Lithium secondary battery

[0001] The present invention relates to a novel lithium secondary battery having a high input/output performance and suitable for hybrid electric vehicles and the like.

[0002] Hybrid electric vehicles, in which an engine and a motor serve as power sources, have been developed and commercialized for environmental protection and energy saving. Moreover, fuel cell hybrid electric vehicles in which a fuel cell is used in place of an engine have been extensively under development for vehicles in the future.

[0003] Secondary batteries, which can undergo a number of charging/discharging cycles, are essential devices as power sources for hybrid electric vehicles.

[0004] Of secondary batteries, lithium secondary batteries are promising, because of their high operational voltage and capability of generating a high output, and are of increasing importance as power sources for hybrid electric vehicles.

[0005] An electrolyte solution for lithium secondary batteries is required to have high voltage-resistant characteristics, and an organic electrolyte solution containing an organic solvent is used.

[0006] However, an organic solvent involves disadvantages of poor solubility for lithium salts and large dependence of its conductivity on temperature, thus resulting in a marked deterioration in operational characteristics at low temperatures over those at room temperature.

[0007] Carbonate ester compounds are now mainly used as solvents for organic electrolyte solutions for lithium secondary batteries, because of their high voltage-resistant characteristics.

[0008] Cyclic carbonate ester solvents have a high viscosity, although they have a high solubility for lithium salts. Linear carbonate ester solvents, on the other hand, have a low solubility for lithium salts, although they have a low viscosity.

[0009] Hence, a mixture of cyclic and linear carbonate esters is generally used as the electrolyte solutions.

[0010] For improvement of low-temperature characteristics of electrolyte solutions, Patent Documents 1 to 5 shown below disclose use of a linear carbonate ester incorporated with ethyl methyl carbonate (EMC) of an asymmetric structure.

[0011] Patent Document 6 shown below discloses use of an acetate ester, which has a lower molecular weight than EMC and works as a solvent of a low viscosity and a low melting point.

Patent Document 1: JP-B-2,705,529

Patent Document 2: JP-A-10-027625

Patent Document 3: JP-A-2001-148258

Patent Document 4: JP-A-2002-305035

Patent Document 5: JP-A-2003-323915

Patent Document 6: JP-A-09-245838

[0012] It is an object of the present invention to provide a lithium secondary battery which uses an electrolyte solution exhibiting no inflammability at room temperature (20° C.) and not deteriorating output characteristics of the battery at low temperatures and room temperature.

[0013] The present invention provides a lithium secondary battery comprises a cathode and an anode, both capable of storing/releasing a lithium ion, a separator which separates these electrodes from each other, and an electrolyte solution, wherein the electrolyte solution comprises as solvents:

[0014] a cyclic carbonate represented by the formula (1):

[0015]
(wherein, R₁, R₂, R₃ and R₄ may be the same or different and are each hydrogen, fluorine, chlorine, an alkyl group or a fluorinated alkyl group, each having 1 to 3 carbons),

[0016] a linear carbonate represented by the formula (2):

[0017]
(wherein, R₅ and R₆ may be the same or different and are each hydrogen, fluorine, chlorine, an alkyl group or a fluorinated alkyl group, each having 1 to 3 carbons, which) and

[0018] a compound represented by the formula (3):

[0019]
(wherein, R₇ and R₈ may be the same or different and are each hydrogen, fluorine, chlorine, an alkyl group or a fluorinated alkyl group, each having 1 to 3 carbons), and

[0020] the composition ratio of the cyclic carbonate represented by the formula (1) is 18.0 to 30.0%, the composition ratio of the linear carbonate represented by the formula (2) is 74.0 to 81.9% and the composition ratio of the compound represented by the formula (3) is 0.1 to 1.0%, based on the whole solvents (100%), all percentages by volume.

[0021] The cathode mixture layer has a porosity of 25 to 40%, inclusive, and the anode mixture layer also has a porosity of 25 to 40%, inclusive, based on the respective layers, all percentages by volume.

