Process and catalyst for preparing alcohols

[0001] 1. Field of the Invention

[0002] The present invention relates to a process for preparing alcohols by reacting carboxylic acids and/or carboxylic esters with hydrogen in the presence of a special catalyst, and to such catalysts.

[0003] 2. Brief Description of the Prior Art

[0004] The hydrogenation of carboxylic acids and carboxylic esters in the presence of catalysts based on copper chromite (Adkins catalyst) has been known for some time. However, the use of chromium-containing catalysts is undesirable for reasons of the associated risks to the environment. Efforts have therefore been made to replace these chromium-containing catalysts by more environmentally friendly chromium-free catalysts.

[0005] For instance, WO 82/03854 Al discloses a process for hydrogenating carboxylic esters in the presence of a catalyst which comprises a reduced mixture of copper oxide and zinc oxide.

[0006] EP-A 0 721 928 describes a process for preparing aliphatic α,ω-diols by hydrogenating carboxylic esters using a catalyst which comprises a reduced mixture of pressed powders of copper oxides, zinc oxides and aluminium oxides, to which iron oxide, nickel oxide or manganese oxide may be added.

[0007] U.S. Pat. No. 5,155,086 describes pulverulent hydrogenation catalysts based on copper/zinc/aluminium which contain a majority of oxides of copper and zinc, and relatively small amounts of aluminium oxide, and the pore volume of the pores which have a diameter of 120 to 1000 Å is at least 40% of the total pore volume. In particular the catalysts are suitable for hydrogenating aldehydes, ketones, carboxylic acids and carboxylic esters.

[0008] Catalysts based on copper/zinc/aluminium are known from methanol synthesis (U.S. Pat. No. 4,305,842, EP 125 689 A2). In these catalysts, aluminium oxide and zinc oxide have the function of a support material for copper. Such catalysts are prepared, for example, by coprecipitating the components and converting to active catalysts by calcining and reducing (Knözinger, Ertl, Weitkamp, Handbook of Catalysis, VCH Wiley, Weinheim 1997, 1836).

[0009] Hydrogenation catalysts based on copper/zinc/aluminium are also known in which colloidal TiO₂ or Al(OH)₃ have been added to the product of coprecipitating copper and zinc (EP 125 689 A2, Petrini et al., Preparation of catalysts III, Studies in surface science and catalysis, 16, Elsevier, Amsterdam, 1983, 735–755.)

[0010] JP J09-173845 describes the preparation of Cu/Zn catalysts which are prepared by saturating γ-aluminium oxides and have an aluminium content of approx. 53%, and the use of such catalysts in the synthesis of dimethyl ether.

[0011] WO 99/4974 describes catalysts which are prepared by precipitating Cu and Zn onto TiO₂. To prepare the tablets from the pulverulent catalyst, metallic copper powder is added as a tableting assistant in order to achieve a sufficient hardness. DE 19942895 likewise describes the effectiveness of metallic copper or cement as tableting assistants for preparing Cu/Zn/Al catalysts for hydrogenating carboxylic esters. This addition also leads to an increase in the lateral fracture hardness.

[0012] WO 97/34694 describes Cu/Al/Zn catalysts having an Al content of greater than 20% which, in the form of extrudates, have a bimodal pore size distribution. These catalysts are very suitable for the hydrogenation of fatty esters.

[0013] When used in fixed bed reactors, the existing catalysts are used as shaped bodies which only have limited mechanical stability under the mechanical stresses occurring there. In addition, the hydrogenation activity of these catalysts, particularly in the hydrogenation of esters of polybasic acids with polyhydric alcohols, for example mixtures of oligomeric esters made from adipic acid and hexanediol, is insufficient for the achievement of high space-time yields.

[0014] It is therefore an object of the invention to provide a process for preparing alcohols by reacting carboxylic acids and/or carboxylic esters with hydrogen in the presence of a catalyst which is notable for its high mechanical stability under the reaction conditions and a high activity so that relatively high space-time yields are achieved.

[0015] It was found that, surprisingly, catalysts having high mechanical stability and high activity are obtained when compounds of copper and zinc are coprecipitated onto a support material of aluminium oxide powder and the subsequent calcining is carried out in such a way that a bimodal pore size distribution is obtained.

