Tuneable Electric Antenna Apparatus Including Ferroelectric Material

1. Field of the Invention

Ferroelectric films such as SrTiO.sub.3, Pb(Sr,Ti)O.sub.3, Sr.sub.x Ba.sub.1-x TiO.sub.3, etc. provide a means for producing tuneable capacitors since the dielectric constant of the ferroelectric films is tuneable by variation of voltage applied to the ferroelectric films. Because of their intrinsically low losses at high frequencies, these materials can be implemented in a variety of microwave components, including delay lines and phase shifters.

One of the principle applications of delay lines and phase shifters is for phased array antennas. The voltage-controlled ferroelectric film modulates the dielectric constant and hence the time delay of either microstrip or coplanar delay lines. Such phase shifters or tuneable delay lines can be used to phase delay microwave and millimeter wave signals either transmitted or received from the individual radiative elements of the antenna array.

Such tuneable ferroelectric films can be used in a large family of tuneable microwave components and devices such as phase shifters, matching networks, oscillators, filters, resonators, loop antennas, superconducting film elements, etc.

2. Description of the Prior Art

Ferroelectric phase shifters are disclosed in "Ceramic Phase Shifters for Electronically Steerable Antenna Systems", Varadan, V. K., et al., Microwave Journal, January 1992, pp. 116-126.

The use of superconductors for microwave frequency transmission is disclosed in "High-Temperature Superconductivity for EW" Ryan, P.A., Journal of Electronic Defense, August 1992, pp. 48-54.

The dielectric properties of thin films of SrTiO.sub.3 used as dielectric layers in superconducting field effect (FET) like devices is disclosed in "Dielectric properties of SrTiO.sub.3 thin films used in high T.sub.c superconducting field-effect devices", Walkenhourst, A., et al. Appl. Phys. Lett. 60(14), 6 Apr. 1992, pp. 1744-1746.

A superconductor phase shifter using SQUIDS is disclosed in "Monolithic HTS Microwave-Phase Shifter and Other Devices", Jackson, C M , et al Journal of Superconductivity, Vol. 5 No. 4, 1992, pp. 419-424.

The use of superconductive feed networks and antenna elements of antenna arrays is disclosed in "A Survey of Possible Passive Antenna Applications of High-Temperature Superconductors", Dinger R. J et al IEEE Transactions on Microwave Theory and Techniques, Vol. 39, No. 9, September, 1991.

A thin superconducting film antenna is disclosed in "Radiation Efficiency Measurements of a Thin-Film Y--Ba--Cu--O Superconducting Half-Loop Antenna at 500 MHZ", Dinger, R. J., et al. Paper Presented at MTT-S, Boston, June, 1991, pp. 1-4.

The dielectric properties of BST material thin films are disclosed in "Microstructure-Induced Schottky Barrier Effects", in Barium Strontium Titanate (BST) Thin Films for 16 and 64 MBIT Dram Cells, Scott, J. F., et al., circa 1992.

The present invention relates to the use of ferroelectric insulating thin films as dielectric layers in superconducting thin film structures for fabrication of microwave and millimeter wave devices which are frequency-tuneable. More particularly, metal oxide ferroelectric and superconducting thin films are used in combination to produce an entire new class of microwave and millimeter wave devices which can be frequency-tuned by the application of voltage bias signals across various portions of the ferroelectric thin films. In such structures, because of the low loss performance of superconductors at high frequency, the microwave and millimeter wave performance of the devices are limited mostly by the loss tangent of the ferroelectric dielectric layers. The fundamental materials compatability of a whole class of metal oxide superconductors with a whole class of metal oxide ferroelectric materials provides a thin film material system with unique flexibility for designing and fabricating a multiplicity of multilayer geometries, including ferroelectric on superconductor structures and superconductor on ferroelectric structures.

The invention is especially useful for producing microwave and millimeter wave devices which have the extreme low loss performance of other superconducting devices, but also have the necessary frequency tuneability required for most practical applications. By this invention, it is possible to realize numerous microwave and millimeter wave devices, including, but not limited to, delay lines, phase shifters, resonators, oscillators, filters, electrically-small antennas, half-loop antennas, directional couplers, patch antennas, and various radiative gratings, which are frequency-tuneable by utilizing voltage-tuneable capacitor structures fabricated from voltage-biased ferroelectric thin films in combination with superconducting thin films.

