Hexacoordinated ruthenium or osmium metal carbene metathesis catalysts

[0007] This application claims the benefit of U.S. Provisional Patent Application No. 60/314,978 filed Aug. 24, 2001 U.S. Provisional Application No. 60/278,311 filed Mar. 23, 2001 U.S. Provisional Application No. 60/288,680 filed May 3, 2001 U.S. Provisional Application No. 60/309,806 filed Aug. 1, 2001, and is a continuation-in-part of U.S. patent application Ser. No. 09/948,115, filed Sep. 5, 2001 now U.S. Pat. No. 6,610,626, the contents of each of which are incorporated herein by reference.

[0009] Metathesis catalysts have been previously described by for example, U.S. Pat. Nos. 5,312,940, 5,342,909, 5,728,917, 5,750,815, 5,710,298, and 5,831,108 and PCT Publications WO 97/20865 and WO 97/29135 which are all incorporated herein by reference. These publications describe well-defined single component ruthenium or osmium catalysts that possess several advantageous properties. For example, these catalysts are tolerant to a variety of functional groups and generally are more active than previously known metathesis catalysts. Recently, the inclusion of an N-heterocyclic carbene (NHC) ligand, such as an imidazolidine or triazolylidene ligand as described in U.S. application Ser. Nos. 09/539,840, 09/576,370 and PCT Publication No. WO 99/51344, the contents of each of which are incorporated herein by reference, in these metal-carbene complexes has been found to improve the already advantageous properties of these catalysts. In an unexpected and surprising result, the shift in structure from the well-established penta-coordinated catalyst structure to the hexacoordinated catalyst structure has been found to significantly improve the properties of the catalyst. For example, these hexacoordinated catalysts of the present invention exhibit increased activity and selectivity not only in ring closing metathesis (“RCM”) reactions, but also in other metathesis reactions including cross metathesis (“CM”) reactions, reactions of acyclic olefins, and ring opening metathesis polymerization (“ROMP”) reactions.

[0010] The present invention relates to novel hexacoordinated metathesis catalysts and to methods for making and using the same. The inventive catalysts are of the formula

[0011] wherein:

[0012] M is ruthenium or osmium;

[0013] X and X¹are the same or different and are each independently an anionic ligand;

[0014] L, L^1′ and L²are the same or different and are each independently a neutral electron donor ligand, wherein at least one L, L^1′ and L²is an N-heterocyclic carbene ligand; and,

[0015] R and R¹are each independently hydrogen or a substituent selected from the group consisting of C₁-C₂₀alkyl, C₂-C₂₀alkenyl, C₂-C₂₀alkynyl, aryl, C₁-C₂₀carboxylate, C₁-C₂₀alkoxy, C₂-C₂₀alkenyloxy, C₂-C₂₀alkynyloxy, aryloxy, C₂-C₂₀alkoxycarbonyl, C₁-C₂₀alkylthio, C₁-C₂₀alkylsulfonyl and C₁-C₂₀alkylsulfinyl. Optionally, each of the R or R¹substituent group may be substituted with one or more moieties selected from the group consisting of C₁-C₁₀alkyl, C₁-C₁₀alkoxy, and aryl which in turn may each be further substituted with one or more groups selected from a halogen, a C₁-C₅alkyl, C₁-C₅alkoxy, and phenyl. Moreover, any of the catalyst ligands may further include one or more functional groups. Examples of suitable functional groups include but are not limited to: hydroxyl, thiol, thioether, ketone, aldehyde, ester, ether, amine, imine, amide, nitro, carboxylic acid, disulfide, carbonate, isocyanate, carbodiimide, carboalkoxy, carbamate, and halogen.

[0016] In preferred embodiments, L²and L^1′ are pyridine and L is a phosphine or an N-heterocyclic carbene ligand. Examples of N-heterocyclic carbene ligands include:

[0017] wherein R, R¹R⁶, R⁷, R⁸, R⁹, R¹⁰and R¹¹are each independently hydrogen or a substituent selected from the group consisting of C₁-C₂₀alkyl, C₂-C₂₀alkenyl, C₂-C₂₀alkynyl, aryl, C₁-C₂₀carboxylate, C₁-C₂₀alkoxy, C₂-C₂₀alkenyloxy, C₂-C₂₀alkynyloxy, aryloxy, C₂-C₂₀alkoxycarbonyl, C₁-C₂₀alkylthio, C₁-C₂₀alkylsulfonyl and C₁-C₂₀alkylsulfinyl. Optionally, each of the R, R¹R⁶, R⁷, R⁸, R⁹, R¹⁰and R¹¹substituent group may be substituted with one or more moieties selected from the group consisting of C₁-C₁₀alkyl, C₁-C₁₀alkoxy, and aryl which in turn may each be further substituted with one or more groups selected from a halogen, a C₁-C₅alkyl, C₁-C₅alkoxy, and phenyl. Moreover, any of the catalyst ligands may further include one or more functional groups. Examples of suitable functional groups include but are not limited to: hydroxyl, thiol, thioether, ketone, aldehyde, ester, ether, amine, imine, amide, nitro, carboxylic acid, disulfide, carbonate, isocyanate, carbodiimide, carboalkoxy, carbamate, and halogen. The inclusion of an NHC ligand to the hexacoordinated ruthenium or osmium catalysts has been found to dramatically improve the properties of these complexes. Because the NHC-based hexacoordinated complexes are extremely active, the amount of catalysts that is required is significantly reduced.

[0018] The present invention generally relates to ruthenium and osmium carbene catalysts for use in olefin metathesis reactions. More particularly, the present invention relates to hexacoordinated ruthenium and osmium carbene catalysts and to methods for making and using the same. The terms “catalyst” and “complex” herein are used interchangeably.

[0019] Unmodified ruthenium and osmium carbene complexes have been described in U.S. Pat. Nos. 5,312,940, 5,342,909, 5,728,917, 5,750,815, and 5,710,298, all of which are incorporated herein by reference. The ruthenium and osmium carbene complexes disclosed in these patents all possess metal centers that are formally in the +2 oxidation state, have an electron count of 16, and are penta-coordinated. These catalysts are of the general formula

[0020] wherein:

[0021] M is ruthenium or osmium;

[0022] X and X¹are each independently any anionic ligand;

[0023] L and L¹are each independently any neutral electron donor ligand;

[0024] R and R¹are the same or different and are each independently hydrogen or a substituent selected from the group consisting of C₁-C₂₀alkyl, C₂-C₂₀alkenyl, C₂-C₂₀alkynyl, aryl, C₁-C₂₀carboxylate, C₁-C₂₀alkoxy, C₂-C₂₀alkenyloxy, C₂-C₂₀alkynyloxy, aryloxy, C₂-C₂₀alkoxycarbonyl, C₁-C₂₀alkylthio, C₁-C₂₀alkylsulfonyl and C₁-C₂₀alkylsulfinyl. Optionally, each of the R or R¹substituent group may be substituted with one or more moieties selected from the group consisting of C₁-C₁₀alkyl, C₁-C₁₀alkoxy, and aryl which in turn may each be further substituted with one or more groups selected from a halogen, a C₁-C₅alkyl, C₁-C₅alkoxy, and phenyl. Moreover, any of the catalyst ligands may further include one or more functional groups. Examples of suitable functional groups include but are not limited to: hydroxyl, thiol, thioether, ketone, aldehyde, ester, ether, amine, imine, amide, nitro, carboxylic acid, disulfide, carbonate, isocyanate, carbodiimide, carboalkoxy, carbamate, and halogen.

[0025] The catalysts of the present invention are similar in that they are Ru or Os complexes; however, in these complexes, the metal is formally in the +2 oxidation state, and has an electron count of 18 and are hexacoordinated. These catalysts are of the general formula:

[0026] wherein

[0027] M is ruthenium or osmium;

[0028] X and X¹are the same or different and are each independently any anionic ligand;

[0029] L, L^1′, and L²are the same or different and are each independently any neutral electron donor ligand;

[0030] R and R¹are the same or different and are each independently hydrogen or a substituent selected from the group consisting of C₁-C₂₀alkyl, C₂-C₂₀alkenyl, C₂-C₂₀alkynyl, aryl, C₁-C₂₀carboxylate, C₁-C₂₀alkoxy, C₂-C₂₀alkenyloxy, C₂-C₂₀alkynyloxy, aryloxy, C₂-C₂₀alkoxycarbonyl, C₁-C₂₀alkylthio, C₁-C₂₀alkylsulfonyl and C₁-C₂₀alkylsulfinyl. Optionally, each of the R or R¹substituent group may be substituted with one or more moieties selected from the group consisting of C₁-C₁₀alkyl, C₁-C₁₀alkoxy, and aryl which in turn may each be further substituted with one or more groups selected from a halogen, a C₁-C₅alkyl, C₁-C₅alkoxy, and phenyl. Moreover, any of the catalyst ligands may further include one or more functional groups. Examples of suitable functional groups include but are not limited to: hydroxyl, thiol, thioether, ketone, aldehyde, ester, ether, amine, imine, amide, nitro, carboxylic acid, disulfide, carbonate, isocyanate, carbodiimide, carboalkoxy, carbamate, and halogen.

[0031] The hexacoordinated complex provides several advantages over the well-known pentacoordinated complexes. For example, the hexacoordinated complexes have greater air stability in the solid state because they are coordinatively saturated. Due to the lability of the additional ligand, e.g. pyridines, the complexes initiate faster than the phosphine based pentacoordinated species. Slow initiation means that only a small amount of complex is actually catalystically active thereby wasting much of the added complex. With faster initiators, catalyst loading is lowered. Further, and without being bound by theory, it is believed that the slower propogation of the hexacoordinated complexes, due to the re-binding of the labile ligands relative to the phosphines, translates to lower polydisperity. Moreover, the coordinatively saturated species crystallize better than their pentacoordinated counterparts. In addition, due to the lability of the ligands in the hexacoordinated complexes (e.g. pyridines and chlorines), these complexes allow access to previously inaccessible complexes and provide with higher purity certain complexes that can be obtained through different routes. For example, the pentacoordinated benzylidene with triphenylphosphine as its phosphine ligand can be prepared in higher yield and with greater purity using the hexacoordinated complex. The pentacoordinated benzylidene with P(p-CF₃C₆H₄)₃as its phosphine ligand is inaccessible through existing routes. Without being bound by theory, it is believe that this is because it would require the substitution of a stronger donor ligand with a weaker donor ligand. Substitution of the anionic ligands of the hexacoordinated complexes is much more rapid than with the corresponding pentacoordinated species (e.g. phosphine bound). Without being bound by theory, it is believed that this results from the requirement of ligand dissociation before anionic ligand substitution. Thus complexes with fast dissociation of their neutral electron donor ligands will undergo faster substitution.

[0032] The catalysts of the invention are also useful for ring-opening metathesis polymerization (ROMP), ring-closing metathesis (RCM), ADMET, and cross-metathesis. The synthesis and polymerization of olefins via these metathesis reactions can be found in, for example, U.S. application Ser. No. 09/891,144 entitled: “Synthesis of Functionalized and Unfunctionalized Olefins, filed Jun. 25, 2001, and U.S. application Ser. No. 09/491,800, now U.S. Pat. No. 6,306,988 the contents of each of which are incorporated herein by reference. Preferred embodiments of the catalysts of the invention possess at least one NHC ligand attached to the metal center, as illustrated by the following general formula:

[0033] In preferred embodiments of the inventive catalysts, the R substituent is hydrogen and the R¹substituent is selected from the group consisting of C₁-C₂₀alkyl, C₂-C₂₀alkenyl, and aryl. In even more preferred embodiments, the R¹substituent is phenyl or vinyl, optionally substituted with one or more moieties selected from the group consisting of C₁-C₅alkyl, C₁-C₅alkoxy, phenyl, and a functional group. In especially preferred embodiments, R¹is phenyl or vinyl substituted with one or more moieties selected from the group consisting of chloride, bromide, iodide, fluoride, —NO₂, —NMe₂, methyl, methoxy and phenyl. In the most preferred embodiments, the R¹substituent is phenyl or —C═C(CH₃)₂. When R¹is vinyl, the catalyst is of the general formula:

[0034] wherein M, L, L¹, L^1′, L², X, X¹, and R are as defined above. R′ and R″ are preferably independently hydrogen or phenyl but can be selected from any of the groups listed for R or R¹.

