US 7,364,798 B2Grant

Internal member for plasma-treating vessel and method of producing the same

Issue Date:2008-04-29

•30 Claims

Abstract

It is to propose an internal member for a plasma treating vessel having excellent resistances to chemical corrosion and plasma erosion under an environment containing a halogen gas and an advantageous method of producing the same, which is a member formed by covering a surface of a substrate with a multilayer composite layer consisting of a metal coating formed as an undercoat, Al₂O₃film formed on the undercoat as a middle layer and Y₂O₃sprayed coating formed on the middle layer as a top coat.

Metadata

Assignees

Tocalo Co., Ltd.
Tokyo Electron Limited

Inventors

Yoshio Harada
Junichi Takeuchi
Nobuyuki Nagayama
Kouji Mitsuhashi

Application Information

Application Number:US 11/072,448

Filing Date:2005-03-07

Priority Date:1999-12-10

Art Unit:1775

Classifications

IPC:

H01L21/00B32B3/10

Patent Drawings

This patent does not have any drawings.

Description

CROSS-REFERENCE TO RELATED APPLICATION

[0001] The present application is a continuation of U.S. application Ser. No. 10/849,797, filed May 21, 2004, now U.S. Pat. No. 6,884,516 which is a continuation of U.S. application Ser. No. 09/890,251, filed Aug. 3, 2001, now U.S. Pat. No. 6,783,863 which is the National Stage of PCT/JP00/08584, filed Dec. 4, 2000, which was not published in English under PCT Article 21(2), and which are hereby incorporated by reference in their entireties. The present application claims priority of Japanese Application No. 11-351546 filed Dec. 10, 1999.

TECHNICAL FIELD

[0002] This invention relates to an internal member for plasma-treating vessel having an excellent resistance to plasma erosion and a method of producing the same.

[0003] Particularly, the invention is a technique capable of applying to members used in a plasma treatment under a plasma environment using a treating gas containing a halogen element such as deposit shield, baffle plate, focus ring, insulator ring, shield ring, bellows cover, electrode and so on.

[0004] Moreover, the invention is applicable to internal parts for plasma-treating vessels in a field of a semiconductor manufacturing device, a manufacturing apparatus for a liquid crystal device or the like.

BACKGROUND ART

[0005] In general, a fluoride such as BF₃or NF₃, a chloride such as BCl₃or SnCl₄, a bromide such as HBr, or the like is used as a treating gas for various treatments in the manufacturing process of semiconductors, liquid crystal devices and the like, so that there is a problem that parts in the treating vessel are considerably corroded and damaged.

[0006] For instance, as a material used in the plasma-treating vessel for the semiconductor manufacturing apparatus, there are known a metallic material such as Al, Al alloy or the like, an anodized oxide film of Al covering the surface of the metallic material, a sprayed coating such as boron carbide or the like, a sintered body film of Al₂O₃, Si₃N₄or the like, and a high polymer film of fluorine resin, epoxy resin or the like. These materials are known to be subjected to a chemical damage when being contacted with a halogen ion indicating a strong corrosive property, or to an erosion damage through fines particles of SiO₂and Si₃N₄and an ion excited by a plasma.

[0007] Especially, a plasma is frequently used for more activating the reaction in the process using a halogen compound. However, the halogen compound is dissociated to atomic F, Cl, Br, I or the like indicating a very strong corrosive property under an environment using such a plasma. Even in this case, if a finely divided solid of SiO₂, Si₃N₄, Si, W or the like is existent in such an environment, the member used in the plasma-treating vessel is strongly subjected to not only the chemical corrosion but also the erosion damage through the above fine particles.

[0008] And also, the environment excited by the plasma is ionized even by a gas having no corrosive property such as Ar gas to cause a phenomenon of strongly impinging to a solid face (ion bombardment), so that various members arranged in the above vessel are subjected to a stronger damage.

[0009] Heretofore, there was a method of forming a then Al₂O₃film or the like as a technique adopted when being subjected to such a chemical corrosion or erosion damage. However, such a technique has the following problems.

[0010] (1) With respect to a material covered with Al₂O₃film (alumite) by subjecting Al and Al alloy to an anodization to provide corrosion resistance, there is a problem that the service life becomes shorter when being subjected to plasma erosion in an environment containing a halogen gas. And also, since it is an Al-containing film, AlF₃particles are created, which bring about a fear of degrading quality of semiconductor product manufactured.

[0011] (2) There is a technique that a dense film of oxide, carbide, nitride, fluoride or the like of Group 3a element in the Periodic Table such as Sc, Y, La, Ce, Yb, Eu, Dy or the like is formed on the surface of a part through PVD or CVD process, or a single crystal of Y₂O₃is applied thereto (JP-A-10-4083). However, this technique has problems that the film forming rate is slow and the productivity is poor and plural film members (composite film) can not simultaneously be formed.

