US 5,300,192 AGrant
Wet Laid Fiber Sheet Manufacturing With Reactivatable Binders for Binding Particles to Fibers
Issue Date:1994-04-05
•45 Claims
•8 Drawing Sheets
Abstract
Binder is applied to fibers during the production of a web on a wet laid sheet manufacturing line. Particles are bound to fibrous material by a binder that has a volatility less than water, wherein the binder has a functional group capable of forming a hydrogen bond with the fibers, and a functional group that is capable of forming a hydrogen bond or a coordinate covalent bond with the particles. The binder may be activated or reactivated by addition of heat, liquid, or mechanical energy such that fibers treated with binder may be shipped to a distribution point before particles are bound to the fibers. The binder may be a polymeric binder selected from the group consisting of polyethylene glycol, polypropylene glycol, polyacrylic acid, polyamides and polyamines, and in which the polymeric binder has a hydrogen bonding functionality or coordinate covalent bond forming functionality on each repeating unit of the polymeric binder. Alternatively, the binder may be a non-polymeric organic binder that includes a functionality such as a carboxylic acid, an alcohol, an amino acid, an amide, and an amine, wherein there are at least two such functionalities on the molecule, which may be the same or different functionality. Particles attached to the fibers in this manner are firmly adhered and are not easily dislodged. Fibrous products produced by this method include fibers to which particles are bound and may also include other fibers.
Metadata
Assignee
- Weyerhaeuser Company
Inventors
- Michael R. Hansen
- Richard H. Young, Sr.
Application Information
Application Number:US 9312137
Filing Date:1992-08-17
Priority Date:1992-08-17
Art Unit:133
Classifications
IPC:
D21H 2322
Field of Search:
16215642826412;135;158;184;168.3;164.3;186305;62.2;181;296;62.6;308.6219;288121
Patent Drawings (8 sheets)
Description
BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention concerns reactivatable polymeric and non-polymeric binders applied to fibers on a wet laid fiber sheet manufacturing line and to the use of such binders in binding particles to fibers. In particular embodiments, it concerns the reactivation and use of such fibers, preferably at an article manufacturing plant at a location remote from a pulp sheet manufacturing line to bind superabsorbent and/or other particles to cellulosic fibers which may then be used, for example, as absorbent fibers incorporated into cellulosic products.
2. General Discussion of the Background
Superabsorbent polymers have been developed in recent years that are capable of absorbing many times their own weight of liquid. These polymers, which are also known as water insoluble hydrogels, have been used to increase the absorbency of sanitary products such as diapers and sanitary napkins. Superabsorbent polymers are often provided in the form of particulate powders, granules, or fibers that are distributed throughout absorbent cellulosic products to increase the absorbency of the product. Superabsorbent particles are described, for example, in U.S. Pat. No. 4,160,059; U.S. Pat. No. 4,676,784; U.S. Pat. No. 4,673,402; U.S. Pat. No. 5,002,814; and U.S. Pat. No. 5,057,166. Products such as diapers that incorporate absorbent hydrogels are shown in U.S. Pat. No. 3,669,103 and U.S. Pat. No. 3,670,731.
One problem with the use of superabsorbents is that the superabsorbent material can be physically dislodged from the cellulosic fibers of an absorbent product and migrate from the product. Separation of the superabsorbent from the product wastes the superabsorbent material and reduces the absorbency of the product and diminishes the effectiveness of the superabsorbent material. This problem was addressed in European Patent Application 442 185 A1, which discloses use of a polyaluminum chloride binder to bind an absorbent polymer to a fibrous substrate. The polyaluminum binder, however, suffers from the drawback of being an inorganic product that is not readily biodegradable. Moreover, that European patent does not offer any guidance for selecting binders other than polyaluminum chloride that would be useful in binding absorbent particles.
A method of immobilizing superabsorbents is disclosed in U.S. Pat. No. 4,410,571 in which a water swellable absorbent polymer is converted to a non-particulate immobilized confluent layer. Polymer particles are converted to a coated film by plasticizing them in a polyhydroxy organic compound such as glycerol, ethylene glycol, or propylene glycol. The superabsorbent assumes a non-particulate immobilized form that can be foamed onto a substrate. The individual particulate identity of the superabsorbent polymer is lost in this process. The confluent nature of the superabsorbent material can also result in gel blocking, in which absorption is diminished as the water swollen polymers block liquid passage through the film layer.
U.S. Pat. No. 4,412,036 and U.S. Pat. No. 4,467,012 disclose absorbent laminates in which a hydrolyzed starch polyacrylonitrile graft copolymer and glycerol mixture is laminated between two tissue layers. The tissue layers are laminated to each other by applying external heat and pressure. The reaction conditions form covalent bonds between the tissue layers that firmly adhere the tissue layers to one another.
Numerous other patents have described methods of applying binders to fibrous webs. Examples include U.S. Pat. No. 2,757,150; U.S. Pat. No. 4,584,357; and U.S. Pat. No. 4,600,462. Such binders are not described as being useful in binding particulates, such as superabsorbent particles, to fibers. Yet other patents disclose crosslinking agents such as polycarboxylic acids that form covalent intrafiber bonds with individualized cellulose fibers, as in European Patent Application 440472 A1; European Patent Application 427 317 A2; European Patent Application 427 316 A2; and European Patent Application 429 112 A2. The covalent intrafiber bonds are formed at elevated temperatures and increase the bulk of cellulose fibers treated with the crosslinker. The covalent bonds between the fibers produce a pulp sheet that is more difficult to compress to conventional pulp sheet densities than in an untreated sheet. Any covalent crosslink bonds that form between the fibers and particles occupy functional groups that would otherwise be available for absorption, hence absorption efficiency is decreased.
Many different types of particles other than superabsorbents may be added to fibers for different end uses. Antimicrobials, zeolites and fire retardants are but a few examples of particles that are added to fibers. It would be advantageous to provide a method of attaching particles that could be accommodated to the many different particle needs of end users. Moreover, it would be advantageous to reduce particulate waste in the attachment process, and simplify shipment of fiber products that require particulate addition. It would be further advantageous to bind particulates to fibers without requiring the shipment of bulk fibers with adhered particulates as shipping and excessive handling of these fibers subject them to mechanical impact which can dislodge some particles from the fibers. It would also be advantageous to incorporate binders onto fibers during the initial pulp sheet manufacturing process so that the fibers are ready for reactivation and use at a remote product manufacturing location.
SUMMARY OF THE INVENTION
The foregoing and other objects are achieved by providing fibers in a wet laid sheet manufacturing line, such as cellulose fibers with or without synthetic or other fibers being wet laid into a web or sheet. The fibers include those with hydrogen bonding functional sites, with or without other fibers, to which a binder is applied to the fibers on the wet laid sheet manufacturing line. The binder has a volatility less than water. The binder also has a functional group that forms a hydrogen bond with the fibers having the hydrogen bonding functional sites, and a functional group that is also capable of forming a hydrogen bond or a coordinate covalent bond with particles that have a hydrogen bonding or coordinate covalent bonding functionality. The binder is capable of attaching the particles to the fibers with the hydrogen bonding functional sites, and forms a bond that has been found to be resistant to mechanical disruption. These particles can be added to the fibers during manufacture of the fibrous sheet on the wet laid sheet manufacturing line. However, preferably the particles are not added until the fibers are processed by an end user during the manufacture of products. Consequently, dislodgement of particles from fibers during shipment of the bulk fibers is eliminated. In addition, customization by the end user is enhanced as the end user can add its desired particles to the fibers at the time the fibers are used. Possible degradation of particulates during shipment and the delay prior to incorporation into products are also minimized. A significant advantage of these binders is that the binders can be present on fibers in an inactive state at the wet laid sheet manufacturing line, then later activated or reactivated at a remote location (e.g. at a user's plant) to bind particles to the fibers.
In this application, the term "wet laid sheet manufacturing line" means a manufacturing line wherein a sheet or mat of fibers is formed from a slurry of fibers. Typically, the slurry is deposited on a wire from a source, such as a headbox, and the fiber sheet is dried on the line. Thus, the term "wet laid sheet manufacturing line" refers to a line in which a sheet or mat is formed by a wet laying process. A specific example of a wet laid sheet manufacturing line is a pulp sheet manufacturing line of type wherein wood pulp or other cellulosic fluff fibers, with or without other fibers, is made into paper or fibrous webs. The term "pulp" refers in this case to fibers which include a hydrogen bonding capability, whether or not blended with fibers without a hydrogen bonding capability. For convenience, and not to be construed as a limitation, the description proceeds with reference at times to a pulp sheet manufacturing line as a specific example of a wet laid sheet manufacturing line.
