US 6,858,547 B2Grant

System and method for forming a gate dielectric

Issue Date:2005-02-22

•31 Claims

•8 Drawing Sheets

Abstract

A method of forming a dielectric stack on a pre-treated surface. The method comprises pre-cleaning a semiconductor wafer to remove native oxide, such as by applying hydroflouric acid to form an HF-last surface, pre-treating the HF-last surface with ozonated deionized water, forming a dielectric stack on the pre-treated surface and providing a flow of NH₃in a process zone surrounding the wafer. Alternately, the method includes pre-treating the HF-last surface with NH₃, forming the stack after the pre-treating, and providing a flow of N₂in a process zone surrounding the wafer after the forming. The method also includes pre-treating the HF-last surface using an in-situ steam generation process, forming the stack on the pre-treated surface, and annealing the wafer after the forming. The pre-treating includes providing an inert gas flow in a process zone surrounding the HF-last surface, reacting hydrogen with an oxidizer in the process zone for a very short duration, and providing an inert gas flew in the process zone after the reacting.

Metadata

Assignee

Applied Materials, Inc.

Inventors

Craig R. Metzner
Shreyas S. Kher
Shixue Han

Application Information

Application Number:US 10/256,563

Filing Date:2002-09-27

Priority Date:2002-06-14

Art Unit:2823

Patent Drawings (8 sheets)

Description

Background of the Invention

[00002] This application claims priority from U.S. Provisional Application Ser. No. 60/388,928 filed Jun. 14, 2002 entitled, “System And Method For Forming A Gate Dielectric”. The foregoing patent application, which is assigned to the assignee of the present application, is incorporated herein by reference in its entirety.

Field of the Invention

[00003] The present invention relates generally to forming gate dielectric in field effect transistors, and particularly to forming metal oxide/metal silicate gate dielectric films using chemical vapor deposition.

Description of the Related Art

[00004] The present invention is especially useful in forming complementary metal oxide semiconductor (CMOS) integrated-circuit devices and will be described in that context. Other applications will also be mentioned. CMOS technology has enabled the microeletronic industry to simultaneously meet several technological requirements to fuel market expansion. This has been accomplished largely by a calculated reduction (scaling) of the dimensions of the field-effect transistor (FET). FIG. 1 illustrates portions of a cross sectional view of a field effect transistor (FET) pair in a typical complimentary metal oxide semiconductor (CMOS) device. Device 100 comprises a silicon wafer 155 doped with a p-type material, a p-type epitaxial silicon layer 165 on wafer 155, a p-type well region 120 and an n-type well region 150 defined in epitaxial layer 165, an n-type transistor (NMOS FET) 110 defined in p-well 120 and a p-type transistor (PMOS FET) 140 defined in n-well 150. Region 180 electrically isolates NMOS 110 and PMOS 140 transistors and region 160 electrically isolates the pair of transistors 110 and 140 from other semiconductor devices on substrate 155.

[00005] NMOS transistor 110 comprises a gate region 122, a source region 114 and a drain region 116. The source and drain regions are n-type regions on opposite sides of gate region 122. Channel region 118 is interposed between source region 114 and drain region 116. A gate dielectric layer 112 separates channel region 118 and gate region 122. Gate dielectric 112 electrically insulates gate region 122 from channel region 118. The gate region comprises a conductor material, typically doped polycrystalline silicon (polysilicon) or amorphous silicon. The dopant may be an n-type dopant such as a phosphorus or a p-type dopant such as boron. When an appropriate voltage is applied between p-type silicon wafer 155 and gate region 122, electrons from p-well 120 move into region 118 directly below dielectric 112 thereby creating an n-type channel 118. A voltage applied between source 114 and drain 116 causes current to flow between source 114 and drain 116.

[00006] PMOS transistor 140 comprises a gate region 152, a source region 144 and a drain region 146. The source and drain regions are p-type regions on opposite sides of gate region 152. Channel region 148 is interposed between source region 144 and drain region 146. A gate dielectric 142 separates channel region 148 and gate region 152. Dielectric 142 electrically insulates gate region 152 from channel region 148. The gate region comprises a conductor material typically doped polysilicon or amorphous silicon. Again, the dopant may be an n-type or p-type material. When an appropriate voltage is applied between p-type silicon wafer 155 and gate region 152, holes from n-well 150 move into region 148 directly below dielectric layer 142 thereby creating a p-type channel 148. A voltage applied between source 144 and drain 146 causes current to flow between source 144 and drain 146.

[00007] With the rapid shrinking of the transistor feature size, the gate dielectric thickness has also decreased. For several decades, silicon dioxide has been the material of choice for the gate dielectric layer. Silicon dioxide offers a stable high-quality Si—SiO₂interface and superior electrical isolation properties.

[00008] However, as the dimensions of the transistor continue to decrease, the continued use of silicon dioxide as a dielectric gate material is problematic. The fundamental problem is the need to keep the capacitance of the gate high while the area of the gate is shrinking faster than the thickness of the gate dielectric. The capacitance C of the gate is given by C=kE₀A/d where A is the area of the gate, d is the thickness of the dielectric layer, k is the dielectric constant, and E₀is the permittivity of free space. In order to ensure higher gate oxide capacitance, the silicon dioxide layer thickness proportionately has been decreased to less than 2 nanometers as the area of the gate has been decreasing. However, future generations will likely require a further reduction to below 1.0 nanometer. The primary issue is that as thickness decreases, leakage current increases. This leakage in current is due primarily to the ability of the electrons to go through the thinner SiO₂dielectric layer. In an example, current density for a 1.5 nanometer thick SiO₂layer at 1 V is 1 A/cm²; however, as the SiO₂thickness decreases to 1 nanometer, the leakage-current density approaches 100 A/cm²at the same operating voltage.

[00009] Consequently, there is a need for an alternative gate dielectric material that can be used in a large enough physical thickness to reduce current leakage density and still provide a high gate capacitance. In order to achieve this, the alternative gate dielectric material must have a dielectric constant that is higher than that of silicon dioxide. Typically, the thickness of such an alternative dielectric material layer is expressed in terms of the equivalent oxide thickness (EOT). Thus, the equivalent oxide thickness (EOT) of an alternative dielectric layer in a particular capacitor is the thickness that the alternative dielectric layer would have if its dielectric constant were that of silicon dioxide.

[00010] Another consideration in selecting an alternative dielectric material is the mobility of charge carries in the transistor channel. The material selected for the dielectric film affects the mobility of the carriers in the transistor channel, thereby affecting overall transistor performance. It is desirable to find an alternative dielectric material for which the mobility of carriers in the transistor channel is equivalent to or higher than that for silicon dioxide gate dielectric films. For future generation transistors, a peak mobility of 400 cm²/Vs or greater is desirable.

Summary of the Invention

[00011] The present invention comprises forming a metal oxide, metal silicate, or combination metal oxide-metal silicate dielectric stack on a semiconductor wafer.

