US 5,438,091 AGrant
Resin Composition Having Excellent Paint Coatability
Issue Date:1995-08-01
•3 Claims
Abstract
A resin composition having excellent paint coatability containing (a) 50-80 weight % of a multi-stage polymerized propylene-ethylene block copolymer consisting essentially of (i) a propylene homopolymer portion, (ii) a propylene-ethylene random copolymer portion, and (iii) an ethylene homopolymer portion, (b) 20-40 weight % of an ethylene-.alpha.-olefin copolymer elastomer, and (c) 20 weight % or less of an inorganic filler, components in the components (a) and (b), which are soluble in p-xylene at a room temperature, having a number-average molecular weight of 4.times.10.sup.4 or more and a weight-average molecular weight of 20.times.10.sup.4 or more.
Metadata
Assignees
- Tonen Chemical Corporation
- Toyota Jidosha Kabushiki Kaisha
Inventors
- Yoshiharu Saito
- Masao Sakaizawa
- Kunio Iwanami
- Kitsusho Kitano
- Michihisa Tasaka
- Kenji Kawazu
- Shizuo Miyazaki
- Takao Nomura
- Takeyoshi Nishio
- Hisayuki Iwai
Application Information
Application Number:US 3291367
Filing Date:1994-10-25
Priority Date:1992-06-04
Art Unit:152
Classifications
IPC:
C08L 5300
Field of Search:
52552488;89;240505;515;528
Patent Drawings
This patent does not have any drawings.
Description
BACKGROUND OF THE INVENTION
The present invention relates to a resin composition for exterior automotive parts, and more particularly to a resin composition having excellent paint coatability and moldability, a good balance of impact resistance, ductility, mechanical strength, thermal deformation resistance, brittle temperature, hardness, etc., small molding shrinkage and linear expansion coefficient, and a high paint coating peeling resistance in high-temperature, high-pressure washing.
Since polypropylene is light and has excellent mechanical strength, it is used in various applications. However, since it is poor in impact resistance, its copolymers such as propylene-ethylene block copolymers are used. Also, proposals have been made to provide a resin composition comprising a propylene-ethylene block copolymer, an ethylene-.alpha.-olefin copolymer elastomer and an inorganic filler such as tale.
Japanese Patent Laid-Open No. 61-12742 discloses a resin composition comprising (a) 62-57 weight % of a propylene-ethylene block copolymer having an ethylene content of 2-3 weight % and a melt flow rate of 40-45 g/10 minutes, (b) 26-28 weight % of an ethylene-propylene copolymer elastomer having an ethylene content of 70-80 weight % and a Mooney viscosity ML.sub.1+4 (100.degree. C.) of 55-58, (c) 2-3 weight % of a high-density polyethylene having a density of 0.955-0.960 g/cm.sup.3 and a melt flow rate of 18-22 g/10 minutes, and (d) 10-12 weight % of talc having an average size of 1.8-2.2 .mu.m and a specific surface area of 36000-42000 cm.sup.2/ g, the resin composition having a melt flow rate of 13-18 g/10 minutes, a density of 0.950-0.980 g/cm.sup.3, a flexural modulus of 11500-14000 kg/cm.sup.2, a linear expansion coefficient of 7.times.10.sup.-5 -10.times.10.sup.-5 cm/cm/.degree. C. in a temperature range between 20.degree. C. and 80.degree. C., and a surface gloss (measured by a 60.degree. -60.degree. method according to JIS Z8741) of 55% or more.
Japanese Patent Laid-Open No. 1-149845 discloses a resin composition comprising (a) 59-74 weight % of a propylene-ethylene block copolymer containing 5-12 weight % of a boiling p-xylene-soluble component having an ethylene content of 20-60 weight %, and having an ethylene content of 1-7 weight % and a melt flow rate of 15-50 g/10 minutes, (b) 35-20 weight % of an ethylene-propylene copolymer elastomer having a propylene content of 20-60 weight % and a Mooney viscosity ML.sub.1+4 (100.degree. C.) of 100-150, and (c) 3-6 weight % of talc having a specific surface area of 30000 cm.sup.2/ g or more and an average size of 0.5-2.0 .mu.m.
However, both resin compositions of Japanese Patent Laid-Open Nos. 61-12742 and 1-149845 are susceptible to thermal deformation, and bumpers made of such resin compositions would be easily deformed due to the difference in a linear expansion coefficient between the resin compositions and the automotive body parts in a high-temperature environment, resulting in the deterioration of automotive body appearance. Also, since beautiful coatings are recently formed on bumpers, etc., the resin compositions for bumpers, etc. should have good paint coatability in order to provide the automotive bodies with good appearance.
In the above-described resin compositions comprising the propylene-ethylene block copolymer, the ethylene-propylene copolymer elastomer (or high-density polyethylene) and talc, their flowability is controlled for various applications by adjusting ethylene/propylene ratios and molecular weights, etc. in the propylene-ethylene block copolymer and the ethylene-propylene copolymer elastomer. However, the control of such parameters fails to provide resin compositions having well balanced properties such as paint coatability, moldability, rigidity, ductility, thermal deformation resistance, brittle temperature, hardness, etc. on levels suitable for exterior automotive parts.
As a polypropylene resin composition for automotive bumpers having an improved paint coatability, Japanese Patent Laid-Open No. 57-55952 discloses a polypropylene resin composition comprising 55-65 weight % of a crystalline propylene-ethylene block copolymer containing 5-10 weight % of ethylene, a propylene component, 97 weight % or more of which is insoluble is boiling n-heptane, and a component soluble in p-xylene at a room temperature having an intrinsic viscosity (in decalin at 135.degree. C.) of 3-4 and a melt flow rate of 2-10; 30-35 weight % of an amorphous ethylene-propylene copolymer elastomer having an intrinsic viscosity (in decalin at 135.degree. C.) of 2.0-3.5 and a Mooney viscosity ML.sub.1+4 (100.degree. C.) of 40-100; and 5-15 weight % of talc having an average size of 0.5-5 .mu.m. This resin composition shows an improved resistance to peeling of coatings formed thereon, but it fails to show a sufficient peeling resistance of the coatings in washing under severe conditions such as high temperature and/or high pressure.
OBJECT AND SUMMARY OF THE INVENTION
Accordingly, an object of the present invention is to provide a resin composition .for exterior automotive parts having excellent paint coatability and moldability, and well balanced impact resistance, ductility, mechanical strength, thermal deformation resistance, brittle temperature and hardness while showing small molding shrinkage and linear expansion coefficient.
Another object of the present invention is to provide a resin composition for exterior automotive parts further having good peeling resistance of coatings under severe conditions such as high-temperature, high-pressure washing.
