US 5,910,218 AGrant
Systems for Forming Films Having High Dielectric Constants
Issue Date:1999-06-08
•25 Claims
•3 Drawing Sheets
Abstract
A method form forming a dielectric film on a substrate includes the steps of placing the substrate in a process chamber wherein said substrate is isolated from an external environment, depositing the dielectric film on the substrate in the process chamber, and annealing the dielectric film in said process chamber. In particular, the dielectric film can be formed from Ta.sub.2 O.sub.5. Systems for forming the dielectric film are also disclosed.
Metadata
Assignee
- Samsung Electronics Co., Ltd.
Inventors
- Young-wook Park
- Moon-yong Lee
- Kyung-hun Kim
- In-sung Park
Application Information
Application Number:US 7079044
Filing Date:1996-09-12
Priority Date:1995-11-28
Art Unit:162
Classifications
IPC:
C23C 1600H01L 27108
Field of Search:
257118310719;728
Patent Drawings (3 sheets)
Description
Field of the Invention
The present invention relates to the field of microelectronics and more particularly to dielectric films for microelectronic circuits.
Background of the Invention
A dynamic random access memory (DRAM) includes an array of memory cells with each memory cell having a capacitor and a transistor. As DRAMs become more highly integrated, the size of the capacitor and the operating voltage both decrease. Because a predetermined charge is required-on the capacitor to discriminate between logic levels, reductions in the size of the capacitor may be limited by the capacitance required to store the predetermined charge. The electrical charge Q of a capacitor is determined by multiplying the capacitance C by the operating voltage V. Accordingly, in order to store a predetermined charge at a lowered operating voltage, the capacitance of the capacitor must be increased.
The capacitance of a capacitor can be increased by increasing the effective area of the capacitor, by increasing the dielectric constant of the dielectric layer, and by decreasing the thickness of the dielectric layer. Because increasing the effective area of a capacitor may require an increase in the size of the capacitor, and because decreasing the thickness of the dielectric layer may be limited by manufacturing constraints, these approaches to increasing capacitance may not be sufficient. The use of dielectric materials having higher dielectric constants may, however, provide increased capacitance while reducing the size of the capacitor without requiring a dielectric thickness which is unnecessarily difficult to produce. For example, Ta.sub.2 O.sub.5 can be used to produce a dielectric film having a significantly higher dielectric constant than a dielectric film of the same thickness formed from silicon oxide SiO.sub.2. The film formed from Ta.sub.2 O.sub.5 can have a dielectric constant on the order of 20 to 25. Accordingly, when using a Ta.sub.2 O.sub.5 film as the dielectric layer of a capacitor, the surface areas of the capacitor electrodes can be reduced without reducing the capacitance and without significantly increasing manufacturing costs.
A flowchart for a method of forming a capacitor including a Ta.sub.2 O.sub.5 dielectric film is illustrated in FIG. 1. A method for forming a capacitor includes the steps of forming a lower electrode of the capacitor S1, cleaning the lower electrode surface to remove a naturally occurring oxide film therefrom S2, rapid thermal processing S3, depositing the Ta.sub.2 O.sub.5 film S4, annealing the Ta.sub.2 O.sub.5 film with ultraviolet light and ozone (O.sub.3) S5, annealing the Ta.sub.2 O.sub.5 film with oxygen (O.sub.2) S6, and forming an upper electrode for the capacitor S7.
The step of rapid thermal processing S3 eliminates an oxidation barrier generated at an interface between the lower electrode and the Ta.sub.2 O.sub.5 film. The rapid thermal processing step may be provided as a succession of heat treatments. The step of annealing the Ta.sub.2 O.sub.5 film with ultraviolet light and ozone (O.sub.3) S5 reduces oxygen vacancies in the Ta.sub.2 O.sub.5 film. The step of oxygen (O.sub.2) annealing S6 reduces weak spots in the Ta.sub.2 O.sub.5 film.
