Ring positionable about a periphery of a contact pad, semiconductor device components including same, and methods for positioning the ring around a contact pad

[0002] This application is a divisional of application Ser. No. 09/589,842, filed Jun. 8, 2000, pending.

[0003] 1. Field of the Invention

[0004] The present invention relates generally to semiconductor devices having rings disposed about the peripheries of the contact pads thereof and, more specifically, to the use of stereolithography to fabricate such rings around the contact pads either before or after securing solder balls to the contact pads. Particularly, the present invention pertains to rings disposed about the peripheries of the contact pads of a semiconductor device component for enhancing the reliability of solder balls secured to the contact pads. The present invention also relates to semiconductor device components including such rings.

[0005] 2. State of the Art

[0006] Some types of semiconductor devices, such as flip-chip type semiconductor dice, including ball grid array (BGA) packages, and chip-scale packages (CSPs), can be connected to higher level substrates by orienting these semiconductor devices face down over the higher level substrate. The contact pads of such semiconductor devices are typically connected directly to corresponding contact pads of the higher level substrate by solder balls.

[0007] Examples of solders that are known in the art to be useful in connecting semiconductor devices face down to higher level substrates include, but are not limited to, lead-tin (Pb/Sn) solder and silver-nickel (Ag/Ni) solder. For example, 63/37 type Pb/Sn solder bumps (i.e., solder having about 63% by weight lead and about 37% by weight tin) and 95/5 type Pb/Sn solder bumps (i.e., solder having about 95% by weight lead and about 5% by weight tin) have been used in flip-chip, ball grid array, and chip-scale packaging type attachments.

[0008] Assemblies that include semiconductor devices connected face down to higher level substrates using solder balls are subjected to thermal cycling during subsequent processing, testing thereof, and in normal use. As these assemblies undergo thermal cycling, the solder balls thereof are also exposed to wide ranges of temperatures, causing the solder balls to expand when heated and contract when cooled. Such expansion and contraction is especially problematic at the interface between a solder ball and the underlying contact pad. Expansion and contraction of solder balls can also occur at the interface between a solder ball and the contact pad of a higher level substrate to which, for example, a die is secured. Repeated variations in temperatures can cause solder fatigue, which can reduce the strength of the solder balls, cause the solder balls to crack and fail, and diminish the reliability of the solder balls as mechanical and electrical connection elements.

[0009] In an attempt to increase the reliability with which solder balls connect semiconductor devices face down to higher level substrates, resins have been applied to semiconductor devices to form rings around the bases of the solder balls protruding from the semiconductor devices. These resinous supports laterally contact the bases of the solder balls to enhance the reliability thereof. The resinous supports are applied to a semiconductor device after solder balls have been secured to the contact pads of the semiconductor device and before the semiconductor device is connected face down to a higher level substrate. As those of skill in the art are aware, however, the shapes of solder balls can change when bonded to the contact pads of a substrate, particularly after reflow thereof. If the shapes of the solder balls change, the solder balls can fail to maintain contact with the resinous supports, which could thereby fail to protect or enhance the reliability of the solder balls.

[0010] The inventor is not aware of any art that discloses a method that can be used to fabricate support rings around the contact pads of a semiconductor device before, as well as after, solder balls are secured to the contact pads.

[0011] In the past decade, a manufacturing technique termed “stereolithography”, also known as “layered manufacturing”, has evolved to a degree where it is employed in many industries.

[0012] Essentially, stereolithography, as conventionally practiced, involves utilizing a computer to generate a three-dimensional (3-D) mathematical simulation or model of an object to be fabricated, such generation usually effected with 3-D computer-aided design (CAD) software. The model or simulation is mathematically separated or “sliced” into a large number of relatively thin, parallel, usually vertically superimposed layers, each layer having defined boundaries and other features associated with the model (and thus the actual object to be fabricated) at the level of that layer within the exterior boundaries of the object. A complete assembly or stack of all of the layers defines the entire object and surface resolution of the object is, in part, dependent upon the thickness of the layers.

[0013] The mathematical simulation or model is then employed to generate an actual object by building the object, layer by superimposed layer. A wide variety of approaches to stereolithography by different companies has resulted in techniques for fabrication of objects from both metallic and nonmetallic materials. Regardless of the material employed to fabricate an object, stereolithographic techniques usually involve disposition of a layer of unconsolidated or unfixed material corresponding to each layer within the object boundaries. This is followed by selective consolidation or fixation of the material to at least a partially consolidated, or semisolid, state in those areas of a given layer corresponding to portions of the object, the consolidated or fixed material also at that time being substantially concurrently bonded to a lower layer of the object to be fabricated. The unconsolidated material employed to build an object may be supplied in particulate or liquid form and the material itself may be consolidated or fixed or a separate binder material may be employed to bond material particles to one another and to those of a previously formed layer. In some instances, thin sheets of material may be superimposed to build an object, each sheet being fixed to a next lower sheet and unwanted portions of each sheet removed, a stack of such sheets defining the completed object. When particulate materials are employed, resolution of object surfaces is highly dependent upon particle size. When a liquid is employed, surface resolution is highly dependent upon the minimum surface area of the liquid which can be fixed and the minimum thickness of a layer that can be generated. Of course, in either case, resolution and accuracy of object reproduction from the CAD file is also dependent upon the ability of the apparatus used to fix the material to precisely track the mathematical instructions indicating solid areas and boundaries for each layer of material. Toward that end, and depending upon the layer being fixed, various fixation approaches have been employed, including particle bombardment (electron beams), disposing a binder or other fixative (such as by ink-jet printing techniques), or irradiation using heat or specific wavelength ranges.

