US 6,143,617 AGrant
Composite Capacitor Electrode for a DRAM Cell
Issue Date:2000-11-07
•18 Claims
•5 Drawing Sheets
Abstract
A process for creating a storage node electrode, for a DRAM cell, exhibiting increased surface area resulting from the formation of an agglomerated metal silicide layer, on the top surface of the storage node electrode, has been developed. The process features creating a polysilicon, storage node electrode shape, followed by the formation of an overlying, agglomerated titanium disilicide layer. The agglomerated titanium disilicide layer is formed from a RTA procedure, applied to a smooth titanium disilicide layer, located on the polysilicon, storage node electrode.
Metadata
Assignee
- Taiwan Semiconductor Manufacturing Company
Inventors
- Shau-Lin Shue
- Cheng-Yeh Shih
Application Information
Application Number:US 0277614
Filing Date:1998-02-23
Priority Date:1998-02-23
Art Unit:175
Classifications
IPC:
H01L 2120H01L 21311
Field of Search:
438387;389;396;397;398;399;391;706;712
Patent Drawings (5 sheets)
Description
Background of the Invention
(1) Field of the Invention
This invention relates to methods used to create semiconductor memory devices, and more specifically to a method used to create a capacitor structure, for a dynamic random access memory, (DRAM), device.
(2) Description of Prior Art
The semiconductor industry is continually striving to increase the density of DRAM chips, while still attempting to maintain, or increase the performance of the DRAM devices. The decreasing dimensions used to obtain high density DRAM devices, have resulted in difficulties in maintaining, or increasing the capacitance, for the high density DRAM devices. The capacitance of a stacked capacitor structure is positively influenced by decreasing the thickness of the dielectric layer, residing between conductive capacitor plates. Capacitance may also be increased by increasing the area of the capacitor. However decreasing the already thin dielectric layers, now used for DRAM capacitors, can lead to yield and reliability concerns, while stacked capacitor structures, formed in an area overlying transfer gate transistors, are now limited in dimension by the shrinking size of the underlying transfer gate transistor, thus limiting available capacitor area.
An approach used to increase stacked capacitor area, without increasing the length and width of the storage node electrode, of the stacked capacitor structure, has been the use of a roughened surface, storage node electrode. The roughened surface, storage node electrode, comprised of concave and convex features, results in an increase in storage node electrode surface area, when compared to flat surface, storage node electrode counterparts. One method used to create roughened surface, storage node electrodes, has been the use of hemi-spherical grain (HSG), silicon for the upper layer of the storage node electrode. Lou, et al, in U.S. Pat. No. 5,597,754, describe a process for forming an HSG, silicon layer on an underlying polysilicon layer, and patterning these layers to form the increased surface area, storage node electrode, for the capacitor structure of DRAM device. However the HSG silicon solution can be difficult to control, since the amount of HSG silicon roughness is obtainable only in a narrow range of deposition conditions, such as temperature and pressure. This invention will show an alternative to the HSG silicon solution, in which the surface roughness, of the storage node electrode, is established using a composite layer of titanium disilicide, on a polysilicon layer. The desired roughness is accomplished via specific heat treatment processes, resulting in agglomeration of the titanium disilicide layer, producing the desired roughened surface. Prior art, such as Armacost et al, in U.S. Pat. No. 5,466,626, suggest the use of agglomerated titanium disilicide as an etch mask, to create crevices, or a roughened surface, in an underlying polysilicon layer, with the titanium disilicide layer, subsequently removed. This invention however will use the agglomerated layer as a critical component of the composite layered, storage node electrode.
Summary of the Invention
It is an object of this invention to increase the surface area of a storage node electrode of a capacitor structure, used for a DRAM device.
It is another object of this invention to form a storage node electrode comprised of a composite layer of metal silicide on a polysilicon layer.
It is still another object of this invention to increase the surface area of the storage node electrode by converting a smooth surface of the metal silicide layer, to a roughened surface, via an agglomeration process.
