US 5,633,522 AGrant
CMOS Transistor With Two-Layer Inverse-T Tungsten Gate
Issue Date:1997-05-27
•12 Claims
•2 Drawing Sheets
Abstract
The present invention is directed to a unique silicon based MOS transistor having an inverse-T refractory metal gate structure. The gate fabricated according to this invention comprises a main CVD tungsten portion and a lower sputtered tungsten portion outwardly extending from the bottom of the CVD portion such that a cross section of the gate appears as an inverted "T". A Cl.sub.2 /O.sub.2 plasma etch is used to etch the CVD tungsten layer and a chemical etch is used to etch the sputtered tungsten layer to form the gate electrode. It has been discovered that sputtered tungsten is more resistant to Cl.sub.2 /O.sub.2 reactive ion etch than is CVD tungsten. The sputtered tungsten layer acts as a shield to protect the underlying gate oxide layer from ion damage throughout the fabrication process.
Metadata
Assignee
- International Business Machines Corporation
Inventors
- Fernand Dorleans
- Liang-Choo Hsia
- Louis L. C. Hsu
- Gerald R. Larsen
- Geraldine C. Schwartz
Application Information
Application Number:US 6484573
Filing Date:1996-05-15
Priority Date:1992-06-18
Art Unit:253
Classifications
IPC:
H01L 2976H01L 2994H01L 31062H01L 31113
Field of Search:
257768;764;760;770;344;382;384;388;412
Patent Drawings (2 sheets)
Description
Background of the Invention
1. Field of the Invention
The present invention generally relates to an improved method for fabricating MOS transistor gates and, more particularly, to a fabrication method for inverse-T type tungsten gate structures by reactive ion etch (RIE).
2. Description of the Prior Art
As will be appreciated by those skilled in the art, an inverse-T MOS transistor gate structure appears in cross section as an inverted "T". An article by Huang et al. entitled "A Novel Submicron LDD Transistor with Inverse-T Gate Structure," IEDM Tech Dig., 1986, pp. 742-745, which is herein incorporated by reference, discloses a typical lightly doped drain (LDD) transistor structure having an inverse-T gate structure made of polysilicon. In an inverse-T gate structure a portion of the gate extends beneath oxide sidewall spacers which surround and insulate the gate structure. Huang disclosed extending a portion of the gate beneath the oxide sidewall spacers improves transistor performance by providing better gate controllability.
Polysilicon inverse-T gates are widely used and are fabricated with methods well established in the art. Briefly, in these methods, a polysilicon film, from which the gate is to be formed, is deposited over a gate silicon oxide layer. The polysilicon is subjected to a reactive ion etch (RIE) which partially removes the polysilicon material adjacent a defined gate region. The etching process is stopped arbitrarily by timed etch so that a thin layer polysilicon of about 50-100 nanometers remains on the lower portion of the gate. Source and drain doping is accomplished by ion implantation directly through the thin polysilicon portion. Sidewall spacers, which act as a mask for additional source and drain implantation and etching steps, are formed around the gate by chemical vapor deposition (CVD). After the RIE and ion implantation steps the gate oxide layer is damaged. Therefore, it is necessary regrow the gate oxide layer to repair it. An additional problem with this approach is that the thickness of the remaining polysilicon is dependent on the etch process control.
Technology has steadily been moving to smaller transistor devices having superior performance characteristics. Polysilicon is the most commonly used material to fabricate MOS gate structures. Unfortunately, polysilicon possesses inherent material limitations which makes it unsuitable for submicron VLSI gate electrode applications. The resistances of polysilicon and silicided polysilicon gates are relatively high at 60 .OMEGA./square and 20 .OMEGA./square, respectively. The resistances of these gates become even higher as size is scaled down. In addition, it is difficult for buried channel MOSFETs to suppress their short channel effects when a polysilicon gate is used.
Naoki Kasai et al., Deep-Submicron Tungsten Gate CMOS Technology, IEDM Tech. Dig., 1988, discusses metal gate technology and, more particularly, focuses on the advantages of tungsten in VLSI gate electrode applications. Tungsten gates possess a resistance of less than 5 .OMEGA./square. Devices having tungsten gates have a 30% transconductance increase and have a low sub-threshold slope value which is responsible for a large on/off ratio.
