US 5,652,280 AGrant
Anionic Photoinitiation
Issue Date:1997-07-29
•11 Claims
•2 Drawing Sheets
Abstract
A method for the anionic photoinitiation of polymerization or crosslinking of a substrate by irradiating a mixture of a substrate and a photoinitiator, where the photoinitiator is an inorganic transition metal complex which releases on irradiation a polymerization initiating substance consisting essentially of an anionically charged nucleophile that initiates the polymerization or crosslinking reaction, under conditions that allow the anion to initiate polymerization.
Metadata
Assignee
- University of Georgia Research Foundation, Inc.
Inventor
- Charles R. Kutal
Application Information
Application Number:US 2437686
Filing Date:1994-05-17
Priority Date:1991-11-12
Art Unit:157
Classifications
IPC:
C08F 248C08J 328
Field of Search:
52243066;65;148;170;172;173;175;178;182;184;186;188270;281;274;289;283;914
Patent Drawings (2 sheets)
Description
DETAILED DESCRIPTION OF THE INVENTION
As used herein, the term substrate refers to the compound, monomer, oligomer, or polymer that is acted on by the anionic photoinitiator. In general, the photoinitiator causes a change in the chemical composition and/or physical structure of the substrate, to produce a product (see equations 2-3).
As used herein, the term inorganic complex refers to an inorganic compound that contains a ligand that is capable of being released as a nucleophilic anion on irradiation with light of the appropriate wavelength.
As used herein, the term nucleophile refers to an electron rich moiety that will attack the nucleus of a carbon atom.
The term alkyl, as used herein, unless otherwise specified, refers to a saturated straight or branched hydrocarbon of C.sub.1 to C.sub.10, and specifically includes methyl, ethyl, propyl, isopropyl, butyl, isobutyl, t-butyl, pentyl, cyclopentyl, isopentyl, neopentyl, hexyl, isohexyl, and cyclohexyl.
The terms alkenyl and alkynyl, as used herein, refers to a C.sub.2 to C.sub.10 straight or branched hydrocarbon with at least one double or triple bond, respectively. phenyl, which can be substituted with one or more aliphatic groups.
The term aliphatic refers to a hydrocarbon, typically of C.sub.1 to C.sub.10, that can contain one or a combination of alkyl, alkenyl, or alkynyl moieties, and which can be straight, branched, or cyclic, or a combination thereof.
A method for anionic photoinitiation is provided that includes exposing the substrate to be polymerized or crosslinked to an inorganic transition metal complex that releases anions in a controlled fashion when irradiated. The metal complex is thermally stable, soluble in the reactants, and nonreactive in the absence of light.
The anionic photoinitiators can be used to prepare new classes of photoresponsive materials possessing optimal properties for specific applications, such as improved thermal stability, photosensitivity, and wavelength response. Such materials are needed in the microelectronics, coatings, and reprographic industries, specifically for lithographic photoresists, photocurable coatings, stereolithographic media, sealants, printing inks and adhesives.
The anionic photoinitiation of selected substrates can be characterized by absorption and luminescence spectroscopies, real-time Fourier transform infrared spectroscopy, quantum yield measurements, flash photolysis, reactive-ion-etching, and scanning electron microscopy.
Anionic polymerization itself has been known, extensively described, and well categorized in the literature for years. Specifically, the conditions under which anionic polymerization occurs, and the conditions under which it is quenched, have been studied and documented. See for example, Principles of Polymerization, by George Odian, Second Edition, 1981, page 372-402; and The Encyclopedia of Polymer Science and Engineering, Volume 2, "Anionic Polymerization to Cationic Polymerization," John Wiley and Sons, N.Y., 1985, pages 1-42. The selection of appropriate reaction systems (solvents and inhibitors or traps) which promote, inhibit, or prevent anionic radical and other types of polymerizations are also well known.
In one embodiment of the invention, a method for the anionic photoinitiation of polymerization or crosslinking of a substrate is presented that includes the step of irradiating a mixture of a substrate and an inorganic transition metal complex, wherein the inorganic complex releases on irradiation a polymerization initiating substance consisting essentially of an anionically charged nucleophile that initiates the polymerization or crosslinking reaction, under conditions that allow the anion to initiate polymerization. This embodiment does not preclude the presence of radicals or other species in the reaction mixture, but only that the radicals or other species do not significantly initiate polymerization. One of ordinary skill in the art can easily determine which species is being released at a given wavelength, and which species is the polymerization initiating substance. For example, the release of anionic chlorine can be measured with a chlorine ion specific electrode or colorometrically by titration. The release of ethylenediamine can be measured for example by assessing the change in pH over time or by use of reagents that react with amines to produce fluorescent products that can be quantitated. If it is determined that either of these species, for example, is released under the conditions of polymerization, then addition of more of that species ought to have an effect on polymerization.
I. Selection of Inorganic Complex as Anionic Photoinitiator
A. Method of Selection of the Inorganic Complex as an Anionic Photoinitiator
An inorganic transition metal complex should be chosen for use as an anionic photoinitiator that has the following characteristics.
1) The inorganic transition metal complex must release a nucleophilic anion on irradiation. The ability of the complex to initiate anionic polymerization or crosslinking is a function of the nucleophilicity of the released anion and the reactivity of the monomer or other substrate. In general, the nucleophilicity of anions in aqueous or alcoholic solution decreases in the order: CN.sup.- >I-->NCS.sup.- >OH.sup.- >Br.sup.- >N.sub.3.sup.- >NO.sub.2.sup.- >Cl.sup.- >F.sup.-. The complex may also release .sup.- OR, wherein R is a straight or branched alkyl group, including but not limited to methyl, ethyl, propyl, butyl, and pentyl (linear and branched analogs). This order will change in nonhydroxylic solvents owing to differences in solvation energies.
