Abstract
A method for producing an oxide glass thin film is provided, in which volatilization of additives in a porous film from which the thin film is formed is effectively suppressed, and which the oxide glass film has a desired arrangement of refractive index with a low optical loss. According to this method, glass fine particles mainly containing SiO.sub.2 with a first additive are deposited on a substrate to form a porous thin film. A gas containing a second additive is supplied to a first chamber and heated to a first predetermined temperature profile to provide a heated gas containing an oxide. After disposing the substrate in a second chamber communicated with the first chamber, the substrate is heated to make the deposited porous glass into transparent glass while controlling a temperature in the second chamber according to a second temperature profile. A carrier gas is flowed from the first chamber to the second chamber to transfer the heated gas and oxide from the first chamber to the second chamber during heating. The temperature of the first predetermined temperature profile is maintained higher than the temperature of the second predetermined temperature profile at the same time. In addition, the heated gas contains a component that is also present in the first additive.
Metadata
Assignee
- Sumitomo Electric Industries, Ltd.
Inventors
- Shinji Ishikawa
- Akira Urano
- Haruhiko Aikawa
- Chizai Hirose
- Hiroo Kanamori
- Masahide Saitoh
Application Information
Application Number:US 4638662
Filing Date:1995-06-05
Priority Date:1992-03-17
Art Unit:133
Classifications
IPC:
C03B 3707C03C 2502
Field of Search:
6542760.5;60.8;17.4;384;386;399;423;430;416;444;32.4108;163.2;165;167
Patent Drawings (8 sheets)
Description
Background of the Invention
1. Field of the Invention
The present invention relates to a method and an apparatus for producing an oxide glass thin film to be used for formation of an optical waveguide or the like.
2. Related Background Art
A glass optical waveguide formed on a silica glass substrate or on a silicon substrate exhibits good matching characteristics with optical fibers, and, therefore, is used as a component for optical communication. There is known a method for forming a glass optical waveguide on a substrate, in which fine particles of glass are deposited on a substrate by a gas phase method using an oxygen-hydrogen burner to form a porous glass thin film thereon (see FIG. According to this method the substrate is then heated at a high temperature by means of an electric oven to finally form a transparent glass thin film on the substrate. Normally, the substrate is a silicon wafer, and the waveguide as so formed contains SiO.sub.2 as its main component. In this case, the melting point of silicon is lower than the glass transition temperature of pure SiO.sub.2. It is a usual practice to lower the glass transition temperature by adding an additive or additives such as P.sub.2 O.sub.5, B.sub.2 O.sub.3, GeO.sub.2, and the like into the SiO.sub.2. The specific contents of the conventional waveguide are described in detail for example in Japanese Laid-open (Kokai) Patent Application No. 58-105111, Japanese Laid-open (Kokai) Patent Application No. 1-192732, and U.S. Pat. No. 4,263,031.
In instances in which the fine particles of glass are deposited on the substrate to form the porous thin film and heated at the high temperature by the electric oven to form the transparent glass thin film, as described above, the following problems tend to occur due to volatilization scattering of the additive components which are added into the oxide glass thin film in order to lower the glass transition temperature.
Components easy to volatilize and thereby scatter, such as P.sub.2 O.sub.5, B.sub.2 O.sub.3, etc., among the additive components are first to exit of the thin film, which raises the glass transition temperature of the glass portion from which the volatile components have been volatilized to scatter. The rise of the glass transition temperature causes an unsintered portion or non-transparent glass portion to be left behind in the glass film produced. This causes a high optical loss in the waveguide thus formed from such a glass film. Additionally, the refractive index of the glass film surface varies depending upon the extent of volatilization of the additive components, which makes it difficult to obtain a desired arrangement of refractive index. This in turn makes the design of the waveguide structure difficult.
Summary of the Invention
It is an object of the present invention, taking the above problems into account, to obtain an oxide glass thin film having a desired refractive index arrangement with a low optical loss by suppressing the volatilization of additives in a porous glass thin film deposited on a substrate during a step of changing the porous film into a transparent glass film.