[0014] An early application of stereolithography was to enable rapid fabrication of molds and prototypes of objects from CAD files. Thus, either male or female forms on which mold material might be disposed might be rapidly generated. Prototypes of objects might be built to verify the accuracy of the CAD file defining the object and to detect any design deficiencies and possible fabrication problems before a design was committed to large-scale production.

[0015] In more recent years, stereolithography has been employed to develop and refine object designs in relatively inexpensive materials and has also been used to fabricate small quantities of objects where the cost of conventional fabrication techniques is prohibitive for the same, such as in the case of plastic objects conventionally formed by injection molding. It is also known to employ stereolithography in the custom fabrication of products generally built in small quantities or where a product design is rendered only once. Finally, it has been appreciated in some industries that stereolithography provides a capability to fabricate products, such as those including closed interior chambers or convoluted passageways, which cannot be fabricated satisfactorily using conventional manufacturing techniques. It has also been recognized in some industries that a stereolithographic object or component may be formed or built around another, pre-existing object or component to create a larger product.

[0016] However, to the inventor's knowledge, stereolithography has yet to be applied to mass production of articles in volumes of thousands or millions, or employed to produce, augment or enhance products including other, pre-existing components in large quantities, where minute component sizes are involved, and where extremely high resolution and a high degree of reproducibility of results is required. In particular, the inventor is not aware of the use of stereolithography to fabricate peripheral rings around the contact pads of semiconductor devices, such as flip-chip type semiconductor devices or ball grid array packages. Furthermore, conventional stereolithography apparatus and methods fail to address the difficulties of precisely locating and orienting a number of pre-existing components for stereolithographic application of material thereto without the use of mechanical alignment techniques or to otherwise assuring precise, repeatable placement of components.

[0017] The present invention includes a dielectric ring that surrounds the periphery of a contact pad of a semiconductor device, semiconductor device components including such rings, and methods for fabricating the rings.

[0018] A ring incorporating teachings of the present invention surrounds the periphery of a contact pad exposed at the surface of a semiconductor device component, such as a semiconductor die, a chip-scale package substrate, or a carrier substrate. The ring protrudes from the surface of the semiconductor device component. If the ring is fabricated before a solder ball is secured to the contact pad, at least a portion of the surrounded contact pad is exposed through an aperture defined by the ring.

[0019] Since the ring protrudes from the surface of the semiconductor device component, when a solder ball is bonded or otherwise secured to the contact pad exposed through the ring, the ring laterally surrounds at least a portion of the solder ball. The ring is preferably configured to substantially conformably contact a solder ball surrounded thereby so as to laterally support at least the contacted portion of the solder ball. Such conformance is enhanced during reflow of the solder ball, where any substantial voids between the solder and the interior of the ring are eliminated. Accordingly, during thermal cycling of the semiconductor device, the ring accommodates expansion and contraction of the solder ball and, most particularly, the portion thereof that contacts and is metallurgically secured to the underlying contact pad, the ring thereby reducing the occurrence of solder fatigue. In addition, use of rings according to the present invention, which may be of substantial height or protrusion from a substrate so as to encompass the solder balls at or approaching their largest diameters, may eliminate the need for an insulative underfill conventionally applied between a die and a higher level substrate.

[0020] Another significant advantage of the rings of the present invention is the containment of the solder of the balls, in the manner of a dam, during solder reflow, thus preventing contamination of the passivation layer surrounding the contact pads.

[0021] Fabricating the ring. In a preferred embodiment of the method, a computer-controlled, 3-D CAD-initiated process known as “stereolithography” or “layered manufacturing” is used to fabricate the ring. When stereolithographic processes are employed, each ring is formed as either a single layer or a series of superimposed, contiguous, mutually adhered layers of material.

[0022] The stereolithographic method of fabricating the rings of the present invention preferably includes the use of a machine vision system to locate the semiconductor devices or other substrates on which the rings are to be fabricated, as well as the features or other components on or associated with the semiconductor devices or other substrates (e.g., solder bumps, contact pads, conductor traces, etc.). The use of a machine vision system directs the alignment of a stereolithography system with each semiconductor device or other substrate for material disposition purposes. Accordingly, the semiconductor devices or other substrates need not be precisely mechanically aligned with any component of the stereolithography system to practice the stereolithographic embodiment of the method of the present invention.

[0023] In a preferred embodiment, the rings to be fabricated upon or positioned upon and secured to a semiconductor device component in accordance with the invention are fabricated using precisely focused electromagnetic radiation in the form of an ultraviolet (UV) wavelength laser under control of a computer and responsive to input from a machine vision system, such as a pattern recognition system, to fix or cure selected regions of a layer of a liquid photopolymer material disposed on the semiconductor device or other substrate.

[0024] The rings of the present invention may be fabricated around the contact pads of the semiconductor device component either before or after solder balls are bonded or otherwise secured to the contact pads.

[0025] Other features and advantages of the present invention will become apparent to those of skill in the art through consideration of the ensuing description, the accompanying drawings, and the appended claims.

