US 7,910,932 B2Grant

Transparent nanowire transistors and methods for fabricating same

Issue Date:2011-03-22

•27 Claims

•15 Drawing Sheets

Abstract

Disclosed are fully transparent nanowire transistors having high field-effect mobilities. The fully transparent nanowire transistors disclosed herein include one or more nanowires, a gate dielectric prepared from a transparent inorganic or organic material, and transparent source, drain, and gate contacts fabricated on a transparent substrate. The fully transparent nanowire transistors disclosed herein also can be mechanically flexible.

Metadata

Assignees

Northwestern University
Purdue Research Foundation
University of Southern California

Inventors

Tobin J. Marks
David B. Janes
Sanghyun Ju
Peide Ye
Chongwu Zhou
Antonio Facchetti

Application Information

Application Number:US 12/131,697

Filing Date:2008-06-02

Priority Date:2007-06-01

Art Unit:2822

Classifications

IPC:

H01L27/14

Patent Drawings (15 sheets)

Description

[0001] This application claims priority benefit of application Ser. No. 60/932,636 filed Jun. 1, 2007, the entirety of which is incorporated herein by reference.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

[0002] This invention, in part, was made with government support under Grant Nos. NCC-2-1363 and DMR0520513 awarded by the National Aeronautics and Space Administration Institute for Nanoelectronics and Computing and the National Science Foundation, respectively, to Northwestern University. The United States Government has certain rights in this invention

BACKGROUND

[0003] Development of optically transparent and mechanically flexible electronic circuitry represents an enabling step toward next-generation display technologies, including “see-through” and conformable products. In addition to transparency and flexibility, transistor performance metrics such as high on-current (I_on), high on/off current ratio (I_on/I_off), high field-effect mobility (μ_eff), steep subthreshold slope (S), and small threshold voltage (V_T) variation during transistor operation are required to realize commercially viable logic circuits and display devices.

[0004] Nanowire transistors (NWTs), i.e., transistors incorporating semiconducting nanowires as charge transporting channel materials, are of particular interest for future display devices because of their high carrier mobilities and stability compared with other thin film transistors (TFTs). The use of pre-formed nanowires also allows low-temperature device processing, which is essential for applications such as circuits fabricated on plastic substrates. While there have been several recent reports of transparent transistors fabricated with ZnO, SnO₂, In₂O₃or other semiconducting oxide thin films, or with carbon nanotube networks as the active channel layers and opaque source and drain metals, or with carbon nanotube films and transparent source/drain electrodes (see e.g., Carcia, P. F. et al., Appl. Phys. Lett., 82: 1117-1119 (2003); Fortunato, E. et al., Thin Solid Films, 487: 205-211 (2005); Hoffman, R. L. et al., Appl. Phys. Lett., 82: 733-735 (2003); Nomura, K. et al., Science, 300: 1269-1272 (2003); Presley, R. E. et al., J. Phys. D: Appl. Phys., 37: 2810-2813 (2004); Wang, L. et al., Nature Mater., 5: 893-900 (2006); Hur, S.-H. et al., Appl. Phys. Lett., 86, 243502-1-3 (2005); and Takenobu, T. et al., Appl. Phy. Lett., 88: 33511-1-3 (2006)), there have been no reports of fully transparent NWTs fabricated with all-transparent gate and source/drain electrodes and displaying high levels of transistor performance.

SUMMARY

[0005] In light of the foregoing, the present teachings provide nanowire-based transistors and circuits that can comprise one or more semiconducting nanowires as the channel material. In some non-limiting embodiments, the nanowire transistor structures of the present teachings can be fully transparent and comprise components made from various transparent materials. Given the small diameter of a nanowire, “fully transparent” nanowire transistors described herein can comprise one or more non-transparent nanowires (e.g., without limitation, nanowires made from Group 14 elements such as Si, Ge, and alloys thereof, one or more Group 13-15 elements such as GaAs, GaN, and InP, and one or more Group 12-16 elements such as CdS and CdSe) as well as transparent oxide nanowires (e.g., without limitation, ZnO, In₂O₃, and SnO₂nanowires), and transparent gate and source/drain electrodes. The nanowire transistors of the present teachings can exhibit high performance n-type transistor characteristics with satisfactory optical transparency. Among various applications, the nanowire transistors of the present teachings can be attractive as pixel switching and driving transistors in active-matrix organic light-emitting diode (AMOLED) displays, and can supply sufficient current to drive pixels employing reported electroluminescent organic materials. The transparency of the drive circuitry can enable significant increases in aperture ratio in active-matrix arrays, which can lead to higher display brightness and decreased power consumption. The high mobility of the nanowire channel materials also can allow faster switching of the transistor circuits, which can allow circuit approaches such as direct digital drive of display elements.

[0006] In certain embodiments, the nanowire transistor devices of the present teachings can comprise one or more semiconducting nanowires extending between a source electrode and a drain electrode, and a gate dielectric in contact with the one or more semiconducting nanowires. In some embodiments, the device can include a single semiconducting nanowire as the channel material. In other embodiments, the device can include a plurality of semiconducting nanowires to fulfill larger current carrying needs. As described above, in some embodiments, the one or more semiconducting nanowires can be prepared from a Group 14 element such as, without limitation, Si and Ge. In other embodiments, transparent semiconducting nanowires prepared from transparent metal oxides such as, without limitation, ZnO, In₂O₃, and SnO₂, can be used.

[0007] In some embodiments, the gate dielectric can be an inorganic layer of one or more transparent metal oxides. For example, the gate dielectric can be a Group 3 metal oxide, a Group 5 metal oxide, or a Group 13 metal oxide such as, but not limited to, aluminum oxide (Al₂O₃), yttrium oxide (Y₂O₃), tantalum pentoxide (Ta₂O₅), hafnium oxide (HfO₂), and vanadium oxide (V₂O₅). Such metal oxides can optionally include one or more dopants. The oxide gate dielectric can be deposited by various techniques known in the art including, without limitation, thermal evaporation, sputtering, metalorganic chemical vapor deposition (MOCVD), atomic layer deposition (ALD), ion-assisted deposition (IAD), and pulsed-laser deposition (PLD).

[0008] In certain embodiments, the gate dielectric can be an organic multi-layer composition. This multi-layer composition can comprise periodically alternating layers of one or more layers that include a polarizable moiety, and one or more layers that can comprise a silyl or siloxane moiety. The polarizable moiety (e.g., without limitation, a π-polarizable moiety) can include conjugated π-electrons. The siloxane moiety can comprise oligomeric or polymeric moieties having —Si—O— bonds. In particular embodiments, there can be one or more layers that comprise a sigma moiety among the periodically alternating layers. The sigma moiety can comprise a hydrocarbon as described in more detail below.

[0009] In some embodiments, the polarizable moiety can be a moiety having at least one of a dipole moment, an electron releasing moiety, an electron withdrawing moiety, a combination of such moieties, a zwitterion and a net charge. For example, the polarizable moiety can be a non-linear optical (NLO) chromophore. In some embodiments, the chromophore can comprise a π-conjugated system, which can comprise a system of atoms covalently bonded with alternating single and multiple (e.g., double) bonds (e.g., C═C—C═C—C and C═C—N═N—C). The π-conjugated system can comprise one or more heteroatoms such as, but not limited to, nitrogen (N), oxygen (O), and sulfur (S). In some embodiments, the π-conjugated system can comprise one or more aromatic rings (aryl or heteroaryl) linked by conjugated hydrocarbon chains. In certain embodiments, the aromatic rings can be linked by conjugated chains that include heteroatoms and heteroatom-containing groups (e.g., azo groups [—N═N—]). For example, the polarizable moiety can be a chromophore that comprises a stilbazolium group.

[0010] Various polarizable moieties that can be used according to the present teachings are described in U.S. Pat. No. 6,855,274, in particular the NLO structures of FIGS. 1-2, 11, and 13-15 thereof, U.S. Pat. No. 6,549,685, in particular the NLO structures of FIGS. 2-3 thereof, and U.S. Pat. No. 5,156,918, in particular the NLO structures of FIGS. 4-5 thereof, each with reference to the corresponding specification regarding alternate embodiments, synthesis, and characterization, and each of which is incorporated by reference herein in its entirety. In particular embodiments, the polarizable moiety can comprise a stilbazonium group.

[0011] At least some of the alternating layers can be coupled to an adjacent layer by a coupling layer that comprises a siloxane matrix. The coupling can be performed via a condensation reaction or chemisorption using known silicon chemistry. For example, two layers including the polarizable moiety can be coupled to each other by a coupling layer that comprises a siloxane matrix, resulting in a three-layered composition that includes alternating layers of a first layer including a polarizable moiety, a coupling layer that includes a siloxane matrix, and a second layer that includes a polarizable moiety. One or more layers including a polarizable moiety also can be crosslinked by a siloxane matrix. In some embodiments, at least some of the alternating layers can be coupled or covalently bonded to one another or the siloxane matrix via a condensation reaction. For example, the three-layer composition described above can include condensation products of a silane-substituted stilbazolium compound (e.g., 4-[[(4-(N,N-bis((hydroxy)ethyl)amino]-phenyl]azo]-1-(4-trichlorosilyl)benzyl-pyridinium iodide, or 4-[[(4-(N,N-bis((hydroxyl)ethyl)amino]-phenyl]azo]-1-(4-dichloroiodosilyl)benzyl-pyridinium iodide) and a trisiloxane compound (e.g., without limitation, octachlorotrisiloxane or other similar compounds including Si—O bonding sequence with hydrolyzable groups). Exemplary hydrolyzable groups comprise, without limitation, halides, hydroxyl groups, alkoxy groups, amine groups, and carboxyl groups.