The invention relates to the utilization of both thin films of high temperature superconductor (HTSC) material and thin films of ferroelectric materials for achieving tuneability in a variety of microwave structures.

Ferroelectric films such a SrTiO.sub.3, Pb(Sr,Ti)O.sub.3, Sr.sub.x Ba.sub.1-x TiO.sub.3, etc. provide a means for producing tuneable capacitor structures at microwave frequencies since the dielectric constant of the ferroelectric films is tuneable by variation of voltage applied to the ferroelectric films. In accordance with the invention, a thin film of ferroelectric material is provided with a thin film (or films) of a high temperature superconductor (HTSC) such as Y--Ba--Cu--O (YBCO) or Tl--Ba--Ca--Cu--O (TBCCO) in order to produce low loss microwave and millimeter wave devices which are frequency tuneable by application of voltage to the thin films of ferroelectric material. The thin film structures of HTSC material and ferroelectric material which are deposited on a substrate result in reduced losses, limited only by the loss tangent of the ferroelectric material and the impedance matching structures. The combination of HTSC thin films and ferroelectric thin films can be used in a large family of tuneable microwave components and devices such as phase shifter devices which offer a method for obtaining true-time delay, superconducting phase shifters, tuneable delay lines, resonators, filters, matching networks, oscillators and tuneable antennas.

The combination of a HTSC thin film and ferroelectric thin films offers a novel class of microwave devices with unique properties including a substantial frequency tunability, simple construction, the potential for optimization of temperature operation ranges, the ability to use variably thin dielectrics, low cost, high level of integration with other components such as antennas and the increased power handling of the circuit. The extent of the tunability of the structures depends upon the ferroelectric material, its form and geometry, (e.g., film thickness), the temperature, and the applied fields or voltage.

Compatibility of YBCO, TBCCO and other superconductors and a broad class of ferroelectric materials enables the optimization of ferroelectric materials and superconducting materials and the growth of alternating layers of each by a variety of deposition methods including evaporation, sol gel, sputtering physical vapor deposition, chemical vapor deposition, laser deposition and others. The combination of HTSC thin films and ferroelectric films provides a novel class of tuneable microwave and millimeter wave devices.

One of the principle applications of the invention comprises phase shifters and tuneable delay lines for phased array antennas. The voltage-controlled ferroelectric thin film modulates the dielectric constant and hence the time delay, of either microstrip line or coplanar delay lines. Such phase shifters or tuneable delay lines can be used to phase delay microwave and millimeter wave signals either transmitted or received from the individual radiative elements of the antenna array. Other applications of the class of tuneable microwave and millimeter wave devices include resonators, filters, matching networks, oscillators, directional couplers and tuneable antennas.

The invention also includes the utilization of a dielectric grating for an individual radiative element in a phased antenna array. Such a grating (with fixed delay between each adjacent element) radiates (or receives) energy at a fixed angle. The angle can be adjusted by biasing the dielectric grating with a single bias voltage. Such a voltage-controlled grating enables steering (in one direction) with the application of a single DC-bias line.

The invention of the dielectric grating can be extended to two-dimensional arrays, with steering in both the x- and y-directions. A simple two-dimensional array of such gratings with a fixed spacing between each grating "patch" antenna provides a similar fixed radiation angle in the second direction. A second, single voltage bias line modulates the dielectric constant and hence the time delay between each grating structure in the array.

The invention also includes several capacitively coupled devices, including a tuneable superconducting resonator with substantial tunability, a superconducting fringe-effect capacitor with substantial tunability, and application of the tuneable devices to a broad range of resonant devices, including tuneable loop antennas.

FIG. 1 is a plan view of a specific embodiment of the invention, a tuneable delay line, showing a microstrip line of HTSC material deposited on/a thin film (substrate) of ferroelectric material, all deposited on a crystalline substrate;

FIG. 2 is a schematic representation of the tuneable superconductor/ferroelectric thin film device of the invention;

FIG. 3 is a plot of the Magnetic Flux Screening-Temperature characteristic for a multilayer superconductor/ferroelectric thin film structure of the invention after deposition as measured by a mutual inductance technique;

FIG. 4 is a plot of Insertion Loss vs. Frequency at 77K for the tuneable resonator of the invention;

FIG. 5 is a fragmentary vertical section view of a thin film of HTSC material contiguous with the opposite surface of a film of ferroelectric material;

FIG. 6 is a schematic representation of the phase shifter of the invention in a phased array antenna system;

