Organic electro-luminescent device, manufacturing method for the same, and electronic equipment

[0001] 1. Field of the Invention

[0002] The present invention relates to an organic electro-luminescent device provided with electric light emitting elements used for displays, and display light sources, and the like, a manufacturing method for the same, and electronic equipment.

[0003] 2. Description of the Related Art

[0004] The development of light emitting elements using organic materials for spontaneous light emitting-type displays in place of liquid crystal displays has recently been proceeding at a rapid pace. With respect to an organic electro-luminescent device equipped with a light emitting component using an organic material in the light emitting layer, a related art method for forming a low molecular weight layer using an evaporation process is disclosed from page 913 in Appl. Phys. Lett. 51 (12), 21 Sep. 1987, and a related art method for coating a large molecular weight layer is disclosed from page 34 of Appl. Phys. Lett. 71 (1), July 1997.

[0005] In the case of using a low molecular weight material for coloring, a light emitting material differing from that of mask lifting is vapor deposited and formed onto the desired image. On the other hand, in the case of a large molecular weight material, much attention is being placed on performing the coloring using an ink jet method, due to refinement and ease with which the patterning can be accomplished. The following examples are related art methods for forming an organic electro-luminescent component by such an ink jet method: Japanese Patent Application, First Publication No. Hei 7-235378, Japanese Patent Application, First Publication No. Hei 10-12377, Japanese Patent Application, First Publication No. Hei 10-153967, Japanese Patent Application, First Publication No. Hei 11-40358, Japanese Patent Application, First Publication No. Hei 11-54270, and Japanese Patent Application, First Publication No. Hei 11-339957.

[0006] In addition, from the standpoint of component manufacturing, in order to enhance the light emitting efficiency and durability, the formation of a hole injection/transport layer between the electrode and light emitting layer is widely performed as disclosed from page 913 in Appl. Phys. Lett. 51 (12), 21 Sep. 1987. Formation of a layer has been performed by a coating process, such as spin coating or the like, using a conductive macromolecule as the buffer layer and/or hole injection/transport layer, e.g., a polythiophene derivative and/or polyaniline derivative (Nature, 357, 477, 1992). With respect to a low molecular weight material, formation of a layer using a phenylamine derivative, as the hole injection/transport layer, by evaporation has been reported.

[0007] The aforementioned ink jet methods are extremely effective for simply forming a layer having a refined pattern without wasting the light emitting layer material including the organic electro-luminescent material.

[0008] When forming a light emitting layer using an organic electro-luminescent material according to an ink jet method, a composition is employed which includes a solute and solvent, wherein the aforementioned solute includes an organic electro-luminescent material.

[0009] As the aforementioned composition, it is possible to use a composition including only one type of organic electro-luminescent material. However, compositions including a plurality of organic electro-luminescent materials are more widely used. For example, by mixing a light emitting material and a fluorescent material, it is possible to change the light illuminated from the aforementioned light emitting material to a light having a different wavelength due to the presence of the aforementioned fluorescent material.

[0010] In this manner, in the case of a plurality of organic electro-luminescent materials, in order to obtain the desired light characteristics, it is necessary to form a layer in a state in which each of the aforementioned organic electro-luminescent materials is uniformly mixed without separation therefrom.

[0011] However, the droplets used in the formation of a thin layer according to the ink jet method are extremely small, and the evaporation time is short. As a result, the solvent molecules that are evaporated from the droplets are saturated prior to being sufficiently dispersed from the substrate area, such that even the resultant thin layer is re-dissolved. Furthermore, at the time of re-dissolving the aforementioned, the respective organic electro-luminescent materials phase separate from each other, which in turn results in problems, such as degradation of the performance characteristics of the organic electro-luminescent device.

[0012] The present invention addresses the above-described problems. An object of the present invention is to provide a manufacturing method, capable of forming a homogeneous luminescent layer which causes no phase separation during formation by the ink-jet method, and which is also capable of providing organic electro luminescence devices having superior display properties. In addition to the manufacturing method, an object of the present invention is to provide organic electro-luminescence devices having homogeneous luminescent layers and also having superior display properties. An object of the present invention is also to provide electronic equipment provided with the present organic electro-luminescent devices.

[0013] A first aspect of the present invention provides a manufacturing method for an organic electro-luminescent device including the steps of forming light emitting layers by discharging above a substrate at least two compositions, each including at least one organic electro-luminescent material, the order of discharging the compositions above the substrate starting with a composition which has the fewest number of organic electro-luminescent materials.

[0014] It was observed that problems of the phase separation occur more easily with compositions including a larger number of organic electro-luminescent materials, and thus in the discharge formation of a layer, those compositions including a larger number of organic electro-luminescent materials are processed after the compositions comprising a fewer number of organic electro-luminescent materials. As a result, the aforementioned phase separation due to re-dissolution following completion of the discharge formation of the film can be prevented, and an organic electro-luminescence device possessing superior display properties can be reliably manufactured.

[0015] According to a second aspect of the present invention, a manufacturing method for an organic electro-luminescent device is provided that includes the steps of forming light emitting layers by discharging, above a substrate, at least two compositions, each including at least one organic electro-luminescent material. When discharging compositions which have the same number of organic electro-luminescent materials, the order of discharging said compositions above the substrate starting with a composition which is most difficult to be phase separated after the layer is formed.