[0012] It is, therefore, an object of the invention to propose a surface-treated member for plasma-treating vessel or the like having large resistances to damage due to chemical corrosion and damage through plasma erosion under environment containing a halogen gas as well as a method of producing the same.

DISCLOSURE OF THE INVENTION

[0013] The invention solves the aforementioned problems and drawbacks of the conventional techniques by adopting means as mentioned below. That is, the construction of the invention is as follows:

[0014] (1) A cover member comprising a substrate and a layer of Y₂O₃sprayed coating having a porosity of 0.2–10% and a thickness of 50–2000 μm formed on a surface of the substrate through a thermal spraying process.

[0015] (2) A cover member comprising a substrate, and a composite layer consisting of a coating of one or more metals or alloys selected from Ni and an alloy thereof, W and an alloy thereof, Mo and an alloy thereof and Ti and an alloy thereof, which are excellent in an adhesion property to Y₂O₃sprayed coating, formed at a thickness of 50–500 μm as an undercoat on a surface of the substrate under a plasma generating condition in an environment containing a halogen compound through, preferably, a thermal spraying process and a Y₂O₃sprayed coating formed at a thickness of 50–2000 μm on the undercoat in case of an environment having a strong corrosion property.

[0016] (3) A cover member comprising a substrate and a multilayer composite layer consisting of the above metal coating (preferably sprayed coating) formed on a surface of the substrate as an undercoat, a Al₂O₃coating (preferably sprayed coating) formed on the undercoat as a middle layer and the above Y₂O₃sprayed coating formed on the middle layer as a topcoat through thermal spraying in case of an environment having a strong corrosion property.

[0017] (4) A cover member comprising a substrate and a multilayer composite layer consisting of the above metal coating (preferably sprayed coating) formed on a surface of the substrate as an undercoat, a film of Al₂O₃and Y₂O₃(preferably sprayed coating) formed on the undercoat as a middle layer and the above Y₂O₃sprayed coating formed on the middle layer as a topcoat through thermal spraying in case of an environment having a strong corrosion property.

[0018] (5) A cover member is covered with the Y₂O₃sprayed coating directly formed on the surface of the substrate or indirectly formed through the undercoat or middle layer in the above method, wherein the sprayed coating is obtained by using Y₂O₃powder having a purity of not less than 95% and adopting a spraying method selected from plasma-spraying the powder in air, plasma-spraying in an Ar gas containing no oxygen under a reduced pressure, high-speed flame spraying, explosion spraying and the like.

[0019] Among them, the method of plasma-spraying under the reduced pressure of Ar gas is also effective for the improvement of the corrosion resistance.

BEST MODE FOR CARRYING OUT THE INVENTION

[0020] The inventors have made studies in order to solve the aforementioned problems of the conventional techniques and confirmed that the damage of the internal member for the plasma-treating vessel is a damage due to chemical corrosion through a halogen gas and a damage due to plasma erosion. And also, it has been found that when the member is used in an environment containing the halogen excited by the plasma, it is important to prevent the damage caused by the resistance to the plasma erosion, which is then effective to prevent the chemical corrosion.

[0021] To this end, the inventors have made mainly the formation of the coating effective for the resistance to plasma erosion. As a result, the above member according to the invention is developed.

[0022] That is, the invention adopted as means for solving the above subject is fundamentally a member obtained by forming a sprayed coating consisting of only Y₂O₃on a surface of a substrate such as metal, ceramic, carbon material or the like through thermal spraying process. In case of a strong corrosive environment using the above member, there is developed a member obtained by forming an undercoat of a metal having a strong resistance to halogen gas corrosion beneath the above Y₂O₃sprayed coating and further forming a middle layer of Al₂O₃or Y₂O₃.

[0023] The construction of the member according to the invention is described in detail below.

(1) Substrate

[0024] As a substrate for forming the sprayed coating, various steels inclusive of stainless steel, aluminum and aluminum alloy, tungsten and tungsten alloy, titanium and titanium alloy, molybdenum and molybdenum alloy, carbon and oxide or non-oxide ceramic sintered body, a carbonaceous material and the like are favorable.

[0025] Moreover, copper and copper alloy are unfavorable because they are subjected to plasma erosion or corrosion through a halogen compound to bring about environmental contamination. Therefore, if the use of copper or copper alloy is required in view of apparatus construction, they are required to be covered with Cr, Ni or the like by electrolytic plating, chemical plating, vapor deposition or the like.

(2) Construction of Sprayed Coating

[0026] The sprayed coating is preferable to be formed on the surface of the substrate by subjecting the substrate to a shot blast treatment and then directly thermal spraying Y₂O₃, or by forming a film or sprayed coating of a metal material having a strong resistance to corrosion through a halogen gas as an undercoat layer on the surface of the substrate by PVD treatment, CVD treatment or thermal spraying treatment and then spraying Y₂O₃powder on the undercoat as a top coat. In the latter case, the film thickness of the metal undercoat (sprayed coating or the like) is within a range of 50–500 μm. When the undercoat layer is thinner than 50 μm, the action and effect as the undercoat become weak, while when it exceeds 500 μm, the effect is saturated and there is no meaning on the thickening.

