Flexible monolayer elastomer films and bag for medical use

[0001] This application is a 371 of PCT/US02/02624, filed Jan. 31, 2002; which claims priority from U.S. Provisional Applications 60/265,324, filed Feb. 1, 2001; 60/265,325, filed Feb. 1, 2001; 60/265,326, filed Feb. 1, 2001; 60/265,882, filed Feb. 5, 2001; and 60/265,883, filed Feb. 5, 2001; the entire disclosures of each of which are herein incorporated by reference.

[0002] The present invention relates to the field of flexible monolayer elastomer films, and more particularly, to an improved elastomer film for medical uses, such as disposable medical devices.

[0003] An important aim of ongoing research in the disposable medical device industry is to provide soft, non-tacky packaging suitable for contact with human skin without the use of plasticizers. A further aim of ongoing research is to provide flexible packaging for biological and pharmaceutical materials, which does not become brittle while undergoing liquid nitrogen storage.

[0004] Films used in the fabrication of disposable medical devices require several specific attributes. Among the attributes are clarity, ability to seal using radio frequency (RF), flexibility, conformance to United States Pharmacopoeia (USP) Class VI and European Pharmacopoeia 3^rd edition 3.1.6 test protocol, extremely low levels of extractables, excellent barriers to water vapor transmission, permeability to gases, resistance to change during sterilization via autoclaving, gamma radiation, or ethylene oxide, and, as required, compatibility with medical products contained in the disposable medical device. In addition, it is desirable that the films have a soft, non-tacky texture because they will come in contact with human skin.

[0005] In certain applications, it is required that the disposable medical devices be capable of prolonged storage in liquid nitrogen. A film that remains flexible and does not become brittle when stored in liquid nitrogen is required for storage of biological products, such as stem cells and bone marrow.

[0006] In addition, the film used for packaging medical products should have extremely low levels of extractable and leachable materials to avoid contamination of the stored material. For example, anti-cancer pharmaceuticals, such as taxol, are particularly prone to contamination by plasticizers, such as oils, leaching from conventional storage bags. In another example, extractable metals, such as aluminum, are unacceptable for peritoneal dialysis uses. Aluminum levels above about 11 ppb exacerbate certain illnesses, including anemia and encephalopathy.

[0007] Polyvinyl chloride (PVC) films conform to a number of these requirements and are conventionally used as a flexible medical product packaging material. PVC provides a relatively inexpensive, clear, soft, and flexible film for medical products packaging. In addition, PVC is relatively inert and contains low levels of extractable materials. However, to impart softness and flexibility to PVC films, plasticizers are added to PVC resins. The plasticizers are typically oils added in the hundreds of ppm range. While the amount of oil is acceptable for many medical end uses, plasticizer tends to leach from the film. The amount of plasticizer that leaches from the PVC film is unacceptable for storage of certain pharmaceuticals, such as the anti-cancer drug taxol.

[0008] PVC formulations also require a heat stabilizer to prevent the PVC from undergoing heat degradation and color change during and after processing. Heat stabilizers are extracted from the PVC by aqueous solutions stored in the bag.

[0009] Another important characteristic of biological packaging is gas permeability. Living cells, such as red blood cells and platelets, need to exchange oxygen and carbon dioxide. PVC gas permeability decreases as plasticizer levels decreases. Thus as the amount of plasticizer is increased to provide high gas permeability in PVC based medical bags, the amount of plasticizer used and the amount of plasticizer that leaches into the stored material also increases.

[0010] PVC is not suitable for liquid nitrogen storage of biological materials, such as stem cells or bone marrow. PVC becomes brittle when stored in liquid nitrogen.

[0011] Various replacements for PVC film as a component of disposable medical devices have been disclosed. U.S. Pat. No. 4,140,162 discloses clear, blow-moldable medical packaging. However, the disclosed composition comprises an antioxidant material and Kraton G, a styrene-ethylene-butylene-styrene copolymer (SEBS). SEBS is tacky and rubbery and does not provide the soft PVC-like texture desired for human skin contact.

