US 7,067,456 B2Grant

Sorbent for separation of carbon dioxide (CO₂) from gas mixtures

Issue Date:2006-06-27

•3 Claims

•13 Drawing Sheets

Abstract

A reaction-based process has been developed for the selective removal of carbon dioxide (CO₂) from a multicomponent gas mixture to provide a gaseous stream depleted in CO₂compared to the inlet CO₂concentration in the stream. The proposed process effects the separation of CO₂from a mixture of gases (such as flue gas/fuel gas) by its reaction with metal oxides (such as calcium oxide). The Calcium based Reaction Separation for CO₂(CaRS-CO₂) process consists of contacting a CO₂laden gas with calcium oxide (CaO) in a reactor such that CaO captures the CO₂by the formation of calcium carbonate (CaCO₃). Once “spent”, CaCO₃is regenerated by its calcination leading to the formation of fresh CaO sorbent and the evolution of a concentrated stream of CO₂. The “regenerated” CaO is then recycled for the further capture of more CO₂. This carbonation-calcination cycle forms the basis of the CaRS-CO₂process. This process also identifies the application of a mesoporous CaCO₃structure, developed by a process detailed elsewhere, that attains >90% conversion over multiple carbonation and calcination cycles. Lastly, thermal regeneration (calcination) under vacuum provided a better sorbent structure that maintained reproducible reactivity levels over multiple cycles.

Metadata

Assignee

The Ohio State University

Inventors

Liang-Shih Fan
Himanshu Gupta

Application Information

Application Number:US 10/359,763

Filing Date:2003-02-06

Priority Date:2003-02-06

Art Unit:1754

Classifications

IPC:

B01J20/00

Patent Drawings (13 sheets)

Description

TECHNICAL FIELD OF THE INVENTION

[0001] The present invention relates to the application of chemical sorbents for the separation of CO₂from gas mixtures.

BACKGROUND OF THE INVENTION

[0002] As used herein, the term “supersorbent” shall mean a sorbent as taught in U.S. Pat. No. 5,779,464 entitled “Calcium Carbonate Sorbent and Methods of Making and Using Same”, the teachings of which are hereby incorporated by reference.

[0003] As used herein, the term “microporous” shall mean a pore size distribution of less than 5 nanometers. As used herein, the term “mesoporous” shall mean a pore size distribution of from about 5 nanometers to about 20 nanometers.

[0004] Atmospheric CO₂concentration has been increasing steadily since the industrial revolution. It has been widely accepted that the while the CO₂concentration was about 280 ppm before the industrial revolution, it has increased from 315 ppmv in 1959 to 370 ppmv in 2001 [Keeling, C. D. and T. P. Whorf. 2002. Atmospheric CO₂records from sites in the SIO air sampling network. In Trends: A Compendium of Data on Global Change. Carbon Dioxide Information Analysis Center, Oak Ridge National Laboratory, U.S. Department of Energy, Oak Ridge, Tenn., U.S.A. This data is also available from http://cdiac.esd.ornl.gov/ftp/maunaloa-co2/maunaloa.co2]. Rising CO₂concentrations has been reported to account for half of the greenhouse effect that causes global warming [IPCC Working Group I. IPCC Climate Change 1995—The Science of Climate Change: The Second Assessment Report of the Intergovernmental Panel on Climate Change; Houghton, J. T., Meira Filho, L. G., Callander, B. A., Harris, N., Kattenberg, A., Maskell K, Eds.; Cambridge University Press: Cambridge, U.K., 1996]. Although the anthropogenic CO₂emissions are small compared to the amount of CO₂exchanged in the natural cycles, the discrepancy between the long life of CO₂in the atmosphere (50–200 years) and the slow rate of natural CO₂sequestration processes leads to CO₂build up in the atmosphere. The IPCC (Intergovernmental Panel on Climate Change) opines that “the balance of evidence suggests a discernible human influence on the global climate.” Therefore, it is necessary to develop cost effective CO₂management schemes to curb its emission.

[0005] Many of the envisaged CO₂management schemes consist of three parts—separation, transportation and sequestration of CO₂[FETC Carbon Sequestration R&D Program Plan: FY 1999–2000. National Energy Technology Laboratory, Department of Energy, Washington, D.C., 1999]. The cost of separation and compression of CO₂to 110 bar (for transportation of CO₂in liquid state) is estimated at $30–50 per ton CO₂, and transportation and sequestration would cost about $1–3 per ton per 100 km and $1–3 per ton of CO₂, respectively [Wallace, D. Capture and Storage of CO₂. What Needs To Be Done. Presented at the 6th Conference of the Parties, COP 6, to the United Nations Framework Convention on Climate Change; The Hague, The Netherlands, Nov. 13–24, 2000; www.iea.org/envissu/index.htm]. The capture of CO₂imposes severe energy penalties thereby reducing the net electricity output by as much as 13–37% [Herzog, H.; Drake, E.; Adams, E. CO₂Capture, Reuse, and Storage Technologies for Mitigating Global Climate Change. A White Paper; Final Report No. DE-AF22-96PC01257, January 1997]. The dominating costs associated with the current CO₂separation technologies necessitate development of economical alternatives.

[0006] Historically, CO₂separation was motivated by enhanced oil recovery [Kaplan, L. J. Cost-Saving Processes Recovers CO₂from Power-Plant Flue gas. Chem. Eng. 1982, 89 (24), 30–31; Pauley, C. P.; Smiskey, P. L.; Haigh, S. N-ReN Recovers CO₂from Flue Gas Economically. Oil Gas J. 1984, 82(20), 87–92]. Currently, industrial processes such as limestone calcination, synthesis of ammonia and hydrogen production require CO₂separation. Absorption processes employ physical and chemical solvents such as Selexol and Rectisol, MEA and KS-2 [Reimer, P.; Audus, H.; Smith, A. Carbon Dioxide Capture from Power Stations. IEA Greenhouse R&D Programme, www.ieagreen.org.uk, 2001. ISBN 1 898373 15 9; Blauwhoff, P. M. M.; Versteeg, G. F.; van Swaaij, W. P. M. A study on the reaction between CO₂and alkanoamines in aqueous solution. Chem. Eng. Sci. 1984, 39(2), 207–225. Mimura, T.; Simayoshi, H.; Suda, T.; lijima, M.; Mitsuake, S. Development of Energy Saving Technology for Flue Gas Carbon Dioxide Recovery by Chemical Absorption Method and Steam System in Power Plant. Energy Convers. Mgmt. 1997, 38, Suppl. P.S57–S62]. Adsorption systems capture CO₂on a bed of adsorbent materials such as molecular sieves and activated carbon [Kikkinides, E. S.; Yang, R. T.; Cho, S. H. Concentration and Recovery of CO₂from flue gas by pressure swing adsorption. Ind. Eng. Chem. Res. 1993, 32, 2714–2720]. CO₂can also be separated from the other gases by condensing it out at cryogenic temperatures. Polymers, metals such as palladium, and molecular sieves are being evaluated for membrane based separation processes [Reimer, P.; Audus, H.; Smith, A. Carbon Dioxide Capture from Power Stations. IEA Greenhouse R&D Programme, www.ieagreen.org.uk, 2001. ISBN 1 898373 15 9].

