Increasing the Useful Range of Cationic Photoinitiators in Stereolithography

This invention relates to the art of stereolithography, which is a technique for forming solid shapes from a liquid polymer precursor. More particularly, the invention relates to improvements in such polymer precursors.

Stereolithography is described in U.S. Pat. No. 4,575,330 to Hull. The method involves building up a predetermined three-dimensional shape by forming a series of layers of polymerized solids. A cross-section of the solid is traced out on the surface of a bath of polymer precursors under the direction of a computer controlled system which causes the liquid to be exposed to a form of radiation such as an ultraviolet laser. After each polymerized layer is formed, it is lowered in the bath so that a new layer can be formed on top. Hull does not discuss in detail the type of polymer precursors which may be used, confining his discussion to the equipment used in the stereolithographic process. He states that the curable liquid (i.e., the polymer precursor) should cure fast enough to allow practical object formation times, should be self-adherent, should have a relatively low viscosity, should absorb UV light, should be soluble when not polymerized but insoluble when polymerized, and should be non-toxic. Hull suggests that acrylate formulations may be used and subsequent publications show that acrylate compositions have been preferred heretofore.

Acrylates are not entirely satisfactory for use in stereolithography. They are not as non-toxic as one would be like and they are not cured as rapidly and completely as would be desired. Post-curing of the solids formed by stereolithography is necessary and it is difficult to obtain rapid and complete curing of acrylates by exposure to intense UV light or exposure to elevated temperatures.

It is possible to employ polymer precursors based on vinyl ether compounds which have significant advantages over the acrylate-based formulations used heretofore in stereolithography. In co-pending U.S. patent application Ser. No. 07/661,766, filed Feb. 27, 1991, compositions of vinyl ether oligomers and monomers were shown to be suitable for stereolithography.

Further improvement in compositions useful in stereolithography have been sought, particularly with regard to improving the accuracy of the finished pans. Improved compositions comprising vinyl ethers and epoxy compounds which provide advantages over those previously disclosed are disclosed in co-pending U.S. Ser. No. 07/693,890, filed May 1, 1991 and Ser. No. 07/855,392, filed Mar. 26, 1992.

Most stereolithographic equipment has used He--Cd lasers which expose the resins to ultraviolet light having a wavelength of about 324 nm. Recently, more powerful equipment has been introduced based on Ar ion lasers which use wavelengths of 351 and 364 nm or a group of wavelengths in the range of 334 to 364 nm. Since the cationic photoinitiators used with vinyl ether-epoxide mixtures respond best to light at about 300 nm, the stereolithography lo equipment using Ar ion lasers does not operate satisfactorily with such cationic photoinitiators, as will be explained in more detail below. Consequently, the present inventors have sought and have found a method of using such cationic photoinitiators successfully with stereolithographic equipment employing Ar ion lasers.

The invention relates to improvements in stereolithography, particularly with respect to equipment which employs Argon ion lasers. Such equipment typically operates at wavelengths between 334 and 364 nm, especially at 351 and 364 nm. At such wavelengths the cationic photoinitiators used with vinyl ether-epoxide monomers, such as onium salts, are not as effective since they respond best to UV light having a wavelength of about 300 nm. The result of the mismatch in wavelengths is that the monomers cure to an excessive depth because the light is not as readily absorbed by the cationic photoinitiators. The present inventors have found that addition of a small amount of UV light-absorbing materials is sufficient to reduce the depth of cure to a predetermined value suitable for the requirements of the specific stereolithographic equipment being used. Less than about 0.2 pph by weight is needed, preferably about 0.02 to 0.2 pph by weight. Typically the UV light absorbers are aromatic compounds, particularly those having fused rings. They absorb at the wavelength of the UV source and are non-volatile, non-basic, and do not produce visible color. The UV absorption is sufficient so that the required concentration is less than 0.2 pph. The preferred compounds are anthracene and its derivatives.

The preferred anthracene and/or anthracene derivatives are selected from the group consisting of anthracene, 9-anthroic acid, 9,10-diphenylanthracene, 9,10-dimethoxy-2-ethyl anthracene, and 9-anthracene methanol. They are added singly or in combination to the monomer mixture along with the photoinitiator before the mixture is used in stereolithography.

Other related compounds which may be used include, 9-phenyl anthracene, 2-methyl anthracene, 9-vinyl anthracene, bianthranyl and 9,10-dinaphthyl anthracene. Stilbene derivatives may also be used.

In another aspect, the invention consists of a polymer precursor composition for use in stereolithography, particularly equipment employing Argon ion lasers. The composition includes vinyl ether functionalized compounds and epoxy functionalized compounds, along with an effective amount of a cationic photoinitiator, preferably an onium salt, and a sufficient amount of an ultraviolet light-absorbing compound, preferably anthracene and/or derivatives thereof to provide a predetermined depth of cure of the vinyl ether and epoxy functionalized compounds.

Another embodiment of the invention is found in an ultraviolet light-absorbing mixture comprising an onium salt cationic photoinitiator and anthracene or its derivatives.

FIGS. 1 and 2 illustrate the effect on polymer cure depth of adding an anthracene derivative to an epoxy-vinyl ether monomer mixture.

