Beta Crystalline Modification of 2,2',2"-Nitrilo[triethyl-Tris-(3,3',5,5'-Tetra-Tert-Butyl-1,1'-Biphenyl- 2,2'-Diyl) Phosphite]

This invention pertains to a novel crystalline modification of 2,2',2"-nitrilo[triethyl-tris-(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2, 2'-diyl) phosphite], to processes for preparing said modification, and to compositions stabilized therewith.

2,2',2"-Nitrilo[triethyl-tris-(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2,2 '-diyl) phosphite] is a compound having the formula I ##STR1##

This compound of formula I is useful as a processing stabilizer for organic polymers as taught in U.S. Pat. Nos. 4,318,845 and 4,374,219. The compound of formula I is disclosed as being a white powder melting at 121.degree.-134.degree. C. As such, the powdery product has defects in terms of handling and apparent density, and exhibiting poor flowability, diffusibility into polymers, meterability, storage stability and hydrolytic stability.

It has now been found that the compound of formula I can be obtained in a different crystalline modification as purified crystalline particles which exhibit acceptable properties in respect to handling, apparent density, flowability, meterability, storage stability, hydrolytic stability and better migration into polymeric substrates.

The new beta modification is characterized by a triclinic crystalline form, melting in the range of 200.degree.-207.degree. C. as given by the peak temperature of the endotherm recorded by differential scanning calorimetry (DSC); and by an X-ray diffraction pattern obtained using Cu-K.alpha. which exhibits diffraction angles (2.THETA.) of very high intensity at 8.4 and 17; lines of high intensity at 9.9, 10.6, 11.4, 17.5, 19.1, 20.2; lines of medium intensity at 4.6, 4.9, 7.1, 12.7, 13.2, 13.6, 15.3, 15.8, 16.4, 16.7, 18.4, 19.7, 21.7, 23.4; and lines of weak intensity at 7.8, 8.8, 9.4, 12, 14.1, 14.6, 21, 22.3, 22.8, 23.9, 24.7, 25.3, 25.5, 26.4, 27.27.7, 28.4 and a relative absolute configuration of the three stereo axes of the dibenzo[d,f][1,3,2]dloxaphosphepin rings of R*,R*,S*.

R* and S* follow the customary convention when the absolute configuration of a molecule is unknown. The nomenclature adopted here is based on recent Chemical Abstracts Service practice as described by L. C. Cross and W. Kylne, Pure Appl. Chem. 45, 11-30 (1976).

The instant invention also relates to processes for the preparation of this novel beta crystalline modification of the compound of formula I.

The instant invention also pertains to a composition stabilized against thermal, oxidative and actinic induced degradation which comprises

(a) an organic material subject to thermal, oxidative or actinic induced degradation, and

(b) an effective stabilizing mount of the beta, triclinic crystalline form of 2,2',2"-nitrilo[triethyl-tris-(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2, 2'-diyl) phosphite], characterized by melting in the range of 200.degree.-207.degree. C. and by an X-ray diffraction pattern exhibiting lines of very high intensity at 8.4 and 17; lines of high intensity at 9.9, 10.6, 11.4, 17.5, 19.1, 20.2; lines of medium intensity at4.6, 4.9, 7.1, 12.7, 13.2, 13.6, 15.3, 15.8, 16.4, 16.7, 18.4, 19.7, 21.7, 23.4; and lines of weak intensity at 7.8, 8.8, 9.4, 12, 14.1, 14.6, 21, 22.3, 22.8, 23.9, 24.7, 25.3, 25.5, 26.4, 27.27.7, 28.4 and a relative absolute configuration of the three stereo axes of the dibenzo[d,f][1,3,2]dioxaphosphepin rings of R*,R*,S*.

The organic material is preferably a polymer processed at elevated temperatures. Particularly preferred organic polymers are the polyolefins, especially polypropylene and polyethylene, and polyamides. Most particularly the organic polymer is polypropylene.

The compounds of this invention are very effective processing stabilizers for polyolefins than the prior art compounds both in preventing molecular weight changes as well as preventing discoloration.

In general polymers which can be stabilized include

1. Polymers of monoolefins and diolefins, for example polypropylene, polyisobutylene, polybut-1-ene, poly-4-methylpent-1-ene, polyisoprene or polybutadiene, as well as polymers of cycloolefins, for instance of cyclopentene or norbornene, polyethylene (which optionally can be crosslinked), for example high density polyethylene (HI)PE), low density polyethylene (LDPE), linear low density polyethylene (LLDPE), branched low density polyethylene (BLDPE).

Polyolefins, i.e. the polymers of monoolefins exemplified in the preceding paragraph, preferably polyethylene and polypropylene, can be prepared by different, and especially by the following, methods:

a) radical polymerisation (normally under high pressure and at elevated temperature).

b) catalytic polymerisation using a catalyst that normally contains one or more than one metal of groups IVb, Vb, VIb or VIII of the Periodic Table. These metals usually have one or more than one ligand, typically oxides, halides, alcoholates, esters, ethers, amines, alkyls, alkenyls and/or aryls that may be either .pi.- or .sigma.-coordinated. These metal complexes may be in the free form or fixed on substrates, typically on activated magnesium chloride, titanium(III) chloride, alumina or silicon oxide. These catalysts may be soluble or insoluble in the polymerisation medium. The catalysts can be used by themselves in the polymerisation or further activators may be used, typically metal alkyls, metal hydrides, metal alkyl halides, metal alkyl oxides or metal alkyloxanes, said metals being elements of groups la, Ha and/or IIIa of the Periodic Table. The activators may be modified conveniently with further ester, ether, mine or silyl ether groups. These catalyst systems are usually termed Phillips, Standard Oil Indiana, Ziegler (-Natta), TNZ (DuPont), metallocene or single site catalysts (SSC).

2. Mixtures of the polymers mentioned under 1), for example mixtures of polypropylene with polyisobutylene, polypropylene with polyethylene (for example PP/HDPE, PP/LDPE) and mixtures of different types of polyethylene (for example LDPE/HDPE).

3. Copolymers of monoolefins and diolefins with each other or with other vinyl monomers, for example ethylene/propylene copolymers, linear low density polyethylene (LLDPE) and mixtures thereof with low density polyethylene (LDPE), propylene/but-1-ene copolymers, propylene/isobutylene copolymers, ethylene/but-1-ene copolymers, ethylene/hexene copolymers, ethylene/methylpentene copolymers, ethylene/heptene copolymers, ethylene/octene copolymers, propylene/butadiene copolymers, isobutylene/isoprene copolymers, ethylene/alkyl acrylate copolymers, ethylene/alkyl methacrylate copolymers, ethylene/vinyl acetate copolymers and their copolymers with carbon monoxide or ethylene/acrylic acid copolymers and their salts (ionomers) as well as terpolymers of ethylene with propylene and a diene such as hexadiene, dicyclopentadiene or ethylidene-norbornene; and mixtures of such copolymers with one another and with polymers mentioned in 1 ) above, for example polypropylene/ethylene-propylene copolymers, LDPE/ethylene-vinyl acetate copolymers (EVA), LDPE/ethylene-acrylic acid copolymers (EAA), LLDPE/EVA, LLDPE/EAA and alternating or random polyalkylene/carbon monoxide copolymers and mixtures thereof with other polymers, for example polyamides.

4. Hydrocarbon resins (for example C.sub.5 -C.sub.9) including hydrogenated modifications thereof (e.g. tackdriers) and mixtures of polyalkylenes and starch.

5. Polystyrene, poly(p-methylstyrene), poly(.alpha.-methylstyrene).

6. Copolymers of styrene or .alpha.-methylstyrene with dienes or acrylic derivatives, for example styrene/butadiene, styrene/acrylonitrile, styrene/alkyl methacrylate, styrene/butadiene/alkyl acrylate, styrenefoutadiene/alkyl methacrylate, styrene/maleic anhydride, styrene/acrylonitrile/methyl acrylate; mixtures of high impact strength of styrene copolymers and another polymer, for example a polyacrylate, a diene polymer or an ethylene/propylene/diene terpolymer, and block copolymers of styrene such as styrene/butadiene/styrene, styrene/isoprene/styrene, styrene/ethylene/butylene/styrene or styrene/ethylene/propylene/styrene.

7. Graft copolymers of styrene or .alpha.-methylstyrene, for example styrene on polybutadiene, styrene on polybutadiene-styrene or polybutadiene-acrylonitrile copolymers; styrene and acrylonitrile (or methacrylonitrile) on polybutadiene; styrene, acrylonitrile and methyl methacrylate on polybutadiene; styrene and maleic anhydride on polybutadiene; styrene, acrylonitrile and maleic anhydride or maleimide on polybutadiene; styrene and maleimide on polybutadiene; styrene and alkyl acrylates or methacrylates on polybutadiene; styrene and acrylonitrile on ethylene/propylene/diene terpolymers; styrene and acrylonitrile on polyalkyl acrylates or polyalkyl methacrylates, styrene and acrylonitrile on acrylate/butadiene copolymers, as well as mixtures thereof with the copolymers listed under 6), for example the copolymer mixtures known as ABS, MBS, ASA or AES polymers.

8. Halogen-containing polymers such as polychloroprene, chlorinated rubbers, chlorinated or sulfochlorinated polyethylene, copolymers of ethylene and chlorinated ethylene, epichlorohydrin homo- and copolymers, especially polymers of halogen-containing vinyl compounds, for example polyvinyl chloride, polyvinylidene chloride, polyvinyl fluoride, polyvinylidene fluoride, as well as copolymers thereof such as vinyl chloride/vinylidene chloride, vinyl chloride/vinyl acetate or vinylidene chloride/vinyl acetate copolymers.

9. Polymers derived from .alpha.,.beta.-unsaturated acids and derivatives thereof such as polyacrylates and polymethacrylates; polymethyl methacrylates, polyacrylamides and polyacrylonitriles, impact-modified with butyl acrylate.

10. Copolymers of the monomers mentioned under 9) with each other or with other unsaturated monomers, for example acrylonitrile/butadiene copolymers, acrylonitrile/alkyl acrylate copolymers, acrylonitrile/alkoxyalkyl acrylate or acrylonitrile/vinyl halide copolymers or acrylonitrile/alkyl methacrylate/butadiene terpolymers.