Liquid binders (which includes aqueous solutions of solid binders or neat liquids) can be placed on the fibers, air dried, and later reactivated by moistening the fibers. In the case of aqueous based binders, these binders can be added prior to or at the drying stage of a pulp sheet manufacturing line so that the drying equipment already present on such a line can dry these binders and fibers to the desired maximum moisture content (e.g. about 10% w/w water, most preferably a maximum moisture content of from about 6% to 8% w/w) to eliminate molding or other degradation of the fibers. Non-aqueous binders, such as glycerin may also be added to the fibers on the pulp sheet manufacturing line at any suitable location. However, these non-aqueous binders are most preferably added after drying of the pulp sheet has commenced or is complete. Consequently, water in the pulp sheet does not tend to interfere with the incorporation of the binders on the fibers. Alternatively, a dry solid binder may be added to the fibers on the pulp sheet manufacturing line and later activated by heat, the addition of a liquid, by the moisture present in the sheet on the line prior to drying, or otherwise. For example, certain inactive binders can also be activated by applying kinetic energy to the fibers after the binder and fibers reach an equilibrium moisture content with the atmosphere (hereinafter referred to as "air drying"). Kinetic energy can be applied to the fibers, for example, by mechanically agitating the binder and fibers. In yet other embodiments, the binder may be activated or reactivated by heating the fibers after applying the binder to the fibers.
The capacity for activation or reactivation allows the binder to be applied to the fibers on the pulp sheet manufacturing line, with the fibers being then shipped to distribution points with the binder in an inactive form. The binder is then activated at the remote distribution point or user's plant where particles are added to the fibers and bound thereto. As used herein, binder "activation" includes both activation of previously inactive binders (such as solid binders in the absence of liquid) or reactivation of previously active binders (such as a liquid binder that has been air dried).
Another advantage of the present invention is that the binder can be activated or reactivated in a pattern that corresponds to a desired distribution of particles in fibrous material. A reactivation liquid, for example, can be applied to target areas of a diaper that will be initially moistened by urine during use. Superabsorbent particles can be added to the activated area of the diaper and adhered almost exclusively in those areas where initial urine absorption is required. Targeted activation of binder allows particles to be efficiently and economically attached to the fibers, with reduced particle wastage. Moreover, targeted binder activation and particle adherence increases the absorptive efficiency of the product by diminishing excessive wicking of liquid within the plane of an absorptive product.
Fibers in accordance with the present invention may have particles bound to the fibers with a polymeric or non-polymeric binder. The polymeric binder may be selected from the group consisting of polypropylene glycol (PPG), polyethylene glycol (PEG), polyacrylic acid (PAA), poly(caprolactone) diol, a polyamide, a polyamine, and copolymers thereof (for example, a polypropylene glycol/polyethylene glycol copolymer), wherein the polymeric binder has a hydrogen bonding functionality or coordinate covalent bond forming functionality on each repeating unit of the polymeric binder. The non-polymeric binder has a volatility less than water, a functional group that forms hydrogen bonds or coordinate covalent bonds with the particles, and a functional group that forms hydrogen bonds with the fibers. The non-polymeric binder is an organic binder, and preferably includes a functionality selected from the group consisting of a carboxylic acid, an alcohol, an aldehyde, an amino acid, an amide, and an amine, wherein there are at least two functionalities on the molecule selected from this group, and the two functionalities are the same or different. Examples of such binders include polyols, polyamines (a non-polymeric organic binder with more than one amine group), polyamides (a non-polymeric organic binder with more than one amide group), polyaldehydes (a non-polymeric organic binder with more than one aldehyde functionality), polycarboxylic acids (a non-polymeric organic binder with more than one carboxylic acid functionality), amino alcohols, hydroxy acids and other binders. These binders have functional groups that are capable of forming the specified bonds with the particles and fibers.
More preferably, the organic non-polymeric binder is selected from the group consisting of glycerin, ascorbic acid, urea, glycine, pentaerythritol, a monosaccharide or a disaccharide, citric acid, tartaric acid, dipropylene glycol, glyoxal, and urea derivatives such as DMDHEU. Suitable saccharides include glucose, sucrose, lactose, ribose, fructose, mannose, arabinose, and erythrose. Each of these preferred binders is a non-polymeric molecule that has a plurality of hydrogen bonding functionalities that permit the binder to form hydrogen bonds to both the fibers and particles. Particularly preferred binders include those that can form five or six membered rings, most preferably six membered rings, with a functional group on the surface of the particle.
The fibrous material to which particles are to be bound may be cellulosic or synthetic fibers that are capable of forming hydrogen bonds with the binder, while the particles are selected to be of the type that form hydrogen bonds or coordinate covalent bonds with the binder. It has unexpectedly been found that this binder system secures particles to fibers exceptionally well. A superior fibrous product is therefore produced that has improved absorbent properties as compared to unbound or covalently bound particles. Formation of the noncovalent bond allows production of a fiber product that is easily manufactured and a web that is easily densified, and that is readily biodegradable and disposable.
In one preferred embodiment, an absorbent product comprises a fibrous cellulosic mat that contains superabsorbent hydrogel particles in particulate form. The superabsorbent particles form hydrogen bonds or coordinate covalent bonds with the binder, depending upon the binder, while the binder in turn forms hydrogen bonds with the hydroxyl groups of the cellulose fibers. These noncovalent, relatively flexible bonds between the binder and particles maintain the particles in contact with the fibers, and resist dislodgement of the particles by mechanical forces applied to the mat during manufacture, storage or use. The binder may suitably be present in an amount of from about 3 to 80 percent of the total weight of the product, while the particles bound to the binder and hence to the fibers in accordance with the present invention (via hydrogen/coordinate covalent bonds) may suitably be present in an amount of 0.05 to 80 percent, preferably 1 to 80 percent or 5 to 80 percent by weight. An especially suitable range of binder is 3 to 40 percent by weight, or 3 to 25 percent by weight, while a particularly suitable range of such particles is 5 to 40 percent by weight. A preferred weight ratio of particle to binder is 2:1 to 4:1. An example of a suitable particle is a superabsorbent polymer such as a starch graft polyacrylate hydrogel fine or larger size particle such as a granule, which forms hydrogen bonds with the binder. The binder also forms hydrogen bonds with the hydroxyl groups of the cellulose or other fibers with hydrogen bonding functional sites, thereby securely attaching the superabsorbent particles to the fibers.
In binding the particles to fibers, the particles are preferably insoluble in the binder and therefore retain their solid particulate form following binding. The particles have functional groups that can form hydrogen bonds or coordinate covalent bonds with the binder, and the binder in turn is capable of forming hydrogen bonds to the fibers.
In especially preferred embodiments, the fibers are cellulosic and the particles are superabsorbent particles that are bound to the binder by hydrogen bonds. The fibers may also be continuous or discontinuous synthetic or natural fibers having a hydrogen bonding functional group that hydrogen bonds with the binder. Rayon is another specific example of these types of fibers. The binder is suitably applied to the fibers in an amount of at least 3 percent, and preferably no more than 80 percent, by total weight of the particle, fiber and binder. The particles may be bound to the fibers at less than 150.degree. C. or without any external application of heat at ambient temperature (e.g., about 25.degree. C.). Particles may also be bound in the absence of any external application of pressure, or in the absence of external heat and pressure.
In some embodiments the binder is associated with the fibers as a solid (for example, a dry powder or a dried liquid), and the fibers with the hydrogen bonding functionality contain at least 7 percent water by weight when the binding step is performed. This level of moisture in the fibers provides sufficient mobility of reactants to allow the particles and fibers to bind well to each other. When a liquid binder is used (for example, glycerin or a solution of glycine powder), the fibers suitably contain at least about 0.5 percent water by weight. A solid binder is suitably used with such fibers having 0.5 percent water by weight if the binder is heated above its melting point to liquefy it. A solid binder may be thermoplastic or meltable, such that it can be heated above its melting point and then cooled to fuse fibers to each other. The thermoplastic properties of the binder can also provide additional mechanical adherence between the particles and fibers. In some embodiments, a thermoplastic binder such as urea may be employed which can adhere particles both thermoplastically and with hydrogen bonding.
It is therefore an object of the present invention to apply binder materials to fibers on a wet laid sheet manufacturing line, the binder materials being capable of binding particles to the fibers.
Another object of the present invention is to provide fibers with binders which may be reactivated at a site remote from the wet laid sheet manufacturing line for the purpose of adhering particulate materials to the fibers.
It is another object of this invention to provide improved fibers from a wet laid sheet manufacturing line which facilitates the binding of particles to fibers in a customized manner to easily allow different end users of the products to select and bind different types or brands of particles to the fibers.
It is also an object of this invention to provide a fiber product from a wet laid sheet manufacturing line with enhanced particulate binding capabilities.
Another object of the invention is to provide improved fiber from a wet laid sheet manufacturing line usable in providing absorbent products in which particulates are firmly bound to fibers such that the particles are less likely dislodged by mechanical forces.