[0016] According to the present invention, the organic electro-luminescent composition, which is liable to be phase separated after the film formation, is discharge formed after the discharge formation of the other organic electro-luminescent composition, which is difficult to be phase separated. Thus, it becomes possible to thereby prevent the phase separation due to re-dissolution after the discharge formation, which results in making it possible to provide a manufacturing method of organic electro-luminescent devices having superior display properties.

[0017] A third aspect of the present invention provides a manufacturing method for the organic electro-luminescent device, such that during two continuous cycles of discharging said compositions, the subsequent discharge of a composition is preferably performed after the droplets of the composition discharged in a first cycle are dried.

[0018] According to a fourth aspect of the present invention, the manufacturing method for an organic electro-luminescent device includes the steps of forming the light emitting layer after forming steps of a plurality of first electrodes corresponding to a plurality of pixel regions, a bank layer that partitions the plurality of pixel regions, and a hole injection/transport layer on said plurality of first electrodes on said firstelectrode. The forming process further includes the step of forming a second electrode on the light emitting layer.

[0019] Providing banks makes it possible to perform the discharge formation of a layer by completely separating the two or more ink compositions into separate pixel regions. As a result, it is possible to easily maintain the independence of each light emitting layer, and thereby obtain an organic electro-luminescent device having superior display properties. In addition, a hole injection/transport layer is provided so as to achieve both a high luminescent efficiency and enhanced durability.

[0020] Furthermore, the counter electrode includes a cathode in the case when the image electrode is anode, and includes an anode electrode in the case when the image electrode is cathode.

[0021] The organic electro-luminescent device of the present invention is obtained by using an aforementioned method for manufacturing an organic electro-luminescent device according to the present invention. It is possible to obtain an organic electro-luminescent device having a uniform light emitting layer and superior display properties.

[0022] The present invention also provides an electronic equipment provided with an organic electro-luminescent device produced by the above manufacturing process.

[0023] According to the present invention, it is possible to provide electronic equipment that is equipped with a display apparatus having superior display properties.

[0034] In the following, a manufacturing method for manufacturing an organic electro-luminescent device according to the present invention will be described with reference to FIGS. 1-7.

[0035] The manufacturing method according to the present embodiment includes a bank formation process; a plasma treatment process; a hole injection/transport layer formation process; a surface reforming process; a light emitting layer formation process; a cathode formation process; and a sealing process.

[0036] As shown in FIG. 1, according to the aforementioned bank formation process, bank layers 12 separating each pixel region are formed by sequentially layering an inorganic substance bank layer 12a and organic substance bank layer 12b on a transparent electrode 11 including ITO or the like, which is formed on a substrate 10 onto which TFT or the like (not shown in the Figures) has been pre-provided when necessary.

[0037] The aforementioned inorganic substance bank layer 12a may be formed by forming an inorganic layer of SiO₂, TiO₂, SiN, and the like on the entire surface of the substrate 10 and transparent electrode 11 according to, for example, a CVD process, a spattering process, an evaporation process, or the like; patterning the aforementioned inorganic layer using etching or the like; and then providing an opening 13a in the aforementioned transparent electrode 11. However, at this time, the inorganic substance bank layer 12a extends to the marginal areas of the transparent electrode 11.

[0038] The layer thickness of the aforementioned inorganic substance bank layer 12a is preferably in the range of 50-200 nm, with a value of 150 nm being particularly preferred.

[0039] Subsequently, an organic substance bank layer 12b is formed on the entire surface of the substrate 10, transparent electrode 11, and inorganic substance bank layer 12a.

[0040] In addition, the organic substance bank layer 12b is formed by first dissolving a standard resist, e.g., acrylic resin, polyamide resin, or the like, in a solvent, and then coating this solution by spin coating, dip coating, or the like.

[0041] The organic substance bank layer 12b is then etched by a photolithography technique or the like to provide an opening 13b. This opening 13b of the aforementioned organic substance bank layer 12b is preferably formed to be slightly larger than the opening 13a of the inorganic substance bank layer 12a. In this manner, an opening 13 which opens through both the inorganic substance bank layer 12a and organic substance bank layer 12b is formed above the transparent electrode 11.

[0042] Furthermore, the plane shape of this opening 13 is not particularly important and may include a circle, oval, square, or stripe. However, in the case of a square or the like, due to the surface tension of the ink composition, it is preferable to round out the corners thereof.

[0043] Subsequently, in the plasma treatment process, a region of ink affinity and an ink repellent region are formed on the surface of the bank member 12.

[0044] This plasma treatment process is divided into a pre-heating process, an ink affinity process that imparts ink-affinity to the entire surface, an ink repellent process that makes the organic substance bank layer 12b ink repellent, and a cooling process.

[0045] In the pre-heating process, the substrate 10 including the bank member 12 is heated to a predetermined temperature. This heating is performed by installing a heater, for example, at a stage in which the substrate 10 is loaded within the plasma treatment chamber, and heating the substrate 10 to 70 to 80° C., for example, using this heater at the desired stage.

[0046] By performing this pre-heating process, even in the case when the plasma treatment is conducted continuously on a plurality of substrates, it is possible to achieve almost constant plasma treatment conditions from immediately after commencing the treatment to immediately prior to terminating the treatment. As a result, it is possible to impart a uniform affinity with respect to the composition ink of the bank portions 12 between substrates 10, which in turn allows for the manufacture of a display apparatus having a constant product quality.

