US 5,747,728 AGrant

Advanced Thermoelectric Materials With Enhanced Crystal Lattice Structure and Methods of Preparation

Issue Date:1998-05-05

•24 Claims

•7 Drawing Sheets

Abstract

New skutterudite phases including Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, RuSb.sub.2 Te, and FeSb.sub.2 Te, have been prepared having desirable thermoelectric properties. In addition, a novel thermoelectric device has been prepared using skutterudite phase Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3. The skutterudite-type crystal lattice structure of these semiconductor compounds and their enhanced thermoelectric properties results in semiconductor materials which may be used in the fabrication of thermoelectric elements to substantially improve the efficiency of the resulting thermoelectric device. Semiconductor materials having the desired skutterudite-type crystal lattice structure may be prepared in accordance with the present invention by using powder metallurgy techniques. Measurements of electrical and thermal transport properties of selected semiconductor materials prepared in accordance with the present invention, demonstrated high Hall mobilities and good Seebeck coefficients. These materials have low thermal conductivity and relatively low electrical resistivity, and are good candidates for low temperature thermoelectric applications.

Metadata

Assignee

California Institute of Technology

Inventors

Jean-Pierre Fleurial
Thierry F. Caillat
Alexander Borshchevsky

Application Information

Application Number:US 4127005

Filing Date:1995-03-29

Priority Date:1993-08-03

Art Unit:253

Classifications

IPC:

H01L 3518

Field of Search:

257136467;930236.1;239;240;203

Patent Drawings (7 sheets)

Description

Technical Field of the Invention

This invention relates to the design and preparation of semiconductor materials having enhanced thermoelectric properties.

Background of the Invention

The basic theory and operation of thermoelectric devices has been developed for many years. Modern thermoelectric cooling devices typically include an array of thermocouples which operate by using the Peltier effect. Thermoelectric devices are essentially small heat pumps which follow the laws of thermodynamics in the same manner as mechanical heat pumps, refrigerators, or any other apparatus used to transfer heat energy. The principal difference is that thermoelectric devices function with solid state electrical components (thermocouples) as compared to more traditional mechanical/fluid heating and cooling components. The efficiency of a thermoelectric device is generally limited to its associated Carnot cycle efficiency reduced by a factor which is dependent upon the thermoelectric figure of merit (ZT) of the materials used in fabrication of the thermoelectric device.

The thermoelectric figure of merit (ZT) is a dimensionless measure of the effectiveness of a thermoelectric device and is related to material properties by the following equation:

where S, .sigma., .kappa., and T are the Seebeck coefficient, electrical conductivity, thermal conductivity and absolute temperature, respectively. The Seebeck coefficient (S) is a measure of how readily the respective carriers (electrons or holes) can change energy in a temperature gradient as they move across a thermoelectric element. The thermoelectric figure of merit is related to the strength of interaction of charge carriers with the lattice structure and the available energy states associated with the respective materials.

The ZT may also be stated by the equation: ##EQU1##

Thermoelectric materials such as alloys of Bi.sub.2 Te.sub.3, PbTe and BiSb were developed thirty to forty years ago. More recently, semiconductor alloys such as SiGe have been used in the fabrication of thermoelectric devices. Commercially available thermoelectric materials are generally limited to use in a temperature range between 300.degree. K and 1300.degree. K with a maximum ZT value of approximately one. The efficiency of such thermoelectric devices remains relatively low at approximately five to eight percent (5-8%) energy conversion efficiency. For the temperature range of -100.degree. C. to 1000.degree. C., maximum ZT of current state of the art thermoelectric materials remains limited to values of approximately 1, except for Te-Ag-Ge-Sb alloys (TAGS) which may achieve a ZT of 1.2 to 1.4 in a very narrow temperature range. Recently developed materials such as Si.sub.80 Ge.sub.20 alloys used in thermoelectric generators to power spacecrafts for deep space missions have a thermoelectric figure of merit approximately equal to 0.5 from 300.degree. C. to 1,000.degree. C.

Summary of the Invention

In accordance with the present invention disadvantages and problems associated with the previous design and preparation of materials used in the manufacture of thermoelectric devices have been substantially reduced or eliminated. The present invention provides the ability to obtain increased efficiency from a thermoelectric device by using materials with a skutterudite-type crystal lattice structure and desired thermoelectric characteristics in fabrication of the thermoelectric device. Examples of semiconductor materials and compounds which are satisfactory for use with the present invention include, but are not limited to, IrSb.sub.3, RhSb.sub.3, CoSb.sub.3, Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, RuSb.sub.2 Te, FeSb.sub.2 Te and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 and alloys of these compounds.

In accordance with one aspect of the present invention, P-type semiconductor materials are formed from alloys of CoSb.sub.3, RhSb.sub.3 or IrSb.sub.3 for use in manufacturing thermoelectric devices with substantially enhanced operating characteristics and improved efficiency as compared to previous thermoelectric devices.

In accordance with another aspect of the present invention, P-type semiconductor materials are formed from skutterudite phases Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, RuSb.sub.2 Te, FeSb.sub.2 Te and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3. These skutterudite phases may also be used for manufacturing thermoelectric devices with substantially enhanced operating characteristics and improved efficiency as compared to previous thermoelectric devices.

In accordance with another aspect of the present invention, N-type semiconductor materials are formed from alloys of CoSb.sub.3, RhSb.sub.3 or IrSb.sub.3 for use in manufacturing thermoelectric devices with substantially enhanced operating characteristics and improved efficiency as compared to previous thermoelectric devices. In accordance with another aspect of the present invention, N-type semiconductor materials are formed from skutterudite phases Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, RuSb.sub.2 Te, FeSb.sub.2 Te and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3. These skutterudite phases may also be used for manufacturing thermoelectric devices with substantially enhanced operating characteristics and improved efficiency as compared to previous thermoelectric devices.

An important technical advantage of the present invention includes the use of gradient freezing techniques in the preparation of semiconductor materials such as IrSb.sub.3, RhSb.sub.3 and CoSb.sub.3. The use of gradient freeze techniques in accordance with the present invention produces a large, single crystal of semiconductor material having a skutterudite lattice structure. A Bridgman Two-Zone furnace and a sealed container have been modified for use in preparation of semiconductor materials in accordance with the present invention.