In order to resolve the above problems, the present invention involves a method of producing an oxide glass thin film, in which fine particles of glass mainly containing SiO.sub.2 with an additive or additives are deposited on a substrate to form a porous thin film thereon and in which the porous thin film is heated to form a transparent glass film on the substrate, wherein vapor of oxide(s) of the additive component(s) is mixed in an atmosphere in which the porous thin film is heated to form the transparent glass film.
That is, the method of producing a glass thin film according to this invention comprises:
a first step of depositing fine particles of glass mainly containing SiO.sub.2 with an additive on a substrate to form a porous glass thin film thereon; and
a second step of heating the porous glass thin film to form a transparent glass thin film on the substrate; the second step being conducted in an atmosphere containing a vapor of an oxide of a component in the additive for suppressing a the volatilization of the additive in the fine particles.
The following methods are suitable for introducing the vapor of the oxides into the atmosphere:
(a) A method in which each of the vapor components (P.sub.2 O.sub.5, B.sub.2 O.sub.3, GeO.sub.2, etc.) is heated to evaporate in a separate manner and then introduced into a heating area of the substrate;
(b) A method in which the vapor of chlorides (PCl.sub.3, POCl.sub.3, BCl.sub.3, GeCl.sub.4, etc.) is oxidized with O.sub.2 gas and then introduced into the heating area of the substrate.
According to the present invention, the heating area temperature of the vapor components in the method (a) or the oxidation area temperature in the method (b) is set at a temperature at which a vapor pressure of the introduced oxides is 50 to 150% of the equilibrium vapor pressure at the substrate heating area temperature.
The volatilization of the additives may be represented by the following chemical formula 1 or chemical formula 2. ##STR1##
The volatilization of the additive components occurs with progress of the rightward reactions in the above formulas. The extent of the volatilization reactions are determined by reference to the chemical equilibrium at a certain treatment temperature. Thus, if the volatile components should exist in the treatment gas at a vapor pressure over the equilibrium pressure at the substrate treating temperature, the reactions indicated arrow (c) in chemical formula 1 and in chemical formula 2 would not proceed and thus cause no volatilization of the additive components. However, a practically sufficient effect can be obtained in actual practice if the volatilizing components are between 50% and 150% of the equilibrium pressure at the substrate treating temperature.
Provided that the heating area temperature of the vapor components or the oxidation area temperature is kept at a higher temperature than the substrate heating area temperature, a vapor pressure of each additive component would become greater than the equilibrium vapor pressure of the chemical formula 1 or the chemical formula 2, thereby enhancing the effect of preventing the volatilization of the additive components as described.
Components easy to volatilize to scatter are P.sub.2 O.sub.5, B.sub.2 O.sub.3, and GeO.sub.2, the equilibrium vapor pressures of which are shown in FIG. 2.
According to the present invention as described above, in the production of the oxide glass thin film to be used for formation of optical waveguides or the like, the vapor of volatile oxide components is introduced into the atmosphere in which the heating process to form the transparent glass film is carried out, so as to stop the volatilization of the additives in the porous film deposited, thereby preventing diffusion of the additives added into a core layer and also preventing the volatilization of glass transition temperature lowering components in the additives (P.sub.2 O.sub.5, B.sub.2 O.sub.3, GeO.sub.2, etc.). In accordance with the present invention, a desired arrangement of refractive index may be obtained, and an oxide glass thin film may be obtained while lowering the optical loss, such as the optical scattering, which could be caused by bubbles in the unsintered portion.
The present invention will become more fully understood from the detailed description given hereinbelow and the accompanying drawings which are given by way of illustration only, and thus are not to be considered as limiting the present invention.
Further scope of applicability of the present invention will become apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and specific examples, while indicating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from this detailed description.
