Universal Well Cement Additives and Methods

1. Field of the Invention

The present invention relates generally to well cement additives, and more particularly, to universal composite additives for improving the properties of well cement slurries.

2. Description of the Prior Art

Hydraulic cement slurries used for cementing subterranean formations or zones in oil and gas wells must have particular properties. For example, the slurries must have properties such that they are capable of being mixed and pumped without prematurely gelling, have sufficiently long pumping times to be placed in subterranean formations or zones, have sufficiently high compressive strengths after setting, and have good fluid loss control.

The American Petroleum Institute (API) has set standards for different classes of oil well cements to insure that the cement slurries formed with them have required properties. The API cements are Portland cements and because of the strict requirements placed on them, they are more difficult to produce and more expensive than the many construction grade cements used for constructing bridges, roads, buildings and the like on the earth's surface.

Surface construction grade cements are commonly available from a variety of manufacturers throughout the world and are very inexpensive as compared to API Portland cements and other comparable cements used in cementing oil and gas wells. The construction grade cements typically contain high quantities of metal sulfates while the cements used in oil well cementing must have relatively low metal sulfate contents.

While cement slurries formed from inexpensive surface construction grade cements are suitable for a large number of surface applications, they do not have the properties required for subterranean oil and gas well cementing such as consistent viscosities, suitable thickening times, high compressive strengths after setting, good fluid loss control and the like. The chemical compositions, and particularly the metal sulfate concentrations, of surface construction grade cements vary from manufacturer to manufacturer making it impossible to predict the properties of cement slurries containing such cements. Thus, there is a need for a universal additive for improving the properties of inexpensive surface construction grade cement slurries whereby the slurries can be used in oil and gas well cementing applications.

A number of low quality oil and gas well cements which are available and used throughout the world also contain high metal sulfate concentrations and/or otherwise lack some of the properties required. For example, such low quality oil and gas well cements often have poor rheology, marginal strength development or poor response to conventional additives. Thus, there is also a need for a universal additive that can be utilized to improve the properties of presently used low quality oil and gas well cements.

The present invention provides universal composite particulate solid additives for improving the properties of well cement slurries which meet the needs described above and overcome the deficiencies of the prior art. When added to a surface construction grade or presently used oil and gas well grade hydraulic cement slurry, an additive of this invention simultaneously improves the viscosity, thickening time, after setting compressive strength, fluid loss control and other properties of the slurry to those which are particularly suitable for cementing oil and gas wells.

The universal additives of this invention are comprised of iron chloride selected from the group of ferrous chloride, ferric chloride and mixtures thereof present in an amount in the range of from about 0.5 to about 30 parts by weight, a dispersing agent present in an amount in the range of from about 1 to about 20 parts by weight, an organic acid present in an amount in the range of from about 0.01 to about 10 parts by weight, a hydratable polymer present in an amount in the range of from about 1 to about 20 parts by weight and an ultra-fine particulate hydraulic cement present in an amount in the range of from about 1 to about 50 parts by weight. Other components which can optionally be included in the additive are a defoaming agent, an alkaline earth metal halide and one or more other agents for increasing the set cement compressive strength.

Additional universal additives of this invention are comprised of iron chloride selected from the group of ferrous chloride, ferric chloride and mixtures thereof present in an amount in the range of from about 0.5 to about 30 parts by weight, an alkali or alkaline-earth metal halide, preferably chloride, present in an amount in the range of from about 5 to about 60 parts by weight, an organic acid present in an amount in the range of from about 0.01 to about 10 parts by weight and a hydratable polymer present in an amount in the range of from about 1 to about 50 parts by weight. Other components which are also preferably included in the additive are a defoaming agent, a dispersing agent, ultra-fine particle size hydraulic cement and other agents for increasing the set cement compressive strength.

The methods of this invention for improving the properties of a cement slurry comprised of a surface construction grade or better hydraulic cement and water comprise combining a universal additive of the present invention with the cement slurry in an amount in the range of from about 0.1% to about 30% by weight of the hydraulic cement in the slurry, the universal additive being comprised of iron chloride selected from the group of ferrous chloride, ferric chloride and mixtures thereof, a dispersing agent, an organic acid, a hydratable polymer and an ultra-fine particulate cement.

