Fibers, Nonwoven Fabrics, and Absorbent Articles Comprising a Biodegradable Polyhydroxyalkanoate Comprising 3-Hydroxybutyrate and 3-Hydroxyhexanoate
Issue Date:2000-01-11
•12 Claims
Abstract
The present invention relates to fibers, and nonwovens comprising said fibers, comprising a biodegradable copolymer, wherein the copolymer comprises at least two randomly repeating monomer units (RRMU) wherein the first RRMU monomer unit has the structure ##STR1## and the second RRMU has the structure ##STR2## wherein at least 50% of the RRMUs have the structure of the first RRMU. The present invention further relates to an absorbent article comprising a liquid previous topsheet, a biodegradable liquid impervious backsheet comprising the above fibers and/or nonwovens, and an absorbent core positioned between the topsheet and the backsheet.
Metadata
Assignee
- The Procter & Gamble Company
Inventor
- Isao Noda
Application Information
Application Number:US 5930278
Filing Date:1996-01-29
Priority Date:1994-01-28
Art Unit:171
Classifications
IPC:
D04H 100
Field of Search:
528442428361;334;355;491414364;365;713
Patent Drawings
This patent does not have any drawings.
Description
TECHNICAL FIELD
The present invention relates to biodegradable copolymers; fibers, and nonwoven fabrics comprising the copolymers; and disposable absorbent articles such as diapers, sanitary napkins and paintiliners, comprising such fibers, and nonwoven fabrics.
BACKGROUND
A wide variety of absorbent articles designed to be efficient for the absorption of body fluids such as blood, urine, menses, and the like, are known. Disposable products of this type generally comprise some sort of fluid-permeable topsheet material, an absorbent core, and a fluid-impermeable backsheet material. Heretofore, such absorbent structures have been prepared using, for example, topsheet materials prepared from woven, nonwoven, or porous formed-film polyethylene or polypropylene materials. Backsheet materials typically comprise flexible polyethylene sheets. Absorbent core materials typically comprise wood pulp fibers or wood pulp fibers in combination with absorbent gelling materials. One aspect of such absorbent articles that has recently been considered is their disposability. Although such products largely comprise materials which would be expected ultimately to degrade, and although products of this type contribute only a very small percentage of the total solid waste materials generated by consumers each year, nevertheless, there is currently a perceived need to devise such disposable products from materials which are compostable.
A conventional disposable absorbent product is already to a large extent compostable. A typical disposable diaper, for example, consists of about 80% of compostable materials, e.g., wood pulp fibers, and the like. In the composting process soiled disposable absorbent articles are shredded and commingled with organic waste prior to the composting per se. After composting is complete, the non-compostable particles are screened out. In this manner even today's absorbent articles can successfully be processed in commercial composting plants.
Nevertheless, there is a need for reducing the amount of non-compostable materials in disposable absorbent articles. There is a particular need to replace polyethylene backsheets and nonwoven fabrics in absorbent articles with liquid impervious films or nonwovens of compostable material, because the backsheet is typically one of the largest non-compostable components of a conventional disposable absorbent article.
In addition to being compostable, the films and nonwovens employed as backsheets for absorbent articles must satisfy many other performance requirements. For example, the resins should be thermoplastic such that conventional film or nonwoven processing methods can be employed. These methods include cast film and blown film extrusion of single layer structures and cast, blown film coextrusion of multilayer structures, or web-making by carding, air-laying, wet-forming, spinbonding, and meltblowing. Other methods include extrusion coating of one material on one or both sides of a compostable substrate such as another film, a nonwoven fabric, or a paper web.
Still other properties are essential in product converting operations where the films, fibers, and nonwovens are used to fabricate absorbent articles. Properties such as tensile strength, tensile modulus, tear strength, and thermal softening point determine to a large extent how well, for example, a film will run on converting lines.
In addition to the aforementioned properties, still other properties are needed to meet the end user requirements of the absorbent article. For example, film properties such as impact strength, puncture strength, and moisture transmission are important since they influence the absorbent article's durability and containment while being worn.
Once the absorbent article is disposed of and enters a composting process, other properties become important. Regardless of whether incoming waste is preshredded or not, it is important that the film, fiber, or large film or nonwoven fragments undergo an initial breakup to much smaller particles during the initial stages of composting. Otherwise, the films, fibers, or large fragments may be screened out of the compost stream and may never become part of the final compost.
In the past, the biodegradability and physical properties of a variety of polyhydroxyalkanoates have been studied. Poly hydroxyalkanoates are polyester compounds produced by a variety of microorganisms, such as bacteria and algae. While polyhydroxyalkanoates have been of general interest because of their biodegradable nature, their actual use as a plastic material has been hampered by their thermal instability. For example, poly-3-hydroxybutyrate (PHB) is a natural energy-storage product of bacteria and algae, and is present in discrete granules within the cell cytoplasm. However, unlike other biologically synthesized polymers such as proteins and polysaccharides, PHB is thermoplastic having a high degree of crystallinity and a well-defined melt temperature of about 180.degree. C. Unfortunately, PHB becomes unstable and degrades at elevated temperatures near its melt temperature. Due to this thermal instability, commercial applications of PHB have been extremely limited.
As a result, investigators have studied other polyhydroxyalkanoates such as poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV), in the hopes of discovering a polyhydroxyalkanoate having sufficient thermal stability and other suitable chemical and physical properties for use in practical applications. Unfortunately, polyhydroxyalkanoates such as PHB and PHBV are difficult to process into films, fibers, and nonwovens suitable for backsheet applications. As previously discussed, the thermal instability of PHB makes such processing nearly impossible. Furthermore, the slow crystallization rates and flow properties of PHB and PHBV make film, fiber, and nonwoven processing difficult. Examples of PHB homopolymer and PHBV copolymers are described in U.S. Pat. No. 4,393,167, Holmes et al., issued Jul. 12, 1983, and U.S. Pat. No. 4,880,592, issued Nov. 14, 1989. PHBV copolymers are commercially available from Imperial Chemical Industries under the tradename BIOPOL. PHBV copolymers are currently produced with valerate contents ranging from about 5 to about 24 mol %. Increasing valerate content decreases the melt temperature, crystallinity, and stiffness of the polymer. An overview of BIOPOL technology is provided in BUSINESS 2000+(Winter, 1990).
Due to the slow crystallization rate, a film, fiber, or nonwoven made from PHBV will stick to itself even after cooling; a substantial fraction of the PHBV remains amorphous and tacky for long periods of time. In cast film operations, where the film is immediately cooled on chill rolls after leaving the film die, molten PHBV often sticks to the rolls restricting the speed at which the film can be processed, or even preventing the film from being collected. In blown films, residual tack of the PHBV causes the tubular film to stick to itself after it has been cooled and collapsed for winding. In spun fibers, the fiber bundle will likewise stick and collapse.
U.S. Pat. No. 4,880,592, Martini et al., issued Nov. 14, 1989, discloses a means of achieving a PHBV monolayer film for diaper backsheet applications by coextruding the PHBV between two layers of sacrificial polymer, for example a polyolefin, stretching and orienting the multilayer film, and then stripping away the polyolefin layers after the PHBV has had time to crystallize. The remaining PHBV film is then laminated to either water soluble films or water insoluble films such as polyvinylidene chloride or other polyolefins. Unfortunately, such drastic and cumbersome processing measures are necessary in an attempt to avoid the inherent difficulties associated with processing PHBV into films.
Based on the foregoing, there is a need for disposable absorbent articles (e.g., diapers) with increased biodegradability. To satisfy this need, there is a preliminary need for a biodegradable copolymer which is capable of being easily processed into a film, fiber, or nonwoven for use in such disposable sanitary garments.
OBJECTS OF THE INVENTION
It is an object of the present invention to provide a film comprising a biodegradable polyhydroxyalkanoate.
It is also an object of the present invention to orovide a fiber comprising a biodegradable PHA.
It is also an object of the present invention to provide a nonwoven comprising a biodegradable PHA.
It is also an object of the present invention to provide a disposable sanitary garment comprising a film, fiber, or nonwoven comprising a biodegradable PHA.
SUMMARY
The present invention relates to a film, fiber, or nonwoven comprising a biodegradable copolymer, wherein the copolymer comprises at least two randomly repeating monomer units (RRMU) whereir the first RRMU has the structure ##STR3## and the second RRMU has the structure ##STR4## wherein at least 50% of the RRMUs have the structure of the first RRMU.
The present invention further relates to an absorbent article comprising a liquid previous topsheet, a biodegradable liquid impervious backsheet comprising the above film or nonwoven, and an absorbent core positioned between the topsheet and the backsheet.
DETAILED DESCRIPTION
The present invention answers the need for a biodegradable copolymer which is capable of being easily processed into a film, fiber, or nonwoven. The present invention further answers the need for disposable absorbent articles with increased biodegradability.
As used herein, "ASTM" means American Society for Testing and Materials.
As used herein, "comprising" means that other steps and other ingredients which do not affect the end result can be added. This term encompasses the terms "consisting of" and "consisting essentially of".
As used herein, "alkyl" means a saturated carbon-containing chain which may be straight or branched; and substituted (mono- or poly-) or unsubstituted.
As used herein, "alkenyl" means a carbon-containing chain which may be monounsaturated (i.e., one double bond in the chain) or polyunsaturated (i.e., two or more double bonds in the chain); straight or branched; and substituted (mono- or poly-) or unsubstituted.
As used herein, "PHA" means a polyhydroxyalkanoate of the present invention.
As used herein, "PHB" means the homopolymer poly(3-hydroxybutyrate).
As used herein, "PHB-Hx" means the copolymer poly(3-hydroxybutyrate-co-3-hydroxyhexanoate).
As used herein, "PHBV" means the copolymer poly(3-hydroxybutyrate-co-3-hydroxyvalerate).
As used herein, "biodegradable" means the aibility of a compound to ultimately be degraded completely into CO.sub.2 and water or biomass by microorganisms and/or natural environmental factors.
As used herein, "compostable" means a material that meets the following three requirements: (1) the material is capable of being processed in a composting facility for solid waste; (2) if so processed, the material will end up in the final compost; and (3) if the compost is used in the soil, the material will ultimately biodegrade in the soil.