Metal complexes that photochemically liberate hydroxide ion are particularly attractive, in light of the fact that this strong base is capable of initiating anionic polymerization or crosslinking of epoxides, as well as other moderately reactive species such as siloxanes. For example, addition of OH.sup.- to the oxirane ring produces a reactive anionic species that can then attack a second ring. Repetition of this process results in polymerization or crosslinking with high effective quantum efficiency.
The presence of the anionic species and the use of an anionic mechanism can be easily determined. Successful polymerization, in the presence of a known radical scavenger, such as hydroquinone or oxygen, clearly indicates that a radical mechanism is not involved. Further confirmation of the anionic mechanism is provided by attempts to polymerize the substrate in the presence of an anion scavenger, such as an acid.
2) The release of the anion should be the result of excitation of the inorganic transition metal complex by visible, near-infrared, or ultra-violet light. Light of wavelength between approximately 400 and 750 nm is visible. Light of wavelength between 750 and 1000 nm is considered near-infrared radiation. Light of wavelength between 200 and 400 nm is considered ultraviolet radiation.
Generally, the absorption process causes the transfer of an electron from a molecular orbital with bonding or nonbonding character to a molecular orbital with antibonding character with respect to the central metal-anion bond. In the typical case, the inorganic metal complex undergoes a ligand field or a ligand-to-metal charge transfer transition when irradiated with light of a specific wavelength. The wavelength at which the absorption takes place can be determined by analysis of the complex's ultraviolet, visible, and near-infrared spectrum. For example, ligand-field absorption maxima occur at 392 and 520 nm for trans-Cr(NH.sub.3).sub.2 (NCS).sub.4.sup.-, at 365, 414 and 487 nm for trans-Cr(en).sub.2 (NCS).sub.2.sup.+, and at 406 and 619 nm for trans-Co(en).sub.2 Cl.sub.2.sup.+ in aqueous solution.
The ligand field absorbance typically occurs at higher wavelength (lower energy) than the ligand to metal charge transfer band for the lighter transition metals (first and second rows). When transition metal complexes absorb energy in the ligand field region, they release ligands from the complex, but do not normally release free radical species. When transition metal complexes absorb energy in the ligand to metal charge transfer region, the complex releases a number of species, including possibly neutral species, anions, and free radicals. Given this basic knowledge that is elementary to one skilled in the art, appropriate reaction conditions and monomers can be selected to prevent radicals from and allow anions to initiate polymerization.
The ability to initiate useful chemistry when excited with long-wavelength light is a highly desirable feature of transition metal complexes. This can be used, for example, in photosensitive systems that respond to the output of inexpensive semiconductor-diode lasers.
3) The release of the anion from the transition metal complex should occur with high quantum efficiency, preferably 0.01 or larger. The term "quantum efficiency" refers to the ratio of the number of anions generated per photon absorbed by the complex. The numerator in this ratio, the moles of released anion, can be determined by several analytical techniques such as colorimetry, gravimetry, and specific-ion electrode measurements. The denominator of the quantum yield ratio, the moles of absorbed photons, is obtained by measuring the incident light intensity with a calibrated power meter or chemical actinometer such as ferrioxalate and then calculating the percentage of this radiation absorbed by the complex by use of Beer's Law.
Quantum efficiencies for photochemical release of anions from transition metal complexes vary depending upon the complex and reaction conditions. Irradiation of an acetonitrile solution of trans-Cr(NH.sub.3).sub.2 (NCS).sup.-.sub.4 with 465-nm light causes NCS.sup.- release with a quantum efficiency of 0.26. Photolysis of an aqueous solution of trans-Co(en).sub.2 Cl.sub.2.sup.+ with 488-nm light generates Cl.sup.- with a quantum efficiency of 0.0011. While quantum efficiencies of anion release near unity are desirable, values as low as 0.0001 may be acceptable in systems that incorporate chemical amplification. The effective quantum efficiency in a chemically-amplified system will be the product of the quantum efficiency of the photochemical step (eq. 2) and the average chain length or number of substrate units reacted per photogenerated initiator/catalyst species (eq. 3).
The number of substrate units undergoing polymerization or crosslinking can be obtained from gel permeation chromatography measurements of number and weight average molecular weights. Consumption of carbon-carbon double bonds in vinylic substrates can be quantitated by real time Fourier transform spectrometry.
EXAMPLE 1
Multiplicity of Response to Reineckate's Anion by Ethyl .alpha.-Cyanoacrylate
FIG. 3 is a plot of percentage polymerization vs. time of irradiation for samples of ethyl .alpha.-cyanoacrylate containing the following concentrations of Reineckate's anion: (.quadrature.) O M; (*) 2.2.times.10.sup.-4 M; (+) 5.4.times.10.sup.-4 M; (.box-solid.) 2.0.times.10.sup.-3 M. Samples were coated onto acid-treated silicon wafers and irradiated with 500 mW/cm.sup.2 of polychromatic (300-630 nm) light. Under the rather conservative assumption that each Reineckate's anion in the sample undergoes photochemical release of one NCS.sup.-, a polymerization chain length of >10.sup.4 was calculated from the data in FIG. 1 for the 2.2.times.10.sup.-4 M sample after irradiation for 30 seconds. This multiplicative response of ethyl .alpha.-cyanoacrylate to NCS.sup.- constitutes chemical amplification and accounts for the high photosensitivity of this system.