Another important technical advantage of the present invention includes the use of liquid-solid phase sintering techniques in the preparation of semiconductor materials such as IrSb.sub.3, RhSb.sub.3 and CoSb.sub.3. The use of liquid-solid phase sintering techniques in accordance with the present invention produces a large ingot of semiconductor material having a skutterudite lattice structure. An isothermal furnace and a sealed container have been modified for use in preparation of semiconductor materials in accordance with the present invention.

Another important technical advantage of the present invention includes the use of powder metallurgy techniques in the preparation of skutterudite phases Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, RuSb.sub.2 Te, FeSb.sub.2 Te and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3. The use of powder metallurgy techniques produces a polycrystalline semiconductor material having a skutterudite lattice structure.

Another aspect of the present invention includes manufacturing a thermoelectric device with P-type thermoelectric elements formed from materials such as Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, RuSb.sub.2 Te, FeSb.sub.2 Te, Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3, CoSb.sub.3, RhSb.sub.3 or IrSb.sub.3 and N-type thermoelectric elements formed from Si.sub.80 Ge.sub.20 or alloys of bismuth (Bi), arsenic (As), antimony (Sb), selenium (Se), and tellurium (Te), the salts of lead with chalcogens sulphur (S), tellurium (Te) and selenium (Se).

The present invention allows the manufacture of thermoelectric energy conversion devices such as electrical power generators, coolers, and thermocouples or temperature detectors with high ZT and associated increased efficiency. By the use of semiconductor phases such as Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, RuSb.sub.2 Te, FeSb.sub.2 Te, and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3, semiconductor compounds IrSb.sub.3, RhSb.sub.3 and CoSb.sub.3, and alloys of these compounds which have been prepared in accordance with the present invention, the overall efficiency of a thermoelectric device may be substantially enhanced.

A further important technical advantage includes the use of semiconductor materials prepared in accordance with the present invention in the manufacture of a radioisotope thermoelectric generator (RTG) to substantially enhance the associated system efficiency. Such thermoelectric devices may be used in space power systems. Other thermoelectric devices manufactured from semiconductor materials fabricated in accordance with the present invention may be used in waste heat recovery systems, automobiles, remote power generators and sensors and coolers for advanced electronic components such as field effect transistors.

Brief Description of the Drawings

For a more complete understanding of the present invention and its advantages, reference is now made to the following description taken in conjunction with the accompanying drawings in which:

FIG. 1 is an isometric drawing of a thermoelectric device which may be manufactured from materials incorporating the present invention;

FIG. 2 is an electrical schematic drawing of the thermoelectric device of FIG. 1;

FIG. 3 is an isometric representation of a skutterudite-type crystal lattice structure associated with semiconductor materials which have been fabricated in accordance with the present invention;

FIG. 4 is an iridium antimony phase diagram;

FIG. 5a is a schematic drawing in elevation and in section with portions broken away showing a Bridgman Two-Zone furnace which may be used to prepare semiconductor materials using gradient freeze techniques in accordance with the present invention;

FIG. 5b is a graph showing the temperature gradient associated with growing large, single crystals of semiconductor materials having a skutterudite lattice structure in accordance with the present invention;

FIG. 6 is a schematic drawing in elevation and in section with portions broken away showing an isothermal furnace which may be used in preparing ingots by liquid-solid phase sintering of semiconductor materials having a skutterudite lattice structure in accordance with the present invention;

FIG. 7 is a graph showing typical electrical resistivity as an inverse function of temperature associated with semiconductor materials prepared in accordance with the present invention;

FIG. 8 is a graph showing typical Hall mobility values as an inverse function of temperature associated with semiconductor materials prepared in accordance with the present invention;

FIG. 9 is a graph showing typical Seebeck coefficients as a function of temperature for semiconductor materials prepared in accordance with the present invention;

FIG. 10 is a graph showing thermal conductivity as a function of temperature for semiconductor materials prepared in accordance with the present invention as compared with presently available thermoelectric materials;

FIG. 11 is a graph showing the performance of a multiple stage thermoelectric cooler fabricated in part from semiconductor materials incorporating the present invention as compared to a multiple stage thermoelectric cooler fabricated from presently available semiconductor materials;

FIG. 12 is a graph showing typical electrical resistivity as an inverse function of temperature associated with semiconductor materials prepared in accordance with the present invention;

FIG. 13 is a graph showing typical Hall mobility values as an inverse function of temperature associated with semiconductor materials prepared in accordance with the present invention;

FIG. 14 is a graph showing typical Hall carrier concentrations as a function of temperature for semiconductor materials prepared in accordance with the present invention;

FIG. 15 is a graph showing typical Seebeck coefficients as a function of temperature for semiconductor materials prepared in accordance with the present invention;

FIG. 16 is a graph showing thermal conductivity as a function of temperature for semiconductor materials prepared in accordance with the present invention as compared with presently available thermoelectric materials;

FIG. 17 illustrates possible substitutions on the cation site to form ternary compounds from binary skutterudites;

FIG. 18 illustrates possible substitutes on the anion site to form ternary compounds from binary skutterudites; and

FIG. 19 illustrates substitutions that can be made on both the anion and cation sites to form ternary compounds from binary skutterudites.

Detailed Description of the Invention

The preferred embodiments of the present invention and its advantages are best understood by reference to FIGS. 1 through 19 of the drawings, like numerals being used for like corresponding parts of the various drawings.

Thermoelectric device 20, as shown in FIGS. 1 and 2, may be manufactured from semiconductor materials and compounds which have been prepared in accordance with the present invention. The use of such semiconductor materials will substantially increase energy conversion efficiency. Thermoelectric device 20, as shown, may be used as a heater and/or a cooler. Thermoelectric device 20 is preferably manufactured with a plurality of thermoelectric elements (sometimes referred to as "thermocouples") 22 disposed between cold plate 24 and hot plate 26. Electrical power connections 28 and 29 are provided to allow attaching thermoelectric device 20 to an appropriate source of DC electrical power. If thermoelectric device 20 were redesigned to function as an electrical power generator, electrical connections 28 and 29 would represent the output terminals from such a power generator operating between hot and cold temperature sources (not shown).

FIG. 2 is a schematic representation of electrical circuit 30 associated with thermoelectric device 20. Electrical circuit 30 is also typical of electrical circuits associated with using thermoelectric elements or thermocouples to convert heat energy into electrical energy. Such electrical power generators may be used in waste heat recovery systems (not shown), space power systems (not shown) and radioisotope power generators (not shown).