[00012] In one embodiment, the method comprises pre-treating the semiconductor wafer, e.g., to remove oxide, with hydrofluoric acid to form an HF-last surface and then pre-treating the HF-last surface with ozonated water for a specified time period. After pre-treating, a dielectric stack is formed on the pre-treated surface using a chemical vapor deposition process. A flow of NH₃is then provided in a process zone surrounding the semiconductor wafer. In one embodiment, after providing the NH₃flow, a polycrystalline or amorphous silicon gate is formed over the dielectric stack using a LPCVD process.

[00013] In another embodiment, the method of forming a dielectric stack on a semiconductor wafer comprises pre-treating the semiconductor wafer with hydrofluoric acid to form an HF-last surface, pre-treating the HF-last surface with NH₃, forming the dielectric stack on the pre-treated surface, and providing a flow of N₂in a process zone surrounding the semiconductor wafer after forming the dielectric stack.

[00014] In yet another embodiment, the method of forming a dielectric stack on a semiconductor wafer comprises pre-treating the semiconductor wafer with hydrofluoric acid to form an HF-last surface, pre-treating the HF-last surface using an in-situ steam generation process, forming the dielectric stack on the pre-treated surface, and annealing the semiconductor wafer after forming the dielectric stack. The in-situ steam generation process comprises providing an inert gas flow in a process zone surrounding the HF-last surface, reacting hydrogen with an oxidizer in the process zone surrounding the HF-last surface for a very short duration, and providing an inert gas flow in the process zone after the reacting step. Preferably, the dielectric stack comprises layers of hafnium oxide, hafnium silicate layers, or a combination thereof formed using a MOCVD process.

Brief Description of the Drawings

[00015] So that the manner in which the above recited features of the present invention, and other features contemplated and claimed herein, are attained and can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to the embodiments which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of this invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.

[00016] Additional objects and features of the invention will be more readily apparent from the following detailed description and appended claims when taken in conjunction with the drawings, in which:

[00017] FIG. 1 illustrates portions of a cross sectional view of field effect transistor (FET) pair in a typical complimentary metal oxide semiconductor (CMOS) device.

[00018] FIG. 2 illustrates a cross-sectional view of a portion of a transistor having a dielectric stack.

[00019] FIG. 3 illustrates the processing steps used to form a hafnium oxide and hafnium silicate gate dielectric stack.

[00020] FIG. 4 illustrates the general chemical structure for the hafnium oxide precursors of the form Hf(NRR′)₄.

[00021] FIG. 5 illustrates the chemical structure of the TDEAH precursor.

[00022] FIG. 6 illustrates the general chemical structure for precursors of the form SiR₁R₂R₃R₄.

[00023] FIG. 7 illustrates the chemical structure of the TDMAS precursor.

[00024] FIG. 8 illustrates the processing steps used to form a hafnium oxide and hafnium silicate gate dielectric stack.

[00025] FIG. 9 illustrates the processing steps that may be used for forming the dielectric stack using a flash in-situ steam generation (ISSG) pre-treatment process.

Detailed Description of the Preferred Embodiment

[00026] FIG. 2 illustrates a cross-sectional view of a portion of a field effect (FET) 200 transistor having a dielectric stack in accordance with an embodiment of the invention. FET 200 comprises a source 250, a drain 240, a gate 210, a dielectric stack 260 and a channel 270 interposed between source 250 and drain 240. Preferably, the transistor is formed on a silicon wafer and the gate is made of polycrystalline or amorphous silicon. In a PMOS FET, source 250 and drain 240 comprise a p-type silicon and in an NMOS FET, source 250 and drain 240 comprise an n-type silicon.

[00027] In one embodiment, dielectric stack 260 comprises at least two layers, where each layer comprises either a metal oxide layer or a metal silicate layer. In the embodiment shown, there is a metal oxide layer 230 and a metal silicate layer 220. The stack is formed using any metal that is capable of forming a high-k layer, e.g. HfO₂, ZrO₂. A high-k layer comprises a dielectric material having a dielectric constant greater than 4. Preferably, metal oxide layer 230 and metal silicate layer 220 comprise any metal that can form amino precursors. More preferably, metal oxide layer 230 comprises hafnium oxide and the metal silicate layer 220 comprises hafnium silicate. In one embodiment, the hafnium oxide layer thickness is about 3 nanometers and the hafnium silicate layer thickness is about 1 nanometer. Such a dielectric stack has an EOT of about 1.12 nanometers. In another embodiment, the hafnium oxide layer thickness is about 4 nanometers and hafnium silicate layer thickness is about 1.5 nanometers. Such a dielectric stack has an EOT of about 1.61 nanometers. An EOT of 1.61 nanometers provides the desired peak mobility of 400 cm²/Vs. In yet another embodiment, the dielectric stack thickness is selected to provide both the desired capacitance corresponding to 1.12 nanometers EOT and the desired peak mobility of 400 cm²/Vs.

Example 1

[00028] FIG. 3 illustrates the processing steps used in accordance with the invention to form a hafnium oxide, hafnium silicate, or combination thereof gate dielectric stack having an EOT of about 1.12 nanometers. At step 310, an HF-last surface is formed on a semiconductor wafer by introducing a dilute hydrofluoric acid solution onto the wafer surface for a specified time period. In one embodiment, the wafer is immersed in a hydrofluoric acid bath for a time period of about 2 minutes to about 15 minutes. More preferably, the wafer is immersed in a 2% hydrofluoric acid bath for about 2 minutes.

[00029] Next, the wafer is placed in a thermal chamber for pre-treating at 1 to 100 torr. A step 320, NH₃is introduced onto the HF-last surface for a specified time period and at a specified temperature. Step 320 adds a nitride “coating” or “layer” that aids in preventing the dopant of the gate layer (210 in FIG. 2) from diffusing into the channel (270 in FIG. 2). Preferably, the specified time period is in the range of about 5 seconds to about 120 seconds and the specified temperature is in the range of about 400° C. to about 1100° C. More preferably, the specified time period is about 30 seconds and the specified temperature is about 600° C. at 30 torr.

[00030] The wafer is then transported from the thermal chamber to a deposition chamber. A hafnium oxide or hafnium silicate layer is then formed at step 330 using deposition processes such as MOCVD, LPCVD, PECVD, VPE, ALD or PVD. Preferably, the hafnium oxide or hafnium silicate layer is formed using a MOCVD process.

[00031] If a hafnium oxide layer is preferred, O₂, N₂and a hafnium oxide precursor are introduced onto the wafer surface. The hafnium oxide precursor is any precursor of the alkylamido or alkylamino ligand group. In one embodiment, the hafnium oxide precursor is selected from a group comprising amino or amido precursors of the form Hf(NRR′)₄where

- [00032] R═H, CH₃, C₂H₅, C₃H₇, CO, NCO, alkyl, and aryl and
- [00033] R′═H, CH₃, C₂H₅, C₃H₇, CO, NCO, alkyl, and aryl.
  FIG. 4 illustrates the general chemical structure for the hafnium oxide precursors of the form Hf(NRR′)₄. Preferably, the hafnium oxide precursor is TetrakisDiEthylAmidoHafnium (TDEAH). FIG. 5 illustrates the chemical structure of the TDEAH precursor.

