US 6,339,114 B1Grant

Liquid crystalline (meth)acrylate compounds, composition and method

Issue Date:2002-01-15

•27 Claims

•1 Drawing Sheets

Abstract

Liquid crystalline (meth)acrylates of the invention include at least three rigid rod-like moieties. One of these moieties is comprised between the (meth)acrylate rests and further two moieties are bonded as side chains. The liquid crystalline (meth)acrylates polymerizable using redox initiators and/or photo initiators. The (meth)acrylates of the invention polymerize quantitative and with very low volume shrinkage of less than 2.5 percent. The invention provides a polymerizable compound within the scope of the general formula:

wherein R₁is a group of the general formula —A—, —A—Y1—B—, —A—Y₁—B—Y₂—C—, or a steroidal moiety, preferably selected of the group of cholesteryl compounds, wherein each A, B and C independently is a substituted or unsubstituted aromatic moiety having 6 to 24 carbon atoms, a substituted or unsubstituted heteroaromatic moiety having 2 to 24 carbon atoms or a substituted or unsubstituted cycloalkylene moiety having 5 to 30 carbon atoms, a substituted or unsubstituted alkylene moiety having 2 to 20 carbon atoms, each Y₁and Y₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O, S, SO₂, O(CO)O, OCS, CH₂—O, CH₂—S,

each L₁and L₂independently is a hydrogen, a alkylene having 1 to 20 carbon atoms or CN, R₃is a covalent bond or a substituted or unsubstituted alkylene having 1 to 20 carbon atoms, oxyalkylene having 1 to 20 carbon atoms, thioalkylene having 1 to 20 carbon atoms or a carboxyalkylene having 1 to 20 carbon atoms, R₄is hydrogen, a substituted or an unsubstituted alkyl having 1 to 20 carbon atoms, cycloalkyl having 5 to 12 carbon atoms, or aryl rest having 6 to 20 carbon atoms, M is a mesogenic group of the general formula —A—Z, —A—Y₁—B—Z, —A—Y₁—B—Y₂—C—Z, or a steroidal moiety, preferably selected of the group of cholesteryl compounds, wherein each A, B and C independently is a substituted or unsubstituted aromatic moiety having 6 to 24 carbon atoms, a substituted or unsubstituted heteroaromatic moiety having 2 to 24 carbon atoms or a substituted or unsubstituted cycloalkylene moiety having 5 to 30 carbon atoms, each Y₁and Y₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O, S, SO₂, O(CO)O, OCS, CH₂—O, CH₂—S,

each L₁and L₂independently is a hydrogen, a alkylene having 1 to 20 carbon atoms or CN, Z is a hydrogen, halogen, CN, —OR, COOR, NO₂, a halogen substituted or unsubstituted alkylene or alkenyl having 1 to 20 carbon atoms, a halogen substituted or unsubstituted oxyalkylene or oxyalkenyl having 1 to 20 carbon atoms, a halogen substituted or unsubstituted thioalkylene or thioalkenyl having 1 to 20 carbon atoms, a halogen substituted or unsubstituted carboxyalkylene or alkanoylenoxy having 1 to 20 carbon atoms, X is a covalent bond, CO, NHCO, OCO and n is an integer from 1 to 10. These compounds are used in dental compositions and methods of use thereof.

Metadata

Assignee

Dentsply DeTrey GmbH

Inventors

Joachim E. Klee
Holger Frey
Dirk Holter
Rolf Mulhaupt

Application Information

Application Number:US 09/391,539

Filing Date:1999-09-08

Priority Date:1993-05-26

Art Unit:7

Classifications

IPC:

A61K 6083

Field of Search:

523115523116523118524559526326

Patent Drawings (1 sheets)

Description

[0005] This is a continuation of application Ser. No. 09/723,443 filed Oct. 7, 1996, now U.S. Pat. No. 5,998,499, which is a continuation-in-part of U.S. patent application Ser. No. 08/543,950 filed Oct. 17, 1995, now abandoned, which is a continuation-in-part of U.S. patent application Ser. No. 08/382,779 Feb. 3, 1995 which is a continuation-in-part of U.S. patent application Ser. No. 08/067,774 filed May 26, 1993, and continuation-in-part of U.S. patent application Ser. No. 08/217,998 filed Mar. 25, 1995 now U.S. Pat. No. 5,624,976 and a continuation-in-part of U.S. patent application Ser. No. 08/231,535 filed Apr. 22, 1994, now abandoned, and a continuation-in-part of U.S. patent application Ser. No. 08/359,217 filed Dec. 19, 1994.

[0006] The invention relates to liquid crystalline (meth)acrylates suitable for dental and medical applications, as well as for optical, electrooptical application such as in liquid-crystal displays. The invention provides (meth)acrylate compounds which are liquid below 50° C., and are useful in compositions for treating natural teeth, such as dental restorative, cement, adhesive, primer, sealant and root canal filling compositions. The invention provides dental cement compositions and methods of using them for binding hard tooth material, metal and ceramic. The cement compositions include polymerizable ethylenically unsaturated monomers. The cements have superior adhesion to tooth without separately acid etching dentin or enamel. Compositions of the invention are useful as dental cements, liners, bases and restoratives. Compositions of the invention include less reactive diluent than prior art compositions. Compositions of the invention polymerize to form polymeric material having low or no residual monomer, preferably less than 1 percent residual monomer.

[0007] A series of acrylate, methacrylate or vinyl terminated compounds comprising a mesogenic or rigid rod-like moiety including (meth)acrylate terminated oligomers I and II with a mesogenic terephthaloyl ester moiety are disclosed by G. G. Barclay, C. K. Ober, Prog. Polym. Sci. 18 (1993) 899; D. J. Broer, G. N. Mol, Polym. Engng. Sci. 31 (1991) 625; R. A. M. Hikmet, J. Lub, J. A. Higgins, Polymer 34 (1993) 1736.

[0008] p-Hydroxy benzoic ester moieties incorporated into vinyl terminated compounds III are disclosed by D. J. Broer, J. Lub, G. N. Mol, Macromol. 26 (1993) 1244.

[0009] A diacrylate (wherein R is H) and a dimethacrylate (wherein R is CH₃) having the formula IV which comprises a biphenylhydroxy moiety is disclosed by H. Litt Morton, Wha-Tzong Whang, Kung-Ti Yen, Xue-Jun Qian, in J. Polym. Sci., Part A,: Polym. Chem. 31 (1993) 183, Morton H. Litt U.S. Ser. No. 89-369205.

[0010] Acetylene terminated aromatic ester having the formula V are described by E. P. Douglas, Polymer Prep. 34 (1993) 702.

[0011] Methacrylates having the formula VI with a ridged rod-like moiety are disclosed in T. Shindo, T. Uryu, Liquid Crystals 15 (1993) 239).

[0012] A vinyl terminated bishydroxybenzoate having formula VII which comprises spacers and exhibits relatively low phase transition temperatures only on cooling (n=11: i65n62s_A47s_B31k) and relatively narrow liquid crystalline phases, are disclosed by H. Anderson, F. Sahlen, and U. W. Gedde, A. Hutt, in Macromol. Symp. (1994) 339.

[0013] Mixtures of (meth)acrylates comprising liquid crystalline monomers, dimethacrylates (2,2-Bis-[p-(2-hydroxy-3-methacryloyloxypropoxy)-phenyl]-propane) and di(meth) acrylates comprising liquid crystalline monomers are described in EP 0379058.

[0014] However, the known liquid crystalline mono- or difunctional molecules have melting temperatures and liquid crystalline behavior at temperatures above 50° C. (Table 1 below, page 25). An application of these molecules in the liquid crystalline phase require temperatures over their melting temperature (50 to 170° C.). An application at room temperature is only possible in the solid state or in solution.

[0015] In accordance with the invention monomers are provided which are liquid at room temperature and which show liquid crystalline behavior at least between 20 and 40° C. These liquid crystalline monomers are useful in dentistry, medicine, microelectronics and optoelectronics.

[0016] It is an object of the invention to provide a polymerizable compound within the scope of the general formula:

[0017] wherein

[0018] R₁is a group of the general formula

[0019] —A—, —A—Y₁—B—, —A—Y₁—B—Y₂—C

[0020] or a steroidal moiety, preferably selected of the group of cholesteryl compounds, wherein

[0021] each A, B and C independently is a substituted or unsubstituted aromatic moiety having 6 to 24 carbon atoms, a substituted or unsubstituted heteroaromatic moiety having 2 to 24 carbon atoms or a substituted or unsubstituted cycloalkylene moiety having 5 to 30 carbon atoms, a substituted or unsubstituted alkylene moiety having 2 to 20 carbon atoms

[0022] each Y₁and Y₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O(CO)O, O, S, SO₂, OCS, CH₂—O, CH₂S,

[0023] each L₁and L₂independently is a hydrogen, a alkylene having 1 to 20 carbon atoms or CN

[0024] R₃is a covalent bond or a substituted or unsubstituted alkylene having 1 to 20 carbon atoms, oxyalkylene having 1 to 20 carbon atoms, thioalkylene having 1 to 20 carbon atoms or a carboxyalkylene having 1 to 20 carbon atoms

[0025] R₄is hydrogen, a substituted or an unsubstituted alkyl having 1 to 20 carbon atoms, cycloalkyl having 5 to 12 carbon atoms, or aryl rest having 6 to 20 carbon atoms,

[0026] M is a mesogenic group of the general formula

[0027] —A—Z, —A—Y₁—B—Z, —A—Y₁—B—Y₂—C—Z

[0028] or a steroidal moiety, preferably selected of the group of cholesteryl compounds, wherein

[0029] each A, B and C independently is a substituted or unsubstituted aromatic moiety having 6 to 24 carbon atoms, a substituted or unsubstituted heteroaromatic moiety having 2 to 24 carbon atoms or a substituted or unsubstituted cycloalkylene moiety having 5 to 30 carbon atoms

[0030] each Y₁and Y₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O(CO)O, O, S, SO₂, OCS, CH₂—O, CH₂—S,

[0031] each L₁and L₂independently is a hydrogen, a alkylene having 1 to 20 carbon atoms or CN

[0032] Z is a hydrogen, halogen, CN, —OR, COOR, NO₂, a halogen substituted or unsubstituted alkylene or alkenyl having 1 to 20 carbon atoms, a halogen substituted or unsubstituted oxyalkylene or oxyalkenyl having 1 to 20 carbon atoms, a halogen substituted or unsubstituted thioalkylene or thioalkenyl having 1 to 20 carbon atoms, a halogen substituted or unsubstituted carboxyalkylene or alkanoylenoxy having 1 to 20 carbon atoms,

[0033] X is a covalent bond, CO, NHCO, OCO,

[0034] n is an integer from 1 to 10.