In stereolithographic applications, the monomers are polymerized in successive layers to build up a solid object by exposure to actinic light, particularly a UV or visible laser beam, such as ultraviolet light from helium/cadmium laser or an argon ion laser or visible light from an argon ion laser. After the three-dimensional shape has been formed, it is removed from the monomer bath, washed as necessary with isopropanol or other suitable solvent, and cured further by thermal means, which could be supplemented by ultraviolet or visible light if desired.

It may be helpful to briefly review the principles on which stereolithography equipment operates in order to understand the problem faced by the present inventors and its solution. Passing a laser beam over the surface of a monomer bath causes the monomers to be polymerized so that a thin layer of polymer is formed. These are built one on top of the other until the desired three-dimensional object is completed. To accomplish this objective one must consider a number of factors.

The laser introduces light energy (photons) into the liquid monomers along a narrow path. If there is sufficient total energy present, the photoinitiator will decompose and cause polymerization to occur. The minimum amount of energy required is termed Ec or E.sub.crit. As the amount of energy (light exposure) is increased, the depth to which the monomers are polymerized is increased. This is termed Cd or cure depth. The relationship between the cure depth and the logarithm of the total light energy provided to each unit of area (commonly called the "working curve") should be linear and where this is so, the slope of the line on a plot of Cd versus log.sub.e E is called the depth of penetration, or Dp. This is a measure of the depth to which the light beam penetrates the liquid monomer. If the value is too large, say 2 to 4 times the desired thickness of the layer being produced, then the volume of the polymer is usually found to be greater than the volume being traced out by the laser beam. On the other hand, if the Dp value is 2 to 4 times smaller than the desired thickness of the layer, then the polymer depth is insufficient.

The actual depth to which the laser light penetrates is determined by the absorbence of the monomers and the photoinitiator. In practice, since the photoinitiator is to absorb light and release the moieties which catalyze the polymerization, the mount of the photoinitiator is adjusted to control the depth of penetration and the cure depth for a given amount of light energy or exposure. Thus, for a given beam of fixed power and wavelength, the amount of the photoinitiator used will control the minimum amount of energy needed to cure the monomer (Ec) and the depth to which it is cured (Cd).

In many stereolithographic machines He-Cd lasers are used, which irradiate the monomer bath with ultraviolet light at a wavelength of about 324 nm. When such lasers are used with conventional acrylate monomers, the radical photoinitiators used respond well, having a useful range of about 300 to 380 nm. When introducing the use of vinyl ether-epoxide compositions, which provide substantial improvements in accuracy of the three-dimensional objects formed, it was necessary to use cationic photoinitiators, particularly onium salts, rather than the radical initiators used with acrylates. Although these cationic photoinitiators respond to ultraviolet light over a frequency range of about 300 to 350 nm, they typically have a peak response at about 300 nm. This means that, although the He-Cd laser has an operating frequency of about 324 nm, it is sufficiently close to the optimum frequency for the cationic initiators that the difference has proven to be no problem in using vinyl ether-epoxide monomers, as is described in the earlier co-pending and commonly-assigned patent applications. This has not been the experience with argon ion lasers which operate at frequencies between 334 and 364 nm.

At the typical operating wavelengths of argon ion lasers, 331 to 364 nm, particularly 351 and 364 nm, the cationic photoinitiators do not absorb the ultraviolet light readily. Consequently, the light penetrates the monomer bath to an undesirably great depth and produces a poorly defined polymer layer which does not accurately represent the desired shape. Previously, one skilled in the art would have concluded that the solution to such a problem would be found in either developing a new photoinitiator having a higher peak absorption wavelength that is in the range of the argon ion laser, or else an energy transfer agent or co-initiator would have to be found to permit the photoinitiator to react more readily at the higher light frequencies typical of the argon ion laser. Another potential method of improving the amount of photoinitiator reacted and thus reducing the depth of light penetration might be to increase the amount of the photoinitiator used. However, this was found to be an impractical solution to the problem since the photoinitiators are not very soluble in the vinyl ether-epoxide monomers. Also, increasing the amount of photoinitiator would reduce shelf life of the mixture and degrade the color of the polymer.

The solution to the problem was found by the present inventors in the addition of small amounts of ultraviolet light-absorbing compounds, particularly of anthracene or anthracene compounds which absorb light in the wavelength range of the argon ion laser, preventing it from penetrating too deeply into the monomer bath. At the same time, these additives also absorb light at wavelengths which will excite the cationic photoinitiators, making it possible to reduce the depth of cure and consequently to produce thinner more accurate polymer layers. While absorbing light at the frequencies of the argon ion laser, the anthracene (or its compounds) fluoresces rather than producing heat, thus having little effect on the temperature of the monomer bath and the speed of polymerization which would result at higher temperatures.

The UV light-absorbing materials should be chosen from those which absorb strongly at the wavelengths of the argon ion laser (between 334 and 364 nm) but not absorb strongly at the lower wavelength of the helium-cadmium laser (325 nm) and below. Also, such materials should not react detrimentally with the photoinitiators or the resins. In particular, compounds which have desirable light-absorbing properties but are basic in nature, such as aromatic compounds which have amine, sulfide, or amide moieties should be avoided since they will interfere with the acid species released by the cationic photoinitiators used with vinyl ether-epoxide resins. In addition to these properties, the UV light absorbers should be reasonably soluble in the resins to be polymerized and should not add undesirable color to the product.