[0012] U.S. Pat. No. 4,440,815 discloses a clear, flexible, thermoplastic medical liquid container comprising a mixture of SEBS, polypropylene, ethylene-lower alkyl acrylate polymer, and mineral oil. The mineral oil is added to improve clarity and flexibility. However, mineral oil is susceptible to leaching and subsequent contamination of the material stored in the medical liquid container.

[0013] U.S. Pat. No. 4,814,375 discloses a soft, high strength elastomeric composition for use in medical and pharmaceutical products comprising SEBS, a mineral oil plasticizer to soften the SEBS, and an acrylic resin.

[0014] U.S. Pat. No. 4,479,989 discloses a film material for use in sterilized medical solution containers comprising linear low-density polyethylene (LLDPE) and SEBS.

[0015] U.S. Pat. No. 6,017,598 discloses a medical bag comprising multiple polymer film layers, wherein one of the layers comprises a matrix comprising a block copolymer, such as SEBS, and a polyolefin.

[0016] EP 0 740 544 B1 discloses a plastic formulation for a storage container for blood components comprising an ethylene-vinyl acetate copolymer (EVA), SEBS, and ultra-low density polyethylene (ULDPE).

[0017] The term “disposable medical devices” as used herein, is not to be limited to the specifically disclosed embodiments. Disposable medical devices, as used herein, includes storage containers for medical products, such as blood component bags, peritoneal dialysis sets, drainage collection bags, intravenous solution storage, and drug delivery systems.

[0018] The term “medical products” as used herein, is not to be limited to the specifically disclosed embodiments. Medical products, as used herein, includes nutritional products; biological products, such as stem cells, blood components, and bone marrow; and pharmaceutical products, such as peritoneal dialysis solutions and drugs, such as taxol.

[0019] The term “essentially free of leachable material”, as used herein, means there is either no leachable material in the flexible monolayer elastomer film or the amount of leachable material is so low as to not adversely affect the medical products stored within disposable medical devices formed from the flexible monolayer elastomer film. No leachable materials, such as plasticizers, are added to the elastomer film material. The flexible monolayer elastomer films meet the European Pharmacopoeia 3^rd edition 3.1.6 and USP Class VI test protocols.

[0020] The term “texture”, as used herein, means the tactile quality of the surface of the flexible monolayer elastomer film.

[0021] The term “the texture being substantially that of plasticized polyvinyl chloride”, as used herein, means that the texture of the flexible monolayer elastomer film is like that of plasticized polyvinyl chloride films conventionally used in disposable medical devices, such as the films in Comparative Examples 1-5 of the instant disclosure.

[0022] There exists a need in the disposable medical device art to provide a medical product packaging material, which has a texture like that of plasticized polyvinyl chloride and is free of any leachable material, such as plasticizer. There exists a need in this art to provide medical product packaging material that can be stored in liquid nitrogen without becoming brittle. There exists a need in this art to provide a medical product packaging material that can be sterilized by autoclaving, irradiation, or ethylene oxide. There exists a need in this art to provide an economical medical product packaging material that is heat welded or radio frequency (RF) welded to form a flexible, monolayer, gas-permeable, elastomer bag for storing liquid medical products.

[0023] These and other needs are met by embodiments of the present invention, which provide a flexible monolayer elastomer film comprising a styrene-ethylene-propylene-styrene block copolymer. The film has a texture substantially that of plasticized polyvinyl chloride and the film is essentially free of leachable material.

[0024] The earlier stated needs are also met by certain embodiments of the instant invention which provide a flexible monolayer elastomer film comprising from about 55% to about 75% by weight of an ethylene-vinyl acetate copolymer and from about 25% to about 45% by weight of a metallocene catalyzed ethylene-octene copolymer. The film has a texture substantially that of plasticized polyvinyl chloride and the film is essentially free of leachable material.

[0025] The earlier stated needs are further met by certain embodiments of the instant invention including a flexible monolayer bag for storing medical products, wherein the bag is RF welded from a flexible monolayer elastomer film comprising a styrene-ethylene-propylene-styrene block copolymer. The film has a texture substantially that of plasticized polyvinyl chloride and the film is essentially free of leachable material.