For example, a polymer film material present in solid waste submitted to a composting facility for processing does not necessarily end up in the final compost. Certain composting facilities subject the solid waste stream to air classification prior to further processing, in order to separate paper and other materials. A polymer film would most probably be separated from the solid waste stream in such an air classification and therefore not be processed in the composting facility. Nevertheless, it may still be a "compostable" material according to the above definition because it is "capable" of being processed in a composting facility.
The requirement that the material ends up in the final compost typically means that it undergoes a form of degradation in the composting process. Typically, the solid waste stream will be subjected to a shredding step in an early phase of the composting process. As a result, the polymer film will be present as shreds rather than a sheet. In the final phase of the composting process, the finished compost will be subjected to a screening step. Typically, the polymer shreds will not pass through the screens if they have retained the size they had immediately after the shredding step. The compostable materials of the present invention will have lost enough of their integrity during the composting process to allow partially degraded shreds to pass through the screens. However, it is conceivable that a composting facility might subject the solid waste stream to a very rigorous shredding and a rather coarse screening, in which case nondegradable polymers like polyethylene would meet requirement (2). Therefore, meeting requirement (2) is not enough for a material to be compostable within the present definition.
What distinguishes the compostable material as defined herein from material like polyethylene is requirement (3), that the material ultimately biodegrade in the soil. This biodegradability requirement is not essential to the composting process or the use of composting soil. Solid waste and the compost resulting therefrom may contain all kinds of nonbiodegradable materials, for example, sand. However, to avoid a build up of man-made materials in the soil, it is required herein that such materials be fully biodegradable. By the same token, it is not at all necessary that this biodegradation be fast. As long as the material itself and intermediate decomposition products are not toxic or otherwise harmful to the soil or crops, it is fully acceptable that their biodegradation takes several months or even years, since this requirement is present only to avoid an accumulation of man-made materials in the soil.
All copolymer composition ratios recited heirein refer to mole ratios, unless specifically indicated otherwise.
A. Films
The present invention relates to biodegradable copolymers which are surprisingly easy to process into films as compared to the homopolymer PHB and copolymer PHBV. Prior to Applicants' invention, polyhydroxyalkanoates studied for use in commercial plastics production presented significant impediments to their use in plastics. As discussed above, polyhydroxyalkanoates such as PHB and the copolymer PHBV are difficult to process due to their thermal instability. Furthermore, such polyhydroxyalkanoates were especially difficult to process into films due to their slow crystallization rate. Applicants have found that PHA copolymers of the present invention, which comprise a second RRMU as defined above having an alkyl branch of at least three (3) carbons, are surprisingly easier to process into films, especially as compared to PHB or PHBV. Applicants surprisingly discovered, such linear, random copolymers with a limited number of medium sized (e.g., C.sub.3 -C.sub.19) branches provide, in addition to biodegradability, the following properties, particularly as compared to PHB or PHBV: a) a lower melt temperature, b) a lower degree of crystallinity, and c) an improved melt rheology.
Without being bound by theory, Applicants believe characteristics a) and b) are achieved by exclusion of the second RRMU from the crystal lattice of the first RRMU, thereby resulting in a decreased temperature for thermal processing and improved stiffness and elongation properties. Again, without being bound by theory, Applicants believe characteristic c) is achieved by increased entanglement between the copolymer chains due to the side chains of the second RRMU. Such increased entanglement may occur by increased hydrodynamic volume of the copolymer (e.g., the second monomer unit creates kinks in the helical structure), the "hooking" or "catching" of the side chains on different copolymer backbones while in the melt, or the decreased chain scission due to the lower Tm (i.e., the enlarged thermal process window).
Biodegradable PHAs useful for processing into the films of the present invention comprises at least two randomly repeating monomer units (RRMU) wherein the first RRMU has the structure ##STR5## and the second RRMU has the structure ##STR6## wherein at least 50% of the RRMUs have the structure of the first RRMU.
In a preferred embodiment, the PHA comprises one or more additional RRMUs having the structure ##STR7## wherein R.sup.1 is H, or a C.sub.2 or C.sub.4, C.sub.5, C.sub.6, C.sub.7, C.sub.8, C.sub.9, C.sub.10, C.sub.11, C.sub.12, C.sub.13, C.sub.14, C.sub.15, C.sub.16, C.sub.17, C.sub.18, or C.sub.19 alkyl or alkenyl; and n is 1 or 2.
As used herein, "film" means an extremely thin continuous piece of a substance having a high length to thickness ratio and a high width to thickness ratio. While there is no requirement for a precise upper limit of thickness, a preferred upper limit would be about 0.254 mm, more preferably still 0.01 mm, more preferably still 0.005 mm. The protective value of any film depends on its being continuous, i.e., without holes or cracks, since it must be an efficient barrier to molecules such as atmospheric water vapor and oxygen. In a preferred embodiment of the present invention, the film of the present invention is liquid impervious and suitable for use in absorbent disposable sanitary garments such as disposable diapers, feminine hygiene products and the like. More preferably, films of the present invention, in addition to increased biodegradability and/or compostability, have the following properties:
a) a machine direction (MD) tensile modulus from about 10,000 to about 100,000 lbs./sq. in. (6.895.times.10.sup.8 dynes/sq. cm to 6.895.times.10.sup.9 dynes/sq. cm),
b) a MD tear strength of at least 70 grams per 25.4 .mu.m of thickness,
c) a cross machine direction (CD) tear strength of at least 70 grams per 25.4 .mu. of thickness,
d) an impact strength of at least 12 cm as measured by falling ball drop,
e) a moisture transport rate less than about 0.0012 grams per square centimeter per 16 hours,
f) a modulus at 60.degree. C. of at least 5.52.times.10.sup.7 dynes/sq. cm (800 lbs./sq. in), and
g) a thickness from about 12 .mu.m to about 75 .mu.m. Methods for testing for such performance criteria are(, discussed in more detail below.
1. Performance Criteria and Test Methods for Films
For a film to perform satisfactorily as a compostable disposable diaper backsheet, it must be made of resins or structures that are biodegradable and it must demonstrate the following properties of high strength, adequate fluid barrier, appropriate modulus or flexibility, and adequately high melting point.
The backsheets of disposable diapers must have sufficient strength both to process on a high speed disposable diaper converting machine and to provide a "wetproof" barrier in use on an infant. It must be sufficiently wetproof so that the clothing or bedding, either that of the infant or of the caregiver, is not wet or soiled. It must have a modulus or flexibility that is, at the same time, low enough to be a soft, pleasing material to be used as the outer covering of an infant diaper yet high enough to handle easily on high speed disposable diaper converters without wrinkling, folding, or creasing. It must have sufficient resistance to heat such that it will not deform, melt, or permanently loose strength in typical hot storage conditions or loose its integrity on high speed disposable diaper converters which typically use hot melt adhesives to bond the components of a disposable diaper together.
Films that are sufficiently strong to be suitable as biodegradable and/or compostable backsheets for disposable diapers preferably demonstrate two properties: (a) resistance to rupture from a dropped weight and (b) resistance to tearing in both the machine direction of manufacture and the cross-machine direction of manufacture. Preferred backsheets of the present invention can withstand the drop of a spherical steel ball of about 19 millimeters in diameter and 27.6 to 28.6 gram mass from a height of 12 centimeters so that at least 50% of the tests result in no rupture of any size (deformation is acceptable). Preferred materials are those that exhibit 50% or less failures from a height of more than 20 centimeters. Similarly, acceptable backsheets of the present invention demonstrate an average tear propagation resistance of 70 grams per 25.4 micron thickness of material in both the machine direction and cross-machine direction of manufacture when a standard Elmendorf pendulum-type test device, such as Elmendorf Model No. 60-100, is employed against 16 plies of material which have been prepared with a cut or notch according to TAPPI Method T 414om-88. More preferable are those backsheets that demonstrate tear propagation resistances of 200 or more grams per 25.4 micron thickness in the cross-machine direction because these are particularly good at avoiding a tendency to fail in use by splitting.
It has also been found that films of sufficient barrier to moisture transport are those that permit less than 0.0012 grams of synthetic urine to pass into an absorbent paper towel per square centimeter of area per 25.4 micron thickness for every 16 hours of time when the test film is located between the absorbent paper towel and a typical absorbent gelling material-containing diaper core and a pressure simulating that of a baby. The specific-conditions of the test are that the area of the core is larger than that of the test material, the core is loaded with synthetic urine to its theoretical capacity and it is under a weight of about 35 g/cm.sup.2 (0.5 psi).
It has also been found that materials of sufficient heat resistance demonstrate a Vicat softening point of at least 45.degree. C. Vicat softening is tested using a Heat Distortion Apparatus Model No. CS-107 or equivalent and a modification of ASTM D-1525. The modification is in the preparation of the sample. A 19 square millimeter size film of 4.5 to 6.5 mm thickness is prepared for Vicat needle penetration tests by melting the material to be tested into a mold using a temperature of 120.degree. C. and pressure of 7.031.times.10.sup.5 g/cm.sup.2 (10,000 psi) (using a Carver or similar press) for two minutes after a warm-up period of at least 2 minutes. The Vicat softening point is the temperature at which a flat-ended needle of 1 sq. mm circular cross section will penetrate the sample to a depth of 0.1 cm under a load 1000 g using a uniform temperature rise rate of 50.degree. C. per hour.
It has also been found that materials of sufficient machine direction modulus demonstrate a 1% secant-type modulus above at least about 6.895.times.10.sup.8 dynes/cm.sup.2 (10,000 psi) and below about 6.895.times.10.sup.9 dynes/cm.sup.2 (100,000 psi). The test is performed on an electronic tensile test machine such as the Instron Model 4201. A 2.54 cm wide strip of material, preferably of 0.00254 cm in thickness, is cut to a length of about 30 cm with the longer dimension parallel to the machine direction of the material. The test strip is clamped into the jaws of the tensile testor so that the gauge or actual length of the material tested is 25.4 cm The jaws are separated at a slow speed in the range of 2.54 cm per minute to 25.4 cm per minute and a stress-strain curve is plotted on a chart within an attached recording device. The 1% secant modulus is determined by reading the stress or tensile from the chart at the 1% elongation strain point. For example, the 1% strain point is achieved when the distance between jaws has increased by 0.254 cm. When the jaws are separating at the rate of 2.54 cm per minute and the recording device is running at a speed of 25.4 cm per minute, the 1% strain point will be located at a distance of 2.54 cm from the initial point. The tensile response is divided by the thickness of the sample material if it is not 0.00254 cm in thickness. Particularly soft, and therefore preferred, materials exhibit 1% secant moduli in the range of 6.895.times.10.sup.8 to 2.068.times.10.sup.9 dynes/cm.sup.2 (10,000 to 30,000 psi).
