US 6,893,896 B1Grant
Method for making multilayer thin-film electronics
Issue Date:2005-05-17
•51 Claims
•2 Drawing Sheets
Abstract
Multilayer thin-film electronics are manufactured at high speed, even while the various component functions are manufactured separately under conditions tailored to optimize component performance and yield. Each function or group of functions is fabricated on a separate flexible substrate. These flexible substrates are bonded to each other using adhesive films that are anisotropic electrical conductors or optical light guides. The bonding is performed by laminating the flexible substrates to each other in a continuous process, using the anisotropic conductor as the bonding layer.
Metadata
Assignee
- The Trustees of Princeton University
Inventor
- Sigurd Wagner
Application Information
Application Number:US 09/647,193
Filing Date:1999-03-26
Priority Date:1998-03-27
Art Unit:2823
Patent Drawings (2 sheets)
Description
Related Applications
[0001] The present application is a U.S. National Phase Application under 35 U.S.C. § 371 of PCT Application No. PCT/US99/06453 filed Mar. 26, 1999, and the claims the benefit of U.S. Provisional Application Ser. No. 60/079,746 filed Mar. 27, 1998, the entire disclosures of which are both expressly incorporated herein by reference.
Statement of Government Rights
[0002] The present invention has been made under a grant of DARPA, federal grant no. F33615-94-1-1464. Accordingly, the government may have certain rights to the present invention.
Background of the Invention
[0003] 1. Field of the Invention
[0004] This invention relates to large-area electronics and to methods for manufacturing thin film electronics continuously on separate carrier substrate foils, and then to combining these foils using anisotropic electrical conductors or light guides.
[0005] 2. Related Art
[0006] In the field of thin film electronics where two or more layers of active circuits are employed, many technologies exist for connection of separate planes of passive circuits. One of these technologies is multilevel metallization on top of integrated silicon circuits, for which several levels of metal lines are built up by alternating between the fabrication of metal patterns, the deposition of insulators, the opening of vertical connections, followed by the fabrication of the next level of metal pattern, etc. Another of these technologies is multilevel printed wire boards (PWBs), for which passive metal connections are deposited on epoxy-based or ceramic boards that are fabricated with openings to make vertical connections. Individual boards are bonded to each other to form multilevel PWBs by bonding techniques that depend on the material of the board. These techniques are used industrially.
[0007] However, there are drawbacks associated with these existing techniques.
Objects and Summary of the Invention
[0008] It is an object of this invention to provide a method of manufacturing macroelectronic circuits.
[0009] It is a further object of this invention to provide a method of manufacturing macroelectronic circuits which results in low cost and high yield.
[0010] It is yet another object of this invention to provide a method for manufacturing electronic circuits in a continuous process.
[0011] It is still a further object of the invention to provide a method of manufacturing electronic circuits where thin film electronics are manufactured continuously on separate carrier substrate foils.
[0012] It is another object of the invention to provide a method of combining the separately manufactured foils.
[0013] It is a still further object of the invention to combine separately manufactured foils using adhesives and anisotropic electrical conductors or light guides.
[0014] The present invention maintains high-speed manufacturing while the various component functions are manufactured separately under conditions tailored to optimize component performance and yield. The method involves the production of each function or group of functions on a separate flexible substrate, and bonding these flexible substrates to each other by using anisotropic electrically conducting or optical lightguide adhesives. The bonding is performed by laminating the flexible substrates to each other via the adhesive in a continuous process. Anisotropic conductors conduct in one direction (i.e. top to bottom) but do not conduct sideways.
Brief Description of the Figures
[0015] FIG. 1 is a schematic drawing of a pixel for a display of organic light emitting diodes driven by an active matrix of thin film transistors made on a steel back plane.
[0016] FIG. 2 is a diagram of a co-laminated thin film transistor using anisotropic electrically conducting adhesive.
Detailed Description of the Invention
[0017] Many electronic products combine several electronic and/or optical functions. An active-matrix liquid-crystal display is an example of such a product. It consists of a light source, a plane of transistor electronics, a layer of liquid crystal sandwiched between transparent conductors and polarizers, and a plane of color filters. Typically, such products are made by separately manufacturing the individual components, such as the light source, the transistor back plane, and the color filter plane, followed by assembly and filling of the liquid crystal material. The separate manufacture allows the individual optimization of the performance of each component. Often, separate manufacture is necessary to obtain the desired functionality. For example, the transistor back plane of a liquid crystal display could not be manufactured after assembly, because assembly renders the required substrate surface inaccessible. However, it is well known that integration of several functions on one substrate leads to savings in cost, improvement of yield, and increased functionality.