[0012] In some embodiments, the multi-layer composition also can include a hydrocarbon layer (i.e., a sigma moiety). Such a hydrocarbon layer can comprise a C₁- about C₂₀alkyl group or a C₁- about C₂₀haloalkyl group. Such a hydrocarbon layer can be coupled to a coupling layer that comprises a siloxane matrix, or it can be coupled to a layer comprising a polarizable moiety directly or via a coupling layer that comprises a siloxane matrix as described above. To allow coupling, the alkyl or haloalkyl group can be functionalized with silyl moieties having hydrolyzable groups. For example, at least some of the alternating layers can include a condensation product of a bis(silyl)-about C₄to about C₂₀alkyl compound (e.g., without limitation, Cl₃Si(CH2)_nSiCl₃, (CH₃O)₃Si(CH₂)_nSi(OCH₃)₃, and (Me₂N)₃Si(CH₂)_nSi(NMe₂)₃, where n can be 4, 5, 6, 7, 8, 9, or 10) and a trisiloxane compound (e.g., without limitation, octachlorotrisiloxane or other similar compounds including Si—O bonding sequence with hydrolyzable groups). Such bis-silylated compounds are hydrolyzable to a degree at least partially sufficient for substrate sorption or condensation or intermolecular crosslinking via siloxane bond formation under the processing or fabrication conditions employed. Similarly, the polarizable moiety can be derivatized to include similar silyl hydrolyzable groups, to allow bond formation with the siloxane coupling layer and/or the hydrocarbon layer. In particular embodiments, the hydrocarbon layers and the layers comprising a polarizable moiety can be individually self-assembled monolayers. Synthesis of such self-assembled nanodielectric (SAND) materials are more fully described in Yoon, M-H. et al., PNAS, 102 (13): 4678-4682 (2005), which is incorporated by reference herein in its entirety.

[0013] In further embodiments, the gate dielectric can be a polymer. For example, the gate dielectric can be a polymer such as, without limitation, polyhydroxystyrene and polystyrene. In certain embodiments, the gate dielectric can be a crosslinked polymer, examples of which include, but are not limited to, the various crosslinked polymeric dielectric materials described in U.S. patent application Ser. Nos. 11/315,076, 60/816,952, and 60/861,308, each of which is incorporated by reference herein in its entirety.

[0014] The source electrode and the drain electrode can be prepared from various transparent conductive oxides. Examples include, without limitation, indium tin oxide (ITO), indium zinc oxide (IZO), indium oxide, zinc oxide, zinc indium tin oxide (ZITO), and other similar optionally doped metal oxides (e.g., fluorinated tin oxide, gallium zinc oxide (GZO), gallium indium oxide (GIO) and gallium indium tin oxide (GITO)). A nanowire transistor device of the present teachings also can, without limitation, comprise a gate electrode prepared from one or more of the transparent conductive oxides described above.

[0015] In various embodiments and to provide a fully transparent nanowire transistor device, the gate dielectric can be deposited on a transparent substrate. Examples of suitable substrates include but are not limited to glass and various transparent plastic materials (both rigid and flexible). Examples of flexible plastic substrates include, but are not limited to, polyethylene terephthalate (PET) and polyethylene naphthalate (PEN).

[0016] The present teachings further provide methods for fabricating a nanowire transistor device. Such a method can comprise applying a gate electrode layer on a substrate, applying a dielectric layer on the gate electrode layer, applying one or more semiconducting nanowires on the dielectric layer, and applying a source electrode and a drain electrode on the dielectric layer, wherein the application of the gate electrode layer, the application of the dielectric layer, the application of the one or more semiconducting nanowires, and the application of the source electrode and the drain electrode are conducted at a temperature less than about 100° C. (e.g., at or near room temperature). Each of the gate electrode layer, the dielectric layer, the source electrode, the drain electrode, and the substrate can be transparent (for example, by using the various suitable materials disclosed herein), and one or more semiconducting nanowires can extend between the source electrode and the drain electrode. In some embodiments, the application of the one or more semiconducting nanowires can involve dispersing a suspension that includes one or more semiconducting nanowires on the dielectric layer. In some embodiments, the application of the dielectric layer can comprise forming at least one condensation product of a silane-substituted stilbazoium compound and a trisiloxane compound, and optionally, at least one condensation product of a bis(silyl)-about C₄to about C₂₀alkyl compound and a trisiloxane compound. The resulting nanowire transistor device can be subjected to ozone treatment to further improve its device performance, for example, to increase its field effect mobility.

[0017] The foregoing, other features, and advantages of the present teachings, will be more fully understood from the following figures, description, and claims.

BRIEF DESCRIPTION OF DRAWINGS

[0018] It should be understood that the drawings described below are for illustration purpose only. The drawings are not necessarily to scale and are not intended to limit the scope of the present teachings in any way. The patent or application file contains at least one drawing executed in color. Copies of this patent or patent application publication with color drawing(s) will be provided by the office upon request and payment of the necessary fee.

[0019] FIG. 1a is a cross-sectional view of an embodiment of a nanowire transistor (NWT) device according to the present teachings. In particular, the illustrated device consists of a SiO₂buffer layer (500 nm), a patterned IZO (In—Zn—O) gate electrode (120 nm), an atomic layer deposition (ALD)-deposited Al₂O₃gate insulator (18 nm), a single In₂O₃nanowire (D˜20 nm) or ZnO nanowire (D˜120 nm) for the active channel, and ITO for the source/drain electrodes (120 nm). Scale bar: 100 μm.

[0020] FIG. 1b is a top-view field-emission scanning electron microscopic (FE-SEM) image of an NWT device analogous to the one illustrated in FIG. 1a. Scale bar: 100 μm.

[0021] FIG. 1c is a top-view SEM image of a single In₂O₃nanowire region (D/L˜20 nm/1.80 μm) of an NWT device analogous to the one illustrated in FIG. 1a. Scale bar: 1.5 μm.

[0022] FIG. 1d is a top-view SEM image of a single ZnO nanowire region (D/L˜120 nm/1.66 μm) of an NWT device analogous to the one illustrated in FIG. 1a. Scale bar: 1.5 μm.

[0023] FIG. 2a shows the gate leakage current (B: black dots) and the drain leakage current (A: red dots) of a representative In₂O₃NWT device according to the present teachings. The inset shows the bias configurations.

[0024] FIG. 2b shows the linear-scale and log-scale I_ds-V_gscharacteristics at V_d=0.5 V of a representative In₂O₃NWT device analogous to the one illustrated in FIG. 1a. Arrows indicate appropriate axis. Data points are shown for the device before (black dots, 1) and after (red solid line, 2) two minutes of ozone treatment.

[0025] FIG. 2c shows the log-scale I_ds-V_gscharacteristics during four successive sweeps from −4 V to +4 V (V_d=0.5 V) of a representative In₂O₃NWT device analogous to the one illustrated in FIG. 1a. Black, red, green and blue (square, circular, up and down triangle) data points correspond to 1^st, 2^nd, 3^rdand 4^thsweeps. The time between sweeps is ˜1 second.

[0026] FIG. 2d shows the measured I_ds-V_gscharacteristics of a representative In₂O₃NWT device analogous to the one illustrated in FIG. 1a, showing sweeps from −2 V_gto +2 V_g(red circles) and from +2 V_gto −2 V_g(blue squares) as indicated by arrows (V_d=0.5 V). The bias sweep rate (dV_g/d_t) is 2 V/sec.

[0027] FIG. 3a shows the I_ds-V_gscharacteristics at V_d=0.5 V of a representative In₂O₃NWT device (D/L˜20 nm/1.80 μm) analogous to the one illustrated in FIG. 1a. Blue (1), red (2), and green (3) data points correspond to linear-scale I_ds-V_gs, log-scale I_ds-V_gsand μ_eff. Arrows indicate appropriate axis.

[0028] FIG. 3b shows the Ids-Vds characteristics of a representative In2O3 NWT device analogous to the one illustrated in FIG. 1a. Vg is from −0.5 V to 2.5 V at 0.5 V steps, with the maximum current observed at Vg=2.5 V.

[0029] FIG. 3c shows the Ids-Vgs characteristics at Vd=0.5 V of a representative ZnO NWT device (D/L˜120 nm/1.66 μm) analogous to the one illustrated in FIG. 1a. Blue (1), red (2), and green (3) data points correspond to linear-scale I_ds-V_gs, log-scale I_ds-V_gsand μ_eff. Arrows indicate appropriate axis.

[0030] FIG. 3d shows the I_ds-V_dscharacteristics of a representative ZnO NWT device analogous to the one illustrated in FIG. 1a. V_gis from 0.0 V to 3.0 V at 0.5 V steps, with the maximum current observed at V_g=3.0 V.

[0031] FIG. 4 shows the optical transmission spectra for regions containing an In₂O₃NWT or a ZnO NWT according to the present teachings on a glass substrate (ITO (source/drain)/In₂O₃or ZnO nanowires/Al₂O₃(dielectric)/IZO (gate)/SiO₂/glass). Blue and red lines correspond to In₂O₃and ZnO NWTs, respectively. The inset shows a photographic image of a glass substrate having 23,000 In₂O₃NWT devices deposited on its surface, with text on an underlying opaque layer clearly visible.

[0032] FIG. 5a is a cross-sectional view of a fully transparent and flexible NWT device according to the present teachings. In particular, the illustrated device consists of a plastic substrate, a patterned ITO gate electrode (120 nm), an ALD-deposited Al₂O₃gate insulator (50 nm), a single In₂O₃nanowire (D/L˜20 nm/1.79 μm) for the active channel, and ITO for the source/drain electrodes (120 nm).

[0033] FIG. 5b is a photographic image of arrays of representative In₂O₃NWTs deposited on a plastic substrate, showing the optical clarity and mechanical flexibility of the NWTs.

[0034] FIG. 5c shows the optical transmission spectrum of one of the transistor array regions containing In₂O₃NWTs on the plastic substrate (ITO(S/D)/In₂O₃NWs/Al₂O₃/ITO(G)/plastic substrate) shown in FIG. 5b.

