Golf Club Treated With Plating

This invention relates to a golf club treated with plating, and more particularly to a golf club having a head treated with super hard plating.

Heads of conventional golf clubs have been made of wood or metal, and recently many golf clubs have their heads made of metal. Representative examples of materials for such a metal head include aluminum, an aluminum alloy, stainless steel, titanium and a titanium alloy. With respect to the performance of a golf club, a driving distance of a ball, as well as a directional stability of a hit ball, is important.

Various proposals have heretofore been made with respect to the dimensions, shape and material of a head of a golf club to obtain a longer driving distance of a hit ball while securing a directional stability of a hit ball. It is known that the driving distance depends on the hardness of a hitting surface of a metal head if the metal head has the same dimensions and shape. In view of this, various proposals have heretofore been made in the prior art with respect to a material of a metal head; however, enhancing of the hardness of the head surface has not been taken into consideration at all.

It is an object of this invention to provide a golf club with a metal head capable of achieving a longer driving distance.

According to the present invention, there is provided a golf club having a head of metal treated with super hard plating.

In the golf club of the present invention, a hardness of the surface of the metal head is extremely high.

In a preferred embodiment of the present invention, Ni alloy-plating is applied to a surface of a head of each of wood Nos. 1 to 5 to form a ternary alloy (Ni--B--W) film thereon.

In a test example, NIBOFRAM (Registered trademark) was used as an electroless plating solution. A weight of a head body was 200 g, and a plating film was 20.mu. in thickness and 3 g in weight. The hardness of the surface of the head was 350.about.450 Hv before the plating, and was 800 Hv after the plating.

Comparing the head before the plating with the head after the plating with respect to driving distances, the following results were obtained. More specifically, when measuring driving distances, using woods of the same specification and golf balls of the same specification, a man increased a driving distance from 200 yards to 220 yards, and a woman increased a driving distance from 180 yards to 197 yards. Thus, the driving distance was increased about 5.about.10%. Measurements were also carried out using a machine (SWING ANALYZER (Registered Trademark) marketed by Osawa Shokai and DISTANCE CADDIE (Registered Trademark) marketed by Bussan Sports Corporation, and measured driving distances for each wood are shown in Table 1. In this Table, the unit is yard.

It will be appreciated from this Table that a driving distance with the heads after the plating is about longer than a driving distance with the heads before the plating.

In this embodiment, although the Ni-alloy plating is used to form the ternary alloy film, hard chrome plating and any other suitable plating can be used.

In the present invention, merely by applying plating to a head of a golf club, there is obtained an advantage that a driving distance is increased about 4% to about 10%.