US 7,683,359 B2Grant
Structured silicon anode
Issue Date:2010-03-23
•19 Claims
•12 Drawing Sheets
Abstract
A silicon/lithium battery can be fabricated from a substrate. This allows the battery to be produced as an integrated unit on a chip. The battery includes an anode formed from an array of submicron structures including silicon fabricated on a substrate and a cathode including lithium.
Metadata
Assignee
- Nexeon Ltd.
Inventor
- Mino Green
Application Information
Application Number:US 12/333,443
Filing Date:2008-12-12
Priority Date:2002-11-05
Art Unit:2894
Classifications
IPC:
H01L29/00
Patent Drawings (12 sheets)
Description
[0001] This application is a continuation of U.S. Ser. No. 12/074,642, filed Mar. 4, 2008 which is a division of U.S. Ser. No. 10/533,822, filed Aug. 31, 2005, now U.S. Pat. No. 7,402,829, issued Jul. 22, 2008. The U.S. Pat. No. 7,402,829 patent in turn was the entry into the National Phase in the U.S. of International Application No. PCT/GB2003/004783, filed Nov. 5, 2003.
[0002] The present invention relates to structured silicon anodes for lithium battery applications.
[0003] Silicon is recognised as a potentially high energy per unit volume host material for lithium in lithium battery applications1. Attempts at realising this potential have met with only partial success when nano-composites of silicon powder and carbon black have been used2. The major technical problem associated with the use of silicon/lithium appears to be the mechanical failure brought about by the repeated large volume expansion associated with alloying1c,3. Metallic and intermetallic anodic host materials, other than layer materials such as graphite, are reported to disintegrate after a few lithium insertion/extraction cycles3,4 unless in fine powder form (sub-micron range). Since we are interested in finding a way to make a lithium battery integrated onto a silicon chip we need to find a solution to this materials problem. It is envisaged that the principal applications area for lithium batteries integrated into a chip would be in the medical field. Thus the well-developed practice of cochlea implants appears to be an area that would benefit from an integrated battery supply5.
[0004] This invention seeks to realise the potential of the silicon-lithium system to allow the possibility of a lithium battery integrated on to a silicon chip.
[0005] Accordingly this invention provides a method of fabricating sub-micron silicon electrode structures on a silicon wafer. Preferably these structures comprise pillars.
[0006] For a silicon-lithium system the basic cell diagram can be represented as Li|Li+-electrolyte|Si, for this cell the cathodic process is, discharge of lithium onto silicon to form an alloy (charging), and the anodic process is lithium extraction or de-alloying (discharging). The EMF data reported by Wen and Huggins6 for the liquid system at 415° C. is shown bracketed below and the solid system at room temperature7 is shown un-bracketed below. Their results (in mV vs, Li) are: Si/Li12Si7-582(332); Li12Si7/Li7Si3-520(288); Li7Si3/Li13Si4-428 (158); Li13Si4/Li21Si5-˜300 (44).
[0007] It will be appreciated that the formation of Li12Si7 in place of Si results in a significant volume change (the alloy is 2.17 times bigger). On a conventional silicon wafer suitable for use as an anode for a lithium battery this volume change leads to crack formation and pulverisation however due to their small size and configuration sub-micron anode structures made in accordance with the invention, are be able to tolerate the conditions occasioned by the massive volume changes occasioned by lithium alloying/de-alloying.
[0008] In tests structured electrodes of sub micron diameter Si pillars maintained their structural integrity throughout the cycling whereas planar Si electrodes showed cracks (2 micron features) after 50 cycles. An appropriate size restriction to achieve suitable electrodes is that the silicon pillars should not exceed a fractional surface coverage (F) of ˜0.5.
[0009] An embodiment of the invention will now be described by way of non-limiting example only, with reference to the accompanying drawings, in which:
[0010] FIG. 1 is a schematic view of a structured electrode;
[0011] FIG. 2 shows one of a series of CV scan sets;
[0012] FIG. 3 shows results for a series of galvanostratic measurements;
[0013] FIG. 4 shows pictures of the structure;
[0014] FIG. 5 shows SEM pictures of the structure; and
[0015] FIG. 6 shows a lithium battery in accordance with the present invention.
[0016] The electrochemical discharge of lithium on silicon and its subsequent chemical reaction destroys the silicon lattice, giving rise to the swelling of the solid, producing amorphous Si/Li phases13. The first new phase to appear in the system is Li12Si7. This compound, and all the rest up to Li, is a so-called Zintl-Phase Compound (ZPC), and consists of simple, electropositive, cations and complex co-valently bound, multiply charged, electronegative, anions. Of course the charge ascribed to the “ions” is purely notional: the actual charge (depending upon definition) is less than the formal value and may be considerably less, hence the bulk lithium will be referred to as Lio and bulk silicon as Sino.
[0017] It is important to form some idea of the mechanism of lithiation and de-lithiation of silicon. It is proposed that:
-
- [0018] (i) Discharged lithium reacts with silicon forming a ZPC film with atomically continuous contact to the silicon.
- [0019] (ii) Lithium excess diffuses (via a vacancy mechanism) through the compact ZPC film to react with silicon at the Si/ZPC interface, thickening the ZPC film, without void formation.