As a result of intense research in view of the above objects, the inventors have found that by blending a propylene-ethylene block copolymer produced by a multi-stage polymerization, an ethylene-.alpha.-olefin copolymer elastomer and an inorganic filler, and by controlling the content of propylene-ethylene random copolymer portion in the resulting resin composition and various parameters of the components, the resulting resin composition shows well balanced impact resistance, ductility, mechanical strength, thermal deformation resistance, brittle temperature and hardness.
With respect to the peeling resistance of a coating formed on a resin molding substrate under severe conditions such as high-temperature, high-pressure washing, the inventors have also found that the peeling resistance is usually determined by a Young's modulus of the coating, the strength of a substrate and an adhesion strength between the coating and the substrate, and that if the adhesion strength between the coating and the substrate is large enough, the peeling resistance is not affected by the adhesion strength, but largely affected by the strength of the substrate itself. However, if it is tried to increase the strength of the resin substrate, the resin substrate is likely to show decreased impact resistance. In order to increase the strength of the resin substrate while preventing a decrease in the impact resistance, the inventors have found that it can effectively be achieved by increasing the strength of elastomer components in the resin composition, specifically a propylene-ethylene random copolymer portion in the propylene-ethylene block copolymer and an ethylene-.alpha.-olefin copolymer elastomer. The present invention has been completed based on these findings.
Thus, the first resin composition having excellent paint coatability comprising;
(a) 50-80 weight % of a multi-stage polymerized propylene-ethylene block copolymer,
(b) 20-40 weight % of an ethylene-.alpha.-olefin copolymer elastomer, and
(c) 20 weight % or less of an inorganic filler, components in the components (a) and (b), which are soluble in p-xylene at a room temperature, having a number-average molecular weight of 4.times.10.sup.4 or more and a weight-average molecular weight of 20.times.10.sup.4 or more.
The second resin composition having excellent paint coatability comprising;
(a) 50-80 weight % of a multi-stage polymerized propylene-ethylene block copolymer,
(b) 20-40 weight % of an ethylene-.alpha.-olefin copolymer elastomer, and
(c) 20 weight % or less of an inorganic filler, components in the components (a) and (b), which are soluble in p-xylene at a room temperature, having a crystallinity of 20-30 %.
The third resin composition having excellent paint coatability comprising;
(a) 50-80 weight % of a multi-stage polymerized propylene-ethylene block copolymer,
(b) 20-40 weight % of an ethylene-.alpha.-olefin copolymer elastomer, and
(c) 20 weight % or less of an inorganic filler, components in the components (a) and (b), which are soluble in p-xylene at a room temperature, having a melting point of 50.degree. C. or higher.
The fourth resin composition having excellent paint coatability comprising;
(a) 50-80 weight % of a multi-stage polymerized propylene-ethylene block copolymer consisting essentially of (i) a propylene homopolymer portion, (ii) a propylene-ethylene random copolymer portion, and (iii) an ethylene homopolymer portion, the propylene-ethylene random copolymer portion having a number-average molecular weight of 20.times.10.sup.4 or more and a weight-average molecular weight of 60.times.10.sup.4 or more;
(b) 20-40 weight % of an ethylene-.alpha.-olefin copolymer elastomer, and
(c) 20 weight % or less of an inorganic filler.
The fifth resin composition having excellent paint coatability comprising;
(a) 50-80 weight % of a multi-stage polymerized propylene-ethylene block copolymer consisting essentially of (i) a propylene homopolymer portion, (ii) a propylene-ethylene random copolymer portion, and (iii) an ethylene homopolymer portion, an ethylene content being 60 weight % or more and the ethylene homopolymer portion (iii) being 40 weight % or more based on the total amount (100 weight %) of the propylene-ethylene random copolymer portion (ii) and the ethylene homopolymer portion (iii);
(b) 20-40 weight % of an ethylene-.alpha.-olefin copolymer elastomer, and
(c) 20 weight % or less of an inorganic filler.
The sixth resin composition having excellent paint coatability comprising;
(a) 50-80 weight % of a multi-stage polymerized propylene-ethylene block copolymer consisting essentially of (i) 80-95 weight % of a propylene homopolymer portion, (ii) 5-20 weight % of a propylene-ethylene random copolymer portion, and (iii) 10 weight % or less of an ethylene homopolymer portion, the propylene homopolymer portion (i) having an intrinsic viscosity of 0.9-1.2 dl/g, the propylene-ethylene random copolymer portion (ii) having an intrinsic viscosity of 4.0 dl/g or more, an ethylene content in the propylene-ethylene random copolymer portion (ii) being 30-70 weight %;
(1) 10-20 weight % of an ethylene-propylene copolymer elastomer;
(b2) 10-20 weight % of an ethylene-butene copolymer elastomer; and
(c) 20 weight % or less of an inorganic filler, the total of the (b1) and (b2) being 25-35 weight %, and a ratio (B/A) of an intrinsic viscosity (B) of the other component than the propylene homopolymer portion (i) in the resin composition to an intrinsic viscosity (A) of the propylene homopolymer portion (i) being within the range of 0.1-2.5.
DETAILED DESCRIPTION OF THE INVENTION
[A] Components of resin composition
[1 ] First resin composition
The first resin composition of the present invention comprises (a) a multi-stage polymerized propylene-ethylene block copolymer, (b) an ethylene-.alpha.-olefin copolymer elastomer, and (c) an inorganic filler.
(a) Multi-stage polymerized propylene-ethylene block copolymer
The propylene-ethylene block copolymer usable in the present invention are those produced by a so-called multi-stage polymerization method. In the multi-stage polymerization, propylene is first polymerized in the presence of a catalyst such as a Ziegler catalyst to form a crystalline propylene homopolymer portion which may contain a small proportion of a comonomer, and then ethylene+propylene are supplied to a reactor to form a propylene-ethylene random copolymer portion.
The propylene-ethylene block copolymer produced by the multi-stage polymerization consists essentially of (i) a crystalline propylene homopolymer portion, (ii) a propylene-ethylene random copolymer portion, and (iii) an ethylene homopolymer portion. These polymer components may exist as separately or in an unseparably combined state. Though each portion of the propylene-ethylene block copolymer consists essentially of propylene and/or ethylene, other .alpha.-olefins and dienes, etc. may be contained in small amounts.
The propylene-ethylene random copolymer portion has a low crystallinity, and preferably contains 30-70 weight % of ethylene. If the ethylene content is lower than 30 weight %, or if it exceeds 70 weight %, the resulting resin composition would show undesirably poor ductility.
The weight-average molecular weight of the propylene-ethylene random copolymer portion (ii) is preferably 20.times.10.sup.4 or more, more preferably 20.times.10.sup.4 -80.times.10.sup.4, most preferably 50.times.10.sup.4 -80.times.10.sup.4. Also, the number-average molecular weight of the propylene-ethylene random copolymer portion is preferably 4.times.10.sup.4 or more, more preferably 4.times.10.sup.4 -10.times.10.sup.4, most preferably 7.times.10.sup.4 -10.times.10.sup.4.