[0027] As the metal material for the undercoat, nickel and nickel alloy, tungsten and tungsten alloy, molybdenum and molybdenum alloy, titanium and titanium alloy and so on are preferable.

[0028] On the other hand, the Y₂O₃sprayed coating as a top coat is favorable to have a thickness of 50–2000 μm even when it is directly formed on the surface of the substrate or when it is sprayed onto the undercoat to form a composite layer or further when Al₂O₃or Al₂O₃+Y₂O₃coated film is formed as a middle layer. Because, when the thickness is less than 50 μm, the effect on the prevention of the damage due to the plasma erosion is poor, while when it exceeds 2000 μm, the effect is saturated and there is no meaning in the economical reason.

[0029] Moreover, the porosity of the Y₂O₃sprayed coating as a top coat is preferably within a range of 0.5–10%. It is difficult to produce the sprayed coating having the porosity of less than 0.5% by the spraying method, while the coating having the porosity of more than 10% is poor in the corrosion resistance and the resistance plasma erosion.

(3) Y₂O₃Sprayed Coating as an Outermost Layer on Member

[0030] A most characteristic construction of the invention lies in that Y₂O₃is adopted as a material indicating the resistance to plasma erosion in an environment containing a halogen gas and formed as a sprayed coating layer as a structure of an outermost surface layer of the substrate. As a result of the inventors' studies, it has been found that since Y₂O₃has a specific gravity of 4.84 and a melting point of 2410° C. and is strong in the chemical bonding force to oxygen, it maintains a stable state even if the action of plasma erosion is suffered in the atmosphere containing the halogen gas. In this case, however, it is required to use Y₂O₃having a purity of not less than 95%. If an impurity such as Fe, Mg, Cr, Al, Ni, Si or the like is contained as an oxide, the erosion resistance is unfavorably lowered. The purity is more favorable to be not less than 98%.

[0031] Moreover, Al₂O₃as a middle layer formed just beneath the Y₂O₃sprayed coating is chemically stable and less in the change under environment of plasma spraying at atmospheric pressure or plasma spraying under a reduced pressure and serves to compensate the resistance to plasma erosion of Y₂O₃.

(4) Coating Method

a. Formation of Sprayed Coating

[0032] In the invention, Y₂O₃coating as a top coat in at least outermost layer is a sprayed coating. Further, it is preferable that the whole structure of the coating is rendered into the following multilayer structure in order to strengthen the sprayed coating of the top coat.

[0033] That is, an undercoat of a metal sprayed coating is formed on the surface of the substrate and Al₂O₃sprayed coating or a mixture sprayed coating of Al₂O₃and Y₂O₃in the gradient compounding is formed thereon as a middle layer and further Y₂O₃sprayed coating is formed thereon as a top coat.

[0034] The reason why the above coating structure is preferable is, due to the fact that by forming as the middle layer Al₂O₃having excellent corrosion resistance and resistance to plasma erosion as compared with the metal sprayed coating is rendered the sprayed coating into a multilayer structure, and the through-holes of the coating is decreased to improve the corrosion resistance and the resistance to erosion. Furthermore, Al₂O₃as the middle layer develops good adhesion property to both of the undercoat and the top coat. In this meaning, the middle layer is favorable to be a mixture layer of Al₂O₃and Y₂O₃. In this case, the mixture layer is favorable to be based on the gradient compounding that the Al₂O₃concentration at the undercoat side becomes high and the Y₂O₃concentration at the top coat side becomes high. The formation of such a middle layer can easily be carried out by adopting a spraying process, so that it is said to be a preferable embodiment that the middle layer is formed as a sprayed coating. Moreover, the thickness of the middle layer is favorable to be within the same range as the Y₂O₃sprayed coating of the top coat.

[0035] In the invention, a plasma spraying process under an atmospheric pressure or a plasma spraying process in an atmosphere containing substantially no oxygen is favorable for forming a sprayed coating of metal or Al₂O₃or Y₂O₃, but it is also possible to conduct a high-speed flame spraying process or an explosion spraying process.

b. Formation of Undercoat, Middle Layer Through CVD Processor PVD Process

[0036] In the CVD process, steam of a halogen compound of a desired metal is reduced by hydrogen or the like and then oxidized by oxygen or an oxygen compound, and changed into an oxide film by heating in air.

[0037] In the PVD process, a sintered body or powder is used as a starting material and evaporated by irradiating an electron beam to precipitate onto the surface of the substrate to form a film.

[0038] In general, the formation of the film through CVD process or PVD process is suitable for forming thin film (e.g. about 50 μm).

(5) Environment Using the Member According to the Invention

[0039] The Y₂O₃sprayed coating covered onto the surface of the member according to the invention is particularly useful for the use under plasma environment generated in an atmosphere containing a halogen compound.

