US 7,122,079 B2Grant

Composition for an etching mask comprising a silicon-containing material

Issue Date:2006-10-17

•5 Claims

•7 Drawing Sheets

Abstract

The present invention includes a composition for a silicon-containing material used as an etch mask for underlying layers. More specifically, the silicon-containing material may be used as an etch mask for a patterned imprinted layer comprising protrusions and recessions. To that end, in one embodiment of the present invention, the composition includes a hydroxyl-functional silicone component, a cross-linking component, a catalyst component, and a solvent. This composition allows the silicon-containing material to selectively etch the protrusions and the segments of the patterned imprinting layer in superimposition therewith, while minimizing the etching of the segments in superposition with the recessions, and therefore allowing an in-situ hardened mask to be created by the silicon-containing material, with the hardened mask and the patterned imprinting layer forming a substantially planarized profile.

Metadata

Assignee

Molecular Imprints, Inc.

Inventors

Frank Y. Xu
Michael N. Miller
Michael P. C. Watts

Application Information

Application Number:US 10/789,319

Filing Date:2004-02-27

Priority Date:2004-02-27

Art Unit:1712

Classifications

IPC:

C08L83/00

Patent Drawings (7 sheets)

Description

BACKGROUND OF THE INVENTION

[0001] The field of invention relates generally to micro-fabrication of structures. More particularly, the present invention is directed to formation of an etching mask comprising a silicon containing material used in semiconductor processing.

[0002] Micro-fabrication involves the fabrication of very small structures, e.g., having features on the order of micro-meters or smaller. One area in which micro-fabrication has had a sizeable impact is in the processing of integrated circuits. As the semiconductor processing industry continues to strive for larger production yields while increasing the circuits per unit area formed on a substrate, micro-fabrication becomes increasingly important. Micro-fabrication provides greater process control while allowing increased reduction of the minimum feature dimension of the structures formed. Other areas of development in which micro-fabrication has been employed include biotechnology, optical technology, mechanical systems and the like.

[0003] An exemplary micro-fabrication technique is shown in U.S. Pat. No. 6,334,960 to Willson et al. Willson et al. disclose a method of forming a relief image in a structure. The method includes providing a substrate having a transfer layer. The transfer layer is covered with a polymerizable fluid composition. An imprint device makes mechanical contact with the polymerizable fluid. The imprint device includes a relief structure formed from lands and grooves. The polymerizable fluid composition fills the relief structure, with the thickness of the polymerizable fluid in superimposition with the lands defining a residual thickness. The polymerizable fluid composition is then subjected to conditions to solidify and polymerize the same, forming a solidified polymeric material on the transfer layer that contains a relief structure complimentary to that of the imprint device. The imprint device is then separated from the solid polymeric material such that a replica of the relief structure in the imprint device is formed in the solidified polymeric material. The transfer layer and the solidified polymeric material are subjected to an environment to selectively etch the transfer layer relative to the solidified polymeric material such that a relief image is formed in the transfer layer. Thereafter, conventional etching processes may be employed to transfer the pattern of the relief structure into the substrate.

[0004] In recent trends in micro-fabrication of semiconductors, a silicon containing material has been utilized as a masking layer for underlying layers during etching. An example of utilizing silicon as a masking layer is found in, U.S. Pat. No. 6,468,896 to Röhr et al., entitled “Method of Fabricating Semiconductor Components,” discloses a method of depositing a silicon layer upon a metal layer, selectively etching the silicon layer with the selectively etched silicon layer serving as a hard mask when etching of the metal layer occurs.

[0005] In another example, U.S. patent application Ser. No. 10/178,947 to Watts et al., entitled “Low Viscosity High Resolution Patterning Material,” discloses a method of forming a conformal layer upon a patterned layer with the conformal layer serving as a hard mask for the patterned layer during etching and the conformal layer being formed from a silicon-containing polymerized fluid.

[0006] It is desired, therefore, to provide an improved composition of the silicon-containing material used in imprint lithography processes.

SUMMARY OF THE INVENTION

[0007] The present invention includes a composition for a silicon-containing material used as an etch mask. More specifically, the silicon-containing material may be used as an etch mask for an imprinted layer comprising protrusions and recessions. To that end, in one embodiment of the present invention, the composition includes a silicone resin, a cross-linking agent, a catalyst, and a solvent. This composition allows the silicon-containing material to selectively etch the protrusions and the segments of the patterned imprinted layer in superimposition therewith, while minimizing the etching of the segments in superposition with the recessions, and therefore allowing an in-situ hardened mask to be created by the silicon-containing material, with the hardened mask and the imprinting layer forming a substantially planarized profile. In a further embodiment, the composition includes an epoxy-functional silane in addition to the aforementioned components. The epoxy-functional silane is added to improve the cross-linking conversion rate of the composition.

BRIEF DESCRIPTION OF THE DRAWINGS

[0008] FIG. 1 is a perspective view of a lithographic system in accordance with the present invention;

[0009] FIG. 2 is a simplified elevation view of a lithographic system, shown in FIG. 1, employed to create a patterned imprinting layer in accordance with the present invention;

[0010] FIG. 3 is a simplified representation of material from which a patterned imprinting layer, shown in FIG. 2, is comprised before being polymerized and cross-linked in accordance with the present invention;

[0011] FIG. 4 is a simplified representation of cross-linked polymer material into which the material shown in FIG. 3 is transformed after being subjected to radiation in accordance with the present invention;

[0012] FIG. 5 is a simplified elevation view of an imprint device spaced-apart from the patterned imprinting layer, shown in FIG. 1, after patterning in accordance with the present invention;

[0013] FIG. 6 is a simplified elevation view of formation of a multi-layered structure on a solidified imprinting layer, shown in FIG. 5, by deposition of a conformal layer, adjacent to the patterned imprinting layer, employing a mold in accordance with one embodiment of the present invention;

[0014] FIG. 7 is a simplified elevation view after a blanket etch of the multi-layered structure, shown in FIG. 6, to format a crown surface in the conformal layer with portions of the patterned imprinting layer being exposed in accordance with one embodiment of the present invention;

[0015] FIG. 8 is a simplified elevation view of the multi-layered structure, shown in FIG. 7, after subjecting the crown surface to an anisotropic etch to expose regions of a substrate in accordance with the present invention;

[0016] FIG. 9 is a simplified elevation view showing planarization of a conformal layer employing a planarized mold in accordance with an alternate embodiment of the present invention;

[0017] FIG. 10 is a simplified plan view of a radiation source employed in the lithographic system shown in FIG. 1, depicting dual radiation sources;

[0018] FIG. 11 is a simplified plan view of a radiation source employed in the lithographic system shown in FIG. 1, depicting single radiation source;

[0019] FIG. 12 is a cross-sectional view of a substrate shown in FIGS. 1, 2, 5, 6, 7 and 8 showing an infra-red absorption layer in accordance with the present invention;

[0020] FIG. 13 is a cross-sectional view of a substrate shown in FIGS. 1, 2, 5, 6, 7 and 8 showing an infra-red absorption layer in accordance with an alternate embodiment of the present invention;

[0021] FIG. 14 is a cross-section view showing a release layer and a planarization layer that may be employed in accordance with the present invention; and

[0022] FIG. 15 is a cross-section view showing a release layer applied to a planarization mold shown in FIG. 13.

DETAILED DESCRIPTION OF THE INVENTION

[0023] FIG. 1 depicts a lithographic system 10 in accordance with one embodiment of the present invention that includes a pair of spaced-apart bridge supports 12 having a bridge 14 and a stage support 16 extending therebetween. Bridge 14 and stage support 16 are spaced-apart. Coupled to bridge 14 is an imprint head 18, which extends from bridge 14 toward stage support 16. Disposed upon stage support 16 to face imprint head 18 is a motion stage 20. Motion stage 20 is configured to move with respect to stage support 16 along X and Y axes and may provide movement along the Z axis as well. A radiation source 22 is coupled to system 10 to impinge actinic radiation upon motion stage 20. As shown, radiation source 22 is coupled to bridge 14 and includes a power generator 23 connected to radiation source 22.

[0024] Referring to both FIGS. 1 and 2, connected to imprint head 18 is a template 24 having a patterned mold 26 thereon. Patterned mold 26 includes a plurality of features defined by a plurality of spaced-apart recesses 28 and projections 30. Projections 30 have a width W₁, and recesses 28 have a width W₂, both of which are measured in a direction that extends transversely to the Z axis. The plurality of features defines an original pattern that forms the basis of a pattern to be transferred into a substrate 32 positioned on motion stage 20. To that end, imprint head 18 is adapted to move along the Z axis and vary a distance “d” between patterned mold 26 and substrate 32. Alternatively, or in conjunction with imprint head 18, motion stage 20 may move template 24 along the Z-axis. In this manner, the features on patterned mold 26 may be imprinted into a flowable region of substrate 32, discussed more fully below. Radiation source 22 is located so that patterned mold 26 is positioned between radiation source 22 and substrate 32. As a result, patterned mold 26 is fabricated from material that allows it to be substantially transparent to the radiation produced by radiation source 22. An exemplary system is available under the trade name IMPRIO 100™ from Molecular Imprints, Inc. having a place of business at 1807-C Braker Lane, Suite 100, Austin, Tex. 78758. The system description for the IMPRIO 100™ is available at www.molecularimprints.com and is incorporated herein by reference.

[0025] Referring to both FIGS. 2 and 3, a flowable region, such as an imprinting layer 34, is disposed on a portion of surface 36 that presents a substantially planar profile. In the present embodiment, the flowable region is deposited as a plurality of spaced-apart discrete droplets 38 of material 40 on substrate 32, discussed more fully below. Material 40 is substantially silicon-free and may be selectively polymerized and cross-linked to record an inverse of the original pattern therein, defining a recorded pattern. Material 40 is shown in FIG. 4 as being cross-linked at points 42, forming cross-linked polymer material 44.

[0026] Referring to FIGS. 2, 3 and 5, the pattern recorded in imprinting layer 34 is produced, in part, by mechanical contact with patterned mold 26. To that end, the distance “d” is reduced to allow imprinting layer 34 to come into mechanical contact with patterned mold 26, spreading droplets 38 so as to form imprinting layer 34 with a contiguous formation of material 40 over surface 36. In one embodiment, distance “d” is reduced to allow sub-portions 46 of imprinting layer 34 to ingress into and fill recesses 28.

[0027] In the present embodiment, sub-portions 48 of imprinting layer 34 in superimposition with projections 30 remain after the desired, usually minimum distance “d”, has been reached, leaving sub-portions 46 with a thickness t₁, and sub-portions 48 with a thickness, t₂. Thickness t₂is referred to as a residual thickness. Thicknesses “t₁” and “t₂” may be any thickness desired, dependent upon the application. The total volume contained in droplets 38 may be such so as to minimize, or avoid, a quantity of material 40 from extending beyond the region of surface 36 in superimposition with patterned mold 26, while obtaining desired thicknesses t₁and t₂.

[0028] Referring to FIGS. 2, 3, and 4, after a desired distance “d” has been reached, radiation source 22 produces actinic radiation that polymerizes and cross-links material 40, forming cross-linked polymer material 44. As a result, the composition of imprinting layer 34 transforms from material 40 to material 44, which is a solid. Specifically, material 44 is solidified to form solidified imprinting layer 134 with a side having a shape that conforms to a shape of a surface 50 of patterned mold 26, shown more clearly in FIG. 5. As a result, solidified imprinting layer 134 is formed having recessions 52 and protrusions 54. After formation of solidified imprinting layer 134, distance “d” is increased so that patterned mold 26 and solidified imprinting layer 134 are spaced-apart. Typically, this process is repeat several times to pattern different regions (not shown) of substrate 32, referred to as a step and repeat process. An exemplary step and repeat process is disclosed in published United States patent application number 20040008334, which assigned to assignee of the present invention and is incorporated by reference.