[0035] FIG. 5d shows the I_ds-V_gscharacteristics at V_d=0.5 V of a representative In₂O₃NWT having the structure as illustrated in FIG. 5a. Blue (1), red (2), and green (3) data points correspond to linear-scale I_ds-V_gs, log-scale I_ds-V_gsand μ_eff. Arrows indicate appropriate axis.

[0036] FIG. 6a is a cross-sectional view of another embodiment of an NWT device according to the present teachings, specifically, one incorporating self-assembled nanodielectrics (SAND) as the gate insulator.

[0037] FIG. 6b is a top-view FE-SEM image of a representative device having the structure illustrated in FIG. 6a. Scale bar: 1.5 μm.

[0038] FIG. 6c is a cross-sectional band diagram of a representative device having the structure illustrated in FIG. 6a at V_gs=0V.

[0039] FIG. 7a shows the I_ds-V_gscharacteristics at V_d=0.5 V of a representative In₂O₃NWT having the structure illustrated in FIG. 6a. Green (1), red (2) and blue (3) data points corresponding to linear-scale I_ds-V_gs, log-scale I_ds-V_gsand field effect mobility.

[0040] FIG. 7b shows the I_ds-V_dscharacteristics of a representative In₂O₃NWT having the structure illustrated in FIG. 6a.

[0041] FIG. 8a shows the transconductance (g_m) at 5 V_gof a representative In₂O₃NWT having the structure illustrated in FIG. 6a.

[0042] FIG. 8b shows the channel conductance (g_d) from 0.0 V_dto 1.8 V_dof a representative In₂O₃NWT having the structure illustrated in FIG. 6a.

[0043] FIG. 9a shows the top and cross-sectional pixel structure of a drive transistor in a NW-AMOLED array. In particular, each NWT in the circuit structures consists of a SiO₂buffer layer (200 nm), a patterned ITO gate electrode (100 nm), a SAND gate dielectric (24 nm), multiple In₂O₃nanowires for the active channel, ITO for the S-D electrodes (100 nm), and a SiO₂passivation layer (200 nm). The ITO pad on the right serves as the cathode for the organic light-emitting diode (OLED).

[0044] FIG. 9b is a top-view FE-SEM image of several 54×176 μm pixels within a 2×2 mm NWT array layout (rectangles with rounded ends), along with control transistors.

[0045] FIG. 9c is a schematic for a circuit as shown in FIG. 9a for a single pixel, consisting of 1 switching transistor (T1), 2 driving transistors (T2 and T3) and 1 storage capacitor. The bias condition to operate transistor circuit (2 V on scan line for fully turn-on, varying 0 V to 4 V on data line, and 5 V on V_ddline).

[0046] FIG. 9d is an FE-SEM image of a representative region within an NWT transistor channel, showing multiple In₂O₃nanowires connected between S-D electrodes. The diameter of a nanowire and the channel length between S-D electrodes of the device are ˜50 nm and ˜1.5 μm, respectively. Scale bar: 1.5 μm.

[0047] FIG. 10a shows the I_ds-V_gscharacteristics (log scale) of a representative In₂O₃NWT (D/L˜50 nm/1.5 μm) analogous to the one illustrated in FIG. 9a, with red (1), blue (2), green (3), dark blue (4) data points corresponding to V_ds=0.1, 0.2, 0.5 and 1.0 V. The inset shows the hysteresis of the representative device at V_ds=0.1 V.

[0048] FIG. 10b shows the I_ds-V_dscharacteristics for the representative device, with V_gsvarying from 0.0 V to 3.0 V in 0.5 V steps.

[0049] FIG. 10c shows the output current-voltage characteristics for a single-pixel circuit consisting of one switching transistor and two driving transistors (I_dsversus V_dsfor the parallel combination of T2 and T3) for various steps in “data” line voltage (2 V on scan line to fully turn-on T1, 0.0 V to 4.0 V on data line in 0.5 V steps).

[0050] FIG. 10d shows the I_on, I_off, V_Tand S values of 10 representative NWT devices, with red lines indicating the average values for the respective parameters.

[0051] FIG. 11 shows the optical transmission spectrum for representative regions within an NWT channel of a 2×2 mm NW-AMOLED display element (SiO₂(passivation)/ITO (source/drain)/In₂O₃(active channel)/SAND (gate insulator)/ITO (gate)). The inset shows an image of a fully transparent NW-AMOLED substrate consisting of three 2×2 mm transistor arrays, 340 unit pixels, 80 test devices, 6 alignment marks, 20 test patterns, and contact pads.

[0052] FIG. 12a is a cross-sectional view of yet another embodiment of an NWT device structure according to the present teachings. In particular, this embodiment consists of a SiO₂buffer layer, a patterned ITO gate electrode (120 nm), a SAND gate insulator (15 nm), and a single SnO₂nanowire. Depending on the materials for the source/drain electrodes, the NWT can be partially (e.g., Al) or fully transparent (e.g., ITO).

[0053] FIG. 12b shows typical linear-scale and log-scale I_ds-V_gstransfer characteristics at V_d=0.5 V of a representative SnO₂NWT having the structure illustrated in FIG. 12a. Arrows indicate the appropriate axis.

[0054] FIG. 12c shows typical output plots for a representative SnO₂NWT device having the structure illustrated in FIG. 12a.

[0055] FIG. 13a is a cross-sectional view of yet another embodiment of an NWT device structure according to the present teachings. In particular, this embodiment consists of a SiO₂buffer layer, a patterned ITO gate electrode (120 nm), a SAND gate insulator (15 nm), and a single Ge nanowire. Depending on the materials for the source/drain electrodes, the NWT can be partially (e.g., Al) or fully transparent (e.g., ITO).

[0056] FIG. 13b shows typical output plots for a p-type Ge NWT device having the structure illustrated in FIG. 13a.

[0057] FIG. 13c shows typical log-scale I_ds-V_gstransfer characteristics at V_d=−4 V of a p-type Ge NWT having the structure illustrated in FIG. 13a.

[0058] FIG. 13d shows typical output plots for an n-type Ge NWT device having the structure illustrated in FIG. 13a.

[0059] FIG. 13e shows typical log-scale I_ds-V_gstransfer characteristics at V_d=−4 V of an n-type Ge NWT having the structure illustrated in FIG. 13a.

[0060] FIGS. 14a-c show photographic images of NW-AMOLED substrates (top row) and NWT channel regions (bottom row) according to the present teachings, specifically, in which the semiconducting nanowires are as follows: a) In₂O₃, b) SnO₂, and c) p-type Ge.

DETAILED SPECIFICATION

[0061] Throughout the description, where compositions are described as having, including, or comprising specific components, or where processes are described as having, including, or comprising specific process steps, it is contemplated that compositions of the present teachings also consist essentially of, or consist of, the recited components, and that the processes of the present teachings also consist essentially of, or consist of, the recited processing steps.

[0062] In the application, where an element or component is said to be included in and/or selected from a list of recited elements or components, it should be understood that the element or component can be any one of the recited elements or components and can be selected from a group consisting of two or more of the recited elements or components. The use of the term “include” should be generally understood as open-ended and non-limiting unless specifically stated otherwise.

[0063] The use of the singular herein includes the plural (and vice versa) unless specifically stated otherwise. In addition, where the use of the term “about” is before a quantitative value, the present teachings also include the specific quantitative value itself, unless specifically stated otherwise.

[0064] It should be understood that the order of steps or order for performing certain actions is immaterial so long as the present teachings remain operable. Moreover, two or more steps or actions may be conducted simultaneously.

[0065] As used herein, “halide” or “halogen” refers to F, Cl, Br, and I.

[0066] As used herein, “amino” refers to —NH₂, an —NH-alkyl group, and an —N(alkyl)₂group.

[0067] As used herein, “alkoxy” refers to an —O-alkyl group. Examples of alkoxy groups include, but are not limited to, methoxy, ethoxy, propoxy (e.g., n-propoxy and isopropoxy), t-butoxy groups, and the like.

[0068] As used herein, “alkyl” refers to a straight-chain or branched saturated hydrocarbon group. Examples of alkyl groups include methyl (Me), ethyl (Et), propyl (e.g., n-propyl and isopropyl), butyl (e.g., n-butyl, isobutyl, sec-butyl, tert-butyl), pentyl groups (e.g., n-pentyl, isopentyl, neopentyl), and the like. In various embodiments, an alkyl group can have 1 to 20 carbon atoms, i.e., a C_1-20alkyl group. In some embodiments, an alkyl group can have 1 to 6 carbon atoms, and can be referred to as a “lower alkyl group.” Examples of lower alkyl groups include methyl, ethyl, propyl (e.g., n-propyl and isopropyl), and butyl groups (e.g., n-butyl, isobutyl, sec-butyl, tert-butyl).

[0069] As used herein, “haloalkyl” refers to an alkyl group having one or more halogen substituents. Examples of haloalkyl groups include, but are not limited to, CF₃, C₂F₅, CHF₂, CH₂F, CCl₃, CHCl₂, CH₂Cl, C₂Cl₅, and the like. Perhaloalkyl groups, i.e., alkyl groups wherein all of the hydrogen atoms are replaced with halogen atoms (e.g., CF₃and C₂F₅), are included within the definition of “haloalkyl.” For example, a C_1-20haloalkyl group can have the formula —C_iX_2j— or —C_iH_2i-jX_j—, wherein X is F, Cl, Br, or I, i is an integer in the range of 1 to 20, and j is an integer in the range of 0 to 40, provided that i is less than or equal to 2j.