[0040] Of course, the invention is effective even to a plasma erosion action in an environment containing no halogen element or halogen compound such as N₂, H₂or the like. In this case, erosion damage becomes gentle as compared with the environment containing the halogen element or compound, so that the sprayed coating member according to the invention develops a stable performance over a long time.

EXAMPLE

Example 1

[0041] In this example, a one-side surface of an aluminum test piece (size: width 50 mm×length 50 mm×thickness 5 mm) is roughened by a shot blast treatment and Y₂O₃sprayed coating having a thickness of 300 μm is formed by using Y₂O₃spraying material through a plasma spraying process under an atmospheric pressure or a plasma spraying process under a reduced pressure controlled to an atmosphere pressure of 50–200 hPa with Ar gas, respectively.

[0042] And also, an undercoat of Ni-20% Al alloy is formed on a one-side surface of an aluminum test piece at a thickness of 100 μm by a plasma spraying process under an atmospheric pressure and the above Y₂O₃is formed thereon at a thickness of 300 μm as a top coat.

[0043] Thereafter, the porosity and adhesion strength of the Y₂O₃sprayed coating formed on the surfaces of these test pieces are measured and thermal shock test (test of repeating a cycle of an operation that the piece is heated in an electric furnace held at 500° C. for 20 minutes and cooled in air at the outside of the furnace 10 times) is conducted. Moreover, Al₂O₃sprayed coatings formed under the same conditions at the same steps as mentioned above are used as a comparative example.

[0044] The test results are shown in Table 1.

[0045] All of the coatings according to the invention, i.e. Y₂O₃sprayed coatings directly coated on the surface of the test piece (Nos. 1, 3) and Y₂O₃sprayed coatings formed on the undercoat (Nos. 2, 4) show good adhesion property and resistance to thermal shock, which are in no way inferior to those of the Al₂O₃film. Particularly, the Y₂O₃coating formed by the plasma spraying process under a reduced pressure is smaller in the porosity as compared with that of the coating formed by the spraying process under an atmospheric pressure and can expect the good corrosion resistance.

[0046]

	TABLE 1

	Structure of			Visual
	coating		Adhesion	appearance
	Spraying	Under	Top	Porosity	strength	in thermal
No.	Process	coat	coat	(%)	(MPa)	shock test	Remarks

1	Atmospheric	None	Y₂O₃	5–9	35–38	No peeling	Example
2	plasma	Ni—20Al	Y₂O₃	6–8	38–41	No peeling
	spray
3	Low	None	Y₂O₃	0.2–3	40–41	No peeling
4	pressure	Ni—20Al	Y₂O₃	0.3–4	40–44	No peeling
	plasma
	spray
5	Atmospheric	None	Al₂O₃	8–12	38–42	No peeling	Comparative
6	plasma	Ni—20Al	Al₂O₃	9–12	35–44	No peeling	Example
	spray
7	Low	None	Al₂O₃	0.5–5	38–44	No peeling
8	pressure	Ni—20Al	Al₂O₃	0.6–7	39–43	No peeling
	plasma
	spray

(Note)
(1) Coating thickness: undercoat 100 μm, top coat 300 μm
(2) Adhesion strength is according to a test method of adhesion strength defined in test method of ceramic coating in JIS H8666
(3) Thermal shock test: 500° C. × 20 min → room temperature (air cooling) observation of appearance after repetition 10 times.

Example 2

[0047] In this example, an aluminum substrate of 50 mm×100 mm×5 mm thickness is used and subjected to a surface treatment as shown in Table 2 and a test piece having a size of 20 mm×20 mm×5 mm is cut out from the substrate and a portion is masked so as to expose the surface treated face in a range of 10 mm×10 mm and irradiated for 20 hours under the following conditions and measured is a damage quantity through plasma erosion as a reduced thickness.

(1) Environmental Gas and Flow Rate Condition

[0048] A mixed gas of CF₄, Ar and O₂is an atmosphere under the condition.

CF₄/Ar/O₂=100/1000/10 (flow rate cm3 per 1 minute)

(2) Plasma Irradiation Output

[0049] High frequency power: 1300 W

[0050] Pressure: 133.3 Pa

[0051] The test results are shown in Table 2. As seen from the results of Table 2, the anodized film (No. 8) of a comparative example (existing technique) and B₄C sprayed coating (No. 10) are large in the damage quantity through the plasma erosion and are not put into practical use. Moreover, the Al₂O₃coating (No. 9) shows a relatively good resistance to plasma erosion among the comparative examples.

[0052] On the contrary, the Y₂O₃sprayed coatings according to the invention develop a very excellent resistance to plasma erosion and maintain good performances even in an environment containing a halogen compound.

