US 5,700,736 AGrant
Method for Making Semiconductor Device
Issue Date:1997-12-23
•6 Claims
•2 Drawing Sheets
Abstract
An SiOF layer is formed by using as raw material an organic Si compound having Si-F bonds. Since an organic Si compound is used as raw material, an intermediate product being formed during the formation of an SiOF layer is liable to polymerize and has fluidity. Moreover, since the organic Si compound has Si-F bonds, low in bond energy, and is thus capable of easily getting only Si-F bonds separated, the SiOF layer is prevented from getting contaminated by reaction by-products and fluorine can be introduced into the SiOF layer in stable fashion. Therefore, an insulator layer, low in dielectric constant, low in hygroscopicity and excellent in step coverage, can be formed by using a low powered apparatus.
Metadata
Assignee
- Sony Corporation
Inventor
- Masakazu Muroyama
Application Information
Application Number:US 570653&
Filing Date:1995-12-11
Priority Date:1994-12-13
Art Unit:117
Classifications
IPC:
H01L 21471
Field of Search:
437427438195;228;235;236255.1;255.3;255.7622;783;784;787;789
Patent Drawings (2 sheets)
Description
Background of the Invention
1. Field of the Invention
The present invention relates to a method for making a semiconductor device having an insulator layer for isolating conductive layers from each other.
2. Description of the Related Art
In a semiconductor device, conductive layers of different layers or of same layer are insulated from each other by being covered with an insulator layer. With ever-increasing miniaturization of design rule of a semiconductor device, however, there has become problematic a delay in operation due to parasitic capacitance originating from an insulator layer together with a semiconductor layer insulated by that insulator layer. Thus, need for an insulator layer having low dielectric constant is growing in order to effectively suppress an increase in capacitance even when the layer thickness is made smaller.
As methods for forming an insulator layer having low dielectric constant, there have been known a method for forming an SiOF layer using TEOS with addition of C.sub.2 F.sub.6 as fluorine source (25th SSDM' 93, p. 161) and a method for forming an SiOF layer using TEOS with addition of NF.sub.3 as fluorine source (40th United Lecture Conference related to Applied Physics, Preprint, 1a-ZV-9).
According to the above-mentioned conventional methods, however, decomposition energy of C.sub.2 F.sub.6 or NF.sub.3 is approximately equal to that of the alkyl groups in TEOS. This leads to contamination of the SiOF layer by reaction by-products. Introduction in stable fashion of fluorine into the SiOF layer also meets difficulty here. For this reason, with increasing amount of fluorine included in the SiOF layer, layer quality of the SiOF layer markedly worsens. This leads to higher hygroscopicity of the SiOF layer, resulting in a decrease in the reliability of a semiconductor device.
In order to form an SiOF layer having an excellent layer quality, there has been proposed a method for forming an SiOF layer using an SiF.sub.4 /O.sub.2 type gas that contains fluorine in the raw material gas structure (40th United Lecture Conference related to Applied Physics, Preprint, 31p-ZV-1).
However, since the SiF.sub.4 /O.sub.2 type gas is relatively difficult to decompose, a high density plasma CVD apparatus is required in order to form an SiOF layer by using this gas. In other words, a new type plasma CVD apparatus, different from the conventional one, is required here. According to this conventional method, it is difficult to manufacture with ease a semiconductor device that is fast in operation and high in reliability.
Summary of the Invention
A method for making a semiconductor device according to a first invention of the present invention is characterized in that an insulator layer is formed by using as raw material an organic Si compound having Si-F bonds.
Among others, the above organic Si compound is preferably a compound having a chain or cyclic structure.
Preferable examples of the above organic Si compound having a chain or cyclic structure are: fluoroalkoxysilane (F.sub.x R.sub.y Si; x+y=4, x.gtoreq.1; R:hydrogen, alkoxy or alkyl group), chain polysilane (F.sub.x R.sub.y Si-O-SiR.sub.m F.sub.n ; x+y=4, m+n=4, x, m.gtoreq.1; R:hydrogen, alkoxy or alkyl group), cyclic polysilane {(F.sub.x R.sub.y).sub.4 SiO.sub.4 ; x+y=4, x, y.gtoreq.1; R:hydrogen, alkoxy or alkyl group} and higher fluorosilane {(F.sub.x R.sub.y).sub.2m+2 Si.sub.m ; x+y=4, x, m.gtoreq.1; R:hydrogen, alkoxy or alkyl group}.
In a method for making a semiconductor device according to the present invention, the above insulator layer is preferably formed by a plasma CVD method using as raw material gas the above organic Si compound.