[0047] In addition, the substrate 10 is pre-heated beforehand, and thus the processing time for the subsequent plasma treatment can also be shortened.

[0048] In the aforementioned process that imparts ink affinity, a plasma treatment (O₂ plasma treatment) is performed in which oxygen in the atmospheric air is used as the reactive gas. Specifically, the substrate 10 including the bank members 12 is placed onto a test stage within the interior of a heater, and oxygen in a plasma state is irradiated thereon.

[0049] This O₂ plasma treatment may be performed under the conditions of a plasma power of 100 to 800 kW, an oxygen gas flow of 50 to 100 cc/min, a substrate transport speed of 0.5 to 10 mm/sec, and a substrate temperature of 70 to 90° C. Furthermore, the heating performed according to this test stage is conducted mainly to maintain the temperature of the pre-heated substrate 10.

[0050] By utilizing this O₂ plasma treatment, hydroxyl groups are introduced in the exposed surfaces of the transparent electrode 11 and inorganic substance bank layer 12a, and on the entire surface of the organic substance bank layer 12b, thereby imparting the aforementioned with ink affinity properties.

[0051] Subsequently, in the aforementioned process that imparts ink repellent properties, a plasma treatment (CF₄ plasma treatment) is performed in the atmospheric air wherein tetrafluoromethane (tetra-fluoro-carbon) is used as the reactive gas.

[0052] Specifically, the substrate 10 including the bank members 12 is placed onto a test stage within the interior of a heater, and tetrafluoromethane in a plasma state is irradiated thereon.

[0053] This CF₄ plasma treatment may be performed under the conditions of a plasma power of 100 to 800 kW, a tetrafluoromethane gas flow of 50 to 100 cc/min, a substrate transport speed of 0.5 to 10 mm/sec, and a substrate temperature of 70 to 90° C. Furthermore, the heating performed according to this test stage is conducted mainly to maintain the temperature of the pre-heated substrate 10, in the same manner as with the first plasma treatment chamber 52.

[0054] Furthermore, the reactive gas is not limited to only tetrafluoromethane, but other fluorocarbon gases may also be used.

[0055] According to this CF₄ plasma treatment, ink repellent properties are imparted by introducing fluorine groups into the organic substance bank layer, which displays an ink affinity by means of the previous process. Hydroxyl groups of the organic substances such as acrylic resin and polyimide resin forming the aforementioned organic substance bank layer 12b are substituted easily by the fluorine groups by irradiating a fluorocarbon in a plasma state so that they are imparted with the aforementioned ink repellent properties.

[0056] On the other hand, the exposed surfaces of the transparent electrode 11 and inorganic bank layer 12a are slightly affected by this CF₄ plasma treatment. However, the CF₄ plasma treatment does not have an affect on the affinity.

[0057] By cooling the substrate 10, which has been heated for the plasma treatment back, to room temperature or to a predetermined temperature (a temperature to execute the ink jet process) in the subsequent cooling process, it is possible to execute formation of the hole injection/transport layer at a constant temperature. As a result, it is possible to continuously discharge the ink droplets at a constant volume, at the time of discharging the composition ink containing the hole injection/transport layer material according to an ink jet method. In this manner, a uniform hole injection/transport layer can be formed.

[0058] According to the aforementioned plasma treatment process, by sequentially performing the aforementioned O₂ plasma treatment and CF₄ plasma treatment with respect to the organic substance bank layer 12a and inorganic bank layer 12b, including different materials, it is possible to easily provide both a region of ink affinity and an ink repellent region in bank member 12.

[0059] Subsequently, in the hole injection/transport layer formation process, a hole injection/transport layer 16 is formed by discharging an ink composition 15 containing the hole injection/transport layer material from an opening 13 above the aforementioned transparent electrode 11, and then drying and heat treating the aforementioned.

[0060] Furthermore, after forming the aforementioned hole injection/transport layer, it is preferable to perform processes in an inert gas environment, such as that of a nitrogen atmosphere and/or argon atmosphere without water and oxygen.

[0061] As shown in FIG. 2, an ink composition 15 containing the hole injection/transport layer material is first filled into an ink jet head 14, the discharge nozzle of which faces an opening 13. While mutually moving this inkjet head 14 and the substrate 10, the ink composition 15, the liquid amount per droplet of which is controlled, is then discharged onto the transparent electrode 11 from the aforementioned ink jet head 14.

[0062] A mixture of a polythiophene derivative, such as polyethylene dioxythiophene (PEDOT) or the like, and a polystyrene sulfonate (PSS), which has been dissolved in a polar solvent, may be used as the ink composition 15, for example. The aforementioned polar solvent may include, for example, isopropyl alcohol (IPA), normal butanol, γ-butyrolactone, N-methyl pyrolidone (NMP), 1,3-dimethyl-2-imidazolidone (DMI), derivatives thereof, and glycol ethers such as carbitol acetate, butylcarbitol acetate, and the like.

[0063] More concrete examples of the ink composition 15 may include a composition including 11.08% by weight of a PEDOT/PSS mixture (wherein the ratio of PEDOT to PSS is 1 to 20); 1.44% by weight of PSS; 10% by weight of IPA; 27.48% by weight of NMP; and 50% by weight of DMI. Furthermore, the viscosity of the ink composition is preferably 2 to 20 Ps, and more preferably approximately 7 to 10 cPs.

[0064] By using the aforementioned ink composition, it is possible to perform stable discharge of the ink composition from a discharge nozzle without plugging of the discharge nozzle of the ink jet head 14.