In addition, tungsten is an ideal metal for CMOS transistor gates because it's work function is coincidentally near silicon's mid-bandgaps. This provides symmetrical operation for n- and p-channel devices with equal threshold values. See C. Y. Ting et al., Gate Materials Consideration for Submicron CMOS, Applied Surface Science, 38 (1989) pp. 416-428.
Although tungsten seems an ideal material for MOS gate electrodes, it is not without it's problems. Due to radical differences between tungsten and silicon processing requirements, no process exists which easily allows tungsten gates to be fabricated together with silicon MOS transistors. The most serious problem with tungsten is it forms volatile oxide at low temperature. As mentioned above, during the transistor fabrication process inherent damage occurs to the gate silicon oxide layer which necessitates regrowth. This is typically accomplished by oxidizing the silicon at temperatures of 900.degree.-1000.degree. C. in oxygen ambient for a period of time. Since, tungsten forms volatile oxides at only 300.degree. C., it is clear that a serious conflict exists.
To overcome this problem, N. Kobayashi et al., Highly Reliable Tungsten Gate Technology, Materials Research Society, 1987, proposes a wet hydrogen oxidation method wherein he suggests that he is able to oxidize the silicon without oxidizing the tungsten. The method involves using hydrogen with the appropriate amount of water along with a thin film if polysilicon, sandwiched between a tungsten gate and a gate oxide layer. This process is complicated and still requires polysilicon as an adhesive layer between the tungsten and the silicon oxide.
Summary of the Invention
It is therefore an object of the present invention to provide method for fabricating a silicon based MOS transistor having a refractory metal gate.
It is another object of the present invention to provide an inverse-T tungsten gate for a MOS transistor which is fabricated from a first layer of relatively high density refractory metal and a second layer of relatively low density refractory metal.
It is yet another object of the present invention to provide a transistor having shallow source/drain junctions.
The present invention is directed to a unique method for fabricating a silicon based MOS transistor having an inverse-T tungsten gate structure. The fabrication method involves depositing a relatively dense layer of refractory metal, for example, chemical vapor deposition (CVD) tungsten, on top of a thinner layer of less dense refractory metal, such as sputter deposition tungsten which, promotes adherence to a gate oxide layer grown on a silicon substrate.
A nitrite mask defines a gate region on the top, CVD tungsten layer. A Cl.sub.2 /O.sub.2 plasma etch is used to etch the top CVD tungsten layer using the nitrite mask. The etching process is slowed down when reaching sputtered tungsten layer.
It has been discovered that Cl.sub.2 /O.sub.2 plasma reactive ion etch removes CVD tungsten approximately three times faster than the sputtered tungsten. The sputtered tungsten is therefore more resistant to the Cl.sub.2 /O.sub.2 reactive ion etch than is the CVD tungsten. Thus, the sputtered tungsten layer acts as a shield to protect the underlying oxide layer from ion damage; therefore, the gate oxide integrity can be maintained and does not require regrowth.
Ion implantation of the source and drain junctions is performed directly into the sputtered tungsten layer prior to forming a gate sidewall spacer. The sidewall spacer is formed around the CVD tungsten gate portion. A sidewall annealing step is performed which also serves to the drive dopant ions into the silicon substrate to formulate shallow source/drain junctions.
The sputtered tungsten layer extending beyond the sidewall spacer is then removed using a mildly basic chemical etching solution.
The thusly fabricated tungsten gate comprises a main CVD tungsten portion and a lower sputtered tungsten portion outwardly extending from the bottom of the CVD portion such that a cross section of the tungsten gate appears as an inverted "T". The silicon oxide layer remains undamaged throughout the fabrication process.
Brief Description of the Drawings
The foregoing and other objects, aspects and advantages will be better understood from the following detailed description of a preferred embodiment of the invention with reference to the drawings, in which:
FIG. 1 is a view of various layers on a silicon substrate prior to etching an inverse-T tungsten gate;
FIG. 2 is a view of FIG. 1 showing a nitrate layer which defines the top of the tungsten gate;
FIG. 3 is a view of FIG. 2 after plasma etching the CVD tungsten layer;
FIG. 4 is view of the source/drain ion implant step;
FIG. 5 is a view showing a sidewall spacer surrounding the tungsten gate electrode;
FIG. 6 is a view showing the remaining sputtered tungsten after excess was removed with a chemical etching solution;
FIG. 7 is a view of the finished MOS transistor having an inverse-T tungsten gate.