The ethylene content in the entire propylene-ethylene block copolymer is preferably 2-10 weight %. Also, On the basis of the total amount (100 weight %) of the components (i)-(iii), the propylene homopolymer portion (i) is preferably 80-95 weight %, the propylene-ethylene random copolymer portion (ii) is preferably 5-20 weight %, and the ethylene homopolymer portion (iii) is preferably 10 weight % or less. Outside the above ranges, the resin composition would not show good properties.
The multi-stage polymerized propylene-ethylene block copolymer preferably shows a melt flow rate (MFR, 230.degree. C., 2.16 kg lead) of 15-120 g/10 minutes. If the MFR is lower than 15 g/10 minutes, the resulting resin composition would have poor moldability, particularly injection-moldability. On the other hand, if the MFR is higher than 120 g/10minutes, the resin composition would be likely to exhibit poor mechanical strength.
(b) Ethylene-.alpha.-olefin copolymer elastomer
The ethylene-.alpha.-olefin copolymer elastomer is a copolymer elastomer composed of ethylene and at least one other .alpha.-olefin. For instance, an ethylene-propylene copolymer elastomer (EPR), an ethylene-propylene-diene copolymer elastomer (EPDM), an ethylene-butene copolymer elastomer (EBR), etc. are used as the ethylene-.alpha.-olefin copolymer elastomer.
Specifically, in the case of the ethylene-propylene copolymer elastomer (EPR) and the ethylene-propylene-diene copolymer elastomer (EPDM), the preferred ethylene content is 50-90 mol % and the preferred propylene content is 50-10 mol More preferably, the ethylene content is 70-80 reel % and the propylene content is 30-20 reel %. In the case of the ethylene-propylene-diene copolymer elastomer (EPDM), the preferred diene monomers are ethylidene norbornene, dicyclopentadiene, 1,4-hexadiene, etc. The diene content is preferably 1-10 mol %.
The ethylene-propylene copolymer elastomer (EPR) and the ethylene-propylene-diene copolymer elastomer (EPDM) may preferably have a melt flow rate (MFR, 230.degree. C., 2.16 kg load) of 0.5-20 g/10 minutes, and more preferably 0.5-10 g/10 minutes.
The ethylene-butene copolymer elastomer (EBR) preferably has an ethylene content of 70-85 mol %, and a butene-1 content of 30-15 tool %. More preferably, the ethylene content is 75-85 tool % and the butene-1 content is 25-15 tool %. The ethylene-butene copolymer elastomer (EBR) preferably has a melt index (MI, 190.degree. C., 2.16 kg load) of 1-30 g/10 minutes, and more preferably 1-20 g/10 minutes.
The ethylene-.alpha.-olefin copolymer elastomer preferably has a number-average molecular weight of 2.times.10.sup.4 -8.times.10.sup.4, more preferably 3.times.10.sup.4 -6.times.10.sup.4, and a weight-average molecular weight of 7.times.10.sup.4 -20.times.10.sup.4, more preferably 10.times.10.sup.4 -20.times.10.sup.4.
The above-described species of the ethylene-.alpha.-olefin copolymer elastomer may be used alone or in combination.
(e) Inorganic filler
The inorganic fillers are generally used as reinforcing fillers for resins, etc. The inorganic fillers are, for instance, talc, mica, fibrous crystalline calcium silicate, calcium carbonate, etc. Among them, talc is preferable.
The inorganic filler preferably has an average size of 15 .mu.m or less. In the case of needle-shaped or fibrous inorganic filler, its diameter is preferably 1-100 .mu.m, and its aspect ratio is preferably 3-30.
(d) P-xylene-soluble component
A component soluble in p-xylene at a room temperature in the components (a) and (b) is an elastomeric component consisting essentially of the propylene-ethylene random copolymer portion (ii) in the component (a), and the ethylene-.alpha.-olefin copolymer elastomer (b). This p-xylene-soluble component has a number-average molecular weight of 4.times.10.sup.4 or more, preferably 4.times.10.sup.4 -7.times.10.sup.4, and a weight-average molecular weight of 20.times.10.sup.4 or more, preferably 20.times.10.sup.4 -30.times.10.sup.4. If the p-xylene-soluble component has a number-average molecular weight lower than 4.times.10.sup.4 or a weight-average molecular weight lower than 20.times.10.sup.4, the resulting resin composition would have poor mechanical strength, resulting in insufficient improvement in peeling resistance of coatings formed thereon.
Incidentally, the above elastomeric component may be obtained by dissolving the resin composition in boiling p-xylene to separate out the inorganic filler, and cooling it to separate out the propylene homopolymer portion (i) and the ethylene homopolymer portion (iii) as insoluble components, leaving the elastomeric component (ii) in a solution in p-xylene.
(e) Proportions of components in first resin composition
The proportions of the above components (a)-(c) in the first resin composition are such that the propylene-ethylene block copolymer is 50-80 weight %, preferably 55-75 weight %, the ethylene-.alpha.-olefin copolymer elastomer is 20-40 weight %, preferably 20-30 weight %, and the inorganic filler is 20 weight or less, preferably 5-15 weight %.
If the amount of the propylene-ethylene block copolymer is less than 50 weight %, the resulting resin composition would fail to show improved elongation. On the other hand, if the amount of the propylene-ethylene block copolymer is larger than 80 weight %, the resulting resin composition would fail to show improved impact resistance.
If the amount of the ethylene-.alpha.-olefin copolymer elastomer is less than 20 weight %, the resulting resin composition would fail to show improved tensile properties such as tensile elongation at break. On the other hand, If the amount of the ethylene-.alpha.-olefin copolymer elastomer is larger than 40 weight %, the resulting resin composition would fail to show improved mechanical strength such as flexural modulus.
If the amount of the inorganic filler is larger than 20 weight %, the resulting resin composition would fail to show improved impact resistance and tensile elongation. Although there is no particular lower limit in the inorganic filler content, 5 weight % or more of the inorganic filler is preferable to achieve sufficient effects.
[2] Second resin composition
The second resin composition of the present invention comprises (a) a multi-stage polymerized propylene-ethylene block copolymer, (b) an ethylene-.alpha.-olefin copolymer elastomer, and (c) an inorganic filler like the first resin composition.
(a) Multi-stage polymerized propylene-ethylene block copolymer
The multi-stage polymerized propylene-ethylene block copolymer in the second resin composition may be the same as in the first resin composition. Incidentally, in this resin composition, the number-average molecular weight and weight-average molecular weight of the propylene-ethylene block copolymer may not be particularly restricted.
(b) Ethylene-.alpha.olefin copolymer elastomer
The ethylene-.alpha.-olefin copolymer elastomer in the second resin composition may be the same as in the first resin composition, but it is preferable that the ethylene-.alpha.-olefin copolymer elastomer has a crystallinity of 20-30%. With respect to the number-average molecular weight and the weight-average molecular weight, the ethylene-.alpha.-olefin copolymer elastomer may not be restricted.