[0035] In preferred embodiments of the inventive catalysts, X and X¹are each independently hydrogen, halide, or one of the following groups: C₁-C₂₀alkyl, aryl, C₁-C₂₀alkoxide, aryloxide, C₃-C₂₀alkyldiketonate, aryldiketonate, C₁-C₂₀carboxylate, arylsulfonate, C₁-C₂₀alkylsulfonate, C₁-C₂₀alkylthio, C₁-C₂₀alkylsulfonyl, or C₁-C₂₀alkylsulfinyl. Optionally, X and X¹may be substituted with one or more moieties selected from the group consisting of C₁-C₁₀alkyl, C₁-C₁₀alkoxy, and aryl which in turn may each be further substituted with one or more groups selected from halogen, C₁-C₅alkyl, C₁-C₅alkoxy, and phenyl. In more preferred embodiments, X and X¹are halide, benzoate, C₁-C₅carboxylate, C₁-C₅alkyl, phenoxy, C₁-C₅alkoxy, C₁-C₅alkylthio, aryl, and C₁-C₅alkyl sulfonate. In even more preferred embodiments, X and X¹are each halide, CF₃CO₂, CH₃CO₂, CFH₂CO₂, (CH₃)₃CO, (CF₃)₂(CH₃)CO, (CF₃)(CH₃)₂CO, PhO, MeO, EtO, tosylate, mesylate, or trifluoromethanesulfonate. In the most preferred embodiments, X and X¹are each chloride.

[0036] L, L¹, L^1′ and L²may be any appropriate monodentate or multidentate neutral electron donor ligands. Multidentate neutral electron donor ligands include bidentate, tridentate, or tetradentate neutral electron donor ligands, for example. In preferred embodiments of the inventive catalysts, L, L¹, L^1′ and L²are each independently selected from the group consisting of phosphine, sulfonated phosphine, phosphite, phosphinite, phosphonite, arsine, stibine, ether, amine, amide, imine, sulfoxide, carboxyl, nitrosyl, pyridine, and thioether, or any derivatives therefrom. At least one L, L¹, L^1′ and L²may also be an N-heterocyclic carbene ligand. Preferred embodiments include complexes where both L^1′ and L²are either the same or different NHC ligands.

[0037] In preferred embodiments, at least one of L, L¹, L^1′ and L²is a phosphine of the formula PR³R⁴R⁵, where R³, R⁴, and R⁵are each independently aryl or C₁-C₁₀alkyl, particularly primary alkyl, secondary alkyl or cycloalkyl. In the even more preferred embodiments, at least one of L, L¹, L^1′ and L²is each selected from the group consisting of —P(cyclohexyl)₃, —P(cyclopentyl)₃, —P(isopropyl)₃, and —P(phenyl)₃. Even more preferably, at least one of L, L¹, L^1′ and L²is an NHC ligand. A preferred embodiment include where L is an NHC, L¹is P(cyclohexyl)₃or —P(cyclopentyl)₃, and L^1′ and L²are each heterocyclic ligands, optionally aromatic, or together form a bidenatate ligand. Preferably L^1′ and L²are each independently pyridine or a pyridine derivative.

[0038] Examples of NHC ligands include ligands of the general formulas:

[0039] wherein R, R¹, R′, R″, R⁶, R⁷, R⁸, R⁹, R¹⁰, and R¹¹are each independently hydrogen or a substituent selected from the group consisting of C₁-C₂₀alkyl, C₂-C₂₀alkenyl, C₂-C₂₀alkynyl, aryl, C₁-C₂₀carboxylate, C₁-C₂₀alkoxy, C₂-C₂₀alkenyloxy, C₂-C₂₀alkynyloxy, aryloxy, C₂-C₂₀alkoxycarbonyl, C₁-C₂₀alkylthio, C₁-C₂₀alkylsulfonyl and C₁-C₂₀alkylsulfinyl. Optionally, each of the R, R¹R⁶, R⁷, R⁸, R⁹, R¹⁰, and R¹¹substituent group may be substituted with one or more moieties selected from the group consisting of C₁-C₁₀alkyl, C₁-C₁₀alkoxy, and aryl which in turn may each be further substituted with one or more groups selected from a halogen, a C₁-C₅alkyl, C₁-C₅alkoxy, and phenyl. Moreover, any of the catalyst ligands may further include one or more functional groups. Examples of suitable functional groups include but are not limited to: hydroxyl, thiol, thioether, ketone, aldehyde, ester, ether, amine, imine, amide, nitro, carboxylic acid, disulfide, carbonate, isocyanate, carbodiimide, carboalkoxy, carbamate, and halogen.

[0040] In preferred embodiments, R⁶, R⁷, R⁸and R⁹are independently selected from the group consisting of hydrogen, phenyl, or together form a cycloalkyl or an aryl optionally substituted with one or more moieties selected from the group consisting of C₁-C₁₀alkyl, C₁-C₁₀alkoxy, aryl, and a functional group selected from the group consisting of hydroxyl, thiol, thioether, ketone, aldehyde, ester, ether, amine, imine, amide, nitro, carboxylic acid, disulfide, carbonate, isocyanate, carbodiimide, carboalkoxy, carbamate, and halogen; and R¹⁰and R¹¹are each is independently C₁-C₁₀alkyl or aryl optionally substituted with C₁-C₅alkyl, C₁-C₅alkoxy, aryl, and a functional group selected from the group consisting of hydroxyl, thiol, thioether, ketone, aldehyde, ester, ether, amine, imine, amide, nitro, carboxylic acid, disulfide, carbonate, isocyanate, carbodiimide, carboalkoxy, carbamate, and halogen.

[0041] In more preferred embodiments, R⁶and R⁷are both hydrogen or phenyl, or R⁶and R⁷together form a cycloalkyl group; R⁸and R⁹are hydrogen and R¹⁰and R¹¹are each either substituted or unsubstituted aryl. Without being bound by theory, it is believed that bulkier R¹⁰and R¹¹groups result in catalysts with improved characteristics such as thermal stability. In especially preferred embodiments, R¹⁰and R¹¹are the same and each is independently of the formula:

[0042] wherein:

[0043] R¹², R¹³, and R¹⁴are each independently hydrogen, C₁-C₁₀alkyl, C₁-C₁₀alkoxy, aryl, or a functional group selected from hydroxyl, thiol, thioether, ketone, aldehyde, ester, ether, amine, imine, amide, nitro, carboxylic acid, disulfide, carbonate, isocyanate, carbodiimide, carboalkoxy, carbamate, and halogen. In especially preferred embodiments, R¹², R¹³, and R¹⁴are each independently selected from the group consisting of hydrogen, methyl, ethyl, propyl, isopropyl, hydroxyl, and halogen. In the most preferred embodiments, R¹², R¹³, and R¹⁴are the same and are each methyl.

[0044] In these complexes, R⁶, R⁷, R⁸, and R⁹are each independently hydrogen or a substituent selected from the group consisting Of C₁-C₂₀alkyl, C₂-C₂₀alkenyl, C₂-C₂₀alkynyl, aryl, C₁-C₂₀carboxylate, C₁-C₂₀alkoxy, C₂-C₂₀alkenyloxy, C₂-C₂₀alkynyloxy, aryloxy, C₂-C₂₀alkoxycarbonyl, C₁-C₂₀alkylthio, C₁-C₂₀alkylsulfonyl and C₁-C₂₀alkylsulfinyl. Iimidazolidine ligands are also referred to as imidizol-2-ylidene ligands.

[0045] Other examples of neutral electron donor ligands include ligands which are derived, for example, from unsubstituted or substituted heteroarenes such as furan, thiophene, pyrrole, pyridine, bipyridine, picolylimine, gamma-pyran, gamma-thiopyran, phenanthroline, pyrimidine, bipyrimidine, pyrazine, indole, coumarone, thionaphthene, carbazole, dibenzofuran, dibenzothiophene, pyrazole, imidazole, benzimidazole, oxazole, thiazole, dithiazole, isoxazole, isothiazole, quinoline, bisquinoline, isoquinoline, bisisoquinoline, acridine, chromene, phenazine, phenoxazine, phenothiazine, triazine, thianthrene, purine, bisimidazole and bisoxazole.

[0046] Examples of substituents are OH, halogen, C(O)OR_s1, OC(O)R_s4, C(O)R_s2, nitro, NH₂, cyano, SO₃M_y, OSO₃M_y, NR₂₀SO₃M_y, N═N—R_s2, C₁-C₁₂alkyl, C₂-C₁₂alkenyl, C₁-C₁₂alkoxy, C₃-C₁₂cycloalkyl, C₃-C₁₂cycloalkenyl, C₁₂-C₁₁heterocycloalkyl, C₂-C₁₁heterocycloalkenyl, C₆-C₁₀aryl, C₆-C₁₀aryloxy, C₅-C₉heteroaryl, C₅-C₉heteroaryloxy, C₇-C₁₁aralkyl, C₇-C₁₁aralkyloxy, C₆-C₁₀heteroaralkyl, C₈-C₁₁aralkenyl, C₇-C₁₀heteroaralkenyl, monoamino, diamino, sulfonyl, sulfonamide, carbamide, carbamate, sulfohydrazide, carbohydrazide, carbohydroxamic acid residue and aminocarbonylamide, in which R_s1is hydrogen, M_y, C₁-C₁₂alkyl, C₂-C₁₂alkenyl, C₃-C₁₂cycloalkyl, C₂-C₁₁heterocycloalkyl, C₆-C₁₀aryl, C₅-C₉heteroaryl, C₇-C₁₁aralkyl or C₆-C₁₀heteroaralkyl, R_s4is hydrogen, C₁-C₁₂alkyl, C₂-C₁₂alkenyl, C₃-C₁₂cycloalkyl, C₂-C₁₁heterocyloalkyl, C₁₆-C₁₀aryl, C₅-C₁₉heteroaryl, C₇-C₁₁aralkyl or C₆-C₁₀heteroaralkyl, and R_s2and R_s20are hydrogen, C₁-C₁₂alkyl, C₂-C₁₂alkenyl, C₃-C₁₂cycloalkyl, C₃-C₁₂cycloalkenyl, C₂-C₁₁heterocycloalkyl, C₁-C₁₁heterocycloalkenyl, C₆-C₁₀aryl, C₅-C₉heteroaryl, C₇-C₁₁aralkyl, C₆-C₁₀heteroaralkyl, C₈-C₁₁aralkenyl or C₇-C₁₀heteroaralkenyl, and alkyl, alkenyl, alkoxy, cycloalkyl, cycloalkenyl, heterocycloalkyl, heterocycloalkenyl, aryl, aryloxy, heteroaryl, heteroaryloxy, aralkyl, aralkyloxy, heteroaralkyl, aralkenyl and heteroaralkenyl in turn are unsubstituted or substituted by one of the above-mentioned substituents; and y is 1 and M is a monovalent metal or y is ½ and M is a divalent metal.