Electrical circuit 30, which is typical for a single stage thermoelectric device such as thermoelectric device 20, generally includes two dissimilar materials such as N-type thermoelectric elements 22a and P-type thermoelectric elements 22b. Thermoelectric elements 22 are typically arranged in an alternating N-type element to P-type element configuration. In many thermoelectric devices, semiconductor materials with dissimilar characteristics are connected electrically in series and thermally in parallel.

N-type semiconductor materials have more electrons than necessary to complete a perfect molecular lattice structure. P-type semiconductor materials have fewer electrons than necessary to complete a lattice structure. The "missing electrons" are sometimes referred to as "holes." The extra electrons in the N-type semiconductor material and the holes in the P-type semiconductor material (hereinafter referred to as "carriers") are the agents, coupled with lattice vibrations (referred to as "phonons"), which transport or move heat energy between cold side or cold plate 24 and hot side or hot plate 26 of thermoelectric elements 22. Ceramic materials are frequently used in the manufacture of plates 24 and 26 which define in part the cold side and hot side, respectively, of thermoelectric device 22.

In thermoelectric device 20, alternating thermoelectric elements 22 of N-type and P-type semiconductor materials have their ends connected in a serpentine fashion by electrical conductors such as 32, 34 and 36. Conductors 32, 34 and 36 are typically metallizations formed on the interior surfaces of plates 24 and 26. Commercially available thermoelectric coolers may include two metallized ceramic plates with P-type and N-type elements of bismuth telluride alloys soldered between the ceramic plates.

When DC electrical power from power supply 38 is applied to thermoelectric device 20 having an array of thermoelectric elements 22, heat energy is absorbed on cold side 24 of thermoelectric elements 22. The heat energy passes through thermoelectric elements 22 and is dissipated on hot side 26. A heat sink (sometimes referred to as the "hot sink", not shown) may be attached to hot plate 26 of thermoelectric device 20 to aid in dissipating heat from thermoelectric elements 22 to the adjacent environment. In a similar manner a heat sink (sometimes referred to as a "cold sink", not shown) may be attached to cold side 24 of thermoelectric device 20 to aid in removing heat from the adjacent environment. Thermoelectric device 20 may sometimes be referred to as a thermoelectric cooler. However, since thermoelectric devices are a type of heat pump, thermoelectric device 20 may function as either a cooler, heater, or power generator.

Semiconductor materials (sometimes referred to as "semiconductor compounds") CoSb.sub.3, RhSb.sub.3 and IrSb.sub.3 have been prepared in accordance with the present invention in the form of a large, single or poly crystal with a skutterudite lattice structure 40 as shown in FIG. 3. Additionally, polycrystalline phases having the skutterudite crystal lattice 40 shown in FIG. 3 such as Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, RuSb.sub.2 Te, FeSb.sub.2 Te and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 have also been prepared. As will be explained later in more detail, such semiconductor materials are preferably prepared in an antimony rich environment.

The skutterudite crystal lattice structure is defined in part by a unit cell with eight members having the formula AB.sub.3. More generally, the skutterudite crystal lattice structure is defined by thirty-two atomic crystallographic sites where eight positions may be occupied by metals and twenty-four positions may be occupied by nonmetals. The unit cell dimension for skutterudites ranges from 7.7 to 9.4. Angstroms. Skutterudite phase Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 has a lattice constant that has been experimentally measured at 9.2944 Angstroms while phase Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 has a lattice constant that has been experimentally measured at 9.1001 Angstroms. Alloys having the formula Co.sub.1-x-y Rh.sub.x Ir.sub.y Sb.sub.3, where 0.ltoreq.x.ltoreq.1 and 0.ltoreq.y.ltoreq.1 have also been prepared using the present invention.

Skutterudite-type crystal lattice structure 40 includes a cubic lattice of metal atoms 42. Metal atoms 42 are preferably selected from the group consisting of ruthenium, palladium, iron, nickel, cobalt, iridium, and/or rhodium. A four-member planary ring 44 of non-metal atoms 46 is disposed within the cubic lattice structure. Planary rings 44 preferably include four atoms of antimony. Each metal atom 42 has six neighbor atoms 42. Non-metal atoms 46 have two adjacent non-metal atoms 46 and two metal atoms 42. The covalent bonding associated with skutterudite-type crystal lattice structure 40 provides high hole mobility and low thermal conductivity.

Semiconductor materials having skutterudite-type crystal lattice structure 40 may be doped with selected impurities to produce N-type thermoelectric elements 22a and P-type thermoelectric elements 22b. For example, adding platinum (Pt) as a doping agent with IrSb.sub.3 semiconductor material produced N-type thermoelectric elements. If desired, thermoelectric device 20 may be manufactured with N-type thermoelectric elements 22b fabricated from IrSb.sub.3 and N-type thermoelectric elements 22a fabricated from previously available semiconductor materials such as alloys of Bi, As, Sb, Te, salts of lead with chalcogen elements, sulphur, tellurium and selenium.

Skutterudite phases Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, RuSb.sub.2 Te, FeSb.sub.2 Te and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 may also be doped with selected elements to produce N-type thermoelectric elements 22a and P-type thermoelectric elements 22b. These phases may be doped with selected elements such as silicon or germanium to produce P-type thermoelectric elements 22b. In addition, the skutterudite phase Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 may be made into an N-type thermoelectric element 22a by substituting some amount of Fe for Ru and/or some amount of Ni or Pt for Pd. The carrier concentration of Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 can also be adjusted by using excess Ru and a deficit of Pd. Similarly, the skutterudite phase Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 may be made into an N-type thermoelectric element 22a by substituting some amount of Ru for Fe and/or some amount of Pd or Pt for Ni. The carrier concentration of Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 can also be adjusted by using excess Fe and a deficit of Ni. Similar substitutions can be made in other skutterudite phases. If desired, thermoelectric device 20 may be manufactured with P-type thermoelectric elements 22b fabricated from Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, RuSb.sub.2 Te, FeSb.sub.2 Te, or Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 and N-type thermoelectric elements 22a fabricated from previously available semiconductor materials such as alloys of Bi, As, Sb, Te, salts of lead with chalcogen elements, sulfur, tellurium, and selenium.

Other ternary compounds can be formed such as CoGe.sub.1.5 Se.sub.1.5 and CoGe.sub.1.5 S.sub.1.5. Such ternary compounds can be formed by simultaneous substitution of the transition metal (T) atom or pnicogen (Pn) atom in a binary skutterudite (TPn.sub.3) by elements on the left and on the right of these atoms in the periodic table of the elements. This substitution results in an isoelectronic phase.