[0016] The invention provides a process for preparing alcohols by reacting carboxylic acids and/or carboxylic esters with hydrogen in the presence of a catalyst which, in the non-reduced state, comprises 20 to 80% by weight of CuO, 10 to 80% by weight of ZnO and 1 to 50% by weight of Al₂O₃, and has such a pore size distribution that 5 to 15% of the total pore volume is in the pore diameter range of less than 150 Å and 80 to 95% is in the pore diameter range of greater than 250 Å, which is determined by mercury intrusion (mercury porosimetry) in a similar manner to DIN 66133 assuming a cylindrical pore model.

[0017] In a preferred embodiment of the invention the catalyst has such a pore size distribution that 5 to 15% of the total pore volume is in the pore diameter range of 37 to 150 Å and 80 to 95% is in the pore diameter range of 250 to 1000000 Å.

[0018] In a particularly preferred embodiment of the invention thre catalyst has such a pore size distribution that 5 to 15% of the total pore volume is in the pore diameter range of 37 to 150 Å and 80 to 95% is in the pore diameter range of 250 to 20000 Å.

[0019] The invention is described more fully hereunder with particular reference to its preferred embodiments. Preference is given to preparing the catalysts to be used according to the invention by precipitating compounds of copper and of zinc onto aluminium oxide powder.

[0020] The catalysts to be used according to the invention are notable in particular for their high hydrogenation activity and an exceptional mechanical and chemical stability, in particular, when used in fixed bed reactors employing the liquid phase method.

[0021] Preference is given to using catalysts which, in the non-reduced state, comprise 40 to 70% by weight of CuO, 20 to 50% by weight of ZnO and 4 to 10% by weight of Al₂O₃.

[0022] Particular preference is given to catalysts which, in the non-reduced state, comprise 60 to 70% by weight of CuO, 20 to 27% by weight of ZnO and 4 to 6% by weight of Al₂O₃.

[0023] The catalysts may additionally comprise compounds of the rare earth metals, alkali metals, alkaline earth metals, Zr, Ti, Co, Mo, V, W, Fe, Co, Ni, Mn and Re in an amount of 0.1 to 3% by weight as promoters.

[0024] The total pore volume is preferably in the range from 150 mm³/g to 250 mm³/g.

[0025] The specific surface area (determined according to BET, similarly to DIN 66131 by nitrogen adsorption at −196° C.) of the catalysts in the non-reduced state is 5 to 150 m²/g, preferably 5 to 60 m²/g and more preferably 5 to 30 m²/g.

[0026] Preference is given to using aluminium oxide powder having a particle size (average particle diameter) of 1 to 100 μm, more preferably 3 to 80 μm, particularly preferably 10 to 50 μm.

[0027] The specific surface area of the aluminium oxide powder (determined according to BET) is preferably 100 to 400 m²/g, more preferably 100 to 300 m²/g, and the pore volume is preferably 0.1 to 1.5 ml/g, more preferably 0.4 to 0.8 ml/g.

[0028] The sodium content of the aluminium oxide powder is advantageously 0 to 2% by weight, preferably 0.01 to 0.1% by weight.

[0029] It is also possible to use pulverulent mixed oxides of aluminium in a similar manner to the aluminium oxide powder, for example those of silicon which have the same physical properties.

[0030] The process according to the invention provides alcohols by hydrogenating carboxylic esters and/or carboxylic acids. The feedstocks may be used in technical quality.

[0031] Particularly advantageously, dihydric alcohols can be obtained by the process according to the invention by hydrogenating dibasic carboxylic acids and/or their esters with the corresponding alcohols, although a portion of the starting material may consist of higher molecular weight esters.

[0032] Particular preference is given to using mixtures of oligomeric esters made from adipic acid and hexanediol as reactants. In this case, the product obtained is 1,6-hexanediol.

[0033] Preference is given to working at a temperature of 100 to 350° C., more preferably at 150 to 300° C. and particularly preferably at 200 to 280° C.

[0034] The pressure at which the process according to the invention is carried out is preferably 50 to 400 bar, more preferably 100 to 300 bar.

[0035] The reaction may, for example, be carried out in a suspension reactor. In this case, the catalyst is used in pulverulent form. The catalyst is preferably a powder having a particle size (average particle diameter) of 20 to 100 μm.