FIG. 7 is a fragmentary vertical section view of a dielectric grating in accordance with the invention for an individual radiative element in an antenna array;

FIG. 8 is a schematic representation of a two-dimensional array of dielectric gratings in accordance with the invention for an antenna array;

FIG. 9 is a perspective view of a coplanar structure of the invention formed on a LaAlO.sub.3 substrate;

FIG. 10 is a perspective view of a resonant cavity formed by coplanar cavities in accordance with the invention;

FIG. 11 is a schematic representation of a capacitively coupled microstrip line resonator with a tuneable ferroelectric capacitor and a capacitively coupled microstrip line resonator without tunability;

FIG. 12 is a plan view of a superconducting fringe effect capacitor in accordance with the invention; and

FIG. 13 is an elevation view of the capacitor of FIG. 12.

FIG. 14 is a cross sectional view of a specific multilayer structure of the invention, with a HTSC layer on top of a ferroelectric layer.

FIG. 15 is a cross sectional view of a more general multilayer structure of the invention, with a HTSC layer on top of a ferroelectric layer on top of a substrate.

FIG. 16 is a cross sectional view of a specific structure of the invention, in which a HTSC layer is deposited directly on a ferroelectric substrate.

FIG. 17 is a cross sectional view of a specific multilayer structure of the invention, with a ferroelectric layer deposited on top of a patterned HTSC layer (deposited on a substrate) with the ferroelectric layer also filling in the etched regions of the HTSC layer.

FIG. 18 is a cross section view of a specific structure of the invention in which a ferroelectric layer and HTSC layer lie in the same plane, with the HTSC-ferroelectric interface of the invention being at the edges of the films.

FIG. 19 is a cross sectional view of a general multilayer structure of the invention with various combinations of HTSC and ferroelectric layers on a bulk crystalline dielectric, insulating, or ferroelectric substrate.

FIG. 20 is a fragmentary vertical section view of coplanar thin films of HTSC material contiguous with one surface of a thin film of ferroelectric material and a thin film of HTSC material contiguous with the other surface of the thin film of ferroelectric material.

FIG. 21 is a plan view of an interdigitated capacitor of the invention;

FIG. 22 is a fragmentary vertical section view of the interdigitated capacitor of FIG. 21;

FIG. 23 is a plan view of a half-loop antenna of the invention;

FIG. 24 is a schematic representation of the resonant circuit of the half loop antenna of FIG. 23.

Discoveries of high temperature superconducting (HTSC) materials such as the 30.degree. K. La--Ba--Cu--O superconductor and the 90.degree. K. Y--Ba--Cu--O superconductor have stimulated a worldwide race for higher temperature superconductors. Breakthroughs have been made by the discoveries of the 90.degree. K. Tl--Ba--Cu--O system, the 110.degree. K. Bi--Ca--Sr--Cu--O system, and the 120.degree. K. Tl--Ba--Ca--Cu--O (TBCCO) system The Y--Ba--Cu--O system is the first rare earth system which reaches zero resistance above the liquid nitrogen boiling point while the Tl--Ba--Ca--Cu--O system reaches zero resistance above 100.degree. K. and has the highest zero-resistance temperature (127.degree. K.).

A number of superconducting phases, including Tl.sub.2 Ba.sub.2 Ca.sub.2 Cu.sub.3 O.sub.10+x (2223) and Tl.sub.2 Ba.sub.2 Ca.sub.1 Cu.sub.2 O.sub.8+x (2212) have been isolated from the Tl--Ba--Ca--Cu--O system. The 2223 superconductor has a 3.85.times.3.85.times.36.25 .ANG. tetragonal unit cell. The 2122 superconductor has a 3.85.times.3.85.times.29.55 .ANG. tetragonal unit cell. The 2223 phase is related to 2122 by addition of extra calcium and copper layers. In addition, the superconducting phase in the Ca--free Tl--Ba--Cu--O system is Tl.sub.2 Ba.sub.2 CuO.sub.6+x (2201).

The new class of tuneable microwave devices of the invention combines the low loss of a high temperature superconductive (HTSC) material (such as Tl--Ba--ca--Cu--O and Y--Ba--Cu--O) in a thin film with the variable dielectric properties of a thin film of ferroelectric material.