It is known, for example, to reduce leakage current of a Ta.sub.2 O.sub.5 film by annealing the film. An annealing method is described in a publication by Shinriki et al. entitled "UV-O.sub.3 DRY-O.sub.2 : Two-Step Annealed Chemical Vapor-Deposited Ta.sub.2 O.sub.5, Films For Storage Dielectrics Of 64-Mb DRAM's", IEEE Transactions On Electron Devices, Vol. 38, No. 3, March 1991, pp. 455-462, the disclosure of which is hereby incorporated herein by reference.
Typically, a deposition system is used to deposit the Ta.sub.2 O.sub.5 film, and separate systems are used to anneal and clean the structure. Accordingly, the Ta.sub.2 O.sub.5 dielectric film may be exposed to air resulting in the adsorption of water and/or free carbon. Accordingly, exposure to air may cause deterioration of the dielectric layer and the adjacent electrodes. In addition, the loading and unloading of the production substrates from one system to the next may result in unnecessary heating and cooling between each step as well as unnecessary transfers of the material thus reducing the efficiency of the process and lowering the throughput.
Summary of the Invention
It is therefor an object of the present invention to provide improved methods and systems for forming dielectric films.
It is another object of the present invention to provide methods and systems for forming dielectric films with improved dielectric characteristics.
It is still another object of the present invention to provide methods and systems for forming dielectric films while reducing exposure to the atmosphere.
These and other objects according to the present invention are provided by methods and systems for forming dielectric films including the steps of placing a substrate in a process chamber, depositing the dielectric film on the substrate in the process chamber, and annealing the dielectric film in the ark process chamber. By both depositing and annealing the dielectric film in the process chamber, the substrate and film can be isolated from the external environment between the steps of depositing and annealing the dielectric film. Accordingly, adsorption of moisture and free carbon from the air can be reduced thus improving the characteristics of the dielectric film.
In particular, the dielectric film may comprise a material with a high dielectric constant, such as Ta.sub.2 O.sub.5. Ta.sub.2 O.sub.5 has a dielectric constant on the order of 20-25 which is significantly higher than that of silicon dioxide. Alternately, the film may comprise another material having a high dielectric constant, such as BaSrTiO.sub.3 (BST) or PbZrTiO.sub.3 (PZT).
In addition, the step of depositing the dielectric film can include raising the temperature inside the process chamber to a first temperature and depositing the dielectric film. The step of annealing the film can include lowering the temperature inside the process chamber from said first temperature to a second temperature and annealing the dielectric film to fill oxygen vacancies therein. By heating the process chamber to different temperatures, the steps of depositing and annealing the dielectric film can be accommodated in the same process chamber. More particularly, the first temperature can be in the range of 350 to 450 degrees C. when depositing the dielectric film, and the second temperature can be in the range of 250 to 350 degrees C.
Furthermore, the annealing step can include providing ozone (O.sub.3) and ultraviolet light in the process chamber. Alternately, the annealing step can include providing an oxygen (O.sub.2) plasma in the process chamber, and this oxygen (O.sub.2) plasma can be generated by RF power.
According to another aspect of the present invention, a system is provided for forming a dielectric film on a microelectronic substrate. This system includes a process chamber which receives the substrate and isolates the substrate from an external atmosphere. This system also includes means for depositing the dielectric film on the substrate in the process chamber, and means for annealing the dielectric film in the process chamber. Accordingly, the dielectric film can be deposited and annealed while reducing exposure to air thus reducing adsorption of moisture and free carbon.
In addition, the system can include a heat source which heats the substrate to a first temperature when depositing the dielectric film and which heats the substrate to a second temperature when annealing the dielectric film. In particular, the first temperature can be in the range of 350 to 450 degrees C., and the second temperature can be in the range of 250 to 350 degrees C. The heat source can be a resistive heater or a lamp. The annealing means can include an ultraviolet lamp located in the process chamber adjacent the susceptor opposite the heat source.
The methods and systems of the present invention thus allow a dielectric film to be deposited and annealed on a substrate while reducing the exposure of the dielectric film to air. Accordingly, adsorption of moisture and free carbon by the dielectric film can be reduced. The dielectric film thus formed can have improved dielectric characteristics.