[0036] However, the reaction may also be effected, for example, in a fixed bed reactor, advantageously using the catalyst as a shaped body.

[0037] It is possible to work in a reactor or a plurality of reactors attached in series.

[0038] The process according to the invention may be carried out either without or with the addition of solvents, for example alcohols.

[0039] When reacting carboxylic acids with hydrogen, it is advantageous to carry out the hydrogenation in an alcohol as solvent.

[0040] Examples of suitable alcohols include methanol, ethanol, propanol, n-propanol, butanediol and hexanediol. Preference is given to using the alcohol as solvent which results from the hydrogenation of the carboxylic acid.

[0041] The invention further provides catalysts for the preparation of alcohols by reacting carboxylic acids and/or carboxylic esters with hydrogen, which are characterized in that, in the non-reduced state, they comprise 20 to 80% by weight of CuO, 10 to 80% by weight of ZnO and 1 to 50% by weight of Al₂O₃ and are prepared by precipitating compounds of copper and of zinc onto aluminium oxide powder, and have such a pore size distribution that 5 to 15% of the total pore volume is in the pore diameter range of less than 150 Å and 80 to 95% of the total pore volume is in the pore diameter range of greater than 250 Å, which is determined by mercury intrusion (mercury pore symmetry) in a similar manner to DIN 66133 assuming a cylindrical pore model.

[0042] Preferred embodiments of the catalyst correspond to that which has already been detailed in the description of the process.

[0043] The catalysts according to the invention may be prepared, for example, as follows: aluminium oxide powder is suspended in water and heated to a temperature of 20 to 90° C., preferably 50 to 80° C. An aqueous solution having a copper salt, preferably copper nitrate, concentration of 0.1 to 3 mol/l, preferably 0.5 to 1.5 mol/l, and a corresponding amount of zinc salt, preferably zinc nitrate, are pumped from a feed vessel to the suspended aluminium oxide powder. The molar ratio of copper to zinc, calculated as metal, is 8:1 to 1:4, preferably 3.5:1 to 1:1.25 and more preferably 3.5:1 to 2.2:1. At the same time, an aqueous solution having a concentration of a base, preferably ammonium carbonate, sodium carbonate, sodium hydroxide or a mixture of these, of 0.1 to 5 mol/l, preferably 0.5 to 2 mol/l is added by pumping. The addition rates of the two solutions are adjusted in such a manner that the pH at the temperature at which the precipitation is carried out is maintained within the range from 5.9 to 9, preferably 5.9 to 8.1. The precipitation is carried out at a very constant temperature in the range from 20 to 90° C., preferably 50 to 80° C. After the precipitation, the resulting suspension is stirred at a temperature of 20 to 90° C., preferably 70 to 90° C. for a further period of 0.5 to 3 hours. The suspension is then filtered and the residue washed with water, preferably at 15 to 70° C., more preferably at 15 to 25° C. The filter cake is dried, for example, at temperatures of 70 to 150° C., optionally under reduced pressure. The drying may also be carried out simultaneously with a spray agglomeration, for example in a spray drier, to give particles having a substantially uniform diameter, preferably in the range from 10 to 80 μm. The dried material is then calcined at a temperature in the range from 300 to 900° C. over a period of 2 to 6 hours. When the catalyst is to be used in powder form, preference is given to calcining in the range from 400 to 800° C., and particular preference to calcining in the range from 450° C. to 700° C. When the material is to be agglomerated for use in a fixed bed reactor, for example by tableting or extruding, preference is given to calcining at 300 to 600° C. and particular preference to calcining at 300° C. to 500° C.

[0044] The calcined catalyst may be reduced by hydrogen, for example in the hydrogenation reactor in which the reaction according to the invention is effected. It is also possible to reduce the calcined catalyst in a separate reduction oven.

[0045] When the catalyst is to be used in a suspension reactor, the catalyst is advantageously used in the form of the powder.

[0046] For use in a fixed bed reactor, it is advantageous to subject the catalyst to a shaping, for example by tableting or extruding. To this end, assistants, for example graphite, magnesium stearate or zinc stearate may be added in an amount of 0.5 to 5% by weight. When shaping by tableting, preference is given to setting a lateral fracture hardness of 30 to 250 N, more preferably of 100 to 200 N, by adjusting the apparatus. The calcined powder may also be reduced before the shaping. After the shaping, there may be an additional calcination to further increase the mechanical stability and improve the chemical properties, for example at 400° C. to 900° C., preferably at 450° C. to 800° C. and more preferably at 450° C. to 700° C.