[0047] In the context of the description of the present invention, the terms metal and corresponding cations refer to an alkali metal, for example Li, Na or K, an alkaline earth metal, for example Mg, Ca or Sr, or Mn, Fe, Zn or Ag, and corresponding cations. Lithium, sodium and potassium ions, with their salts, are preferred. NH₂, monoamino, diamino, carbamide, carbamate, carbohydrazide, sulfonamide, sulfohydrazide and aminocarbonylamide correspond preferably to a group R₈C(O)(NH)_pN(R₉)—, —C(O)(NH)_pNR₈R₉, R₈OC(O)(NH)_pN(R₉)—, R₈R₄₀NC(O)(NH)_pN(R₉)—, —OC(O)(NH)_pNR₈R₉, —N(R₄₀)C(O)(NH)_pNR₈R₉, R₈S(O)₂(NH)_pN(R₉)—; —S(O)₂(NH)_pNR₈R₉; R₈R₄₀NS(O)₂N(R₉)—or —NR₄₀S(O)₂NR₈R₉, in which R₈, R₉and R₄₀independently of one another are hydrogen, OH, C₁-C₁₂alkyl, C₁-C₁₂alkenyl, C₃-C₁₂cycloalkyl, C₃-C₁₂cycloalkenyl, C₂-C₁₁heterocycloalkyl, C₂-C₁₁heterocycloalkenyl, C₆-C₁₀aryl, C₅-C₉heteroaryl, C₇-C₁₆aralkyl, C₈-C₁₆aralkenyl with C₂-C₆alkenylene and C₆-C₁₀aryl, C₆-C₁₅heteroaralkyl, C₆-C₁₅heteroaralkenyl, or di-C₆-C₁₀aryl-C₁-C₆alkyl, or R_8′R_9′N, in which R_8′ and R_9′ independently of one another are hydrogen, OH, SO₃M_y, OSO₃M_y, C₁-C₁₂alkyl, C₃-C₁₂cycloalkyl, C₂-C₁₁heterocycloalkyl, C₆-C₁₀aryl, C₅-C₉heteroaryl, C₇-C₁₁aralkyl, C₆-C₁₀heteroaralkyl, C₈-C₁₆aralkenyl with C₂-C₆alkenylene and C₆-C₁₀aryl, or di-C₆-C₁₀aryl-C₁-C₆alkyl, which are unsubstituted or substituted by one or more substituents from the group consisting of OH, halogen, C(O)OR_s1, OC(O)R_s4, C(O)R_s2, nitro, NH₂, cyano, SO₃Z_y, OSO₃Z_y, NR₂₀SO₃Z_y, C₁-C₁₂alkyl, C₂-C₁₂alkenyl, C₁-C₁₂alkoxy, C₃-C₁₂cycloalkyl, C₃-C₁₂cycloalkenyl, C₂-C₁₁heterocycloalkyl, C₂-C₁₁heterocycloalkenyl, C₆-C₁₀aryl, C₆-C₁₀aryloxy, C₅-C₉heteroaryl, C₅-C₉heteroaryloxy, C₇-C₁₁aralkyl, C₇-C₁₁aralkyloxy, C₆-C₁₀heteroaralkyl, C₈-C₁₁aralkenyl, C₇-C₁₀heteroaralkenyl, monoamino, diamino, sulfonyl, sulfonamide, carbamide, carbamate, sulfohydrazide, carbohydrazide, carbohydroxamic acid residue and aminocarbonylamide, in which R_s1is hydrogen, Z_y, C₁-C₁₂alkyl, C₂-C₁₂alkenyl, C₃-C₁₂cycloalkyl, C₂-C₁₁heterocycloalkyl, C₆-C₁₀aryl, C₅-C₉heteroaryl, C₇-C₁₁aralkyl or C₆-C₁₀heteroaralkyl, R_s4is hydrogen, C₁-C₁₂alkyl, C₂-C₁₂alkenyl, C₃-C₁₂cycloalkyl, C₂-C₁₁heterocycloalkyl, C₆-C₁₀aryl, C₅-C₉heteroaryl, C₇-C₁₁aralkyl or C₆-C₁₀heteroaralkyl, and R_s2is hydrogen C₁-C₁₂alkyl, C₂-C₁₂alkenyl, C₃-C₁₂cycloalkyl, C₃-C₁₂cycloalkenyl, C₂-C₁₁heterocycloalkyl, C₂-C₁₁heterocycloalkenyl, C₆-C₁₀aryl, C₅-C₉heteroaryl, C₇-C₁₁aralkyl, C₆-C₁₀heteroaralkyl, C₈-C₁₁aralkenyl or C₇-C₁₀heteroaralkenyl, and alkyl, alkenyl, alkoxy, cycloalkyl, cycloalkenyl, heterocycloalkyl, heterocycloalkenyl, aryl, aryloxy, heteroaryl, heteroaryloxy, aralkyl, aralkyloxy, heteroaralkyl, aralkenyl and heteroaralkenyl in turn are unsubstituted or substituted by one of the above-mentioned substituents; p is 0 or 1 and y is 1 and Z is a monovalent metal or y is ½ and Z is a divalent metal; or R₈and R₉or R_8′ and R_9′ or R₈and R₄₀in the case of —NR₈R₉or —NR_8′R_9′ or R₈R₄₀N— together are tetramethylene, pentamethylene, —(CH₂)₂—O—(CH₂)₂—, —(CH₂)₂—S—(CH₂)₂— or —(CH₂)₂—NR₇—(CH₂)₂—, and R₇is H, C₁-C₆alkyl, C₇-C₁₁aralkyl, C(O)R_s2or sulfonyl.

[0048] The sulfonyl substituent is, for example, of the formula R₁₀—SO₂— in which R₁₀is C₁-C₁₂alkyl, C₃-C₁₂cycloalkyl, C₂-C₁₁heterocycloalkyl, C₆-C₁₀aryl, C₅-C₉heteroaryl, C₇-C₁₁aralkyl or C₆-C₁₀heteroaralkyl which are unsubstituted or substituted by one or more substituents selected from the group consisting of OH, halogen, C(O)OR_s1, OC(O)R_s4, C(O)R_s2, nitro, NH₂, cyano, SO₃Z_y, OSO₃Z_y, NR₂₀SO₃Z_y, C₁-C₁₂alkyl, C₂-C₁₂alkenyl, C₁-C₁₂alkoxy, C₃-C₁₂cycloalkyl, C₃-C₁₂cycloalkenyl, C₂-C₁₁heterocycloalkyl, C₂-C₁₁heterocycloalkenyl, C₆-C₁₀aryl, C₆-C₁₀aryloxy, C₅-C₉heteroaryl, C₅-C₉heteroaryloxy, C₇-C₁₀aralkyl, C₆-C₁₀heteroaralkyl, C₈-C₁₁aralkenyl, C₇-C₁₀heteroaralkenyl, monoamino, diamino, sulfonyl, sulfonamide, carbamide, carbamate, sulfonhydrazide, carbohydrazide, carbohydroxamic acid residue and aminocarbonylamide, in which R_s1is hydrogen, Z_y, C₁-C₁₂alkyl, C₂-C₁₂alkenyl, C₃-C₁₂cycloalkyl, C₂-C₁₁heterocycloalkyl, C₆-C₁₀aryl, C₅-C₉heteroaryl, C₇-C₁₁aralkyl or C₆-C₁₀heteroaralkyl, R_s4is hydrogen, C₁-C₁₂alkyl, C₂-C₁₂alkenyl, C₃-C₁₂cycloalkyl, C₂-C₁₁heterocycloalkyl, C₆-C₁₀aryl, C₅-C₉heteroaryl, C₇-C₁₁aralkyl or C₆-C₁₀heteroaralkyl, and R_s2and R₂₀are hydrogen, C₁-C₁₂alkyl, C₂-C₁₂alkenyl, C₃-C₁₂cycloalkyl, C₃-C₁₂cycloalkenyl, C₂-C₁₁heterocycloalkyl, C₂-C₁₁heterocycloalkenyl, C₆-C₁₀aryl, C₅-C₉heteroaryl, C₇-C₁₁aralkyl, C₆-C₁₀heteroaralkyl, C₈-C₁₁aralkenyl or C₇-C₁₀heteroaralkenyl, and alkyl, alkenyl, alkoxy, cycloalkyl, cycloalkenyl, heterocycloalkyl, heterocycloalkenyl, aryl, aryloxy, heteroaryl, heteroaryloxy, aralkyl, heteroaralkyl, aralkenyl and heteroaralkenyl in turn are unsubstituted or substituted by one of the above-mentioned substituents; and y is 1 and Z is a monovalent metal or y is ½ and Z is a divalent metal. Preferred neutral electron donor ligands are derived, for example, from heteroarenes of the group

[0049] A more preferred group of compounds is formed when L²and L^1′ independently of one another are pyridyl which is unsubstituted or substituted by one or more substituents from the group consisting Of C₁-C₁₂alkyl, C₂-C₁₁heterocycloalkyl, C₅-C₉heteroaryl, halogen, monoamino, diamino and —C(O)H. Examples are

[0050] Another preferred group of compounds is formed when L²and L^1′ together are bipyridyl, phenanthrolinyl, bithiazolyl, bipyrimidinyl or picolylimine which are unsubstituted or substituted by one or more sub stituents from the group consisting of C₁-C₁₂alkyl, C₆-C₁₀aryl and cyano, the substituents alkyl and aryl being in turn unsubstituted or substituted by one or more substituents from the group consisting of C₁-C₁₂alkyl, nitro, monoamino, diamino and nitro- or diamino-substituted —N═.N—C₆-C₁₀aryl. Examples are:

[0051] Even more preferably, L²and L^1′ are each independently selected from the group consisting of:

[0052] wherein R is selected from the group consisting of hydrogen or a substituent selected from the group consisting of C₁-C₂₀alkyl, C₂-C₂₀alkenyl, C₂-C₂₀alkynyl, aryl, C₁-C₂₀carboxylate, C₁-C₂₀alkoxy, C₂-C₂₀alkenyloxy, C₂-C₂₀alkynyloxy, aryloxy, C₂-C₂₀alkoxycarbonyl, C₁-C₂₀alkylthio, C₁-C₂₀alkylsulfonyl and C₁-C₂₀alkylsulfinyl. Optionally, the R group may be substituted with one or more moieties selected from the group consisting of C₁-C₁₀alkyl, C₁-C₁₀alkoxy, and aryl which in turn may each be further substituted with one or more groups selected from a halogen, a C₁-C₅alkyl, C₁-C₅alkoxy, and phenyl. Moreover, any of the heterocycles may further include one or more functional groups. Examples of suitable functional groups include but are not limited to: hydroxyl, thiol, thioether, ketone, aldehyde, ester, ether, amine, imine, amide, nitro, carboxylic acid, disulfide, carbonate, isocyanate, carbodiimide, carboalkoxy, carbamate, and halogen. Preferably R is selected from the group consisting of C₁-C₂₀alkyl, aryl, ether, amine, halide, nitro, ester and pyridyl.

[0053] Preferably complexes 1-4 are used to make the preferred embodiments 5-29 of the inventive complex:

[0054] wherein sIMES is

[0055] Most preferably, L is an NHC, preferably an imidazolidine ligand, and L²and L^1′ are pyridines.

[0056] The carbene complexes of the invention may also be cumulated. For example, one aspect of the invention is a catalyst of the general structure:

[0057] wherein M, L, L¹, L^1′, L², X, X¹, R and R¹are as defined above

[0058] In all of the above carbene complexes, at least one of L, L¹, L^1′, L², X, X¹, R and R¹, may be linked to at least one other of L, L¹, L^1′, L², X, X¹, R and R¹to form a bidentate or multidentate ligand array.

[0059] Synthesis

[0060] In general, the inventive catalysts are made by contacting excess neutral electron donor ligand, such as a pyridine, with the previously described penta-coordinated metal carbene catalyst complex of the formula:

[0061] wherein:

[0062] M, X, X¹, L, L¹, R and R¹are as previously defined; and wherein the third neutral electron donor ligand attaches to the metal center. Scheme 1 shows the general synthesis reaction for forming the inventive hexacoordinated metal carbene complexes:

[0063] wherein:

[0064] M, X, X¹, L, L¹, L^1′, L², R and R¹are as previously defined.

[0065] The synthesis of a preferred embodiment is shown in Scheme 2:

[0066] As shown by Schemes 1 and 2, in the presence of excess ligand L², the pentacoordinated complex loses the L¹ligand and ligands L²and L^1′ attach to the metal center. Ligands L²and L^1′ may be the same compound, for example, pyridines (when excess pyridine is used), or may together form a bidentate ligand. Alternatively, L¹and L^1′ may be the same, in which case, the pentacoordinated compound does not necessarily lose the L¹ligand in the presence of excess L².

[0067] The inventive complex may also be a cumulated carbene complex of the general formulas:

[0068] wherein M, X, X¹, L, L¹, L^1′, L², R and R¹are as previously defined. The synthesis of these compounds would follow Scheme 1 except that the starting compound would be a pentacoordinated vinylidene or pentacoordinated cumulene, respectively. The synthesis of preferred embodiments of the vinylidenes can be seen in Scheme 3:

[0069] Other preferred compounds synthesized by the inventive method include where L²and L^1′ form a bidentate ligand:

[0070] The inventive hexacoordinated catalyst complexes provide synthetic utility and utility in catalytic reactions. Without being bound by theory, these complexes contain substitutionally labile ligands, for example, pyridine and chloride ligands, and serve as a versatile starting material for the synthesis of new ruthenium metal carbene complexes. The chloride ligands are more labile than in the corresponding pentacoordinated phosphine-based complexes. As stated above, X and X¹are any anionic ligand. Preferably X and X¹are selected from the group consisting of chloride, bromide, iodide, Tp, alkoxide, amide, and thiolate. The pyridine ligands are more labile than the phosphines in the corresponding pentacoordinated phosphine-based complexes. Again, as stated above, L, L¹, L^1′, and L²can be any neutral electron donor ligands, including a NHC ligand. Depending on the size of the ligand, one or two neutral ligands (in addition to the NHC) may bind to the metal center.