4) The inorganic metal complex should be soluble in the pure substrate or in a solvent that also dissolves the substrate. Solubility of the complex in nonaqueous solutions is necessary to enable formulation with a range of organic substrates such as epoxides and acrylates. A typical photoresist formulation used for photolithography consists of an organic substrate, a photoinitiator, and a casting solvent. This formulation is spin-coated onto a silicon wafer to form a thin film and the solvent is then removed by heating. Common casting solvents include 2-butanone, cyclohexanone, and propylene glycol methyl ether acetate. For polymerization reactions, solubility of the inorganic photoinitiator in the monomer obviates the need for a solvent.
5) The inorganic metal complex should be thermally stable for a reasonable length of time, to provide a suitable shelf life. For many applications, a shelf life of 3-6 months at room temperature is desirable. Transition metal complexes in which the central metal possesses a d.sup.3, low-spin d.sup.6, or low-spin d.sup.8 electronic configuration are especially resistant to thermal release of ligands. Other examples of thermally stable complexes include those with metals in high formal oxidation states such as Mo(CN).sub.8.sup.-4. Shelf life is improved by minimizing the exposure of the complex to heat or light. Photopolymerizable solutions of trans-Cr(NH.sub.3).sub.2 (NCS).sub.4.sup.- in ethyl .alpha.-cyanoacrylate remain usable for up to one month when stored in the dark at room temperature.
One approach for retarding the thermal substitution reactions of coordination complexes involves tethering the central metal with a macrocyclic ligand. For example, trans-Cr(cyclam)Cl.sub.2.sup.+ (cyclam is 1,4,8,11-tetraazacyclotetradecane) undergoes thermal release of Cl.sup.- .about.10.sup.3 times more slowly than trans-Cr(en).sub.2 Cl.sub.2.sup.+. While the quantum yield for photoinduced Cl.sup.- loss experiences a comparable reduction, this factor is easily compensated by employing a more intense light source (e.g. a laser rather than a conventional arc lamp).
B. Examples of Anionic Photoinitiators
Reineckate's Anion
Reineckate's anion, trans-[Cr(NH.sub.3).sub.2 (NCS).sub.4 ].sup.-, is a preferred transition metal complex for anionic photoinitiation. The anion dissolves readily in a variety of nonaqueous solvents, resists thermal substitution in nonhydroxylic media, and undergoes quantum efficient release of the nucleophile NCS.sup.- upon ligand-field excitation with near-ultraviolet/visible light at greater than 350 nm. Photochemical release of NH.sub.3 or radicals from the Reineckate anion only occurs at much shorter wavelengths.
The photogenerated thiocyanate anion will attack an electron deficient carbon to create a new anionic reactive center.
Trans-Cr(en).sub.2 (NCS).sub.2.sup.+, a cationic analogue of Reineckate's salt, undergoes photochemical release of NCS.sup.- under green light, and therefore can function as a photoinitiator for anionic polymerization. The complex is soluble in acetonitrile and acetone.
EXAMPLE 2
Anionic Polymerization of Ethyl .alpha.-Cyanoacrylate with Trans-Cr(en).sub.2 (NCS).sub.2.sup.+
A solution containing 95% by volume of ethyl .alpha.-cyanoacrylate, 5% by volume of acetonitrile, and 1.1.times.10.sup.-3 M trans-[Cr(en).sub.2 (NCS).sub.2 ]PF.sub.6 was exposed to 532-nm light from a Nd-YAG laser at an intensity of 2.9.times.10.sup.-6 einsteins/s. A solid plug of polymer formed in the path of the light beam after irradiation for 90 s.
Trans-[Cr(en).sub.2 Cl.sub.2 ]Cl can be prepared by the method described by G. Brauer in Handbook of Preparative Inorganic Chemistry, 2nd Ed., vol. 2, Academic Press: New York, 1965, p. 1357-1358. Simple metathesis with NH.sub.4 PF.sub.6 converts the complex to its PF.sub.6.sup.- salt. Irradiation into the first spin-allowed ligand field absorption band of trans-Cr(en).sub.2 Cl.sub.2.sup.+ is known to cause release of Cl.sup.- with a quantum efficiency of 0.32 in aqueous solution (see Canadian Journal of Chemistry, vol. 48, 1524, 1971). It has been discovered that Cl.sup.- is an effective initiator for the anionic polymerization of ethyl .alpha.-cyanoacrylate. Thus as little as 1.3.times.10.sup.-4 M Cl.sup.- causes 0.5 mL of ethyl .alpha.-cyanoacrylate to polymerize in less than 1 second. A 532-nm irradiation of a solution containing 95% by volume of ethyl .alpha.-cyanoacrylate, 5% by volume of acetonitrile as co-solvent, and 2.0.times.10.sup.2 M trans-[Cr(en).sub.2 Cl.sub.2 ]PF.sub.6 can be used to induce photoinitiated anionic polymerization of the acrylate monomer.
It has been discovered that Pt(acac).sub.2 at concentrations as low as 105 ppm and wavelengths slightly less than 300 nm to greater than 300 nm are effective in initiating anionic polymerization reactions. The photolysis time required for polymerization depends upon several variables, including Pt(acac).sub.2 concentration, light intensity and excitation wavelength.
The electronic structure and spectroscopy of Pt(acac)2 has been described in Inorg. Chem., 1993, 32, 1251-1258. It appears that irradiation of Pt(acac).sub.2 initially excites a ligand-localized .pi.--.pi.* transition rather than a ligand field or ligand-to metal charge transfer transition. The complex releases an anionic polymerization initiating species on irradiation, that is probably acac-.