11. Polymers derived from unsaturated alcohols and amines or the acyl derivatives or acetals thereof, for example polyvinyl alcohol, polyvinyl acetate, polyvinyl stearate, polyvinyl benzoate, polyvinyl maleate, polyvinyl butyral, polyallyl phthalate or polyallyl melamine; as well as their copolymers with olefins mentioned in 1) above.

12. Homopolymers and copolymers of cyclic ethers such as polyalkylene glycols, polyethylene oxide, polypropylene oxide or copolymers thereof with bisglycidyl ethers.

13. Polyacetals such as polyoxymethylene and those polyoxymethylenes which contain ethylene oxide as a comonomer, polyacetals modified with thermoplastic polyurethanes, acrylates or MBS.

14. Polyphenylene oxides and sulfides, and mixtures of polyphenylene oxides with styrene polymers or polyamides.

15. Polyurethanes derived from hydroxyl-terminated polyethers, polyesters or polybutadienes on the one hand and aliphatic or aromatic polyisocyanates on the other, as well as precursors thereof.

16. Polyamides and copolyamides derived from diamines and dicarboxylic acids and/or from aminocarboxylic acids or the corresponding lactams, for example polyamide 4, polyamide 6, polyamide 6/6, 6/10, 6/9, 6/12, 4/6, 12/12, polyamide 11, polyamide 12, aromatic polyamides starting from m-xylene diamine and adipic acid; polyamides prepared from hexamethylenediamine and isophthalic or/and terephthalic acid and with or without an elastomer as modifier, for example poly-2,4,4,-trimethylhexamethylene terephthalamide or poly-m-phenylene isophthalamide; and also block copolymers of the aforementioned polyamides with polyolefins, olefin copolymers, ionomers or chemically bonded or grafted elastomers; or with polyethers, e.g. with polyethylene glycol, polypropylene glycol or polytetramethylene glycol; as well as polyamides or copolyamides modified with EPDM or ABS; and polyamides condensed during processing (RIM polyamide systems).

17. Polyureas, polyimides, polyamide-imides and polybenzimidazoles.

18. Polyesters derived from dicarboxylic acids and diols and/or from hydroxycarboxylic acids or the corresponding lactones, for example polyethylene terephthalate, polybutylene terephthalate, poly-1,4-dimethylolcyclohexane terephthalate and polyhydroxybenzoates, as well as block copolyether esters derived from hydroxyl-terminated polyethers; and also polyesters modified with polycarbonates or MBS.

19. Polycarbonates and polyester carbonates.

20. Polysulfones, polyether sulfones and polyether ketones.

21. Crosslinked polymers derived from aldehydes on the one hand and phenols, ureas and melamines on the other hand, such as phenol/formaldehyde resins, urea/formaldehyde resins and melamine/formaldehyde resins.

22. Drying and non-drying alkyd resins.

23. Unsaturated polyester resins derived from copolyesters of saturated and unsaturated dicarboxylic acids with polyhydric alcohols and vinyl compounds as crosslinking agents, and also halogen-containing modifications thereof of low flammability.

24. Crosslinkable acrylic resins derived from substituted acrylates, for example epoxy acrylates, urethane acrylates or polyester acrylates.

25. Alkyd resins, polyester resins and acrylate resins crosslinked with melamine resins, urea resins, polyisocyanates or epoxy resins.

26. Crosslinked epoxy resins derived from polyepoxides, for example from bisglycidyl ethers or from cycloaliphatic diepoxides.

27. Natural polymers such as cellulose, rubber, gelatin and chemically modified homologous derivatives thereof, for example cellulose acetates, cellulose propionates and cellulose butyrates, or the cellulose ethers such as methyl cellulose; as well as rosins and their derivatives.

28. Blends of the aforementioned polymers (polyblends), for example PP/EPDM, Polyamide/EPDM or ABS, PVC/EVA, PVC/ABS, PVC/MBS, PC/ABS, PBTP/ABS, PC/ASA, PC/PBT, PVC/CPE, PVC/acrylates, POM/thermoplastic PUR, PC/thermoplastic PUR, POM/acrylate, POM/MBS, PPO/HIPS, PPO/PA 6.6 and copolymers, PA/HDPE, PA/PP, PA/PPO.

29. Naturally occurring and synthetic organic materials which are pure monomeric compounds or mixes of such compounds, for example mineral oils, animal and vegetable fats, oil and waxes, or oils, fats and waxes based on synthetic esters (e.g. phthalates, adipates, phosphates or trimellitates) and also mixes of synthetic esters with mineral oils in any weight ratios, typically those used as spinning compositions, as well as aqueous emulsions of such materials.

30. Aqueous emulsions of natural or synthetic rubber, e.g. natural latex or latices of carboxylated styrene/butadiene copolymers.

31. Polysiloxanes such as the soft, hydrophilic polysiloxanes described, for example, in U.S. Pat. No. 4,259,467; and the hard polyorganosiloxanes described, for example, in U.S. Pat. No. 4,355,147.

32. Polyketimines in combination with unsaturated acrylic polyacetoacetate resins or with unsaturated acrylic resins. The unsaturated acrylic resins include the urethane acrylates, polyether acrylates, vinyl or acryl copolymers with pendant unsaturated groups and the acrylated melamines. The polyketimines are prepared from polyamines and ketones in the presence of an acid catalyst.

33. Radiation curable compositions containing ethylenically unsaturated monomers or oligomers and a polyunsaturated aliphatic oligomer.

34. Epoxymelamine resins such as light-stable epoxy resins crosslinked by an epoxy functional coetherified high solids melamine resin such as LSE-4103 (Monsanto).

In general, the compounds of the present invention are employed in from about 0.01 to about 5% by weight of the stabilized composition, although this will vary with the particular substrate and application. An advantageous range is from about 0.05 to about 3%, and especially 0.05 to about 1%.

The stabilizers of the instant invention may readily be incorporated into the organic polymers by conventional techniques, at any convenient stage prior to the manufacture of shaped articles therefrom. For example, the stabilizer may be mixed with the polymer in dry powder form, or a suspension or emulsion of the stabilizer may be mixed with a solution, suspension, or emulsion of the polymer. The resulting stabilized polymer compositions of the invention may optionally also contain from about 0.01 to about 5%, preferably from about 0.025 to about 2%, and especially from about 0.1 to about 1% by weight of various conventional additives, such as the materials listed below, or mixtures thereof.

1.1. Alkylated monophenols, for example,

2,6-di-tert-butyl-4-methylphenol

2- tert- butyl-4,6- dimethylphenol

2,6-di-tert-butyl-4-ethylphenol

2,6-di-tert-butyl-4-n-butylphenol

2,6-di-tert-butyl-4-i-butylphenol

2,6-di-cyclopentyl-4-methylphenol

2- (.alpha.-methhylcyclohexyl)-4,6-dimethylphenol

2,6-di-octadecyl-4-methylphenol

2,4,6-tri-cyclohexylphenol

2,6-di-tert-butyl-4-methoxymethylphenol

1.2. Alkylated hydroquinones, for example,

2,6-di-tert-butyl-4-methoxyphenol

2,5-di-tert-butyl-hydroquinone

2,5-di-tert-amyl-hydroquinone

2,6-diphenyl-4-octadecyloxyphenol

1.3. Hydroxylated thiodiphenyl ethers, for example,

2,2'-thio-bis-(6-tert-butyl-4-methylphenol)

2,2'-thio-bis-(4-octylphenol)

4,4'-thio-bis-(6-tert-butyl-3-methylphenol)

4,4'-thio-bis-(6-tert-butyl-2-methylphenol)

1.4. Alkylidene-bisphenols, for example,

2,2'-methylene-bis-(6-tert-butyl-4-methylphenol)

2,2'-methylene-bis-(6-tert-butyl-4-ethylphenol)

2,2'-methylene-bis-[4-methyl-6-(.alpha.-methylcyclohexyl)-phenol]

2,2'-methylene-bis-(4-methyl-6-cyclohexylphenol)

2,2'-methylene-bis-(6-nonyl-4-methylphenol)

2,2'-methylene-bis-[6-(.alpha.-methylbenzyl)-4-nonylphenol]

2,2'-methylene-bis-[6-(.alpha.,.alpha.-dimethylbenzyl)-4-nonylphenol]

2,2'-methylene-bis-(4,6-di-tert-butylphenol)

2,2'-ethylidene-bis-(4,6-di-tert-butylphenol)

2,2'-ethylidene-bis-(6-tert-butyl-4-isobutylphenol)

4,4'-methylene-bis-(2,6-di-tert-butylphenol)

4,4'-methylene-bis-(6-tert-butyl-2-methylphenol)

1,1-bis-(5-tert-butyl-4-hydroxy-2-methylphenyl)-butane

2,6-di-(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4-methylphenol

1,1,3-tris-(5-tert-butyl-4-hydroxy-2-methylphenyl)-butane

1,1-bis-(5-tert-butyl-4-hydroxy-2-methylphenyl)-3-n-dodecylmercaptobutane

ethyleneglycol bis-[3,3-bis-(3'-tert-butyl-4'-hydroxyphenyl)-butyrate]

di-(3-tert-butyl-4-hydroxy-5-methylphenyl)-dicyclopentadiene

di-[2-(3'-tert-butyl-2'-hydroxy-5'-methyl-benzyl)-6-tert-butyl-4-methylphen yl] terephthalate.