[0018] The need for combining several electronic functions at low cost with high yield becomes paramount in the field of macroelectronics, also called large-area electronics or giant electronics. Macroelectronic products are expected to have very low cost per unit area, rather than per function as is the case for conventional microelectronics. This requirement is apparent for typical examples of future macroelectronic products, such as disposable, intelligent shipping/shopping labels, digital wallpaper, and dial-your-pattern dresses. These products may include transistor electronics, input/output devices such as antennae, optoelectronic functions including photodetectors and light-emitting diodes, and microelectromechanical devices.
[0019] To keep costs low and achieve high yield, the manufacture of macroelectronic products must combine high-speed production of these functions with their integration at high yield. High-speed production can be achieved by the printing of macroelectronics on flexible substrates. The substrate will spool off a roll, run through equipment that is configured like a multi-color printing press, and then will be coiled up or cut into product. The diversity of macroelectronic component functions (transistors, LEDs, photodetectors, etc.) requires diverse materials and manufacturing processes. Superposing these materials and processes in a fully integrated sequence reduces yield because the temperature and chemicals required for producing a given function may damage a function that was introduced earlier in a lower layer of the multi layer structure.
[0020] The present invention maintains high-speed manufacturing while the various component functions are manufactured separately under conditions tailored to optimize component performance and yield. The basic concept is to produce each function or group of functions on a separate flexible substrate, and to bond these flexible substrates to each other by using anisotropic electrically conducting or optical lightguide adhesives. The bonding is performed by laminating the flexible substrates to each other via the adhesive in a continuous process.
[0021] FIG. 1 shows a pixel for a display of organic light emitting diodes driven by an active matrix of thin film transistors made on a steel back plane. In such devices, thin film transistors must make good electrical contact to the OLEDs to provide sufficient drive current. This is an active matrix emissive display which consists of a back plane of thin film transistors that drive organic light emitting diodes. Such a pixel is shown in the paper by Wu, et al. Integration of Organic LEDs and Amorphous TFTs onto Unbreakable Metal Foil Substrates, published in the Tech. Digest Internat. Electron Devices Meeting, San Francisco, Calif., December 8011, 1996, IEEE, Piscataway, N.J. 1996, Paper 308.1, pp. 957-959.
[0022] The display shown in FIG. 1 is manufactured in a sequence of steps that adds the TFT and OLED layers to one substrate. A substrate foil, for example, stainless steel, has patterned TFT circuits added first. The OLED circuits are then placed on the substrate. Optionally, a plastic substrate could be provided, and active electronics can be formed thereon. A transparent encapsulation layer (not shown) is then applied. The top contact to the OLED layer must be transparent to transmit the light, which is emitted from the organic semicondutor. In this structure this contact is made in one of the last processing steps. It was found experimentally that this transparent contact to the OLED functions best when made first, i.e., when the OLED is made on top of it (“Organic LEDs integrated with a-Si TFTs on lightweight metal substrates”, C.C. Wu, et al, Society of Information Display, Internat. Symp. Digest, Vol. XXVIII, SID, Santa Ana, Calif. 1997, pp. 66-70). However, making the OLEDs first on a transparent substrate, followed by making the TFTs on top of the OLEDs is not possible, because the typical TFT process temperature of 200° to 350° C. will destroy the OLED, which must not be heated much above room temperature.
[0023] The present invention addresses this problem by making the TFT back plane and the OLEDs separately, and connecting them electrically with an anisotropic conductor, which conducts only in the direction perpendicular to the layers. This sequence of steps is illustrated in FIG. 2. More particularly, the OLED's 6 are formed on a transparent conductor 4 which is, in turn formed onto a transparent substrate/encapsulation 2. The back plane comprises thin film transistors (TFTs) formed onto structural substrate 10. When the substrate 10 is conducted as is the case for metal foils, an insulated barrier layer 12 must be deposited between the TFT layer and the substrate. The front plane OLED's and the back plane TFT's are connected together with an anistropic conductive adhesive 8. The resultant structure is the finished thin film display.
[0024] Nothing is changed in TFT manufacture as compared to the sequence described above. However, the OLEDs are made on a transparent conductor, which in turn is deposited on a transparent substrate. In this way, the best possible electrical contact to the OLEDs is made, and the transparent substrate ultimately serves as the transparent encapsulant. The other electrical contact to the OLEDs may be opaque and is made of a suitable metal. The two planes, TFT and OLED, are then laminated to each other, using an adhesive foil of anisotropic conductor (for example, ARclad® 8257 from Adhesives Research, Inc., a 1-mil thick acrylic product). The final assembly step therefore is the co-lamination of TFT foil, anisotropic conductor foil, and OLED foil.
[0025] It is important to note that the proper TFT-OLED connections are made automatically by this procedure, as long as the TFT and OLED planes are aligned with each other.
