PECVD Method of Depositing Fluorine Doped Oxide Using a Fluorine Precursor Containing a Glass-Forming Element

The field of the invention is that of integrated circuits, in particular the formation of oxide dielectric layers doped with fluorine.

In the interests of providing higher speed, the art has searched for dielectric layers having a lower dielectric constant. It has been suggested in an article by J. Ida, et al entitled "Reduction of Wiring Capacitance with New Dielectric SiOF Interlayer Film for High Speed/Low Power Sub-Half Micron CMOS", 1994 Symposium on VLSI Technology Digest of Technical Papers 0-7803-19212-4/94 IEEE, that the use of C.sub.2 F.sub.6 in connection with TEOS (Si(OC.sub.2 H.sub.5).sub.4) may provide a silicon dioxide (oxide) layer with fluorine doping (fluorosilicate glass or F-glass) that provides such a lower dielectric constant. Another suggestion in an article by Fukada and Akahori entitled "Preparation of SiOF Films with Low Dielectric Constant by ECR Plasma Chemical Vapor Deposition" in Extended Abstracts of the 1993 International Conference on Solid State Devices and Materials, Makuhari, 1993 pp. 158-160, has been the use of silicon tetrafluoride (SiF.sub.4) in connection with O.sub.2. An article by Anand, et al entitled "Fully Integrated Back End of the Line Interconnect Process for High Performance ULSIs" in the 1994 VMIC Conference 1994 ISIMC--103/94/0015, suggests the use of CF.sub.4 and C.sub.2 F.sub.6. The C.sub.2 F.sub.6 method renders a film that is susceptible to the absorption of water, and the SiF.sub.4 ECR deposition method is susceptible to outgassing of hydrogen fluoride or fluorine, since the excess F atoms dissociated in the high density Electron Cyclotron Resonance plasma are incorporated in the F-SiOx network as weakly bonded fluorine. When more water is absorbed and F* is lost, the fluorine forms HF, which corrodes metallization. The art has not yet found a satisfactory method of forming a stable film of F-glass with sufficiently high fluorine content to significantly lower the dielectric constant and increase gap-fill capacity.

The invention relates to a method of forming a layer of oxide incorporating fluorine in which an oxygen precursor gas containing silicon is used in connection with a glass-forming precursor gas containing glass-forming molecules to form a stable water resistant film.

An advantage of the invention is that the glass forming species can be incorporated in the deposited film in the form of Si--F without breaking up the glass network, in contrast to the incorporation of C or N.

A feature of the invention is the presence of F and H, which react with one another to remove free F and/or H that could weaken the film.

FIG. 1 illustrates schematically a reaction apparatus used in connection with the invention.

FIG. 2 illustrates an FTIR showing a comparison between undoped oxide and fluoro-silicate glass.

FIG. 3 illustrates a comparison of water absorption between a fluoro-silicon glass formed by the invented method and a fluoro-silicon glass formed from C.sub.2 F.sub.6.

FIG. 4 illustrates variation of refractive index as a function of the ratio of Si--F bonds to Si--O bonds.

Referring now to FIG. 1, there is shown schematically a reaction apparatus such as an Applied Materials 5000 CVD reactor. At the center of the figure, reaction chamber 100 includes a grounded electrode 112 and an RF driven electrode 120. Wafer 110 rests on ground electrode 122. Driven electrode 120 is driven by an RF source 125 comprising preferably two frequency sources and a matching network. At the left of the drawing, a box labeled SUPPLY and indicated with the numeral 150 is a schematic representation of a source of gases including a carrier gas such as argon, a silicon precursor such as TEOS, and a fluorine precursor such as SiF.sub.4.

In operation, the gases are mixed and pass into the chamber in a conventional manner. An oxidant is not needed in this case, since TEOS is also an oxygen source. Other configurations beside that shown in FIG. 1 may also be used for deposition. Preferably, a dual frequency apparatus is used in which power is delivered at a first frequency to create a plasma and simultaneously at a second frequency to enhance and control ion bombardment, but such a dual-frequency apparatus is not required. If a dual-frequency apparatus is used, the frequencies may be applied to either one or two electrodes.