Preferred light-absorbing materials include aromatic compounds which have fused rings and particularly anthracene and its derivatives. Especially preferred are members of the group consisting of anthracene, 9-anthroic acid, 9,10-diphenyl anthracene, 9,10-dimethoxy-2-ethyl anthracene, and 9-anthracene methanol.

Other related compounds which may be useful include 9-phenyl anthracene, 2-methyl anthracene, 9-vinyl anthracene, bianthranyl and 9,10-dinaphthyl anthracene.

Additional aromatic compounds may have application where they satisfy the requirements above, for example, stilbene derivatives, such as BPSB (p-bis(p-propylstryl) benzene) and BMSB (p-bis(methylstryl)benzene).

The absorbers are used in small quantities, generally less than 0.2 pph based on the monomers, preferably about 0.02 to 0.2 pph. The amounts added to the monomer bath will be chosen to control the penetration depth, Dp, so that the cure depth will satisfy the requirements of the laser and of the layer thickness wanted.

Compositions for use in stereolithography comprise vinyl ethers and epoxides. In general, vinyl ether functionalized compounds of interest would include those derived from urethanes, phenols, esters, ethers, siloxanes, carbonates and aliphatic or aromatic hydrocarbons. The epoxides will generally include the broad classes of available epoxy functionalized compounds such as those derived from phenols, particularly bisphenol A, novolacs, linear or cycloaliphatic diols, polyether diols and siloxanes.

By combining vinyl ethers with epoxides it is possible to rapidly cure the vinyl ethers while leaving the epoxide largely uncured. This provides a "green part" having sufficient strength to be handled but having little distortion. Then, the green piece can be thermally post-cured so that the epoxide cures under the influence of the photo acids generated during the UV or visible laser exposure. Thermal post-curing preferably is isotropic and any additional shrinkage that occurs should not produce additional distortion in the part.

The vinyl ethers may include vinyl ether oligomers and/or multifunctional and/or monofunctional vinyl ether monomers.

The vinyl ether oligomers may be generally described as

where

R' and R" are H or an alkyl group having 1 to 10 carbon atoms

A is a moiety derived from urethanes, phenols, polyesters, polyethers, polycarbonates, or polysiloxanes and has a molecular weight of about 400 to 10,000

Z is a moiety derived from a saturated aliphatic or cycloaliphatic hydrocarbon or a polyalkylene ether and has a molecular weight of about 28 to 250

n is an integer from 2 to 6, preferably 2 or more.

Such oligomers are described in detail below.

Where A is derived from a urethane the vinyl ether urethane oligomer may be obtained by reacting

(i) a hydroxyl-terminated polyester having the formula ##STR1## where

X and Y are divalent radicals having a molecular weight of about 28 to 500 and selected from the group consisting of alkylene, arylene, aralkylene, and cycloalkylene radicals

m has an average value of about 1 to 100

and (ii) a diisocyanate having the formula

where

Q is a divalent radical selected from the group consisting of alkylene, arylene, aralkylene, and cycloalkylene radicals

or a polyisocyanate having a functionality greater than 2 and (iii) a hydroxy monovinyl ether having the formula

where

R' and R" are monovalent radicals selected from the group consisting of H and alkyl groups having 1-10 carbon atoms

Z is a divalent radical having a molecular weight of about 28 to 250 and selected from the group consisting of alkylene, cycloalkylene, or polyalkylene ether radicals

In an alternative embodiment, the vinyl ether urethane oligomer may be one in which the polyester of (i) is replaced entirely or in part by a hydroxy-terminated polyether having the general formula

where

m and x are as defined for the polyester of (i).

The moieties X and Y may be alkylene groups, especially those containing up to about 20 carbon atoms, a cycloalkylene group, an arylene, or aralkylene group. Examples of the alkylene moieties which may be used include ethylene, propylene, butylene, pentylene, hexylene, heptylene, octylene, nonylene, decylene, undecylene, dodecylene, tridecylene, tetradecylene, pentadecylene, hexadecylene, heptadecylene, octa-decylene, nonadecylene, and eicosylene. Examples of arylene groups include phenylene, naphthylene, anthrylene, phenanthrylene, etc. Cycloalkylene groups include the cyclopentylene, cyclohexylene, cycloheptylene, cyclooctylene, and cycloalkylene groups containing 1 or more alkyl groups on the nucleus. Similarly, the arylene groups which may be used for Y also may contain one or more alkyl groups on the aromatic ring, especially where such alkyl groups contain up to about 6 carbon atoms. Examples of aralkylene groups include benzylene, 1-phenethylene, 2-phenethylene, 3-phenylpropylene, 2-phenylpropylene, 1-phenylpropylene, etc. Particularly useful Y groups are --(CH.sub.2).sub.n -- groups where n is 2, 3, or 4; 1,2, 1,3, or 1,4 phenylene groups; and 1,4 cyclohexylene groups. Particularly useful X groups are --CH.sub.2 CH.sub.2 --; --CH.sub.2 CH.sub.2 --O--CH.sub.2 CH.sub.2 --; --CH.sub.2 --(CH.sub.3)CH--; --(CH.sub.2).sub.n -- where n is 4 or 6; --CH.sub.2 --(CH.sub.3).sub.2 C--CH.sub.2 --; 1,4 phenylene; and 1,4-bis(methyl)phenylene.

m will be an integer from 1 to about 100, preferably from 1 to 10.