FIGS. 17-19 summarize several possible substitutions to form ternary compounds from binary skutterudites. For example, as illustrated in FIG. 17, for substitutions on the cation site, a ternary compound can be formed of the formula T'.sub.0.5 T".sub.0.5 Pn.sub.3 where T'.sub.0.5 may be selected from the group consisting of Fe, Ru, and Os. T".sub.0.5 may be selected from the group consisting of Ni, Pd, and Pt. Pn may be selected from the group consisting of P, As and Sb. Known skutterudite phases formed by such substitutions include Fe.sub.0.5 Ni.sub.0.5 As.sub.3. The thermoelectric properties of this phase were previously unknown. Newly discovered skutterudite phases formed by such substitutions and prepared using powder metallury techniques include Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3, Fe.sub.0.5 Pd.sub.0.5 Sb.sub.3, Fe.sub.0.5 Pt.sub.0.5 Sb.sub.3, Ru.sub.0.5 Ni.sub.0.5 Sb.sub.3, Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, and Ru.sub.0.5 Pt.sub.0.5 Sb.sub.3.

Alternatively, as illustrated in FIG. 18, substitutions may also be made on the anion site to form a ternary compound having the formula TA.sub.1.5 B.sub.1.5. T may be selected from the group consisting of Co, Rh and Ir; A may be selected from the group consisting of Si, Ge, Sn and Pb. B may be selected from the group consisting of S, Se, and Te. Known skutterudite phases formed by such substitutions include CoGe.sub.1.5 S.sub.1.5, CoGe.sub.1.5 Se.sub.1.5, RhGe.sub.1.5 S.sub.1.5, IrGe.sub.1.5 S.sub.1.5, IrGe.sub.1.5 Se.sub.1.5, and IrSn.sub.1.5 S.sub.1.5. The thermoelectric properties of these phases were previously unknown. Newly discovered skutterudite phases formed by such substitutions and prepared using powder metallurgy techniques include CoSn.sub.1.5 Te.sub.1.5 and IrSn.sub.1.5 Te.sub.1.5.

Finally, other substitutions may be made as illustrated in FIG. 19. The compounds RuSb.sub.2 Te and PtSnSb.sub.2 contain substitutions on both a cation site and an anion site. Thus, skutterudite phases can be formed by substituting atoms at the cation site, anion site, or both, so long as the valence electron count remains constant. Known skutterudite phases formed by such substitutions include PtSn.sub.1.2 Sb.sub.1.8. The thermoelectric properties of this phase were previously unknown. Newly discovered skutterudite phases formed by such substitutions and prepared using powder metallurgy techniques include FeSb.sub.2 Se, FeSb.sub.2 Te, RuSb.sub.2 Se, and RuSb.sub.2 Te. These phases as well as those phases discussed in connection with FIGS. 17 and 18 may all be used as semiconductors for thermoelectric devices.

Large, single crystals of semiconductor materials have been prepared in accordance with the present invention using both gradient freeze techniques and liquid-solid phase sintering techniques. The phase diagram for iridium-antimony, as shown in FIG. 4, demonstrates that growth of the desired skutterudite-type crystal lattice structure is very difficult. Such crystal growth is preferably initiated from a narrow range of compositions. In addition, the liquid crystal curve in the region forming IrSb.sub.3 is relatively sharp which further increases the difficulty of separating liquid and solid phases during crystallization.

Depending upon the type of semiconductor material and the relationship of cobalt, rhodium and iridium, either gradient freeze techniques or liquid-solid phase sintering techniques may be used to produce the desired skutterudite-type crystal lattice structure. For some semiconductor materials such as CoSb.sub.3 and RhSb.sub.3, gradient freeze techniques have produced the desired large, single crystal. For other semiconductor materials such as single phase IrSb.sub.3, liquid-solid phase sintering techniques have produced the desired large, single crystals.

Large, single crystals of semiconductor materials with the desired skutterudite lattice structure 40 may be grown by using gradient freeze techniques and furnace 50 as shown in FIG. 5a. Furnace 50 is frequently referred to as a Bridgman Two-Zone furnace. Furnace 50 includes housing 52 with a first or upper heater assembly 54 and a second or lower heater assembly 56. Housing 52 defines in part chamber 60. Thermal baffle 58 is preferably disposed between first heater assembly 54 and second heater assembly 56 intermediate chamber 60. Various components which comprise furnace 50 are preferably disposed vertically within chamber 60 of housing 52.

As shown in FIG. 5a, housing 52 includes end closure 62 which seals the upper portion of chamber 60 and end closure 64 which seals the lower portion of chamber 60. Quartz rod 66 may be vertically disposed within chamber 60. Container 68 is preferably secured to one end of rod 66 adjacent to thermal baffle 58.

The lower portion 70 of container 68 is preferably pointed or tapered with respect to rod 66. Various types of containers 68 may be satisfactorily used with the present invention. A sealed quartz crystal or quartz ampoule has been found satisfactory for use with furnace 50. If desired, housing 52 and end closure 64 may be modified to allow a conveyor (not shown) with a plurality of rods 66 and containers 68 to be passed sequentially through furnace 50.

Elements such as Co, Rh and Sb powders which will be formed into the desired semiconductor material using furnace 50 are preferably sealed within container 68 under a vacuum. Pointed or tapered end 70 of container 68 is attached to quartz rod 66 and disposed vertically within chamber 60. Tapered end 70 and its attachment to rod 66 cooperate to maintain the desired temperature gradients in container 68. Furnace 50 is then heated to establish the temperature gradients 68 and 67 as shown in FIG. 5b. Various temperature gradients may be used depending upon the elements placed within container 68 to produce the desired semiconductor material.

Samples of CoSb.sub.3 and RhSb.sub.3 were directionally crystallized from non-stoichiometric melts 72 rich in antimony. Crystals of CoSb.sub.3 and RhSb.sub.3 were grown with an axial temperature gradient of about 50.degree. C./cm and a growth rate about 1 mm/day. The crystals of CoSb.sub.3 and RhSb.sub.3 were approximately 10 mm long and 6 mm in diameter. The average density of the CoSb.sub.3 crystals was measured and found to be 99.7% of the theoretical density (7.69 g/cm.sup.3). The average density of the RhSb.sub.3 crystals was measured and found to be 99.5% of the theoretical density (7.69 g/cm.sup.3). Crystals of the Ir.sub.x Co.sub.1-x Sb.sub.3 solid solutions were also successfully grown by the gradient freeze technique from antimony-rich melts in furnace 50.