[0022] The cathode comprises a cathode mixture and a cathode-side current collector, wherein the cathode mixture comprises a cathode-active material, an electroconductive agent and a binder, and is spread over the cathode-side current collector to form a cathode mixture layer thereon.

[0023] The anode comprises an anode mixture and an anode-side current collector, wherein the anode mixture comprises an anode-active material, an electroconductive agent and a binder, and is spread over the anode-side current collector to form an anode mixture layer thereon.

[0024] The present invention can provide a lithium secondary battery which uses an electrolyte solution exhibiting no inflammability at room temperature (20° C.) and not deteriorating output characteristics of the battery at low temperatures and room temperature.

[0025] Other objects, features and advantages of the invention will become apparent from the following description of the embodiments of the invention taken in conjunction with the accompanying drawings.

• [0028] 1 Cathode-side current collector
• [0029] 2 Cathode mixture layer
• [0030] 3 Anode-side current collector
• [0031] 4 Anode mixture layer
• [0032] 7 Separator
• [0033] 9 Anode-side lead
• [0034] 10 Cathode-side lead
• [0035] 11 Cathode-side insulator
• [0036] 12 Anode-side insulator
• [0037] 13 Anode battery can
• [0038] 14 Gasket
• [0039] 15 Cathode battery lid

[0040] The present invention comprises a cathode of a cathode mixture comprising a lithium composite oxide, an electroconductive agent mainly composed of graphite-base carbon and a binder, spread on an aluminum foil, wherein the cathode mixture layer has a porosity of 25 to 40% by volume, inclusive, based on the layer. When the porosity is less than 25%, the electrolyte solution may not permeate the cathode mixture layer in a sufficient quantity to decrease the number of lithium ions in the layer. As a result, the lithium secondary battery may not produce a sufficient output due to short supply of the lithium ions to the cathode-active material, in particular at low temperatures. When the porosity is more than 40%, on the other hand, the content of the cathode mixture in the layer may be insufficient to cause insufficient input/output.

[0041] The anode for the present invention comprises an anode mixture comprising amorphous carbon, an electroconductive agent and a binder, spread on a copper foil, wherein the anode mixture layer has a porosity of 25 to 40% by volume, inclusive, based on the layer. When the porosity is less than 25%, the electrolyte solution may not permeate the anode mixture layer in a sufficient quantity. As a result, the lithium secondary battery may not produce a sufficient input due to short supply of lithium ions to the anode-active material, in particular at low temperatures. When the porosity is more than 40%, on the other hand, the content of the anode mixture in the layer may be insufficient to cause insufficient input/output.

[0042] The solvents represented by the formula (1) include ethylene carbonate (EC), trifluoropropylene carbonate (TFPC), chloroethylene carbonate (ClEC), trifluoroethylene carbonate (TFEC), difluoroethylene carbonate (DFEC) and vinyl ethylene carbonate (VEC).

[0043] Of the above compounds, EC is more preferable, viewed from formation of a coating film on the anode.

[0044] Incorporation of a small quantity (2% by volume or less) of ClEC, TFEC or VEC imparts good cycle characteristics to a coating film on the electrode.

[0045] Moreover, TFPC or DFEC may be incorporated in a small quantity (2% by volume or less) for facilitating formation of a coating film on the cathode.

[0046] The solvents represented by the formula (2) include dimethyl carbonate (DMC), ethyl methyl carbonate (EMC), diethyl carbonate (DEC), methyl propyl carbonate (MPC), ethyl propyl carbonate (EPC), trifluoromethyl ethyl carbonate (TFMEC) and 1,1,1-trifluoroethyl methyl carbonate (TFEMC).

[0047] DMC is highly compatible with many solvents, and is suitable for being mixed with EC or the like.

[0048] DEC has a lower melting point than DMC, and is suitable for improving low-temperature (−30° C.) characteristics.