[0047] In a particular embodiment of the invention, a pore former may also be added to the powder before compacting, which results in an additional formation of pores by a subsequent calcination. Examples of useful pore formers include the uncalcined dried precipitation product of copper and zinc salts on aluminium oxide described here.

[0048] The invention is illustrated hereinbelow with the aid of examples. The examples represent individual embodiments of the invention, but the invention is not restricted to the examples.

[0049] 72 g of aluminium oxide powder (specific surface area 146.5 m²/g) is suspended in 4 l of water in a precipitating vessel and heated to 70° C. 15 kg of an aqueous solution comprising 2628 g of Cu(NO₃)₂.2.5H₂O and 1200 g of Zn(NO₃)₂.6H₂O are pumped from a feed vessel into the precipitation vessel within 3 hours. At the same time, an aqueous sodium carbonate solution of concentration 1 mol/l is added by pumping. The addition rate of the sodium carbonate solution is adjusted in such a manner that the pH is maintained within the range from 6.8 to 7. The precipitation is carried out at a temperature of 70° C. After the precipitation, the suspension is stirred at 70° C. for a further period of 2 hours. The suspension is then filtered and the residue is washed with water. The filter cake is dried at 120° C. under reduced pressure for 12 hours. The dried material is then calcined at 400° C. over a period of 4 hours. The calcination product is ground, mixed with 5% by weight of graphite and tableted using a tableting press to give cylinders having a height of 5 mm and a diameter of 5 mm. The lateral fracture hardness is set to 117 N. The specific surface area (BET) is 41.2 m²/g and was determined according to DIN 66131. The lateral fracture hardness in the reduced state is 78 N. The total pore volume is 188.8 mM³/g. The pore size distribution is such that 17.9% of the total pore volume is in the pore diameter range of less than 150 Å and 41.4% of the total pore volume is in the pore diameter range of greater than 250 Å. The exact pore size distribution is presented in Table 1.

[0050] The catalyst from Example 1 as a finished oxidic tablet is calcined at 480° C. for a further 4 h. The lateral fracture hardness is 300 N. The specific surface area (BET) is 26.4 m²/g. The lateral fracture hardness in the reduced state is 50 N. The total pore volume is 211.2 mm³/g. The pore size distribution is such that 11.1% of the total pore volume is in the pore diameter range of less than 150 Å and 84.9% of the total pore volume is in the pore diameter range of greater than 250 Å. The exact pore size distribution is presented in Table 1.

[0051] The preparation is similar to Example 1, except that the powder is calcined at 480° C. for 4 h before compacting. 5% of graphite is then added and the powder is tableted to give tablets having a diameter of 5 mm and a height of 3 mm. The lateral fracture hardness is 121 N. The specific surface area (BET) is 24.0 m²/g. The lateral fracture hardness in the reduced state is 47 N. The total pore volume is 191.9 mm³/g. The pore size distribution is such that 12.3% of the total pore volume is in the pore diameter range of less than 150 Å and 81.5% of the total pore volume is in the pore diameter range of greater than 250 Å. The exact pore size distribution is presented in Table 1.

[0052] 72 g of aluminium oxide powder (specific surface area 146.5 m²/g) is suspended in 4 1 of water in a precipitating vessel and heated to 60° C. 15 kg of an aqueous solution comprising 2628 g of Cu(NO₃)₂.2.5H₂O and 1200 g of Zn(NO₃)₂.6H₂O are pumped from a feed vessel into the precipitation vessel within 3 hours. At the same time, an aqueous sodium carbonate solution of concentration 1 mol/l is added by pumping. The addition rate of the sodium carbonate solution is adjusted in such a manner that the pH is maintained within the range from 5.9 to 6.1. The precipitation is carried out at a temperature of 60° C. After the precipitation, the suspension is stirred at 60° C. for a further period of 2 hours. The suspension is then filtered and the residue is washed with water. The filter cake is dried at 120° C. under reduced pressure for 12 hours. The dried material is then calcined at 400° C. over a period of 4 hours. The calcination product is ground, mixed with 5% by weight of graphite and tableted using a tableting press to give cylinders having a height of 5 mm and a diameter of 5 mm. The lateral fracture hardness is set to 110 N. The specific surface area (BET) is 56.4 m²/g. The lateral fracture hardness in the reduced state is 36 N. The total pore volume is 240.0 mm³/g. The pore size distribution is such that 15.9% of the total pore volume is in the pore diameter range of less than 150 Å and 21.6% of the total pore volume is in the pore diameter range of greater than 250 Å. The exact pore size distribution is presented in Table 1.