In accordance with the present invention a process is described for forming a composite layered, storage node electrode, for a DRAM device, in which the surface area of the storage node electrode is increased as a result of the use of an agglomerated metal silicide layer, used as the upper layer of the composite layered, storage node electrode. An underlying transfer gate transistor is provided with a storage node contact hole, opened in an insulator layer, exposing a source and drain region of the underlying transfer gate transistor. A conductive contact plug is formed in the storage node contact hole followed by the deposition of a first polysilicon layer, and of an overlying insulator layer. A mesa shape, comprised of the insulator layer, and of the first polysilicon layer, is formed on the underlying composite insulator layer, and contacting the top surface of the conductive contact plug, in the storage node contact hole. A second polysilicon layer is deposited and subjected to an anisotropic reactive ion etch, (RIE), procedure, resulting in second polysilicon layer spacers, formed on the sides of the mesa shape. Removal of the insulator layer, exposed in the mesa shape, results in a polysilicon cylindrical profile, comprised of a bottom polysilicon shape, formed from the first polysilicon layer, and vertical polysilicon shapes, formed from the second polysilicon layer. A metal layer is next deposited, and annealed to convert the metal layer, to a metal silicide layer, in regions in which the metal layer interfaced the polysilicon cylindrical profile, followed by selective removal of the unreacted metal layer. A second anneal is used to convert the smooth surfaced, metal silicide layer, on the underlying polysilicon cylindrical profile, to a roughened surface, metal silicide layer, resulting in a storage node electrode, with increased surface area. The formation of a dielectric layer, on the roughened surface metal silicide layer, followed by the formation of an overlying polysilicon electrode, complete the fabrication of the DRAM capacitor structure, featuring increased surface area, as a result of a roughened surface, storage node electrode.
Brief Description of the Drawings
The object and other advantages of this invention are best described in the preferred embodiment with reference to the attached drawings that include:
FIGS. 1-9, which schematically, in cross-sectional style, describe the process of forming a storage node electrode, for a DRAM cell, in which the surface of the storage node electrode is comprised of an agglomerated, metal silicide layer.
Description of the Preferred Embodiment
The process used to create a storage node electrode, for a DRAM cell, in which the surface area of the storage node electrode is increased via use of an agglomerated, metal silicide layer, will now be described in detail. The storage node electrode, comprised of an agglomerated, metal silicide layer, and used as part of a capacitor structure for a DRAM cell, will be applied to a DRAM cell featuring an N channel, transfer gate transistor. However this invention can be easily implemented using a DRAM cell with a P channel, transfer gate transistor. In addition, this invention illustrates a cylindrical shaped, capacitor structure, for the DRAM cell. However it should be noted that this invention, the formation of an agglomerated, metal silicide layer, for a storage node electrode, can be applied to any desired storage node electrode shape.
FIG. 1, schematically describes, in cross-sectional style, the formation of the transfer gate transistor, used for the DRAM cell, that will subsequently accept an overlying stacked capacitor structure, featuring a storage node electrode, comprised of an agglomerated, metal silicide layer. A P type, semiconductor substrate 1, comprised of single crystalline silicon, with a <100> crystallographic orientation, is used. A shallow trench isolation, (STI), region 2, is formed in semiconductor substrate 1, to a depth between about 3000 to 5000 Angstroms. STI region 2, is formed via initially creating a shallow trench in semiconductor substrate 1, using conventional photolithographic and reactive ion etching, (RIE), procedures, using Cl.sub.2 as an etchant, and after removal of the patterning photoresist shape, filling the shallow trench with an insulator layer, such as SiO.sub.2. Removal of unwanted insulator layer is accomplished using either an anisotropic RIE procedure, or a chemical mechanical polishing procedure, (CMP), resulting in the insulator filled, STI region 2, shown schematically in FIG. 1.
A gate insulator layer 3, of silicon dioxide, is thermally grown, followed by the deposition of a polysilicon layer, accomplished via a low pressure chemical vapor deposition, (LPCVD), procedure. The polysilicon layer can be doped during an in situ deposition procedure, via the addition of arsine or phosphine, to a silane ambient, or the polysilicon layer can be deposited intrinsically and doped via ion implantation of either arsenic or phosphorous. Conventional photolithographic and RIE procedures, using Cl.sub.2 as an etchant, are used to create polysilicon gate structure 4, shown schematically in FIG. 1. After photoresist removal, accomplished via plasma oxygen ashing and careful wet cleans, a lightly doped source and drain region 5, is created via an ion implantation procedure of arsenic or phosphorous. Insulator spacers 6, are formed on the sides of polysilicon gate structure 4, via initially depositing a silicon oxide, or a silicon nitride layer, via an LPCVD or a plasma enhanced chemical vapor deposition, (PECVD), procedure, followed by an anisotropic RIE procedure, using CHF.sub.3 as an etchant. A heavily doped source and drain region 7, is than formed, again via ion implantation procedures, again using arsenic or phosphorous. The result of these procedures is schematically shown in FIG. 1. An insulator layer 8, comprised of silicon oxide, is deposited using LPCVD or PECVD procedures. A CMP procedure is used for planarization purposes, creating a smooth top surface for insulator layer 8, shown schematically in FIG. 1.