Brief Description of the Drawings
FIG. 1 is a perspective view of an apparatus for depositing fine particles of glass on a substrate;
FIG. 2 is a graph indicating equilibrium vapor pressures of major additive components;
FIG. 3 is a schematic diagram of an apparatus used in Example 1 according to the present invention;
FIG. 4 is a graph showing a temperature control procedure practiced in Example 1 according to the present invention;
FIG. 5 is a schematic diagram of an apparatus used in Example 2 according to the present invention;
FIG. 6 is a graph showing a temperature control procedure practiced in Example 2 according to the present invention;
FIGS. 7A-7F are sectional views respectively showing schematic steps of forming an optical waveguide, using a production method of a glass thin film according to the present invention;
FIG. 8 is a sectional view illustrating the effect in the present invention; and
FIG. 9 is a graph showing a relation between a ratio (P.sub.i /P.sub.is), which is a ratio of a vapor pressure (P.sub.i) of introduced oxides to a saturated vapor pressure (P.sub.is), and a ratio (b/a), which is a ratio of a parameter .DELTA. (b) on the surface side to a parameter .DELTA. (a) on the substrate side.
Description of the Preferred Embodiments
The preferred embodiments according to the present invention will be described in detail in the following.
Example 1
Using an apparatus as shown in FIG. 1, fine particles of glass mainly containing SiO.sub.2 are deposited on a substrate of Si to form a deposit film of the glass fine particles.
First explained is the apparatus for depositing the glass fine particles on the substrate as shown in FIG. 1. There are a plurality of substrates 1, onto which the glass fine particles through a torch 3 are to be deposited and which are disposed in a reaction vessel 6 having a bottom defined by a rotatable turn table 2. Glass fine particles which are not deposited on the substrates 1 and the exhaust gas are removed through an exhaust pipe 4. The turn table 2 on which the substrates 1 are placed is driven to rotate relative to the reaction vessel 6 by means of a motor (not shown), and the torch 3 reciprocates in the radial direction of the turn table 2. Such an arrangement permits the glass fine particles to be uniformly deposited on the substrates 1. A lower heater 5 is provided on the turn table 2 to uniformly heat the substrates 1 placed on the turn table 2.
Using the above-described apparatus, fine particles of glass for optical waveguide film were deposited on the substrates. The substrates 1 were arranged on the turn table 2, and the substrates 1 were heated by the lower heater 5 to increase the temperature thereof while turning the turn table 2. Then, O.sub.2 gas and H.sub.2 gas were supplied to the torch 3, and an oxygen-hydrogen flame was formed at a blow-off portion of the torch 3 toward the substrates 1. At the same time, the torch 3 was reciprocated in the radial direction of the turn table 2. After the substrate temperature reached a predetermined temperature, a raw material of glass was fed to the torch 3 to undergo the hydrolysis in the flame, thereby depositing the glass fine particles on the substrates 1.
Conditions followed for the deposition of the glass fine particles were as follows: A rotation speed of the turn table 2 was 10 [rpm]; a moving speed of the torch 3 was 120 [mm/min]; a moving distance of the torch 3 was 200 [mm]; a feed rate of O.sub.2 gas into the torch 3 was 8 [l/min]; and a feed rate of H.sub.2 gas into the torch 3 was 10 [l/min]. The glass raw material was supplied to the torch 3 under the following conditions.
First deposition conditions
Fine particles of glass for a lower cladding layer (deposition time: 30 min)
SiCl.sub.4 : 250 [cc/min];
BCl.sub.3 : 10 [cc/min];
PCl.sub.3 : 25 [cc/min].
Second deposition conditions
Fine particles of glass for a core layer (deposition time: 20 min)
SiCl.sub.4 : 250 [cc/min];
GeCl.sub.4 : 40 [cc/min];
PCl.sub.3 : 20 [cc/min];
BCl.sub.3 : 5 [cc/min].
After that, the glass fine particles thus deposited on the substrate 1 were heated using a heating oven 10.