[0026] The earlier stated needs are further met by certain embodiments of the instant invention including a flexible monolayer bag for storing medical products, wherein the bag is formed from a flexible monolayer elastomer film comprising from about 55% to about 75% by weight of an ethylene-vinyl acetate copolymer and from about 25% to about 45% by weight of a metallocene catalyzed ethylene-octene copolymer. The film has a texture substantially that of plasticized polyvinyl chloride and the film is essentially free of leachable material.

[0028] The present invention enables the production of disposable medical devices with improved inertness towards medical products stored therein, improved flexibility, improved gas permeability, and improved low temperature storage properties. The present invention provides soft plasticized polyvinyl chloride-like texture without the use of leachable plasticizers and surfactants. The present invention further provides a gas permeable disposable medical device which main remains flexible when stored in liquid nitrogen. These benefits are provided by a flexible monolayer elastomer film comprising a styrene-ethylene-propylene-styrene block copolymer (SEPS) that is essentially free of leachable materials. These benefits are also provided by a flexible monolayer elastomer film that is essentially free of leachable materials comprising an ethylene-vinyl acetate copolymer (EVA) and a metallocene catalyzed ethylene-octene copolymer.

[0029] The flexible monolayer elastomer film of the instant invention has a soft, flexible, dry feel similar to that of conventional plasticized PVC medical films. The flexible monolayer elastomer film of the instant invention has suppleness similar to that of conventional plasticized PVC medical films. The elastomer film of the instant invention also has excellent clarity. Disposable medical devices are easily fabricated from the film by radio frequency (RF) welding or heat welding enabling its use on current device manufacturing equipment. Certain embodiments of the flexible monolayer elastomer film of the instant invention can be sterilized by gamma radiation. There is minimal visual or physical property changes when the elastomer film is exposed to high levels of gamma radiation. Other certain embodiments of the flexible monolayer elastomer film of the instant invention can be sterilized by autoclaving. The film of the instant invention has excellent performance at low temperatures. Certain embodiments of the film of the instant invention remain flexible, and do not become brittle when stored in liquid nitrogen.

[0030] The absence of extractables exhibited by the flexible monolayer elastomer film of the instant invention makes it ideally suited for the most critical of device applications. No plasticizer or surfactants are added to the film of the instant invention. Therefore, the flexible monolayer elastomer film of the instant invention is free or at least essentially free of leachable materials, such as plasticizers. In addition, the film of the instant invention is resistant to most acids and bases.

[0031] The flexible monolayer elastomer films of the instant invention have excellent strength to thickness ratios. The excellent strength to thickness ratio allows for significant down gauging. For example, an article fabricated from a 0.009″ thick film of the instant invention will exhibit the strength and durability equivalent to a 0.014″ thick soft PVC film. The yield for a 0.009″×12″ films of the instant invention is 7.8 yards per pound. For comparison, a typical 0.014″×12″ PVC film has a yield of only 4.0 yards per pound.

[0032] The unique combination of properties of the film of the instant invention allows the film's use in applications such as intravenous solution storage, drug delivery, nutritional solutions, storage of blood components, stem cell storage, bone marrow storage, peritoneal dialysis, and drainage collection as well as many other critical end uses.

[0033] Certain embodiments of the flexible monolayer elastomer film of the instant invention can be manufactured in thicknesses ranging from 0.006″ to 0.020″ at widths up to 34″ and with surface finishes of polish/matte, taffeta/matte or matte/matte. Typical tolerance for the film thickness is +/−0.001″ and +/−0.125″ for the film width.

[0034] Certain embodiments of the flexible monolayer elastomer film of the instant invention are specially formulated to meet USP Class VI and European Pharmacopoeia requirements.

