tested.

[0129] Al³⁺ is electrochemically inactive and therefore reduces the amount of Li that can be extracted. Thus many of the samples prepared were lower Al content samples, typically in the range of 5-15% Al doping. The X-ray patterns for a selection of samples so prepared are shown in FIG. 17.

[0130] The electrochemical properties of the samples so prepared are shown in FIG. 18.

EXAMPLE 11

[0131] An electrode active material comprising Li₃V₂(PO₄)₃was made according to the following reaction scheme.
Li₃PO₄+2VPO₄→Li₃V₂(PO₄)₃
LiPO₄(11.58 g) and VPO₄(29.18 g) were used. The precursors were mixed using a mortar and pestle and then pelletized. The pellet was transferred to an oven equipped with a flowing argon atmosphere. The samples were heated at a ramp rate of 2° per minute to an ultimate temperature of about 650° C. to about 850° C. and preferably 700 to 750° C. and maintained at these temperatures for about 1 to about 8 hours. The sample is cooled and removed from the furnace.

[0132] FIG. 19 shows a representative X-ray pattern of a sample prepared as above.

[0133] An electrode is made with 84% of the active material, 6% of Super P conductive carbon, and 10% poly vinylidene difluoride. A cell with that electrode as cathode and a lithium anode is constructed with an electrolyte comprising 1 M LiPF₆dissolved in 2:1 by weight mixture of ethylene carbonate:dimethyl carbonate.

[0134] FIG. 20 shows the electrochemical properties of the sample.

EXAMPLE 12

[0135] An electrode active material comprising Na₃V₂(PO₄)₂F₃is made as follows. First, a VPO₄precursor is made according to the following reaction scheme.
V₂O₅+2(NH₄)₂HPO₄+2 C→2 VPO₄+4 NH₃+3 H₂O+2 CO
A mixture of 18.2 g (0.1 mol) of V₂O₅, 26.4 g (0.2 mol) of (NH₄)₂HPO₄, and 2.64 g (0.2 mol+10% mass excess) of elemental carbon was made, using a mortar and pestle. The mixture was pelletized, and transferred to a box oven equipped with an argon gas flow. The mixture was heated to a temperature of about 350° C., and maintained at this temperature for 3 hours. The mixture was then heated to a temperature of about 750° C., and maintained at this temperature for 8 hours. The product is then cooled to ambient temperature (about 21° C.).

[0136] Na₃V₂(PO₄)₂F₃was then made from the VPO₄precursor. The material was made according to the following reaction scheme.
2 VPO₄+3 NaF→Na₃V₂(PO₄)₂F₃
A mixture of VPO₄(2.918 g) and NaF (1.26 g) was made, using a mortar and pestle. The mixture was pelletized, and transferred to a temperature-controlled tube furnace equipped with an argon gas flow. The mixture is heated at a ramp rate of about 220 /minute to an ultimate temperature of about 750° C. for 1 hour Temperatures can be in the region of 700-800° C. for these samples and can be heated in this region for about one to about four hours. The product is then cooled to ambient temperature (about 20° C.). A representative X-ray powder pattern is shown in FIG. 21 X-ray powder diffraction analysis for the Na₃V₂(PO₄)₂F₃material indicated the material to be single phase with a tetragonal structure (space group P42/mnm). The unit cell parameters (a=9.0304(5) Å, c=10.6891(9) Å) were calculated from a least squares refinement procedure, in fair agreement with the structural analysis for Na₃V₂(PO₄)₂F₃described by Meins et al., J. Solid State Chem., 148, 260, (1999). (i.e. a=9.047(2) Å, c=10.705(2) Å).

