US 5,488,123 AGrant
Polycondensates Containing Polysiloxane Groups
Issue Date:1996-01-30
•15 Claims
Abstract
The present invention relates to polycondensates of the general formula I ##STR1## in which ##STR2## and the other variables are defined as indicated in claim 1, processes for their preparation and their use.
Metadata
Assignee
- Cassella AG
Inventors
- Fritz Engelhardt
- Jurgen Kuhlwein
- Wilfried Schuler
- Ralf Zerrer
- Werner Antwerpen
Application Information
Application Number:US 3844048
Filing Date:1995-02-06
Priority Date:1994-02-11
Art Unit:124
Classifications
IPC:
C07F 708
Field of Search:
5565288437;439;440;442;42826DIG. 1;DIG. 4;115.64
Patent Drawings
This patent does not have any drawings.
Description
The present invention relates to polycondensates containing polysiloxane groups, processes for their preparation and their use.
It has been known for a long time that hydrophilic block copolymers can be employed both as soil release agents and as antistatics in the field of textile finishing.
Recently, certain polycondensation products have increasingly been employed as soil release components in detergent formulations. The hydrophilicity necessary for this purpose is achieved by 0 to 30 mol % of dicarboxylic acids or diol components carrying sulpho groups or salts thereof. Additionally, the hydrophilicity can be increased by use of long-chain poly (oxyalkylene) oxy units.
The chain length or the molecular weight of such products can be set by appropriate conduct of the reaction or alternatively by use of monofunctional components which function as chain caps (so-called "end caps"). Such "end caps" can be anionic or non-ionic and, for example, carboxylic acids or alcohols (see, for example, U.S. Pat. No. 4,721,580, U.S. Pat. No. 4,702,857, U.S. Pat. No. 4,711,730 and U.S. Pat. No. 4,713,194).
The present invention relates to polycondensates of the general formula I ##STR3##
in which
x denotes ##STR4##
R.sup.1 and R.sup.1' independently of one another denote hydrogen, (C.sub.1 -C.sub.22) alkyl, (C.sub.2 -C.sub.22) -alkenyl, (C.sub.3 -C.sub.8) -cycloalky, (C.sub.6 -C.sub.14)-aryl, (C.sub.6 -C.sub.14) -aryl- (C.sub.1 -C.sub.8) -alkyl, MO.sub.3 S--R.sup.6 --, MO.sub.3 S--, ##STR5##
R.sup.2 to R.sup.2g independently of one another denote (C.sub.1 -C.sub.30)-alkylene, (C.sub.3 -C.sub.8) -cycloalkylene and/or (C.sub.2 -C.sub.30)-alkenylene, each of which can be substituted by a radical R.sup.1 ;
R.sup.3 and R.sup.3' independently of one another denote (C.sub.1 -C.sub.22)-alkylene, (C.sub.3 -C.sub.8) -cycloalkylene, (C.sub.2 -C.sub.22)-alkenylene and/or (C.sub.6 -C.sub.14)-arylene, where 0 to 30% of all the radicals R.sup.3 and R.sup.3' carry an --SO.sub.3 M substituent;
R.sup.4 denotes (C.sub.1 -C.sub.30)-alkylene, (C.sub.3 -C.sub.8)-cycloalkylene or (C.sub.2 -C.sub.30 )-alkenylene;
R.sup.5 , R.sup.5' and R.sup.5" independently of one another denote hydrogen, (C.sub.1 -C.sub.30)-alkyl, (C.sub.3 -C.sub.8)-cycloalkyl or (C.sub.2 -C.sub.30)-alkenyl;
R.sup.6 is defined as R.sup.3, but independently of this;
R.sup.7 denotes (C.sub.1 --C.sub.22)-alkyl, (C.sub.3 -C.sub.8) -cycloalkyl or (C.sub.2 -C.sub.22)-alkenyl, where 0 to 30% of all the radicals R.sup.7 carry an --SO.sub.3 M substituent;
M denotes hydrogen, an alkali metal, the ammonium group or a substituted ammonium group;
n.sup.1 to n.sup.7 independently of one another denote an integer from 0 to 40;
p and q independently of one another denote an integer from 2 to 20;
s denotes 0 or 1;
t denotes an integer from 0 to 80;
w denotes an integer from 0 to 80; and
v denotes an integer from 0 to 80 and
y denotes an integer from 1 to 20.