[0053] The catalyst from Example 4 as a finished oxidic tablet is calcined at 700° C. for a further 4 h. The lateral fracture hardness is 350 N. The specific surface area (BET) is 7.0 m²/g. The total pore volume is 112.0 mm³/g. The pore size distribution is such that 17.2% of the total pore volume is in the pore diameter range of less than 150 Å and 79.2% of the total pore volume is greater than 250 Å. The exact pore size distribution is presented in Table 1.

[0054] 61.5 g of aluminium oxide powder (specific surface area 146.5 m²/g) is suspended in 4 l of water in a precipitating vessel and heated to 70° C. 12.8 kg of an aqueous solution comprising 2234 g of Cu(NO₃)₂.2.5H₂O and 896 g of Zn(NO₃)₂ 6H₂O are pumped from a feed vessel into the precipitation vessel within 6 hours. At the same time, an aqueous sodium carbonate solution of concentration 1 mol/l is added by pumping. The addition rate of the sodium carbonate solution is adjusted in such a manner that the pH is maintained within the range from 7.9 to 8.1. The precipitation is carried out at a temperature of 70° C.

[0055] After the precipitation, the suspension is stirred at 70° C. for a further period of 2 hours. The suspension is then filtered and the residue is washed with water. The filter cake is dried at 120° C. under reduced pressure for 12 hours. The dried material is then calcined at 350° C. over a period of 4 hours. The calcination product is ground, mixed with 5% by weight of graphite and tableted using a tableting press to give cylinders having a height of 5 mm and a diameter of 5 mm. The lateral fracture hardness is set to 176 N. The specific surface area (BET) is 57.3 m²/g. The lateral fracture hardness in the reduced state is 34 N. The total pore volume is 165.8 mm³/g. The pore size distribution is such that 53.8% of the total pore volume is in the pore diameter range of less than 150 Å and 26.8% of the total pore volume is in the pore diameter range of greater than 250 Å. The exact pore size distribution is presented in Table 1.

[0056] The catalyst from Example 6 as a finished oxidic tablet is calcined at 600° C. for a further 4 h. The lateral fracture hardness is 158 N. The specific surface area (BET) is 15.4 m²/g. The total pore volume is 214.4 mm³/g. The pore size distribution is such that 10.2% of the total pore volume is in the pore diameter range of less than 150 Å and 88.9% of the total pore volume is in the pore diameter range of greater than 250 Å. The exact pore size distribution is presented in Table 1.

[0057]

