Method for making a carbon nanotube-based field emission display

[0001] 1. Field of the Invention

[0002] The present invention relates to a method for making a field emission display device, and more particularly to a method for making a carbon nanotube field emission display device.

[0003] 2. Description of Prior Art

[0004] Carbon nanotubes are a novel carbonaceous material discovered by Iijima, a researcher of NEC corporation, in 1991. Relevant information was reported in an article by Iijima, entitled “Helical Microtubules of Graphitic Carbon” (Nature, Vol. 354, P56, 1991). Carbon nanotubes can transmit an extremely high electrical current and emit electrons easily at a very low voltage of less than 100 volts, which make it a very promising potential material for field emission applications.

[0005] Referring to FIG. 13, U.S. Pat. No. 6,232,706, invented by Hongjie Dai et al., discloses a field emission device using aligned parallel bundles of carbon nanotubes 100 extending from patterned catalyst layers 130 deposited on a layer of porous silicon 120 which is formed on a substrate 110 using a chemical vapor deposition (CVD) process. The carbon nanotubes produced by the CVD process have a variety of heights in a wide range so that the bundles of carbon nanotubes each forms a top which may be flat, concave, or in different pattern since the grown height is neither predictable nor controllable. Furthermore, a thin layer is formed on the top of the bundle which includes nanotubes with a variety of sizes, a number of remaining catalyst particles and amorphous carbon. These defects usually result in uniformity and unreliability of the field emission from the bundles of carbon nanotubes.

[0006] In order to optimize electron emissions, a triode-type field emission device is used. U.S. Pat. No. 6,515,415 discloses a typical triode-type field emission device, which generally includes a cathode electrode having carbon nanotube array emitters, an anode electrode with a phosphor screen, and a gate electrode positioned between the cathode electrode and the anode electrode to control emission of electrons from the carbon nanotube array emitters. The carbon nanotube arrays are usually produced using a chemical vapor deposition process.

[0007] In order to lower the emission turn-on voltage, a precisely controlled distance between the emitters and the gate electrode is required. Although the carbon nanotubes array growth higher with longer the reaction time, it is very difficult to control the growth height precisely. Therefore, the distance between the emitters and the gate electrodes is difficult to control merely by growth.

[0008] Accordingly, an object of the present invention is to provide a method for making a carbon nanotube-based field emission display device wherein a distance between emission tips and gate electrodes is precisely controllable.

[0009] In order to achieve the object set above, a method for making a carbon nanotube-based field emission display device in accordance with a preferred embodiment of the invention comprises the following steps: providing an insulative layer having a first surface; depositing a layer of catalyst on the first surface of the insulative layer; forming a spacer having a plurality of openings therein such that patterned areas of the layer of catalyst are exposed; forming arrays of carbon nanotubes extending from the layer of catalyst in the openings of the spacer; forming a cathode electrode on a top of each of the arrays of carbon nanotubes; forming gate electrodes on a second, opposite surface of the insulative layer offset from the patterned areas; removing portions of the insulative layer corresponding to the arrays of carbon nanotubes so as to expose the arrays of carbon nanotubes; and attaching an anode electrode having a phosphor screen to the above obtained structure. A flatness of the first surface of the insulative layer is less than 1 micron so that the arrays of carbon nanotubes grown therefrom have a same flatness. A thickness of the insulative layer can be controlled through a deposition process so that a distance between the arrays of carbon nanotubes and the gate electrodes is controllable. Preferably, the thickness of the insulative layer is in the range from 1 micron to 1000 microns.

[0010] Other objects, advantages and novel features of the present invention will become more apparent from the following detailed description when taken in conjunction with the accompanying drawings, in which:

[0024] A preferred method for making a carbon nanotube-based field emission display device in accordance with the invention will be described below with reference to FIG. 1.

[0025] Step 1 is providing a working plate. This is an optional step for the purpose of conveniently carrying out the subsequent steps. The working plate can be a nonmetallic material or a metallic material that is sufficiently heat stable to endure high temperatures at which carbon nanotubes are produced.

[0026] Step 2 is forming an insulative layer on the working plate. The insulative layer is made of insulative material such as silicon oxide, and has a predetermined thickness. In order to form carbon nanotubes from a common surface, a first surface of the insulative layer should be smooth and flat. Preferably, a variation in flatness of the first surface is less than 1 micron.

[0027] Step 3 is depositing a layer of catalyst on the first surface of the insulative layer. Generally, the catalyst is a transition metal such as Fe (Iron), Co (Cobalt), Ni (Nickel), or an alloy thereof. A thickness of the layer of catalyst is in the range from 1 nm to 10 nm, and preferably in the range from 3 nm to 5 nm. Further, the layer of catalyst is preferably annealed at a temperature of 300 degree˜400 degree.

[0028] Step 4 is forming a barrier on the layer of catalyst. The barrier has a predetermined height according to a height of carbon nanotubes produced in the following step. The height of the barrier is generally in the range from 1 micron to 1000 microns, and preferably in the range from 10 microns to 500 microns. The barrier has a plurality of perforations (not labeled) so as to define a plurality of pixel areas within which carbon nanotubes can subsequently be grown. The material of the barrier should be a heat stable material that can endure the high temperatures at which carbon nanotubes grow. Such material can be heatproof glass, metal coated with insulative material, silicon, silicon oxide, ceramic material, or mica.

[0029] Step 5 is growing arrays of carbon nanotubes from the catalyst within the plurality of perforations of the barrier. A preferred chemical vapor deposition process for growing arrays of carbon nanotubes includes: heating carbon-containing gas, such as ethylene or acetylene, to a temperature of about 700 degree, introducing the carbon-containing gas to a reaction region having catalyst pattern, and producing arrays of carbon nanotubes on the catalyst. The reaction is stopped when the arrays of carbon nanotubes have reached or just exceeded the height of the barrier.