In order to have the above crystallinity, it is preferable to use both an ethylene-propylene copolymer elastomer (EPR) and an ethylene-butene copolymer elastomer (EBR). Specifically, it is preferable to use an ethylene-propylene copolymer elastomer (EPR) containing 70-80 tool % of ethylene and 20-30 tool % of propylene and having a crystallinity of 10-20%, and an ethylene-butene copolymer elastomer (EBR) containing 70-85 tool % of ethylene and 15-30 tool % of butene-1 and having a crystallinity of 20-30%. By combining 25-75 weight %, preferably 30-70 weight %, of the ethylene-propylene copolymer elastomer (EPR) and 75-25 weight %, preferably 70-30 weight %, of the ethylene-butene copolymer elastomer (EBR), it is possible to provide the ethylene-.alpha.-olefin copolymer elastomer with the desired crystallinity of 20-30%.
Also, the crystallinity of the ethylene-.alpha.-olefin copolymer elastomer can be increased by adding polyethylene such as linear low-density polyethylene, low-density polyethylene, ultra low-density polyethylene, etc. to the ethylene-.alpha.-olefin copolymer elastomer in such a range that elastomeric properties of the ethylene-.alpha.-olefin copolymer elastomer are not deteriorated. Specifically, the polyethylene may be added in an amount of about 20 weight % or less per 100 weight % of the entire resin (including the polyethylene).
(c) Inorganic filler
The inorganic filler in the second resin composition may be the same as in the first resin composition.
(d) P-xylene-soluble component
The p-xylene-soluble component (elastomeric component) contained in the overall resin composition preferably has a crystallinity of 20-30%. If the crystallinity of the elastomeric component is lower than 20%, the elastomeric component does not have sufficient mechanical strength. On the other hand, if the crystallinity of the elastomeric component is higher than 30%, the resin composition would show poor impact resistance.
(e) Proportions of components in second resin composition
The proportions of the above components (a)-(c) in the second resin composition may be the same as in the first resin composition.
[3] Third resin composition
The third resin composition of the present invention comprises (a) a multi-stage polymerized propylene-ethylene block copolymer, (b) an ethylene-.alpha.-olefin copolymer elastomer, and (c) an inorganic filler like the first resin composition.
(a) Multi-stage polymerized propylene-ethylene block copolymer
The multi-stage polymerized propylene-ethylene block copolymer in the third resin composition may be the same as in the first resin composition. Incidentally, in the third resin composition, the number-average molecular weight, weight-average molecular weight and crystallinity of the elastomeric components (propylene-ethylene random copolymer portion (ii) and ethylene-.alpha.-olefin copolymer elastomer (b)) may not be particularly restricted.
(b) Ethylene-.alpha.-olefin copolymer elastomer
The ethylene-.alpha.-olefin copolymer elastomer in the third resin composition may be the same as in the first resin composition, but it is preferable that the ethylene-.alpha.-olefin copolymer elastomer has a melting point of 50.degree.-70.degree. C. With respect to the number-average molecular weight, the weight-average molecular weight and the crystallinity, the ethylene-.alpha.-olefin copolymer elastomer may not be restricted.
Since the ethylene-propylene copolymer elastomer (EPR) including the ethylene-propylene-diene copolymer elastomer (EPDM) has a melting point of 10.degree.-50.degree. C., particularly 30.degree.-50.degree. C., and since the ethylene-butene copolymer elastomer (EBR) has a melting point of 60-90.degree. C., particularly 70.degree.-90.degree. C., it is preferable to combine the ethylene-propylene copolymer elastomer (EPR) and the ethylene-butene copolymer elastomer (EBR) in order to achieve the above crystallinity. Specifically, by combining 25-75 weight %, preferably 30-70 weight %, of the ethylene-propylene copolymer elastomer (EPR) and 75-25 weight %, preferably 70-30 weight %, of the ethylene-butene copolymer elastomer (EBR), it is possible to provide the ethylene-.alpha.-olefin copolymer elastomer with the desired melting point of 50.degree.-70.degree. C.
(c) Inorganic filler
The inorganic filler in the third resin composition may be the same as in the first resin composition.
(d) P-xylene-soluble component
The p-xylene-soluble component (elastomeric component) contained in the overall resin composition preferably has a melting point of 50.degree. C. or higher, more preferably 55.degree.-65.degree. C. If the melting point of the elastomeric component is lower than 50.degree. C., the elastomeric component does not have sufficient heat resistance and high-temperature peeling resistance.
(e) Proportions of components in third resin composition
The proportions of the above components (a)--(c) in the third resin composition are such that the propylene-ethylene block copolymer is 50-80 weight %, preferably 55-75 weight %, the ethylene-.alpha.-olefin copolymer elastomer is 20-40 weight %, preferably 20-30 weight %, and the inorganic filler is 20 weight % or less, preferably 5-15 weight %.
[4] Fourth resin composition
The fourth resin composition of the present invention comprises (a) a multi-stage polymerized propylene-ethylene block copolymer, (b) an ethylene-.alpha.-olefin copolymer elastomer, and (c) an inorganic filler like the first resin composition.
(a) Multi-stage polymerized propylene-ethylene block copolymer
The propylene-ethylene block copolymer usable in the fourth resin composition are those produced by a multi-stage polymerization method as described above with respect to the first resin composition.
The propylene-ethylene block copolymer produced by the multi-stage polymerization consists essentially of (i) a crystalline propylene homopolymer portion, (ii) a propylene-ethylene random copolymer portion, and (iii) an ethylene homopolymer portion.
The propylene-ethylene random copolymer portion has a low crystallinity, and preferably contains 30-70 weight % of ethylene. If the ethylene content is lower than 30 weight %, or if it exceeds 70 weight %. the resulting resin composition would show undesirably poor ductility.
The multi-stage polymerized propylene-ethylene random copolymer portion preferably has a melt flow rate (MFR, 230.degree. C., 2.16 kg lead) of 15-120 g/10 minutes, particularly 60-100 g/10 minutes. If the MFR is lower than 15 g/10 minutes, the resulting resin composition would have poor moldability, particularly injection-moldability. On the other hand, if the MFR is higher than 120 g/10 minutes, the resin composition would be likely to exhibit poor mechanical strength.
The ethylene content in the entire propylene-ethylene block copolymer is preferably 2-10 weight %. Also, On the basis of the total amount (100 weight %) of the components (i)-(iii), the propylene homopolymer portion (i) is preferably 80-95 weight %, the propylene-ethylene random copolymer portion (ii) is preferably 5-20 weight %, and the ethylene homopolymer portion (iii) is preferably 10 weight % or less.