BRIEF DESCRIPTION OF THE DRAWINGS

[0035] FIG. 1 is a graph of the thermomechanical properties of a composition in accordance with the invention.

BRIEF DESCRIPTION OF THE INVENTION

[0036] The invention provides a polymerizable compound within the scope of the general formula:

[0037] wherein R₁is a group of the general formula —A—, —A—Y₁—B—, —A—Y₁—B—Y₂—C—, or a steroidal moiety, preferably selected of the group of cholesteryl compounds, wherein each A, B and C independently is a substituted or unsubstituted aromatic moiety having 6 to 24 carbon atoms, a substituted or unsubstituted heteroaromatic moiety having 2 to 24 carbon atoms or a substituted or unsubstituted cycloalkylene moiety having 5 to 30 carbon atoms, a substituted or unsubstituted alkylene moiety having 2 to 20 carbon atoms, each Y₁and Y₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O, S, SO₂, O(CO)O, OCS, CH₂—O, CH₂—S,

[0038] each L₁and L₂independently is a hydrogen, a alkylene having 1 to 20 carbon atoms or CN,

[0039] Alternatively, R₁is expressed as a group of the general formula —R₁₀—, —R₁₀—Z₁—R₁₁—, —R₁₀—Z₁—R₁₁—Z₂—R₁₂—, or a steroidal moiety, preferably selected from the group of cholesteryl compounds, wherein each R₁₀, R₁₁and R₁₂independently is a substituted or unsubstituted aromatic moiety having 6 to 24 carbon atoms, a substituted or unsubstituted heteroaromatic moiety having 2 to 24 carbon atoms or a substituted or unsubstituted cycloalkylene moiety having 5 to 30 carbon atoms, a substituted or unsubstituted alkylene moiety having 2 to 20 carbon atoms, each Y₁and Y₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O, S, SO₂, O(CO)O, OCS, CH₂—O, CH₂—S,

[0040] each L₁and L₂independently is a hydrogen, a alkylene having 1 to 20 carbon atoms or CN,

[0041] R₃is a covalent bond or a substituted or unsubstituted aklkyene having 1 to 20 carbon atoms, oxyalkylene having 1 to 20 carbon atoms, thioalkylene having 1 to 20 carbon atoms or a carboxyalkylene having 1 to 20 carbon atoms,

[0042] R₄is hydrogen, a substituted or an unsubstituted alkyl having 1 to 20 carbon atoms, cycloalkyl having 5 to 12 carbon atoms, or aryl rest having 6 to 20 carbon atoms,

[0043] M is a mesogenic group of the general formula —A—Z, —A—Y₁—B—Z, —A—Y₁—B—Y₂—C—Z, or a steroidal moiety, preferably selected of the group of cholesteryl compounds, wherein each A, B and C independently is a substituted or unsubstituted aromatic moiety having 6 to 24 carbon atoms, a substituted or unsubstituted heteroaromatic moiety having 2 to 24 carbon atoms or a substituted or unsubstituted cycloalkylene moiety having 5 to 30 carbon atoms, each Y₁and Y₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O, SO₂, O(CO)O, OCS, CH₂—O, CH₂—S,

[0044] Alternatively, M is expressed as a mesogenic group of the general formula —R₁₀—Z, —R₁₀—Z₁—R₁₁—Z, —R₁₀—Y₁—R₁₁—Z₂—R₁₃—, or a steroidal moiety, preferably selected of the group of cholesteryl compounds, wherein each R₁₀, R₁₁and R₁₂independently is a substituted or unsubstituted aromatic moiety having 6 to 24 carbon atoms, a substituted or unsubstituted heteroaromatic moiety having 2 to 24 carbon atoms or a substituted or unsubstituted cycloalkylene moiety having 5 to 30 carbon atoms, each Z₁and Z₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O, S, SO₂, O(CO)O, OCS, CH₂—O, CH₂—S,

[0045] each L₁and L₂independently is a hydrogen, a alkylene having 1 to 20 carbon atoms or CN,

[0046] Z is a hydrogen, halogen, CN, —OR, COOR, NO₂, a halogen substituted or unsubstituted alkylene or alkylidene having 1 to 20 carbon atoms, a halogen substituted or unsubstituted oxyalkylene or oxyalkylidene having 1 to 20 carbon atoms, a halogen substituted or unsubstituted thioalkylene or thioalkylidene having 1 to 20 carbon atoms, a halogen substituted or unsubstituted carboxyalkylene or alkanoylenoxy having 1 to 20 carbon atoms,

[0047] X is a covalent bond, CO, NHCO, OCO and n is an integer from 1 to 10.

DESCRIPTION OF THE INVENTION

[0048] Preparation of Liquid Crystalline (meth)acrylates

[0049] In accordance with the invention are prepared liquid crystalline (meth)acrylates within the scope of general formula 1 which have at least two polymerizable double bonds and at least two rigid rod-like moieties R₁and M

[0050] General formula 1 is alternatively written as general formula 1A as follows:

[0051] In formula 1 and 1A R₁is a group of the general formula

[0052] —A—, —A—Y₁—B—, —A—Y₁—B—Y₂—C—

[0053] or a steroidal moiety, preferably selected of the group of cholesteryl compounds, wherein

[0054] each A, B and C independently is a substituted or unsubstituted aromatic moiety having 6 to 24 carbon atoms, a substituted or unsubstituted heteroaromatic moiety having 2 to 24 carbon atoms or a substituted or unsubstituted cycloalkylene moiety having 5 to 30 carbon atoms, a substituted or unsubstituted alkylene moiety having 2 to 20 carbon atoms

[0055] each Y₁and Y₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O(CO)O, O, S, SO₂, OCS, CH₂—O, CH₂—S,

[0056] each L₁and L₂independently is a hydrogen, a alkylene having 1 to 20 carbon atoms or CN

[0057] R₃is a covalent bond or a substituted or unsubstituted alkylene having 1 to 20 carbon atoms, oxyalkylene having 1 to 20 carbon atoms, thioalkylene having 1 to 20 carbon atoms or a carboxyalkylene having 1 to 20 carbon atoms

[0058] R₄is hydrogen, a substituted or an unsubstituted alkyl having 1 to 20 carbon atoms, cycloalkyl having 5 to 12 carbon atoms, or aryl rest having 6 to 20 carbon atoms,

[0059] M is a mesogenic group of the general formula

[0060] —A—Z, —A—Y₁—B—Z, —A—Y₁—B—Y₂—C—Z

[0061] or a steroidal moiety, preferably selected of the group of cholesteryl compounds, wherein

[0062] each A, B and C independently is a substituted or unsubstituted aromatic moiety having 6 to 24 carbon atoms, a substituted or unsubstituted heteroaromatic moiety having 2 to 24 carbon atoms or a substituted or unsubstituted cycloalkylene moiety having 5 to 30 carbon atoms

[0063] each Y₁and Y₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O(CO)O, O, S, SO₂, OCS, CH₂—O, CH₂—S,

[0064] each L₁and L₂independently is a hydrogen, a alkylene having 1 to 20 carbon atoms or CN

[0065] Z is a hydrogen, halogen, CN, —OR, COOR, NO₂, a halogen substituted or unsubstituted alkylene or alkenyl having 1 to 20 carbon atoms, a halogen substituted or unsubstituted oxyalkylene or oxyalkenyl having 1 to 20 carbon atoms, a halogen substituted or unsubstituted thioalkylene or thioalkenyl having 1 to 20 carbon atoms, a halogen substituted or unsubstituted carboxyalkylene or alkanoylenoxy having 1 to 20 carbon atoms,

[0066] X is a covalent bond, CO, NHCO, OCO,

[0067] n is an integer from 1 to 10.

[0068] Compounds with the scope of geneal formulas A and B are within the scope of general formula 1 and 1A.

[0069] Preferably liquid crystalline (meth)acrylates have structures A and B.

[0070] A macrononomer within the scope of general formula 5 is formed by reaction of a 2,3-epoxypropyl (meth)acrylate compound within the scope of general formula 4, a diphenol compound within the scope of general formula 3 and a diepoxide compound within the scope of general formula 2 as follows.