Alkyl groups can be straight-chain or branched and are, for example, methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl, sec-butyl, tert-butyl, n-pentyl, 3-methylbutyl, 3-pentyl, n-hexyl, 2-ethylbutyl, n-heptyl, i-heptyl, 2-octyl, 2-ethylhexyl, i-nonyl n-decyl, i-decyl, n-dodecyl, n-hexadecyl or n-octadecyl. (C.sub.1 -C.sub.5) -alkyl is preferred and (C.sub.1 -C.sub.3)-alkyl is particularly preferred.
Alkylene groups can likewise be straight-chain or branched. Examples are ethylene, n-propylene, i-propylene, n-butylene, i-butylene, sec-butyl, tert-butylene, n-pentylene, 1,3-methylbutylene, n-hexylene, 2-ethylbutylene, n-heptylene, i-heptylene, octylene, 2-ethylhexylene, i-nonylene, n-decylene, i-decylene, n-dodecylene, n-hexadecylene and n-octadecylene.
R.sup.2 to R.sup.2f alkylene groups preferably have 2 to 5 carbon atoms and particularly preferably denote ethylene, n-propylene or i-propylene.
R.sup.3, R.sup.3' and R.sup.4' alkylene groups preferably have 1 to 5 carbon atoms.
Cycloalkyl radicals are in particular cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl and cyclooctyl, cyclopentyl and cyclohexyl being preferred. Cycloalkyl, however, is also understood as meaning, for example, dimethylcycloalkyl. The same applies to cycloalkylene groups.
Alkenyl groups can also be straight-chain or branched and correspond, for example, to the abovementioned alkyl groups. Preferred alkenyl groups have 2 to 5 carbon atoms, vinyl and allyl being particularly preferred.
Alkenylene groups can likewise be straight-chain or branched and correspond, for example, to the abovementioned alkylene groups. Preferred alkenylene groups have 2 to 5 carbon atoms, vinylene and propenylene being particularly preferred.
Aryl groups are preferably phenyl, naphthyl, biphenylyl or fluorenyl, phenyl being particularly preferred.
The same applies to arylene groups, 1,2 -phenylene, 1,3-phenylene and 1,4-phenylene being particularly preferred.
Preferred arylalkyl groups are benzyl and phenethyl.
An alkali metal M is preferably sodium or potassium. As for substituted ammonium groups M, all customary mono-, di-, tri- or or tetra-substituted ammonium groups can be employed. Suitable substituents are in this case in particular alkyl groups and optionally substituted phenyl. Tetra-(C.sub.1 -C.sub.4) -alkylammonium is preferred.
R.sup.6 preferably denotes (C.sub.1 -C.sub.4) -alkylene or (C.sub.2 -C.sub.4)-alkylenylene.
R.sup.7 preferably denotes (C.sub.1 -C.sub.4) -alkyl.
Any of the individual radicals R.sup.2 to R.sup.2g, provided n>1, can also have various meanings within a polycondensate according to the invention. Within a polymeric partial structure, e.g. --(R.sup.2a O).sub.n2 --, these various meanings can follow one another in a random sequence or blockwise. The same applies to R.sup.3 and R.sup.3' and also to n.sup.2, n.sup.3 and n.sup.4.
In preferred polycondensates of the general formula I
R.sup.1 and R.sup.1' independently of one another denote methyl or ethyl,
R.sup.2 to R.sup.2g independently of one another denote ethylene, n-propylone or i-propylene,
R.sup.3 and R.sup.3' independently of one another denote (C.sub.1 -C.sub.4) -alkylene, phonylone or naphthylene,
R.sup.4 denotes (C.sub.2 -C.sub.4) -alkylene,
R.sup.5, R.sup.5' and R.sup.5" independently of one another denote hydrogen or (C.sub.1 -C.sub.5 )-alkyl,
M denotes hydrogen, sodium or potassium,
n.sup.1 to n.sup.8 independently of one another denote an integer from 2 to 35,
p and q independently of one another denote an integer from 2 to 20,
t denotes an integer from 0 to 40,
w denotes an integer from 1 to 30,
v denotes an integer from 0 to 4 and
y denotes an integer from 1 to 5.