Particularly preferred hydroxyl-terminated polyesters include poly(propylene adipate), poly(neopentyl adipate), poly(1,4-butane adipate), poly(1,6-hexane adipate), poly(neopentyl isophthalate), and poly(1,6-hexane isophthalate). Polyesters derived from mixed polyols or acids may be useful. Particularly important are polyesters in which triols such as trimethylol propane or glycerol are incorporated into the polyester to produce a polyester with a functionality >2. The preferred molecular weights for the polyesters will be about 500 to 5000.

In the alternative embodiment where polyethers are used, X preferably will be --CH.sub.2 CH.sub.2 --, --CH.sub.2 (CH.sub.3)CH--, and --CH.sub.2 CH.sub.2 CH.sub.2 CH.sub.2 --. The molecular weight preferably will be about 250 to 5,000. Mixed polyethers may also be used, for example, those derived from a polyol, such as ethoxylated or propoxylated trimethylol propane.

A broad variety of diisocyanates may be used and may be exemplified by such materials as the toluene diisocyanates (TDI), p- and m-phenylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, 2,2,4-trimethylhexamethylene diisocyanate, 1,4-cyclohexane diisocyanate, 4,4'-di-cyclohexylmethane diisocyanate (Desmodur W), 4,4'-diphenylmethane diisocyanate (MDI), 3,3'-dimethyl-4,4-diphenylmethane diisocyanate, 1,5-tetrahydronaphthalene diisocyanate, naphthalene-1,5'-diisocyanate, bis(2-methyl-3-isocyanatephenyl)methane, 4,4'-diphenylpropane diisocyanate, tetramethylxylene diisocyanate (TMXDI), isophorone diisocyanate (IPDI).

Polyisocyanates with a functionality of 2 or more such as are described and discussed in U.S. Pat. No. 4,433,067, especially the polyisocyanates based on methylenediphenyl diisocyanate, especially the 4,4'-isomer and the uretonimine modified MDI as described there, also may be utilized. The term polyisocyanate also includes quasi prepolymers of polyisocyanates with active hydrogen containing materials where the polyisocyanate is typically reacted with from about 0.05 to about 0.3 equivalents of a polyol. Although a vast number of polyisocyanates are suitable, in practice polyisocyanates based on MDI and TDI may be preferred for economy and general availability.

Among the most desirable isocyanates may be mentioned 4,4'-diphenylmethane diisocyanate, toluene diisocyanate, isophorone diisocyanate, m-tetramethylxylene diisocyanate, 4,4'-dicyclohexylmethane diisocyanate (Desmodur W), and 1,6-hexamethylene diisocyanate.

The vinyl ether terminated alcohols which are used in preparing the oligomeric esters have a structure corresponding to the adduct of an alkyne and a diol. In one method, a diol may be reacted with acetylene. However, these vinyl ether terminated alcohols also can be made in other ways, and the method of producing them is not part of this invention. The resulting hydroxy monovinyl ether may be purified or in many cases the reaction mixture, which includes divinyl ether and residual diol may be used directly. The alkyne has the generic formula R'C.tbd.CR", and the diol has the generic formula HO--Z--OH. The generic formula of the vinyl ether terminated alcohols of our invention is

The groups R' and R" are independently selected from the group consisting of hydrogen and lower alkyl moieties containing from 1 to 10 carbon atoms, although those with from 1 to about 4 carbon atoms are favored. It is preferable that both R' and R" are not alkyl moieties, for in the case where both are lower alkyl groups this causes an undesirable reduction in polymerization rate of the oligomers of our invention. Where R' is an alkyl moiety it is preferred that R" be hydrogen, and conversely; where R' is hydrogen then R' should be an alkyl of 1 to 4 carbons. In a preferred embodiment R' or R" is a methyl group and R" and R' is hydrogen. In a still more preferred embodiment both R' and R" are hydrogen.

Z will be a divalent radical having a molecular weight of 28 to about 250 and selected from the group consisting of alkylene, cycloalkylene, or polyalkylene ether radicals. In one preferred embodiment, Z is ethylene, butylene, or dimethylene cyclohexane radicals.

Among the diols one important class consists of alkylene glycols, HO(C.sub.n H.sub.2n)OH, where n is an integer from 2 to about 10. The linear alkylene glycols, HO(CH.sub.2).sub.n OH, (polymethylenediols), where n is an integer from 2 to about 10, are particularly useful, especially where n is from 2 to about 6. Illustrative of the members of this group are such diols as ethylene glycol, 1,3-propylene glycol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,7-heptanediol, 1,8-octanediol, 1,9-nonanediol, and 1,10-decanediol (decamethylene glycol).

The nonlinear or branched alkylene diols also may be used, where such glycols contain from 3 up to about 10 carbon atoms. Examples include 1,2-propylene glycol, 2,3-butanediol, 2,3-dimethyl-2-3-butanediol, 2,3-dimethyl-1,4-butanediol, 2,2-dimethyl-1,3-propanediol(neopentylglycol).