FIG. 3 shows a schematic construction of an apparatus used in Example 1. A heating oven 10 is provided which includes an oven core tube 15, heaters 13, 14, a gas supplying unit 17 for supplying gas into the oven core tube 15, and a gas evacuating unit 18 for evacuating the gas out from the oven core tube 15. The oven core tube 15 is a spatially continuous tube. The oven core tube 15 has a heating area (i.e., a first chamber) 11 for heating vapor components, which is located on the upstream side of gas flow, and a heating area (i.e., a second chamber) 12 for heating the substrates, which is located on the downstream side. The two heating areas are independently controlled by a control unit 19 to have respective temperatures through the heaters 13, 14, as shown in FIG. 3.
Platinum crucibles 16 were situated in the heating area 11 of the vapor components, in which respective oxides of P.sub.2 O.sub.5, B.sub.2 O.sub.3, and GeO.sub.2 were separately set, and were heated. The substrates 1 were placed in the heating area 12 of substrate.
The vapor component heating area 11 was initially set at 850 [.degree.C.] and the substrate heating area 12 at 800 [.degree.C.], and mixture gas of O.sub.2 at 5 [l/min] and He at 5 [l/min] was supplied to flow through the areas. The temperature was raised at a rate of 5 [.degree.C./min]. The vapor component heating area 11 and the substrate heating area 12 were then maintained at 1300 [.degree.C.] and at 1250 [.degree.C.], respectively, for one hour, and then the temperature of the vapor component heating area 11 and the temperature of the substrate heating area 12 were decreased down to 850 [.degree.C.] and to 800 [.degree.C.], respectively, as shown in FIG. 4. After stopping the supply of the mixture gas, the substrates 1 were removed. In this heating process, the temperature of the vapor component heating area 11 was always set higher by 50 [.degree.C.] than the temperature of the substrate heating area 12. There were no remaining bubbles recognized in the films obtained on the substrates 1. Analysis of element components using EPMA (electron probe micro analyser) showed no element volatilizatare and no diffusion in an interface area between the core layer and the lower cladding layer and in the outermost layer of the core.
Example 2
Using the apparatus of FIG. 1, a glass fine particle deposited film mainly containing SiO.sub.2 was formed on Si substrates 1 in the same manner as in Example 1. The deposition conditions of the glass fine particle deposited film were also the same as those in Example 1. Then, glass fine particles deposited on the substrates 1 were heated using a heating oven 20.
FIG. 5 shows a schematic construction of an apparatus used in Example 2. The heating oven 20 is provided which includes an oven core tube 25, heaters 23, 24, a gas supplying unit 27 for supplying gas into the oven core tube 25, and a gas evacuating unit 28 for evacuating the gas out from the oven core tube 25. The oven core tube 25 is a spatially continuous tube. The oven core tube 25 has an oxidation area 21 located on the upstream side of gas flow and a substrate heating area 22 on the downstream side. These two areas are independently controlled by a control unit 29 to have respective temperatures through the heaters 23, 24, as shown in FIG. 5. The substrates 1 were placed in the substrate heating area 22.
Initially, the temperature of the oxidation area 21 was set at 1350 [.degree.C.] and the temperature of the substrate heating area 22 at 800 [.degree.C.]; chloride vapor of GeCl.sub.4 at 5 [cc/min], POCl.sub.3 at 10 [cc/min], and BCl.sub.3 at 10 [cc/min], and a mixture gas of O.sub.2 at 5 [l/min] and He at 5 [l/min] were introduced into the heating oven. The chloride vapor introduced into the heating oven was preliminarily oxidized in the oxidation area 21. Then, the temperature of the substrate heating area 22 was raised at a rate of 5 [.degree.C./min], and then maintained at 1250 [.degree.C.] for one hour, and was lowered thereafter down to 800 [.degree.C.], as shown in FIG. 6. After stopping the supply of the mixture gas, the substrates 1 were taken out. There were no remaining bubbles recognized in the films on the substrates 1 obtained in this example. Patterning was effected on the films to produce buried waveguides.