[0065] Moreover, with regard to the material including the hole injection/transport layer 16, the same material may be used for each light emitting layer of R, G and B. Alternatively, these materials may also differ from each other as well.

[0066] The discharged ink composition 15 then spreads onto the transparent electrode 11 and the inorganic bank layer 12a of the opening 13, both of which have been imparted with ink affinity properties. In addition, even if the ink composition 15 falls out of the predetermined discharge position, and is discharged onto the organic substance bank layer 12b, this ink composition 15 falls away from the organic substance bank layer 12b and flows into an opening 13 without wetting the organic substance bank layer 12b.

[0067] The discharge amount of the ink composition 15 may be determined according to the size of the opening 13, thickness of the hole injection/transport layer, concentration of the hole injection/transport layer in the ink composition 15, and the like.

[0068] In addition, the discharge of the ink composition 15 to the opening 13 may be divided over several cycles instead of discharging all at once. In such a case, the discharge amount of the ink composition 15 may be identical each time, or alternatively may vary with each cycle. Furthermore, the ink composition is not necessarily discharged onto the same location within opening portions 13 every time, and the ink composition 15 may be discharged to different locations within opening portion 13.

[0069] Subsequently, a hole injection/transport layer 16 is formed, as shown in FIG. 3, by drying the discharged ink composition 15, and evaporating the polar solvent contained in the ink composition 15.

[0070] The drying process, for example, may be performed at room temperature under a pressure of approximately 133.3 Pa (1 Torr) in nitrogen atmosphere. A pressure that is excessively low leads to clumping of the ink composition 15, and hence is not desirable. Furthermore, a small amount of the ink composition 15 remains on and adheres to the surrounding wall surface of the bank member 12. Thus, if the aforementioned drying temperature exceeds room temperature, the evaporation speed of the polar solvent is increased, which leads to an excessive amount of the ink composition 15 remaining on the aforementioned wall surface. Accordingly, the aforementioned drying process is preferably performed at a temperature not to exceed room temperature.

[0071] After the drying process, the polar solvent and water remaining in the hole injection/transport layer 16 are preferably removed by heat treating the aforementioned for approximately 10 minutes at 200° C. in nitrogen, or preferably in vacuum.

[0072] In the aforementioned hole injection/transport layer formation process, the discharged ink composition 15 blends into the exposed surface portions of the transparent electrode 11 and inorganic bank layer 12a, which exhibit ink affinity properties, while for the most part not adhering to the ink repellent, organic substance bank layer 12b. Therefore, even in the case when the ink composition 15 is mistakenly discharged onto the aforementioned organic substance bank layer 12b, this ink composition 15 falls away and flows onto the exposed surface portions of the transparent electrode 11 and inorganic bank layer 12a, both of which exhibits ink affinity properties. As a result, a hole injection/transport layer 16 can be reliably formed onto the aforementioned transparent electrode 11.

[0073] Subsequently, a surface reforming process is performed prior to conducting the light emitting layer forming process. In other words, in order to prevent the hole injection/transport layer 16 from being re-dissolved while forming the light emitting layer, a non-polar and insoluble solvent to the hole injection/transport layer 16 is used with respect to the hole injection/transport layer 16, as the solvent for the ink composition at the time of forming the light emitting layer.

[0074] However, on the other hand, the aforementioned hole injection/transport layer 16 has a low affinity with the aforementioned non-polar solvent. Thus, even when the ink composition of the light emitting layer comprising the non-polar solvent is discharged onto the aforementioned hole injection/transport layer 16, the ink composition may be repelled by the hole injection/transport layer 16, which makes it impossible to adhere the light emitting layer with the hole injection/transport layer 16, or alternatively makes it impossible to form uniform coating of the light emitting layer.

[0075] Hence, in order to increase the surface affinity of the aforementioned hole injection/transport layer 16 with the aforementioned non-polar solvent, it is preferable to perform a surface reforming process prior to the formation of the light emitting layer.

[0076] In this surface reforming process, a solvent for use in surface reforming, which is identical or similar to the non-polar solvent of the ink composition used at the time of forming the light emitting layer, is coated onto the aforementioned hole injection/transport layer 16 by an ink jet method, spin coating method, or dip method, and dried thereon.

[0077] According to an ink jet method, the aforementioned coating is performed by filling a solvent for use in surface reforming into an ink jet head, and then discharging this surface reforming solvent onto the hole injection/transport layer 16, while moving this ink jet head and the substrate 10 to each other, with the discharge nozzle of the ink jet head facing the aforementioned hole injection/transport layer 16.

[0078] In addition, according to a spin coat method, a substrate 10 is, for example, loaded onto a stage, and a surface reforming solvent is added thereto in a dropwise manner from above. Subsequently, the substrate 10 is rotated to spread the surface reforming solvent over the entire hole injection/transport layer 16 on the substrate 10. Furthermore, although the surface reforming solvent is temporarily spread over the ink repellent organic substance bank layer 12b, this surface reforming solvent is blown aside by the centrifugal force of the aforementioned rotation, and hence ends up coating only the aforementioned hole injection/transport layer 16.

[0079] Furthermore, the coating according to a dip method involves immersing a substrate 10 in a surface reforming solvent, and following removal, spreading this surface reforming solvent over the entire hole injection/transport layer 16. In this case as well, the surface reforming solvent is temporarily spread over the ink repellent organic substance bank layer 12b, but falls away from the ink repellent organic substance bank layer 12b and removed from the surface reforming solvent. As a result, the surface reforming solvent ends up coating only the aforementioned hole injection/transport layer 16.