Brief Description of the Drawings
FIG. 1 is a flowchart illustrating a method for manufacturing a capacitor including a Ta.sub.2 O.sub.5 dielectric film according to the prior art.
FIG. 2 is a time-temperature chart illustrating a sequence of steps in a method for forming a Ta.sub.2 O.sub.5 film according to the present invention.
FIG. 3 is a time-temperature chart illustrating a sequence of steps in a second method for forming a Ta.sub.2 O.sub.5 film according to the present invention.
FIGS. 4 and 5 are cross-sectional views illustrating the structure of a system for forming a Ta.sub.2 O.sub.5 film according to the present invention.
Detailed Description
The present invention will now be described more fully hereinafter with reference to the accompanying drawings, in which preferred embodiments of the invention are shown. This invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein; rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. Like numbers refer to like elements throughout.
According to the present invention, a method for forming a Ta.sub.2 O.sub.5 film includes the steps of depositing and annealing the Ta.sub.2 O.sub.5 film in-situ in a single process chamber. As shown in FIG. 2, this method can include the steps of increasing the temperature inside the chamber to a first temperature on the order of 350-450.degree. C. S112, and depositing the Ta.sub.2 O.sub.5 film S113 on the substrate inside the process chamber. The temperature of the substrate inside the chamber is then lowered to a second temperature on the order of 250-350.degree. C. S114 after depositing the Ta.sub.2 O.sub.5 film. The Ta.sub.2 O.sub.5 film is then annealed by providing ultraviolet light and ozone (O.sub.3) S115 in the process chamber thus filling oxygen vacancies in the Ta.sub.2 O.sub.5 film. The temperature is then lowered again S116 allowing the substrate with the Ta.sub.2 O.sub.5 dielectric film to be removed from the process chamber. Alternately, the annealing step S175 can be accomplished by providing an oxygen (O.sub.2) plasma adjacent the substrate in the process chamber. In the event that an oxygen plasma anneal is used, an RF generator can be used to produce the oxygen plasma. When using ultraviolet light and ozone, a UV lamp can be used to generate the ultraviolet light.
The process chamber of the present invention can include a single process area where the Ta.sub.2 O.sub.5 film is both deposited and annealed. Alternately, the process chamber can include a first subchamber to deposit the Ta.sub.2 O.sub.5 film, and a second subchamber to anneal the deposited Ta.sub.2 O.sub.5 film. Accordingly, the substrate is moved from the first subchamber to the second subchamber between the steps of depositing and annealing the Ta.sub.2 O.sub.5 film. Because each of the subchambers is located within the process chamber, the Ta.sub.2 O.sub.5 film is not exposed to air during this transition.
In the event that two subchambers are used within a single process chamber, the method for forming the Ta.sub.2 O.sub.5 film may include the steps of increasing the temperature of the substrate within the first subchamber S112 to the deposition temperature, depositing the Ta.sub.2 O.sub.5 film S113, and lowering the temperature of the substrate within the first subchamber S113 to a temperature appropriate for transferring the substrate to the second subchamber as shown in FIG. 3. The substrate is then transferred to the second subchamber S123, and the temperature of the substrate is raised to the annealing temperature in the second subchamber S125. The Ta.sub.2 O.sub.5 film is then annealed using ultraviolet light and ozone (O.sub.3) S115, and the temperature of the substrate is lowered within the second subchamber S116 to a temperature suitable for removing the substrate. Alternately, the Ta.sub.2 O.sub.5 film can be annealed using an oxygen plasma as discussed above.
A system for forming the Ta.sub.2 O.sub.5 film according to the method of the present invention is illustrated in FIGS. 4 and 5. The deposition of the Ta.sub.2 O.sub.5 film and the ultraviolet ozone annealing of the Ta.sub.2 O.sub.5 film (or alternately the oxygen plasma annealing of the Ta.sub.2 O.sub.5 film) can be sequentially performed in a single process chamber, thus enhancing the quality of the Ta.sub.2 O.sub.5 film and increasing the manufacturing throughput. The process chamber includes a light source 11 which emits ultraviolet light, a quartz window 12 which transmits the ultraviolet light and a predetermined gas such as oxygen, and a susceptor 14 on which the substrate 13 is placed. The ultraviolet light source 11 can alternately be replaced by a plasma generator when a plasma oxygen annealing step is used in place of the ultraviolet ozone annealing step. The process chamber also includes a lifter pin 15 which controls the height at which the substrate is held relative to the susceptor 14, and a heat source 16 which heats the susceptor 14 and/or the substrate 13. In addition, the substrate 13 rotates about the rotation shaft 17 thus enhancing the uniformity of the Ta.sub.2 O.sub.5 film deposited thereon.
