Abstract
A MOSFET with raised source/drains that can readily be silicidated and have shallow source/drain extensions. The invention uses chemical vapor epitaxy to create raised source/drains. The invention provides molecules containing silicon and molecules containing germanium, preferably GeH4, for the chemical vapor epitaxy. Initially, the concentration of GeH4is between 5 to 10% of the concentration of molecules containing silicon. During the chemical vapor epitaxy, the concentration of GeH4is reduced to zero. The raised source/drains and the gate are subjected to silicidation. The higher concentrations of GeH4allow more selective epitaxy to silicon, thus preventing deposition on the polysilicon gate, nitride spacers and isolation trenches. It also allows for the use of lower epitaxy temperatures reducing movements of dopants in the source/drain extension. The slow reduction in concentration of GeH4allows for the epitaxy temperature to be kept low. The reduced germanium concentration near the end of the epitaxy allows better silicidation of the raised source/drain.
Metadata
Assignee
- Advanced Micro Devices, Inc.
Inventor
- Bin Yu
Application Information
Application Number:US 09/773,829
Filing Date:2001-01-31
Priority Date:1999-02-19
Art Unit:7
Classifications
IPC:
H01L 21331H01L 218222H01L 2976H01L 2994H01L 31062
Field of Search:
257616257751257407438300438592438301438303
Patent Drawings (5 sheets)
Description
Cross-Reference to Related Application
[0002] This divisional application is related to U.S. patent application Ser. No. 09/253,574, filed Feb. 19, 1999, now U.S. Pat. No. 6,218,711 entitled “A RAISED SOURCE/DRAIN PROCESS BY SELECTIVE SiGe EPITAXY.
Field of the Invention
[0003] The present invention relates to MOSFET devices. Even more particularly, the present invention relates to MOSFET devices with a raised (or elevated) source and a raised drain (raised S/D).
Background of the Invention
[0004] In the prior art, deep source and drain (deep source/drain) contact junctions are desirable to allow silicidation of the source and drain. Silicidation is the process of combining silicon with a metal such as titanium forming titanium silicide TiSi2. Silicides provide the advantages of being stable during contact with polysilicon and having a lower RC time delay than silicon. A lower RC time delay is important in high speed circuits. In opposition, shallow source and drain (source/drain) extensions are desirable to provide immunity to the “short-channel effect”, One cause for the short-channel effect is that as MOSFET devices are made with shorter gate lengths, the depletion layer widths of the source and drain junction become comparable to channel length, resulting in punch-through, where the gate loses control of the current. To obtain the benefits from deep source and drain contact junctions and shallow source/drain extensions the raised (or elevated) source/drain structure is used.
[0005] In the prior art, shallow source and drain extensions are first formed on a substrate. Pure Silicon (Si) selective epitaxy growth (SEG) is then used to form an elevated source and an elevated drain (elevated source/drain). The selective Si epitaxy process done in the prior art is a high temperature (>900° C.) process. This high temperature process causes further diffusion of the source/drain extensions making the source/drain extensions deep, which degrades transistor short channel performance.
[0006] The prior art also teaches the use of Silicon Germanium (SiGe) selective epitaxy growth (SEG) to form raised source/drain, using a 5-10% Germanium (Ge) concentration. This process uses a temperature that is 100-200° C. lower than the temperature used in the pure Si selective epitaxy growth, allowing for shallow source/drain extensions. In addition, SiGe provides improved epitaxy selectivity between Silicon and dielectric in the trench isolation and spacer region. A problem with the use of SiGe selective epitaxy growth is that a 5-10% concentration of Ge in the raised source/drain region makes the silicidation of the raised source/drain difficult.
Brief Summary of the Invention
[0007] It is an object of the invention to provide a lower temperature epitaxy growth with improved selectivity, to provide raised source/drains without silicidation problems.
[0008] Accordingly, the foregoing object is accomplished by providing a method and apparatus for performing SiGe epitaxy where the concentration of Germanium to Silicon is gradually reduced from above 5% to close to 0% during the epitaxy process, resulting in a device with raised source/drains which have the highest concentration (5-10%) of Germanium near the bottom of the source/drain and gradually reduced to 0% Germanium near the top of the source/drain.