[00035] TDEAH is flowed onto the wafer surface at a rate in the range of about 1 mg/min to about 50 mg/min. Preferably, TDEAH is flowed onto the wafer surface at a rate of about 7 mg/min. O₂is flowed onto the wafer surface at a rate in the range of about 30 sccm to about 3000 sccm. Preferably, O₂is flowed onto the wafer surface at a rate of about 1000 sccm. N₂is flowed onto the wafer surface at a rate in the range of about 30 sccm to about 3000 sccm. Preferably, N₂is flowed onto the wafer surface at a rate of about 1500 sccm. O₂, N₂and TDEAH are introduced onto the wafer surface either simultaneously or sequentially or a combination thereof.

[00036] The hafnium oxide layer is formed at temperatures in the range of about 225° C. to about 700° C. Preferably, the hafnium oxide layer is formed at about 485° C. The pressure in the deposition chamber is in the range of about 1.5 torr to about 8 torr. Preferably, the pressure is about 4 torr. The hafnium oxide layer formed has a thickness in the range of about 5 Å to about 50 Å. Preferably, the hafnium oxide layer formed has a thickness of about 30 Å.

[00037] In one embodiment, the wafer is transported to a second chamber after forming the hafnium oxide layer in a first chamber. The process conditions of the first chamber are then adjusted for forming the hafnium silicate layer. The wafer is then transported back to the first chamber for forming the second layer. Alternatively, the wafer can remain in the same chamber for sequential deposition of the second layer. The choice of whether to use single- or multiple-chamber deposition depends on a number of factors including the deposition process chosen for each layer (e.g., MOCVD for one layer and ALD for another or MOCVD for both layers), the capabilities or limitations of the system (transfer speed between chambers, temperature ramping capabilities), whether the wafers are being processed in a development or production environment, and/or whether an anneal process is performed between the deposition of the two dielectric layers.

[00038] Alternatively, the hafnium silicate layer may be formed at step 330 using deposition processes such as MOCVD, LPCVD, PECVD, VPE, ALD or PVD. Preferably, the hafnium silicate layer is formed using a MOCVD process, where O₂, N₂, and hafnium silicate precursors are introduced onto the wafer surface and the process temperature is about 480° C. to about 600° C. and the pressure is adjusted to about 4 torr.

[00039] The hafnium silicate precursors are precursors of the alkylamido or alkylamino ligand group. The hafnium silicate precursors are selected from precursors of the form Hf(NRR′)₄and SiR₁R₂R₃R₄where

- [00040] R═H, CH₃, C₂H₅, C₃H₇, CO, NCO, alkyl, and aryl;
- [00041] R′═H, CH₃, C₂H₅, C₃H₇, CO NCO, alkyl, and aryl;
- [00042] R₁═H, NH₂, N(CH₃)₂, N(C₂H₅), N(C₃H₇), NCO, alkoxy, amino, alkyl and aryl;
- [00043] R₂═H, NH₂, N(CH₃)₂, N(C₂H₅), N(C₃H₇), NCO, alkoxy, amino, alkyl and aryl;
- [00044] R₃═H, NH₂, N(CH₃)₂, N(C₂H₅), N(C₃H₇), NCO, alkoxy, amino, alkyl and aryl; and
- [00045] R₄═H, NH₂, N(CH₃)₂, N(C₂H₅), N(C₃H₇), NCO, alkoxy, amino, alkyl and aryl.
  The general chemical structure for the precursors of the form Hf(NRR′)₄is shown in FIG. 4. FIG. 6 illustrates the general chemical structure for precursors of the form SiR₁R₂R₃R₄. Preferably, the hafnium silicate precursors are TetrakisDiEthylAmidoHafnium (TDEAH) and TetrakisDiMethylAmidoSilicon (TDMAS). FIG. 7 illustrates the chemical structure of the TDMAS precursor. The chemical structure for the TDEAH precursor is shown in FIG. 5.

[00047] TDEAH is flowed onto the wafer surface at a rate in the range of about 1 mg/min to about 50 mg/min. Preferably, TDEAH is flowed onto the wafer surface at a rate of about 6 mg/min. TDMAS is flowed onto the wafer surface at a rate of about 1 mg/min to about 50 mg/min. Preferably, TDMAS is flowed at a rate of 50 mg/min. O₂is flowed onto the wafer surface at a rate of about 30 sccm to about 1000 sccm, preferably about 1000 sccm, and N₂is flowed onto the wafer surface at a rate of about 30 sccm to about 3000 sccm, preferably about 1500 sccm. O₂, N₂, TDEAH and TDMAS are introduced onto the wafer surface either simultaneously or sequentially or a combination thereof.

[00048] The hafnium silicate layer is formed at temperatures in the range of about 325° C. to about 700° C. and pressure is in the range of about 1.5 torr to about 8 torr. Preferably, the hafnium silicate layer is formed at about 600° C. at a pressure of about 4 torr. The hafnium silicate layer thickness is about 5-20 Å, preferably 10 Å. The SiO₂concentration of the hafnium silicate layer is from about 5 mol % to about 80 mol %. More preferably, the SiO₂concentration is about 10 mol %.

[00049] Thus, either a hafnium oxide or hafnium silicate layer can be formed at steps 330 and 340. Should, for example, hafnium oxide be used to form both layers, it is preferred that the hafnium oxide layers have differing compositions or stoichiometries, for example, a first layer comprised of HfO₂and a second layer comprised of Hf₂O₃. Similarly, should both layers be comprised of hafnium silicate, it is preferable that the hafnium silicate layers have differing compositions and/or stoichiometries.

[00050] After forming the hafnium silicate layer or hafnium oxide layer at step 340, the wafer is transported back to the thermal chamber for further processing at 1 to 100 torr. At step 350, N₂is introduced onto the wafer surface for a specified time period and at a specified temperature. Preferably, the specified time period is in the range of about 5 seconds to about 60 seconds at temperatures in the range of about 400° C. to about 1100° C. More preferably, N₂is introduced onto the wafer surface for about 60 seconds at a temperature of about 800° C. at 10 torr.

[00051] In one embodiment, a gate electrode is next formed at step 360 on the hafnium oxide or hafnium silicate layer. The gate electrode layer may be made of polycrystalline or amorphous silicon and is formed using a chemical vapor deposition process such as MOCVD, LPCVD, PECVD, VPE, ALD or PVD. In one embodiment, the gate electrode is formed using an LPCVD process where silane or disilane is flowed onto the wafer at temperatures in the range of about 400° C. to about 900° C. Preferably, the gate electrode is formed at a temperature of about 570° C.

[00052] In some embodiments, a nitride layer may be formed on the hafnium oxide or hafnium silicate layer before formation of the polysilicon gate (i.e., to form a layer between the hafnium silicate layer 220 and the polysilicon gate 210, see FIG. 2). This embodiment is illustrated at step 850 of FIG. 8. Alternatively, for example, a nitride layer may be formed between the channel 270 and the hafnium oxide layer 220. This embodiment is shown at step 320 of FIG. 3. The nitride layer prevents dopant diffusion from the gate electrode into the silicon channel. In such embodiments, the polysilicon gate electrode 210 is implanted with dopants such as boron and phosphorus; and the structure is then annealed at ˜1000° C. for activation and distribution of the dopant in the polysilicon layer. It is undesirable for dopant to diffuse from the gate electrode layer 210 into the silicon channel 270. In small doses, such diffusion can affect threshold voltages, and in larger doses such diffusion can increase leakage currents. Either case drastically affects transistor performance.