An ozone (O.sub.3) injector and an RF generator can be provided in the process chamber so that the deposition of the Ta.sub.2 O.sub.5 film and the annealing thereof can both be performed in situ in the process chamber. Furthermore, the heat source 16 can generate the temperatures required to perform the deposition S113 and the anneal S115, as well as the temperature ramps S112, S114, and S116 shown in FIG. 2. In particular, the lifter pins 15 can be used to vary the height of the substrate 13 relative to the susceptor 14 and the heat source 16 thus controlling the temperature of the substrate.
When using a system having a process chamber including first and second subchambers, the step of depositing the Ta.sub.2 O.sub.5 film S13 can be performed in the first subchamber, and the step of annealing the Ta.sub.2 O.sub.5 film S15 can be performed in the second subchamber, as shown in FIG. 3. Accordingly, each subchamber can include a susceptor 14, a lifter pin 15, a heat source 16, and a quartz window 12. In addition, the first subchamber can include a rotation shaft 17 which enhances the deposition uniformity. The second subchamber can include a UW light source 11 and an ozone source, or an oxygen plasma generator for the annealing step. As discussed above, the first and second subchambers are provided in a single process chamber to prevent the substrate from being exposed to air during the transfer from the first subchamber to the second subchamber.
A method for forming a Ta.sub.2 O.sub.5 film according to the present invention will now be discussed with reference to FIGS. 2-5. Generally, a method for forming a capacitor including a Ta.sub.2 O.sub.5 dielectric film for a dynamic random access memory cell includes the steps of forming the lower electrode of the capacitor S1, cleaning the surface of a lower electrode S2, rapid thermal processing S3 resulting in nitridation, forming the Ta.sub.2 O.sub.5 film S4, annealing the Ta.sub.2 O.sub.5 film with ultraviolet light and ozone S5, and annealing with oxygen S6. The methods and systems of the present invention relate in particular to the steps of forming and annealing the Ta.sub.2 O.sub.5 film S4-S6.
The Ta.sub.2 O.sub.5 film is formed by providing a liquid source of Ta(OC.sub.2 H.sub.5).sub.5 and oxygen (O.sub.2) in the process chamber which is heated to a temperature in the range of 350-450.degree. C. Accordingly, a Ta.sub.2 O.sub.5 film is deposited on the substrate 13. When annealing the Ta.sub.2 O.sub.5 film using ultraviolet light and ozone, ozone is generated by an ozone generator and decomposed by ultraviolet light from the UV lamp 11 wherein the ultraviolet light has a wave length on the order of 254 nm and wherein the substrate is maintained at a temperature in the range of 250-350 degrees C. Accordingly, oxygen fills oxygen vacancies in the Ta.sub.2 O.sub.5 film. Alternately, the annealing step can be performed by forming an oxygen plasma.
Because the desired temperature for the deposition step (350-450 degrees C.) S13 and the desired temperature for the ultraviolet ozone annealing step (250-350.degree. C.) S15 are within the controllable temperature range of the heat source 16, the steps of depositing and annealing the Ta.sub.2 O.sub.5 film can be performed in a single process chamber. Accordingly, the UW lamp 11 and ozone source are installed in the same process chamber used to deposit the Ta.sub.2 O.sub.5 film.