The invention also includes the products produced by any of the methods described herein.
This invention relates to the foregoing features and objects individually as well as in combination. The foregoing and other features and advantages of the invention will become more apparent from the following detailed description and accompanying drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a schematic illustration of a wet laid sheet manufacturing line illustrating the application of binders in accordance with the present invention during the manufacture of a fiber sheet.
FIG. 2 is a schematic illustration of a binder reactivation and particulate attachment process in accordance with the present invention.
FIG. 3 is a top plan view of a structure into which fibers of the present invention are incorporated with attached particles, the fibers being in the form of an illustrated absorbent pad.
FIG. 4 represents a partial sectional view of the pad of FIG. 3.
FIG. 5 illustrates a plan view of a bandage incorporating fibers of the present invention.
FIG. 6 is a sectional view of a portion of the bandage of FIG. 5, taken along line of FIG. 5.
FIG. 7 is a perspective view of an absorbent structure of fibers of the present invention.
FIG. 8 is a cross-sectional view of the structure of FIG. 7, taken along line 8--8 of FIG. 7.
FIG. 9 is a plan view of a feminine hygiene appliance incorporating fibers of the present invention.
FIG. 10 is a sectional view of the appliance of FIG. 9 taken along line 10--10 of FIG. 9.
FIG. 11 is a plan view of a disposable diaper including a core of fibers of the present invention.
FIG. 12 is a vertical sectional view of the diaper of FIG. 11.
FIG. 13 is a view of an enlarged fiber with particles bonded to the fiber with the binders of the present invention.
FIG. 14 is a schematic view of a cellulose mat with particles bound to all its surfaces and throughout its depth.
FIG. 15 is a photomicrograph of particles adhered to fibers with an ascorbic acid binder.
FIGS. 16A, 16B, 16C, and 16D are photomicrographs of particles bound to fibers with lactose.
DETAILED DESCRIPTION OF SEVERAL PREFERRED EMBODIMENTS OF THE INVENTION
Processing of Fibers
FIG. 1 illustrates a wet laid sheet manufacturing line such as a pulp sheet manufacturing line 10. In this manufacturing line, a pulp slurry 12 is delivered from a headbox 14 through a slice 16 and onto a Fourdrinier wire 18. The pulp slurry 12 typically includes cellulose fibers such as wood pulp fibers and may also include synthetic or other non-cellulose fibers as part of the slurry. Water is drawn from the pulp deposited on wire 18 by conventional vacuum system, not shown, leaving a deposited pulp sheet 20 which is carried through a dewatering station 22, illustrated in this case as two sets of calendar rolls 24, 26 each defining a respective nip through which the pulp sheet or mat 20 passes. From the dewatering station, the pulp sheet 20 enters a drying section 30 of the pulp manufacturing line. In a conventional pulp sheet manufacturing line, drying section 30 may include multiple canister dryers with the pulp mat 20 following a serpentine path around the respective canister dryers and emerging as a dried sheet or mat 32 from the outlet of the drying section 30. Other alternate drying mechanisms, alone or in addition to canister dryers, may be included in the drying stage 30. The dried pulp sheet 32 has a maximum moisture content pursuant to the manufacturer's specifications. Typically, the maximum moisture content is no more than 10% by weight of the fibers and most preferably no more than about 6% to 8% by weight. Otherwise, the fibers tend to be too damp. Unless overly damp fibers are immediately used, these fibers are subject to degradation by, for example, mold or the like. The dried sheet 32 is taken up on a roll 40 for transportation to a remote location, that is, one separate from the pulp sheet manufacturing line, such as at a user's plant for use in manufacturing products. Alternatively, the dried sheet 32 is collected in a baling apparatus 42 from which bales of the pulp 44 are obtained for transport to a remote location.
A binder of the type explained in detail below is applied to the pulp sheet from one or more binder applying devices, one of which is indicated at 50 in FIG. 1. Any binder applying device may be used, such as sprayers, roll coaters, immersion applicators or the like. Sprayers are typically easier to utilize and incorporate into a pulp sheet manufacturing line. As indicated by the arrows 52, 54 and 56, the binder may be applied at various locations on the pulp sheet manufacturing line, such as ahead of the drying stage 30 (indicated by line 52), intermediate the drying stage 30 (as indicated by line 54), or downstream from the drying stage 30 (as indicated by the line 56). Water based binders, such as non-polymeric urea, are typically applied at a location where sufficient drying can still take place in the drying stage to produce a dried binder containing fiber sheet with no more than the maximum desired moisture content. Consequently, to take advantage of the drying stage 30, water based binders are typically applied at locations 52 or 54. At location 52, the water remaining in the sheet or mat 20 at this stage tends to interfere with the penetration of the binder into the sheet. Consequently, application of the binder after some drying has taken place, for example at location 54, is preferable. If water based binders are applied at location 56 in an amount which would cause the moisture content of the sheet to exceed the desired maximum level, an additional drying stage (not shown) may be included in the pulp manufacturing line to bring the moisture content down to the desired level.
A non-aqueous based binder, such as glycerin, is most preferably added downstream from the drying stage at location 56 or during the drying stage as indicated by location 54. However, liquid non-aqueous binders may also be added at location 52 upstream of the drying stage. At this latter location, the water in the wet web at this point may tend to attract these binders into the mat or sheet as the binders tend to be hydroscopic. Since non-aqueous binders typically do not enhance the degradation of the product due to the addition of moisture to the sheet, they can be applied downstream from the drying stage without bringing the moisture content of the sheet above the desired maximum level.
The particulate materials, selected as explained below, may be added to the sheet and adhered thereto by the binders on the pulp manufacturing line, such as indicated by the particulate applicator 60, which may comprise a bulk or volumetric metering device. These particles may be sprinkled, poured or otherwise added to the sheet. To facilitate the adherence of these particulates to the sheet at this location, enough moisture must remain in the sheet, in the case of aqueous binders, to enable the bonding between the particles and fibers as explained below. For non-aqueous binders, the particles in this case are preferably added while the binder is still wet or heated to facilitate the reaction. Although particles can be added on the pulp sheet manufacturing line in this manner, with a subsequent drying stage being utilized to reduce the moisture content following particulate addition. However, if a water based binder makes the fibers too wet following the addition of the particles, this is not the preferred approach. Also, during transportation of rolls or bales of these fibers, particles can become dislodged by mechanical impact during transport. In addition, this approach interferes with the customization of the fiber application at a user's location. For example, a user may want the capability of selecting particular types or brands of particles for adherence to the fibers in the user's products, without having this selection having been made by a pulp sheet manufacturer who incorporates the particles into the pulp sheet during its manufacture. Also, certain particles may degrade over time, making it advantageous to add such particles immediately prior to incorporation into products. For example, superabsorbent particles are susceptible to absorbing moisture from the atmosphere during shipment. Particles with a relatively short shelf life, such as certain zeolites (e.g. Abscents with odor absorbing materials which can become saturated with odors over time) being one example, may also degrade over time. Another example is zeolites with silver salts as antimicrobial agents which can photodegrade. Therefore, it is advantageous to provide a product in which the end user of the product may incorporate the desired particles at the time the fibers are converted into products.
Therefore, in keeping with this preferred approach, as illustrated in FIG. 2, the respective rolls 40 or bales 44 of binder containing fibers, without particles, are transported to a remote location for use by a user. These rolls or bales (or otherwise transported fibers, e.g. bagged, containerized or otherwise in bulk form) are then refiberized by a fiberizing apparatus 70. Although any fiberizer may be used, a typical fiberizing apparatus 70 is a hammermill which may be used alone or in conjunction with other devices such as picker rolls or the like for breaking up the sheet 32 or bales 42 into individual fibers.
A particulate material adding mechanism 72 (like mechanism 30) delivers the desired particulate materials to the fibers at the desired location in the user's process. Again, the device 72 typically comprises a metering mechanism, although any suitable device for adding particulates to fibrous materials may be used. For example, the particulates may be delivered as indicated by line 74 to the fiberizing apparatus 70. In the case of some binders, agitation of fibers within the fiberizer 70, as explained in greater detail below, reactivates the binders and causes the particulates to be adhered to the fibers by the binder. Alternatively, a reactivating liquid, such as water, may be sprayed or otherwise applied to the fibers, such as from a reactivation liquid tank or source 78 by way of a sprayer (not shown) at location 80. The particles may then be applied, as indicated by line 84 to the fibers downstream from the application of the reactivation liquid 80. Alternatively, the particles added prior to location 80 are adhered to the fibers by the binder upon reactivation of the binder at location 80. As yet another alternative, the fiberized fibers are delivered to an air laying device 90 and reformed into a desired product such as a web indicated at 92. In the case of air laid fibers, the reactivation liquid may be applied to the web at location 96 with the particles then being added at location 98 as shown with the reactivated binder then adhering the particles to the fibers. The particles may be applied at a location in the process upstream from the application of the reactivating liquid at location 96. In addition, the binder may be reactivated at specifically defined locations on the web 92, such as in target zones of an absorbent core of a product with the particles then only being applied to these target zones, thereby minimizing the wasting of the particulate material. The web 92, with or without other components of the end user's product, is then processed into the user's product, such as being included within a disposable diaper 100.
