US 7,521,365 B2Grant
Selective epitaxy process with alternating gas supply
Issue Date:2009-04-21
•10 Claims
•5 Drawing Sheets
Abstract
In one example, a method of epitaxially forming a silicon-containing material on a substrate surface is presented which includes positioning a substrate into a process chamber. The substrate has a monocrystalline surface and at least a second surface, such as an amorphous surface and/or a polycrystalline surface. The substrate is exposed to a deposition gas to deposit an epitaxial layer on the monocrystalline surface and a polycrystalline layer on the second surface. The deposition gas preferably contains a silicon source and at least a second elemental source, such as a germanium source, a carbon source and/or combinations thereof. Thereafter, the method further provides exposing the substrate to an etchant gas to etch the polycrystalline layer and the epitaxial layer in a manner such that the polycrystalline layer is etched at a faster rate than the epitaxial layer. The method may further include a deposition cycle that includes repeating the exposure of the substrate to the deposition and etchant gases to form a silicon-containing material with a predetermined thickness.
Metadata
Assignee
- Applied Materials, Inc.
Inventors
- Yihwan Kim
- Arkadii V. Samoilov
Application Information
Application Number:US 11/421,156
Filing Date:2006-05-31
Priority Date:2004-12-01
Art Unit:1792
Classifications
IPC:
H01L21/302
Patent Drawings (5 sheets)
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application is a divisional application of U.S. patent application Ser. No. 11/001,774, filed Dec. 1, 2004, and issued as U.S. Pat. No. 7,312,128, which application is incorporated by reference herein.
BACKGROUND OF THE INVENTION
[0002] 1. Field of the Invention
[0003] Embodiments of the invention generally relate to the field of electronic manufacturing processes and devices, more particular, to methods of depositing silicon-containing films while forming electronic devices.
[0004] 2. Description of the Related Art
[0005] As smaller transistors are manufactured, ultra shallow source/drain junctions are becoming more challenging to produce. Generally, sub-100 nm CMOS (complementary metal-oxide semiconductor) devices require a junction depth to be less than 30 nm. Selective epitaxial deposition is often utilized to form epilayers of silicon-containing materials (e.g., Si, SiGe and SiC) into the junctions. Generally, selective epitaxial deposition permits growth of epilayers on silicon moats with no growth on dielectric areas. Selective epitaxy can be used within semiconductor devices, such as elevated source/drains, source/drain extensions, contact plugs or base layer deposition of bipolar devices.
[0006] Generally, a selective epitaxy process involves a deposition reaction and an etch reaction. The deposition and etch reactions occur simultaneously with relatively different reaction rates to an epitaxial layer and to a polycrystalline layer. During the deposition process, the epitaxial layer is formed on a monocrystalline surface while a polycrystalline layer is deposited on at least a second layer, such as an existing polycrystalline layer and/or an amorphous layer. However, the deposited polycrystalline layer is generally etched at a faster rate than the epitaxial layer. Therefore, by changing the concentration of an etchant gas, the net selective process results in deposition of epitaxy material and limited, or no, deposition of polycrystalline material. For example, a selective epitaxy process may result in the formation of an epilayer of silicon-containing material on a monocrystalline silicon surface while no deposition is left on the spacer.
[0007] Selective epitaxy deposition of silicon-containing materials has become a useful technique during formation of elevated source/drain and source/drain extension features, for example, during the formation of silicon-containing MOSFET (metal oxide semiconductor field effect transistor) devices. Source/drain extension features are manufactured by etching a silicon surface to make a recessed source/drain feature and subsequently filling the etched surface with a selectively grown epilayers, such as a silicon germanium (SiGe) material. Selective epitaxy permits near complete dopant activation with in-situ doping, so that the post annealing process is omitted. Therefore, junction depth can be defined accurately by silicon etching and selective epitaxy. On the other hand, the ultra shallow source/drain junction inevitably results in increased series resistance. Also, junction consumption during silicide formation increases the series resistance even further. In order to compensate for junction consumption, an elevated source/drain is epitaxially and selectively grown on the junction. Typically, the elevated source/drain layer is undoped silicon.
[0008] However, current selective epitaxy processes have some drawbacks. In order to maintain selectivity during present epitaxy processes, chemical concentrations of the precursors, as well as reaction temperatures must be regulated and adjusted throughout the deposition process. If not enough silicon precursor is administered, then the etching reaction may dominate and the overall process is slowed down. Also, harmful over etching of substrate features may occur. If not enough etchant precursor is administered, then the deposition reaction may dominate reducing the selectivity to form monocrystalline and polycrystalline materials across the substrate surface. Also, current selective epitaxy processes usually require a high reaction temperature, such as about 800° C., 1,000° C. or higher. Such high temperatures are not desirable during a fabrication process due to thermal budget considerations and possible uncontrolled nitridation reactions to the substrate surface.
[0009] Therefore, there is a need to have a process for selectively and epitaxially depositing silicon and silicon-containing compounds with optional dopants. Furthermore, the process should be versatile to form silicon-containing compounds with varied elemental concentrations while having a fast deposition rate and maintaining a process temperature, such as about 800° C. or less.
SUMMARY OF THE INVENTION
[0010] In one example, a method of epitaxially forming a silicon-containing material on a substrate surface is presented which includes positioning in a process chamber a substrate containing a monocrystalline surface and at least a second surface, such as an amorphous surface and/or a polycrystalline surface. The substrate is exposed to a deposition gas to deposit an epitaxial layer on the monocrystalline surface and a polycrystalline layer on the second surface. The deposition gas preferably contains a silicon source and at least a second elemental source, such as a germanium source, a carbon source and/or combinations thereof. Thereafter, the method further provides exposing the substrate to an etchant gas to etch the polycrystalline layer and the epitaxial layer in a manner such that the polycrystalline layer is etched at a faster rate than the epitaxial layer. The method may further include a deposition cycle that includes repeating the exposure of the substrate to the deposition and etchant gases to form the silicon-containing material with a predetermined thickness.
[0011] In another example, a method of epitaxially forming a silicon-containing material on a substrate surface is presented which includes positioning in a process chamber a substrate containing a monocrystalline surface and at least a second surface, such as an amorphous surface and/or a polycrystalline surface. The substrate is exposed to a deposition gas to deposit an epitaxial layer on the monocrystalline surface and a polycrystalline layer on the second surface. Thereafter, the method further provides exposing the substrate to an etchant gas containing chlorine gas and etching the polycrystalline layer and the epitaxial layer in a manner such that the polycrystalline layer is etched at a faster rate than the epitaxial layer.
[0012] In another example, a method of epitaxially forming a silicon-containing material on a substrate surface is presented which includes positioning in a process chamber a substrate containing a monocrystalline surface and at least a second surface, such as an amorphous surface and/or a polycrystalline surface. The process chamber is heated to a temperature in a range from about 500° C. to about 750° C. The substrate is exposed to a deposition gas to deposit an epitaxial layer on the monocrystalline surface and a polycrystalline layer on the second surface. The deposition gas contains a silicon source and an inert carrier gas for depositing an epitaxial layer on the monocrystalline surface and a polycrystalline layer on the second surface. Thereafter, the method further provides exposing the substrate to an etchant gas comprising an etchant and the inert carrier gas and etching the polycrystalline layer and the epitaxial layer in a manner such that the polycrystalline layer is etched at a faster rate than the epitaxial layer.
[0013] In another example, a method of epitaxially forming a silicon-containing material on a substrate surface is presented which includes positioning in a process chamber a substrate containing a monocrystalline surface and at least a second surface, such as an amorphous surface and/or a polycrystalline surface. The substrate is exposed to a deposition gas to deposit an epitaxial layer on the monocrystalline surface and a polycrystalline layer on the second surface. The deposition gas preferably contains a silicon source and a dopant compound containing an elemental source of boron, arsenic, phosphorous, aluminum, gallium, germanium, carbon and/or combinations thereof. Thereafter, the method further provides exposing the substrate to an etchant gas to etch the polycrystalline layer and the epitaxial layer in a manner such that the polycrystalline layer is etched at a faster rate than the epitaxial layer.
[0014] In another example, a method of epitaxially forming a silicon-containing material on a substrate surface is presented which includes positioning in a process chamber a substrate containing a monocrystalline surface and at least a second surface, such as an amorphous surface and/or a polycrystalline surface. The substrate is exposed to a deposition gas to deposit an epitaxial layer on the monocrystalline surface and a polycrystalline layer on the second surface. The method further includes exposing the substrate to a second deposition gas to deposit a second epitaxial layer on the first epitaxial layer and a second polycrystalline layer on the first polycrystalline layer. The second deposition gas may comprise an elemental source of boron, arsenic, phosphorous, aluminum, gallium, germanium, carbon and/or combinations thereof. Thereafter, the method further provides exposing the substrate to an etchant gas to etch the first and second polycrystalline layers and the first and second epitaxial layers in a manner such that the first and second polycrystalline layer are etched at faster rates than the first and second epitaxial layers. The method may further include a deposition cycle that includes repeating the exposure of the substrate to the deposition and etchant gases to form the silicon-containing material with a predetermined thickness.
BRIEF DESCRIPTION OF THE DRAWINGS
[0015] So that the manner in which the above recited features of the present invention can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of this invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.
[0016] FIG. 1 is a flow chart describing a process to selectively and epitaxially deposit silicon-containing materials in one embodiment described herein;
[0017] FIGS. 2A-2E show schematic illustrations of fabrication techniques for a source/drain extension device within a MOSFET;
[0018] FIGS. 3A-C show several devices containing selectively and epitaxially deposited silicon-containing layers by applying embodiments described herein; and
[0019] FIG. 4 is a flow chart describing a process to selectively and epitaxially deposit silicon-containing materials in another embodiment described herein.
DETAILED DESCRIPTION
[0020] Embodiments of the invention generally provide processes to selectively and epitaxially deposit silicon-containing materials on monocrystalline surfaces of a substrate during fabrication of electronic devices. A patterned substrate containing a monocrystalline surface (e.g., silicon or silicon germanium) and at least a secondary surface, such as an amorphous surface and/or a polycrystalline surface (e.g., oxide or nitride), is exposed to an epitaxial process to form an epitaxial layer on the monocrystalline surface while forming limited or no polycrystalline layer on the secondary surfaces. The epitaxial process, also referred to as the alternating gas supply (AGS) process, includes repeating a cycle of a deposition process and an etching process until the desired thickness of an epitaxial layer is grown.
[0021] The deposition process includes exposing the substrate surface to a deposition gas containing at least a silicon source and a carrier gas. The deposition gas may also include a germanium source or carbon source, as well as a dopant source. During the deposition process, an epitaxial layer is formed on the monocrystalline surface of the substrate while a polycrystalline layer is formed on secondary surfaces, such as amorphous and/or polycrystalline surfaces. Subsequently, the substrate is exposed to an etching gas. The etching gas includes a carrier gas and an etchant, such as chlorine gas or hydrogen chloride. The etching gas removes silicon-containing materials deposited during the deposition process. During the etching process, the polycrystalline layer is removed at a faster rate than the epitaxial layer. Therefore, the net result of the deposition and etching processes forms epitaxially grown silicon-containing material on monocrystalline surfaces while minimizing growth, if any, of polycrystalline silicon-containing material on the secondary surfaces. A cycle of the deposition and etching processes may be repeated as needed to obtain the desired thickness of silicon-containing materials. The silicon-containing materials which can be deposited by embodiments of the invention include silicon, silicon germanium, silicon carbon, silicon germanium carbon, and dopant variants thereof.