Ferroelectric thin films such a SrTiO.sub.3, Pb(Sr,Ti)O.sub.3, Sr.sub.x Ba.sub.1-x TiO.sub.3, etc. provide a means for producing low-loss tuneable capacitor structures at microwave and millimeter wave frequencies since the dielectric constant of the ferroelectric thin films is tuneable by variation of voltage applied to the films. A thin film of ferroelectric material is provided with a thin film of a high temperature superconductor (HTSC) material such as Y--Ba--Cu--O or Tl--Ba--Ca--Cu--O. The HTSC thin film results in a multilayer structure with reduced losses, limited only by the loss tangent of the ferroelectric material and the impedance matching structures. The combination of HTSC thin films and ferroelectric films can be used in a large family of tuneable microwave components and devices such as phase shifter devices which offer a method for obtaining true-time delays in tuneable delay lines, tuneable filters, matching networks, oscillators, loop antennas, directional couplers, resonators, etc.

The thin film of ferroelectric material, e.g., SrTiO.sub.3 and various barium doped strontium titanate materials provide an excellent substrate for the deposition of an HTSC material such as YBa.sub.2 Cu.sub.3 O.sub.7-8 (YBCO) or Tl--Ba--Ca--Cu--O (TBCCO). SrTiO.sub.3, and its relatives, have a perovskite crystal structure with an excellent lattice match and thermal expansion coefficient close to that of YBCO, Tl--Ba--Ca--Cu--O, and other thallium copper oxide superconductors. In general other substrates can also be used, such as lanthanum aluminate, etc.

The combination of HTSC thin films-and ferroelectric thin films offers a novel class of tuneable microwave and millimeter wave devices with unique properties including a substantial frequency tuneability, simple construction, the potential for optimization of temperature operation ranges, the ability to use variably thin dielectrics, low cost, high level of integration with other components such as antennas, and the power handling of the circuit. The extent of the tuneability of the structures depends on the materials, their forms and geometrics (e.g. film thickness), the temperature, and the applied voltage.

High quality SrTiO.sub.3, BaSrTiO.sub.3, LaA1O.sub.3 and other dielectric thin films can be deposited on HTSC thin films (e.g., YBCO or Tl--Ba--Ca--Cu--O) films by sol-gel, plasma-spray, sputtering, physical vapor deposition, chemical vapor deposition, laser deposition, and other techniques. Superconducting properties of the HTSC layer depend on the compatability with the ferroelectric thin film and vice-versa, as well as on processing conditions. In practical circuits, a fixed temperature of operation is required to provide good impedance matching. Broadband, compact, low loss, thin-film, superconducting matching circuits are available. A thin film multilayer implementation of the class of tuneable superconducting/ferroelectric structures of the invention has the added benefit that monolithic devices and integrated circuits can be designed.

As shown in FIG. 1, a tuneable delay line 20 is formed by a patterned microstrip line 21 of a thin film of HTSC material, for example YBCO material, deposited on a thin film 22 of ferroelectric material which is deposited on ground plane 23. In turn ground plane 23 is deposited on a crystalline substrate such as SrTiO.sub.3 (not shown). The ferroelectric thin film 22 can be, for example, from 100 .ANG. to 10000 .ANG. thickness. By applying a voltage between the superconductor or microstrip line 21 and a ground plane 23, a DC bias is provided to the ferroelectric layer, thereby changing the dielectric constant and the wave propagation velocity within the layer. Note that both the microstrip line and the ground plane can be made from HTSC material.

The microstrip line or pattern 21 of a YBCO thin film is deposited on the SrTiO.sub.3 thin film substrate 22 by using sol-gel, chemical vapor deposition, physical vapor deposition, sputtering, laser deposition, or other techniques. Sol-gel deposition and chemical vapor deposition of superconducting thin films and ferroelectric thin films is disclosed in U.S. Pat. Nos. 5,119,760 and 5,138,520, assigned to Symetrix Corporation of Colorado Springs, Colo.

FIG. 2 shows a schematic representation of the tuneable delay line 20 including the microstrip line or thin film of the (HTSC) YBCO material 21. A normal metal (e.g. silver) or HTSC material ground plane 23 is deposited on the rear surface 22a of substrate or film 22. Variable voltage source 25 enables a variable voltage V to be applied as an electric field to the ferroelectric layer 22 by means of microstrip line 21 and ground plane 23.