[0030] Step 6 is forming a cathode electrode on a top of each of the arrays of carbon nanotubes. Generally, the forming of cathode electrodes employs a coating process or chemical deposition of metallic material.

[0031] Step 7 is forming a base and removing the working plate. The base is made of insulative material, such as glass, plastic, or ceramic material. The base has an inner configuration complementary with an outer configuration of the cathode electrodes and the barrier, so that the base can be coupled thereto. After removing the working plate, a second surface of the insulative layer is exposed.

[0032] Step 8 is forming gate electrodes on the exposed second surface of the insulative layer according to the pixel areas.

[0033] Step 9 is removing portions of the insulative layer corresponding to the pixel areas so as to expose the arrays of carbon nanotubes. Electrons emitting from the arrays of nanotubes can thereby pass out from the assembly. A further recommended step is to treat the exposed surfaces of the arrays of carbon nanotubes with a laser to clean the surfaces and improve the uniformity of electron emissions therefrom.

[0034] Step 10 is packaging a phosphor screen with an anode electrode onto the assembly to form the assembled carbon nanotube field emission display device.

[0035] It is to be understood that the exposed surfaces of the arrays of carbon nanotubes have a same flatness as the first surface of the insulative layer. Further, that a distance between the arrays of carbon nanotubes and the gate electrodes is determined by a thickness of the insulative layer, because a thickness of the layer of catalyst is negligible compared with that of the insulative layer. Accordingly, said distance is precisely controllable through regulation of the deposition of the insulative layer.

[0036] Referring to FIGS. 2 through 12, each step of the preferred method is described in more detailed below:

[0037] Referring to FIG. 2, a working plate 20 is provided with a plurality of grooves (not labeled) define therein, the grooves facilitating subsequent removal of the working plate 20. In order to flatten the surface of the working plate 20, the grooves can be filled with an easily removable material such as wax (not shown).

[0038] Referring to FIG. 3, a silicon oxide layer 22 is deposited on the working plate 20. The silicon oxide layer 22 has a first surface, and is removable by a wet etching process. Preferably, a variation in flatness of the first surface is less than 1 micron. A thickness of the silicon oxide layer 22 is precisely controllable through the deposition process. The thickness is generally in the range from 1 micron to 1000 microns, and preferably in the range from 10 microns to 200 microns.

[0039] Referring to FIG. 4, a protective layer 24 is deposited on the silicon oxide layer 22. The protective layer 24 is made of silicon, which can endure wet etching and is removable by a dry etching process. A thickness of the protective layer 24 is in the range from 10 nm to 100 nm.

[0040] Referring to FIG. 5, a layer of catalyst 26 is deposited with a thickness from 1 nm to 10 nm on the protective layer 24. The catalyst is made of Fe, Co, Ni, or an alloy thereof.

[0041] Referring to FIG. 6, a barrier 28 is formed with a plurality of perforations (not labeled), and carbon nanotube arrays 30 are grown from the layer of catalyst 26 within the perforations. The barrier 28 is made of insulative material, and has a predetermined height in the range from 10 microns to 500 microns. The carbon nanotube arrays 30 are produced by a chemical vapor deposition process, and heights of the arrays 30 are approximately equal to a height of the barrier 28.

[0042] Referring to FIG. 7, a negative feedback layer 32 is formed on a top of each of the carbon nanotube arrays 30, so that the carbon nanotube arrays 30 electrically contact the negative feedback layers 32. The negative feedback layers 32 are made of a material having a suitable resistance, such as silicon or alloys.

[0043] Referring to FIG. 8, a cathode electrode 34 is formed on each negative feedback layer 32. The cathode electrodes 34 are made of metallic material having a heat expansion coefficient compatible with that of the negative feedback layers 32.

[0044] Referring to FIG. 9, a base 36 is formed on the cathode electrodes 34. The base 36 is made of insulative material, such as glass, plastic or ceramic material. The base 36 has an inner configuration complementary with an outer configuration of the cathode electrodes 34 and the barrier 28, so that the base 36 can be coupled thereto.

[0045] Referring to FIG. 10, the working plate 20 is removed to expose a second surface of the silicon oxide layer 22. Gate electrodes 40 are then deposited on the second surface offset from the positions of the carbon nanotube arrays 30.

[0046] Referring to FIG. 11, portions of the silicon oxide layer 22 and the protective layer 24 are removed by a wet etching process and a dry etching process respectively. Consequently, the carbon nanotube arrays 30 are exposed. Furthermore, if considered necessary, the carbon nanotube arrays 30 are exposed to laser irradiation in order to clean the surfaces thereof.

[0047] Referring to FIG. 12, an anode electrode 50 having a phosphor layer 52 is packaged onto the assembly, thereby providing the assembled carbon nanotube-based field emission display device.

[0048] In the above-described embodiment, a distance between the gate electrodes 40 and the carbon nanotube arrays 30 is mainly determined by the thickness of the silicon oxide layer 22, because the nano-scale thicknesses of the protective layer 24 and the catalyst layer 26 are both negligible compared with the micron-level thickness of the silicon oxide layer 22. The uniformity of the exposed surfaces of the carbon nanotube arrays 30 is thus mainly determined by a flatness of the protective layer 24.

[0049] It should be noted that the working plate 20 and the protective layer 24 are both optional for practicing the present invention. In addition, the negative feedback layer 32 is an optional element for adjusting resistance if necessary.

[0050] It is understood that the invention may be embodied in other forms without departing from the spirit thereof. Thus, the present examples and embodiments are to be considered in all respects as illustrative and not restrictive, and the invention is not to be limited to the details given herein.