Electrolyte for Electrolytic Capacitors and Electrolytic Capacitor Using the Electrolyte

This invention relates to an electrolyte for use in electrolytic capacitors and also to an electrolytic capacitor using the electrolyte.

A typical electrolyte for electrolytic capacitors which has been hitherto used is an electrolyte of an ionogen dissolved in ethylene glycol. However, this type of electrolyte has a low specific conductance and tends to cause an impedance characteristic to deteriorate. To avoid this, usual practice is to add water to the electrolyte, but such an electrolyte is elevated in vapor pressure at high temperatures and is apt to react with an aluminum electrode, thus being unsuitable for use in a high temperature range.

In order to improve the above drawbacks, there have been proposed an electrolyte using .UPSILON.-butyrolactone as a solvent and a triethylamine salt of phthalic acid as described in Japanese Laid-open Patent Application No. 61-70711 and an electrolyte an amine salt of maleic acid dissolved in a mixed solvent of .UPSILON.-butyrolactone and ethylene glycol as described in Japanese Laid-open Patent Application No. 54-7564.

Moreover, Japanese Laid-open Patent Application No. 59-78522 describes electrolytes using quaternary ammonium salts of linear dicarboxylic acids, and Japanese Laid-open Patent Application No. 61-93610 teaches electrolytes using tetralkyl ammonium salts of 1,10-decanedicarboxylic acid or 1,6-decanedicarboxylic acid.

However, the known electrolytes comprising triethylamine salts of phthalic acid or maleic acid dissolved in a .UPSILON.-butyrolactone solvent are disadvantageous in that the acid dissociation is caused by the proton equilibrium of the triethylamine, so that ions are produced only in small amounts. Thus, a sufficiently high specific conductance cannot be obtained. On the other hand, with electrolytes using the quaternary ammonium salts of linear dicarboxylic acids or the tetraalkyl ammonium salts of 1,10-decanedicarboxylic acid or 1,6-decanedicarboxylic acid, the specific conductance becomes low because of the rather inappropriate combination with the acid. Accordingly, electrolytic capacitors using these electrolytes cannot disadvantageously lower the impedance characteristic.

The present invention contemplates to provide an electrolyte for electrolytic capacitors and an electrolytic capacitor using the electrolyte in which a solute of the electrolyte used is a quaternary ammonium salt of either a carboxylic acid selected from the group consisting of phthalic acid, tetrahydrophthalic acid, hexahydrophthalic acid and maleic acid, or an alkyl or nitro-substituted compound of the acid, whereby the resultant electrolytic capacitor has improved low temperature characteristics and improved characteristics with time at high temperatures, thus ensuring a prolonged life.

FIG. 1 is a schematic perspective view illustrating the respective members of an electrolytic capacitor; and FIGS. 2-4 are, respectively, graphs of characteristics, in relation to time, of aluminum electrolytic capacitors having ratings 10 V and 2200 .mu.F (o16.times.32) and using known electrolytes and electrolytes of the invention, in which FIG. 2 is a characteristic graph showing a variation in electrostatic capacity by application of a rated voltage, FIG. 3 is a characteristic graph showing a variation in tangent of the loss angle by application of a rated voltage, and FIG. 4 is a characteristic graph of a variation in leakage current in the absence of an applied voltage.

The present invention provides an electrolyte for use in an electrolytic capacitor which comprises a solution, in an organic solvent, of a quaternary ammonium salt of a carboxylic acid selected from the group consisting of phthalic acid, a tetrahydrophthalic acid, hexahydrophthalic acid and maleic acid, or of an alkyl or nitro-substituted compound of the carboxylic acid, and also provides an electrolytic capacitor using the electrolyte.

The quaternary ammonium salts are those compounds of the following general formula ##STR1##

in which X.sub.1 represents ##STR2##

X.sub.2 represent ##STR3##

in which each R.sub.1, each R.sub.2, each R.sub.3 and each R.sub.4 independently represent an alkyl group, an aryl group, a cycloalkyl group, an aralkyl group and/or a hydroxyalkyl group, or the two of these substituents may combine to form a divalent group which forms a ring along with the nitrogen atom, and A represents a carboxylic acid residue.