For example, photolysis (.lambda.>300 nm) of a 1.07.times.10.sup.-4 M (42 ppm) Pt(acac).sub.2 methanolic solution for six minutes resulted in the loss of discernible bands due to Pt(acac).sub.2 and the formation of a single intense absorption centered at 272 nm. The ultraviolet.backslash.visible spectra of the material also indicated the formation of colloidal platinum. The shape and position of the absorption band at 272 nm, that was formed as a result of photolysis, are consistent with the UV/Vis spectrum of an authentic sample of 2,4-pentanedione in methanol. This indicates that the species responsible for initiating polymerization is the photo-liberated acetylacetonate anion.
EXAMPLE 3
Anionic Polymerization of Ethyl .alpha.-Cyanoacrylate with Pt(acac).sub.2
A solution containing 95% by volume of 2-cyanoethylacrylate, 5% by volume of acetonitrile, and varying concentrations Pt(acac).sub.2 ("PA") was exposed to light from a 200-watt high pressure mercury lamp. The time for polymerization of the 2-cyanoethylacrylate for the various concentrations of photoinitiator is shown in Table 1 below.
The anionic mechanism of these polymerizations was confirmed by carrying out the reaction with a known free radical scavenger, hydroquinone, and a known anion scavenger, methyl sulfonic acid. The photolysis time required to initiate 2-cyanoethylacrylate polymerization was unchanged in the presence of a large excess of hydroquinone. In contrast, polymerization was inhibited in samples when the concentration of an anion scavenger, methyl sulfonic acid, was increased to 100 ppm or greater.
As with the other anionic photoinitiators described herein, samples of 2-cyanoethylacrylate containing Pt(acac).sub.2 were stable in the dark. For this system, no apparent decomposition or polymerization occurred after 6 days. When the methylsulfonic acid concentration in 2-cyanoethylacrylate samples containing Pt(acac)2 was raised from 5 ppm to 40 ppm, samples were stable in the dark for at least 40 days without significant decrease in photosensitivity.
Cyclopentadienyl Metallo Complexes
It has also been discovered that iron and ruthenium cyclopentadienyl complexes can act as polymerization initiating species for anionic polymerization. The cyclopentadientyl groups can be unsubstituted, or one or both of the cyclopentadienyl groups can be independently substituted with one, two, or more substituents of the formula --C(O)R, wherein R is a C.sub.1 to C.sub.10 aliphatic group (alkyl, alkenyl, or alkynyl) or aryl. Typical wavelengths for photoinitiation using these complexes range from 290 to 500 nm. The optimal wavelength of irradiation for each complex can be determined by simple inspection of the ultraviolet/visible spectrum for the complex.
The photochemistry of complexes such as (.eta..sup.5 --C.sub.5 H.sub.5) (.eta..sup.5 --C.sub.5 H.sub.4 COR).sub.2 Fe (where R=C.sub.6 H.sub.5, H, CH.sub.3) and (.eta..sup.5 --C.sub.5 H.sub.4 COR).sub.2 Fe (where R=C.sub.6 H.sub.5) has been relatively well studied. Photolysis of these complexes, in solvents which contain trace impurities of water, results in the formation of (.pi.--C.sub.5 H.sub.5 Fe(solv).sub.n.sup.+ PhCO.sub.2.sup.- +C.sub.5 H.sub.4.sup.- +(.eta..sup.5 --C.sub.5 H.sub.5).sub.2 Fe (as a minor product). Either anionic species is capable of initiating anionic polymerization. FIG. 1 is a graph of the UV-visible spectrum of (.eta..sup.5 --C.sub.5 H.sub.4 COC.sub.6 H.sub.5).sub.2 Fe (2.92.times.10.sup.-4 M or 115 ppm, extinction coefficient 365=3,976) in acetonitrile. FIG. 2 is a graph of the UV-visible spectrum of (.eta..sup.5 --C.sub.5 H.sub.5).sub.2 Ru (2.77.times.10.sup.-3 M), extinction coefficient 365=264 M.sup.-1 cm.sup.-1).
It is generally accepted that the photolysis of ruthenocene, in relatively polar solvents, results in oxidation leading to the formation of the ruthenicenium ion and solvated electrons. The species responsible for initiating the anionic polymerization of 2-cyanoethylacrylate may be a photoejected solvated electron. Solvated electrons are capable of initiating anionic polymerization reactions.
EXAMPLE 4
Anionic Polymerization of Ethyl a-Cyanoacrylate with (.eta..sup.5 --C.sub.5 H.sub.5).sub.2 RU
Solutions containing 95% by volume of ethyl .alpha.-cyanoacrylate, 5% by volume of acetonitrile, and varying concentrations of (.eta..sup.5 --C.sub.5 H.sub.5).sub.2 Ru was exposed to light having a wavelength of greater than 300 nm from a 200-watt high pressure mercury lamp passed through Pyrex. The time for polymerization of the 2-cyanoethylacrylate for the various concentrations is shown in Table 3 below.
The anionic mechanism of the reaction was confirmed by conducting polymerizations in the presence of a known radical scavenger, hydroquinone, or a known anion scavenger, methylsulfonic acid. The photolysis time required to initiate 2-cyanoethylacrylate polymerization was relatively unaffected by the presence of a large excess of hydroquinone. In contrast, polymerization was completely inhibited in samples where the concentration of the anion scavenger, methyl sulfonic acid, had been increased to 296 ppm or greater.
Samples of 2-cyanoethylacrylate containing (.eta..sup.5 --C.sub.5 H.sub.5).sub.2 Ru were stable in the dark with no apparent decomposition or polymerization occurring for as long as 14 days.