A storage node contact hole 10, is formed in insulator layer 8, exposing the top surface of heavily doped source and drain region 7. Storage node contact hole 10, is formed using conventional photolithographic and RIE procedures, using CHF.sub.3 as an etchant. After removal of the photoresist shape used as a mask for storage node contact hole formation, via plasma oxygen ashing and careful wet cleans, a conductive plug 11, is formed in storage node contact hole 10. Conductive plug 11, can be tungsten, tungsten silicide, or doped polysilicon. The conductive plug is formed via deposition of tungsten, tungsten silicide, or doped polysilicon, using LPCVD procedures, followed by removal of unwanted material, via a selective RIE procedure, using Cl.sub.2 as an etchant, or via a CMP procedure, creating conductive plug 11, in storage node contact hole 10, schematically shown in FIG. 2.
A polysilicon layer 12a, is next deposited via LPCVD procedures. Polysilicon layer 12a, is doped either during an in situ deposition procedure, via the addition of arsine, or phosphine, to a silane ambient, or polysilicon layer 12a can be deposited intrinsically and doped via ion implantation procedures, using arsenic or phosphorous. An insulator layer 13a, comprised of either boro-phosphosilicate glass, (BPSG), or phosphosilicate glass, (PSG), is deposited on polysilicon layer 12a, via PECVD or LPCVD procedures. A photoresist shape 14, shown schematically in FIG. 3, is formed on insulator 13a. A selective, anisotropic RIE procedure, using CHF.sub.3 as an etchant for insulator layer 13a, and using Cl.sub.2 as an etchant for polysilicon layer 12a, is used to create insulator mesa 13b, and polysilicon shape 12b, directly underlying insulator mesa 13b. After removal of photoresist shape 14, via plasma oxygen ashing and careful wet cleans, polysilicon layer 15a, is deposited, via LPCVD procedures, using an N type in situ doping procedure, to a thickness between about 500 to 2000 Angstroms. This is schematically illustrated in FIG. 4.
An anisotropic RIE procedure, using Cl.sub.2 as an etchant, is next employed to form polysilicon spacers 15b, on the sides of insulator mesa 13b, and on the sides of polysilicon shape 12b. Insulator mesa 13b, in then subjected to a vapor HF procedure, completely removing insulator mesa 13b, and resulting in a polysilicon, storage node electrode shape, comprised of vertical polysilicon spacers 15b, connected at the bottom to polysilicon shape 12b, with opening 16, resulting from the removal of insulator mesa 13b. This is schematically shown in FIG. 5. The vapor HF removal procedure provides a faster removal rate for BPSG or PSG, than for silicon oxide layer 9. Therefore insulator mesa 13b, can be completely removed without attacking insulator layer 8.
A metal layer 17a, of either titanium, cobalt, nickel, or platinum, is deposited via an r.f. sputtering procedure, to a thickness between about 100 to 500 Angstroms. This is shown schematically in FIG. 6. A first rapid thermal anneal, (RTA), procedure is performed, at a temperature between about 400 to 750.degree. C., for between about 30 to 90 sec., to convert metal layer 17a, to metal silicide layer 17b, such as titanium disilicide, cobalt silicide, nickel silicide, or platinum silicide, in regions in which metal layer 17a, overlaid polysilicon spacers 15b, and polysilicon shape 12b. Metal layer 17a, such as titanium, cobalt, nickel, or platinum remained unreacted in regions overlying insulator layer 8. This is schematically shown in FIG. 7. Unreacted metal layer 17a, such as titanium, cobalt, nickel, or platinum, is then selectively removed using a sulfuric hydrogen peroxide solution. Metal silicide layer 17b, is not removed during this wet procedure. This is schematically illustrated in FIG. 8. A second RTA procedure is next used, to convert the smooth metal silicide layer 17b, to an agglomerated metal silicide layer 17c. The RTA procedure used to create the roughened surface, agglomerated metal silicide layer, is performed at a temperature between about 800 to 1000.degree. C., for a time between about 30 to 90 sec. The result of this procedure is schematically shown in FIG. 9. The roughened surface of agglomerated metal silicide layer 17c, used as the top layer of a storage node structure of a DRAM device, will result in increased surface area, when compared to counterparts, fabricated with smooth surfaces. The use of agglomerated metal silicide layers, such as titanium silicide, cobalt silicide, nickel silicide, and platinum silicide can be used.