[0007] Reaction based processes, as promulgated in this work, can be applied to separate CO₂from gas mixtures. This process is based on a heterogeneous gas-solid non-catalytic carbonation reaction where gaseous CO₂reacts with solid metal oxide (represented by MO) to yield the metal carbonate (MCO₃). The reaction can be represented by:
MO+CO₂→MCO₃ (1)
Once the metal oxide has reached its ultimate conversion, it can be thermally regenerated to the metal oxide and CO₂by the calcination of the metal carbonate product. The calcination reaction can be represented by:
MCO₃→MO+CO₂ (2)
As an example of the above-mentioned scheme, FIG. 1 shows the variation in the free energy of the carbonation reaction as a function of temperature for calcium oxide. From the figure, we can see that the carbonation reaction is thermodynamically favored with a decrease in temperature (Gibbs free energy declines with a decrease in temperature). However, at lower temperatures, the carbonation-reaction is kinetically slow. In fact, it takes geological time scales for the formation of CaCO₃by the reaction between CaO and atmospheric CO₂(at 280–360 ppm) at ambient temperatures. It should also be noted that the carbonation reaction would be favored as long as the free energy is negative. This creates an upper bound of 890° C. for carbonation to occur under a CO₂partial pressure of 1 atm. The equilibrium temperature for this reaction is a function of the partial pressure of CO₂. A reaction based CO₂separation process offers many advantages. Under ideal conditions, MEA captures 60 g CO₂/kg, silica gel adsorbs 13.2 g CO₂/kg and activated carbon adsorbs 88 g CO₂/kg. The sorption capacity of some metal oxides (such as the modified CaO, presented in this study) is about 700 g CO₂/kg of CaO. This is about an order of magnitude higher than the capacity of adsorbents/solvents used in other CO₂separation processes and would significantly reduce the size of the reactors and the material handling associated with CO₂separation.

[0008] Numerous metal oxides exhibit the carbonation and calcination reaction. The calcination temperature of a few metal carbonates (CaCO₃˜750° C., MgCO₃˜385° C., ZnCO₃˜340° C., PbCO₃˜350° C., CuCO₃˜225–290° C. and MnCO₃˜440° C.) makes them viable candidates for this process. Apart from CaO, gas-solid carbonation of other metal oxides has not been widely studied. The carbonation of ZnO to ZnCO₃at 8–13° C. was low when exposed to CO₂and H₂O for over 100 days (Sawada, Y.; Murakami, M.; Nishide, T. Thermal analysis of basic zinc carbonate. Part 1. Carbonation process of zinc oxide powders at 8 and 13° C. Thermochim. Acta. 1996, 273, 95–102.). MnCO₃undergoes a more complex thermal degradation phenomena. MnCO₃first decomposes to MnO₂at 300° C., which in turn changes to Mn₂O₃at 440° C. At higher temperatures (˜900° C.), the final thermal decomposition product was identified as Mn₃O₄(Shaheen, W. M.; Selim, M. M. Effect of thermal treatment on physicochemical properties of pure and mixed manganese carbonate and basic copper carbonate. Thermochim. Acta. 1998, 322(2), 117–128.). Different oxides of manganese provide the flexibility of exploiting the carbonation/calcination reaction over a wider temperature range. Aqueous phase MgO carbonation has been studied for its suitability for mineral-based CO₂sequestration (Fernandez, A. I.; Chimenos, J. M.; Segarra, M.; Fernandez, M. A.; Espiell, F. Kinetic study of carbonation of MgO slurries. Hydrometallurgy. 1999, 53,155–167). The carbonation extent of Mg(OH)₂was about 10% between 387–400° C. and 6% formation between 475–500° C. (Butt, D. P.; Lackner, K. S.; Wendt, C. H.; Conzone, S. D.; Kung, H.; Lu, Y-C.; Bremser, J. K. Kinetics of Thermal Dehydroxylation and Carbonation of Magnesium Hydroxide. J. Am. Ceram. Soc. 1996, 79(7), 1892–1898). They attributed the low conversions to the formation of a non-porous carbonate product layer. This layer hinders the inward diffusion of CO₂and the outward diffusion of H₂O (a product of the carbonation reaction) leading to low conversions. The carbonation of PbO was studied as a part of the chemical heat pump process (Kato, Y.; Saku, D.; Harada, N.; Yoshizawa, Y. Utilization of High Temperature Heat from Nuclear Reactor using Inorganic Chemical Heat Pump. Progress in Nuclear Energy. 1998, 32(3–4), 563–570. & Kato, Y.; Harada, N.; Yoshizawa, Y. Kinetic feasibility of a chemical heat pump for heat utilization from high temperature processes. Applied Thermal Engineering. 1999, 19, 239–254). They reported 30% conversion in an hour under 100% CO₂atmosphere at 300° C. Furthermore, they found the reactivity of PbO to drop with the number of carbonation-calcination cycles.

[0009] Carbonation of calcium oxide has been widely studied. Related applications of the CaO carbonation and calcination include the storage of energy (Barker, R. The Reversibility of the Reaction CaCO₃=CaO+CO₂. J. Appl. Chem. Biotechnol. 1973, 23, 733–742) and the zero emission coal alliance process, consisting of hydrogasification of coal fueled by the heat of the carbonation reaction (Tinkler, M. J.; Cheh, C. Towards a Coal-capable Solid Oxide Fuel Cell System. Proceedings of the 26^thInternational Technical Conference on Coal Utilization and Fuel Systems; Clearwater, Fla., Mar. 5–8, 2001; pp 569–570). The gas-solid CaO—CO₂reaction proceeds through two rate-controlling regimes. The first regime involves a rapid, heterogeneous chemical reaction. In the second regime, the reaction slows down due to the formation of an impervious layer of CaCO₃. This product layer prevents the exposure of unreacted CaO in the particle core to CO₂for further carbonation. The kinetics of the second regime is governed by the diffusion of ions through the CaCO₃product layer. The activation energy was estimated to be 21 kcal/mol below 688 K and 43 kcal/mol above it for the product layer diffusion, based on the counter migration of CO₃²⁻ and O²⁻ ions through the product layer (Bhatia, S. K.; and Perlmutter, D. D. Effect of the product layer on the kinetics of the CO₂-Lime Reaction. AlChE J. 1983, 29(1), 79–86).