[0049] EMC has an asymmetric structure and also a low melting point, and is suitable for improving low-temperature characteristics.

[0050] EPC and TFMEC have a propylene side chain and asymmetric structure, and are suitable as solvents for adjusting low-temperature characteristics.

[0051] TFEMC has a molecule partly fluorinated to have an increased dipole moment, and is suitable for keeping dissociation of lithium salts at low temperatures and also for improving low-temperature characteristics.

[0052] The compounds represented by the formula (3) include vinylene carbonate (VC), methylvinylene carbonate (MVC), dimethylvinylene carbonate (DMVC), ethylvinylene carbonate (EVC) and diethylvinylene carbonate (DEVC).

[0053] VC has a low molecular weight, and is considered to form a dense coating film on the electrode. MVC, DMVC, EVC, DEVC or the like is a VC substituted with an alkyl group and is considered to form a low-density coating film on the electrode, magnitude of density depending on size of the alkyl chain with which the compound is substituted, thus to have the effect of improving low-temperature characteristics.

[0054] The lithium salt for the electrolyte solution is not limited. The lithium salts useful for the present invention include inorganic lithium salts, e.g., LiPF₆, LiBF₄, LiClO₄, LiI, LiCl and LiBr; and organic lithium salts, e.g., LiB[OCOCF₃]₄, LiB[OCOCF₂CF₃]₄, LiPF₄(CF₃)₂, LiN(SO₂CF₃)₂ and LiN(SO₂CF₂CF₃)₂.

[0055] In particular, LiPF₆, which has been widely used for batteries for domestic purposes, is a suitable compound because of its quality stability.

[0056] Moreover, LiB[OCOCF₃]₄ is an effective compound, because it exhibits high dissociation capability and solubility, and also high conductivity even at a low content.

[0057] An electrolyte solution preferably has a flash point of 21° C. or higher and an ion conductivity of 2 mS/cm or more at −30° C. to simultaneously satisfy safety and low-temperature characteristics.

[0058] It is preferable to incorporate DMC and EMC in a ratio of 0.6 to 1.3 by volume, particularly preferably 0.8 to 1. A DMC/EMC ratio of 0.6 to 1.3 will secure an electrolyte solution having a flash point of 21° C. or higher and an ion conductivity of 2 mS/cm or more at −30° C. Moreover, a DMC/EMC ratio of 0.8 to 1 will secure an electrolyte solution having a flash point of 21° C. or higher and an ion conductivity of 2.2 mS/cm or more at −30° C., and hence is more preferable.

[0059] The anode-active materials useful for the present invention include natural graphite, composite carbonaceous material with natural graphite coated with a film formed by dry chemical vapor deposition (CVD) or wet spraying, synthetic graphite produced by sintering a resin (e.g., epoxy or phenolic resin) or pitch from petroleum or coal, another carbonaceous material (e.g., amorphous material), lithium metal having a capability of storing/releasing lithium by forming a compound with lithium, silicon reacting with lithium to form a compound to have a capability of storing/releasing lithium by being held in the interstices between the crystals, and oxide or nitride of an element belonging to the IV group (e.g., germanium or tin). They may be generally referred to as anode-active materials. In particular, a carbonaceous material is an excellent material because of its high electroconductivity, low-temperature characteristics and good cycle stability.

[0060] Of carbonaceous materials, those having a wide interlayer space between carbon network planes (d₀₀₂) are suitable for their rapid charging/discharging capability and excellent low-temperature characteristics.

[0061] It should be noted, however, that some carbonaceous materials having a wide d₀₀₂ value show insufficient capacity or charging/discharging efficiency during the initial stage of charging, and hence they preferably have a d₀₀₂ value of 0.39 nm or less. Such a material may be sometimes referred to as pseudo-anisotropic carbon.

[0062] Moreover, the electrode may be incorporated with a highly electroconductive carbonaceous material, e.g., graphite-like material, amorphous material or activated carbon.