Since absorbent articles may experience temperatures as high as 140.degree. F. (60.degree. C.) during warehouse storage or shipping in trucks or railcars, it is important that the backsheet film and other components retain their integrity at these temperatures. Although it is expected that the modulus of the films will decrease somewhat between 20.degree. C. and 60.degree. C., the modulus should not decrease too far and allow the film to deform in the package before it reaches the end user.
For example, a polyethylene backsheet with a room temperature modulus of about 4.times.10.sup.9 dynes/cm.sup.2 (58,000 psi) may have a 60.degree. C. modulus of 1.2.times.10.sup.9 dynes/cm.sup.2 (18,560 psi) which is acceptable. A softer polyethylene backsheet with a room temperature modulus of about 8.0.times.108 dynes/cm.sup.2 (11,600 psi) may have a 60.degree. C. modulus of about 3.5.times.10.sup.8 dynes cm.sup.2 (5,076 psi) which is still acceptable. In general, an acceptable backsheet film of the present invention will have a 60.degree. C. modulus of at least 5.52.times.10.sup.7 dynes/cm.sup.2 (800 psi).
The modulus dependence on temperature, also called a modulus/temperature spectrum, is best measured on a dynamic mechanical analyzer (DMA) such as a Perkin Elmer 7 Series/Unix TMA 7 Thermomechanical Analyzer equipped with a 7 Series/Unix DMA 7 Temperature/Time software package, hereinafter referred to as the DMA 7, available from the Perkin-Elmer Corporation of Norwalk, Conn. Many other types of DMA devices exist, and the use of dynamic mechanical analysis to study the modulus/temperature spectra of polymers is well known to those skilled in the art of polymer (or copolymer) characterization. This information is well summarized in two books, the first being DYNAMIC MECHANICAL ANALYSIS OF POLYMERIC MATERIAL, MATERIALS SCIENCE MONOGRAPHS VOLUME 1 by T. Murayama (Elsevier Publishing Co., 1978) and the second being MECHANICAL PROPERTIES OF POLYMERS AND COMPOSITES, VOLUME 1 by L. E. Nielsen (Marcel Dekker, 1974).
The mechanism of operation and procedures for using the DMA 7 are found in Perkin-Elmer Users' Manuals 0993-8677, and 0993-8679, both dated May, 1991. To those skilled in the use of the DMA 7, the following run conditions should be sufficient to replicate the 60.degree. C. modulus data presented hereinafter.
To measure the modulus/temperature spectrum of a film specimen, the DMA 7 is set to run in temperature scan mode and equipped with an extension measuring system (EMS). A film specimen approximately 3 mm wide, 0.0254 mm thick, and of sufficient length to allow 6 to 8 mm of length between the specimen grips is mounted in the EMS. The apparatus is then enclosed in an environmental chamber swept continuously with helium gas. Stress is applied to the film in the length direction to achieve a deformation or strain of 0.1 percent of the original length. A dynamic sinusoidal strain is applied to the specimen at a frequency of 5 cycles per second. In the temperature scan mode, the temperature is increased at a rate of 3.0.degree. C./minute from 25.degree. C. to the point where the specimen melts or breaks, while the, frequency and stress are held constant. Temperature-dependent behavior is characterized by monitoring changes in strain and the phase difference in time between stress and strain. Storage modulus values in Pascals are calculated by the computer along with other data and displayed as functions of temperature on a video display terminal. Normally the data are saved on computer disk and a hard copy of the storage modulus/temperature spectrum printed for further review. The 60.degree. C. modulus is determined directly from the spectrum.
2. Method of Film Manufacture
The films of the present invention used as backsheets having increased biodegradability and/or compostability may be processed using conventional procedures for producing single or multilayer films on conventional film-making equipment. Pellets of the PHAs of the present invention can be first dry blended and then melt mixed in a film extruder. Alternatively, if insufficient mixing occurs in the film extruder, the pellets can be first dry blended and then melt mixed in a precompounding extruder followed by repelletization prior to film extrusion.
The PHAs of the present invention can be melt processed into films using either cast or blown film extrusion methods both of which are described in PLASTICS EXTRUSION TECHNOLOGY--2nd Ed., by Allan A. Griff (Van Nostrand Reinhold--1976). Cast film is extruded through a linear slot die. Generally the flat web is cooled on a large moving polished metal roll. It quickly cools, and peels off this first roll, passes over one or more auxiliary cooling rolls, then through a set of rubber-coated pull or "haul-off" rolls, and finally to a winder. A method of making a cast backsheet film for the absorbent articles of the present invention is described in an example below.
In blown film extrusion, the melt is extruded upward through a thin annular die opening. This process is also referred to as tubular film extrusion. Air is introduced through the center of the die to inflate the tube and thereby causing it to expand. A moving bubble is thus formed which is held at a constant size by control of internal air pressure. Thie tube of film is cooled by air, blown through one or more chill rings surrounding the tube. The tube is then collapsed by drawing it into a flattening frame through a pair of pull rolls and into a winder. For backsheet applications the flattened tubular film is subsequently slit open, unfolded, and further slit into widths appropriate for use in products.
Both cast film and blown film processes can be used to produce either monolayer or multilayer film structures. For the production of monolayer films from a single thermoplastic material or blend of thermoplastic components only a single extruder and single manifold die are required.
For the production of multilayer films of the present invention, coextrusion processes are preferably employed. Such processes require more than one extruder and either a coextrusion feedalock or multi-manifold die system or combination of the two to achieve the multilayer film structure.
U.S. Pat. Nos. 4,152,387, and 4,197,069, disclose the feedblock principle of coextrusion. Multiple extruders are connected to the feedblock which employs moveable flow dividers to proportionally change the geometry of each individual flow channel in direct relation to the volume of polymer passing through said flow channels. The flow channels are designed such that at their point of confluence, the materials flow together at the same flow rate and pressure eliminating interfacial stress and flow instabilities. Once the materials are joined in the feedblock, they flow into a single manifold die as a composite structure. It is important in such processes that thie melt viscosities and melt temperatures of the materials do not differ too greatly; otherwise flow instabilities can result in the die leading to poor control of layer thickness distribution in the multilayer film.
An alternative to feedblock coextrusion is a multi-manifold or vane die as disclosed in aforementioned U.S. Pat. Nos. 4,152,387, 4,197,069, and in U.S. Pat. No. 4,533,308. Whereas in the feedblock system melt streams are brought together outside and prior to entering the die body, in a multi-manifold or vane die each melt stream has its own manifold in the die where the polymers spread independently in their respective manifolds. The melt streams are married near the die exit with each melt stream at full die width. Moveable vanes provide adjustability of the exit of each flow channel in direct proportion to the volume of material flowing through it, allowing the melts to flow together at the same linear flow rate, pressure, and desired width.
Since the melt flow properties and melt temperatures of the processed materials may vary widely, use of a vane die has several advantages. The die lends itself toward thermal isolation characteristics wherein materials of greatly differing melt temperatures, for example up to 175.degree. F. (80.degree. C.), can be processed together.
Each manifold in a vane die can be designed and tailored to a specific polymer (or copolymer). Thus the flow of each polymer is influenced only by the design of its manifold, and not by forces imposed by other polymers. This allows materials with greatly differing melt viscosities to be coextruded into multilayer films. In addition, the vane die also provides the ability to tailor the width of individual manifolds, such that an internal layer, for example a water soluble biodegradable polymer like Vinex 2034, can be completely surrounded by water insoluble materials leaving no exposed edges susceptible to water. The aforementioned patents also disclose the combined use of feedblock systems and vane dies to achieve more complex multilayer structures.
The multilayer films of the present invention may comprise two or more layers. In general, balanced or symmetrical three-layer and five-layer films are preferred. Balanced three-layer multilayer films comprise a center core layer and two identical outer layers, wherein said center core layer is positioned between said two outer layers. Balanced five-layer multilayer films comprise a center core layer, two identical tie layers, and two identical outer layers, wherein said center core layer is positioned between said two tie layers, and a tie layer is positioned between said center core layer and each outer layer. Balanced films, though not essential to the films of the present invention, are less prone to curling or warping than unbalanced multilayer films.
In three layer films, the center core layer may comprise 30 to 80 percent of the films' total thickness and each outer layer comprises 10 to 35 percent of the films' total thickness. Tie layers, when employed, each comprise from about 5 percent to about 10 percent of the films' total thickness.
3. Crystallinity
The volume percent crystallinity (.PHI..sub.c) of a semi-crystalline polymer (or copolymer) often determines what type of end-use properties the polymer possesses. For example, highly (greater than 50%) crystalline polyethylene polymers are strong and stiff, and suitable for products such as plastic milk containers. Low crystalline polyethylene, on the other hand, is flexible and tough, and is suitable for products such as food wraps and garbage bags. Crystallinity can be determined in a number of ways, including x-ray diffraction, differential scanning calorimetry (DSC), density measurements, and infrared absorption. The most suitable method depends upon the material being tested.
X-ray diffraction is most appropriate when little is known about the thermal properties of the material and crystal structural changes may occur. The basic principle relies on the fact that amorphous parts of the material scatter x-rays in a diffuse or broad range of angles while crystals diffract x-rays into sharp, precisely defined angles. The total scattered intensity is constant, however. This allows calculation of the amount of crystalline material in a sample if the amorphous and crystalline diffracted intensities can be separated. A very precise method has been developed by Ruland, which can detect differences in percent crystallinity as small as 2% (see Vonk, C., F. J. Balta-Calleja, X-RAY SCATTERING FROM SYNTHETIC POLYMERS, Elsevier: Amsterdam, (1989); and Alexander, L., X-RAY DIFFRACTION METHODS IN POLYMER SCIENCE, Robert Kreiger Pub. Co., New York, (1979)).
Upon melting, crystals require a fixed amount of heat at the melting temperature transforming from crystalline to molten matter. This heat of fusion can be measured by a number of thermal techniques, the most popular being DSC. If the heat of fusion of a 100% crystalline material is known, and no significant annealing, or melt/recrystallisation phenomena occur upon heating to the melt, then DSC can quite accurately determine weight fraction crystallinity (see THERMAL CHARACTERIZATION OF POLYMER MATERIALS, E. Turi, Ed., Academic Press, New York, (1980); and Wunderlich, B., MACROMOLECULAR PHYSICS, Academic Press, New York, (1980)).