Additional methods of this invention for improving the properties of a cement slurry comprised of a surface construction grade or better hydraulic cement and water comprise combining a universal additive of the present invention with the cement slurry in an amount in the range of from about 0.1% to about 30% by weight of the hydraulic cement in the slurry, the universal additive being comprised of iron chloride selected from the group of ferrous chloride, ferric chloride and mixtures thereof, an alkali or alkaline-earth metal halide, an organic acid, and a hydratable polymer.

Methods of cementing a subterranean zone penetrated by a well bore utilizing a cement slurry comprised of a surface construction grade or better hydraulic cement and water are also provided by the present invention. The methods comprise the steps of combining a universal additive of this invention as described above with the cement slurry in an amount in the range of from about 0.1% to about 30% by weight of the hydraulic cement in the slurry, pumping the cement slurry containing the additive into the subterranean zone to be cemented by way of the well bore and then allowing the cement slurry to set into a hard impermeable mass therein.

It is, therefore, a general object of the present invention to provide universal well cement additives and methods of using the additives.

Other and further objects, features and advantages of the present invention will be readily apparent to those skilled in the art upon a reading of the description of the preferred embodiments which follows.

As mentioned above, construction grade cements for use in surface applications and low quality oil and gas well cements are readily available from a variety of manufacturers around the world and are very inexpensive as compared to the high quality API cements often used in cementing oil and gas wells. The surface construction grade and low quality oil and gas well cements typically contain high quantities of alkali and/or alkaline-earth metal sulfates, i.e., from about 0.75% to about 3.0% of such metal sulfates by weight of the cement. High quality API oil and gas well cements typically contain less than about 0.3% of such metal sulfates by weight of the cement. The presence of the high amounts of metal sulfates in the cements causes the cements to have varying and erratic properties such as thickening time and compressive strength when slurried in water.

The present invention provides single universally applicable particulate solid additives which contain mixtures of components that react synergistically with cement slurries to optimize the properties of the cement slurries and their performance in cementing oil and gas wells. The additives are not only useful in improving the properties and performance of surface construction grade and low quality oil and gas well cement slurries, but they also improve the properties and performance of other well cements including those meeting API standards. The additives are particularly useful in improving the properties of cements available in remote locations throughout the world whereby the cements can be effectively utilized in oil and gas well cementing.

The four basic properties of a cement slurry which the additives of the present invention improve to make the cement slurry suitable for oil and gas well cementing are viscosity (also referred to as rheology), thickening time, after setting compressive strength and fluid loss control. As mentioned, the additives of this invention are universally applicable to cement slurries formed with low quality high sulfate content cements as well as those formed with higher quality cements. The additives can be used to improve the properties of cement slurries which are to be subjected to temperatures up to about 230.degree. F. and which have densities in the range of from about 12 to about 17 pounds per gallon.

The universal additives of this invention are basically comprised of iron chloride selected from the group of ferrous chloride, ferric chloride and mixtures thereof present in an amount in the range of from about 0.5 to about 30 parts by weight, a dispersing agent present in an amount in the range of from about 1 to about 20 parts by weight, an organic acid present in an amount in the range of from about 0.01 to about 10 parts by weight, a viscosity increasing hydratable polymer present in an amount in the range of from about 1 to about 20 parts by weight and an ultra-fine particulate hydraulic cement present in an amount in the range of from about 1 to about 50 parts by weight.

As indicated above, the iron chloride can be ferrous chloride, ferric chloride or mixtures thereof. The iron chloride functions synergistically with the other components of the additive to overcome the effect of a high metal sulfate concentration in a cement and to shorten the thickening time of a slurry of the cement to an acceptable range. That is, the iron chloride in combination with the other components of the additive causes the cement to hydrate in a normal and predictable manner. Also, the iron chloride contributes to improving the compressive strength of the cement slurry after it sets.

The dispersing agent in the additive helps control the rheology of the cement slurry and contributes to making the slurry a stable suspension over a broad density range. While various dispersing agents can be utilized, a particularly suitable dispersing agent is the condensation polymer product of an aliphatic ketone, e.g., acetone, an aliphatic aldehyde, e.g., formaldehyde, and a compound which introduces acid groups into the polymer, e.g., sodium sulfite. Such a dispersing agent is described in U.S. Pat. No. 4,557,763 issued to George et al. on Dec. 10, 1985, which is incorporated herein by reference, and is commercially available under the trade designation "CFR-3.TM." from Halliburton Energy Services of Duncan, Okla.