[0026] The accompanying drawings illustrate exemplary embodiments of the invention, wherein some dimensions may be exaggerated for the sake of clarity, and wherein:

[0027] FIG. 1 is an enlarged perspective view of a semiconductor device having rings positioned around the exposed contact pads thereof;

[0028] FIG. 2 is a cross-section taken along line 2—2 of FIG. 1, depicting the apertures of the rings;

[0029] FIG. 3 is a cross-sectional view illustrating the face-down connection of the semiconductor device of FIGS. 1 and 2 to a higher level substrate;

[0030] FIG. 4 is an enlarged perspective view of another semiconductor device having rings positioned around the contact pads thereof, each ring laterally surrounding a portion of a solder ball bonded to the surrounded contact pad;

[0031] FIG. 5 is a cross-section taken along line 5—5 of FIG. 4, depicting solder balls extending through and laterally supported by the rings;

[0032] FIG. 6 is a cross-sectional view illustrating the face-down connection of the semiconductor device of FIGS. 4 and 5 to a higher level substrate;

[0033] FIG. 7 is a perspective view of a portion of a wafer having a plurality of semiconductor devices thereon, depicting rings being fabricated around each of the contact pads of the semiconductor devices at the wafer level;

[0034] FIG. 8 is a schematic representation of an exemplary stereolithography apparatus that can be employed in the method of the present invention to fabricate the rings of the present invention; and

[0035] FIG. 9 is a partial cross-sectional side view of a semiconductor device disposed on a platform of a stereolithographic apparatus for the formation of rings around the contact pads of the semiconductor device.

[0036] With reference to FIGS. 1 and 2, a semiconductor device 10 having contact pads 12 on a surface 14 thereof is illustrated. Semiconductor device 10 can be a semiconductor die, partial wafer, wafer, or other large-scale substrate of semiconductor material, a chip-scale package, a ball grid array package, a carrier substrate, or any other type of semiconductor device component having contact pads to which solder balls can be attached.

[0037] As illustrated, a ring 50 surrounds the periphery of each contact pad 12. Each ring 50 defines an aperture 52 through which at least a portion of the surrounded contact pad 12 is exposed. Each ring 50 protrudes from surface 14 of semiconductor device 10 so as to laterally surround and contact at least a portion of a solder ball to be bonded or otherwise secured to bond pad 12 and to support that portion of the solder ball to prevent fatigue thereof during thermal cycling of semiconductor device 10.

[0038] Referring now to FIG. 3, semiconductor device 10 is shown in a face-down orientation over a higher level substrate 30. Substrate 30 has contact pads or terminals 32 exposed at a surface 34 thereof. Contact pads 32 are preferably arranged so as to align with corresponding ones of contact pads 12 upon positioning semiconductor device 10 face down over substrate 30. Each contact pad 12 of semiconductor device 10 is electrically connected to its corresponding contact pad 32 of substrate 30 by way of a solder ball 20.

[0039] As will be explained in greater detail below, rings 50 are at least partially fabricated prior to connecting solder balls 20 to contact pads 12. As depicted in FIG. 3, a base portion 22 of each solder ball 20, which is bonded or otherwise secured to the contact pad 12 exposed through aperture 52 of ring 50, has a shape that is complementary to the configuration of aperture 52. Thus, each ring 50 contacts the solder ball 20 that extends through aperture 52.

[0040] With continued reference to FIG. 3, semiconductor device 10 is connected face down to a higher level substrate 30, such as a carrier substrate. Solder balls 20 connect contact pads 12 of semiconductor device 10 to corresponding contact pads 32 exposed at surface 34 of substrate 30. Rings 50 contact solder balls 20 so as to laterally support and protect at least the contacted portions of solder balls 20.

[0041] As depicted in FIG. 3, rings 54 can also be secured or formed around contact pads 32 of substrate 30. Rings 54 contact and laterally support the contacted portions of solder balls 20 so as to accommodate expansion and contraction of at least the portions of solder balls 20 contacting contact pads 32 during testing or use of semiconductor device 10 and to, therefore, prevent solder fatigue at the interface between solder balls 20 and contact pads 32.

[0042] FIGS. 4 and 5 illustrate another semiconductor device 10, which has solder balls 20′ protruding from each of the contact pads 12 on the surface 14 thereof. The portion of each solder ball 20′ adjacent surface 14 and the periphery of each bond pad 12 is laterally surrounded by another embodiment of ring 50′, which protrudes from surface 14. Rings 50′ are fabricated after solder balls 20′ have been secured to contact pads 12.

[0043] As shown in FIG. 5, solder ball 20′ extends through an aperture 52′ of ring 50′ to contact pad 12. Ring 50′ contacts the sides of the portion of solder ball 20′ extending through aperture 52′. FIG. 5 also depicts portions of ring 50′ located beneath solder ball 20′. These portions of ring 50′ are referred to herein as “shadowed” areas 54′.

[0044] Turning now to FIG. 6, semiconductor device 10 is depicted as being invertedly disposed over and connected to a higher level substrate 30. Solder balls 20′ connect each contact pad 12 of semiconductor device 10 to a corresponding contact pad 32 exposed at a surface 34 of substrate 30. As depicted, rings 50′ prevent material of solder balls 20′ from contacting surface 14 of semiconductor device 10.

[0045] FIG. 7 illustrates rings 50 on semiconductor devices 10, in this case semiconductor dice that have yet to be singulated, or diced, from a wafer 72 or from a portion of a wafer 72. Each semiconductor device 10 on wafer 72 is separated from adjacent semiconductor devices 10 by a street 74.