If the densities of the pure crystalline and pure amorphous material is known then density measurements of a material can yield the degree of crystallinity. This assumes additivity of specific volumes, but this requirement is fulfilled for polymers (or copolymers) of homogeneous structure. This method depends on careful sample preparation so that no bubbles or large voids exist in the sample.
If purely crystalline and amorphous absorption bands can be identified, then the infrared absorption spectrum offers a convenient way of determining crystallinity (see Tadokoro, H., STRUCTURE OF CRYSTALLINE POLYMERS, John Wiley & Sons, New York, (1979)).
It should be noted that different techniques will often give rise to slightly different values of .phi..sub.c, because they are based on different physical principles. For example, density measurements often give higher values than x-ray diffraction. This is due to the continuous changing of the density in the interface between crystalline and amorphous polymear (or copolymer) material. While x-ray diffraction does not detect this matter as crystalline, density measurements will be affected by this interface region.
For purposes of processing into a film, the PHAs of the present invention preferably have a crystallinity of from about 2% to about 65% as measured via x-ray diffraction; more preferably from about 5% to about 50%; more preferably still from about 20% to about 40%.
B. Fibers
Applicants have further discovered the biodegradable PHAs of the present invention are surprisingly easy to process into fibers. As used herein, "fiber" refers to a flexible, macroscopically homogeneous body having a high length-to-width ratio and a small cross section. A general overview of fibers can be found in the ENCYCLOPEDIA OF POLYMER SCIENCE AND ENGINEERING, Vol. 6, p. 647-755 and pp. 802-839, John Wiley and Sons, New York, (1986) (hereinafter referred to as "EPSE-1"). The fibers of the present invention are useful as textiles in yarns for garments. For example, the fibers can be used to form a nonwoven backsheet for an absorbent article. Such use is particularly attractive in, e.g., diapers, thereby providing a disposable biodegradable backsheet imparting a cloth-like feel.
The fibers of the present invention are also useful for manufacturing lightweight fibrous materials useful in agricultural applications to protect, promote, or control plant growth. They are also used in green house thermal screens, crop row covers, turf covers, weed barriers and hydroponics. Key properties are light, air, and moisture permeability. An important aspect is cost effectiveness when considered in terms of weight, strength, and dimension stability.
An elastomeric fiber is a fiber that consists of polymers (or copolymers) with a main glass transition temperature much below room temperature (see EPSE-1). This criterion excludes some fibers with elastic properties, such as crimped hard fibers, but allows inclusion of multi-constituent fibers where one of the constituents is an elastomer. All elastomeric fibers are characterized by a higher elongation at break, lower modulus, and higher recovery from large deformation than normal fibers.
1. Methods of Fiber Manufacture
The fibers of the present invention may be processed using a variety of conventional techniques well-known in the art including, but not limited to, melt spinning, dry spinning, and wet spinning. Combinations of these three basic processes are often used.
In melt spinning the PHA of the present invention is heated above its melting point and the molten PHA is forced through a spinneret. A spinneret is a die with many small orifices which are varied in number, shape and diameter (see EPSE-1). The jet of molten PHA is passed through a cooling zone where the PHA solidifies and is then transferred to post-drawing and take-up equipment.
In dry spinning, the PHA of the present invention is dissolved and the PHA solution is extruded under pressure through a spinneret (see EPSE-1). The jet of PHA solution is passed through a heating zone where the solvent evaporates and the filament solidifies.
In wet spinning, the PHA of the present invention is also dissolved and the solution is forced through a spinneret which is submerged in a coagulation bath (see ESPE-1). As the PHA solution emerges from the spinneret orifices within the coagulation bath, the PHA is either precipitated or chemically regenerated. Usually, all these processes need further drawing for useful properties to be obtained, for example to serve as textile fibers. "Drawing" refers to stretching and attenuation of fibers to achieve an irreversible extension, induce molecular orientation, and develop a fiber-fine structure (see ESPE-1). This fine structure is characterized by a high degree of crystallinity and by orientation of both the crystallites and the amorphous PHA chain segments.
C. Nonwovens
In another embodiment of the present invention, the PHA is formed into a nonwoven. As used herein "nonwoven" means porous, textile like materials, usually in flat sheet form, composed primarily, or entirely, of fibers assembled in webs that are manufactured by processes other than spinning, weaving, or knitting. A general overview of nonwoven fabrics can be found in the ENCYCLOPEDIA OF POLYMER SCIENCE AND ENGINEERINIG, Second Edition, Vol. 10, pp. 204-226 (referred to hereafter as "EPSE-2") Other names for these materials are bonded fabrics, formed fabrics, or engineered fabrics. The thickness of the fabric sheets may vary from 25 mm to several centimeters, and the weight from 10 g/m.sup.2 to 1 kg/m.sup.2. Nonwoven fabrics have a wide range of physical properties depending on the material and process used in forming the web. A fabric may be self-supporting and stiff as paper or drapable as a conventional cloth fabric.
In contrast to conventional textiles, the fundamental structure of all nonwovens is a web of fibers arranged more or less randomly (NONWOVENS IND., Vol. 17, p. 36 (March 1986), NONWOVENS WORLD, Vol. 1, p. 36 (May-June 1986)). Thus, the key element is the single fiber. Tensile, tear, and tactile properties in the nonwoven arise from adhesive or other chemical and physical bonding, fiber-to-fiber friction created by entanglement, and reinforcement by other materials such as foams and films (see EPSE-2).
1. Method of Manufacture of Nonwoven Fabrics
The nonwoven fabrics of the present invention may be made by conventional techniques known in the art. The production of nonwoven fabrics involves: 1) making fibers of various lengths and diameters; 2) creating a web of these fibers; and 3) bonding of fibers within the web by adhesive, or mechanical-frictional forces created by fiber contact or entanglement. In addition to these steps, reinforcing the web by forming a composite with other materials (e.g., yarns, scrims, films, nettings, and unbonded webs) is sometimes preferred. Variations of one or several of these steps allows for the enormous range of nonwoven fiber types. The term "staple fibers" was originally applied to fibers of natural origin long enough to be processed on textile machinery, but excluding endless filaments, eg, silk. In the present context, as applied to PHA of the present invention, "staple fibers" are of relatively uniform length, ca. 1.3-10.2 cm, with a regular crimp i.e., a three-dimensional wavelike shape. Regenerated and other extruded fibers are endless as formed. They are cut during the manufacturing process to a specified length to meet a processing or market need. Extruded fibers are also produced as continuous filaments without crimp. The processes for forming webs from staple fibers are different from those using continuous filaments. The products obtained from staple and filament fiber webs may differ substantially in properties (see EPSE-2).
The mechanical properties of the fibers as defined by their chemical composition, determine the ultimate properties of the fabric. Web structure and bonding maximize inherent fiber characteristics (see EPSE-2). Other materials that may be used in the nonwovens of the present invention in combination with the PHA are wood pulp; regenerated fibers including viscose rayon and cellulose acetate; and synthetic fibers like poly(ethylene terephthalate) (PET), nylon-6, nylon 6,6, polypropylene (PP), and poly(vinyl alcohol). Facings of disposable diapers or sanitary napkins made from PHA nonwoven fabrics of the present invention preferably feel dry even when the absorbent, inner absorbent layer is saturated. Important fiber characteristics that affect performance include length, diameter, density, crimp, cross section shape, spin-finish (lubricant that is added to the surface of extruded fibers to enhance processability), delustering (small amounts of TiO.sub.2 pigment added before extrusion to increase whiteness or to reduce sheen) and the draw ratio.
a. Web-making Methods
The characteristics of the fiber web determine the physical properties of the final product. These characteristics depend largely on fiber architecture, which is determined by the mode of web formation. Fiber architecture includes the predominant fiber direction, whether oriented or random, fiber shape (straight, hooked, or curled), the extent of interfiber engagement or entanglement, crimp, and compaction (web-density control). Web characteristics are also influenced by fiber diameter, length, web weight, and chemical and mechanical properties of the polymer (see EPSE-2).
The choice of method for forming the web is determined by fiber length. Initially, the methods for forming webs from staple-length fibers (fibers long enough to be handled by conventional spinning equipment, usually from about 1.2 to about 20 cm long, but not endless) are based on the textile-carding process, whereas web formation from short fibers is based on papermaking technologies. Although these technologies are still in use, other methods have been subsequently developed. For example, webs are formed from long, virtually endless filaments directly from bulk polymer; both web and fibers are produced simultaneously (see EPSE-2). A variety of web-making methods are known, including carding, air-laying, wet-forming, spinbonding, and meltblowing.
The carding process is derived from the ancient manual methods of fiber carding, where natural staple fibers were manipulated by beds of needles. In carding, clumps of staple fibers are separated mechanically into individual fibers and formed into a coherent web by the mechanical action of moving beds of closely spaced needles.
In the air-laying process, the orientation created by carding is effectively improved by capturing fibers on a screen from an airstream (see U.S. Pat. No. 3,338,992, G. A. Kinney, assigned to E.I. du Port de Nemours & Co., Inc., issued Aug. 29, 1967). The fibers are separated by teeth or needles and introduced into an airstream. Total randomization would exclude any preferential orientation when the fibers are collected on the screen.
Wet-forming processes employ very short fibers. Initially, webs are formed from short fibers by modified papermaking techniques. The fibers are continuously dispersed in a large volume of water and caught on a moving endless wire screen. Once the web is caught on the screen, it is transferred to belts or felts and dried on heated drums (see EPSE-2).
The spunbonded web process involves making fibers and web simultaneously, directly from bulk polymer. The bulk polymer is melted, extruded, and drawn (often by triboelectric forces) to filaments that are randomized and deposited onto belts as a continuous web. The filaments are virtually endless. The spunbond process produces viebs of low crimp filaments in the normal diameter range of about 1.7 dtex (1.5 den) or slightly higher. The birefringence and uniformity of diameter of these filaments are similar to standard textile fibers and filaments (see EPSE-2). Each production line is suitable for a specific polymer and a single-bonding system (see U.S. Pat. No. 4,163,305 (Aug. 7, 1979), V. Semjonow and J. Foedrowitz (to Hoechst AG)).