Large ingots of semiconductor materials with a skutterudite lattice structure may also be prepared by using liquid-solid phase sintering techniques and furnace 80 as shown in FIG. 6. Furnace 80 may be referred to as an isothermal furnace as compared to furnace 50 which has two different temperature zones. Furnace 80 includes housing 82 with heater assembly 84 disposed therein. Housing 82 defines in part chamber 90. Various components which comprise furnace 80 are preferably vertically disposed within chamber 90 of housing 82.

As shown in FIG. 6, housing 82 includes end closure 92 which seals the upper portion of chamber 90 and end closure 94 which seals the lower portion of chamber 90. Quartz rod 66 is preferably disposed vertically within chamber 90. Container 68 is preferably secured within chamber 90 intermediate end closures 94 and 92 at approximately the mid point of chamber 90.

The elements such as Ir, Rh, Co and Sb which will be used to form the desired semiconductor material may be sealed within container 68. The lower portion 70 of container 68 is preferably pointed or tapered with respect to quartz rod 66. The relationship of tapered end 70 with quartz rod 66 cooperate to maintain the desired temperature gradient in container 68 during growth of the skutterudite-type crystal structure 40. Various types of containers 68 may be satisfactorily used with the present invention. A sealed quartz ampoule has been found satisfactory for use with the present invention. As previously noted for furnace 50, housing 82 and end closure 94 may be modified to allow a conveyor (not shown) to pass a plurality of rods 66 and containers 68 sequentially through furnace 80.

Liquid-solid phase sintering techniques have been used to prepare large, single crystals of semiconductor material IrSb.sub.3 and also some alloys of (Ir.sub.1-x-y Rh.sub.x Co.sub.y) Sb.sub.3 solid solutions using furnace 80 and container 68. The samples produced had good semiconducting properties including exceptional P-type Hall mobilities as high as 7725 cm.sup.2.V.sup.-1.s.sup.-1 at room temperature. The crystals were approximately 10 mm long and 6 mm in diameter.

The liquid-solid phase sintering technique used to produce IrSb.sub.3 and (Ir.sub.1-x-y Rh.sub.x Co.sub.y)Sb.sub.3 solid solutions included placing a first layer 98 of elemental iridium, cobalt and/or rhodium powders together with a second layer 100 of antimony shots in a container sealed under vacuum. In the case of the preparation of a solid solution (Ir.sub.1-x-y Rh.sub.x Co.sub.y)Sb.sub.3, the powders of iridium, cobalt and rhodium in the desired amount were loaded in plastic vials, mixed and shaken in a mixer mill for about thirty minutes. The container 68 with material layers 98 and 100 was then held vertical and heated in furnace 80 as illustrated in FIG. 6. Several different reaction times and temperatures were tried. For some mixtures, the best results were obtained with a reaction time of 24 hours at a temperature of 1000.degree. C. Under these conditions, the resulting crystals were the most dense.

Transport properties measurements performed on samples of CoSb.sub.3, RhSb.sub.3 and (Ir.sub.1-x-y Rh.sub.x Co.sub.y)Sb.sub.3 prepared using the previously described procedures and apparatus demonstrated excellent semiconducting and thermoelectric properties. For example, the compounds with skutterudite crystallographic structure 40 had exceptional high P-type Hall mobilities. Room temperature values as high as 7725 cm.sup.2.v.sup.-1.s.sup.-1 were measured on a RhSb.sub.3 sample at a doping level of 2.4 10.sup.18 cm.sup.-3. Although linked to the particular crystal structure of this compound, this high value is also a result of the good quality of the sample. For example, lower mobilities were measured on hot-pressed RhSb.sub.3 samples such as a maximum value of 1500 cm.sup.2.V.sup.-1.s.sup.-1. Mobility as high as 1732 cm.sup.2.V.sup.-1.s.sup.-1 were measured on P-type CoSb.sub.3 single crystals compared to a maximum value of 290 cm.sup.2.V.sup.-1.s.sup.-1 for samples prepared by other procedures. IrSb.sub.3 samples also possessed high P-type Hall mobilities as high as 1241 cm.sup.2.V.sup.-1.s.sup.-1 at a doping level of 7.2 10.sup.18 cm.sup.-3.

Semiconductor compounds and related solid solutions have also been prepared by sintering elemental powders of iridium, cobalt, rhodium and antimony in various ratios. Completion of the reaction was achieved in times as short at six hours at a temperature of 600.degree. C. These powders have been successfully hot-pressed under specific conditions into large ingots (not shown).

Powders of IrSb.sub.3 compound and several compositions of the (Ir.sub.1-x-y Rh.sub.x Co.sub.y)Sb.sub.3 solid solutions were also prepared in relatively short times (as low as six hours) by hot press sintering elemental powders or iridium, cobalt, antimony and rhodium. Several different mixtures of elemental powders were successfully hot-pressed in a graphite die (not shown) into dense ingots about 15 mm long and 6 mm in diameter. The resulting compounds demonstrated desirable thermoelectric properties.

Doping of the elemental powders can be achieved by introducing the desired amount of dopant in the initial powder load. By using commercially available hot presses and graphite die containers, this process is quick, cost effective and may be easily adapted to industrial manufacturing of large quantities of (Ir.sub.1-x-y Rh.sub.x Co.sub.y)Sb.sub.3 samples of different compositions and doping level.

Ternary skutterudite-type phases can be obtained by simultaneous substitution of the transition-metal or pnicogen atom in a binary skutterudite by elements on the left and on the right of this atom in the periodic table. The result is an isoelectronic phase. For example, the ternary phases CoGe.sub.1.5 Se.sub.1.5 and CoGe.sub.1.5 S.sub.1.5 can be derived from the binary compound CoAs.sub.3. The existence of a compound Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 formed by the substitution of the Co atom by Fe and Ni in the compounds CoSb.sub.3 has also been reported but thermoelectric properties of this phase were previously unknown.