[0071] Interestingly, the inventive catalyst complexes may be used in both metathesis reactions or the formation of an NHC ligand based complex. As shown in Scheme 4, the hexacoordinated complex can lose a neutral electron donor ligand to produce the pentacoordinated catalyst complex. The reaction may also proceed the other way to produce a hexacoordinated complex in the presence of excess L².

[0072] The pentacoordinated complex may also lose the L¹ligand to form the metathesis active tetracoordinated species (Scheme 5):

[0073] As shown in Scheme 5, the L¹ligand may also attach to a tetracoordinated species to form the pentacoordinated complex.

[0074] The tetracoordinated species may then initiate polymerization when in the presence of an olefin, as shown in Scheme 6, or may form the NHC-ligand based pentacoordinated complex when in the presence of a protected NHC-ligand (Scheme 7):

[0075] The following structure NHC—A—B indicates generally the protected form of a N-Heterocyclic Carbene (NHC).

[0076] It is also envisioned that the protected NHC—A—B may be of an unsaturated variety, such as

[0077] In the above structures, A is preferably H and B may be selected from the group consisting of CCl₃; CH₂SO₂Ph; C₆F₅; OR²¹; and N(R²²)(R²³), wherein R²¹is selected from the group consisting of Me, C₂H₅, i-C₃H₇, CH₂CMe₃, CMe₃, C₆H₁₁(cyclohexyl), CH₂Ph, CH₂norbomyl, CH₂norbomenyl, C₆H₅, 2,4,6-(CH₃)₃C₆H₂(mesityl), 2,6-i-Pr₂C₆H₂, 4-Me—C₆H₄(tolyl), 4-Cl—C₆H₄; and wherein R²²and R²³are independently selected from the group consisting of Me, C₂H₅, i-C₃H₇, CH₂CMe₃, CMe₃, C₆H₁₁(cyclohexyl), CH₂Ph, CH₂norbomyl, CH₂norbornenyl, C₆H₅, 2,4,6-(CH₃)₃C₆H₂(mesityl), 2,6-i-Pr₂C₆H₂, 4-Me-C₆H₄(tolyl), 4-Cl—C₆H₄). This approach relates to the thermal generation of a NHC ligand from a stable (protected) NHC derivative with a release of a quantity of A—B. One of the more preferred methods to generate a reactive NHC ligand is to employ a stable carbene precursor where the A—B compound is also a reactive NHC ligand. A detailed description of the protected NHC and related methods of synthesis and use can be seen in U.S. Provisional Patent Application No. 60/278,311 and No. 60/288,680, the contents of each of which are incorporated herein by reference. The following structure for the sImesHCCl₃shows a preferred embodiment of a protected NHC ligand for use with the inventive hexacoordinated complexes:

[0078] The NHC ligand based pentacoordinated complex may then lose the L ligand to form the metathesis active tetracoordinated species and proceed to initiate the polymerization reaction in the presence of an olefin (Scheme 8):

[0079] It should also be noted that the hexacoordinated complex can undergo a ligand exchange such that the NHC replaces another neutral electron donor ligand resulting in an NHC ligand based hexacoordinated complex (Scheme 9):

[0080] In all the above schemes and complexes M, X, X¹, L, L¹, L^1′, L², R, R¹, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹, and R^yare as previously defined.

[0081] The reaction of complex 1 with a large excess (˜100 equiv) of pyridine results in a rapid color change from red to bright green, and transfer of the resulting solution to cold (−10° C.) pentane leads to the precipitation of the bis-pyrdine adduct (ImesH₂)(Cl)₂(C₅H₅N)₂Ru═CHPh (31). Complex 31 can be purified by several washes with pentane and is isolated as an air-stable green solid that is soluble in CH₂Cl₂, benzene and THF. This procedure provides complex 31 in 80-85% yield and is easily carried out on a multigram scale.

[0082] Crystals suitable for X-ray crystal structure determination were grown by vapor diffusion of pentane into a saturated benzene solution of 31 at room temperature. The collection and refinement parameters for the crystallographic analysis are summarized in Table 1.

[0083] A labeled view of complex 31 is shown in FIG. 1 and representative bond lengths and bond angles are reported in Table 2:

[0084] Several structural isomers of the bis-pyridine adduct can be envisioned, but the solid-state structure reveals that the pyridines bind in a cis geometry, occupying the coordination sites trans to the benzylidene and the N-heterocyclic carbene ligand. The Ru═C(1) (benzylidene carbon) bond length of 1.873(4) Å is slightly longer than those in five-coordinate ruthenium olefin metathesis catalysts, including (Cl)₂(PCy₃)₂Ru═CHPh [d(Ru═C_α)=1.838(2) Å] and complex 1 [d(Ru═C_α)=1.835(2) Å]. The elongated Eu═C_α bond in 31 likely results from the presence of a trans pyridine ligand. The Ru—C(38) (N-heterocyclic carbene) bond length of 2.033(4) Å is approximately 0.05 Å shorter than that in complex 1, which is likely due to the relatively small size and moderate trans influence of pyridine relative to PCy₃. The 0.15 Å difference in the Ru—C(1) and Ru—C(38) bond distances highlights the covalent nature of the former and the dative nature of the latter ruthenium-carbene bond. Interestingly, the two Ru—N bond distances differ by more than 0.15 Å, indicating that the benzylidene ligand exerts a significantly larger trans influence than the N-heterocyclic carbene.

[0085] The kinetics of the reaction between complex 1 and pyridine was investigated in order to determine the mechanism of this ligand substitution. The reaction of complex 1 (0.88 M in toluene) with an excess of pyridine-d₅(0.18-0.69 M) is accompanied by a 150 nm red shift visible MLCT absorbance, and this transformation can be followed by UV-vis spectroscopy. The disappearance of starting material (502 nm) was monitored at 20° C., and in all cases, the data fit first-order kinetics over five half-lives. A plot of k_obsversus [C5D5N] is presented in FIG. 2. The data show an excellent linear fit (R²=0.999) even at high concentrations of pyridine, and the y-intercept of this line (1.1×10⁻³) is very close to zero. The rate constant for phosphine dissociation (k_B) in complex 1 has been determined independently by ³¹p magnetization transfer experiments, and at 20° C., k_Bis 4.1×10⁻⁵s⁻¹. This value of k_Bplaces an upper limit on the rate of dissociative ligand exchange in 1, and the observed rate constants for pyridine substitution are clearly 3 orders of magnitude larger than k_B. Taken together, these results indicate that the substitution of PCy₃with pyridine proceeds by an associative mechanism with a second-order rate constant of 5.7×10⁻²M⁻¹s⁻¹at 20° C. In marked contrast, displacement of the phosphine ligand of 1 with olefinic substrates (which is the initiation event in olefin metathesis reactions) occurs via a dissociative mechanism.

[0086] Initial reactivity studies of complex 31 revealed that both pyridine ligands are substitutionally labile. For example, benzylidene 31 reacts instantaneously with 1.1 equiv. of PCy₃to release pyridine and regenerate complex 1. This equilibrium can be driven back toward the pyridine adduct by addition of an excess of C₅D₅N, but it is readily reestablished by removal of the volatiles under vacuum.

[0087] The facile reaction of 31with PCy₃suggested that the pyridines may be displaced by other incoming ligands and it was discovered that reaction of the bis-pyridine complex with a wide variety of phosphines provides a simple and divergent route to new ruthenium benzylidenes of the general formula (ImesH₂)(PR₃)(Cl)₂Ru═CHPh. The combination of 31 and 1.1 equiv. of PR₃results in a color change from green to red/brown and formation of the corresponding PR₃adduct. The residual pyridine can be removed under vacuum, and the ruthenium products are purified by several washes with pentane and/or by column chromatography. This ligand substitution works well for a variety of alkyl- and aryl-substituted phosphines including PPH₃, PBn₃, and P(n-Bu)₃to produce complexes 32, 33 and 34.

[0088] Additionally, the para-substituted triphenylphosphine derivatives 35, 36 and 37 (containing para substituents CF₃, Cl, and OMe, respectively) can be prepared using the inventive method. The synthetic accessibility of complex 35 is particularly remarkable, because P(p-CF₃C₆H₄)₃is an extremely electron-poor phosphine (χ=20.5 cm⁻¹) The triarylphosphine ruthenium complexes 32, 35-37 are valuable catalysts as they are almost 2 orders of magnitude more active for olefin metathesis reactions than the parent complex 1.

[0089] There appear to be both steric and electronic limitations on the incoming phosphine ligand in the pyridine substitution reaction. For example, complex 31 does not react with P(o-tolyl)₃to produce a stable product, presumably due to the prohibitive size of the incoming ligand. The cone angle of P(o-tolyl)₃is 194°, while that of PCy₃(one of the larger phosphines shown to successfully displace the pyridines of 31) is 170°. Additionally, the electron-poor phosphine P(C₆F₆)₃shows no reaction with 31, even under forcing conditions. This ligand has a significantly lower electron donor capacity (χ=33.6 cm⁻¹) than P(p-CF₃C₆H₄)₃(χ=20.5 cm⁻¹) and also has a larger cone angle than PCy₃(θ=184°).

[0090] The methodology described herein represents a dramatic improvement over previous synthetic routes to the complexes (NHC)(PR₃)(Cl)₂Ru═CHPh. Earlier preparations of these compounds involved reaction of the bis-phosphine precursor (PR₃)₂(Cl)₂Ru═CHPh with an NHC ligand. These transformations were often low yielding (particularly when the NHC was small), and required the parallel synthesis of ruthenium precursors containing each PR₃ligand. Furthermore, bis-phosphine starting materials containing PR₃ligands that are smaller and less electron-donating than PPh₃(θ=145°; χ=13.25 cm⁻¹; pK_a=2.73) cannot be prepared, placing severe limitations on the complexes that are available by the earlier preparation methods.

[0091] The chlorine ligands of 31 are also substantially labile relative to those in the parent complex 1. For example, 31 reacts quantitatively with NaI within 2 hours at room temperature to afford (ImesH₂)(I)₂(C₅H₅N)Ru═CHPh (38). In contrast, the reaction between 1 and NaI takes approximately 8 hours to reach completion under identical conditions. Interestingly, ¹H NMR spectroscopy reveals that the diiodide complex 38 contains only one pyridine ligand, while the analogous dichloride species 31 coordinates 2 equiv. of pyridine. The relatively large size of the iodide ligands and the lower electrophilicity at the metal center in 38 (as compared to 31) are both believed to contribute to the formation of a five-coordinate complex in this system.

[0092] Complex 31 also reacts quantitatively with KTp [Tp=tris(pyrazolyl)borate] within 1 h at 25° C. to produce the bright green product Tp(ImesH₂)(Cl)Ru═CHPh (39), while the analogous reaction between complex 1 and KTp is extremely slow. (The latter proceeds to less than 50% completion even after several days at room temperature). Removal of the solvents under vacuum followed by filtration and several washes with pentane and methanol provides 39 as an air and moisture stable solid. Preliminary ¹H NMR studies also show that the combination of 31 with an excess of KO^t-Bu produces the four-coordinate benzylidene, (ImesH₂)—(O^tBu)₂Ru═CHPh (40), quantitatively within 10 min. at ambient temperature. In contrast, the reaction between 1 and KO^t-Bu to form 40 does not proceed to completion, even after several days at 35° C. Complex 40 may be considered a model for the 14-electron intermediate, (IMesH₂)(Cl)₂Ru═CHPh, involved in olefin metathesis reactions of 1.