Many methods of plasma-enhanced chemical vapor deposition (PECVD) including sub-atmospheric CVD (SACVD) in the pressure range less than 750 Torr and high density CVD (with an electron density of greater than 10.sup.11 -10.sup.12 electrons/cm.sup.3) may also be used to produce satisfactory films.

In an illustrative example, a dual-frequency PECVD process was used in an Applied Materials 5000 reactor, using He as a carrier, a high frequency of 13.56 MHz and a low frequency of 0.35 MHz, with a SiF.sub.4 :TEOS:O.sub.2 ratio of 7:1:10 at a total pressure of 5 Torr and a wafer temperature of 400.degree. C.

In another example, SiF.sub.4 and SiH.sub.4 were used, together with N.sub.2 O, in the same apparatus and parameters at a SiF.sub.4 :SiH.sub.4 :N.sub.2 O ratio of 20:1:35 at 2.8 Torr and a wafer temperature of 400.degree. C. For the SiF.sub.4 :SiH.sub.4 :N.sub.2 O gas mixture, the hydrogen precursor may be added after mixing SiF.sub.4 and N.sub.2 O in order to reduce particle formation. In this embodiment, an appropriate range for the ratio R.sub.SiF4-SiH4 of SiF.sub.4 to SiH.sub.4 is between 1 and 200, with a preferred range for R.sub.SiH4-SiF4 being between 10 and 50.

The fraction of fluorine in the final film will depend on a tradeoff between dielectric constant and water absorption. A film with a high fraction of F tends to absorb water and a film with a low fraction of F has a dielectric constant that is less attractive. A preferred range for the fraction of fluorine is that the ratio R.sub.F-O of Si--F bonds to Si--O bonds in the oxide is 1/200.ltoreq.R.sub.F-O .ltoreq.1/4. The preferred ratio within this range is a ratio R.sub.F-O of about 1/20.

Referring now to FIG. 2, there is shown an FTIR (Fourier Transform Infrared Spectroscopy) plot in arbitrary units of wavenumbers on the x-axis and percentage transmittance on the y axis.

The upper trace is that of undoped oxide showing a pronounced dip indicating the presence of SiOH in the film that serves as a defect because SiOH raises the dielectric constant of oxide films, degrades the electrical properties and dissociates at high temperatures. The bottom trace, coming from a sample produced with SiF.sub.4 and TEOS, shows minimal SiOH bonding which indicates a much lower SiOH concentration.

Referring now to FIG. 3, there is shown a comparison of traces for samples formed with the invented method (SiF.sub.4 and TEOS) and a sample formed by the use of C.sub.2 F.sub.6. A humidity test in which the films were exposed to 100% humidity at 60.degree. C. for 24 hours indicates clearly that the C.sub.2 F.sub.6 sample has absorbed a substantial amount of water and the SiF.sub.4 sample has not.

FIG. 4 shows a typical variation of refractive index (RI) versus Si--F/Si--O bonding ratio (R). It shows an inverse relationship between RI and R. For higher R, films having RI as low as 1.37 have been observed.

Those skilled in the art will appreciate that the principle of the invention can be applied in many embodiments. For example, SiF.sub.4 can be replaced with Si.sub.x F.sub.y without changing the principle of the invention. Also, TEOS can be replaced with Si.sub.x H.sub.y and oxygen. In addition, if the well known benefits of boron or phosphorous doping are desired, B.sub.2 H.sub.6, B.sub.2 F.sub.6, PH.sub.3, PF.sub.3 or any other convenient B or P precursors can be added in any desired combination to produce boron or phosphorous doped F-glass.

An advantage of using precursors that contain a Si--F or other glass-forming element-F bond (meaning by "glass-forming" an element that is capable of forming a glassy structure, such as Si, B, P, Ge, As, Se, Sb, In, Tl, Sn, or Pb) is that radicals containing these bonds may be incorporated in the glass film without breaking up the overall glass bonding network. This is in contrast with the use of C or N precursors, which disturb the network, leading to instability of the film.

For convenience in terminology, the term "precursor gas" will be taken to include the element itself; i.e. O.sub.2, as well as TEOS, will be taken to be a precursor gas for oxygen. Also, the term will be taken to include a mixture of two or more gases, as well as a single gas.

Those skilled in the art will readily appreciate that different embodiments of the invention may be made in view of the enclosed teaching and the following claims are not meant to be limited to the embodiments disclosed.