[0022] In one example of the AGS process, use of chlorine gas as an etchant lowers the overall process temperature below about 800° C. In general, deposition processes may be conducted at lower temperatures than etching reactions, since etchants often need a high temperature to be activated. For example, silane may be thermally decomposed to deposit silicon at about 500° C. or less, while hydrogen chloride requires an activation temperature of about 700° C. or higher to act as an effective etchant. Therefore, if hydrogen chloride is used during an AGS process, the overall process temperature is dictated by the higher temperature required to activate the etchant. Chlorine contributes to the overall AGS process by reducing the required overall process temperature. Chlorine may be activated at a temperature as low as about 500° C. Therefore, by incorporating chlorine into the AGS process as the etchant, the overall AGS process temperature may be significantly reduced, such as by 200° C. to 300° C., over processes which use hydrogen chloride as the etchant. Also, chlorine etches silicon-containing materials faster than hydrogen chloride. Therefore, chlorine etchants increase the overall rate of the AGS process.
[0023] In another example of the AGS process, an inert gas, such as nitrogen, is used as a carrier gas during the deposition and etching processes, instead of a traditional carrier gas, such as hydrogen. The use of an inert carrier gas has several attributes during an AGS process. For one, an inert carrier gas may increase the deposition rate of the silicon-containing material. While hydrogen may be used as a carrier gas, during the deposition process, hydrogen has a tendency to adsorb or react to the substrate to form hydrogen-terminated surfaces. A hydrogen-terminated surface reacts much slower to epitaxial growth than a bare silicon surface. Therefore, the use of an inert carrier gas increases the deposition rate by not adversely effecting the deposition reaction.
[0024] Although noble gasses, such as argon or helium, may be used as an inert carrier gas, nitrogen is the economically preferred inert carrier gas. Nitrogen is generally much less expensive than hydrogen, argon or helium. One drawback that may occur from using nitrogen as a carrier gas is the nitridizing of materials on a substrate during deposition processes. However, high temperature, such as over 800° C., is required to activate nitrogen in such a manner. Therefore, nitrogen is advantageously used as an inert carrier gas in AGS processes conducted at temperatures below the nitrogen activation threshold. The combined effect of using chlorine as an etchant and nitrogen as a carrier gas greatly increases the rate of the overall AGS process.
[0025] Throughout the application, the terms “silicon-containing” materials, compounds, films or layers should be construed to include a composition containing at least silicon and may contain germanium, carbon, boron, arsenic, phosphorous gallium and/or aluminum. Other elements, such as metals, halogens or hydrogen may be incorporated within a silicon-containing material, compound, film or layer, usually in part per million (ppm) concentrations. Compounds or alloys of silicon-containing materials may be represented by an abbreviation, such as Si for silicon, SiGe, for silicon germanium, SiC for silicon carbon and SiGeC for silicon germanium carbon. The abbreviations do not represent chemical equations with stoichiometrical relationships, nor represent any particular reduction/oxidation state of the silicon-containing materials.
[0026] FIG. 1 illustrates an example of epitaxial process 100 used to deposit a silicon-containing layer. The process 100 includes step 110 for loading a patterned substrate into a process chamber and adjusting the conditions within the process chamber to a desired temperature and pressure. Step 120 provides a deposition process to form an epitaxial layer on a monocrystalline surface of the substrate while forming a polycrystalline layer on the amorphous and/or polycrystalline surfaces of the substrate. During step 130, the deposition process is terminated. Step 140 provides an etching process to etch the surface of the substrate. Preferably, the polycrystalline layer is etched at a faster rate than the epitaxial layer. The etching step either minimizes or completely removes the polycrystalline layer while removing only a marginal portion of the epitaxial layer. During step 150, the etching process is terminated. The thickness of the epitaxial layer and the polycrystalline layer, if any, is determined during step 160. If the predetermined thickness of the epitaxial layer or the polycrystalline layer is achieved, then epitaxial process 100 is terminated at step 170. However, if the predetermined thickness is not achieved, then steps 120-160 are repeated as a cycle until the predetermined thickness is achieved.
[0027] A patterned substrate is loaded in to a process chamber during step 110. Patterned substrates are substrates that include electronic features formed into or onto the substrate surface. The patterned substrate usually contains monocrystalline surfaces and at least one secondary surface that is non-monocrystalline, such as polycrystalline or amorphous surfaces. Monocrystalline surfaces include the bare crystalline substrate or a deposited single crystal layer usually made from a material such as silicon, silicon germanium or silicon carbon. Polycrystalline or amorphous surfaces may include dielectric materials, such as oxides or nitrides, specifically silicon oxide or silicon nitride, as well as amorphous silicon surfaces.
[0028] Epitaxial process 100 begins by adjusting the process chamber containing the patterned substrate to a predetermined temperature and pressure during step 110. The temperature is tailored to the particular conducted process. Generally, the process chamber is maintained at a consistent temperature throughout epitaxial process 100. However, some steps may be performed at varying temperatures. The process chamber is kept at a temperature in the range from about 250° C. to about 1,000° C., preferably from about 500° C. to about 800° C. and more preferably from about 550° C. to about 750° C. The appropriate temperature to conduct epitaxial process 100 may depend on the particular precursors used to deposit and/or etch the silicon-containing materials during steps 120 and 140. In one example, it has been found that chlorine (Cl2) gas works exceptionally well as an etchant for silicon-containing materials at temperatures lower than processes using more common etchants. Therefore, in one example, a preferred temperature to pre-heat the process chamber is about 750° C. or less, preferably about 650° C. or less and more preferably about 550° C. or less. The process chamber is usually maintained at a pressure from about 0.1 Torr to about 200 Torr, preferably from about 1 Torr to about 50 Torr. The pressure may fluctuate during and between process steps 110-160, but is generally maintained constant.
[0029] The deposition process is conducted during step 120. The patterned substrate is exposed to a deposition gas to form an epitaxial layer on the monocrystalline surface while forming a polycrystalline layer on the secondary surfaces. The substrate is exposed to the deposition gas for a period of time of about 0.5 seconds to about 30 seconds, preferably from about 1 second to about 20 seconds, and more preferably from about 5 seconds to about 10 seconds. The specific exposure time of the deposition process is determined in relation to the exposure time during the etching process in step 140, as well as particular precursors and temperature used in the process. Generally, the substrate is exposed to the deposition gas long enough to form a maximized thickness of an epitaxial layer while forming a minimal thickness of a polycrystalline layer that may be easily etched away during subsequent step 140.
[0030] The deposition gas contains at least a silicon source and a carrier gas, and may contain at least one secondary elemental source, such as a germanium source and/or a carbon source. Also, the deposition gas may further include a dopant compound to provide a source of a dopant, such as boron, arsenic, phosphorous, gallium and/or aluminum. In an alternative embodiment, the deposition gas may include at least one etchant, such as hydrogen chloride or chlorine.
[0031] The silicon source is usually provided into the process chamber at a rate in a range from about 5 sccm to about 500 sccm, preferably from about 10 sccm to about 300 sccm, and more preferably from about 50 sccm to about 200 sccm, for example, about 100 sccm. Silicon sources useful in the deposition gas to deposit silicon-containing compounds include silanes, halogenated silanes and organosilanes. Silanes include silane (SiH4) and higher silanes with the empirical formula SixH(2x+2), such as disilane (Si2H6), trisilane (Si3H8), and tetrasilane (Si4H10), as well as others. Halogenated silanes include compounds with the empirical formula X′ySixH(2x+2−y), where X′=F, Cl, Br or I, such as hexachlorodisilane (Si2Cl6), tetrachlorosilane (SiCl4), dichlorosilane (Cl2SiH2) and trichlorosilane (Cl3SiH). Organosilanes include compounds with the empirical formula RySixH(2x+2−y), where R=methyl, ethyl, propyl or butyl, such as methylsilane ((CH3)SiH3), dimethylsilane ((CH3)2SiH2), ethylsilane ((CH3CH2)SiH3), methyldisilane ((CH3)Si2H5), dimethyldisilane ((CH3)2Si2H4) and hexamethyldisilane ((CH3)6Si2). Organosilane compounds have been found to be advantageous silicon sources as well as carbon sources in embodiments which incorporate carbon in the deposited silicon-containing compound. The preferred silicon sources include silane, dichlorosilane and disilane.
[0032] The silicon source is usually provided into the process chamber along with a carrier gas. The carrier gas has a flow rate from about 1 slm (standard liters per minute) to about 100 slm, preferably from about 5 slm to about 75 slm, and more preferably from about 10 slm to about 50 slm, for example, about 25 slm. Carrier gases may include nitrogen (N2), hydrogen (H2), argon, helium and combinations thereof. An inert carrier gas is preferred and includes nitrogen, argon, helium and combinations thereof. A carrier gas may be selected based on the precursor(s) used and/or the process temperature during the epitaxial process 100. Usually the carrier gas is the same throughout each of the steps 110-150. However, some embodiments may use different carrier gases in particular steps. For example, nitrogen may be used as a carrier gas with the silicon source in step 120 and with the etchant in step 140.
[0033] Preferably, nitrogen is utilized as a carrier gas in embodiments featuring low temperature (e.g., <800° C.) processes. Low temperature processes are accessible due in part to the use of chlorine gas in the etching process further discussed in step 140. Nitrogen remains inert during low temperature deposition processes. Therefore, nitrogen is not incorporated into the deposited silicon-containing material during low temperature processes. Also, a nitrogen carrier gas does not form hydrogen-terminated surfaces as does a hydrogen carrier gas. The hydrogen-terminated surfaces formed by the adsorption of hydrogen carrier gas on the substrate surface inhibit the growth rate of silicon-containing layers. Finally, the low temperature processes may take economic advantage of nitrogen as a carrier gas, since nitrogen is far less expensive than hydrogen, argon or helium.
[0034] The deposition gas used during step 120 may also contain at least one secondary elemental source, such as a germanium source and/or a carbon source. The germanium source may be added to the process chamber with the silicon source and carrier gas to form a silicon-containing compound, such as a silicon germanium material. The germanium source is usually provided into the process chamber at a rate in the range from about 0.1 sccm to about 20 sccm, preferably from about 0.5 sccm to about 10 sccm, and more preferably from about 1 sccm to about 5 sccm, for example, about 2 sccm. Germanium sources useful to deposit silicon-containing compounds include germane (GeH4), higher germanes and organogermanes. Higher germanes include compounds with the empirical formula GexH(2x+2), such as digermane (Ge2H6), trigermane (Ge3H8) and tetragermane (Ge4H10), as well as others. Organogermanes include compounds such as methylgermane ((CH3)GeH3), dimethylgermane ((CH3)2GeH2), ethylgermane ((CH3CH2)GeH3), methyldigermane ((CH3)Ge2H5), dimethyldigermane ((CH3)2Ge2H4) and hexamethyldigermane ((CH3)6Ge2). Germanes and organogermane compounds have been found to be advantageous germanium sources and carbon sources in embodiments while incorporating germanium and carbon into the deposited silicon-containing compounds, namely SiGe and SiGeC compounds. The germanium concentration in the epitaxial layer is in the range from about 1 at % to about 30 at %, for example, about 20 at %. The germanium concentration may be graded within an epitaxial layer, preferably graded with a higher germanium concentration in the lower portion of the epitaxial layer than in the upper portion of the epitaxial layer.