Preferred polycondensates of the general formula I are moreover those which have molecular weights from 2000 to 20,000.
In particularly preferred polycondensates of the general formula I, all the values n.sup.1 to n.sup.8 are identical or stand only for 2 or 3 different integers.
Moreover, it is particularly preferred if all the radicals R.sup.2 to R.sup.2g are identical or only 2 or 3 have different meanings.
Furthermore, the sum p+q particularly preferably denotes an integer from 5 to 15.
The polycondensates of the general formula I according to the invention can be prepared by reacting with one another
a) a compound of the general formula IIa
in which R.sup.3 is defined as indicated above and R.sup.8 denotes hydrogen, (C.sub.1 -C.sub.4)-alkyl, halogen, in particular chlorine, or R.sup.8 OOC--R.sup.3 --CO--, and a compound of the general formula IIb
in which R.sup.3' is defined as indicated above and R.sup.9 denotes hydrogen, (C.sub.1 -C.sub.4)-alkyl, halogen, in particular chlorine, or R.sup.8 OOC--R.sup.3' --CO--and
b) a compound of the general formula IIIa ##STR6## and/or a compound of the general formula IIIb ##STR7## and/or a compound of the general formula IIIc ##STR8## and/or a compound of the general formula IIId ##STR9## and/or a compound of the general formula IIIe ##STR10## in which R.sup.2 to R.sup.2d and n.sup.1 to n.sup.5 are defined as indicated above, and
c) a compound of the general formula IVa
in which R.sup.1 is defined as indicated above, and a compound of the general formula IVb
in which R.sup.1' is defined as indicated above, and
d) a compound of the general formula V ##STR11##
in which R.sup.2b, R.sup.4, R.sup.5, n.sup.3, s and t are defined as indicated above.
Compounds of the general formula IIa and IIb are, for example, malonic acid, succinic acid, glutaric acid, adipic acid, suberic acid, maleic acid, ftunaric acid, iraconic acid, cyclohexane-1,4-dicarboxylic acid, cyclohexane-1,3-dicarboxylic acid, phthalic acid, isophthalic acid, terephthalic acid, 1,4- and 1,5-naphthalenedicarboxylic acid, diphenic acid, norbornanedicarboxylic acid and also their methyl, ethyl, propyl and butyl esters, anhydrides and chlorides. In addition sodium, potassium and ammonium sulphonatosuccinic acid, sodium and potassium 4-sulphonatophthalic acid, sodium 2-sulphonatoterephthalic acid, sodium 5-sulphonatoisophthalic acid, sodium sulphonatosuccinic acid and also their methyl, ethyl, propyl and buryl esters, anhydrides and chlorides.
Compounds of the general formulae IIIa to IIIe are, for example, ethylene glycol, propane-1,2- and -1,3-diol, ethylene glycol mono(3-hydroxypropyl) ether, ethylene glycol mono(3-hydroxy-2-propyl) ether, ethylene glycol mono(2-hydroxypropyl) ether, butanediols, in particular butane-1,4-diol, pentanediols, such as pentane-1,5-diol, hexanediols, in particular hexane-1,6-diol, decane-1,10-diol, diethylene glycol, dipropylene glycol, bis(3-hydroxypropyl) ether, triethylene glycol, tetraethylene glycol, tripropylene glycol, 4,8-dioxadecane-1,10-diol, polyethylene glycols of molecular weight 300 to 2000, polypropylene glycols of molecular weight 300 to 2000, polyethers of propane-1,3-diol and mixed polyethers of ethylene glycol with propylene glycol and/or optionally propane-1,3-diol, the polyethers mentioned having molecular weights from 300 to 2000, bis (4-hydroxybutyl) ether, 2-methylenepropane-1,3-diol, 2,4-dimethyl-2-ethylhexane-1,3-diol, 2-ethyl-2-butylpropane-1,3 -diol, 2,2 -dimethylpropane-1,3-diol, 2-ethyl-2-isobutylpropane-1,3 -diol, 2,2,4-trimethylhexane-1, 6-diol, 1,3-dihydroxycyclohexane and 1,4-dihydroxycyclohexane (quinitol).