In the above general formula, R.sub.1, R.sub.2, R.sub.3 and R.sub.4 are, respectively, a C.sub.1-12 alkyl group (such as methyl, ethyl, propyl, buryl, octyl, dodecyl and the like), an aryl group (such as phenyl and the like), a cycloalkyl group (such as cyclohexyl and the like), an aralkyl group (such as benzyl and the like), and a C.sub.2-4 hydroxyalkyl group (such as hydroxyethyl and the like). Alternatively, these two substituents may combine to give a divalent group such for example, -(CH.sub.2)n- wherein n is 5 or 6, or - CH.sub.2 CH.sub.2 OCH.sub.2 CH.sub.2 -, and form a ring along with the nitrogen atom.

In the practice of the invention, the tetrahydrophthalic acid includes cyclohexene-1,2-dicarboxylic acid and cyclohexene-4,5-dicarboxylic acid.

The alkyl-substituted compound of the carbaxylic acid is one whose alkyl moiety has 1-3 carbon atoms, e.g. a methyl-substituted compound. Examples at the alkyl substituted compound include methylmaleic acid (citracanic acid) and dimethylmaleic acid. Examples of the nitro-substituted compounds include 3- ar 4-nitraphthalic acid. These carbaxylic acids and their alkyl or nitro-substituted compounds may be used in combination.

Examples of the quaternary ammonium salts include tetraalkylammonium salts (whose alkyl moiety has generally 1-12 carbon atoms, e.g. a tetramethylammonium salt, a tetraethylammonium salt, a tetrapropylammonium salt, a tetrabutylammonium salt, a methyltriethylammonium salt, an ethyltrimethylammonium salt and the like), aryltrialkylammonium salts (such as a phenyltrimethylammonium salt and the like), cyclohexyltrialkyl ammonium salts (such as a cyclohexyltrimethylammonium salt and the like), arylalkyltrialkyl ammonium salts (such as a benzyltrimethylammonium salt and the like), trialkylhydroxyalkylammonium salts (such as a trimethylhydroxyethylammonium salt and the like), N,N-dialkylpiperidinium salts (such as an N,N-dimethylpiperidinium salt and the like), and mixtures thereof.

Of these quaternary ammonium salts, the tetraalkylammonium salts and the trialkylydroxyalkylammonium salts are preferred. Most preferably, a tetraethylammonium salt is used.

The equivalent ratio between the carboxyl groups of a carboxylic acid and the quaternary ammonium base is generally in the range of 1.2:1.0-2.8:1.0, preferably 1.5:1.0-2.5:1.0, and most preferably 2.0:1.0. In other words, a mono-salt having a molar ratio between the acid and the base of 1:1 is most preferably used.

The electrolyte for an electrolytic capacitor according to the invention comprises the above-defined salt and an organic solvent. Examples of the organic solvent include alcohols, e.g. monohydric alcohols such as butyl alcohol, diacetone alcohol, benzyl alcohol , amino alcohol s and the like, dihydric alcohols such as ethylene glycol, propylene glycol, dithylene glycol, hexylene glycol, phenyl glycol and the like, trihydric alcohols such as glycerins, 3-methylpentane-1,3,5-triol and the like, and hexitol; ethers, e.g. monoethers such as ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, ethylene glycol phenyl ether and the like, diethers such as ethylene glycol dimethyl ether, ethylene glycol diethyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether and the like amides, e.g. formamides such as N-methylformamide, N,N-dimethylformamide, N-ethylformamide, N,N-diethylformamide and the like, aceramides such as N-methylacetamide, N,N-dimethylacetamide, N-ethylacetamide, N,N-diethylacetamide and the like, propionamides such as N,N-dimethylpropionamide and the like, and hexamethylphosphoryl amide; oxazolidinones such as N-methyl-2-oxazolidinone, N-ethyl-2-oxazolidinone, dimethyl-2-oxazolidinone and the like; dimethylsulfoxide, .UPSILON.-butyrolactone and the like; and mixtures thereof.

Of these, amides, oxazlidinones and .UPSILON.-butyrolactone are preferred. More preferably, .UPSILON.-butyrolactone alone or a mixed solvent comprising a major proportion of .UPSILON.-butyrolactone is used. In the latter case, the content of the .UPSILON.-butyrolactone is preferably in the range of 50-100% based on the total weight of the solvent.

The electrolyte of the invention may further comprise water, if necessary. The content of water is generally not larger than 10% based on the weight of the electrolyte.