Detailed Description of a Preferred Embodiment of the Invention
Referring now to the drawings, and more particularly to FIG. 1, a gate oxide layer 10 which has been grown on a silicon substrate 12, supports tungsten layers 14 and 16, which comprise the gate electrode of a finished MOS transistor.
There are three common methods by which tungsten layers may be deposited: chemical vapor deposition (CVD), evaporation and sputtering. CVD tungsten films have high purity and low resistivity; however they are large grained films and do not adhere well to silicon oxide. Evaporated tungsten films have a fine grain structure; however they have high electrical resistance and high stress and exhibit poor adhesion to silicon oxide. Sputtered tungsten films have a fine grain structure, low electrical resistivity and an adjustable stress level for good silicon oxide adhesion. See C. Y. Ting et al., cited above.
Tungsten layer 16 is deposited on gate oxide layer 10 a suitable sputter deposition method. Sputter deposition methods are well known in the art and are generally performed in a high vacuum deposition system. A tungsten target material is bombarded by ions. Tungsten atoms are released from the tungsten target and deposit to form a thin tungsten film over the gate oxide layer 10. In the preferred embodiment the sputtered tungsten layer 16 is approximately 800 .ANG. thick.
A second tungsten layer 14 is deposited by CVD techniques on top of the sputtered tungsten layer 16. CVD techniques are well known in the art and entail passing a vapor containing tungsten atoms over the silicon substrate 12 in a suitable CVD apparatus such that a tungsten film is formed. In the preferred embodiment, the CVD tungsten layer 14 is approximately 3500 .ANG. thick.
A nitride mask 18 is deposited over the CVD tungsten layer 14 using plasma enhanced chemical vapor deposition or photo enhancement (PECVD) techniques. PECVD techniques are also well known in the art. PECVD techniques take advantage of laser or UV light and allow deposition at lower temperatures.
A resist mask 20 is applied over the nitride mask 18 and is patterned to define a gate electrode. The nitride layer 18 is etched in a CF.sub.4 plasma etch to form a nitride mask 18A. At this point the resist is stripped.
Referring now to FIG. 2, the nitride mask 18A now defines placement and pattern the gate electrode. A Cl.sub.2 /O.sub.2 plasma etch process is used to etch the CVD tungsten layer 14 which are not protectedby the nitrite mask 18A. In the preferred embodiment, the Cl.sub.2 /O.sub.2 etch takes place in a single plasma etch reactor which typically consists of pressurized chamber, a vacuum supply, an rf power supply connected to an electrode and a grounded electrode. In the preferred embodiment the chamber pressure is 100 mTorr, the oxygen flow rate is 12 sccm, the chlorine flow rate is 40 sccm, the rf power is 625 Watts and the electrode spacing is kept at 8 cm. Under these conditions, the etch rate of CVD tungsten is approximately 5000 .ANG./min and the etch rate of sputtered tungsten is significantly less at only 1700 .ANG./min. This shows about a 3:1 difference between CVD tungsten and sputtered tungsten films. The sputtered tungsten shows greater resistivity to the Cl.sub.2 /O.sub.2 reactive ion etch processes than does the CVD tungsten. The sputtered tungsten acts as a shield for the underlying oxide layer to protect it from ion damage throughout the fabrication process. With this process, the etch ratio of CVD tungsten to mask nitride is more than 10:1.
FIG. 3 shows a top portion of tungsten gate electrode 14A after the Cl.sub.2 /O.sub.2 plasm etch. An over-etch of about 30% into the sputtered tungsten layer 16 is needed to compensate for tungsten film non-uniformity and surface topographyto ensure that all CVD tungsten not protected by the nitrite mask 18A is removed. The gate oxide layer 10 is completely covered and protected by the sputtered tungsten layer 16 throughout the etching process. It is estimated that the thickness of the remaining sputtered tungsten 16 is about 500.+-.50 .ANG., which is thick enough to effectively shield the oxide layer 10 from reactive ion damage.