Compounds of the general formulae IVa and IVb are, for example, methanol, ethanol, n-propanol, i -propanol, n-butanol, cyclohexanol, cyclopentanol, benzyl alcohol, phenol, allyl alcohol, sulphonic acid, benzoic acids of the formula VI ##STR12##
in which R.sup.2f, R.sup.7, M and n.sup.7 are defined as indicated above, compounds of the formula ##STR13##
in which R.sup.2e, M and n.sup.6 are defined as indicated above and polysiloxanes of the formula VII ##STR14##
in which R.sup.5', R.sup.5", R.sup.2g, n.sup.8, v and w are defined as indicated above.
The benzoic acids of the formula VI can also be employed in the form of their (C.sub.1 -C.sub.4) -alkyl esters or their halides, in particular chlorides.
In a preferred embodiment of the preparation process according to the invention,
a) the compounds of the formulae IIa and IIb are employed in amounts of altogether 100 mol %,
b) the compounds of the formulae IIIa to IIIe are employed in amounts of altogether 150 to 250 mol %,
c) the compounds of the formulae Ira and IVb are employed in amounts of altogether 20 to 40 mol % and
d) the compounds of the formula V are employed in amounts of 10 to 50 mol %.
The reaction can be controlled by means of a specific conduct of the reaction and thus structure and molecular weights of the products prepared can be affected. Suitable parameters are temperature, pressure or alternatively amount and sequence of the addition of the starting compounds as in a) to d) .
Customarily, the reaction is subdivided into an esterification reaction (if R.sup.8 and R.sup.9 denote hydrogen) or transesterification reaction (if R.sup.8 and R.sup.9 have a meaning other than hydrogen) and a condensation reaction. The (trans)esterification reaction is in this case normally carried out at normal pressure and the condensation reaction is carried out at a pressure of 1013 to 5 mbar. It is preferred to carry out the (trans)esterification reaction in the presence of an esterification or transesterification catalyst. Suitable catalysts of this type are, for example, titanium alkoxides, in particular titanium tetraisopropoxide, or manganese acetate and zinc acetate.
The process according to the invention is normally carried out at temperatures from 100.degree. to 300.degree. C., particularly preferably at 150.degree. to 250.degree. C. The reaction times are in this case 1 to 10 hours, preferably 2 to 5 hours.
If volatile products are formed during the reaction, these are distilled off after or preferably continuously during the reaction.
The compounds of the formulae IIa, IIb, IIIa to IIIe, IVa, IVb, V, VI and VII are known, can be purchased or are available according to known preparation processes.
The polycondensates according to the invention can be dissolved or dispersed in water, clear to opalescent, viscous solutions resulting. On account of their soil release effects, they can be used for the textile finishing of polyester materials.
Polyester materials are in this case in particular to be understood as meaning threads, yams or textile fabrics composed of polyester.
They are treated with the polycondensates according to the invention, for example, by applying the latter in a manner known per se, preferably in the form of dispersions, and after the customary drying, fixing by a heat treatment. Application is carried out, for example, by the exhaust process, by means of pad application or by spraying.
The polycondensates according to the invention are preferably applied here in amounts from 0.3 to 1.5 % by weight, particularly preferably 0.6 to 1.2% by weight, relative to the substrate weight.
Accordingly, dispersions of the polycondensates according to the invention are applied which as a rule have a polycondensate content of from 5 to 45% by weight, preferably 10 to 35% by weight, preferably in an amount from 0.9 to 30% by weight, particularly preferably 2.4 to 12% by weight, relative to the substrate weight.
Mechanically applied dirt, such as oils and fats, can be removed significantly more easily from materials which have been treated with the polycondensates according to the invention (soil release effect).
A considerable advantage of the polycondensates according to the invention in comparison to the products of the prior art is that, as a result of the incorporation of the polysiloxane units, particularly advantageous handle properties are imparted to the textiles finished with the polycondensates according to the invention.