The organic acid in the additive controls the viscosity of the cement slurry, i.e., it prevents the premature gelation of the slurry and improves the rheology of the slurry over a broad density range. Various organic acids can be utilized in the additive including, but not limited to, tartaric acid, citric acid, gluconic acid, oleic acid, phosphoric acid and uric acid. Of these, tartaric acid is preferred.

A variety of viscosity increasing hydratable polymers can also be utilized in the additive including, but not limited to, carboxymethylcellulose, hydroxyethylcellulose, carboxymethylhydroxyethylcellulose, vinyl sulfonated polymers, hydratable graft polymers and other hydratable polymers known to those skilled in the art. Of these, hydroxyethylcellulose is preferred. The hydratable polymer utilized adds viscosity to the cement slurry and functions to reduce fluid loss from the slurry.

The ultra-fine particulate hydraulic cement in the additive preferably has a maximum particle size of about 15 microns and a specific surface area of about 12,000 square centimeters per gram. The distribution of the various size particles within the ultra-fine cement is preferably such that about 90% of the particles have diameters no greater than about 10 microns, 50% have diameters no greater than about 5 microns, and 20% of the particles have diameters no greater than about 3 microns. The specific surface area of the ultra-fine hydraulic cement (sometimes also referred to as Blaine fineness) is an indication of the ability of the cement to chemically interact with other materials. The specific surface area is preferably greater than about 12,000 square centimeters per gram, and more preferably, greater than about 13,000 square centimeters per gram.

Ultra-fine cements having maximum particle sizes and surface areas as set out above are disclosed in various prior U.S. patents including U.S. Pat. No. 4,761,183 issued to Clarke during August 1988 which discloses ultra-fine particle size cements formed of slag and mixtures thereof with Portland cement and U.S. Pat. No. 4,160,674 issued to Sawyer during July 1979 which discloses ultra-fine particle size Portland cements, both of which are incorporated herein by reference. The ultra-fine hydraulic cement preferred for use in accordance with this invention is Portland cement. Such a cement is commercially available under the trade designation "MICRO-MATRIX.TM." from Capitol Cement Co. of San Antonio, Tex. The presence of the ultra-fine cement in the cement slurry adds compressive strength to the cement slurry after it sets and contributes to shortening the thickening time of the cement slurry to a preferred range.

As indicated above, the additive can also include a number of other components which provide improved properties to a cement slurry. That is, the additive can include a defoaming agent such as polydimethylsiloxane present in the additive in an amount in the range of from about 0.01 to about 5 parts by weight. Such a defoaming agent is commercially available under the trade name "D-AIR.TM." from Halliburton Energy Services of Duncan, Okla. The defoaming agent prevents a cement slurry containing the additive from excessively foaming during mixing and pumping.

Another component which can be included in the additive is an alkali or alkaline-earth metal halide which functions with the iron chloride to overcome the effect of high metal sulfate concentration. Preferred such compounds are calcium chloride, sodium chloride, potassium chloride and ammonium chloride, with calcium chloride being the most preferred. When used, the alkali or alkaline earth metal halide is generally included in the additive in an amount in the range of from about 5 to about 20 parts by weight.

Still another component which can be included in the additive is a particulate ASTM Type III cement which contributes to increasing the after setting compressive strength of the cement slurry and decreasing the thickening time of the slurry. Such a cement is commercially available under the trade designation "TXI III.TM." from Texas Industries, Inc. of Midlothian, Tex. When used, the ASTM Type III cement is generally included in the additive in an amount in the range of from about 1 part to about 50 parts by weight.

Yet another component which can be included in the additive is a particulate silica such as fumed silica or ultra-fine silica. The silica functions in a cement slurry to prevent after setting compressive strength retrogression in hot wells. When used, the silica is preferably included in the additive in an amount in the range of from about 0.1 to about 50 parts by weight.

A preferred universal particulate solid additive of this invention for improving the properties of a cement slurry is comprised of iron chloride selected from the group of ferrous chloride, ferric chloride and mixtures thereof present in an amount of about 10 parts by weight, a dispersing agent comprised of the condensation polymer product of acetone, formaldehyde and sodium sulfite present in an amount of about 13 parts by weight, tartaric acid present in an amount of about 0.4 parts by weight, hydroxyethylcellulose present in an amount of about 2 parts by weight and an ultra-fine particulate hydraulic cement having a maximum particle size of about 15 microns and a specific surface of about 12,000 square centimeters per gram present in an amount of about 8 parts by weight.