[0035] In certain embodiments of the flexible monolayer elastomer film of the instant invention, the film comprises SEPS. The film has a texture substantially that of plasticized polyvinyl chloride and the film is essentially free of leachable material. The film is essentially free of plasticizers, such as oils, and surfactants. In embodiments of the instant invention containing SEPS, the amount of SEPS in the film is from about 5% to about 90% by weight of the film. In certain embodiments, the amount of SEPS in the film is from about 15% to about 90% by weight of the film. In other certain embodiments the amount of SEPS in the film is from about 15% to about 25% of the weight of the film. A suitable SEPS for certain embodiments of the present invention is a medical grade SEPS, Hybrar® 7125, from Kuraray Co., Ltd.

[0036] The film of the instant invention can further comprise a polyolefin in an amount of about 5% to about 50% by weight of the film. In certain embodiments the amount of polyolefin is from about 14% to about 30% by weight of the film. Among the polyolefins in certain embodiments of the instant invention are: a metallocene catalyzed polyethylene-octene copolymer, a syndiotactic polypropylene, a polypropylene homopolymer, a polypropylene copolymer, a metallocene catalyzed isotactic polypropylene, a low-density polyethylene, and a linear low-density polyethylene.

[0037] Suitable polyolefins for certain embodiments of the instant invention include: Engage EG 8100 metallocene catalyzed saturated ethylene-octene extremely low density copolymer (VvLDPE) from Dow Plastics, Tenite 800A low density polyethylene (LDPE) from Eastman Chemical Company, EOD 96-30 and EOD 99-19 syndiotactic polypropylenes from Atofina Petrochemical, Inc., Dowlex 2045 linear low density polyethylene (LLDPE), Inspire H701-20NA polypropylene homopolymer and H707-12 polypropylene copolymer from Dow Plastics, 3727W Ziegler-Natta catalyzed polypropylene homopolymer, EOD 00-11 metallocene catalyzed isotactic polypropylene and EOD 96-30 syndiotactic polypropylene from Atofina Petrochemical, Inc.

[0038] The films of the instant invention can additionally comprise an ethylene-vinyl acetate copolymer (EVA) in an amount of from about 40% to about 90% by weight of the film. In certain embodiments, the amount of ethylene-vinyl acetate copolymer is from about 50% to about 65%. In certain embodiments, the amount of vinyl acetate in the ethylene-vinyl acetate copolymer is about 20% to about 28% by weight of the ethylene-vinyl acetate copolymer. In certain embodiments, the amount of vinyl acetate in the copolymer is about 28%.

[0039] Suitable ethylene-vinyl acetate copolymers for use in the films of the instant invention include Escorene Ultra LD 760 and Escorene Ultra LD 768 from ExxonMobil Chemicals, Ateva® 2803MG from AT Plastics, and Ultrathene® UE 634-000 from Equistar Chemicals.

[0040] The flexible monolayer elastomer films of the instant invention have high oxygen and carbon dioxide transmission rates and low water vapor transmission rates. The films of the instant invention containing SEPS have an oxygen transmission rate of from about 50 cm³/100 in²/24 hours to about 300 cm³/100 in²/24 hours, a carbon dioxide transmission rate of from about 300 cm³/100 in²/24 hours to about 2100 cm³/100 in²/24 hours, and a water vapor transmission rate of from about 0.05 g/100 in²/24 hours to about 1.25 g/100 in²/24 hours; for 0.006″ thick films. Certain embodiments of the film have an oxygen transmission rate of from about 140 cm³/100 in²/24 hours to about 250 cm³/100 in²/24 hours, a carbon dioxide transmission rate of from about 1050 cm³/100 in²/24 hours to about 1800 cm³/100 in²/24 hours, and a water vapor transmission rate of from about 0.38 g/100 in²/24 hours to about 1.25 g/100 in²/24 hours; for 0.006″ thick films.