[0035] Alternatively, a carbon source may be added during step 120 to the process chamber with the silicon source and carrier gas to form a silicon-containing compound, such as a silicon carbon material. A carbon source is usually provided into the process chamber at a rate in the range from about 0.1 sccm to about 20 sccm, preferably from about 0.5 sccm to about 10 sccm, and more preferably from about 1 sccm to about 5 sccm, for example, about 2 sccm. Carbon sources useful to deposit silicon-containing compounds include organosilanes, alkyls, alkenes and alkynes of ethyl, propyl and butyl. Such carbon sources include methylsilane (CH3SiH3), dimethylsilane ((CH3)2SiH2), ethylsilane (CH3CH2SiH3), methane (CH4), ethylene (C2H4), ethyne (C2H2), propane (C3H8), propene (C3H6), butyne (C4H6), as well as others. The carbon concentration of an epitaxial layer is in the range from about 200 ppm to about 5 at %, preferably from about 1 at % to about 3 at %, for example 1.5 at %. In one embodiment, the carbon concentration may be graded within an epitaxial layer, preferably graded with a higher carbon concentration in the lower portion of the epitaxial layer than in the upper portion of the epitaxial layer. Alternatively, a germanium source and a carbon source may both be added during step 120 into the process chamber with the silicon source and carrier gas to form a silicon-containing compound, such as a silicon germanium carbon material.
[0036] The deposition gas used during step 120 may further include at least one dopant compound to provide a source of elemental dopant, such as boron, arsenic, phosphorous, gallium or aluminum. Dopants provide the deposited silicon-containing compounds with various conductive characteristics, such as directional electron flow in a controlled and desired pathway required by the electronic device. Films of the silicon-containing compounds are doped with particular dopants to achieve the desired conductive characteristic. In one example, the silicon-containing compound is doped p-type, such as by using diborane to add boron at a concentration in the range from about 1015 atoms/cm3 to about 1021 atoms/cm3. In one example, the p-type dopant has a concentration of at least 5×1019 atoms/cm3. In another example, the p-type dopant is in the range from about 1×1020 atoms/cm3 to about 2.5×1021 atoms/cm3. In another example, the silicon-containing compound is doped n-type, such as with phosphorous and/or arsenic to a concentration in the range from about 1015 atoms/cm3 to about 1021 atoms/cm3.
[0037] A dopant source is usually provided into the process chamber during step 120 at a rate in the range from about 0.1 sccm to about 20 sccm, preferably from about 0.5 sccm to about 10 sccm, and more preferably from about 1 sccm to about 5 sccm, for example, about 2 sccm. Boron-containing dopants useful as a dopant source include boranes and organoboranes. Boranes include borane, diborane (B2H6), triborane, tetraborane and pentaborane, while alkylboranes include compounds with the empirical formula RxBH(3−x), where R=methyl, ethyl, propyl or butyl and x=1, 2 or 3. Alkylboranes include trimethylborane ((CH3)3B), dimethylborane ((CH3)2BH), triethylborane ((CH3CH2)3B) and diethylborane ((CH3CH2)2BH). Dopants may also include arsine (AsH3), phosphine (PH3) and alkylphosphines, such as with the empirical formula RxPH(3−x), where R=methyl, ethyl, propyl or butyl and x=1, 2 or 3. Alkylphosphines include trimethylphosphine ((CH3)3P), dimethylphosphine ((CH3)2PH), triethylphosphine ((CH3CH2)3P) and diethylphosphine ((CH3CH2)2PH). Aluminum and gallium dopant sources may include alkylated and/or halogenated derivates, such as described with the empirical formula RxMX(3−x), where M=Al or Ga, R=methyl, ethyl, propyl or butyl, X=Cl or F and x=0, 1, 2 or 3. Examples of aluminum and gallium dopant sources include trimethylaluminum (Me3Al), triethylaluminum (Et3Al), dimethylaluminumchloride (Me2AlCl), aluminum chloride (AlCl3), trimethylgallium (Me3Ga), triethylgallium (Et3Ga), dimethylgalliumchloride (Me2GaCl) and gallium chloride (GaCl3).
[0038] During step 130, the deposition process is terminated. In one example, the process chamber may be flushed with a purge gas or the carrier gas and/or the process chamber may be evacuated with a vacuum pump. The purging and/or evacuating processes remove excess deposition gas, reaction by-products and other contaminates. In another example, once the deposition process has terminated, the etching process in step 140 is immediately started without purging and/or evacuating the process chamber.
[0039] The etching process in step 140 removes silicon-containing materials deposited during step 120 from the substrate surface. The etching process removes both epitaxial or monocrystalline materials and amorphous or polycrystalline materials. Polycrystalline layers, if any, deposited on the substrate surface are removed at a faster rate than the epitaxial layers. The time duration of the etching process is balanced with the time duration of the deposition process to result in net deposition of the epitaxial layer selectively formed on desired areas of the substrate. Therefore, the net result of the deposition process in step 120 and etching process in step 140 is to form selective and epitaxially grown silicon-containing material while minimizing, if any, growth of polycrystalline silicon-containing material.
[0040] During step 140, the substrate is exposed to the etching gas for a period of time in the range from about 10 seconds to about 90 seconds, preferably, from about 20 seconds to about 60 seconds, and more preferably from about 30 seconds to about 45 seconds. The etching gas includes at least one etchant and a carrier gas. The etchant is usually provided into the process chamber at a rate in the range from about 10 sccm to about 700 sccm, preferably from about 50 sccm to about 500 sccm, and more preferably from about 100 sccm to about 400 sccm, for example, about 200 sccm. The etchant used in the etching gas may include chlorine (Cl2), hydrogen chloride (HCl), boron trichloride (BCl3), carbon tetrachloride (CCl4), chlorotrifluoride (ClF3) and combinations thereof. Preferably, chlorine or hydrogen chloride is used as the etchant.
[0041] The etchant is usually provided into the process chamber with a carrier gas. The carrier gas has a flow rate in the range from about 1 slm to about 100 slm, preferably from about 5 slm to about 75 slm, and more preferably from about 10 slm to about 50 slm, for example, about 25 slm. Carrier gases may include nitrogen (N2), hydrogen (H2), argon, helium and combinations thereof. In some embodiment, an inert carrier gas is preferred and includes nitrogen, argon, helium and combinations thereof. A carrier gas may be selected based upon specific precursor(s) and/or temperature used during the epitaxial process 100. The same carrier gas is usually used throughout each of the steps 110-150. However, some embodiments may use a different carrier gas during the etching process as used in the deposition process. In one embodiment, the preferred etchant is chlorine gas, especially when the AGS process is conducted at a low temperature (e.g., <800° C.). For example, an etching gas contains chlorine as an etchant and nitrogen as a carrier gas and is exposed to the substrate surface at a temperature in a range from about 500° C. to about 750° C. In another example, an etching gas containing chlorine and nitrogen is exposed to the substrate surface at a temperature in a range from about 250° C. to about 500° C.
[0042] The etching process is terminated during step 150. In one example, the process chamber may be flushed with a purge gas or the carrier gas and/or the process chamber may be evacuated with a vacuum pump. The purging and/or evacuating processes remove excess etching gas, reaction by-products and other contaminates. In another example, once the etching process has terminated, step 160 is immediately started without purging and/or evacuating the process chamber.
[0043] The thicknesses of the epitaxial layer and the polycrystalline layer may be determined during step 160. If the predetermined thicknesses are achieved, then epitaxial process 100 is terminated at step 170. However, if the predetermined thicknesses are not achieved, then steps 120-160 are repeated as a cycle until the desired thicknesses are achieved. The epitaxial layer is usually grown to have a thickness at a range from about 10 Å to about 2,000 Å, preferably from about 100 Å to about 1,500 Å, and more preferably from about 400 Å to about 1,200 Å, for example, about 800 Å. The polycrystalline layer is usually deposited with a thickness, if any, in a range from an atomic layer to about 500 Å. The desired or predetermined thickness of the epitaxial silicon-containing layer or the polycrystalline silicon-containing layer is specific to a particular fabrication process. In one example, the epitaxial layer may reach the predetermined thickness while the polycrystalline layer is too thick. The excess polycrystalline layer may be further etched by repeating steps 140-160 while skipping steps 120 and 130.
[0044] In one example, as depicted in FIGS. 2A-2E , a source/drain extension is formed within a MOSFET device wherein the silicon-containing layers are epitaxially and selectively deposited on the surface of the substrate. FIG. 2A depicts a source/drain region 232 formed by implanting ions into the surface of a substrate 230. The segments of source/drain region 232 are bridged by the gate 236 formed on gate oxide layer 235 and spacer 234. In order to form a source/drain extension, a portion of the source/drain region 232 is etched and wet-cleaned to produce a recess 238, as in FIG. 2B . Etching of the gate 236 may be avoided by depositing a hardmask prior to etching the portion of source/drain region 232.
[0045] FIG. 2C illustrates one embodiment of an epitaxial process described herein, in which a silicon-containing epitaxial layer 240 and optional polycrystalline layer 242 are simultaneously and selectively deposited without depositing on the spacer 234. Polycrystalline layer 242 is optionally formed on gate 236 by adjusting the deposition and etching processes in steps 120 and 140 of epitaxial process 100. Alternatively, polycrystalline layer 242 is continually etched away from gate 236 as epitaxial layer 240 is deposited on the source/drain region 232.
[0046] In another example, silicon-containing epitaxial layer 240 and polycrystalline layer 242 are SiGe-containing layers with a germanium concentration in a range from about 1 at % to about 50 at %, preferably about 24 at % or less. Multiple SiGe-containing layers containing varying amounts of silicon and germanium may be stacked to form silicon-containing epitaxial layer 240 with a graded elemental concentration. For example, a first SiGe-layer may be deposited with a germanium concentration in a range from about 15 at % to about 25 at % and a second SiGe-layer may be deposited with a germanium concentration in a range from about 25 at % to about 35 at %.
[0047] In another example, silicon-containing epitaxial layer 240 and polycrystalline layer 242 are SiC-containing layers with a carbon concentration in a range from about 200 ppm to about 5 at %, preferably about 3 at % or less, preferably, from about 1 at % to about 2 at %, for example, about 1.5 at %. In another embodiment, silicon-containing epitaxial layer 240 and polycrystalline layer 242 are SiGeC-containing layers with a germanium concentration in the range from about 1 at % to about 50 at %, preferably about 24 at % or less and a carbon concentration at about 200 ppm to about 5 at %, preferably about 3 at % or less, more preferably from about 1 at % to about 2 at %, for example, about 1.5 at %.