[0029] Referring to FIGS. 1, 2 and 3, the characteristics of material 40 are important to efficiently pattern substrate 32 in light of the unique deposition process employed. As mentioned above, material 40 is deposited on substrate 32 as a plurality of discrete and spaced-apart droplets 38. The combined volume of droplets 38 is such that the material 40 is distributed appropriately over an area of surface 36 where imprinting layer 34 is to be formed. In this fashion, the total volume of imprinting material 40 in droplets 38 defines the distance “d”, to be obtained so that the total volume occupied by the material 40 in the gap defined between patterned mold 26 and the portion of substrate 32 in superimposition therewith once the desired distance “d” is reached is substantially equal to the total volume of material 40 in droplets 38. As a result, imprinting layer 34 is spread and patterned concurrently, with the pattern being subsequently set by exposure to radiation, such as ultraviolet radiation. To facilitate the deposition process, it is desired that material 40 have certain characteristics to provide rapid and even spreading of material 40 in droplets 38 over surface 36 so that the all thicknesses t₁are substantially uniform and all residual thicknesses t₂are substantially uniform.

[0030] An exemplary composition for material 40 is silicon-free and consists of the following:

Composition 1

isobornyl acrylate

n-hexyl acrylate

ethylene glycol diacrylate

2-hydroxy-2-methyl-1-phenyl-propan-1-one

[0031] In COMPOSITION 1, isobornyl acrylate comprises approximately 55% of the composition, n-hexyl acrylate comprises approximately 27%, ethylene glycol diacrylate comprises approximately 15% and the initiator 2-hydroxy-2-methyl-1-phenyl-propan-1-one comprises approximately 3%. The initiator is sold under the trade name DAROCURE® 1173 by CIBA® of Tarrytown, N.Y. The above-identified composition also includes stabilizers that are well known in the chemical art to increase the operational life of the composition. To provide suitable release properties, COMPOSITION 1 may be employed with a template treated to have a mold surface that is hydrophobic and/or low surface energy, e.g., an a priori release layer.

[0032] Referring to FIGS. 3 and 5, to improve the release properties of patterned mold 26 and solidified imprinting layer 134 and to ensure that solidified imprinting layer 134 does not adhere to patterned mold 26, an additive may be included in COMPOSITION 1. To that end, material 40 may include, as an additive, a surfactant. For purposes of this invention a surfactant is defined as any molecule, one tail of which is hydrophobic. Surfactants may be either fluorine containing, e.g., include a fluorine chain, or may not include any fluorine in the surfactant molecule structure. An exemplary surfactant is available under the trade name ZONYL® FSO-100 from DUPONT™ that has a general structure of R₁R₂where R₁═F(CF₂CF₂)_Y, with y being in a range of 1 to 7, inclusive and R₂═CH₂CH₂O(CH₂CH₂O)_xH, where X is in a range of 0 to 15, inclusive. This provides material 40 with the following composition:

Composition 2

isobornyl acrylate

n-hexyl acrylate

ethylene glycol diacrylate

2-hydroxy-2-methyl-1-phenyl-propan-1-one

[0033]
R_fCH₂CH₂O(CH₂CH₂O)_xH,

[0034] The ZONYL® FSO-100 additive comprises less than 1% of the composition, with the relative amounts of the remaining components being as discussed above with respect to COMPOSITION 1. However, the percentage of ZONYL® FSO-100 may be greater than 1%.

[0035] Referring to FIGS. 5 and 6, to facilitate transferring of the pattern in patterned mold 26 into substrate 32, a multi-layered structure 56 is generated by formation of a silicon-containing conformal layer 58 adjacent to solidified imprinting layer 134. To that end, silicon-containing material is deposited adjacent to solidified imprinting layer 134. Specifically, a silicon-containing material may be deposited adjacent to solidified imprinting layer 134 using any known technique to form conformal layer 58, such as the technique discussed above with respect to deposition of material 40. Alternatively, the silicon-containing material may be deposited adjacent to solidified imprinting layer 134 employing spin-coating techniques.

[0036] In an exemplary technique for forming conformal layer 58, silicon-containing material is deposited adjacent to solidified imprinting layer 134 using spin-coating techniques and subsequently thermally curing the silicon-containing material to form conformal layer 58. To that end, exemplary material that may be employed to form conformal layer 58 includes silicone resin, a cross-linking agent, a catalyst, and a solvent.

[0037] The silicone resin is process compatible, satisfying ionic, purity, and by-product contamination requirements desired. The cross-linking agent is included to cross-link the silicone resin, providing conformal layer 58 with the properties to record a pattern thereon having very small feature sizes, i.e., on the order of a few nanometers. To that end, the catalyst is provided to produce a condensation reaction in response to thermal energy, e.g., heat, causing the silicone resin and the cross-linking agent to polymerize and cross-link, forming a cross-linked polymer material. The solvent selected is compatible with the silicone resin and represents the remaining balance of the silicon-containing material. It is desired that the solvent minimize, if not avoid, causing distortions in solidified imprinting layer 134 due, for example, to swelling of solidified imprinting layer 134.

[0038] The silicone resin can be any alkyl and/or aryl substituted polysiloxane, copolymer, blend or mixture thereof. Examples of a silicone resin include ultraviolet (UV) curable sol-gels, UV curable epoxy silicone, UV curable acrylate silicone, and UV curable silicone via thiolene chemistry; and non-cured materials such as hydrogen silsesquioxane, and poly(meth)acrylate/siloxane copolymers. Silsesquixanes, or T-resins, having a general repeating unit with a formula: RSiO_1.5. Preferably, a hydroxyl-functional polysiloxane is used such as a hydroxyl-functional organo-siloxane, with examples of organo-siloxanes including methyl, phenyl, propyl and their mixtures. The silicone resin may be present in the silicon-containing composition in amounts of approximately 2 to 40% by weight, depending on the thicknesses desired for conformal layer 58. An example of a hydroxyl-functional polysiloxane used in the present invention is a silicon T-resin intermediate available from Dow Corning® (Midland, Mich.) under the trade name Z-6018.

[0039] The cross-linking agent is a compound that includes two or more polymerizable groups. The cross-linking agent may be present in the silicon-containing composition in amounts of approximately 2 to 50% by weight in relation to the quantity of silicone resin present. Typically, the cross-linking agent is present in the silicon-containing composition in an amount of approximately 20 to 30%. An example of a cross-linking agent used in the present invention is a hexamethoxymethylmelamine (HMMM) based aminoplast cross-linking agent available from Cytec Industries, Inc. (West Paterson, N.J.) under the trade name CYMEL 303ULF.

[0040] The catalyst may be any component that catalyzes a condensation reaction. Suitable catalysts may include, but are not limited to, acidic compounds such as sulfonic acid. The catalyst may be present in the silicon-containing material in amounts of approximately 0.05% to 5% by weight in relation to the silicone resin present. Typically, the catalyst is present in the silicon-containing material in an amount of approximately 1 to 2%. An example of a catalyst used in the present invention is toluenesulfonic acid available from Cytec Industries, Inc. (West Paterson, N.J.) under the trade name CYCAT 4040.

[0041] For the balance of the composition, a solvent is utilized. The solvent can be any solvent or combination of solvents that satisfies several criteria. As mentioned above, the solvent should not cause solidified imprinting layer 134 to swell. In addition, the evaporation rate of the solvent should be established so that a desired quantity of the solvent evaporates as a result of the spin-coating process while providing sufficient viscosity to facilitate planarization of silicon-containing material in furtherance of forming conformal layer 58. Suitable solvents may include, but are not limited to, alcohol, ether, a glycol or glycol ether, a ketone, an ester, an acetate and mixtures thereof. The solvent may be present in the silicon-containing material used to form conformal layer 58 in amounts of approximately 60 to 98% by weight, dependent upon the desired thicknesses of conformal layer 58. An example of a solvent used in the present invention is methyl amyl ketone available from Aldrich Co. (St. Louis, Miss.) under the trade name MAK.

[0042] In a further embodiment, the composition of conformal layer 58 is altered to include an epoxy-functional silane coupling agent to improve the cross-linking reaction and improve the rate of cross-linking. Examples of epoxy-functional silanes may include glycidoxymethyltrimethoxysilane, 3-glycidoxypropyltrihydroxysilane, 3-glycidoxypropyldimethylhydroxysilane, 3-glycidoxypropyltrimeth oxysilane, 2,3-epoxypropyltrimethoxysilane, and the like. The epoxy-functional silane may be present in conformal layer 58 in amounts of approximately 2 to 30% by weight of silicon-containing compound in relation to the silicone resin and typically in an amount of 5 to 10%. An example of epoxy-functional silane used in the present invention is gamma-glycidoxypropyltrimethoxysilane available from GE Silicone/OSi Specialty (Wilton, Conn.) under the trade name A187.

[0043] Exemplary compositions from which to form conformal layer 58 are as follows:

Composition 3

hydroxyl-functional polysiloxane

hexamethoxymethylmelamine

toluenesulfonic acid

methyl amyl ketone

Composition 4

hydroxyl-functional polysiloxane

hexamethoxymethylmelamine

gamma-glycidoxypropyltrimethoxysilane

toluenesulfonic acid

methyl amyl ketone

[0044] In COMPOSITION 3, hydroxyl-functional polysiloxane comprises approximately 4% of the composition, hexamethoxymethylmelamine comprisies approximately 0.95%, toluenesulfonic acid comprises approximately 0.05% and methyl amyl ketone comprises approximately 95%. In COMPOSITION 4, hydroxyl-functional polysiloxane comprises approximately 4% of the composition, hexamethoxymethylmelamine comprisies approximately 0.7%, gamma-glycidoxypropyltrimethoxysilane comprisies approximately 0.25%, toluenesulfonic acid comprises approximately 0.05%, and methyl amyl ketone comprises approximately 95%.

[0045] Both COMPOSITIONS 3 and 4 are made up of at least 4% of the silicone resin. Upon curing, however, the quantity of silicon present in conformal layer 58 is at least 5% by weight and typically in a range of 20% or greater. Specifically, the quantity and composition of the solvent present in COMPOSITIONS 3 and 4 is selected so that a substantial portion of the solvent evaporates during spin-coating application of the COMPOSITION 3 or 4 on solidified imprinting layer 134. In the present exemplary silicon-containing material, approximately 90% of the solvent evaporates during spin-coating. Upon exposing the silicon-containing material to thermal energy, the remaining 10% of the solvent evaporates, leaving conformal layer 58 with approximately 20% silicon by weight.

[0046] An exemplary method of forming conformal layer 58 includes spinning-on approximately 4 mL of the silicon-containing material deposited proximate to a center of solidified imprinting layer 134. To that end, substrate 32 is spun at 1000 rev/min for 1 min by placing substrate 32 on a hot plate. Thereafter, the silicon-containing material is subjected to thermal energy by baking at 150° C. for 1 min. This produces the silicon-containing material from which conformal layer 58 is formed, with thickness variations of 20 nm or less. Were it desired to increase the thickness of the solidified silicon-containing layer, e.g., to provide the solidified silicon-containing layer with a thickness of 200 nm, the aforementioned spin-coating and curing processes are simply repeated. As a result, the solvent employed is selected so as not to remove, “wash away,” silicon-containing material in a well-cured conformal layer 58.

[0047] Referring to FIGS. 5 and 6, the spin-coating and curing processes, conformal layer 58 includes first and second opposed sides. First side 60 faces imprinting layer 134 and has a profile complementary to the profile of the imprinting layer 134. The second side faces away from imprinting layer 134 forming a normalization surface 62, which is substantially smooth and typically planar. In this manner, normalization surface 62 provides a solidified conformal layer 58 with a substantially normalized profile. It is believed that normalization surface 62 is provided with a smooth, e.g., substantially planar, topography by ensuring that COMPOSITIONS 3 and 4 have a glass transition temperature lower than the curing temperature. Specifically, it is desired that the temperature difference between the glass transition temperature and the curing temperature be sufficient to allow the silicon-containing material to reflow during curing to maximize smoothness, e.g., planarity of normalization surface 62 in a minimum amount of time. For example, the COMPOSITIONS 3 and 4 each have a glass transition temperature of approximately 50° C. and a curing temperature of 150° C. As a result, of the topography of normalization surface 62, the distances, k₂, k₄, k₆, k₈and k₁₀, between the apex 64 of each of the protrusions 54 and normalization surface 62 are substantially the same. Similarly, the distance, k₁, k₃, k₅, k₇, k₉and k₁₁between a nadir surface 66 of each of the recessions 52 and normalization surface 62 are substantially the same.