The number-average molecular weight of the propylene-ethylene random copolymer portion (ii) is preferably 20.times.10.sup.4 or more, more preferably 30.times.10.sup.4 -50.times.10.sup.4. Also, the weight-average molecular weight of the propylene-ethylene random copolymer portion (ii) is preferably 60.times.10.sup.4 or more, more preferably 100.times.10.sup.4 -200.times.10.sup.4. If the number-average molecular weight is less than 20.times.10.sup.4 or if the weight-average molecular weight is less than 60.times.10.sup.4, the elastomeric component in the propylene-ethylene block copolymer does not have sufficient mechanical strength, resulting in insufficient peeling resistance of coatings under severe conditions such as high-temperature, high-pressure washing.
In order to achieve the above number-average molecular weight and weight-average molecular weight, it is preferable to reduce a hydrogen concentration in the multi-stage polymerization.
(b) Ethylene-.alpha.-olefin copolymer elastomer
The ethylene-.alpha.-olefin copolymer elastomer is a copolymer elastomer composed of ethylene and at least one other .alpha.-olefin as described with respect to the first resin composition. For instance, an ethylene-propylene copolymer elastomer (EPR), an ethylene-propylene-diene copolymer elastomer (EPDM), an ethylene-butene copolymer elastomer (EBR), etc. are used as the ethylene-.alpha.-olefin copolymer elastomer.
Specifically, in the case of the ethylene-propylene copolymer elastomer (EPR) and the ethylene-propylene-diene copolymer elastomer (EPDM), the preferred ethylene content is 50-90 mol % and the preferred propylene content is 50-10 mol % More preferably, the ethylene content is 70-80 mol % and the propylene content is 30-20 reel %.
The ethylene-propylene copolymer elastomer (EPR) and the ethylene-propylene-diene copolymer elastomer (EPDM) may preferably have a melt flow rate (MFR, 230.degree. C., 2.16 kg lead) of 0.5-20 g/10 minutes, and more preferably 0.5-10 g/10 minutes.
The ethylene-butene copolymer elastomer (EBR) preferably has an ethylene content of 70-85 mol %, and a butene-1 content of 30-15 reel %. More preferably, the ethylene content is 75-85 mol % and the butene-1 content is 25-15 mol %. The ethylene-butene copolymer elastomer (EBR) preferably has a melt index (MI, 190.degree. C., 2.16 kg lead) of 1-30 g/10 minutes, and more preferably 1-20 g/10 minutes.
(c) Inorganic filler
The inorganic filler in the fourth resin composition may be the same as in the first resin composition.
(d) Proportions of components in fourth resin composition
The proportions of the above components (a)-(c) in the fourth resin composition are such that the propylene-ethylene block copolymer is 50-80 weight %, preferably 55-75 weight %, the ethylene-.alpha.-olefin copolymer elastomer is 20-40 weight %, preferably 20-30 weight %, and the inorganic filler is 20 weight % or less, preferably 5-15 weight %.
[5] Fifth rosin composition
The fifth rosin composition of the present invention comprises (a) a multi-stage polymerized propylene-ethylene block copolymer, (b) an ethylene-.alpha.-olefin copolymer elastomer, and (c) an inorganic filler like the first resin composition.
(a) Multi-stage polymerized propylene-ethylene block copolymer
The multi-stage polymerized propylene-ethylene block copolymer in the fifth resin composition may be the same as in the fourth rosin composition. In this propylene-ethylene block copolymer, the ethylene content is (60 weight % or more, preferably 60-70 weight %, and the crystalline ethylene homopolymer portion (iii) is 40 weight % or more, preferably 40-60 weight %, based on the total amount (100 weight %) of the propylene-ethylene random copolymer portion (ii) and the crystalline ethylene homopolymer portion (iii).
If the ethylene content is lower than 60 weight %, or if the ethylene homopolymer portion is lower than 40 weight %, the elastomeric component in the propylene-ethylene block copolymer does not have sufficient mechanical strength, resulting in insufficient peeling resistance of coatings under severe conditions such as high-temperature, high-pressure washing.
The ethylene content in the entire propylene-ethylene block copolymer is preferably 2-15 weight %. Also, On the basis of the total amount (100 weight %) of the components (i)-(iii), the propylene homopolymer portion (i) is preferably 80-95 weight %, more preferably 80-90 weight %, the propylene-ethylene random copolymer portion (ii) is preferably 5-20 weight %, more preferably 5-10 weight %, and the ethylene homopolymer portion (iii) is preferably 10 weight % or less, more preferably 5-10 weight %.
Incidentally, in this resin composition, the number-average molecular weight and weight-average molecular weight of the propylene-ethylene block copolymer may not be particularly restricted.
In order to achieve the above ethylene content, it is preferable to increase a ratio of ethylene to propylene in the multi-stage polymerization.
(b) Ethylene-.alpha.-olefin copolymer elastomer
The ethylene-.alpha.-olefin copolymer elastomer in the fifth resin composition may be the same as in the first resin composition.
(c) Inorganic filler
The inorganic filler in the fifth resin composition may be the same as in the first resin composition.
(d) Proportions of components in fifth resin composition
The proportions of the above components (a)-(c) in the fifth resin composition are such that the propylene-ethylene block copolymer is 50-80 weight %, preferably 55-75 weight %, the ethylene-.alpha.-olefin copolymer elastomer is 20-40 weight %, preferably 20-30 weight %, and the inorganic filler is 20 weight % or less, preferably 5-15 weight %.
[6] Sixth resin composition
The sixth resin composition of the present invention comprises (a) a multi-stage polymerized propylene-ethylene block copolymer, (b 1) an ethylene-propylene copolymer elastomer, (b2) an ethylene-butene copolymer elastomer, and (c) an inorganic filler.
(a) Multi-stage polymerized propylene-ethylene block copolymer
The propylene-ethylene block copolymer produced by a multi-stage polymerization method consists essentially of (i) a crystalline propylene homopolymer portion, (ii) a propylene-ethylene random copolymer portion, and (iii) an ethylene homopolymer portion.
The propylene homopolymer portion (i) preferably has an intrinsic viscosity [.eta.].sub.H of 0.9-1.2 dl/g. If the intrinsic viscosity [.eta.].sub.H is lower than 0.9 dl/g. the resin composition would show poor ductility. On the other hand, if the intrinsic viscosity [.eta.].sub.H is higher than 1.2 dl/g, the resin composition would show poor flowability.
The propylene-ethylene random copolymer portion (ii) has a low crystallinity, and preferably contains 30-70 weight % of ethylene. If the ethylene content is lower than 30 weight %, or if it exceeds 70 weight %, the resulting resin composition would show undesirably poor ductility.
The propylene-ethylene random copolymer portion (ii) preferably has an intrinsic viscosity [.eta.].sub.CXS of 4.0 dl/g or more. If the intrinsic viscosity [.eta.].sub.CXS is lower than 4.0 dl/g, the resin composition would not show sufficient impact resistance. The preferred intrinsic viscosity [.eta.].sub.CXS is 4-10 dl/g.