Again, with this approach, the end user of the fibers may readily select particles to be applied to its product and may activate the binder as required to enhance the efficient production of the user's product. In addition, the user has flexibility in air laying or otherwise combining the binder containing fibers into a finished product with the desired particulates. The binder containing fibers, because the binders are all water soluble, are preferably not wet laid because wet laying would remove at least some of the binder. Not only is handling and shipping of the particulate containing products avoided by the manufacturer of the pulp sheet, enhanced adhesion of particulates to the fibers results because the particles are not subjected to mechanical forces between the location of manufacture of the fibers and the location at which the particulate materials are added.
Fiber Characteristics
In particularly preferred embodiments, the fibers being processed are cellulosic or synthetic fibers to which superabsorbent hydrogel polymer particles and/or other particles are adhered by a binder, with products then being made therefrom. Suitable fibers include wood pulp fibers, which can be obtained from well known chemical processes such as the kraft and sulfite processes. In these processes, the best starting material is prepared from long fiber coniferous wood species, such as pine, douglas fir, spruce and hemlock. Wood pulp fibers can also be obtained from mechanical processes, such as ground wood, mechanical, thermomechanical, chemimechanical, and chemithermomechanical pulp processes. The fibers are preferably elongated, for example having a length to width ratio of about 10:1 to 5:1.
The fibers used in the present invention also include fibers that are pretreated prior to the application of a binder to the fibers as explained below. This pretreatment may include physical treatment, such as subjecting the fibers to steam or chemical treatment, such as cross-linking the fibers. Although not to be construed as a limitation, examples of pretreating fibers include the application of fire retardants to the fibers, such as by spraying the fibers with fire retardant chemicals. Specific fire retardant chemicals include, by way of example, sodium borate/boric acid, non-polymeric urea, urea/phosphates, etc. In addition, the fibers may be pretreated with surfactants or other liquids, such as water or solvents, which modify the surface of the fibers. Other pretreatments include exposure to antimicrobials or pigments.
The fibers may also be pretreated in a way which increases their wettability. For example, natural fibers may be pretreated with a liquid sodium silicate, as by spraying the fibers with this material, for pretreatment purposes. Wettability of the surface of fibers is also improved by subjecting the fibers to a corona discharge pretreatment in which electrical current is discharged through the fibers in a conventional manner. In the case of both synthetic fibers and wood pulp fibers, corona discharge pretreatment results in an oxygen functionality on the surface of the fibers, making them more wettable and more bondable. The fibers may also be pretreated with conventional cross-linking materials and may be twisted or crimped, as desired. Pretreating cellulose fibers with chemicals which result in lignin or cellulose rich fiber surfaces may also be performed in a conventional manner.
Bleaching processes, such as chlorine or ozone/oxygen bleaching may be used in pretreating the fibers. In addition, the fibers may be pretreated, as by slurrying the fibers in baths containing antimicrobial solutions (such as solutions of antimicrobial particles as set forth below), fertilizers and pesticides, and/or fragrances and flavors for release over time during the life of the fibers. Fibers pretreated with other chemicals, such as thermoplastic and thermoset resins may also be used. Combinations of pretreatments may also be employed with the resulting pretreated fibers then being subjected to the application of the binder coating as explained below.
Ground wood fibers, recycled or secondary wood pulp fibers, and bleached and unbleached wood pulp fibers can be used. Details of the production of wood pulp fibers are well known to those skilled in the art. These fibers are commercially available from a number of companies, including Weyerhaeuser Company, the assignee of the present invention.
The fibers can also be any of a variety of other natural or synthetic fibers, however, all of the fibers to which particles are to be attached in accordance with the present invention include a hydrogen bonding functionality. This does not preclude the blending of such fibers with fibers lacking this characteristic. However, the fibers lacking a hydrogen bonding functionality will not have particles bonded thereto with the strength of the bonds that would be present if the fibers had a hydrogen bonding functionality.
A hydrogen bond is an intermolecular force that occurs between hydrogen atoms that are covalently bonded to small, strongly electronegative elements (such as nitrogen and oxygen) and nonbonding electron pairs on other such electronegative elements. A hydrogen bonding functionality is a functional group that contains an oxygen or nitrogen atom, for example hydroxyls, carboxyls, ethers, esters, epoxides, carbonyls, amines, urethanes and others, that is capable of forming a hydrogen bond. The orbitals of the nonbonding electron pairs on the oxygen or nitrogen overlap with the relatively empty 1s orbital of the hydrogen covalently bonded to another nitrogen or oxygen atom. The 1s orbital of the hydrogen is relatively empty due to the unequal sharing of the electrons in the covalent bond between it and the small electronegative atom (oxygen or nitrogen) to which it is bound.
Specific examples of natural fibers that contain a hydrogen bonding functionality include chopped silk fibers, wood pulp fibers, bagasse, hemp, jute, rice, wheat, bamboo, corn, sisal, cotton, flax, kenaf, peat moss, and mixtures thereof. Suitable synthetic fibers with hydrogen bonding functionalities include acrylic, polyester, carboxylated polyolefins, rayon and nylon. The hydrogen bonding functionality is an ester in acrylic fibers and a carboxylic acid in carboxylated polyolefin fibers, an ester in polyester, an amide in nylon, and a hydroxyl in rayon. Polyethylene and polypropylene would be unsuitable fibers for use in particle to fiber bonding in accordance with the present invention because they include only carbons and hydrogens without any oxygens or nitrogens that can participate in hydrogen bonds.
Blends of fibers comprised of fibers with hydrogen bonding functionality and those without may be used with the binder bonding being strongest to the fibers with the prescribed functionality. Typically, the non-hydrogen bonding functional fibers are present in an amount of from 0-80% by weight of the fiber blend and most preferably in an amount of from 5% to 30% by weight. Blends of multiple types of fibers may also be used.
For purposes of convenience, and not to be construed as a limitation, the following description proceeds with reference to the treatment of chemical wood pulp fibers. The fibers are formed into a sheet or equivalently a mat on a pulp sheet manufacturing line and are subjected to the application of a binder during the manufacture of the pulp sheet. Mats of NB 416 wood pulp fibers from Weyerhaeuser Company with the applied binders are a specific example.
Particle Characteristics
In accordance with the present invention, particles are added to the sheet or fibers before, during or following fiberization of the sheet to give these fibers desired properties, such as increased absorbency, abrasiveness, or antimicrobial activity. The particle can be any particulate material that has the desired property and which is capable of forming hydrogen bonds or coordinate covalent bonds with the binder. Hydrogen bonds can be formed, as discussed above, by particles that contain functional groups having an oxygen or nitrogen. Coordinate covalent bonds, in contrast, are formed by donation of a lone pair of electrons on one atom to an empty orbital of another atom. Coordinate covalent bonds differ from covalent bonds in that covalent bonds are formed by a pair of electrons wherein one of the electrons is donated from each of the atoms that participate in the bond. Particles can form coordinate covalent bonds if they have an empty p or d or f orbital that is capable of accepting a pair of electrons from the binder.
A coordinate covalent bond occurs between a donor compound that has a lone pair of electrons to donate to the bond, and an acceptor that has an empty orbital to accept the lone pair of electrons from the donor. According to the Aufbau and Pauli principles, electrons occupy the lobes of atomic orbitals one at a time with a maximum of two electrons (with opposite spins) per lobe. The most basic orbital is the s orbital, which is available for bonding the elements in the first row of the periodic table. In the second row of the periodic table, electrons fill first the 2s orbital of Li and Be, but metals in Groups IA and IIA do not have sufficient affinity for electrons to participate in coordinate covalent bonding. Beginning with column IIIA (boron), the three p orbitals participate in coordinate covalent bonding and the lobes of the p orbitals begin to fill. Boron has one electron in one of the 2p orbitals thus leaving the other two p orbitals empty and available for coordinate covalent bonding. An example of a coordinate covalently bonded boron containing particle is boric acid, which is used as an astringent, antiseptic and fire retardant. Boric acid is shown below wherein the boron is coordinate covalently bonded to a polypropylene glycol (PPG) binder. ##STR1## The next element, carbon, usually hybridizes to have one electron in the 2s orbital and the three remaining electrons are singly placed in the three p orbitals. This leaves no lobes empty for coordinate covalent bonding and electron additions proceeding further across that row of the periodic table also leave no lobes empty. Hence, boron is the only element in the second row of the periodic table that is capable of forming coordinate covalent bonds.