[0046] While rings 50, 50′ are preferably substantially simultaneously fabricated on or secured to a collection of semiconductor devices 10, such as prior to singulating semiconductor dice from a wafer 72, rings 50, 50′ can also be fabricated on or secured to collections of individual semiconductor devices 10 or other substrates, such as substrate 30 (on which rings 54 would be fabricated), or to individual semiconductor devices 10 or other substrates. As another alternative, rings 50, 50′ can be substantially simultaneously fabricated on or secured to a collection of more than one type of semiconductor device 10 or other substrate (e.g., rings 54 on substrate 30).

[0047] Rings 50, 50′ can be fabricated directly on semiconductor devices 10. Alternatively, rings 50 and can be fabricated separately from semiconductor devices 10, then secured thereto as known in the art, such as by the use of a suitable adhesive.

[0048] Rings 50, 50′ are preferably fabricated from a photo-curable polymer, or “photopolymer”, by stereolithographic processes. When fabricated directly on a semiconductor device 10, rings 50, 50′ can be made either before or after solder balls 20, 20′ are connected to contact pads 12 of semiconductor device 10.

[0049] For simplicity, the ensuing description is limited to an explanation of a method of fabricating rings 50 on a semiconductor device 10 prior to securing solder balls 20 to contact pads 12 of semiconductor device 10. As should be appreciated by those of skill in the art, however, the method described herein is also useful for fabricating rings 50′ on semiconductor device 10 and for fabricating rings 54 on substrate 30, as well as for fabricating rings 50′ on one or more semiconductor devices 10 or other substrates having solder balls 20′ already secured to the contact pads 12 thereof.

[0050] FIG. 8 schematically depicts various components and operation of an exemplary stereolithography apparatus 80 to facilitate the reader's understanding of the technology employed in implementation of the method of the present invention, although those of ordinary skill in the art will understand and appreciate that apparatus of other designs and manufacture may be employed in practicing the method of the present invention. The preferred, basic stereolithography apparatus for implementation of the method of the present invention, as well as operation of such apparatus, are described in great detail in United States Patents assigned to 3D Systems, Inc., of Valencia, Calif., such patents including, without limitation, U.S. Pat. Nos. 4,575,330; 4,929,402; 4,996,010; 4,999,143; 5,015,424; 5,058,988; 5,059,021; 5,059,359; 5,071,337; 5,076,974; 5,096,530; 5,104,592; 5,123,734; 5,130,064; 5,133,987; 5,141,680; 5,143,663; 5,164,128; 5,174,931; 5,174,943; 5,182,055; 5,182,056; 5,182,715; 5,184,307; 5,192,469; 5,192,559; 5,209,878; 5,234,636; 5,236,637; 5,238,639; 5,248,456; 5,256,340; 5,258,146; 5,267,013; 5,273,691; 5,321,622; 5,344,298; 5,345,391; 5,358,673; 5,447,822; 5,481,470; 5,495,328; 5,501,824; 5,554,336; 5,556,590; 5,569,349; 5,569,431; 5,571,471; 5,573,722; 5,609,812; 5,609,813; 5,610,824; 5,630,981; 5,637,169; 5,651,934; 5,667,820; 5,672,312; 5,676,904; 5,688,464; 5,693,144; 5,695,707; 5,711,911; 5,776,409; 5,779,967; 5,814,265; 5,850,239; 5,854,748; 5,855,718; 5,855,836; 5,885,511; 5,897,825; 5,902,537; 5,902,538; 5,904,889; 5,943,235; and 5,945,058. The disclosure of each of the foregoing patents is hereby incorporated herein by this reference.

[0051] With continued reference to FIG. 8 and as noted above, a 3-D CAD drawing of an object to be fabricated in the form of a data file is placed in the memory of a computer 82 controlling the operation of apparatus 80 if computer 82 is not a CAD computer in which the original object design is effected. In other words, an object design may be effected in a first computer in an engineering or research facility and the data files transferred via wide or local area network, tape, disc, CD-ROM, or otherwise, as known in the art to computer 82 of apparatus 80 for object fabrication.

[0052] The data is preferably formatted in an STL (for STereoLithography) file, STL being a standardized format employed by a majority of manufacturers of stereolithography equipment. Fortunately, the format has been adopted for use in many solid-modeling CAD programs, so translation from another internal geometric database format is often unnecessary. In an STL file, the boundary surfaces of an object are defined as a mesh of interconnected triangles.

[0053] Apparatus 80 also includes a reservoir 84 (which may comprise a removable reservoir interchangeable with others containing different materials) of an unconsolidated material 86 to be employed in fabricating the intended object. In the currently preferred embodiment, the unconsolidated material 86 is a liquid, photo-curable polymer, or “photopolymer”, that cures in response to light in the UV wavelength range. The surface level 88 of material 86 is automatically maintained at an extremely precise, constant magnitude by devices known in the art responsive to output of sensors within apparatus 80 and preferably under control of computer 82. A support platform or elevator 90, precisely vertically movable in fine, repeatable increments in direction 116 responsive to control of computer 82, is located for movement downward into and upward out of material 86 in reservoir 84.