[0048] Referring to FIGS. 6 and 7, after formation of the normalization surface 62, a blanket etch is employed to remove portions of conformal layer 58 to provide multi-layered structure 56 with a crown surface 70. For example and without limitation, the blanket etch may be achieved in a system available from LAM Research 9400SE obtained from Lam Research, Inc. of Fremont, Calif. In this manner, normalization surface 62 is subjected to an isotropic halogen reactive ion etch (“RIE”) rich in fluorine, i.e., wherein at least one of the precursors was a fluorine-containing material, for example, and without limitation, a combination of CHF₃and O₂. Other suitable halogen compounds include, for example, and without limitation, CF₄. It is desirable that oxygen be absent from the plasma chemistry. Normalization surface 62 is subjected to the blanket etch sufficient to expose crown surface 70.

[0049] Crown surface 70 is defined by an exposed surface 72 of each of protrusions 54 and upper surfaces of portions 74 that remain on conformal layer 58 after the blanket etch. The composition of conformal layer 58 is such that when the blanket etch is applied to conformal layer 58, crown surface 70 is provided with a substantially planar profile. That is, the thickness of protrusions 54, shown as “a”, is substantially the same as the thickness of portions 74, shown as “b”. An exemplary blanket etch may be a plasma etch process employing a fluorine-based chemistry.

[0050] Referring to FIGS. 7 and 8, crown surface 70 is subjected to an anisotropic etch. The etch chemistry of the anisotropic etch is selected to maximize etching of protrusions 54 and the segments of imprinting layer 134, in superimposition therewith, while minimizing etching of the portions 74 in superimposition with recessions 52. In the present example, advantage was taken of the distinction of the silicon content between the imprinting layer 134 and the conformal layer 58. Specifically, employing an anisotropic plasma etch, e.g., an RIE plasma etch with an oxygen-based chemistry would create an in-situ hardened mask 76 in the regions of portions 74 proximate to crown surface 70. This results from the interaction of the silicon-containing polymerizable material with the oxygen plasma. As a result of the hardened mask 76 and the anisotropicity of the etch process, regions 78 of substrate 32 in superimposition with protrusions 54 are exposed. The width U′ of regions 78 are optimally equal to width W₂, shown in FIG. 2.

[0051] Referring to FIGS. 2, 7 and 8, the advantages of this patterning process are manifold. For example, the relative etch rate differential between portions 74 and exposed surfaces 72 facilitates providing precise etch selectivity. As a result, the dimensional width U′ of regions 78 may be precisely controlled, thereby reducing transfer distortions of the pattern into substrate 32. The resulting structure may be used as a mask to facilitate transfer of a pattern into substrate 32. Specifically, the etch differential provided by hardened mask 76 and the portions of solidified imprinting layer 134 in superimposition therewith would provide an etch differential in the presence of a blanket etch. In this manner, regions 78 of substrate 32 would etch sooner than regions of substrate 32 in superimposition with hardened mask 76. By properly selecting materials and etch chemistries, the relational dimensions between the differing features of the pattern eventually transferred into substrate 32 may be controlled as desired. For example, it was found beneficial to include an oxygen plasma etch after the fluorine etch and before the oxygen etch. Specifically, the etch selectivity during the oxygen plasma etch was improved. It is believed that residual fluorine is present on normalization surface 62 and that the Argon etch removes the residual fluorine, thereby further reducing the fluorine available during the oxygen plasma etch.

[0052] It has been found that additional planarization may be desired when forming conformal layer 58, shown in FIG. 6, when features of sub ten micron dimension are to be transferred into substrate 32. To that end, as shown in FIGS. 2 and 9, the silicon-containing material may be spun-on as discussed above with respect to forming conformal layer 58 or may be deposited as a plurality of droplets discussed above with respect to imprinting layer 34. After deposition of the silicon-containing material, a planarizing mold 80 having a substantially smooth, if not planar, surface 82 is employed to contact normalization surface 62, before solidification of the silicon-containing material in conformal layer 58. In this manner, conformal layer 58 is provided with a normalized surface with respect to solidified imprinting layer 134. This is typically achieved by providing an optical flat which has sufficient area to concurrently planarize all regions of substrate 32 that includes silicon-containing material employed to form normalization layer 58. Thereafter, the silicon-containing material in conformal layer 58 is solidified and planarized mold 80 is separated from conformal layer 58; and the normalization surface 62 may be processed as discussed above to pattern the same and transfer a pattern into substrate 32.

[0053] Referring to both FIGS. 2, 6 and 10, it may be desired to implement a step and repeat planarization process when forming normalization layer 58. To that end, radiation source 22 may be selected to provide actinic radiation to both effectuate cross-linking using both infrared (IR) radiation and ultraviolet radiation. An exemplary radiation source 22 may include multiple sources each of which produces a single range of wavelengths of radiation and is shown including two radiation sources 84 and 86. Radiation source 84 may be any known in the art capable of producing IR radiation, and radiation source 86 may be any known in the art capable of producing actinic radiation employed to polymerize and cross-link material in droplets 38, such as UV radiation. Specifically, radiation produced by either of sources 84 and 86 propagates along optical path 88 toward substrate 32. A circuit (not shown) is in electrical communication with radiation sources 84 and 86 to selectively allow radiation in the UV and IR spectra to impinge upon substrate 32.

[0054] Referring to FIG. 11, alternatively, radiation source 22 may include a single radiation source that produces multiple ranges of wavelength, which may be selectively controlled to impinge upon substrate 32 sequentially or concurrently. An exemplary radiation source 22 consists of a single broad spectrum radiation source 90 that produces UV and IR radiation, which may consist of a mercury (Hg) lamp. To selectively impinge differing types of radiation upon substrate 32, a filtering system 92 is utilized. Filtering system 92 comprises a high pass filter (not shown) and a low pass filter (not shown), each in optical communication with radiation source 90. Filtering system 92 may position the high pass filter (not shown) such that optical path 88 comprises IR radiation or filtering system 92 may position the low pass filter (not shown) such that optical path 88 comprises UV radiation. The high pass and low pass filters (not shown) may be any known in the art, such as interference filters comprising two semi-reflective coatings with a spacer disposed therebetween. The index of refraction and the thickness of the spacer determine the frequency band being selected and transmitted through the interference filter. Therefore, the appropriate index of refraction and thickness of the spacer is chosen for both the high pass filter (not shown) and the low pass filter (not shown), such that the high pass filter (not shown) permits passage of IR radiation and the low pass filter (not shown) permits passage of UV radiation. A processor (not shown) is in data communication with radiation source 90 and filtering system 92 to selectively allow the desired wavelength of radiation to propagate along optical path 88. The circuit enables high pass filter (not shown) when IR radiation is desired and enables the low pass filter (not shown) when UV radiation is desired.

[0055] Referring to FIG. 12, substrate 32 may have one or more existing layers disposed thereon before deposition of imprinting layer 34. As a result, heating the silicon-containing material may be problematic, because the material from which the wafer is formed and/or the preexisting layers on the wafer, e.g., solidified imprinting layer 134, are substantially non-responsive to infrared radiation. As a result, very little energy transfer may occur, resulting in it being difficult to raise the temperature of the silicon-containing material sufficient to achieve cross-linking.

[0056] To facilitate cross-linking of the silicon-containing material in conformal layer 58, one of the layers included with substrate 32 may be an infrared absorption layer 94. Absorption layer 94 comprises a material that is excited when exposed to IR radiation and produces a localized heat source. Typically, absorption layer 94 is formed from a material that maintains a constant phase state during the heating process, which may include a solid phase state. Specifically, the IR radiation impinging upon absorption layer 94 causes an excitation of the molecules contained therein, generating heat. The heat generated in absorption layer 94 is transferred to the silicon-containing material via conduction through the wafer and/or any intervening layer of material thereon, e.g., absorption layer 94 may be disposed on surface 36 so as to be disposed between substrate 32 and solidified imprinting layer 134. As a result, absorption layer 94 and substrate 32 provide a bifurcated heat transfer mechanism that is able to absorb IR radiation and to produce a localized heat source sensed by the silicon-containing material in conformal layer 58. In this manner, absorption layer 94 creates a localized heat sources on surface 36. To that end, absorption layer 94 may be deposited using any known technique, including spin-coating, chemical vapor deposition, physical vapor deposition, atomic layer deposition and the like. Exemplary materials that may be formed from a carbon based PVD coating, organic thermo set coating with carbon black filler or molybdenum disulfide (MoS₂) based coating.

[0057] Referring to FIG. 13, absorption layer 94 may be disposed on a side of substrate 32 disposed opposite to solidified imprinting layer 134. As a result, absorption layer 94 may be permanently or removably attached. Exemplary materials that may be employed as absorption layer 94 include black nickel and anodized black aluminum. Also, black chromium may be employed as absorption layer 94. Black chromium is typically deposited as a mixture of oxides and is used as a coating for solar cells.

[0058] Furthermore, as shown in FIG. 2, patterned mold 26 may be fabricated from any material, such as, but not limited to, fused-silica, quartz, silicon, organic polymers, siloxane polymers, borosilicate glass, fluorocarbon polymers, metal, and combinations of the above. However, it the present embodiment, the actinic radiation propagates through patterned mold 26. Therefore, it is desired that patterned mold 26 be fabricated from material that is substantially transparent to the actinic radiation. The plurality of features on patterned mold 26 are shown as recesses 28 extending along a direction parallel to projections 30 that provide a cross-section of patterned mold 26 with a shape of a battlement. However, recesses 28 and projections 30 may correspond to virtually any feature required to create an integrated circuit and may be as small as a few tenths of nanometers.

[0059] Referring to FIGS. 2 and 14, similarly, it may be desirable to provide substrate 32 with a planarized surface upon which to forming imprinting layer 34. To that end, a primer layer 96 may be formed upon substrate 32. Primer layer 96 has proved beneficial when surface 36 of substrate 32 appears rough when compared to the features dimensions to be formed in imprinting layer 34. Additionally, it has been found beneficial to deposit primer layer 96 when forming imprinting layer 34 upon a previously disposed patterned layer present on substrate 32. Primer layer 96 may also functions, inter alia, to provide a standard interface with imprinting layer 34, thereby reducing the need to customize each process to the material from which substrate 32 is formed. In addition, primer layer 96 may be formed from an organic material with the same etch characteristics as imprinting layer 34. Primer layer 96 is fabricated in such a manner so as to possess a continuous, smooth, relatively defect-free surface that may exhibit excellent adhesion to imprinting layer 34. An exemplary material to use to form primer layer 96 is available from Brewer Science, Inc. of Rolla Mo. under the trade name DUV30J-6.

[0060] Referring to FIGS. 5 and 14, to reduce the probability that solidified imprinting layer 134 does not adhere to patterned mold 26, surface 50 may be treated with a low surface energy coating 98. Low surface energy coating 98 may be applied using any known process. For example, processing techniques may include chemical vapor deposition method, physical vapor deposition, atomic layer deposition or various other techniques, brazing and the like. In a similar fashion a low surface energy coating 198 may be applied to planarizing mold 94, shown in FIG. 15. Typically, the surfactant has a surface energy associated therewith that is lower than a surface energy of the polymerizable material in the layer. An exemplary material and process by which to form the aforementioned surfactant is discussed by Bender et al. in MULTIPLE IMPRINTING IN UV-BASED NANOIMPRINT LITHOGRAPHY: RELATED MATERIAL ISSUES, Microelectronic Engineering pp. 61–62 (2002). The low surface energy of the surfactant provides the desired release properties to reduce adherence of either imprinting layer 34 or conformal layer 58 to patterned mold 26. It should be understood that the surfactant may be used in conjunction with, or in lieu of, low surface energy coatings 98 and 198.