1.5. Benzyl compounds, for example,

1,3,5-tri-(3,5-di-tert-butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzene

di-(3,5-di-tert-butyl-4-hydroxybenzyl) sulfide

3,5-di-tert-butyl-4-hydroxybenzyl-mercapto-acetic acid isooctyl ester

bis-(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)dithiol terephthalate

1,3,5-tris-(3,5-di-tert-butyl-4-hydroxybenzyl) isocyanurate

1,3,5-tris-(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl) isocyanurate

3,5-di-tert-butyl-4-hydroxybenzyl-phosphoric acid dioctadecyl ester

3,5-di-tert-butyl-4-hydroxybenzyl-phosphoric acid monoethyl ester, calcium-salt

1.6. Acylaminophenols, for example,

4-hydroxy-lauric acid anilide

4-hydroxy-stearic acid anilide

2,4-bis-octylmercapto-6-(3,5-tert-butyl-4-hydroxyanilino)-s-triazine

octyl-N-(3,5-di-tert-butyl-4-hydroxyphenyl)-carbamate

1.7. Esters of .beta.-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid with monohydric or polyhydric alcohols, for example,

1.8. Esters of .beta.-(5-tert-butyl-4-hydroxy-3-methylphenyl)-propionic acid with monohydride or polyhydric alcohols, for example,

1.9. Amides of .beta.-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid for example,

N,N'-di-(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-hexamethylenediamine

N,N'-di-(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-trimethylenediamine

N,N'-di-(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-hydrazine

1.10 Diarylamines, for example, diphenylamine, N-phenyl-1-naphthylamine, N-(4-tert-octylphenyl)-1-naphthylamine, 4,4'-di-tert-octyl-diphenylamine, reaction product of N-phenylbenzylamine and 2,4,4-trimethylpentane, reaction product of diphenylamine and 2,4,4-trimethylpentene, reaction product of N-phenyl-1-naphthylamine and 2,4,4-trimethylpentene.

2.1.2-(2'-Hydroxyphenyl)-benzotriazoles, for example, the 5'-methyl-, 3',5'-di-tert-butyl-, 5'-tert-butyl-, 5'-(1,1,3,3-tetramethylbutyl)-, 5-chloro-3',5'-di-tert-butyl-, 5-chloro-3'-tert-butyl-5'-methyl-, 3'-sec-butyl-5'-tert-butyl-, 4'-octoxy, 3',5'-di-tert-amyl-, 3',5'-bis-(.alpha.,.alpha.-dimethylbenzyl), 3'-tert-butyl-5'-(2-(omega-hydroxy-octa-(ethyleneoxy)carbonyl-ethyl)-, 3'-dodecyl-5'-methyl-, and 3'-tert-butyl-5'-(2-octyloxycarbonyl)ethyl-, and dodecylated-5'-methyl derivatives.

2.2. 2-Hydroxy-benzophenones, for example, the 4-hydroxy-, 4-methoxy-, 4-octoxy, 4-decyloxy-, 4-dodecyloxy-, 4-benzyloxy, 4,2',4'-trihydroxy- and 2'-hydroxy-4,4'-dimethoxy derivatives.

2.3. Esters of optionally substituted benzoic acids for example, phenyl salicylate, 4-tert-butylphenyl salicylate, octylphenyl salicylate, dibenzoylresorcinol, bis-(4-tert-butylbenzoyl)-resorcinol, benzoylresorcinol, 3,5-di-tert-butyl-4-hydroxybenzoic acid 2,4-di-tert-butylphenyl ester and 3,5-di-tert-butyl-4-hydroxybenzoic acid hexadecyl ester.

2.4. Acrylates, for example, .alpha.-cyano-.beta.,.beta.-diphenylacrylic acid ethyl ester or isooctyl ester, .alpha.-carbomethoxy-cinnamic acid methyl ester, .alpha.-cyano-.beta.-methyl-p-methoxy-cinnamic acid methyl ester or butyl ester, .alpha.-carbomethoxy-p-methoxy-cinnamic acid methyl ester, N-(.beta.-carbomethoxy-.beta.-cyanovinyl)-2-methyl-indoline.

2.5. Nickel compounds, for example, nickel complexes of 2,2'-thio-bis-[4-(1,1,3,3-tetramethylbutyl)-phenol], such as the 1: 1 or 1:2 complex, optionally with additional ligands such as n-butylamine, triethanolamine or N-cyclohexyl-diethanolamine, nickel dibutyldithiocarbamate, nickel salts of 4-hydroxy-3,5-di-tert-butylbenzylphosphonic acid monoalkyl esters, such as of the methyl, ethyl or butyl ester, nickel complexes of ketoximes such as of 2-hydroxy-4-methyl-phenyl undecyl ketoxime, nickel complexes of 1-phenyl-4-1auroyl-5-hydroxy-pyrazole, optionally with additional ligands.

2.6. Sterically hindered mines, for example bis-(2,2,6,6-tetramethylpiperidyl) sebacate, bis-(1,2,2,6,6-pentamethylpiperidyl) sebacate, n-butyl-3,5-di-tert.butyl-4-hydroxybenzyl malonic acid bis-(1,2,2,6,6-pentanemethylpiperidyl)ester, condensation product of 1-hydroxyethyl-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid, condensation product of N,N'-(2,2,6,6-tetramethylpiperidyl)-hexamethylenediamine and 4-tert-octylarnino-2,6-dichloro-s-triazine, tris-(2,2,6,6-tetramethylpiperidyl)-nitrilotriacetate, tetrakis-(2,2,6,6-tetramethyl-4-piperidyl) 1,2,3,4-butanetetracarboxylate, 1,1'(1,2-ethanediyl)-bis-(3,3,5,5-tetramethylpiperazinone), bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate.

2.7. Oxalic acid dimides, for example, 4,4'-di-octyloxy-oxanilide, 2,2'-di-octyloxy-5,5'-di-tert-butyl-oxanilide, 2,2'-di-dodecyloxy-5,5'-di-tert-butyl-oxanilide, 2-ethoxy-2'-ethyl-oxanilide, N,N'-bis (3-dimethylarninopropyl)-oxalamide, 2-ethoxy-5-tert-butyl-2'-ethyloxanilide and its mixture with 2-ethoxy-2'-ethyl-5,4'-di-tert-butyloxanilide and mixtures of ortho- and para-methoxy- as well as of o- and p-ethoxy-disubstituted oxanilides.

2.8. Hydroxyphenyl-s-triazines, for example 2,6-bis-(2,4-dimethylphenyl)-4-(2-hydroxy-4-octyloxyphenyl)-s-triazine; 2,6-bis-(2,4-dimethylphenyl)-4-(2,4-dihydroxyphenyl)-s-triazine; 2,4-bis(2,4-dihydroxyphenyl)-6-(4-chlorophenyl)-s-triazine; 2,4-bis[2-hydroxy-4-(2-hydroxy-4-(2-hydroxyethoxy)phenyl]-6-(4-chloropheny l)-s-triazine; 2,4-bis[2-hydroxy-4-(2-hydroxy-4-(2-hydroxyethoxy)phenyl]-6-(2,4-dimethylp henyl)-s-triazine; 2,4-bis[2-hydroxy-4-(2-hydroxyethoxy)phenyl]-6-(4-bromophenyl)-s-triazine; 2,4-bis[2-hydroxy-4-(2-acetoxyethoxy)phenyl]-6-(4-chloro-phenyl)-s-triazin e, 2,4-bis(2,4-dihydroxyphenyl)-6-(2,4-dimethylphenyl)-s-triazine.

3. Metal deactivators, for example, N,N'-diphenyloxalic acid diamide, N-salicylal-N'-salicyloylhydrazine, N,N'-bis-salicyloylhydrazine, N,N'-bis-(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-hydrazine, 3-salicyloylamino- 1,2,4-triazole, bis-benzylidene-oxalic acid dihydrazide.

4. Phosphites and phosphonites, for example, triphenyl phosphite, diphenylalkyl phosphites, phenyldialkyl phosphites, tri-(nonylphenyl) phosphite, trilauryl phosphite, trioctadecyl phosphite, di-stearyl-pentaerythritol diphosphite, tris-(2,4-di-tert-butylphenyl) phosphite, di-isedecyl-pentaerythritol diphosphite, di-(2,4-di-tert-butylphenyl)pentaerythritol diphosphite, tristearylsorbitol triphosphite, tetrakis-(2,4-di-tert-butylphenyl) 4,4'-diphenylylenediphosphonite.

5. Compounds which destroy peroxide, for example, esters of .beta.-thiodipropionic acid, for example the lauryl, stearyl, myristyl or tridecyl esters, mercapto-benzimidazole or the zinc salt of 2-mercaptobenzimidazole, zinc dibutyl-dithiocarbamate, dioctadecyl disulfide, pentaerythritol tetrakis-(.beta.-dodecylmercapto)-propionate.

6. Hydroxylamines, for example, N,N-dibenzylhydroxylamine, N,N-diethylhydroxylamine, N,N-dioctylhydroxylamine, N,N-dilaurylhydroxylamine, N,N-ditetradecylhydroxylamine, N,N-dihexadecylhydroxylamine, N,N-dioctadecylhydroxylamine, N-hexadecyl-N-octadecylhydroxylamine, N-heptadecyl-N-octadecylhydroxylamine, N,N-dialkylhydroxylamine derived from hydrogenated tallow amine.

7. Nitrones, for example, N-benzyl-alpha-phenyl nitrone, N-ethyl-alpha-methyl nitrone, N-octyl-alpha-heptyl nitrone, N-lauryl-alpha-undecyl nitrone, N-tetradecyl-alpha-tridecyl nitrone, N-hexadecyl-alpha-pentadecyl nitrone, N-octadecyl-alpha-heptadecylnitrone, N-hexadecyl-alpha-heptadecyl nitrone, N-octadecyl-alpha-pentadecyl nitrone, N-heptadecyl-alpha-heptadecyl nitrone, N-octadecyl-alpha-hexadecyl nitrone, nitrone derived from N,N-dialkylhydroxylamine derived from hydrogenated tallow amine.

8. Polyamide stabilizers, for example copper salts in combination with iodides and/or phosphorus compounds and salts of divalent manganese.

9. Basic co-stabilizers, for example, melamine, polyvinylpyrrolidone, dicyandiamide, triallyl cyanurate, urea derivatives, hydrazine derivatives, amines, polyamides, polyurethanes, alkali metal salts and alkaline earth metal salts of higher fatty acids for example Ca stearate, Zn stearate, Mg stearate, Na ricinoleate and K palmitate, antimony pyrocatecholate or zinc pyrocatecholate.