[0048] Multiple layers containing Si, SiGe, SiC or SiGeC may be deposited in varying order to form graded elemental concentrations within the silicon-containing epitaxial layer 240. The silicon-containing layers are generally doped with a dopant (e.g., boron, arsenic, phosphoric, gallium or aluminum) having a concentration in the range from about 1×1019 atoms/cm3 to about 2.5×1021 atoms/cm3, preferably from about 5×1019 atoms/cm3 to about 2×1020 atoms/cm3. Dopants added to individual layers of the silicon-containing material form graded dopants. For example, silicon-containing epitaxial layer 240 is formed by depositing a first SiGe-containing layer with a dopant concentration (e.g., boron) in a range from about 5×1019 atoms/cm3 to about 1×1020 atoms/cm3 and a second SiGe-containing layer with a dopant concentration (e.g., boron) in a range from about 1×1020 atoms/cm3 to about 2×1020 atoms/cm3.
[0049] Carbon incorporated in SiC-containing layers and SiGeC-containing layers is generally located in interstitial sites of the crystalline lattice immediately following the deposition of the silicon-containing layer. The interstitial carbon content is about 10 at % or less, preferably less than about 5 at % and more preferably from about 1 at % to about 3 at %, for example, about 2 at %. The silicon-containing epitaxial layer 240 may be annealed to incorporate at least a portion, if not all of the interstitial carbon into substitutional sites of the crystalline lattice. The annealing process may include a spike anneal, such as rapid thermal process (RTP), laser annealing or thermal annealing with an atmosphere of gas, such as oxygen, nitrogen, hydrogen, argon, helium or combinations thereof. The annealing process is conducted at a temperature from about 800° C. to about 1,200° C., preferably from about 1,050° C. to about 1,100° C. The annealing process may occur immediately after the silicon-containing layer is deposited or after a variety of other process steps the substrate will endure.
[0050] During the next step, FIG. 2D shows a spacer 244, generally a nitride spacer (e.g., Si3N4) deposited on the spacer 234. Spacer 244 is usually deposited in a different chamber by a CVD or ALD technique. Therefore, the substrate is removed from the process chamber that was used to deposit silicon-containing epitaxial layer 240. During the transfer between the two chambers, the substrate may be exposed to ambient conditions, such as the temperature, pressure or the atmospheric air containing water and oxygen. Upon depositing the spacer 244, or performing other semiconductor process (e.g., anneal, deposition or implant), the substrate may be exposed to ambient conditions a second time prior to depositing elevated layer 248. In one embodiment, an epitaxial layer (not shown) with no or minimal germanium (e.g., less than about 5 at %) is deposited on the top of epitaxial layer 240 before exposing the substrate to ambient conditions since native oxides are easier to remove from epitaxial layers containing minimal germanium concentrations than from an epitaxial layer formed with a germanium concentration greater than about 5 at %.
[0051] FIG. 2E depicts another example in which an elevated layer 248 comprised of a silicon-containing material is selectively and epitaxially deposited on epitaxial layer 240 (e.g., doped-SiGe). During the deposition process, polycrystalline layer 242 is further grown, deposited or etched away on the gate 236.
[0052] In a preferred embodiment, elevated layer 248 is epitaxial deposited silicon containing little or no germanium or carbon. However, in an alternative embodiment, elevated layer 248 does contain germanium and/or carbon. For example, elevated layer 248 may have about 5 at % or less of germanium. In another example, elevated layer 248 may have about 2 at % or less of carbon. Elevated layer 248 may also be doped with a dopant, such as boron, arsenic, phosphorous, aluminum or gallium.
[0053] Silicon-containing compounds are utilized within embodiments of the processes to deposit silicon-containing layers used for Bipolar device fabrication (e.g., base, emitter, collector, emitter contact), BiCMOS device fabrication (e.g., base, emitter, collector, emitter contact) and CMOS device fabrication (e.g., channel, source/drain, source/drain extension, elevated source/drain, substrate, strained silicon, silicon on insulator and contact plug). Other embodiments of processes teach the growth of silicon-containing layers that can be used as gate, base contact, collector contact, emitter contact, elevated source/drain and other uses.
[0054] The processes are extremely useful for depositing selective, epitaxial silicon-containing layers in MOSFET and bipolar transistors as depicted in FIGS. 3A-3C . FIGS. 3A-3B show the epitaxially grown silicon-containing compounds on a MOSFET device. The silicon-containing compound is deposited on the source/drain features of the device. The silicon-containing compound adheres and grows from the crystal lattice of the underlying layer and maintains this arrangement as the silicon-containing compound is grown to a desired thickness. FIG. 3A demonstrates the silicon-containing compound deposited as a recessed source/drain layer, while FIG. 3B shows silicon-containing compounds deposited as recessed source/drain layer and an elevated source/drain layer.
[0055] The source/drain region 312 is formed by ion implantation. Generally, the substrate 310 is doped n-type while the source/drain region 312 is doped p-type. Silicon-containing epitaxial layer 313 is selectively grown on the source/drain region 312 and/or directly on substrate 310. Silicon-containing epitaxial layer 314 is selectively grown on the silicon-containing layer 313 according to aspects herein. A gate oxide layer 318 bridges the segmented silicon-containing layer 313. Generally, gate oxide layer 318 is composed of silicon dioxide, silicon oxynitride or hafnium oxide. Partially encompassing the gate oxide layer 318 is a spacer 316, which is usually an isolation material such as a nitride/oxide stack (e.g., Si3N4/SiO2/Si3N4). Gate layer 322 (e.g., polysilicon) may have a protective layer 319, such as silicon dioxide, along the perpendicular sides, as in FIG. 3A . Alternately, gate layer 322 may have a spacer 316 and off-set layers 320 (e.g., Si3N4) disposed on either side.
[0056] In another example, FIG. 3C depicts the deposited silicon-containing epitaxial layer 334 as a base layer of a bipolar transistor. Silicon-containing epitaxial layer 334 is selectively grown with the various embodiments of the invention. Silicon-containing epitaxial layer 334 is deposited on an n-type collector layer 332 previously deposited on substrate 330. The transistor further includes isolation layer 333 (e.g., SiO2 or Si3N4), contact layer 336 (e.g., heavily doped poly-Si), off-set layer 338 (e.g., Si3N4), and a second isolation layer 340 (e.g., SiO2 or Si3N4).
[0057] In an alternative embodiment, FIG. 4 illustrates an epitaxial process 400 that may be used to selectively deposit silicon-containing materials/layer. Epitaxial process 400 includes at least two deposition processes followed by an etching process. The first deposition process includes a deposition gas containing a silicon source while the second deposition process includes a deposition gas containing a secondary elemental source, such as germanium, carbon or a dopant (e.g., boron, arsenic, phosphorous, gallium or aluminum). Similar process parameters used in epitaxial process 100 are used in epitaxial process 400, such as temperatures, pressures, flow rates, carrier gases and precursors.
[0058] Epitaxial process 400 includes step 410 for loading a patterned substrate into the process chamber and adjusting the process chamber to a predetermined temperature. Step 420 provides a first deposition process to form an epitaxial layer on a monocrystalline surface while forming a polycrystalline layer on secondary surfaces, such as amorphous and/or polycrystalline surfaces. The epitaxial layer and the monocrystalline layer are formed from a deposition gas containing a silicon source. During step 430, the first deposition process is terminated. Step 440 provides a second deposition process to continue growing the epitaxial layer on a monocrystalline surface and continue forming the polycrystalline layer on the secondary surface. The epitaxial layer and the polycrystalline layer are further grown by exposing the substrate surface to a deposition gas containing a secondary elemental source. At step 450, the second deposition process is terminated. Step 460 provides an etching process to etch the exposed silicon-containing layers. The etching process either minimizes or completely removes the polycrystalline layer while removing only a marginal portion of the epitaxial layer as a result of the rate at which each material is removed. During step 470, the etching process is terminated. The thicknesses of the epitaxial layer and the polycrystalline layer, if any, are determined during step 480. If the predetermined thickness is achieved, then epitaxial process 400 is terminated at step 490. However, if the predetermined thickness of either layer is not achieved, then steps 420-480 are repeated as a cycle until the predetermined thicknesses are achieved.
[0059] Epitaxial process 400 starts at step 410 by adjusting the process chamber containing the patterned substrate to a predetermined temperature. The temperature and pressure is tailored to the particular process conducted. Generally, the process chamber is maintained at a consistent temperature throughout epitaxial process 400. However, some steps may be performed at varying temperatures. The process chamber is kept at a temperature in the range from about 250° C. to about 1,000° C., preferably from about 500° C. to about 800° C. and more preferably from about 550° C. to about 750° C. The appropriate temperature to conduct epitaxial process 400 may depend on the particular precursors used to deposit and/or etch the silicon-containing materials during steps 420-480. In one embodiment, it has been found that chlorine (Cl2) gas works exceptionally well as an etchant for silicon-containing materials at temperatures lower than processes using other more common etchants. Therefore, in one embodiment a preferred temperature to pre-heat the process chamber is about 750° C. or less, preferably about 650° C. or less and more preferably about 550° C. or less. The process chamber is usually maintained with a pressure from about 0.1 Torr to about 200 Torr, preferably from about 1 Torr to about 50 Torr. The pressure may fluctuate during and between process steps 410-480, but is generally maintained constant.
[0060] The first deposition process is conducted during step 420. The patterned substrate is exposed to a first deposition gas to form an epitaxial layer on the monocrystalline surface while forming a polycrystalline layer on the secondary surfaces. The substrate is exposed to the first deposition gas for a period of time of about 0.5 seconds to about 30 seconds, preferably from about 1 second to about 20 seconds, and more preferably from about 5 seconds to about 10 seconds. The specific exposure time of the deposition process is determined in relation to the exposure time during the etching process in step 460, as well as particular precursors and temperature used in the process. Generally, the substrate is exposed to the first deposition gas long enough to form the maximized thickness of an epitaxial layer while forming the minimized thickness of a polycrystalline layer that may be easily etched away during subsequent step 460.
[0061] The first deposition gas contains at least a silicon source and a carrier gas. The first deposition gas may also contain a secondary elemental source and/or a dopant compound, but preferably, the secondary elemental source and the dopant compound are in the second deposition gas. Therefore, in one aspect, the first deposition gas may contain a silicon source, a secondary elemental source and a dopant source. In another aspect, the first deposition gas may contain a silicon source and a secondary elemental source. In yet another aspect, the first deposition gas may contain a silicon source and a dopant source. In an alternative embodiment, the first deposition gas may also include at least one etchant, such as hydrogen chloride or chlorine.
[0062] The silicon source is usually provided into the process chamber at a rate in the range from about 5 sccm to about 500 sccm, preferably from about 10 sccm to about 300 sccm, and more preferably from about 50 sccm to about 200 sccm, for example, about 100 sccm. The preferred silicon sources include silane, dichlorosilane and disilane.