[0080] The surface reforming solvent used here may include compounds identical to the non-polar solvent of the ink composition, such as cyclohexylbenzene, dihydrobenzofuran, trimethylbenzene, tetramethylbenzene, and the surface reforming solvent such as toluene, xylene, and the like are preferable for the spin coat method and the dipping method.

[0081] In particular, when performing the aforementioned coating according to an ink jet method, dihydrobenzofuran, trimethylbenzene, tetramethylbenzene, cyclohexylenzene, a mixture of these compounds, especially the same solvent mixture used in the ink composition and the like are preferably used. In the case when performing the aforementioned coating according to a spin coating or dip method, toluene, xylene, and the like are preferably used.

[0082] With regard to the drying process, in the case when the coating has been performed according to an ink jet method, it is preferable to perform the aforementioned drying by loading the substrate 10 onto a hot plate and heating the aforementioned to a temperature of no greater than 200° C. in order to dry the surface reforming solvent. On the other hand, in the case when the coating has been performed according to a spin coating or dip method, the surface reforming solvent is preferably dried by either blowing nitrogen onto the substrate 10, or by generating an air flow onto the surface of the substrate 10 by rotating the aforementioned substrate.

[0083] Moreover, it is also possible to perform the coating of the surface reforming solvent after the drying process of the aforementioned hole injection/transport layer formation process, and then conduct the heat treating process of the hole injection/transport layer formation process after drying the coated surface reforming solvent.

[0084] By virtue of performing the aforementioned surface reforming process, the surface of the hole injection/transport layer 16 blends in easier with the non-polar solvent. In addition, by virtue of the subsequent processes, it is possible to uniformly coat the ink composition containing the light emitting layer material onto the aforementioned hole injection/transport layer 16.

[0085] Moreover, it is also possible to form an ultra thin hole transport layer onto the aforementioned hole injection/transport layer by forming an ink composition by dissolving a commonly used hole transport layer material, such as arylamine-type compound and the like, in the aforementioned surface reforming solvent. The resultant ink composition is then coated onto the hole injection/transport layer according to an ink jet method, and dried thereon.

[0086] Although the majority of this hole transport layer is dissolved into the light emitting layer coated in a subsequent process, a small amount remains as a thin layer between the hole injection/transport layer 16 and the light emitting layer. As a result, the energy barrier between the hole injection/transport layer 16 and the light emitting layer is reduced, which in turn allows for easy movement of the hole and enhancement of light emitting efficiency.

[0087] In the subsequent light emitting layer formation process, the ink compositions 17a, 17b and 17c (not shown), each including a solute component, e.g., an organic electro-luminescent material or the like, and a solvent, are discharged according to the following sequence onto a hole injection/transport layer 16 which has undergone surface reformation. Drying and heat treatment of the aforementioned are then performed to sequentially form the light emitting layers 18a, 18b and 18c.

[0088] The aforementioned organic electro-luminescent material may include fluorene-type high molecular weight derivatives such as shown in chemical formula 1 to chemical formula 5, shown below.

[0089] Examples of the organic electro-luminescent materials include (poly)-paraphenylene-vinylene derivatives, polyphenylene derivatives, polyfluorene derivatives, polyvinyl carbazol, polythiophene derivatives, perylene-type pigments, coumarin-type pigments, rhodamine-type pigments, as well as low molecular weight organic EL materials and large molecular weight EL materials that are soluble in other benzene derivatives. For example, it is possible use rublene, perylene, 9,10-diphenyl anthracene, tetraphenyl butadiene, Nile Red, coumarin 6, quinacridone, and the like.

[0090] Furthermore, in the chemical formula 1 to the chemical formula 5, n represents the degree of polymerization. In the chemical formula 1, n is in a range of 1,000 to 500,000, in the chemical formula 2, n is in a range of 1,000 to 500,000, in the chemical formula 3, n is in a range of 1,000 to 500,000; in the chemical formula 4, n ranges 1,000 to 500,000, and in the chemical formula 5, n ranges 1,000 to 500, 00. In addition, in the chemical formula 5, R represents H, CH₃, C₂H₅ and so on.

[0091]

[0092] As the non-polar solvent, it is preferable to use a compound that is insoluble in the hole injection/transport layer 16, for example, cyclohexylbenzene, dihydrobenzofuran, trimethylbenzene, tetramethylbenzene, and the like.

[0093] By employing the non-polar solvent in the ink composition of the light emitting layer, it is possible to coat the ink composition without re-dissolving the hole injection/transport layer 16.

[0094] Furthermore, as the solute component, beside the organic electro-luminescent material, it is also possible to include an appropriate amount of a binder, such as a surface active agent, a thickener and the like.

[0095] As shown in FIG. 4, an ink composition 17a is discharged onto a hole injection/transport layer 16 by filling the ink composition 17a into an ink jet head 14 and then discharging this ink composition, the liquid amount per droplet of which is controlled, from a discharge nozzle while moving both this ink jet head 14 and substrate 10 with respect to each other, with the discharge nozzle of the ink jet head 14 facing the aforementioned hole injection/transport layer 16.