Another useful class of diols are the polyalkylene glycols, especially poly(ethylene) glycols, HO[--CH.sub.2 CH.sub.2 O--].sub.m OH, and poly(propylene) glycol, HO[--CH(CH.sub.3)CH.sub.2 O--].sub.m OH, where m is an integer from 1 up through about 50, although more usually m is an integer from 1 up to about 10, and most preferably from 1 up to about 5. Examples of these glycols include diethylene glycol, triethylene glycol, tetraethylene glycol, pentaethylene glycol, hexaethylene glycol, etc., along with the analogs of the propylene glycols.

Of particular importance is the case where Z is a divalent radical whose parent is a cycloalkane, such as cyclopentane, cyclohexane, cycloheptane, or cyclooctane, preferably the bishydroxy alkyl derivatives. The preferred diols are the 1,3-bis(hydroxyalkyl)cyclopentanes and the 1,4-bis(hydroxyalkyl)cyclohexanes, -cycloheptanes, and -cyclooctanes, particularly the cyclohexanes. Diols substituted at positions different from those specified above may be used in the practice of this invention, but not necessarily with equivalent results. The bis(hydroxymethyl)cyclohexanes are preferred as they are readily available from the reduction of the corresponding phthalic acids, and among these 1,4-bis(hydroxymethyl)cyclohexane is favored.

Of the hydroxy monovinyl ethers which are produced by the reaction of acetylene with the diols described above, those which are especially preferred include 4-hydroxybutyl vinyl ether, 4-hydroxymethyl cyclohexylmethyl vinyl ether, 2-hydroxy ethyl vinyl ether, triethylene glycol monovinyl ether, and diethylene glycol monovinyl ether. In addition to the pure hydroxymonovinyl ether, mixtures containing the corresponding divinyl ether R'HC.dbd.CR"--O--Z--O--R" C.dbd.CHR' and/or the parent diol HO--Z--OH may also be used.

An important characteristic of the vinyl ether terminated urethane oligomers is that in all cases there are few hydroxyl groups derived from the polyester, polyether or hydroxy monovinyl ether in the final product. That is, less than about 10% of the initial hydroxyl groups remain unreacted. It is most preferable that the oligomeric vinyl ether terminated product contain no detectable free hydroxyl groups, i.e., less than about 1% of the initial hydroxyl groups of the reactant mixture remain unreacted. It is also important that there should be essentially no free isocyanate groups remaining in the product, that is, less than about 1% of the initial isocyanate groups of the reactant mixture. In general, the ratios of polyester (a), diisocyanate (b) and monovinyl ether (c) are selected to provide an equal number of equivalents of hydroxyl and isocyanate groups.

The vinyl ether urethane oligomers may be formed by reacting the hydroxyl-terminated polyester (a) with the isocyanate compound (b) or by reacting the isocyanate (b) with the hydroxy vinyl ether (c) and thereafter reacting the adduct with the remaining component or alternatively, the three components may be co-reacted. The ratios of (a), (b), and (c) will be chosen so that the ratio of the total number of hydroxyl groups from (a) and (c) to the number of isocyanate groups from (b) is about 1:1. The ratio of the number of hydroxyl groups from (a) to the number of hydroxyl groups from (c) should be in the range from about 0.5 to 5. The reaction may be carried out at temperatures in the range of 0.degree. to 150.degree. C. Solvents such as diethyl ether, methylene chloride, or toluene may be employed and later removed from the oligomers, or the components may be reacted in the absence of solvents. Divinyl ether monomers such as 1,4-cyclohexane dimethanol divinyl ether or triethylene glycol divinyl ether may also be used as solvents. Such compounds may be obtained as by-products in the preparation of hydroxy monovinyl ethers. Since they have no free hydroxyl groups they do not react with the isocyanates, but may remain with the oligomers and become included in the formulations used for stereolithography.

The reaction may be carried out without a catalyst, but a tin containing catalyst such as dibutyl tin dilaurate may be used.

Where A is derived from a polyester, they may be considered the product obtained by reacting

(a) a dicarboxylic acid having the formula ##STR2##

where X, Y, and m are defined above with respect to vinyl ether urethane oligomers

(b) with a hydroxy monovinyl ether having the formula

where R', R" and Z are defined above with respect to vinyl ether urethane oligomers

Where A is derived from a polysiloxane, they will typically include those in which a polysiloxane having Si--H groups is reacted by hydrosilation with a vinyl ether containing a second C.dbd.C group not directly bonded to an oxygen atom. The vinyl ether polysiloxanes may be defined as

where

R', R", and Z are as defined above.

n is an integer from 2 to 8

A' is a polysiloxane having n Si--H groups and a molecular weight of 140 to 5,000

The polysiloxane may be linear, cyclic, or a combination of both types and may be substituted with aliphatic or aromatic moieties. Preferred substituents on the Si atoms are methyl and phenyl groups.

Where A is derived from a phenol, they may be defined as

A" is a polyvalent aromatic radical having a molecular weight of about 152 to 5,000

R', R" and Z are as defined above

n is 2 to 6

In one preferred embodiment Z is ethylene and A" is derived from 4',4'-isopropylidene diphenol (i.e. bisphenol A).

Where A is derived from a polyether they may be obtained by reacting poly(ethylene oxy), poly(propylene oxy) or poly(butyleneoxy) glycols, i.e., HO--[--CH.sub.2 CH.sub.2 O].sub.m --H, HO--[--CH(CH.sub.3)CH.sub.2 O].sub.m --H, or HO--[--(CH.sub.2)4O].sub.m --H, respectively, where m has an average value from 2 to 50 with acetylene or a vinyloxy alkyl halide, for example, 2-chloroethyl vinyl ether.