[0061] The embodiments of the present invention described above are exemplary. Many changes and modifications may be made to the disclosure recited above, while remaining within the scope of the invention. The scope of the invention should, therefore, be determined not with reference to the above description, but instead should be determined with reference to the appended claims along with their full scope of equivalents.

Claims

What is claimed is:

1. A composition for forming a layer on a surface, said composition comprising:

hydroxyl-functional polysiloxane;

hexamethoxymethylmelamine;

toluenesulfonic acid; and

methyl amyl ketone.

2. The composition as recited in claim 1 wherein said hydroxyl-functional polysiloxane is approximately 4% of said composition, said hexamethoxymethylmelamine is approximately 0.95% of said composition, said toluenesulfonic acid is approximately 0.05% of said composition, and said methyl amyl ketone is approximately 95% of said composition.

3. The composition as recited in claim 1 further including gamma-glycidoxypropyltrimethoxysilane.

4. The composition as recited in claim 3 wherein said hydroxyl-functional polysiloxane is approximately 4% of said composition, said hexamethoxymethylmelamine is approximately 0.7% of said composition, said gamma-glycidoxypropyltrimethoxysilane is approximately 0.25% of said composition, said toluenesulfonic acid is approximately 0.05% of said composition, and said methyl amyl ketone is approximately 95% of said composition.

5. The composition as recited in claim 1 wherein relative proportions of said hydroxyl-functional polysiloxane, hexamethoxymethylmelamine, gamma-glycidoxypropyltrimethoxysilane, said toluenesulfonic acid, and methyl amyl ketone provides said composition with approximately 20% by weight of silicon atoms upon transitioning from a liquid state to a solidified state.

Patent Citations (424)