SrTiO.sub.3 belongs to the BaTiO.sub.3 group in the classification of ferroelectric materials. BaTiO.sub.3 is a well known ferroelectric material and its phase transition from cubic to tetragonal, where a small displacement of Ti in the tetragonal phase under the external electric field, is responsible for ferroelectricity. SrTiO.sub.3 has three crystalline phase transitions at lower temperatures (see Table 1).

Other ferroelectric materials which can be used for thin film 22 include BaTiO.sub.3, LiNbO.sub.3, Pb(Sr,Ti)O.sub.3, Sr.sub.x Ba.sub.1-x TiO.sub.3. etc. Other materials from the III-V, and II-VI groups could be used with other buffer layers to solve any lattice matching problems which arise should epitaxial deposition be required.

The extent of tuneability of the tuneable delay line 20 depends upon the ferroelectric material, the temperature, and the applied field or voltage.

An advantage of the superconductor/ferroelectric tuneable delay line 20 of the invention is its power handling capability. Distortion can arise in a non-linear transmission line when the RF voltages become comparable to the DC control voltages. The power handling of a microstrip line can be estimated from the minimum bias voltage to be used. Power is given by P=V.sup.2 /Z where P=power, V=voltage, and Z=impedance. Accordingly, for a 5 volt bias and a 1 ohm impedance, 25 watts (i.e. >40 dBm) could be handled before the non-linearities become apparent. The level of high power will set the microstrip line width requirement to insure that the critical current carrying capacity of the line is not exceeded.

FIG. 3 shows changes in resistance in terms of voltage with changes of temperature of the multilayer superconductor/ferroelectric thin film structure of the invention after deposition. Thus FIG. 3 shows the temperature dependence for a multilayer superconductor/ferroelectric thin film structure. The sharp changes at the superconductor critical temperature are characteristic of a superconductor, indicating that the ferroelectric material deposition and processing does not destroy the properties of the superconducting thin film.

FIG. 4 shows the change in insertion loss in dB plotted against frequency in GHz at 77.degree. K. for the tuneable resonator of the invention and resonant frequency peaks thereof. The measured frequency response of the resonator circuit as shown in FIG. 4 clearly indicates a shift in frequency of the fundamental resonance and the third harmonic when a biasing voltage is applied to the tuning element.

FIG. 5 shows a microstrip line 31 of HTSC material in section. As shown in FIG. 5, the thin film of the HTSC material 32 of microstrip line 31 is deposited upon thin film 34 of the ferroelectric material. Thin film 34 of ferroelectric material is contiguous with thin film 33 of HTSC material. Crystalline substrate 35 supports thin films 33, 34 and 32.

Where size, weight, and drive mechanisms are limited, the traditional moving reflector antenna is being replaced in some applications by phased array antennas. Generally planar in shape, conventional phased array antennas are formed by a substantial number of closely spaced, individual radiators, whose composite beam can be shaped and spacially directed in microseconds, thereby enabling the antenna to track a multitude of targets at one time. This is accomplished electronically by RF phase shifters associated with each individual radiating element. No moving parts are required.

State of the art passive phased array antennas are limited in their application by cost, more than any other factor. The required phase shifters are not cheap and with a typical array requiring thousands of individual antenna elements, each with its own phase shifter, the price of the total system becomes prohibitive.

The principal difficulty of such phased arrays is that for large arrays, i.e. antenna arrays with a large number of radiative elements, the need to control each individual time delay to each radiative element requires that each individual phase shifter be independently voltage-biased. Arrays as large as 100.times.100 radiative elements necessarily require 10,000 independently-controlled bias voltage lines, which can be prohibitive in complexity and cost.

The ferroelectric phase shifter design is based upon a material whose dielectric permittivity can be made to vary by application of a DC electric field, parallel to the polarization of the RF energy, and normal to its direction of propagation. Variations in permittivity alter the RF propagation velocity, and if connected to a waveguide structure, will change the cutoff wavelength and dispersion of the waveguide itself. These two effects translate into propagation phase variation. A short waveguide section containing a phase shifter of ferroelectric material and HTSC material constitutes the key element for accomplishing electronic scanning in a phased array antenna configuration.

A typical application of the thin film HTSC material and ferroelectric thin film technology of the invention is for phase shifters for phased array antennas. The voltage-controlled ferroelectric thin film can be used to modulate the dielectric constant, and hence the time delay, of either microstrip line or coplanar delay lines. Such phase shifters or tuneable delay lines can be used to phase delay microwave and millimeter wavelength signals either transmitted or received from the individual radiative elements of the antenna array.