More particularly, during the step of depositing the Ta.sub.2 O.sub.5 film, the UV lamp is not turned on and ozone is not injected. After the Ta.sub.2 O.sub.5 film has been deposited, however, the temperature of the susceptor 14 on which the substrate 13 is placed can be lowered by 5-10.degree. C., and then the UV lamp can be turned on and ozone injected thus performing the annealing step S15. Accordingly, the deposition and ultraviolet ozone annealing steps can be sequentially performed in a single process chamber without moving the substrate 13 between steps. Production throughput can thus be enhanced, and the problems of moisture adsorption and free carbon adsorption can be reduced.
FIG. 3 illustrates a time-temperature chart for a method of forming a Ta.sub.2 O.sub.5 film wherein the Ta.sub.2 O.sub.5 film is deposited in a first subchamber, and the deposited film is annealed in a second subchamber wherein the two subchambers are contained in a single process chamber. In other words, a Ta.sub.2 O.sub.5 film is deposited on the substrate in the first subchamber and then transferred to the second subchamber where the deposited film is annealed such as by ultraviolet ozone annealing. Because the substrate is not removed from the process chamber within which both of the subchambers are enclosed, the environment within the process chamber can be controlled to reduce the problems of adsorption of moisture and free carbon.
Furthermore, the temperature of each subchamber can be independently controlled. Accordingly, there is no need to change the temperature from the deposition temperature to the annealing temperature within either subchamber. Stated in other words, the temperature in the first subchamber can be set to the deposition temperature, and the temperature for the second subchamber can be set to the annealing temperature.
In FIGS. 4 and 5, the process chamber includes a ultraviolet lamp 11 or a plasma generator, and a quartz window 12. The quartz window transmits ultraviolet light to the substrate and also provides for the supply of oxygen O.sub.2. The substrate 13 is placed on the susceptor 14, and the susceptor 14 heats the substrate 13 to a predetermined temperature. The temperature of the substrate 13 can thus be maintained to provide a stable reaction when a reaction gas is provided in the process chamber. The susceptor 14 can be formed from transparent quartz; an opaque metal with a high thermal conductivity and a metal compound thereof; or a material coated with a ceramic.
The lifter pin 15 can be used when transferring or positioning the substrate 13. Because the height of the lifter pin 15 is controllable, the temperature of the substrate 13 can be controlled by controlling a distance between it and the susceptor 14. In other words, the temperature of the substrate can be controlled by controlling a distance between it and the susceptor. The heat source 16 heats one or both of the susceptor and the substrate. For example, a refractory coil or a heat lamp can be used to provide the heat source 16. The rotation shaft 17 rotates the substrate 13 thus enhancing the uniformity of the Ta.sub.2 O.sub.5 formed thereon.
When depositing the Ta.sub.2 O.sub.5 film, the substrate 13 is placed on the susceptor 14, and the substrate 13 is heated by the heat source 16 below the susceptor 14. The temperature of the heated substrate 13 can be controlled within a range on the order of 250-550.degree. C. When the substrate 13 reaches the desired deposition temperature (350-450 degrees C.), Ta(OC.sub.2 H.sub.5).sub.5 is injected into the process chamber from the side of the substrate 13, and oxygen (O.sub.2) is provided through the quartz window 12 from an oxygen source. Accordingly, a Ta.sub.2 O.sub.5 film is deposited on the substrate 13.
To reduce oxygen vacancies within the Ta.sub.2 O.sub.5 film, ozone (O.sub.3) is provided in the process chamber from an ozone source, as shown in FIG. 5. By providing the ozone and ultraviolet light from the UV lamp 11, while maintaining the substrate at a temperature (250-350 degrees C.) lower than the deposition temperature, oxygen vacancies in the Ta.sub.2 0.sub.5 film can be reduced. The lower temperature is preferred during the annealing step because when ozone is provided at the higher deposition temperature, the ozone may not be excited by the ultraviolet light, but may instead recombine to form stable oxygen (O.sub.2). The oxygen vacancies may thus not be sufficiently reduced at the higher deposition temperature. The substrate temperature is thus preferably maintained below 350.degree. C. during the annealing step.