[0010] The extent of the carbonation reaction reported in many studies has also shown considerable variation. Stoichiometrically, 56 g of CaO should react with 44 g of CO₂to form 100 g of CaCO₃. This translates to about 78.6-wt % capacity for CaO. However, the structural limitations prevent the attainment of theoretical conversion. The extent of carbonation was only 23-wt % in 30 minutes at 600° C. (Dedman, A. J.; Owen, A. J. Calcium Cyanamide Synthesis, Part 4.—The reaction CaO+CO₂=CaCO₃. Trans. Faraday Soc. 1962, 58, 2027–2035). A higher surface area CaO sorbent provided 55-wt % CO₂sorption (Bhatia, S. K.; and Perlmutter, D. D. Effect of the product layer on the kinetics of the CO₂-Lime Reaction. AlChE J. 1983, 29(1), 79–86). 64-wt % CO₂sorption was achieved at 1050° C. temperature and 11.74 atm CO₂pressure in 32 hours (Mess, D.; Sarofim, A. F.; Longwell, J.P. Product Layer Diffusion during the Reaction of Calcium Oxide with Carbon Dioxide. Energy and Fuels. 1999, 13, 999–1005). However, the extent of carbonation at lower temperature/pressure conditions that are more characteristic of CO₂containing gaseous mixtures is absent in their work. The limitation in total conversion stems essentially from the nature of the initial pore size distribution of the CaO sorbent. Microporous sorbents (pore size <2 nm) are very susceptible to pore blockage and plugging due to the formation of higher molar volume product (molar volume of CaO: 17 cm³/mol; molar volume of CaCO₃: 37 cm³/mol). CaO sorbents obtained from naturally occurring precursors are usually microporous in nature. At the end of the kinetically controlled regime, diffusion processes through the product layer control the reaction rate. Similar structural limitations have prevented calcium-based sorbents from attaining theoretical conversion for the sulfation reaction between CaO and sulfur dioxide (SO₂) as well (Wei, S.-H.; Mahuli, S. K.; Agnihotri, R.; Fan, L.-S. High Surface Area Calcium Carbonate: Pore Structural Properties and Sulfation Characteristics. Ind. Eng. Chem. Res. 1997, 36(6), 2141–2148). They suggested that a mesoporous structure, which maximizes porosity in the 5–20 nm pore size range, would be less susceptible to pore pluggage. This structure would also be able to provide sufficient surface area to ensure rapid kinetics. Their modified precipitation technique resulted in a mesoporous CaCO₃structure that also had a high BET surface area determined by nitrogen (60 m²/g). A similar approach could also enhance the reactivity of CaO sorbents towards the carbonation reaction, which is the focus of this study.

[0011] Lastly, it is important that the CaO sorbents maintain their reactivity over many carbonation and calcination cycles. The conversion of CaO dropped from about 73% in the first carbonation cycle to 43% at the end of the 5^thcycle at 866° C. (Barker, R. The Reversibility of the Reaction CaCO₃=CaO+CO₂. J. Appl. Chem. Biotechnol. 1973, 23, 733–742 & Barker, R. The Reactivity of Calcium Oxide Towards Carbon Dioxide and its use for Energy Storage. J. Appl. Chem. Biotechnol. 1974, 24, 221–227). Barker suggested that the CaCO₃layer is about 22 nm thick and his latter work showed repeated 93% conversion over 30 cycles at 629° C. on 10 nm CaO particles. In another study, cyclical studies conducted at a carbonation temperature of 880° C. and calcination at 860° C. led to a drop in conversion from 70% in the first carbonation to 38% in the 7^thcarbonation step (Kato, Y.; Harada, N.; Yoshizawa, Y. Kinetic feasibility of a chemical heat pump for heat utilization from high temperature processes. Applied Thermal Engineering. 1999, 19, 239–254). The process described here leads to >95% conversion due to the application of novel mesoporous CaO sorbents for CO₂capture and maintains their reactivity over repeated cycles of carbonation and calcination.

SUMMARY OF THE INVENTION

[0012] The present invention includes a calcium oxide, its usage for the separation of CO₂from multicomponent gas mixtures and the optimum process conditions necessary for enhancing the repeatability of the process.

[0013] A preferred method for separating carbon dioxide from a flow of gas comprising carbon dioxide comprises the steps of: (1) directing the flow of gas to a gas-solid contact reactor, the gas-solid contact reactor contains at least one sorbent comprising at least one metal oxide; (2) reacting the carbon dioxide with the at least one sorbent so as to remove the carbon dioxide from said flow of gas, thereby converting the at least one sorbent into spent sorbent; (3) calcining the spent sorbent so as to liberate the carbon dioxide from the spent sorbent, thereby regenerating the sorbent; and (4) repeating the aforementioned steps.

[0014] Although any metal oxide may be employed, it is preferred that the at least one metal oxide is selected from the group consisting of: ZnO, MgO, MnO₂, NiO, CuO, PbO, and CaO. Further, it is preferred that the spent sorbent is a metal carbonate.

[0015] It is preferred that the sorbent has a sorption capacity of at least about 70 grams of carbon dioxide per kilogram of sorbent. However, it is even more preferred that the sorbent has a sorption capacity of at least about 300 grams of carbon dioxide per kilogram of sorbent. Irrespective of the sorption capacity of the sorbent, it is preferred that the sorbent has substantially the same sorption capacity after calcining as the sorbent had prior to adsorbing the carbon dioxide.

[0016] Although any calcination method may be employed, it is preferred that the calcining is performed under at least partial vacuum. It is also preferred that the calcining is performed by steam.

[0017] The present invention includes facilities practicing the aforementioned method.

[0018] A method for separating carbon dioxide from a flow of gas comprising carbon dioxide of the present invention comprises the steps of: (1) directing the flow of gas to a first gas-solid contact reactor, the first gas-solid contact reactor containing at least one sorbent, the sorbent comprising at least one metal oxide; (2) reacting the carbon dioxide in the flow of gas on the sorbent in the first gas-solid contact reactor so as to remove the carbon dioxide from the flow of gas; (3) directing the flow of gas to a second gas-solid contact reactor when the sorbent in the first gas-solid contact reactor is spent thereby forming spent sorbent, the second gas-solid contact reactor containing at least one sorbent, the sorbent comprising at least one metal oxide; (4) reacting the carbon dioxide in the flow of gas on the sorbent in the second gas-solid contact reactor so as to remove the carbon dioxide from the flow of gas; (5) calcining the spent sorbent from the first gas-solid contact reactor so as to generate carbon dioxide and to regenerate the sorbent; (6) directing the flow of gas to the first gas-solid contact reactor when the sorbent in the second gas-solid contact reactor is spent, thereby forming spent sorbent; and (7) calcining the spent sorbent from the second gas-solid contact reactor so as to generate carbon dioxide and to regenerate the sorbent.

