Sterile Gel Compositions for Wound Treatment

The present invention relates to sterile gel compositions for application to the surface of wounds, such as decubitus ulcers and burns. The present invention also relates to a method of making such sterile gel compositions.

Aqueous gel compositions for application to the surface of wounds to assist healing are known. The purpose of applying the gels is to form a wound-friendly and humectant wound contact layer between the wound surface and conventional wound dressing layers. This also helps to reduce the adherence of conventional wound dressings, such as bandages or gauzes, to the wound surface. The aqueous gel can also serve as a vehicle for pharmaceutically active agents such as antiseptics or antibiotics.

U.S. Pat. No. 4,393,048 describes protective gel compositions for wounds comprising about 0.5 to 3% by weight alkali metal alginate, about 8 to 12% by weight glycerol and about 82 to 90% by weight water. Medicaments in an amount of 0.01 to 10% by weight may optionally be included in the compositions. The resulting gel is brushed over the surface of the wound and dries in air to form a non-toxic, flexible and stretchable film covering the wound.

A drawback of the gel compositions described in U.S. Pat. No. 4,393,048 is that they cannot readily be prepared in a sterile form suitable for medical applications. This is because the usual methods of sterilisation, namely gamma-ray irradiation or autoclaving, result in hydrolysis of the alginate and consequent drastic reduction in the gel viscosity. This rules out sterilisation of the alginate gel after it has been manufactured and filled into packages. In fact, the only way to manufacture an alginate gel of this type that is sterile would be to sterilise all the ingredients dry and then mix and package them under aseptic conditions. This method of manufacture would be prohibitively expensive for the wound dressings market.

WO84/00111 describes heat sterilisable pharmaceutical gel compositions for the treatment of burns, cuts, wounds or abrasions. The gel compositions comprise a pharmaceutically acceptable glycol and a cellulose derivative which is heat sterilizable. The preferred glycol is propylene glycol, preferably in an amount of 20-30% w/v. The preferred cellulose derivative is hydroxy ethyl cellulose, preferably in an amount of 1-4% w/v. The gel compositions optionally contain medicaments and/or dissolved physiologically acceptable salts. The use of hydroxy ethyl cellulose gives a gel that is heat sterilisable. That is to say, the gel retains its consistency and does not break down into a liquid when it is sterilised in an autoclave.

A drawback of the gel compositions described in W084/00111 is that the heat sterilisable cellulose derivatives are inherently less effective in promoting wound healing than natural biopolymers such as alginates.

Accordingly, it is an object of the present invention to provide a heat sterilisable alginate gel for use in the treatment of burns, cuts, wounds, ulcers or abrasions.

The present invention provides an aqueous gel composition for use as a wound dressing comprising from 2% to 10% w/v of alginate and from 15% to 40% w/v of polyhydric alcohol, said composition being substantially sterile.

Surprisingly, it has been found that the inclusion of relatively large amounts of polyhydric alcohol (more than 15% w/v) results in an alginate gel that is stabilised against hydrolysis and consequent loss of viscosity during autoclave sterilisation. Sterilisation can be carried out by autoclaving using standard conditions. Compositions containing more than 40% w/v of polyhydric alcohol tend to separate on autoclaving. Such compositions can also cause discomfort or stinging when applied to a wound.

The alginate may consist of one or more of alginic acid and its salts. Preferably, the alginate consists of sodium alginate and/or potassium alginate. Preferably, the gel compositions comprise 3% to 6% w/v of the alginate. Preferably, the molecular weight of the alginate is in the range of 50,000 to 500,000.

The polyhydric alcohol preferably comprises one or more C.sub.3 -C.sub.6 dihydric or trihydric alcohols, more preferably C.sub.3 -C.sub.6 dihydric alcohols and most preferably propylene glycol or hexylene glycol. Other preferred polyhydric alcohols include ethylene glycol, butylene glycol, glycerol, diethylene glycol, dipropylene glycol, polyethylene glycol and polypropylene glycol. Preferably, the composition contains a total of 20% to 35% w/v of the one or more polyhydric alcohols.