EXAMPLE 5
Anionic Polymerization of Ethyl .alpha.-Cyanoacrylate with (.eta..sup.5 --C.sub.5 H.sub.5) (.eta..sup.5 --C.sub.5 H.sub.4 COR).sub.2 Fe (where R=C.sub.6 H.sub.5)
Solutions containing 95% by volume of ethyl .alpha.-cyanoacrylate, 5% by volume of acetonitrile, and varying concentrations of (.eta..sup.5 --C.sub.5 H.sub.5)(.eta..sup.5 --C.sub.5 H.sub.4 COR).sub.2 Fe (where R=C.sub.6 H.sub.5) was exposed to light having a wavelength of region .lambda.>320 nm. The time for polymerization of the 2-cyanoethylacrylate for the concentrations is shown in Table 5 below.
The anionic mechanism of the polymerization process was again confirmed by carrying out the reaction in the presence of the radical scavenger hydroquinone, and the anion scavenger methyl sulfonic acid. The photolysis time required to initiate 2-cyanoethylacrylate polymerization was unchanged in the presence of a large excess of hydroquinone. In contrast, polymerization was inhibited in samples where the concentration of the anion scavenger, methyl sulfonic acid, had been increased to 494 ppm or greater.
As with the other photoiniatiors, samples of 2-cyanoethylacrylate containing (.eta..sup.5 --C.sub.5 H.sub.5) (.eta..sup.5 --C.sub.5 H.sub.4 COR).sub.2 Fe (where R=C.sub.6 H.sub.5, H, CH.sub.3) or (.eta..sup.5 --C.sub.5 H.sub.4 COR).sub.2 Fe (where R=C.sub.6 H.sub.5) are stable in the dark with no apparent decomposition or polymerization occurring for as long as 14 days. In particular, a 2-cyanoethylacrylate sample containing 685 ppm of (.eta..sup.5 --C.sub.5 H.sub.5) (.eta..sup.5 --C.sub.5 H.sub.4 COR).sub.2 Fe (where R=C.sub.6 H.sub.5) was stable, in the dark for 20 days.
II. Examples of Substrates that can be Treated with the
Anionic Photoinitiator
Monomers, oligomers, and polymers that can be modified by anionic photoinitiation are those that are capable of reaction on attack by an anionically charged nucleophile, including but not limited to ethylene, 1,3-dienes, styrene and .alpha.-methyl styrene, acrylates and methacrylates, acrylonitrile, methacrylonitrile, acrylamide and methacrylamide, and aldehydes and ketones, and oligomers and polymers containing these moieties. Suitable substrates also include monomers, oligomers, and polymers that undergo anionic ring-opening polymerization or crosslinking reactions, for example, N-carboxy-.alpha.-amino anhydrides, cyclic amides, cyclic esters, epoxides and siloxanes.
Preferred monomers are ethylenically unsaturated monomers that contains electron-withdrawing substituents to stabilize the negative charge, for example, ethyl .alpha.-cyanoacrylate (see equation 5) and methyl .alpha.-trifluoromethylacrylate. ##STR1##
In general, an anionic photoinitiator is selected that will react with the substrate to be modified or polymerized. The more nucleophilic the anion released from the excited metal complex, the less electrophilic the substrate is required to be. For example, ethyl .alpha.-cyanoacrylate is quite reactive because the electron-withdrawing effect of the cyano group causes the .beta.-carbon to be highly electrophilic. Almost any anion will initiate polymerization of this monomer, including thiocyanate, bromide, and azide ion. Methyl .alpha.-trifluoromethylacrylate is also quite reactive because the .alpha.-trifluoromethyl group has a strong inductive effect. In contrast, ethylene does not contain an electron withdrawing group and thus polymerization of this monomer must be initiated by a strong nucleophile, such as n-butyl carbanion. N-carboxy-.alpha.-amino anhydrides, cyclic amides, cyclic esters, epoxides and siloxanes can be initiated with alkoxide or hydroxide ion.
Numerous polymer textbooks describe in detail whether monomers are active toward anionic, cationic, or radical polymerization, or a mixture thereof, and therefore this type information is known, or can be easily determined without undue experimentation using standard assays by one skilled in the art. One of the goals of this invention is to avoid free radical polymerization, because it is sensitive to atmospheric oxygen.
III. Anionic Photoinitiation Process
The photoinitiator can be dissolved in neat monomer (e.g. Reineckate's salt in ethyl .alpha.-cyanoacrylate) or in a solution of substrate and a co-solvent (e.g. trans-Cr(en).sub.2 (NCS).sub.2.sup.+ in 95% ethyl .alpha.-cyanoacrylate and 5% acetonitrile).
The anionic process can be carried out by either dissolving the photoinitiator in neat monomer or in a solution of substrate and a co-solvent. If a co-solvent is employed, it should not undergo proton transfer equilibria, since this will provide a pathway for scavenging anion species active in initiating and propagating polymerization. Water and aqueous acids are classic examples of solvents that undergo proton transfer equilibria. Water has an especially negative effect on anionic polymerization, since it is an active chain transfer agent. Examples of preferred solvents are diethyl ether, tetrahydrofuran, and acetonitrile. It is typically desired, but not required, that the complex have a solubility of at least 1.times.10.sup.4 M in the cosolvent.
The anionic photoinitiation reaction can be carried out at any temperature that provides the desired results. A temperature of between 20.degree.-30.degree. C. is suitable in many cases, since higher temperatures favor thermal release of anions and lower temperatures may cause solubility problems.
Any amount of photoinitiator can be used that suitably initiates the desired reaction. An amount of photoinitiator in the formulation ranging from parts per million to part per hundred is typically suitable depending upon the system and desired applications.
Anionic photoinitiation is retarded in the presence of acids that neutralize the anion, or nucleophile. Certain unsaturated monomers used in chain polymerization reactions contain compounds that act as radical or basic scavengers, that are in fact acids and that can interfere with the anionic polymerization reaction.