10. Nucleating agents, for example, 4-tert-butyl-benzoic acid, adipic acid, diphenylacetic acid.

11. Fillers and reinforcing agents, for example, calcium carbonate, silicates, glass fibers, asbestos, talc, kaolin, mica, barium sulfate, metal oxides and hydroxides, carbon black, graphite.

12. Other additives, for example, plasticizers, lubricants, emulsifiers, pigments, optical brighteners, flameproofing agents, anti-static agents, blowing agents and thiosynergists such as dilauryl thiodipropionate or distearyl thiodipropionate.

13. Benzofuranones and indolinones, for example those disclosed in US-A-4 325 863, U.S. Pat. No. 4,338,244 or U.S. Pat. No. 5,175,312, or 3-[4-(2-acetoxyethoxy)phenyl]-5,7-di-tert-butyl-benzofuran-2-one, 5,7-di-tert-butyl-3-[4-(2-stearoyloxyethoxy)phenyl]benzofuran-2-one, 3,3'-bis[5,7-di-tert-butyl-3-(4-[2-hydroxyethoxy]phenyl)benzofurran-2-one] , 5,7-di-tert-butyl-3-(4-ethoxyphenyl)-benzofuran-2-one, 3-(4-acetoxy-3,5-dimethylphenyl)-5,7-di-ten-butyl-benzofuran-2-one, 3-(3,5-dimethyl-4-pivaloyloxyphenyl)-5,7-di-tert-butyl-benzofuran-2-one.

The co-stabilizers, with the exception of the benzofuranones listed under 11, are added for example in concentrations of 0.01 to 10%, relative to the total weight of the material to be stabilized.

Further preferred compositions comprise, in addition to components (a) and (b) further additives, in particular phenolic antioxidants, light stabilizers or processing stabilizers.

Particularly preferred additives are phenolic antioxidants (item 1 of the list), sterically hindered amines (item 2.6 of the list), phosphites and phosphonites (item 4 of the list) and peroxide-destroying compounds (item 5.) of the list.

Additional additives (stabilizers) which are also particularly preferred are benzofuran-2-ones, such as described, for example, in U.S. Pat. No. 4,325,863, U.S. Pat. No. 4,338,244 or U.S. Pat. No. 5,175,312.

Examples of such benzofuran-2-ones are compounds of the formula ##STR2## in which

R.sub.11 is phenyl or phenyl which is substituted by 1 to 3 alkyl radicals together having at most 18 carbon atoms, alkoxy having 1 to 12 carbon atoms, alkoxycarbonyl having 2 to 18 carbon atoms or chlorine;

R.sub.12 is hydrogen;

R.sub.14 is hydrogen, alkyl having 1 to 12 carbon atoms, cyclopentyl, cyclohexyl or chlorine;

R.sub.13 has the meaning of R.sub.12 or R.sub.14 or is a radical of the formula ##STR3## in which

R.sub.16 is hydrogen, alkyl having 1 to 18 carbon atoms, alkyl having 2 to 18 carbon atoms which is interrupted by oxygen or sulfur, dialkylaminoalkyl having a total of 3 to 16 carbon atoms, cyclopentyl, cyclohexyl, phenyl or phenyl which is substituted by 1 to 3 alkyl radicals together having at most 18 carbon atoms;

n is 0, 1 or 2;

the substituents R.sub.17, independently of one another, are hydrogen, alkyl having 1 to 18 carbon atoms, cyclopentyl, cyclohexyl, phenyl, phenyl which is substituted by 1 or 2 alkyl radicals together having at most 16 carbon atoms, a radical of the formula --C.sub.2 H.sub.4 OH, --C.sub.2 H.sub.4 --O--C.sub.m H.sub.2m+1 or ##STR4## or together with the nitrogen atom to which they are attached form a piperidine or morpholine radical;

m is 1 to 18;

R.sub.20 is hydrogen, alkyl having 1 to 22 carbon atoms or cycloalkyl having 5 to 12 carbon atoms;

A is alkylene having 2 to 22 carbon atoms which may be interrupted by nitrogen, oxygen or sulfur;

R.sub.18 is hydrogen, alkyl having 1 to 18 carbon atoms, cyclopentyl, cyclohexyl, phenyl, phenyl which is substituted by 1 or 2 alkyl radicals together having at most 16 carbon atoms, or is benzyl;

R.sub.19 is alkyl having 1 to 18 carbon atoms;

D is --O--, --S--, --SO--, --SO.sub.2 -- or --C(R.sub.21).sub.2 --;

the substituents R.sub.21, independently of one another, are hydrogen, C.sub.1 -C.sub.16 alkyl, the two R.sub.21 together containing 1 to 16 carbon atoms, R.sub.21 is furthermore phenyl or a radical of the formula ##STR5## in which n, R.sub.16 and R.sub.17 are as defined above;

E is a radical of the formula ##STR6## in which R.sub.11, R.sub.12 and R.sub.14 are as defined above; and

R.sub.15 is hydrogen, alkyl having 1 to 20 carbon atoms, cyclopentyl, cyclohexyl, chlorine or a radical of the formula ##STR7## in which R.sub.16 and R.sub.17 are as defined above, or R.sub.15 together with R.sub.14 forms a tetramethylene radical.

Preference is given to those benzofuran-2-ones in which R.sub.13 is hydrogen, alkyl having 1 to 12 carbon atoms, cyclopentyl, cyclohexyl, chlorine or a radical of the formula ##STR8## or --D--E, in which n, R.sub.16, R.sub.17, D and E are as defined above, R.sub.16 is in particular hydrogen, alkyl having 1 to 18 carbon atoms, cyclopentyl or cyclohexyl.

Preference is given furthermore to those benzofuran-2-ones in which R.sub.11 is phenyl or phenyl which is substituted by 1 or 2 alkyl radicals together having at most 12 carbon atoms; R.sub.12 is hydrogen; R.sub.14 is hydrogen or alkyl having 1 to 12 carbon atoms; R.sub.13 is hydrogen, alkyl having 1 to 12 carbon atoms, ##STR9## or --D--E; R.sub.15 is hydrogen, alkyl having 1 to 20 carbon atoms, ##STR10## or R.sub.15 together with R.sub.14 forms a tetramethylene radical, n, R.sub.16, R.sub.17, D and E being as defined at the beginning.

Of particular interest are also those benzofuran-2-ones in which R.sub.11 is phenyl; R.sub.13 is hydrogen, alkyl having 1 to 12 carbon atoms or --D--E; R.sub.12 and R.sub.14, independently of one another, are hydrogen or alkyl having 1 to 4 carbon atoms; and R.sub.15 is alkyl having 1 to 20 carbon atoms, D and E being as defined at the beginning.

Of special interest are finally also those benzofuran-2-ones in which R.sub.11 is phenyl; R.sub.13 is alkyl having 1 to 4 carbon atoms or --D--E; R.sub.12 and R.sub.14 are hydrogen; and R.sub.15 is alkyl having 1 to 4 carbon atoms, cyclopentyl or cyclohexyl, D being a group --C(R.sub.21).sub.2 -- and E being a radical of the formula ##STR11## the substituents R.sub.21 being identical to or different from one another and each alkyl having 1 to 4 carbon atoms, and R.sub.11, R.sub.12, R.sub.14 and R.sub.15 being as defined.

The amount of additional additives, in particular stabilizers, for example of benzofuran-2-ones mentioned, can vary within wide limits. For example, 0.0005 to 10, preferably 0.001 to 5, in particular 0.01 to 2, % by weight thereof can be present in the compositions according to the invention.

Incorporation of the beta, triclinic crystalline form of 2,2',2"-nitrilo[triethyl-tris-(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2, 2'-diyl) phosphite] and, if desired, further additives in the polymer organic material is carried out by known methods, for example before or during moulding or by applying the dissolved or dispersed compounds to the polymer organic material, if appropriate with subsequent slow evaporation of the solvent. The beta, triclinic modification according to the invention can also be added to the materials to be stabilized in the form of a masterbatch containing them, for example, in a concentration of 2.5 to 25% by weight.

The beta, triclinic modification according to the invention can also be added before or during polymerization or before crosslinking.

The beta, triclinic modification according to the invention can be incorporated in the material to be stabilized in pure form or encapsulated in waxes, oils or polymers.

The beta, triclinic modification according to the invention can also be sprayed onto the polymer to be stabilized. They are capable of diluting other additives (for example the above-mentioned customary additives) or their melts, thus enabling them to be sprayed onto the polymer to be stabilized also together with these additives. Addition by spraying during deactivation of the polymerization catalysts is particularly advantageous, it being possible, for example, for the steam used for deactivation to be used for spraying.

In the case of bead polymerized polyolefins, it may be advantageous, for example, to apply the beta, triclinic modification according to the invention, if desired together with other additives, by spraying.

The materials thus stabilized can be used in a wide range of forms, for example as films, fibres, tapes, moulding compositions, profiles or as binders for paints, adhesives or cements.

As already mentioned, the organic materials to be protected are preferably organic, in particular synthetic, polymers. Of these, the materials being protected are particularly advantageously thermoplastic materials, in particular polyolefins. The excellent efficiency of the beta, triclinic form of 2,2',2"-nitrilo[triethyl-tris-(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2, 2'-diyl) phosphite as processing stabilizer (thermal stabilizer) should be mentioned in particular. To this end, it is advantageously added to the polymer before or during its processing. It is however also possible to stabilize other polymers (for example elastomers) or lubricants or hydraulic fluids against degradation, for example light-induced or thermal-oxidative degradation. For elastomers, see the above list of possible organic materials.

Suitable lubricants and hydraulic fluids are based, for example, on mineral or synthetic oils or mixtures thereof. Lubricants are known to one skilled in the art and described in the relevant technical literature, for example in Dieter Klamann, "Schmierstoffe und verwandte Produkte" (Verlag Chemic, Weinheim 1982), in Schewe-Kobek, "Das Schmiermittel-Taschenbuch" (Dr. Alfred Huthig-Verlag, Heidelberg, 1974) and in "Ullmanns Enzyklopadie der technischen Chemic" vol. 13, pages 85-94 (Verlag Chemic, Weinheim, 1977).