[0019] Although any calcination method may be employed, it is preferred that the calcining is performed under at least partial vacuum. It is also preferred that the calcining is performed by steam. This applies to both gas-solid contact reactors.

[0020] Although any metal oxide may be utilized, it is preferred that the at least one metal oxide is selected from the group consisting of: ZnO, MgO, MnO₂, NiO, CuO, PbO, and CaO.

[0021] It is preferred that the sorbent has a sorption capacity of at least about 70 grams of carbon dioxide per kilogram of sorbent. However, it is even more preferred that the sorbent has a sorption capacity of at least about 300 grams of carbon dioxide per kilogram of sorbent. Irrespective of the sorption capacity of the sorbent, it is preferred that the sorbent has substantially the same sorption capacity after calcining as the sorbent had prior to adsorbing the carbon dioxide.

[0022] The present invention also includes facilities practicing the aforementioned method

[0023] A method for regenerating a spent sorbent for carbon dioxide of the present invention comprises the steps of: (1) providing a spent sorbent, the spent sorbent comprising metal carbonate; and (2) calcining the spent sorbent so as to liberate carbon dioxide gas and so as to regenerate the spent sorbent thereby forming a sorbent comprising a metal oxide.

[0024] It is preferred that the spent sorbent is calcium carbonate. It is further preferred that the metal oxide is calcium oxide.

[0025] It is preferred that the sorbent has substantially the same sorption capacity after calcining as the sorbent had prior to adsorbing the carbon dioxide.

[0026] Although any calcination method may be employed, it is preferred that the calcining is performed under at least partial vacuum. It is also preferred that the calcining is performed by steam. This applies to both gas-solid contact reactors.

[0027] The present invention includes facilities practicing the aforementioned method.

[0028] A method for producing a sorbent of the present invention comprises the steps of: (1) obtaining a structurally altered high surface area calcium carbonate having a surface area of at least 25.0 m²/g, a pore volume of at least 0.05 cm³/g, and a mesoporous pore size distribution; and (2) calcining the structurally altered high surface area calcium carbonate so as to produce a sorbent having a surface area of less than 22 m²/g, a pore volume of at least 0.005 cm³/g, and a mesoporous pore size distribution.

[0029] Although any calcination method may be employed, it is preferred that the calcining is performed under at least partial vacuum. It is also preferred that the calcining is performed by steam. This applies to both gas-solid contact reactors.

[0030] The present invention includes sorbents made according to the aforementioned method.

[0031] A sorbent according to the present invention comprising calcium oxide having a surface area of at least 12.0 m²/g and a pore volume of at least 0.015 cm³/g, the calcium carbonate sorbent having sorption capacity of at least about 70 grams of carbon dioxide per kilogram of sorbent.

[0032] In addition to the novel features and advantages mentioned above, other objects and advantages of the present invention will be readily apparent from the following descriptions of the drawing(s) and preferred embodiment(s).

BRIEF DESCRIPTION OF THE DRAWINGS

[0033] FIG. 1 depicts the Gibbs Free Energy diagram for the carbonation reaction as a function of temperature.

[0034] FIG. 2 illustrates the performance of calcium oxide for the carbonation reaction.

[0035] FIG. 3 compares the XRD diffractograms of CaO derived from various precursors.

[0036] FIG. 4 is a schematic diagram of a carbonator reactor for the synthesis of precipitated calcium carbonate.

[0037] FIG. 5 shows the change in the pH of the slurry as, a function of Ca(OH)₂loading. (500 mL water, 0.0575% N40V dispersant, 4 scfh CO₂).

[0038] FIG. 6 depicts the effect of Ca(OH)₂loading on the morphology of Precipitated Calcium Carbonate (PCC) (500 mL water, 0.0575% N40V dispersant, 4 scfh CO₂).

[0039] FIG. 7 compares the pore size distribution of four CaO precursors.

[0040] FIG. 8 compares the conversion of four CaO sorbents under pure CO₂at 650° C.

[0041] FIG. 9 illustrates the effect of temperature on the carbonation of PCC-CaO.

[0042] FIG. 10 illustrates the carbonation-calcination cycles on Aldrich CaCO₃and PCC at 700° C.

[0043] FIG. 11 shows extended carbonation-calcination cycles on precipitated calcium carbonate (PCC) powder at 700° C.

[0044] FIG. 12 compares the effect of initial surface area of PCC-CaO to its reactivity towards the carbonation reaction at 700° C.

[0045] FIG. 13 depicts the effect of vacuum calcination on the reactivity of PCC-CaO towards the carbonation reaction at 700° C.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT(S)

[0046] In accordance with the foregoing summary, the following presents a detailed description of the preferred embodiment(s) of the invention that are currently considered to be the best mode.

Chemicals, Sorbents and Gases

[0047] Naturally occurring limestone (CaCO₃) and hydrated lime (Ca(OH)₂), synthesized from it were obtained from Linwood Mining and Minerals. Dolomite (CaCO₃.MgCO₃) was procured from the National Dolomite Company. The purity of these ores was above 90%. High purity metal oxides such as ZnO, MgO, MnO₂, NiO, CuO, PbO, CaO were obtained from Aldrich Chemical Company. Precipitated calcium carbonate (PCC) was synthesized from Linwood hydrate by the procedure described in a following section. N40V dispersant, a sodium salt of a carboxylic acid, used in the synthesis of PCC was obtained from Allied Colloid. The synthesis procedure is described in detail in a following section. N₂and CO₂used for calcination and carbonation experiments were 99.999% and 99.9% pure, respectively.

Sorbent Reactivity Testing and Structural Analysis

[0048] The reactivity testing of CaO sorbents for carbonation was carried out in a Perkin Elmer Thermogravimetric Analyzer (TGA-7) apparatus. The balance can accurately measure up to 1 microgram. A small sample of the sorbent (5–20 mg) is placed in a quartz boat. The weight of the sample was recorded every second. The structural properties of CaO sorbents and their precursors were tested in a NOVA 2200 analyzer (Quantachrome Company). The BET surface area, pore volume, and pore size distribution were measured at −196° C. using nitrogen as the adsorbent.