The process used to create the capacitor structure, comprised of a storage node electrode, featuring increased surface area resulting from the roughened surface titanium disilicide layer, continues with the formation of the capacitor dielectric layer 18. Capacitor dielectric layer 18, can be a Ta.sub.2 O.sub.5 layer, deposited using r.f. sputtering procedures. Capacitor dielectric layer 18, can also be a titanium nitride, silicon nitride, or an ONO, (silicon oxide--silicon nitride--silicon oxide), layer. A polysilicon layer is next deposited, via LPCVD procedures, and doped during an in situ deposition procedure, or doped using an ion implantation procedure. Conventional photolithographic and RIE procedures, are used to pattern the polysilicon layer, creating upper polysilicon electrode 19, for the capacitor structure of the DRAM cell. This is schematically displayed in FIG. 10.
While this invention has been particularly shown and described with reference to, the preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and detail s may be made without departing from the spirit and scope of this invention.
Claims
Certificate of Correction present
The claims shown below may not include correction changes. Use the corrected PDF for authoritative text.
What is claimed is:
1. A method for fabricating a two layer, storage node electrode, for a DRAM device, on a semiconductor substrate, comprising the steps of: providing a transfer gate transistor, on said semiconductor substrate; forming a conductive plug, in a storage node contact hole, in an insulator layer, with said conductive plug contacting underlying source/drain region, of said underlying transfer gate transistor; forming a storage node electrode shape, comprised of a first conductive layer, with a first portion of said storage node electrode shape contacting underlying conductive plug, and with a second portion of said storage node shape overlying a portion of the top surface of said insulator layer; depositing a metal layer; performing a first anneal procedure to form a smooth first metal silicide layer, at a temperature of 750.degree. C., or less, on all surfaces of said first conductive layer, located only on all surfaces of said storage node electrode shape, leaving a portion of said metal layer, overlying a portion of the top surface of said insulator layer, unreacted; selectively removing portion of said unreacted metal layer; performing a second anneal procedure, at a temperature between about 800 to 1000.degree. C., to convert said smooth first metal silicide layer to a agglomerated, second metal silicide layer, on said first conductive layer, of said storage node electrode shape, resulting in said two layer, storage node electrode, comprised of said agglomerated metal silicide layer, on said first conductive layer.
2. The method of claim 1, wherein said storage node contact hole is formed in a silicon oxide layer, via anisotropic RIE procedures, using CHF.sub.3 as an etchant.
3. The method of claim 1, wherein said conductive plug is tungsten, formed in said storage node contact hole, via deposition of tungsten, using LPCVD procedures, followed by removal of unwanted tungsten using CMP procedures.
4. The method of claim 1, wherein said storage node electrode shape, is a cylindrical shape.
5. The method of claim 1, wherein said first conductive layer, used for formation of said storage node electrode shape, is an N type doped, polysilicon layer, obtained using an LPCVD procedure, and in situ doped during the LPCVD procedure, or doped via an N type, ion implantation procedure, applied to an intrinsically deposited, polysilicon layer.
6. The method of claim 1, wherein said smooth first metal silicide layer is a smooth titanium disilicide layer, obtained via deposition of a titanium layer, using r.f. sputtering procedures, and converted to said smooth titanium disilicide layer via said first anneal, performed using RTA procedures, at a temperature between about 400 to 750.degree. C. for a time between about 30 to 90 sec.
7. The method of claim 1, wherein said smooth first metal silicide layer is a cobalt disilicide layer.
8. The method of claim 1, wherein said agglomerated, second metal silicide layer, is an agglomerated titanium disilicide layer, obtained via said second anneal, performed using an RTA procedure, applied to said smooth first metal silicide layer, at a temperature between about 800 to 1000.degree. C., for a time between about 30 to 90 sec.