[0096] In this case, the discharged ink composition 17a spreads out and blends into the hole injection/transport layer 16, without for the most part adhering to the organic substance bank layer 12b, which has previously undergone an ink repellent treatment. As a result, even when this ink composition 17a is mistakenly discharged onto the organic substance bank layer 12b, it falls away and flows onto the hole injection/transport layer 16. In this manner, it is possible to form a layer of the ink composition 17a which is tightly adherent to the hole injection/transport layer 16.

[0097] The amount of the ink composition 17a is determined based on the thickness of the light emitting layer 18a to be formed, the concentration of the light emitting layer material within the ink composition, and the like.

[0098] In addition, the discharge of the ink composition 17a onto the hole injection/transport layer 16 may be performed with the dropwise addition of the ink composition 17a divided over several cycles instead of discharging all at once. In such a case, the droplet amount of the ink composition 17a may be identical each time, or alternatively may vary with each cycle. Furthermore, instead of being discharged to the same location on the hole injection/transport layer 16 each time, the ink composition 17a droplets may also be discharged arranging different locations within the hole injection/transport layer 16.

[0099] Subsequently, a light emitting layer 18a is formed, as shown in FIG. 5, by drying the discharged ink composition 17a, and evaporating the polar solvent contained in the ink composition 17a.

[0100] The drying process, for example, may be performed at room temperature under a pressure of approximately 133.3 Pa (1 Torr) in nitrogen atmosphere for 5-10 minutes, or by spraying nitrogen thereon at 40° C. for 5-10 minutes.

[0101] Other methods for performing the aforementioned drying may include, for example, a far infrared irradiation method, a high-temperature nitrogen gas spraying method, and the like.

[0102] Subsequently, as shown in FIG. 6, a second light emitting layer 18b (FIG. 7) is formed by dropwise addition and drying of an ink composition 17b, in the same manner as with the aforementioned ink composition 17a. Thereafter, a third light emitting layer 18c is formed in a similar manner by dropwise addition and drying of an ink composition 17c, as shown in FIG. 7, to yield a substrate having three types of light emitting layers 18a, 18b, and 18c formed thereon.

[0103] Here, the formation sequence of the aforementioned three types of light emitting layers 18a, 18b, and 18c is determined in the following manner.

[0104] First, in the case when the number of organic electro-luminescent materials is different, the formation sequence starts with the layer including the fewest organic electro-luminescent materials. If a light emitting layer including a color having a large number of components is formed first, phase separation may occur due to re-dissolution of the initially formed light emitting layer, by the solvent vapor evaporated from the ink composition of a light emitting layer including a different color, which has been formed later.

[0105] In addition, in the case when the number of organic electro-luminescent materials including the respective ink compositions is identical, the aforementioned formation sequence starts with the ink composition including the organic electro-luminescent materials that are most difficult to phase separate. The degree of difficulty for phase separation may be determined by drying the ink compositions to be compared under identical drying conditions, and comparing the degree of phase separation of the resultant light emitting layers. At this time, the aforementioned “identical” drying conditions may include natural retention, drying by heating, and drying under reduced pressure, and the natural retention is preferably selected.

[0106] The degree of phase separation may be determined by the amount of light of a wavelength obtained at the time of complete phase separation that remains in the light emitting spectrum of the resultant light emitting layer. In addition, it is also possible to determine the degree of phase separation by the proportion of light of a wavelength resulting when complete phase separation does not occur, in the light emitting spectrum of the resultant light emitting layer.

[0107] In the cathode formation process, a cathode 19 is formed over the entire surfaces of the light emitting layers 18a, 18b, 18c, and organic substance bank layer 12b. This cathode 19 may be formed by laminating a plurality of materials.

[0108] For example, it is preferable to use a material such as Ca and Ba, whose work function is low, to form a layer close to the light emitting layer, and sometimes it is more preferable to form a thin LiF layer as an underlayer, depending on the nature of the layer material formed on the light emitting layer. In addition, the cathode upper layer (sealing side) is preferably formed by materials such as an Al layer, an Ag layer, a Mg/Ag layer and the like, which have a larger work function than that of the lower layer. The thickness of the upper cathode layer is preferably within a range of 100 to 1,000 nm, and more preferably, within a range of 200 to 500 nm.

[0109] The aforementioned cathode layer is preferably formed by, for example, an evaporation method, spattering method, CVD method or the like. In particular, formation according to an evaporation method is preferable from the point of view of preventing the light emitting layers 18a, 18b and 18c from being damaged by heat.

[0110] In addition, it is also possible to form the lithium fluoride layer on only the light emitting layers 18a, 18b and 18c, or alternatively only on a specified light emitting layer. In such as case, the cathode upper layer formed from calcium contacts the other light emitting layers.

[0111] In addition, it is also possible to provide a protective layer comprising SiO, SiO₂, SiN, or the like onto the cathode layer to prevent from oxidation.

[0112] Lastly, in the sealing process, a sealing layer 20 is formed by coating a sealing agent including a thermosetting resin or ultraviolet light cured resin onto the entire surface of the cathode 19. Furthermore, a substrate used to seal (not shown in the figures), is then laminated onto the sealing layer 20.

[0113] This sealing process is preferably conducted in the environment of an inactive gas, such as nitrogen, argon, helium, or the like. In the case when performing the aforementioned sealing process in air and a defect, such as pin hole or the like, is generated in the cathode layer, water, oxygen, and the like may penetrate into the cathode 19 through the aforementioned defect, resulting in the undesirable oxidation of the cathode 19.