[0093] The invention provides a high-yielding procedure for the preparation of (IMesH₂)(Cl)₂(C₅H₅N)₂Ru═CHPh (31) from (IMesH₂)(Cl)₂(PCy₃)Ru═CHPh (1). In contrast to the reaction of 1 with olefinic substrates, this ligand substitution proceeds by an associative mechanism. Complex 31 reacts readily with phosphines, providing access to new complexes discussed herein. Complex 31 also undergoes reaction with KO^t-Bu, NaI, and KTp to provide new four-, five-, and six-coordinate ruthenium benzylidenes. The inventive methodology is useful for facilitating the development of new ruthenium olefin metathesis catalysts containing structurally diverse ligand arrays.

[0094] Olefin Metathesis

[0095] The inventive complexes are useful in olefin metathesis reactions, particularly for polymerization reactions. These catalysts can be used in various metathesis reactions, including but not limited to, ring-opening metathesis polymerization of strained and unstrained cyclic olefins, ring-closing metathesis of acyclic dienes, acyclic diene metathesis polymerization (“ADMET”), self- and cross-metathesis reactions, alkyne polymerization, carbonyl olefination, depolymerization of unsaturated polymers, synthesis of telechelic polymers, and olefin synthesis.

[0096] The most preferred olefin monomer for use in the invention is substituted or unsubstituted dicyclopentadiene (DCPD). Various DCPD suppliers and purities may be used such as Lyondell 108 (94.6% purity), Veliscol UHP (99+% purity), B.F. Goodrich Ultrene® (97% and 99% purities), and Hitachi (99+% purity). Other preferred olefin monomers include other cyclopentadiene oligomers including trimers, tetramers, pentamers, and the like; cyclooctadiene (COD; DuPont); cyclooctene (COE, Alfa Aesar); cyclohexenylnorbornene (Shell); norbornene (Aldrich); norbornene dicarboxylic anhydride (nadic anhydride); norbornadiene (Elf Atochem); and substituted norbornenes including butyl norbornene, hexyl norbornene, octyl norbornene, decyl norbornene, and the like. Preferably, the olefinic moieties include mono-or disubstituted olefins and cycloolefins containing between 3 and 200 carbons. Most preferably, metathesis-active olefinic moieties include substituted or unsubstituted cyclic or multicyclic olefins, for example, cyclopropenes, cyclobutenes, cycloheptenes, cyclooctenes, [2.2.1]bicycloheptenes, [2.2.2]bicyclooctenes, benzocyclobutenes, cyclopentenes, cyclopentadiene oligomers including trimers, tetramers, pentamers, and the like; cyclohexenes. It is also understood that such compositions include frameworks in which one or more of the carbon atoms carry substituents derived from radical fragments including halogens, pseudohalogens, alkyl, aryl, acyl, carboxyl, alkoxy, alkyl- and arylthiolate, amino, aminoalkyl, and the like, or in which one or more carbon atoms have been replaced by, for example, silicon, oxygen, sulfur, nitrogen, phosphorus, antimony, or boron. For example, the olefin may be substituted with one or more groups such as thiol, thioether, ketone, aldehyde, ester, ether, amine, amide, nitro, carboxylic acid, disulfide, carbonate, isocyanate, phosphate, phosphite, sulfate, sulfite, sulfonyl, carbodiimide, carboalkoxy, carbamate, halogen, or pseudohalogen. Similarly, the olefin may be substituted with one or more groups such as C₁-C₂₀alkyl, aryl, acyl, C₁-C₂₀alkoxide, aryloxide, C₃-C₂₀alkyldiketonate, aryldiketonate, C₁-C₂₀carboxylate, arylsulfonate, C₁-C₂₀alkylsulfonate, C₁-C₂₀alkylthio, arylthio, C₁-C₂₀alkylsulfonyl, and C₁-C₂₀alkylsulfinyl, C₁-C₂₀alkylphosphate, arylphosphate, wherein the moiety may be substituted or unsubstituted.

[0097] These olefin monomers may be used alone or mixed with each other in various combinations to adjust the properties of the olefin monomer composition. For example, mixtures of cyclopentadiene dimer and trimers offer a reduced melting point and yield cured olefin copolymers with increased mechanical strength and stiffness relative to pure poly-DCPD. As another example, incorporation of COD, norbornene, or alkyl norbornene co-monomers tend to yield cured olefin copolymers that are relatively soft and rubbery. The resulting polyolefin compositions formed from the metathesis reactions are amenable to thermosetting and are tolerant of additives, stabilizers, rate modifiers, hardness and/or toughness modifiers, fillers and fibers including, but not limited to, carbon, glass, aramid (e.g., Kevlar® and Twaron®), polyethylene (e.g., Spectra® and Dyneema®), polyparaphenylene benzobisoxazole (e.g., Zylon®), polybenzamidazole (PBI), and hybrids thereof as well as other polymer fibers.

[0098] The metathesis reactions may optionally include formulation auxiliaries. Known auxiliaries include antistatics, antioxidants (primary antioxidants, secondary antioxidants, or mixtures thereof), ceramics, light stabilizers, plasticizers, dyes, pigments, fillers, reinforcing fibers, lubricants, adhesion promoters, viscosity-increasing agents, and demolding enhancers. Illustrative examples of fillers for improving the optical physical, mechanical, and electrical properties include glass and quartz in the form of powders, beads, and fibers, metal and semi-metal oxides, carbonates (e.g. MgCO₃, CaCO₃), dolomite, metal sulfates (e.g. gypsum and barite), natural and synthetic silicates (e.g. zeolites, wollastonite, and feldspars), carbon fibers, and plastics fibers or powders.

[0099] The UV and oxidative resistance of the polyolefin compositions resulting from the metathesis reactions using the inventive carbene complex may be enhanced by the addition of various stabilizing additives such as primary antioxidants (e.g., sterically hindered phenols and the like), secondary antioxidants (e.g., organophosphites, thioesters, and the like), light stabilizers (e.g., hindered amine light stabilizers or HALS), and UV light absorbers (e.g., hydroxy benzophenone absorbers, hydroxyphenylbenzotriazole absorbers, and the like), as described in U.S. application Ser. No. 09/498,120, filed Feb. 4, 2000, the contents of which are incorporated herein by reference.

[0100] Exemplary primary antioxidants include, for example, 4,4′-methylenebis (2,6-di-tertiary-butylphenol) (Ethanox 702®; Albemarle Corporation), 1,3,5-trimethyl-2,4,6-tris (3,5-di-tert-butyl-4-hydroxybenzyl) benzene (Ethanox 330®; Albermarle Corporation), octadecyl-3-(3′,5′-di-tert-butyl-4′-hydroxyphenyl) propionate (Irganox 1076®; Ciba-Geigy), and pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate)(Irganox® 1010; Ciba-Geigy). Exemplary secondary antioxidants include tris(2,4-ditert-butylphenyl)phosphite (Irgafos® 168; Ciba-Geigy), 1:11(3,6,9-trioxaudecyl)bis(dodecylthio)propionate (Wingstay® SN-1; Goodyear), and the like. Exemplary light stabilizers and absorbers include bis(1,2,2,6,6-pentamethyl-4-piperidinyl)-[[3,5-bis(1,1-dimethylethyl)-4-hydroxyphenyl]methyl]butylmalonate (Tinuvin® 144 HALS; Ciba-Geigy), 2-(2H-benzotriazol-2-yl)-4,6-ditertpentylphenol (Tinuvino® 328 absorber; Ciba-Geigy), 2,4-di-tert-butyl-6-(5-chlorobenzotriazol-2-yl)phenyl (Tinuvin® 327 absorber; Ciba-Geigy), 2-hydroxy-4-(octyloxy)benzophenone (Chimassorb® 81 absorber; Ciba-Geigy), and the like.

[0101] In addition, a suitable rate modifier such as, for example, triphenylphosphine (TPP), tricyclopentylphosphine, tricyclohexylphosphine, triisopropylphosphine, trialkylphosphites, triarylphosphites, mixed phosphites, or other Lewis base, as described in U.S. Pat. No. 5,939,504 and U.S. application Ser. No. 09/130,586, the contents of each of which are herein incorporated by reference, may be added to the olefin monomer to retard or accelerate the rate of polymerization as required.

[0102] The resulting polyolefin compositions, and parts or articles of manufacture prepared therefrom, may be processed in a variety of ways including, for example, Reaction Injection Molding (RIM), Resin Transfer Molding (RTM) and vacuum-assisted variants such as VARTM (Vacuum-Assisted RTM) and SCRIMP (Seemann Composite Resin Infusion Molding Process), open casting, rotational molding, centrifugal casting, filament winding, and mechanical machining. These processing compositions are well known in the art. Various molding and processing techniques are described, for example, in PCT Publication WO 97/20865, the disclosure of which is incorporated herein by reference.

[0103] The metathesis reactions may occur in the presence or absence of a solvent. Examples of solvents that can be used in the polymerization reaction include organic, protic, or aqueous solvents, which are preferably inert under the polymerization conditions. Examples of such solvents include aromatic hydrocarbons, chlorinated hydrocarbons, ethers, aliphatic hydrocarbons, alcohols, water, or mixtures thereof. Preferred solvents include benzene, toluene, p-xylene, methylene chloride, dichloroethane, dichlorobenzene, chlorobenzene, tetrahydrofuran, diethylether, pentane, methanol, ethanol, water or mixtures thereof. More preferably, the solvent is benzene, toluene, p-xylene, methylene chloride, dichloroethane, dichlorobenzene, chlorobenzene, tetrahydrofuran, diethylether, pentane, methanol, ethanol, or mixtures thereof. Most preferably, the solvent is toluene, or a mixture of benzene and methylene chloride. The solubility of the polymer formed in the polymerization reaction will depend on the choice of solvent and the molecular weight of the polymer obtained.

[0104] The inventive complexes have a well-defined ligand environment that enables flexibility in modifying and fine-tuning the activity level, stability, solubility and ease of recovery of these catalysts. The solubility of the carbene compounds may be controlled by proper selection of either hydrophobic or hydrophilic ligands as is well known in the art. The desired solubility of the catalyst will largely be determined by the solubility of the reaction substrates and reaction products.

[0105] The inventive metal carbene complexes have shown a high rate of initiation allowing for most, if not all, of the complex added to the reaction to be consumed. Thus, less catalyst is wasted in the metathesis reaction. In contrast, the previous pentacoordinated initiators had a higher amount of extractibles (i.e. unpolymerized monomer) remaining after the reaction concluded. The rate of propagation is also slowed by the presence of the two pyridine ligands. The high rate of initiation and low rate of propagation yields polymers with narrow polydisperities relative to those achieved with the earlier pentacoordinated complexes. Moreover, it was determined that heat increases the rate of the initiation. Thermal initiation of the pentacoordinated complexes can be seen in U.S. Pat. No. 6,107,420, the contents of which are incorporated herein by reference. In general, the initiation and/or rate of the metathesis polymerization using the inventive catalysts is controlled by a method comprising contacting the inventive catalyst with an olefin and heating the reaction mixture. In a surprising and unexpected result, the T_maxfor the thermal initiation of the inventive catalyst is significantly higher than the T_maxfor the previous pentacoordinated catalysts. Without being bound by theory, this is significant in that in a reaction using a metathesis catalyst, if the part or article being prepared is a type of filled system (e.g., a system containing reinforcing fillers, fibers, beads, etc.), the filling material may act as a heat sink. With the previous pentacoordinated catalysts, post-curing was sometimes necessary due to the effect of the heat sink resulting from a filled system. ROMP polymerization in the presence of peroxide cross linking agents using pentacoordinated catalysts is discussed in U.S. Pat. No. 5,728,785, the contents of which are incorporated herein by reference. In contrast, the reactions using the inventive hexacoordinated catalysts generate significantly more internal heat. This high T_maxreduces the need for post cure. Additionally, even if peroxides or radicals are added to promote crosslinking, the degree of crosslinking in the part that uses the radical mechanism is increased in comparison to a part prepared using the previous pentacoordinated metathesis catalysts. Moreover, the half-life is dependent on the maximum temperature. Using the inventive catalysts, the half life is reduced substantially, and therefore less catalyst is needed, providing a significant commercial advantage. Without being bound by theory, the higher T_maxindicates that in a ROMP reaction, more rings are opened, and there is a better degree of cure. With a higher T_max, the extractibles are almost to zero, indicating that almost every molecule that can be reacted is reacted. For example, the vinylidenes are advantageous in that they are more stable at higher temperatures than the alkylidenes. When the protected NHC (e.g., a saturated Imes ligand as described in U.S. Provisional Patent Application No. 60/288,680 and No. 60/278,311, the contents of each of which are incorporated herein by reference), is added to the reaction mixture, a dramatic increase in peak exotherm is seen. Additionally, the time to reach the peak is significantly reduced. A high peak exotherm means more catalyst is available for polymerization, indicating that the extractibles are close to zero. Accordingly, the inventive catalysts have better conversion, better properties, even in the presence of fillers and additives.