Additional universal additives of this invention are basically comprised of iron chloride selected from the group of ferrous chloride, ferric chloride and mixtures thereof present in an amount in the range of from about 0.5 to about 30 parts by weight, an alkaline-earth metal halide, preferably chloride, present in an amount in the range of from about 5 to about 60 parts by weight, an organic acid present in an amount in the range of from about 0.01 to about 10 parts by weight, and a viscosity increasing hydratable polymer present in an amount in the range of from about 1% to about 50% by weight.

As indicated above, the iron chloride can be ferrous chloride, ferric chloride or mixtures thereof. The iron chloride functions synergistically with the alkali or alkaline-earth metal halide and other components of the additive to overcome the effect of a high metal sulfate concentration in a cement and to shorten the thickening time of a slurry of the cement to an acceptable range. That is, the iron chloride in combination with the alkali or alkaline-earth metal halide and other components of the additive cause the cement to hydrate in a normal and predictable manner.

A variety of alkali or alkaline-earth metal halides can be utilized in the additive which function synergistically with the iron chloride as described above. Preferred such compounds are calcium chloride, sodium chloride, potassium chloride and ammonium chloride, with calcium chloride being the most preferred.

The organic acid in the additive controls the viscosity of the cement slurry, i.e., it prevents the premature gelation of the slurry and improves the rheology of the slurry over a broad density range. Various organic acids can be utilized in the additive including, but not limited to, tartaric acid, citric acid, gluconic acid, oleic acid, phosphoric acid and uric acid. Of these, tartaric acid is preferred.

A variety of viscosity increasing hydratable polymers can also be utilized in the additive including, but not limited to, carboxymethylcellulose, hydroxyethylcellulose, carboxymethylhydroxyethylcellulose, vinyl sulfonated polymers, hydratable graft polymers and other hydratable polymers known to those skilled in the art. Of these, hydroxyethylcellulose is preferred. The hydratable polymer utilized adds viscosity to the cement slurry and functions to reduce fluid loss from the slurry.

As indicated above, the additive preferably also includes a number of other components which provide improved properties to a cement slurry. That is, the additive preferably also includes a defoaming agent such as polydimethylsiloxane present in the additive in an amount in the range of from about 0.01 to about 5 parts by weight, a dispersing agent as described above in an amount in the range of from about 1 to about 20 parts by weight, an ultra-fine particulate hydraulic cement in an amount in the range of from about 1 to about 50 parts by weight, an ASTM Type III cement as described above in an amount in the range of from about 1 part to about 50 parts by weight and fumed or ultra-fine silica in an amount in the range of from about 0.1 to about 50 parts by weight.

Another preferred universal particulate solid additive of this invention for improving the properties of a cement slurry is comprised of iron chloride selected from the group of ferrous chloride, ferric chloride and mixtures thereof present in an amount of about 10 parts by weight, calcium chloride present in an amount of about 14 parts by weight, tartaric acid present in an amount of about 0.3 parts by weight, hydroxyethylcellulose present in an amount of about 12 parts by weight, a defoaming agent comprised of polydimethylsiloxane present in an amount of about 0.3 parts by weight, a dispersing agent comprised of the condensation polymer product of acetone, formaldehyde and sodium sulfite present in an amount of about 11 parts by weight, an ultra-fine particulate hydraulic cement having a maximum particle size of about 15 microns and a specific surface of about 12,000 square centimeters per gram present in an amount of about 8 parts by weight, a particulate ASTM Type III cement present in an amount of about 8 parts by weight and fumed silica present in an amount of about 8 parts by weight.

The additives of this invention can be mixed with a cement slurry using various techniques known to those skilled in the art. A particularly suitable technique is to combine the additive used with the water utilized in a mixer followed by the hydraulic cement used.

The present invention also provides methods of converting the viscosity, thickening time, after setting compressive strength, fluid loss and other properties of a cement slurry comprised of a surface construction grade or better hydraulic cement and water to those properties which are particularly suitable for cementing oil and gas wells. Such methods basically comprise combining a universal particulate solid additive of this invention as described above with the construction grade or better cement slurry in an amount in the range of from about 0.1% to about 30% by weight of the cement in the slurry. As described above, the resulting cement slurry containing the additive has properties particularly suitable for use in cementing oil and gas wells.