[0041] In embodiments of the instant invention where the film comprises from about 55% to about 75% by weight of an ethylene-vinyl acetate copolymer and from about 25% to about 45% by weight of an metallocene catalyzed ethylene-octene copolymer the films, the film has an oxygen transmission rate of from about 100 cm³/100 in²/24 hours to about 600 cm³/100 in²/24 hours, a carbon dioxide transmission rate of from about 1000 cm³/100 in²/24 hours to about 5000 cm³/100 in²/24 hours, and a water vapor transmission rate of from about 1.7 g/100 in²/24 hours to about 2.7 g/100 in²/24 hours; for 0.006″ thick films. Certain embodiments of the films of the instant invention containing EVA and metallocene catalyzed ethylene-octene copolymer have an oxygen transmission rate of from about 300 cm³/100 in²/24 hours to about 400 cm³/100 in²/24 hours and a carbon dioxide transmission rate of from about 2500 cm³/100 in²/24 hours to about 3500 cm³/100 in²/24 hours; for 0.006″ thick films.

[0042] The flexible monolayer elastomer films of the instant invention are formed by mixing the individual polymer components according to the weight fraction of each polymer component in the film. The ingredients of the film may be tumble-blended in a ribbon blender and then heated and fused into pellets. Films of the instant invention and articles are formed from the pellets by extrusion. Alternatively, articles can be formed from the pellets by molding.

[0043] Comparative Example 1 is EH-222 polyvinyl chloride film with trioctyl trimellitate (TOTM) plasticizer from Solvay Draka. Comparative Example 2 is EH-3125 polyvinyl chloride film with (TOTM) plasticizer from Solvay Draka. Comparative Example 3 is ES-3049 polyvinyl chloride film with tributyl citrate plasticizer from Solvay Draka. ES-3000 polyvinyl chloride film is di(2-ethyl hexyl) phthalate from Solvay Draka is Comparative Example 4. Medipak 3250 polyvinyl chloride film from Solvay Draka is Comparative Example 5. Comparative Example 6 is EVA-1800 from Solvay Draka.

[0044] Example 1 is an extruded monolayer film formed from a mixture of SEPS, EVA, syndiotactic polypropylene, and low-density polypropylene. The film consists of 50% by weight of an EVA containing about 28% by weight vinyl acetate, 20% by weight of Hybrar 7125F SEPS, 15% by weight Atofina Petrochemical EOD 96-30 syndiotactic polypropylene, and 15% by weight Engage 8100 metallocene catalyzed polyethylene-octene copolymer.

[0045] Example 2 is an extruded monolayer film formed from a mixture of SEPS, EVA, and extremely low-density polypropylene. The film consists of 50% by weight of an EVA containing about 28% by weight vinyl acetate, 20% by weight of Hybrar 7125F SEPS, and 30% by weight Engage 8100 metallocene catalyzed polyethylene-octene copolymer.

[0046] Example 3 is an extruded monolayer film formed from a mixture of SEPS, EVA, and syndiotactic polypropylene. The film consists of 65% by weight of an EVA containing about 28% by weight vinyl acetate, 21% by weight of Hybrar 7125F SEPS, and 14% by weight Atofina Petrochemical EOD 96-30 syndiotactic polypropylene.

[0047] Examples 1-3 have excellent clarity, with a light transmission of 89% and have only minimal visual or physical property changes when exposed to high levels of gamma radiation. Examples 1 and 2 have excellent low temperature properties and Example 2 has superior low temperature properties. Disposable medical devices are easily fabricated from the films of Examples 1-3 by RF welding or heat sealing.

[0048]