[0063] The silicon source is usually provided into the process chamber in a carrier gas. The carrier gas has a flow rate from about 1 slm to about 100 slm, preferably from about 5 slm to about 75 slm, and more preferably from about 10 slm to about 50 slm, for example, about 25 slm. Carrier gases may include nitrogen (N2), hydrogen (H2), argon, helium and combinations thereof. In some embodiment, an inert carrier gas is preferred and includes nitrogen, argon, helium and combinations thereof. Preferably, the carrier gas used throughout epitaxial process 400 is nitrogen, for reasons discussed above.
[0064] During step 430, the first deposition process is terminated. In one example, the process chamber may be flushed with a purge gas or the carrier gas and/or the process chamber may be evacuated with a vacuum pump. The purging and/or evacuating processes remove excess deposition gas, reaction by-products and other contaminates. In another example, once the first deposition process has terminated, the second deposition process in step 440 is immediately started without purging and/or evacuation the process chamber.
[0065] The deposition gas used during step 440 contains a carrier gas and at least one secondary elemental source, such as a germanium source, a carbon source and/or a dopant compound. Alternatively, a silicon source may be included in the second deposition gas. The secondary elemental source is added to the process chamber with the carrier gas to continue the growth of the silicon-containing compounds deposited during step 420. The silicon-containing compounds may have varied compositions controlled by the specific secondary elemental source and the concentration of the secondary elemental source. A secondary elemental source is usually provided into the process chamber at a rate in the range from about 0.1 sccm to about 20 sccm, preferably from about 0.5 sccm to about 10 sccm, and more preferably from about 1 sccm to about 5 sccm, for example, about 2 sccm. Germanium sources, carbon sources and dopant compounds are selected from the aforementioned precursors discussed above.
[0066] During step 450, the second deposition process is terminated. In one example, the process chamber may be flushed with a purge gas or the carrier gas and/or the process chamber may be evacuated with a vacuum pump. The purging and/or evacuating processes remove excess deposition gas, reaction by-products and other contaminates. In another example, once the second deposition process has terminated, the etching process in step 460 is immediately started without purging and/or evacuation the process chamber.
[0067] The etching process in step 460 removes materials deposited during steps 420 and 440 from the substrate surface. The etching process removes both epitaxial or monocrystalline materials and amorphous and/or polycrystalline materials. Polycrystalline layers, if any, deposited on the substrate surface is removed at a faster rate than the epitaxial layers. The time duration of the etching process is balanced with the time duration of the two deposition processes. Therefore, the net result of the deposition processes in steps 420 and 440 and etching process in step 460 is to form selective and epitaxially grown silicon-containing material while minimizing, if any, growth of polycrystalline silicon-containing material.
[0068] During step 460, the substrate is exposed to the etching gas for a period of time in a range from about 10 seconds to about 90 seconds, preferably, from about 20 seconds to about 60 seconds, and more preferably from about 30 seconds to about 45 seconds. The etching gas includes at least one etchant and a carrier gas. The etchant is usually provided into the process chamber at a rate in a range from about 10 sccm to about 700 sccm, preferably from about 50 sccm to about 500 sccm, and more preferably from about 100 sccm to about 400 sccm, for example, about 200 sccm. The etchant used in the etching gas may include chlorine (Cl2), hydrogen chloride (HCl), boron trichloride (BCl3), carbon tetrachloride (CCl4), chlorotrifluoride (ClF3) and combinations thereof. Preferably, chlorine or hydrogen chloride is used as the etchant.
[0069] The etchant is usually provided into the process chamber along with a carrier gas. The carrier gas has a flow rate in a range from about 1 slm to about 100 slm, preferably from about 5 slm to about 75 slm, and more preferably from about 10 slm to about 50 slm, for example, about 25 slm. Carrier gases may include nitrogen (N2), hydrogen (H2), argon, helium and combinations thereof. In some embodiment, an inert carrier gas is preferred and includes nitrogen, argon, helium and combinations thereof. A carrier gas may be selected based upon specific precursor(s) and/or temperature used during the epitaxial process 400. The same carrier gas is usually used throughout each of steps 420-480. However, some embodiments may use a different carrier gas during the etching process as used in the deposition process. In one embodiment, the preferred etchant is chlorine gas, especially when the AGS process is conducted at a low temperature (e.g., <800° C.). For example, an etching gas contains chlorine as an etchant and nitrogen as a carrier gas and is exposed to the substrate surface at a temperature in a range from about 500° C. to about 750° C.
[0070] The etching process is terminated during step 470. In one example, the process chamber may be flushed with a purge gas or the carrier gas and/or the process chamber may be evacuated with a vacuum pump. The purging and/or evacuating processes remove excess etching gas, reaction by-products and other contaminates. In another example, once the etching process has terminated, step 480 is immediately started without purging and/or evacuating the process chamber.
[0071] The thicknesses of epitaxial layer and the polycrystalline layer may be determined during step 480. If the predetermined thicknesses are achieved, then epitaxial process 400 is ended at step 490. However, if the predetermined thicknesses are not achieved, then steps 420-180 are repeated as a cycle until the desired thicknesses are achieved. The epitaxial layer is usually grown to have a thickness at a range from about 10 Å to about 2,000 Å, preferably from about 100 Å to about 1,500 Å, and more preferably from about 400 Å to about 1,200 Å, for example, about 800 Å. The polycrystalline layer is usually deposited on have a thickness, if any, at a range from about an atomic layer to about 500 Å. The desired or predetermined thickness of the epitaxial silicon-containing layer or the polycrystalline silicon-containing layer is specific to a particular fabrication process. In one example, the epitaxial layer may reach the predetermined thickness while the polycrystalline layer is too thick. The excess polycrystalline layer may be further etched by repeating steps 140-160 while omitting steps 460 and 470. Likewise, in other examples, steps 420, 440 and 460 may be individually omitted while proceeding through epitaxial process 400. By skipping steps 420, 440 and 460, the elemental concentration and the thicknesses of deposited silicon-containing materials may be controlled.
[0072] Embodiments of the invention teach processes to deposit silicon-containing compounds on a variety of substrates. Substrates on which embodiments of the invention may be useful include, but are not limited to semiconductor wafers, such as crystalline silicon (e.g., Si<100> and Si<111>), silicon oxide, silicon germanium, doped or undoped wafers and patterned or non-patterned wafers. Substrates have a variety of geometries (e.g., round, square and rectangular) and sizes (e.g., 200 mm OD, 300 mm OD).
[0073] In one embodiment, silicon-containing compounds deposited by process described herein include a germanium concentration within the range from about 0 at % to about 95 at %. In another embodiment, a germanium concentration is within the range from about 1 at % to about 30 at %, preferably from about 15 at % to about 30 at %, for example, about 20 at %. Silicon-containing compounds also include a carbon concentration within the range from about 0 at % to about 5 at %. In other aspects, a carbon concentration is within the range from about 200 ppm to about 3 at %, preferably about 1.5 at %.
[0074] The silicon-containing compound films of germanium and/or carbon are produced by various processes of the invention and can have consistent, sporadic or graded elemental concentrations. Graded silicon germanium films are disclosed in U.S. Pat. No. 6,770,134 and U.S. patent application Ser. No. 10/014,466, published as United States Patent Publication 20020174827, both assigned to Applied Materials, Inc., and are incorporated herein by reference in entirety for the purpose of describing methods of depositing graded silicon-containing compound films. In one example, a silicon source (e.g., SiH4) and a germanium source (e.g., GeH4) are used to selectively and epitaxially deposit silicon germanium containing films. In this example, the ratio of silicon source and germanium source can be varied in order to provide control of the elemental concentrations, such as silicon and germanium, while growing graded films. In another example, a silicon source and a carbon source (e.g., CH3SiH3) are used to selectively and epitaxially deposit silicon carbon containing films. The ratio of silicon source and carbon source can be varied in order to provide control of the elemental concentration while growing homogenous or graded films. In another example, a silicon source, a germanium source and a carbon source are used to selectively and epitaxially deposit silicon germanium carbon containing films. The ratios of silicon, germanium and carbon sources are independently varied in order to provide control of the elemental concentration while growing homogenous or graded films.
[0075] MOSFET devices formed by processes described herein may contain a PMOS component or a NMOS component. The PMOS component, with a p-type channel, has holes that are responsible for channel conduction, while the NMOS component, with a n-type channel, has electrons that are responsible channel conduction. Therefore, for example, a silicon-containing material such as SiGe may be deposited in a recessed area to form a PMOS component. In another example, a silicon-containing film such as SiC may be deposited in a recessed area to form a NMOS component. SiGe is used for PMOS application for several reasons. A SiGe material incorporates more boron than silicon alone, thus the junction resistivity may be lowered. Also, the SiGe/silicide layer interface at the substrate surface has a lower Schottky barrier than the Si/silicide interface.
[0076] Further, SiGe grown epitaxially on the top of silicon has compressive stress inside the film because the lattice constant of SiGe is larger than that of silicon. The compressive stress is transferred in the lateral dimension to create compressive strain in the PMOS channel and to increase mobility of the holes. For NMOS application, SiC can be used in the recessed areas to create tensile stress in the channel, since the lattice constant of SiC is smaller than that of silicon. The tensile stress is transferred into the channel and increases the electron mobility. Therefore, in one embodiment, a first silicon-containing layer is formed with a first lattice strain value and a second silicon-containing layer is formed with a second lattice strain value. For example, a SiC layer with a thickness from about 50 Å to about 200 Å is deposited on the substrate surface and sequentially, a SiGe layer with a thickness from about 150 Å to about 1,000 Å is deposited on the SiC layer. The SiC layer may be epitaxially grown and has less strain than the SiGe layer epitaxially grown on the SiC layer.
[0077] In embodiments described herein, silicon-containing compound films are selectively and epitaxially deposited by chemical vapor deposition (CVD) processes. Chemical vapor deposition processes include atomic layer deposition (ALD) processes and/or atomic layer epitaxy (ALE) processes. Chemical vapor deposition includes the use of many techniques, such as plasma-assisted CVD (PA-CVD), atomic layer CVD (ALCVD), organometallic or metalorganic CVD (OMCVD or MOCVD), laser-assisted CVD (LA-CVD), ultraviolet CVD (UV-CVD), hot-wire (HWCVD), reduced-pressure CVD (RP-CVD), ultra-high vacuum CVD (UHV-CVD) and others. In one embodiment, the preferred process is to use thermal CVD to epitaxially grow or deposit the silicon-containing compound, whereas the silicon-containing compound includes silicon, SiGe, SiC, SiGeC, doped variants thereof and combinations thereof.
[0078] The processes of the invention can be carried out in equipment known in the art of ALE, CVD and ALD. The apparatus may contain multiple gas lines to maintain the deposition gas and the etching gas separated prior to entering the process chamber. Thereafter, the gases are brought into contact with a heated substrate on which the silicon-containing compound films are grown. Hardware that can be used to deposit silicon-containing films includes the Epi Centura® system and the Poly Gen® system available from Applied Materials, Inc., located in Santa Clara, Calif. An ALD apparatus is disclosed in U.S. patent Ser. No. 10/032,284, filed Dec. 21, 2001, published as United States Patent Publication No. 20030079686, assigned to Applied Materials, Inc., and entitled, “Gas Delivery Apparatus and Methods for ALD,” and is incorporated herein by reference in entirety for the purpose of describing the apparatus. Other apparatuses include batch, high-temperature furnaces, as known in the art.