Additional methods are provided by the present invention for cementing a subterranean zone penetrated by a well bore. The subterranean zone can have a static temperature of up to about 230.degree. F. and the construction grade or better cement slurry utilized can have a density in the range of from about 12 to 17 pounds per gallon. In accordance with the methods, a universal particulate solid additive of this invention is combined with the construction grade or better cement slurry in an amount in the range of from about 0.1% to about 30% by weight of the cement in the slurry. The resulting cement slurry having improved properties is pumped into the subterranean zone to be cemented by way of the well bore penetrating it and the cement slurry is then allowed to set into a hard impermeable mass in the zone.

In order to further illustrate the universal additives and methods of this invention, the following examples are given.

A variety of cement slurries having various densities and utilizing various API hydraulic cements, fresh water or salt water and various quantities of a universal additive of this invention were prepared. The slurries were tested for thickening time, fluid loss, rheology (plastic viscosity/yield point), compressive strengths and shear bond strengths at various temperatures. The tests were run in accordance with the procedures set forth in the API Specification For Materials And Testing For Well Cements, API Specification 10, 5th Edition, dated Jul. 1, 1990, of the American Petroleum Institute.

The universal additive utilized in the tests was comprised of 10 parts by weight ferric chloride, 13 parts by weight of a dispersing agent comprised of the condensation polymer product of acetone, formaldehyde and sodium sulfite, 0.4 parts by weight tartaric acid, 2 parts by weight hydroxyethylcellulose and 8 parts by weight of a particulate ultra-fine hydraulic cement having a maximum particle size of about 15 microns and a specific surface area of about 12,000 square centimeters per gram. The additive was mixed with the cement slurries tested in the amounts indicated in Table I below. In a number of the tests, the cement slurry was tested with and without the additive of this invention. In order of the tests, a conventional set retarding agent was substituted for the universal additive of this invention or included in the cement slurry with the universal additive. Also, fumed silica was included in some of the cement slurries tested.