Examples
The following Table I names compounds of the formula V which can be employed in the following examples.
Example 1
282.47 g (1.70) mol of isophthalic acid, 80.45 g (0.30 mol) of sodium 5-sulphoisophthalic acid, 213.0 g (2.80 mol) of propane-1,2-diol, 127.40 g (1.20 mol) of diethylene glycol and 0.82 g (0.010 mol) of anh. sodium acetate are introduced into a 1 four-necked flask having a KPG stirrer, 40 cm injection column, internal thermometer and dropping funnel having an attached gas inlet tube. After this, the atmosphere is rendered inert with nitrogen and 0.19 g (0.0007 mol) of titanium tetraisopropoxide is then added. The mixture is then heated to an internal temperature of 175.degree. to 180.degree. C., water being removed by distillation in the course of 2.5-3 h. (70 g, 97% of theory)
After cooling to 80.degree. to 85.degree. C., 300 g (0.20 mol) of Si4 as in Table 1 are added. The internal temperature is then increased to 200.degree. to 210.degree. C. After reaching this temperature, the pressure is lowered to 1 mbar in the course of 30 min, and the temperature is raised to 255.degree. to 260.degree. C. Further condensation is carried out for 2.5 to 3 h under these reaction conditions, a distillate amount of 196 g being produced. After completion of the condensation, the flask is first cooled to about 150.degree. C. and then pressurized with inert gas. After cooling to room temperature, the solidified melt is broken into small pieces and removed.
Example 2
388.36 g (2.0 mol) of dimethyl terephthalate, 260.7 g (4.20 mol) of ethane-1,2-diol and 0.82 g (0.010 mol) of anh. sodium acetate are introduced into a 1 l four-necked flask having a KPG stirrer, 40 cm injection column, internal thermometer and dropping funnel having an attached gas inlet tube. After this, the atmosphere is rendered inert with nitrogen and 0.19 g (0.0007 mol) of titanium tetraisopropoxide are then added. The flask is then heated to an internal temperature of 175.degree. to 180.degree. C., methanol being removed by distillation in the course of 2.5 to 3 h (121 g, 94.5% of theory).
After cooling to 80.degree. to 85.degree. C., 324 g (0.24 mol) of MPEG 1350, 300 g (0.20 mol) of PEG 1500 and 361.80 g (0.20 mol) of Si2 as in Table 1 are added. The internal temperature is then increased to 200.degree. to 210.degree. C. After reaching this temperature, the pressure is lowered to 1 mbar in the course of 30 min., and the temperature is raised to 220.degree. to 235.degree. C. The mixture is further condensed under these reaction conditions for 2.5 to 3 h, a distillate amount of 220 g being produced. After completion of the condensation, the flask is first cooled to about 150.degree. C. and then pressurized with inert gas. After cooling to room temperature, the solidified melt is broken into small pieces and removed.
Example 3
330.10 g (1.7 mol) of dimethyl terephthalate, 88.86 g (0.3 mol) of sodium dimethyl 5-sulphoisophthalate, 47.64 g (0.20 mol) of sodium methyl 3-sulphobenzoate, 289.10 g (3.80 mol) of propane-1,2-diol, 42.46 g (0.40 mol) of diethylene glycol and 0.82 g (0.010 mol) of anh. sodium acetate are introduced into a 1 l four-necked flask having a KPG stirrer, 40 cm injection column, internal thermometer and dropping funnel having an attached gas inlet tube. After this, the atmosphere is rendered inert with nitrogen and 0.19 g (0.0007 mol) of titanium tetraisopropoxide is then added. The flask is then heated to an internal temperature of 175.degree. to 180.degree. C., methanol being removed by distillation in the course of 2.5 to 3 h (121 g, 94.5% of theory).