[0106] For the purposes of clarity, the specific details of the invention will be illustrated with reference to especially preferred embodiments. However, it should be appreciated that these embodiments and examples are for the purposes of illustration only and are not intended to limit the scope of the invention.

[0107] General Procedures

[0108] Manipulation of organometallic compounds was performed using standard Schlenk techniques under an atmosphere of dry argon or in a nitrogen-filled Vacuum Atmospheres drybox (O₂<2 ppm). NMR spectra were recorded on a Varian Inova (499.85 MHz for ¹H; 202.34 MHz for ³¹P; 125.69 MHz for ¹³C) or a Varian Mercury 300 (299.817 for ¹H; 121.39 MHz for ³¹P; 74.45 MHz for ¹³C). ³¹P NMR spectra were referenced using H₃PO₄(ò=0 ppm) as an external standard. UV-vis spectra were recorded on an HP 8452A diode-array spectrophotometer.

[0109] Materials and Methods

[0110] Pentane, toluene, benzene, and benzene-d₆were dried by passage through solvent purification columns. Pyridine was dried by vacuum transfer from CaH₂. All phosphines as well as KTp were obtained from commercial sources and used as received. Ruthenium complex 1 was prepared according to literature procedures.

[0111] Synthesis of (IMesH₂)(C₁₂H₈N₂)(Cl)₂Ru═CHPh

[0112] Complex 1 (2.0 grams) was dissolved in toluene (10 mL), and 1,10-phenanthroline (0.85 grams, 2 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to brown-orange was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a brown-orange solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₁₂H₈N₂)(Cl)₂Ru═CHPh 5 as an brown-orange powder (1.7 gram, 96% yield).

[0113] Synthesis of (IMesH₂)(C₅H₄BrN)₂(Cl)₂Ru═CHPh

[0114] Complex 1 (2.0 grams) was dissolved in toluene (10 mL), and 3-bromopyridine (1.50 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to light green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a light green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₅H₄BrN)₂(Cl)₂Ru═CHPh 6 as a light green powder (1.8 grams, 86% yield).

[0115] Synthesis of (IMesH₂)(C₉H₁₂N₂)₂(Cl)₂Ru═CHPh

[0116] Complex 1 (2.0 grams) was dissolved in toluene (10 mL), and 4-pyrrolidinopyridine (1.40 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to light green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a light green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₉H₁₂N₂)₂(Cl)₂Ru═CHPh 7 as a light green powder (1.9 gram, 93% yield).

[0117] ¹H NMR (300 MHz, CD₂Cl₂): δ19.05 (s, 1H, CHPh), 8.31 (d, 2H, pyridine CH, J_HH=6.6 Hz), 7.63 (d, 2H, ortho CH, J_HH=8.4 Hz), 7.49 (t, 1H, para CH, J_HH=7.4 Hz), 7.33 (d, 2H, pyridine CH, J_HH=6.9 Hz), 7.10 (t, 2H, meta CH, J_HH=8.0 Hz), 7.03 (br. s, 2H, Mes CH), 6.78 (br. s, 2H, Mes CH), 6.36 (d, 2H, pyridine CH, J_HH=6.3 Hz), 6.05 (d, 2H, pyridine CH, J_HH=6.9 Hz), 4.08 (br. d, 4H, NCH₂CH₂N), 3.30 (m, 4H, pyrrolidine CH₂), 3.19 (m, 4H, pyrrolidine CH₂), 2.61-2.22 (multiple peaks, 18H, Mes CH₃), 2.02 (m, 4H, pyrrolidine CH₂), 1.94 (m, 4H, pyrrolidine CH₂).

[0118] A 75 gram mass of DCPD (containing about 24% trimerized DCPD) was polymerized using (IMesH₂)(C₉H₁₂N₂)₂(Cl)₂Ru═CHPh=0.0151 grams at a DCPD:Ru ratio of (about 30,000:1) at a starting temperature of about 24.2° C. Result: Time to reach maximum temperature (T_max)=194 seconds. T_max=208.9° C. Glass transition temperature measured by thermal mechanical analysis (TMA)=165° C. Percent residual monomer (toluene extraction at room temperature)=1.23%.

[0119] Synthesis of (IMesH₂)(C₆H₇N)₂(Cl)₂Ru═CHPh

[0120] Complex 1 (2.0 grams) was dissolved in toluene (10 mL), and 4-methylpyridine (0.88 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to light green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a light green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₆H₇N)₂(Cl)₂Ru═CHPh 8 as an light green powder (1.5 grams, 84% yield).

[0121] Synthesis of (IMesH₂)(C₁₀H₈N₂)₂(Cl)₂Ru═CHPh

[0122] Complex 1 (2.0 grams) was dissolved in toluene (10 mL), and 4,4′-bipyridine (0.74 grams, 2 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to brown-orange was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and an brown-orange solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₁₀H₈N₂)₂(Cl)₂Ru═CHPh 9 as a brown-orange powder (1.4 gram, 71% yield).

[0123] ¹H NMR (500 MHz, CD₂Cl₂): δ19.15 (s, 1H, CHPh), 8.73-8.68 (multiple peaks, 8H pyridine CH), 7.63-6.77 (multiple peaks, 17H, pyridine CH, para CH, meta CH, Mes CH), 4.08 (br. d, 4H, NCH₂CH₂N), 2.61-2.24 (multiple peaks, 18H, Mes CH₃).

[0124] A 75 gram mass of DCPD (containing about 24% trimerized DCPD) was polymerized using (IMesH₂)(C₁₀H₈N₂)₂(Cl)₂Ru═CHPh=0.0153 grams at a DCPD:Ru ratio of (about 30,000:1) at a starting temperature of about 24.2° C. Result: Time to reach maximum temperature (T_max)=953 seconds. T_max=124.2° C.

[0125] Synthesis of (IMesH₂)(C₇H₁₀N₂)₂(Cl)₂Ru═CHPh

[0126] Complex 1 (2.0 grams) was dissolved in toluene (10 mL), and 4-dimethylaminopyridine (1.18 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to light green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a light green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₇H₁₀N₂)₂(Cl)₂Ru═CHPh 10 as a light green powder (1.9 gram, 99% yield).

[0127] ¹H NMR (500 MHz, CD₂Cl₂): δ19.10 (s, 1H, CHPh), 8.18 (d, 2H, pyridine CH, J_HH=6.5 Hz), 7.64 (d, 2H, ortho CH, J_HH=7.5 Hz), 7.48 (t, 11H, para CH, J_HH=7.0 Hz), 7.38 (d, 2H, pyridine CH, J_HH=6.5 Hz), 7.08 (t, 2H, meta CH, J_HH=7.5 Hz), 7.00 (br. s, 2H, Mes CH), 6.77 (br. s, 2H, Mes CH), 6.49 (d, 2H, pyridine CH, J_HH=6.0 Hz), 6.15 (d, 2H, pyridine CH, J_HH=7.0 Hz), 4.07 (br. d, 4H, NCH₂CH₂N), 2.98 (s, 6H, pyridine CH₃), 2.88 (s, 6H, pyridine CH₃), 2.61-2.21 (multiple peaks, 18H, Mes CH₃).

[0128] A 75 gram mass of DCPD (containing about 24% trimerized DCPD) was polymerized using (IMesH₂)(C₇H₁₀N₂)₂(Cl)₂Ru═CHPh=0.0141 grams at a DCPD:Ru ratio of (about 30,000:1) at a starting temperature of about 24.2° C. Result: Time to reach maximum temperature (T_max)=389 seconds. T_max=175.3° C.

[0129] Synthesis of (IMesH₂)(C₁₀H₈N₂)(Cl)₂Ru═CHPh

[0130] Complex 1 (2.0 grams) was dissolved in toluene (10 mL), and 2,2′-bipyridine (0.74 grams, 2 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to brown-red was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and an brown-red solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₁₀H₈N₂)(Cl)₂Ru═CHPh 11 as a brown-red powder (0.7 gram, 41% yield).

[0131] Synthesis Of (IMeSH₁₂)(C₆H₁₅NO)₂(Cl)₂Ru═CHPh

[0132] Complex 1 (2.0 grams) was dissolved in toluene (10 mL), and 2-pyridinecarboxaldehyde (1.01 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to dark blue was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a dark blue solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₆H₅NO)₂(Cl)₂Ru═CHPh 12 as a dark blue powder (1.3 gram, 70% yield).

[0133] Synthesis of (IMesH₂)(C₁₁H₉N)₂(Cl)₂Ru═CHPh

[0134] Complex 1 (2.0 grams) was dissolved in toluene (10 mL), and 4-phenylpyridine (1.50 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to dark green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a dark green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₁₁H₉N)₂(Cl)₂Ru═CHPh 13 as a dark green powder (2.0 grams, 97% yield).

[0135] ¹H NMR (500 MHz, CD₂Cl₂): δ19.23 (s, 1H, CHPh), 8.74 (br. s, 2H, pyridine), 7.91 (br. s, 2H, pyridine), 7.70-7.08 (multiple peaks, 19H, ortho CH, para CH, meta CH, pyridine), 6.93 (br. S, 2H, Mes CH) 6.79 (br. s, 2H, Mes CH), 4.05 (br. s, 4H, NCH₂CH₂N), 2.62-2.29 (multiple peaks, 18H, Mes CH₃).

[0136] A 75 gram mass of DCPD (containing about 24% trimerized DCPD) was polymerized using (IMesH₂)(C₁₁H₉N)₂(Cl)₂Ru═CHPh=0.0153 grams at a DCPD:Ru ratio of (about 30,000:1) at a starting temperature of about 13.4° C.

[0137] Result

[0138] Time to reach maximum temperature (T_max)=145 seconds. T_max=202.2° C. Glass transition temperature measured by thermal mechanical analysis (TMA)=168° C. Percent residual monomer (toluene extraction at room temperature)=1.17%.

[0139] Synthesis of (IMesH₂)(C₁₈H₁₂N₂)₂(Cl)₂Ru═CHPh

[0140] Complex 1 (2.0 grams) was dissolved in toluene (10 mL), and 2,2′-biquinoline (1.21 grams, 2 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a slight color change from dark purple to brown-purple was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a brown-purple solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₁₈H₁₂N₂)₂(Cl)₂Ru═CHPh 14 as a brown-purple powder (1.8 gram, 93% yield).

[0141] Synthesis of (IMesH₂)(C₅H₁₅N)₂(Cl)₂Ru═CHPh

[0142] Complex 1 (1.1 g, 1.3 mmol) was dissolved in toluene, and pyridine (110 mL) was added. The reaction was stirred for 10 min during which time a color change from pink to bright green was observed. The reaction mixture was cannula transferred into 75 mL of cold (about 0° C.) pentane, and a green solid precipitated. The precipitate was filtered, washed with 4×20 mL of pentane, and dried under vacuum to afford (IMesH₂)(C₅H₅N)₂(Cl)₂Ru═CHPh as a green powder (0.75 g, 80% yield). Samples for elemental analysis were prepared by recrystallization from C₆H₆/pentane followed by drying under vacuum. These samples analyze as the monopyridine adduct (IMesH₂)(C₅H₅N) (Cl)₂Ru═CHPh, probably due to loss of pyridine under vacuum.

[0143] ¹H NMR (C₆H₆): δ19.67 (s, 1H, CHPh), 8.84 (br. S, 2H, pyridine), 8.39 (br. s, 2H, pyridine), 8.07 (d, 2H, ortho CH, J_HH=8 Hz), 7.15 (t, 1H, para CH, J_HH=7 Hz), 6.83-6.04 (br multiple peaks, 9H, pyridine, and Mes CH), 3.37 (br d, 4H, CH₂CH₂), 2.79 (br s, 6H, Mes CH₃), 2.45 (br s, 6H, Mes CH₃), 2.04 (br s, 6H, Mes CH₃).