	TABLE I
	Comparative	Comparative	Comparative
	Example 1	Example 2	Example 3	Example 1	Example 2	Example 3
PHYSICAL PROPERTIES
Process	Calender	Calender	Calender	Extruder	Extruder	Extruder
RF Weldability	Yes	Yes	Yes	Yes	Yes	Yes
Thickness, mils.	15.0	15.0	15.0	6.0	9.0	6.0
Hardness, Shore A	71	68	67	71	67	70
Specific Gravity	1.20	1.19	1.19	0.90	0.92	0.91
Tensile Strength MD(TD), psi	2000(1800)	1800(1900)	2400(2400)	2580(2150)	3000(2600)	2300(2400)
Elongation MD(TD), %	300(300)	260(300)	330(330)	620(720)	640(700)	600(790)
Modulus MD(TD), Lbs./in.	1000(900)	1000(900)	1050(1050)	570(470)	440(380)	600(440)
Tear MD(TD), Lbs./in.	275(250)		220(220)	235(271)	239(261)	240(270)
Low Temp. Brittleness ° C.	−32	−34	−40	−75	−195	−70
GAS & WATER PROPERTIES:
WVTR (gms/100in2/24 Hrs.)@25° C.;		0.82	1.70	0.97	0.69	0.75
100% RH; 0.006″ thick
O2 Transmission (cm3/100in2/24 Hrs.)@25° C.;		78	143	241	186	205
0% RH; 0.006″ thick
CO2 Transmission (cm3/100in2/24 Hrs.)@25° C.;		412	1450	1770	1242	1551
0% RH; 0.006″ thick
STERILIZATION:
Gamma Resistance, Color Change	Minimal	Minimal	Minimal	Minimal	Minimal	Minimal
Steam, 121° C.	Yes	Yes	Yes	No	No	No
BIOSAFETY CONFORMITY:	NAmSA, ′01	NAmSA, ′01	NamSA, ′01	Toxikon, ′01	Toxikon, ′01	Toxikon, ′01
European Pharmacopoeia Protocol Testing(*)		Conforms		Conforms	Conforms
Biocompability Testing(**)	Pass	Pass	Pass	Pass	Pass	Pass
CHEMICAL PROPERTIES:
Reducing Substances	0.5	0.3	0.4	0.1	0.2	0.2
UV220	0.09	0.17	0.09	0.00	0.02	0.01
pH	5.6	6.0	5.9	6.0	6.1	5.9
pH Shift	0.4	0.1	0.1	0.2	0.2	0.1
Extractable Aluminum, ppm	0.01	0.00	0.00	0.01	0.01	0.00
Extractable Calcium, ppm	0.0	0.3	0.5	0.2	0.3	0.1
Extractable Zinc, ppm	0.7	0.7	1.3	0.0	0.0	0.0
(*)Conforms to the European Pharmacopoeia 3rd edition 3.1.6 test protocol.
(**)USP Class VI

[0049] The various physical characteristics displayed in Tables I, II, and III are determined via the test methods listed below.

[0050]

	Physical Characteristic	Test Method
	Durometer Hardness, Shore A	ASTM D-2240
	Specific Gravity	ASTM D-792
	Tensile Strength, psi	ASTM D-638
	Elongation at Break, %	ASTM D-638
	Modulus at 100% Elong. psi	ASTM D-638
	Tear Resistance, lbf/in.	ASTM D-1004
	Low Temperature Brittleness, ° C.	ASTM D-1790
	WVTR (gms/100 in2/24 Hrs.)@	ASTM E-96-80
	(25° C.; 100% RH); (0.006″ thick)
	Oxygen Transmission	ASTM D-3985
	(cm3/100 in2/24 Hrs.)@
	(25° C.; 0% RH); (0.006″ thick)
	Carbon Dioxide Trans.	ASTM D-1434
	(cm3/100 in2/24 Hrs.)@
	(25° C.; 0% RH); (0.006″ thick)
	European Pharmacopoeia Tests	Specification
	Reducing Substances, mg/20 ml	2.0 max.
	UV at 220 nm,	0.20 max.
	pH	5.0 to 7.0
	pH Shift	−1 to +1
	Extractable Aluminum, ppm	0 to 0.05
	Extractable Calcium, ppm	0 to 2.0
	Extractable Zinc, ppm	0 to 2.0

[0051] Example 4 is an extruded monolayer film formed from a mixture of SEPS and Ziegler-Natta catalyzed polypropylene. The film consists of 70% by weight of Hybrar 7125F SEPS, and 30% by weight Atofina Petrochemical 3727W polypropylene. The film of example 4 provides excellent clarity with a light transmission of 90%. The film of Example 4 can be easily fabricated by heat sealing and can be sterilized by gamma irradiation, ethylene oxide, or autoclaving at 121° C. In addition, the film of Example 4, has extremely low levels of extractable metals.