[0071] In general formulas 2 through 5 R₂is a group of the general formula

[0072] —A—, —A—Y₁—B—, —A—Y₁—B-—₂—C—

[0073] or a steroidal moiety, preferably selected of the group of cholesteryl compounds, wherein

[0074] each A, B and C independently is a substituted or unsubstituted aromatic moiety having 6 to 24 carbon atoms, a substituted or unsubstituted heteroaromatic moiety having 2 to 24 carbon atoms or a substituted or unsubstituted cycloalkylene moiety having 5 to 30 carbon atoms, a substituted or unsubstituted alkylene moiety having 2 to 20 carbon atoms

[0075] each Y₁and Y₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O(CO)O, O, S, SO₂, OCS, CH₂—O, CH₂—S,

[0076] each L₁and L₂independently is a hydrogen, a alkylene having 1 to 20 carbon atoms or CN

[0077] R₄is hydrogen, a substituted or an unsubstituted alkyl having 1 to 20 carbon atoms, cycloalkyl having 5 to 12 carbon atoms, or aryl rest having 6 to 20 carbon atoms,

[0078] R₁is a substituted or unsubstituted aryl having from 6 to 24 carbon atoms and/or a substituted or unsubstituted cycloalkyl having from 5 to 12 carbon atoms. Preferably R₁is

[0079] wherein R₅is hydrogen, alkyl having from 1 to 12 carbon atoms, cycloalkyl having from 5 to 12 carbon atoms, aryl having from 6 to 18 carbon atoms and

[0080] Y is substituted or unsubstituted alkylene having from 1 to 5 carbon atoms, O, CO, OCO, S, SO₂and,

[0081] n is an integer from 1 to 10. Preferably n is 1, 2, or 3.

[0082] The reaction of epoxide di(meth)acrylates compounds within the scope of general formula 5 with organic acids within the scope of general formula 6 or derivatives thereof, with isocyanates within the scope of general formula 7 or alcohols 8 within the scope of general formula leads to modified di(meth)acrylates having ester moieties, urethane linkages or ether moieties 1 and 1A within the scope of general formula. M—R₃—NCO 7

[0083] M—R₃—OH 8

[0084] In the general formulas 6, 7 and 8 are

[0085] R₃is a covalent bond or a substituted or unsubstituted alkylene having 1 to 20 carbon atoms, oxyalkylene having 1 to 20 carbon atoms, thioalkylene having 1 to 20 carbon atoms or a carboxyalkylene having 1 to 20 carbon atoms

[0086] M is a mesogenic group of the general formula

[0087] —A—Z, —A—Y₁—B—Z, —A—Y₁—B—Y₂—C—Z

[0088] or a steroidal moiety, preferably selected of the group of cholesteryl compounds, wherein

[0089] each A, B and C independently is a substituted or unsubstituted aromatic moiety having 6 to 24 carbon atoms, a substituted or unsubstituted heteroaromatic moiety having 2 to 24 carbon atoms or a substituted or unsubstituted cycloalkylene moiety having 5 to 30 carbon atoms

[0090] each Y₁and Y₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O(CO)O, O, S, SO₂, OCS, CH₂—O, CH₂—S,

[0091] each L₁and L₂independently is a hydrogen, a alkylene having 1 to 20 carbon atoms or CN

[0092] Z is a hydrogen, halogen, CN, —OR, COOR, NO₂, a halogen substituted or unsubstituted alkylene or alkenyl having 1 to 20 carbon atoms, a halogen substituted or unsubstituted oxyalkylene or oxyalkenyl having 1 to 20 carbon atoms, a halogen substituted or unsubstituted thioalkylene or thioalkenyl having 1 to 20 carbon atoms, a halogen substituted or unsubstituted carboxyalkylene or alkanoylenoxy having 1 to 20 carbon atoms.

[0093] The esterification, etherification and urethane formation of the di(meth)acrylate hydroxyl groups is carried out in solutions. As solvents for the esterification were used tetrahydrofurane, dioxane, CH₂Cl₂, DMF or others, or polymerizable monomers such as triethyleneglycol bismethacrylate, diethyleneglycol bismethacrylate, dioxolan bismethacrylate, vinyl-, vinylene- or vinylidene-, acrylate- or methacrylate substituted spiroorthoesters and 2,2-bis[p-(acryloxyethoxy)phenyl]propane.

[0094] For example a liquid crystalline di(meth)acrylate within the scope of structural formula 9 is synthesized in the following manner 2,3-epoxy propoxy methacrylate and 4,4′-dihydroxy biphenyl are mixed and reacted for 15 hours at 115° C. to form a methacrylate terminated macromonomer having hydroxyl groups. The macromonomer hydroxyl groups are then esterified by mixing at 23° C. with 4′-cyano-biphenyl 4-oxy-valeric carboxylic acid and dicyclohexylcarbodiimid and than for further 24 hours at 23° C. to form a compound of the structural formula:

[0095] The compositions of the invention are formulated as one, two or more components, UV curable, visible light curable, self cure, and/or dual cure product or combinations of these. The composition of a preferred embodiment of the invention includes polymerizable carboxylic acid monomer, an optional filler and/or diluent, a cationic elutable glass or other source of polybent cations, and a polymerization catalyst system.

[0096] Fillers which are suited for use in compositions of the invention are organic and/or inorganic particles, for example inorganic glasses such as are used in glass ionomer cements. Exemplary of such fillers are those of U.S. Pat. No. 4,814,362 which is incorporated herein by reference in its entirety. Preferred fillers are glasses formed from or including, barium, calcium, strontium, lanthanum, tantalum, and/or tungsten silicates and aluminates and/or aluminosilicates, silica, including submicron silica, quartz, and/or ceramics for example, calcium hydroxy apatite. In a preferred embodiment of the invention reactive cations, especially those of calcium, strontium and aluminium, and anions especially fluoride ions; are eluted from the fillers. The fillers used in the invention preferably are reduced in particle size and are preferably silanated before they are incorporated into such compositions. Preferred levels of filler are from about 20% to about 85% based on the total weight of the composition, with from about 40% to about 85% being more preferable and about 50-80% being most preferred. If a more finely particulated filler is used, amounts of filler may be decreased due to the relative increase in surface area which attends the smaller sizes of particles. Preferred particle size distributions are from 0.02 to 50 microns, more preferably 0.1 to 10 microns, and most preferably 1 to 6 microns.

[0097] Mixing the compositions of the present invention may be achieved using standard compounding techniques. For example, liquids, photoinitiator(s), and accelerator(s) are blended first, and fillers are added incrementally thereafter. When blending light sensitive compositions, however, a photosafe room illumination, i.e., one that does not contain substantial amounts of wavelengths of electromagnetic radiation that would activate the photoiniatiing system is used to avoid initiating polymerization of the composition prematurely.

[0098] The compounds of the present invention also have medical applications such as in self adhesive bone cements. However, they are most preferred to use in dental treatment by application to a tooth or a number of teeth in vivo, in the mouth of a live patient by a dentist or dental practitioner.

[0099] The application of the compositions of the invention is preferably as a polymerizable dental composition applied to tooth. In a preferred embodiment of the invention a dental cement composition includes a compound within the scope of general formula 1, and other ingredients, such as curing catalysts, initiators, accelerators, diluents and/or adjuvants. The composition is applied as a cement using conventional techniques and preferably cured with application of visible light in a conventional manner. Cements in accordance with the invention are self adhesive to dentin and enamel. These cements are used in bonding dentin to structures, for example, to bond a ceramic inlay to a prepared cavity of a tooth. Inlays preferably are polymers, or ceramics which are cast or built-up from porcelain frits and fired. Afternatively, inlays are machined from metal such as titanium or gold or performed polymeric composite or homogeneous monolithic polymer compositions, for example by CAD-CAM procedures. In accordance with a preferred embodiment of the invention metal or ceramic superstructures for crowns, and bridges and/or orthodontic appliances are bonded to teeth using cement compositions of the invention. Such cement compositions join metal or ceramic to tooth by application of the cement composition by bringing them into contact until the cement hardens.

[0100] A preferred composition of the invention includes a two-part system. One part includes an initiator. The second part comprises filler and the co-initiator. The two parts are spatuled to form a cement prior to placement on tooth. The placement is by standard technique(s). Preferably the cement includes a visible light and/or a self-curing redox polymerization initiator system. In a preferred embodiment of the invention luting cement compositions have low viscosity and film thicknesses less than about 25 μm to bond close fitting appliances to prepared teeth. In one embodiment luting cement compositions of the present invention may be prepared of such high viscosity and consistency that they form adhesive “glue” lines of thicknesses up to several hundred microns to lute less close fitting restorations, for example inlays prepared using present state-of-the-art CAD-CAM devices. Compositions of the invention are mechanically strong, abrasion resistant, and are esthetically suitable and serve as the sole structural element to retain inlay, crowns and bridges or other appliances to tooth structure.

[0101] A preferred dental treatment in accordance with the invention is the application of dental filling compositions which include an initiator and at least one compound within the scope of general formula 1. Preferably the dental filling composition includes finely divided filler. Preferably the composition is applied to a tooth as a filling material using conventional techniques as a one-component material and is cured with application of visible light in conventional manner.