EXAMPLES
[0079] The following hypothetical examples were conducted to form an elevated source drain (ESD) structure on a substrate surface. The patterned substrates contained monocrystalline surfaces with source/drain features formed within the substrate surface and gate and spacers formed therebetween.
Example 1
Selective Epitaxy of Silicon with Cl2 Etchant
[0080] The substrate was placed into a process chamber heated and maintained at 550° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm and nitrogen with a flow rate of 25 slm for 7 seconds. The substrate was thereafter exposed to an etching gas containing chlorine gas with a flow rate of 20 sccm and nitrogen with a flow rate of 25 slm for 10 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 50 times to form an epitaxially grown silicon layer on the exposed monocrystalline portion of the substrate. The silicon epitaxial layer had a thickness of about 1,000 Å.
Example 2
Selective Epitaxy of Silicon Germanium with Cl2 Etchant
[0081] The substrate was placed into a process chamber heated and maintained at 550° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm, germane with a flow rate of 3 sccm and nitrogen with a flow rate of 25 slm for 8 seconds. The substrate was thereafter exposed to an etching gas containing chlorine gas with a flow rate of 20 sccm and nitrogen with a flow rate of 25 slm for 10 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 50 times to form an epitaxially grown silicon-containing layer on the exposed monocrystalline portion of the substrate. The silicon-containing epitaxial layer had a thickness of about 1,700 Å.
Example 3
Selective Epitaxy of Silicon Germanium with Cl2 Etchant
[0082] The substrate was placed into a process chamber heated and maintained at 550° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm and nitrogen with a flow rate of 25 slm for 7 seconds. The substrate surface was thereafter exposed to a flow of second deposition gas containing germane with a flow rate of 5 sccm and nitrogen with a flow rate of 25 slm for 7 seconds. The substrate was exposed to an etching gas containing chlorine gas with a flow rate of 20 sccm and nitrogen with a flow rate of 25 slm for 10 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 50 times to form an epitaxially grown silicon-containing layer on the exposed monocrystalline portion of the substrate. The silicon-containing epitaxial layer had a thickness of about 1,800 Å.
Example 4
Selective Epitaxy of Silicon Carbon with Cl2 Etchant
[0083] The substrate was placed into a process chamber heated and maintained at 550° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was thereafter exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm, methylsilane with a flow rate of 1 sccm and nitrogen with a flow rate of 25 slm for 8 seconds. The substrate was exposed to an etching gas containing chlorine gas with a flow rate of 20 sccm and nitrogen with a flow rate of 25 slm for 10 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 50 times to form an epitaxially grown silicon-containing layer on the exposed monocrystalline portion of the substrate. The silicon-containing epitaxial layer had a thickness of about 1,600 Å.
Example 5
Selective Epitaxy of Silicon Carbon with Cl2 Etchant
[0084] The substrate was placed into a process chamber heated and maintained at 550° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was thereafter exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm and nitrogen with a flow rate of 25 slm for 7 seconds. The substrate surface was exposed to a flow of second deposition gas containing methylsilane with a flow rate of 5 sccm and nitrogen with a flow rate of 25 slm for 7 seconds. The substrate was exposed to an etching gas containing chlorine gas with a flow rate of 20 sccm and nitrogen with a flow rate of 25 slm for 10 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 50 times to form an epitaxially grown silicon-containing layer on the exposed monocrystalline portion of the substrate. The silicon-containing epitaxial layer had a thickness of about 1,800 Å.
Example 6
Selective Epitaxy of Silicon with HCl Etchant
[0085] The substrate was placed into a process chamber heated and maintained at 700° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was thereafter exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm and hydrogen with a flow rate of 25 slm for 7 seconds. The substrate was exposed to an etching gas containing hydrogen chloride with a flow rate of 200 sccm and hydrogen with a flow rate of 25 slm for 40 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 10 times to form an epitaxially grown silicon layer on the exposed monocrystalline portion of the substrate. The silicon epitaxial layer had a thickness of about 800 Å.
Example 7
Selective Epitaxy of Silicon Germanium with HCl Etchant
[0086] The substrate was placed into a process chamber heated and maintained at 700° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was thereafter exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm, germane with a flow rate of 3 sccm and hydrogen with a flow rate of 25 slm for 8 seconds. The substrate was exposed to an etching gas containing hydrogen chloride with a flow rate of 200 sccm and hydrogen with a flow rate of 25 slm for 40 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 20 times to form an epitaxially grown silicon-containing layer on the exposed monocrystalline portion of the substrate. The silicon-containing epitaxial layer had a thickness of about 1,500 Å.
Example 8
Selective Epitaxy of Silicon Germanium with HCl Etchant
[0087] The substrate was placed into a process chamber heated and maintained at 700° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was thereafter exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm and hydrogen with a flow rate of 25 slm for 7 seconds. The substrate surface was exposed to a flow of second deposition gas containing germane with a flow rate of 5 sccm and hydrogen with a flow rate of 25 slm for 7 seconds. The substrate was exposed to an etching gas containing hydrogen chloride with a flow rate of 200 sccm and hydrogen with a flow rate of 25 slm for 40 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 20 times to form an epitaxially grown silicon-containing layer on the exposed monocrystalline portion of the substrate. The silicon-containing epitaxial layer had a thickness of about 1,600 Å.
Example 9
Selective Epitaxy of Silicon Carbon with HCl Etchant
[0088] The substrate was placed into a process chamber heated and maintained at 700° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was thereafter exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm, methylsilane with a flow rate of 1 sccm and hydrogen with a flow rate of 25 slm for 8 seconds. The substrate was exposed to an etching gas containing hydrogen chloride with a flow rate of 200 sccm and hydrogen with a flow rate of 25 slm for 40 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 20 times to form an epitaxially grown silicon-containing layer on the exposed monocrystalline portion of the substrate. The silicon-containing epitaxial layer had a thickness of about 1,500 Å.
Example 10
Selective Epitaxy of Silicon Carbon with HCl Etchant
[0089] The substrate was placed into a process chamber heated and maintained at 700° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was thereafter exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm and hydrogen with a flow rate of 25 slm for 7 seconds. The substrate surface was exposed to a flow of second deposition gas containing germane with a flow rate of 5 sccm and hydrogen with a flow rate of 25 slm for 7 seconds. The substrate was exposed to an etching gas containing hydrogen chloride with a flow rate of 200 sccm and hydrogen with a flow rate of 25 slm for 40 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 20 times to form an epitaxially grown silicon-containing layer on the exposed monocrystalline portion of the substrate. The silicon-containing epitaxial layer had a thickness of about 1,600 Å. The exposed dielectric portions of the substrate surface, such as the gate, formed either limited or no polycrystalline growth from the deposition gas.
Example 11
Selective Epitaxy of Silicon Doped with B and Etched with Cl2
[0090] The substrate was placed into a process chamber heated and maintained at 550° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm, diborane with a flow rate of 3 sccm and nitrogen with a flow rate of 25 slm for 7 seconds. The substrate was thereafter exposed to an etching gas containing chlorine gas with a flow rate of 20 sccm and nitrogen with a flow rate of 25 slm for 10 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 50 times to form an epitaxially grown silicon layer on the exposed monocrystalline portion of the substrate. The silicon epitaxial layer had a thickness of about 1,000 Å.
Example 12
Selective Epitaxy of Silicon Germanium Doped with B and Etched with Cl2
[0091] The substrate was placed into a process chamber heated and maintained at 550° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm, germane with a flow rate of 3 sccm, diborane with a flow rate of 3 sccm and nitrogen with a flow rate of 25 slm for 8 seconds. The substrate was thereafter exposed to an etching gas containing chlorine gas with a flow rate of 20 sccm and nitrogen with a flow rate of 25 slm for 10 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 50 times to form an epitaxially grown silicon-containing layer on the exposed monocrystalline portion of the substrate. The silicon-containing epitaxial layer had a thickness of about 1,700 Å.
Example 13
Selective Epitaxy of Silicon Germanium Doped with B and Etched with Cl2
[0092] The substrate was placed into a process chamber heated and maintained at 550° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm, diborane with a flow rate of 3 sccm and nitrogen with a flow rate of 25 slm for 7 seconds. The substrate surface was thereafter exposed to a flow of second deposition gas containing germane with a flow rate of 5 sccm and nitrogen with a flow rate of 25 slm for 7 seconds. The substrate was thereafter exposed to an etching gas containing chlorine gas with a flow rate of 20 sccm and nitrogen with a flow rate of 25 slm for 10 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 50 times to form an epitaxially grown silicon-containing layer on the exposed monocrystalline portion of the substrate. The silicon-containing epitaxial layer had a thickness of about 1,800 Å.
Example 14
Selective Epitaxy of Silicon Carbon Doped with P and Etched with Cl2
[0093] The substrate was placed into a process chamber heated and maintained at 550° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm, methylsilane with a flow rate of 1 sccm, phosphine with a flow rate of 3 sccm and nitrogen with a flow rate of 25 slm for 8 seconds. The substrate was thereafter exposed to an etching gas containing chlorine gas with a flow rate of 20 sccm and nitrogen with a flow rate of 25 slm for 10 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 80 times to form an epitaxially grown silicon-containing layer on the exposed monocrystalline portion of the substrate. The silicon-containing epitaxial layer had a thickness of about 1,600 Å.
Example 15
Selective Epitaxy of Silicon Carbon Doped with P and Etched with Cl2
[0094] The substrate was placed into a process chamber heated and maintained at 550° C. The process chamber was maintained at a pressure of about 15 Torr. The substrate surface was exposed to a flow of deposition gas containing silane with a flow rate of 100 sccm, phosphine with a flow rate of 3 sccm and nitrogen with a flow rate of 25 slm for 7 seconds. The substrate surface was thereafter exposed to a flow of second deposition gas containing methylsilane with a flow rate of 5 sccm and nitrogen with a flow rate of 25 slm for 7 seconds. The substrate was thereafter exposed to an etching gas containing chlorine gas with a flow rate of 20 sccm and nitrogen with a flow rate of 25 slm for 10 seconds. A cycle of deposition gas exposure and etching gas exposure was repeated 80 times to form an epitaxially grown silicon-containing layer on the exposed monocrystalline portion of the substrate. The silicon-containing epitaxial layer had a thickness of about 1,800 Å.
[0095] While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.
Claims
The invention claimed is:
1. A method for selectively and epitaxially forming a silicon-containing material on a substrate surface, comprising:
positioning a substrate comprising a monocrystalline surface and at least a dielectric surface into a process chamber; and
performing a deposition sequence at least two times, the deposition sequence comprising:
depositing an epitaxial material on the monocrystalline surface while simultaneously depositing a second material on the dielectric surface, the second material comprising a material selected from the group consisting of a polycrystalline material, an amorphous material, and combinations thereof; and subsequently
etching the second material, wherein the net result of the deposition sequence consists essentially of the epitaxial material selectively grown on the monocrystalline surface, wherein the epitaxial material comprises silicon-carbon.