[0054] An object may be fabricated directly on platform 90 or on a substrate disposed on platform 90. When the object is to be fabricated on a substrate disposed on platform 90, the substrate may be positioned on platform 90 and secured thereto by way of one or more base supports 122 (see FIG. 9). Such base supports 122 may be fabricated before or simultaneously with the stereolithographic fabrication of one or more objects on platform 90 or a substrate disposed thereon. These supports 122 may support, or prevent lateral movement of, the substrate relative to a surface 100 of platform 90. Supports 122 may also provide a perfectly horizontal reference plane for fabrication of one or more objects thereon, as well as facilitate the removal of a substrate from platform 90 following the stereolithographic fabrication of one or more objects on the substrate. Moreover, where a so-called “recoater” blade 102 is employed to form a layer of material on platform 90 or a substrate disposed thereon, supports 122 can preclude inadvertent contact of recoater blade 102, to be described in greater detail below, with surface 100 of platform 90.

[0055] Apparatus 80 has a UV wavelength range laser plus associated optics and galvanometers (collectively identified as laser 92) for controlling the scan of laser beam 96 in the X-Y plane across platform 90. Laser 92 has associated therewith a mirror 94 to reflect beam 96 downwardly as beam 98 toward surface 100 of platform 90. Beam 98 is traversed in a selected pattern in the X-Y plane, that is to say, in a plane parallel to surface 100, by initiation of the galvanometers under control of computer 82 to at least partially cure, by impingement thereon, selected portions of material 86 disposed over surface 100 to at least a partially consolidated (e.g., semisolid) state. The use of mirror 94 lengthens the path of the laser beam, effectively doubling the same, and provides a more vertical beam 98 than would be possible if the laser 92 itself were mounted directly above platform surface 100, thus enhancing resolution.

[0056] Referring now to FIGS. 8 and 9, data from the STL files resident in computer 82 is manipulated to build an object, such as ring 50, illustrated in FIGS. 1-3 and 7, or base supports 122, one layer at a time. Accordingly, the data mathematically representing one or more of the objects to be fabricated are divided into subsets, each subset representing a slice or layer of the object. The division of data is effected by mathematically sectioning the 3-D CAD model into at least one layer, a single layer or a “stack” of such layers representing the object. Each slice may be from about 0.0001 to about 0.0300 inch thick. As mentioned previously, a thinner slice promotes higher resolution by enabling better reproduction of fine vertical surface features of the object or objects to be fabricated.

[0057] When one or more base supports 122 are to be stereolithographically fabricated, supports 122 may be programmed as a separate STL file from the other objects to be fabricated. The primary STL file for the object or objects to be fabricated and the STL file for base support(s) 122 are merged.

[0058] Before fabrication of a first layer for a support 122 or an object to be fabricated is commenced, the operational parameters for apparatus 80 are set to adjust the size (diameter if circular) of the laser light beam used to cure material 86. In addition, computer 82 automatically checks and, if necessary, adjusts, by means known in the art, the surface level 88 of material 86 in reservoir 84 to maintain the same at an appropriate focal length for laser beam 98. U.S. Pat. No. 5,174,931, referenced above and previously incorporated herein by reference, discloses one suitable level control system. Alternatively, the height of mirror 94 may be adjusted responsive to a detected surface level 88 to cause the focal point of laser beam 98 to be located precisely at the surface of material 86 at surface level 88 if level 88 is permitted to vary, although this approach is more complex. Platform 90 may then be submerged in material 86 in reservoir 84 to a depth equal to the thickness of one layer or slice of the object to be formed, and the liquid surface level 88 is readjusted as required to accommodate material 86 displaced by submergence of platform 90. Laser 92 is then activated so laser beam 98 will scan unconsolidated (e.g., liquid or powdered) material 86 disposed over surface 100 of platform 90 to at least partially consolidate (e.g., polymerize to at least a semisolid state) material 86 at selected locations, defining the boundaries of a first layer 122A of base support 122 and filling in solid portions thereof. Platform 90 is then lowered by a distance equal to thickness of second layer 122B and laser beam 98 scanned over selected regions of the surface of material 86 to define and fill in the second layer while simultaneously bonding the second layer to the first. The process may then be repeated as often as necessary, layer by layer, until base support 122 is completed. Platform 90 is then moved relative to mirror 94 to form any additional base supports 122 on platform 90 or a substrate disposed thereon or to fabricate objects upon platform 90, base support 122, or a substrate, as provided in the control software. The number of layers required to erect support 122 or one or more other objects to be formed depends upon the height of the object or objects to be formed and the desired layer thickness 108, 110. The layers of a stereolithographically fabricated structure with a plurality of layers may have different thicknesses.

[0059] If a recoater blade 102 is employed, the process sequence is somewhat different. In this instance, surface 100 of platform 90 is lowered into unconsolidated (e.g., liquid) material 86 below surface level 88 a distance greater than a thickness of a single layer of material 86 to be cured, then raised above surface level 88 until platform 90, a substrate disposed thereon, or a structure being formed on platform 90 or a substrate thereon is precisely one layer's thickness below blade 102. Blade 102 then sweeps horizontally over platform 90 or (to save time) at least over a portion thereof on which one or more objects are to be fabricated to remove excess material 86 and leave a film of precisely the desired thickness. Platform 90 is then lowered so that the surface of the film and material level 88 are coplanar and the surface of the unconsolidated material 86 is still. Laser 92 is then initiated to scan with laser beam 98 and define the first layer 130. The process is repeated, layer by layer, to define each succeeding layer 130 and simultaneously bond the same to the next lower layer 130 until all of the layers of the object or objects to be fabricated are completed. A more detailed discussion of this sequence and apparatus for performing the same is disclosed in U.S. Pat. No. 5,174,931, previously incorporated herein by reference.