[0063] Graphite-like materials useful for the present invention include those having one of the following characteristics (1) to (3):

(1) an R value, or I_D/I_G ratio, of 0.2 to 0.4, inclusive, wherein I_D is intensity of the peak in a range from 1300 to 1400 cm⁻¹, and I_G is intensity of the peak in a range from 1580 to 1620 cm⁻¹, both in a Raman spectral pattern,

(2) a half width Δ of 40 to 100 cm⁻¹, inclusive, of the peak in a range from 1300 to 1400 cm⁻¹ in a Raman spectral pattern, and

(3) an X value, or I(₁₁₀)/I(₀₀₄) ratio, of 0.1 to 0.45, inclusive, wherein I(₁₁₀) is peak intensity from the (110) plane and I(₀₀₄) is peak intensity from the (004) plane, both in an X-ray diffraction pattern.

[0064] A lithium composite oxide as the cathode-active material preferably has a composition represented by the formula Li_αMn_xM1_yM2_zO₂ (wherein, M1 is at least one selected from the group consisting of Co and Ni, M2 is at least one selected from the group consisting of Co, Ni, Al, B, Fe, Mg and Cr, x+y+z=1, 0<α<1.2, 0.2≦x≦0.6, 0.2≦y≦0.4 and 0.05≦z≦0.4).

[0065] Of these materials, those having Ni or Co as M1, and Co or Ni as M2 are more preferable. LiMn_1/3Ni_1/3Co_1/3O₂ is still more preferable. The composition has an increased capacity as the Ni content increases, an increased output at low temperatures as the Co content increases, and decreases in production cost as the Mn content increases. The additive elements have effects of improving cycle characteristics. Other compounds, e.g., those represented by the general formula LiM_xPO₄ (M: Fe or Mn, and 0.01≦X≦0.4), and orthorhombic phosphorus compounds having space group Pmnb symmetry represented by LiMn_1-xM_xPO₄ (M: divalent cation other than Mn, and 0.01≦X≦0.4) may be also used for the present invention.

[0066] LiMn_1/3Ni_1/3Co_1/3O₂, in particular, is suitable as a lithium battery material for hybrid electric vehicles (HEVs) because of its high low-temperature characteristics and cycle stability.

[0067] The lithium secondary battery described above as one embodiment of the present invention has improved safety over conventional lithium secondary batteries, mainly coming from use of an electrolyte solution which is not inflammable at room temperature (20° C.) while not deteriorating output characteristics at low temperatures and room temperature or output maintenance characteristics during storage at high temperatures over an extended period. As such, it can find wide use in various areas, e.g., power sources for hybrid electric vehicles, and power sources including back-up power sources for electrically driven control systems for vehicles. Moreover, it is also suitable as a power source for industrial machines, e.g., electrically driven tools and forklifts.

[0068] Moreover, the lithium secondary battery as one embodiment of the present invention has improved characteristics, in particular output characteristics at low temperatures, and useful for vehicles frequently working in cold districts. The improved output characteristics at low temperatures reduce size and weight of a module in which the batteries are assembled to produce power of several hundred volts by reducing a required number of the batteries.

[0069] The best mode for carrying out the present invention is specifically described by Examples.

[0070] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 19.4:0.6:40:40 by volume. The electrolyte solution was not inflammable as confirmed by the flash point test carried out at 20° C.

[0071] Flash point was determined using an automatic tag closed flash point tester in accordance with JIS K-2265.

(Evaluation of Ion Conductivity)

[0072] The sample solution (5 mL) put in a glass bottle was measured for its ion conductivity at −30° C. by a digital electroconductivity meter (CM-60V, Toa Denpa) whose electrodes were immersed in the sample solution, where the measurement was started 90 minutes after the bottle was held in a constant-temperature bath.