[0102] In a preferred embodiment of the invention a one or two component pit and fissure sealant which includes at least one compound within the scope of general formula 1 is applied to anatomic defects and/or the exterior of teeth. The sealant limits the ability of caries-forming bacteria to colonize the pits, fissures and other surfaces of the teeth. Pit and fissure sealant compositions in accordance with the invention are an especially valuable means of reducing caries by filling and eliminating enamel defects. The pit and fissure sealants of the invention are preferably applied with or without prior acid etching or the use of rubber dam to teeth. In one embodiment fluoride eluting compounds and glasses are preferably included in compositions of the invention. Fluoride is eluted to reduce the incidence of caries in tooth substance adjacent the compositions of the invention.

[0103] Preferred compositions of the invention include two or more ethylenically unsaturated materials are included in compositions of the invention. The polymerizable monomer is preferably liquid at 23° C., and comprises from about 0.5 to about 99.998% by weight of the composition, with amounts ranging from about 1 to about 99.98% being preferred, and amounts ranging from about 1.5 to about 99.8% being more preferred.

[0104] Preferred compositions of the invention include an adhesion promoter for example a phosphorus-containing adhesion promoter which is free from any halogen atoms covalently or otherwise bonded directly to a phosphorus atom. The phosphorus derivative may be polymerizable or non-polymerizable, however the preferred phosphorus-containing adhesion promoters comprise polymerizable phosphorus materials having ethylenic unsaturation and include, among others, organic esters of one or more acids of phosphorus (hereinafter referred to as phosphorus acid esters), wherein the organic portion of the ester contains at least one polymerizable ethylenically unsaturated group. The organic portion of the ester may be alkenyl, alkenoxy, cycloalkenyl, aralkenyl, or alkenaryl, and preferably may have from 2 to 40 carbon atoms. The organic portion may be straight chain, branched, or cyclic, can contain skeletal hetero atoms, i.e., atoms other than carbon, and can be unsubstituted or substituted with moieties which do not interfere with the free radical polymerization of the phosphorus acid esters.

[0105] Examples of saturated and unsaturated phosphorus acid esters which may be used include, but are not limited to, monomers containing phosphoric acid groups such as hydroxyethyl methacrylate monophosphate, 2,2,′-bis(alpha-methacryloxy-beta-hydroxypropoxyphenyl)propane diphosphonate (BIS-GMA diphosphonate), BIS-GMA diphosphate, dibutyl phosphite, di-2-ethylhexyl phosphite, di-2-ethylhexyl phosphate, glyceryl-2-phosphate, glycerylphosphoric acid, methacryloxyethyl phosphate, and glyceryl dimethacrylate phosphate. Other suitable polymerizable phosphorus acid esters are disclosed, for example, in U.S. Pat. No. 4,499,251 to Omura et al, U.S. Pat. No. 4,222,780 to Shibantani et al, U.S. Pat. No. 4,235,633 to Tomioka, U.S. Pat No. 4,259,117 to Yamauchi et al, U.S. Pat. No, 4,368,043 to Yamauchi et al. Of the polymerizable phosphorus acid compounds disclosed in the above patents and application, each of which is incorporated herein by reference, the preferred compounds are those polyethylenically unsaturated monophosphates of the formula:

[0106] and salts thereof, in which

[0107] R is an organic radical having a valency of n+1; and R may be interrupted by one or more oxygen atoms and may be substituted or unsubstituted, and may comprise an aliphatic radical, or a cycloaliphatic radical, or an aryl radical;

[0108] R¹is a hydrogen atom, alkyl having from 1 to 3 carbon atoms, halogen or —C═N, and

[0109] n is an integer of at least 1. Preferably n is an integer of 2 or more, and more preferably from 3 to 6. Examples of the preferred compounds include pentaerythritol triacrylate monophosphate, pentaerythritol trimethacrylate monophosphate, dipentaerythritol pentaacrylate monophosphate, and dipentaerythrtol pentamethacrylate monophosphate. When included the phosphorus acid compound may comprise from about 0.25 to about 99.998% by weight of the adhesive composition, with amounts ranging from about 1 to about 50% being preferred. In a more preferred embodiment the phosphorus acid compound would comprise from about 2 to about 29.8% by weight of the composition.

[0110] Preferred compositions of the invention include a catalyst component which may comprise any free radical initiators normally used in conjunction with polymerizable ethylenically unsaturated materials, although those which will initiate polymerization at room temperature are more preferred. Thus, the catalyst may comprise, for example, an organic peroxide type initiator such as dibenzoyl peroxide, dilauroyl peroxide, acetyl peroxide, t-butyl peroxybenzoate, cumene hydroperoxide and the like. In a preferred aspect, the catalyst comprises an actinic light sensitive initiator, such as ultraviolet light-sensitive initiators or visible light sensitive initiators. As examples of suitable ultraviolet light-sensitive initiators there may be mentioned the monoketals of an aromatic 1,2-diketone, benzophenones, substituted benzophenones, benzoin methyl ether, isopropoxybenzoin, benzoin phenyl ether or benzoin isobutyl ether. Among the suitable visible light sensitive initiators, alpha-diketones, such as camphoroquinone, are particularly preferred. The preferred initiators are the visible light sensitive initiators. The catalyst generally is employed in the range of from about 0.001 to about 10% of the composition. In a preferred embodiment the catalyst is used within the range of from 0.01 to about 5%. In a still further preferred embodiment from about 0.1 to about 2% by weight of catalyst is employed.

[0111] In a preferred embodiment of the invention, polymerizable compositions are provided which include an accelerator system comprising (1) an amine or amine salt and/or (2) a sulfinic acid or salt thereof and/or (3) a metal salt or organo metal compound. In a preferred embodiment both the amine or amine salt and the sulfinic acid or salt thereof are present. The amine or amine salt may be present in an amount from 0 to about 20% by weight of the composition, whereas the sulfinic acid or salt thereof is present in an amount of from about 0 to about 10%, the combined amount being from about 0.001 to about 20 percent. In a preferred embodiment, the amine or amine salt is in the range of 0.001 to about 10% by weight of the polymerizable composition, and the sulfinic acid or a sulfinic acid salt is in the range from about 0.01 to about 5 percent by weight of the polymerizable composition, the combined weight being in the range from about 0.01-15% by weight. In a still more preferred embodiment, the amine or amine salt is in an amount from about 0.1-8 percent by weight of the polymerizable composition and the sulfinic acid or salt thereof is in an amount from 0.1-2 percent by weight of the polymerizable composition, the combined amount ranging from about 0.2 to 10 percent by weight of the polymerizable composition.

[0112] The amine or amine salt employed in a preferred embodiment of this invention desirably is a secondary or tertiary amine rather than a primary amine, since the use of a secondary or tertiary amine leads to significantly accelerated curing. Examples of suitable amines include N,N-dimethylaniline, N,N-dimethyl-p-toluidine, N-methyl-N-beta-hydroxyethylaniline.

[0113] Primers and adhesives of the invention may be filled to such an extent that they would serve not only as primers and adhesives, but also as pit and fissure sealants and dental filling composites. A primer, composition of the invention comprises by weight about 5-20% PENTA, 0-61% hydroxyethyl methacrylate, 0.1% butylated hydroxytoluene.

[0114] Preferably the compound having mesogenic groups has a melting point below 20° C. Preferably this compound is used in a composition comprising at least 25 percent by volume volatile organic solvent. This composition preferably includes at least 30 percent by weight of a volatile organic solvent.

[0115] All of the percentages recited herein are by weight based on the weight of the entire composition unless otherwise stated.

EXAMPLE 1

Synthesis of 4,4′-Bis-(2-hydroxy-3-methacryloylpropoxy)-biphenyl

[0116] 60.00 g (0.422 mol) 2,3-Epoxypropoxy methacrylate, 0.40 g 2,6-Di-tert.-butyl-cresol, 39.3 g (0.211 mol) 4,4′-Dihydroxybiphenyl and 250 ml 1-Methoxy-2-propanol are heated until a homogeneous clear liquid is formed. After adding 0.30 g 1,8-Diaza-bicyclo-[5.4.0]-undec-7-ene the mixture were kept for 15 hours at 115° C. Then the mixture is concentrated and dropped into petrolether and cooled onto 0° C. The separated solid is filtered and washed with petrolether and dried. The crude product is recrystallized from 200 ml ethanol dissolved in a small amount DMSO and filtered over Al₂O₃(act. II/III, app. 500 g) using acidic ethyl ester/petrol ether. After removing the solvents 14 g of pure 4,4′-Bis-(2-hydroxy-3-methacryloylpropoxy)-biphenyl is obtained.

[0117] ¹H NMR: 7.6/7.05 (Ar), 6.1/5.7 (CH₂═C—), 5.45 (OH), 4.3, 4.1 (CH, CH₂OCO), 4.0 (CH₂OAr), 1.9 (CH₃).

[0118] ¹³C NMR: 166.3 (CO), 157.4/132.3/127.1/114.7 (Ar), 135.6 (C═), 125.8 (CH₂═), 69.0 (CH₂O), 66.6 (CH), 65.5 (CH₂OCO), 17.8 (CH₃).