[0060] As an alternative to the above approach to preparing a layer of material 86 for scanning with laser beam 98, a layer of unconsolidated (e.g., liquid) material 86 may be formed on surface 100 of support platform 90, on a substrate disposed on platform 90, or on one or more objects being fabricated by lowering platform 90 to flood material 86 over surface 100, over a substrate disposed thereon, or over the highest completed layer of the object or objects being formed, then raising platform 90 and horizontally traversing a so-called “meniscus” blade horizontally over platform 90 to form a layer of unconsolidated material having the desired thickness over platform 90, the substrate, or each of the objects being formed. Laser 92 is then initiated and a laser beam 98 scanned over the layer of unconsolidated material to define at least the boundaries of the solid regions the next higher layer of the object or objects being fabricated.

[0061] Yet another alternative to layer preparation of unconsolidated (e.g., liquid) material 86 is to merely lower platform 90 to a depth equal to that of a layer of material 86 to be scanned, and to then traverse a combination flood bar and meniscus bar assembly horizontally over platform 90, a substrate disposed on platform 90, or one or more objects being formed to substantially concurrently flood material 86 thereover and to define a precise layer thickness of material 86 for scanning.

[0062] All of the foregoing approaches to liquid material flooding and layer definition and apparatus for initiation thereof are known in the art and are not material to the practice of the present invention, therefore, no further details relating thereto will be provided herein.

[0063] In practicing the present invention, a commercially available stereolithography apparatus operating generally in the manner as that described above with respect to apparatus 80 of FIG. 8 is preferably employed, but with further additions and modifications as hereinafter described for practicing the method of the present invention. For example and not by way of limitation, the SLA-250/50HR, SLA-5000 and SLA-7000 stereolithography systems, each offered by 3D Systems, Inc., of Valencia, Calif., are suitable for modification. Photopolymers believed to be suitable for use in practicing the present invention include Cibatool SL 5170 and SL 5210 resins for the SLA-250/50HR system, Cibatool SL 5530 resin for the SLA-5000 and 7000 systems, and Cibatool SL 7510 resin for the SLA-7000 system. All of these photopolymers are available from Ciba Specialty Chemicals Corporation.

[0064] By way of example and not limitation, the layer thickness of material 86 to be formed, for purposes of the invention, may be on the order of about 0.0001 to 0.0300 inch, with a high degree of uniformity. It should be noted that different material layers may have different heights so as to form a structure of a precise, intended total height or to provide different material thicknesses for different portions of the structure. The size of the laser beam “spot” impinging on the surface of material 86 to cure the same may be on the order of 0.001 inch to 0.008 inch. Resolution is preferably ±0.0003 inch in the X-Y plane (parallel to surface 100) over at least a 0.5 inch×0.25 inch field from a center point, permitting a high resolution scan effectively across a 1.0 inch×0.5 inch area. Of course, it is desirable to have substantially this high a resolution across the entirety of surface 100 of platform 90 to be scanned by laser beam 98, such area being termed the “field of exposure”, and being substantially coextensive with the vision field of a machine vision system employed in the apparatus of the invention as explained in more detail below. The longer and more effectively vertical the path of laser beam 96/98, the greater the achievable resolution.

[0065] Referring again to FIG. 8, it should be noted that apparatus 80 useful in the method of the present invention includes a camera 140 which is in communication with computer 82 and preferably located, as shown, in close proximity to optics and mirror 94 located above surface 100 of support platform 90. Camera 140 may be any one of a number of commercially available cameras, such as capacitive-coupled discharge (CCD) cameras available from a number of vendors. Suitable circuitry as required for adapting the output of camera 140 for use by computer 82 may be incorporated in a board 142 installed in computer 82, which is programmed as known in the art to respond to images generated by camera 140 and processed by board 142. Camera 140 and board 142 may together comprise a so-called “machine vision system” and, specifically, a “pattern recognition system” (PRS), operation of which will be described briefly below for a better understanding of the present invention. Alternatively, a self-contained machine vision system available from a commercial vendor of such equipment may be employed. For example, and without limitation, such systems are available from Cognex Corporation of Natick, Mass. For example, the apparatus of the Cognex BGA Inspection Package™ or the SMD Placement Guidance Package™ may be adapted to the present invention, although it is believed that the MVS-8000™ product family and the Checkpoint® product line, the latter employed in combination with Cognex PatMax™ software, may be especially suitable for use in the present invention.

[0066] It is noted that a variety of machine vision systems are in existence, examples of which and their various structures and uses are described, without limitation, in U.S. Pat. Nos. 4,526,646; 4,543,659; 4,736,437; 4,899,921; 5,059,559; 5,113,565; 5,145,099; 5,238,174; 5,463,227; 5,288,698; 5,471,310; 5,506,684; 5,516,023; 5,516,026; and 5,644,245. The disclosure of each of the immediately foregoing patents is hereby incorporated by this reference.

[0067] In order to facilitate fabrication of one or more rings 50 in accordance with the method of the present invention with apparatus 80, a data file representative of the size, configuration, thickness and surface topography of, for example, a particular type and design of semiconductor device 10 or other substrate upon which one or more rings 50 are to be mounted is placed in the memory of computer 82. Also, if it is desired that the rings 50 be so positioned on semiconductor device 10 taking into consideration features of a higher level substrate 30 (see FIG. 3) to which semiconductor device 10 is to be connected, a data file representative of substrate 30 and the features thereof may be placed in memory.