Screening of Metal Oxides

[0049] Metal oxides such as ZnO, MgO, CuO, MnO₂, NiO, PbO and CaO that undergo the CCR scheme in the 800–200° C. temperature range were analyzed for their reactivity in a TGA. A powdered sample of these oxides was placed in a quartz pan and pure CO₂was passed over the sample metal oxide. The temperature was then slowly raised and the weight of the sample was continuously monitored. An increase in the weight of the sample is an indication of the formation of metal carbonate. FIG. 2 provides experimental data for the carbonation of lime (Ca(OH)₂) under flowing pure CO₂gas. With an increase in temperature, the weight of the sample increases till the temperature reaches about 890° C. Calcination, which is thermodynamically favored above 890° C. at 1 atm CO₂partial pressure, causes a rapid decrease in weight until the sorbent converts completely to CaO. When the sample is reheated, the weight starts to increase again and the process is repeated once more. Besides proving that CaO is a viable candidate, the data also shows recyclability of the sorbent.

XRD Analysis of CaO Obtained from its Precursors

[0050] CaO was identified as a viable candidate for the carbonation-calcination reactions. However, a variety of precursors can be calcined to obtain the CaO sorbents necessary for the carbonation reaction. Common and economical precursors include calcium carbonate, calcium hydroxide and dolomite. The other important source of CaO is via the calcination of synthesized high surface area precipitated calcium carbonate. In order to compare the crystal structure of the CaO sorbents obtained from these sources, XRD patterns were obtained on all the CaO sorbents. FIG. 3 depicts these diffractograms. From this figure we can conclude that the crystal structure of the CaO sorbents obtained from numerous sources is identical. Only the XRD pattern corresponding to dolomite-derived CaO shows extra peaks due to the presence of MgO in the calcined dolomite. Based on the similarity in all the CaO structures, it can be assumed that any difference in reactivity of CaO for carbonation is an artifact of the sorbent morphology and not due to the chemistry of the gas-solid reaction that occurs on the CaO surface.

Precipitated Calcium Carbonate (PCC) Synthesis

[0051] Structurally altered high surface area CaO precursors were synthesized based on the procedure outlined elsewhere (Fan, L.-S.; Ghosh-Dastidar, A.; Mahuli, S.; Calcium Carbonate Sorbent and Methods of Making the Same. U.S. Pat. No. 5,779,464 and Agnihotri, R.; Chauk, S.; Mahuli, S.; Fan, L.-S. Influence of Surface Modifiers on Structure of Precipitated Calcium Carbonate. Ind. Eng. Chem. Res. 1999, 38, 2283–2291). A schematic diagram of the slurry bubble column used for this purpose is shown in FIG. 4. The carbonator consists of a 2″ OD Pyrex tube. A porous frit at the bottom provides good distribution of CO₂through the slurry. A K-type thermocouple inserted in the slurry continuously records the slurry temperature. A pH probe monitors the pH of the slurry as the reaction medium changes from a basic to an acidic solution as the reaction proceeds. First, 500 ml of distilled water is poured into the carbonator, followed by the addition of 0.0575 g of N40V. 12.8 g of Ca(OH)₂is added to the solution to provide a loading of 2.56% by weight. This corresponds to a concentration of 16-sat (concentration of Ca(OH)₂is 16 times its saturation solubility limit). The solubility of Ca(OH)₂(˜0.16 g/100 g water) leads to a pH of 12 at the start of the experiment. The remaining Ca(OH)₂remains suspended in the solution. The ratio of N40V and Ca(OH)₂loading is chosen to create a surface charge of zero on the incipiently formed CaCO₃particles. The flow of CO₂into the carbonator is then started and the pH was continuously monitored. FIG. 5 shows the change in pH with reaction time as a function of Ca(OH)₂loading. CO₂dissolved in water provides carbonate ions that react with Ca⁺⁺ ions to form CaCO₃according to the reaction below:
Ca²⁺+CO₃²⁻→CaCO₃ (3)
CaCO₃has a much lower solubility in water (˜0.0012 g/100 g water) compared to Ca(OH)₂and thus precipitates out. As the reaction proceeds, Ca²⁺ ions get depleted, but are continuously replenished by the suspended Ca(OH)₂. Hence the pH remains 12. As the reaction proceeds, Ca(OH)₂ultimately gets depleted and the concentration of Ca²⁺ ions cannot be maintained at its solubility limit. On the other hand, continued dissolution of CO₂gas leads to the accumulation of H⁺ ions causing the solution to become acidic. Eventually, the pH settles at about 6.0, corresponding to equilibrium solubility of CO₂in water at ambient temperature. This also signals the end of the carbonation of all Ca(OH)₂. The slurry is then removed from the precipitator, vacuum filtered and stored in a vacuum oven at 90–110° C. for 20 hours to completely remove the moisture. Higher Ca(OH)₂loading requires more reaction time as evident from FIG. 5.

Effect of the Ratio of Ca(OH)2 and Dispersant on PCC Morphology

[0052] Precipitated calcium carbonate can be obtained by the reaction between carbonate and calcium ions in solution. It is known that the CaCO₃nuclei that precipitate out have positive surface charge on them that prevent agglomeration (Agnihotri, R.; Chauk, S.; Mahuli, S.; Fan, L.-S. Influence of Surface Modifiers on Structure of Precipitated Calcium Carbonate. Ind. Eng. Chem. Res. 1999, 38, 2283–2291). The resulting structure is also microporous in nature. However, the structural properties of the synthesized PCC can be altered by the use of negatively charged dispersants that neutralize the surface charges. This makes the ratio between the Ca(OH)₂loading and the dispersant used very critical. Besides, the effect of Ca(OH)₂loading in the slurry was studied to enhance the productivity of the precipitation process by synthesizing more PCC from the same slurry volume. 8-sat, 1.6-sat and 24-sat were used as Ca(OH)₂loading levels, all other factors remaining constant. It can be seen from FIG. 6 and Table 1 that at a concentration of 8-sat, there is proportionally more dispersant in the slurry causing the incipiently formed CaCO₃particles to be negatively charged. The negative charge prevents the agglomeration of these nuclei eventually leading to the formation of microporous PCC as shown in FIG. 6. Its surface area is also relatively lower. At a Ca(OH)₂loading corresponding to 16-sat, the ratio of N40V and CaCO₃is balanced and the surface charge on the nuclei is zero. This allows optimal association of these nuclei leading to a predominantly mesoporous structure. The SA of PCC under these optimum conditions is also the highest at 38.3 m²/g. As the loading of Ca(OH)₂is raised to 24-sat, there is not enough N40V dispersant to neutralize the surface charge on all the incipiently formed nuclei. There could possibly be some positively charged particles. This again creates non-optimum conditions leading to a loss in SA and PV compared to the 16-sat case. Another experiment was conducted to process a 32-sat Ca(OH)₂slurry keeping the Ca(OH)₂to N40V ratio constant. The SA/PV of PCC synthesized from a 32-sat slurry was 37.07 m²/g and 0.139 cm³/g respectively; lending support to the fact that higher mass of PCC can be synthesized from the same amount of slurry.