[0052]

TABLE II
	Comparative	Comparative
	Example 4	Example 5	Example 4
PHYSICAL PROPERTIES:
Process	Calender	Extruder	Extruder
RF Weldablity	Yes	Yes	No
Thickness, mils	15.0	14.0	10.0
Hardness, Shore A	75	80	70
Specific Gravity	1.23	1.24	0.91
Tensile Strength MD(TD), psi	2800(2600)	3600(3500)	2545(2771)
Elongation MD(TD), %	280(300)	340(390)	752(821)
Modulus MD(TD), psi	1250(1050)	1700(160O)	453(449)
Tear MD(TD), Lbs./in.	300(300)	550(520)	234(248)
Low Temp. Brittleness ° C.	−29	−26	−15
GAS & WATER PROPERTIES:
WVTR (gms/100 in2/24 Hrs.)	0.53	0.32	0.09
25° C.; 100% RH;
0.006″ thick
O2 Transmission	44	28	68
(cm3/100 in2/24 Hrs.)
25° C.; 0% RH; 0.006″ thick
CO2 Transmission	299	183	328
(cm3/100 in2/24 Hrs.)
25° C.; 0% RH; 0.006″ thick
STERILIZATION:
Gamma Resistance, Color Change	Minimal	Moderate	Slight
Steam, 121° C.	Yes	yes	Yes
BIOSAFETY CONFORMITY	NAmSA, '01	Toxikon, 100	Toxikon, '01
European Pharmacopoeia Protocol Testing(*)		Conforms
Bicompatibility Testing(**)	Pass	pass	Pass
CHEMICAL PROPERTIES:
Reducing Substances	0.3	1.0	0.2
UV220	0.09	0.12	0.01
pH	5.6	5.5	5.9
pH Shift	0.4	−0.2	0.0
Extractable Aluminum, ppm	0.01	0.00	0.00
Extractable Calcium, ppm	0.2	0.4	0.1
Extractable Zinc, ppm	0.6	1.0	0.0
(*)Conforms to tie European Pharmacopoeia 3rd edition 3.1.6 test protocol.
(**)USP Class VI

[0053] Example 5 is an extruded monolayer film formed from a mixture of EVA and extremely low density polyethylene. The film consists of 65% by weight of an EVA containing about 28% by weight vinyl acetate, and 35% by weight Engage 8100 metallocene catalyzed polyethylene-octene copolymer. Example 5 provides superior low temperature properties, and excellent clarity with a light transmission of 91%. The film of Example 5 can be easily fabricated by RF welding or heat sealing. Extremely high oxygen and carbon dioxide transmission is provided by the film of Example 5. In addition, the film of Example 5, has extremely low levels of extractable metals.

[0054] The Exemplary films and the Comparative Examples underwent in vitro and in vivo testing by independent labs, such as NAmSA and Toxikon to demonstrate compliance with biomedical safety standards. The following tests, in accordance with USP and European ISO 10993 protocols were performed:

[0055] ISO Intracutaneous Reactivity, Part 10

[0056] ISO Systemic Toxicity, Part 11

[0057] ISO Muscle Implantation with Hystopathology, Part 6

[0058] ISO Hemolysis in Vitro, Part 4

[0059] ISO Cytotoxicity (MEM Extraction), Part 5.

[0060] USP Physico-Chemical Tests

[0061] USP LAL Endotoxin Test in Vitro.

The films of Examples 1-5 passed all of the above-listed biomedical safety standards.

[0062]