As shown in FIG. 6, the phased array antenna 40 of the invention includes a plurality of radiators 41. The antenna input 42 from a source of a electromagnetic radiation such as that at a microwave frequency is provided with a power distribution network 43. The distribution network connects the antenna input to each of a plurality of phase shifters 44 in accordance with the invention. The thin superconducting film of each of phase shifters 44 is connected by leads 45 to control circuit 46. The control circuit is driven by programmer 47 to control the voltage applied by the thin superconductor film to the ferroelectric film of each of the phase shifters 44. Thus, the dielectric permittivity of the ferroelectric thin film of each of phase shifters 44 can be varied by the application thereto of a variable DC electric field. The DC electric field is applied normal to the direction of propagation of the RF energy and parallel to the polarization of the RF energy being transmitted through the phase shifter to the radiators 41 of phased array antenna 40. Variations in permittivity of the ferroelectric thin film material alter the RF propagation velocity and can change the cutoff wavelength and dispersion of the RF energy being delivered to the radiators 41 of the antenna. As a result there is a variation in the propagation phase of one radiator with respect to another. Thus programmer 47 by means of control circuit 46 can effect electronic scanning of the phase shifters 44 connected to the radiators 41 of antenna 40 and thereby enable the beam produced by antenna 40 to be shaped into a predetermined form and to be directed in microseconds. In this way the RF energy radiated by the antenna can track a multitude of targets at one time. In FIG. 6, .theta..sub.0 is the angle of the beam shaped by the phased array antenna with respect to an axis extending at right angles to the line of radiators 41. The interval "d" is the spacing between radiators 41. ".lambda." is the wavelength of the radiation. ".theta." is the phase angle of the radiation from source 47. Thus, the phase shifter 44 furtherst to the right is set at a phase angle of zero degrees, which equate to no phase shift. ".DELTA..theta." is the difference in the propagation phase of each of radiators 41 of antenna 40 with respect to the other radiators "x", of "2x", "3x", "4x", "5x", "6x", and "7x", is a constant applied to ".DELTA..theta.".

Another embodiment of the invention as shown in FIG. 7 comprises a dielectric grating 50 for an individual radiative element in an antenna array. The grating comprises a base portion 50a and a plurality of elements 50b projecting from base portion 50a and spaced apart from one another. Grating 50 which is formed, for example, of a thin film of ferroelectric material with a fixed time delay determined by the spacing between each adjacent element 50b intrinsically radiates (or receives) RF energy at a fixed angle .theta.. The angle .theta. is adjusted by biasing the dielectric grating 50 with a bias voltage from variable bias voltage source 51. Such a voltage-controlled grating enables changing or steering (in one plane) of the radiation angle .theta. with the application of a variable bias voltage from the source 51 to the grating 50 by lead 52.

In FIG. 8 there is shown a two-dimensional array antenna with steering of the radiation angle .theta. in both the x-z and y-z planes. A two-dimensional array 53 of gratings 54 is shown in FIG. 8. A fixed spacing between each grating "patch" antenna element 55 is formed by a grating 50 as shown in FIG. 7 and provides a similar radiation angle in the second plane. Voltage bias lines 56 and 57 connected to arrays 58 and 59, respectively, modulate the dielectric constant of the gratings and thereby the time delay between each antenna element 55 in the arrays 50 and 59 which make up antenna 53.

The thin film superconductor/ferroelectric technology of the invention can also be used with:

(1) Tuneable cavities and resonators;

(2) Tuneable frequency and wavelength filters;

(3) Ferrite thin film isolators;

(4) Directional coupler switches;

(5) Phase shift feeder networks for patch antennas;

(6) Coplanar lines with variable impedance using voltage-tuned meander lines as the center conductor of the coplanar line;

(7) tuneable resonant antennas;

(8) tuneable electrically small antennas; and

(9) Tuneable, one-dimensional confocal i.e., (having the same focus) resonators which can provide higher Q.

A coplanar structure 60 in accordance with the invention is shown in FIG. 9. Structure 60 includes ferroelectric film 61 overlying LaAlO.sub.3 substrate 62. Thin films 63 of HTSC (e.g., YBCO or TBCCO) material are deposited on film 61 of ferroelectric dielectric material such as barium strontum titanate (BST) material, the lower surface of which is contiguous with the upper surface of the substrate of a LaAlO.sub.3 (LAO) material.