[0053]

TABLE 2

				Damaged
			Presence	depth
			or	through
	Sprayed	Surface	absence of	erosion
No.	materials	treatment	undercoat	(μm)	Remarks


1	Y₂O₃(99.9%)	Spraying	Presence	6.2	Example
2			Absence	6.1
3	Y₂O₃(99.8%)	Spraying	Presence	7.6
4			Absence	7.2
5	Y₂O₃(99.5%)	Spraying	Presence	6.5
6			Absence	6.3
7	Y₂O₃(99.9%)	PVD	Absence	6.6	Comparative
8	Al₂O₃	Anodizing	Absence	39.5	example
9	Al₂O₃	Spraying	Presence	8.1
10	B₄C	Spraying	Presence	28.0
11	Quartz	—	Absence	39.0

(Note)
(1) The spraying is carried out by a plasma spraying process under an atmospheric pressure and the thickness of undercoat is 80 μm and the thickness of top coat such as Y₂O₃, Al₂O₃or the like is 200 μm.
(2) Material of undercoat is 80% Ni—20% Al.
(3) Anodizing is carried out according to AA25 defined in JIS H8601.

Example 3

[0054] In this example, 80% Ni-20% Al of 80 μm in thickness as an undercoat, Al₂O₃or a mixture of Al₂O₃50 vol %/Y₂O₃50 vol % of 100 μm as a middle layer and Y₂O₃of 200 μm in thickness are formed on an aluminum substrate of width 50 mm×length 100 mm×thickness 5 mm by a plasma spraying process under an atmospheric pressure, respectively, and then a plasma erosion test is carried out under the same conditions as in Example 2.

[0055] As a result, since the Y₂O₃sprayed coating is formed on the outermost surface layer portion (top coat), even when Al₂O₃or the mixture layer of Al₂O₃/Y₂O₃is formed as the middle layer, the resistance to plasma erosion is not influenced in the sprayed coating according to the invention and only a loss of 6.1–7.5 μm is observed by irradiation for 20 hours, and hence it is recognized to develop sufficient performances even in the multilayer structure coating.

Example 4

[0056] In this example, with respect to a test piece obtained by anodizing the existing aluminum substrate (alumite treatment) and a test piece formed by covering a 80% Ni-20% Al alloy coating of 100 μm in thickness on the substrate as an undercoat and coating a Y₂O₃coating of 250 μm in thickness thereon as a top coat through plasma spraying process is carried out a plasma etching under the following conditions to measure the number of particles flied through the etching as particle numbers adhered onto a surface of a silicon wafer of 8 inches in diameter placed on the same chamber. Moreover, the number of particles adhered is examined by a surface inspection apparatus based on particles having a particle size of not less than approximately 0.2 μm.

(1) Environmental Gas and Flow Rate Condition

[0057] A mixed gas of CHF₃, O₂and Ar is an atmosphere under the condition.

CHF₃/O₂/Ar=80/100/160 (flow rate cm3 per 1 minute)

(2) Plasma Irradiation Output

[0058] High frequency power: 1300 W

[0059] Pressure: 4 Pa

[0060] Temperature: 60° C.

[0061] As a result of this experiment, in the anodized test piece (alumite film), the particle number exceeds 30 particles as a particle control value in the general chamber after 17.5 hours of the plasma irradiation and is not less than 150 particles after 25 hours. The composition of the particle consists of Al and F.

[0062] On the contrary, in the Y₂O₃sprayed coating according to the invention, the particle number only exceeds the control limit value even after 70 hours of the irradiation and the excellent resistance to plasma erosion is indicated.

INDUSTRIAL APPLICABILITY

[0063] As mentioned above, according to the invention, the member obtained by directly forming Y₂O₃sprayed coating on the metallic or non-metallic substrate or by forming a metallic undercoat and then forming Y₂O₃sprayed coating shows an excellent resistance when it is used under an environment subjected to plasma erosion action in a gas atmosphere containing a halogen compound. To this end, even when plasma etching operation is continued over a long time, the contamination through particles in the chamber is less and it is possible to efficiently produce a high quality product. And also, the contamination rate of the particle in the chamber becomes slower, so that the interval for the cleaning operation becomes long and the improvement of the productivity can be expected. As a result, the members according to the invention are very effective as an internal member for a plasma treating vessel in the field of semiconductor production apparatus, liquid crystal device or the like.

Claims

What is claimed:

1. An internal member for a plasma treating vessel comprising:

a substrate configured to be coupled to the plasma treating vessel; and

a Y₂O₃sprayed coating covered on a surface of the substrate.

2. An internal member for a plasma treating vessel according to claim 1, wherein the substrate is a baffle plate.

3. An internal member for a plasma treating vessel according to claim 1, wherein the substrate is a deposit shield.

4. An internal member for a plasma treating vessel according to claim 1, wherein the substrate is a focus ring.

5. An internal member for a plasma treating vessel according to claim 1, wherein the substrate is an insulator ring.

6. An internal member for a plasma treating vessel according to claim 1, wherein the substrate is a shield ring.

7. An internal member for a plasma treating vessel according to claim 1, wherein the substrate is a bellows cover.

8. An internal member for a plasma treating vessel according to claim 1, wherein the substrate is an electrode.

9. An internal member for a plasma treating vessel according to claim 1, wherein the Y₂O₃sprayed coating covered onto the surface of the member is used under plasma environment generated in an atmosphere containing a halogen compound.