[0068] One or more semiconductor devices 10, wafers 72 (see FIG. 7), or other substrates may be placed on surface 100 of platform 90 for fabrication of rings 50 around contact pads 12 thereof. If one or more semiconductor devices 10, wafers 72, or other substrates are to be held on or supported above platform 90 by stereolithographically formed base supports 122, one or more layers of material 86 are sequentially disposed on surface 100 and selectively altered by use of laser 92 to form base supports 122.

[0069] Camera 140 is then activated to locate the position and orientation of each semiconductor device 10, including those on a wafer 72 (see FIG. 7), or other substrate upon which rings 50 are to be fabricated. The features of each semiconductor device 10, wafer 72, or other substrate are compared with those in the data file residing in memory, the locational and orientational data for each semiconductor device 10, wafer 72, or other substrate then also being stored in memory. It should be noted that the data file representing the design, size, shape and topography for each semiconductor device 10 or other substrate may be used at this juncture to detect physically defective or damaged semiconductor devices 10 or other substrates prior to fabricating rings 50 thereon or before conducting further processing or assembly of semiconductor device 10 or other substrates. Accordingly, such damaged or defective semiconductor devices 10 or other substrates can be deleted from the process of fabricating rings 50, from further processing, or from assembly with other components. It should also be noted that data files for more than one type (size, thickness, configuration, surface topography) of each semiconductor device 10 or other substrate may be placed in computer memory and computer 82 programmed to recognize not only the locations and orientations of each semiconductor device 10 or other substrate, but also the type of semiconductor device 10 or other substrate at each location upon platform 90 so that material 86 may be at least partially consolidated by laser beam 98 in the correct pattern and to the height required to define rings 50 in the appropriate, desired locations on each semiconductor device 10 or other substrate.

[0070] Continuing with reference to FIGS. 8 and 9, wafer 72 or the one or more semiconductor devices 10 or other substrates on platform 90 may then be submerged partially below the surface level 88 of liquid material 86 to a depth greater than the thickness of a first layer of material 86 to be at least partially consolidated (e.g., cured to at least a semisolid state) to form the lowest layer 130 of each ring 50 at the appropriate location or locations on each semiconductor device 10 or other substrate, then raised to a depth equal to the layer thickness, surface 88 of material 86 being allowed to become calm. Photopolymers that are useful as material 86 exhibit a desirable dielectric constant, low shrinkage upon cure, are of sufficient (i.e., semiconductor grade) purity, exhibit good adherence to other semiconductor device materials, and have a similar coefficient of thermal expansion (CTE) to the material of solder balls 20 (FIG. 3) (e.g., solder or other metal or metal alloy). As used herein, the term “solder ball” may also be interpreted to encompass conductive or conductor filled epoxy. Preferably, the CTE of material 86 is sufficiently similar to that of solder balls 20 to prevent undue stressing thereof during thermal cycling of semiconductor device 10 or another substrate in testing, subsequent processing, and subsequent normal operation. Exemplary photopolymers exhibiting these properties are believed to include, but are not limited to, the above-referenced resins from Ciba Specialty Chemical Company. One area of particular concern in determining resin suitability is the substantial absence of mobile ions and, specifically, fluorides.

[0071] Laser 92 is then activated and scanned to direct beam 98, under control of computer 82, toward specific locations of surface 88 relative to each semiconductor device 10 or other substrate to effect the aforementioned partial cure of material 86 to form a first layer 50A of each ring 50. Platform 90 is then lowered into reservoir 84 and raised a distance equal to the desired thickness of another layer 50B of each ring 50 and laser 92 is activated to add another layer 50B to each ring 50 under construction. This sequence continues, layer by layer, until each of the layers of rings 50 have been completed.

[0072] In FIG. 9, the first layer of ring 50 is identified by numeral 50A and the second layer is identified by numeral 50B. Likewise, the first layer of base support 122 is identified by numeral 122A and the second layer thereof is identified by numeral 122B. As illustrated, both base support 122 and ring 50 have only two layers. Rings 50 with any number of layers are, however, within the scope of the present invention. The use of a large number of layers may be employed to substantially simulate the curvature of a solder ball to be encompassed thereby.

[0073] Each layer 50A, 50B of ring 50 is preferably built by first defining any internal and external object boundaries of that layer with laser beam 98, then hatching solid areas of ring 50 located within the object boundaries with laser beam 98. An internal boundary of a layer may comprise aperture 52, a through-hole, a void, or a recess in ring 50, for example. If a particular layer includes a boundary of a void in the object above or below that layer, then laser beam 98 is scanned in a series of closely-spaced, parallel vectors so as to develop a continuous surface, or skin, with improved strength and resolution. The time it takes to form each layer depends upon the geometry thereof, the surface tension and viscosity of material 86, and the thickness of that layer.

[0074] Alternatively, rings 50 may each be formed as a partially cured outer skin extending above surface 14 of semiconductor device 10 forming a dam within which unconsolidated material 86 can be contained. This may be particularly useful where the rings 50 protrude a relatively high distance 56 from surface 14. In this instance, support platform 90 may be submerged so that material 86 enters the area within the dam, raised above surface level 88, and then laser beam 98 activated and scanned to at least partially cure material 86 residing within the dam or, alternatively, to merely cure a “skin” comprising the contact surface aperture 52, a final cure of the material of the rings 50 being effected subsequently by broad-source UV radiation in a chamber or by thermal cure in an oven. In this manner, rings 50 of extremely precise dimensions may be formed of material 86 by apparatus 80 in minimal time.