The ethylene content in the entire propylene-ethylene block copolymer is preferably 2-10 weight %, preferably 2-5 weight %. Also, On the basis of the total amount (100 weight %) of the components (i)-(iii), the propylene homopolymer portion (i) is preferably 80-95 weight %, more preferably 90-96 weight %, the propylene-ethylene random copolymer portion (ii) is preferably 5-20 weight %, more preferably 4-10 weight %, and the ethylene homopolymer portion (iii) is preferably 10 weight % or less, more preferably 5 weight % or less.
The multi-stage polymerized propylene-ethylene block copolymer preferably shows a melt flow rate (MFR, 230.degree. C., 2.16 kg load) of 40-120 g/10 minutes, particularly 60-100 g/10 minutes. If the MFR is lower than 40 g/10 minutes, the resulting resin composition would have poor moldability, particularly injection-moldability. On the other hand, if the MFR is higher than 120 g/10 minutes, the resin composition would be likely to exhibit poor mechanical strength.
(b) Ethylene-.alpha.-olefin copolymer elastomer
The ethylene-.alpha.-olefin copolymer elastomer in the sixth resin composition may be the same as in the first resin composition.
(c) Inorganic filler
The inorganic filler in the fifth resin composition may be the same as in the first resin composition.
(d) Intrinsic viscosity ratio
The sixth resin composition should meet the requirement that a ratio of the intrinsic viscosity [.eta.].sub.B of the other polymer component than the propylene homopolymer portion in the resin composition to the intrinsic viscosity [.eta.].sub.A of the propylene homopolymer portion, which is simply referred to as "B/A ratio", is within the range of 0.1-2.5. Outside the above range, the injection moldings of the resin composition would show large molding shrinkage and linear expansion coefficient, leading to poor dimension stability. Particularly, the dimension stability required for large moldings (molding shrinkage: less than 8/1000, and linear expansion coefficient: less than 8.times.10.sup.-5 /.degree. C.) cannot be obtained if the above intrinsic viscosity ratio requirement is not met.
(e) Proportions of components in sixth resin composition
The proportions of the above components (a)-(c) in the sixth resin composition are such that the multi-stage polymerized propylene-ethylene block copolymer (a) is 50-80 weight %, preferably 55-75 weight %, the ethylene-propylene copolymer elastomer (b1) is 10-20 weight %, preferably. 5-15 weight %, the ethylene-butene copolymer elastomer (b2) is 10-20 weight %, preferably 5-15 weight %, and the inorganic filler (c) is 20 weight % or less, preferably 5-15 weight %. Incidentally, the total amount of the ethylene-propylene copolymer elastomer (b1) and the ethylene-butene copolymer elastomer (b2) is preferably 20-40 weight %, particularly 25-35 weight %.
If the amount of the propylene-ethylene block copolymer is less than 50 weight %, the resulting resin composition would fail to show improved elongation. On the other hand, if the amount of the propylene-ethylene block copolymer is larger than 80 weight %, the resulting resin composition would fail to show improved impact resistance.
If the amount of the ethylene-propylene copolymer elastomer is less than 10 weight %, the resulting resin composition would fail to show improved tensile properties such as tensile elongation at break. On the other hand, If the amount of the ethylene-propylene copolymer elastomer is larger than 20 weight %, the resulting resin composition would fail to show improved mechanical strength such as flexural modulus.
If the amount of the ethylene-butene copolymer elastomer is less than 10 weight %, the resulting resin composition would fail to show improved hardness On the other hand, If the amount of the ethylene-butene copolymer elastomer is larger than 20 weight %, the resulting resin composition would fail to show improved mechanical strength such as flexural modulus.
If the total amount of the ethylene-propylene copolymer elastomer and the ethylene-butene copolymer elastomer is less than 20 weight %, the resulting resin composition would fail to show improved tensile elongation at break and impact resistance. On the other hand, If the total amount of the ethylene-propylene copolymer elastomer and the ethylene-butene copolymer elastomer is larger than 40 weight %, the resulting resin composition would fail to show improved flexural modulus, hardness, thermal deformation resistance, etc.
If the amount of the inorganic filler is larger than 20 weight %, the resulting resin composition would fail to show improved impact resistance and tensile elongation. Although there is no particular lower limit in the inorganic filler content, 5 weight % or more of the inorganic filler is preferable to achieve sufficient effects.
By satisfying two or more requirements in the above first to sixth resin compositions, it is possible to provide a resin composition with highly improved paint coatability, peeling resistance of coatings formed thereon, and other properties.
[B] Other components in resin composition
To improve the properties of the first to sixth resin compositions, various other additives such as heat stabilizers, antioxidants, photostabilizers, flame retardants, plasticizers, antistatic agents, parting agents, foaming agents, etc. may be added.
Typical examples of the preferred combinations of the parameters other than those of the first to sixth resin compositions will be shown below.
(1) Components in the components (a) and (b), which are soluble in p-xylene at a room temperature, have an Mn of 4.times.10.sup.4 or more, an Mw of 20.times.10.sup.4 or more, and a crystallinity of 20-30%.
(2) Components in the components (a) and (b), which are soluble in p-xylene at a room temperature, have an Mn of 4.times.10.sup.4 or more, an Mw of 20.times.10.sup.4 or more, and a melting point of 50.degree. C. or higher.
(3) Components in the components (a) and (b), which are soluble in p-xylene at a room temperature, have a crystallinity of 20-30%, and a melting point of 50.degree. C. or higher.
(4) Components in the components (a) and (b), which are soluble in p-xylene at a room temperature, have an Mn of 4.times.10.sup.4 or more, an Mw of 20.times.10.sup.4 or more, a crystallinity of 20-30%, and a melting point of 50.degree. C. or higher.
(5) The propylene-ethylene random copolymer portion has a number of 20.times.10.sup.4 or more and an Mw of 60.times.10.sup.4 or more, and an ethylene content is 60 weight % or more and the ethylene homopolymer portion (iii) is 40 weight % or more based on the total amount of (ii) and (iii).
[C] Method of producing resin compositions
The first to sixth resin compositions of the present invention can be produced by blending the components at 150.degree.-300.degree. C., preferably 190.degree.-250.degree. C. in a single-screw extruder or a double-screw extruder.
The present invention will be explained in further detail by way of the following Examples without intention of restricting the scope of the present invention.
EXAMPLES 1-12, COMPARATIVE EXAMPLES 1 AND 2
Starting materials used in those Examples and Comparative Examples are as follows:
(a) Multi-stage polymerized propylene-ethylene block copolymer
BPP-1: [ethylene content: 4 weight %, melt flow rate (MFR, 230.degree. C., 2.16 kg lead): 60 g/10 minutes].
(b1) Ethylene-propylene copolymer elastomer
EPR-1: [propylene content: 23 weight %, melt flow rate (MFR, 230.degree. C., 2.16 kg lead): 0.8 g/10 minutes, hardness (JIS A): 74, melting point: 43.degree. C., crystallinity: 11%, number-average molecular weight: 5.7.times.10.sup.4, weight-average molecular weight: 14.2.times.10.sup.4 ].