Esterification of 4,4′-bis-(2-hydroxy-3-methacryloylpropoxy)-biphenyl with 4′-Cyano-4biphenyloxyvaleric carboxylic acid

[0119] 6,50 g (22 mmol) 4′-Cyano4-biphenyloxyvalerian carboxylic acid, 4,71 g (10 mmol) 4,4′-bis-(2-hydroxy-3-methacryloylpropoxy)-biphenyl and 0,25 g dimethylamino pyridine were dissolved in 85 ml CH₂Cl₂/DMF (vol.-ratio 9:8). To the mixture were added 5,00 g (24,2 mmol) dicyclohexyl carbodiimid. Then the mixture were stirred for 24 hours at room temperature. After this time the precipitated solid was filtered off. To the filtrate were added 0,1 g BHT and the solvent was removed by vacuum distillation. The viscose residue was dissolved in 100 ml CH₂Cl₂and cooled to 0° C. The precipitating solid was removed and the filtrate was washed twice with 50 ml 1 n HCl, 50 ml 1 n NaHCO₃solution and with 150 ml water and filtered over silica. Furthermore, the solution was dried over NaSO₄and the solvent was removed to obtain 5.5 g of 4,4′-bis-(2-hydroxy-3-methacryloylpropoxy)-biphenyl esterified with 4′-Cyano-biphenyl4oxyvaleric carboxylic acid.

Application Example 1

[0120] To 5.00 g liquid crystalline di(meth)acrylate of Example 1 are added and 0,05 g JRAGCURE 651 (Ciba-Geigy). Using a curing unit (Dentsply De Trey) the mixture is polymerized by irradiation with visible light during 40 seconds. The degree of polymerization is about 85%. The obtained material shows a volume shrinkage of 2.4 percent. The thermo-mechanical properties are shown in FIG. 1 wherein E′ (storage modulus) is 2.8·10⁹Ps (25° C.), E″ (loss modulus) is 2.9·10⁸Pa (25° C.) and tan δ(E″/E′) is 0.22.

Comparative Example 1

[0121] To 7.000 g of (2,2-Bis-[p-(2-hydroxy-3-methacryloyloxypropoxy)-phenyl]-propane) and 3.000 g of triethyleneglycol dimethacrylate were added 0,050 g N,N-di(β-hydroxyethyl)-p-toluidine and 0.050 g champhorquinone. Using a curing unit (Dentsply De Trey) the mixture was polymerized by irradiation with visible light during 40 seconds. The degree of polymerization is about 65%. The obtained material shows a volume shrinkage of 6.5 percent.

EXAMPLE 2

Synthesis of 4,4′-bis-(2-hydroxy-3-methacryloylpropoxy)-biphenyl as described in example 1

Esterification of 4,4′-bis-(2-hydroxy-3-methacryloylpropoxy)-biphenyl with 4′-Cyano-biphenyl-4-oxyundecane carboxylic acid

[0122] 11.39 g (30 mmol) 4′-Cyano-biphenyl-4-oxyundecane carboxylic acid, 6.59 g (14 mmol) 4,4′-bis-(2-hydroxy-3-methacryloylpropoxy)-biphenyl and 0.32 g (2,6 mol) dimethylamino pyridine were dissolved in 160 ml CH₂Cl₂/DMF (having a volume ratio 5:3). To the mixture were added 6,60 g (32 mmol) dicyclohexyl carbodiimid. Then the mixture were stirred for 27 hours at room temperature. After this time the precipitated solid was filtered off. To the filtrate were added 0.15 g BHT and the solvent was removed by vacuum distillation. The viscose residue was dissolved in 250 ml CH₂Cl₂and cooled to 0° C. The precipitating solid was removed and the filtrate was washed twice with 150 ml with 1 n HCl, 150 ml 1 n NaHCO₃solution and with 75 ml water and filtered over silica. Furthermore, the solution is dried over NaSO₄and the solvent is removed.

[0123] Yield: 6.9 g

[0124] Table 1 shows the Melting Points (° C.) of LC-Monomers II-VI and the glass transition temperatures of Examples 1 and 2.


LC-Monomer	R/X	Melting point (° C.)

EXAMPLE 3

Self-Curing, Two Component, Powder and Liquid Cement

[0125] 0.92 grams of the dried product prepared as described in Example 2 and 0.08 grams of triethyleneglycol dimethacrylate are dissolved in one another to form a liquid. 1.0 grams of this liquid is added to 2.0 grams of the strontium aluminofluorosilicate containing powder. The consistency of the mixture is suitable for use as a luting or crown and bridge or orthodontic cement or as a filling material. Polymerization is induced by the redox polymerization system of benzoyl peroxide, ascorbyl palmitate and copper acetyl acetonate. The powder and liquid compositions are as follows:


		PERCENT
		BY
		WEIGHT

[0126] The powder and liquid are mixed in a 1:1 ratio by volume to form a cement. This cement is adhesive to dentin and enamel without further treatment except cleansing with pumice.

EXAMPLE 4

[0127] Esterification of (2,2-Bis-[(2-hydroxy-3-methacryloyloxypropoxy)-phenyl]-propane) with 11-[4′(trans-4-propyl-cyclohexyl)-phenoxy]-undecane carboxylic acid

[0128] 1.50 g (3.73 mmol) 11-[4′(trans-4-propyl-cyclohexyl)-phenoxy]-undecane carboxylic acid. 0.87 g (1.69 mmol) (2.2-Bis-[p-(2-hydroxy-3-methacryloyloxypropoxy)-phenyl]-propane) and 0.05 g dimethylamino pyridine were dissolved in 20 ml CH₂Cl₂. To the mixture were added 0.85 g (4.10 mmol) dicydohexyl carbodiimid at 0° C. Then the mixture stirred for 24 hours at room temperature. After this time the precipitated solid was filtered off. To the filtrate were added 0.05 g BHT and the solvent was removed by vacuum distillation. The viscose residue was washed with pentane and filtered over aluminum oxide. The separation of the disubstituted product from mono-substituted impurities occurs by column chromatography(silica, CHCl₃). After evaporation of the solvent was obtained a highly viscous, slightly yellow liquid crystalline substance. The liquid crystalline dimethacrylate exhibits a glass transition temperature of T_g−10° C. It shows a liquid crystalline behavior between −10 and 19° C. (smectic phase). The yield is 0.77 g.

[0129] ¹³C-NMR: 14.4 (CH₂—CH₃). 18.3 (C═C—CH₃). 20.1 (CH₂—CH₃). 24.9-37.0 (aliphatic CH₂and cyclohexyl). 29.5 (C—CH₃). 39.8 (CH₂-cyclohexyl). 43.7 (C—CH₃). 62.9 (COO-CH₂). 66.3 (Ph-OCH₂). 69.4 (CH—O). 114.2-135.8 (aromatic carbons). 126.2 (═CH₂). 135.8 (═C). 157.2-157.5 (aromatic carbons). 166.9 (═C(CO₂)—). 173.1 ((CH₂)₄—CO₂—).

[0130] It should be understood that while the present invention has been described in considerable detail with respect to certain specific embodiments thereof, it should not be considered limited to such embodiments but may be used in other ways without departure from the spirit of the invention and the scope of the appended claims.

Claims

We claim:

1. A method of making a polymeric dental product comprising

providing a composition comprising a liquid crystalline compound, said liquid crystalline compound having a mesogenic group comprising two rings,

applying said liquid crystalline compound to a tooth in a patient's mouth, and

polymerizing said liquid crystalline compound to form a polymeric dental product.

2. The method of claim 1 wherein said composition further comprises filler.

3. The method of claim 2 wherein said mesogenic group is within the general formula

—A²—Z, —A²—R⁰₁—R²—Z, —A²—R⁰₁—R²—R⁰₂—R₃—Z

or a steroidal moiety, wherein

each A²independently is a cycloalkylene moiety having up to 30 carbon atoms

each R²independently is an aromatic moiety having up to 24 carbon atoms, a heteroaromatic moiety having up to 24 carbon atoms

each R³independently is an aromatic moiety having up to 24 carbon atoms, a heteroaromatic moiety having up to 24 carbon atoms or a cycloalrylene moiety having up to 30 carbon atoms, an alkylene moiety having up to 20 carbon atoms

each R⁰₁and R⁰₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O(CO)O, O, S, SO₂, OCS, CH₂—O, CH₂—S,

each L₁and L₂independently is a hydrogen, alkyl having 1 to 20 carbon atoms, alkylene having 2 to 20 carbon atoms or CN

Z is a hydrogen, halogen, CN, —OR, COOR, NO₂, a halogen alkylene or alkenyl having 1 to 20 carbon atoms, an alkylene or alkenyl having 1 to 20 carbon atoms, a halogen substituted oxyalkylene or oxyalkenyl having up to 20 carbon atoms, a oxyalkylene or oxyalkenyl having up to 20 carbon atoms, a halogen substituted thioalkylene or thioalkenyl having up to 20 carbon atoms, a thioalkylene or thioalkenyl having up to 20 carbon atoms, a halogen substituted carboxyalkylene or alkanoylenoxy having up to 20 carbon atoms or a carboxyalkylene or alkanoylenoxy having up to 20 carbon atoms.