[0026] The same principle can be used to co-laminate component planes with anisotropic light guides, if optical interconnects are desired. The lamination step may be repeated to combine more than two active planes in one product.
[0027] Having a body of easily deformable adhesive also provides another advantage in production yield and product lift. The anisotropic conductor will accommodate mechanical strain between the circuit planes that it connects. If a rigid connection were used, any strain developing during fabrication or in produce use will be accommodated by the layer with the lowest elastic modulus. This may be an active layer, for example, the organic light-emitter. Straining this layer may destroy the OLED. Straining the adhesive layer will only lead to local shifts in the contact alignment, which will be self-correcting due to the anisotropic conduction or light guiding.
[0028] Anisotropic conductors are used today to make connections between groups of passive conductors on to different planes. One well-known application is the surface-mount of integrated driver circuits to the row and column conductors of liquid crystal displays. The use of a sheet of an anisotropically conducting adhesive for the direct connection of two active circuit planes is new. The problem solved here is coming into being only now, as macroelectronic integrated circuits are developed.
[0029] While several advantageous embodiments have been chosen to illustrate the invention, it will be understood by those skilled in the art that various changes and modifications can be made therein without departing from the scope of the invention as defined in the appended claims.
[0030] Having thus described the invention in detail, it is to be understood that the foregoing description is not intended to limit the spirit and scope thereof. What is desired to be protected by Letters Patent is set forth in the appended claims.
Claims
1. A process for manufacturing macroelectronics comprising the steps of:
producing thin film active electronics on separate carrier substrates;
positioning the thin film active electronics in facing relation; and
combining said substrates using anisotropic electrical conductors or light guides so that the thin film active electronics are encapsulated by the anisotropic electrical conductors or the light guides.
2. The process of claim 1 wherein one of said substrates is a flexible foil.
3. The process of claim 1 wherein one of said substrates is a rigid plate.
4. The process of claim 2 wherein the material for one of said substrates is plastic.
5. The process of claim 3 wherein the material for one of said substrates is plastic.
6. The process of claim 2 wherein the material for one of said substrates is glass.
7. The process of claim 3 wherein the material for one of said substrates is glass.
8. The process of claim 2 wherein the material for one of said substrates is metal.
9. The process of claim 3 wherein the material for one of said substrates is metal.
10. The process of claim 1 wherein the thin film active electronics are produced continuously on separate carrier substrates.
11. The process of claim 4 wherein organic light emitting diodes are formed on the plastic substrate.
12. The process of claim 5 wherein organic light emitting diodes are formed on the plastic substrate.
13. The process of claim 6 wherein organic light emitting diodes are formed on the glass substrate.
14. The process of claim 7 wherein organic light emitting diodes are formed on the glass substrate.
15. The process of claim 6 wherein thin film transistors are formed on the glass substrate.
16. The process of claim 7 wherein thin film transistors are formed on the glass substrate.
17. A process of making electronic circuits comprising the steps of:
forming at least two active circuits on separate carrier substrates;
positioning the at least two active circuits in facing relation; and
connecting said active circuits with a material which conducts in a direction perpendicular to the separate carrier substrates, wherein the at least two active circuits are encapsulated by the material.
18. A method of manufacturing an electronic display comprising the steps of:
depositing a transparent conductor on a transparent substrate;
forming a thin film organic light emitting diode circuit on said transparent conductor;
forming a thin film transistor circuit on a second transparent substrate;
positioning the organic light emitting diode and thin film transistor circuits in facing relating; and
laminating said circuits to each other.
19. The method of claim 18 wherein said laminating step uses an adhesive anisotropic conductor.
20. The method of claim 19 wherein the conductor is an electrical or optical conductor.
21. The method of claim 19 wherein the bonding layer is the conductor.
22. A method of manufacturing an electronic circuit comprising the steps of:
forming a first active circuit on a first plane;
forming a second active circuit on a second plane;
positioning the first and second active circuits in facing relation; and
co-laminating said first and second planes with an anisotropic conductor, wherein the anisotropic conductor encapsulates the first and second circuits.
23. The process of claim 4, wherein the thin film active electronics comprise thin film transistors.
24. The process of claim 8, wherein the metal comprises steel.
25. The process of claim 24, wherein the thin film active electronics comprise organic light emitting diodes.
26. A process for manufacturing macroelectronics comprising the steps of:
producing thin film active electronics on separate carrier substrates;
positioning the active electronics of the carrier substrates in facing relation with respect to each other; and
combining said substrates using anisotropic electrical conductors or light guides, the anisotropic electrical conductors or light guides encapsulating the active electronics.