[0075] When rings 50′, depicted in FIGS. 4-6, are being fabricated on a substrate, such as semiconductor device 10, having solder balls 20′ already secured to the contact pads 12 thereof, some of material 86 may be located in shadowed areas 54′ (see FIGS. 5 and 6) lying under portions of the substantially spherical solder balls 20′. As laser beam 98 is directed substantially vertically downwardly toward surface 88 of material 86, material 86 located in shadowed regions 54′ will not be contacted or altered by laser beam 98. Nonetheless, the unconsolidated material 86 in shadowed areas 54′ will become trapped therein as material 86′ adjacent to and laterally outward from shadowed areas 54′ is at least partially consolidated as ring 50′ is built up around solder ball 20′. Such trapped, unconsolidated material 86′ will eventually cure due to the cross-linking initiated in the outwardly adjacent photopolymer and the cure can be subsequently accelerated and polymerized as known in the art, such as by a thermal cure.

[0076] Once rings 50, or at least the outer skins thereof, have been fabricated, platform 90 is elevated above surface level 88 of material 86 and platform 90 is removed from apparatus 80, along with any substrate (e.g., semiconductor device 10, wafer 72 (see FIG. 7), or other substrate) disposed thereon and any stereolithographically fabricated structures, such as rings 50. Excess, unconsolidated material 86 (e.g., excess uncured liquid) may be manually removed from platform 90, from any substrate disposed thereon, and from rings 50. Each semiconductor device 10, wafer 72, or other substrate is removed from platform 90, such as by cutting the substrate free of base supports 122. Alternatively, base supports 122 may be configured to readily release semiconductor devices 10, wafers 72, or other substrates. As another alternative, a solvent may be employed to release base supports 122 from platform 90. Such release and solvent materials are known in the art. See, for example, U.S. Pat. No. 5,447,822 referenced above and previously incorporated herein by reference.

[0077] Rings 50 and semiconductor device 10 may also be cleaned by use of known solvents that will not substantially degrade, deform, or damage rings 50 or a substrate to which rings 50 are secured.

[0078] As noted previously, rings 50 may then require postcuring. Rings 50 may have regions of unconsolidated material contained within a boundary or skin thereof or in a shadowed area 54′ (see FIGS. 5 and 6), or material 86 may be only partially consolidated (e.g., polymerized or cured) and exhibit only a portion (typically 40% to 60%) of its fully consolidated strength. Postcuring to completely harden rings 50 may be effected in another apparatus projecting UV radiation in a continuous manner over rings 50 or by thermal completion of the initial, UV-initiated partial cure.

[0079] It should be noted that the height, shape, or placement of each ring 50 on each specific semiconductor device 10 or other substrate may vary, again responsive to output of camera 140 or one or more additional cameras 144, 146, or 148, shown in broken lines, detecting the protrusion of unusually high (or low) preplaced solder balls which could affect the desired distance 56 that rings 50 will protrude from surface 14. Likewise, the lateral extent (i.e., diameter) of each preplaced solder ball may be recognized and the radial girth of the outer boundary of each ring 50 adjusted accordingly. In any case, laser 92 is again activated to at least partially cure material 86 residing on each semiconductor device 10 or other substrate to form the layer or layers of each ring 50.

[0080] Although FIGS. 8 and 9 illustrate the stereolithographic fabrication of rings 50 on a substrate, such as a semiconductor device 10, a wafer 72 (FIG. 7), or another substrate, including a plurality of semiconductor devices 10 or other substrates, rings 50 can be fabricated separately from a substrate, then secured to a substrate by known processes, such as by the use of a suitable adhesive material.

[0081] The use of a stereolithographic process as exemplified above to fabricate rings 50 is particularly advantageous since a large number of rings 50 may be fabricated in a short time, the ring height and position are computer controlled to be extremely precise, wastage of unconsolidated material 86 is minimal, solder coverage of passivation materials is avoided, and the stereolithography method requires minimal handling of semiconductor devices 10, wafers 72, or other substrates.

[0082] Stereolithography is also an advantageous method of fabricating rings 50 according to the present invention since stereolithography can be conducted at substantially ambient temperature, the small spot size and rapid traverse of laser beam 98 resulting in negligible thermal stress upon semiconductor devices 10, wafers 72, or other substrates, as well as on the features thereof.

[0083] The stereolithography fabrication process may also advantageously be conducted at the wafer level or on multiple substrates, saving fabrication time and expense. As the stereolithography method of the present invention recognizes specific semiconductor devices 10 or other substrates 20, variations between individual substrates are accommodated. Accordingly, when the stereolithography method of the present invention is employed, rings 50 can be simultaneously fabricated on different types of semiconductor devices 10 or other substrates, as well as on both semiconductor devices 10 and other substrates.

[0084] While the present invention has been disclosed in terms of certain preferred embodiments, those of ordinary skill in the art will recognize and appreciate that the invention is not so limited. Additions, deletions and modifications to the disclosed embodiments may be effected without departing from the scope of the invention as claimed herein. Similarly, features from one embodiment may be combined with those of another while remaining within the scope of the invention.