[0114] In this manner, an organic electro-luminescent device shown in FIG. 8 is obtained.

[0115] According to the present embodiment, the discharge formation of a layer of the ink composition including a greater number of organic materials is performed after that of the ink composition including fewer organic electro-luminescent materials. In addition, in the case when the ink compositions include the same number of organic electro-luminescent materials, this discharge formation of a layer is performed in a discharge sequence, starting with the ink composition include the organic electro-luminescent materials that are most difficult to phase separate. As a result, it is possible to prevent the phase separation occurring due to re-dissolution after the discharge formation of a layer. Accordingly, an organic electro-luminescent device having superior display properties can be reliably manufactured.

[0116] In the following, the electronic equipment including the organic electro-luminescent device manufactured according to the aforementioned embodiment will be described using concrete examples.

[0117] FIG. 10A is a perspective view showing an example of a portable telephone. In FIG. 10A, reference numeral 600 denotes a main body 600 of the portable telephone, and 601 denotes a display unit 601 including an organic electro-luminescent device.

[0118] FIG. 10B is a perspective view showing an example of a portable information processing apparatus, e.g., word processor, personal computer, or the like. FIG. 10B shows an information processing apparatus 700, an input unit 701, such as a keyboard or the like, the main body 703 of the information processing apparatus, and an organic electro-luminescent device as a display unit 702.

[0119] FIG. 10C is a perspective view showing an example of an electronic wristwatch. In FIG. 10C, the main body 800 of the watch, and an organic electro-luminescent device as a display unit 801 are shown.

[0120] According to the present embodiment, it is possible to provide electronic equipment that is equipped with a display apparatus possessing superior display properties.

[0121] The organic electro-luminescent devices of the Examples and Comparative Examples were manufactured according to the above-described embodiments. The concrete manufacturing conditions are described below. The conditions are common to all of the Examples and Comparative Example except the formation sequence for manufacturing the light emitting layer.

Bank Formation Process

[0122] A bank layer was formed so as to be opened on the transparent pixel electrode made of ITO. Since the transparent electrode was formed in a matrix form having a pitch of 70.5 micron meter, the bank layer was also formed in a matrix form having a pitch of 70.5 micron meter. The bank layer (bank) was formed by laminating inorganic bank layers made of SiO₂ and organic substance bank layers made of polyimide. Each layer was formed on the etched layer formed by photolithographic technique. Circular openings were made for the bank layers and the opening for the organic substance bank layer was formed in a diameter of 28 micron meter and the opening for the inorganic bank layer was formed in a diameter of 44 micron meter. The organic substance bank layer was formed at a height of 2 micron meter and the inorganic bank layer was formed at a height of 150 nm.

Plasma Treatment Process

[0123] An O₂ plasma treatment was performed as a process for imparting ink affinity. This O₂ plasma treatment was conducted under the conditions of roomtemperature, atmospheric pressure, a power of 300 W, an electrode-substrate distance of 1 mm, an oxygen gas flow amount of 100 cc/min, a helium gas flow amount of 10 l/min, and a table transfer rate of 10 mm/s. Subsequently, a CF₄ plasma treatment was performed as a process for imparting ink repellent properties. This CF₄ plasma treatment was conducted under the conditions of a CF₄ gas flow amount of 100 cc/min, a helium gas flow amount of 10/min, and a table transfer rate of 3 mm/s.

Hole Injection/Transport Layer Formation Process

[0124] An ink composition (a mixture of “Baytron P” manufactured by Bayer AG and a polystyrene sulfonate) for use in a hole injection/transport layer shown in Table 1 was discharged from the head of an ink jet printer (MJ-9300 manufactured by Epson) at 15 pl to form a pattern coat. The solvent was then removed at room temperature under a vacuum (1 Torr) for 20 minutes. The same ink composition for use in a hole injection/transport layer was then discharged at 15 pl to form a pattern coat. After removing the solvent at room temperature under a vacuum (1 Torr) for 20 minutes, a heat treatment was performed in air atmosphere at 200° C. (on a hot plate) for 10 minutes to form a hole injection/transport layer.

[0125]

TABLE 1
Ink Composition for Hole Injection/Transport Layer
		Composition
Composition	Material name	(wt %)
hole injection/transport layer	Bytron P	11.08
materials
	Polystyrene sulfonate	1.44
Polar solvents	Isopropyl alcohol	10
	N-methyl pyrolidone	27.48
	1,3-dimethyl-2-	50
	imidazolidone

Surface Reforming Process

[0126] 1,2,3,4-tetramethyl benzene was discharged from an ink jet printer (MJ-930C manufactured by Epson) to form a coat. Subsequently, the aforementioned was placed on a hot plate that was heated to a temperature below 200° C. and dried.

Light emitting layer Formation Process

[0127] The ink compositions shown in Tables 2 to 4 were prepared. Table 2 shows an ink composition (green) for a light emitting layer, Table 3 shows an ink composition (blue) for a light emitting layer; and Table 4 shows an ink composition (red) for a light emitting layer. Furthermore, compounds 1, 2, 4, and 5 in the Tables are respectively described above in Chemical Formula 1 to 5.