Webs are also made directly from bulk polymers by the meltblown process (see U.S. Pat. No. 3,322,607, S. L. Jung, assigned to E.I. duPont de Nemours & Co., Inc., May 30, 1967). The molten PHA is forced through very fine holes in a special die into a high velocity airstream where the PHA is formed into very fine, although irregular, filaments of indeterminate lengths. The filaments are simultaneously formed into a web where melting and resolidification, and possibly static forces, hold them together (see EPSE-2). The web consists primarily of filaments with very fines diameters.
b. Web Bonding
The bonding of fibers gives the strength to the web and influences other properties. Both adhesive and mechanical means are used. Mechanical bonding employs the engagement of fibers by frictional forces. Bonding can also be achieved by chemical reaction, i.e., formation of covalent bonds between binder and fibers (see EPSE-2).
D. Melt Temperature
Preferably, the biodegradable PHAs of the present invention have a melt temperature (Tm) of from about 30.degree. C. to about 160.degree. C., more preferably from about 60.degree. C. to about 140.degree. C., more preferably still from about 90.degree. C. to about 120.degree. C.
E. Absorbent Articles
The present invention further relates to absorbent articles comprising a PHA of the present invention. Such absorbent articles include, but are not limited to, infant diapers, adult incontinent briefs and pads, and feminine hygiene pads and liners. Films of the present invention used as liquid impervious backsheets in absorbent articles of the present invention, such as disposable diapers, typically have a thickness of from 0.01 mm to about 0.2 mm, preferably from 0.012 mm to about 0.051 mm.
In general, the liquid impervious backsheet is, combined with a liquid previous topsheet and an absorbent core positioned between the topsheet and the backsheet. Optionally, elastic members and tape tab fasteners can be included. While the topsheet, the backsheet, the absorbent core and elastic members may be assembled in a variety of well known configurations, a preferred diaper configuration is described generally in U.S. Pat. No. 3,860,003, entitled "Contractible Side Portion for Disposable Diaper" which issued to Kenneth B. Buell on Jan. 14, 1975.
The topsheet is preferably, soft-feeling, and non-irritating to the wearer's skin. Further, the topsheet is liquid previous, permitting liquids to readily penetrate through its thickness. A suitable topsheet may be manufactured from a wide range of materials such as porous foams, reticulated foams, apertured plastic films, natural fibers (e.g., wood or cotton fibers), synthetic fibers (e.g., polyester or polypropylene fibers) or from a combination of natural and synthetic fibers. Preferably, the topsheet is made of a hydrophobic material to isolate the wearer's skin from liquids in the absorbent core.
A particularly preferred topsheet comprises staple-length fibers having a denier of about 1.5. As used herein, the term "staple-length fibers" refers to those fibers having a length of at least about 16 mm.
There are a number of manufacturing techniques which may be used to manufacture the topsheet. For example, the topsheet may be woven, nonwoven, spunbonded, carded, or the like. A preferred topsheet is carded, and thermally bonded by means well known to those skilled in the fabrics art.
Preferably, the topsheet has a weight from about 18 to about 25 g/m.sup.2, a minimum dried tensile strength of at least about 400 g/cm in the machine direction, and a wet tensile strength of at least about 55 g/cm in the cross-machine direction.
The topsheet and the backsheet are joined together in any suitable manner. As used herein, the term "joined" encompasses configurations whereby the topsheet is directly joined to the backsheet by affixing the topsheet directly to the backsheet, and configurations whereby the topsheet is indirectly joined to the backsheet by affixing the topsheet to intermediate members which in turn are affixed to the backsheet. In a preferred embodiment, the topsheet and the backsheet are affixed directly to each other in the diaper periphery by attachment means such as an adhesive or any other attachment means known in the art. For example, a uniform, continuous layer of adhesive, a patterned layer of adhesive, or an array of separate lines or spots of adhesive may be used to affix the topsheet to the backsheet.
Tape tab fasteners are typically applied to the back waistband region of the diaper to provide a fastening means for holding the diaper on the wearer. The tape tab fasteners can be any of those well known in the art, such as the fastening tape disclosed in U.S. Pat. No. 3,848,594 issued to Kenneth B. Buell on Nov. 19, 1974. These tape tab fasteners or other diaper fastening means are typically applied near the corners of the diaper.
Preferred diapers have elastic members disposed adjacent the periphery of the diaper, preferably along each longitudinal edge so that the elastic members tend to draw and hold the diaper against the legs of the wearer. The elastic members are secured to the diaper in an contractible condition so that in a normally unrestrained configuration the elastic members effectively contract or gather the diaper. The elastic members can be secured in an contractible condition in at least two ways. For example, the elastic members may be stretched and secured while the diaper is in an uncontracted condition. Alternatively, the diaper may be contracted, for example, by pleating, an elastic member secured and connected to the diaper while the elastic members are in their relaxed or unstretched condition.
The elastic members may take a multitude of configurations. For example, the width of the elastic members may be varied from about 0.25 mm to about 25 mm or more; the elastic members may comprise a single strand of elastic material or the elastic members may be rectangular or curvilinear. Still further, the elastic members may be affixed to the diaper in any of several ways which are known in the art. For example the elastic members may be ultrasonically bonded, heat and pressure sealed into the diaper using a variety of bonding patterns, or the elastic members may simply be glued to the diaper.
The absorbent core of the diaper is positioned between the topsheet and backsheet. The absorbent core may be manufactured in a wide variety of sizes and shapes (e.g., rectangular, hour-glass, asymmetrical, etc.) and from a wide variety of materials. The total absorbent capacity of the absorbent core should, however, be compatible with the designed liquid loading for the intended use of the absorbent article or diaper. Further, the size anid absorbent capacity of the absorbent core may vary to accommodate wearers ranging from infants through adults.
A preferred embodiment of the diaper has an hour-glass shaped absorbent core. The absorbent core is preferably an absorbent member comprising a web or batt of airfelt, wood pulp fibers, and/or a particulate absorbent polymeric composition disposed therein.
Other examples of absorbent articles according to the present invention are sanitary napkins designed to receive and contaiin vaginal discharges such as menses. Disposable sanitary napkins are designed to be held adjacent to the human body through the agency of a garment, such as an undergarment or a panty or by a specially designed belt. Examples of the kinds of sanitary napkins to which the present invention is readily adapted are shown in U.S. Pat. No. 4,687,478, entitled "Shaped Sanitary Napkin With Flaps" which issued to Kees J. Van Tilburg on Aug. 18, 1987, and in U.S. Pat. No. 4,589,876, entitled "Sanitary Napkin" which issued to Kees J. Van Tilburg on May 20, 1986. It will be apparent that the films of the present invention comprising a PHA of the present invention described herein may be used as the liquid impervious backsheet of such sanitary napkins. On the other hand it will be understood the present invention is not limited to any specific sanitary napkin configuration or structure.
In general, sanitary napkins comprise a liquid impervious backsheet, a liquid previous topsheet, and an absorbent core placed between the backsheet and the topsheet. The backsheet comprises a PHA of the present invention. The topsheet may comprise any of the topsheet materials discussed with respect to diapers.
Importantly, the absorbent articles according to the present invention are biodegradable and/or compostable to a greater, extent than conventional absorbent articles which employ materials such as a polyolefin (e.g., a polyethylene backsheet).
F. Synthesis of Biodegradable PHAs
The biodegradable PHAs of the present invention can be synthesized by synthetic chemical or biological based methods. A chemical approach involves the ring-opening polymerization of .beta.-lactone monomers as described below. The catalysts or initiators used can be a variety of materials such as aluminoxanes, distannoxanes, or alkoxy-zinc and -aluminum compounds (see Agostini, D. E., J. B. Lando, and J. R. Shelton, POLYM. SCI. PART A-1, Vol. 9, pp. 2775-2787 (1971); Gross, R. A., Y. Zhang, G. Konrad, and R. W. Lenz, MACROMOLECULES, Vol. 21, pp. 2657-2668 (1988); and Dubois, P., I. Barakat, R. Jerome, and P. Teyssie, MACROMOLECULES, Vol. 26, pp. 4407-4412 (1993); Le Borgne, A. and N. Spassky, POLYMER, Vol. 30, pp. 2312-2319 (1989); Tanahashi, N., and Y. Doi, MACROMOLECULES, Vol. 24, pp. 5732-5733 (1991); Hori, Y., M. Suzuki, Y. Takahashi, A. Ymagluchi, and T. Nishishita, MACROMOLECULES, Vol. 26, pp. 4388-4390 (1993) and Kemnitzer, J. E., S. P. McCarthy, and R. A. Gross, MACROMOLECULES, Vol. 26, pp. 1221-1229 (1993)). The production of isotactic polymer can be accomplished by polymerization of an enantiomerically pure monomer and a non-racemizing initiator, with either retention or inversion of configuration of the stereocenter, or by polymerization of racemic monomer with an initiator which preferentially polymerizes one enantiomer. For example: ##STR8##
The naturally derived PHAs of the present invention are isotactic and have the R absolute configuration at the stereocenters in the polymer backbone. Alternatively, isotactic polymers may be made where the configuration of the stereocenters is predominantly S. Both isotactic materials will have the same physical properties and most of the same chemical reactivities except when a stereospecific reagent, such as an enzyme, is involved. Atactic polymers, polymers with random incorporation of R and S stereocenters, can be produced from racemic monomers and polymerization initiators or catalysts that show no preference for either enantiomer while such initiators or catalysts often polymerize monomers of high optical purity to isotactic polymer (e.g., distannoxane catalysts) (see, Hori, Y., M. Suzuki, Y. Takahashi, A. Yamaguchi, T. Nishishita, MACROMOLECULES, Vol. 26, pp. 5533-5534 (1993)). Alternatively, isotactic polymer can be produced from racemic monomers if the polymerization catalyst has an enhanced reactivity for one enantiomer over the other. Depending on the degree of preference, separate R or S stereo-homopolymers, stereo-block copolymers, or a mixture of stereo-block copolymers and stereo-homopolymers may be produced (see Le Borgne, A. and N. Spassky, N., POLYMER, Vol. 30, pp. 2312-2319 (1989); Tanahashi, N., and Y. Doi, MACROMOLECULES, Vol. 24, pp. 5732-5733 (1991); and Benvenuti, M. and R. W. Lenz, J. POLYM. SCI.: PART A: POLYM. CHEM., Vol. 29, pp. 793-805 (1991)). Some initiators or catalysts are known to produce predominantly syndiotactic polymer, polymers with alternating R and S stereocenter repeat units, from racemic monomer (see Kemnitzer, J. E., S. P. McCarthy and R. A. Gross, MACROMOLECULES, Vol. 26, pp. 1221-1229 (1993)) while some initiators or catalysts may produce all three types of stereopolymers (see Hocking, P. J. and R. H. Marchessault, POLYM. BULL., Vol. 30, pp. 163-170 (1993)).