Next the third row begins to fill, and the two 3s electrons fill first in sodium and magnesium, but these metals in groups IA and IIA do not form coordinate covalent bonds as discussed above. Then aluminum, like boron, places one electron in one of the 3p lobes, and the two other 3p lobes are empty and available for coordinate covalent bonding. The same trends continue across the third row, but the third row elements also have available five 3d lobes so the potential for coordination bonding exists even though 3p orbitals are occupied in the third row. Hence, Al, P, S, and Cl are capable of accepting a pair of electrons from an electron pair donor to form a coordinate covalent bond. An example of this is found in the bonding in PCl.sub.5, aluminum trihydrate, or phosphorous pentasulfide. A phosphorous pentasulfide particle can be used to increase flammability of a product, while aluminum trihydrate is a fire retardant. An example of a coordinate covalently bonded aluminum compound is ##STR2## wherein aluminum trihydrate is coordinate covalently bonded to a polypropylene glycol (PPG) polymer.
In the next row, the 4s orbital is filled first, then the 3d lobes begin to fill--one electron per lobe until all have a single then a second electron to each lobe until all lobes are filled. However, 4p and 4f orbitals are also available, hence many of the transition elements are capable of forming coordinate covalent bonds.
The elements that have empty orbitals that participate in coordinate covalent bonding include all those except the metals (which excludes hydrogen) in groups IA and IIA, and C, N, O, F, Ne and He. Especially preferred particles contain boron, aluminum, iron, rhodium, osmium, platinum, and palladium, particularly boron. Examples of particles in accordance with the present invention that are capable of coordinate covalent bonding are aluminum trihydrate, antimony oxide, arsenic disulfide, bismuth aluminate, bismuth iodide oxide, bismuth phosphate, bismuth subcarbonate, bismuth subgallate, cadmium salycilate, chromic carbonate, chromic hydroxide, chromic oxide, and chromic phosphate. All of the polymeric binders used in manufacturing the pulp sheet on line in accordance with the present invention (PPG, PAA, polyamide, polyamine and poly(caprolactone) diol) are are capable of donating a lone pair of electrons from an oxygen or nitrogen to form a coordinate covalent bond with a suitable particle that has an empty orbital for coordinate covalent bonding.
Superabsorbent Particles
In one disclosed embodiment the added particles are superabsorbent particles, which comprise polymers that swell on exposure to water and form a hydrated gel (hydrogel) by absorbing large amounts of water. Superabsorbents are defined herein as materials that exhibit the ability to absorb large quantities of liquid, i.e. in excess of 10 to 15 parts of liquid per part thereof. These superabsorbent materials generally fall into three classes, namely starch graft copolymers, crosslinked carboxymethylcellulose derivatives and modified hydrophilic polyacrylates. Examples of such absorbent polymers are hydrolyzed starch-acrylonitrile graft copolymer, a neutralized starch-acrylic acid graft copolymer, a saponified acrylic acid ester-vinyl acetate copolymer, a hydrolyzed acrylonitrile copolymer or acrylamide copolymer, a modified cross-linked polyvinyl alcohol, a neutralized self-crosslinking polyacrylic acid, a crosslinked polyacrylate salt, carboxylated cellulose, and a neutralized crosslinked isobutylene-maleic anhydride copolymer. Natural materials, such as peat, also are capable of behaving as superabsorbent particles.
Superabsorbent particles are available commercially, for example starch graft polyacrylate hydrogel fines (IM 1000F) from Hoechst-Celanese of Portsmouth, Va., or larger particles such as granules. Other superabsorbent particles are marketed under the trademarks SANWET (supplied by Sanyo Kasei Kogyo Kabushiki Kaisha), SUMIKA GEL (supplied by Sumitomo Kagaku Kabushiki Kaisha and which is emulsion polymerized and spherical as opposed to solution polymerized ground particles), FAVOR (supplied by Stockhausen of Greensboro, N.C.), and NORSOCRYL (supplied by Atochem). The superabsorbent particles come in a variety of sizes and morphologies, for example IM 1000 and IM 1000F. The 1000F is finer and will pass through a 200 mesh screen whereas IM 1000 has particles that will not pass through a 60 mesh screen. Another type of superabsorbent particle is IM 5600 (agglomerated fines). Superabsorbent particulate hydrophilic polymers are also described in detail in U.S. Pat. No. 4,102,340, which is incorporated herein by reference. That incorporated patent discloses hydrocolloid absorbent materials such as cross-linked polyacrylamides.
Other Particles
Many particles that form hydrogen bonds or coordinate covalent bonds are suitable for use with the present invention. Some such particles are listed in Table 1 with an indication of the function of the listed particles.
Other suitable particles include proteins, vitamins zeolites and silica, which contain oxygen or nitrogen groups, or both. An example of a suitable zeolite is Abscents odor absorber available from UOP of Tarrytown, N.Y. An example of a suitable antimicrobial particle is chlorhexidine (N,N"-Bis(4-chlorophenyl)-3,12-diimino-2,4,11,13-tetraazatetradecanediimid amide). The list in Table I is by no means exhaustive as it can be readily determined for each type of particle whether it is capable of forming a hydrogen bond or a coordinate covalent bond. Many of the particles are non-absorbent, or not superabsorbent polymers.
The particles listed in Table 1 have chemical properties that make them suitable for binding to fibers with the binders of the present invention. The listed particles are organic or inorganic compounds that have little or no water solubility, yet have the capacity to hydrogen bond. Water solubility is preferably low, for example, less than 10 g dissolves completely in 300 ml of water at 25.degree. C., more preferably less than about 1 g in 300 ml at 25.degree. C. This low solubility allows the particles to remain solid, and the hydrogen bonding capacity allows them to adhere to the fibers. Once bound, the particles substantially retain a discrete particulate form instead of dissolving or fusing. More of the particles are discrete than fused once bound.
The amount of binder added to the fibers can vary widely, for example from 0.05 to 80 percent of the total weight of the fibrous material, binders and particles. Antimicrobials such as chlorhexidine are effective in very low amounts, such as 0.05 percent. Superabsorbent particles are preferably added in an amount of 3-40 percent, especially 15-25 percent by weight.
Polymeric Binder Characteristics
The particles may be bound to the fibers by a water soluble polymeric binder selected from a predetermined group of polymeric binders that each have a hydrogen bonding functionality or coordinate covalent bond forming functionality on each repeating unit of the polymer. Again, these binders are applied on the wet laid sheet or pulp sheet manufacturing line. The pulp sheet manufacturing line refers to the manufacturing line at which the pulp sheet is formed and includes the locations within a plant at which processes (e.g. sheet formation, dewatering, drying, etc.) are performed prior to rolling, baling or otherwise gathering or packing the fiber for transport to an end use location. In accordance with the present invention, the predetermined groups of polymeric binders includes the set of binders consisting of polypropylene glycol (PPG); a PPG/PEG copolymer; polyacrylic acid; a polyamide such as polyglycine or another polypeptide; a polyamine such as polyethyleneimine or polyvinyl pyridine; or a polyol such as poly(caprolactone) diol. As used herein, a polymer is a macromolecule formed by chemical union of 5 or more identical combining units (monomers). A polyamine is a polymer that contains amine functional groups and a polyamide is a polymer that contains amide functional groups. Each of the binders has a hydrogen bonding or a coordinate covalent bonding functionality on each repeating unit (monomer) of the polymer. This repeating functionality may be a hydroxyl, carboxylic acid, amide, ether or amine. These binders are capable of forming hydrogen bonds because they have a functional group that contains an oxygen or a nitrogen.
The polyglycol has repeating ether units with hydroxyl groups at the terminal ends of the molecule, and polyacrylic acid has a repeating carboxyl group in which a hydrogen is bound to an electronegative oxygen, creating a dipole that leaves the hydrogen partially positively charged. The polyamide (such as a polypeptide) or polyamine has a repeating NR group in which a hydrogen may be bound to an electronegative nitrogen that also leaves the hydrogen partially positively charged. The hydrogen in both cases can then interact with an oxygen or nitrogen on the particle or fiber to form a hydrogen bond that adheres the binder to the particle and fiber. The electronegative oxygen or nitrogen of the binder can also form a hydrogen bond with hydrogens on the particle or fiber that have positive dipoles induced by oxygens or nitrogens to which the hydrogen is attached. The polyamide also has a carboxyl group with an electronegative oxygen that can interact with hydrogen atoms in the particles or fibers.
Thus, the polymeric binders enhance the hydrogen bonding (a) between the fibers and binder; and (b) in the case of particles with hydrogen bonding functionalities, between the binder and the particles.