Skutterudite phases Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 may be prepared with powder metallurgy techniques using a single zone isothermal furnace. For example, single phase, polycrystalline samples of Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 can be prepared by direct combination of the elements. Ruthenium (99.997%), palladium (99.9%) and antimony (99.9999%) powders are mixed in stoichiometric ratio in a plastic vial before being loaded and sealed in a quartz ampoule under vacuum. The ampoule is then heated for eight days at 600.degree. C. Next, the product is removed from the ampoule and crushed in an agate mortar. The mixture is then reloaded in a second quartz ampoule, and heated for four days at 550.degree. C. The skutterudite phase Feo.sub.0.5 Ni.sub.0.5 Sb.sub.3 may be prepared similarly. Iron (99.999%), nickel (99.996%) and antimony (99.9999%) powders are mixed in stoichiometric ratio in a plastic vial and then loaded in a quartz ampoule under vacuum. The ampoule is then heated for four days at 750.degree. C., the mixture is crushed and then made subject to a second annealing for four days at 550.degree. C.

After synthesis of these powders, high density samples can be prepared by hot pressing. Powders of the skutterudite phases Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 can be hot pressed into cylinders approximately 6 mm in diameter and 6 mm long. Hot pressing may be conducted, for example, at a pressure of about 20,000 psi and a temperature of 500.degree. C. for two hours.

Other skutterudite phases may also be prepared similarly using powder metallurgy techniques. Examples of newly discovered phases that may be prepared in this manner include RuSb.sub.2 Te, FeSb.sub.2 Te, RuSb.sub.2 Se, FeSb.sub.2 Se, Ru.sub.0.5 Pt.sub.0.5 Sb.sub.3, Ru.sub.0.5 Ni.sub.0.5 Sb.sub.3, Fe.sub.0.5 Pt.sub.0.5 Sb.sub.3, Fe.sub.0.5 Pd.sub.0.5 Sb.sub.3, IrSn.sub.1.5 Te.sub.1.5 and CoSn.sub.1.5 Te.sub.1.5.

Semiconductor compounds of CoSb.sub.3, RhSb.sub.3 and IrSb.sub.3 with skutterudite-type crystal lattice structure prepared in accordance with the present invention have demonstrated the characteristics shown in the following Table I.

Semiconductor compounds of Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 with skutterudite-type crystal lattice structures prepared in accordance with the present invention have demonstrated the characteristics shown in the following Table II.

Semiconductor compounds of RuSb.sub.2 Te and FeSb.sub.2 Te with skutterudite type crystal lattice structures prepared in accordance with the present invention have demonstrated the characteristics shown in the following Table III.

FIG. 7 is a graphical representation of typical electrical resistivity values as a function of inverse temperature for semiconductor compounds CoSb.sub.3, RhSb.sub.3 and IrSb.sub.3 having skutterudite-type crystal lattice structure 40. FIG. 8 is a graphical representation of typical Hall mobility values as a function of inverse temperatures for semiconductor compounds CoSb.sub.3, RhSb.sub.3 and IrSb.sub.3 having skutterudite-type crystal lattice structure 40. FIG. 9 is a graphic representation of typical Seebeck coefficient values as a function of temperature for semiconductor compounds CoSb.sub.3 and IrSb.sub.3 having skutterudite-type crystal lattice structure 40.

FIG. 10 comparisons of thermal conductivity as a function of temperature for semiconductor materials IrSb.sub.3 and Ir.sub.0.75 Co.sub.0.25 Sb.sub.3 prepared in accordance with the present invention as compared with previously available thermoelectric materials SiGe alloys and PbTe alloys. Curves 110 and 112 show thermal conductivity measured for semiconductor materials SiGe and PbTe respectively. Curves 114 and 116 are based on thermal conductivity measurements for semiconductor materials IrSb.sub.3 and Ir.sub.0.75 Co.sub.0.25 Sb.sub.3 respectively.

A multiple stage thermoelectric cooler (not shown) is typically fabricated by vertically stacking two or more single stage thermoelectric devices 20. Each ascending thermoelectric device will have fewer thermoelectric elements or thermocouples 22. A multiple stage thermoelectric cooler is therefore typically pyramid shaped because the lower stage requires more thermoelectric elements to transfer the heat dissipated from the upper stage in addition to the heat pumped from the object being cooled by the multiple stage thermoelectric cooler. Field effect transistors are often cooled from 300.degree. C. to 125.degree. C. by using such multiple stage thermoelectric coolers.

P-type semiconductor material IrSb.sub.3 prepared in accordance with the present invention may be used to provide a portion of thermoelectric elements 22. Currently available N-type semiconductor materials Bi.sub.2 Te.sub.3 may be used to provide another portion of thermoelectric elements 22. The resulting combination substantially enhances the performance of thermoelectric device 20. This combination of P-type and N-type semiconductor materials is particularly useful in the 100.degree. C. to 400.degree. C. temperature range. FIG. 11 is a graphical representation showing the increase in multiple stage thermoelectric cooler performance resulting from the use of P-type semiconductor materials IrSb.sub.3. FIG. 11 shows the coefficient of performance (COP.sub.MAX) as a function of the number of stages in each thermoelectric cooler.

FIG. 12 is a graphical representation of typical electrical resistivity values as a function of inverse temperature for two samples of skutterudite phase Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 prepared in accordance with the invention and one sample of Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3. These phases have the skutterudite-type crystal lattice structure 40.

FIG. 13 is a graphical representation of typical Hall mobility functions as a measure of inverse temperature for phases Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 having skutterudite-type crystal lattice structure 40.

FIG. 14 is a graphical representation of typical Hall carrier concentration values as a function of inverse temperature for phases Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3 having skutterudite-type crystal lattice structure 40. The electrical properties show that these phases are heavily doped semiconductors. For example, for sample 3RPS4 of phase Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 as illustrated in FIG. 12, the electrical resistivity increases with temperature up to about 560.degree. C. and then decreases with an activation energy of 0.25 Ev. Relatively high Hall mobilities were achieved in phases produced in accordance with the teachings of the present invention in spite of the high Hall carrier concentration measured for the samples. The skutterudite structure favors large Hall carrier mobility. These two phases have a more complex structure and significantly lower decomposition temperature than many other skutterudites such as CoSb.sub.3, RhSb.sub.3 and IrSb.sub.3 and their thermal conductivity is substantially lower.

FIG. 15 is a graphical representation of typical Seebeck coefficient values as a function of temperature for skutterudite phases Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 and Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3. FIG. 16 compares thermal conductivity as a function of temperature for skutterudite phase Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 and semiconductor material IrSb.sub.3 with a previously available thermoelectric material Bi.sub.2 Te.sub.3. A room temperature value of 8.times.10.sup.-3 W.cm.sup.-1.K.sup.-1 was measured at room temperature for Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, ten times lower than typical P-type IrSb.sub.3 which has the same crystal structure but higher melting point and bandgap.