The entire balance of the gel compositions other than the alginate and polyhydric alcohol may consist of water. However, preferably, the gel compositions also contain 0.01% to 10% w/v of one or more pharmaceutically active compounds, more preferably 0.1% to 5% w/v of such compounds. Preferred pharmaceutically active compounds are selected from: antiseptics such as chlorhexidine or silver sulphadiazine; antibiotics such as pencillins or tetracyclines; analgesics such as aspirin, paracetamol, ibuprofen or naproxen; steroids; glycosaminoglycans such as ihyaluronic acid and its salts, chondroitin sulfate or heparan sulfate; vitamins such as vitamins A and E; haemostats; cytokines; antibodies; enzymes; inflammatory agents; anti-inflammatory agents, and growth factors. Preferably, the total water content of the aqueous gel is from 55% to 79% w/v.

The aqueous gel preferably further comprises from 0.1% to 5% w/v of dissolved salts. The salts we preferably selected from the chlorides, iodides, sulfates, phosphates, bromides, carbonates, bicarbonates and hydroxides of sodium, potassium, ammonium, aluminum, zinc, silver and calcium. The dissolved salts preferably comprise sodium chloride, since it has been found that the presence of small amounts of sodium chloride can significantly affect the change in viscosity of the gel on sterilisation. The sodium chloride content thus provides a further parameter with which to control the viscosity of the sterile gel compositions. Also preferably, the gel compositions comprise phosphate salts or other suitable buffers to regulate the pH of the gel.

As noted above, an advantageous feature of the gels according to the present invention is that they retain useful viscosity after sterilisation. This allows the gels to be coated onto the wound site reasonably conveniently.

The present invention also provides a process to prepare a substantially sterile gel for application to burns, cuts, wounds, ulcers or grazes, the process comprising the steps of: providing an aqueous gel comprising from 2% to 10% w/v of alginate and from 15% to 40% w/v of polyhydric alcohol; and heat sterilizing the aqueous gel.

Preferred compositions and constituents of the aqueous gel are the same as those described above for the gel compositions according to the present invention.

Preferably, the step of sterilizing is carried out by heating at a temperature for a period sufficient to give a sterility measure of FO.sub.4, more preferably FO.sub.8, and most preferably FO.sub.12. Preferably, this step of heat-sterilising is carried out under pressure in an autoclave.

Preferably, the process according to the present invention further comprises the step of inserting the aqueous gel into a package prior to carrying out the step of sterilising. Preferably, the package is a tube, can or sachet. This procedure is advantageous because it enables the aqueous gels to be made under non-sterile conditions, packaged and then sterilised, thereby providing a relatively low-cost route to packaged sterile alginate gels.

In order for the aqueous gel to be easily packaged prior to sterilisation, it is preferable for the viscosity of the aqueous gel before sterilisation to be less than 150,000 cps, preferably less than 100,000 cps.

Specific embodiments of the gel compositions and processes according to the present invention will now be described further in and by the following Examples:

The effect of propylene glycol (PG) content on the heat sterilisability of aqueous alginate gels is determined as follows.

A number of aqueous alginate gels is made up according to the following proportions. The sodium alginate (Protanal LF 10/60) has a stated molecular weight in the range 70,000 to 200,000. The potassium alginate has a molecular weight range of 300,000 to 350,000. Each gel is then sterilised in an autoclave to give a sterility measure of FO.sub.12.

The viscosity in centipoise (cps) at 20.degree. C. is measured before and after sterilisation for each of the gels. The viscosity measurements are carried out with a rotating spindle, dial reading mechanical viscometer manufactured by Brookfield Viscometers Ltd. Brookfield Spindle No. 7 is used at a speed of 10 revolutions per minute. The sample is held in a cylindrical container measuring at least 50 mm in diameter and holding sample to a depth of at least 70 mm.

The results are as follows (, denotes a comparative example).

These results demonstrate clearly that, by selecting the level of alginate and propylene glycol, it is possible to produce an alginate gel which maintains, or even increases, its viscosity on autoclaving.

The procedure of Example 1 is followed for the following compositions, in which the propylene glycol (PG) of Example 1 has been replaced by hexylene glycol (HG). The results are as follows (* denotes a comparative example).

These results demonstrate that hexylene glycol can also be used to form autoclave-stable alginate gels. It appears that less hexylene glycol than propylene glycol is needed to achieve equivalent stabilisation.

The effect of adding 0.6% w/v of sodium chloride to a 3% sodium alginate gel is illustrated by the following data (* denotes a comparative

It can be seen that the addition of 0.6% w/v sodium chloride to the aqueous alginate gel at 25% w/v PG content results in a gel having satisfactory viscosity after autoclaving.

The above embodiments have been described by way of example only. Many other embodiments falling within the scope of the accompanying claims will be apparent to the skilled reader.