[0144] ¹³C{¹H}NMR (C₆D₆): δ314.90 (m, Ru═CHPh), 219.10 (s, Ru—C(N)₂), 152.94, 150.84, 139.92, 138.38, 136.87, 135.99, 134.97, 131.10, 130.11, 129.88, 128.69, 123.38, 51.98, 51.37, 21.39, 20.96, 19.32. Anal. Calcd for C₃₃H₃₇N₃Cl₂Ru: C, 61.20; H, 5.76; N, 6.49. Found: C, 61.25; H, 5.76; N, 6.58.

[0145] A 75 gram mass of DCPD (containing about 24% trimerized DCPD) was polymerized using (IMesH₂)(C₅H₅N)₂(Cl)₂Ru═CHPh=0.0127 grams at a DCPD:Ru ratio of (about 30,000:1) at a starting temperature of about 12.1° C. Result: Time to reach maximum temperature (T_max)=173 seconds. T_max=201.9° C. Glass transition temperature measured by thermal mechanical analysis (TMA)=164° C. Percent residual monomer (toluene extraction at room temperature)=1.05%.

[0146] A 50 gram mass of hexylnorbornene was polymerized using (IMesH₂)(C₅H₅N)₂(Cl)₂Ru═CHPh=0.0068 grams at a H_xN:Ru ratio of (about 30,000:1) at a starting temperature of about 12.2° C.

[0147] Result

[0148] Time to reach maximum temperature (T_max)=99 seconds. T_max=140.7° C.

[0149] Synthesis of (PCp₃)(C₁₂H₈N₂)(Cl)₂Ru═CH—CH═C(CH₃)₂

[0150] Complex 2 (2.0 grams) was dissolved in toluene (10 mL), and 1,10-phenanthroline (1.01 grams, 2 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to red-brown was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a red-brown solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (PCp₃)(C₁₂H₈N₂)(Cl)₂Ru═CH—CH═C(CH₃)₂15 as an red-brown powder (1.8 gram, 98% yield).

[0151] Synthesis of (PCp₃)(C₅H₄BrN)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0152] Complex 2 (2.0 grams) was dissolved in toluene (10 mL), and 3-bromopyridine (1.76 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (PCp₃)(C₅H₄BrN)₂(Cl)₂Ru═CH—CH═C(CH₃)₂16 as an green powder (0.2 gram, 10% yield).

[0153] Synthesis of (PCp₃)(C₅H₅N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0154] Complex 2 (2.0 grams) was dissolved in toluene (10 mL), and pyridine (0.88 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (PCp₃)(C₅H₅N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂17 as a green powder (0.6 gram, 34% yield).

[0155] Synthesis of (PCp₃)(C₆H₇N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0156] Complex 2 (2.0 grams) was dissolved in toluene (10 mL), and 4-methylpyridine (1.04 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to light green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a light green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (PCp₃)(C₆H₇N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂18 as a light green powder (1.4 gram, 75% yield).

[0157] Synthesis of (PCy₃)(C₁₂H₈N₂)(Cl)₂Ru═CH—CH═C(CH₃)₂

[0158] Complex 3 (2.0 grams) was dissolved in toluene (10 mL), and 1,10-phenanthroline (0.91 grams, 2 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to orange-brown was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and an orange-brown solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (PCy₃)(C₁₂H₉N₂)(Cl)₂Ru═CH—CH═C(CH₃)₂19 as an orange-brown powder (1.7 gram, 97% yield).

[0159] Synthesis of (PCy₃)(C₅H₄BrN)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0160] Complex 3 (2.0 grams) was dissolved in toluene (10 mL), and 3-bromopyridine (1.58 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time no dramatic color change from dark purple was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a purple solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (PCy₃)(C₅H₄BrN)₂(Cl)₂Ru═CH—CH═C(CH₃)₂20 as a purple powder (1.4 gram, 67% yield).

[0161] Synthesis of (PCy₃)(C₁₁H₉N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0162] Complex 3 (2.0 grams) was dissolved in toluene (10 mL), and 4-phenylpyridine (1.55 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to brown was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a brown solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (PCy₃)(C₁₁H₉N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂21 as a brown powder (1.6 gram, 77% yield).

[0163] Synthesis of (PCy₃)(C₆H₇N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0164] Complex 3 (2.0 grams) was dissolved in toluene (10 mL), and 4-methylpyridine (0.93 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (PCy₃)(C₆H₇N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂22 as a green powder (1.6 gram, 91% yield).

[0165] Synthesis of (PCy₃)(C₅H₅N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0166] Complex 3 (2.0 grams) was dissolved in toluene (10 mL), and pyridine (0.79 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from dark purple to light green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a light green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (PCy₃)(C₅H₅N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂23 as a light green powder (1.4 gram, 83% yield).

[0167] A 75 gram mass of DCPD (containing about 24% trimerized DCPD) was polymerized using (PCy₃)(C₅H₁N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂=0.0237 grams at a DCPD:Ru ratio of (about 15,000:1) at a starting temperature of about 52.2° C.

[0168] Result

[0169] Time to reach maximum temperature (T_max)=1166 seconds. T_max=60.2° C.

[0170] A 75 gram mass of DCPD (containing about 24% trimerized DCPD) was polymerized using (PCy₃)(C₅H₅N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂=0.0237 grams in the presence of sImesHCCl₃=0.0297 grams at a DCPD:Ru:sImesHCCl₃ratio of (about 15,000:1:2) at a starting temperature of about 49.4° C. Result: Time to reach maximum temperature (T_max)=715 seconds. T_max=173.3° C.

[0171] Synthesis of (IMesH₂)(C₁₁H₉N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0172] Complex 4 (1.5 grams) was dissolved in toluene (10 mL), and 4-phenylpyridine (1.13 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 2 hours at about 20° C. to about 25° C. during which time a color change from brown to green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₁₁H₉N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂24 as a green powder (0.9 gram, 58% yield).

[0173] Synthesis of (IMesH₂)(C₉H₁₂N₂)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0174] Complex 4 (1.5 grams) was dissolved in toluene (10 mL), and 4-pyrrolidinopyridine (1.08 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 2 hours at about 20° C. to about 25° C. during which time a color change from brown to green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₉H₁₂N₂)₂(Cl)₂Ru═CH—CH═C(CH₃)₂25 as a green powder (1.0 gram, 65% yield).

[0175] ¹H NMR (300 MHz, CD₂Cl₂): δ19.05 (d, 1H, CH—CH═C(CH₃)₂, J_HH=11 Hz), 8.14 (br. s, 2H, pyridine CH), 7.69 (d, 1H, CH—CH═C(CH₃)₂, J_HH=11 Hz), 7.36 (d, 2H, pyridine CH, J_HH=6.0 Hz), 7.04 (s, 2H, Mes CH), 6.81 (s, 2H, Mes CH), 6.36 (br. s, 2H, pyridine CH), 6.12 (d, 2H, pyridine CH, J_HH=6.0 Hz), 4.06 (m. d, 4H, NCH₂CH₂N), 3.29 (br. s, 4H, pyrrolidine CH₂), 3.23 (br. s, 4H, pyrrolidine CH₂), 2.55-2.12 (multiple peaks, 18H, Mes CH₃), 2.02 (br. s, 4H, pyrrolidine CH₂), 1.97 (br. s, 4H, pyrrolidine CH₂), 1.10 (s, 3H, CH—CH═C(CH₃)₂), 1.08 (s, 3H, CH—CH═C(CH₃)₂).

[0176] A 75 gram mass of DCPD (containing about 24% trimerized DCPD) was polymerized using (IMesH₂)(C₉H₁₂N₂)₂(Cl)₂Ru═CH—CH═C(CH₃)₂=0.0147 grams at a DCPD:Ru ratio of (about 30,000:1) at a starting temperature of about 24.7° C. Result: Time to reach maximum temperature (T_max)=181 seconds. T_max=200.9° C. Glass transition temperature measured by thermal mechanical analysis (TMA)=144° C. Percent residual monomer (toluene extraction at room temperature)=3.93%.

[0177] Synthesis of (IMesH₂)(C₁₀H₈N₂)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0178] Complex 4 (1.5 grams) was dissolved in toluene (10 mL), and 4,4′-bipyridine (0.57 grams, 2 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 2 hours at about 20° C. to about 25° C. during which time no dramatic color change from brown was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a brown solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₁₀H₈N₂)₂(Cl)₂Ru═CH—CH═C(CH₃)₂26 as a brown powder (1.0 gram, 64% yield).

[0179] Synthesis of (IMesH₂)(C₇H₁₀N₂)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0180] Complex 4 (1.5 grams) was dissolved in toluene (10 mL), and 4-dimethylaminopyridine (0.89 grams, 4 mol equivalents) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 2 hours at about 20° C. to about 25° C. during which time a color change from brown to green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford (IMesH₂)(C₇H₁₀N₂)₂(Cl)₂Ru═CH—CH═C(CH₃)₂27 as a green powder (0.9 gram, 63% yield).

[0181] ¹H NMR (500 MHz, CD₂Cl₂): δ19.10 (d, 1H, CH—CH═C(CH₃)₂, J_HH=11.5 Hz,), 8.18 (br. s, 2H, pyridine CH), 7.69 (d, 1H, CH—CH═C(CH₃)₂, J_HH=11.5 Hz), 7.41 (br. s, 2H, Mes CH), 6.49 (br. s, 2H, pyridine CH), 6.24 (br. s, 2H, Mes CH), 4.06 (br. m, 4H, NCH₂CH₂N), 2.99 (s, 6H, pyridine CH₃), 2.59 (s, 6H, pyridine CH₃), 2.36-2.12 (multiple peaks, 18H, Mes CH₃), 1.07 (s, 3H, CH—CH═C(CH₃)₂), 1.06 (s, 3H, CH—CH═C(CH₃)₂).

[0182] A 75 gram mass of DCPD (containing about 24% trimerized DCPD) was polymerized using (IMesH₂)(C₇H₁₀N₂)₂(Cl)₂Ru═CH—CH═C(CH₃)₂=0.0138 grams at a DCPD:Ru ratio of (about 30,000:1) at a starting temperature of about 24.2° C. Result: Time to reach maximum temperature (T_max)=200 seconds. T_max=200.9° C. Glass transition temperature measured by thermal mechanical analysis (TMA)=145° C. Percent residual monomer (toluene extraction at room temperature) 4.57%.

[0183] A 50 gram mass of hexylnorbornene was polymerized using (IMesH₂)(C₇H₁₀N₂)₂(Cl)₂Ru═CH—CH═C(CH₃)₂=0.0074 grams at a H_xN:Ru ratio of (about 30,000:1) at a starting temperature of about 16.2° C.

[0184] Result

[0185] Time to reach maximum temperature (T_max)=182 seconds. T_max=141.7° C.

[0186] Synthesis of (IMesH₂)(C₅H₅N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0187] Complex 4 (0.5 grams) was dissolved in toluene (10 mL), and pyridine (10 mL) was added. The reaction flask was purged with argon and the reaction mixture was stirred for approximately 12 hours at about 20° C. to about 25° C. during which time a color change from brown to brown-green was observed. The reaction mixture was transferred into 75 mL of cold (about 0° C.) pentane, and a green solid precipitated. The precipitate was filtered, washed with 4×20 mL of cold pentane, and dried under vacuum to afford 28 (IMesH₂)(C₅H₅N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂as green crystals (0.2 gram, 47% yield).

[0188] ¹H NMR (300 MHz, CD₂Cl₂): δ19.19 (d, 1H, Ru═CH—CH═C(CH₃)₂, J_HH=10.8 Hz), 8.60-6.85 (multiple peaks, 15H, pyridine, Mes CH, Ru═CH—CH═C(CH₃)₂, 4.07 (m, 4H, NCH₂CH₂N), 2.58-2.27 (multiple peaks, 12H, Mes CH₃), 2.31 (s, 3H, Mes CH₃), 2.19 (s, 3H, Mes CH₃), 1.09 (s, 3H, CH—CH═C(CH₃)₂), 1.08 (s, 3H, CH—CH═C(CH₃)₂).