Example 2

[00053] FIG. 8 illustrates the processing steps used in accordance with the invention to form a hafnium oxide and hafnium silicate gate dielectric stack having a peak mobility of about 400 cm²/Vs. At step 810, an HF-last surface is formed on a semiconductor wafer by introducing a dilute hydrofluoric acid solution onto the wafer surface for a specified time period. In one embodiment, the wafer is immersed in a hydrofluoric acid bath for a time period of about 1 minute to about 15 minutes. More preferably, the wafer is immersed in a 2% hydrofluoric acid bath for about 2 minutes.

[00054] Next, at step 820, the HF-last surface is exposed to ozonated water by, for example, immersing the wafer in an ozonated water bath. Preferably, the ozone concentration in the ozonated water is in the range of about 10 ppm to about 30 ppm. Preferably, the ozone concentration in the water is about 20 ppm. Preferably, the HF-last surface is exposed to the ozonated water for about 5 minutes to about 15 minutes. More preferably, the HF-last surface is exposed to the ozonated water for about 10 minutes.

[00055] The wafer is next placed in a deposition chamber. A hafnium oxide layer is then formed at step 830 using deposition processes such as MOCVD, LPCVD, PECVD, VPE, ALD or PVD. Preferably, the hafnium oxide layer is formed using a MOCVD process.

[00056] O₂, N₂and a hafnium oxide precursor are introduced onto the wafer surface. The hafnium oxide precursor is any precursor of the alkylamido or alkylamino ligand group. In one embodiment, the hafnium oxide precursor is selected from a group comprising amino or amido precursors of the form Hf(NRR′)₄where

- [00057] R═H, CH₃, C₂H₅, C₃H₇, CO, NCO, alkyl, and aryl and
- [00058] R′═H, CH₃, C₂H₅, C₃H₇, CO, NCO, alkyl, and aryl.
  FIG. 4 illustrates the general chemical structure for the hafnium oxide precursors of the form Hf(NRR′)₄. Preferably, the hafnium oxide precursor is TetrakisDiEthylAmidoHafnium (TDEAH). FIG. 5 illustrates the chemical structure of the TDEAH precursor.

[00060] TDEAH is flowed onto the wafer surface at a rate of about 1 mg/min to about 50 mg/min, preferably about 7 mg/min, O₂is flowed onto the wafer surface from about 30 sccm to about 3000 sccm, preferably 30 sccm, and N₂is flowed onto the wafer surface at a rate of about 30 sccm to about 3000 sccm, preferably about 1500 sccm. O₂, N₂and TDEAH are introduced onto the wafer surface either simultaneously or sequentially or a combination thereof.

[00061] The hafnium oxide layer is formed at temperatures in the range of about 225° C. to about 700° C., preferably, at about 485° C. The pressure in the deposition chamber is in the range of about 3 torr to about 8 torr, preferably about 4 torr. Preferably, the hafnium oxide layer formed has a thickness of about 2-5 nanometers, and preferably about 4 nanometers.

[00062] After forming the hafnium oxide layer, the wafer is transported from the deposition chamber another chamber. For example, the chamber may be an anneal chamber, a cooldown chamber or a loadlock chamber. Preferably, an anneal step is performed between deposition of the hafnium oxide layer and the hafnium silicate layer. Once the wafer is transferred, the temperature and pressure in the first deposition chamber are adjusted for forming the hafnium silicate layer. For an MOCVD process, the temperature is adjusted to about 600° C. and the pressure is adjusted to about 4 torr. The wafer is then transported from the cooldown chamber to the deposition chamber. A hafnium silicate layer is then formed at step 840 using deposition processes such as MOCVD, LPCVD, PECVD, VPE, ALD or PVD. In another embodiment, the wafer is not transported to another chamber after forming the hafnium oxide layer, but the wafer remains in the deposition chamber while the process conditions of the deposition chamber are adjusted for forming the hafnium silicate layer. In this case, ramping the temperature from the processing temperature of the hafnium oxide processing conditions to the temperature of the hafnium silicate processing conditions provides an anneal-like environment and a separate anneal step may be eliminated.

[00063] Preferably, the hafnium silicate layer is formed using a MOCVD process. O₂, N₂, and hafnium silicate precursors are introduced onto the wafer surface. The hafnium silicate precursors are precursors of the alkylamido or alkylamino ligand group. The hafnium silicate precursors are selected from precursors of the form Hf(NRR′)₄and SiR₁R₂R₃R₄where

- [00064] R═H, CH₃, C₂H₅, C₃H₇, CO, NCO, alkyl, and aryl;
- [00065] R═H, CH₃, C₂H₅, C₃H₇, CO NCO, alkyl, and aryl;
- [00066] R₁═H, NH₂, N(CH₃)₂, N(C₂H₅), N(C₃H₇), NCO, alkoxy, amino, alkyl and aryl;
- [00067] R₂═H, NH₂, N(CH₃)₂, N(C₂H₅), N(C₃H₇), NCO, alkoxy, amino, alkyl and aryl;
- [00068] R₃═H, NH₂, N(CH₃)₂, N(C₂H₅), N(C₃H₇), NCO, alkoxy, amino, alkyl and aryl; and
- [00069] R₄═H, NH₂, N(CH₃)₂, N(C₂H₅), N(C₃H₇), NCO, alkoxy, amino, alkyl and aryl.
  The general chemical structure for the precursors of the form Hf(NRR′)₄is shown in FIG. 4. FIG. 6 illustrates the general chemical structure for precursors of the form SiR₁R₂R₃R₄. Preferably, the hafnium silicate precursors are TetrakisDiEthylAmidoHafnium (TDEAH) and TetrakisDiMethylAmidoSilicon (TDMAS). FIG. 7 illustrates the chemical structure of the TDMAS precursor. The chemical structure for the TDEAH precursor is shown in FIG. 5.

[00071] TDEAH is flowed onto the wafer surface at a rate of about 1 mg/min to about 50 mg/min, preferably about 6 mg/min, TDMAS is flowed onto the wafer surface at a rate of about 1 mg/min to about 50 mg/min, preferably about 10 mg/min, O₂is flowed onto the wafer surface at a rate of about 30 sccm to about 3000 sccm, preferably about 1000 sccm, and N₂is flowed onto the wafer surface at a rate of about 30 sccm to about 3000 sccm, preferably about 1500 sccm. O₂, N₂, TDEAH and TDMAS are introduced onto the wafer surface either simultaneously or sequentially or a combination thereof.

[00072] The hafnium silicate layer is formed at temperatures in the range of about 325° C. to about 700° C. and at pressure in the range of about 3 torr to about 8 torr. Preferably, the hafnium silicate layer is formed at about 600° C. at a pressure of about 4 torr. The hafnium silicate layer thickness is from 5 to 20 Å, preferably about 1.5 nanometers. The SiO₂concentration of the layer is about 5-80 mol %, preferably about 45 mol % to about 50 mol %. More preferably, the SiO₂concentration is about 50 mol %.