[0073] The electrolyte solution preferably has a flash point of 21° C. or higher and an ion conductivity of 2 mS/cm or more at −30° C. to simultaneously satisfy safety and low-temperature characteristics. FIG. 2 shows an ion conductivity of mixed electrolyte solutions of EC/VC/DMC/EMC having a composition ratio of 19.4/0.6/X/80-X % by volume, changing with the DMC/EMC volume ratio. The results indicate that the electrolyte solution has a flash point of 21° C. or higher and an ion conductivity of 2 mS/cm or more at −30° C. when the DMC/EMC volume ratio is set at 0.6 to 1.3. The ratio of 0.8 to 1 is more preferable, because it gives a flash point of 21° C. or higher and an ion conductivity of 2.2 mS/cm or more at −30° C.

(Fabrication of Spirally Wound Battery)

[0074] A spirally wound battery of Example 1 was fabricated by the following procedure. FIG. 1 is a cross-sectional view illustrating one side of the battery.

[0075] A cathode material paste was prepared using LiMn_1/3Ni_1/3Co_1/3O₂ as a cathode-active material, carbon black (CB1) and graphite (GF1) as electroconductive materials, polyvinylidene fluoride (PVDF) as a binder, and N-methylpyrrolidone (NMP) as a solvent to have a composition ratio of LiMn_1/3Ni_1/3Co_1/3O₂:CB1:GF1:PVDF of 86:9:2:3 by mass (dry basis).

[0076] The cathode material paste was spread over an aluminum foil, which became a cathode-side current collector 1, dried at 80° C., roll-pressed, and dried at 120° C. to prepare a cathode mixture layer 2 on the cathode-side current collector 1. The cathode mixture layer had a porosity set at 30% based on the whole layer (the value is hereinafter referred to as cathode porosity).

[0077] Next, an anode material paste was prepared using pseudo-anisotropic carbon as amorphous carbon serving as an anode-active material, carbon black (CB2) as an electroconductive material, PVDF as a binder and NMP as a solvent, to have a composition of pseudo-anisotropic carbon:CB2:PVDF of 88:5:7 by mass (dry basis).

[0078] The anode material paste was spread over a copper foil, which became an anode-side current collector 3, dried at 80° C., roll-pressed, and dried at 120° C. to prepare an anode mixture layer 4 on the anode-side current collector 3. The anode mixture layer had a porosity set at 35% based on the whole layer (the value is hereinafter referred to as anode porosity), so as to form a battery.

[0079] A separator 7 was placed between the cathode and anode prepared above to form a spirally wound assembly, which was encased in an anode battery can 13. The electrolyte solution prepared in Example 1 was injected into the assembly and sealed by caulking to form a spirally wound battery.

[0080] The other components shown in FIG. 1 are 9: anode-side lead, 10: cathode-side lead, 11: cathode-side insulator, 12: anode-side insulator, 14: gasket, and 15: cathode battery lid.

(Evaluation of Porosity)

[0081] Porosity was determined by mercury porosimetry for the cathode and anode after the mixture layer was separated from the current collector of each side.

(Evaluation of Battery)

[0082] The spirally wound battery illustrated in FIG. 1 was evaluated for direct current resistance (DCR) at 25 and −30° C., and pulse cycle characteristics (characteristics after the battery was subjected to pulse cycles for 1000 hours).

[0083] The battery was charged with electricity at a constant current of 0.7 A to 4.1 V, and then at a constant voltage of 4.1 V until the amperage reached 20 mA. Then, it was allowed to discharge electricity to 2.7 V at 0.7 A, after it was halted for 30 minutes. These cycles were repeated 3 times.

[0084] Next, the battery was charged with electricity at a constant current of 0.7 A to 3.8 V, allowed to discharge electricity at 10 A for 10 seconds, again charged with electricity to 3.8 V at a constant current, allowed to discharge electricity at 20 A for 10 seconds, again charged with electricity to 3.8 V, and allowed to discharge electricity at 30 A for 10 seconds.

[0085] The battery was evaluated for DCR based on the I-V characteristics observed.