For example, preparation of poly(3-hydroxybutyrate-co-3-hexanoate-co-3-hydroxyalkanoate) copolymers wherein the 3-hydroxyalkanoate comonomer is a 3-alkyl-.beta.-propiolactone wherein the alkyl group is at least 3 carbons long, are carried out in the following manner. Proper precautions are made to exclude air and moisture. The lactone monomers (purified, dried, and stored under inert atmosphere), .beta.-butyrolactone and a 3-alkyl-.beta.-propiolactone in the desired molar ratio, are charged via syringe or canula to an oven-dried, argon-purged, and flamed borosilicate-glass tube or flask capped with a rubber septum. The polymerization catalyst is added as a toluene solution via syringe. The tube is carefully swirled to mix the reagents (but not contact the rubber septum) and then heated in an oil bath at the desired temperature for the prescribed time. As the reaction proceeds the mixture becomes viscous and may solidify. If isotactic polymer is produced, solid polymer precipitates out until the entire mass solidifies. The product can then be cooled, removed from the tube, and rid of residual monomer by vacuum drying. Alternatively, the product can be dissolved in an appropriate solvent (e.g., chloroform) and recovered by precipitation in a nonsolvent (e.g., ether-hexane mixture, 3:1 v/v), and vacuum dried. Molecular weight is determined by standard methods such as size exclusion chromatography (SEC, also known as gel permeation chromatography or GPC). The comonomer content of the polymers is determined by nuclear magnetic resonance (NMR).
In a preferred method of synthesizing the PHAPs of the present invention, the initiator is an alkylzinc alkoxide, as disclosed in the U.S. Patent Application entitled "Polymerization of Beta-Substituted-Beta-Propiolactones Initiated by Alkylzinc Alkoxides", L. A. Schechtman and J. J. Kemper, assigned to The Procter and Gamble Company, filed Jan. 28, 1994. Such initiators have the general formula R.sup.1 ZnOR.sup.2, wherein R.sup.1 and R.sup.2 are independently a C.sub.1 -C.sub.10 alkyl. In a preferred method of synthesis, the initiator is selected from the group consisting of ethylzinc isopropoxide, methylzinc isopropoxide, ethyl zinc ethoxide, or ethylzinc methoxide; more preferably ethylzinc isopropoxide.
Other copolymers useful in the present invention can be made by substituting the starting materials (monomers) in the above procedure with 3-alkyl-.beta.-lactones corresponding to the monomer units desired in the final copolymer product.
Alternatively, biological synthesis of the biodegradable PHAs useful in the present invention may be carried out by fermentation with the proper organism (natural or genetically engineered) with the proper feedstock (single or multicomponent). The production of poly(3-hydroxyalkanoate-co-3-hydroxybutyrate) by Aeromonas caviae is disclosed in European Patent Application No. 533 144, Shiotani and Kobayashi, published Mar. 24, 1993. Biological synthesis may also be carried out with botanical species genetically engineered to express the copolymers of interest (see World Patent Application No. 93-02187, Somerville, Poirier and Dennis, published Feb. 4, 1993; and U.S. patent application Ser. No. 08/108,193, Somerville, Nawrath and Poirier, filed Aug. 17, 1993; and Poole, R., SCIENCE., Vol. 245, pp. 1187-1189 (1989)).
G. EXAMPLES
Example 1
Poly(3-hydroxybutyrate-co-hydroxyhexanoate)
Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHB-Hx) is prepared according to the general methods described above and based on the published procedure of Hori et al. (Hori, Y., M. Suzuki, Y. Takahashi, A. Yomaguchi, and T. Nishishita, MACROMOLECULES, Vol. 26, pp. 5533-5534 (1993)) for the polymerization of .beta.-butyrolactone. Specifically, purified [S]-3-methylpropiolactone ([S]-.beta.-butyrolactone) (9.50 g, 110 mmol) and [S]-3-propylpropiolactone (0.66 g, 5.8 mmol) are charged into a septum sealed, argon purged, dry, glass tube via syringe. The initiator, 1,3-dichloro-1,1,3,3-tetrabutyldistannoxane prepared according to R. Okawara and M. Wada, (J. ORGANOMET. CHEM. (1963), Vol. 1, pp. 81-88) and dried overnight in vacuo at 80.degree. C. is dissolved in dry toluene to make a 0.18 M solution. Via syringe, 0.65 mL of the initiator solution (0.12 mmol distannoxane) is added to the tube. The tube is gently swirled to mix the contents and then heated at 100.degree. C. for 4 h by immersing its lower half in an oil bath. As the reaction proceeds, the contents of the tube become viscous. After the required time, the tube is removed from the oil bath and allowed to cool to room temperature. The solid is dissolved in chloroform. It is recovered by precipitation into a hexane-ether mixture, collected by filtration, and dried under vacuum. The comonomer composition of the copolymer is determined by .sup.1 H-NMR spectroscopy and found, within experimental error, to be the same as the charge ratio (95:5). Molecular weight is determined by size exclusion chromatography with chloroform as the mobile phase, and narrow polystyrene standards are used for calibration.
Example 2
Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate-co-3-hydroxyoctanoate)
Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate-co-3-hydroxyoctan-oate) is prepared by following the same procedure as in Example 1, with the exception that [S]-3-methylpropiolactone (9.50 g, 110 mmol), [S]-3-propylpropiolactone (0.40 g, 3.5 mmol) and [S]-3-pentylpropiolactone (0.50 g, 3.5 mmol) are used as the monomer charge.
Example 3
Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate-co-3-hydroxydecanoate)
Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate-co-3-hydroxydecanoate) is prepared by following the same procedure as in Example 1, with the exception that [S]-3-methylpropiolactone (9.50 g, 110 mmol), [S]-3-propylpropiolactone (0.40 g, 3.5 mmol) and [S]-3-heptylpropiolactone (0.60 g, 3.5 mmol) are used as the monomer charge.
Example 4
Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate-co-3-hydroxyheptanoate)
Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate-co-3-hydroxyheptanoate) is prepared by following the same procedure as in Example 1, with the exception that [S]-3-methylpropiolactone (9.50 g, 110 mmol), [S]-3-propylpropiolactone (0.40 g, 3.5 mmol) and [S]-3-butylpropiolactone (0.45 g, 3.5 mmol) are used as the monomer charge.
Example 5
Compostable Single Layer Film
PHB-Hx of composition 8 mole % hexanoate/92 mole % butyrate is introduced into a single screw extruder (Rheomix Model 202) with screw diameter of 0.75 inch. A constant taper screw having 20:1 length to diameter ratio and a 3:1 compression ratio is employed. The temperature of both heating zones of the extruder barrel is 25.degree. C. above the melt temperature of the PHB-Hx. The extruder is equipped with a die of width 6 inch and a die gap of 0.04 inch. The die is maintained at 20.degree. C. above the melt temperature of the PHB-Hx. The copolymer is melted within the extruder and pumped to the die at the other end of the extruder. The screw rpm is kept constant at 30 rpm. The copolymer is forced through the die and is collected on a take-up roll collection system (Postex) at a rate that allows crystallization of the copolymer before take-up. The width of these films are nominally 4 inch and the thickness are approximately 0.002 inch.
Example 6
Compostable Single Layer Film
Films of PHB-Hx are made by melting the material between Teflon sheets in a Carver Press (Fred S. Carver Inc., Menomonee Falls, Wis.) at 20.degree. C. above the melt temperature. Pressure on the sheets are adjusted to produce films of approximately 0.25 mm thick. The films are then identically cooled to room temperature by placing the molds between large (5 kg) aluminum plates and allowing the films to cool to room temperature.
Example 7
Compostable Multilayer Film
Sheets of PHB-Hx film may be prepared as in Example 6. These sheets may then encase a sheet of a polymer with good oxygen barrier properties but a poor water vapor transmission rate, or a polymer film that may be water soluble such a poly(vinyl alcohol) (PVA). The films are placed in carver press stacked in the following order PHB-Hx(95:5), PHB-Hx(50:50), PVA, PHB-Hx(50:50), PHB-Hx(95:5). The material is then pressed at a temperature 5.degree. C. above the melt temperature of PHB-Hx(50:50), but still below the melting temperature of the PHB-Hx(95:5). After compression at 2000 lb for 30 min, the pressure is released and the film is allowed to cool to room temperature.
Example 8
Compostable Disposable Diaper
A disposable baby diaper according to this invention is prepared as follows. The dimensions listed are for a diaper intended for use with a child in the 6-10 kilogram size range. These dimensions can be modified proportionately for different size children, or for adult incontinence briefs, according to standard practice.
1. Backsheet: 0.020-0.038 mm film consisting of a PHB-Hx copolymer (prepared as described in Example 6); width at top and bottom 33 cm; notched inwardly on both sides to a width-at-center of 28.5 cm; length 50.2 cm.
2. Topsheet: carded and thermally bonded staple-length polypropylene fibers (Hercules type 151 polypropylene); width at top and bottom 33 cm; notched inwardly on both sides to a width-at-center of 28.5 cm; length 50.2 cm.
3. Absorbent core: comprises 28.6 g of cellulose wood pulp and 4.9 g of absorbent gelling material particles (commercial polyacrylate from Nippon Shokubai); 8.4 mm thick, calendered; width at top and bottom 28.6 cm; notched inwardly at both sides to a width-at-center of 10.2 cm; length 44.5 cm.
4. Elastic leg bands: four individual rubber strips (2 per side); width 4.77 mm; length 370 mm; thickness 0.178 mm (all the foregoing dimensions being in the relaxed state).
The diaper is prepared in standard fashion by positioning the core material covered with the topsheet on the backsheet and gluing.
The elastic bands (designated "inner" and "outer", corresponding to the bands closest to, and farthest from, the core, respectively) are stretched to ca. 50.2 cm and positioned between the topsheet/backsheet along each longitudinal side (2 bands per side) of the core. The inner bands along each side are positioned ca. 55 mm from the narrowest width of the core (measured from the inner edge of the elastic bank). This provides a spacing element along each side of the diaper comprising the flexible topsheet/backsheet material between the inner elastic and the curved edge of the core. The inner bands are glued down along their length in the stretched state. The outer bands are positioned ca. 13 mm from the inner bands, and are glued down along their length in the stretched state. The topsheet/backsheet assembly is flexible, and the glued-down bands contract to elasticize the sides of the diaper.