4. The method of claim 1 wherein said liquid crystalline compound has a melting point below 20° C.

5. The method of claim 1 wherein said liquid crystalline compound is within the scope of the general formula

Q₁—Q₂—Q₃

wherein

—A—Z, —A³—R⁰₁—R⁴—Z, —A³—R⁰₁—R⁴—R₀₂—R⁵—Z

Q₁is a mesogenic group of the general formula

or a steroidal moiety, wherein

each A³, R⁴and R⁵independently is an aromatic moiety having 6 to 24 carbon atoms, a heteroaromatic moiety having 2 to 24 carbon atoms or a cycloalkylene moiety having 5 to 30 carbon atoms

each R⁰₁and R⁰₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O(CO)O, O, S, SO₂, OCS, CH₂—O, CH₂—S,

each L₁and L₂independently is a hydrogen, a alkylene having 1 to 20 carbon atoms or CN

Z is a hydrogen, CN, —OR, COOR, NO₂, alkyl having 1 to 20 carbon atoms, alkylene or alkenyl having 2 to 20 carbon atoms, halogen substituted alkylene or alkenyl having 2 to 20 carbon atoms, oxyalkylene or oxyalkenyl having 1 to 20 carbon atoms, a halogen substituted oxyalkylene or oxyalkenyl having 1 to 20 carbon atoms, thioalkylene or thioalkenyl having 1 to 20 carbon atoms, a halogen substituted thioalkylene or thioalkenyl having 1 to 20 carbon atoms, carboxyalkylene or alkanoylenoxy having 1 to 20 carbon atoms,

a halogen substituted carboxyalkylene or alkanoylenoxy having 1 to 20 carbon atoms,

Q₂is a covalent bond or an alkylene having 1 to 20 carbon atoms, oxyalkylene having 1 to 20 carbon atoms, thioalkylene having 1 to 20 carbon atoms or a carboxyalkylene having 2 to 20 carbon atoms,

Q₃is hydrogen, —OCH₃, —OH, —Cl, —Br, —COOH, —NCO, or Si(R₃H₅O)₃.

6. The method of claim 1 wherein said composition further comprises at least 25 percent by volume of a volatile organic solvent.

7. The method of claim 1 wherein said composition is a dental cement and further comprises at least 20 percent by volume filler.

8. The method of claim 1 wherein said compound is within the general formula:

wherein

R₃is a covalent bond, alkyl having 1 to 20 carbon atoms, an alkylene having 2 to 20 carbon atoms, halogen substituted alkylene having 2 to 20 carbon atoms, oxyalkylene having 1 to 20 carbon atoms, thioalkylene having 1 to 20 carbon atoms or a carboxyalkylene having 2 to 20 carbon atoms

R₄is hydrogen, halogen substituted alkyl having 1 to 20 carbon atoms, an alkyl having 1 to 20 carbon atoms, cycloalkyl having 5 to 12 carbon atoms, or aryl having 6 to 20 carbon atoms,

Z is a hydrogen, halogen, CN, —OR, COOR, NO₂, a halogen, alkyl having 1 to 20 carbon atoms, an alkylene or alkenyl having 2 to 20 carbon atoms, a halogen oxyalkylene or oxyalkenyl having 1 to 20 carbon atoms, an oxyalkylene or oxyalkenyl having 1 to 20 carbon atoms, a halogen thioalkylene or thioalkenyl having 1 to 20 carbon atoms, a thioalkylene or thioalkenyl having 1 to 20 carbon atoms, a halogen carboxyalkylene or alkanoylenoxy having 1 to 20 carbon atoms, or a carboxyalkylene or alkanoylenoxy having 1 to 20 carbon atoms,

X is a covalent bond, CO, NHCO, OCO.

9. The method of claim 1 wherein said liquid crystalline compound is liquid at 23° C. and is within the general formula:

wherein

—A²—Z, —A²—R⁰₁—R₂—Z, —A²—R⁰₁—R²—R⁰₂—R₃—Z

R₃is a covalent bond, alkyl having 1 to 20 carbon atoms, alkylene having 2 to 20 carbon atoms, halogen alkylene having 2 to 20 carbon atoms, oxyalkylene having 1 to 20 carbon atoms, thioalkylene having 2 to 20 carbon atoms or a carboxyalkylene having 2 to 20 carbon atoms

M is a mesogenic group comprising two rings and of the general formula:

or a steroidal moiety, wherein

each A², R²and R³independently is an aromatic moiety having 6 to 24 carbon atoms, a heteroaromatic moiety having 6 to 24 carbon atoms or a cycloalkylene moiety having 5 to 30 carbon atoms

each R⁰₁and R⁰₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O(CO)O, O, S, SO₂, OCS, CH₂—O, CH₂—S,

each L₁and L₂independently is hydrogen, alkyl having 1 to 20 carbon atoms, alkylene having 2 to 20 carbon atoms or CN

Z is hydrogen, CN, —OR, COOR, NO₂, halogen, alkyl having 1 to 20 carbon atoms, alkylene or alkylidene having 2 to 20 carbon atoms, halogen substituted alkylene or alkylidene having 2 to 20 carbon atoms, oxyalkylene or oxyalkylidene having 1 to 20 carbon atoms, a halogen substituted oxyalkylene or oxyalkylidene having 1 to 20 carbon atoms, thioalkylene or thioalkylidene having 1 to 20 carbon atoms, a halogen substituted thioalkylene or thioalkylidene having 1 to 20 carbon atoms, carboxyalkylene or alkanoylenoxy having 2 to 20 carbon atoms, a halogen substituted carboxyalkylene or alkanoylenoxy having 2 to 20 carbon atoms;

each A₂independently is an aromatic moiety having up to 24 carbon atoms, a heteroaromatic moiety having up to 24 carbon atoms

each R²and R³independently is an aromatic moiety having up to 24 carbon atoms, a heteroaromatic moiety having up to 24 carbon atoms or a cycloalkylene moiety having up to 30 carbon atoms

each R⁰₁and R⁰₂independently is a covalent bond, OCO, N═N, CH═N, C═C, CO, O(CO)O, O, S, SO₂, OCS, CH₂—O, CH₂—S,

each L₁and L₂independently is a hydrogen, alkyl having 1 to 20 carbon atoms, alkylene having 1 to 20 carbon atoms or CN

Z is hydrogen, halogen, CN, —OR, COOR, NO₂, alkyl having 1 to 20 carbon atoms, alkylene or alkylidene having up to 20 carbon atoms, halogen substituted alkylene or alkylidene having up to 20 carbon atoms, oxyalkylene or oxyalkylidene having up to 20 carbon atoms, a halogen substituted oxyalkylene or oxyalkylidene having up to 20 carbon atoms, thioalkylene or thioalkylidene having up to 20 carbon atoms, a halogen substituted thioalkylene or thioalkylidene having up to 20 carbon atoms, carboxyalkylene or alkanoylenoxy having 2 to 20 carbon atoms, a halogen substituted carboxyalkylene or alkanoylenoxy having 2 to 20 carbon atoms,

X is a covalent bond, CO, NHCO, OCO

n is an integer from 1 to 10, said liquid crystalline compound being in a mesomorphic state.

10. The method of claim 1 wherein said composition comprises at least 50 percent by weight of particles of filler.

11. The method of claim 1 wherein said composition further comprises a polymerization initiator.

12. The method of claim 1 wherein said composition further comprises a photoinitiator.

13. The method of claim 1 wherein said composition further comprises at least 30 percent by weight particles of filler.

14. The method of claim 1 wherein said composition further comprises at least 30 percent by weight of a volatile organic solvent.

15. The method of claim 1 wherein said compound is a liquid crystalline between −10° C. and 19° C.

16. A dental material comprising:

at least one polymerizable monomer which has liquid crystalline properties and mesogenic groups; and

a polymerization initiator which initiates polymerization of the at least one polymerizable monomer.

17. A method of producing a polymerized dental material comprising:

providing a polymerizable monomer with liquid crystalline properties and mesogenic groups;

mixing the polymerizable monomer with a polymerization initiator to form a mixture; and polymerizing the mixture to produce a dental material.

18. The method of claim 17 further comprising adding a filler to the mixture prior to said polymerizing.

19. A dental material comprising:

at least one polymerizable monomer having liquid crystalline properties and mesogenic groups;

at least one filler; and

a polymerization initiator adapted to initiate polymerization of said polymerizable monomer.

20. The dental material according to claim 19, wherein said polymerizable monomer has said liquid crystalline properties below 50° C.

21. The dental material according to claim 19, characterized in that said polymerizable monomer has at least one or more polymerizable groups.

22. The dental material according to claim 21, wherein said polymerizable groups are selected from the group consisting of one or more ethylenically unsaturated groups, one or more epoxide groups, and vinyl ether groups.

23. The dental material according to claim 19, wherein said polymerizable monomer has one or more mesogenic groups.

24. A method of producing a polymerized dental material comprising:

providing a polymerizable monomer having liquid crystalline properties and mesogenic groups;

mixing the polymerizable monomer and a polymerization initiator to form a mixture; and

polymerizing the mixture to produce a polymerized dental material.

25. A method of producing a polymerized dental material comprising:

providing a composition comprising a polymerization initiator and a polymerizable monomer having liquid crystalline properties and mesogenic groups; and

polymerizing the composition to produce a polymerized dental material.