[0086] Moreover, the battery was subjected to a pulse cycle test in which charging/discharging were repeated at 20 A for 2 seconds in a constant-temperature bath kept at 50° C., and evaluated for DCR at 25 and −30° C., after it was subjected to the pulse cycles for 1000 hours. The evaluation results are given in Table 1.

[0087] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 19.5:0.5:40:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0088] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0089] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 19.6:0.4:40:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0090] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0091] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 19.8:0.2:40:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0092] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0093] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 19.7:0.3:40:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0094] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0095] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 21.7:0.3:38:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0096] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0097] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 23.7:0.3:36:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0098] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0099] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 29.7:0.3:30:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0100] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0101] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1.2 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 23.7:0.3:36:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0102] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0103] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1.1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 23.7:0.3:36:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0104] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0105] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1.1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 23.7:0.3:36:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0106] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 25% and anode porosity of 25%, all percentages by volume. The evaluation results are given in Table 1.

[0107] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1.1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 23.7:0.3:36:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0108] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 35% and anode porosity of 40%, all percentages by volume. The evaluation results are given in Table 1.

[0109] An electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1.1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 23.7:0.3:36:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0110] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 40% and anode porosity of 40%, all percentages by volume. The evaluation results are given in Table 1.

[0111] A comparative electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1 M in a mixed solvent of EC:VC:DMC:EMC:methyl acetate (MA) having a composition ratio of 29.4:0.6:30:30:10 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0112] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0113] A comparative electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 34:0:33:33 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0114] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0115] A comparative electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 15:0:35:50 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0116] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0117] A comparative electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 18:2:40:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0118] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 30% and anode porosity of 35%, all percentages by volume. The evaluation results are given in Table 1.

[0119] A comparative electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1.1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 23.7:0.3:36:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0120] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 20% and anode porosity of 20%, all percentages by volume. The evaluation results are given in Table 1.

[0121] A comparative electrolyte solution was prepared by dissolving LiPF₆ as a lithium salt to a concentration of 1.1 M in a mixed solvent of EC:VC:DMC:EMC having a composition ratio of 23.7:0.3:36:40 by volume, and evaluated for ion conductivity and inflammability in the same manner as in Example 1.

[0122] A spirally wound battery was prepared, and evaluated for porosity and battery characteristics in the same manner as in Example 1. It was confirmed to have a cathode porosity of 38% and anode porosity of 40%, all percentages by volume. The evaluation results are given in Table 1.

[0123]

	TABLE 1
	Pulse cycle
	characteristics after
	subjected to pulse cycles
	for 1000 hours
				Ion	Initial	Output	Output
	Electrolyte solution composition	Porosity		conduc-	characteristics	maintenance	maintenance
	EC	VC	DMC	EMC	MA	(vol %)	Inflam-	tivity	DCR	DCR	ratio	ratio
	LiPF6	(vol	(vol	(vol	(vol	(vol	Cath-	An-	mability	@−30° C.	@25° C.	@−30° C.	@25° C.	@−30° C.
	(M)	%)	%)	%)	%)	%)	ode	ode	at 20° C.	(mS/cm)	(mΩ)	(mΩ)	(%)	(%)
Example 1	1	19.4	0.6	40	40	0	30	35	Not observed	2.3	67	610	84	83
Example 2	1	19.5	0.5	40	40	0	30	35	Not observed	2.3	66	603	85	84
Example 3	1	19.6	0.4	40	40	0	30	35	Not observed	2.3	66	595	85	83
Example 4	1	19.8	0.2	40	40	0	30	35	Not observed	2.3	65	595	86	85
Example 5	1	19.7	0.3	40	40	0	30	35	Not observed	2.3	63	590	88	87
Example 6	1	21.7	0.3	38	40	0	30	35	Not observed	2.3	63	590	88	87
Example 7	1	23.7	0.3	36	40	0	30	35	Not observed	2.3	62	592	88	87
Example 8	1	29.7	0.3	30	40	0	30	35	Not observed	2.0	62	615	84	83
Example 9	1.2	23.7	0.3	36	40	0	30	35	Not observed	2.2	63	592	88	87
Example 10	1.1	23.7	0.3	36	40	0	30	35	Not observed	2.2	61	592	88	87
Example 11	1.1	23.7	0.3	36	40	0	25	25	Not observed	2.2	63	600	88	87
Example 12	1.1	23.7	0.3	36	40	0	35	40	Not observed	2.2	65	610	88	87
Example 13	1.1	23.7	0.3	36	40	0	40	40	Not observed	2.2	66	620	88	87
Comparative	1	29.4	0.6	30	30	10	30	35	Observed	2.3	68	675	83	82
Example 1
Comparative	1	34	0	33	33	0	30	35	Not observed	1.9	68	850	72	69
Example 2
Comparative	1	15	0	35	50	0	30	35	Not observed	2.3	75	680	68	67
Example 3
Comparative	1	18	2	40	40	0	30	35	Not observed	2.3	70	750	83	82
Example 4
Comparative	1.1	23.7	0.3	36	40	0	20	20	Not observed	2.2	70	730	82	75
Example 5
Comparative	1.1	23.7	0.3	36	40	0	45	45	Not observed	2.2	70	700	83	77
Example 6