[0070] FIG. 1a shows a cross-sectional view of an NWT structure with an individually addressed bottom gate. As one embodiment of the present teachings, the structure of FIG. 1a includes a SiO₂buffer layer, a patterned IZO gate electrode, an atomic layer deposition (ALD)-derived high-κ Al₂O₃gate insulator, a single-crystal semiconducting In₂O₃or ZnO nanowire for the active channel, and ITO for the source/drain electrodes. In the embodiment shown, no further passivation layers are used so that the dielectric above the nanowire is air. In₂O₃nanowires and ZnO nanowires can be prepared according to procedures described in Li, C. et al., Adv. Mater., 15: 143-145 (2003) and Banerjee, D. et al., Nanotechnology, 15: 404-409 (2004), both of which are incorporated by reference herein in their entireties.

[0071] FIG. 1b shows a top view field-emission scanning electron microscopic (FE-SEM) image of an NWT device analogous to the one illustrated in FIG. 1a. As shown, the IZO gate overlaps with the ITO source/drain electrodes. By fully covering the nanowire channel, transistor performance can be improved. FE-SEM images of single In₂O₃and ZnO nanowires between source and drain electrodes are shown in FIGS. 1c and 1d, respectively. For the particular embodiments shown, the corresponding nanowire diameters (D) and lengths (L) of single In₂O₃or ZnO nanowires addressed between source and drain on the glass substrates are 20 nm/1.80 μm and 120 nm/1.66 μm, respectively.

[0072] FIG. 2a shows the gate and drain leakage currents of a representative In₂O₃NWT device for the bias configurations shown in the inset. The drain leakage current here is the summation of the body current leakage of the In₂O₃nanowire (˜40 pA at 2 V) and the leakage current through the gate dielectric (˜1 pA at 2 V). The Al₂O₃gate dielectric exhibits good insulating properties with an electrical breakdown field larger than about 8 MV/cm (see Lin, H. C., et al., Appl. Phys. Lett., 87: 182904-1-3 (2005)), and a dielectric constant of ˜9. The thin Al₂O₃gate dielectric allows the channel potential to be modulated at a relatively low gate voltage without significant gate leakage, resulting in a steep S and a high I_on/I_off.

[0073] FIG. 2b shows the linear-scale and log-scale drain current versus gate-source voltage (I_ds-V_gs) characteristics at V_d=0.5 V for a representative In₂O₃NWT device analogous to the one illustrated in FIG. 1a before (black dots) and after (red solid line) two minutes of ozone treatment. As shown, ozone treatments for two minutes resulted in significant device performance enhancements in terms of S, V_Tand I_on. Compared to as-fabricated devices, the S value was reduced from 600 mV/dec to 160 mV/dec along with improvement in the I_on/I_off(˜10⁶), and a shift in V_Tfrom −1.16 V to −0.27 V. Without wishing to be bound by any particular theory, the improvement in the S value can be due to the change in terms of a reduction in the interfacial trap states and in fixed surface charge states. See e.g., Ju, S. et al., Appl. Phys. Lett., 89: 193506-1-3 (2006). Ozone treatment not only can remove defects and contamination from the nanowire surface, but can also change the work function. See e.g., Lang, O. et al., J. Appl. Phys., 86: 5687-5691 (1999) and Gassenbauer, Y. et al., Phys. Review B, 73: 245312-1-11 (2006). Ozone is also expected to increase the density of oxygen vacancies near the nanowire surface. Because oxygen vacancies can act as donor states, ozone treatment can increase the conductivity of the nanowire. Although the ITO and IZO microstructures and chemical bonding states are somewhat more complex, the basic crystal structures are sufficiently similar to those of In₂O₃and ZnO to reasonably expect that the In₂O₃and ZnO nanowire work functions will increase similarly upon ozone treatment. Thus, the source/drain—nanowire contact should not significantly change on ozone treatment. However, and again without wishing to be bound by any particular theory, because the ozone treatment can plausibly reduce nanowire surface dangling bonds and carbon contamination and can form an oxygen vacancy-rich surface, transistor characteristics including I_on/I_off, S, and V_Tare expected to be enhanced. See Kim, S. Y. et al., J. Appl. Phys., 95: 2560-2563 (2004).

[0074] FIG. 2c shows the log-scale drain current versus gate-source voltage (I_ds-V_gs) characteristics of a representative In₂O₃NWT device analogous to the one illustrated in FIG. 1a during four successive sweeps from −2 V to +2 V, illustrating the stability of the In₂O₃NWTs of the present teachings. The I_ds-V_gscurves are comparable following bias sweeps, with consistent I_on/I_off, S, and V_Tvalues. Furthermore, for the same device, I_ds-V_gscurves were swept from negative gate voltage (V_g(−)) to positive gate voltage (V_g(+)) and back to V_g(−) as shown in FIG. 2d. Over this bias range, the hysteresis is modest, which illustrates the high quality of the Al₂O₃gate insulator and indicates negligible charge trapping and detrapping in the gate insulator.

[0075] FIGS. 3a and 3c show the drain current versus gate-source voltage (I_ds-V_gs) characteristics for representative single In₂O₃and ZnO NWTs. The In₂O₃device (same device as in FIGS. 2a and 2b) exhibited S=160 mV/dec, I_on/I_off=10⁶, and V_T=−0.27 V. The μ_effof the representative In₂O₃NWT, deduced from transconductance (g_m=dI_d/dV_g) varied from ˜514 to 300 cm²/V-sec as the gate bias was increased from 0 V to 2 V, following a trend that is observed in NWTs, TFTs and MOSFETs. The ZnO NWT device exhibited S=0.3 V/dec, I_on/I_off˜10⁶, V_T=−0.07 V, and μ_effvaried from ˜96 to 70 cm²/V-sec over the gate bias range of 0 V to 3 V. One important device performance metric for high-speed and low-power operation is the S=dV_gs/dlog I_ds(mV/dec). A small S value is required for switching transistors, ideally approaching the theoretical limit of about 60 mV/dec. The present S values were extracted from the linear portion of the log I_dsversus V_gsplot (FIGS. 3a and 3c). The very small S values in the In₂O₃and ZnO devices of the present teachings are comparable with those of previously reported non-transparent In₂O₃and ZnO NWT devices. See Liu, F. et al., Appl. Phys. Lett., 86: 213101-1-3 (2005) and Chang, P.-C. et al., Appl. Phys. Lett., 89: 133113 (2006).

[0076] FIGS. 3b and 3d show the drain current versus drain-source voltage (I_ds-V_ds) characteristics of representative fully transparent single In₂O₃and ZnO NWTs according to the present teachings. These devices exhibited typical enhancement mode long-channel FET behavior. For the fully transparent In₂O₃single NWT device, I_onis about 1×10⁻⁵μA at V_ds=1.0 V and V_gs=2.0 V. The I_onof a ZnO single NWT device was about 2 μA at V_ds=1.0 V and V_gs=2.0 V. The performance of these In₂O₃and ZnO NWT devices is comparable with that of previously reported non-transparent In₂O₃and ZnO NWT devices. See e.g., Liu, F. et al., Appl. Phys. Lett., 86: 213101-1-3 (2005); Chang, P.-C. et al., Appl. Phys. Lett., 89: 133113 (2006); Zhang, D. et al., Appl. Phy. Lett., 82: 112-114 (2003); Cha, S. N. et al., Appl. Phy. Lett., 89: 263102-1-3 (2006); Moon, T.-H. et al., Nanotechnology, 17: 2113-2121 (2006); Ju, S. et al., Nano. Lett., 5: 2281-2286 (2005). Because the extraction procedure for μ_effinvolves uncertainties due to the required capacitance estimation (see Example 4 infra), NWTs can be compared to planar transistors by comparing the I_onand g_mper unit width (g_m/W), using the nanowire diameter as the device width. The In₂O₃nanowire on glass exhibited an I_ondensity of about 600 mA/mm and a g_m/W of ˜212 mS/mm. Both values are more than 5 times higher than those obtained in prior studies on transparent transistors using In₂O₃thin films, even after adjusting for the differences in gate lengths and gate capacitance. Without wishing to be bound by any particular theory, the single-crystal nature of the nanowires, along with the formation of relatively high quality interfaces, are believed to play key roles.

[0077] FIG. 4 shows the optical transmission spectra through the In₂O₃and ZnO NWT structures, with the substrate absorption removed. As shown in FIG. 4, an average transmittance of greater than about 90% were observed in the visible and near-infrared spectrum for both transistor types. With the substrate included, optical transmissions of about 82% (In₂O₃NWT+glass substrate) and about 83% (ZnO NWT+glass substrate) in the 350 nm-1350 nm wavelength range were observed. The NWT array regions measured 1.0″×0.5″ (the glass substrate measured 1.5″×1.0″), and contained 23,000 NWT device patterns. In the embodiments studied, the substrates were entirely covered by the SiO₂buffer layer and the Al₂O₃gate insulator. The source/drain regions and the gate regions covered about 45% and about 25% of the total NWT array region, respectively. Due to their small diameter, the optical absorption of the In₂O₃and ZnO nanowires should thus be negligible, and the area covered by the nanowires was relatively small compared to the entire NWT array. The observation of a greater than about 90% optical transmission indicates that the transmission losses due to the various layers, including the nanowires, were negligible, and that visible light could readily penetrate the dense NWTs. The inset in FIG. 4 shows a transparent In₂O₃NWT device structure, with text on an underlying opaque layer clearly visible.

[0078] In some embodiments, NWT devices according to the present teachings can include a flexible plastic substrate. For example, fully transparent and flexible In₂O₃NWT devices using a polyethylene terephthalate (PET) plastic substrate (e.g., Melinex, DuPont) were fabricated and characterized. A cross-sectional view of a representative fully transparent and flexible In₂O₃NWT device structure with an individually addressed bottom gate is shown in FIG. 5a. Specific embodiments of such devices can include a single In₂O₃nanowire addressed between the source and drain contacts having D and L of 20 nm and 1.79 μm, respectively. The gate and source/drain electrodes can be made from ITO. To suppress the leakage current due to tensile/compressive stress of the plastic substrate during photolithographic processing (up to 130° C.) and gate insulator deposition (up to 200° C.), a relatively thick Al₂O₃gate insulator (50 nm) can be used. FIG. 5b is a photographic image of a plastic substrate (PET) containing arrays of In₂O₃NWTs according to these embodiments, showing their optical clarity and mechanical flexibility.