The results of these tests are given in Table I below. - Properties Of Cement Slurries Containing Universal Cement Additive Cement In The Water In Universal Set Fumed Slurry Fluid Compressive Strength, psi Slurry Tested, Slurry, Additive, Retarder, Silica, Density, Loss at 140.degree. F. 180.degree. F. 250.degree. F. Country, % by % by % by % by Pounds 140.degree. F., Time to Time to Time to Time to Time to Time to Test Manufacturer and Weight of Weight of Weight of Weight of Per Thickening Time, Hrs:Min cc/30 PV/YP 50 psi, 500 psi, 50 psi, 50 psi 50 psi, 500 psi, No. API Class Cement Cement Cement Cement Gallon 140.degree. F. 180.degree. F. 250.degree. F. min 80.degree. F. 140.degree. F. hr:min hr:min 24 hr hr:min hr:min 24 hr hr:min hr:min 24 hr 1 Nigeria Eagle G 44 -- -- -- 15.9 0:52 -- -- 1907 39/27 54/71 1:21 2.02 3073 -- -- -- -- -- -- 2 Nigeria Eagle G 44 1.5 -- -- 15.9 1:07 -- -- 450 60/8 57/50 1:12 2:40 3185 -- -- -- -- -- -- 3 Bolivia Warnes A 46 -- -- -- 15.6 0:55 -- -- 1950 51/78 -- 1:59 3:16 2030 -- -- -- -- -- -- 4 Bolivia Warnes A 46 1.5 -- -- 15.6 1:21 -- -- 477 65/30 48/28 3:22 5:39 2108 -- -- -- -- -- -- 5 India Kujang G 44 -- -- -- 15.9 1:10 -- -- 1900 30/22 57/11 1:40 2:54 2816 -- -- -- -- -- -- 6 India Kujang G 44 1.5 -- -- 15.9 1:13 -- -- 600 44/10 39/16 1:56 2:55 3123 -- -- -- -- -- -- 7 Bolivia Warnes A 46 -- 0.5.sup.2 -- 15.6 -- 2:22 -- -- -- -- -- -- -- 6:46 7:57 2079 -- -- -- 8 Bolivia Warnes A 46 1.5 0.5.sup.2 -- 15.6 -- 6:06 -- -- -- -- -- -- -- 19:00 22:44 574 -- -- -- 9 India Kujang G 56 -- 0.65.sup.3 35 15.8 -- -- 4:28 -- -- -- -- -- -- -- -- -- 4:22 5:00 2628 10 India Kujang G 56 1.5 0.65.sup.3 35 15.8 -- -- 2:16 -- -- -- . -- -- -- -- -- 4:31 5.05 2526 11 USA Capital H 48.6 -- 0.65.sup.3 35 16.4 -- -- 7:50 -- -- -- -- -- -- -- -- -- 16:09 18:43 1481 12 USA Capital H 48.6 1.3 0.65.sup.3 35 16.4 -- -- 2:59 -- -- -- -- -- -- -- -- -- 1:25 5:20 2512 13 .sub.------ Baturaja A 58.2 -- 0.65.sup.3 35 15.6 -- -- 4:44 -- -- -- -- -- -- -- -- -- 8:47 10:35 2173 14 .sub.------ Baturaja A 58.2 1.5 0.65.sup.3 35 15.6 -- -- 3:17 -- -- -- -- -- -- -- -- -- 6.01 6:41 2621 15 .sub.------ Baturaja A 53.7 .sup. 5.18.sup.1 0.65.sup.3 35 15.6 -- -- 2:56 -- -- -- -- -- -- -- -- -- 1:42 4:41 2429 16 USA Capital H 39.1 -- 0.5.sup.3 -- 16.4 -- 5:50 -- -- -- -- -- -- -- 14:03 15:20 1455 -- -- -- 17 USA Capital H 39.1 1.5 0.5.sup.2 -- 16.4 -- 8:44 -- -- -- -- -- -- -- 14.00 18:23 1571 -- -- -- 18 India Kujang G 44.8 -- 0.5.sup.2 -- 15.8 -- 3:23 -- -- -- -- -- -- -- 4:51 5:55 2800 -- -- -- 19 India Kujang G 44.8 1.5 0.5.sup.2 -- 15.8 -- 4:21 -- -- -- . -- -- -- 9:38 11:22 2543 -- -- -- 20 .sub.------ Baturaja A 46.3 -- 0.5.sup.2 -- 15.6 -- 3:38 -- -- -- -- -- -- -- 7:37 8:58 2200 -- -- -- 21 .sub.------ Baturaja A 46.3 1.5 0.5.sup.2 -- 15.6 -- 6:12 -- -- -- -- -- -- -- 14:10 16:32 1866 -- -- -- 22 .sub.------ Baturaja A 42.3 .sup. 5.18.sup.1 0.5.sup.2 -- 15.6 -- 13:20 -- -- -- -- -- -- -- No Set No Set No Set -- -- -- 23 .sub.------ Baturaja A 42.3 .sup. 5.18.sup.1 0.5.sup.2 -- 15.6 -- 12:17 -- -- -- -- -- -- -- 28:54 38:20 No Set -- -- -- 24 .sub.------ Baturaja A 53.7 .sup. 5.18.sup.1 0.65.sup.3 35 15.6 -- -- 5:12 -- -- -- -- -- -- -- -- -- 7:52 8:53 2514 .sup.1 Additive dissolved in .sub.------ fresh water in an amount of .sub.-- % by weight of solution .sup.2 Set retarder was sodium lignosulfonate .sup.3 Set retarder was calcium lignosulfonate

From Table I, it can be seen that all of the various slurries tested which contained the additive of this invention had excellent properties and were suitable for oil and gas well cementing applications.

A variety of cement slurries having various densities and utilizing various API hydraulic cements, fresh water or salt water and various quantities of another universal additive of this invention were prepared. The slurries were tested for thickening time, fluid loss, rheology (plastic viscosity/yield point), compressive strengths and shear bond strengths at various temperatures. The tests were run in accordance with the procedures set forth in the API Specification For Materials And Testing For Well Cements, API Specification 10, 5th Edition, dated Jul. 1, 1990, of the American Petroleum Institute.

The universal additive utilized in the tests was comprised of 10 parts by weight ferric chloride, 14 parts by weight calcium chloride, 0.3 parts by weight tartaric acid, 12 parts by weight hydroxyethylcellulose, 0.3 parts by weight of a polydimethylsiloxane defoaming agent, 11 parts by weight of a dispersing agent comprised of the condensation product of acetone, formaldehyde and sodium sulfite, 8 parts by weight of a particulate ultra-fine hydraulic cement having a maximum particle size of about 15 microns and a specific surface area of about 12,000 square centimeters per gram, 8 parts by weight of ASTM Type III cement (commercially available, for example from Texas Industries of Midlothian, Tex.) and 8 parts by weight of fumed silica. The additive was mixed with the cement slurries tested in the amounts indicated in Table II below.