On initiation of an anionic polymerization process, a large number of monomer anions are formed that react with other monomers to form polymers. If a small number of acidic groups are present in the polymerizing solution, for example, in the form of a stabilizer or comonomer, those acidic groups will quench an equivalent number of propagating monomer anions. The remaining anions will continue to react with other monomers to form polymers. Based on the amount of acidic groups present, the anionic reaction will either be retarded or quenched completely. When a solvent is used that contains an active hydrogen, such as water or acid, since the solvent is almost always present in a molar quantity that exceeds, and usually greatly exceeds, the molar quantity of the anions in solution, the anionic polymerization reaction cannot occur because all anions formed are immediately quenched.
The material with the anionic photoinitiator should be maintained in the absence of radiation of the wavelength that will initiate reaction, until reaction is desired.
The method is described below for convenience with reference to the reaction of ethyl .alpha.-cyanoacrylate with Reineckate's anion. However, it should be understood that the present invention is not limited to these examples but includes all of the embodiments described above.
EXAMPLE 6
Anionic Photoinitiation of .alpha.-Cyanoacrylate by Reineckate's Anion
Neat ethyl .alpha.-cyanoacrylate (99.88% purity from Loctite Corporation) is a colorless liquid with a viscosity of 2.8 cP at 22.degree. C. The sample employed in this study contained scavengers for adventitious radical and basic impurities. Commercially available ammonium salt of Reineckate's anion (Alfa) was converted to the potassium salt (K.sup.+ R.sup.-). Solutions of ethyl .alpha.-cyanoacrylate containing K.sup.+ R.sup.- (0.19-2.7.times.10.sup.-3 M) undergo no change in viscosity when kept in the dark for one week at room temperature. In contrast, mixing one drop of a 5.2.times.10.sup.-3 M solution of K.sup.+ NCS.sup.- in acetonitrile with 0.5 mL of ethyl .alpha.-cyanoacrylate causes immediate (<1 s) solidification accompanied by considerable evolution of heat. This dramatic response establishes NCS.sup.- as an effective initiator for the polymerization of ethyl .alpha.-cyanoacrylate.
The electronic absorption spectrum of K.sup.+ R.sup.- dissolved in ethyl .alpha.-cyanoacrylate exhibits bands at 400 nm (.epsilon.=89 M.sup.-1 cm.sup.-1) and 528 nm (.epsilon.=114 M.sup.-1 cm.sup.-1) arising from spin-allowed ligand field transitions. Selective excitation (532 or 546 nm) of the lower-energy transition causes the solution to thicken and eventually solidify. This behavior is the direct consequence of the photochemical release of NCS.sup.- which, as noted above, functions as an effective initiator for polymerization. The key role played by anionic species is underscored by the observation that increased levels of base scavenger (a protonic acid) in the monomer sample inhibits polymerization. This effect is attributed to the ability of the protonic acid to scavenge photogenerated NCS.sup.- and/or anionic sites on the growing polymer chain.
EXAMPLE 7
The Effect of Concentration of Anionic Photoinitiator and Incident Light Intensity on Rate of Polymerization
Ethyl .alpha.-cyanoacrylate (2 mL) containing various concentrations of K.sup.+ R.sup.- were irradiated (with stirring in runs a-c) in a 1-cm rectangular Pyrex cell, as described in Table 7. No attempt was made to exclude air from the sample. The dependence of photoinitiated polymerization on the K.sup.+ R.sup.- concentration and the incident light intensity is provided in Table 7. At constant intensity, polymerization proceeds more rapidly at higher complex concentration (compare runs a and c). Such behavior reflects the greater fraction of light absorbed by the more concentrated sample and the correspondingly higher photochemical rate of NCS.sup.- release. An analogous explanation accounts for the faster polymerization observed upon increasing light intensity at constant K.sup.+ R.sup.- concentration (compare runs a and b).
EXAMPLE 8
Effect of a Free Radical Trap, Hydroquinone, on the Photoinitiated Anionic polymerization of Ethyl Cyanoacrylate using Reineckate's Anion
KCr(NH.sub.3).sub.2 (NCS).sub.4 (0.0092 grams) was weighed out and dissolved in 10 mls of ethyl .alpha.-cyanoacrylate yielding a solution that was 2.573.times.10.sup.-3 M (920 ppm) KCr(NH.sub.3).sub.2 (NCS).sub.4. This solution was allowed to stir for 60 minutes, in the dark, prior to any photolysis experiments. Subsequently, 3 mls of the solution was transferred to a Pyrex test tube equipped with a stir bar. The sample was then photolyzed with the 546 nm filtered output from a 200 W high pressure mercury lamp. The sample polymerized after 446 seconds of irradiation.
An additional 3 ml sample of the stock solution was transferred to a Pyrex test tube similarly equipped with a stir bar. However, to this sample was added 7 mg of the well-known free radical trap, hydroquinone. That now made this sample 2.573.times.10.sup.-3 M or 920 ppm in KCr(NH.sub.3).sub.2 (NCS).sub.4 and 2.12.times.10.sup.-2 M or 2,333 ppm in hydroquinone. The 2,333 ppm hydroquinone concentration does not take into account the 1000 ppm of hydroquinone present in ethyl .alpha.-cyanoacrylate as purchased. This sample was then allowed to stir for 40 minutes prior to photolysis. This sample was then photolyzed with the identical set up as the previous sample. The ethyl .alpha.-cyanoacrylate polymerized after 388 seconds of irradiation. The hydroquinone clearly had no detrimental effects on the polymerization.