Vinyl ether terminated carbonates may be described by the formula ##STR3## where

p is 4 to 10

Z is a divalent radical as defined above

X is a diester, diol, or polyol moiety

The structure of the vinyl ether monomers may be similar to those of the oligomers described above but the monomers will have lower molecular weights. When their viscosity is low, they are useful as reactive diluents in the stereolithography formulations.

The vinyl ether monomers may be generally described by the formula

where

R' and R" are as defined above

Z is as defined above

n is an integer from 1 to 4

B is derived from aromatic and aliphatic hydrocarbons, esters, ethers, siloxanes, urethanes, and carbonates, and has a molecular weight of about 60 to 400

Monofunctional monomers are those which have n=1, while the multifunctional monomers are those which have n=2 to 4.

Vinyl ether terminated ester monomers may be described by the formula ##STR4## where

n is 1 to 4,

M.sub.1 is a mono, di, tri, or tetra functional radical having a molecular weight of 15 to 180 and selected from the group consisting of alkylene, arylene, aralkylene and cycloalkylene radicals,

Z is a divalent radical having a molecular weight of 28 to 290 and selected from the group consisting of alkylene, cycloalkylene, or polyalkylene ether radicals,

R' and R" are monovalent radicals selected from the group consisting of H and alkyl groups having 1-10 carbon atoms

In one preferred embodiment M.sub.1 is a mono, di, tri, or tetra functional radical of benzene. In another embodiment, M.sub.1 is alkylene with 2-4 carbon atoms and Z is the .alpha.,.alpha.' diradical derived from 1,4-dimethylcyclohexane.

Vinyl ether terminated ether monomers are related to the polyether oligomers described above but the molecular weight is much lower, i.e., "m" is only about 1 to 5.

Vinyl ether terminated aliphatic monomers may be described by the formula

where

n is 1 to 4

M.sub.2 is a mono, di, tri, or tetra functional aliphatic or cycloaliphatic radical having a molecular weight of about 56 to 500

Z is a divalent radical as defined above

R' and R" are monovalent radicals as defined above

Vinyl ether terminated aromatic monomers may be described by the formula

where

n is 1 to 4

M.sub.3 is a mono, di, tri, or tetrafunctional aromatic radical having a molecular weight of about 77 to 500

Z is a divalent radical as defined above

R' and R" are monovalent radicals as defined above

Vinyl ether terminated siloxane monomers are related to the polysiloxane oligomers described above but the molecular weight is lower, i.e. A' has a molecular weight of about 140-500.

Vinyl ether terminated carbonate monomers are related to the oligomers described above but the molecular weight is lower, i.e. p is only about 0 to 3.

The vinyl ethers found to be useful may also be characterized by their physical properties and will generally have as many as possible of the following properties.

have a fast cure under UV laser exposure so that a rigid "green" part can be made

have low viscosity to facilitate flow of the prepolymers over the surface of the article being formed

have a relatively high modulus as first formed by the laser beam, i.e., in the green form

have a functionality of at least 2, that is, have at least two vinyl ether moieties in each molecule

have minimal absorption of light from the laser beam

Preferred vinyl ethers which have been found to be particularly useful include bisphenol A derivatives and other aromatic vinyl ethers including ##STR5## where

x is 2 or 4

y is 2 or 3 ##STR6## where

y is 2

and ester derived vinyl ethers including ##STR7## where

x is 2, 3, or 4

y is 2 or 4

and ##STR8## where

x is 2, 3, or 4

and cycloaliphatic diol derived vinyl ethers including ##STR9## and poly ether derived divinyl ethers including

where

x is 2, 3, or 4 ##STR10## where

x is 2, 3, or 4

and phenol derived vinyl ethers including ##STR11## where

R is H or CH.sub.3

Vinyl ether oligomers may include urethane oligomers derived from isocyanates, such as MDI (4,4'-diphenylmethane diisocyanate), reacted with a hydroxyl terminated polyester such as poly(propylene adipate) and a mono vinyl ether such as cyclohexane dimethanol vinyl ether. Polyether oligomers may include polytetrahydrofuran reacted with acetylene to form the vinyl ether. Polyester oligomers include the reaction product of polytetrahydrofuran with dimethyl adipate, end-capped by reaction with bis(4-vinyloxybutyl)isophthalate.

The epoxides which are useful in the invention should have as many as possible of the following properties

have a functionality of at least two; that is, have at least two oxirane moieties for each molecule

have a low cure rate relative to the vinyl ethers used in the formulation

contribute a low viscosity to the formulation

do not plasticize vinyl ether polymerized by the laser

are miscible with the selected vinyl ethers

have minimal absorption of light from the laser beam

Preferred epoxides include those derived from phenols, particularly bisphenol A, novolacs, linear and cyclo aliphatic polyols, poly ether polyols and siloxanes. In general, many of the available epoxides may find application in the invention. Of particular interest are glycidyl ethers of phenols. Cycloaliphatic epoxides, which may be used but not necessarily with equivalent results. Examples of glycidyl ethers are bisphenol A diglycidyl ethers (e.g. DER 331, 332, Dow Chemical) and Epon 828, Shell Chemical). Other examples are epoxy novolacs (e.g. Quatrex 240, DEN 431, Dow Chemical) and epoxy cresols (e.g. Quatrex 3310, Dow Chemical). Examples of cycloaliphatic epoxides (e.g. ERL-4221, ERL-4299, ERL-4234, Union Carbide).