2. A method for selectively and epitaxially forming a silicon-carbon-containing material on a substrate surface, comprising:
positioning a substrate comprising a monocrystalline surface and at least a dielectric surface into a process chamber; and
performing a deposition sequence at least two times, the deposition sequence, comprising:
depositing an epitaxial material on the monocrystalline surface while simultaneously depositing a second material on the dielectric surface, the second material comprising a material selected from the group consisting of a polycrystalline material, an amorphous material, and combinations thereof; and subsequently
etching the second material, wherein the net result of the deposition sequence consists essentially of the epitaxial material selectively grown on the monocrystalline surface, the epitaxial material having a graded carbon concentration.
3. The method of claim 2, wherein the deposition sequence is repeated until a predetermined thickness of the silicon-carbon-containing material is achieved.
4. The method of claim 2, wherein the second material is deposited to a thickness up to about an atomic layer in each sequence.
5. The method of claim 2, wherein the deposition sequence is conducted at a temperature within a range from about 500° C. to about 750° C.
6. The method of claim 2, wherein the etching comprises providing an etching gas comprising a compound selected from the group consisting of hydrogen chloride, chlorine gas, and combinations thereof.
7. A method for selectively and epitaxially forming a silicon-containing material on a substrate surface, comprising:
positioning a substrate comprising a monocrystalline surface and at least a dielectric surface into a process chamber; and
performing a deposition sequence at least two times, the deposition sequence comprising:
depositing a first epitaxial material on the monocrystalline surface while simultaneously depositing a second material on the dielectric surface, the second material comprising a material selected from the group consisting of a polycrystalline material, an amorphous material, and combinations thereof;
depositing a third epitaxial material on the first epitaxial material while simultaneously depositing a fourth material on the second material; and subsequently
etching the second and fourth materials, wherein the net result of the deposition sequence consists essentially of the first epitaxial material selectively grown on the monocrystalline surface and the third epitaxial material selectively grown on the first epitaxial material.
8. The method of claim 7, wherein the deposition sequence further comprises:
purging after either deposition.
9. The method of claim 7, wherein the deposition sequence further comprises:
purging after the etching.
10. The method of claim 7, wherein the deposition sequence is repeated until a predetermined thickness of the silicon-containing material is achieved.
Patent Citations (193)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3675619(A) | 1972-07-01 | Burd | Applicant |
| US4429324(A) | 1984-01-01 | Wilkens | Applicant |
| US4834831(A) | 1989-05-01 | Nishizawa et al. | Applicant |
| US5112439(A) | 1992-05-01 | Reisman et al. | Applicant |
| US5273930(A) | 1993-12-01 | Steele et al. | Applicant |
| US5288658(A) | 1994-02-01 | Ishihara | Applicant |
| US5294286(A) | 1994-03-01 | Nishizawa et al. | Applicant |
| US5360760(A) | 1994-11-01 | Hayashi | Applicant |
| US5372860(A) | 1994-12-01 | Fehlner et al. | Applicant |
| US5374570(A) | 1994-12-01 | Nasu et al. | Applicant |
| US5469806(A) | 1995-11-01 | Mochizuki et al. | Applicant |
| US5480818(A) | 1996-01-01 | Matsumoto et al. | Applicant |
| US5503875(A) | 1996-04-01 | Imai et al. | Applicant |
| US5521126(A) | 1996-05-01 | Okamura et al. | Applicant |
| US5527733(A) | 1996-06-01 | Nishizawa et al. | Applicant |
| US5674304(A) | 1997-10-01 | Fukada et al. | Applicant |
| US5693139(A) | 1997-12-01 | Nishizawa et al. | Applicant |
| US5796116(A) | 1998-08-01 | Nakata et al. | Applicant |
| US5807792(A) | 1998-09-01 | Ilg et al. | Applicant |
| US5819684(A) | 1998-10-01 | Hawkins et al. | Applicant |
| US5906680(A) | 1999-05-01 | Meyerson | Applicant |
| US5916365(A) | 1999-06-01 | Sherman | Applicant |
| US6025627(A) | 2000-02-01 | Forbes et al. | Applicant |
| US6042654(A) | 2000-03-01 | Comita et al. | Applicant |
| US6124158(A) | 2000-09-01 | Dautartas et al. | Applicant |
| US6144060(A) | 2000-11-01 | Park et al. | Applicant |
| US6159852(A) | 2000-12-01 | Nuttall et al. | Applicant |
| US6200893(B1) | 2001-03-01 | Sneh | Applicant |
| US6207487(B1) | 2001-03-01 | Kim et al. | Applicant |
| US6228728(B1) | 2001-05-01 | Furukawa et al. | Applicant |
| US6232196(B1) | 2001-05-01 | Raaijmakers et al. | Applicant |
| US6270572(B1) | 2001-08-01 | Kim et al. | Applicant |
| US6284646(B1) | 2001-09-01 | Leem | Applicant |
| US6284686(B1) | 2001-09-01 | Marlor | Applicant |
| US6287965(B1) | 2001-09-01 | Kang et al. | Applicant |
| US6291319(B1) | 2001-09-01 | Yu et al. | Applicant |
| US6305314(B1) | 2001-10-01 | Sneh et al. | Applicant |
| US6335280(B1) | 2002-01-01 | van der Jeugd | Applicant |
| US6342277(B1) | 2002-01-01 | Sherman | Applicant |
| US6348420(B1) | 2002-02-01 | Raaijmakers et al. | Applicant |
| US6352945(B1) | 2002-03-01 | Matsuki et al. | Applicant |
| US6358829(B2) | 2002-03-01 | Yoon et al. | Applicant |
| US6383955(B1) | 2002-05-01 | Matsuki et al. | Applicant |
| US6391749(B1) | 2002-05-01 | Park et al. | Examiner |
| US6391785(B1) | 2002-05-01 | Satta et al. | Applicant |
| US6391803(B1) | 2002-05-01 | Kim et al. | Applicant |
| US6399491(B2) | 2002-06-01 | Jeon et al. | Applicant |
| US6410463(B1) | 2002-06-01 | Matsuki | Applicant |
| US6451119(B2) | 2002-09-01 | Sneh et al. | Applicant |
| US6458718(B1) | 2002-10-01 | Todd | Applicant |
| US6462367(B2) | 2002-10-01 | Marsh et al. | Applicant |
| US6468924(B2) | 2002-10-01 | Lee et al. | Applicant |
| US6489241(B1) | 2002-12-01 | Thilderkvist et al. | Applicant |
| US6492283(B2) | 2002-12-01 | Raaijmakers et al. | Applicant |
| US6511539(B1) | 2003-01-01 | Raaijmakers | Applicant |
| US6534395(B2) | 2003-03-01 | Werkhoven et al. | Applicant |
| US6544900(B2) | 2003-04-01 | Raaijmakers et al. | Applicant |
| US6559520(B2) | 2003-05-01 | Matsuki et al. | Applicant |
| US6562720(B2) | 2003-05-01 | Thilderkvist et al. | Applicant |
| US6620670(B2) | 2003-09-01 | Song et al. | Applicant |
| US6630413(B2) | 2003-10-01 | Todd | Applicant |
| US6632279(B1) | 2003-10-01 | Ritala et al. | Applicant |
| US6797558(B2) | 2004-09-01 | Nuttall et al. | Applicant |
| US6821825(B2) | 2004-11-01 | Todd | Applicant |
| US6998305(B2) | 2006-02-01 | Arena et al. | Examiner |
| US2001/0000866(A1) | 2001-05-01 | Sneh et al. | Applicant |
| US2001/0020712(A1) | 2001-09-01 | Raaijmakers et al. | Applicant |
| US2001/0024387(A1) | 2001-09-01 | Raaijmakers et al. | Applicant |
| US2001/0024871(A1) | 2001-09-01 | Yagi | Applicant |
| US2001/0028924(A1) | 2001-10-01 | Sherman | Applicant |
| US2001/0034123(A1) | 2001-10-01 | Jeon et al. | Applicant |
| US2001/0041250(A1) | 2001-11-01 | Werkhoven et al. | Applicant |
| US2001/0046567(A1) | 2001-11-01 | Matsuki et al. | Applicant |
| US2001/0055672(A1) | 2001-12-01 | Todd | Applicant |
| US2002/0000598(A1) | 2002-01-01 | Kang et al. | Applicant |
| US2002/0016084(A1) | 2002-02-01 | Todd | Applicant |
| US2002/0031618(A1) | 2002-03-01 | Sherman | Applicant |
| US2002/0047151(A1) | 2002-04-01 | Kim et al. | Applicant |
| US2002/0060363(A1) | 2002-05-01 | Xi et al. | Applicant |
| US2002/0074588(A1) | 2002-06-01 | Lee | Applicant |
| US2002/0076837(A1) | 2002-06-01 | Hujanen et al. | Applicant |
| US2002/0090818(A1) | 2002-07-01 | Thilderkvist et al. | Applicant |
| US2002/0093042(A1) | 2002-07-01 | Oh et al. | Applicant |
| US2002/0098627(A1) | 2002-07-01 | Pomarede et al. | Applicant |
| US2002/0117399(A1) | 2002-08-01 | Chen et al. | Applicant |
| US2002/0145168(A1) | 2002-10-01 | Bojarczuk, Jr. et al. | Applicant |
| US2002/0155722(A1) | 2002-10-01 | Satta et al. | Applicant |
| US2002/0168868(A1) | 2002-11-01 | Todd | Applicant |
| US2002/0172768(A1) | 2002-11-01 | Endo et al. | Applicant |
| US2002/0173113(A1) | 2002-11-01 | Todd | Applicant |
| US2002/0173130(A1) | 2002-11-01 | Pomerede et al. | Applicant |
| US2002/0197831(A1) | 2002-12-01 | Todd et al. | Applicant |
| US2002/0197881(A1) | 2002-12-01 | Ramdani et al. | Applicant |
| US2003/0013320(A1) | 2003-01-01 | Kim et al. | Applicant |
| US2003/0015764(A1) | 2003-01-01 | Raaijmakers et al. | Applicant |
| US2003/0022528(A1) | 2003-01-01 | Todd | Applicant |
| US2003/0032281(A1) | 2003-02-01 | Werkhoven et al. | Applicant |
| US2003/0036268(A1) | 2003-02-01 | Brabant et al. | Applicant |
| US2003/0049942(A1) | 2003-03-01 | Haukka et al. | Applicant |