[00073] After forming the hafnium silicate layer, the wafer is transported from the deposition chamber to the thermal chamber for further processing. At step 850 NH₃is then introduced onto the wafer surface at 1 to 100 torr for a specified time period and a specified temperature. Preferably, the specified time period is in the range of about 5 seconds to about 60 seconds. More preferably, the specified time period is about 60 seconds. Preferably, the specified temperature is in the range of about 400° C. to about 1100° C. More preferably, the specified temperature is about 700° C. at 30 torr.

[00074] In one embodiment, a polycrystalline-Si or amorphous-Si gate electrode is next formed at step 860 on the hafnium silicate layer. The gate electrode layer is formed using a chemical vapor deposition process such as MOCVD, LPCVD, PECVD, VPE, ALD or PVD. In one embodiment, the gate electrode is formed using an LPCVD process where silane or disilane is flowed onto the wafer at temperatures in the range of about 400° C. to about 900° C. Preferably, the gate electrode is formed at a temperature of about 550° C. As described supra, to avoid undesired dopant diffusion from the gate electrode into the silicon channel, the wafer may be treated with NH₃(step 850 of FIG. 8) after deposition of the dielectric layer 220 and before deposition of the polysilicon gate 210 (layers shown in FIG. 3). Such a treatement forms a nitride coating or layer that prevents dopant diffusion. Alternately, a nitride layer may be formed between the dielectric layer 230 and the silicon channel 270 by treating the wafer with NH₃(FIG. 3, step 330) after formation of the Hf-last.

[00075] As described previously, as an alternative to forming first a hafnium oxide layer then forming a hafnium silicate layer, two hafnium oxide layers may be used or two hafnium silicate layers may be used, or first a hafnium silicate layer followed by a hafnium oxide layer may be used. Optionally, a third layer may be formed over the second layer as just described, Such a third layer would comprise hafnium silicate.

[heading-00076] Gate Formation Using a Flash In-Situ Steam Generation (ISSG) Process

[00077] In the flash in-situ steam generation (ISSG) process in accordance with the invention, the reactants, hydrogen and an oxidizer, are introduced onto an HF-last wafer surface for a very short duration to form hydroxyl groups and water vapor in the thermal chamber The hydroxyl groups then bond to the HF-last surface, thereby enhancing high-k nucleation. In accordance with the invention, the growth of interfacial SiO₂between the silicon channel and the hafnium oxide layer is minimized due to a very short flash in-situ steam generation process and by introducing inert gases before and after the flash ISSG process.

[00078] FIG. 9 illustrates the processing steps that may be used in accordance with the invention for forming the dielectric stack using a flash in-situ steam generation (ISSG) pre-treatment process. At step 910, an HF-last surface is formed on a semiconductor wafer by introducing a dilute hydrofluoric acid solution onto the wafer surface for a specified time period. In one embodiment, the wafer is immersed in a hydroflouric acid bath for a time period of about 1 minute to about 15 minutes. More preferably, the wafer is immersed in a 2% hydroflouric acid bath for about 2 minutes.

[00079] After the HF-last processing, the wafer is placed in a thermal chamber. The HF-last surface is then pre-treated using a flash ISSG process. First, at step 920, an inert gas such as helium or nitrogen is introduced into the chamber for a specified time period. Then, at step 930, the reactants, hydrogen and an oxidizer such as O₂or N₂O, are introduced into the chamber for a very short duration. The flow of reactants is then stopped at step 940 while the inert gas continues to flow onto the wafer surface at step 950. Table 1 provides some illustrative temperatures, flow rates and reactant flow times for a flash ISSG process.

[00002]

	TABLE I

	Temp.		Oxidizer		Reactamt
	(° C.)	H₂(sccm)	(sccm)	He (sccm)	Flow Time(s)


Example 1	750	8	2980 (O₂₎	2980	6
Example 2	750	15	2980 (N₂O)	2980	6
Example 3	750	15	2980 (O₂)	2980	6
Example 4	800	5	1000 (O₂)	0	3
Example 5	800	5	1000 (N₂O)	0	3

[00080] After the pre-treating, the wafer is transported to a deposition chamber. A metal oxide and a metal silicate layer are then formed on the pre-treated surface. Preferably, any metal that forms amino precursors, including alkoxides or halides, may be used to form the metal oxide and metal silicate layers. In one embodiment, hafnium oxide and hafnium silicate layers are formed at steps 960 and 970 using the processes described earlier in reference to FIGS. 3 and 8. Table 2 provides illustrative parameters for forming the hafnium oxide and hafnium silicate layers.

[00002]

	TABLE 2

	Hf	Si	O₂	N₂	Temp.	Pressure
	(mg/min)	(mg/min)	(sccm)	(sccm)	(° C.)	(Torr)


Example 6	7	0	1000	1500	485	4
Example 7	6	50	1750	750	425	3
Example 8	6	50	1750	750	525	5.5
Example 9	6	50	1750	750	575	8

[00081] After forming the metal oxide and metal silicate layers, the wafer is transported from the deposition chamber to the thermal chamber for post-deposition processing. In one embodiment, the post-deposition processing comprises the post-treatment processes described earlier in reference to FIGS. 3 and 8. In another embodiment, the post-deposition processing comprises annealing the wafer surface at step 980 in a thermal or plasma environment using H₂, O₂, N₂O, NO, NH₃, O₃, N₂, He or a combination thereof.

[00082] In one embodiment, a polycrystalline-Si or amorphous-Si gate electrode is next formed at step 990 after post-deposition processing. The gate electrode layer is formed using a deposition process such as MOCVD, LPCVD, PECVD, VPE, ALD or PVD. In one embodiment, the gate electrode is formed using an LPCVD process where silane or disilane is flowed onto the wafer at temperatures in the range of about 400° to about 900°. Preferably, the gate electrode is formed at a temperature of about 550° C. To avoid undesired dopant diffusion, a nitride layer may be formed between the dielectric layer 220 and the polysilicon gate 210 prior to formation of the polysilicon gate. Alternately, a nitride layer may be formed between the dielectric layer 230 and the silicon channel 260.

[00083] Various modifications may occur to those skilled in the art without departing from the true spirit and scope of the invention as defined by the appended claims. For example, although the specific embodiments are described using a hafnium oxide and hafnium silicate dielectric gate stack, those skilled in the art will appreciate that the dielectric stack may be formed using any metal that is capable of forming films with the desired capacitance and mobility. Additionally, although the specific embodiments use metal oxide and metal silicate films, other film compositions that provide the desired capacitance and mobility may also be used to form the dielectric stack.

[00084] While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.

Claims

1. A method of forming a dielectric stack on a wafer comprising:

treating the wafer with hydrofluoric acid to form an HF-last surface;

pre-treating the HF-last surface with ozonated deionized water for a specified time period to form a pre-treated surface;

forming the dielectric stack on the pre-treated surface, wherein the dielectric stack comprises a hafnium oxide layer or a hafnium silicate layer; and

providing a flow of NH₃in a process zone surrounding the wafer after forming the dielectric stack.