For comparison, typical thermal conductivity values of P-type Bi.sub.2 Te.sub.3 -based alloys were also plotted in FIG. 16. Lower thermal conductivity values are observed for the phase Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 over the entire range of temperature. As temperature falls, the thermal conductivity of P-type Bi.sub.2 Te.sub.3 -based alloys varies as 1/T. For Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, the thermal conductivity decreases as for a glassy material. Most of the crystalline materials where low thermal conductivity is observed do not have good electrical conductivity. Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3 is a unique material where low thermal conductivity and good electrical resistivity are combined, making this material an excellent candidate for low temperature thermoelectric applications. This phase may, therefore, be useful in the low temperature range (-200.degree., 225.degree. C.).

Although the present invention has been described in detail, it should be understood that various changes, substitutions and alterations can be made herein without departing from the spirit and the scope of the invention as defined in the following claims.

Claims

What is claimed is:

1. A thermoelectric devices comprising: a first material comprising a skutterudite-type crystal lattice structure having thirty-two atomic crystallographic sites including eight metal atom sites and twenty-four non-metal atom sites, the first material further comprising a first amount of a first type of dopant; and a second material electrically connected to the first material and comprising a second amount of a second type of dopant.

2. The thermoelectric device of claim 1 wherein four of said metal atom sites are occupied by Ruthenium.

3. The thermoelectric device as defined in claim 1 wherein four of said metal atom sites are occupied by palladium.

4. The thermoelectric device as defined in claim 1 wherein said twenty-four non-metal atom sites are occupied by antimony.

5. The thermoelectric device as defined in claim 1 wherein the first material further comprises a semiconductor compound having the formula:

6. The thermoelectric device as defined in claim 1 wherein the first material further comprises a semiconductor compound having the formula: 7.

7. The thermoelectric device as defined in claim 1 wherein the first material further comprises a semiconductor compound having the formula:

8. The thermoelectric device as defined in claim 1 wherein the first material further comprises a semiconductor compound having the formula:

9. The thermoelectric device as defined in claim 1 wherein the first material further comprises a semiconductor compound having the formula:

10. The thermoelectric device as defined in claim 1 wherein the first material further comprises a semiconductor compound having the formula: 11.

11. The thermoelectric device as defined in claim 1 wherein the first material further comprises a semiconductor compound having the formula:

12. The thermoelectric device as defined in claim 1 wherein the first material further comprises a semiconductor compound having the formula:

13. The thermoelectric device as defined in claim 1 wherein the first material further comprises a semiconductor compound having the formula: 14.

14. The thermoelectric device as defined in claim 1 wherein the second material comprises a material selected from the group consisting of alloys of Bi, As, Sb, Te, salts of lead with chalcogen elements, sulphur, tellurium and selenium.

15. The thermoelectric device of claim 1, wherein the first type of dopant comprises a p-type dopant.

16. The thermoelectric device of claim 1, wherein the first type of dopant comprises an n-type dopant.

17. The thermoelectric device of claim 1, wherein the second type of dopant comprises a p-type dopant.

18. The thermoelectric device of claim 1, wherein the second type of dopant comprises an n-type dopant.

19. The thermoelectric device of claim 1, wherein the second material comprises a skutterudite-type crystal lattice structure having thirty-two atomic crystallographic sites including eight metal atom sites and twenty-four non-metal atom sites.

20. The thermoelectric device of claim 1, wherein the first material further comprises a semiconductor compound selected from the group consisting of Ru.sub.0.5 Pd.sub.0.5 Sb.sub.3, Fe.sub.0.5 Ni.sub.0.5 Sb.sub.3, RuSb.sub.2 Te, CoSn.sub.1.5 Te.sub.1.5, PtSnSb.sub.2, FeSb.sub.2 Se, FeSb.sub.2 Te, RuSb.sub.2 Se, RuSb.sub.2 Te, Co.sub.1-x-y Rh.sub.x Ir.sub.y Sb.sub.3, IrSn.sub.1.5 Te.sub.1.5, Fe.sub.0.5 Pd.sub.0.5, Sb.sub.3,Fe.sub.0.5 Pt.sub.0.5 Sb.sub.3, Ru.sub.0.5 Ni.sub.0.5 Sb.sub.3, and Ru.sub.0.5 Pt.sub.0.5 Sb.sub.3.

21. The thermoelectric device of claim 1, wherein the first material further comprises a semiconductor compound selected from the group consisting of CoSb.sub.3, RhSb.sub.3, and IrSb.sub.3.

22. A thermoelectric device comprising a first material having the formula:

23. The thermoelectric device as defined in claim 22 wherein the first material further comprises a skutterudite-type crystal lattice structure.

24. The thermoelectric device as defined in claim 22 further comprising a second material selected from the group consisting of alloys of Bi, As, Sb, Te, salts of lead with chalcogen elements, sulphur, tellurium and selenium.

Patent Citations (40)

Patent	Date	Inventor
US2588254	1952-03-01	Lark-Horowitz et al.
US2798989	1957-07-01	Welker
US3124936	1964-03-01	Melehy
US3259759	1966-07-01	Giaever
US3296033	1967-01-01	Scuro et al.
US3338753	1967-08-01	Horsting
US3342567	1967-09-01	Dingwall
US3356464	1967-12-01	Hulliger
US3626583	1971-12-01	Abbott et al.
US3674568	1972-07-01	Caprarola
US3721583	1973-03-01	Blakeslee
US3873370	1975-03-01	Hampl, Jr. et al.
US4029520	1977-06-01	Hampl, Jr.
US4088515	1978-05-01	Bladeslee et al.
US4261771	1981-04-01	Dingle et al.
US4368416	1983-01-01	James
US4457897	1984-07-01	Stanley et al.
US4469977	1984-09-01	Quinn et al.
US4620897	1986-11-01	Nakajima
US4644753	1987-02-01	Burke
US4664960	1987-05-01	Ovshinsky
US4786335	1988-11-01	Knowles et al.
US4847666	1989-07-01	Heremans et al.
US4855810	1989-08-01	Gelb et al.
US4869971	1989-09-01	Nee et al.
US4999082	1991-03-01	Kremer et al.
US5006178	1991-04-01	Bijvoets
US5021224	1991-06-01	Nakajima
US5051786	1991-09-01	Nicollian et al.
US5064476	1991-11-01	Recine, Sr.
US5156004	1992-10-01	Wu et al.
US5181086	1993-01-01	Yoshida
US5210428	1993-05-01	Goossen
US5288336	1994-02-01	Strachan et al.
US5415699	1995-05-01	Harman
US5436467	1995-07-01	Elsner et al.
US5439528	1995-08-01	Miller
US5448109	1995-09-01	Cauchy
US5610366	1997-03-01	Fleurial et al.
GBX1216001	1968-01-01