26. The method of claim 25 further comprising applying said composition to a tooth in a patient's mouth.

27. The method of claim 26 wherein said composition further comprises at least 20 percent by weight of a filler.

Patent Citations (280)

Patent	Date	Inventor	Cited By
US150262(A)	1874-04-01	Slavin	Applicant
US173850(A)	1876-02-01	Emde	Applicant
US212975(A)	1879-04-01	Perkins et al.	Applicant
US543829(A)	1895-07-01	Gurnee	Applicant
US3066112(A)	1962-11-01	Bowen	Applicant
USD195391(S)	1963-06-01	Pakison	Applicant
US3150801(A)	1964-09-01	Hamilton	Applicant
US3200142(A)	1965-08-01	Bowen	Applicant
US3256226(A)	1966-06-01	Fekete	Applicant
US3317469(A)	1967-05-01	Feichtinger et al.	Applicant
US3327016(A)	1967-06-01	Lee	Applicant
US3327017(A)	1967-06-01	Huang et al.	Applicant
US3466259(A)	1969-09-01	Jernigan	Applicant
US3503128(A)	1970-03-01	Boyd et al.	Applicant
US3539533(A)	1970-11-01	Lee, II et al.	Applicant
US3564074(A)	1971-02-01	Swisher et al.	Applicant
US3586527(A)	1971-06-01	Aronoff et al.	Applicant
US3595969(A)	1971-07-01	Shepherd et al.	Applicant
US3634542(A)	1972-01-01	Dowd et al.	Applicant
US3673558(A)	1972-06-01	Toepel et al.	Applicant
US3709866(A)	1973-01-01	Waller	Applicant
US3742949(A)	1973-07-01	Hill	Applicant
US3754054(A)	1973-08-01	Khnura et al.	Applicant
US3769336(A)	1973-10-01	Lee, Jr. et al.	Applicant
US3815239(A)	1974-06-01	Lee, Jr. et al.	Applicant
US3835090(A)	1974-09-01	Gander et al.	Applicant
US3845009(A)	1974-10-01	Gander	Applicant
US3853962(A)	1974-12-01	Gander	Applicant
US3882187(A)	1975-05-01	Takiyama et al.	Applicant
US3889385(A)	1975-06-01	Dougherty	Applicant
US3926906(A)	1975-12-01	Lee, II et al.	Applicant
US3971765(A)	1976-07-01	Green et al.	Applicant
US3973972(A)	1976-08-01	Muller	Applicant
US3980483(A)	1976-09-01	Nishikubo et al.	Applicant
US4002669(A)	1977-01-01	Gross et al.	Applicant
US4051195(A)	1977-09-01	McWhorter	Applicant
US4081492(A)	1978-03-01	Traenckner et al.	Applicant
US4097569(A)	1978-06-01	Waters	Applicant
US4097994(A)	1978-07-01	Reaville et al.	Applicant
US4098735(A)	1978-07-01	Tobias	Applicant
US4100045(A)	1978-07-01	Bogan et al.	Applicant
US4135868(A)	1979-01-01	Schainholz	Applicant
US4141865(A)	1979-02-01	Bogan	Applicant
US4150012(A)	1979-04-01	Joos	Applicant
US4177563(A)	1979-12-01	Schmitz-Josten et al.	Applicant
US4182035(A)	1980-01-01	Yamauchi et al.	Applicant
US4182833(A)	1980-01-01	Hicks	Applicant
US4197390(A)	1980-04-01	Jackson	Applicant
US4220582(A)	1980-09-01	Orlowski et al.	Applicant
US4229376(A)	1980-10-01	Rogier	Applicant
US4253830(A)	1981-03-01	Kazen et al.	Applicant
US4255468(A)	1981-03-01	Olson	Applicant
US4256457(A)	1981-03-01	Behring	Applicant
US4284742(A)	1981-08-01	Bowerman, Jr. et al.	Applicant
US4293074(A)	1981-10-01	Dunsky	Applicant
US4296004(A)	1981-10-01	Rogier	Applicant
US4308085(A)	1981-12-01	Horhold et al.	Applicant
US4362889(A)	1982-12-01	Bowen	Applicant
US4368889(A)	1983-01-01	Reker, Jr.	Applicant
US4383826(A)	1983-05-01	Butler et al.	Applicant
US4383879(A)	1983-05-01	Le Du et al.	Applicant
US4384853(A)	1983-05-01	Welsh	Applicant
US4391590(A)	1983-07-01	Dougherty	Applicant
US4405766(A)	1983-09-01	Bertram et al.	Applicant
US4406625(A)	1983-09-01	Orlowski et al.	Applicant
US4413105(A)	1983-11-01	Koenig	Applicant
US4431421(A)	1984-02-01	Kawahara et al.	Applicant
US4446246(A)	1984-05-01	McGinniss	Applicant
US4467079(A)	1984-08-01	Hechenberger et al.	Applicant
US4514342(A)	1985-04-01	Billington et al.	Applicant
US4515634(A)	1985-05-01	Wu et al.	Applicant
US4524161(A)	1985-06-01	Feuerhahn	Applicant
US4541992(A)	1985-09-01	Jerge et al.	Applicant
US4547531(A)	1985-10-01	Waknine	Applicant
US4548689(A)	1985-10-01	Sakashita et al.	Applicant
US4557848(A)	1985-12-01	Sung et al.	Applicant
US4569662(A)	1986-02-01	Dragan	Applicant
US4579904(A)	1986-04-01	Orlowski et al.	Applicant
US4595734(A)	1986-06-01	O'Hearn	Applicant
US4629746(A)	1986-12-01	Michl et al.	Applicant
US4643303(A)	1987-02-01	Arp et al.	Applicant
US4656031(A)	1987-04-01	Lane et al.	Applicant
US4714751(A)	1987-12-01	Schornick et al.	Applicant
US4758643(A)	1988-07-01	Tanaka et al.	Applicant
US4767326(A)	1988-08-01	Bennett et al.	Applicant
US4774063(A)	1988-09-01	Runnells	Applicant
US4781921(A)	1988-11-01	Smith et al.	Applicant
US4789620(A)	1988-12-01	Sasaki et al.	Applicant
US4806381(A)	1989-02-01	Engelbrecht et al.	Applicant
US4816495(A)	1989-03-01	Blackwell et al.	Applicant
US4816528(A)	1989-03-01	Dervan et al.	Applicant
US4854475(A)	1989-08-01	Riihimaki et al.	Applicant
US4863993(A)	1989-09-01	Montgomery	Applicant
US4866146(A)	1989-09-01	Janda et al.	Applicant
US4872936(A)	1989-10-01	Engelbrecht	Applicant
US4874799(A)	1989-10-01	Hung et al.	Applicant
US4883899(A)	1989-11-01	Muramoto et al.	Applicant
US4918136(A)	1990-04-01	Kawaguchi et al.	Applicant
US4931096(A)	1990-06-01	Fujisawa et al.	Applicant
US4936775(A)	1990-06-01	Bennett	Applicant
US4950697(A)	1990-08-01	Chang et al.	Applicant
US4959199(A)	1990-09-01	Brewer	Applicant
US4963093(A)	1990-10-01	Dragan	Applicant
US4964911(A)	1990-10-01	Ibsen et al.	Applicant
US4969816(A)	1990-11-01	Drumm	Applicant
US4985198(A)	1991-01-01	Hirawawa et al.	Applicant
US4985516(A)	1991-01-01	Sakashita et al.	Applicant
USD315956(S)	1991-04-01	Dragan	Applicant
US5006066(A)	1991-04-01	Rouse	Applicant
US5032669(A)	1991-07-01	Kantor et al.	Applicant
US5052927(A)	1991-10-01	Discko, Jr.	Applicant
US5063255(A)	1991-11-01	Hasegawa et al.	Applicant
US5083921(A)	1992-01-01	Dragan	Applicant
US5100320(A)	1992-03-01	Martin et al.	Applicant
US5106301(A)	1992-04-01	Miyahara et al.	Applicant
US5108287(A)	1992-04-01	Yee et al.	Applicant
US5122057(A)	1992-06-01	Discko, Jr.	Applicant
US5129825(A)	1992-07-01	Discko, Jr.	Applicant
US5137990(A)	1992-08-01	Corley	Applicant
US5151479(A)	1992-09-01	Mukai et al.	Applicant
US5165890(A)	1992-11-01	Discko, Jr.	Applicant
US5166117(A)	1992-11-01	Imai et al.	Applicant
US5172810(A)	1992-12-01	Brewer	Applicant
US5173273(A)	1992-12-01	Brewer	Applicant
US5178851(A)	1993-01-01	Gaffar et al.	Applicant
US5189077(A)	1993-02-01	Kerby	Applicant
US5204398(A)	1993-04-01	Cohen et al.	Applicant
US5210157(A)	1993-05-01	Schutyser et al.	Applicant
US5215726(A)	1993-06-01	Kudla et al.	Applicant
US5217372(A)	1993-06-01	Truocchio	Applicant
US5235008(A)	1993-08-01	Hefner, Jr. et al.	Applicant
US5236362(A)	1993-08-01	Cohen et al.	Applicant
US5252629(A)	1993-10-01	Imai et al.	Applicant
US5267859(A)	1993-12-01	Discko, Jr.	Applicant
US5279800(A)	1994-01-01	Berr, Jr.	Applicant
US5284632(A)	1994-02-01	Kudla et al.	Applicant
US5294413(A)	1994-03-01	Riihimaki et al.	Applicant
US5322440(A)	1994-06-01	Steele	Applicant
US5324273(A)	1994-06-01	Discko, Jr.	Applicant
US5340551(A)	1994-08-01	Berry, Jr.	Applicant
US5346677(A)	1994-09-01	Risk	Applicant
US5360877(A)	1994-11-01	Hwang et al.	Applicant
USD353673(S)	1994-12-01	Discko, Jr. et al.	Applicant
US5384103(A)	1995-01-01	Miller	Applicant
USRE35135(E)	1995-12-01	Sakashita et al.	Applicant
US5567349(A)	1996-10-01	Kelly et al.	Applicant
US6031015(A)	2000-02-01	Ritter et al.	Examiner
CA563464	1958-09-01		Applicant
CA817442	1969-07-01		Applicant
CA878004	1971-08-01		Applicant
CA878006	1971-08-01		Applicant
CA1107751	1971-08-01		Applicant
CA966500	1975-04-01		Applicant
CA983491	1976-02-01		Applicant
CA987044	1976-04-01		Applicant
CA995667	1976-08-01		Applicant
CA1018294	1977-09-01		Applicant
CA1030979	1978-05-01		Applicant
CA1099848	1981-04-01		Applicant
CA1100990	1981-05-01		Applicant
CA1107293	1981-08-01		Applicant
CA1115289	1981-12-01		Applicant
CA1131827	1982-09-01		Applicant
CA1140939	1983-02-01		Applicant
CA1151667	1983-08-01		Applicant
CA1153391	1983-09-01		Applicant
CA1155141	1983-10-01		Applicant
CA1175196	1984-09-01		Applicant
CA1183144	1985-02-01		Applicant
CA1185982	1985-04-01		Applicant
CA1189996	1985-07-01		Applicant
CA1200555	1986-02-01		Applicant
CA1202749	1986-04-01		Applicant
CA1210777	1986-09-01		Applicant
CA1219990	1987-03-01		Applicant
CA1227202	1987-09-01		Applicant
CA1235423	1988-04-01		Applicant
CA1248126	1989-01-01		Applicant
CA1258465	1989-08-01		Applicant
CA2002017	1990-05-01		Applicant
CA1270846	1990-06-01		Applicant
CA2005912	1990-06-01		Applicant
CA2006431	1990-06-01		Applicant
CA2006432	1990-06-01		Applicant
CA2006433	1990-06-01		Applicant
CA2006434	1990-06-01		Applicant
CA2004624	1990-07-01		Applicant
CA2026009	1990-07-01		Applicant
CA1272735	1990-08-01		Applicant
CA2008895	1990-08-01		Applicant
CA2009471	1990-08-01		Applicant
CA2012824	1990-09-01		Applicant
CA2014027	1990-10-01		Applicant
CA2014359	1990-10-01		Applicant
CA1276168	1990-11-01		Applicant
CA1276648	1990-11-01		Applicant
CA1277070	1990-11-01		Applicant
CA2054747	1990-11-01		Applicant
CA2010210	1990-12-01		Applicant
CA2018728	1990-12-01		Applicant
CA2019410	1990-12-01		Applicant
CA2054710	1990-12-01		Applicant
CA2054757	1990-12-01		Applicant
CA1281734	1991-03-01		Applicant
CA2026467	1991-03-01		Applicant
CA1283121	1991-04-01		Applicant
CA1283663	1991-04-01		Applicant
CA2027887	1991-04-01		Applicant
CA2042587	1991-04-01		Applicant
CA2028728	1991-05-01		Applicant
CA2032556	1991-06-01		Applicant
CA2033405	1991-07-01		Applicant
CA2035650	1991-08-01		Applicant
CA2026417	1991-09-01		Applicant
CA2038332	1991-09-01		Applicant
CA1290766	1991-10-01		Applicant
CA2045762	1991-12-01		Applicant
CA2046373	1992-01-01		Applicant
CA1296015	1992-02-01		Applicant
CA2049725	1992-03-01		Applicant
CA2061230	1992-08-01		Applicant
CA2061539	1992-08-01		Applicant
CA2041828	1992-11-01		Applicant
CA1242213	1998-09-01		Applicant
CZ227363	1984-01-01		Applicant
DE1003448	1958-08-01		Applicant
DE2126419	1971-12-01		Applicant
DE141667	1980-05-01		Applicant
DE154945	1982-06-01		Applicant
DE209358	1984-04-01		Applicant
DE208365	1984-05-01		Applicant
DE214381	1984-10-01		Applicant
DE229140	1985-10-01		Applicant
DE244748	1987-04-01		Applicant
DE3536076	1987-04-01		Applicant
DE3536077	1987-04-01		Applicant
DE248598	1987-08-01		Applicant
DE261365	1988-10-01		Applicant
DE277078	1990-03-01		Applicant
DE277689	1990-04-01		Applicant
DE279667	1990-08-01		Applicant
DE295758	1991-11-01		Applicant
DE4141174	1992-06-01		Applicant
DE4109048	1992-09-01		Applicant
DE4217761	1993-02-01		Applicant
EP37759	1981-10-01		Applicant
EP120559	1983-01-01		Applicant
EP104491	1984-04-01		Applicant
EP115410	1984-04-01		Applicant
EP115948	1984-08-01		Applicant
EP188752	1984-12-01		Applicant
EP212193	1987-03-01		Applicant
EP219058	1987-04-01		Applicant
EP277413	1988-10-01		Applicant
EP356868	1990-03-01		Applicant
EP367341	1990-05-01		Applicant
EP379058	1990-07-01		Applicant
EP675186	1995-10-01		Applicant
GB1304987	1973-01-01		Applicant
GB2045269	1980-10-01		Applicant
GB2199839	1988-07-01		Applicant
JP57042977	1982-03-01		Applicant
JP62063541	1987-03-01		Applicant
JP3-27308	1989-06-01		Applicant
JP1-143846	1989-06-01		Applicant
JP1-254727	1989-10-01		Applicant
JP4-4219	1992-01-01		Applicant
JP4-120540	1992-04-01		Applicant
SU52106	1937-11-01		Applicant
SU311637	1971-08-01		Applicant
SU311638	1971-08-01		Applicant
SU349396	1972-09-01		Applicant
SU545353	1977-02-01		Applicant
SU549150	1977-03-01		Applicant
SU1050706	1982-04-01		Applicant
SU1510131	1986-11-01		Applicant
WO90/15083	1990-12-01		Applicant
WO90/15084	1990-12-01		Applicant
WO91/03502	1991-03-01		Applicant
WO93/10176	1993-05-01		Applicant