10. An internal member for a plasma treating vessel according to claim 9, wherein the halogen compound is fluorine.

11. An internal member for a plasma treating vessel according to claim 1, wherein the substrate is aluminum, aluminum alloy, steel, stainless steel, titanium, a titanium alloy, tungsten, a tungsten alloy, molybdenum, a molybdenum alloy, carbon, an oxide, a non-oxide ceramic sintered body or a carbonaceous material.

12. An internal member for a plasma treating vessel according to claim 1, wherein the Y₂O₃sprayed coating is formed in an environment containing substantially no oxygen.

13. An internal member for a plasma treating vessel according to claim 1, wherein the Y₂O₃sprayed coating is a coating having a porosity of 5–10%.

14. A method of producing an internal member for a plasma treating vessel, which comprises covering Y₂O₃on a surface of a substrate configured to be coupled to the plasma treating vessel through a spraying process to form a Y₂O₃sprayed coating.

15. A method of producing an internal member for a plasma treating vessel according to claim 14, wherein the substrate is a baffle plate.

16. A method of producing an internal member for a plasma treating vessel according to claim 14, wherein the substrate is a deposit shield.

17. A method of producing an internal member for a plasma treating vessel according to claim 14, wherein the substrate is a focus ring.

18. A method of producing an internal member for a plasma treating vessel according to claim 14, wherein the substrate is an insulator ring.

19. A method for producing an internal member for a plasma treating vessel according to claim 14, wherein the substrate comprises a shield ring.

20. A method of producing an internal member for a plasma treating vessel according to claim 14, wherein the substrate is a bellows cover.

21. A method of producing an internal member for a plasma treating vessel according to claim 14, wherein the substrate is an electrode.

22. A method of producing an internal member for a plasma treating vessel according to claim 14, wherein the Y₂O₃sprayed coating covered onto the surface of the member is used under plasma environment generated in an atmosphere containing a halogen compound.

23. A method of producing an internal member for a plasma treating vessel according to claim 22, wherein the halogen compound is fluorine.

24. A method of producing an internal member for a plasma treating vessel according to claim 14, wherein the substrate is aluminum, aluminum alloy, steel, stainless steel, titanium, a titanium alloy, tungsten, a tungsten alloy, molybdenum, a molybdenum alloy, carbon, an oxide, a non-oxide ceramic sintered body, or a carbonaceous material.

25. A method of producing an internal member for a plasma treating vessel according to claim 14, wherein the Y₂O₃sprayed coating is a coating having a porosity of 5–10%.

26. An internal member for a plasma treating vessel comprising:

a substrate configured to be coupled to the plasma treating vessel; and

a Y₂O₃sprayed coating covered on a surface of the substrate, the Y₂O₃sprayed coating has an adhesion strength to the substrate ranging from 35 MPa to 38 MPa, when the substrate is aluminum and the sprayed coating is formed using an atmospheric plasma spray.

27. An internal member for a plasma treating vessel comprising:

a substrate configured to be coupled to the plasma treating vessel; and

a Y₂O₃sprayed coating covered on a surface of the substrate, the Y₂O₃sprayed coating has an adhesion strength to the substrate ranging from 40 MPa to 41 MPa, when the substrate is aluminum and the sprayed coating is formed using a low pressure plasma spray.

28. An internal member for a plasma treating vessel comprising:

a substrate configured to be coupled to the plasma treating vessel; and

a Y₂O₃sprayed coating covered on a surface of the substrate, the Y₂O₃sprayed coating has an adhesion strength to the substrate ranging from 38 MPa to 41 MPa, when the substrate is a surface having nickel 20% aluminum alloy and the sprayed coating is formed using an atmospheric plasma spray.

29. An internal member for a plasma treating vessel comprising:

a substrate configured to be coupled to the plasma treating vessel; and

a Y₂O₃sprayed coating covered on a surface of the substrate, the Y₂O₃sprayed coating has an adhesion strength to the substrate ranging from 40 MPa to 44 MPa, when the substrate is a surface having nickel 20% aluminum alloy and the sprayed coating is formed using a low pressure plasma spray.

30. An internal member for a plasma treating vessel comprising:

a substrate configured to be coupled to the plasma treating vessel;

a Y₂O₃sprayed coating covered on a surface of the substrate; and

an erosion depth into the Y₂O₃sprayed coating is less than 7.6 microns, when the Y₂O₃sprayed coating is exposed to plasma irradiation formed using a pressure of 133.3 Pa, a flow rate of CF₄of 100 sccm, a flow rate of argon of 1000 sccm a flow rate of O₂of 10 sccm, and a radio frequency power of 1300 W for 20 hours.