In order to reduce the temperature of the substrate, the substrate 13 may be lifted from the susceptor 14 by a predetermined distance using lifter pins 15, as shown in FIG. 5. By increasing the distance between the substrate 13 and the susceptor 14, the heat transferred from the susceptor 14 and/or heat source 16 to the substrate 13 can be reduced thus reducing the temperature of the substrate 13. The temperature of the substrate can thus be lowered relatively quickly without transferring the substrate to a second susceptor. Once the substrate 13 has been suitably cooled, the ozone generated by the ozone generator can be provided from outside the process chamber through the quartz window 12 to perform the ultraviolet ozone annealing step.
As described above, the steps of depositing and annealing a Ta.sub.2 O.sub.5 film can be performed at different temperatures and for different times in a single process chamber thus eliminating the need to transfer the substrate. Alternately, the step of depositing the Ta.sub.2 O.sub.5 film can be performed in a first subchamber and the step of annealing the film can be performed in a second subchamber wherein the first and second subchambers are enclosed within a process chamber. Accordingly, the first subchamber includes a heat source, a susceptor, a rotating shaft, a quartz window, a source of oxygen, and a source of Ta(OC.sub.2 H.sub.5).sub.5. The second subchamber includes a heat source, a susceptor, a quartz window, a UV lamp (or a plasma generator), and an ozone source. With two subchambers, there is no need to provide both a deposition and an annealing temperature within either subchamber.
According to methods and systems of the present invention, the deposition and annealing of a dielectric film having a high dielectric constant can be performed in a process chamber. More particularly, the dielectric film can be deposited at a first temperature and annealed at a second temperature which is low relative to the first temperature without removing the substrate from the process chamber. Accordingly, unnecessary contact of the dielectric film with moisture and free carbon can be reduced thus simplifying the manufacturing process and increasing the quality of the dielectric film produced thereby.
In the drawings and specification, there have been disclosed typical preferred embodiments of the invention and, although specific terms are employed, they are used in a generic and descriptive sense only and not for purposes of limitation, the scope of the invention being set forth in the following claims.
Claims
Certificate of Correction present
The claims shown below may not include correction changes. Use the corrected PDF for authoritative text.
That which is claimed is:
1. A system for forming a dielectric on a microelectronic substrate, said system comprising: a process chamber which receives the substrate and isolates the substrate from an external atmosphere; means for depositing the dielectric film on the substrate in said processing chamber wherein the dielectric film comprises a material chosen from the group consisting of Ta.sub.2 O.sub.5, BaSrTiO.sub.3 (BST) and PbZrTiO.sub.3 (PZT); and means for annealing the dielectric film in said process chamber so that exposure to air is reduced during and between said deposition and said annealing.
2. A system according to claim 1 further comprising a heat source which heats the substrate to a first temperature when depositing the dielectric film and which heats the substrate to a second temperature when annealing the dielectric film.
3. A system according to claim 1 wherein said process chamber comprises: an ultraviolet lamp which generates ultraviolet light when annealing the dielectric film; a quartz window which transmits said ultraviolet light from said ultraviolet lamp and which transmits oxygen within said process chamber; a susceptor on which the substrate is placed in said process chamber; and lifting means for controlling a position of the substrate relative to said susceptor in said process chamber.
4. A system according to claim 1 further comprising: rotation means for rotating the substrate.
5. A system according to claim 1 further comprising an ozone (O.sub.3) source which injects ozone into said process chamber.
6. A system according to claim 1 further comprising a plasma generator which generates an oxygen (O.sub.2) plasma in said process chamber when annealing the dielectric film.
7. A system according to claim 2 wherein said first temperature is in the range of 350 to 450 degrees C., and wherein said second temperature is in the range of 250 to 350 degrees C.
8. A system according to claim 2 wherein said heat source comprises one of a resistive heater and a lamp.
9. A system according to claim 2 wherein said annealing means includes an ultraviolet lamp located in said process chamber adjacent said susceptor opposite said heat source.