FIG. 10 shows a tuneable coplanar resonator structure 65 having a coplanar line 66 of YBCO material forming a half wave-length resonator with coplanar lines 66 and 67 which are disposed between coplanar lines 68 and 69. The lines 66-69 are deposited on a dielectric film 70 of BST material. Changes in the thickness of the substrate 71 which, for example, can be LaAlO.sub.3 material, modify the effective dielectric constant of film 70 of BST material and the percentage change of this dielectric constant with the variable voltage applied to dielectric film 71 by voltage source 72.

FIG. 11 shows an capacitively coupled microstrip resonator 80. The dimensions shown on FIG. 11 are by way of example. The resonator includes microstrips 81 and 82 of superconductor (HTSC) material which, by way of example, extend for 9 mm and, by way of example, have a width of 3.73 mm. Strip 83 of thin film ferroelectric material extends over capacitor 84 between strips 81 and 82. Strips 85 and 86 of HTSC material are connected by leads 87 and 88, respectively, to strips 81 and 82, respectively. Strip 85 and 86, by way of example, each can have an area of 1 mm by 1.27 mm and each can be disposed, from microstrips 81 and 82, respectively. The spacing between strips 85 and 86, by way example, can be 13 mm. If the resonator 80 of FIG. 11, by way of example, is deposited on 17 mils of LaAlO.sub.3 (LAO) material with .di-elect cons..sub.r =24.5, then the effective dielectric constant, .di-elect cons..sub.eff is .di-elect cons..sub.eff .congruent.20.

Inductively coupled resonator 90 in FIG. 11 having no tunability includes strip 91 of HTSC material connected by leads 92 and 93 to strips 94 and 95 of HTSC material, respectively. Concerning the dimensions shown in FIG. 11, S1 refers to the distance between the microstrips 81 and 82 of superconductor material and the strip 91; S2 refers to the distance from the lower end of the microstrip 82 to the upper end of the strip 86; L1 refers to the combined length of the microstrips 81 and 82 and the length of the strip 91; L2 refers to the length of the strip 86; W1 refers to the width of the microstrips 81 and 82; and W2 refers to the width of the strip 86. If the untuneable resonator 90 is approximated as a section of transmission line comprising two parallel spaced conductors with open ends, then its resonant frequencies is: ##EQU1##

This gives f.apprxeq.3.7 GHz, 7.4 GHz, 11.2 GHz, etc.

The thin film ferroelectric strip 83 in series with strips 81 and 82 form a ferroelectric capacitor 84 in the tuneable resonator 80 will affect those resonant modes with large currents in the region of the ferroelectric capacitor. These are the antisymmetric resonant modes, i.e., modes with odd "n" in the above equation. Transmission line analysis yields a transcendental equation for the increased resonant frequencies of these modes: ##EQU2## where C=capacitance

Z.sub.0 =characteristic impendance .apprxeq.7

l=effective length of the resonator (open end to open end length) ##EQU3## where c is the speed of light and

f is the frequency of the resonant mode.

It is estimated that the capacitance is C.about.1 pF. This gives a resonant frequency spectrum of:

6.7 GHz, 7.4 GHz, 13.43 GHz, . . . Under a DC bias, the 6.7 Ghz, 13.43 Ghz, . . . modes will increase in frequency due to the voltage tuneable dielectric constant change.

In FIGS. 12 and 13 there is shown a superconducting fringe effect capacitor 100 comprising a thin film of ferroelectric material 101 disposed on a substrate 101a (see FIG. 13). Thin films 102 and 103 of HTSC material are deposited on ferroelectric thin film 101. Pads 104 and 105 (see FIG. 12) are connected by leads 107 and 108, respectively, to thin films 102 and 103, respectively. Variable voltage source 106 is connected by lead 107 and 108 (see FIG. 12) to pads 104 and 105, respectively, and thereby across thin films 102 and 103. The thin film of ferroelectric material 101 has a fringe effect capacitance region 109 of a width "t" disposed between thin films 102 and 103 of HTSC material. By applying a variable voltage V across the thin films 102 and 103, the dielectric constant of the ferroelectric material 101 can be tuned.

As shown in FIG. 14, a HTSC layer A1 is deposited on a ferroelectric layer A2, and the HTSC layer can be subsequently patterned to produce a variety of structures A3. In this geometry, the HTSC/ferroelectric interface A4 is perpendicular to the C-axis of the layers, and lies in the plane of the layers.