These processes might be represented by: Li+(el)+e− (solid)→Li(ads.); Li(ads.)+V(ZPC)→Lio (ZPC)s; Lio (ZPC)s→diffusion→Lio (ZPC)ZPC/Si; x Lio +ySio →ZPC (Lix/ySi).
(Li(ads) is Li adsorbed on ZPC; V is a Lio vacancy in ZPC) - [0020] (iii) The amorphous13 ZPC film is deformable and so does not give rise to significant stress induced cracking on volume change.
The diffusion coefficient, D, for Li in crystalline Si14 is ˜10−14 cm2s−1, Li in ZPC is expected to be faster; a value of D 10−12 cm2s−1 would be enough to account for all the processes carried out in this study. This model for ZPC film formation is in many ways analogous to the model of SiO2 layer formation on silicon due to Deal and Grove15: but the details are different and will be treated elsewhere.
[0021] The model for ZPC decomposition is, in broad terms, the reverse of the above steps. Discharge of Lio at the electrolyte interface produces a surface vacancy in the ZPC. Locally Lio moves into the vacancy so the vacancy diffuses back to the ZPC/Si interface: at the interface Sin rejoins the Si phase (where it is said to be polycrystalline13) and vacancies coalesce to produce larger void spaces. These spaces, as they coalesce further and grow, give rise to the crack like features seen in the SEM pictures in FIGS. 4 c,d and 5. Such a process has been described by Beaulieu et al16 for lithium removal from silicon/tin alloys.
[0022] It has been shown that repeated Li alloying/de-alloying of planar Si can be carried out without pulverisation of the substrate, cf. FIG. 5 . However, as noted, the alloy/de-alloy process is limited by diffusion through the ZPC layer. In order to obtain charging rates suitable for various applications it is necessary to increase the surface area of the Si/electrolyte interface; and this has been done using pillar fabrication. Previous attempts using silicon particles have failed because the particle-to-particle contacts change and part with cycling2. The pillar structures, on the other hand, are largely maintained as evidenced by the flatness of the pillar tops after 50 cycles, cf. FIG. 4 .
[0023] Efficiencies of <100% reported here are attributed mainly to reaction, on alloying, with the electrolyte, and to a lesser extent isolation of regions of ZPC. The data presented here show that reduced current density on both alloying and de-alloying results in improving efficiency. It is supposed that this improvement comes mainly from a reduced surface concentration of adsorbed Li on alloying and accessing all the lithium in the ZPC on de-alloying.
[0024] There is large scope for further increasing the surface-to-volume ratio of the pillar construction, for example, pillars of diameter (d) ˜0.3 microns and 6 micron height (H). The pillar volume (v) would be, FH, and for F=0.4, v=2.4×10−4 cc/cm2, which is equivalent, when converted to Li12Si7, to a capacity of 3.81×103 v=914 microAhrcm−2. The surface area of such a pillar structure is ˜4 FH/d, which is the basis of the much improved characteristics.
[0025] To make structures in accordance with the invention the following method may be used, namely “Island Lithography” as disclosed in international patent No. WO01/13414. This method employs cesium chloride as the resist in the lithographic step in the fabrication of pillar arrays. It works as follows. A thin film of CsCl is vacuum deposited on the clean, hydrophilic, surface of the Si substrate. This system is then exposed to the atmosphere at a controlled relative humidity. A multilayer of water absorbs on the surface, the CsCl is soluble in the water layer (being more soluble at places of higher radius of curvature). The CsCl re-organises into a distribution of hemispherical islands, driven by the excess surface energy associated with CsCl surface curvature. Such arrays are useful in making structures for various studies involving nano-scale phenomena. In this case reactive ion etching is preferably used, with the islands acting as X masks so that removal of the surrounding silicon forms the desired pillar structures.
[0026] A study of the kinetics of the formation of island arrays has been carried out on GaAs surfaces9 and more recently, and more extensively, on Si/SiO2 surfaces10 where the technique and results are described in detail. The process variables are: CsCl film thickness (L); humidity (RH), time of exposure (t). The resulting island array has a Gaussian distribution of diameters, average diameter (<d>) standard deviation (±s) and surface fractional coverage (F). Having made the CsCl resist array the next step is reactive ion etching (RIE) to produce the corresponding array of pillars11. The RIE process variables are: feed-gas composition, flow rate and chamber pressure; RF power; dc bias; etch time. The results are characterised by the etch depth, corresponding to pillar height (H), and the wall angle, namely the angle that the pillar wall makes with the wafer plane; it is chosen in this study to be close to 90°. The examples reported in this work were etched in a Oxford Plasmalab 80 apparatus. The etch gas was (O2:Ar:CHF3) in the ratio 1:10:20; feed rate 20 sccm; chamber pressure, 50 milli pascals; RF power, 73 watts; dc bias 200V.
[0027] The pillar structure reported in this study (K-series) was characterised as <d>=580 nm±15 nm; F=0.34; H=810 nm: it was made using, L=80 nm; RH=40%; t=17.5 hrs. After fabrication the silicon samples were washed in water; etched for 20 seconds in NH4OH(28 w % NH3):H2O2(100 v/v):H2O in equal volume ratios; the etchant was flooded away with de-ionized water and blow dried.
[0028] Of course the structures may also be fabricated by other known techniques, such as photolithography, which produce regular arrays of features rather than the scattered distribution produced by island lithography.