10. A system for forming a dielectric on a microelectronic substrate, said system comprising: a process chamber which receives the substrate and isolates the substrate from an external atmosphere; means for depositing the dielectric film on the substrate in said process chamber; and means for annealing the dielectric film in said process chamber; wherein said process chamber comprises, an ultraviolet lamp which generates ultraviolet light when annealing the dielectric film, a quartz window which transmits said ultraviolet light from said ultraviolet lamp and which transmits oxygen within said process chamber, a susceptor on which the substrate is placed in said process chamber, and lifting means for controlling a position of the substrate relative to said susceptor in said process chamber: wherein said susceptor comprises a material chosen from the group consisting of quartz, a metal with a metal compound thereof, and a ceramic.
11. A system according to claim 10 wherein the dielectric film comprises Ta.sub.2 O.sub.5.
12. A system according to claim 10 wherein the dielectric film comprises a material chosen from the group consisting of BaSrTiO.sub.3 (BST) and PbZrTiO.sub.3 (PZT).
13. A system for forming a dielectric on a microelectronic substrate, said system comprising: a process chamber which receives the substrate and isolates the substrate from an external atmosphere wherein said process chamber comprises an ultraviolet lamp which generates ultraviolet light when annealing the dielectric film, a quartz window which transmits said ultraviolet light from said ultraviolet lamp and which transmits oxygen within said process chamber, a susceptor on which the substrate is placed in said process chamber, and lifting means for controlling a position of the substrate relative to said susceptor in said process chamber; means for depositing the dielectric film on the substrate in said process chamber; means for annealing the dielectric film in said process chamber; and a thermocouple which provides temperature feedback for said lifting means.
14. A system for forming a dielectric on a microelectronic substrate, said system comprising: a process chamber which receives the substrate and isolates the substrate from an external atmosphere wherein said process chamber comprises, an ultraviolet lamp which generates ultraviolet light when annealing the dielectric film, a quartz window which transmits said ultraviolet light from said ultraviolet lamp and which transmits oxygen within said process chamber, a susceptor on which the substrate is placed in said process chamber, and lifting means for controlling a position of the substrate relative to said susceptor in said process chamber wherein said lifting means includes height control means for controlling a height of the substrate relative to said susceptor to control a temperature of the substrate; means for depositing the dielectric film on the substrate in said process chamber; and means for annealing the dielectric film in said process chamber.
15. A system for forming a dielectric film on a microelectronic substrate, said system comprising: a process chamber which isolates an interior thereof from an external atmosphere; a first sub-chamber in said process chamber which receives the substrate and deposits the dielectric film on the substrate wherein the dielectric film comprises a material chosen from the group consisting of Ta.sub.2 O.sub.5, BaSrTiO.sub.3 (BST) and PbZrTiO.sub.3 (PZT); and a second sub-chamber in said process chamber which receives the substrate and anneals the dielectric film so that exposure to air is reduced during and between said deposition and annealing.
16. A system according to claim 15: wherein said first sub-chamber comprises a first susceptor on which the substrate is received, a first heat source which heats the substrate to a first temperature, and a first gas source which supplies a first reactant gas, to deposit the dielectric film; and wherein said second sub-chamber comprises an ultraviolet light generator which generates ultraviolet light, a second susceptor on which the substrate with the dielectric film is received, a quartz window which transmits said ultraviolet light, a second gas source which supplies a second reactant gas, and a second heat source which heats the substrate to a second temperature to anneal the dielectric film.
17. A system according to claim 16 wherein said first temperature is in the range of 350 to 450 degrees C., and said second temperature is in the range of 250 to 350 degrees C.
18. A system according to claim 15 wherein said first sub-chamber comprises a first heat source which heats the substrate to a first temperature when depositing the dielectric film; and wherein said second sub-chamber comprises a second heat source which heats the substrate to a second temperature when annealing the dielectric film.
19. A system according to claim 18 wherein said first temperature is in the range of 350 to 450 degrees C., and said second temperature is in the range of 250 to 350 degrees C.