Patent Citations (62)

Patent	Date	Inventor	Cited By
US4877757(A)	1989-10-01	York et al.	Examiner
US5126102(A)	1992-06-01	Takahashi et al.	Applicant
US5489449(A)	1996-02-01	Umeya et al.	Applicant
US5637237(A)	1997-06-01	Oehrlein et al.	Applicant
US5798016(A)	1998-08-01	Oehrlein et al.	Applicant
US5834070(A)	1998-11-01	Movchan et al.	Applicant
US5955182(A)	1999-09-01	Yasuda et al.	Applicant
US5968377(A)	1999-10-01	Yuasa et al.	Examiner
US6120640(A)	2000-09-01	Shih et al.	Applicant
US6383964(B1)	2002-05-01	Nakahara et al.	Applicant
US6613442(B2)	2003-09-01	O'Donnell et al.	Examiner
US6632549(B1)	2003-10-01	Ohashi et al.	Applicant
US6738863(B2)	2004-05-01	Butterworth et al.	Applicant
US6776873(B1)	2004-08-01	Sun et al.	Examiner
US6783863(B2)	2004-08-01	Harada et al.	Applicant
US6783875(B2)	2004-08-01	Yamada et al.	Examiner
US6798519(B2)	2004-09-01	Nishimoto et al.	Examiner
US6805952(B2)	2004-10-01	Chang et al.	Examiner
US6806949(B2)	2004-10-01	Ludviksson et al.	Examiner
US6811651(B2)	2004-11-01	Long	Examiner
US6833279(B2)	2004-12-01	Choi	Examiner
US6837966(B2)	2005-01-01	Nishimoto et al.	Examiner
US6852433(B2)	2005-02-01	Maeda	Examiner
US6875477(B2)	2005-04-01	Trickett et al.	Examiner
US6884516(B2)	2005-04-01	Harada et al.	Applicant
US6894769(B2)	2005-05-01	Ludviksson et al.	Examiner
US2001/0003271(A1)	2001-06-01	Otsuki	Examiner
DE9421671	1996-08-01		Applicant
EP326318	1989-08-01		Applicant
EP799904	1997-10-01		Applicant
GB2252567	1992-08-01		Applicant
JP61-207566	1986-09-01		Applicant
JP62-067161	1987-03-01		Applicant
JP63-000450	1988-01-01		Applicant
JP64039728	1989-02-01		Applicant
JP3115535	1991-05-01		Applicant
JP5-117064	1993-05-01		Applicant
JP5238859	1993-09-01		Applicant
JP6057396	1994-03-01		Applicant
JP6136505	1994-05-01		Applicant
JP6142822	1994-05-01		Applicant
JP6-256926	1994-09-01		Applicant
JP6-287739	1994-10-01		Applicant
JP7126827	1995-05-01		Applicant
JP7176524	1995-07-01		Applicant
JP8037180	1996-02-01		Applicant
JP8339895	1996-12-01		Applicant
JP9069554	1997-03-01		Applicant
JP9-228070	1997-09-01		Applicant
JP9272987	1997-10-01		Applicant
JP10-4083	1998-01-01		Applicant
JP10-45461	1998-02-01		Applicant
JP10-45467	1998-02-01		Applicant
JP10-226869	1998-08-01		Applicant
JP10-251871	1998-09-01		Applicant
JP11-001757	1999-01-01		Applicant
JP11080925	1999-03-01		Applicant
JP11-310451	1999-11-01		Applicant
JP2001-31484	2001-02-01		Applicant
JP11207161	2001-02-01		Applicant
KR8095	1994-09-01		Applicant
KR1999-13565	1998-03-01		Applicant

Non-Patent Literature (27)

English Language Abstract of JP 61-207566.Applicant
English Language Abstract of JP 10-251871.Applicant
English Language Abstract of JP 10-4083.Applicant
English Language Abstract of JP 10-45467.Applicant
English Language Abstract of JP 5-117064.Applicant
English Language Abstract of JP 10-45461.Applicant
English Language Abstract of JP 2001-31484.Applicant
English Language Abstract of JP 6136505.Applicant
English Language Abstract of JP 8037180.Applicant
English Language Abstract of JP 5238859.Applicant
English Language Abstract of JP 9272987.Applicant
English Language Abstract of JP 6057396.Applicant
English Language Abstract of JP 64039728.Applicant
English Language Abstract of JP 8339895.Applicant
English Language Abstract of JP 7176524.Applicant
English Language Abstract of JP 6142822.Applicant
English Language Abstract of JP 11-080925.Applicant
English Language Abstract of JP 3115535.Applicant
English Language Abstract of JP 7126827.Applicant
JIS using Series, “Spraying Techniques Manual” p. 95 (Oct. 30, 1998, Japanese Standard Association), with English Translation.Applicant
English Language Abstract of JP 9069554.Applicant
English Language Abstract of JP 11-001757.Applicant
English Language Abstract of JP 10-226869.Applicant
English Language Abstract of JP 09-228070.Applicant
English Language Abstract of JP 06-287739.Applicant
English Language Abstract of JP 63-000450.Applicant
English Language Abstract of JP 62-067161.Applicant

Abstract

Description

CROSS-REFERENCE TO RELATED APPLICATION

TECHNICAL FIELD

[0002] This invention relates to an internal member for plasma-treating vessel having an excellent resistance to plasma erosion and a method of producing the same.