Additionally, a glass fine particle deposited layer mainly containing SiO.sub.2 was formed on the Si substrates 1 under the same deposition conditions as in Example 1. Then, the substrates with the glass fine particle deposited layer were subject to the same heating treatment as in Example 1 without the presence of the vapor components (P.sub.2 O.sub.5, B.sub.2 O.sub.3, GeO.sub.2) by means of the electric oven 10 as shown in FIG. 3. Glass films thus obtained on the substrates 1 had cloudiness on the outermost surfaces thereof. Further, element analysis by EPMA showed that the amount of each P, B, and Ge at the outermost surfaces was decreased to be a quarter of the amount of each inside the films.
The present invention is not limited to the examples as described, but may be applied to a production method and a production apparatus obtained by combination of Example 1 and Example 2.
The introduced oxide vapor of the additive components rarely presented such an influence that the additives diffuse in the surface or in the inside of glass film, but rather showed the desired effect of preventing the volatilization of the additive components from the outermost surface of glass film at the high temperature.
The following explains schematic steps practiced to for an optical waveguide, using the production method of the glass thin film according to the present invention, with reference to sectional views as shown in FIGS. 7A to 7F.
A first porous glass film 50a, which is to become a lower cladding layer, is first deposited on a Si substrate 1 (FIG. 7A). A second porous glass film 60a, which is to become a core layer, is then deposited on the first porous glass film 50a (FIG. 7B). The deposition conditions of the first and second porous glass films 50a, 60a are the same as those as shown in Example 1.
The first and second porous glass films 50a, 60a are heated in a heating oven, into which the oxide vapor is introduced, to form transparent glass layers of a lower cladding layer 50 and a core layer 60, respectively (FIG. 7C). The core layer is subject to etching so as to leave a desired region behind, thus forming an optical waveguide 61 (FIG. 7D).
Further, a third porous glass film 70a, which is to become an upper cladding layer, is deposited over the lower cladding layer 50 and the optical waveguide 61 (FIG. 7E). The deposition conditions of the third porous glass film 70a are the same as those of the first porous glass film 50a, that is, as the first deposition conditions in Example 1. Then, the third porous glass film 70a is heated in the heating oven, into which the oxide vapor is introduced, to form a transparent glass layer of the upper cladding layer 70 (FIG. 7F).
An optical loss of the thus produced buried optical waveguide was measured, and the measured loss was not more than 0.1 [dB/cm], which was very good.
The relationship between the pressure of the introduced oxide vapor and an effect thereof is now described. FIG. 8 is a schematic sectional view of a glass layer 80, which is obtained by depositing a porous glass film on a substrate 1 and then heating it to form a transparent glass layer. A parameter .DELTA. at the bottom, or on the substrate side of a glass layer 80 is denoted by a, and a parameter .DELTA. at the top, or on the surface side of the glass layer 80 by b.
The parameter .DELTA. is a relative refractive index difference to a silica glass, which is defined by the following equation:
where n.sub.0 is a refractive index of the silica glass and n.sub.1 is a refractive index of an object.
FIG. 9 shows the results of measurements conducted on an example to investigate the relationship between a ratio (P.sub.i /P.sub.is), which is a ratio of a pressure (P.sub.i) of the introduced oxide vapor to the saturated vapor pressure (P.sub.is), and a ratio (b/a), which is a ratio of a parameter .DELTA. (b) of the glass layer 80 on the surface side to a parameter .DELTA. (a) of the glass layer 80 on the substrate side. This measurement example shows a case with additives of GeO.sub.2 and P.sub.2 O.sub.5, and the similar results are obtained with other additives.
The following briefly explains the graph of FIG. 9. When the pressure (P.sub.i) of the introduced oxide vapor is 40% of the saturated vapor pressure (P.sub.is), the parameter .DELTA. (b) on the surface side is about 0.93 times as large as the parameter .DELTA. (a) on the substrate side, while when the P.sub.i is 160% of P.sub.is, b is about 1.06 times as large as a. As the pressure (P.sub.i) of the introduced oxide vapor increases, the parameter .DELTA. (b) on the surface side gradually becomes larger.