EPR-2: [propylene content: 22 weight %, melt flow rate (MFR, 230.degree. C., 2.16 kg lead): 3.6 g/10 minutes, hardness (JIS A): 73, melting point: 41.3.degree. C., crystallinity: 12%, number-average molecular weight: 4.5.times.10.sup.4, weight-average molecular weight: 9.9.times.10.sup.4 ].
(b2) Ethylene-butene copolymer elastomer
EBR-1: [butene-1 content: 20 weight %, melt index (MI, 190.degree. C., 2.16 kg lead): 1.3 g/10 minutes, hardness (JIS A): 87, melting point: 78.2.degree. C., crystallinity: 26%, number-average molecular weight: 6.5.times.10.sup.4, weight-average molecular weight: 12.7.times.10.sup.4 ].
EBR-2: [butene-1 content: 20 weight %, melt index (MI, 190.degree. (2, 2.16 kg lead): 3.5 g/10 minutes, hardness (JIS A): 85, melting point: 70.8.degree. C:, crystallinity: 25%, number-average molecular weight: 3.8.times.10.sup.4, weight-average molecular weight: 8.3.times.10.sup.4 ].
(c) Inorganic filler
Talc: [LMS300 available from Fuji Talc K. K., average size: 1.25 .mu.m]
(d) Linear low-density polyethylene
LLDPE: [density: 0.930 g/cm.sup.3, melt index (MI, 190.degree. C., 2.16 kg load): 1.0 g/10 minutes].
A multi-stage polymerized propylene-ethylene block copolymer (BPP-1), an ethylene-propylene copolymer elastomer (EPR-1, EPR-2), an ethylene-butene copolymer elastomer (EBR-1, EBR-2), talc and optionally linear low-density polyethylene were dry-blended in proportions shown in Table 1 below by a supermixer and introduced into a double-screw extruder to conduct their blending at 190.degree.-250.degree. C. and at 200 rpm to produce composition pellets.
The resulting composition was dissolved in boiling p-xylene to separate out an inorganic filler (talc) as an insoluble component, and then cooled to separate out a propylene homopolymer portion and an ethylene homopolymer portion as insoluble components. The remaining elastomeric component was measured with respect to a weight-average molecular weight (Mw), a number-average molecular weight (Mn), a crystallinity and a melting point. The results are shown in Table 1.
The composition pellets were injection-molded at 210.degree. C. to form specimens for measuring their properties (melt flow rate, flexural modulus, Izod impact strength, peeling resistance of coating formed thereon, and resistance to washing). The results are shown in Table 2.
As is clear from Table 2, the resin compositions of the present invention are excellent in paint coatability, peeling resistance at high temperature and resistance to high-temperature, high-pressure washing.
EXAMPLES 13-17, COMPARATIVE EXAMPLE 3
Starting materials used in these Examples and Comparative Examples are as follows:
(a) Multi-stage polymerized propylene-ethylene block copolymers shown in Table 3 below.
(b1 ) Ethylene-propylene copolymer elastomer
EPR-1: [propylene content: 23 weight %, melt flow rate (MFR, 230.degree. C., 2.16 kg lead): 0.8 g/10 minutes, hardness (JIS A): 74, melting point: 43.degree. C., crystallinity: 11%, number-average molecular weight: 5.7.times.10.sup.4, weight-average molecular weight: 14.2.times.10.sup.4 ].
(b2) Ethylene-butene copolymer elastomer
EBR-1: [butene-1 content: 20 weight %, melt index (MI, 190.degree. C., 2.16 kg lead): 1.3 g/10 minutes, hardness (JIS A): 87, melting point: 78.2.degree. C., crystallinity: 26%, number-average molecular weight: 6.5.times.10.sup.4, weight-average molecular weight: 12.7.times.10.sup.4 ].
(c) Inorganic filler
Talc: [LMS300 available from Fuji Talc K. K., average size: 1.25 .mu.m]
A multi-stage polymerized propylene-ethylene block copolymer (BPP-1), an ethylene-propylene copolymer elastomer (EPR-1), an ethylene-butene copolymer elastomer (EBR-1) and talc were dry-blended in proportions shown in Table 4 below by a supermixer and introduced into a double-screw extruder to conduct their blending at 190.degree.-250.degree. C. and at 200 rpm to produce composition pellets.
The composition pellets were injection-molded at 210.degree. C. to form specimens for measuring their properties (melt flow rate, flexural modulus, Izod impact strength, peeling resistance of coating formed thereon, and resistance to washing). The results are shown in Table 5.
As is clear from Table 5, the resin composition of the present invention are excellent in paint coatability, peeling resistance at high temperature and peeling resistance to high-temperature, high-pressure washing.
EXAMPLES 18-24, COMPARATIVE EXAMPLE 4-12
Starting materials used in these Examples and Comparative Examples are as follows:
(a) Two-stage polymerized propylene-ethylene block copolymer shown in Table 6.
(b1) Ethylene-propylene copolymer elastomer
EPR-1: [propylene content: 23 weight %, melt flow rate (MFR, 230.degree. C., 2.16 kg load): 0.8 g/10 minutes, hardness (JIS A): 74, melting point: 43.degree. C., crystallinity: 11%, number-average molecular weight: 5.7.times.10.sup.4, weight-average molecular weight: 14.2.times.10.sup.4 ].
EPR-2: [propylene content: 22 weight %, melt flow rate (MFR, 230.degree. C., 2.16 kg load): 3.6 g/10 minutes, hardness (JIS A): 73, melting point: 41.3.degree. C., crystallinity: 12%, number-average molecular weight: 4.5.times.10.sup.4, weight-average molecular weight: 9.9.times.10.sup.4 ].
EPR-3: [propylene content: 23 weight %, intrinsic viscosity [.eta.] (in decalin at 135.degree. C.): 2.5 dl/g].
(b2) Ethylene-butene copolymer elastomer
EBR-2:[butene-1 content: 20 weight %, melt index (MI, 190.degree. C., 2.16 kg load): 3.5 g/10 minutes, hardness (JIS A): 85, melting point: 70.8.degree. C., crystallinity: 25%, number-average molecular weight: 3.8.times.10.sup.4, weight-average molecular weight: 8.3.times.10.sup.4 ].
EBR-3: [butene-1 content: 17 weight %, melt index (MI, 190.degree. C., 2.16 kg load): 20 g/10 minutes, hardness (JIS A): 89].
EBR-4:[butene-1 content: 20 weight %, intrinsic viscosity [.eta.] (in decalin at 135.degree. C.): 2.0 dl/g].