A method for making a semiconductor device according to a second invention of the present invention is characterized in that the above insulator layer is formed by repeating more than once by turns a step of adsorption of a raw material gas comprising the above organic Si compound by a substrate on which the above insulator layer is to be formed and a step of removal of unreacted matters from the adsorption layer by plasma treatment .
Brief Description of the Drawings
FIGS. 1A and 1B are sectional side views of a semiconductor device, showing first to third embodiments of the present invention in sequence of processing steps; and
FIG. 2 is a concept representation of a CVD apparatus used in the first to third embodiments of the present invention.
Detailed Description of the Preferred Embodiments
In the method for making a semiconductor device according to the first invention of the present invention, an insulator layer is formed by using as raw material an organic Si compound. Since an intermediate product being formed during the formation of the insulator layer is liable to polymerize and has fluidity, the insulator layer thus formed is excellent in step coverage.
Moreover, since the organic Si compound has Si-F bonds, whose bond energy is higher than that of C-O bond of an alkoxy group, separation solely of alkoxy groups from an organic Si compound can be easily effected. Therefore, the insulator layer formed is prevented from getting contaminated by reaction by-products and fluorine can be introduced into the insulator layer in stable fashion. Thus, an insulator layer, excellent in layer quality despite its low dielectric constant and low in hygroscopicity, can be formed by using a low powered apparatus.
Since the insulator layer can be formed at relatively low temperature by using plasma CVD method, no damage is inflicted on existing Al wirings.
In the method for making a semiconductor device according to the second invention of the present invention, probability is low of the reaction between the surface of the insulator layer being formed and the molecules of the raw material gas. Moreover, there is formed a liquefied layer of the molecules of the raw material gas so that this layer has fluidity. These altogether lead to a formation of an insulator layer further improved in step coverage. On the other hand, unreacted matters are removed from the adsorption layer by the plasma treatment after the adsorption so that an insulator layer is formed with further improved layer quality and further reduced hygroscopicity, without that the step coverage is negatively affected.
In the following referring to FIGS. 1 and 2, there will be explained first to third embodiments of the present invention which is applied to making a semiconductor device having as interlayer insulator an SiOF layer.
Prior to an explanation of the embodiments, there will be made an explanation of a parallel plate type plasma CVD apparatus that is used for forming the SiOF layer in the first to third embodiments. In this CVD apparatus as indicated in FIG. 2, out of parallel plate electrodes located in a reaction chamber 11, a lower electrode 13, on which a semiconductor substrate 12 is placed and which is grounded, is either heated or cooled by a heater/cooler 14 such that the treatment is carried out at lowest possible temperature in order not to cause a deterioration in the layer quality.
On the other hand, an upper electrode 15, to which an RF voltage is applied, is formed as a shower electrode; as indicated with an arrow in FIG. 2, a gas dispersing plate 17 is placed between the upper electrode 15 and a gas inlet pipe 16 in order to uniformly disperse in the reaction chamber 11 both a raw material gas to form the SiOF layer and a plasma treatment gas.
Next, the first embodiment will be explained. In the first embodiment, as shown in FIG. 1A, an interlayer insulator 21 such as an SiO.sub.2 layer or the like is formed on the semiconductor substrate 12 such as an Si substrate or the like, and Al wirings 22 are patterned on the interlayer insulator 21. Thereafter, by using a CVD apparatus shown in FIG. 2 and using as the raw material gas difluoro-diethoxysilane that is an organic Si compound having Si-F bonds, an SiOF layer 23 is formed as shown in FIG. 1B under the following condition:
Flow rate of F.sub.2 (C.sub.2 H.sub.5 O).sub.2 Si gas : 200 sccm
Flow rate of O.sub.2 : 200 sccm
Pressure : 1200 Pa
Temperature of the semiconductor substrate : 300.degree. C.
Thereafter, the SiOF layer 23 is annealed in a forming gas whose H.sub.2 concentration was reduced to 3% by dilution with N.sub.2, under the following condition:
Flow rate of the forming gas : 8 liters/minute
Annealing time : 60 minutes
Pressure : atmospheric pressure
Annealing temperature : 400.degree. C.
In the first embodiment as illustrated so far, difference in bond energy is large between C-O bond and Si-F bond in F.sub.2 (C.sub.2 H.sub.5 O).sub.2 Si gas. It is therefore possible to selectively break C.sub.2 H.sub.5 O between C and O by regulating RF power of the plasma CVD apparatus. In this way, not only an SiOF layer 23 thus formed is prevented from getting contaminated by reaction by-products but also an excellent SiOF layer 23 in layer quality(see below) can be formed by introduction in stable fashion of fluorine into that SiOF layer 23.