In general, the formulations should have a viscosity in the range of 50 to 50,000 mPas, preferably 50-5000 mPas. The viscosity of the formulation should be relatively low in order to facilitate the movement of the liquid prepolymers over the solid piece being formed by the stereolithography apparatus. The vinyl ethers may have a high viscosity with the epoxides having low viscosity or vice versa. Alternatively, both may have low viscosity. High viscosities are useable, but not preferred.

The proportions of vinyl ethers and epoxides do not depend on their reaction with each other, since they primarily form homopolymers and the final product may be an interpenetrating polymer network. However, the proportions must be selected so that the green structure has acceptable strength and can retain the substantially unreacted epoxides until thermal post-curing can be carried out. It has been found that the proportions of vinyl ethers and epoxides should be within the boundaries defined by the formula ##EQU1## where

M is the vinyl ether equivalent weight of the composition

F is the total weight in grams of the composition, including both vinyl ether and epoxy compounds

E is the number of vinyl ether equivalents in the composition

The vinyl ether equivalent weight (M) should be between 80 and 800 and preferably between 120 and 450. The defining equation takes no account of the relative number of equivalents of epoxide groups, only the equivalents of vinyl ether groups. If the vinyl ether equivalent weight (M) is too high, the green strength may be too low. If M is too low, the curl distortion may be too high. In practice, the M value chosen will depend on the amount of distortion or linear shrinkage which can be tolerated for the parts to be made from the formulation.

Another factor to be considered is the relative reaction speed of the vinyl ethers. Generally, the vinyl ether oligomers are less reactive, particularly the urethane oligomers. Since they also have a greater weight for the number of vinyl ether equivalents the value of M will be higher, making it desirable to include lower molecular weight polyfunctional vinyl ethers to decrease the value of M.

The value of E.sub.c or E.sub.crit is also a factor which must be considered when formulating for a stereolithographic application. This is defined as the lowest light exposure which forms a polymer. It is commonly measured by the technique described in Example 2 below. Too low a value of E.sub.c is undesirable since the formula may prematurely polymerize or it may decrease the accuracy of the parts. A high value of E.sub.c implies a slower rate of reaction and reduced production of parts. However, compensation is possible when formulating so that a desired value of E.sub.c is obtained by adjusting the amount of the photoinitiator. Among the vinyl ether oligomers and monomers the value of E.sub.c is affected by the molecular composition and structure of the substituents. For example, adding low molecular weight vinyl ethers will generally decrease the value of E.sub.c, while increasing the amount of vinyl ether oligomers will generally increase the value. The present inventors have found that E.sub.c is not significantly affected by addition of anthracene or its derivatives in the small amounts required to change the depth of cure of the monomers.

Ambient humidity will affect the rate of polymerization. Consequently, it may be necessary to adjust the value of E.sub.c by reformulation, typically to lower the E.sub.c to compensate for the effect of increased humidity.

Still another factor to be considered is the effect of heat released during polymerization. When the polymerization reaction is too fast, damage to the polymer may result. Less reactive vinyl ethers would be chosen to avoid such a result or the value of M could be increased. An advantage of using anthracene or its derivatives to adjust the depth of cure that their response is to fluoresce rather than to generate heat which could adversely affect the polymerization of vinyl ethers and epoxides.

An effective mount of a cationic photoinitiator is used to cause the vinyl ethers to react and produce the desired polymer. The recognized classes of cationic photoinitiators include various compounds which respond to irradiation by producing acid species capable of catalyzing cationic polymerization. See Crivello, Advances in Polymer Science, 62, p. 1-48 (1984). Onium salts of Group V, VI, and VII elements are stated to be the most efficient and versatile of the cationic photoinitiators. They generate strong Lewis acids which can promote cationic polymerization. Curing of the vinyl ether compositions of the invention is not limited to a particular class of such photoinitiators, although certain types are preferred, including onium salts based on halogens and sulfur. More specifically, the onium salt photoinitiators described in Crivello's U.S. Pat. No. 4,058,400 and in particular iodonium and sulfonium salts of BF.sub.4 --, PF.sub.6 --, SbF.sub.6 --, and SO.sub.3 CF.sub.3 --. Preferred photoinitiators are triarylsulfonium salts, and diaryliodonium salts. Preferred anions are hexafluorophosphate and hexafluoroantimonate. They are usually required in amounts from about 0.1 to 5 wt. % in the blended formula of vinyl ethers and epoxides. Preferred initiators include: ##STR12## where

X is SbF.sub.6 -- or PF6--

Commercially available initiators include UVI-6974 (an SbF6- salt) and UVI-6990 (a PF6- salt) supplied by Union Carbide. Other cationic photoinitiators are defined by the formulas ##STR13## where

y is 1 to 18

In addition to the principal ingredients discussed above, the formulations may also contain dyes, stabilizers, fillers, pigments, and antioxidants such as hindered phenols, wetting agents such as fluorosurfactants e.g. FC-430 from 3-M, photosensitizers such as benzophenone, thioxanthone, perylene and other components familiar to those skilled in the art.