As shown in FIG. 15, a HTSC layer A1 is deposited on a ferroelectric layer A2 which is deposited on a substrate A5. Again, the HTSC/ferroelectric interface A4, and the ferroelectric/substrate interface A6 lie in the plane of the layers.

As shown in FIG. 16, a HTSC layer A1 is deposited directly on a ferroelectric substrate A7, with the HTSC/ferroelectric interface A4 being coincident with the HTSC/substrate interface, again lying in the plane of the layers.

As shown in FIG. 17, a ferroelectric layer A2 is deposited on top of a patterned HTSC layer AS (with example etched feature A9 shown), which-is deposited on a substrate A7. The ferroelectric layer A9 fills the etched regions A9 and forms HTSC/ferroelectric interfaces A4 between the overlying ferroelectric layer A2 and HTSC layer A8 and interfaces A10 between the ferroelectric layer A2 and the edges of the patterned HTSC film AS. The interface All between the ferroelectric film A2 and the crystalline (or film) substrate A7 (made of dielectric, insulator, ferroelectric, or other material) is also shown.

As shown in FIG. 18, a ferroelectric layer A12 and HTSC layer A8 are deposited in the same plane, with the HTSC/ferroelectric interface A10 lying at the edges of the layers. Such layers can be deposited on a variety of substrates A7.

As shown in FIG. 19, a variety of structures A1 - A9 are shown in combination, representing one example of the more general multi-layer structure of the invention, with various patterned A3 and A8 and unpatterned HTSC A1 and ferroelectric layers A2 lying on top of each other, in various orders, and with the entire structure lying on a substrate A7. In the general structure, the substrate could be made of a bulk crystalline sample or film of any number of materials, including dielectrics, insulators, ferroelectrics, etc.

All the layers described can be deposited by a variety of techniques, including physical vapor deposition, chemical vapor deposition, laser deposition, sputtering, sol gel, etc.

In FIG. 20 there is shown a multilayer component 110 of the invention comprising thin films 111 and 112 of HTSC material contiguous with thin film 113 of ferroelectric material. The lower surface of ferroelectric thin film is contiguous with the upper surface of thin film 114 of HTSC material. The lower surface of thin film 114 is contiguous with the upper surface of substrate 115.

FIG. 21 is a plan view of an interdigitated capacitor structure 120 in accordance with the invention. Thin films 121 and 122 of HTSC material have a plurality of projections 121a and 122a, (see FIG. 12) respectively, which nest with respect to one another, thereby forming a meandering slot 123 in structure 120. As shown in FIGS. 21 and 22, a thin film 124 of ferroelectric material overlies the portions of thin films 121 and 122 adjacent meandering slot 123 and extends into the slot itself. The structure 120 enables the overall value of the capacitance of structure 120 to be increased while maintaining tuneability of the capacitance by the application of predetermined voltages to thin film 124.

FIG. 23 shows a tuneable antenna 130 in accordance with the invention. The tuneable antenna comprises half-loop 131 of a thin film of HTSC material. Layers of insulating material 132 and 133 support the half-loop antenna 131. Layers 132 and 133 are separated by thin film 134 of HTSC material. Thin film 135 of HTSC material is connected to half-loop 131. Thin film 136 of ferroelectric material is disposed between thin film 135 and thin film 140 of HTSC material which is disposed on substrate 138. Thin films 135 and 140 with ferroelectric thin film 136 therebetween form tuneable capacitor 141.

In FIG. 24 there is shown the equivalent circuit of the half-loop antenna 130 of FIG. 23. Driving signal source 142 is connected to the half loop antenna element 131 via the tuneable capacitor 141. Driving signal source 142 is connected to thin film 140. As shown in FIG. 24, inductance 143 and resistance 144 are the lumped values of the resistance R and the inductance L of the half-loop antenna. The application of a DC voltage across capacitor 141 tunes the capacitance thereof and hence the frequency of the resonance of the circuit comprising the half-loop antenna 131 and the capacitor 141.

The advantages of the present invention, as well as certain changes and modifications of the disclosed embodiments thereof, will be readily apparent to those skilled in the art. It is the applicants' intention to cover in their claims all those changes and modifications which could be made to the embodiments of the invention herein chosen for the purpose of the disclosure without departing from the spirit and scope of the invention.