[0029] FIG. 1 is a schematic view of a structured electrode, in accordance with the invention and as used in the following tests, it shows a part sectional view of the anode in which the pillars 2 can clearly be seen on the silicon wafer 3.
[0030] FIG. 6 shows a lithium battery, comprising a typical embodiment of the present invention, and including an anode 1, a cathode 4, a polymer electrolyte 5, a first strip 6 representing a rectifier circuit connected to a coil encircling the anode for charging purposes, a second strip 7 representing the output circuit (driven by the battery), and a pair of wires 8 for connection to the device to be driven.
[0031] Electrochemical tests were performed in a three-electrode, glass, cell where the Si sample is the working electrode and metallic Li is used for both the counter and reference electrodes. A 1 M solution of LiClO4 (Merck Selectipurâ) in ethylene carbonate:diethyl carbonate (Merck Selectipurâ), (1:1) w/w solvent was used as the electrolyte. The cell was assembled under a dry argon atmosphere in a glove box. Ohmic contact was made to the rear side of the silicon samples electrodes using a 1:1 In—Ga eutectic alloy12. The electrode area was delineated using an O-ring configuration in a PTFE holder. No adhesive is used and a good electrolyte/atmosphere seal is obtained. In an earlier study we found that epoxy adhesive, used to mount a Si electrode, contaminated the active electrode surface causing spurious currents at high voltages (>2V).
[0032] Electrochemical behaviour of the cell was investigated by cyclic voltammetry (CV) and by galvanostatic measurement (voltage vs. time at constant current), using an electrochemical workstation (VMP PerkinElmer™ Instruments). The capacity referred to here is the total charge inserted into the projected electrode surface area exposed to the electrolyte (this ignores any surface area due to structuring), given as mAhcm−2 (micro Amp hours cm−2).
[0033] The results obtained were:
[0034] The response of the Li|Li+-electrolyte|Si cell was measured: for this cell the cathodic process is, discharge of lithium onto silicon to form an alloy (charging), and the anodic process is lithium extraction or de-alloying (discharging). FIG. 2 shows one series of CV scan sets (details in caption). The first cycle, and to quite a large extent the second, differs from those that follow. It is conjectured that this difference is due to a “formation” effect, associated with the filming of the electrode during the first Li discharge. After the first and second cycles, the scans assume a repeatable general shape. Since these are scans in which the potential is changed slowly and the current densities are therefore small, there are no IR drop or diffusion overpotential terms, and assuming no activation overpotential, the electrode potential is a measure of the surface lithium activity. The first cathodic feature is the rapid increase in current at ˜330 mV that, according to room temperature data7, corresponds to the presence of Li12Si7. The lowest potential reached is 25 mV and this is taken to be associated with the presence of higher Li compounds, e.g. Li21Si5. The cycling sequence shows a progressive “activation” of the sample, associated with increasing breakdown of the crystalline silicon structure (see discussion). The anodic, part of the CV curve is associated with progressive de-lithiation of the electrode according to the various ZPC equilibrium potentials. For a scan rate of 1 mVs−1 the capacity (260 mAhcm−2) of the electrodes is roughly comparable to the pillar volume being converted to Li12Si7, while for the slower scan rates the capacity exceeds that of the pillar volume. The latter results point to the participation of the substrate in the alloying/de-alloying process.
[0035] FIG. 3 shows the results for a series of galvanostratic measurements on structured Si at two different charge/discharge current densities (details in caption).
[0036] FIG. 4 shows the structure of the K-series of silicon electrodes that were used in this study and the effects of extensive galvanostatic cycling upon that structure. The structure are clearly intact, but at the higher current density slight cracking of the bulk Si surface, below the pillars, is observed.
[0037] FIG. 5 shows the SEM pictures of the structures obtained on planar (un-pillared) Si electrodes before cycling and, separately, after galvanostatic cycling. When cycled at the lower current densities, the surface is deformed, though crack formation does not occur. Cycling at higher current densities produces wide cracks.
References
- [0038] 1. (a): R. A. Sharma and R. N. Seefurth, J. Electrochem. Soc., 123, 1763 (1976); (b): B. A. Boukamp, G. C. Lash and R. A. Huggins, J. Electrochem. Soc., 128, 725 (1981); (c): R. A. Huggins, Lithium Alloy Anodes in “Handbook of Battery Materials”, J. O. Besenhard Ed, Wiley-VCH, Weinheim, 359 (1999); (d): S. Bourderau, T. Brousse and D. M. Schleich, J. Power Sources, 233, 81 (1999); (e): O. Z. Zhuo, Bo Bao and S. Sinha, U.S. Pat. No. 6,334,939 B1 Jan. 1, 2002: There are many other patents relating to the use of various host materials for Li anodes.
- [0039] 2. Hong Li, Xuejie Huang, Liquan Chen, Zhengang Wu and Yong Liang, Electrochem. Solid-State Lett., 2, 547 (1999).
- [0040] 3. J. O. Besenhard, J. Yang and M. Winter, J. Power Sources, 68, 87 (1997)
- [0041] 4. L. Y. Beaulieu, D. Larcher, R. A. Dunlap and J. R. Dahn, J. Electrochem. Soc., 147, 3206 (2000).