FIG. 4 shows the source/drain implant which is performed directly into the remaining sputtered tungsten layer 16. Dopant ions 22 are implanted into the sputtered tungsten 16. The power of the of the ion implant is regulated such that dopant ions do not penetrate and reach active areas of the gate oxide layer 10 wherein they would cause harm.
FIG. 5 shows a sidewall spacer 24 formed around the CVD tungsten gate electrode 14A and extending laterally over a portion of the sputtered tungsten layer 16. The sidewall spacer 24 is made by directional etch back of a suitable CVD dielectric film, such as oxide, nitride, or CVD TEOS (tetraethyl orthosilicate), to leave the film on the sidewalls of the gate electrode. Concurrent with a sidewall spacer 24 annealing step, the source 26 and drain 28 regions are formed as the dopants 22 implanted into the sputtered tungsten layer 16 in the source and drain regions diffuse through the gate oxide layer 10 and into the silicon substrate 12. Since the gate oxide layer 10 beneath the gate region is completely protected bysputtered tungsten layer 16 throughout this process, neither RIE nor ion implant damage is incurred. Subsequently, oxide regrowth, which would otherwise damage the tungsten gate, is avoided.
Referring now to FIG. 6, portions of the sputtered tungsten layer 16 which are not covered by the sidewall spacer 24 are selectively etched away leaving portion 16A using a buffered, mildly basic chemical etching solution such as, for example, KH.sub.2 PO.sub.4 /KOH/K.sub.3 Fe(CN).sub.6. This solution will not attack the spacer oxide or the gate oxide material. Such solutions suitable for the practice of the present invention are known in the art and are discussed in T. S. Shakoff et al., High Resolution Tungsten Patterning Using Buffered, Mildly Basic Etching Solutions, J. Electrochem. Soc., Vol. 122, February, 1975, which is herein incorporated by reference.
FIG. 7 shows the finished MOS transistor. The gate oxide layer 10 in the source 26 and drain 28 areas is removed using a hydrofluoric acid (BHF) solution. A CVD oxide is deposited and etched back to form a second sidewall spacer 30 on the gate electrode sidewalls. This is preferably done in a multi-chamber cluster dep/etch tool. The second spacer is used to prevent the gate from shorting with the source 26 and drain 28. Silicide, 34 and 32, is formed on top of the exposed source 26 and drain 28 on the silicon surface 12. An additional dopant implantation step and subsequent drive-in step may be preformed directly into the silicide 32 and 34 in order to reduce contact and series resistance.
While the invention has been described in terms of a single preferred embodiment, those skilled in the art will recognize that the invention can be practiced with modification within the spirit and scope of the appended claims. For example, refractory metals other than tungsten, may be used in the practice of the present invention. Molybdenum is an example of such a refractory metal.
Claims
Having thus described my invention, what we claim as new and desire to secure by Letters Patent is as follows:
1. An MOS transistor with an inverted-T refractory metal gate, comprising in combination: a semiconductor substrate; a gate insulating layer on said semiconductor substrate; a first refractory metal layer formed on said insulating gate layer comprising a material formed to have a low density relative to the density of a second refractory metal layer; said second refractory metal layer formed on said first refractory metal layer comprising said material formed to have a high density relative to said low density of said first refractory metal layer; said first refractory metal layer extending laterally beyond said second refractory metal layer; and a source and drain region in said semiconductor substrate extending under said first refractory metal layer, wherein said first refractory metal layer and said second refractory metal layer comprise a same material.
2. An MOS transistor with an inverted-T refractory metal gate as in claim 1, wherein said first refractory metal layer is formed by sputtering molybdenum onto said gate insulating layer and said second refractory metal layer is formed by chemical vapor deposition of molybdenum onto said first refractory metal layer.
3. An MOS transistor with an inverted-T refractory metal gate as in claim 1, wherein said first refractory metal layer is formed by sputtering tungsten onto said gate insulating layer and said second refractory metal layer is formed by chemical vapor deposition of tungsten onto said first refractory metal layer.
4. An MOS transistor with an inverted-T refractory metal gate as in claim 1, wherein said first refractory metal portion is thinner than said second refractory metal portion.
5. An MOS transistor with an inverted-T refractory metal gate as in claim 1, wherein said first refractory metal portion is between 450-550 .ANG. thick and said second refractory metal portion is approximately 3500 .ANG. thick.