Corrosion tests are carried out in a hydrochloric acid solution under the following condition:
Concentration of the hydrochloric acid solution : 5%
Test duration : 5 minutes
Temperature of the hydrochloric acid solution : 25.degree. C. No corrosion of the Al wirings 22 is observed. This can be understood as an indication that the layer quality of the SiOF layer 23 is excellent and that, as shown in FIG. 1B, the step portions of the Al wirings 22 are sufficiently covered by the SiOF layer 23.
Next, the second embodiment will be explained. The second embodiment also follows essentially the same processing steps as in the above first embodiment except that the SiOF layer 23 is formed under the condition described below; in the second embodiment, there is used as raw material gas 2,4,6,8-tetrafluoro, 2,4,6,8-tetramethoxy type one that is a cyclic polysilane which is supposed to be able to bring about a very excellent step coverage:
Flow rate of SiF.sub.4 (OC.sub.2 H.sub.5)O.sub.4 gas : 300 sccm
Flow rate of O.sub.2 : 100 sccm
Pressure : 1200 Pa
Temperature of the semiconductor substrate : 300.degree. C.
After the SiOF layer 23 has been formed, corrosion tests are carried out under the same condition as in the first embodiment. No corrosion of the Al wirings 22 is observed in this second embodiment, too.
Next, the third embodiment will be explained. The third embodiment also follows essentially the same processing steps as in the above first embodiment except for the forming step of the SiOF layer 23. That is, in the third embodiment, both the adsorption of the raw material gas and the removal of unreacted matters in the adsorption layer by the plasma treatment are repeated ten times by turns under the following condition, respectively:
The adsorption of the raw material gas:
Flow rate of F.sub.2 (C.sub.2 H.sub.5 O).sub.2 Si.sub.2 O gas : 200 sccm
Pressure : 1200 Pa
Temperature of the semiconductor substrate : 50.degree. C.
Adsorption time : 30 sec
The plasma treatment:
Flow rate of O.sub.2 gas : 200 sccm
Pressure : 1200 Pa
RF power : 500 W
Temperature of the semiconductor substrate : 400.degree. C.
Treatment duration : 30 sec
After the SiOF layer 23 has been formed, corrosion tests are carried out under the same condition as in the first embodiment. No corrosion of the Al wirings 22 is observed in this third embodiment, too.
Conclusively, by the method for making a semiconductor device according to the first invention of the present invention, an insulator layer, low in dielectric constant, low in hygroscopicity and excellent in step coverage can be formed by using a low powered apparatus. Therefore, there can easily be made a semiconductor device less in delay in operation due to parasitic capacitances and thus fast in operation, and of high reliability.
By the method for making a semiconductor device according to the second invention of the present invention, an insulator layer, still more excellent in step coverage and still less in hygroscopicity, can be formed. Thus, a still more reliable semiconductor device can be made.
Claims
What is claimed is:
1. A method for making a semiconductor device, comprising the steps of: forming a first wiring layer on a substrate; forming an insulator layer comprising SiOF by adsorption of a raw material gas comprising an organic Si compound on said first wiring layer; removing, after said adsorption step, unreacted material from said insulator layer by plasma treatment; repeating more than once by turns said steps of adsorption and plasma treatment until formation of said insulator layer is substantially complete; and thereafter, forming a second wiring layer on said insulator layer, wherein said organic Si compound includes Si-F bonds.
2. A method for making a semiconductor device according to claim 1, wherein said organic Si compound is selected from the group consisting of: fluoroalkoxysilane (F.sub.x R.sub.y Si; x+y=4, x.gtoreq.1; R:hydrogen, alkoxy or alkyl group), chain polysilane (F.sub.x R.sub.y Si-O-SiR.sub.m F.sub.n ; x+y=4, m+n=4, x, n.gtoreq.1; R:hydrogen, alkoxy or alkyl group), cyclic polysilane {(F.sub.x R.sub.y).sub.4 ; x+y=4, x, y.gtoreq.1; R:hydrogen, alkoxy or alkyl group} and higher fluorosilane {(F.sub.x R.sub.y).sub.2m+2 Si.sub.m ; x+y=4, x, m.gtoreq.1; R:hydrogen, alkoxy or alkyl group}.
3. A method as defined in claim 1, wherein in the step of forming the insulator layer by adsorption of a raw material gas on said first wiring layer is performed by a plasma chemical vapor deposition method.
4. A method as defined in claim 1, wherein said plasma treatment comprises treating the adsorbed layer in an O.sub.2 gas at a pressure of about 1200 Pa, an RF power of about 500 W and at a substrate temperature of about 400.degree. C.
5. A method as defined in claim 1, wherein the steps of adsorption and plasma treatment are each performed for a duration of about 30 seconds.
6. A method as defined in claim 1, wherein the steps of adsorption and plasma treatment are repeated about 10 times.