- [0042] 5. J. K. Niparko (Editor), “Cochlea Implants”, Pub., Lippincott Williams and Wilkins,
- [0043] Philadelphia, (2000)
- [0044] 6. C. J. Wen and R. A. Huggins, J. Solid State Chem., 37, 271 (1981).
- [0045] 7. W. J. Weydanz, M. Wohlfahrt-Mehrens and R. A. Huggins, J. Power Sources
- [0046] 81-82, 237 (1999).
- [0047] 8. J-P. Colinge, “Silicon-on-Insulator Technology: Materials to VLSI”,
- [0048] Kluwer Acad. Pub, Boston, Chapter 2, (1991).
- [0049] 9. Mino Green, M. Garcia-Parajo, F. Khaleque and R Murray, Appl. Phys. Lett.,
- [0050] 63, 264 (1993.)
- [0051] 10. Mino Green and Shin Tsuchiya, J. Vac. Sci. & Tech. B, 17, 2074 (1999).
- [0052] 11. Shin Tsuchiya, Mino Green and RRA Syms, Electrochem. Solid-State Lett,
- [0053] 3, 44 (2000).
- [0054] 12. L-C. Chen, M. Chen, T-H Tsaur, C Lien and C-C. Wan, Sensors and Actuators,
- [0055] A49, 115 (1995).
- [0056] 13. H. Li, X. Huang, L. Chen, G. Zhou, Z. Zhang, D. Yu, Y. J. Mo and N. Pei, Solid
- [0057] State Ionics, 135, 181 (2000).
- [0058] 14. “Properties of Silicon”, Pub. INSPEC, The Institution of Electrical Engineers,
- [0059] London, (1988): p. 461 for solubility; p. 455 for diffusion data.
- [0060] 15. B. E. Deal and A. S. Grove, J. Appl. Phys., 36, 3770 (1965).
- [0061] 16. L. Y. Beaulieu, K. W. Eberman, R. L. Turner, L. J Krause and J. R. Dahn,
- [0062] Electrochem. Solid-State Lett., 4, A137 (2001).
Claims
The invention claimed is:
1. An energy storage device comprising:
an anode comprising an array of sub-micron structures comprising silicon, on a substrate;
a cathode comprising lithium; and
a lithium-based electrolyte, arranged to form a battery.
2. A device according to claim 1 wherein the substrate comprises silicon.
3. A device according to claim 1 wherein the anode is arranged to tolerate the conditions occasioned by the volume changes caused by charging/discharging of the battery.
4. A device according to claim 1 wherein the anode is arranged to maintain structural integrity throughout a cycling of the battery.
5. A device according to claim 1 wherein the anode is arranged to withstand repeated volume expansion associated with alloying during use of the battery.
6. A device according to claim 1 wherein the array of sub-micron structures comprise an array of sub-micron pillars.
7. A device according to claim 6 wherein the pillars have a surface area of about 4 FH/d times the substrate area wherein F is the surface fractional coverage, H is the height of the pillar and d is the diameter of the pillar.
8. A device according to claim 6 in which the sub-micron pillars do not exceed a fractional coverage of 0.5 of the substrate.
9. A device according to claim 6 wherein the pillars are 0.1 to 1.0 microns in diameter and 1 to 10 microns in height.
10. A device according to claim 6 wherein the pillars are approximately 0.3 microns in diameter and 6 microns in height.
11. A device according to claim 1 in which the substrate comprises n-type silicon.
12. A device according to claim 1 made on a wafer-bonded silicon-on-insulator substrate.
13. A battery including an anode comprising: an array of sub-micron pillars comprising silicon fabricated on a substrate; and a lithium cathode, wherein a compound film is formed on the pillars in a charging step.
14. A battery according to claim 13 wherein the film is a Zintl-Phase Compound.
15. A battery according to claim 13 wherein the compound film is deformable so as not to give rise to significant stress-induced cracking during the volume change in a charging or discharging step.
16. The battery according to claim 13 wherein the substrate comprises silicon.
17. An electrode for a battery comprising sub-micron pillars comprising silicon supported on a substrate and arranged to form a battery with a lithium cathode and a lithium-based electrolyte.
18. The electrode according to claim 17 wherein the substrate comprises silicon.
19. An energy storage device comprising:
an anode comprising an array of submicron structures comprising silicon, supported on a substrate;
a cathode comprising lithium; and
an electrolyte comprising lithium.