Accordingly, a preferred embodiment of the present invention is the process of using the beta, triclinic form of 2,2',2"-nitrilo[triethyl-tris-(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2, 2'-diyl) phosphite] for stabilizing organic materials against oxidative, thermal or light-induced degradation.

The beta, triclinie modification according to the invention is preferably used as processing stabilizer (thermal stabilizer) of thermoplastic polymers.

The present invention also provides a process for stabilizing an organic material against oxidative, thermal or light-induced degradation, which comprises incorporating therein or applying thereto the beta, triclinic form of 2,2',2"-nitrilo[triethyl-tris-(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2, 2'-diyl) phosphite].

The phenolic antioxidant of particular interest is selected from the group consisting of n-octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate, neopentanetetrayl tetralds(3,5-di-tert-butyl-4-hydroxyhydrocinammate), di-n-octadecyl 3,5-di-tert-butyl-4-hydroxybenzylphosphonate, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)isocyanurate, thiodiethylene bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), 1,3,5-trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)-benzene, 3,6-dioxaoctamethylene bis(3-methyl-5-tert-butyl-4-hydroxyhydrocinnamate), 2,6-di-tert-butyl-p-cresol, 2,2'-ethylidene-bis(4,6-di-tert-butylphenol), 1,3,5-tris(2,6-dimethyl-4-tert-butyl-3-hydroxybenzyl)isocynurate, 1,1,3,-tris(2-methyl-4-hydroxy-5-tert-butylphenyl)butane, 1,3,5-tris[2-(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyloxy)ethyl]isocyanur ate, 3,5-di-(3,5-di-tert-butyl-4-hydroxybenzyl)mesitol, hexamethylene bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), 1-(3,5-di-tert-butyl-4-hydroxyanilino)-3,5-di(octylthio)-s-triazine, N,N'-hexamethylene-bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamamide), calcium bis(ethyl 3,5-di-tert-butyl-4-hydroxybenzylphosphonate), ethylene bis[3,3-di(3-tert-butyl-4-hydroxyphenyl)butyrate], octyl 3,5-di-tert-butyl-4-hydroxybenzylmercaptoacetate, bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyl)hydrazide, and N,N'-bis[2-(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyloxy)-ethyl]-oxamide.

A most preferred phenolic antioxidant is neopentanetetrayl tetrakis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), n-octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate, 1,3,5-trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)benzene, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)isocyanurate, 2,6-di-tert-butyl-p-cresol or 2,2'-ethylidene-bis(4,6-di-tertbutylphenol).

The hindered amine compound of particular interest is selected from the group consisting of bis(2,2,6,6-tetramethylpiperidin-4-yl) sebacate, bis(1,2,2,6,6-pentarnethylpiperidin-4-yl) sebacate, di(1,2,2,6,(>-pentamethylpiperidin-4-yl) (3,5-di-tert-butyl-4-hydroxybenzyl)butylmalonate, 4-benzoyl-2,2,6,6-tetramethylpiperidine, 4-stearyloxy-2,2,6,6-tetramethylpiperidine, 3-n-octyl-7,7,9,9-tetramethyl- 1,3,8-triaza-spiro[4.5]decane-2,4-dione, tris(2,2,6,6-tetramethylpipericlin-4-yl) nitrilotriacetate, 1,2-bis(2,2,6,6-tetramethyl-3-oxopiperazin-4-yl)ethane, 2,2,4,4-tetramethyl-7-oxa-3,20-diaza-21-oxodispiro[5.1.11.2] heneicosane, polycondensation product of 2,4-dichloro-6-tert-octylamino-s-triazine and 4,4'-hexamethylenebis(amino-2,2,6,6-tetramethylpiperidine), polycondensation product of 1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid, polycondensation product of 4,4'-hexamethylenebis-(amino-2,2,6,6-tetramethylpiperidine) and 1,2-dibromoethane, tetrakis(2,2,6,6-tetramethylpiperidin-4-yl) 1,2,3,4-butanetetracarboxylate, tetrakis(1,2,2,6,6-pentamethylpiperidin-4-yl) 1,2,3,4-butanetetracarboxylate, polycondensation product of 2,4-dichloro-6-morpholino-s-triazine and 4,4'-hexamethylenebis(amino-2,2,6,6-tetramethylpiperidine), N,N',N",N'"-tetrakis[(4,6-bis(butyl-2,2,6,6-tetramethyl-piperidin-4-yl)-am ino-s-triazin-2-yl]-1,10-diamino-4,7-diazadecane, mixed [2,2,6,6-tetramethylpiperidin-4-yl/.beta.,.beta.,.beta.',.beta.'-tetrameth yl-3,9-(2,4,8, 10-tetraoxaspiro[5.5]-undecane) diethyl] 1,2,3,4-butanetetracarboxylate, mixed [1,2,2,6,6-pentamethylpiperidin-4-yl/.beta.,.beta.,.beta.',.beta.'-tetrame thyl- 3,9- (2,4,8,10-tetraoxaspiro[5.5]-undecan)diethyl] 1,2,3,4-butanetetracarboxylate, octamethylene bis(2,2,6,6-tetramethylpiperidin-4-carboxylate), 4,4'-ethylenebis(2,2,6,6-tetramethylpiperazin-3-one), and bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate.

A most preferred hindered amine compound is bis(2,2,6,6-tetramethylpiperidin-4-yl) sebacate, the polycondensation product of 1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperdine and succinic acid, the polycondensation product of 2,4-dichloro-6-tert-octylamino-s-triazine and 4,4'-hexamethylenebis(amino-2,2,6,6-tetramethylpiperidine), N,N',N",N'"-tetrakis[(4,6-bis(butyl-(2,2,6,6-tetramethyl-piperidin-4-yl)am ine)-s-triazine-2-yl]-1,10-diamino-4,7-diazadecane or bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate.

The lubricating oil may be a mineral oil, a synthetic oil or any mixture of such oils. Mineral oils are preferred and examples of these include paraffinic hydrocarbon oils e.g. a mineral oil having a viscosity of 46 mm.sup.2 /s at 40.degree. C.; "150 Solvent Neutral" a solvent refined neutral mineral oil having a viscosity of 32 mm.sup.2 /s at 40.degree. C.; and "solvent bright-stocks", a high boiling residue from the process of refining mineral oil, and having a viscosity of 46 mm.sup.2 /s at 40.degree. C.

Synthetic lubricating oils which may be present may be synthetic hydrocarbons such as polybutenes, alkyl benzenes and poly-alpha olefins as well as simple di-, tri- and tetra-esters, complex esters and polyesters derived from carboxylic acid esters of formula: G.sub.1 -OCC-alkylene-COOG.sub.2 wherein "alkylene" denotes an alkylene residue having from 2 to 14 carbon atoms and G.sub.1 and G.sub.2 are the same or different and each is an alkyl group having from 6 to 18 carbon atoms. Tri-esters which are of use as lubricating oil base stocks are those derived from trimethylolpropane and C.sub.6 -C.sub.18 mono-carboxylic acids or mixtures thereof, whereas suitable ten-esters include those derived from pentaerythritol and a C.sub.6 -C.sub.18 mono-carboxylic acid or mixtures thereof.

Complex esters suitable for use as components of the composition of the present invention are those derived from monobasic acids, dibasic acids and polyhydric alcohols, for instance the complex ester derived from trimethylol propane, caprylic acid and sebacic acid.

Suitable polyesters are those derived from any aliphatic dicarboxylic acid having from 4 to 14 carbon atoms and at least one aliphatic dihydric alcohol having from 3 to 12 carbon atoms, e.g. those derived from azelaic acid or sebacic acid and 2,2,4-trimethylhexane-1,6-diol.

Other lubricating oils are those known to the art-skilled and described e.g. in Schewe-Kobek, "Schrniermittel-Taschenbuch", (Huethig Verlag, Heidelberg 1974), and in D. Klamann, "Schmierstoff und verwandte Produkte", (Verlag Chemic, Weinheim 1982).

The lubricating oils applicational media can also contain other additives which may be added to improve the basic properties of lubricants e.g. metal passivators, viscosity-index improvers, pour-point depressants, dispersing agents, detergents, additional rust inhibitors, extreme pressure additives, anti-wear additives and antioxidants.

1. Alkylated Monophenols

2,6-Di-tert-butyl-4-methylphenol, 2,6-di-tert-butylphenol, 2-tert-butyl-4,6-dimethylphenol,2,6-di-tert-butyl-4-ethyl-phenol, 2,6-di-tert-butyl-4-n-butylphenol, 2,6-di-tert-butyl-4-i-butylphenol, 2,6-di-cyclopentyl-4-methylphenol, 2-(.beta.-methylcyclohexyl)-4,6-dimethylphenol, 2,6-di-octa-decyl-4-methylphenol, 2,4,6-tri-cyclohexylphenol, 2,6-di-tert-butyl-4-methoxymethylphenol, o-tert-butylphenol.

2. Alkylated Hydroquinones

2,6-Di-tert-butyl-4-methoxyphenol, 2,5-di-tert-butyl-hydroquinone, 2,5-di-tert-amyl-hydroquinone, 2,6-diphenyl-4-octa-decyloxyphenol.

3. Hydroxylated Thiodiphenylethers

2,2'-Thio-bis-(6-tert-butyl-4-methylphenol), 2,2'-thio-bis-(4-octyl-phenyl), 4,4'-thio-bis-(6-tert-butyl-3-methylphenol ), 4,4'-thio-bis-(6-tert-butyl-2-methylphenol).