(c) Inorganic filler
Tale: [LMS300 available from Fuji Tale K. K., average size: 1.25 .mu.m]
Multi-stage polymerized propylene-ethylene block copolymers (BPP-7 -BPP-14), ethylene-propylene copolymer elastomers (EPR-1 -EPR-3), ethylene-butene copolymer elastomers (EBR-2 -EBR-4) and tale were dry-blended in proportions shown in Table 7 below by a supermixer and introduced into a double-screw extruder to conduct their blending at 190.degree.-250.degree. C. and at 200 rpm to produce composition pellets.
The composition pellets were injection-molded at 210.degree. C. and at a pressure of 600 kg/cm.sup.2 to form specimens for measuring their properties (melt flow rate, tensile elongation at break, flexural modulus, Izod impact strength, thermal deformation resistance, Rockwell hardness, heat sag, brittle temperature, molding shrinkage, linear expansion coefficient, and intrinsic viscosity ratio of other polymer components than the propylene homopolymer portion in the resin composition to the propylene homopolymer portion). The results are shown in Table 8.
As is clear from Table 8, the resin compositions of the present invention are excellent in moldability (expressed by MFR), tensile elongation at break, paint coatability, flexural modulus, impact resistance, thermal deformation resistance, Rockwell hardness, heat sag, brittle temperature, molding shrinkage and linear expansion coefficient. On the other hand, those of Comparative Examples are poor in at least one of these properties. Incidentally, in Comparative Example 12, in which the intrinsic viscosity ratio was outside the range required on the sixth resin composition of the present invention, the resin composition showed poor molding shrinkage and linear expansion coefficient though it had good mechanical strength and moldability.
All specimens of Examples and Comparative Examples were washed with a trichloroethane vapor, coated with a primer and a urethane topcoat paint according to a standard coating method, and a cross-cut adhesion test was conducted before and after immersion in warm water at 40.degree. C. for 240 hours to observe the adhesion and blisters of the coat. As a result, it was confirmed that all specimens of Examples showed good adhesion of the coat with no blisters. Therefore, it can be concluded that the resin compositions of the present invention arc excellent in paint coatability expressed by adhesion and water resistance, etc.
As described above in detail, since the resin composition of the present invention comprises a multi-stage polymerized propylene-ethylene block copolymer, an ethylene-.alpha.-olefin copolymer elastomer and an inorganic filler, and since the elastomeric component (total of a propylene-ethylene random copolymer portion in the propylene-ethylene block copolymer, and an ethylene-.alpha.-olefin copolymer elastomer) in the resin composition is designed to have high strength, the resin composition shows excellent paint coatability, peeling resistance of paint coatings and resistance to high-temperature, high-pressure washing, in addition to welled balanced mechanical properties such as impact resistance, ductility, tensile elongation, thermal deformation resistance, brittle temperature, and hardness. Also, it suffers from only small molding shrinkage and linear expansion coefficient.
Such resin compositions of the present invention are usable in various applications, and particularly suitable for exterior automotive parts, etc.
Claims
What is claimed is:
1. A resin composition having excellent paint coatability comprising: (a) 50-80 weight % of a multi-stage polymerized propylene-ethylene block copolymer consisting essentially of (i) 80-95 weight % of a propylene homopolymer portion, (ii) 5-20 weight % of a propylene-ethylene random copolymer portion, and (iii) 10 weight % or less of an ethylene homopolymer portion, said propylene homopolymer portion (i) having an intrinsic viscosity of 0.9-1.2 dl/g, said propylene-ethylene random copolymer portion (ii) having an intrinsic viscosity of 4.0 dl/g or more, an ethylene content in said propylene-ethylene random copolymer portion (ii) being 30-70 weight %; (b) 10-20 weight % of an ethylene-propylene copolymer elastomer and 10-20 weight % of an ethylene-butene copolymer elastomer, the total amount of said ethylene-propylene copolymer and said ethylene-butene copolymer elastomer being 25-35 weight %, and (c) 20 weight % or less of an inorganic filler, wherein an elastomeric component consisting essentially of said propylene-ethylene random copolymer portion (ii) in said multi-stage polymerized propylene-ethylene block copolymer, said ethylene-propylene copolymer elastomer and said ethylene-butene copolymer elastomer, which is soluble in p-xylene at room temperature, meets at least one of the following requirements of: (i) a number-average molecular weight of 4.times.10.sup.4 or more and a weight-average molecular weight of 20.times.10.sup.4 or more; (ii) a crystallinity of 20-30%; and (iii) a melting point of 50.degree. C. or higher.
2. A resin composition having excellent paint coatability comprising; (a) 50-80 weight % of a multi-stage polymerized propylene-ethylene block copolymer consisting essentially of (i) 80-95 weight % of a propylene homopolymer portion, (ii) 5-20 weight % of a propylene-ethylene random copolymer portion, and (iii) 10 weight % or less of an ethylene homopolymer portion, said propylene homopolymer portion (i) having an intrinsic viscosity of 0.9-1.2 dl/g, said propylene-ethylene random copolymer portion (ii) having an intrinsic viscosity of 4.0 dl/g or more, an ethylene content in said propylene-ethylene random copolymer portion (ii) being 30-70 weight %; (b1)10-20 weight % of an ethylene-propylene copolymer elastomer; (b2) 10-20 weight % of an ethylene-butene copolymer elastomer; and (c) 20 weight % or less of an inorganic filler, the total of said (b1) and said (b2) being 25-35 weight %, and a ratio (B/A) of an intrinsic viscosity (B) of the other component than said propylene homopolymer portion (i) in said resin composition to an intrinsic viscosity (A) of said propylene homopolymer portion (i) being within the range of 0.1-2.5.
3. The resin composition according to claim 2, wherein said multi-stage polymerized propylene-ethylene block copolymer has a melt flow rate (MFR, 230.degree. C., 2.16 kg load) of 40-120 g/10 minutes.
Patent Citations (15)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US4480065 | 1984-10-01 | Kawai et al. | |
| US4705818 | 1987-11-01 | Kawai et al. | |
| US4748206 | 1988-04-01 | Nogiwa et al. | |
| US4764404 | 1988-08-01 | Genske et al. | |
| US4960823 | 1990-10-01 | Komatsu et al. | |
| US5045589 | 1991-09-01 | Ueno | |
| US5308908 | 1994-05-01 | Fukai et al. | |
| EPX132968 | 1984-07-01 | ||
| JPX1204946 | 1989-08-01 | ||
| JPX4153243 | 1992-05-01 | ||
| GBX2097408 | 1982-03-01 | ||
| GBX265075 | 1987-09-01 | ||
| GBX2206886 | 1988-06-01 | ||
| GBX2246358 | 1991-09-01 | ||
| WOXWO90/01519 | 1990-02-01 |
Non-Patent Literature (2)
- European Search Report, Examiner E. K-H Kaumann, Application Number EP 93 30 2604, Sep. 15, 1993 and Annex.
- Brochure of TAFMER A/P (Ethylene/Alpha-Olefin Copolymer).