It is most preferable as waveguide properties that the parameter .DELTA. (b) on the surface side coincides with the parameter .DELTA. (a) on the substrate side, which is b/a=1. In order to stabilize the properties of waveguide, it is preferable that the ratio of parameter .DELTA. (b/a) be set substantially between 0.95 and 1.05. It is accordingly preferable that the pressure (P.sub.i) of the introduced oxide vapor be kept at 50 to 150% of the saturated vapor pressure (P.sub.is).
The silicon substrate was employed as a substrate in the above examples, but the substrate may be a silica glass substrate. The present invention can be also applied to cases with various additives which could be volatilized to scatter during heating to form a transparent glass film, in addition to the examples as described above with the additives added to form the porous glass films.
From the invention thus described, it will be obvious that the invention may be varied in many ways. Such variations are not to be regarded as a departure from the spirit and scope of the invention, and all such modifications as would be obvious to one skilled in the art are intended to be included within the scope of the following claims.
Claims
What is claimed is:
1. A method for producing a glass thin film with a first additive on a substrate, said method comprising the steps of: depositing SiO.sub.2 porous glass with the first additive on the substrate; supplying a chloride gas having a component of the first additive to a first chamber; heating the chloride gas having the component of the first additive in the first chamber while controlling a temperature in the first chamber according to a first predetermined temperature profile so as to produce a heated gas containing an oxide; heating said substrate located in a second chamber communicated with the first chamber to make the deposited porous glass into transparent glass while controlling a temperature in the second chamber according to a second predetermined temperature profile; and flowing a carrier gas from the first chamber to the second chamber to transfer the heated gas containing an oxide from the first chamber to the second chamber during said heating steps, wherein the temperature at any given time of the first predetermined temperature profile is higher than the temperature of the second predetermined temperature profile at the same time, and further wherein the oxide of the heated gas containing an oxide is an oxide of the component of the first additive.
2. A method according to claim 1, wherein the substrate is a silica glass substrate or silicon substrate.
3. A method according to claim 1, wherein the oxide of the component of the first additive comprises at least one of GeO.sub.x, PO.sub.x AND BO.sub.x.
4. A method according to claim 1, wherein the temperature at any given time of said first predetermined temperature profile is higher than the temperature of said second predetermined temperature profile at the same time by a predetermined temperature.
5. A method according to claim 1, wherein said step of heating the chloride gas having the component of the first additive oxidizes the chloride gas to form the oxide of the component of the first additive.
6. A method according to claim 5, wherein the substrate is a silicon gas substrate or silicon substrate.
7. A method according to claim 5, wherein the oxide of the component of the first additive comprises at least one of GeO.sub.x, PO.sub.x and BO.sub.x.
8. A method according to claim 5, wherein the temperature at any given time of said first predetermined temperature profile is higher than the temperature of said second predetermined temperature profile at the same time by a predetermined temperature.
Patent Citations (15)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3653862 | 1972-04-01 | Lynch | |
| US3801294 | 1974-04-01 | Schultz et al. | |
| US3934061 | 1976-01-01 | Keck et al. | |
| US3954431 | 1976-05-01 | Fleming, Jr. et al. | |
| US4597787 | 1986-07-01 | Jacobson | |
| US4642129 | 1987-02-01 | Douklias et al. | |
| US4787927 | 1988-11-01 | Mears et al. | |
| US4799946 | 1989-01-01 | Ainslie et al. | |
| US5039325 | 1991-08-01 | Miller et al. | |
| EPX111901 | 1983-12-01 | ||
| JPX58-125621 | 1983-07-01 | ||
| JPX59-073443 | 1984-04-01 | ||
| JPX60-231435 | 1985-11-01 | ||
| JPX4260632 | 1992-09-01 | ||
| GBX2066805 | 1980-02-01 |
Non-Patent Literature (1)
- Kingery et al., Introduction to Ceramics, Second Edition, 1976, pp. 402-403, Wiley.