Patent Citations (144)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3351445(A) | 1967-11-01 | Fielder et al. | Applicant |
| US4002541(A) | 1977-01-01 | Streander | Applicant |
| US4436796(A) | 1984-03-01 | Huggins et al. | Applicant |
| US4950566(A) | 1990-08-01 | Huggins et al. | Applicant |
| US5262021(A) | 1993-11-01 | Lehmann et al. | Applicant |
| US5907899(A) | 1999-06-01 | Dahn et al. | Applicant |
| US6022640(A) | 2000-02-01 | Takada et al. | Applicant |
| US6042969(A) | 2000-03-01 | Yamada et al. | Applicant |
| US6296969(B1) | 2001-10-01 | Yano et al. | Applicant |
| US6334939(B1) | 2002-01-01 | Zhou et al. | Applicant |
| US6337156(B1) | 2002-01-01 | Narang et al. | Applicant |
| US6353317(B1) | 2002-03-01 | Green et al. | Applicant |
| US6399177(B1) | 2002-06-01 | Fonash et al. | Examiner |
| US6916679(B2) | 2005-07-01 | Snyder et al. | Applicant |
| US7070632(B1) | 2006-07-01 | Visco et al. | Applicant |
| US7094499(B1) | 2006-08-01 | Hung | Applicant |
| US7147894(B2) | 2006-12-01 | Zhou et al. | Applicant |
| US7192673(B1) | 2007-03-01 | Ikeda et al. | Applicant |
| US7311999(B2) | 2007-12-01 | Kawase et al. | Applicant |
| US7318982(B2) | 2008-01-01 | Gozdz et al. | Applicant |
| US7348102(B2) | 2008-03-01 | Li et al. | Applicant |
| US7358011(B2) | 2008-04-01 | Fukuoka et al. | Applicant |
| US7378041(B2) | 2008-05-01 | Asao et al. | Applicant |
| US7425285(B2) | 2008-09-01 | Asao et al. | Applicant |
| US2001/0023986(A1) | 2001-09-01 | Mancevski | Applicant |
| US2001/0038125(A1) | 2001-11-01 | Ohyanagi et al. | Examiner |
| US2002/0192441(A1) | 2002-12-01 | Kalkan et al. | Examiner |
| US2003/0135989(A1) | 2003-07-01 | Huggins et al. | Applicant |
| US2003/0185743(A1) | 2003-10-01 | Ramasamy et al. | Examiner |
| US2004/0072067(A1) | 2004-04-01 | Minami et al. | Applicant |
| US2004/0185346(A1) | 2004-09-01 | Takeuchi et al. | Applicant |
| US2004/0197660(A1) | 2004-10-01 | Sheem et al. | Applicant |
| US2004/0224231(A1) | 2004-11-01 | Fujimoto et al. | Applicant |
| US2004/0241548(A1) | 2004-12-01 | Nakamoto et al. | Applicant |
| US2005/0042515(A1) | 2005-02-01 | Hwang et al. | Applicant |
| US2005/0079420(A1) | 2005-04-01 | Cho et al. | Applicant |
| US2005/0118503(A1) | 2005-06-01 | Honda et al. | Applicant |
| US2005/0191550(A1) | 2005-09-01 | Satoh et al. | Applicant |
| US2005/0193800(A1) | 2005-09-01 | DeBoer et al. | Applicant |
| US2005/0214644(A1) | 2005-09-01 | Aramata et al. | Applicant |
| US2006/0019115(A1) | 2006-01-01 | Wang et al. | Applicant |
| US2006/0019168(A1) | 2006-01-01 | Li et al. | Applicant |
| US2006/0024582(A1) | 2006-02-01 | Li et al. | Applicant |
| US2006/0057463(A1) | 2006-03-01 | Gao et al. | Applicant |
| US2006/0088767(A1) | 2006-04-01 | Li et al. | Applicant |
| US2006/0134516(A1) | 2006-06-01 | Im et al. | Applicant |
| US2006/0134518(A1) | 2006-06-01 | Kogetsu et al. | Applicant |
| US2006/0147800(A1) | 2006-07-01 | Sato et al. | Applicant |
| US2006/0154071(A1) | 2006-07-01 | Homma et al. | Applicant |
| US2006/0166093(A1) | 2006-07-01 | Zaghib et al. | Applicant |
| US2006/0175704(A1) | 2006-08-01 | Shimizu et al. | Applicant |
| US2006/0257307(A1) | 2006-11-01 | Yang | Applicant |
| US2006/0263687(A1) | 2006-11-01 | Leitner et al. | Applicant |
| US2006/0275663(A1) | 2006-12-01 | Matsuno et al. | Applicant |
| US2006/0275668(A1) | 2006-12-01 | Peres et al. | Applicant |
| US2006/0286448(A1) | 2006-12-01 | Snyder et al. | Applicant |
| US2007/0031733(A1) | 2007-02-01 | Kogetsu et al. | Applicant |
| US2007/0059598(A1) | 2007-03-01 | Yang | Applicant |
| US2007/0087268(A1) | 2007-04-01 | Kim et al. | Applicant |
| US2007/0099084(A1) | 2007-05-01 | Huang et al. | Applicant |
| US2007/0099085(A1) | 2007-05-01 | Choi et al. | Applicant |
| US2007/0105017(A1) | 2007-05-01 | Kawase et al. | Applicant |
| US2007/0117018(A1) | 2007-05-01 | Huggins | Applicant |
| US2007/0122702(A1) | 2007-05-01 | Sung et al. | Applicant |
| US2007/0148544(A1) | 2007-06-01 | Le | Applicant |
| US2007/0172732(A1) | 2007-07-01 | Jung et al. | Applicant |
| US2007/0184345(A1) | 2007-08-01 | Neudecker et al. | Applicant |