[0053]

TABLE 1

Morphological properties of PCC as a function of N40V:Ca(OH)₂
loading ratio (500 ml water, 0.0575% N40V dispersant, 4 scfh CO₂).
Ca(OH)₂loading	Surface Area	Pore Volume
weight %	(m²/g)	(cm³/g)

1.28	13.8	0.03
2.56	38.3	0.14
3.84	36.8	0.11

Pore Structure of CaO Sorbents

[0054] CaO sorbents were synthesized by calcining various CaO precursors such as Linwood calcium carbonate (LC), dolomite (DL), Linwood calcium hydroxide (LH), and precipitated calcium carbonate (PCC). For convenience, the oxides derived from these sources are termed as LC-CaO, FCD-CaO (for fully calcined dolomite-CaO), LH-CaO, and PCC-CaO, respectively. The procedure involved heating the precursor in flowing nitrogen beyond the calcination temperature (800–950° C.) for an hour followed by its storage in a desiccator. Structural properties such as surface area (SA) and pore volume (PV) of these chemicals are listed in Table 2 and their pore size distributions are shown in FIG. 7. The SA of naturally occurring minerals, LC and dolomite was very low, 1.06 and 1.82 m²/g, respectively. LH was synthesized by first calcining the LC followed by its hydration. LH exhibited a considerably higher SA (13.19 m²/g) and PV compared to the LC. The SA of PCC (38.3 m²/g), however, was the highest among all precursors. From FIG. 5, we can infer that the structures of LC, DL and LH are predominantly microporous in nature. Most of the porosity lies in pores below 5 nm in diameter. In contrast, the maximum in PV occurs at 15 nm for PCC and most of its PV originates from mesopores in the 5–25 nm range.

[0055]

TABLE 2

Morphological properties (surface area and pore volume)
of various CaO sorbents and their precursors.
		Surface Area	Pore Volume
	Sorbent Name	(m²/g)	(cm³/g)

	LC	1.1	0.003
	LC-CaO	17.8	0.078
	Dolomite	1.8	0.004
	FCD-CaO	29.8	0.08
	LH	13.2	0.0453
	LH-CaO	33.3	0.1
	PCC	38.3	0.11
	PCC-CaO	12.8	0.027

Carbonation of CaO Sorbents

[0056] The performance of these four CaO sorbents was tested in a TGA. The experimental procedure consisted of placing 6–12 mg of the chosen CaO sorbent in a thin layer in a quartz pan to minimize external mass transfer resistances. The sorbent was then heated in flowing nitrogen (5.0 grade, 99.999% pure) to the desired temperature. The representative temperatures used in these experiments were 550° C., 600° C. and 650° C. Once the desired temperature was reached, the flow was switched to 100% CO₂stream. The increase in weight with time was recorded and the conversion of CaO to CaCO₃was calculated from the increase in weight. Only the data obtained at 650° C. is reported here. The performance of the four CaO sorbents, LC-CaO, FCD-CaO, LH-CaO and PCC-CaO at 650° C. is depicted in FIG. 8. Initially, CO₂diffuses into the pores of the LC-CaO and the reaction takes place on the CaO surface provided by the pores. The figure shows that there is a rapid increase in weight in the first 1–2 minutes. The conversion attained in this kinetically controlled regime depends on the initial surface area of the CaO sorbent. LC-CaO and FCD-CaO attained 40–45% conversion, while LH-CaO and PCC-CaO attained about 60% and 54% conversion, respectively, in this regime. After this regime, conversion increases relatively slowly with time. The increase in conversion is only about 2–4% in the next hour for LC-CaO and FCD-CaO. This confirms the susceptibility of micropores to pore filling and pore pluggage described earlier due to the formation of a higher volume product, CaCO₃. The trend is not as dramatic for the case of LH-CaO because of its relatively higher initial surface area. The conversion for LH-CaO increases by another 18% in the diffusion controlled regime. However, the increase in conversion for PCC-CaO is about 34–36% more in the second regime. Since the PCC-CaO structure is mesoporous, the formation of CaCO₃product layer is not able to plug all the pore mouths. This in turn allows the heterogeneous reaction to occur on a larger CaO surface. Once the kinetically controlled regime is over, diffusion of ions occurs through a larger area, ultimately leading to a higher conversion of 88–90% for PCC-CaO. FIG. 9 shows the effect of temperature on the carbonation of PCC-CaO. It can be seen that the extent of conversion in the kinetic regime is different at different temperatures. However, unlike LC-CaO, the conversion at any temperature does not seem to taper off and given sufficient time, PCC-CaO is capable of attaining 90% or higher conversion at all of these temperatures.

Cyclic Calcination and Carbonation

[0057] One of the possible hurdles in the utilization of metal oxides for the carbonation and calcination reaction scheme is its vulnerability to sintering due to the thermal cycling imposed by the cyclical nature of these reactions. Cyclical studies were carried out to quantify any loss in reactivity of these sorbents upon multiple cycles. The temperature chosen for cyclical studies was 700° C. This temperature is sufficient to achieve carbonation in the presence of pure CO₂, and also to calcine the CaCO₃so formed after the gas is switched from CO₂to N₂. A variety of precursors were first calcined in nitrogen at 700° C. The gas was then switched to pure CO₂and the weight gain continuously tracked. After reaching the ultimate conversion, the gas was switched back to N₂. This process was repeated for 2–3 cycles. The data obtained on Aldrich CaCO₃and PCC undergoing this cyclical study is shown in FIG. 10. It can be seen that the reactivity of Aldrich CaCO₃exhibited a gradual decrease even after the first cycle. In contrast, PCC completely regained its mass after the first calcination and carbonation cycle. At 700° C., we can deduce that the conversion is almost complete (>95%). The figure also shows that the reactivity did not decrease in the second cycle either. Under the reaction conditions chosen, any sintering did not seem to adversely affect the sorbent morphology. We continued an extended study of eleven calcination and carbonation cycles lasting over three days on PCC. The data is provided in FIG. 11. It can be seen that the sorbent reactivity remained high and if enough reaction time is provided, the conversion could reach beyond 90% in every cycle. This is a positive result for the structural viability of this sorbent under multiple cycles.