TABLE 1
	Relative Hg	Relative Hg	Relative Hg	Relatives Hg	Relative Hg	Relative Hg	Relative Hg	Relative Hg
	pore volume	pore volume	pore volume	pore volume	pore volume	pore volume	pore volume	pore volume
	[mm3/g]	[%]	[mm3/g]	[%]	[mm3/g]	[%]	[mm3/g]	[%]
	Catalyst	Catalyst	Catalyst	Catalyst	Catalyst	Catalyst	Catalyst	Catalyst
	from	from	from	from	from	from	from	from
Pore diameter interval	Example 1	Example 1	Example 2	Example 2	Example 3	Example 3	Example 4	Example 4
2000000 Å–1000000 Å	0	0	0	0	0.00	0.00	0	0
1000000 Å–500000 Å	0.27	0.14	0.78	0.37	0.00	0.00	0.82	0.34
500000 Å–200000 Å	0.41	0.21	0.49	0.23	0.38	0.20	0.47	0.19
200000 Å–100000 Å	0.81	0.43	0.29	0.14	0.19	0.10	0.35	0.15
100000 Å–50000 Å	1.22	0.64	0.39	0.18	0.38	0.20	0.58	0.24
50000 Å–20000 Å	0.81	0.43	0.19	0.09	0.38	0.20	0.35	0.15
20000 Å–10000 Å	0.00	0.00	0.10	0.05	0.00	0.00	0.12	0.05
10000 Å–5000 Å	0.00	0.00	0.39	0.18	0.00	0.00	0.35	0.15
5000 Å–2000 Å	0.00	0.00	4.18	1.98	0.76	0.39	0.82	0.34
2000 Å–1000 Å	4.32	2.29	21.87	10.36	14.19	7.40	1.64	0.68
1000 Å–600 Å	19.32	10.24	39.56	18.74	29.71	15.48	3.04	1.27
600 Å–400 Å	18.38	9.74	52.98	25.09	54.68	28.50	6.20	2.58
400 Å–300 Å	15.95	8.45	46.37	21.96	42.57	22.19	11.46	4.77
300 Å–250 Å	16.62	8.80	11.57	5.48	13.06	6.80	25.72	10.72
250 Å–200 Å	37.16	19.69	4.96	2.35	7.19	3.75	74.46	31.03
200 Å–150 Å	39.73	21.05	3.60	1.70	4.73	2.47	75.51	31.47
150 Å–100 Å	22.03	11.67	11.18	5.29	12.30	6.41	28.05	11.69
100 Å–50 Å	10.27	5.44	11.08	5.25	9.27	4.83	8.65	3.60
50 Å–37 Å	1.49	0.79	1.17	0.55	2.08	1.08	1.40	0.58
Sum	188.79	100	211.15	100	191.87	100	239.99	100

[0058]

	Relative Hg	Relative Hg	Relative Hg	Relative Hg	Relative Hg	Relative Hg
	pore volume	pore volume	pore volume	pore volume	pore volume	pore volume
	[mm3/g]	[%]	[mm3/g]	[%]	[mm3/g]	[%]
	Catalyst from	Catalyst from	Catalyst from	Catalyst from	Catalyst from	Catalyst from
Pore diameter interval	Example 5	Example 5	Example 6	Example 6	Example 7	Example 7
2000000 Å–1000000 Å	0.00	0.00	0	0	0	0
1000000 Å–500000 Å	0.18	0.16	0.46	0.28	0.40	0.19
500000 Å–200000 Å	0.00	0.00	0.58	0.35	0.40	0.19
200000 Å–100000 Å	0.00	0.00	0.35	0.21	0.13	0.06
100000 Å–50000 Å	0.45	0.40	0.00	0.00	0.13	0.06
50000 Å–20000 Å	1.18	1.05	0.23	0.14	1.20	0.56
20000 Å–10000 Å	1.09	0.97	0.12	0.07	7.71	3.60
10000 Å–5000 Å	7.89	7.04	0.35	0.21	17.01	7.94
5000 Å–2000 Å	25.02	22.35	1.27	0.76	24.72	11.53
2000 Å–1000 Å	39.26	35.06	6.67	4.02	57.02	26.60
1000 Å–600 Å	10.52	9.39	11.27	6.80	46.52	21.70
600 Å–400 Å	1.54	1.38	10.24	6.18	24.99	11.66
400 Å–300 Å	0.82	0.73	7.71	4.65	8.77	4.09
300 Å–250 Å	0.73	0.65	5.18	3.12	1.59	0.74
250 Å–200 Å	1.18	1.05	8.17	4.93	0.93	0.43
200 Å–150 Å	2.90	2.59	24.05	14.50	1.06	0.50
150 Å–100 Å	10.97	9.80	57.52	34.70	6.51	3.04
100 Å–50 Å	7.80	6.96	31.64	19.08	15.28	7.13
50 Å–37 Å	0.45	0.40	0.00	0.00	0.00	0.00
Sum	111.98	100	165.81	100	214.37	100

[0059] A vertical, heat-insulated, high pressure tube made of non-rusting, acid-resistant material of diameter 45 mm and length 1 m which has been purged in advance with nitrogen to free it of oxygen is charged with 1.4 l of the catalysts from Examples 1 to 7. To activate the catalyst, a nitrogen stream (5 m³/h, STP) is initially passed through the catalyst bed at 200° C. for 6 hours. The catalyst is then reduced by gradually admixing in hydrogen at a temperature between 180 and 200° C. at a nitrogen pressure of 200 bar, and the starting content may not exceed 10 to 15% by volume. Over the period of 24 hours, the proportion of nitrogen is decreased more and more until finally pure hydrogen flows through the reactor. The reaction is complete when no more water of reaction is formed.