After cooling to 80.degree. to 85.degree. C., 300 g (0.020 mol) of Si4 as in Table 1 are added. The internal temperature is then increased to 200.degree. to 210.degree. C. After reaching this temperature, the pressure is lowered to 1 mbar in the course of 30 min and the temperature is raised to 220.degree. to 235.degree. C. The mixture is further condensed under these reaction conditions for 2.5 to 3 h, a distillate amount of 220 g being produced. After completion of the condensation, the flask is first cooled to about 150.degree. C. and then pressurized with inert gas. After cooling to room temperature, the solidified melt is broken into small pieces and removed.
Polycondensates according to the invention can also be prepared using the following starting compounds analogously to Examples 1 to 3:
Example 4
0.3 mol of dimethyl sodium 5-sulphoisophthalate
1.7 mol of dimethyl isophthalate
2.0 mol of ethane-1,2-diol
2.0 mol of propane-1,2-diol
0.05 mol of compound Si1 as in Table 1
Example 5
0.2 mol of 5-sodium dimethyl sulphoisophthalate
1.7 mol of dimethyl terephthalate
1.5 mol of ethane-1,2-diol
2.5 mol of propane-1,3 -diol
0.02 mol of compound Si5 as in Table 1
0.12 mol of polyethylene glycol monomethyl ether 750
Example 6
0.4 mol of sodium 5-sulphoisophthalic acid
1.6 mol of dimethyl terephthalate
1.0 mol of ethane-1,2-diol
3.0 mol of propane-1,3-diol
0.01 mol of compound Si8 as in Table 1
0.3 mol of sodium 3-sulphobenzoic acid
Example 7
0.2 mol of sodium dimethyl 5-sulphoisophthalate
1.8 mol of dimethyl terephthalate
2.0 mol of butane-1,4-diol
2.0 mol of propane-1,3-diol
0.05 mol of compound Si3 as in Table 1
Example 8
1.0 mol of sodium 5-sulphoisophthalic acid
1.0 mol of isophthalic acid
2.0 mol of ethane-1,2-diol
2.0 mol of diethylene glycol
0.1 mol of compound Si4 as in Table 1
Example 9
0.3 mol of sodium dimethyl 5-sutphoisophthalate
1.7 mol of diethyl isophthalate
1.0 mol of ethane-1,2-diol
3.0 mol of 2,2-dimethylpropanediol
0.02 mol of compound Si10 as in Table 1
Example 10
2.0 mol of dimethyl terephthalate
3.0 mol of propane-1,2-diol
1.0 mol of polyethylene glycol 1500
0.15 mol of compound Si6 as in Table 1
0.1 mol of polyethylene glycol monomethyl ether 750
Example 11
0.2 mol of sodium 5-sulphoisophthalic acid
1.8 mol of isophthalic acid
2.0 mol of ethane-1,2-diol
2.0 mol of 1,4-bishydroxymethylcyclohexane
0.1 mol of compound Si5 as in Table 1
0.3 mol of 2-hydroxyethanesulphonic acid, Na salt
Example 12
2.0 mol of dimethyl terephthalate
1.0 mol of polyethylene glycol 1500
3.0 mol of diethylene glycol
0.15 mol of compound Si14 as in Table 1
0.25 mol of 2-hydroxyethanesulphonic acid, Na salt
Example 13
1.0 mol of dimethyl succinate
1.0 mol of dimethyl terephthalate
2.0 mol of polyethylene glycol 750
2.0 mol of propane-1,2-diol
0.1 mol of compound Si1 as in Table 1
Claims
We claim:
1. Polycondensates of the formula I ##STR16## in which X denotes ##STR17## R.sup.1 and R.sup.1' independently of one another denote hydrogen, (C.sub.1 -C.sub.22)-alkyl, (C.sub.2 -C.sub.22)-alkenyl, (C.sub.3 -C.sub.8)cycloalkyl, (C.sub.6 -C.sub.14)-aryl, (C.sub.6 -C.sub.14)-aryl-(C.sub.1 -C.sub.8)-alkyl, MO.sub.3 S--R.sup.6 --, MO.sub.3 S--, ##STR18## R.sup.2 to R.sup.2g independently of one another denote (C.sub.1 -C.sub.30)-alkylene, (C.sub.3 -C.sub.8)-cycloalkylene and/or (C.sub.2 -C.sub.30)-alkenylene, each of which can be substituted by a radical R.sup.1 ; R.sup.3 and R.sup.3' independently of one another denote (C.sub.1 -C.sub.22)-alkylene, (C.sub.3 -C.sub.8)-cycloalkylene, (C.sub.2 -C.sub.22)-alkylenylene and/or (C.sub.6 -C.sub.14)-arylene, where 0 to 30% of all the radicals R.sup.3 and R.sup.3' carry an --SO.sub.3 M substituent; R.sup.4 denotes (C.sub.1 -C.sub.30)-alkylene, (C.sub.3 -C.sub.8)-cycloalkylene or (C.sub.2 -C.sub.30)-alkenylene; R.sup.5, R.sup.5' and R.sup.5" independently of one another denote hydrogen, (C.sub.1 -C.sub.30)-alkyl, (C.sub.3 -C.sub.8)-cycloalkyl or (C.sub.2 -C.sub.30)-alkenyl; R.sup.6 is defined as R.sup.3, but independently of this; R.sup.7 denotes (C.sub.1 -C.sub.22)-alkyl, (C.sub.3 -C.sub.8)-cycloalkyl or (C.sub.2 -C.sub.22)-alkenyl, where 0 to 30% of all the radicals R.sup.7 carry an --SO.sub.3 M substituent; M is hydrogen, an alkali metal, the ammonium group or a substituted ammonium group; n.sup.1 to n.sup.8 independently of one another denote an integer from 0 to 40; p and q independently of one another denote an integer from 2 to 20; s denotes 0 or 1; t denotes an integer from 0 to 80; w denotes an integer from 0 to 80; v denotes an integer from 0 to 80 and y denotes an integer from 1 to 20.
2. Polycondensates according to claim 1, wherein R.sup.1 and R.sup.1' independently of one another denote methyl or ethyl, R.sup.2 to R.sup.2f independently of one another denote ethylene, n-propylene or i-propylene, R.sup.3 and R.sup.3' independently of one another denote (C.sub.1 -C.sub.4)-alkylene, phenylene or naphthylene, R.sup.4 denotes (C.sub.1 -C.sub.4)-alkylene, R.sup.5, R.sup.5' and R.sup.5" independently of one another denote hydrogen or (C.sub.1 -C.sub.5)-alkyl, M denotes hydrogen, sodium or potassium, n.sup.1 to n.sup.8 independently of one another denote an integer from 2 to 35, p and q independently of one another denote an integer from 2 to 20, t denotes an integer from 0 to 40, w denotes an integer from 1 to 30, v denotes an integer from 0 to 4, and y denotes an integer from 1 to 5.
3. Polycondensates according to claim 1, wherein all the values n.sup.1 to n.sup.8 are identical or only stand for 2 or 3 different integers.
4. Polycondensates according to claim 1, wherein all the radicals R.sup.2 to R.sup.2g are identical or only have 2 or 3 different meanings.
5. Polycondensates according to claim 1, wherein the sum p+q is an integer from 5 to 15.
6. Polycondensates according to claim 1, wherein said polycondensates having molecular weights of 2,000 to 20,000.
7. Polycondensates according to claim 2, wherein all the values n.sup.1 to n.sup.8 are identical or only stand for 2 or 3 different integers, all the radicals R.sup.2 to R.sup.2g are identical or only have 2 or 3 different meanings, the sum p+q is an integer from 5 to 15 and said polycondensates having molecular weights of 2,000 to 20,000.