4. AlkyIidene-Bisphenols

2,2'-Methylene-bis-(6-tert-butyl-4-methylphenol), 2,2'-methylene-bis-(6-tert-butyl-4-ethylphenol), 2,2 '-methylene-bis-(4-methyl-6-(.alpha.-methyl-cyclohexyl)-phenol), 2,2'-methylene-bis-(4-methyl-6-cyclohexylphenol), 2,2'-methylene-bis-(6-nonyl-4-methylphenol), 2,2'-methylene-bis-(4,6-di-tert-butylphenol), 2,2'-ethylidene-bis-(4,6-di-tert-butylphenol), 2,2'-ethylidene-bis-(6-tert-butyl-4- or -5-isobutylphenol), 2,2'-methylene-bis-(6-(.alpha.-methylbenzyl-4-nonylphenol), 2,2'-methylene-bis-(6-(.alpha.,.alpha.-di-methylbenzyl)-4-nonylphenol), 4,4'-methylene-bis-(2,6-di-tert-butyl-phenol), 4,4'-methylene-bis-(6-tert-butyl-2-methylphenol), 1,1-bis-(5-tert-butyl-4-hydroxy-2methyl-phenol)-butane, 2,6-di-(3-tert-butyl-5-methyl-2-hydroxy-benzyl)-4-methyl-phenol, 1,1,3-tris-(5-tert-butyl-4-hydroxy-2-methylphenyl)-3-n-dodecyl)-mercaptobu tane, ethyleneglycol-bis-[3,3-bis-(3'-tert-butyl-4'-hydroxyphenyl)-butyrate], bis-(3-tert-butyl-4hydroxy-5-methylphenyl)-dicyclopentadiene, bis-[2-(3'-tert-butyl-2'-hydroxy-5'-methyl-benzyl)-6-tert-butyl-4-methyl-p henyl]-terephthalate.

5. Benzyl Compounds

1,3,5-Tri-(3,5-di-tert-butyl-4-hydroxybenzyl)-2,4,6-trimethyl-benzene, bis(3,5-di-tert-butyl-4-hydroxybenzyl)-sulfide, 3,5-di-tert-butyl-4-hydroxybenzyl-mercaptoacetic acid-isooctylester, bis-(4-tert-butyl-3-hydroxy-2,6-dimethyl-benzyl)dithiolterephthalate, 1,3,5-tris-(3,5-di-tert-butyl-4-hydroxybenzyl)-isocyanurate, 1,3,5-tris-(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)-isocyanurate, 3,5-di-tert-butyl-4-hydroxybenzyl-phosphonic acid-dioctadecylester, 3,5-di-tert-butyl-4-hydroxybenzyl-phosphonic acid-monoethylester, calcium-salt.

6. Acylaminophenols

4-Hydroxy-lauric acid anilide, 4-hydroxy-stearic acid anilide, 2,4-bis-octyl-mercapto-6- (3,5-di-tert-butyl-4-hydroxyanilino)-s-triazine, N-(3,5-di-tert-butyl-4-hydroxyphenyl)-carbamic acid octyl ester.

7. Esters of [5-(3,5-Di-tert-butyl-4-hydroxypheny1)-propionic acid with mono- or polyhydric alcohols, for example with methanol, isooctyl alcohol, 2-ethylhexanol, diethylene glycol, octadecanol, triethylene glycol, 1,6-hexanediol, pentaerythritol, neopentyl glycol, tris-hydroxyethyl isocyanurate, thiodiethylene glycol, bis-hydroxyethyl-oxalic acid diamide.

8. Esters of .beta.-(5-tert-butyl-4-hydroxy-3-methylphenyl)-propionic acid with mono- or polyhydric alcohols, for example with methanol, isooctyl alcohol, 2-ethylhexanol, diethylene glycol, octadecanol, triethylene glycol, 1,6-hexanediol, pentaerythritol, neopentyl glycol, tris-hydroxyethyl isocyanurate,thiodiethylene glycol, di-hydroxyethyl-oxalic acid diamide.

9. Amides of .beta.-(3,5-Di-tert-butyl-4-hydroxyphenyl)-propionic acid for example N,N'-Bis-(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-hexamethylene-diamin e, N,N'-bis-(3,5-di-tert-butyl-4-hydroxy-phenylpropionyl)-trimethylene-diamin e, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-hydrazine.

N,N'-Di-isopropyl-p-phenylenediamine, N,N'-di-sec.-butyl-p-phenylenediamine, N,N'-bis(1,4-dimethyl-pentyl)-p-phe nylenediamine, N,N'-bis(1 -ethyl-3-methyl-pentyl)-p-phenylenediamine, N,N'-bis(1-methyl-heptyl)-p-phenylenediamine, N,N'-dicyclohexyl-p-phenylenediamine, N,N'-diphenyl-p-phenylenediamine, N,N'-di-(naphthyl-2-)-p-phenylenediamine, N-isopropyl-N'-phenyl-p-phenylenediamine, N-(1,3-dimethylbutyl)-N'-phenyl-p-phenylenediamine, N-(1-methyl-heptyl)-N'-phenyl-p-phenylene-diamine, N-cyclohexyl-N'-phenyl-p-phenylenediamine, 4-(p-toluene-sulfonamido)-diphenylamine, N,N'-dimethyl-N,N'-di-sec-butyl-p-phenylenediamine, di-phenylamine, N-allyldiphenylamine, 4-isopropoxy-diphenylamine, N-phenyl-1-naphthylamine, N-phenyl-2-naphthylamine, octylated diphenylamine, e.g. p,p'-di-tert-octyldiphenylamine, 4-n-butylaminophenol, 4-butyrylamino-phenol, 4-nonanoylamino-phenol, 4-dodecanoyl-amino-phenol, 4-octadecanoyl-amino-phenol, di-(4-methoxy-phenyl)-amine, 2,6-di-tert-butyl-4-dimethyl-amino-methyl-phenol, 2,4'-diamino-diphenylmethane, 4,4'-diamino-diphenyl-methane, N,N,N',N'-tetramethyl-4,4'-diamino-diphenylmethane, 1,2-di-(phenyl-amino)-ethane, 1,2-di-[2-methyl-phenyl)-amino]-ethane, 1,3-di-(phenylamino)-propane, (o-tolyl)-biguanide, di-[4-1',3'-dimethyl-butyl)-phenyl]amine, tert-octylated N-phenyl-1-naphthylamine, mixture of mono- and dialkylated tert-butyl-/tert-octyldiphenylamines, 2,3-dihydro-3,3-dimethyl-4H-1,4-benzothiazine, phenothiazine, N-allylphenothiazine, tert-octylated phenothiazine, 3,7-di-tert-octylphenothiazine.

Aliphatic or aromatic phosphates, esters of thiodipropionic acid or of thiodiacetic acid, or salts of dithiocarbamic or dithiophosphoric acid.

Examples of metal passivators, for example for copper, are:

Triazoles, benzotriazoles and derivatives thereof, tolutriazole and derivatives thereof, e.g. di(2-ethylhexyl)-arninomethyltolutriazole, 2-mercaptobenzothiazole, 5,5'-methylene-bis-benzotriazole, 4,5,6,7-tetrahydrobenzo-triazole, salicyclidene-propylene-diamine and salicyclamino-guanidine and salts thereof, 1,2,4-triazole and N,N'-disubstituted aminomethyl triazoles of formula ##STR12## in which R.sub.8 and R.sub.9 are, independently, e.g. alkyl, alkenyl, or hydroxyethyl, obtained by reacting 1,2,4-triazole with formaldehyde and an amine, HNR.sub.8 R.sub.9, as disclosed in European Patent Application No. 160620; and the Mannich reaction products derived from benzotriazole or tolutriazole, formaldehyde and an amine HNR.sub.8 R.sub.9.

a) Organic acids, their esters, metal salts and anhydrides, e.g. N-oleoyl-sarcosine, sorbitan-mono-oleate, lead-naphthenate, alkenyl-succinic acids and -anhydrides, e.g. dodecenyl-succinic acid anhydride, succinic acid partial esters and amines, 4-nonyl-phenoxy-acetic acid.

b) Nitrogen-containing compounds, e.g.

I. Primary, secondary or tertiary aliphatic or cycloaliphatic amines and amine-salts of organic and inorganic acids, e.g. oil-soluble alkyl-ammonium carboxylates

II. Heterocyclic compounds, e.g. substituted imidazolines and oxazolines.

c) Phosphorus-containing compounds, e.g. amine salts of phosphonic acid or phosphoric acid partial esters, zinc dialkyldithio phosphates.

d) Sulfur-containing compounds, e.g. barium-dinonylnaphthalene-n-sulfonates, calcium petroleum sulfonates.

e) Derivatives of gamma-alkoxypropylamines described in Japanese Patent Publication No. 15783/1973; and

f) Salts having the formula Y--NH.sub.3 --R.sub.10 CO.sub.2 -- in which Y is a group R.sub.11 X.sub.1 CH.sub.2 CH(OH)CH.sub.2 in which R.sub.10 and R.sub.11, independently, are e.g. alkyl and X.sub.1 is O, CO.sub.2, NH, N(alkyl), N(alkenyl) or S, these salts being prepared by mixing an amine Y--NH.sub.2 with an acid R.sub.10 CO.sub.2 H, as disclosed in DE-OS 3437 876 (German Offenlegungsschrift).

g) Compounds having the formula

in which X.sub.2 is --O--, --S--, --SO.sub.2 --C(O)--O-- or --N(Rd) in which R.sub.12 is H or C.sub.1 -C.sub.12 alkyl, R.sub.13 is unsubstituted C.sub.1 -C.sub.4 alkyl or C.sub.2 -C.sub.5 alkyl substituted by one to three hydroxyl groups, R.sub.14 is hydrogen, unsubstituted C.sub.1 -C.sub.4 alkyl or C.sub.2 -C.sub.5 alkyl substituted by one to three hydroxyl groups provided that at least one of R.sub.13 and R.sub.14 is hydroxy-substituted, and R.sub.12 is C.sub.2 -C.sub.20 alkyl --CH.sub.2 --CH(OH)--CH.sub.2 NR.sub.13 R.sub.14 or R.sub.12 is C.sub.2 -C.sub.18 alkenyl, C.sub.2 -C.sub.3 alkynyl or C.sub.5 -C.sub.12 cycloallcyl provided that, when X.sub.2 is --O-- or --C(O)--O--, R.sub.12 is branched C.sub.4 -C.sub.20 alkyl. These compounds are described in GB Patent Specification 2172284A.

h) Compounds having the formula: ##STR13## in which R.sub.15, R.sub.16, R.sub.17 are, independently, hydrogen, C.sub.1 -C.sub.15 alkyl, C.sub.5 -C.sub.12 cycloalkyl, C.sub.6 -C.sub.15 aryl or C.sub.7 -C.sub.12 aralkyl and R.sub.18 and R.sub.19, independently, are hydrogen, 2-hydroxyethyl or 2-hydroxypropyl, provided that R.sub.18 and R.sub.19 are not simultaneously hydrogen and, when R.sub.18 and R.sub.19 are each --CH.sub.2 CH.sub.2 OH, R.sub.15 and R.sub.16 are not simultaneously hydrogen and R.sub.17 is not pentyl. These compounds are described in EP Patent specification 0 252 007.