EXAMPLE 13

[0137]
0.5 V₂O₅+(NH₄)₂HPO₄+C→VPO₄+NH₃+1.5 H₂O+CO

[0138] Vanadium oxide (V₂O₅; 9.10 g), diammonium hydrogen phosphate (13.2 g) and elemental carbon (1.32 g, 10% mass excess) were weighed and poured into a micronising pot. The materials were then micronised for 15 minutes. This process step has the dual purpose of providing intimate mixing and dispersion of the raw materials to produce a homogenous mixture and reducing particles size of the material due to the grinding/milling action. After micronising, the resulting powder was pressed to form a pellet. The pellet was placed in a crucible and placed in a tube furnace. The pellet was fired at 700° C. at a ramp rate of 2° C./minute with a 16 hour dwell under an inert atmosphere. After firing, the pellet was broken up and ground to produce a powder. FIG. 23 shows the X-rd trace for the resulting VPO₄. The trace shows that the VPO₄is an amorphous V—P—O/C precursor.
VPO₄+LiF→LiVPO₄F

[0139] The VPO₄(1.46 g) precursor so obtained was then micronised for 15 minutes with LiF (0.26 g). After micronising, the resultant powder was pressed to form a pellet was placed in a crucible, sealed by a second crucible and placed in a tube furnace. The pellet is fired at 700° C. at a ramp rate of 2° C./minute with a one hour dwell under an inert atmosphere. After firing, the pellet was broken up and ground to produce the final LiVPO₄F material. FIG. 24 shows the Xrd trace for the resulting LiVPO₄F.

[0140] The examples and other embodiments described herein are exemplary and not intended to be limiting in describing the full scope of compositions and methods of this invention. Equivalent changes, modifications and variations of specific embodiments, materials, compositions and methods may be made within the scope of the present invention, with substantially similar results.

Claims

Certificate of Correction present

The claims shown below may not include correction changes. Use the corrected PDF for authoritative text.

What is claimed is:

1. A method for making a vanadium phosphate precursor comprising mixing V₂O₅with a phosphate compound and a carbon containing compound or a carbon precursor to form a mixture, milling or micronizing the mixture, and heating the milled or micronized mixture at a temperature of about 600° C. and for a time sufficient to form an amorphous V—P—O—carbon composite precursor.

2. The method according to claim 1 wherein the phosphate compound is (NH₄)₂HPO₄or (NH₄)H₂PO₄.

3. The method according to claim 1 wherein the carbon is a conductive high surface area carbon with a surface area of from about 1 to about 1000 m²/g.

4. The method according to claim 3 wherein the carbon is carbon black.

5. The method according to claim 2 wherein the carbon is selected from a graphitic carbon or organic precursor materials.

6. A method for making a vanadium phosphate compound of the formula:

A_aV_1-xM_x(PO₄)_dZ_f. (I)

wherein A is selected from the group consisting of Li, Na, K and mixtures thereof;

a is greater than 0.1 and less than or equal to 3;

x is greater than or equal to zero and less than 1;

d is greater than 0 and less than or equal to 3;

M is a metal selected from the group consisting of Al, Ti, Cr, Fe, Mn, Mo, and Nb;

Z is F, CI, or OH:

and f is greater than or equal to zero but less than or equal to three;

comprising mixing the V—P—O—carbon composite precursor produced according to the method of claim 1 with an alkali metal containing compound to form a mixture and heating the mixture at a temperature and for a time sufficient to form the vanadium phosphate compound.

7. The method according to claim 6 wherein the mixture further comprises a second metal containing compound.

8. The method according to claim 6 wherein the alkali metal compound is selected from the group consisting of LiF, NaF, NaOH, LiOH, Na₂CO₃and Li₃PO₄.

9. The method according to claim 7 wherein the metal containing compound comprises a metal ion of a metal selected from the group consisting of Al, Ti, Cr, Fe, Mn, Mo and Nb.

10. The method according to claim 6 wherein the vanadium phosphate compound produced is selected from LiVPO₄, Li_0.1Na_0.9VPO₄F, NaVPO₄F, NaVPO₄OH, NaVPO₄F, Li₃V₂(PO₄)₃, LiV_0.75Al_0.25PO₄F, LiV_0.5Al_0.5PO₄F, Na_1.2VPO₄F_1.2or Na₃V₂(PO₄)₂F₃.