In an electrolyte using .UPSILON.-butyrolactone alone or a mixed solvent comprised mainly of .UPSILON.-butyrolactone as a solvent and a tetraethylammonium salt of phthalic acid or maleic acid as a solute, when a mono salt having a molar ratio of the acid and the base of 1:1 is used, a maximum specific conductance is shown. Accordingly, monotetraethylammonium phthalate or monotetraethylammonium maleate is preferred.

The amount of the quaternary ammonium salt in the electrolyte is generally in the range of 1 wt%-40 wt%, preferably 5 wt%-30 wt%. The amount of the organic solvent is in the range of 60 wt%-99 wt%, preferably 70 wt%-95 wt%.

The electrolyte of the invention obtained as described above has a high specific conductance and good stability at high temperatures. The use of the electrolytes results in an electrolytic capacitor which has a low impedance and is stable at high temperatures. More particularly, when a solute which is used in combination with a solvent comprised mainly of .UPSILON.-butyrolactone is phthalic acid, maleic acid, nitrophthalic acid, hexahydrophthalic acid or citraconic acid, very high conductance is obtained. In .UPSILON.-butyrol actone, phthalic acid, maleic acid, nitrophthalic acid, tetrahydrophthalic acid, hexahydrophthalic acid, citraconic acid, and tetraethylammonium are very stable at high temperatures. In addition, the reaction between the solute and the solvent and the reaction between phthalic acid, maleic acid, nitrophthalic acid, tetrahydrophthalic acid, hexahydrophthalic acid or citraconic acid and tetraethylammonium do rarely take place. Presumably, this is why the stability at high temperatures is excellent.

In the practice of the invention, the concentration of the quaternary ammonium salt is in the range of 1 wt%-40 wt%. If the amount is less than 1 wt%, the specific conductance does not become satisfactorily high. Over 40 wt%, precipitation will take place.

The present invention is illustrated by way of examples.

In Table 1, there are shown electrolytic compositions according to the invention and for comparison along with their specific conductance at normal temperatures.

As will be clear from Table 1, higher specific conductances can be obtained than the conductances of the known electrolytes.

In Table 2, there are shown initial characteristics capacitors using the electrolytes of References 1, 2 and 3 and Examples, 1, 2, 3, 4, 5, 6, 7, 8, 9, 11, 12, 13, 15, 16 and 17 indicated in Table 1. The capacitor used was an aluminum electrolytic capacitor having ratings of V and 220 .mu.F (o16.times.32). FIG. 1 schematically shows an arrangement of the respective parts or members of this type of aluminum electrolytic capacitor. In FIG. 1, an anode foil 1 used as an anode of aluminum and a cathode foil used as a cathode of aluminum are convolutely wound so that they are in face-to-face relation through a separator 3, thereby providing a capacitor element. The anode foil 1 and the cathode foil 2 of the element have leading tabs respectively.

The thus arranged element is impregnated with each electrolyte and is sealingly encased in a case to obtain an electrolytic capacitor.

As will be apparent from Table 2, the electrolytes of Examples of the invention have significantly lower tan .delta. 120Hz) and impedance (100 KHz) characteristics than the known electrolytes.

FIGS. 2 to 4 show variations in the respective characteristics at 105.degree. C. of the aluminum electrolytic capacitors using the electrolytes of References 1, 2 and 3 and Examples 1, 2, 3, 4, 7 and 15 in relation to time. More particularly, FIG. 2 shows a variation in electrostatic capacity obtained by application of a rated voltage, FIG. 3 shows a variation in tangent of the loss angle obtained by application of a rated voltage, and FIG. 4 shows a variation in leakage current without application of any voltage.

As will be clear from FIGS. 2-4, the characteristic variations under high temperature conditions are very small and thus, highly reliable capacitors can be obtained.

As described hereinbefore, the electrolytes for electrolytic capacitors and capacitors using such electrolytes according to the invention have high specific conductance, and the loss of the capacitor can be improved over a wide range of normal to low temperatures. Because the electrolytes do rarely deteriorate at high temperatures, electrolytic capacitors whose characteristics do not vary over a long term can be obtained.

Thus, the present invention provides an electrolytic capacitor which exhibits stable characteristics over a wide temperature range of from low to high temperatures.