[0060] After the activation of the catalyst, the hydrogen pressure is increased to 300 bar and a volume stream of 5 m³/h (STP) is set. Hexanediol 1,6-adipate which has been obtained by esterifying adipic acid with 1,6-hexanediol in a ratio of 1:1.1 (cf. EP-A 0 721 928) is then conveyed through the reactor. The feed amount and the corresponding temperature can be taken from Table 2 which follows. Each of the pairs of feed amount and temperature values quoted in Table 2 is maintained for at least 48 h. The reaction mixture leaving the reaction tube is cooled in a second heat exchanger (water cooler) to less than 60° C. at 300 bar of hydrogen pressure and separated in a gas separator from excess hydrogen which is recycled into the hydrogenation system. After further cooling to a temperature of less than 30° C. and decompression to atmospheric pressure, the reaction product is investigated by gas chromatography. The crude yield of 1,6-hexanediol is likewise quoted in Table 2.

[0061]

TABLE 2
		Feed amount		Crude yield of
Example	Catalyst	of ester	Temperature	1,6-hexanediol
Example 8	from	200 ml/h	240° C.	96.7%
	Example 1	400 ml/h	240° C.	84.6%
		600 ml/h	240° C.	77.7%
		600 ml/h	260° C.	80.6%
		400 ml/h	260° C.	81.7%
The experiment was completed after a total running time of 2080 h. At this
time, the activity of the catalyst was still virtually unchanged.
Example 9	from	200 ml/h	240° C.	94.9%
	Example 2	400 ml/h	240° C.	94.0%
		600 ml/h	240° C.	89.2%
		600 ml/h	260° C.	87.4%
		400 ml/h	260° C.	92.4%
The experiment was completed after a total running time of 900 h. At this
time, the activity of the catalyst was still virtually unchanged.
Example 10	from	200 ml/h	240° C.	97.3%
	Example 3	400 ml/h	240° C.	97.5%
		600 ml/h	240° C.	96.6%
		600 ml/h	260° C.	93.0%
		400 ml/h	260° C.	91.9%
		900 ml/h	260° C.	93.4%
		1000 ml/h	260° C.	91.7%
The experiment was completed after a total running time of 3412 h. At this
time, the activity of the catalyst was still virtually unchanged.
Example 11	from	200 ml/h	240° C.	96.2%
	Example 4	400 ml/h	240° C.	80.5%
		600 ml/h	240° C.	73.1%
		600 ml/h	260° C.	74.7%
		400 ml/h	260° C.	85.0%
The experiment was completed after a total running time of 526 h. At this
time, the activity of the catalyst was still virtually unchanged.
Example 12	from	200 ml/h	240° C.	90.6%
	Example 5	400 ml/h	240° C.	93.0%
		600 ml/h	240° C.	83.6%
		600 ml/h	260° C.	86.3%
		400 ml/h	260° C.	91.3%
The experiment was completed after a total running time of 862 h. At this
time, the activity of the catalyst was still virtually unchanged.
Example 13	from	200 ml/h	240° C.	97.5%
	Example 6	400 ml/h	240° C.	89.2%
		600 ml/h	240° C.	85.3%
		600 ml/h	260° C.	85.4%
		400 ml/h	260° C.	88.3%
The experiment was completed after a total running time of 520 h. At this
time, the activity of the catalyst was still virtually unchanged.
Example 14	from	200 ml/h	240° C.	97.9%
	Example 7	400 ml/h	240° C.	97.3%
		600 ml/h	240° C.	96.5%
		600 ml/h	260° C.	96.1%
		800 ml/h	240° C.	93.7%
		800 ml/h	250° C.	95.8%
		1000 ml/h	260° C.	94.7%
		1100 ml/h	260° C.	93.1%
The experiment was completed after a total running time of 642 h. At this
time, the activity of the catalyst was still virtually unchanged.

[0062] Although the invention has been described in detail in the foregoing for the purpose of illustration, it is to be understood that such detail is solely for that purpose and that variations can be made therein by those skilled in the art without departing from the spirit and scope of the invention except as it may be limited by the claims.