Patent	Date	Inventor	Cited By
US3527062(A)	1970-09-01	Belinski et al.	Applicant
US3783520(A)	1974-01-01	King	Applicant
US3807027(A)	1974-04-01	Heisler	Applicant
US3807029(A)	1974-04-01	Troeger	Applicant
US3810874(A)	1974-05-01	Mitsch et al.	Applicant
US3811665(A)	1974-05-01	Seelig	Applicant
US4062600(A)	1977-12-01	Wyse	Applicant
US4070116(A)	1978-01-01	Frosch et al.	Applicant
US4098001(A)	1978-07-01	Watson	Applicant
US4119688(A)	1978-10-01	Hiraoka	Applicant
US4155169(A)	1979-05-01	Drake et al.	Applicant
US4201800(A)	1980-05-01	Alcorn et al.	Applicant
US4202107(A)	1980-05-01	Watson	Applicant
US4267212(A)	1981-05-01	Sakawaki	Applicant
US4326805(A)	1982-04-01	Feldman et al.	Applicant
US4337579(A)	1982-07-01	De Fazio	Applicant
US4355469(A)	1982-10-01	Nevins et al.	Applicant
US4414750(A)	1983-11-01	De Fazio	Applicant
US4426247(A)	1984-01-01	Tamamura et al.	Applicant
US4440804(A)	1984-04-01	Milgram	Applicant
US4451507(A)	1984-05-01	Beltz et al.	Applicant
US4507331(A)	1985-03-01	Hiraoka	Applicant
US4512848(A)	1985-04-01	Deckman et al.	Applicant
US4517337(A)	1985-05-01	Lockhart et al.	Examiner
US4544572(A)	1985-10-01	Sandvig et al.	Applicant
US4552832(A)	1985-11-01	Blume et al.	Applicant
US4552833(A)	1985-11-01	Ito et al.	Applicant
US4600309(A)	1986-07-01	Fay	Applicant
US4610442(A)	1986-09-01	Oku et al.	Applicant
US4614667(A)	1986-09-01	Larson et al.	Applicant
US4617238(A)	1986-10-01	Crivello et al.	Applicant
US4657845(A)	1987-04-01	Frechet et al.	Applicant
US4692205(A)	1987-09-01	Sachdev et al.	Applicant
US4694703(A)	1987-09-01	Routson	Applicant
US4707218(A)	1987-11-01	Giammarco et al.	Applicant
US4724222(A)	1988-02-01	Feldman	Applicant
US4731155(A)	1988-03-01	Napoli et al.	Applicant
US4737425(A)	1988-04-01	Lin et al.	Applicant
US4763886(A)	1988-08-01	Takei	Applicant
US4772878(A)	1988-09-01	Kane	Applicant
US4808511(A)	1989-02-01	Holmes	Applicant
US4826943(A)	1989-05-01	Ito et al.	Applicant
US4846931(A)	1989-07-01	Gmitter et al.	Applicant
US4848179(A)	1989-07-01	Ubhayakar	Applicant
US4848911(A)	1989-07-01	Uchida et al.	Applicant
US4857477(A)	1989-08-01	Kanamori	Applicant
US4883561(A)	1989-11-01	Gmitter et al.	Applicant
US4887283(A)	1989-12-01	Hosno	Applicant
US4891303(A)	1990-01-01	Garza et al.	Applicant
US4908298(A)	1990-03-01	Hefferon et al.	Applicant
US4909151(A)	1990-03-01	Fukui et al.	Applicant
US4919748(A)	1990-04-01	Bredbenner et al.	Applicant
US4921778(A)	1990-05-01	Thackeray et al.	Applicant
US4929083(A)	1990-05-01	Brunner	Applicant
US4931351(A)	1990-06-01	McColgin et al.	Applicant
US4959252(A)	1990-09-01	Bonnebat et al.	Applicant
US4964145(A)	1990-10-01	Maldonado	Applicant
US4964945(A)	1990-10-01	Calhoun et al.	Applicant
US4976818(A)	1990-12-01	Hashimoto et al.	Applicant
US4980316(A)	1990-12-01	Huebner	Applicant
US4999280(A)	1991-03-01	Hiraoka	Applicant
US5028366(A)	1991-07-01	Harakal et al.	Applicant
US5053318(A)	1991-10-01	Gulla et al.	Applicant
US5063321(A)	1991-11-01	Carter	Applicant
US5071694(A)	1991-12-01	Uekita et al.	Applicant
US5072126(A)	1991-12-01	Progler	Applicant
US5073230(A)	1991-12-01	Maracas et al.	Applicant
US5074667(A)	1991-12-01	Miyatake	Applicant
US5108875(A)	1992-04-01	Thackeray et al.	Applicant
US5110514(A)	1992-05-01	Soane	Applicant
US5126006(A)	1992-06-01	Cronin et al.	Applicant
US5148036(A)	1992-09-01	Matsugu et al.	Applicant
US5148037(A)	1992-09-01	Suda et al.	Applicant
US5151754(A)	1992-09-01	Ishibashi et al.	Applicant
US5155749(A)	1992-10-01	DiMilia et al.	Applicant
US5169494(A)	1992-12-01	Hashimoto et al.	Applicant
US5171490(A)	1992-12-01	Fudim	Applicant
US5173393(A)	1992-12-01	Sezi et al.	Applicant
US5179863(A)	1993-01-01	Uchida et al.	Applicant
US5198326(A)	1993-03-01	Hashimoto et al.	Applicant
US5204739(A)	1993-04-01	Domenicali	Applicant
US5206983(A)	1993-05-01	Guckel et al.	Applicant
US5212147(A)	1993-05-01	Sheats	Applicant
US5218193(A)	1993-06-01	Miyatake	Applicant
US5234793(A)	1993-08-01	Sebald et al.	Applicant
US5240550(A)	1993-08-01	Boehnke et al.	Applicant
US5240878(A)	1993-08-01	Fitzsimmons et al.	Applicant
US5242711(A)	1993-09-01	DeNatale et al.	Applicant
US5244818(A)	1993-09-01	Jokerst et al.	Applicant
US5259926(A)	1993-11-01	Kuwabara et al.	Applicant
US5270984(A)	1993-12-01	Mine	Applicant
US5277749(A)	1994-01-01	Griffith et al.	Applicant
US5314772(A)	1994-05-01	Kozicki et al.	Applicant
US5318870(A)	1994-06-01	Hartney	Applicant
US5324683(A)	1994-06-01	Fitch et al.	Applicant
US5328810(A)	1994-07-01	Lowrey et al.	Applicant
US5330881(A)	1994-07-01	Sidman et al.	Applicant
US5331020(A)	1994-07-01	Brown et al.	Applicant
US5348616(A)	1994-09-01	Hartman et al.	Applicant
US5355219(A)	1994-10-01	Araki et al.	Applicant
US5357122(A)	1994-10-01	Okubora et al.	Applicant
US5362606(A)	1994-11-01	Hartney et al.	Applicant
US5366851(A)	1994-11-01	Novembre	Applicant
US5374454(A)	1994-12-01	Bickford et al.	Applicant
US5376810(A)	1994-12-01	Hoenk et al.	Applicant
US5380474(A)	1995-01-01	Rye et al.	Applicant
US5389696(A)	1995-02-01	Dempsey et al.	Applicant
US5392123(A)	1995-02-01	Marcus et al.	Applicant
US5414514(A)	1995-05-01	Smith et al.	Applicant
US5417802(A)	1995-05-01	Obeng	Applicant
US5421981(A)	1995-06-01	Leader et al.	Applicant
US5422295(A)	1995-06-01	Choi et al.	Applicant
US5424549(A)	1995-06-01	Feldman	Applicant
US5425848(A)	1995-06-01	Haisma et al.	Applicant
US5425964(A)	1995-06-01	Southwell et al.	Applicant
US5431777(A)	1995-07-01	Austin	Applicant
US5439766(A)	1995-08-01	Day et al.	Applicant
US5452090(A)	1995-09-01	Progler et al.	Applicant
US5453157(A)	1995-09-01	Jeng	Applicant
US5458520(A)	1995-10-01	DeMercurio et al.	Applicant
US5468542(A)	1995-11-01	Crouch	Applicant
US5480047(A)	1996-01-01	Tanigawa et al.	Applicant
US5504793(A)	1996-04-01	Chen	Applicant
US5507411(A)	1996-04-01	Peckels	Applicant
US5508527(A)	1996-04-01	Kuroda et al.	Applicant
US5512131(A)	1996-04-01	Kumar et al.	Applicant
US5515167(A)	1996-05-01	Ledger et al.	Applicant
US5523878(A)	1996-06-01	Wallace et al.	Applicant
US5527662(A)	1996-06-01	Hashimoto et al.	Applicant
US5542978(A)	1996-08-01	Kindt-Larsen et al.	Applicant
US5545367(A)	1996-08-01	Bae et al.	Applicant
US5563702(A)	1996-10-01	Emery et al.	Applicant
US5566584(A)	1996-10-01	Briganti	Applicant
US5594042(A)	1997-01-01	Glover et al.	Applicant
US5601641(A)	1997-02-01	Stephens	Applicant
US5629095(A)	1997-05-01	Bujanowski et al.	Applicant
US5633505(A)	1997-05-01	Chung et al.	Applicant
US5654238(A)	1997-08-01	Cronin et al.	Applicant
US5669303(A)	1997-09-01	Maracas et al.	Applicant
US5670415(A)	1997-09-01	Rust	Applicant
US5700626(A)	1997-12-01	Lee et al.	Applicant
US5723176(A)	1998-03-01	Keyworth et al.	Applicant
US5724145(A)	1998-03-01	Kondo et al.	Applicant
US5725788(A)	1998-03-01	Maracas et al.	Applicant
US5726548(A)	1998-03-01	Chiba et al.	Applicant
US5731981(A)	1998-03-01	Simard	Applicant
US5736424(A)	1998-04-01	Prybyla et al.	Applicant
US5737064(A)	1998-04-01	Inoue et al.	Applicant
US5743998(A)	1998-04-01	Park	Applicant
US5747102(A)	1998-05-01	Smith et al.	Applicant
US5753014(A)	1998-05-01	Van Rijn	Applicant
US5760500(A)	1998-06-01	Kondo et al.	Applicant
US5772905(A)	1998-06-01	Chou	Applicant
US5776748(A)	1998-07-01	Singhvi et al.	Applicant
US5779799(A)	1998-07-01	Davis	Applicant
US5785918(A)	1998-07-01	Hull	Applicant
US5802914(A)	1998-09-01	Fassler et al.	Applicant
US5804474(A)	1998-09-01	Sakaki et al.	Applicant
US5808742(A)	1998-09-01	Everett et al.	Applicant
US5825482(A)	1998-10-01	Nikoonahadetal	Applicant
US5837314(A)	1998-11-01	Beaton et al.	Applicant
US5849209(A)	1998-12-01	Kindt-Larsen et al.	Applicant
US5849222(A)	1998-12-01	Jen et al.	Applicant
US5855686(A)	1999-01-01	Rust	Applicant
US5861467(A)	1999-01-01	Bujanowski et al.	Applicant
US5876550(A)	1999-03-01	Feygin et al.	Applicant
US5877036(A)	1999-03-01	Kawai	Applicant
US5877861(A)	1999-03-01	Ausschnitt et al.	Applicant
US5884292(A)	1999-03-01	Baker et al.	Applicant
US5888650(A)	1999-03-01	Calhoun et al.	Applicant
US5895263(A)	1999-04-01	Carter et al.	Applicant
US5900160(A)	1999-05-01	Whitesides et al.	Applicant
US5905104(A)	1999-05-01	Eklund et al.	Applicant
US5907782(A)	1999-05-01	Wu	Applicant
US5912049(A)	1999-06-01	Shirley	Applicant
US5926690(A)	1999-07-01	Toprac et al.	Applicant
US5937758(A)	1999-08-01	Maracas et al.	Applicant
US5942871(A)	1999-08-01	Lee	Applicant
US5948219(A)	1999-09-01	Rohner	Applicant
US5948470(A)	1999-09-01	Harrison et al.	Applicant
US5948570(A)	1999-09-01	Kornblut et al.	Applicant
US5952127(A)	1999-09-01	Yamanaka	Applicant
US5988859(A)	1999-11-01	Kirk	Applicant
US6033977(A)	2000-03-01	Gutsche et al.	Applicant
US6035805(A)	2000-03-01	Rust	Applicant
US6036055(A)	2000-03-01	Mogadam et al.	Applicant
US6038280(A)	2000-03-01	Rossiger et al.	Applicant
US6039897(A)	2000-03-01	Lochhead et al.	Applicant
US6046056(A)	2000-04-01	Parce et al.	Applicant
US6051345(A)	2000-04-01	Huang	Applicant
US6074827(A)	2000-06-01	Nelson et al.	Applicant
US6081334(A)	2000-06-01	Brimbergen et al.	Applicant
US6088103(A)	2000-07-01	Everett et al.	Applicant
US6091485(A)	2000-07-01	Li et al.	Applicant
US6096655(A)	2000-08-01	Lee et al.	Applicant
US6117708(A)	2000-09-01	Wensel	Applicant
US6125183(A)	2000-09-01	Jiawook et al.	Applicant
US6128085(A)	2000-10-01	Buermann et al.	Applicant
US6133576(A)	2000-10-01	Shafer et al.	Applicant
US6137562(A)	2000-10-01	Masuyuki et al.	Applicant
US6143412(A)	2000-11-01	Schueller et al.	Applicant
US6150231(A)	2000-11-01	Muller et al.	Applicant
US6150680(A)	2000-11-01	Eastman et al.	Applicant
US6168845(B1)	2001-01-01	Fontana, Jr. et al.	Applicant
US6180239(B1)	2001-01-01	Whitesides et al.	Applicant
US6182042(B1)	2001-01-01	Peevers	Applicant
US6188150(B1)	2001-02-01	Spence	Applicant
US6204343(B1)	2001-03-01	Barucha et al.	Applicant
US6204922(B1)	2001-03-01	Chalmers	Applicant
US6218316(B1)	2001-04-01	Marsh	Applicant
US6234379(B1)	2001-05-01	Donges	Applicant