Example 9
Compostable Lightweight Pantiliner
A lightweight pantiliner suitable for use between menstrual periods comprises a pad (surface area 117 cm.sup.2 ; SSK air felt 3.0 g) containing 1.0 g of absorbent gelling material particles (commercial polyacrylate; Nippon Shokubai); said pad being interposed between a porous formed-film topsheet according to U.S. Pat. No. 4,463,045 and a backsheet which comprises a 0.03 mm thickness PHB-Hx copolymer film, as prepared in accordance with Example 1.
Example 10
Compostable Sanitary Napkin
A catamenial product in the form of a sanitary napkin having two flaps extending outward from its absorbent core is prepared using a pad in the manner of Example 9 (surface area 117 cm.sup.2 ; 8.5 g SSK air felt), per the design of U.S. Pat. No. 4,687,478, Van Tillburg, Aug. 18, 1987. The backsheet and topsheet materials are the same as described in Example 6.
Example 11
Compostable Disposable Diaper
The diaper of Example 9 is modified by replacing the backsheet with a backsheet consisting of a 0.020 to 0.038 mm thickness film comprising a PHB-Hx copolymer film (prepared as described in Examples 6).
Example 12
Compostable Fiber
PHB-Hx of composition 5 mole % hexanoate/95 mole % butyrate is introduced into a single screw extruder (Rheomix Model 202) with screw diameter of 0.75 inch. A constant taper screw having 20:1 length to diameter ratio and a 3:1 compression ratio is employed. The temperature of both heating zones of the extruder barrel is 25.degree. C. above the melt temperature of the PHB-Hx. The extruder is equipped with a nozzle die containing 5 orifices of diameter 500 mm. The die is maintained at 20.degree. C. above the melt temperature of the PHB-Hx. The polymer is melted within the extruder and pumped to the die at the other end of the extruder. The screw rpm is kept constant at 30 rpm. The polymer is forced through the die and the melted extruded fibers are lead through a region where a rapid air stream is applied such that the polymer fibers elongates and thins to approximately one fifth of the diameter of the orifices (ca. 100 mm). The fibers are collected on a cardboard mat. A wide distribution of fiber lengths are obtained up several cm in length. Most fiber lengths (over 50%) are in the range of 1.3 to 15 cm.
Example 13
Compostable Nonwoven Fabric
PHB-Hx of composition 4 mole % hexanoate/96 mole % butyrate is introduced into a single screw extruder (Rheomix Model 202, Paramus, N.J.) with screw diameter of 0.75 inch. A constant taper screw having 20:1 length to diameter ratio and a 3:1 compression ratio is employed. The temperature of both heating zones of the extruder barrel is 25.degree. C. above the melt temperature of the PHB-Hx. The extruder is equipped with a nozzle die containing 5 orifices of diameter 500 mm. The die is maintained at 20.degree. C. above the melt temperature of the PHB-Hx. The polymer is melted within the extruder and pumped to the die at the other end of the extruder. The screw rpm is kept constant at 30 rpm. The polymer is forced through the die and the melted extruded fibers are lead through a region where a rapid air stream is applied such that the polymer fibers elongates and thins to approximately one fifth of the diameter of the orifices (ca. 100 mm). The fibers are collected on a cardboard mat. The mat is moved in a fashion so that a 10 cm.times.10 cm area is covered uniformly with fibers. Collection of fibers on the mat continues, until there is approximately 0.5 cm thick fiber mat. A wide distribution of fiber lengths are obtained up several inches in length. Most fiber lengths (over 50%) are in the range of 0.5 to 6 inches. The mat is then transferred to a Carver Press (Fred S. Carver Inc., Menomonee Falls, Wis.) and pressed at a 1000 lb force for 10 minutes at temperature 5.degree. C. below the melting temperature of the PHB-Hx. The resulting nonwoven sheet is removed from the press.
All publications mentioned hereinabove are hereby incorporated in their entirety by reference.
It is understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to one skilled in the art and are to be included in the spirit and purview of this application and scope of the appended claims.
Claims
What is claimed is:
1. A fiber comprising a biodegradable copolymer, wherein the biodegradable copolymer comprises at least two randomly repeating monomer units wherein the first randomly repeating monomer unit has the structure ##STR9## the second randomly repeating monomer unit has the structure ##STR10## and wherein at least 50% of the randomly repeating monomer units have the structure of the first randomly repeating monomer unit and wherein said biodegradable copolymer has a melt temperature of from about 30.degree. C. to about 160.degree. C.
2. The fiber of claim 1, wherein the copolymer comprises one or more additional randomly repeating monomer units having the structure ##STR11## wherein R.sup.1 is H, or a C.sub.2 or C.sub.4 -C.sub.19 alkyl or alkenyl; and n is 1 or 2.
3. The fiber of claim 2, wherein R.sup.1 is a C.sub.2 or C.sub.4 -C.sub.19 alkyl.
4. A nonwoven comprising the fiber of claim 1.
5. A nonwoven comprising the fiber of claim 2.
6. A nonwoven comprising the fiber of claim 3.
7. The fiber of claim 1 wherein said biodegradable copolymer has a melt temperature of from about 60.degree. C. to about 140.degree. C.
8. The fiber of claim 7, wherein the copolymer comprises one or more additional randomly repeating monomer units having the structure ##STR12## wherein R.sup.1 is H, or a C.sub.2 or C.sub.4 -C.sub.19 alkyl or alkenyl; and n is 1 or 2.
9. The fiber of claim 8, wherein R.sup.1 is a C.sub.2 or C.sub.4 -C.sub.19 alkyl.
10. A nonwoven comprising the fiber of claim 7.
11. A nonwoven comprising the fiber of claim 8.
12. A nonwoven comprising the fiber of claim 9.
Patent Citations (46)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US4393167 | 1983-07-01 | Holmes et al. | |
| US4477654 | 1984-10-01 | Holmes et al. | |
| US4603070 | 1986-07-01 | Steel et al. | |
| US4880592 | 1989-11-01 | Martini et al. | |
| US5004664 | 1991-04-01 | Fuller et al. | |
| US5023316 | 1991-06-01 | Benvenuti et al. | |
| US5135859 | 1992-08-01 | Witholt et al. | |
| US5135966 | 1992-08-01 | Chatterjee et al. | |
| US5191016 | 1993-03-01 | Yalpani | |
| US5191037 | 1993-03-01 | Doi et al. | |
| US5231148 | 1993-07-01 | Kleinke et al. | |
| US5292860 | 1994-03-01 | Shiotani et al. | |
| US5350627 | 1994-09-01 | Nemphos et al. | |
| US5391423 | 1995-02-01 | Wnuk et al. | |
| US5502116 | 1996-03-01 | Noda | |
| EPX400855 | 1990-12-01 | ||
| EPX416624A2 | 1991-03-01 | ||
| EPX533144A2 | 1993-03-01 | ||
| EPX540182A2 | 1993-05-01 | ||
| EPX540182A3 | 1993-05-01 | ||
| EPX560014A1 | 1993-09-01 | ||
| EPX606923A2 | 1994-07-01 | ||
| DEX290914A5 | 1991-06-01 | ||
| DEX4040158A1 | 1992-06-01 | ||
| DEX4212801A1 | 1992-11-01 | ||
| JPX5-159 | 1991-09-01 | ||
| JPX3-277656 | 1991-12-01 | ||
| JPX4-89004 | 1992-03-01 | ||
| JPX4-136067 | 1992-05-01 | ||
| JPX5-320323 | 1992-05-01 | ||
| JPX5-017590 | 1993-01-01 | ||
| JPX5034343 | 1993-02-01 | ||
| JPX5-093317 | 1993-04-01 | ||
| JPX5-093318 | 1993-04-01 | ||
| JPX5-230351 | 1993-09-01 | ||
| GBX2243327A | 1991-10-01 | ||
| WOX91/13207 | 1991-09-01 | ||
| WOX91/18994 | 1991-12-01 | ||
| WOX92/09211 | 1992-06-01 | ||
| WOX92/09210 | 1992-06-01 | ||
| WOX92/18553 | 1992-10-01 | ||
| WOX92/19747 | 1992-11-01 | ||
| WOX92/21708A1 | 1992-12-01 | ||
| WOX93/02194 | 1993-02-01 | ||
| WOX94/00506 | 1994-01-01 | ||
| WOX94/28070 | 1994-12-01 |
Non-Patent Literature (44)
- Abstract of Japanese Patent publication 04136066-A, published Nov. 5, 1992.
- Abe, H., Y. Doi, T. Fukushima and H. Eya, "Biosynthesis From Gluconate of a Random Copolyester Consisting of 3-hydroxy-butyrate and medium-chain-length 3-hydroxyalkanoates by Pseudomonas sp. 61-3", Int J Biol Macromol., vol. 16, No. 3, (May/Jun. 1994).
- Agostini, D.E., J.B. Lando & J.R. Shelton, "Synthesis and Characterization of Poly-.beta.-hydroxybutyrate. I. Synthesis of Crystalline DL-poly-.beta.-hydroxybutyrate from DL-.beta.-butyrolactone", Journal of Polymer Science, Part A-1, vol. 9, No. 10, pp. 2775-2787 (Oct. 1971).
- Aida, T., Y. Maekawa, S. Asano and S. Inoue, "Immortal Polymerization. Polymerization of Epoxide and .beta.-Lactone with Aluminum Porphyrin in the Presence of Protic Compound", Macromolecules, vol. 21, No. 5, pp. 1195-1202 (May 1988).
- Amos, D.A. & M.J. McInerney, "Composition of Poly-.beta.-hydroxyalkanoate From Syntrophomonas wolfei Grown on Unsaturated Fatty Acid Substrates", Arch. Microbiol., vol. 155, No. 2, pp. 103-106 (Mar. 1991).
- Anderson, A.J., G.W. Haywood, D.R. Williams & E.A. Dawes, "The Production of Polyhydroxyalkanoates From Unrelated Carton Sources", Novel Biodegradable Microbial Polymers, Dawes, E.A. Ed., Kluwer Academic Publ., Boston, pp. 119-129, (1990) (NATO ASI Series E. Applied Sciences--vol. 186).