[0009] The higher concentration of Germanium near the bottom of the source/drain helps to provide good epitaxy selectivity over other parts of the device area, such as trench isolation and gate stack dielectric spacers. The lower concentration of Germanium near the top of the source/drain allows for an easier silicidation of the source/drain. The lower temperature (100-200° C. below temperatures used in pure Si epitaxy), can be maintained even when the Germanium concentration becomes zero, since as long as SiGe seed has been formed, the Germanium concentration may be gradually reduced without raising temperature.
[0010] Other features of the present invention are disclosed or apparent in the section entitled: “DETAILED DESCRIPTION OF THE INVENTION.”
Brief Description of Drawings
[0011] For a filler understanding of the present invention, reference is made to the accompanying drawings wherein:
[0012] FIG. 1 is a cross sectional view of part of a silicon wafer and the first phase of a MOSFET on the silicon chip.
[0013] FIG. 2 is a schematic illustration of a chemical vapor epitaxy device.
[0014] FIG. 3 is a cross sectional view of part of a silicon wafer with the MOSFET after chemical vapor epitaxy according to the invention.
[0015] FIG. 4 is a cross sectional view of part of a silicon wafer with the MOSFET undergoing dopant implantation.
[0016] FIG. 5 is a cross sectional view of part of a silicon wafer with the MOSFET after the MOSFET has undergone silicidation.
[0017] Reference numbers refer to the same or equivalent parts of the present invention throughout the several figures of the drawing.
Detailed Description of the Invention and Best Mode of the Invention
[0018] FIG. 1 is a cross sectional view of part of a silicon wafer 10 and the first phase of a MOSFET 11 on the silicon wafer 10. The surface of the silicon wafer 10 forms a substrate 12 for the MOSFET 11. The first phase of the MOSFET 11 has isolation trenches 15 cut in to the substrate 12. A poly-silicon gate 17 is placed on a gate oxide 19 placed on the surface of the substrate 12. Ion implantation is used to provide shallow source/drain extensions 21. Nitride spacers 23 are created on the sides of the poly-silicon gate 17 and gate oxide 19. The manufacture of the first phase of the MOSFET is according to conventional means.
[0019] FIG. 2 is a schematic view of the silicon wafer 10 in an epitaxy device 25, which in the preferred embodiment is a chemical vapor epitaxy device. The wafer 10 is placed on a susceptor 27, which in this embodiment is a graphite block. The susceptor 27 is placed in a reactor 29. Radio frequency heating elements 31 are used to heat the susceptor 27 to a temperature between 650-750° C., more generally below 800° C. Gases such as silane (SiH4), and germane (GeH4) are provided to the susceptor 27, through an input pipe, and over the wafer 10. GeH4initially is 5-10% by mole fraction (or number of molecules) compared to SiH4that is passed through the susceptor 27. The percentage of GeH4is gradually reduced to close to zero percent (between 0.5% and 0%). More generally, during the epitaxy process the percentage by mole fraction of GeH4gas to SiH4goes from greater than 4% near the beginning of the epitaxy process to less than 1% near the end of the epitaxy process. The gases are removed from the reactor 29 by a vent pipe 35.
[0020] FIG. 3 is a cross sectional view of part of the silicon wafer 10 with the MOSFET 11 after chemical vapor epitaxy according to the invention. The MOSFET 11 has raised source/drains 37. The MOSFET 11 then undergoes ion implantation, as shown in FIG. 4. In the preferred embodiment, the ion implantation dopes the raised source/drain 37 and the gate 17 with a dopant of the same species as the dopant used to create the shallow source/drain extension 21 through implantation.
[0021] The wafer 10 is then subjected to a silicidation process to form CoSi2, TiSi2, or NiSi2in the source/drain and gate area. In one embodiment, titanium powder is deposited on the source/drain and gate and then sintered to the source/drain or gate to form TiSi2(titanium silicide), as shown in FIG. 5. Other methods of silicidation that may be used in the invention are discussed in “Semiconductor Devices Physics and Technology” by S.M. Sze, 1985, pp 376-379.