Alternatively, the polymeric binder may form a coordinate covalent bond with the particles and a hydrogen bond to the fibers. For example, the oxygen or nitrogen on the binder has an unbound pair of electrons that can be donated to an empty orbital in the particle to form a coordinate covalent bond. For example, one free pair of electrons on the oxygen or nitrogen can be donated to the empty p orbital of a boron containing particle to form a coordinate covalent bond that adheres the particle to the binder. The fibers themselves contain functional groups that can form hydrogen bonds with the binder, and allow the binder to adhere to the fiber. Cellulosic and synthetic fibers, for example, contain hydroxyl, carboxyl, amide, ether and ester groups that will hydrogen bond with the hydroxyl, carboxylic acid, amide or amine groups of the binder. Hence the polymeric binder will adhere the particle with a coordinate covalent bond and the fiber will adhere with a hydrogen bond.
In some preferred embodiments, the polymeric binder is bound to both the fibers and the particle by hydrogen bonds. A polypropylene glycol binder, for example, can be used to bind polyacrylate hydrogel particles to cellulosic fibers. The hydroxyl and ether groups on the glycol binder participate in hydrogen bonding interactions with the hydroxyl groups on the cellulose fibers and the carboxyl groups on the polyacrylate hydrogel, as shown below: ##STR3## Hence the binder will adhere both the particle and fiber with hydrogen bonds. The presence of a hydrogen bonding functionality on each repeating unit of the polymeric binder has been found to increase the number of hydrogen bonding interactions per unit mass of polymer, which provides superior binding efficiency and diminishes separation of particles from the fibers. The repeating ether functionality on the glycol binder provides this efficiency in the example diagrammed above. A repeating carboxyl group is the repeating functionality on polyacrylic acid, while repeating carbonyls and NR groups (wherein R is either an H or alkyl, preferably lower alkyl i.e. less than five carbon atoms, where the alkyls are normal or in an iso configuration) of the amide linkages are the repeating functionalities on polyamides such as polypeptides. A repeating amine group is present on polyamines.
The polymeric organic binders of the present invention have been found to increase in binding efficiency as the length of the polymer increases, at least within the ranges of molecular weights that are reported in the examples below. This increase in binding efficiency is attributable to the increased number of hydrogen bonding or coordinate covalent bonding groups on the polymer with increasing molecular length. Each of the polymeric binders has a hydrogen bonding or coordinate covalent bonding functionality on each repeating unit of the polymer, hence longer polymers provide more hydrogen bonding groups or coordinate covalent bonding groups that can participate in hydrogen bonding interactions or coordinate covalent bonds.
Although the invention is not limited to polymeric binders of particular molecular weights, polymeric binders having a molecular weight greater than 500 grams/mole are preferred because they provide attractive physical properties, and the solid is less volatile and more thermoplastic as compared to small polymeric binders. Polymeric binders with molecular weights greater than 4000 grams/mole are especially preferred, because they have minimal volatility and are less likely to evaporate from the fibers. In some particular embodiments, polymers with molecular weights between 4000 and 8000 grams/mole have been used. Polymers with molecular weights above 8000 may be used, but exceedingly high molecular weight polymers may decrease binding efficiency because of processing difficulties.
Certain polymeric binders have greater binding efficiency because their repeating functionality is a more efficient hydrogen bonding group. It has been found that repeating amide groups are more efficient than repeating carboxyl functionalities, which are more efficient than repeating hydroxyl functionalities, which in turn are more efficient than amine or ether functionalities. Hence, polymeric binders may be preferred that have repeating amine or ether functionalities, more preferably repeating hydroxyl functionalities, and even more preferably repeating carbonyl or carboxyl functionalities, and most preferably repeating amide functionalities. Binding may occur at any pH, but is suitably performed at a neutral pH of 5-8, preferably 6-8, to diminish acid hydrolysis of the resulting fibrous product. Suitable binders may be selected from the group consisting of polyethylene glycol; polyethylene glycol and polypropylene glycol, including copolymers thereof; polyethylene glycol, polypropylene glycol and polyacrylic acid; polyethylene glycol, polypropylene glycol, polyacrylic acid, and a polyamide; polyethylene glycol, polypropylene glycol, polyacrylic acid, a polyamide and a polyamine; polypropylene glycol alone; polypropylene glycol and polyacrylic acid; polypropylene glycol alone; polypropylene glycol, polyacrylic acid and a polyamide; and polypropylene glycol, polyacrylic acid, a polyamide and a polyamine; polyacrylic acid alone; polyacrylic acid and a polyamide; polyacrylic acid, a polyamide and a polyamine; a polyamide alone; a polyamide and a polyamine; or a polyamine alone.
The group consisting of polyacrylic acid, polyamide and polyamine has been found to have a especially good binding efficiency. Among polyamides, polypeptides are especially preferred.
Non-Polymeric Binder Characteristics
The particles may be bound to the fibers by a non-polymeric organic binder selected from a predetermined group of binders that each have a volatility less than water. Again, these binders are applied on-line during the manufacture of the fibrous sheet or web. The vapor pressure of the binder may, for example, be less than 10 mm Hg at 25.degree. C., and more preferably less than 1 mm Hg at 25.degree. C. The non-polymeric binder has a functional group that forms hydrogen bonds or coordinate covalent bonds with the particles. In accordance with the present invention, the predetermined group of non-polymeric binders may include a functionality such as an alcohol, a carboxylic acid, an amino acid, an amide, or an amine, wherein each binder includes at least two such functionalities, and the two functionalities are the same or different. A requirement for the non-polymeric binder is that it have a plurality of functional groups that are capable of hydrogen bonding, or at least one group that can hydrogen bond and at least one group that can form coordinate covalent bonds. As used herein, the term "non-polymeric" refers to a monomer, dimer, trimer, tetramer, and oligomers, although some particular non-polymeric binders are monomeric and dimeric, preferably monomeric.
Particularly preferred non-polymeric organic binders are capable of forming five or six membered rings with a functional group on the surface of the particle. An example of such a binder is an amine or amino acid (for example, a primary amine or an amino acid such as glycine) which forms six membered rings by forming hydrogen bonds: ##STR4##
A six membered ring is also formed by the hydroxyl groups of carboxylic acids, alcohols, and amino acids. ##STR5##
A five membered ring can be formed by the binder and the functionality on the surface of the particle, for example ##STR6## wherein the particle is SAP and the binder is an alcohol, such as a polyol with hydroxyl groups on adjacent carbons, for example 2,3-butanediol.
Other alcohols that do not form a five membered ring can also be used, for example alcohols that do not have hydroxyl groups on adjacent carbons. Examples of suitable alcohols include primary, secondary or tertiary alcohols.
Amino alcohol binders are alcohols that contain an amino group (--NR.sub.2), and include binders such as ethanolamine (2-aminoethanol), diglycolamine (2-(2-aminoethoxy)ethanol)). Non-polymeric polycarboxylic acids contain more than one carboxylic acid functional group, and include such binders as citric acid, propane tricarboxylic acid, maleic acid, butanetetracarboxylic acid, cyclopentanetetracarboxylic acid, benzene tetracarboxylic acid and tartaric acid. A polyol is an alcohol that contains a plurality of hydroxyl groups, and includes diols such as the glycols (dihydric alcohols) ethylene glycol, propylene glycol and trimethylene glycol; triols such as glycerin (1,2,3-propanetriol); and polyhydroxy or polycarboxylic acid compounds such as tartaric acid or ascorbic acid (vitamin C): ##STR7## Hydroxy acid binders are acids that contain a hydroxyl group, and include hydroxyacetic acid (CH.sub.2 OHCOOH) and lactic, tartaric, ascorbic, citric, and salicylic acid. Amino acid binders include any amino acid, such as glycine, alanine, valine, serine, threonine, cysteine, glutamic acid, lysine, or .beta. alanine. Non-polymeric polyamide binders are small molecules (for example, monomers or dimers) that have more than one amide group, such as oxamide, urea and biuret. Similarly, a non-polymeric polyamine binder is a non-polymeric molecule that has more than one amino group, such as ethylene diamine, EDTA or the amino acids asparagine and glutamine.
Each of the non-polymeric binders disclosed above is capable of forming hydrogen bonds because it has a functional group that contains an oxygen or nitrogen, or has oxygen or nitrogen containing groups that include a hydrogen. The amino alcohol, amino acid, carboxylic acid, alcohol and hydroxy acid all have a hydroxyl group in which a hydrogen is bound to an electronegative oxygen, creating a dipole that leaves the hydrogen partially positively charged. The amino alcohol, amino acid, amide and amine all have an NR group in which a hydrogen may be bound to an electronegative nitrogen that also leaves the hydrogen partially positively charged. The partially positively charged hydrogen in both cases then can interact with an oxygen or nitrogen on the particle or fiber that adheres the binder to the particle and fiber. The polycarboxylic acid, hydroxy acid, amino acid and amide also have a carboxyl group with an electronegative oxygen that can interact with hydrogen atoms in the particles and fibers. Similarly, electronegative atoms (such as oxygen or nitrogen) on the fiber or particle can interact with hydrogen atoms on the binder that have positive dipoles, and partially positive hydrogen atoms on the fiber or particle can interact with eleotronegative atoms on the binder.