[0189] A 75 gram mass of DCPD (containing about 24% trimerized DCPD) was polymerized using (IMesH₂)(C₅H₅N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂=0.0123 grams at a DCPD:Ru ratio of (about 30,000:1) at a starting temperature of about 12.5° C. Result: Time to reach maximum temperature (T_max)=129 seconds. T_max=197.1° C. Glass transition temperature measured by thermal mechanical analysis (TMA)=157° C. Percent residual monomer (toluene extraction at room temperature)=2.13%.

[0190] Synthesis of (IMesH₂)(C₅H₅N)₂(Cl)₂Ru═CHPh (31)

[0191] Complex 1 (4.0 g, 4.7 mmol) was dissolved in toluene (10 mL), and pyridine (30 mL, 0.37 mol) was added. The reaction was stirred for 10 min during which time a color change from red to bright green was observed. The reaction mixture was cannula transferred into 100 mL of cold (−10° C.) pentane, and a green solid precipitated. The precipitate was filtered, washed with 4×50 mL of pentane, and dried under vacuum to afford 31 as a green powder (2.9 g, 85% yield). Samples for elemental analysis were prepared by recrystallization from C₆H₆/pentane followed by drying under vacuum. These samples analyze as the monopyridine adduct (IMesH₂)(C₅H₅N)(Cl)₂Ru═CHPh, probably due to loss of pyridine under vacuum. ¹H NMR (C₆D₆): δ19.67 (s, 1H, CHPh), 8.84 (br. s, 2H, pyridine), 8.39 (br. s, 2H, pyrdine), 8.07 (d, 2H, ortho CH, J_HH=8 Hz), 7.15 (t, 1H, para CH, J_HH=7 Hz), 6.83-6.04 (br. multiple peaks, 9H, pyridine, Mes CH), 3.37 (br. d, 4H, CH₂CH₂), 2.79 (br. s, 6H, Mes CH₃), 2.45 (br. s, 6H, Mes CH₃), 2.04 (br. s, 6H, Mes CH₃). C{¹H} NMR (C₆D₆): δ314.90 (m, Ru═CHPh), 219.10 (s, Ru—C(N)₂), 152.94, 150.84, 139.92, 138.38, 136.87, 135.99, 134.97, 131.10, 130.11, 129.88, 128.69, 123.38, 51.98, 51.37, 21.39, 20.96, 19.32. Anal. Calcd for C₃₃H₃₇N₃Cl₂Ru: C, 61.20; H, 5.76; N, 6.49. Found: C, 61.25; H, 5.76; N, 6.58.

[0192] Represententative Synthesis of a Phosphine Complex: IMesH₂)(PPh₃)(Cl)₂Ru═CHPh (41)

[0193] Complex 31 (150 mg, 0.21 mmol) and PPh₃(76 mg, 0.28 mmol) were combined in benzene (10 mL) and stirred for 10 min. The solvent was removed under vacuum, and the resulting brown residue was washed with 4×20 mL of pentane and dried in vacuo. Complex 41 was obtained as a brownish powder (125 mg, 73% yield). ³¹p {¹H} NMR (C₆D₆): δ37.7 (s). ¹H NMR (C₇D₈): δ19.60 (s, ¹H, Ru═CHPh), 7.70 (d, 2H, ortho CH, J_HH=8 Hz), 7.29-6.71 (multiple peaks, 20H, PPh₃, para CH, meta CH, and Mes CH), 6.27 (s, 2H, Mes CH), 3.39 (m, 4H, CH₂CH₂), 2.74 (s, 6H, ortho CH₃), 2.34 (s, 6H, ortho CH₃), 2.23 (s, 3H, para CH₃), 1.91 (s, 3H, para CH₃). ¹³C{¹H} NMR (C₆D₆): δ305.34 (m, Ru—CHPh), 219.57 (d, Ru—C(N)₂, J_CP=92 Hz), 151.69 (d, J_CP=4 Hz), 139.68, 138.35, 138.10, 138.97, 137.78, 135.89, 135.21, 135.13, 131.96, 131.65, 131.36, 130.47, 129.83, 129.59 (d, J_CP=2 Hz), 129.15, 128.92, 128.68, 128.00, 52.11 (d, J_CP=4 Hz), 51.44 (d, J_CP=2 Hz), 21.67, 21.35, 21.04, 19.21. Anal. Calcd for C₄₆H₄₇N₂Cl₂PRu: C, 66.50; H, 5.70; N, 3.37. Found: C, 66.82; H, 5.76; N, 3.29.

[0194] Synthesis of (IMesH₂)(O^tBu)₂Ru═CHPh (42)

[0195] Complex 31 (7.5 mg, 0.010 mmol) and KO^tBu (3 mg, 0.027 mmol) were combined in C₆D₆(0.6 mL) in an NMR tube under nitrogen. The reaction mixture was allowed to stand for 15-20 min, during which time a color change from green to dark red was was observed, and NMR spectra were recorded after 30 min. ¹H NMR (C₆D₆): δ16.56 (s, 1H, Ru═CHPh), 7.63 (d, 2H, ortho CH, J_HH=7 Hz), 7.2-7.1 (multiple peaks, 3H, meta CH and ortho CH), 6.97 (s, 4H, Mes CH), 3.43 (s, 4H CH₂CH₂), 2.59 (s, 12H, ortho CH₃), 2.29 (s, 6H, para CH₃), 1.18 (s, 18H, ^tBu).

[0196] Synthesis of Tp(IMesH₂)(Cl)Ru═CHPh (43)

[0197] KTp (87 mg, 0.34 mmol) and complex 31 (125 mg, 0.17 mmol) were combined in CH₂Cl₂(10 mL) and stirred for 1 hour. Pentane (20 mL) was added to precipitate the salts, and the reaction was stirred for an additional 30 min and then cannula filtered. The resulting bright green solution was concentrated, and the solid residue was washed with pentane (2×10 mL) and methanol (2×10 mL) and dried under vacuum to afford 43 (84 mg, 66% yield) as an analytically pure green powder. ¹H NMR (CD₂Cl₂): δ18.73 (s, 1H, Ru═CHPh), 7.87 (d, 1H, Tp, J_HH=2.4 Hz), 7.41 (d, 1H, Tp, J_HH=2.1 Hz), 7.35-7.30 (multiple peaks, 3H, Tp and para CH), 7.08 (d, 1 h, Tp, J_HH=1.5 Hz), 6.82 (br. s, 5H, Mes CH, ortho CH and meta CH), 6.24 (br. s, 3H, Mes CH), 6.16 (t, 1H, Tp, J_HH=1.8 Hz) 5.95 (d, 1H, Tp, J_HH=1.5 Hz), 5.69 (t, 1H, Tp, J_HH=2.4 Hz), 5.50 (t, 1H, Tp, J_HH=1.8 Hz), 3.77 (br. d, 4H, CH₂CH₂), 2.91-0.893 (br. multiple peaks, 18H, ortho CH₃, para CH₃). ¹³C{¹H} (CD₂Cl₂): δ324.29 (m, Ru═CHPh), 220.57 (s, Ru—C(N)₂), 151.50, 146.08, 145.39, 142.07, 137.94, 136.57, 134.41, 133.18, 130.60 (br), 129.55, 127.98, 106.41, 105.19, 104.51, 53.77 (br), 21.26, 20.32 (br). Anal. Calcd for C₃₇H₄₂N₈C1BRu: C, 59.56; H, 5.67; N, 15.02. Found: C, 59.20; H, 5.67; N, 14.72.

[0198] Kinetics of the Reaction of 1 with C₅D₅N

[0199] In a cuvette fitted with a rubber septum, a solution of 1 (0.88 mM) in toluene (1.6 mL) was prepared. This solution was allowed to thermally equilibrate in the Uv-vis spectrometer at 20° C. Neat pyridine-d5 (25-100 μL) was added via microsyringe, and the reaction kinetics was followed by monitoring the disappearance of starting material (502 nm). For each run, the data were collected over 5 half-lives and were fitted to a first-order expoential. Typical R²values for the exponential curve fits were greater than 0.999.

[0200] X-ray Crystal Structure of 31

[0201] Crystal, intensity collection, and refinement details were summarized in Table 1. The selected crystal was mounted on a glass fiber with Paratone-N oil and transferred to a Bruker SMART 1000 CCD area detector equipped with a Crystal Logic CL24 low-temperature device. Data were collected with ω-scans at seven φ values and subsequently processed with SAINT. No absorption or decay corrections were applied. SHELXTL was used to solve (by direct methods and subsequent difference Fourier maps) and to refine (full-matrix least-squares on F²) the structure. There are two molecules in the asymmetric unit. All non-hydrogen atoms were refined anisotropically; the hydrogen atoms were placed at calculated positions with U_isovalues based on the U_eqof the attached atom. Pertinent bond lengths and angles for one molecule are presented in Table 2.

[0202] Synthesis of (IMes)(C₅H₅N)₂(Cl)₂Ru═CHPh

[0203] In a nitrogen filled glovebox, 0.120 g (0.142 mmol) of (IMes)(PCy₃)C₁₂Ru═CHPh were dissolved in 1 mL of pyridine (large excess). The solution, which turned green immediately, was stirred at room temperature for 30 minutes. Then 20 mL of hexanes was added, and the flask was stored at −10° C. overnight. The supernatant was decanted from the green precipitate. The precipitate was washed twice with 20 mL hexanes and dried under vacuum to obtain 0.080 g (78% yield) of the bright green product (IMes)(py)₂Cl₂Ru═CHPh.

[0204] ¹H NMR (499.852 MHz, CD₂Cl₂): δ19.41 (s, 1H, CHPh), 8.74 (d, 2H, J=7.5 Hz), 7.96 (d, 2H, J=8.5 Hz), 7.70 (d, 2H, J=12.5 Hz), 7.55 (t, 1H, J=12.5 Hz), 7.44 (t, 1H, J=12 Hz), 7.33 (t, 1H, J=12 Hz), 7.06 (m, 3H), 7.05 (s, 2H), 6.83 (m, 1H), 6.79 (s, 6H), 2.28 (s, 6H, para CH₃on Mes), 2.22 (br s, 12H, ortho CH₃on Mes).

[0205] Characterization of (PCy₃)(C₅H₅N)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0206] ¹H NMR (499.852 MHz, C₆D₆): δ20.18 (overlapping dd, 1H, J=10.3 Hz, Ru═CH), 9.14 (br s, 4H, pyridine), 8.07 (d, 1H, J=11.5 Hz, —CH═), 6.68 (br s, 3H, pyridine), 6.43 (br m, 3H, pyridine), 2.54 (qt, 3H, J=11.5 Hz, PCy₃), 2.27 (d, 6H, J=11.5 Hz, PCy3), 1.91 (qt, 6H, J=12 Hz, PCy₃), 1.78 (d, 6H, J=10.5 Hz, PCy₃), 1.62 (m, 4H, PCy₃), 1.26 (s, 3H, CH₃), 1.23 (m, 8H, PCy₃), 0.75 (s, 3H, CH₃). ³¹P{¹H} NMR (121.392 MHz, C₆D₆): δ37.17 (s).

[0207] Observation of (Ph₃Tri)(C₇H₁₀N₂)₂(Cl)₂Ru═CH—CH═C(CH₃)₂

[0208] 0.020 g of (Ph₃Tri)(PCy₃)(Cl)₂Ru═CH—CH═C(CH₃)₂, 0.020 g of 4-dimethylaminopyridine (excess), and 0.060 mL of CD₂Cl₂were added to a screw-cap NMR tube. The ¹H NMR spectrum after 2 hours at room temperature showed complete conversion to the desired product (Ph₃Tri)(C₇H₁₀N₂)₂(Cl)₂Ru═CH—CH═C(CH₃)₂.

[0209] ¹H NMR (499.852 MHz, C₆D₆): δ18.57 (d, 1H, J=13 Hz, Ru═CH), 8.53 (d, J=8 Hz), 7.84 (d, J=6.5 Hz), 7.73-6.84 (multiplets), 6.26 (d, J=7 Hz), 6.09 (m), 6.04 (d, J=10.5 Hz), 6.01 (d, J=10.5 Hz), 5.42 (d, J=10.5 Hz), 5.38 (d, J=17.5 Hz), 3.22 (s), 3.01 (s), 2.99 (s), 1.73 (s), 1.23 (s).