US6245213(B1)	2001-06-01	Olsson et al.	Applicant
US6245581(B1)	2001-06-01	Bonser et al.	Applicant
US6274294(B1)	2001-08-01	Hines	Applicant
US6309580(B1)	2001-10-01	Chou	Applicant
US6316290(B1)	2001-11-01	Wensel	Applicant
US6326627(B1)	2001-12-01	Putvinski et al.	Applicant
US6329256(B1)	2001-12-01	Ibok	Applicant
US6334960(B1)	2002-01-01	Willson et al.	Applicant
US6337262(B1)	2002-01-01	Pradeep et al.	Applicant
US6342097(B1)	2002-01-01	Terry et al.	Applicant
US6355198(B1)	2002-03-01	Kim et al.	Applicant
US6361831(B1)	2002-03-01	Sato et al.	Applicant
US6383928(B1)	2002-05-01	Eissa	Applicant
US6387783(B1)	2002-05-01	Furukawa et al.	Applicant
US6387787(B1)	2002-05-01	Mancini et al.	Applicant
US6388253(B1)	2002-05-01	Su	Applicant
US6391217(B1)	2002-05-01	Schaffer et al.	Applicant
US6391798(B1)	2002-05-01	DeFelice et al.	Applicant
US6407340(B1)	2002-06-01	Wikstrom et al.	Applicant
US6411010(B1)	2002-06-01	Suzuki et al.	Applicant
US6420892(B1)	2002-07-01	Krivy et al.	Applicant
US6423207(B1)	2002-07-01	Heidari et al.	Applicant
US6437891(B1)	2002-08-01	Chandrasekhar et al.	Applicant
US6447919(B1)	2002-09-01	Brown et al.	Applicant
US6455411(B1)	2002-09-01	Jiang et al.	Applicant
US6467761(B1)	2002-10-01	Amatucci et al.	Applicant
US6468642(B1)	2002-10-01	Bray et al.	Applicant
US6468896(B1)	2002-10-01	Rohr et al.	Applicant
US6482742(B1)	2002-11-01	Chou	Applicant
US6489068(B1)	2002-12-01	Kye	Applicant
US6495624(B1)	2002-12-01	Brown	Applicant
US6503914(B1)	2003-01-01	Benish et al.	Applicant
US6514672(B1)	2003-02-01	Young et al.	Applicant
US6517977(B1)	2003-02-01	Resnick et al.	Applicant
US6517995(B1)	2003-02-01	Jacobenson et al.	Applicant
US6518168(B1)	2003-02-01	Clem et al.	Applicant
US6518189(B1)	2003-02-01	Chou	Applicant
US6521324(B1)	2003-02-01	Debe et al.	Applicant
US6522411(B1)	2003-02-01	Moon et al.	Applicant
US6534418(B1)	2003-03-01	Plat et al.	Applicant
US6539286(B1)	2003-03-01	Jiang	Applicant
US6541356(B1)	2003-04-01	Seshan	Applicant
US6541360(B1)	2003-04-01	Plat et al.	Applicant
US6544594(B1)	2003-04-01	Linford et al.	Applicant
US6561706(B1)	2003-05-01	Singh et al.	Applicant
US6565776(B1)	2003-05-01	Li et al.	Applicant
US6565928(B1)	2003-05-01	Sakamoto et al.	Applicant
US6580172(B1)	2003-06-01	Mancini et al.	Applicant
US6580505(B1)	2003-06-01	Bareket	Applicant
US6588632(B1)	2003-07-01	Nicol	Applicant
US6600969(B1)	2003-07-01	Sudolcan et al.	Applicant
US6632742(B1)	2003-10-01	Yang et al.	Applicant
US6633391(B1)	2003-10-01	Oluseyi et al.	Applicant
US6635581(B1)	2003-10-01	Wong	Applicant
US6646662(B1)	2003-11-01	Nebashi et al.	Applicant
US6649272(B1)	2003-11-01	Moore et al.	Applicant
US6664306(B1)	2003-12-01	Gaddam et al.	Applicant
US6677252(B1)	2004-01-01	Marsh	Applicant
US6696157(B1)	2004-02-01	David et al.	Applicant
US6696220(B1)	2004-02-01	Bailey et al.	Applicant
US6703190(B1)	2004-03-01	Elian et al.	Applicant
US6713238(B1)	2004-03-01	Chou et al.	Applicant
US6716767(B1)	2004-04-01	Shih et al.	Applicant
US6719915(B1)	2004-04-01	Willson et al.	Applicant
US6721529(B1)	2004-04-01	Chen et al.	Applicant
US6730256(B1)	2004-05-01	Bloomstein et al.	Applicant
US6737202(B1)	2004-05-01	Gehoski et al.	Applicant
US6737489(B1)	2004-05-01	Linert et al.	Applicant
US6743713(B1)	2004-06-01	Mukherjee-Roy et al.	Applicant
US6753972(B1)	2004-06-01	Hirose et al.	Applicant
US6767983(B1)	2004-07-01	Fujiyama et al.	Applicant
US6770852(B1)	2004-08-01	Steger	Applicant
US6774183(B1)	2004-08-01	Palumbo et al.	Applicant
US6776094(B1)	2004-08-01	Whitesides et al.	Applicant
US6777170(B1)	2004-08-01	Bloomstein et al.	Applicant
US6790905(B1)	2004-09-01	Fitzgerald et al.	Applicant
US6802870(B1)	2004-10-01	Chang et al.	Applicant
US6805054(B1)	2004-10-01	Meissl et al.	Applicant
US6809356(B1)	2004-10-01	Chou	Applicant
US6828244(B1)	2004-12-01	Chou	Applicant
US6830819(B1)	2004-12-01	Kaplan et al.	Applicant
US2001/0023829(A1)	2001-09-01	Olsson et al.	Applicant
US2001/0040145(A1)	2001-11-01	Willson et al.	Applicant
US2001/0044075(A1)	2001-11-01	Nishimura et al.	Applicant
US2002/0042027(A1)	2002-04-01	Chou et al.	Applicant
US2002/0069525(A1)	2002-06-01	Hada et al.	Applicant
US2002/0093122(A1)	2002-07-01	Choi et al.	Applicant
US2002/0094496(A1)	2002-07-01	Choi et al.	Applicant
US2002/0098426(A1)	2002-07-01	Sreenivasan et al.	Applicant
US2002/0132482(A1)	2002-09-01	Chou	Applicant
US2002/0150398(A1)	2002-10-01	Choi et al.	Applicant
US2002/0167117(A1)	2002-11-01	Chou	Applicant
US2002/0177319(A1)	2002-11-01	Chou	Applicant
US2003/0034329(A1)	2003-02-01	Chou	Applicant
US2003/0080471(A1)	2003-05-01	Chou	Applicant
US2003/0080472(A1)	2003-05-01	Chou	Applicant
US2003/0081193(A1)	2003-05-01	White et al.	Applicant
US2003/0092261(A1)	2003-05-01	Kando et al.	Applicant
US2003/0113638(A1)	2003-06-01	Mancini et al.	Applicant
US2003/0129542(A1)	2003-07-01	Shih et al.	Applicant
US2003/0133126(A1)	2003-07-01	Sarfaly et al.	Applicant
US2003/0179354(A1)	2003-09-01	Araki et al.	Applicant
US2003/0205657(A1)	2003-11-01	Voisin	Applicant
US2003/0205658(A1)	2003-11-01	Voisin	Applicant
US2003/0215577(A1)	2003-11-01	Willson et al.	Applicant
US2003/0235787(A1)	2003-12-01	Watts et al.	Applicant
US2004/0007799(A1)	2004-01-01	Choi et al.	Applicant
US2004/0008334(A1)	2004-01-01	Sreenivasan et al.	Applicant
US2004/0009673(A1)	2004-01-01	Sreenivasan et al.	Applicant
US2004/0010341(A1)	2004-01-01	Watts et al.	Applicant
US2004/0021254(A1)	2004-02-01	Sreenivasan et al.	Applicant
US2004/0021866(A1)	2004-02-01	Watts et al.	Applicant
US2004/0022888(A1)	2004-02-01	Sreenivasan et al.	Applicant
US2004/0029041(A1)	2004-02-01	Shih et al.	Applicant
US2004/0036201(A1)	2004-02-01	Chou et al.	Applicant
US2004/0038552(A1)	2004-02-01	Watts et al.	Applicant
US2004/0046271(A1)	2004-03-01	Watts	Applicant
US2004/0046288(A1)	2004-03-01	Chou	Applicant
US2004/0053146(A1)	2004-03-01	Sreenivasan et al.	Applicant
US2004/0065252(A1)	2004-04-01	Sreenivasan et al.	Applicant
US2004/0065976(A1)	2004-04-01	Sreenivasan et al.	Applicant
US2004/0086793(A1)	2004-05-01	Sreenivasan et al.	Applicant
US2004/0089979(A1)	2004-05-01	Rubin	Applicant
US2004/0090611(A1)	2004-05-01	Choi et al.	Applicant
US2004/0104641(A1)	2004-06-01	Choi et al.	Applicant
US2004/0110856(A1)	2004-06-01	Young et al.	Applicant
US2004/0112153(A1)	2004-06-01	Choi et al.	Applicant
US2004/0112861(A1)	2004-06-01	Choi et al.	Applicant
US2004/0112862(A1)	2004-06-01	Willson et al.	Applicant
US2004/0116548(A1)	2004-06-01	Willson et al.	Applicant
US2004/0118809(A1)	2004-06-01	Chou et al.	Applicant
US2004/0122862(A1)	2004-06-01	Willson et al.	Applicant
US2004/0124566(A1)	2004-07-01	Sreenivasan et al.	Applicant
US2004/0131718(A1)	2004-07-01	Chou et al.	Applicant
US2004/0137734(A1)	2004-07-01	Chou et al.	Applicant
US2004/0141163(A1)	2004-07-01	Bailey et al.	Applicant
US2004/0141168(A1)	2004-07-01	Sreenivasan et al.	Applicant
US2004/0146792(A1)	2004-07-01	Nimmakayala et al.	Applicant
US2004/0149687(A1)	2004-08-01	Choi et al.	Applicant
US2004/0150129(A1)	2004-08-01	Hougham et al.	Applicant
US2004/0156108(A1)	2004-08-01	Chou et al.	Applicant
US2004/0163563(A1)	2004-08-01	Sreenivasan et al.	Applicant
US2004/0168586(A1)	2004-09-01	Bailey et al.	Applicant
US2004/0168588(A1)	2004-09-01	Choi et al.	Applicant
US2004/0168613(A1)	2004-09-01	Nguyen	Applicant
US2004/0169441(A1)	2004-09-01	Choi et al.	Applicant
US2004/0170770(A1)	2004-09-01	Nguyen	Applicant
US2004/0170771(A1)	2004-09-01	Bailey et al.	Applicant
US2004/0188381(A1)	2004-09-01	Sreenivasan et al.	Applicant
US2004/0189994(A1)	2004-09-01	Sreenivasan et al.	Applicant
US2004/0189996(A1)	2004-09-01	Sreenivasan et al.	Applicant
US2004/0192041(A1)	2004-09-01	Jeong et al.	Applicant
US2004/0197843(A1)	2004-10-01	Chou et al.	Applicant
US2004/0200411(A1)	2004-10-01	Willson et al.	Applicant
US2004/0202865(A1)	2004-10-01	Homola et al.	Applicant
US2004/0202872(A1)	2004-10-01	Fang et al.	Examiner
US2004/0209177(A1)	2004-10-01	Sreenivasan et al.	Applicant
US2004/0211754(A1)	2004-10-01	Sreenivasan	Applicant
US2004/0241338(A1)	2004-12-01	Foster et al.	Examiner
US2004/0251775(A1)	2004-12-01	Choi et al.	Applicant
DE2800476	1978-07-01		Applicant
DE19648844	1997-09-01		Applicant
EP244884	1987-03-01		Applicant
EP733455	1996-09-01		Applicant
EP803555(A2)	1997-04-01		Examiner
EP867775	1998-09-01		Applicant
JP55-88332	1980-07-01		Applicant
JP57-7931	1982-01-01		Applicant
JP58-129074	1983-08-01		Applicant
JP63-138730	1988-06-01		Applicant
JP1-196749	1989-08-01		Applicant
JP2-24848	1990-01-01		Applicant
JP2-92603	1990-04-01		Applicant
JP2192045	1990-07-01		Applicant
JP2-219881(A)	1990-09-01		Examiner
JP4-70379	1992-05-01		Applicant
WO87/02935	1987-05-01		Applicant
WO92/17883	1992-10-01		Applicant
WO98/10121	1998-03-01		Applicant
WO99/05724	1999-02-01		Applicant
WO99/45753	1999-09-01		Applicant
WO99/63535	1999-12-01		Applicant
WO/21689	2000-04-01		Applicant
WO/54107	2000-09-01		Applicant
WO1/33232	2001-05-01		Applicant
WO1/33300	2001-05-01		Applicant
WO1/47003(A2)	2001-06-01		Applicant
WO1/53889	2001-07-01		Applicant
WO1/63361	2001-08-01		Applicant
WO1/69317	2001-09-01		Applicant
WO1/79589	2001-10-01		Applicant
WO1/79591	2001-10-01		Applicant
WO1/79592	2001-10-01		Applicant
WO1/79933	2001-10-01		Applicant
WO1/90816	2001-11-01		Applicant
WO2/006902	2002-01-01		Applicant
WO2/07199	2002-01-01		Applicant
WO2/008835	2002-01-01		Applicant
WO2/17383	2002-02-01		Applicant
WO2/22916	2002-03-01		Applicant
WO2/24977	2002-03-01		Applicant
WO2/067055	2002-08-01		Applicant
WO3/010289	2003-02-01		Applicant
WO3/079416	2003-09-01		Applicant
WO3/099536	2003-12-01		Applicant
WO2004/006120	2004-01-01		Applicant
WO2004/016406	2004-02-01		Applicant
WO2004/034424	2004-04-01		Applicant
WO2004/044651	2004-05-01		Applicant
WO2004/054784	2004-07-01		Applicant
WO2004/055594	2004-07-01		Applicant
WO2004/063815	2004-07-01		Applicant
WO2004/114016	2004-12-01		Applicant