- Anderson, A.J. & E.A. Dawes, Occurance, Metabolism, Metabolic Role, and Industrial Uses of Bacterial Polyhydroxyalkanoates, Microbiological Reviews, vol. 54, No. 4, pp. 450-472 (Dec. 1990).
- Barakat, I., R.J. Dubois and Teyssie, "Living Polymerization and Selective End Functionalization of e-Caprolactone Using Zinc Alkoxides as Initiators", Macromolecules, vol. 24, No. 24, pp. 6542-6545 (Nov. 1991).
- Bero, M., J. Kasperczyk & G. Adamus, "Coordination of Polymerization of Lactides, 3", Macromol. Chem., vol. 194, No. 3, pp. 907-912 (Mar. 1993).
- Billingham, N.C., M.G. Proctor & J.D. Smith, "Polymerization and Copolymerization of .beta.-butyrolactone by Aluminum Compounds", Journal of Organometallic Chemistry, vol. 341, pp. 83-93 (1988).
- Brandl, H., E.J. Knee, Jr., R.C. Fuller, R.A. Gross & R.W. Lenz, "Ability of the Phototrophic Bacterium Rhodospirillum rubrum to Produce Various Poly(.beta.-hydroxyalkanoates): Potential Sources for Biodegradable Polyesters", Int J Biol Macromol., vol. 11, pp. 49-55 (Feb. 1989).
- "Novel Biodegradable Microbial Polymers", E.A. Dawes, Ed., NATO ASI Series, Series E:Applied Sciences, vol. 186 (1990).
- Doi, Y. (ed) "Microbial Polyesters", Chapter 1, VCH Publishers, New York, pp. 1-9 (1990).
- Doi, Y., "Microbial Synthesis, Physical Properties and Biodegradability of Polyhydroxyalkanoates", Advances in Biopolymer Engineering Conference, (Jan. 23-28, 1994).
- Doi, Y., "Microbial Polyesters", Chapter 3, 4 and 5, VCH Publishers, New York, pp. 33-98 (1990).
- Dubois, P., I. Barakat, R. Jerome & P. Teyssie, "Macromolecular Engineering of Polylactones and Polylactides. 12. Study of the Depolymerization Reactions of Poly(e-caprolactone) with Functional Aluminum Alkoxide End Groups", Macromolecules, vol. 26, No. 17, pp. 4407-4412 (Aug. 1993).
- Gross, R.A., C. DeMello, R.W. Lenz, H. Brandl & R.C. Fuller, "Biosynthesis and Characterization of Poly (.beta.-hydroxyalkanoates Produced By Pseudomonas oleovorans", Macromolecules, vol. 22, No. 3, pp. 1106-1115 (Mar. 1989).
- Gross, R.A., Y. Zhang, G. Konrad & R.W. Lenz, "Polymerization of .beta.-monosubstituted-.beta.-propiolactones Using Trialkylaluminum-water Catalytic Systems and Polymer Characterization", Macromolecules, vol. 21, No. 9, pp. 2657-2668 (Sep. 1988).
- Haywood, G.W., A.J. Anderson & E. A. Dawes, A Survey of the Accumulation of Novel Polyhydroxyalkanoates by Bacteria:, Biotechnology Letters, vol. 11, No. 7, pp. 471-476 (1989).
- Hocking, P.J. & R.H. Marchessault, "Syndiotactic Poly[(R,S)-.beta.-hydroxybutyrate] Isolated from Methylaluminoxane-catalyzed Polymerization", Polymer Bulletin, vol. 30, pp. 163-170 (1993).
- Holmes, P.A., "Developments In Crystalline Polymers-2", D.C. Bassett, Ed., Elsevier Applied Science Publishing Co.(1988).
- Hori, Y., M. Suzuki, A. Yamaguchi & T. Nishishita, Ring-opening Polymerization of Optically Active .beta.-butyrolactone Using Distannoxane Catalysts: Synthesis of High Molecular Weight Poly(3-hydroxybutyrate), Macromolecules, vol. 26, No. 20, pp. 5533-5534 (Sep. 1993).
- Inoue, S., Y. Tomoi, T. Tsuruta & J. Furukawa, "Organometallic-catalyzed Polymerization of Propiolactone", (1961).
- Kaspercayk, J. & M. Bero, "Coordination Polymerization of lactides, 4", Makromol. Chem., vol. 194, No. 3, pp. 913-925 (Mar. 1993).
- Kemnitzer, J.E., S.P. McCarthy & R.A. Gross, "Preparation of Predominantly Syndiotactic Poly(.beta.-hydroxybutyrate) by the Tributyltin Methoxide Catalized Ring-Opening Polymerization of Racemic .beta.-butyrolactone", Macromolecules, vol. 26, No. 6, pp. 1221-1229 (Mar. 1993).
- Kobayashi, G. and T. Shiotani, "Biosynthesis and Characterization of Poly(3-hydroxybutyrate-co-hydroxyhexanoate)", SPSJ 41st Annual Meeting (May 29, 1992).
- Kumagai, Y. & Y. Doi, "Sythesis of a Block Copolymer of Poly(3-hydroxybutyrate) and Poly(Ethylene Glycol) and Its Application to Biodegradable Polymer Blends", Journal of Environment Polymer Degradation, vol. 1, No. 2, pp. 81-87 (1993).
- Lauzier, C.A., C.J. Monasterios, I. Saracovan, R.H. Marchessault and B.A. Ramsay, "Film Formation and Paper Coating with Poly(.beta.-hydroxyalkanoate), a Biodegradable Latex", Tappi Journal, vol. 76, No. 5, pp. 71-77 (May 1993).
- Le Borgne, A. & N. Spassky, "Stereoelective Polymerization of .beta.-butyrolactone", Polymer, vol. 30, pp. 2312-2319 (Dec. 1989).
- Liebergesell, M., F. Mayer & A. Steinbuchel, "Analysis of Polyhydroxyalkanoic Acid-biosynthesis Genes of Anoxygenic Phototrophic Bacteria Reveals Synthesis of a Polyester Exhibiting an Unusual Composition", Applied Microbiology and Biotechnology, vol. 40, pp. 292-300 (Nov. 1993).
- Liebergesell, M., E. Hustede, A. Timm, A. Steinbuchel, R.C. Fuller, R.W. Lenz & H.G. Schlegel, "Formation of Poly(3-hydroxyalkanoates) by Phototrophic and Chemolithotrophic Bacteria", Arch. Microbiol., vol. 155, No. 5, pp. 415-421 (Oct. 1991).
- Marchessault, R.H., P. Rioux and I. Saracovan, "Direct Electrostatic Coating of Paper", Nordic Pulp and Paper Research Journal No. 1, pp. 211-216 (Apr. 1993).
- Muller, H. and D. Seebach, "Poly(hydroxyalkanoates): A Fifth Class of Physiologically Important Organic Biopolymers?", Angew. Chem. Int. Ed. Engl., vol. 32, pp. 477-502 (1993).
- Poirier, Y., D.E. Dennis, C. Nawreth & C. Somerville, "Progress Toward Biologically Produced Biodegradable Thermoplastics", Advanced Materials, vol. 5, No. 1, pp. 30-36 (1993).
- Ramsay, B. A., I. Saracovan, J. A. Ramsay and R. H. Marchessault, "Continuous Production of Long-Side-Chain Poly-.beta.-Hydroxyalkanoates by Pseudomonas oleovorans", Applied and Environmental Microbiology, vol. 57, No. 3, pp. 625-629 (Mar. 1991).
- Shelton, J.R., D.E. Agostini & J.B. Lando, "Synthesis and Characterization of Poly-.beta.-hydroxybutyrate. II. Synthesis of D-poly-.beta.-hydroxybutyrate and the Mechanism of Ring-opening Polymerization of .beta.-butyrolactone", Journal of Polymer Science, Part A-1, vol. 9, No. 10, pp. 2789-2799 (Oct. 1971).
- Shimamura, E., M. Scandola and Y. Doi, "Microbiol Synthesis and Characterization of Poly(3-hydroxybutyrate-co-3-hydroxypropionate)", Macromolecules, vol. 27, No. 16, pp. 4429-4435 (Aug. 1, 1994).
- Shimamura, E., K. Kasuya, G. Kobayashi, T. Shiotani, Y. Shima and Y. Doi, Physical Properties and Biodegradability of Microbial Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate), Macromolecules, vol. 27, No. 4, pp. 878-880 (Jan. 1994).
- Steinbuchel & H.G. Schlegel, "Physiology and Molecular Genetics of Poly(.beta.-hydroxyalkanoic acid) Synthesis in Alcaligenes eutrophus", Molecular Microbiology, vol. 5, No. 3, pp. 535-542 (Mar. 1991).
- Tanahashi, N. & Y. Doi, "Thermal Properties and Stereoregularity of Poly(3-hydroxybutyrate) Prepared from Optically Active .beta.-butyrolactone With a Zinc-based Catalyst", Macromolecules, vol. 24, No. 20, pp. 5732-5733 (Sep. 1991).
- Timm, A. & A. Steinbuchel, "Formation of Polyesters Consisting of Medium-Chain-Length 3-hydroxyalkanoic Acids from Gluconate by Pseudonomads aeruginosa and Other Fluorescent Pseudomonads", Applied and Environmental Microbiology, vol. 56, No. 11, pp. 3360-3367 (Nov. 1990).
- Timm, A. & A. Steinbuchel, "Formation of Poly(3-hydroxyalkanoates) by Wild Type and Recombinant Strains of Pseudomonas aeruginosa and Other Fluorescent Pseudomonods", Novel Biodegradable Microbial Polymers, Dawes, E.A., Ed., Kluwer, Academic Publ., Boston, pp. 445-447 (1990) (NATO ASI Series E, Applied Sciences--vol. 186).
- Ulmer, H.W., R.A. Gross, M. Posada, P. Weisbach, R.C. Fuller & R.W. Lenz, "Bacterial Production of Poly(.beta.-hydroxyalkanoates) Containing Unsaturated Repeating Units by Rhodospirillum ribrum", Macromolecules, vol. 27, No. 7, pp. 1675-1679 (Mar. 1994).
- Zhang, Y., R.A., Gross & R.W. Lenz, "Stereochemistry of the Ring-opening Polymerization of (S)-.beta.-butyrolactone", Macromolecules, vol. 23, No. 13, pp. 3206-3212 (Jun. 1990).