Examples of viscosity-index improvers are:

Polyacrylates, polymethacrylates, vinylpyrrolidone/methacrylate-copolymers, polyvinylpyrrolidones, polybutanes, olefin-copolymers, styrene/-acrylate-copolymers, polyethers.

Examples of pour-point depressants are:

Polymethacrylates, alkylated naphthalene derivatives.

Examples of dispersants/detergents are:

Polybutenylsuccinic acid-amides or -imides, polybutenyl-phosphonic acid derivatives, basic magnesium-, calcium-, and baxiumsulfonates and -phenolates.

Examples of anti-wear additives and extreme pressure additives are:

Sulphur- and/or phosphorus- and/or halogen-containing compounds e.g. sulphurised vegetable oils, zinc dialkyldithiophosphates, tritolylphosphate, chlorinated paraffins, alkyl- and aryldi- and trisulphides, triphenylphosphorothionate.

One process for the preparation of the instant beta crystalline modification comprises heating a melt of the compound of formula I at a temperature in the range of 170 to 200.degree. C until the novel beta crystalline modification forms or optionally seed the melt with the novel beta crystalline form in order to increase the rate and efficiency of the melt crystallization. The melt crystallization is optionally carried out under reduced pressure of from 400 mm Hg to 0. 1 mm Hg. The melt crystallization can also be carried out in an extruder or kneader as described in U.S. Pat. No. 4,683,326, the relevant parts of which are herein incorporated by reference.

An alternative process for the preparation of the beta crystalline modification of the compound of formula I is crystallizing or recrystallizing the compound of formula I from a mixture of an aromatic hydrocarbon solvent and an alcohol of 4 to 8 carbon atoms; from a mixture of an aliphatic ketone and an alcohol of 1 to 8 carbon atoms; or from a mixture of an aromatic hydrocarbon solvent and an aliphatic ketone.

Examples of aromatic hydrocarbon solvents useful in the instant process are benzene. toluene, o-xylene, m-xylene, p-xylene, 1,2,3-trimethylbenzene, 1,3,5-wimethylbenzene, 1,2,4-trimethylbenzene, 1,2,4,5-tetramethylbenzene, ethylbenzene, cumene, o-cymene, m-cymene, p-cymene, o-diisopropylbenzene, m-diisopropylbenzene, p-diisopropylbenzene, and mixtures of such aromatic hydrocarbon solvents.

Examples of alcohols useful in the instant process are methanol, ethanol, 1-propanol, isopropanol, 1-butanol, 2-butanol, tert-butyl alcohol, isobutanol, arnyl alcohol, 1-hexanol, 2-ethylhexanol, 1-octanol and mixtures of such alkanols.

Examples of aliphatic ketones are acetone, 2-butanone, 2-pentanone, 3-pentanone, 2-heptanone and the like.

A preferred process for preparing the novel beta, triclinic crystalline modification is by crystallizing or recrystallizing the compound of formula I from a mixture of benzene, toluene, o-xylene, m-xylene, p-xylene, 1,2,3-trimethylbenzene, 1,3,5-trimethylbenzene, 1,2,4-trimethylbenzene, 1,2,4,5-tetramethylbenzene, ethylbenzene, cumene, o-cymene, m-cymene, p-cymene, o-diisopropylbenzene, m-diisopropylbenzene or p-diisopropylbenzene and 1-butanol, 2-butanol, tert-butyl alcohol, isobutanol, amyl alcohol, 1-hexanol, 2-ethylhexanol or 1-octanol; from a mixture of acetone, 2-butanone, 2-pentanone, 3-pentanone or 2-heptanone and methanol, ethanol, 1-propanol, isopropanol, 1-butanol, 2-butanol, tert-butyl alcohol, isobutanol, amyl alcohol, 1-hexanol, 2-ethylhexanol or 1-octanol; or from a mixture of benzene, toluene, o-xylene, m-xylene, p-xylene, 1,2,3-trimethylbenzene, 1,3,5-trimethylbenzene, 1,2,4-trimethylbenzene, 1,2,4,5-tetramethylbenzene, ethylbenzene, cumene, o-cymene, m-cymene, p-cymene, o-diisopropylbenzene, m-diisopropylbenzene or p-diisopropylbenzene and acetone, 2-butanone, 2-pentanone, 3-pentanone or 2 heptanone.

A preferred process for preparing the novel beta, triclinic crystalline modification is also by crystallizing or recrystallizing the compound of formula I from a mixture of benzene, toluene, o-xylene, m-xylene or p-xylene and 1-butanol, 2-butanol or isobutanol; from a mixture of acetone or 2-butanone and isopropanol, 1-butanol or 2-butanol; or from a mixture of benzene, toluene, o-xylene, m-xylene or p-xylene and acetone or 2-butanone.

An especially preferred process for preparing the novel beta crystalline modification is by crystallizing or recrystallizing the compound of formula I from a mixture of toluene and 1-butanol; from a mixture of 2-butanone and 1-butanol; or from a mixture of toluene and acetone.

The present invention also provides a process for stabilizing an organic material against oxidative, thermal or light-induced degradation, which comprises incorporating therein or applying thereto the beta, triclinic crystalline form of 2,2',2"-nitrilo[triethyl-tris-(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2, 2'-diyl) phosphite].

Differential scanning calorimetry (DSC) measurements are obtained on a TA Instrument Inc., 910 differential scanning calorimeter, with a 100 mL/min nitrogen purge, aligned aluminum pan, temperature scan at 5.degree. C./rain to 230.degree. C.

X-ray diffraction patterns are recorded on a Philips Norelco X-ray Diffractometer unit, using Cu-K.alpha. radiation with a nickel filter.

The compound of formula I, 2,2',2"-nitrilo[triethyl-tris-(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2, 2'-diyl) phosphite], is prepared according to procedure of Example 4 of U.S. Pat. No. 4,318,845. The product obtained is heated at 180.degree.-185.degree. C. in vacuo (0.1 mm Hg) to obtain a melt. The melt is heated until a crystalline mass forms, approximately 16 hours. The crystalline mass is then ground into a white powder using a mortar and pestle. A 93% yield of the novel beta crystalline modification of the compound of formula I is obtained: m.p.=206.degree. C (the melting point is determined by differential scanning calorimetry and the peak temperature in the endotherm is recorded as the melting point).

An X-ray diffraction pattern obtained using Cu-K.alpha. exhibits diffraction angles (20) of very high intensity at 8.4 and 17; lines of high intensity at 9.9, 10.6, 11.4, 17.5, 19.1, 20.2; lines of medium intensity at4.6, 4.9,7.1, 12.7, 13.2, 13.6, 15.3, 15.8, 16.4, 16.7, 18.4, 19.7, 21.7, 23.4; and lines of weak intensity at 7.8, 8.8, 9.4, 12, 14.1, 14.6, 21, 22.3, 22.8, 23.9, 24.7, 25.3, 25.5, 26.4, 27.27.7, 28.4.

Analysis:

Calcd for C.sub.90 H.sub.132 NO.sub.9 P.sub.3 : C, 73.8; H, 9.1; N, 0.96. Found: C, 73.5; H, 9.4; N, 0.9.

The compound of formula I is prepared according to the procedure of Example 4 of U.S. Pat. No. 4,318,845. The compound is recrystallized from the following solvent systems to obtain the novel beta crystalline modification of the instant invention.

Suitable crystals for X-ray analysis are grown from acetone/toluene (3.6/1, wt/wt). Intensity data are measured on a NONIUS CAD4 automatic diffractometer as described in Table 1. The structure is solved by direct methods using SHELXS. Full-matrix least-squares refinements are carried out to a final R value of 0.083. The relative configuration is determined to be R*,R*,S*.

The compound of formula I, prepared according to the procedure of Example 4 of U.S. Pat. No. 4,318,845 and not recrystallized according to the procedures of this invention, is heated at 210.degree. C. until a clear melt is obtained. The melt is cooled rapidly to ambient temperature to yield a glassy solid with a T.sub.g (DSC) of 105.degree.-110.degree. C. The X-ray diffraction pattern of this product obtained using Cu-K.alpha. is featureless.

Analysis: Calcd for C.sub.90 H.sub.132 NO.sub.9 P.sub.3 : C, 73.8; H, 9.1; N, 0.96. Found: C, 73.4; H, 9.3; N, 0.9.

This example illustrates the much greater resistance to hydrolysis of the beta crystalline modification of the compound of formula I as prepared in Example 1 as compared to the lesser resistance of the amorphous form of the compound of formula I as prepared in Example 3 and of the compound of Example 4 of U.S. Pat. No. 4,318,845.

The test compounds are exposed to 80% relative humidity at 50.degree. C. and their rate of hydrolysis is monitored by liquid chromatography. The results below are stated in the percent product remaining after 1000 hours of exposure under the conditions stated above.

This example illustrates the superior packaging properties of the novel beta crystalline modification of the compound of formula I, Example 1, over that of the powder form of Example 4 in U.S. Pat. No. 4,318,845.

The apparatus bulk density of the solids is measured according to the method of ASTM D-1895 (79). A higher apparent bulk density allows for a greater mass per unit volume which affords advantages in packaging of the solid product, such as lower costs for the packaging material, less storage space is required, etc.

The blank formation comprises unstabilized polypropylene (PROFAX 6501, Himont) containing 0.075% by weight of calcium stearate. The test additives are incorporated into the polypropylene by dry blending or, when the additive is a liquid, using a minimum amount of methylene chloride solvent. The solvent is then removed by evaporation under reduced pressure. The stabilized resin formulation is extruded by 90 rpm from a 1 inch (2.54 cm) diameter extruder at 525.degree. F. (274.degree. C.) with a residence time of 90 seconds.