8. Polycondensates according to claim 7, wherein t denotes an integer from 1 to 40 and v denotes an integer from 1 to 4.
9. A process for the preparation of the polycondensates of formula I ##STR19## in which X denotes ##STR20## R.sup.1 and R.sup.1' independently of one another denote hydrogen, (C.sub.1 -C.sub.22)-alkyl, (C.sub.2 -C.sub.22)-alkenyl, (C.sub.3 -C.sub.8)cycloalkyl, (C.sub.6 -C.sub.14)-aryl, (C.sub.6 -C.sub.14)-aryl-(C.sub.1 -C.sub.8)-alkyl, MO.sub.3 S-R.sup.6 - , MO.sub.3 S-, ##STR21## R.sup.2 to R.sup.2g independently of one another denote (C.sub.1 -C.sub.30)-alkylene, (C.sub.3 -C.sub.8)-cycloalkylene and/or (C.sub.2 -C.sub.30)-alkenylene, each of which can be substituted by a radical R.sup.1 ; R.sup.3 and R.sup.3' independently of one another denote (C.sub.1 -C.sub.22)-alkylene, (C.sub.3 -C.sub.8)-cycloalkylene, (C.sub.2 -C.sub.22)-alkenylene and/or (C.sub.6 -C.sub.14)-arylene, where 0 to 30% of all the radicals R.sup.3 and R.sup.3' carry an --SO.sub.3 M substituent; R.sup.4 denotes (C.sub.1 -C.sub.30)-alkylene, (C.sub.3 -C.sub.8)-cycloalkylene or (C.sub.2 -C.sub.30)-alkenylene; R.sup.5, R.sup.5' and R.sup.5" independently of one another denote hydrogen, (C.sub.1 -C.sub.30)-alkyl, (C.sub.3 -C.sub.8)-cycloalkyl or (C.sub.2 -C.sub.30)-alkenyl; R.sup.6 is defined as R.sup.3, but independently of this; R.sup.7 denotes (C.sub.1 -C.sub.22)-alkyl, (C.sub.3 -C.sub.8)-cycloalkyl or (C.sub.2 -C.sub.22)-alkenyl, where 0 to 30% of all the radicals R.sup.7 carry an --SO.sub.3 M substituent; M is hydrogen, an alkali metal, the ammonium group or a substituted ammonium group; n.sup.1 to n.sup.8 independently of one another denote an integer from 0 to 40; p and q independently of one another denote an integer from 2 to 20; s denotes 0 or 1; t denotes an integer from 0 to 80; w denotes an integer from 0 to 80; v denotes an integer from 0 to 80 and y denotes an integer from 1 to 20, comprising reacting a) a compound of the formula (IIa) in which R.sup.3 is defined as indicated above and R.sup.8 denotes hydrogen, (C.sub.1 -C.sub.4)-alkyl, halogen, or R.sub.8 OOC-R.sup.3 -CO-, and a compound of the formula IIb in which R.sup.3' is defined as indicated above and R.sup.9 denotes hydrogen, (C.sub.1 -C.sub.4)-alkyl, halogen or R.sup.8 OOC-R.sup.3' -CO- and b) a compound of the formula IIIa ##STR22## and/or a compound of the formula IIIb ##STR23## and/or a compound of the formula IIIc ##STR24## and/or a compound of the formula IIId ##STR25## and/or a compound of the formula IIIe ##STR26## in which R.sup.2 to R.sup.2d and n.sup.1 to n.sup.5 are defined as indicated above and c) a compound of the formula IVa in which R.sup.1 is defined as indicated above and a compound of the formula IVb p1 in which R.sup.1' is defined as indicated above, and d) a compound of the formula V ##STR27## in which R.sup.2b, R.sup.4, R.sup.5, n.sup.3, s and t are defined as indicated above.
10. The process according to claim 9, wherein a) the compounds of the formulae IIa and IIb are employed in amounts of altogether 100 mol %, b) the compounds of the formulae ]IIa to ]lie are employed in amounts of altogether 150 to 250 mol %, c) the compounds of the formulae IVa and IVb are employed in amounts of altogether 20 to 40 mol % and d) the compounds of the formula V are employed in amounts of 10 to 50 mol %.
11. The process according to claim 9, wherein R.sup.8 and R.sup.9 are chlorine.
12. The process according to claim 10, wherein R.sup.8 and R.sup.9 are chlorine.
13. The process according to claim 9, wherein the reaction is carried out at a temperature range from about 100.degree. to 300.degree. C. for about 1 to about 10 hours.
14. The process according to claim 12, wherein the reaction is carried out at a temperature range from about 100.degree. to 300.degree. C. for about 1 to about 10 hours.
15. A process for textile finishing of polyester fabrics comprising dissolving or dispersing the polycondensates according to claim 1, into water to from a solution and treating said polyester fabric with said solution.