| US2007/0190413(A1) | 2007-08-01 | Lee et al. | Applicant |
| US2007/0202395(A1) | 2007-08-01 | Snyder et al. | Applicant |
| US2007/0207080(A1) | 2007-09-01 | Yang | Applicant |
| US2007/0207385(A1) | 2007-09-01 | Liu et al. | Applicant |
| US2007/0209584(A1) | 2007-09-01 | Kalynushkin et al. | Applicant |
| US2007/0218366(A1) | 2007-09-01 | Kalynushkin et al. | Applicant |
| US2007/0224508(A1) | 2007-09-01 | Aramata et al. | Applicant |
| US2007/0224513(A1) | 2007-09-01 | Kalynushkin et al. | Applicant |
| US2007/0238021(A1) | 2007-10-01 | Liu et al. | Applicant |
| US2007/0243469(A1) | 2007-10-01 | Kim et al. | Applicant |
| US2007/0264564(A1) | 2007-11-01 | Johnson et al. | Applicant |
| US2007/0264574(A1) | 2007-11-01 | Kim et al. | Applicant |
| US2007/0269718(A1) | 2007-11-01 | Krause et al. | Applicant |
| US2007/0277370(A1) | 2007-12-01 | Kalynushkin et al. | Applicant |
| US2008/0003496(A1) | 2008-01-01 | Neudecker et al. | Applicant |
| US2008/0003503(A1) | 2008-01-01 | Kawakami et al. | Applicant |
| US2008/0020281(A1) | 2008-01-01 | Kogetsu et al. | Applicant |
| US2008/0038638(A1) | 2008-02-01 | Zhang et al. | Applicant |
| US2008/0090149(A1) | 2008-04-01 | Sano et al. | Applicant |
| US2008/0096110(A1) | 2008-04-01 | Bito et al. | Applicant |
| US2008/0107967(A1) | 2008-05-01 | Liu et al. | Applicant |
| US2008/0113271(A1) | 2008-05-01 | Ueda et al. | Applicant |
| US2008/0118834(A1) | 2008-05-01 | Yew et al. | Applicant |
| US2008/0124631(A1) | 2008-05-01 | Fukui et al. | Applicant |
| US2008/0131782(A1) | 2008-06-01 | Hagiwara et al. | Applicant |
| US2008/0138710(A1) | 2008-06-01 | Liaw et al. | Applicant |
| US2008/0138716(A1) | 2008-06-01 | Iwama et al. | Applicant |
| US2008/0145752(A1) | 2008-06-01 | Hirose et al. | Applicant |
| US2008/0145759(A1) | 2008-06-01 | Sung et al. | Applicant |
| US2008/0160415(A1) | 2008-07-01 | Wakita et al. | Applicant |
| US2008/0176139(A1) | 2008-07-01 | White et al. | Applicant |
| US2008/0206631(A1) | 2008-08-01 | Christensen et al. | Applicant |
| US2008/0206641(A1) | 2008-08-01 | Christensen et al. | Applicant |
| US2008/0233479(A1) | 2008-09-01 | Sung et al. | Applicant |
| US2008/0233480(A1) | 2008-09-01 | Sung et al. | Applicant |
| DE10347570(A1) | 2005-05-01 | Applicant | |
| EP820110(A2) | 1998-01-01 | Applicant | |
| EP1011160(A1) | 2000-06-01 | Applicant | |
| EP936687(B1) | 2001-12-01 | Applicant | |
| EP1231654(A1) | 2002-08-01 | Applicant | |
| EP1258937(A1) | 2002-11-01 | Applicant | |
| EP1083614(B1) | 2003-05-01 | Applicant | |
| EP1313158(A2) | 2003-05-01 | Applicant | |
| EP1335438(A1) | 2003-08-01 | Applicant | |
| EP1289045(B1) | 2006-03-01 | Applicant | |
| EP1657769(A1) | 2006-05-01 | Applicant | |
| EP1850409(A1) | 2007-10-01 | Applicant | |
| EP1771899(B1) | 2008-02-01 | Applicant | |
| EP1657768(B1) | 2008-05-01 | Applicant | |
| FR2885913(B1) | 2007-08-01 | Applicant | |
| GB2395059(A) | 2004-05-01 | Applicant | |
| JP10-83817 | 1998-03-01 | Applicant | |
| JP10-199524 | 1998-07-01 | Applicant | |
| JP2001-291514 | 2001-10-01 | Applicant | |
| JP2002-313319(A) | 2002-10-01 | Applicant | |
| JP2003-017040 | 2003-01-01 | Applicant | |
| JP2003-168426 | 2003-06-01 | Applicant | |
| JP2004-296386(A) | 2004-10-01 | Applicant | |
| NL1015956 | 2000-08-01 | Applicant | |
| WO99/33129 | 1999-07-01 | Applicant | |
| WO1/13414(A1) | 2001-02-01 | Applicant | |
| WO1/35473(A1) | 2001-05-01 | Applicant | |
| WO1/96847(A1) | 2001-12-01 | Applicant | |
| WO2/47185(A2) | 2002-06-01 | Applicant | |
| WO3/063271(A1) | 2003-07-01 | Applicant | |
| WO3/075372(A2) | 2003-09-01 | Applicant | |
| WO2004/042851(A2) | 2004-05-01 | Applicant | |
| WO2004/052489(A2) | 2004-06-01 | Applicant | |
| WO2004/083490(A2) | 2004-09-01 | Applicant | |
| WO2006/073427(A2) | 2006-07-01 | Applicant | |
| WO2006/120332(A2) | 2006-11-01 | Applicant | |
| WO2007/044315(A1) | 2007-04-01 | Applicant | |
| WO2007/083155(A1) | 2007-07-01 | Applicant | |
| WO2007/114168(A1) | 2007-10-01 | Applicant | |
| WO2008/029888(A1) | 2008-03-01 | Applicant | |
| WO2008/044683(A1) | 2008-04-01 | Applicant | |
| WO2008/072460(A1) | 2008-06-01 | Applicant |
Non-Patent Literature (53)