After each of the first, third and fifth extrusions, the melt flow rate (in grams/10 minutes) is determined by ASTM method D1238 on the pellets obtained from the extruder. The results are given in the table below:

The instant beta, triclinic crystalline compound is particularly effective in stabilizing polypropylene against thermal and oxidative degradation as shown by a minimum change in the melt flow rate in the presence of a representative phenolic antioxidant and is equal or more effective that the prior art compound of U.S. Pat. No. 4,318,845.

Pellets obtained after the first, third and fifth extrusions are compression molded into 125 mil (3.2 mm) plaques at 450.degree. C. (232.degree. C.) and the yellowness index (YI) values are determined according to ASTM Method D1925. Lower YI values indicate less discoloration. The results are given in the table blow:

The instant beta, triclinic crystalline compound is particularly effective in stabilizing polypropylene against discoloration as shown by a minimum change in the yellowness index in the presence of a representative phenolic antioxidant and is equal or more effective that the prior art compound of U.S. Pat. No. 4,318,845.

The procedure for the X-ray analysis performed here is the same as provided in instant Example 1.

The x-ray analyses of the two compounds listed below are carried out to show that the beta, triclinic crystalline form is distinctly different from the prior art compound of U.S. Pat. No. 4,318,845.

Compound A=beta, triclinic crystalline form of 2,2',2"-nitrilo[triethyl-tris-(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2, 2'-diyl) phosphite], prepared in accordance with instant Example 2.

Compound B=Spivack form of 2.2',2"-nitrilo[triethyl-tris-(3,3', 5,5'-tetra-tert-butyl-1,1'-biphenyl-2,2'diyl) phosphite], prepared in accordance with Example 4 of U.S. Pat. No. 4,318,845.

These data show that the instant beta crystalline form and the prior art crystalline form of Spivack et al. are entirely different in unit cell dimensions, unit cell volume, density and crystal system. Said compounds also differ greatly in melting point and are clearly not the same.

The unit cell of Compound B contains an entrapped molecule of toluene. This was not recognized by Spivack et al., and the Spivack reference fails to mention this. In contrast, the crystall cell of Compound A does not contain a molecule of solvent from any of the claimed recrystallization solvent systems.

The above fact is clearly reflected in the large difference in melting points between the beta crystalline form (compound A) and the prior art material (compound B). Additionally, this fact is seen in comparing the difference between the cell dimensions, volume and density. In particular, a significant difference can be seen by comparing the volumes of the beta crystalline form (4542 .ANG..sup.3) and the prior art material (9966 .ANG..sup.3).

The instant compound of Example 1 is evaluated in an emulsion of SBR (cold polymerized, 23.5 % styrene with a 52 Mooney Viscosity). The unstabilized SBR (60 g) is added to the mixing chamber of a Brabender Plasticorder set at 150.degree. C. and 60 rpm. After 30 seconds, 0.5 % by weight of the compound of instant Example 1 is added to the chamber. Stability of the SBR is determined by the time until onset of crosslinking of the rubber as indicated by an increase in the torque curve. The sample stabilized by the instant compound has a longer induction time fill crosslinking occurs than does the unstabilizer SBR.

A premix of 10 g of water, 0.25 g of triethylenetetramine, 2 g of L-5740 (silicone surfactant, Union Carbide) and 20 g of ANTIBLAZE.RTM. AB-100 (chlorinated aromatic flame retardant, Albright & Wilson) is added to 200 g of 3000 molecular weight polyether polyol containing the stabilizer package listed below*. The mixture is stirred for five minutes with a high speed Lightning Mixer. Then 0.4 g of stannous octoate is added and the mixture is stirred for 5 seconds. Finally, 125 g of toluene diisocyanate (80% 2,6-isomer, 20% 2,4-isomer) is added. The mixture is stirred for 7 seconds at high speed mixing and is then poured into a 10".times.10".times.5" (25.4 cm.times.25.4 cm.times.12.7 cm) cardboard box. The foam is allowed to rise completely. After standing 5 minutes, the box is removed and the sample cured in a microwave over for five minutes at 50% power. The foam is then immediately air over cured at 125.degree. C. for three minutes. The foams are then cut in half for visual assessment of discoloration or scorch.

Control is 2,6-di-tert-butyl-4-methylphenol (BHT) 2000 ppm; and NAUGARD.RTM. 445 (diphenylamine antioxidant, Uniroyal) 2000 ppm.

Instant package is the above plus 1000 ppm of the compound of Example 1.

Visual inspection of the two foams shows that the foam containing the instant stabilizer package with the compound of Example 1 present is less discolored than the foam stabilized with the control stabilizer package. The instant compound demonstrates better scorch protection.

Additive free bisphenol A polycarbonate (LEXAN.RTM. 141-111N, General Electric) is dried and blended with 0.3 weight percent of a benzotriazole UV absorber (TINUVIN.RTM. 329, Ciba-Geigy) and 0.08 weight percent of instant compound of Example 1. The mixture is extruded and pelletized at 550.degree. F. (288.degree. C.) on a 1" (2.54 cm) single screw extruder. Injection molded plaques (2".times.2".times.125 mil; 5.08 cm.times.5.08 cm.times.3.175 mm) are prepared in a BOY 30M injection molder at 560.degree. F. (293.degree. C.) with a mold temperature of 150.degree. C. The resulting plaques are measured for yellowness index (YI) using ASTM D 1925-70. The plaques containing the instant compound of Example 1 have a lower YI values than those containing the UV absorber alone demonstrating the better performance achieve by the concomitant presence of the instant phosphite.

Poly(ethylene terephthalate), PET (KODAPAR.RTM. 7352, Eastman Chemical) is tumble blended with 0.5% by weight of the compound of instant Example 1. The polymer is then extruded and pelletized at 50 0.degree. F. (260.degree. C.) in a MPM 1" (2.54 cm) single screw extruder. The pellets are collected, redried and reextruded 5 times. Pellets are collected from each extrusion pass and the polymer intrinsic viscosity measured. PET containing the instant compound of Example 1 shows a higher retention of original intrinsic viscosity through the five extrusion passes than does PET containing no stabilizer.

Poly(butylene terephthalate), PBT (RYNITE.RTM. 9160, DuPont) is tumble blended with 0.3% by weight of the compound of instant Example 1. The polymer is then extruded and pelletized at 260.degree. C. A portion of the collected pellets are reextruded under the same conditions for a second pass. The remainder from the first extrusion is injection molded into 2".times.2".times.125 mil (5.08 cm.times.5.08 cm.times.3.175 mm) plaques at 540.degree. F. (282.degree. C.) with a 100.degree. C. mold temperature in a BOY 30M molder. Intrinsic viscosities of the second pass extrudate and the injection molded plaques are determined. The PBT containing the instant compound of Example 1 shows a better retention of intrinsic viscosity value than does PBT containing no stabilizer.

The plaques are measured for yellowness index (color) using ASTM D1925-70. The plaques containing the instant compound of Example 1 have a lower YI values (less discoloration) than do the plaques prepared from the control unstabilized PBT.

6,6-Nylon (ZYTEL.RTM. 101, DuPont) is thoroughly dried in a vacuum oven and tumble blended with 0.5% by weight of the compound of instant Example 1. The polyamide is extruded on a 1" (2.54 cm) MPM extruder at 575.degree. F. (302.degree. C.). The collected pellets are injection molder at 575.degree. F. (302.degree. C.) with the mold at 150.degree. C. in a BOY 30M injection molder. The plaques obtained are measured for yellowness index (YI) values using ASTM D1925-70. The plaques containing the instant compound of Example 1 exhibit lower YI values (less discoloration) than do the unstabilized control plaques.

A solution of 0.25 g of the instant compound of Example 1 in 40 ml of hexane/methanol is added to a rapidly stirred suspension of 100 g of ABS (acrylonitrile/butadiene/styrene terpolymer) in 600 g of water. The suspension is filtered and dried under vacuum at 40.degree. C. for 40 hours. To the dried powder is added 2% by weight of titanium dioxide and 1% by weight of N,N'-ethylenebisstearamide on a two roll mill at 180.degree. C. over four minutes. Compression molded plaques (0.8 mm) are prepared at 175.degree. C. and placed in an air oven at 180.degree. C. for 45 minutes. The color of said plaques are determined as yellowness index values using ASTM D1925-70. The plaques containing the instant compound of Example 1 exhibit lower yellowness index values (less discoloration) than do the control plaques from unstabilized ABS resin.

Experiments are carried out to determine the solubility of the instant compound into linear low density polyethylene (LLDPE) films at 20.degree. C., 40.degree. C. and 60.degree. C. by diffusion-in of a relatively homogeneous particle size (<70 microns) of the test sample suspended in silicon oil.

Each sample is carefully ground with a mortar and pestle and the particle size below 70 microns is separated by sieving with a 200 mesh screen. The powder is then suspended in silicon oil (polydimethylsiloxane, L-45, Union Carbide Chemicals) at a concentration of approximately 38% (wt/wt). A few drops of this suspension is placed on a 10 mil (0.254 mm) thick, 2".times.2" (5.08 cm.times.5.08 cm) compression molded film and a second film of the same dimension is placed on top. The films are gently pressed together so that the suspension forms a thin liquid layer between the polymer films. Excess suspension is removed and the procedure is repeated fill a stack of eight films (six films for evaluation) are prepared. The stack is then placed between two 2.5".times.2.5" (6.35 cm.times.6.35 cm) ceramic files and wrapped in aluminum foil and held together with a G-clamp. Each stack is aged at 20.degree. C., 40.degree. C. and 60.degree. C. under a nitrogen atmosphere. At specified intervals, a single film is removed from the stack and the excess suspension is washed from the film with hexane. The film is then analyzed by X-ray fluorescence for total phosphorus content. LLDPE containing 0, 1000 ppm and 2000 ppm of the test compound are used as standard controls for this X-ray fluorescence method.

The solubility data are given in the Table below.

It is clear from these data that the instant beta, triclinic crystalline compound of Example 1 is considerably more soluble in LLDPE than is the prior art compound of Example 4 of U.S. Pat. No. 4,318,845.