[0079] FIG. 5c shows the optical transmission spectrum of one of the transistor array regions containing In₂O₃NWTs on the plastic substrate (ITO(S/D)/In₂O₃NWs/Al₂O₃/ITO(G)/plastic substrate) shown in FIG. 5b. The optical transmission through the NWT structure and substrate was measured to be about 81% in the 350 nm-1350 nm wavelength range. FIG. 5d shows the I_ds-V_gscharacteristic of a representative single In₂O₃NWT on the plastic substrate. The S value was determined to be about 0.9 V/dec, I_on/I_offwas in the order of 10⁵, V_T=−0.6 V, and μ_effvaried from ˜167 to 120 cm²/V-sec over the gate bias range of 1 V to 3.5 V. The lower but respectable response characteristics on the plastic substrate could reflect the effects of high temperature deposition (300° C.) and post rapid thermal annealing (RTP, 500° C. for 30 s in N₂).

[0080] As an alternative to using inorganic oxides as the gate dielectric, NWTs of the present teachings can include a gate dielectric made from an organic multi-layered composition. This multi-layered composition can include periodically alternating layers of one or more layers that include a polarizable moiety, and one or more layers that include a silyl or siloxane moiety. In particular embodiments, these layers can be individually self-assembled monolayers. Synthesis of such self-assembled nanodielectric (SAND) materials are more fully described in Yoon, M-H. et al., PNAS, 102 (13): 4678-4682 (2005), which is incorporated by reference herein in its entirety.

[0081] In a preliminary study, nanowire transistors using individual In₂O₃nanowires as the channel material and a ˜15 nm thick SAND as the dielectric (capacitance ˜180 nF/cm²and leakage current density ˜1×10⁻⁶A/cm²up to 2.0 V) were investigated. The NWTs studied used an individually addressable indium zinc oxide (IZO) bottom-gate and Al source/drain electrodes (FIG. 6), which rendered the channel region completely transparent. The diameter and length of the In₂O₃nanowires were 20 nm and 1.6 μm, respectively. The device characteristics (FIG. 7) following ozone treatment to improve and optimize the device performance exhibited n-type transistor characteristics with a subthreshold slope (S) of 0.2 V/dec, a current on-off ratio (I_on/I_off) of 10⁶, a threshold voltage (V_T) of 0.0 V, and transconductance (g_m) and channel conductance (g_d) as illustrated in FIG. 8. The g_mat V_d=0.5 V peaked at ˜5.87 μS, and the g_dwas proportional with the gate voltage. The drain current versus drain-source voltage (I_ds-V_ds) characteristics of a representative SAND-based In₂O₃NWT are shown in FIG. 7b. The device exhibited high I_on˜12 μA for the single In₂O₃nanowire at V_ds=1 V, V_gs=1.5 V, respectively. This current level would be sufficient to drive a 71×213 μm pixel at 300 cd/m²in current-generation electroluminescent technologies. The field-effect mobility (μ_eff) which was extracted from the g_mand g_dof the NWTs, along with an estimated gate-to-channel capacitance, is also plotted versus gate bias in FIG. 7a. The value of μ_effvaried from ˜1447 cm²/V-sec to ˜300 cm²/V-sec over the reported gate bias range. The peak value was much higher than recently reported results for In₂O₃nanowires (electron mobility of 279 cm²/V-sec and 98.1 cm²/V-sec, effective mobility 6.93 cm²/V-sec) and ideal single-crystal In₂O₃bulk mobility (˜160 cm²/V-sec). Without wishing to be bound by any particular theory, it is believed that the single crystal nature of the nanowires, along with the quasi-one-dimensional nature of nanowires which inhibits low-angle scattering, could contribute to the relatively high μ_eff. As shown, the SAND dielectric also appeared suitable for realizing relatively high performance in oxide nanowires. The device performance of SAND-based NWTs according to the present teachings is better than other In₂O₃nanowire transistors and comparable with poly-Si TFTs and α-Si TFTs, in terms of S and μ_eff. Because it is desirable to obtain high μ_effand a steep S to fabricate fast switching transistors and high-speed logic electronic devices, these results indicate that SAND-based In₂O₃NWTs can support the requirements of these devices.

[0082] Possible applications of the present transparent NWTs include pixel drivers for active matrix displays such as active matrix liquid crystal displays (AMLCDs), active matrix light-emitting diodes (AMLEDs), and active matrix organic light-emitting diodes (AMOLEDs). For example, for AMOLEDs, increasing the aperture ratio is necessary to increase efficiency and reduce power consumption. For non-transparent transistors, maximizing the aperture ratio corresponds to minimizing the transistor and capacitor physical sizes. Transparent transistors would allow stacking of the drive transistors with the OLEDs, which would allow a larger transistor size (width/length) and capacitor size (single or dual capacitors). Device geometries could then be optimized to improve metrics such as peak luminescence, Commission Internationale de L'Eclairage Coordinates (CIE), and power consumption. Importantly, the present NWTs can exhibit relatively high performance in comparison to typical TFTs for display applications, which should allow higher operating speeds and/or smaller device areas. For instance, in order to produce white peak luminance of ˜300 cd/m²(71×213 μm pixel size, 40% aperture ratio, 40% polarizer transmission, 5.1 cd/A of red, 13 cd/A of green, 5.7 cd/A of blue, and (0.31, 0.32) of white CIE) using phosphorescent materials, driving transistors on RGB pixels must provide ˜2.44 μA (red), ˜1.01 μA (green), ˜1.46 μA (blue) and ˜3.9 μA (white), respectively. The present transparent NWTs were found to be suitable for switching and driving transistors on such pixels. It is also expected that the required current for AMOLED operation will decrease with the increasing aperture ratio provided by all-transparent components. The realization of flexible and transparent NWTs such as those according to the present teachings therefore could also enable high resolution and low-power consumption products such as heads-up displays.

[0083] Accordingly, the present teachings also provide fully transparent transistor display circuit elements (e.g., usable to drive a AM display), in which the switching and driving circuits are comprised of transistors using In₂O₃nanowires as active channel materials. In some embodiments, these transistors can include a multilayer self-assembled gate dielectric (SAND) as a gate insulator and indium tin oxide (ITO) as transparent conductive gate and S-D electrodes. For these devices, a coplanar transistor structure consisting of ITO S-D electrodes/In₂O₃NW/SAND/bottom ITO gate electrodes can be used. A robust gate insulator typically is required to maintain high breakdown voltage and low density of defect states. Use of the SAND dielectric (thickness ˜24 nm) can ensure high μ_eff, a steep S, low operating voltage and a high on-off current ratio (I_on/I_off).

[0084] FIG. 9 shows FE-SEM images of several 54×176 μm pixels within a 2×2 mm array (30×10 pixels). The equivalent circuit usable for a single active pixel, shown in FIG. 9c, can include one switching transistor (T1), two driving transistors (T2 and T3) and one storage capacitor (C_st). Using optimized layout design, the transparent driving and switching NWTs regions can allow significant reductions in the area of the transistor circuitry. FIG. 9d shows an FE-SEM image of representative In₂O₃nanowires which are connected between S-D electrodes. In the embodiments shown, the ITO gate overlaps with the ITO S-D electrodes to ensure gating of the full length of the nanowire channel, thereby improving transistor performance. Twenty device regions were observed by FE-SEM, and the number of In₂O₃nanowires connected between source and drain electrodes on the switching and driving transistors of each pixel were between 4 and 8, with an average value of 6. The diameters of the In₂O₃nanowires were between 40 and 50 nm, and the channel lengths distance between S-D electrodes, along axis of each nanowire were between 1.2 and 1.6 μm, respectively.

[0085] FIG. 10 shows the measured current-voltage (I-V) characteristics of representative NWTs. The design of these patterns, including width and length, are exactly same as those of the NWT circuits in the pixel array, except for the addition of extended contact pads for electrical probing. To improve transistor performance, several surface treatments were performed: i) following deposition of nanowires, plasma ashing was performed for 90 seconds in Ar and O₂ambient on only the S-D contact region of nanowires (active regions of nanowires were covered by photoresist); and ii) after ITO metal deposition, active regions of NWTs were subjected to an ozone treatment for 1 minute to remove defects and contamination on the nanowire surface, and change the relative work functions of In₂O₃and ITO S-D metals. The electron affinity of In₂O₃, χ_In2O3, was 3.7 eV and a surface Fermi level position of E_F−E_V=3.0 eV, yielding an effective work functions Φ_In2O3=4.54 eV for n-type material. Based on the work function of ITO (Φ_ITO=4.9 eV), it is expected that ITO S-D contacts form relatively low barrier height interfaces to n-type In₂O₃. After these process treatments, the device performance of transistor characteristics in terms of I_on/I_off, S, and V_Twas improved significantly.

[0086] FIG. 10a shows a family of drain current versus gate-source voltage (I_ds-V_gs) characteristics for a representative NWT. The tested In₂O₃NWTs exhibited an I_onof ˜1 μA (at V_gs=3.0 V, V_ds=0.1 V), an I_on/I_offof 10⁻⁵, a V_Tof 0.1 V, an S value of 0.25 V/dec, and a μ_effof ˜258 cm²V⁻¹s⁻¹, respectively. The mobility of SAND-based In₂O₃NWTs devices according to the present teachings, therefore, was observed to be compatible or higher than the recently reported results for In₂O₃nanowires (electron mobility of 279.05 cm²V⁻¹s⁻¹and 98.1 cm²V⁻¹s⁻¹, effective mobility 6.93 cm²V⁻¹s⁻¹) and ideal single-crystal In₂O₃bulk mobility (˜160 cm²V⁻¹s⁻¹).