2. A method of forming a dielectric stack on a wafer comprising:

treating the wafer with hydrofluoric acid to form an HF-last surface;

pre-treating the HF-last surface with ozonated deionized water for a specified time period to form a pre-treated surface;

forming the dielectric stack on the pre-treated surface; and

providing a flow of NH₃in a process zone surrounding the wafer after forming the dielectric stack, wherein forming the dielectric stack comprises:

forming a first layer of hafnium oxide or hafnium silicate on the pre-treated surface, and

forming a second layer of hafnium oxide or hafnium silicate on the first layer.

3. The method of claim 2 wherein forming the dielectric stack further comprises an annealing step between the forming steps.

4. The method of claim 2, wherein the first layer is hafnium oxide and the second layer is hafnium silicate.

5. The method of claim 2 wherein the first and second layers are formed using metal-organic chemical vapor deposition (MOCVD) process.

6. The method of claim 4 wherein

the hafnium oxide layer is formed using TetrakisDiethylamidoHafnium (TDEAH) precursor; and

the hafnium silicate layer is formed using TetrakisDiethylamidoHafnium (TDEAH) and TetrakisDimethylamidoSilicon (TDMAS) precursors.

7. The method of claim 6 wherein:

the ozonated deionized water has an O₃concentration that is in the range of about 10 ppm to about 30 ppm;

the specified time period for pre-treating is in the range of about 5 minutes to about 15 minutes;

the hafnium oxide layer is formed at a pressure in the range of about 2 torr to about 8 torr and at a temperature in the range of 225° C.-700° C.;

the hafnium silicate layer is formed at a temperature in the range of 225° C.-700° C. and at a pressure in the range of about 3 torr to about 8 torr; and

the flow of NH₃is provided at a temperature in the range of about 400° C. to about 1100° C. for about 5 seconds to about 60 seconds.

8. The method of claim 7 wherein the dielectric stack has an effective oxide thickness (EOT) of less than about 1.7 nanometers.

9. The method of claim 7 wherein the dielectric stack has an effective oxide thickness (EOT) of less than about 1.25 nanometers.

10. The method of claim 6 wherein:

the ozonated deionized water has an O₃concentration that is about 20 ppm;

the specified time period for pre-treating is about 10 minutes;

the hafnium oxide layer is formed at a temperature of about 485° C. and at a pressure of about 4 torr;

the hafnium silicate layer is formed at a temperature of about 600° C. and at a pressure of about 4 torr; and

the flow of NH₃is provided for about 60 seconds at a temperature of about 700° C.

11. The method of claim 6 wherein the hafnium oxide layer is about 4 nanometers thick, the hafnium silicate layer is about 1.5 nanometers thick.

12. The method of claim 6 wherein the hafnium silicate layer comprises about 50% SiO₂.

13. The method of claim 2 wherein the first and second layers are formed using alkylamido or alkylamino ligand precursors.

14. The method of claim 2 wherein the hafnium oxide precursors are selected from a group consisting of amino or amido precursors of the form, Hf(NRR′)₄, wherein R is alkyl and R′ is alkyl and the hafnium silicate precursors are selected from a group consisting of amino or amido precursors of the form SiR₁R₂R₃R₄where

R₁═H, NH₂, N(CH₃)₂, NCO, alkoxy, amino, alkyl, or aryl;

R₂═H, NH₂, N(CH₃)₂, NCO, alkoxy, amino, alkyl, or aryl;

R₃═H, NH₂, N(CH₃)₂, NCO, alkoxy, amino, alkyl, or aryl; and

R₄═H, NH₂, N(CH₃)₂, NCO, alkoxy, amino, alkyl, or aryl.

15. The method of claim 2 wherein the hafnium oxide and the hafnium silicate layers are formed using MOCVD, LPCVD, PECVD, VPE, ALD or PVD.

16. The method of claim 1 further comprising:

removing the wafer from a first chamber to a second chamber after forming the hafnium oxide layer;

adjusting a temperature and a pressure of the first chamber; and

returning the wafer to the first chamber after adjusting the temperature and the pressure of the first chamber.

17. A method of forming a dielectric stack on a wafer comprising:

treating the wafer with hydrofluoric acid to form an HF-last surface;

pre-treating the HF-last surface with ozonated deionized water for a specified time period to form a pre-treated surface;

forming the dielectric stack on the pre-treated surface wherein the dielectric stack comprises a hafnium oxide layer or a hafnium silicate layer;

providing a flow of NH₃in a process zone surrounding the wafer after forming the dielectric stack;

transporting the wafer to a LPCVD chamber after providing the flow of NH₃; and

forming a polycrystalline-Si layer or an amorphous-Si layer over the dielectric stack.

18. The method of claim 17 wherein the polycrystalline-Si layer or the amorphous-Si layer is formed by introducing silane or disilane in a process zone surrounding the wafer at a specified temperature.

19. The method of claim 18 wherein the specified temperature is less than about 600°C.

20. The method of claim 16 wherein the temperature is in a range from about 400° C. to about 1100° C.

21. The method of claim 20 wherein forming the dielectric stack comprises:

forming a first layer of hafnium oxide or hafnium silicate on the pre-treated surface; and

forming a second layer of hafnium oxide or hafnium silicate on the first layer.

22. The method of claim 21 wherein forming the dielectric stack further comprises an annealing step between the forming steps.

23. The method of claim 21, wherein the second layer comprises hafnium silicate.

24. The method of claim 21 wherein the first and second layers are formed using LPCVD, PECVD, VPE, ALD or PVD.

25. The method of claim 21 wherein the first and second layers are formed using pulsed CVD.

26. The method of claim 21, wherein the first layer comprises hafnium oxide and the second layer comprises hafnium silicate.

27. The method of claim 26 wherein

the hafnium oxide layer is formed using TetrakisDiethylamidoHafnium (TDEAH) precursor; and

the hafnium silicate layer is formed using TetrakisDiethylamidoHafnium (TDEAH) and TetrakisDimthylamidoSilicon (TDMAS) precursors.

28. The method of claim 27 wherein

a specified duration for providing a flow of NH₃is in the range of about 5 seconds to about 60 seconds;

a specified temperature for providing a flow of NH₃is in the range of about 400° C. to about 1100° C.;

the hafnium oxide layer is formed at a pressure in the range of about 2 torr to about 8 torr and at a temperature in the range of 225° C.-700° C.;

the hafnium silicate layer is formed at a temperature in the range of 225° C.-700° C. and at a pressure in the range of about 3 torr to about 8 torr; and

a the flow of N₂is provided for about 5 seconds to about 60 seconds and at a temperature in the range of about 400° C. to about 1100° C.

29. The method of claim 28 wherein

the specified duration for providing a flow at NH₃is about 60 seconds;

the specified temperature for providing a flow of NH₃is about 700° C.;

the hafnium oxide layer is formed at a pressure of about 4 torr and at a temperature of about 485° C.;

the hafnium silicate layer is formed at a temperature of about 600° C. and at a pressure of about 4 torr; and

the flow of N₂, is provided for about 60 seconds and at a temperature of about 800° C.