EXAMPLE 9
Effect of a Free Radical Scavenger, Oxygen, on the Photoinitiated Anionic Polymerization of Ethyl .alpha.-Cyanoacrylate using Reineckate's Anion
KCr(NH.sub.3).sub.2 (NCS).sub.4 (0.0082 g) was weighed out and dissolved in 10 mls of ethyl .alpha.-cyanoacrylate yielding a solution that was 2.294.times.10.sup.-3 M or 820 ppm in KCr(NH.sub.3).sub.2 (NCS).sub.4. This solution was allowed to stir for 60 minutes prior to any photolysis experiments.
After stirring for 60 minutes, 3 mls of the stock solution was transferred to a Pyrex test tube equipped with a stir bar. This first sample was not bubbled with any gas and no effort was made to exclude oxygen from the system. The sample was then photolyzed with the 546 nm filtered output from a 200 W high pressure mercury lamp. After 358 seconds of irradiation, the ethyl .alpha.-cyanoacrylate had polymerized.
A second 3 ml sample of the initial solution was transferred to a new Pyrex test tube and a stir bar was added. The test tube was then capped with a rubber septum. Two needles were then forced through the rubber septum. One long needle was for bubbling the solution with oxygen and one short needle was for venting the excess gas. The solution was bubbled for ten minutes and then the short needle was removed first and then the long needle, leaving a static atmosphere of oxygen in the test tube. This sample was then photolyzed using the identical set up just described. The ethyl .alpha.-cyanoacrylate polymerized after 398 seconds of irradiation.
A third sample was prepared with 3 mls of the initial solution and a stir bar. The rubber septum was again placed on the test tube and the two needles were inserted. However, in this case, the bubbling gas was 99.999% pure Argon. The sample was bubbled for 10 minutes and then the needles were removed. This sample was then photolyzed, with the identical set up previously described. The ethyl .alpha.-cyanoacrylate polymerized after 321 seconds of irradiation.
Within our experimental error, the percent of free radical scavenging oxygen present had no effect on the rate of polymerizing ethyl .alpha.-cyanoacrylate. The results of the two sets of experiments just described are clearly not consistent with a free radical process being responsible for the polymerization.
EXAMPLE 10
Kinetic Characterization of Anionic Photoinitiation
A more detailed kinetic characterization of the photoinitiated polymerization process of ethyl .alpha.-cyanoacrylate using Reineckate's anion was obtained by real-time Fourier-transform infrared spectroscopy. This relatively new technique allows continuous monitoring (up to 204 infrared spectra collected per minute) of the sample during irradiation. The extent of polymerization is directly related to the decrease in absorbance of the C=C stretching band of ethyl .alpha.-cyanoacrylate at 1616 cm.sup.-1. This relationship is expressed in eq. 6, where A.sub.0 denotes the initial (dark) area of the band and A.sub.t is the area after t ##EQU1## seconds of irradiation.
FIG. 3 is a plot of percentage polymerization vs. time of irradiation for samples of ethyl .alpha.-cyanoacrylate containing the following concentrations of Reineckate's anion: (.quadrature.) O M; (*) 2.2.times.10.sup.-4 M; (+) 5.4.times.10.sup.-4 M; (.box-solid.) 2.0.times.10.sup.-3 M. Samples were coated onto acid-treated silicon wafers and irradiated with 500 mW/cm.sup.2 of polychromatic (300-630 nm) light.
The data shown in FIG. 1 agree with earlier observations (Table 7) that polymerization occurs more rapidly in samples containing higher K.sup.+ R.sup.- concentrations. The rate of photoinitiated polymerization, R.sub.p, can be calculated from eq. 7, where A.sub.t1 and A.sub.t2 represent the areas under the 1616 cm.sup.-1 band at irradiation times t1 and t2, and M is the molar concentration of vinyl groups in ethyl .alpha.-cyanoacrylate. Maximum rates of 3.0, 1.3, and 0.60 M.multidot.s.sup.-1 result for ethyl .alpha.-cyanoacrylate samples containing 2.0.times.10.sup.-3, 5.4.times.10.sup.-4, and 2.2.times.10.sup.-4 M concentrations of K.sup.+ R.sup.-, respectively. ##EQU2##
This data demonstrates that visible-light irradiation of trans-[Cr(NH.sub.3).sub.2 (NCS).sub.4 ].sup.- dissolved in ethyl .alpha.-cyanoacrylate initiates anionic polymerization. The initiation step involves addition of photoreleased NCS.sup.- to the carbon-carbon double bond of the acrylate monomer.
This invention has been described with reference to its preferred embodiments. Variations and modifications of the invention, method for anionic polymerization, will be obvious to those skilled in the art from the foregoing detailed description of the invention. It is intended that all of these variations and modifications be included within the scope of the appended claims.
Claims
Certificate of Correction present
The claims shown below may not include correction changes. Use the corrected PDF for authoritative text.
We claim:
1. A method for polymerizing a monomer, or crosslinking or polymerizing an oligomer or crosslinking a polymer by anionic photoinitiation comprising irradiating a mixture of the monomer, oligomer, or polymer, which is selected from the group consisting of ethylene, 1,3-diene, styrene, .alpha.-methylstyrene, acrylate ester, methacrylate ester, acrylonitrile, methacrylonitrile, acrylamide, methacrylamide, aldehydes, ketones, N-carboxy-.alpha.-amino anhydrides, cyclic amides, cyclic esters, epoxides, and siloxanes, and an inorganic transition metal complex Pt(acac).sub.2, under irradiation conditions wherein the inorganic complex photochemically reacts to release an anionically charged nucleophile and said anionically charged nucleophile initiates a polymerization reaction of said monomer, or a crosslinking or polymerization reaction of said oligomer, or a crosslinking reaction of said polymer.