Several hydrogen bonding interactions of two of the binders (glycine and 1,3-propanediol) with cellulose are shown below: ##STR8##
The hydrogen bonding interactions are shown as dotted lines. One such interaction is shown between the nitrogen of glycine and a hydrogen of an OH on cellulose. A hydrogen bond with glycine is also shown between an oxygen of the OH on glycine and the hydroxy hydrogen of an alcohol sidechain on cellulose. Hydrogen bonding interactions of the 1,3-propanediol are shown in dotted lines between an oxygen on an OH group of the binder and a hydrogen of an OH group on the cellulose molecule. Another hydrogen bond is also shown between a hydrogen on an OH group of the glycol binder and an oxygen in an alcohol sidechain of the cellulose.
Alternatively, the oxygen or nitrogen on the binder has an unbound pair of electrons that can be donated to an empty orbital in the particle to form a coordinate covalent bond. The free pair of electrons on the oxygen or nitrogen can be donated to the empty p, d or f orbital of a particle (for example a boron containing particle) to form a coordinate covalent bond that adheres the particle to the binder. The fibers themselves do not normally contain functional groups that can form coordinate covalent bonds with the binders, but hydrogen bonding interactions allow the binder to adhere to the fiber. Cellulosic and synthetic fibers, for example, contain hydroxyl, carboxyl and ester groups that will hydrogen bond with the hydroxyl, carboxylic acid, amide or amine groups of the binder. Non-cellulosic or non-synthetic fibers that have these functionalities can also be used, for example silk, which has an amide linkage. Hence the binder will adhere the particle with a coordinate covalent bond and the fiber with a hydrogen bond.
In some preferred embodiments, the binder is bound to both the fibers and the particle by hydrogen bonds. A polyol binder, for example, can be used to bind polyacrylate hydrogel particles to cellulosic fibers. The hydroxyl groups on the polyol binder participate in hydrogen bonding interactions with the hydroxyl groups on the cellulose fibers and the carboxyl groups on the polyacrylate hydrogel. Hence the binder will adhere both the particle and fiber with hydrogen bonds. These hydrogen bonds provide excellent binding efficiency and diminish separation of bound particles from the fibers.
A structural drawing is shown below in which citric acid, vitamin C and urea adhere polyacrylate particles to cellulose with hydrogen bonds. Some of the possible hydrogen bonding interactions are shown as dashed lines. ##STR9##
Particularly efficient hydrogen bonding binders include those with carboxyl groups, such as ascorbic acid, or amide groups, such as urea. Hydroxyl groups are also very efficient binders. Amine and ether functionalities are less efficient binders.
Binders have functional groups that may be selected independently or in combination from the group consisting of a carboxylic acid, an alcohol, an amide and an amine, wherein the binder has at least two of these functional groups, and each of the functional groups can be the same (for example, a polyol, polycarboxylic and polyamine or polyamide) or different (for example, an amino alcohol, hydroxyamide, carboxyamide, or amino acid). Functional groups may also be selected independently or in combination from the group consisting of a carboxylic acid alone; a carboxylic acid and an alcohol; a carboxylic acid, an alcohol and an amide; a carboxylic acid, an alcohol, an amide and an amine; an alcohol alone; an alcohol and an amide; an alcohol, an amide and an amine; an amide alone; an amide and an amine; and an amine alone.
Preferred functional groups for the non-polymeric binders may be selected independently or in combination from the group consisting of an amino alcohol, a polycarboxylic acid, a polyol, a hydroxy acid, an amino acid, an amide, and a polyamine. Other preferred groups of binders include an amino alcohol alone, an amino alcohol and a polycarboxylic acid, an amino alcohol, a polycarboxylic acid and a polyol; an amino alcohol, a polycarboxylic acid, a polyol and a hydroxy acid; an amino alcohol, a polycarboxylic acid, a polyol, a hydroxy acid and an amino acid; an amino alcohol, a polycarboxylic acid, a polyol, a hydroxy acid, an amino acid and an amide; a polycarboxylic acid and a polyol; a polycarboxylic acid, a polyol and a hydroxy acid; a polycarboxylic acid, a polyol, a hydroxy acid, and an amino acid; a polycarboxylic acid, a polyol, a hydroxy acid, an amino acid and an amide; a polycarboxylic acid, a polyol, a hydroxy acid, an amino acid, an amide and a polyamine; a hydroxy acid and an amino acid; a hydroxy acid, amino acid and amide; a hydroxy acid, amino acid, amide and polyamine; an amino acid and an amide; an amino acid, amide and a polyamine; an amide and a polyamine; an amino alcohol alone, a polycarboxylic acid alone, a polyol alone, a hydroxy acid alone, an amino acid alone, an amide alone and a polyamine alone.
More specifically, the functionalities of the non-polymeric binder may be selected from the group of glycerin (a polyol), ascorbic acid (a polycarboxylic acid and a hydroxy acid), urea (a polyamide), glycine (an amino acid), pentaerythritol (a polyol), a monosaccharide, a disaccharide (a polyhydric alcohol), as well as citric acid, tartaric acid, dipropylene glycol, and urea derivatives such as DMDHEU. Suitable subgroupings of these binders include glycerin alone; glycerin and ascorbic acid; glycerin, ascorbic acid and urea; glycerin, ascorbic acid, urea and glycine; glycerin, ascorbic acid, urea, glycine and pentaerythritol; glycine, ascorbic acid, urea, glycine, pentaerythritol and a monosaccharide; glycerin, ascorbic acid, urea, glycine, pentaerythritol, a monosaccharide and a disaccharide; ascorbic acid alone; ascorbic acid and urea; ascorbic acid, urea and glycine; ascorbic acid, urea, glycine and pentaerythritol; ascorbic acid, urea, glycine, pentaerythritol and a monosaccharide; ascorbic acid, urea, glycine, pentaerythritol, monosaccharide and a disaccharide; urea alone; urea and glycine; urea, glycine and pentaerythritol; urea, qlycine, pentaerythritol and a monosaccharide; urea, glycine, pentaerythritol, a monosaccharide and a disaccharide; glycine alone; glycine and pentaerythritol; glycine, pentaerythritol and a monosaccharide; glycine, pentaerythritol, a monosaccharide and a disaccharide; pentaerythritol alone; pentaerythritol and a monosaccharide; pentaerythritol, a monosaccharide and a disaccharide; a monosaccharide alone; a monosaccharide and a disaccharide; and a disaccharide alone.
Process Advantages
The binders of the present invention also provide numerous process advantages. Binding of particles to the fibers can occur, for example, without external application of heat. Hence particle binding may occur at ambient temperature if desired. This aspect of the present invention is therefore distinct from prior art crosslinking processes in which elevated temperatures are required to covalently crosslink cellulose groups to one another. Moreover, the binders of the present invention have the advantage of being reactivatable by addition of a liquid solvent such as water. Hence, a liquid binder (which would include a solution of a solid or liquid binder, or a binder that has a melting point below room temperature) can be applied to a cellulose mat on the pulp sheet manufacturing line 10 (FIG. 1) in the absence of the particles to be bound and the binder dried, for example, until it reaches an equilibrium moisture content with the moisture in the ambient air. Thereafter, at a remote location or less preferably on line, the binder may be activated to adhere the selected particles to the fibers. Alternatively, the binder can be applied as a solid, for example as particles or a powder e.g., at the user's plant). At a later stage of processing, water or another liquid is added to those portions of a mat containing binder and fibers where particulate binding is desired. The particles may then be added to the mat and adhered to fibers of those portions of the mat that have been moistened. Alternatively, the particles may be added to the mat prior to activation of the binder.
The binders may be liquids at room temperature (such as glycerin), or liquid solutions of binders that are solids at room temperature (for example, an aqueous solution of glycine), or liquid hot melts of solid binders. Solid binders may be added to fibers in particulate form, for example, by sprinkling binder particles on the fibers.
The binding reaction of the present invention can occur across a broad range of pH without requiring a catalyst. A suitable pH range without a catalyst is 1-14, but preferred ranges are 5-8 or 6-8 because such neutral pH ranges will produce fibrous products (such as cellulose products) that are less prone to damage by acid hydrolysis.