[0124] The battery prepared in Comparative Example 1 with an electrolyte solution containing MA exhibits good characteristics, in particular lower DCR at −30° C. than the other Comparative Examples; with MA-free electrolyte solutions. Nevertheless, it is not preferable because of inflammability observed at 20° C., and lower pulse cycle characteristics after it is subjected to pulse cycles for 1000 hours than those prepared in Examples 1 to 13.

[0125] The battery prepared in Comparative Example 2 with an electrolyte solution containing EC at a higher content of 34% by volume than those prepared in Examples 1 to 13 is not preferable, because of its higher DCR at −30° C.

[0126] The battery prepared in Comparative Example 3 with an electrolyte solution containing EC at a lower content of 15% by volume than those prepared in Examples 1 to 13 is not preferable, because of its lower DCR at 25° C.

[0127] The battery prepared in Comparative Example 4 with an electrolyte solution containing VC at a higher content of 2% by volume than those prepared in Examples 1 to 13 is not preferable, because of its lower DCR at 25 and −30° C.

[0128] The battery prepared in Comparative Example 5 with lower porosities of 20% by volume in the cathode and anode than those prepared in Examples 1 to 13 is not preferable, because of its higher DCR at 25 and −30° C.

[0129] The battery prepared in Comparative Example 6 with a higher porosity of 45% by volume in each of the cathode and anode than those prepared in Examples 1 to 13 is not preferable, because of its higher DCR at 25 and −30° C.

[0130] As discussed above, each of Examples 1 to 13 can provide a lithium secondary battery which exhibits improved safety, in particular with an electrolyte solution exhibiting no inflammability at room temperature (20° C.), while not deteriorating output characteristics at low temperatures and room temperature, and output maintenance characteristics when the battery is preserved at high temperature (50° C.).

[0131] Moreover, the lithium secondary battery prepared in each of Examples 1 to 13 as a high-output battery has improved DCR at low temperatures and low-temperature input/output characteristics over conventional ones.

[0132] Still more, the lithium secondary battery prepared in each of Examples 1 to 13 has improved characteristics, in particular output characteristics at low temperatures, which make the battery effective for use in vehicles frequently working in cold districts. The improved output characteristics at low temperatures bring advantages of reducing size and weight of a module in which the batteries are assembled to produce power of several hundred volts by reducing a required number of the batteries.

[0133] It should be further understood by those skilled in the art that although the foregoing description has been made on embodiments of the invention, the invention is not limited thereto and various changes and modifications may be made without departing from the spirit of the invention and the scope of the appended claims.