The results of these tests are given in Table II below. - Properties Of Cement Slurries Containing Universal Additive Cement In The Water In Universal Slurry Thickening 24 Hr 48 Hr 140.degree. F. Slurry Tested, Slurry, % Additive, % Density, Time, Fluid Loss, Compressive Compressive Shear Bond Test Manufacturer and by Weight By Weight Pounds Per Hrs:Min CC/30 Min P V/YP Strength, psi Strength, psi Strength, psi No. API Class Cement of Cement Gallon 100.degree. F. 140.degree. F. 80.degree. F. 140.degree. F. 800.degree. F. 140.degree. F. 100.degree. F. 140.degree. F. 100.degree. F. 140.degree. F. 7 days 48 hrs 1 Capital H 54.53 4 15 -- 3:33 0 210 144/39 107/21 770 91 1895 2140 -- -- 2 Capital H 100.3 11 12.8 13:12 -- 0 64 125/25 117/18 0 0 425 398 -- -- 3 Fredonia H 54.53 4 15 -- 4:40 0 267 168/31 119/36 949 2810 3020 3720 -- -- 4 Fredonia H 100.3 11 12.8 18:00 -- 0 91 125/25 102/23 0 88 662 1055 -- -- 5 Lone Star H 54.53 4 15 -- 4:00 0 240 122/28 116/22 1051 860 2130 1656 193 273 6 Lone Star H 100.3 11 12.8 13:30 -- 0 72 107/18 85/15 0 0 709 566 119 178 7 Capital A 59.5 4.5 14.6 -- 2:22 0 266 138/47 95/30 2540 3100 3780 4170 -- -- 8 Capital A 100.3 11 12.8 6:20 -- 0 82 117/28 117/28 554 906 975 1378 -- -- 9 Blue Circle A 59.5 4.5 14.6 -- 2:55 0 160 131/50 120/68 2000 3250 . 3810 4490 -- -- 10 BIue Circle A 100.3 11 12.8 10:10 -- 0 76 113/22 165/35 250 425 856 1050 -- -- 11 TX. Lehigh A 59.5 4.5 14.6 -- 2:10 0 196 114/21 72/18 2280 3060 2430 2270 336 433 12 TX. Lehigh A 100.3 11 12.8 8:22 -- 0 42 129/24 79/16 416 634 770 1086 148 183 13 Lone Star A 59.5 4.5 14.6 -- 2:20 0 231 108/44 98/37 1858 3210 3670 4020 -- -- 14 Lone Star A 100.3 11 12.8 9:00 -- 0 64 156/33 153/30 412 528 924 1206 -- -- 15 Ekshaw G 57.25 4.25 14.8 -- 2:40 0 194 113/44 111/42 1920 2910 3460 4060 -- -- 16 Ekshaw G 100.3 11 12.8 14:00 -- 0 68 128/22 128/22 25 13 704 900 -- -- 17 Dykerhoff G 57.25 4.25 14.8 -- 3:20 0 300 116/18 77/20 2140 2670 3220 3510 -- -- 18 Dykerhoff G 100.3 11 12.8 12:59 -- 0 80 102/20 81/17 203 11 575 944 -- -- 19 Bolivja G#4 57.25 4.25 14.8 -- 3:40 0 250 137/21 110/20 1326 2730 3100 4600 -- -- 20 Bolivia G#4 100.3 11 12.8 13:50 -- 0 44 111/16 90/8 0 0 641 1026 -- --

From Table II it can be seen that all of the various slurries tested had excellent properties and were suitable for oil and gas well cementing applications.

The tests described above were repeated utilizing five cement slurries at two different densities with and without the universal additive of this invention. The results of these tests are given in Table III below.

From Table III it can be seen that the presence of the universal additive of this invention in the various cement slurries tested significantly improved the properties of the cement slurries.

Thus, the present invention is well adapted to carry out the objects and attain the ends and advantages mentioned as well as those which are inherent therein. While numerous changes may be made by those skilled in the art, such changes are encompassed within the spirit of this invention as defined by the appended claims.