BACKGROUND ART

DISCLOSURE OF THE INVENTION

[0013] The invention solves the aforementioned problems and drawbacks of the conventional techniques by adopting means as mentioned below. That is, the construction of the invention is as follows:

[0019] Among them, the method of plasma-spraying under the reduced pressure of Ar gas is also effective for the improvement of the corrosion resistance.

BEST MODE FOR CARRYING OUT THE INVENTION

[0021] To this end, the inventors have made mainly the formation of the coating effective for the resistance to plasma erosion. As a result, the above member according to the invention is developed.

[0023] The construction of the member according to the invention is described in detail below.

(1) Substrate

(2) Construction of Sprayed Coating

[0027] As the metal material for the undercoat, nickel and nickel alloy, tungsten and tungsten alloy, molybdenum and molybdenum alloy, titanium and titanium alloy and so on are preferable.

(3) Y₂O₃Sprayed Coating as an Outermost Layer on Member

(4) Coating Method

a. Formation of Sprayed Coating

b. Formation of Undercoat, Middle Layer Through CVD Processor PVD Process

[0037] In the PVD process, a sintered body or powder is used as a starting material and evaporated by irradiating an electron beam to precipitate onto the surface of the substrate to form a film.

[0038] In general, the formation of the film through CVD process or PVD process is suitable for forming thin film (e.g. about 50 μm).

(5) Environment Using the Member According to the Invention

EXAMPLE

Example 1

[0044] The test results are shown in Table 1.

[0046]

	TABLE 1

	Structure of			Visual
	coating		Adhesion	appearance
	Spraying	Under	Top	Porosity	strength	in thermal
No.	Process	coat	coat	(%)	(MPa)	shock test	Remarks

1	Atmospheric	None	Y₂O₃	5–9	35–38	No peeling	Example
2	plasma	Ni—20Al	Y₂O₃	6–8	38–41	No peeling
	spray
3	Low	None	Y₂O₃	0.2–3	40–41	No peeling
4	pressure	Ni—20Al	Y₂O₃	0.3–4	40–44	No peeling
	plasma
	spray
5	Atmospheric	None	Al₂O₃	8–12	38–42	No peeling	Comparative
6	plasma	Ni—20Al	Al₂O₃	9–12	35–44	No peeling	Example
	spray
7	Low	None	Al₂O₃	0.5–5	38–44	No peeling
8	pressure	Ni—20Al	Al₂O₃	0.6–7	39–43	No peeling
	plasma
	spray

(Note)
(1) Coating thickness: undercoat 100 μm, top coat 300 μm
(2) Adhesion strength is according to a test method of adhesion strength defined in test method of ceramic coating in JIS H8666
(3) Thermal shock test: 500° C. × 20 min → room temperature (air cooling) observation of appearance after repetition 10 times.

Example 2

(1) Environmental Gas and Flow Rate Condition

[0048] A mixed gas of CF₄, Ar and O₂is an atmosphere under the condition.

CF₄/Ar/O₂=100/1000/10 (flow rate cm3 per 1 minute)

(2) Plasma Irradiation Output

[0049] High frequency power: 1300 W

[0050] Pressure: 133.3 Pa

[0053]

TABLE 2

				Damaged
			Presence	depth
			or	through
	Sprayed	Surface	absence of	erosion
No.	materials	treatment	undercoat	(μm)	Remarks


1	Y₂O₃(99.9%)	Spraying	Presence	6.2	Example
2			Absence	6.1
3	Y₂O₃(99.8%)	Spraying	Presence	7.6
4			Absence	7.2
5	Y₂O₃(99.5%)	Spraying	Presence	6.5
6			Absence	6.3
7	Y₂O₃(99.9%)	PVD	Absence	6.6	Comparative
8	Al₂O₃	Anodizing	Absence	39.5	example
9	Al₂O₃	Spraying	Presence	8.1
10	B₄C	Spraying	Presence	28.0
11	Quartz	—	Absence	39.0

(Note)
(1) The spraying is carried out by a plasma spraying process under an atmospheric pressure and the thickness of undercoat is 80 μm and the thickness of top coat such as Y₂O₃, Al₂O₃or the like is 200 μm.
(2) Material of undercoat is 80% Ni—20% Al.
(3) Anodizing is carried out according to AA25 defined in JIS H8601.