| US2003/0060057(A1) | 2003-03-01 | Raaijmakers et al. | Applicant |
| US2003/0072884(A1) | 2003-04-01 | Zhang et al. | Applicant |
| US2003/0072975(A1) | 2003-04-01 | Shero et al. | Applicant |
| US2003/0073293(A1) | 2003-04-01 | Ferro et al. | Examiner |
| US2003/0082300(A1) | 2003-05-01 | Todd et al. | Applicant |
| US2003/0089308(A1) | 2003-05-01 | Raaijmakers | Applicant |
| US2003/0089942(A1) | 2003-05-01 | Bhattacharyya | Applicant |
| US2003/0101927(A1) | 2003-06-01 | Raaijmakers | Applicant |
| US2003/0106490(A1) | 2003-06-01 | Jallepally et al. | Applicant |
| US2003/0108674(A1) | 2003-06-01 | Chung et al. | Applicant |
| US2003/0116804(A1) | 2003-06-01 | Visokay et al. | Applicant |
| US2003/0124262(A1) | 2003-07-01 | Chen et al. | Applicant |
| US2003/0129826(A1) | 2003-07-01 | Werkhoven et al. | Applicant |
| US2003/0143841(A1) | 2003-07-01 | Yang et al. | Applicant |
| US2003/0160277(A1) | 2003-08-01 | Bhattacharyya | Applicant |
| US2003/0162370(A1) | 2003-08-01 | Sukegawa et al. | Examiner |
| US2003/0166318(A1) | 2003-09-01 | Zheng et al. | Applicant |
| US2003/0172872(A1) | 2003-09-01 | Thakur et al. | Applicant |
| US2003/0173586(A1) | 2003-09-01 | Moriwaki et al. | Applicant |
| US2003/0185980(A1) | 2003-10-01 | Endo | Applicant |
| US2003/0186561(A1) | 2003-10-01 | Law et al. | Applicant |
| US2003/0188682(A1) | 2003-10-01 | Tois et al. | Applicant |
| US2003/0189208(A1) | 2003-10-01 | Law et al. | Applicant |
| US2003/0189232(A1) | 2003-10-01 | Law et al. | Applicant |
| US2003/0190423(A1) | 2003-10-01 | Yang et al. | Applicant |
| US2003/0190497(A1) | 2003-10-01 | Yang et al. | Applicant |
| US2003/0194853(A1) | 2003-10-01 | Jeon | Applicant |
| US2003/0198754(A1) | 2003-10-01 | Xi et al. | Applicant |
| US2003/0207555(A1) | 2003-11-01 | Takayanagi et al. | Applicant |
| US2003/0213560(A1) | 2003-11-01 | Wang et al. | Applicant |
| US2003/0213977(A1) | 2003-11-01 | Toyoda et al. | Applicant |
| US2003/0215570(A1) | 2003-11-01 | Seutter et al. | Applicant |
| US2003/0216981(A1) | 2003-11-01 | Tillman | Applicant |
| US2003/0232554(A1) | 2003-12-01 | Blum et al. | Applicant |
| US2003/0235961(A1) | 2003-12-01 | Metzner et al. | Applicant |
| US2004/0007747(A1) | 2004-01-01 | Visokay et al. | Applicant |
| US2004/0009307(A1) | 2004-01-01 | Koh et al. | Applicant |
| US2004/0009675(A1) | 2004-01-01 | Eissa et al. | Applicant |
| US2004/0016973(A1) | 2004-01-01 | Rotondaro et al. | Applicant |
| US2004/0023462(A1) | 2004-02-01 | Rotondaro et al. | Applicant |
| US2004/0033674(A1) | 2004-02-01 | Todd | Applicant |
| US2004/0033698(A1) | 2004-02-01 | Lee et al. | Applicant |
| US2004/0043149(A1) | 2004-03-01 | Gordon et al. | Applicant |
| US2004/0043569(A1) | 2004-03-01 | Ahn et al. | Applicant |
| US2004/0053484(A1) | 2004-03-01 | Kumar et al. | Applicant |
| US2004/0171238(A1) | 2004-09-01 | Arena et al. | Applicant |
| US2004/0226911(A1) | 2004-11-01 | Dutton et al. | Applicant |
| US2004/0235229(A1) | 2004-11-01 | Hokazono | Applicant |
| US2004/0253776(A1) | 2004-12-01 | Hoffmann et al. | Applicant |
| US2004/0259333(A1) | 2004-12-01 | Tomasini et al. | Applicant |
| US2005/0026400(A1) | 2005-02-01 | Todd et al. | Examiner |
| US2005/0054171(A1) | 2005-03-01 | Chu et al. | Applicant |
| US2005/0079691(A1) | 2005-04-01 | Kim et al. | Applicant |
| US2005/0079692(A1) | 2005-04-01 | Samoilov et al. | Examiner |
| US2005/0170604(A1) | 2005-08-01 | Orlowski et al. | Applicant |
| US2005/0208768(A1) | 2005-09-01 | Finlay et al. | Applicant |
| US2005/0241671(A1) | 2005-11-01 | Dong et al. | Applicant |
| US2005/0263795(A1) | 2005-12-01 | Choi et al. | Applicant |
| US2006/0046442(A1) | 2006-03-01 | Ramaswamy et al. | Applicant |
| EP1150345 | 2001-10-01 | Applicant | |
| GB2355727 | 2001-05-01 | Applicant | |
| JP5-047665 | 1983-02-01 | Applicant | |
| JP58-098917 | 1983-06-01 | Applicant | |
| JP62-171999 | 1987-07-01 | Applicant | |
| JP63-062313 | 1988-03-01 | Applicant | |
| JP1-143221 | 1989-06-01 | Applicant | |
| JP1-270593 | 1989-10-01 | Applicant | |
| JP2-172895 | 1990-07-01 | Applicant | |
| JP3-286522 | 1991-12-01 | Applicant | |
| JP5-102189 | 1993-04-01 | Applicant | |
| JP5-251339 | 1993-09-01 | Applicant | |
| JP6-196809 | 1994-07-01 | Applicant | |
| JP300649 | 1995-11-01 | Applicant | |
| JP2001-111000 | 2001-04-01 | Applicant | |
| JP2001-189312 | 2001-05-01 | Applicant | |
| JP2001-172767 | 2001-08-01 | Applicant | |
| WO98/20524 | 1998-05-01 | Applicant | |
| WO/16377 | 2000-03-01 | Applicant | |
| WO1/15220 | 2000-03-01 | Applicant | |
| WO/54320 | 2000-09-01 | Applicant | |
| WO1/17692 | 2001-03-01 | Applicant | |
| WO1/29893 | 2001-04-01 | Applicant | |
| WO1/40541 | 2001-06-01 | Applicant | |
| WO1/41544 | 2001-06-01 | Applicant | |
| WO1/66832 | 2001-09-01 | Applicant | |
| WO2/43115 | 2002-05-01 | Applicant | |
| WO2/45167 | 2002-06-01 | Applicant | |
| WO2/064853 | 2002-08-01 | Applicant | |
| WO2/065508 | 2002-08-01 | Applicant | |
| WO2/065516 | 2002-08-01 | Applicant | |
| WO2/065517 | 2002-08-01 | Applicant | |
| WO2/065525 | 2002-08-01 | Applicant | |
| WO2/080244 | 2002-10-01 | Applicant | |
| WO2/097864 | 2002-12-01 | Applicant |
Non-Patent Literature (22)
- PCT International Search Report and the Written Opinion for International Application No. PCT/US07/64038 dated Oct. 17, 2007.Applicant
- Agarwal, et al., “Challenges in integrating the High-K Gate Dielectric Film to the Conventional CMOS Process Flow,” Mat. Sac. Soc. Sump. Proc. vol. 670 (2001) pp. K2.1.1-K2.1.11.Applicant
- Bedair, S.M. “Atomic Layer Epitaxy Deposition Processes,” J. Vac. Sci. Technol. B., vol. 12, No. 1, Jan./Feb. 1994.Applicant
- Choi, et al. “Stability of TiB2 as a Diffusion Barrier on Silicon,” J. Electrochem. Soc., vol. 138, No. 10, Oct. 1991.Applicant
- Choi, et al. “The Effect of Annealing on Resistivity of Low Pressure Chemical Vapor Deposited Titanium Diboride,” J. Appl. Phys. 69(11), Jun. 1, 1991.Applicant
- Derbyshire, K “Applications of Integrated Processing,” Solid State Technology, Dec. 1994 pp. 45-48.Applicant
- Elers, et al. “NbCI5 as a Precursor in Atomic Layer Epitaxy,” Applied Surface Science 82/83 (1994) pp. 468-474.Applicant
- George, et al. “Surface Chemistry for Atomic Layer Growth,” J. Phys. Chem. 1996, 100, pp. 13121-13131.Applicant
- Hwang, et al. “Nanometer-Size α-PbO2 -Type TiO2 in Garnet: A Thermobarometer for Ultrahigh-Pressure Metamorphism,” Science Vo. 288 (Apr. 14, 2000) pp. 321-324.Applicant
- Jeong, et al. “Growth and Characterization of Aluminum Oxide (AI2O3) Thin Films by Plasma-Assisted Atomic Layer Controlled Deposition,” J. Korean Inst. Met. Mater., vol. 38, No. 10, Oct. 2000 pp. 1395-1399.Applicant
- Jeong, et al. “Plasma-assisted Atomic Layer Growth of High-Quality Aluminum Oxide Thin Films,” Jpn. J. Appl. Phys. 1, Regul. Pap. Short Notes, vol. 40, No. 1, Jan. 2001 pp. 285-289.Applicant
- Lee, et al. “Cyclic Technique for the Enhancement of Highly Oriented Diamond Film Growth,” Thin Solid Films 303 (1997) pp. 264-269.Applicant
- Min, et al., “Chemical Vapor Deposition of Ti-Si-N Films with Alternating Source Supply,” Mat. Res. Soc. Symp. Proc. vol. 564 (1999) pp. 207-210.Applicant
- Min, et al. “Metal-organic Atomic-layer Deposition of Titanium-silicon-nitride Films,” Applied Physics Letters, vol. 75, No. 11 (Sep. 11, 1999) pp. 1521-1523.Applicant
- Paranjpe, et al. “Atomic Layer Deposition of AIOx for Thin Film Head Gap Applications,” J. Electrochem. Soc., vol. 148, No. 9, Sep. 2001 pp. G465-G471.Applicant
- Ritala, et al. “Atomic Layer Deposition of Oxide Thin Films with Metal Alkoxides as Oxygen Sources,” Science vol. 288 Apr. 14, 2000 pp. 319-321.Applicant
- International Search Report mailed Feb. 22, 2005 for PCT/US2004/030872.Applicant
- Kamins, et al. “Kinetics of selective epitaxial deposition of Si1-xGex”, Applied Physics Letters, American Institute pf Physics. New York, US, vol. 61, No. 6, Aug. 10, 1992, pp. 669-671.Applicant
- Menon, et al. “Loading effect in SiGe layers grown by dichlorosilane-and silane-based epitaxy”, Journal of Applied Physics, American Institute of Physics. New York, US, vol. 90, No. 9, Nov. 1, 2001, pp. 4805-4809.Applicant
- Sedgwick, et al. “Selective SiGe and heavily As doped Si deposited at low temperature by atmospheric pressure chemical vapor deposition”, Journal of Vacuum Science and Technology: Part B, American Institute of Physics. New York, US, vol. 11, No. 3, May 1, 1993, pp. 1124-1128.Applicant
- Uchino, et al. “A Raised Source/Drain Technology Using In-situ P-doped SiGe and B-doped Si for 0.1 μm CMOS ULSIs”, Electron Devices Meeting, 1997, Technical Digest, International Washington, DC, USA Dec. 7-10, 1991, New York, NY, USA, IEEE, US, Dec. 7, 1997, pp. 479-482.Applicant
- PCT International Search Report and the Written Opinion for International Application No. PCT/US05/42991 dated Nov. 20, 2006.Applicant