20. A system for forming a dielectric film on a microelectronic substrate, said system comprising: a process chamber which isolates an interior thereof from an external atmosphere; a first sub-chamber in said process chamber which receives the substrate and deposits the dielectric film on the substrate; and a second sub-chamber in said process chamber which receives the substrate and anneals the dielectric film; wherein said first sub-chamber comprises a first susceptor on which the substrate is received, a first heat source which heats the substrate to a first temperature, and a first gas source which supplies a first reactant gas, to deposit the dielectric film; wherein said second sub-chamber comprises an ultraviolet light generator which generates ultraviolet light, a second susceptor on which the substrate with the dielectric film is received, a quartz window which transmits said ultraviolet light, a second gas source which supplies a second reactant gas, and a second heat source which heats the substrate to a second temperature to anneal the dielectric film; wherein said first heat source comprises first lifting means for controlling a position of the substrate relative to said first susceptor; and wherein said second heat source comprises second lifting means for controlling a position of the substrate relative to said second susceptor.
21. A system according to claim 20 wherein the dielectric film comprises Ta.sub.2 O.sub.5.
22. A system according to claim 20 wherein the dielectric film comprises a material chosen from the group consisting of BaSrTiO.sub.3 (BST) and PbZrTiO.sub.3.
23. A system for depositing and annealing a dielectric on a microelectronic substrate, said system comprising: a chamber including a susceptor therein which receives the substrate wherein said chamber isolates the substrate from an external atmosphere during the deposition and annealing of the dielectric on the substrate; a heater which heats the substrate on the susceptor to a first temperature during the deposition of the dielectric and which heats the substrate on the susceptor to a second temperature during the annealing of the dielectric; and a UV light source which provides UV light in said process chamber during the annealing.
24. A system according to claim 23 further comprising: lifting means for controlling a height of the substrate relative to said susceptor to control a temperature of the substrate.
25. A system according to claim 24 further comprising: a thermocouple which provides temperature feedback for said lifting means.
Patent Citations (3)
Non-Patent Literature (12)
- Caplus 1991:197622, 1991.
- Caplus 1994:258897, 1994.
- Caplus 1995:513462, 1995.
- Inspec 94:4702250, 1994.
- Inspec 94:4687689, 1994.
- Hiroshi Shinriki et al., UV-O.sub.3 and Dry-O.sub.2 : Two-Step Annealed Chemical Vapor-Deposited Ta.sub.2 O.sub.5 Films for Storage Dielectrics of 64-Mb DRAM's, IEEE Transactions On Electron Devices, vol. 38, No. 3, Mar. 1991, pp. 455-462.
- Shinriki et al., UV-Ozone And Dry-Oxygen: Two-Step Annealed Chemical Vapor-Deposited Tantalum Pentoxide Films For Storage Dielectrics Of 64-Mb DRAM's, (Abstract), IEEE Trans. Electron Devices (1991), vol. 38, No. 3, pp. 455-462.
- Ohji et al., Improvement In Stoichiometric Composition Of CVD-Ta205 Capacitor Dielectric Films For DRAM, (Abstract), Proc.-Electrochem. Soc. (1993), 93-25 (Interconnects, Contact Metallization, and Multilevel Metallization/Reliability for Semiconductor Devices, Interconnects, and Thin Insulator Materials), pp. 400-409.
- Maeda, Ozone Applied In Semiconductor Industry, (Abstract), VLSI, Kurin Tekunoroji (1995), 5, pp. 45-49.
- Fujino et al., Low-Temperature Atmospheric-Pressure Chemical Vapor Deposition Using 2,4,6,8-tetramethylcyclotetrasiloxane And Ozone, (Abstract), Japanese Journal of Applied Physics, Part 1: Regular Papers & Short Notes & Review Papers, vol. 33, No. 4A, Apr. 1994, pp. 2019-2024.
- Treichel et al., Deposition, Annealing, And Characterization Of Tantalum Pentoxide Films, (Abstract), Proceedings of the 3.sup.rd Biennial Meeting of Chemical Perspectives of Microelectronic Materials, Mater. Res. Soc, vol. 282, 1993, pp. 557-568.
- Ichinose et al., Preparation and Rapid Thermal Annealing Effect of (Ba, Sr)TiO.sub.3 Thin Films, Jpn. J. Appl. Phys., vol. 34, Pt. 1, No. 9B, 1995, pp. 5198-5201.