30. The method of claim 26 where the hafnium oxide layer is annealed before the hafnium silicate layer is formed.

31. The method of claim 26 wherein the hafnium oxide layer is about 3 nanometers thick, the hafnium silicate layer is about 1.0 nanometer thick and the hafnium silicate layer comprises about 50% SiO₂.

Patent Citations (146)

Patent	Date	Inventor	Cited By
US5290609(A)	1994-03-01	Horiike et al.	Applicant
US6013553(A)	2000-01-01	Wallace et al.	Applicant
US6020243(A)	2000-02-01	Wallace et al.	Applicant
US6060755(A)	2000-05-01	Ma et al.	Applicant
US6174809(B1)	2001-01-01	Kang et al.	Applicant
US6200893(B1)	2001-03-01	Sneh	Applicant
US6203613(B1)	2001-03-01	Gates et al.	Applicant
US6207487(B1)	2001-03-01	Kim et al.	Applicant
US6238734(B1)	2001-05-01	Senzaki et al.	Applicant
US6270572(B1)	2001-08-01	Kim et al.	Applicant
US6287965(B1)	2001-09-01	Kang et al.	Applicant
US6291283(B1)	2001-09-01	Wilk	Applicant
US6297539(B1)	2001-10-01	Ma et al.	Applicant
US6299294(B1)	2001-10-01	Regan	Applicant
US6305314(B1)	2001-10-01	Sneh et al.	Applicant
US6348386(B1)	2002-02-01	Gilmer	Applicant
US6372598(B2)	2002-04-01	Kang et al.	Applicant
US6391785(B1)	2002-05-01	Satta et al.	Applicant
US6391803(B1)	2002-05-01	Kim et al.	Applicant
US6395650(B1)	2002-05-01	Callegari et al.	Applicant
US6399491(B2)	2002-06-01	Jeon et al.	Applicant
US6416577(B1)	2002-07-01	Suntoloa et al.	Applicant
US6420279(B1)	2002-07-01	Ono et al.	Applicant
US6451119(B2)	2002-09-01	Sneh et al.	Applicant
US6451695(B2)	2002-09-01	Sneh	Applicant
US6452229(B1)	2002-09-01	Krivokapic	Applicant
US6475276(B1)	2002-11-01	Elers et al.	Applicant
US6475910(B1)	2002-11-01	Sneh	Applicant
US6482262(B1)	2002-11-01	Elers et al.	Applicant
US6599572(B2)	2003-07-01	Saanila et al.	Applicant
US6620723(B1)	2003-09-01	Byun et al.	Applicant
US6674138(B1)	2004-01-01	Halliyal et al.	Applicant
US20010000866(A1)	2001-05-01	Sneh et al.	Applicant
US20010002280(A1)	2001-05-01	Sneh	Applicant
US20010009695(A1)	2001-07-01	Saanila et al.	Applicant
US20010021589(A1)	2001-09-01	Wilk	Applicant
US20010024387(A1)	2001-09-01	Raaijmakers et al.	Applicant
US20010029092(A1)	2001-10-01	Park et al.	Applicant
US20010029891(A1)	2001-10-01	Oh et al.	Applicant
US20020000598(A1)	2002-01-01	Kang et al.	Applicant
US20020005556(A1)	2002-01-01	Cartier et al.	Applicant
US20020008297(A1)	2002-01-01	Park et al.	Applicant
US20020014647(A1)	2002-02-01	Seidl et al.	Applicant
US20020015790(A1)	2002-02-01	Baum et al.	Applicant
US20020029092(A1)	2002-03-01	Gess	Applicant
US20020043666(A1)	2002-04-01	Parsons et al.	Applicant
US20020064970(A1)	2002-05-01	Chooi et al.	Applicant
US20020076837(A1)	2002-06-01	Hujanen et al.	Applicant
US20020081826(A1)	2002-06-01	Rotondaro et al.	Applicant
US20020081844(A1)	2002-06-01	Jeon et al.	Applicant
US20020086111(A1)	2002-07-01	Byun et al.	Applicant
US20020093046(A1)	2002-07-01	Morlya et al.	Applicant
US20020093781(A1)	2002-07-01	Bachhofer et al.	Applicant
US20020098627(A1)	2002-07-01	Pomarede et al.	Applicant
US20020106536(A1)	2002-08-01	Lee et al.	Applicant
US20020142500(A1)	2002-10-01	Foglietti et al.	Examiner
US20020146895(A1)	2002-10-01	Ramdani et al.	Applicant
US20020151152(A1)	2002-10-01	Shimamoto et al.	Applicant
US20020153579(A1)	2002-10-01	Yamamoto	Applicant
US20020155722(A1)	2002-10-01	Satta et al.	Applicant
US20020162506(A1)	2002-11-01	Sneh et al.	Applicant
US20020172768(A1)	2002-11-01	Endo et al.	Applicant
US20020175393(A1)	2002-11-01	Baum et al.	Applicant
US20020177282(A1)	2002-11-01	Song	Applicant
US20020182320(A1)	2002-12-01	Leskela et al.	Applicant
US20020187256(A1)	2002-12-01	Elers et al.	Applicant
US20020195643(A1)	2002-12-01	Harada	Examiner
US20020197881(A1)	2002-12-01	Ramdani et al.	Applicant
US20030031807(A1)	2003-02-01	Elers et al.	Applicant
US20030049931(A1)	2003-03-01	Byun et al.	Applicant
US20030049942(A1)	2003-03-01	Haukka et al.	Examiner
US20030060057(A1)	2003-03-01	Raaijmakers et al.	Examiner
US20030072975(A1)	2003-04-01	Shero et al.	Applicant
US20030082296(A1)	2003-05-01	Elers et al.	Applicant
US20030082301(A1)	2003-05-01	Chen et al.	Applicant
US20030089942(A1)	2003-05-01	Bhattacharyya	Applicant
US20030096473(A1)	2003-05-01	Shih et al.	Examiner
US20030104710(A1)	2003-06-01	Visokay et al.	Applicant
US20030106490(A1)	2003-06-01	Jallepally et al.	Applicant
US20030109114(A1)	2003-06-01	Niwa	Applicant
US20030116804(A1)	2003-06-01	Visokay et al.	Applicant
US20030133861(A1)	2003-07-01	Bowen et al.	Applicant
US20030168750(A1)	2003-09-01	Basceri et al.	Applicant
US20030173588(A1)	2003-09-01	Moriwaki et al.	Applicant
US20030185980(A1)	2003-10-01	Endo	Applicant
US20030186495(A1)	2003-10-01	Saanila et al.	Applicant
US20030188682(A1)	2003-10-01	Tois et al.	Applicant
US20030190423(A1)	2003-10-01	Yang et al.	Applicant
US20030194853(A1)	2003-10-01	Jeon	Applicant
US20030205729(A1)	2003-11-01	Basceri et al.	Applicant
US20030213987(A1)	2003-11-01	Basceri et al.	Applicant
US20030227033(A1)	2003-12-01	Ahn et al.	Applicant
US20030232501(A1)	2003-12-01	Kher et al.	Applicant
US20030232506(A1)	2003-12-01	Metzner et al.	Applicant
US20030232511(A1)	2003-12-01	Metzner et al.	Applicant
US20030234417(A1)	2003-12-01	Raaijmakers et al.	Applicant
US20030235961(A1)	2003-12-01	Metzner et al.	Applicant
US20040007747(A1)	2004-01-01	Visokay et al.	Applicant
US20040009307(A1)	2004-01-01	Koh et al.	Applicant
US20040009675(A1)	2004-01-01	Elssa et al.	Applicant
US20040016973(A1)	2004-01-01	Rotondaro et al.	Applicant
US20040018723(A1)	2004-01-01	Byun et al.	Applicant
US20040018747(A1)	2004-01-01	Lee et al.	Applicant
US20040023461(A1)	2004-02-01	Ahn et al.	Applicant
US20040023462(A1)	2004-02-01	Rotondaro et al.	Applicant
US20040028952(A1)	2004-02-01	Cartier et al.	Applicant
US20040029321(A1)	2004-02-01	Ang et al.	Applicant
US20040033698(A1)	2004-02-01	Lee et al.	Applicant
US20040036111(A1)	2004-02-01	Nishikawa et al.	Applicant
US20040038554(A1)	2004-02-01	Ahn et al.	Applicant
US20040040501(A1)	2004-03-01	Vaartstra	Applicant
US20040043149(A1)	2004-03-01	Gordon et al.	Applicant
US20040043569(A1)	2004-03-01	Ahn et al.	Applicant
US20040043630(A1)	2004-03-01	Vaarstra et al.	Applicant
US20040046197(A1)	2004-03-01	Bascerl et al.	Applicant
US20040048491(A1)	2004-03-01	Jung et al.	Applicant
US20040051152(A1)	2004-03-01	Nakajima	Applicant
US20040053484(A1)	2004-03-01	Kumar et al.	Applicant
EP1146141	2001-10-01		Applicant
EP1170804	2002-01-01		Applicant
GB2355727	2001-05-01		Applicant
JP2001-111000	2001-04-01		Applicant
JP2001-172767	2001-06-01		Applicant
JP2002-060944	2002-02-01		Applicant
JP2002-69641(A)	2002-03-01		Applicant
JP2002-69641	2002-03-01		Applicant
JP2002-93804	2002-03-01		Applicant
JP2002-167672	2002-06-01		Applicant
WO9929924	1999-06-01		Applicant
WO54320	2000-09-01		Applicant
WO70674	2000-11-01		Applicant
WO115520	2001-03-01		Applicant
WO125502	2001-04-01		Applicant
WO127346	2001-04-01		Applicant
WO127347	2001-04-01		Applicant
WO129280	2001-04-01		Applicant
WO129891(A1)	2001-04-01		Applicant
WO129893	2001-04-01		Applicant
WO140541	2001-06-01		Applicant
WO166832	2001-09-01		Applicant
WO182390	2001-11-01		Applicant
WO201628(A2)	2002-01-01		Applicant
WO209167	2002-01-01		Applicant
WO227063	2002-04-01		Applicant
WO243115	2002-05-01		Applicant
WO245167	2002-06-01		Applicant