TABLE III
	Comparative	Comparative
	Example 4	Example 5	Example 4
PHYSICAL PROPERTIES:
Process	Calender	Extruder	Extruder
RF Weldability	Yes	Yes	Yes
Thickness, mils.	15.0	14.0	6.0
Hardness, Shore A	75	90	70
Specific Gravity	1.23	0.939	0.92
Tensile Strength MD(TD), psi	2800(2600)	2550(2500)	3000(2800)
Elongation MD(TD), %	280(300)	400(700)	600(700)
Modulus MD(TD), Lbs./in.	1250(1050)	980(860)	630(480)
Tear MD(TD), Lbs./in.	300(300)	4(5)	280(280)
Low Temp. Brittleness ° C.	−29	−59	−195
GAS & WATER PROPERTIES:
WVTR (gms/100 in2/24 Hrs.)
@25° C.; 100% RH;
0.006″ thick	0.53	0.30	2.2
O2 Transmission	44	73	359
(cm3/100 in2/24 Hrs.)
@25° C.; 0% RH;
0.006″ thick
CO2 Transmission	299	386	2,954
(cm3/100 in2/24 Hrs.)
@25° C.; 0% RH;
0.006″ thick
STERILIZATION:
Gamma Resistance, Color Change	Minimal	Minimal	Slight
Steam, 121° C.	Yes	No	No
BIOSAFETY CONFORMITY:	NAmSA, '01	NAmSA, '97	Toxikon, '01
European Pharmacopoeia Protocol Testing(*)			Conforms
Biocompability Testing(**)	Pass	Pass	Pass
CHEMICAL PROPERTIES:
Reducing Substances	0.3	0.1	0.3
UV220	0.09	0.04	0.02
pH	5.6	4.7	6.0
pH Shift	0.4	−1.0	0.1
Extractable Aluminum, ppm	0.01	0.00	0.00
Extractable Calcium, ppm	0.2	0.0	0.1
Extractable Zinc, ppm	0.6	0.0	0.0
(*)Conforms to the European Pharmacopoeia 3rd edition 3.1.6 test protocol.
(**)USP Class VI

[0063] Other embodiments of the flexible monolayer elastomer film of the instant invention include a film consisting of 60% by weight of an EVA containing about 28% by weight vinyl acetate, 20% by weight of Hybrar 7125F SEPS, and 20% by weight of Tenite 800A LDPE. Another embodiment consists of 60% by weight of an EVA containing about 28% by weight vinyl acetate, 20% by weight of Hybrar 7125F SEPS, and 20% by weight of Atofina Petrochemical EOD 99-19 syndiotactic polypropylene. Other embodiments consist of 50% by weight of an EVA containing about 28% by weight vinyl acetate, 20% by weight of Hybrar 7125F SEPS, and 15% by weight of Atofina Petrochemical EOD 65-30 syndiotactic polypropylene, and 15% by weight of Dowlex 2045 LLDPE; 70% by weight of Hybrar 7125F SEPS and 30% by weight of Dow Inspire H701-20NA polypropylene or H707-12 polypropylene copolymer; 80% by weight of Hybrar 7125F SEPS and 20% by weight Dow Inspire H701-20NA polypropylene or H707-12 polypropylene copolymer; and 85% by weight of Hybrar 7125F SEPS and 15% by weight Atofina Petrochemical 3727W Ziegler-Natta catalyzed polypropylene or EOD 00-11 metallocene catalyzed isotactic polypropylene.

[0064] FIG. 1 embodies one aspect of the instant invention. Disposable medical devices, such as the blood component bag 10 of FIG. 1 are formed by heat sealing or RF welding monolayer films of the instant invention. Blood component bag 10 comprises a connector 12 connected to a length of flexible tubing 14, through which the blood components are introduced into the blood component bag 10. The tubing 14 may contain a phlebotomy needle (not shown) at its terminal end or may be connected to another container (not shown). The blood component bag 10 additionally comprises one or more sealable access ports 16. The connector 12, flexible tubing 14, access ports 16, and bag walls 18 are all made from the flexible monolayer elastomer film of the instant invention.

[0065] The flexible bag 10 of the instant invention is formed by RF welding or heat sealing the monolayer elastomer walls 18 of the bag 10 along the edges 20. Certain embodiments of the flexible bag 10 can be stored in liquid nitrogen without becoming brittle. Other embodiments of blood component bag 10 have excellent high temperature properties and can be sterilized by autoclaving at a temperature of about 121° C. or higher. Alternatively, the flexible bag 10 can be sterilized by gamma radiation or ethylene oxide.

[0066] The embodiments described in the instant disclosure are for illustrative purposes only. They should not be construed to limit the scope of the claims. As is clear to one of ordinary skill in the art, the instant disclosure encompasses a wide variety of embodiments not specifically described herein.