[0022] The wafer 10 and MOSFET 11 are further processed according to conventional means to form contacts and interconnects between various MOSFET's and other devices.
[0023] By using a 5-10% concentration of GeH4at the beginning of the epitaxy process, a lower temperature is needed, which minimizes diffusion of the source/drain extension, allowing for shallower source/drain extensions. In addition, the addition of GeH4increases the epitaxy selectivity between Si and the dielectric in the isolation trenches 15 and the nitride spacers 23, which decreases Si epitaxy deposition in the isolation trenches 15 and on the nitride spacers 23. Once the SiGe seed is formed, the GeH4concentration can be reduced, and still provide epitaxy without increasing the temperature in the reactor 29. The reduction of the GeH4concentration causes the Ge concentration to diminish closer to the top of the raised source/drain 37. Since the top of the raised source/drain 37 has a lower Ge concentration, it is easier to form silicides on the top part of the source/drain 37.
[0024] The use of the inventive epitaxy process provides an improved MOSFET. In other embodiments, different methods of epitaxy may be used. The invention may be used for other semiconductor wafers besides silicon. In other embodiments, GeH4, may be substituted with other germanium molecules such as GeCIH3. In other embodiments germanium may be substituted with carbon or nitrogen, but germanium is used in the preferred embodiment.
[0025] The present invention has been particularly shown and described with respect to certain preferred embodiments and features thereof. However, it should be readily apparent to those of ordinary skill in the art that various changes and modifications in form and detail may be made without departing from the spirit and scope of the inventions as set forth in the appended claims. The inventions illustratively disclosed herein may be practiced without any element which is specifically disclosed herein.
Claims
I claim:
1. A method of fabricating a semiconductor device, comprising the steps of:
providing a silicon substrate;
forming a source extension and a drain extension in the substrate;
forming a gate oxide on the substrate extending from the source extension to the drain extension;
forming a gate on the gate oxide,
a first part of the gate comprising poly-silicon, and
a second part of the gate comprising a silicide; and
forming a raised source and a raised drain on the substrate and respectively over the source extension and the drain extension,
a first part of the raised source and a first part of the raised drain comprising silicon and germanium,
a second part of the raised source and a second part of the raised drain comprising a silicide,
the raised source and a raised drain each comprising a proximal portion to the substrate and a distal portion from the substrate, and each comprising a germanium concentration gradient of less than 1% at the distal portion and greater than 4% at the proximal portion.
2. A method, as recited in claim 1, wherein the raised source and the raised drain each comprise a germanium concentration gradient of approximately less than 0.5% at the distal portion and greater than 5% at the proximal portion.
3. A method, as recited in claim 2, further comprising the steps of:
forming a first nitride spacer at a first end of the gate;
forming a second spacer at a second end of the gate;
forming a first isolation trench in the substrate adjacent to the source extension; and
forming a second isolation trench in the substrate adjacent to the drain extension.
Patent Citations (14)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US4529455(A) | 1985-07-01 | Bean et al. | Examiner |
| US4875086(A) | 1989-10-01 | Malhi et al. | Examiner |
| US5084411(A) | 1992-01-01 | Laderman et al. | Examiner |
| US5461250(A) | 1995-10-01 | Burghartz et al. | Examiner |
| US5646058(A) | 1997-07-01 | Taur et al. | Examiner |
| US5821577(A) | 1998-10-01 | Crabbe' et al. | Examiner |
| US5830775(A) | 1998-11-01 | Maa et al. | Examiner |
| US5864161(A) | 1999-01-01 | Mitani et al. | Examiner |
| US6074919(A) | 2000-06-01 | Gardner et al. | Examiner |
| US6130559(A) | 2000-08-01 | Gardner et al. | Examiner |
| US6124627(A) | 2000-09-01 | Rodder et al. | Examiner |
| US6162688(A) | 2000-12-01 | Gardner et al. | Examiner |
| US6214681(B1) | 2001-04-01 | Yu | Examiner |
| US6281559(B1) | 2001-08-01 | Yu et al. | Examiner |