A stereolithographic composition was prepared by mixing 56% by weight of isophthaloyl-dibutyoxy vinyl ether (4010 SF, AlliedSignal) and 44% by weight of the diglycidyl ether of bisphenol (DER-33 1, Dow Chemical) with 0.475 pph of UVI-6974 (Union Carbide) a triaryl sulfonium salt as a cationic photoinitiator.

A sample of the composition of Example 1 was placed in a shallow dish in a 3D Systems Model SLA-190 stereolithographic unit and maintained at 30.degree. C. The He--Cd laser (325 nm and 10.0 mW) was scanned across the resin to produce a series of small rectangular shaped cured layers which had been exposed to different doses of UV light by varying the speed of the laser beam's movement. The test part was removed from the bath after less than one minute and the thickness of the rectangular layers were measured with a micrometer to provide the depth of cure obtained with each dose of UV light. This information when plotted yields a straight line relationship between the logarithm of the light dose (exposure) and the depth of cure. Where the line intersects the exposure axis defines the critical exposure Ec, which is the least exposure which will produce polymerization. The slope of the line defines Dp, which is called the "penetration depth" although it is more accurately stated as the change in cure depth for a change in exposure (light dose). Such a graph will be found in FIG. 1 below, which illustrates the effect of adding 0.2 pph of an anthracene derivative (2-ethyl-9-10-dimethoxy anthracene) to an epoxy-vinyl ether mixture.

The variation of the minimum exposure needed to cure the monomers (Ec) and depth of cure with exposure (Dp) with the amount of the photoinitiator was measured by the method of Example 2 is shown in the table below, for measurements made with the SLA-190 He--Cd laser.

It can be seen that addition of the photoinitiator decreases both the UV exposure needed for polymerization (Ec) and the change of the depth of cure with UV exposure (Dp).

The measurements of Example 3 were repeated using a SLA-190 (3D Systems, Inc.) stereolithographic apparatus employing an Argon ion UV laser as an excitation source, operating at a wavelength of 351 nm and power of 19.2 mW. The variation of E.sub.c and Dp are reported in the following table.

Comparing the results in Table B with those of Table A, it can be seen that the minimum UV dose required with the Argon ion laser is much larger than with the He--Cd laser. This is believed to be the result of the longer wavelengths of the Argon laser which are further removed from the optimum wavelength (300 nm) to which the onium salt photoinitiator responds. The cure depth change is also much larger for the Argon laser. The result is that the laser beam penetrates too deeply and the definition of the region where the polymer is formed is degraded. While the preferred value of Dp will depend on a number of factors, it is generally the case that values of about 5.5 to 8.0 mils (0.14 to 0.20 mm) are preferred.

The effect of adding an anthracene derivative, 9-anthracene methanol (AM), to the composition of Example 1 was determined as in Examples 2 to 4, with the results obtained being reported in the following table.

It can be seen that the addition of the anthracene methanol has the effect of reducing the UV exposure required to polymerize the monomers and of reducing the depth of polymer curing. The changes in Ec and Dp are particularly noticeable in the case of the Argon ion laser. The practical effect of these changes is that with the addition of the light screen the resin is able to be used with Argon ion lasers to make useful three-dimensional parts.

The experiments of Example 5 were repeated in greater detail with respect to the performance of the Argon ion laser equipment. The results of tests in which the concentration of the photoinitiator and the 9-anthracene methanol were varied in a monomer mixture as in Example 1 are presented in the following table.

It may be concluded from the above table that Dp is affected mainly by changes in AM concentration, while E.sub.c is mainly affected by changes in photoinitiator concentration.

The absorbance or optical density was measured by ultraviolet spectroscopy using monomer compositions according to Example 1 in which the amounts of photoinitiator and 9-anthracene methanol were varied. Values which correspond to the characteristic wavelengths of He--Cd (324 nm) and Argon ion (332, 334, 350, 352, 364 nm) lasers are reported in the following table.

It can be seen that the addition of 9-anthracene methanol markedly changed the absorption of the AR light at all of the wavelengths measured. This increase in light absorption is particularly noticeable in the region of the Argon ion laser. This means that Dp will change and thus, the slope of the "working curve" of the cured polymer.

The monomer composition of Example 1 was tested according to the method of Example 2 using an Argon ion laser providing wavelengths of 333.6, 334.4, 335.8, 351.4, 351.1, and 363.8 nm (Innova 305). The concentration of 2-ethyl-9,10 dimethoxy anthracene was varied to show the effect on the minimum exposure for polymerization (Ec) and the change in cure depth for each unit of UV exposure (Dp). The results are shown in the following table and in FIG. 2.

It can be seen that the minimum UV exposure (Ec) did not correlate with the concentration of AM, but Dp was a linearly decreasing function of AM concentration.

The viscosity at various temperatures was measured with a Brookfield DV-I instrument (spindle #28) for the formulation of Example 1 and a second formulation including 0.1 pph of 9-anthracene methanol. The results are shown in the following table.

The change in viscosity upon aging appears not to have been affected by adding anthracene methanol. It may be concluded that the shelf life of the formulation was not significantly affected.