Non-Patent Literature (27)

G. G. Dartau, "Thermoelectric Properties of Cobalt Antimonides," Electronic Phenomena, vol. 55, May 1961, 8058.
Vining, C.B. & J.-P. Fleurial, "Silicon-Germanium: an Overview of Recent Developments," Proceedings of the Xth Intl. Conference on thermoelectrics, Univ. of Wales, Cardiff, UK, pp. 1-14, Sep. 10-12, 1991.
Caillat, T., et al., "Search for New High Temperature Thermoelectric Materials," Proceedings of the 27th Intersociety Energy Conversion Engineering Conference, pp. 3499-3503, 8/3-7/92.
Caillat, T., et al., "Thermoelectric Properties of a New Semiconductor IrSb.sub.3," Proceedings of the XIth Intl. Conference on Thermoelectrics, Univ. of Texas, Arlington, TX pp. 98-101, Oct. 7-9, 1992.
Caillat, T., et al., "Phase Diagram of the Ir-Sb System on the Antimony-Rich Part," Journal of Alloys and Compounds, 1993.
Kjekshus, A., "Thigh Temperature X-Ray Study of the Thermal Expansion of IrAs.sub.3 and IrSb.sub.3," Acta Chemica Scandinava, pp. 678-681, 1961.
Fleurial, J.-P. "Thermal and Electrical Transport Properties Modeling of Bi.sub.2 Te.sub.3 -Based Alloys," Proceedings of the XIth Intl. Conf. on Thermoelectrics, Univ. of Texas, Arlington, TX pp. 276-281, Oct. 7-9, 1992.
Bass, J.C. and N. Elsner, "Current Thermoelectric Programs at Hi-Z Technology, Inc.," Proceedings of the XIth Intl. Conference on Thermoelectrics, Univ. of Texas, Arlington, TX, pp. 1-3, Oct. 7-9, 1992.
Borshchevsky, A., et al., "Two-Zone Bridgman Furnace with Sharp Thermal Gradient," NASA Tech Brief, 18 (3) Item #74, Mar. 1994.
Dudkin, L.D., et al., "On the Doping of the Semiconductor Compound CoSb.sub.3," Zhur. Neorg. Khim., 1958.
Feschotte P., and D. Lorin, "Les Systemes Binaires Fe-Sb, Co-Sb et Ni-Sb," J. Less Common Metals, pp. 155, 255-269, 1989.
Kajikawa, T., et al., "Advancement of Thermoelectric Energy Conversion Systems in Japan," Proceedings of the XIth Intl. Conference on Thermoelectrics, Univ. of Texas, Arlington, TX, pp. 175-180, Oct. 7-9, 1992.
Kliche, G. W. Bauhofer, "Infrared Reflection Spectra and Electrical Properties of the Skutterudite RhSb.sub.3," Mat. Res. Bull., (22), pp. 551-555, 1987.
Korenstein, R. et al., "Preparation and Characterization of the Skutterudite-Related Phases CoGe.sub.1.5 and CoGe.sub.1.5 Se.sub.1.5," Inorg. Chemist., 16(9), pp. 2344-2346, 1977.
Lutz, H.D., et al. "Far-Infrared Spectra, Optical and Dielectric Constants, Effective Charges and Lattice Dynamics of the Skutterudites CoP.sub.3 CoAs.sub.3 and CoSb.sub.3," Phys. Stat. Sol. (b), pp. 112, 549-557, 1982.
Lyons, A., et al., "The Preparation and Characterization of Some Skutterudite Related Compounds," Mat. Res. Bull., (13), pp. 125-128, 1978.
Nikolaev, Yu V., et al., "A Terrestrial Solar Power Plant with Direct Energy Conversion," Proceedings of the 27th Intersociety Energy Conversion Conference, pp. 3433-3436, Aug. 3-7, 1992.
Vining, C.B., "The Thermoelectric Limit ZT=1: Fact or Artifact . . . ," Proceedings of the XIth Intl. Conference on Thermoelectrics, Univ. of Texas, Arlington, TX, pp. 223-231, Oct. 7-9, 1992.
Zhuravlev, N.N., et al., Vestn. Mosk. Univ., Ser. Mat., Mekh, Astron., Fix. I Khim., 13 (5) pp. 79-82, 1958.
Caillat, T., Borshchevsky, A., and Fleurial, J.P., "Existence and Some Properties of New Ternary Skutterudite Phases", Proceedings of the XIII Intl. Conf. on Thermoelectrics, Kansas City, MO, Aug. 30-Sep. 1, 1994, pp. 1-9.
G. D. Mahan, et al., "Thermoelectric Devices Using Semiconductor Quantum Wells" 1994 American Institute of Physics, J. App. Phys. 76 (3) 1 Aug. 1994, pp. 1899-1901.
L.D. Hicks, et al., "Use of Quantum-Well Superlattice to Obtain a High Figure of Merit from Nonconventional Thermoelectric Materials" 1993 American Institute of Physics, Appl. Phys. Lett. 63 (23) 6 Dec. 1993, pp. 3230-3232.
International Search Report dated Dec. 20, 1994 for International Application No. PCT/US94/08452 filed 28 Jul. 1994.
L. D. Dudkin, N. Kh. Abrikosov, "A Physicochemical Investigation of Cobalt Antimonides" Zhurnal Neorganicheskoi Khimii, vol. I, No. 9, 1956, pp. 2096-2105 (Journal of Inorganic Chemistry, USSR), pp. 169-180.
L. D. Dudkin, "The Chemical Bond in Semiconducting Cobalt Triantimonide" Sov. Phys.--Tech. Phys., (1958) pp. 216-219.
L. D. Dudkin and N. Kh. Abrikosov, "On The Doping of the Semiconducttor Compound CoSb.sub.3 " Sov. Phys. Solid State, (1959), pp. 126-133.
L. D. Dudkin, N. Kh. Abrikosov, "Effect of Nickel on the Properties of The Semiconducting Compound, CoSb.sub.3 " Zhurnal Neorganicheskoi Khimii, vol. II, No. 1, 1957, pp. 212-221 (Journal of Inorganic Chemistry, USSR), pp. 325-338.

Abstract

Description