2. The method of claim 1, wherein the monomer, oligomer, or polymer is selected from the group consisting of ethylene, 1,3-diene, styrene, .alpha.-methyl styrene, acrylate ester, methacrylate ester, acrylonitrile, methacrylonitrile, acrylamide, methacrylamide, aldehydes, ketones and oligomers or polymers of said monomers.
3. The method of claim 1, wherein the monomer, oligomer, or polymer is selected from the group consisting of N-carboxy-.alpha.-amino anhydrides, cyclic amides, cyclic esters, epoxides, siloxanes and oligomers or polymers of said monomers.
4. The method of claim 1, wherein said acrylate ester monomer is 2-cyanoethylacrylate.
5. The method of claim 1, wherein a polymer or oligomer is crosslinked by said photoinitiation.
6. The method of claim 1, wherein an oligomer or monomer is polymerized by said photoinitiation.
7. The method of claim 1, wherein said polymerization or crosslinking occurs at a temperature between 20.degree. and 30.degree. C.
8. The method of claim 1, wherein the radiation is near-ultraviolet or visible light.
9. The method of claim 1, wherein the inorganic complex is thermally stable.
10. The method of claim 1, wherein the irradiation causes a ligand field or ligand-to-metal charge transfer transition in the inorganic complex.
11. The method of claim 1, further comprising forming the crosslinked or polymerized monomer, oligomer, or polymer into a material selected from the group consisting of lithographic photoresists, stereolithographic media, photocurable coatings, adhesives, sealants and printing inks.
Patent Citations (11)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3794497 | 1974-02-01 | Pratt et al. | |
| US4094852 | 1978-06-01 | Sundermann et al. | |
| US4130426 | 1978-12-01 | Takeda et al. | |
| US4184874 | 1980-01-01 | Takeda | |
| US4675270 | 1987-06-01 | Woods et al. | |
| US4857654 | 1989-08-01 | Reidiker et al. | |
| US4963300 | 1990-10-01 | Meier et al. | |
| US4992572 | 1991-02-01 | Desobry et al. | |
| US5091439 | 1992-02-01 | Berner et al. | |
| US5143785 | 1992-09-01 | Pujol et al. | |
| US5215860 | 1993-06-01 | McCormick |
Non-Patent Literature (18)
- Aslam, et al., "Photopolymerization of Vinyl Monomer Initiated by Diacidobis (Ethylenediamine) Cobalt (III) Complexes," Polymer Photochemistry, vol. 5, (1984) pp. 41-48.
- Delzenne, G.A., et al., "Photopolymerization of Vinyl Monomers Initiated by Pentaaminecobalt (III) Complexes," J. Polymer science, No. 16, pp. 1027-1036 (1967).
- Fukuchi, Y., et al. "Photointiated Anionic Coordination Polymerization of Epoxides, a Novel Polymerization Process," Macromolecules vol. 20; pp. 2316-2317 (1987).
- Fukuchi, Y., et al., "Thermo-Initiated Anionic Polymerization of Expoxides Using the Titanium Tetraisopropoxide and Protected Aryl Alcohol System," J. Polymer Science, 1988, vol. 25; pp. 269-272.
- Fukuchi, Y.; et al., "Polymerization of Epoxides Catalyzed by the Titanium Tetraisoporpoxide/Phenol System and its Mechanism," J. Polymer Science, 1988, vol. 26, pp. 401-403.
- Kimura, K., et al., "Photocurable Arcylic Adhesives," Chem. Abstracts,107:24498x .
- Korshak, V.V., "Photoinitation of Polymerization of Ethyl .alpha.-cyacoacrylate," Chem. Abstracts, 100:7215r
- Kutal, et al., "New Inorganic Photoinitiators for Deep-UV Resist Material," Journal of Coating Technology, vol. 62, No. 786 (1990) pp. 63-67.
- Kutal, et al., "Novel Base-Generating Photoinitiators for Deep-UV Lithography," SPIE--The International Society for Optical Engineering,vol. 1466 (1991) pp. 362-367.
- Kutal, et al., "Photoinitiated Cross-Linking and Image Formation in Thin Polymer Films Containing a Transition Metal Compound," Journal of the Electrochemical Society, vol. 134, No. 9(1987) pp. 2280-2285.
- Lewis, F.D., et al., "Electronic Structure and Spectroscopy of Nickel(II), Palladium(II); and Platinum(II), Acetylacetonate Complexes," Inorg. Chem., vol. 32, pp. 1251-1258 (1993).
- Nataraian, L.V., et al., "Polymerization of Acrylamide and Methacrylamide by Azidopentamminecobalt (III) Chloride," J. Polymer Science,vol.6, 3245-3257 (1968).
- Polyakova; A.M., "Effect of Impurities on the Photochemical Polymerization of Ethyl .alpha.-Cyanoacrylate," Chem. Abstracts, 106:33490v.
- Said-Galiev, E.E., et al., "Temperature Dependence of the Photopolymerization Rate of Ethyl .alpha.-Cyanacrylate," Chem. Abstracts, 100:34900s.
- Uchida, Y. et al., "Photoinitiated Anionic Coordination Polymerization of Epoxides, a Novel Polymerization Process," Macromolecules, 1987, vol. 20, pp. 2316-2317.
- Principles of Polymerization by George Odian, 2nd Ed. (1991) pp. 372-402.
- "Anionic Polymerization to Cationic Polymerization," The Encyclopedia of Polymer Science and Engineering,John Wiley & Sons, New York, (1985) vol. 2; pp. 1-42.
- Curtis, H., et al., "Organometallic Photoinitiated Polymerisations".