[0087] Without wishing to be bound by any particular theory, the single crystal nature of the In₂O₃nanowire is expected to allow high mobilities by decreasing scattering at the intergrain regions. In addition, the SAND dielectric has previously been found to be suitable for realizing relatively high performance in other oxide nanowires. The inset in FIG. 10a shows the hysteresis of the devices for bias sweeps from negative gate voltage (V_g(−)) to positive gate voltage (V_g(+)) and from V_g(+) to V_g(−). The hysteresis was modest over the bias range, which illustrates the high quality of the SAND gate dielectric and In₂O₃NW materials, and indicates negligible charge trapping and detrapping in/on the SAND and at the nanowire/SAND interface.

[0088] FIG. 10d shows the I_on, I_off, V_Tand S characteristics of ten representative transistors, with the red lines indicated the average values. The average values of I_on, I_off, V_Tand S were 2.73 μA, 143 pA, 0.02 V and 0.35 V/dec, respectively (these values were extracted from I_ds-V_gscurves at 0.1 V_ds). The drain current versus drain-source voltage (I_ds-V_ds) characteristics of representative In₂O₃NWTs are shown in FIG. 10b. As can be seen from FIG. 10b, these representative In₂O₃NWTs exhibited typical n-type transistor characteristics. The desirable features of these In₂O₃transistors are illustrated by their high I_on˜6 μA at V_ds=2.0 V, and V_gs=2.0 V, respectively. In order to operate the transistor circuit, 2.0 V was applied to fully turn on the gate of switching transistor (T1).

[0089] FIG. 10c shows the measured output current of the circuit (I_dsof T2 and T3 in parallel) versus the output voltage (V_dd). The various curves correspond to various values of data line voltage (0 V to 4 V in 0.5 V steps). The steps in data line voltage correspond to changes in Vgs for the drive transistors (T2 and T3). The transistor circuit shows ˜5 μA at V_dd=2.0 V and V_g2=3.0 V. The total capacitance on a unit pixel was calculated to be about 0.25 pF/cm². Of the 70 transistor circuits that were measured, more than 65 circuits were working uniformly, while 5 circuits showed low on-current levels compared with other transistor circuits. The NWTs circuits showed more than 90% yield.

[0090] The higher μ_effand steeper S of SAND-based In₂O₃NWTs can allow smaller transistor area and can support the requirements of fast switching transistors and high-speed transistors for NW-AMOLED. Faster switching could enable approaches such as direct digital drive of pixels, which would reduce the complexity of interface circuitry.

[0091] The OLED parameters and target display specifications such as the peak RGB luminescence and efficiency, Commission Internationale de L'Eclairage Coordinates (CIE), and power consumptions dictate specific performance levels which must be considered in the design/simulation/extraction of the transistor current levels and minimum storage capacitor size. In order to extract the required current levels sufficient to operate an NW-AMOLED, the target values are as follows: i) target peak luminescence of 300 cd/m²l; ii) target color coordinates of red (0.65, 0.34), green (0.27, 0.63), blue (0.14, 0.16), and white (0.31, 0.32); and iii) EL efficiency of 6 cd/A (red at 300 cd/m2), 23 cd/A (green at 600 cd/m2), and 6 cd/A (blue at 200 cd/m2). Note that a unit pixel size is 54×176 μm, the EL opening area on a unit pixel is 20×106 μm, an aperture ratio is 46%, and polarizer transmission is 40%. As a result, the driving transistors on RGB pixels should provide at least ˜2.44 μA on a unit red pixel, ˜1.01 μA on a unit green pixel, and ˜1.46 μA on a unit blue pixel, respectively. This shows that the current level of SAND-based In₂O₃NWTs (˜5 uA on V_dd=2.0 V and V_g2=3.0 V) should be sufficient to drive a 54×176 μm pixel at 300 cd/m²in current-generation EL device technologies. While poly-Si TFT AMOLED devices can also provide the required drive currents, they require relatively large areas and have relatively low operating voltages. The resolution of the present NWT-integrated arrays is similar to that of a Quarter eXtended Graphics Array (QXGA: resolution of 2048×1536) of a 12-inch display. FIG. 11 shows the optical transmission spectra through the 2×2 mm nanowire-based region usable for AM-OLED. The optical transmission was measured to be about 72% in the 350 nm-1350 nm wavelength range. The inset shows a photographic image of the 1×1 inch glass substrate which consists of three 2×2 mm transistor arrays, 340 unit pixels, 80 test NWT devices, 6 alignment marks, 20 test patterns, and contact pads.

[0092] The following examples are provided to illustrate further and to facilitate the understanding of the present teachings and are not in any way intended to limit the invention.

EXAMPLE 1

Fabrication of In2O3 and ZnO NWT Devices with Al2O3 as the Gate Insulator

[0093] A 500 nm thick layer of SiO₂was deposited by plasma-enhanced chemical vapor deposition (PECVD) on Corning 1737 glass substrates and served as a buffer and planarization layer. Individual gate electrodes were formed by sputtering IZO (R_sheet=40Ω/□) and by ion-assisted deposition (IAD) at room temperature (R_sheet=60Ω/□) and subsequent patterning by photolithography and etching. An 18 nm thick layer of Al₂O₃was then deposited using atomic layer deposition (ALD) at 300° C. in an ASM Microchemistry F-120 ALCVD™ system using trimethyl aluminum (Al(CH₃)₃) (TMA) and water as precursors. Following Al₂O₃deposition, the substrates were annealed at 500° C. for 30 seconds under N₂to improve the film quality. Next, a suspension of In₂O₃or ZnO nanowires in VLSI grade 2-propanol solution was disbursed on the gate-patterned substrates. Single-crystal semiconducting In₂O₃nanowires were synthesized by a pulsed laser ablation process (see Li, C. et al., Adv. Mater., 15: 143-145 (2003)), with average diameter and length of 20 nm and 5 μm, respectively. Powdered ZnO nanowires synthesized by thermal evaporation and condensation were purchased from Nanolab Inc. The average diameter and length were 120 nm and 5 μm, respectively, and microstructural characterization indicated that they were highly crystalline (see Banerjee, D. et al. Nanotechnology, 15: 404-409 (2004)). Finally, ITO source/drain electrodes were deposited by IAD at room temperature and patterned by photolithography. Following source/drain electrode patterning, the NWTs, while shielded from UV light, were subjected to an ozone treatment (UV-Ozone cleaner, UVO 42-220, Jelight Co. Ltd.) for 2 minutes to achieve optimum transistor performance in terms of I_on, I_on:I_off, S, and μ_eff. The ozone environment was obtained by setting the oxygen content to 50 ppm, the UV wavelength to 184.9 nm and UV lamp power to 28 milliwatts per cm²at 254 nm. Fully transparent and flexible In₂O₃NWT devices using PET (Melinex, DuPont) also were fabricated with a PET/ITO(G)/Al₂O₃/In₂O₃nanowire/ITO(S/D) structure (FIG. 5a). The 50 nm thick layer of Al₂O₃layer was deposited at 200° C. ITO for the gate and source/drain electrodes was deposited by IAD. The lengths of the nanowires of given transistors between source and drain were obtained from the FE-SEM images, and accounted for the angle between the nanowire and the electrode edges.

EXAMPLE 2

Fabrication of In2O3 NWT Devices with SAND as the Gate Insulator

[0094] The 200 nm thick layer of SiO₂was deposited on Corning 1737A glass substrates as a buffer layer for planarization. The 100 nm thick ITO thin film was deposited by IAD at room temperature (R_sheet=60 ohms per square), and subsequently patterned by photolithography for individually addressed bottom gate electrodes. A 24 nm thick layer of SAND was then deposited on the patterned ITO gate metals using a self-assembly method. Following SAND deposition, contact holes were patterned for anode opening for electroluminescence and bottom gate electrode contacts on the pixel. Next, a suspension of In₂O₃nanowires in VLSI grade 2-propanol solution was disbursed on the device substrates. Single-crystal semiconducting In₂O₃nanowires were synthesized by a pulsed laser ablation process, with average diameter and length of 50 nm and 5 μm, respectively. Al source/drain contacts were fabricated by spattering. In the case of ITO S-D electrodes, they were deposited by IAD at room temperature and patterned by lift-off method. Nanowires on the unnecessary regions were removed by ultrasonication except nanowires which were addressed between S-D electrodes. Following S-D electrode patterning, the NWTs, while shielded from UV light, were subjected to an ozone treatment using UV-Ozone cleaner for 1 minute to achieve optimum transistor performance in terms of I_on, I_on:I_off, S, and μ_eff. After ozone treatment, the devices were passivated by depositing a 200 nm of e-beam evaporated SiO₂as a passivation layer to planarize NWTs array for EL deposition.

EXAMPLE 3

Fabrication of SnO2 NWT Devices with SAND as the Gate Insulator

[0095] A 200 nm thick SiO₂layer was deposited on Si or Corning 1737A glass substrates as a buffer layer for planarization. A 100 nm thick ITO thin film was deposited by ion-assisted deposition (IAD) at room temperature (R_sheet=60 ohms per square), and subsequently patterned by photolithography for individually addressed bottom gate electrodes. A 15 nm thick layer of SAND was then deposited on the patterned ITO gate metals using a self-assembly method. Next, a suspension of SnO₂nanowires in VLSI grade 2-propanol solution was disbursed on the device substrates. Al source/drain contacts were fabricated by spattering. ITO S-D electrodes were deposited by IAD at room temperature and patterned by a lift-off method. Nanowires on the unnecessary regions were removed by ultrasonication except nanowires which were addressed between S-D electrodes.