27. The process of claim 26, wherein one of said substrates is a flexible foil.
28. The process of claim 26, wherein one of said substrates is a rigid plate.
29. The process of claim 27, wherein the material for one of said substrates is plastic.
30. The process of claim 28, wherein the material for one of said substrates is plastic.
31. The process of claim 27, wherein the material for one of said substrates is glass.
32. The process of claim 28, wherein the material for one of said substrates is glass.
33. The process of claim 27, wherein the material for one of said substrates is metal.
34. The process of claim 28, wherein the material for one of said substrates is metal.
35. The process of claim 26, wherein the thin film active electronics are produced continuously on separate carrier substrates.
36. The process of claim 29, wherein organic light emitting diodes are formed on the plastic substrate.
37. The process of claim 30, wherein organic light emitting diodes are formed on the plastic substrate.
38. The process of claim 29, wherein organic light emitting diodes are formed on the glass substrate.
39. The process of claim 30, wherein organic light emitting diodes are formed on the glass substrate.
40. The process of claim 29, wherein thin film transistors are formed on the glass substrate.
41. The process of claim 30, wherein thin film transistors are formed on the glass substrate.
42. The process of claim 1, wherein at least one of the substrates is flexible.
43. The process of claim 1, wherein both of the substrates are flexible.
44. The process of claim 17, wherein at least one of the substrates is flexible.
45. The process of claim 17, wherein both of the substrates are flexible.
46. The process of claim 18, wherein at least one of the substrates is flexible.
47. The process of claim 18, wherein both of the substrates are flexible.
48. The process of claim 22, wherein at least one of the planes is flexible.
49. The process of claim 22, wherein both of the substrates are flexible.
50. The process of claim 26, wherein at least one of the substrates is flexible.
51. The process of claim 26, wherein both of the substrates are flexible.
Patent Citations (19)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US4796975(A) | 1989-01-01 | Lukas et al. | Applicant |
| US4810637(A) | 1989-03-01 | Szydlo et al. | Applicant |
| US5049527(A) | 1991-09-01 | Merrick et al. | Applicant |
| US5249245(A) | 1993-09-01 | Lebby et al. | Applicant |
| US5302456(A) | 1994-04-01 | Matsui | Examiner |
| US5409798(A) | 1995-04-01 | Kondo et al. | Examiner |
| US5471552(A) | 1995-11-01 | Wuu et al. | Applicant |
| US5496743(A) | 1996-03-01 | Luryi | Applicant |
| US5698452(A) | 1997-12-01 | Goosen | Applicant |
| US5699073(A) | 1997-12-01 | Lebby et al. | Applicant |
| US5944537(A) | 1999-08-01 | Smith et al. | Examiner |
| US6020220(A) | 2000-02-01 | Gilleo et al. | Examiner |
| US6025857(A) | 2000-02-01 | Obata et al. | Examiner |
| US6060332(A) | 2000-05-01 | Martin | Examiner |
| US6063647(A) | 2000-05-01 | Chen et al. | Examiner |
| US6121070(A) | 2000-09-01 | Akram | Examiner |
| US6137162(A) | 2000-10-01 | Park et al. | Examiner |
| US6380597(B1) | 2002-04-01 | Gudesen et al. | Examiner |
| JP10335830(A) | 1998-12-01 | Examiner |
Non-Patent Literature (8)
- Gleskova, et al., “Photoresist-Free Fabrication Process for a:Si:H TFTs,” 17th International Conference Amorphous and Microcryst, Semiconductors, Budapest, Aug. 25-29,1997.Applicant
- Hong, et al., “Direct Writing and Lift-Off Patterning of Copper Lines at 200C Maximum Process Temperature,” Materials Research Society Symposium Proceedings, vol. 471, pp. 35-40 (1997).Applicant
- Ma, et al., “Organic Light-Emitting Diode/Thin Film Transistor Integration for Foldable Displays,” pp. L-78-L-81, 1997.Applicant
- Ma, et al., “Thin Film Transistors for Foldable Displays,” IEEE, 1997.Applicant
- Theiss, et al. “Flexible, Lightweight Steel-Foil Substrates for a-Si:H Thin-Film Transistors,” Mat. Res. Soc. Symp. Proc. vol. 471, pp. 21-27, 1997.Applicant
- Wu, et al., “Integration of Organic LED's and Amorphous Si TFT's onto Flexible and Lightweight Metal Foil Substrates,” IEEE Electron Device Letters, vol. 18, No. 12, pp. 609-612, Dec. 1997.Applicant
- Wu, et al., “Integration of Organic LED's and Amorphous Si TFT's onto Unbreakable Metal Foil Substrates,” IEDM 96, pp. 957-959.Applicant
- Wu, et al., “Organic LEDs Integrated with a-Si TFTs on Lightweight Metal Substrates,” SID 97 Digest, pp. 67-70, 1997.Applicant