Non-Patent Literature (171)

MSDS for Dow Corning Z-6018 intermediate.Examiner
U.S. Appl. No. 10/948,511, filed Sep. 23, 2004, Xu et al.Applicant
U.S. Appl. No. 10/967,740, filed Oct 18, 2004, Xu et al.Applicant
U.S. Appl. No. 10/919,062, filed Aug. 16, 2004, Xu et al.Applicant
Chou et al., Nanoimprint Lithography, Journal of Vacuum Science Technolgoy B 14(16), pp. 4129-4133, Nov. 1, 1996.Applicant
Colburn et al., Development and Advantages of Step-and-Flash Lithography, Solid State Technology, Jul. 1, 2001.Applicant
Colburn et al., Characterization and Modeling of Volumetric and Mechanical Properties for Step and Flash Imprint Lithography Photopolymers, Journal of Vacuum Science Technology. Vol b. 19(6), Nov. 1, 2001.Applicant
Yu et al., Properties of Fluorinated Amorphous Diamond Like Carbon Films by PECVD, Applied Surface Science 219 (3-4); pp. 228-237, Dec. 1, 2003.Applicant
Compon et al., Electroanalysis at Diamond-Like and Doped-Diamond Electrodes, Electroanalysis 15(17); pp. 1349-1363, Sep. 1, 2003.Applicant
Mansano et al., Protective Carbon Layer for Chemical Corrosion of Stainless Steel, Diamond and Related Materials 12 (3-7); pp. 749-752, Mar. 1, 2003.Applicant
Butter et al., Production and Wetting Properties of Fluorinated Diamond-Like Carbon Coatings, Thin Solid Films, 311(1-2); pp. 107-113, Dec. 31, 1997.Applicant
Hakovirta et al., Heat Resistance of Fluorinated Diamond-Like Carbon Films, Diamond and Related Materiasl 10(8); pp. 1486-1490, Aug. 1, 2001.Applicant
Zhu et al., The Improvement of the Oxidation Resistance of TiAl Alloys by Fluorine Plasma-Based Ion Implantation, Surface and Coatings Technology 158; pp. 502-507, Sep. 1, 2002.Applicant
Yao et al., Structural, Mechanical and Hydrophobic Properties of Fluorine-Doped Diamond-Like Carbon Films Synthesized by Plasma Immersion Ion Implantation and Deposition (PIII-D), Applied Surface Science 230; pp. 172-178, Apr. 17, 2004.Applicant
Bailey et al., Step and Flash Imprint Lithography: Defect Analysis, Journal of Vacuum Science, B 19(6), pp. 2806-2810, Nov. 1, 2001.Applicant
Bailey et al., Step and Flash Imprint Lithography: Template Surface Treatment and Defect Analysis, Journal of Vacuum Science, B 18(6), pp. 3572-3577, Nov. 1, 2000.Applicant
Schneider et al., Stripes of Partially Fluorinated Alkyl Chains: Dipolar Langmuir Monolayers.Applicant
Data Sheet for MAK (Methyl n-Amyl Ketone), www.sp-chem.com/fine—e, Jan. 1, 2003.Applicant
Data Sheet for gamma-Glycidoxypropyltrimethoxysilane, www.powerchemical.net/3100.htm, Dec. 5, 2003.Applicant
Silicon or Silica, www.mii.org/Minerals/photosil, Mar. 31, 2005.Applicant
Electronic Devices and Circuits, people.deas.harvard.edu/˜jones/es154/lectures/lecture—2/materials/materials.html, Mar. 31, 2005.Applicant
Data Sheet for Cymel 303ULF, www.cytec.com, 12:00:00 AM.Applicant
Data Sheet for Cycat 4040, www.cytec.com, 12:00:00 AM.Applicant
International Chemical Safety Card for p-Toluenseulfonic Acid, www.itcilo.it/english/actrav/teleam/osh/ic/104154.htm, Dec. 5, 2003.Applicant
Data Sheet for p-Toluenesulfonic Acid, NIOSH Manual of Analytical Methods (NMAM), Fourth Edition, 12:00:00 AM.Applicant
Data Sheet for Dow Corning Z-6018, , 12:00:00 AM.Applicant
Data Sheet for Methyl Amyl Ketone, www.arb.ca.gov/db/solvents/solvent—pages/Ketones-HTML/methyl—amyl.htm, Mar. 31, 2005.Applicant
Abstract of Japanese Patent 02-24848, Jan. 26, 1990.Applicant
Abstract of Japanese Patent 02-92603, Aug. 12, 2004.Applicant
Abstract of Japanese Patent 55-88332, Apr. 14, 2004.Applicant
Abstract of Japanese Patent 57-7931, Apr. 14, 2004.Applicant
Abstract of Japanese Patent 58-129074, Aug. 1, 1983.Applicant
Abstract of Japanese Patent 63-138730, Apr. 14, 2004.Applicant
Ananthasuresh et al., “Strategies for Systematic Synthesis of Compliant Mems.”, DSC-vol. 55-2, Dynamic Systems and Control: vol. 2, pp. 677-686, Nov. 1, 1994.Applicant
Arai et al., “Calibration and Basic Motion of Micro Hand Module.”, IEEE, Jan. 1, 1993, pp. 1660-1665.Applicant
Arai et al., “Development of a New Parallel Manipulator with Fixed Linear Actuator.”, In Proceedings of Japan/USA Symposium on Flexible Automation, Jan. 1, 1996, vol. 1, ASME, New York, pp. 145-149.Applicant
Armitage, “Analysis of Overlay Distortion Patterns.”, Journal of Vacuum Science. B 20(6) pp. 2891-2895, Nov. 1, 2002.Applicant
Bender et al., “Fabrication of Nanostructures using a UV-based Imprint Technique.”, Microelectronic Engineering 53, Jan. 1, 2000, pp. 233-236.Applicant
Bender et al., “Multiple Imprinting in UV-based Nanoimprint Lithography: Related Material Issues.”, Microelectronic Engineering 61-62, Jan. 1, 2002, pp. 407-413.Applicant
Blomquist et al., “Fluorinated Acrylates in making Low-Loss, Low-Birefringence, and Single-Mode Optical Waveguides with Exceptional Thermo-Optic Properties.”, SPIE Conference on Linear Optical Properties of Waveguides and Fibers, Jul. 1, 1999, vol. 3799, pp. 266-279.Applicant
Braeuer et al., “Precise Polymer Micro-Optical Systems.”, MRS Bulletin, Jul. 1, 2001, pp. 519-522.Applicant
Chen et al., “Adaptive Alignment of Photomasks for Overlay Placement.”, Journal of Vacuum Science. B20(6) pp. 3099-3105, Nov. 1, 2002.Applicant
Choi et al., “Design of Orientation Stages for Step and Flash Imprint Lithography.”, Precision Engineering, Jan. 1, 2001, pp. 192-199.Applicant
Chou et al., “Imprint Lithography with 25-Nanometer Resolution.” Science vol. 272, Apr. 5, 1996, pp. 85-87.Applicant
Chou et al., “Imprint Lithography with Sub-10 nm Feature Size and High Throughput.”, Microelectronic Engineering 35, Jan. 1, 1997, pp. 237-240.Applicant
Chou et al., “Imprint of Sub-25 nm Vias and Trenches in Polymers.”, Applied Physics Letter, Nov. 20, 1995, 67 (21).Applicant
Chou et al., “Lithographically Induced Self-assembly of Periodic Polymer Micropillar Arrays.”, J. Vac. Sci. Technol., Nov. 1, 1999, B 17(6), pp. 3197-3202.Applicant
Chou et al., “Nanoimprint Lithography and Lithographically Induced Self-Assembly.”, MRS Bulletin, Jul. 1, 2001, pp. 512-517.Applicant
Chou, Ultrafast and Direct Imprint of Nanostructures in Silicon, Nature, Col. 417, (Jun. 2002), pp. 835-837.Applicant
CIBA Specialty Chemicals, “What is UV Curing?”, www.cibasc.com/image.asp?id=4040.Applicant
Colburn et al., “Step and Flash Imprint Lithography for sub-100 nm Patterning.”, Proceedings of SPIE, Jan. 1, 2000, vol. 3997, pp. 453-457.Applicant
Colburn et al., “Step and Flash Imprint Lithography: A New Approach to High-Resolution Patterning.”, Proc of SPIE, vol. 3676.Applicant
Cowie, “Polymers: Chemistry and Physics of Modern Materials.”, 2nd Ed., Jan. 1, 1991, pp. 408-409.Applicant
Eldada et al., “Advanced Polymer Systems for Optoelectronic Integrated Circuit Applications.”, SPIE, Jan. 1, 1997, vol. 3006, pp. 344-361.Applicant
Eldada et al., “Affordable WDM Components: The Polymer Solution.”, SPIE, Jan. 1, 19998, vol. 3234, pp. 161-174.Applicant
Eldada et al., “Robust Photopolymers for MCM, Board, and Backplane Optical Interconnects.”, SPIE, Jan. 1, 1998, vol. 3288, pp. 175-191.Applicant
Feldman et al., “Wafer Chuck Magnification Correction in X-Ray Lithography.”, J. Vac. Sci. Technol. B 16(6), Nov. 1, 1998, pp. 3476-3479.Applicant
Feynman, “There's Plenty of Room at the Bottom.”, International Appl. No. PCT/US2002/015551.Applicant
Gokan et al., “Dry Etch Resistance of Organic Materials.”, J. Electrochem. Soc.: Solid-State Science and Technology, Jan. 1, 1983, pp. 143-146.Applicant
Goldfarb et al., “A Well-Behaved Revolute Flexure Joint for Compliant Mechanism Design.”, ASME Journal of Mechanical Design, Sep. 1, 1999, vol. 121, No. 3, pp. 424-429.Applicant
Howell et al., “A Loop-Closure Theory for the Analysis and Synthesis of Compliant Mechanisms.”, Journal of Mechanical Design, Mar. 1, 1996, vol. 188, pp. 121-125.Applicant
Hu et al., “Fluorescence Probe Techniques (FPT) for Measuring the Relative Efficiencies of Free-Radical Photoinitiators.”, Macromolecules, May 29, 1998, 31, pp. 4107-4113.Applicant
International Application No. PCT/US2002/015551, Communication Relating to the Results of the Partial International Search.Applicant
International Search Report for PCT/US 00/30041, Oct. 18, 2001.Applicant
International Search Report for PCT/US 01/26049, Feb. 19, 2002.Applicant
Johnson et al., “Advances in Step and Flash Imprint Lithography.”, SPIE Microlithography Conference, Feb. 23, 2003.Applicant
Kanetomo et al., “Robot for Use in Ultrahigh Vacuum.”, Solid State Technology, Aug. 1, 1997, pp. 63-72.Applicant
Kawata et al., “Imprint/Photo Hybrid Lithography Using Conventional Contact Aligner.”, Japanese Journal of Applied Physics, Jun. 29, 2004, vol. 43, No. 68, pp. 4027-4030.Applicant
Kim et al., “High-precision Magnetic Levitation Stage for Photolithography.”, Precision Engineering, Apr. 1, 1998, vol. 22, No. 2, pp. 66-77.Applicant
Kim et al., “Reducing Photocurable Polymer Pattern Shrinkage and Roughness during Dry Etching in Photo-Nanoimprint Lithography.”, Japanese Journal of Applied Physics, Jun. 29, 2004, vol. 43, No. 6B, pp. 4022-4026.Applicant
Kim et al., “Surface Energy and Polarity of Treated Indium-Tin-Oxide Anodes for Polymer Light-Emitting Diodes Studied by Contact Angle Measurements.”, Journal of Applied Physics, 1999, pp. 2774-2778, vol. 86, No. 5.Applicant
Martin et al., “Predication of Fabrication Distortions in Step and Flash Imprint Lithography Templates.”, Journal of Vacuum Science. B 20(6) pp. 2891-2895, Nov. 1, 2002.Applicant
Merlet, “Parallel Manipulators: State of the Art and Perspectives.”, Advanced Robotics, Jan. 1, 1994, vol. 8, pp. 589-596.Applicant
Mirkin et al., “Emerging Methods for Micro-and-Nanofabrication.”, MRS Bulletin, Jul. 1, 2001, pp. 506-509.Applicant
Mitsui et al., “Application of Two-Wavelength Optical Heterodyne Alignment System in XS-1.”, Part of the SPIE Conference on Emerging Lithographic Technologies III, Mar. 1, 1999, SPIE vol. 3676, pp. 455-464.Applicant
Mittal, “Precision Motion Control of a Magnetic Suspension Actuator Using a Robust Nonlinear Compensation Scheme”, IEE/ASME Transactions on Mechatronics., Dec. 1, 1997, vol. 2., No. 4, pp. 268-280.Applicant
Moon et al., Interferometric-Spatial-Phase Imaging for Six-Axis Mask Control, Oct. 17, 2003, MIT Nanostructures Laboratory, Research Laboratory of Electronics.Applicant
Nakamatsu et al., “Bilayer Resist Method for Room-Temperature Nanoimprint Lithography.”, Japanese Journal of Applied Physics, Jun. 29, 2004, vol. 43, No. 6B, pp. 4050-4053.Applicant
NERAC.COM Retro Search, “Imprint Lithography.” Oct. 16, 2004.Applicant
NERAC.COM Retro Search, “Multi-Layer Resists”, Sep. 2, 2004.Applicant
NERAC.COM Retro Search, “Reduction of Dimension of Contact Holes”, Aug. 31, 2004.Applicant
NERAC.COM Retro Search, “Trim Etching of Features Formed on an Organic Layer”, Sep. 2, 2004.Applicant
Nguyen, “Asymmetric Fluid-Structure Dynamics in Nanoscale Imprint Lithography.” The University of Texas at Austin, Aug. 1, 2001, pp. 1-111.Applicant
Office Action from U.S. Pub. 2003-0133126-A1.Applicant
Ohya et al., “Development of 3-DOF Finger Module for Micro Manipulation”, Proc. of IEEE, Mar. 1, 1999, Intl. Conf. on Intelligent Robots and Systems, pp. 894-899.Applicant
Otto et al., “Characterization and Application of a UV-based Imprint Technique”, Microelectronic Engineering 57-58, Jan. 1, 2001, pp. 361-366.Applicant
Otto et al., “Reproducibility and Homogeneity in Step and Repeat UV-Nanoimprint Lithography”, Microelectronic Engineering 73-74, Jan. 1, 2004, pp. 152-156.Applicant
Otto et al., “Step and Repeat UV-Nanoimprint Lithography: Material Issues”, NNT02 San Francisco, Dec. 11, 2002.Applicant
Papirer et al., “Abstract of The Grafting of Perfluorinated Silanes onto the Surface of Silica: Characterization by Inverse Gas Chromatography”, Journal of Colloid and Interface Science 159, Aug. 1, 1993, pp. 238-242.Applicant
Papirer et al., “The Grafting of Perflourinated Silanes onto the Surface of Silica: Characterization by Inverse Gas Chromatography”, Journal of Colloid and Interface Science 159, Aug. 1, 2003, pp. 238-242.Applicant