Non-Patent Literature (22)

Ullmann's Encyclopedia of Industrial Chemistry, fifth edition, vol. A8, “Dental Materials”, pp. 281-282 (1987).Applicant
Antonucci, et al., “New Initiator Systems for Dental Resins Based on Ascorbic Acid,” J. Dent. Res., 58(9): 19887-1899 (1979).Applicant
Kawaguchi, et al., “Synthesis and Physical Properties of Polyfunctional Methacrylates (Part 4). Synthesis and Physical Properties of Aromatic Dimethacrylate Copolymers,” Dental Materials Journal, 3(2): 272-279 (1984).Applicant
Lal et al; Journal of Polymer Science: vol. XXIV, pp. 75-84 (1957) New Pllymerization Catalysts for Methyl Methacrylate.Applicant
Beaunez et al: Journal of Polymer Science: Part A: Polymer Chemistry, vol. 32, pp. 1459-1469 (1994).Applicant
Antonucci et al; Journal of Dental Research 58(9), pp. 1887-1899, Sep. 1979; New Initiator Systems for Dental Resins based on Ascorbic Acid.Applicant
Chemistry Abstract 115 (1991) 78952z and Chemistry Abstract 115 (1991) 78973g.Applicant
Klee et al, Polymer Bulletin 27 (1992); pp. 511-517.Applicant
Chemical Abstract, vol. 89, No. 18, Oct. 30, 1978, Columbus OH, US; Abstract No. 148211C; p. 71, Column 2; abstract & Lakokras Mater. IKH, Primen., No. 4, 1978, pp. 50-52.Applicant
Dusek et al; American Chemical Society (1984) Transesterification and Gelation of Polyhydroxy Esters Formed from Diepoxides and Dicarboxylic Acids.Applicant
Hartel et al; (Nov. 1984) Zur Synthese linearer Additionspolymere aus Diandiglycidether und Dicarbonsauren.Applicant
Klee; Acta Polymer 44, 163-167 (1993); Synthesis and investigation of α, w-methacryloyl poly (epoxide-carboxylic acid and α, w-methacryloyl poly (epoxide-phenol)—macromonomers.Applicant
J. Klee et al, Acta Polymer 42 (1991) 17-20.Applicant
Fukushima et al; Dental Materials Journal 4(1): pp. 33-39 (1985): Application of Functional Monomers for Dental Use (Part 9) Sysntheses of Succinoxy Methacrylates and Their Adhesion to Polished and Etched Tooth Surfaces.Applicant
Lin et al; Journal of Polymer Science; Part A: Polymer Chemistry, vol. 30, 1941-1951 (1992).Applicant
Allard et al; Journal of Polymer Science: Polymer Chemistry Edition, vol. 22, 3827-3842 (1984).Applicant
Hage et al; American Chemical Society (1986) Poly(acrylourethane)—Polyepoxide Semi-interpenetrating Networks Formed by Electron-Beam Curing.Applicant
Dubuisson et al; Rheol. Acta 20, 463-470 (1981).Applicant
Klee; Acta Polymer., 45, 73-82 (1994) Telechelic prepolymers and macromonomers by step growth processes.Applicant
John Wiley & Sons; Encyclopedia of Polymer Science and Engineering, vol. 8, Identification to Lignin (1987).Applicant
Litt et al, J. Polymer Science, Part A: Polymer Chemistry; “Crosslinked Liquid Crystal Polymers from Liquid Crystal Monomers: Synthesis and Mechanical Properties” vol. 31, No. 1, pp. 183-191; 1993.Applicant
Holter et al, Macromolecules (MAMOBX, 00249297); “Liquid Crystalline Themosets Based on Branched Bismethacrylates”; vol. 29 (22); pp. 7003-7011 (1996).Applicant

Abstract