Effect of Vacuum Calcination

[0058] The effect of initial surface area of CaO sorbents was studied. CaO sorbents were synthesized from PCC under different calcination conditions. The role of surface area on the extent of carbonation is shown in FIG. 12. Different surface area PCC-CaO sorbents were synthesized by the calcination of PCC at a range of calcination temperature to induce varying degrees of sintering. It can be seen that a higher initial surface area (and its associated pore volume) leads to higher reactivity and conversion. Thus, it is necessary to identify calcination conditions that optimize the SA/PV and pore size distribution of PCC-CaO. It has been suggested in literature that CaO procured from the calcination of limestone under vacuum has a higher reactivity. It was observed that under air calcination at 650–800° C., sharp edges of calcite powder were replaced by rounded surfaces and neck areas indicating severe sintering (Beruto, D., and Searcy, A. W., “Calcium oxides of high reactivity.” Nature, 1976, 263, 221–222). The resulting CaO structure was highly crystalline as well. In contrast, the sharp edges of calcite were retained in the CaO obtained under vacuum. The CaO however did not possess a high degree of crystallinity. The latter also showed high reactivity towards hydration. Vacuum calcination leads to the formation of a metastable-nanocrystalline calcia structure while calcination in helium atmosphere lead to a stable microcrystalline calcia structure (Dash, S., Kamruddin, M., Ajikumar, P. K., Tyagi, A. K., and Raj, B., “Nanocrystalline and metastable phase formation in vacuum thermal decomposition of calcium carbonate.” Thermochimica acta, 2000, 363,129–135). Beruto et al., [1980] estimated the surface area and pore volume of limestone based CaO to be about 78–89 m²/g and 0.269 ml/g respectively.

[0059] The effect of vacuum calcination was studied in this process. The surface area of Linwood carbonate increased from 17.79 to 21.93 m²/g and pore volume from 0.07815 to 0.1117 ml/g for calcination under nitrogen and under vacuum, respectively. Similar enhancements were observed for PCC based CaO sorbents as well. It has been observed that PCC-CaO is susceptible to high degree of sintering and the surface area of the sorbent falls off rapidly. Calcination in nitrogen resulted in surface areas below 13 m²/g repeatedly. However, vacuum calcination lead to a surface area of 19.84 m²/g and 0.04089 ml/g pore volume. The carbonation characteristics are shown in FIG. 13.

[0060] Vacuum calcination of PCC followed by the carbonation of PCC-CaO was repeated over two cycles. PCC was first vacuum calcined to CaO-1 at 750° C. CaO-1 was carbonated to CC-2 at 700° C. followed by its vacuum decomposition to CaO-2 that is carbonated to CC-3. The values of surface area and pore volume of the sorbent at various stages are provided in Table 3 below:

[0061]

TABLE 3

Structural properties of Calcium based sorbents undergoing vacuum
calcination at 750° C. and carbonation at 700° C.
	Surface Area	Pore Volume
	(m²/g)	(cc/g)

	PCC	38.3	0.1416
	CaO-1	12.63	0.02409
	CC-2	6.5	0.0103
	CaO-2	15.93	0.04008
	CC-3	2.361	0.004483

[0062] The data shows that PCC is susceptible to sintering because the CaO obtained in the first cycle has a surface area of only 12.63 m²/g compared to 38.3 m2/g of PCC. As expected, pore filling leads to a drop in both properties when CaO 1 carbonates. The extent of carbonation was beyond 90%. However, it can be seen that the SA of CaO obtained after the second vacuum calcination step, CaO 2, is 15.93 m²/g, which is higher than the SA of CaO 1. The pore volume of CaO 2 is also higher than that of CaO 1. These results prove that there is no systematic decline in SA and PV of sorbents with increasing calcination-carbonation cycles and that this combination is capable of providing a sustained conversion over many cycles.

[0063] The article “Carbonation-Calcination Cycle Using High Reactivity Calcium Oxide for Carbon Dioxide Separation from Flue Gas” by Himanshu Gupta and Liang-S. Fan, published on the web Jul. 11, 2002 by Ind. Eng. Chem. Res. 2002, 41, 4035–4042 is hereby incorporated in its entirety by reference.

[0064] While the invention has been described in connection with what is presently considered to be the most practical and preferred embodiments, it is to be understood that the invention is not to be limited to the disclosed embodiment(s), but on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims, which are incorporated herein by reference.

Claims

What is claimed is:

1. A method for producing a sorbent, said method comprising the steps of:

obtaining a structurally altered high surface area calcium carbonate having a surface area of at least 25.0 m²/g, a pore volume of at least 0.05 cm³/g, and a mesoporous pore size distribution; and

calcining said structurally altered high surface area calcium carbonate so as to produce a sorbent having a surface area of less than 22 m²/g, a pore volume of at least 0.005 cm³/g, and a mesoporous pore size distribution.

2. The method according to claim 1 wherein said calcining is conducted under at least partial vacuum.

3. The method according to claim 1 wherein said calcining is conducted by steam.

Patent Citations (9)

Patent	Date	Inventor	Cited By
US4226839(A)	1980-10-01	O'Neill et al.	Examiner
US4533532(A)	1985-08-01	Gebhard et al.	Applicant
US4729889(A)	1988-03-01	Flytani-Stephanopoulos et al.	Applicant
US4950409(A)	1990-08-01	Stanforth	Applicant
US5084256(A)	1992-01-01	McElroy et al.	Examiner
US5087597(A)	1992-02-01	Leal et al.	Examiner
US5160715(A)	1992-11-01	Pinnavaia et al.	Applicant
US5275739(A)	1994-01-01	Grant et al.	Applicant
US5779464(A)	1998-07-01	Fan et al.	Applicant

Non-Patent Literature (35)