[0128]

TABLE 2
Ink Composition (Green) for a Light emitting layer
		Composition
Composition	Material name	weight
Light emitting layer	Compound 1	0.76	g
Materials
	Compound 2	0.20	g
	Compound 4	0.04	g
Solvent	1,2,3,4-tetramethyl benzene	100	ml

[0129]

TABLE 3
Ink Composition (Blue) for a Light emitting layer
		Composition
Composition	Material name	weight
Light emitting layer	Compound 1	1.00	g
Material
Solvent	1,2,3,4-tetramethyl benzene	100	ml

[0130]

TABLE 4
Ink Composition (Red) for a Light emitting layer
		Composition
Composition	Material name	weight
Light emitting layer	Compound 1	0.7	g
Materials
	Compound 2	0.2	g
	Compound 5	0.1	g
Solvent	1,2,3,4-tetramethyl benzene	100	ml

[0131] Initially, a blue light emitting layer was prepared by discharging the ink composition (blue) for a light emitting layer comprising a concentration of 1% (wt/vol) shown in Table 3, from an ink jet printer (MJ-930C manufactured by Epson) by 20 pl under an N₂ gas flow, and then drying under the conditions of 25° C. and 1 atm.

[0132] Subsequently, a green light emitting layer was prepared by discharging the ink composition (green) for a light emitting layer including a concentration of 1% (wt/vol) shown in Table 2, into a neighboring opening 13 at 20 pl under an N₂ gas flow, and then drying under the conditions of 25° C. and 1 atm.

[0133] Initially, a blue light emitting layer was prepared by discharging the ink composition (blue) for a light emitting layer including a concentration of 1% (wt/vol) shown in Table 3, from an ink jet printer (MJ-930C manufactured by Epson) at 20 pl under an N₂ gas flow, and then drying under the conditions of 25° C. and 1 atm.

[0134] Subsequently, a red light emitting layer was prepared by discharging the ink composition (red) for a light emitting layer including a concentration of 1% (wt/vol) shown in Table 4, into a neighboring opening 13 at 20 μl under an N₂ gas flow, and then drying under the conditions of 25° C. and 1 atm.

[0135] Thereafter, a green light emitting layer was prepared by discharging the ink composition (green) for a light emitting layer including a concentration of 1% (wt/vol) shown in Table 2, into a neighboring opening 13 at 20 pl under an N₂ gas flow, and then drying under the conditions of 25° C. and 1 atm.

[0136] Initially, a green light emitting layer was prepared by discharging the ink composition (green) for a light emitting layer including a concentration of 1% (wt/vol) shown in Table 2, from an ink jet printer (MJ-930C manufactured by Epson) at 20 pl under an N₂ gas flow, and then drying under the conditions of 25° C. and 1 atm.

[0137] Subsequently, a blue light emitting layer was prepared by discharging the ink composition (blue) for a light emitting layer including a concentration of 1% (wt/vol) shown in Table 3, into a neighboring opening 13 at 20 pl under an N₂ gas flow, and then drying under the conditions of 25° C. and 1 atm.

Cathode Formation Process

[0138] After forming a LiF layer having a thickness of 2 nm by a vapor deposition method as the cathode layer, a calcium layer having a thickness of 20 nm was formed by a vapor deposition method. An aluminum layer of 200 nm was then formed as the cathode layer by a spattering method.

Sealing Process

[0139] A sealing layer was formed by coating a sealing agent including an epoxy resin onto the entire surface of the cathode. Furthermore, a substrate for use in sealing was laminated onto the aforementioned sealing layer to prepare the organic electro-luminescent device according to the Examples and Comparative Example.

Evaluation

[0140] The light emitting spectrums of the green light emitting layers of the organic electro-luminescent device according to the Comparative Example and Example 1 are shown in FIGS. 9A and 9B. As shown in FIG. 9A, a blue luminescent (430 nm) originated from the compound 1 remained in the green light emitting layer of the Comparative Example showed a spotty luminescent exhibiting color of light blue.

[0141] In contrast, as shown in FIG. 9B, the green light emitting layer of Example 1 displayed a green fluorescent luminescent (530 nm) having an approximately uniform spectrum.

[0142] In addition, the blue light emitting layers of the Comparative Example and Example 1 both displayed a uniform spectrum of blue luminescent (430 nm) originated by the compound 1.

[0143] Hence, the formation efficiency of forming the light emitting layers in the order starting with the layers having the fewest number of organic electro-luminescent materials was confirmed from the aforementioned.

[0144] In addition, the blue light emitting layer (430 nm), red light emitting layer (640 nm), and green light emitting layer (530 nm) of the organic electro-luminescent device according to Example 2 each showed a uniform spectrum.

[0145] Both the ink compositions of the (red) light emitting layer and (green) light emitting layer include three organic electro-luminescent materials, however, upon comparing the difficulty of phase separation of these ink compositions under the conditions of N₂ flow, the ink composition of the (red) light emitting layer was found to be more difficult to phase separate.

[0146] Hence, in the case when the ink compositions include an identical number of organic electro-luminescent materials, the efficiency of forming the light emitting layers in the order starting with the layer that is the most difficult to phase separate was confirmed from the aforementioned.

[0147] As described above, according to the method for manufacturing an organic electro-luminescent device of the present invention, it is possible to manufacture an organic electro-luminescent device having superior display properties in which phase separation due to re-dissolution after completion of forming layer can be prevented.

[0148] In addition, the organic electro-luminescent device according to the present invention includes a uniform light emitting layer(s) and also exhibits superior display properties.

[0149] In addition, the present invention provides the electronic equipment which is capable of having superior display properties.