9. A method of fabricating a capacitor structure, for a DRAM cell, on a semiconductor substrate, featuring a storage node electrode, comprised of a agglomerated titanium disilicide layer, on an underlying polysilicon layer, comprising the steps of: providing a transfer gate transistor, on said semiconductor substrate, comprised of a polysilicon gate structure on a gate insulator layer, and source and drain regions, in said semiconductor substrate, in regions of said DRAM cell not covered by said polysilicon gate structure; depositing a first insulator layer; opening a storage node contact hole in said first insulator layer, exposing top surface of said source and drain region; depositing a conductive layer on top surface of said first insulator layer, and completely filling said storage node contact hole; removing said conductive layer from the top surface of said first insulator layer, forming a conductive plug in said storage node contact hole; depositing a first polysilicon layer; depositing a second insulator layer; patterning of said second insulator layer, and of said first polysilicon layer, to form an insulator mesa overlying, a first polysilicon shape, with said insulator mesa comprised of said second insulator layer, and with said first polysilicon shape, comprised of said first polysilicon layer, contacting underlying, said conductive plug; depositing a second polysilicon layer; anisotropic etching of said second polysilicon layer, to form polysilicon spacers on the sides of said insulator mesa, and on the sides of said first polysilicon shape; removing said insulator mesa from underlying, said first polysilicon shape, resulting in a cylindrical, polysilicon storage node electrode shape, comprised of said polysilicon spacers, extending upwards from said first polysilicon shape; depositing a titanium layer; a first rapid thermal annealing procedure, performed at a temperature of 750.degree. C., or less, converting said titanium layer, on said cylindrical, polysilicon storage node electrode shape, to a smooth titanium disilicide layer, while leaving said titanium layer, on the top surface of said second insulator layer, unreacted; removing said titanium layer from the top surface of said first insulator layer; a second rapid thermal annealing procedure, performed at a temperature between about 800 to 1000.degree. C., converting said smooth titanium disilicide layer to said agglomerated titanium silicide layer, resulting in said storage node electrode, comprised of said agglomerated titanium disilicide layer, on said cylindrical, polysilicon storage node electrode shape; forming a capacitor dielectric layer on said storage node electrode; and forming a cell plate electrode, for said capacitor structure.
10. The method of claim 9, wherein said conductive plug is comprised of either tungsten, tungsten silicide, or polysilicon.
11. The method of claim 9, wherein said first polysilicon layer is deposited using LPCVD procedures, and in situ doped during deposition, via the addition of arsine, or phosphine, to a silane ambient, or said first polysilicon layer is deposited intrinsically, and doped via ion implantation of arsenic or phosphorous.
12. The method of claim 9, wherein said second insulator layer is a BPSG or PSG layer, deposited using LPCVD or PECVD procedures.
13. The method of claim 9, wherein said second polysilicon layer is deposited using LPCVD procedures, and in situ doped during deposition via the addition of arsine, or phosphine, to a silane ambient, or said second polysilicon layer is deposited intrinsically and doped via ion implantation of arsenic or phosphorous.
14. The method of claim 9, wherein said polysilicon spacers are formed via an anisotropic RIE procedure, applied to said second polysilicon layer, using Cl.sub.2 as an etchant.
15. The method of claim 9, wherein said insulator mesa is removed using a HF vapor procedure.
16. The method of claim 9, wherein said titanium layer is deposited using an r.f. sputtering procedure.
17. The method of claim 9, wherein said first RTA procedure, used to convert said titanium layer to said smooth titanium disilicide layer, is performed at a temperature between about 400 to 750.degree. C., for a time between about 30 to 90 sec.
18. The method of claim 9, wherein said second RTA procedure, used to convert said smooth titanium disilicide layer to said agglomerated titanium disilicide layer, is performed at a temperature between about 800 to 1000.degree. C., for a time between about 30 to 90 sec.
Patent Citations (11)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US5053917 | 1991-10-01 | Miyasaka et al. | |
| US5110752 | 1992-05-01 | Lu | |
| US5182232 | 1993-01-01 | Chhabra et al. | |
| US5381302 | 1995-01-01 | Sandhu et al. | |
| US5432129 | 1995-07-01 | Hodges | |
| US5466626 | 1995-11-01 | Armacost et al. | |
| US5480826 | 1996-01-01 | Sugahara et al. | |
| US5597754 | 1997-01-01 | Lou et al. | |
| US5656529 | 1997-08-01 | Fukase | |
| US5723384 | 1998-03-01 | Park et al. | |
| US5907772 | 1999-03-01 | Iwasaki |