Herzog et al., CO2 Capture, Reuse, and Storage Technologies for Mitigating Global Climate Change, A White Paper Final Report, Energy Laboratory, Jan., 1997, pp. 1-66.Applicant
Barker, The Reactivity of Calcium Oxide Towards Carbon Dioxide and its Use for Energy Storage, J. Appl. Chem. Biotechnol. 1974, 24, 221-227.Applicant
Dedman et al., Calcium Cyanamide Synthesis, Explosives Research and Development Establishment, Ministry of Aviation, Mar., 1962, pp. 2027-2035.Applicant
Mess et al., Product Layer Diffusion During the Reaction of Calcium Oxide With Carbon Dioxide, Energy & Fuels 1999, 13, 999-1005.Applicant
Wei, et al., High Surface Area Calcium Carbonate: Pore Structurual Properties and Sulfation Characteristics, Ind. Eng. Chem. Res., 1997, 36, 2141-2148.Applicant
Agnihotri et al., Influence of Surface Modifiers on the Structure of Precipitated Calcium Carbonate, Ind. Eng. Chem. Res. 1999, 38, 2283-2291.Applicant
Bhatia et al., Effect of the Product Layer on the Kinetics of the CO2-Lime Reaction,AIChE Journal, vol. 29, No. 1, Jan. 1983, 79-86.Applicant
Barker, The Reversibility of the Reaction CaCO3 ←→ CaCO+CO2, J. Appl. Chem. Biotechnol. 1973, 23, 733-742.Applicant
Kato et al., Kinetic Feasibility of a Chemical Heat Pump for Heat Utilization of High-Temperature Processes, Applied Thermal Engineering 19, 1999, 239-254.Applicant
Butt et al., Kinetics of Thermal Dehydroxylation and Carbonation of Magnesium Hydroxide, J. Am. Ceram. Soc., vol. 79, No. 7, 1996, 1892-1898.Applicant
Kato et al., Utilization of High Temperature Heat From Nuclear Reactor Using Inorganic Chemical Heat Pump, Progress in Nuclear Energy, vol. 32, No. 3 / 4, 1998, 563-570.Applicant
Fernandez et al., Kinetic Study of Carbonation of MgO Slurries, Hydrometallurgy 53, 1999, 155-167.Applicant
Shaheen et al., Effects of Thermal Treatment on Physiocochemical Properties of Pure and Mixed Manganese Carbonate and Basic Copper Carbonate, Thermochimica Acta 322, 1998, 117-128.Applicant
Mimura et al., Development of Energy Saving Technology for Flue Gas Carbon Dioxide Recovery in Power Plant by Chemical Absorption Method and Steam System, Energy Convers. Mgmt., vol. 38, Suppl., 1997, S57-S62.Applicant
Sawada et al., Thermal Analysis of Basic Zinc Carbonate, Part 1. Carbonation Process of Zinc Oxide Powders at 8 and 13° C., Thermochimica Acta 273, 1996, 95-102.Applicant
Kikkinides et al., Concentration and Recovery of CO2 From Flue Gas by Pressure Swing Adsorption, Ind. Eng. Chem. Res. 1993, 32, 2714-2720.Applicant
Blauwhoff et al., A Study on the Reaction Between CO2 and Alkanolamines in Aqueous Solutions, Chemical Engineering Science, vol. 39, No. 2, 1984, 207-225.Applicant
Pauley et al., N-ReN Recovers CO2 From Flue Gas Economically, Technology Oil and Gas Journal, 1984, 87-92.Applicant
Kaplan, Cost-Saving Process Recovers CO2 From Power-Plant Fluegas, Chemical Engineering, 1982, 30-31.Applicant
Tinkler et al., Towards a Coal-Capable Solid Oxide Fuel Cell System, Proceedings of the 26th International Technical Conference on Coal Utilization and Fuel Systems; Clearwater, Florida, Mar. 5-8, 2001; pp. 569-570.Applicant
Gupta et al., Carbonation-Calcination Cycle Using High Reactivity Calcium Oxide for Carbon Dioxide Separation From Flue Gas, Ind. Eng. Chem. Res. 2002, 41, 4035-4042.Applicant
Keeling, C.D., Atmospheric CO2 concentrations (ppmv) derived from in situ air samples collected at Mauna Loa Observatory, Hawaii, http://cdiac.esd.ornl.gov/ftp/maunaloa-co2/maunaloa.co2, Jul. 25, 2003, 2 pp.Applicant
Milne et al., High-Temperature, Short-Time Sulfation of Calcium-Based Sorbents, Ind. Eng. Chem. Res., vol. 29, No. 11, pp. 2201-2214 (1990).Applicant
Borgwardt, Sintering of Nascent Calcium Oxide, Chemical Engineering Science, vol. 44, No. 1, pp. 53, 60 (1989).Applicant
Bortz and Flament, Recent IFRF Fundamental and Pilot Scale Studies on the Direct Sorbent Injection Process, International Flame Research Foundation, pp. 17-1-17-22 (1985).Applicant
Kirchgessner, D. A., & Jozewicz, W., Enhancement of Reactivity in Surfactant-Modified Sorbents for Sulfurdioxide Control, Ind. Eng. Chem. Res., 28(4), pp. 413-418 (1989).Applicant
Raghunathan et al. Raghunathan K., A. Ghosh-Dastidar, and L.-S. Fan, A Technique for the Study of Ultrafast Gas-Solid Reactions for Residence Times less than 100 ms, Rev. Sci. Instrum., 63(11), 5469 (1992).Applicant
Ghosh-Dastidar, et al. Ghosh-Dastidar, A., Mahuli, S., Agnihotri, R., and Fan, L.-S., Ultrafast Calcination and Sintering of Ca(OH)2 powder: Experimental & Modeling, Chem. Eng. Sci., vol. 50, No. 13, pp. 2029-2040, (1995).Applicant
Kirchgessner, Lorrain, Lignosulfonate-Modified Calcium Hydroxide for Sulfur Dioxide Control,m Ind. Eng. Chem. Res., 1987, 26, pp. 2397-2400.Applicant
B.K. Gullett, K.R. Bruce, Pore Distribution Changes of Calcium-Based Sorbents Reacting with Sulfur Dioxide, AIChE Journal, Oct. 1987, vol. 33, No. 10, pp. 1719-1726.Applicant
K.R. Bruce, B.K. Gullet, L.O. Beach, Comparative SO2 Reactivity of CaO Drived from CaCO3 and Ca(OH)2. AIChE Journal, Jan. 1989, vol. 35, No. 1, pp. 37-41.Applicant
Ghosh-Dastidar, S. Mahuli, R. Agnitiotri and L.-S. Fan, Selenium Capture Using Sorbent Powders: Mechanisms of Sorption by Hydrated Lime. Sep. 11, 1995.Applicant
S.W. Wei et al. High Surface Area Calcium Carbonate: Pore Structural Properties and Sulfation Characteristics, Ind. Eng. Chem. Res., 1997, vol. 36, No. 6, pp. 2141-2148.Applicant
Suhas K. Mahuli, et al., Pore-Structure Optimization of Calcium Carbonate for Enhanced Sulfation, 1997, 13 pp.Applicant
Gupta, H., NOx Reduction by Carbonaceous Materials and CO2 Separation Using Regenerative Metal Oxides From Fossil Fuel Based Flue Gas, Dissertation, The Ohio State University, cataloged Oct. 1, 2001, 75 pages.Applicant

Abstract