- Badel et al., “Formation of Ordered Pore Arrays at the Nanoscale by Electrochemical Etching of N-Type Silicon”, Superlattices and Microstructures, 36 (2004) 245-253.Applicant
- Beaulieu et al., “Colossal Reversible Volume Changes in Lithium Alloys”, Electrochemical and Solid-State Letters, 4 (9) (2001) A137-A140.Applicant
- Beaulieu et al., “Reaction of Li with Grain-Boundary Atoms in Nanostructured Compounds”, Journal of the Electrochemical Society, 147 (9) (2000) 3206-3212.Applicant
- Besenhard et al., “Will Advanced Lithium-Alloy Anodes Have a Chance in Lithium-Ion Batteries?”, Journal of Power Sources, 68 (1997) 87-90.Applicant
- Boukamp et al., “All-Solid Lithium Electrodes with Mixed-Conductor Matrix”, J. Electrochem. Soc.: Electrochemical Science and Technology, vol. 128, No. 4, (1981) 725-729.Applicant
- Bourderau, et al., “Amorphous Silicon as a Possible Anode Material for Li-Ion Batteries”, Journal of Power Sources, 81-82 (1999) 233-236.Applicant
- Colinge, Jean-Pierre, “Silicon-on-Insulator Technology: Materials to VLSI”, Chapter 2, SOI Materials, (1991), Cover page and p. 38.Applicant
- Deal et al., “General Relationship for the Thermal Oxidation of Silicon”, Journal of Applied Physics, vol. 36, No. 12, (Dec. 1965) 3770-3778.Applicant
- Feng et al., “Lithography-Free Silicon Micro-Pillars as Catalyst Supports for Microfabricated Fuel Cell Applications”, Electrochemistry Communications, 8 (2006) 1235-1238.Applicant
- Green et al., “Quantum Pillar Structures on n+ Gallium Arsenide Fabricated Using “Natural” Lithography”, Appl. Phys. Lett., 62 (3) (1993) 264-266.Applicant
- Green et al., “Structured Silicon Anodes for Lithium Battery Applications”, Electrochemical and Solid-State Letters, 6 (5) (2003) A75-A79.Applicant
- Green et al., “Mesoscopic Hemisphere Arrays for use as Resist in Solid State Structure Fabrication”, J. Vac. Sci. Technol. B 17(5) (1999) 2074-2083.Applicant
- Yan et al., “Growth of Amorphous Silicon Nanowires via a Solid-Liquid-Solid Mechanism”, Chemical Physics Letters, 323 (2000) 224-228.Applicant
- Shin et al., “Porous Silicon Negative Electrodes for Rechargeable Lithium Batteries”, Journal of Power Sources, 139 (2005) 314-320.Applicant
- Li et al., “A High Capacity Nano-Si Composite Anode Material for Lithium Rechargeable Batteries”, Electrochemical and Solid-State Letters, 2 (11) (1999) 547-549.Applicant
- Li et al., “The Crystal Structural Evolution of Nano-Si Anode Caused by Lithium Insertion and Extraction at Room Temperature”, Solid State Ionics, 135 (2000) 181-191.Applicant
- Huggins, Robert A., “Lithium Alloy Anodes” in Handbook of Battery Materials, J.O. Besenhard Ed., Wiley-VCH, Weinheim, 361-381 (1999).Applicant
- Chang et al., “Ultrafast Growth of Single-Crystalline Si Nanowires”, Materials Letters, 60 (2006) 2125-2128.Applicant
- Kim et al., “Improvement of Silicon Powder Negative Electrodes by Copper Electroless Deposition for Lithium Secondary Batteries”, Journal of Power Sources, 147 (2005) 227-233.Applicant
- Jianfeng et al., “Large-Scale Array of Highly Oriented Silicon-Rich Micro/Nanowires Induced by Gas Flow Steering”, Solid State Communications, 133 (2005) 271-275.Applicant
- Lu et al., “A Study of the Mechanisms of Erosion in Silicon Single Crystals Using Hertzian Fracture Tests”, Wear, 186-187 (1995) 105-116.Applicant
- Kleimann et al., “Formation of Wide and Deep Pores in Silicon by Electrochemical Etching”, Materials Science and Engineering, B69-70 (2000) 29-33.Applicant
- Kolasinski, Kurt W., “Silicon Nanostructures from Electroless Electrochemical Etching”, Current Opinion in Solid State and Materials Science, 9 (2005) 73-83.Applicant
- Pei et al., “Silicon Nanowires Grown from Silicon Monoxide Under Hydrothermal Conditions”, Journal of Crystal Growth, 289 (2006) 423-427.Applicant
- Chen et al., “Selective Etching of Silicon in Aqueous Ammonia Solution”, Sensors and Actuators, A 49 (1995) 115-121.Applicant
- Maranchi et al., “Interfacial Properties of the a-Si/Cu:Active-Inactive Thin-Film Anode Systems for Lithium-Ion Batteries”, Journal of the Electrochemical Society: 153 (6) (2006) A1246-A1253.Applicant