11. A method for making a vanadium phosphate compound of the formula:

A_aV_1-xM_xM_xP₂O₇ (I)

wherein A is selected from the group consisting of Li, Na, K and mixtures thereof;

a is greater than 0.1 and less than or equal to 3;

x is greater than or equal to zero and less than 1; and

M is a metal selected from the group consisting of Al, Ti, Cr, Fe, Mn, Mo and Nb;

12. The method according to claim 11 wherein the mixture further comprises a second metal containing compound.

13. The method according to claim 11 wherein the alkali metal compound is selected from the group consisting of LiF, NaF, NaOH, LiOH, Na₂CO₃and Li₃PO₄.

14. The method according to claim 12 wherein the metal containing compound comprises a metal ion of a metal selected from the group consisting of Al, Ti, Cr, Fe, Mn, Mo and Nb.

15. The method according to claim 11 wherein the vanadium phosphate compound produced is LiVP₂O₇.

Patent Citations (10)

Patent	Date	Inventor	Cited By
US6387568(B1)	2002-05-01	Barker et al.	Applicant
US6645452(B1)	2003-11-01	Barker et al.	Applicant
US6777132(B2)	2004-08-01	Barker et al.	Applicant
US6964827(B2)	2005-11-01	Barker et al.	Applicant
US2003/0013019(A1)	2003-01-01	Barker et al.	Applicant
US2004/0126300(A1)	2004-07-01	Barker et al.	Applicant
US2004/0214084(A1)	2004-10-01	Barker et al.	Applicant
US2005/0255383(A1)	2005-11-01	Barker et al.	Applicant
US2006/0014078(A1)	2006-01-01	Swoyer et al.	Applicant
US2007/0009800(A1)	2007-01-01	Barker et al.	Applicant

Non-Patent Literature (11)

Gover et al., “LiVPO4F: A New Active Material for Safe Lithium-Ion Batteries”, Solid State Ionics 177 (2006) 2635-2638.Applicant
Barker et al., “Structural and Electrochemical Properties of Lithium Vanadium Fluorophosphate, LiVPO4F”, Journal of Power Sources 146 (2005) 516.Applicant
Barker et al., “Performance Evaluation of Lithium Vanadium Fluorophosphate in Lithium Metal and Lithium-Ion Cells”, J.Electro Society 152(9), A1776-A1779 (2005).Applicant
Barker et al., “A Comparative Investigation of the Li Insertion Properties of the Novel Fluorophosphate Phases, NaVPO4F”, J.Electro Society, 151(10), A1670 (2004).Applicant
Barker et al., “Electrochemical Insertion Properties of the Novel Lithium Vanadium Fluorophosphate, LiVPO4F”, J.Electrochemical Soc., 150(10), A1394-A1398 (2003).Applicant
Barker et al., “LiVP2O7: A Viable Lithium-Ion Cathode Material?”, Electrochemical and Solid-State Letters, 8(9), A446-A448, (2005).Applicant
Barker et al., “Hybrid-Ion: A Lithium-Ion Cell Based on a Sodium Insertion Material”, Electrochemical and Solid-State Letters, 9(4), A190-A192 (2006.Applicant
Barker et al, “A Symmetrical Lithium-Ion Cell Based on Lithium Vanadium Fluorophosphate, LiVPO4F”, Electrochemical and Solid-State Letters, 8(6), A285-A287 (2005).Applicant
Barker et al., “A Lithium-Ion Cell Based on Li4/3Ti5/3O4 and LiVPO4F”, Electrochemical and Solid State Letters, 10(5), pp. A130-A133 (2007).Applicant
Gover et al., “The Electrochemical Insertion Properties of Sodium Vanadium Fluorophosphate, Na3V2(PO4)2F3”, Solid State Ionics 177 (2006) 1495-1500.Applicant
PCT International Search Report PCT/US08/55801 dated Aug. 4, 2008.Applicant

Abstract