[0096] FIG. 12 shows the structure and electrical characteristic of a representative single SnO₂NWT using SAND as the gate dielectric. Different substrates (Si—SiO₂, Glass-SiO₂) and source/drain contact (Al, ITO) materials were used. For these devices, typical performance before ozone treatment were: S=0.1-0.4 V/dec, I_on/I_off˜10⁵-10⁶, V_T=±0.2 V, and μ_effvaried from ˜15 to 30 cm²/V-sec over the gate bias range of 1 V to 4 V. Improved device performance is expected with ozone treatment and encapsulation.

EXAMPLE 4

Fabrication of Ge NWT Devices with SAND as the Gate Insulator

[0097] A 200 nm thick SiO₂was deposited on Si or Corning 1737A glass substrates as a buffer layer for planarization. A 100 nm thick ITO thin film was deposited by ion-assisted deposition (IAD) at room temperature (R_sheet=60 ohms per square), and subsequently patterned by photolithography for individually addressed bottom gate electrodes. A 15 nm thick layer of SAND was then deposited on the patterned ITO gate metals using a self-assembly method. Next, a suspension of p- or n-type Ge nanowires in VLSI grade 2-propanol solution was disbursed on the device substrates. Al source/drain contacts were fabricated by spattering. ITO S-D electrodes were deposited by IAD at room temperature and patterned by a lift-off method. Nanowires on the unnecessary regions were removed by ultrasonication except nanowires which were addressed between S-D electrodes.

[0098] FIG. 13 shows the structure and electrical characteristic of representative single p-type and n-type Ge NWTs using SAND as the gate dielectric. Different substrates (Si—SiO₂, Glass-SiO₂) and source/drain contact (Al, ITO) materials were used. For the p-type Ge NWTs, typical performance before ozone treatment were: S˜1 V/dec, I_on/I_off˜10⁶, V_T=0−(−1) V, and μ_eff˜30 to 50 cm²/V-sec over the gate bias range of −1 V to −5 V. For the n-type Ge NWTs, typical performance before ozone treatment were: S˜1 V/dec, I_on/I_off˜10⁴-10⁵, V_T=0-1 V, and μ_eff˜8 to 12 cm²/V-sec over the gate bias range of −1 V to +5 V. Improved device performance is expected with ozone treatment and encapsulation.

[0099] FIG. 14 shows photographic images of NW-AMOLED substrates (top row) and NWT channel regions (bottom row) according to the present teachings, specifically, in which the semiconducting nanowires are as follows: a) In₂O₃, b) SnO₂, and c) p-type Ge. The respective device structures consist of a glass-SiO₂substrate, an ITO gate electrode, a SAND gate dielectric, ITO source/drain electrodes, and a single nanowire channel region of In₂O₃(FIG. 14a), SnO₂(FIG. 14b), or Ge (FIG. 14c). As shown in FIG. 14, the Ge-based devices have similar optical transparency compared to similar devices based on metal oxide nanowires.

EXAMPLE 5

Characterization Methodology

[0100] The work function of an as-grown ITO thin film was measured using an AC-2, RKI Instruments photoelectron spectrometer. The UV-Vis spectra were recorded with a Varian Cary 1E spectrophotometer. Electrical I-V measurements were performed using a Keithley 4200 semiconductor characterization system. The NWs within a device were imaged with a Hitachi S-4800 FE-SEM following electrical characterization.

EXAMPLE 6

Calculation of Mobility and Threshold Voltage

[0101] In contrast to planar transistors in which carrier concentration and mobility can be determined independently, e.g., through the Hall effect and conductivity measurements, the lack of extended lateral geometries in NWTs dictates an alternative approach for determining mobility. Following the typical approach from prior NWT studies, field effect mobilities (μ_eff) were calculated using a combination of the cylinder-on-plate (COP) capacitance model

[0102]

C_{i} = \frac{2 π ɛ_{0} k_{eff} L}{\cosh^{- 1} (1 + t_{ox} / r)}

and the relationship

[0103]

μ = \frac{ⅆ I_{ds}}{ⅆ V_{gs}} \times \frac{L^{2}}{C_{i}} \times \frac{1}{V_{ds}}

obtained from the MOSFET linear region model (see Wang, D. et al., Appl. Phys. Lett., 83: 2432-2434 (2003)), where k_eff˜9.0 is the effective dielectric constant of Al₂O₃, L is the channel length of the NWTs (˜1.80 μm for In₂O₃NW, ˜1.66 μm for ZnO NW), where μ_eff˜9.0 is the effective dielectric constant of Al₂O₃, L is the channel length of the NWTs (˜1.80 μm for In₂O₃NW, ˜1.66 μm for ZnO NW), r is the radius of the NWTs (10 nm for In₂O₃NR, 60 nm for ZnO NW), t_ox˜18 nm is the thickness of gate insulator, dl_ds/dV_gsis the transconductance, and V_dsis drain voltage. In the case of flexible and transparent In₂O₃NWTs, L˜1.79 μm and r˜10 nm were used. The geometry of certain devices disclosed herein consisted of the gate dielectric (k_eff˜9) below and air (k_eff˜1) above the nanowire. A prior comparision (see Vashaee, D. et al., J. Appl. Phy., 99: 54310-1-5 (2006)) between electrostatic simulations and an analytic formula for capacitance (a form of the COP equation valid for t_ox>>r.) for a comparable geometry with SiO₂/air showed good agreement between the two capacitances over a range of t_ox/r from 8 to 40, provided that a value of k_eff=0.5ε_R1SiO2was used. Because the geometry of the tested devices used a higher k dielectric constant and smaller t_ox/r (˜1.8), the fringing fields were more tightly confined to the gate dielectric layer. Accordingly, a value of k_eff˜ε_R1Al2O3was chosen, which would tend to overestimate the capacitance (as the appropriate correction factor is greater than 0.5 but less than 1.0), and therefore underestimate the mobility. The transconductances shown in FIGS. 3a, 3b and 4d have been smoothed by polynomial fit to 3 orders with 20 points fit to the curve. In order to extract V_T, the extrapolated

[0104]

V_{T} (V_{T} = V_{G} (g_{m_max}) - \frac{I_{D} (g_{m_max})}{g_{m_max}}

where

[0105]

g_{m} = \frac{\partial I_{D}}{\partial V_{G}}

(at V_d=0.5V)) was used as it gives an accurate V_T. The gate voltage at the maximum g_m(V_g(g_m_—_max)), the drain current at the maximum g_m, I_d(g_m_—_max), and the maximum g_m(g_m_—_max) were obtained from FIGS. 3a, 3c and 5d. These values were confirmed with V_Tvalues obtained from the I_ds-V_dscurve at V_d=0.1 V.\

[0106] The present teachings encompass embodiments in other specific forms without departing from the spirit or essential characteristics thereof. The foregoing embodiments are therefore to be considered in all respects illustrative rather than limiting on the present teachings described herein. Scope of the present invention is thus indicated by the appended claims rather than by the foregoing description, and all changes that come within the meaning and range of equivalency of the claims are intended to be embraced therein.

Claims

Certificate of Correction present

The claims shown below may not include correction changes. Use the corrected PDF for authoritative text.

What is claimed is:

1. A nanowire transistor device comprising:

one or more semiconducting nanowires extending between a source electrode and a drain electrode, and

a gate dielectric in contact with the one or more nanowires,

wherein each of the gate dielectric, the source electrode and the drain electrode is transparent, and

wherein the gate dielectric comprises a multi-layer composition, the multi-layer composition comprising periodically alternating layers, wherein the alternating layers comprise one or more layers comprising a polarizable moiety, and one or more layers comprising a silyl or siloxane moiety.

2. A nanowire transistor device comprising:

one or more semiconducting nanowires extending between a source electrode and a drain electrode, and

a gate dielectric in contact with the one or more nanowires,

wherein each of the gate dielectric, the source electrode and the drain electrode is transparent, and

wherein each of the source electrode and the drain electrode independently comprises indium tin oxide, indium zinc oxide, indium oxide, zinc oxide, zinc indium tin oxide, fluorinated tin oxide, gallium zinc oxide, gallium indium oxide, or gallium indium tin oxide.

3. A nanowire transistor device comprising:

one or more semiconducting nanowires extending between a source electrode and a drain electrode, and

a gate dielectric in contact with the one or more nanowires,

wherein each of the gate dielectric, the source electrode and the drain electrode is transparent, and

wherein the transparent gate electrode is defined under the gate dielectric and comprises indium tin oxide, indium zinc oxide, indium oxide, zinc oxide, zinc indium tin oxide, fluorinated tin oxide, gallium zinc oxide, gallium indium oxide, or gallium indium tin oxide.

4. The device of claim 2, wherein the one or more semiconducting nanowires comprise one or more elements selected from Group 12, Group 13, Group 14, Group 15 and Group 16.

5. The device of claim 4, wherein the one or more semiconducting nanowires are selected from p-type Ge nanowires and n-type Ge nanowires.

6. The device of claim 2, wherein the one or more semiconducting nanowires comprise a transparent metal oxide.

7. The device of claim 6, wherein the one or more metal oxide nanowires are selected from ZnO nanowires, In₂O₃nanowires, and SnO₂nanowires.

8. The device of claim 2, wherein the nanowire transistor comprises a single semiconducting nanowire.

9. The device of claim 2, wherein the nanowire transistor comprises a plurality of semiconducting nanowires.

10. The device of claim 2, wherein the gate dielectric comprises one or more transparent metal oxides.

11. The device of claim 1, wherein the polarizable moiety comprises a stilbazonium group.

12. The device of claim 1, wherein at least some of the alternating layers are coupled to an adjacent layer by a coupling layer comprising a siloxane matrix.

13. The device of claim 12, wherein at least some of the alternating layers are coupled to one another or the siloxane matrix via a condensation reaction.

14. The device of claim 1, wherein at least some of the alternating layers comprise a condensation product of a silane-substituted stilbazolium compound and a trisiloxane compound.