- Nakahata et al., “Fabrication of Lotus-Type Porous Silicon by Unidirectional Solidification in Hyrdogen”, Materials Science and Engineering A 384 (2004) 373-376.Applicant
- Niparko, J.K. (Editor), “Cochlear Implant Technology”, Pub., Lippincott Williams and Wilkins, Philadelphia, (2000) 108-121.Applicant
- Ohara et al., “A Thin Film Silicon Anode for Li-Ion Batteries Having a Very Large Specific Capacity and Long Cycle Life”, Journal of Power Sources, 136 (2004) 303-306.Applicant
- Peng et al., “Dendrite-Assisted Growth of Silicon Nanowires in Electroless Metal Deposition”, Adv. Funct. Mater., 13, No. 2 (2003) 127-132.Applicant
- Peng et al., “Synthesis of Large-Area Silicon Nanowire Arrays via Self-Assembling Nanoelectrochemistry”, Adv. Mater., 14, No. 16 (2002) 1164-1167.Applicant
- Peng et al., “Uniform, Axial-Orientation Alignment of One-Dimensional Single-Crystal Silicon Nanostructure Arrays”, Angew. Chem. Ind. Ed., 44 (2005) 2737-2742.Applicant
- Peng et al., “Simultaneous Gold Deposition and Formation of Silicon Nanowire Arrays”, Journal of Electroanalytical Chemistry, 558 (2003) 35-39.Applicant
- Canham, L. T., “Diffusion of Li IN Si”, Properties of Silicon, EMIS Datareviews Series No. 4 (1987) 454-462.Applicant
- Qiu et al., “Self-Assembled Growth and Optical Emission of Silver-Capped Silicon Nanowires”, Applied Physics Letters, vol. 84, No. 19, (2004) 3867-3869.Applicant
- Kim et al., “(110) Silicon Etching for High Aspect Ratio Comb Structures”, 1997 6th International Conference on Emerging Technologies and Factory Automation Proceedings, (1997) 248-252.Applicant
- Sharma et al., “Thermodynamic Properties of the Lithium-Silicon System”, J. Electrochem. Soc.: Electrochemical Science and Technology, vol. 123 (1976) 1763-1768.Applicant
- Qiu et al., “From S1 Nanotubes to Nanowires: Synthesis, Characterization, and Self-Assembly”, Journal of Crystal Growth, 277 (2005) 143-148.Applicant
- Tokoro et al., “Anisotropic Etching Properties of Silicon in KOH and TMAH Solutions”, Proceedings of the 1998 International Symposium on Micromechatronics and Human Science (1998) 65-70.Applicant
- Tsuchiya et al., “Structural Fabrication Using Cesium Chloride Island Arrays as a Resist in a Fluorocarbon Reactive Ion Etching Plasma”, Electrochemical and Solid-State Letters, 3 (1) (2000) 44-46.Applicant
- Wagner et al., “Vapor-Liquid-Solid Mechanism of Single Crystal Growth”, Applied Physics Letters, vol. 4, No. 5 (1964) 89-90.Applicant
- Lang, Walter, “Silicon Microstructuring Technology”, Materials Science and Engineering, R17 (1996) 1-55.Applicant
- Liu et al., “Effect of Electrode Structure on Performance of Si Anode in Li-Ion Batteries: Si Particle Size and Conductive Additive”, Journal of Power Source, 140 (2005) 139-144.Applicant
- Wen et al., “Chemical Diffusion in Intermediate Phases in the Lithium-Silicon System”, Journal of Solid State Chemistry, 37 (1981) 271-278.Applicant
- Weydanz et al., “A Room Temperature Study of the Binary Lithium-Silicon and the Ternary Lithium-Chromium-Silicon System for use in Rechargeable Lithium Batteries”, Journal of Power Sources, 81-82 (1999) 237-242.Applicant
- Yan et al., “H2-Assisted Control Growth of Si Nanowires”, Journal of Crystal Growth, 257 (2003) 69-74.Applicant
- Liu et al., “A Novel Method of Fabricating Porous Silicon Material: Ultrasonically Enhanced Anodic Electrochemical Etching”, Solid State Communications, 127 (2003) 583-588.Applicant
- Zhang et al., “Bulk-Quantity Si Nanowires Synthesized by SiO Sublimation”, Journal of Crystal Growth, 212 (2000) 115-118.Applicant
- Wong et al., “Controlled Growth of Silicon Nanowires Synthesized Via Solid-Liquid-Solid Mechanism”, Science and Technology of Advanced Materials, 6 (2005) 330-334.Applicant
- Zhang et al., “Synthesis of Thin Si Whiskers (Nanowires) Using SiCl4”, Journal of Crystal Growth, 2006 (2001) 185-191.Applicant
- Yoshio et al., “Electrochemical Behaviors of Silicon Based Anode Material”, Journal of Power Sources, 153 (2006) 375-379.Applicant
- Zhang et al., “Catalytic Growth of x-FiSi2 and Silicon Nanowires”, Journal of Crystal Growth, 280 (2005) 286-291.Applicant
- Japanese Search Report dated Sep. 24, 2009.Applicant