Non-Patent Literature (17)

Ritala, Mikko Kalervo, Atomic Layer Epitaxy Growth of Titanium, Zirconium and Hafnium Dioxide Thin Films(Titanium Dioxide, Zirconium Dioxide), Ann. Acad. Sci. Fenn. Sr. All, vol. 57/02-C of Dissertation Abstracts International, 1994, pp. 3-48.Applicant
Balog, et al., “Chemical Vapor Deposition and Characterization of HfO2 Films From Organo-Hafnium Compounds,” Thin Solid Films, 41 (1977), pp. 247-259.Applicant
Ritala, et al., “Development of crystallinity and morphology in hafnium dioxide thin films grown by atomic layer epitaxy,” Thin Solid Films, 250 (1994), pp. 72-80.Applicant
Kattelus, et al., “Electrical Properties of Tantalum Based Composite Oxide Films,” Mat. Res. Soc. Symp. Proc., 284 (1983), pp. 511-516.Applicant
Cheon, et al., “Gas Phase Photoproduction of Diatomic Metal Nitrides During Metal Nitride Laser Chemical Vapor Deposition,” Inorg. Chem., American Chemical Society, 38 (19999), Pag s 2238-2239.Applicant
Oshita, et al., “HfO2 growth by low-pressure chemical vapor deposition using the Hf(N(C2H5)2)4/O2 gas system,” Journal of Crystal Growth, 233 (2001) pp. 292-297.Applicant
Ninisto, et al., “Synthesis of oxide thin films and overlayers by atomic layer epitaxy for advanced applications,” Materials Science and Engineering, B41 (1996) pp. 23-29.Applicant
Hendrix, et al., “Composition control of Hf1-xSixO2 films deposited on Si by chemical-vapor deposition using amide precursors.” Applied Physics Letter. American Journal of Physics, 80 No. 13 (Apr. 1, 2002) pp. 2362-2364.Applicant
“A Novel Atomic Layer Deposition Process to Deposit Hafnium Silicate Thin Films”, Senzaki, Yoshihide, et al., Electrochemical Society Proceedings vol. 2004-01, pp 264-70.Applicant
“Nitridation of Hafnium Silicate Thin Films”, Chatham, Hood; et al., Mat. Res. Soc. Symp. Proc. vol. 811, Apr. 12-16, 2004, D7.5.1.Applicant
“Interval Annealing During Alternating Pulse Deposition”, Conley, J.F.; et al., Mat. Res. Soc. Symp. Proc. vol. 811, Apr. 12-16, 2004, D1.3.1.Applicant
Ritala, “Atomic Layer Epitaxy,” Ann. Acad. Sci. Fenn. Ser. All, Chemica, vol. 257 (1994).Applicant
Kukil, et al. “Tailoring the Dielectric Properties of HfO2-Ta2Os Nanolaminates,” Applied Physics Letters, vol. 88, No. 26 (Jun. 24, 1996), pp. 3737-3739.Applicant
George, et al. “Surface Chemistry for Atomic Layer Growth,” J. Phys. Chem. (1996), 100, 13121-13131.Applicant
Hwang, et al. “Nanometer-Size α-PbO2-type TiO2 in Garnet: A Thermobarometer for Ultrahigh-Pressure Metamorphism,” Science Vo. 288 (Apr. 14, 2000).Applicant
Argarwal, et al. “Challenges In Integrating the High-K Gate Dielectric Film to the Conventional CMOS Process Flow,” Mat. Sec. Soc. Sump. Proc. vol. 670 (2001).Applicant
Clark-Phelps, et al. “Engineered Tantalum Aluminate and Hafnium Aluminate ALD Films for Ultrathin Dielectric Films with Improved Electrical and Thermal Properties,” Mat. Res. Soc. Symp. Proc. vol. 670 (2001).Applicant

Abstract