15. The device of claim 1, wherein the alternating layers comprise one or more layers comprising a sigma moiety.

16. The device of claim 15, wherein at least some of the alternating layers comprise a condensation product of a bis(silyl)-C₄- about C₁₀alkyl compound and a trisiloxane compound.

17. The device of claim 2, wherein the gate dielectric comprises a crosslinked polymeric material.

18. The device of claim 2 comprising a transparent gate electrode defined under the gate dielectric.

19. The device of claim 2, wherein the gate dielectric is deposited on a transparent substrate.

20. The device of claim 19, wherein the transparent substrate is glass or plastic.

21. An array comprising a device of claim 2.

22. An electronic circuit comprising the array of claim 21.

23. The device of claim 1, wherein the one or more semiconducting nanowires are selected from p-type Ge nanowires and n-type Ge nanowires.

24. The device of claim 1, wherein the one or more semiconducting nanowires are selected from ZnO nanowires, In₂O₃nanowires, and SnO₂nanowires.

25. The device of claim 2, wherein the gate dielectric comprises a multi-layer composition, the multi-layer composition comprising periodically alternating layers, wherein the alternating layers comprise one or more layers comprising a polarizable moiety, and one or more layers comprising a silyl or siloxane moiety.

26. The device of claim 18, wherein the transparent gate electrode comprises indium tin oxide, indium zinc oxide, indium oxide, zinc oxide, zinc indium tin oxide, fluorinated tin oxide, gallium zinc oxide, gallium indium oxide, or gallium indium tin oxide.

27. The device of claim 3, wherein the one or more semiconducting nanowires are selected from p-type Ge nanowires, n-type Ge nanowires, ZnO nanowires, In₂O₃nanowires, and SnO₂nanowires.

Patent Citations (13)

Patent	Date	Inventor	Cited By
US5156918(A)	1992-10-01	Marks et al.	Applicant
US6459685(B1)	2002-10-01	Mahe	Applicant
US6855274(B1)	2005-02-01	Marks et al.	Applicant
US6863943(B2)	2005-03-01	Wang et al.	Applicant
US7151281(B2)	2006-12-01	Shei et al.	Examiner
US7233041(B2)	2007-06-01	Duan et al.	Examiner
US7405129(B2)	2008-07-01	Afzali-Ardakani et al.	Examiner
US2002/0090738(A1)	2002-07-01	Cozzette et al.	Applicant
US2004/0031975(A1)	2004-02-01	Kern et al.	Applicant
US2004/0105810(A1)	2004-06-01	Ren et al.	Applicant
US2006/0003485(A1)	2006-01-01	Hoffman et al.	Applicant
US2006/0169788(A1)	2006-08-01	Empedocles et al.	Applicant
WO2008089401	2008-07-01		Applicant

Non-Patent Literature (25)

Ju et al. “Fabrication of fully transparent nanowire transistors for transparent and flexible electronics,” Nature Nanotechnology, vol. 2, pp. 378-384, Jun. 2007, entire document.Applicant
Xu et al. “Fabrication and photoluminescence of Zinc silicate/silica modulated ZnO nanowires,” Nanotechnology, vol. 16, No. 12, pp. 2808-2812, Dec. 2005, entire document.Applicant
Li, C., Zhang, D., Han, S., Liu, X., Tang, T., Zhou, C. “Diameter-Controlled Growth of Single-Crystalline In2O3 Nanowires and Their Electronic Properties.” Adv. Mater. 2003, 15, No. 2, Jan. 16, pp. 143-146.Applicant
Hoffman, R.L., Norris, B.J., Wager, J.F. “ZnO-Based Transparent Thin-Film Transistors.” Applied Physics Letters, vol. 82, No. 5, Feb. 3, 2003, pp. 733-735.Applicant
Zhang, D., Li, C., Han, S., Liu, X., Tang, T., Jin, W., Zhou, C. “Electronic Transport Studies of Single-Crystalline In203 Nanowires.” Applied Physics Letters, V. 82, No. 1, Jan. 6, 2003, pp. 112-114.Applicant
Carcia, P.F., McLean, R.S., Reilly, M.H., Nunes Jr., G. “Transparent ZnO Thin-Film Transistor Fabricated by rf Magnetron Sputtering.” Applied Physics Letters, V. 82, No. 7, Feb. 17, 2003, pp. 1117-1119.Applicant
Wang, D., Wang, Q., Javey, A., Tu, R., Dai, H., Kim, H., McIntyre, P.C., Krishnamohan, T., Saraswat, K.C. “Germanium Nanowire Field-Effect Transistors with SiO2 and High-κ HfO2 Gate Dielectrics.” Applied Physics Letters, V. 83, No. 12, Sep. 22, 2003, pp. 2432-2434.Applicant
Liu, F., Bao, M., Wang, K.L., Li, C., Lei, B., Zhou, C. “One-Dimensional Transport of In2O3 Nanowires.” Applied Physics Letters 86, 213101 (2005), pp. 213101-1 21310-3.Applicant
Hur, S.-H., Park, O.O., Rogers, J.A. “Extreme Bendability of Single-Walled Carbon Nanotube Networks Transferred from High-Temperature Growth Substrates to Plastic and Their Use in Thin-Film Transistors.” Applied Physics Letters 86, 243502 (2005).Applicant
Takenobu, T., Takahashi, T., Kanbara, T., Tsukagoshi, K., Aoyagi, Y., Iwasa, Y. “High-Performance Transparent Flexible Transistors Using Carbon Nanotube Films.” Applied Physics Letters 88, 033511 (2006).Applicant
Chang, P.-C., Fan, Z., Chien, C.-J., Stichtenoth, D., Ronning, C., Lu, J. G. “High-Performance ZnO Nanowire Field Effect Transistors.” Applied Physics Letters 89, 133113 (2006).Applicant
Ju, S., Janes, D.B., Lu, G., Facchetti,A., Marks, T.J. “Effects of Bias Stress on ZnO Nanowire Field-Effect Transistors Fabricated with Organic Gate Nanodielectrics.” Applied Physics Letters 89, 263102 (2006).Applicant
Cha, S.N., Jang, J.E., Choi, Y., Amaratunga, A.J., Ho, G.W., Welland, M.E., Hasko, D.G., Kang, D.-J., Kim, J.M. “High Performance ZnO Nanowire Field Effect Transistor Using Self-Assigned Nanogap Gate Electrodes.” Applied Physics Letters 89, 263102 (2006).Applicant
Lang, O, Pettenkofer, C., Sanchez-Royo, J.F., Segura, A., Klein, A., Jaegermann, W. “Thin Film Growth and Band Lineup of In2O3 on the Layered Semiconductor InSe.” J. of Applied Physics, V. 86, No. 10, Nov. 15, 1999, pp. 5687-5691.Applicant
Kim, S.Y., Lee, J.-L., Kim, K-B, Tak, Y.-H. “Effect of Ultraviolet-Ozone Treatment of Indium-Tin-Oxide on Electrical Properties of Organic Light Emitting Diodes.” J. of Applied Physics, V. 96. No. 5, Mar. 1, 2004, pp. 2560-2563Applicant
Vashaee, D., Shakouri, A., Goldberger, J., Kuykendall, T., Pauzauskie, P., Yang, P. “Electrostatics of Nanowire Transistors with Triangular Cross Sections.” J. of Applied Physics, 99, 054310 (2006).Applicant
Presley, R.E., Munsee, C.L., Park, C.-H., Hong, D; Wager, J.F., Keszler, D.A. “Tin Oxide Transparent Thin-Film Transistors.” J. Physics D: Applied Physics, 37 (2004) 2810-2813.Applicant
Ju, Sanghyun, Lee, K., Janes, D.B., Yoon, M-H., Facchetti, A., Marks. T.J. “Low Operating Voltage Single ZnO Nanowire Field-Effect Transistors Enabled by Self-Assembled Organic Gate Nanodielectrics.” Nano Letters (2005) V. 5, No. 11, 2281-2286.Applicant
Banerjee, D., Lao, J.Y., Wang, D.Z., Huang, J.Y., Steeves, D., Kimball, B., Ren, Z.F. “Synthesis and Photoluminescence Studies on ZnO Nanowires.” Nanotechnology, 15 (2004) 404-409.Applicant
Moon, T.-H., Jeong, M.-C., Oh, B.-Y., Ham, M.-H., Jeun, M.-H., Lee, W.-Y., Myoung, J.-M. “Chemical Surface Passivation of HfO2 Films in a ZnO Nanowire Transistor.” Nanotechnology 17 (2006) 2116-2121.Applicant
Wang, L., Yoon, M.-H., Lu, G., Yang, Y., Facchetti, A., Marks, T.J. “High Performance Transparent Inorganic-Organic Hybrid Thin-Film N-Type Transistors.” Nature Materials, V. 5, Nov. 2006, pp. 293-317.Applicant
Gassenbauer, Y., Schafranek, R., Klein, A., Zafeiratos, S., Hävecker, M., Knop-Gericke, A., Schlögl, R. “Surface States, Surface Potentials, and Segregation at Surfaces of Tin-Doped In2O3.” Physical Review B. 73. 245312 (2006).Applicant
Yoon, M.-H., Facchetti, A., Marks, T.J. “σ-π Molecular Dielectric Multilayers for Low-Voltage Organic Thin-Film Transistors.” PNAS, V. 102, No. 13, 4678-4682, Mar. 29, 2005.Applicant
Nomura, K., Ohta, H., Ueda, K., Kamiya, T., Hirano, M., Hosono, H. “Thin-Film Transistor Fabricated in Single-Crystalline Transparent Oxide Semiconductor.” Science, 00368075, V. 300, Issue 5623, May 23, 2003.Applicant
Fortunato, E., Barquinha, P., Pimentel, A., Gonçalves, A., Marques, A., Pereira, L., Martins, R. “Recent Advances in ZnO Transparent Thin Film Transistors.” Thin Solid Films 487 (2005) 205-211.Applicant

Abstract