Parikh et al., “An Intrinsic Relationship between Molecular Structure in Self-Assembled n-Alkylsiloxane Monolayers and Deposition Temperature.”, Journal of Phys. Chem., Jul. 1, 1994, pp. 7577-7590.Applicant
Paros et al., “How to design Flexure Hinges.”, Machine Design, Nov. 25, 1965, pp. 151-156.Applicant
Peng et al., “Compliant Motion Control of Kinematically Redundant Manipulators.”, IEEE Transactions on Robotics and Automation, Dec. 1, 1993, vol. 9, No. 6, pp. 831-837.Applicant
Sagiv, “Organized Monolayers by Absorption. 1, Formation and Structure of Oleophobic Mixed Monolayers on Solid Surfaces.”, Journal of American Chemical Society/102:1, Jan. 2, 1980.Applicant
Scheer et al., “Problems of the Nanoimprinting Technique for Nanometer Scale Pattern Definition.”, J. Vac. Sci. Techno. B., Nov. 1, 1998, pp. 3917-3921.Applicant
Schneider et al., “The Wave-Printer: Towards Large-Area, Multilayer Microcontact Printing.”, Proc. of 4th Euspen International Conference, Glasgos, Scotland (UK), May 1, 2004.Applicant
Slocum, “Precision Machine Design: Macromachine Design Philosophy and Its Applicability to the Design of Micromachines.”, Micro Electro Mechanical Systems, Feb. 4, 1992.Applicant
Sowah, “Diamond Used to Break the Mould [online].”, [Retrieved on Sep. 2, 2003.] Retried from the Internet: <URL: http: HTTP://eetuk.com/showArticle,jhtml?articleID=19203691>., Sep. 2, 2003.Applicant
Sreenivasan et al., “IDF Spin Cast Imprinting.”, Oct. 21, 2004, Powerpoint Presentation.Applicant
Srinivasan et al., “Alkyltrichlorosilane-Based Self-Assembled Monolayer Films for Stiction Reduction in Silicon Micromachines.”, Journal of Microelectromechanical Systems, Jun. 1, 1998, vol. 7, No. 2, p. 252-260.Applicant
Stewart, “A Platform With Six Degrees of Freedom.”, Proc Instn Mech Engrs, May 28, 1965, vol. 180, Pt1, No. 15, pp. 371-378.Applicant
Stix, “Getting More from Moores”, Scientific American.Applicant
Sung et al., “Abstract of Micro/nano-tribological Characteristics of Self-Assembled Monolayer and its Application in Nano-Structure Fabrication”, Elsevier Science B.V., Jul. 1, 2003, vol. 255, No. 7.Applicant
Sung et al., “Micro/nano-tribological Characteristics of Self-Assembled Monolayer and its Application in Nano-Structure Fabrication.”, Elsevier Science B.V., Jul. 1, 2003, vol. 255, No. 7, pp. 808-818.Applicant
Tajbakhsh et al., “Three-Degree-of-Freedom Optic Mount for Extreme Ultraviolet.”, American Society for Precision Engineering, Jan. 1, 1998, pp. 359-362.Applicant
Tanikawa et al., “Development of Small-sized 3 DOF Finger Module in Micro Hand for Micro Manipulation.”, Proc. of IEEE, Mar. 1, 1999, Intl. conf. on Intelligent Robots and Systems, pp. 876-881.Applicant
Tomita et al., “A 6-axes Motion Control Method for Parallel-Linkage-Type Fine Motion Stage.”, JSPE-58-04, pp. 118-124.Applicant
Translation of Japanese Patent 02-24848, Jan. 26, 1990.Applicant
Translation of Japanese Patent 02-92603, Apr. 3, 1990.Applicant
Trilogy Systems, “Linear Motors 310”, www.trilogysystems.com, Jan. 1, 2001.Applicant
Uchida et al., “A Mask-to-Wafer Alignment and Gap Setting Method for X-ray Lithography Using Graftings”, Journal Vacuum Science Technology, Nov. 1, 1991, B 9 (6), pp. 3202-3206.Applicant
U.S. Appl. No. 09/698,317, filed Oct. 27, 2000, Choi et al., “High Precision Orientation Alignment and Gap Control Stages for Imprint Lithography Processes.”Applicant
U.S. Appl. No. 10/463,396, filed Jun. 17, 2003, Choi et al., “Method to Reduce Adhesion Between a Conformable Region and a Pattern of a Mold.”Applicant
U.S. Appl. No. 10/614,716, filed Jul. 7, 2003, Sreenivasan et al., “A Conforming Template for Patterning Liquids Disposed on Substrates.”Applicant
U.S. Appl. No. 10/666,527, filed Sep. 18, 2003, Bailey et al., “Imprint Lithography Templates having Alignment Marks.”Applicant
U.S. Appl. No. 10/677,639, filed Oct. 2, 2003, McMackin et al., “Single Phase Fluid Imprint Lithography Method.”Applicant
U.S. Appl. No. 10/687,519, filed Oct. 16, 2003, Truskett et al., “Low Surface Energy Templates.”Applicant
U.S. Appl. No. 10/687,562, filed Oct. 16, 2003, Cherala et al., “Applying Imprinting Material to Substrates Employing Electromagnetic Fields.”Applicant
U.S. Appl. No. 10/694,284, filed Oct. 27, 2003, Xu, “Methods for Fabricating Patterned Features Utilizing Imprint Lithography.”Applicant
U.S. Appl. No. 10/760,821, filed Jan. 20, 2004, Sreenivasan et al., “Method for Concurrently Employing Differing Materials to Form a Substrate.”Applicant
U.S. Appl. No. 10/784,911, filed Feb. 23, 2004, Xu, “Materials for Imprint Lithography.”Applicant
U.S. Appl. No. 10/785,248, filed Feb. 24, 2004, Choi et al., “A Method to Control the Relative Position Between a Body and a Surface.”Applicant
U.S. Appl. No. 10/788,700, filed Feb. 27, 2004, Sreenivasan et al., “Full-Wafer or Large Area Imprinting with Multiple Separated Sub-Fields for High Throughput Lithography.”Applicant
U.S. Appl. No. 10/864,214, filed Jun. 9, 2004, Sreenivasan et al., “An Imprint Lithography System to Produce a Light to Impinge upon and Polymerize a Liquid in Superimposition with Template Overlay Marks.”Applicant
U.S. Appl. No. 10/898,034, filed Jul. 23, 2004, McMackin et al., “A Method of Creating a Turbulent Flow of Fluid between a Mold and a Substrate.”Applicant
U.S. Appl. No. 10/898/037, filed Jul. 23, 2004, McMackin et al., “A System of Creating a Turbulent Flow of Fluid between a Mold and a Substrate.”Applicant
U.S. Appl. No. 60/394,458, filed Jul. 8, 2002, Sreenivasan et al., “Method and Apparatus for Whole Wafer Planarization using Optical Flats and Light Curable Liquids.”Applicant
U.S. Appl. No. 10/616,294, filed Jul. 9, 2003, Choi et al., “Systems for Magnification and Distortion Correction for Imprint Lithography Processes.”Applicant
Vanderbilt, “VU9730 Specifications for Improved Flexure Device”, Vanderbilt University Office of Transfer Technology, 101, 25, 192-199.Applicant
Wang et al., “Passive Compliance versus Active Compliance in Robot-Based Automated Assembly Systems”, Industrial Robot, Jan. 1, 1998, vol. 25, No. 1, pp. 48-57.Applicant
White et al., “Novel Alignment System for Imprint Lithography”, J. Vac. Sci. Technol. B 18(6), Nov. 1, 2000, pp. 3552-3556.Applicant
Williams et al., “Six Degree of Freedom Mag-Lev Stage Development”, SPIE, Jan. 1, 1997, vol. 3051, pp. 856-867.Applicant
Wu, “Large Area High Density Quantized Magnetic Disks Fabricated Using Nanoimprint Lithography”, J. Vac. Sci. Technol., Nov. 1, 1998, B 16(6), pp. 3825-3829.Applicant
Xia et al., “Soft Lithography”, Angew. Chem. Int. Ed., Jan. 1, 1998, pp. 551-575.Applicant
Xia et al., “Soft Lithography”, Annu Rev. Mater. Sci., 1998, 28: 153-184.Applicant
Data sheet for Silsesquioxanes, Aldrich website-printed Sep. 20, 2005.Applicant
Dent et al., “Microelectronic Grade Silicone Materials for CSP, ” 1999.Applicant
Barclay et al., “Bilayer Resist Solutions for Sub 100nm Device Production”. publication date that is known to applicant is before the filing date of the instant application.Applicant
Pernette et al., “Design of Parallel Robots in Microbotics”, Robotica, Jan. 1, 1997, vol. 15, pp. 417-420.Applicant
Physik Instruments, “Hexapod Six-Axts Parallel Kinematics Robot”, Nano Positioning, Jan. 1, 1998, pp. 8.4-8.5.Applicant
Physik Instruments, “NanoPositioning, MicroPositioning, Piezo Technology”, Pl Online Catalog, Jan. 1, 1999, www.physikinstruments.com.Applicant
Physik Instruments, “Product Catalog for Micropositioning”, 1997.Applicant
“Photoresist Coating Methods”, E-Mail from Susan Bagen ([email protected]) to Dhaval Shah, Sep. 18, 1997.Applicant
Raibert et al., “Hybrid Position/Force Control of Manipulators”, Journal of Dynamic Systems, Measurement, and Control, Jun. 1, 1981, vol. 102, pp. 126-133.Applicant
Rong et al., “Design and Analysis of Flexure-Hige Mechanism Used in Micro-Positioning Stages”, ASME, Jan. 1, 1994, vol. 2, pp. 979-985.Applicant
Rong et al., “Dynamics of Parallel Mechanism with Direct Compliance Control”, IEEE, Jan. 1, 1997, pp. 1753-1758.Applicant
Roos et al., “Abstract of Nanoimprint Lithography with a Commercial 4 inch Bond System for Hot Embossing”, Proceedings of SPIE, Oct. 1, 2001, vol. 4343, pp. 427-435.Applicant
Roos et al., “Nanoimprint Lithography with a Commercial 4 inch Bond System for Hot Embossing”, Proceedings of SPIE, Oct. 1, 2001, vol. 4343, pp. 427-435.Applicant
Ruchhoeft et al., “Patterning Curved Surfaces: Template Generation by Ion Beam Proximity Lithography and Relief Transfer by Step and Flash Imprint Lithography”, Journal of Vacuum Science and Technology, pp.1-17.Applicant
Koseki, “Design and Accuracy Evaluation of High-Speed and High Precision Parallel Mechanism.”, Proc. Of IEEE, Jan. 1, 1998, Intl. Conf. on Robotics & Automation, pp. 1340-1345.Applicant
Kotachi et al., “Si-Containing Positive Resist for Arf Excimer Laser Lithography.”, Photopolymer Science and Technology, Nov. 4, 1995, pp. 615-622.Applicant
Krauss et al., “Fabrication of Nanodevices Using Sub-25 nm Imprint Lithography.”, Appl. Phy. Lett., Jan. 1, 1995, 67 (21), pp. 3114-3116.Applicant
Krug et al., “Fine Patterning of Thin Sol-gel Films.”, Journal of Non-Crystalline Solids, Jan. 1, 1992, 147 & 148, pp. 447-450.Applicant
Kumar et al., “Features of Gold Having Micrometer to Centimeter Dimensions can be Formed Through a Combination of Stamping with an Elastomeric Stamp and an Alkanethiol “ink” followed by Chemical Etching.”, Applied Physics Letters, Oct. 4, 1993, vol. 63, Issue 14, pp. 2002-2004.Applicant
Lee et al., “An Ultraprecision Stage for Alignment of Wafers in Advanced Microlithography.”, Precision Engineering, Sep. 1, 1997, pp. 113-122.Applicant
Lee et al., “Ultra Precision Positioning System for Servo Motor-piezo Actuator Using the Dual Servo Loop and Digital filter Implementation.”, American Society for Precision Engineering, Jan. 1, 1998, pp. 287-290.Applicant
Lin, “Multi-Layer Resist Systems.”, Introduction to Microlithography, Feb. 14, 1983, pp. 287-349.Applicant
Lucas Aerospace, Free-Flex® Pivot Catalog, Jan. 1, 1999.Applicant
Luurtsema, “Spin Coating for Rectangular Substrates.”, Retrieved May 23, 2002 from URL: http://buffy.eecs.berkelye.edu/IRO/Summary/97abstracts/gluurts.2.html, May 23, 1992.Applicant
Mansky et al., “Large-Area Domain Alignment in Block Copolymer Thin Films Using Electric Fields.”, Macromolecules, Jun. 9, 1998, vol. 31, No. 13, pp. 4399-4401.Applicant
Goldfarb et al., “Compliant Micromanipulator Design for Scaled Bilateral Telemanipulation of Small-Scale Environments.”, ASME International Mechanical Engineering Conference and Exposition, Nov. 1, 1998, DSC- vol. 64, pp. 213-218.Applicant
Haisma et al., “Mold-assisted Nanolithography: A Process for Reliable Pattern Replication.”, J. Vac. Sci. Technol. B, Nov. 1, 1996, pp. 4124-4128.Applicant
Hashimoto et al., “Design and Characteristics of a Parallel Link Compliant Wrist.” IEEE, May 1, 1994, Department of Mechanical Engineering, Kagoshiam University, pp. 2457-2462.Applicant
Heidari, “Nanoimprint Lithography at the 6 in. Wafer Scale.”, J. Vac. Sci. Technol. B 18 (6), Nov. 1, 2000, pp. 3557-3560.Applicant
HEXAPODS, “G1000-PS Power SerIes”, www.hexapods.com.Applicant
Hexel Coporation, “Tornado 2000 System Specifications.”, www.hexel.com, Nov. 12, 1999.Applicant
Hirai et al., “Abstract of Mold Surface Treatment for Imprint Lithography”, Journal of Photopolymer Science and Technology, Aug. 28, 2001, pp. 457-462, vol. 14, No. 3.Applicant
Hirai et al., “Mold Surface Treatment for Imprint Lithography.”, Journal of Photopolymer Science and Technology, Aug. 1, 2001, vol. 14, No. 3, pp. 457-462.Applicant
Hiroshima et al., “Step-and-Repeat Photo-Nanoimprint System Using Active Orientation Head.”, Japanese Journal of Applied Physics, Jun. 29, 2004, vol. 43, No. 68, pp. 4012-4016.Applicant
Hogan et al., “Impedance Control: An Approach to Manipulation: Part 1- Theory.”, Journal of Dynamic Systems, Measurement, and Control, Mar. 1, 1985, vol. 107, pp. 1-7.Applicant
Hollis et al., “A Six-Degree-of-Freedom Magnetically Levitated Variable Compliance Fine-Motion Wrist: Design, Modeling, and Contro.”, IEEE Transactions on Robotics and Automation, Jun. 1, 1991, vol. 7., No. 3, pp. 320-332.Applicant

Abstract