6. An MOS transistor with an inverted-T refractory metal gate as in claim 1, further comprising: a first sidewall spacer surrounding said second refractory metal portion, said first refractory metal portion partially extending beneath said first sidewall space, a second sidewall spacer surrounding said first sidewall spacer, said second sidewall spacer partially extending beneath said first sidewall spacer and contacting said first refractory metal portion.
7. An MOS transistor with an inverted-T refractory metal gate as in claim 1, wherein said material comprises tungsten.
8. An MOS transistor with an inverted-T refractory metal gate as in claim 1, wherein said material comprises molybdenum.
9. An MOS transistor with an inverted-T refractory metal gate as in claim 1, wherein said first refractory metal layer has a first etch rate and said second refractory metal layer has a second etch rate different than said first etch rate.
10. An MOS transistor with an inverted-T refractory metal gate as in claim 9, wherein said first etch rate is less than said second etch rate.
11. An MOS transistor with an inverted-T refractory metal gate as in claim 9, wherein said first refractory metal layer has a first etch rate and said second refractory metal layer has said second etch rate when said first refractory metal layer and said second refractory metal layer are being etched with a single etch process.
12. An MOS transistor with an inverted-T refractory metal gate as in claim 11, wherein said single etch process comprises a Cl.sub.2 /O.sub.2 reactive ion etch.
Patent Citations (14)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US4356623 | 1982-11-01 | Hunter | |
| US4478678 | 1984-10-01 | Watanabe | |
| US4672419 | 1987-06-01 | McDavid | |
| US4901128 | 1990-02-01 | Sanami et al. | |
| US4906589 | 1990-03-01 | Chao | |
| US4963504 | 1990-10-01 | Huang | |
| US4984042 | 1991-01-01 | Pfiester et al. | |
| US5097301 | 1992-03-01 | Sanchez | |
| US5140403 | 1992-08-01 | Hikichi et al. | |
| US5162884 | 1992-11-01 | Liou et al. | |
| US5182619 | 1993-01-01 | Pfiester | |
| EPX284795 | 1988-10-01 | ||
| DEX3813665 | 1987-09-01 | ||
| JPX62-073779 | 1987-04-01 |
Non-Patent Literature (11)
- "High Resolution Tungsten Patterning Using Buffered, Mildly Basic Etching Solutions"; T. A. Shankoff et al.; Bell Laboratories; Murray Hill, NJ; pp. 294-297; vol. 122, No. 2.
- "Metal Vapor Effects on Chemical Reactions in an Argon Plasma"; Paul Meubus; Universite du Quebec a Chicoutimi; Quebec, Canada; Dept. of Applied Sciences; J. electrochem. Soc.; Feb. 1975; p. 298.
- "Composite Refractory metal Gate Elecrtrodes for High Speed NMOS and CMOS FET"; IBM Technical Disclosure Bulletin 30 (1987); Dec., No. 7.
- "Two Step Deposition Method for Reducing Surface States of Mo Gate MOS Devices With Thin Gate Oxides"; T. Amazawa et al.; 2419 Japanese Journal of Applied Physics. Supplements 1983); 15th Conf., Tokyo, Japan; pp. 229-232.
- "Effect of W Film Stress on W-Gate MOS Characteristics"; Hideaki Matsuhashi et al.; 2419 Japanese Journal of applied Physics (1989) 28-30 Aug.; 21st Conf.; Tokyo, Japan; pp. 17-20.
- T.A. Shankoff et al., High Resolution Tugnsten Patterning Using Buffered, Mildly Basic Etching Solutions, J. Electrochem. Soc. (1975).
- James R. Pfiester et al., A Selectively Deposited Poly-Gate ITLDD Process with Self-Aligned LDD/Channel Implantation, IEEE 1990.
- Tiao-yuan Huang et al., A Novel Submicron LDD Transistor With Inverse-T Gate Structure, 1986 IEEE.
- Naoki Kasai et al., Deep-Submicron Tungsten Gate CMOS Technology, 1988 IEEE.
- C.Y. Ting et al., Gate Materials Consideration for Submicron CMOS, Applied Surface Science 38 (1989) 416-427.
- N. Kobayashi et al., Highly Reliable Tungsten Gate Technology, 1987 Materials Research Society.