The moisture content of the fibers during the binding reaction is 0.5-50%, suitably 5-40%, and most preferably 5-20% water by weight of the fibers, binder and particle. A moisture content greater than 20%, more preferably greater than 30%, or in the range of 20-50%, more preferably 30-50%, interferes with the formation of covalent bonds in the production of high bulk fibers. Particles may be added to the fibers (e.g., blended with fibers in fiberizer 70 or during air laying) such that the particles are distributed throughout a fibrous product without being confined to a surface of the product. The particles can be distributed throughout the depth of a fiber product or in varying concentrations throughout the product, such as a mat or web.
The binder is suitably present in the treated fibers in an amount of at least 3 percent and no more than 80 percent by weight of the fibers, particles, and binder ("percent by weight"). In especially preferred embodiments, the binder is present in an amount of 5-30 percent by weight. Below about 3 percent, an insufficient amount of binder is present to achieve adequate binding, while using excessive amounts of binder can introduce unnecessary expense into the binding process. High percentages of binder can also cause processing problems because the binder material transfers to equipment surfaces.
Thermoplastic binders may also be used to help bind fibers to each other and particles to fibers. The binder that has the hydrogen bonding or coordinate covalent bonding functionalities may itself be thermoplastic. Some of the polymeric binders used in the present invention have the advantage of being thermoplastic solids. Hence fibers treated in accordance with the present invention can be thermobonded by elevating the fiber temperature above the melting temperature of the binder to melt the thermoplastic binder and thermoplastically bind the fibers to each other and the fibers to the particles. Alternatively, an auxiliary or second binder can be applied to the fibers as a solid or liquid at room temperature, and the temperature of the second binder elevated above its melting point to thermobond the fibers and particles. The auxiliary binder may be applied to the fibers either before or after the primary binder is applied on the pulp sheet manufacturing line, but before thermobonding.
The binders used in the present invention may be used with fibers that have substantial intrafiber covalent crosslinks (such as HBA available from Weyerhaeuser) or fibers which are substantially free of intrafiber covalent crosslinking. Examples of individualized intrafiber crosslinked fibers are seen in European Patent Applications 440 472 A1 and 427 317 A2, which produce products that those publications describe as being substantially free of interfiber bonds. Those fibers have been individualized and then cured in the presence of a crosslinking material at an elevated temperature to produce high bulk fibers having intrafiber covalent crosslinks. The fibers of the present invention do not need to be processed as in those European applications to eliminate interfiber bonds. Binders of the present invention can therefore be used with natural fibers that have substantial interfiber bonding, which is defined as fibers that have not been processed as in European Applications 440 472 A1 and 427 317 A2 to substantially eliminate interfiber bonds. Cellulose fibers that have not been so processed are substantially free of intrafiber bonds.
Although intrafiber covalent crosslinking is not required for the present invention, such high bulk fibers can be used with the binders disclosed herein. However, although they could be, these fibers are not typically blended with other fibers in a slurry in a headbox of a wet laid sheet manufacturing line. Fibers that have high bulk from intrafiber covalent crosslinks are prepared by individualizing the fibers and curing them at an elevated temperature (above 150.degree. C.) in the presence of a crosslinking material such as citric acid. Initial application of the binder on such high bulk fibers may occur after the curing step and on the wet laid sheet manufacturing line, particularly if the binder is capable of functioning as a crosslinking material. The binders disclosed herein that can also crosslink are polyols, polycarboxylic acids, and polyamines (both polymeric and nonpolymeric binders that have more than one amine group); none of the other specifically disclosed binders are known to form covalent, intrafiber ester bonds.
Binding is performed under conditions that favor formation of hydrogen bonds or coordinate covalent bonds, and discourage formation of covalent bonds. Conditions that favor covalent bonds are those disclosed in U.S. Pat. No. 4,412,036 and U.S. Pat. No. 4,467,012 wherein particle and binder would be laminated between tissue layers under high temperature and pressure to form laminated adherent tissue layers. That patent teaches that minimal adhesion occurs at 200 pli (pounds per linear inch, as in a calendar press) if no external heat is supplied, but adhesion improves as the reaction temperature increases. Improved adhesion of the tissue layers occurs because of enhanced covalent bonding as the temperature increases.
Conditions that favor covalent bond formation are also shown in European Patent Applications 440 472 A1; 427 317 A2; 427 316 A2; and 429 112 A2. These European publications use polycarboxylic acid crosslinkers, and require elevated temperatures (for example above 145.degree. C.) and acidic conditions (pH less than 7) to promote formation of intrafiber covalent ester bonds and inhibit reversion of the ester bonds. The present invention, in contrast, can form hydrogen or coordinate covalent bonds below 145.degree. C., below 100.degree. C., and even at room temperature. The binders of the present invention can also bind particles to fibers under neutral or alkaline conditions, i.e., at a pH above 7, but preferably at a pH of 5-8 or 7-8.
The intrafiber covalent bond forming processes described in the above European publications require formation of an anhydride that then reacts with a hydroxy group on cellulose to form a covalent ester bond. The presence of more than about 15% water by weight in the fibers interferes with formation of the anhydride and inhibits covalent bond formation. Hence, in processes that use binders that are also crosslinkers (polycarboxylic acid, polyols and polyamines) as binders in the present invention, the fibers should contain at least 15% water by weight if the particles and binder are present in the fibers when curing occurs. The water inhibits covalent bond formation, and prevents all of the binder from being used to form covalent intrafiber crosslinks. Hence, some of the binder remains available to form the non-covalent bonds with the particles and produce ease of densification in fiber products made by the process of the present invention.
The present invention, in contrast, produces a product under conditions that favor formation of hydrogen or coordinate covalent bonds. Hence, the particles can be bound to the fibers in the absence of the external application of heat or pressure. Particles may also be bound and the resulting fiber product densified, for example at less than 200 pli (about 8000 psi), or less than 100 pli (about 4000 psi), in the absence of external application of heat to produce a product in which a substantial portion of the particles are bound by non-covalent bonds (hydrogen or coordinate covalent bonds). A substantial portion of particles bound by non-covalent bonds means at least half of the particles are bound by other than covalent bonds, for example by hydrogen or coordinate covalent bonds.
In yet other examples, particles may be bound in the absence of external application of pressure, but at elevated temperatures.
In particularly preferred embodiments, the particles are substantially entirely bound to the fibers non-covalently.
Binding Examples for Polymeric Binders
Several examples are given below illustrating use of the polymeric binders of the present invention to attach superabsorbent particles to southern bleached kraft pulp.
EXAMPLE I
Southern bleached kraft fibers may be slurried in a headbox and delivered to a Fourdrinier wire to form a sheet. Following drying of the resulting mat to a 10 w/w % moisture content, a polyethylene glycol binder (100 grams/100 ml deionized water average molecular weight=4,600; supplied by Union Carbide Corporation of Danbury, Conn.) may be sprayed onto the mat as a binder. The application rate being 100 grams polyethylene glycol per 321 grams (dry weight) fibers. Thereafter, the web or mat is dried and then, at a separate location, starch graft polyacrylate hydrogel fines (IM 1000F; supplied by Hoechst-Celanese of Portsmouth, Va.) may be blended with the binder coated fibers. These superabsorbent particles are added at the rate of 435 grams per 321 grams of fibers. The mixed fiber and particle mass may then be airlaid and thermobonded at 140.degree. C. for one minute to produce a web containing 40% superabsorbent particles (SAP) attached to the individualized fibers. The polyethylene glycol has a low melting point, hence raising the temperature to 140.degree. C. melts the binder and allows it to flow over the fibers and particles to enhance hydrogen bonding interactions and provide mechanical encapsulation that further binds the fibers and particles. This is an example of activating a solid binder by heating it, without liquid addition.
EXAMPLE II
The same procedure as in Example I, except without the thermobonding step, may be repeated utilizing other binders, such as 154 grams of a 65% solution of polyacrylic acid (average molecular weight=2,000; supplied by Aldrich Chemical Company of Milwaukee, Wis.) diluted with 100 ml of deionized water per 321 grams (dry weight) wood pulp. Other hydrogels may be used, such as 435 grams of polyacrylate hydrogel (FAVOR 800 supplied by Stockhausen of Greensboro, N.C.) per 321 grams pulp.
EXAMPLE III
As another example, using the process of Example I without the thermobonding step, the binder may be 100 grams of polyglycine (molecular weight=5,000-5,000; supplied as a dry powder by Sigma Chemical Company of St. Louis, Miss.) diluted with 100 ml of deionized water is sprayed per 321 grams (dry weight) wood pulp. The resulting product may be dried and fed into a hammermill with a three-eights inch round hole screen. Then 435 grams of starch graft polyacrylate hydrogel fines (IM 1000F; supplied by Hoechst-Celanese of Portsmouth, Va.) per 321 grams (dry weight) wood pulp is added and mixed. The mixture is shunted to an airlay line to produce a web containing 40% SAP attached to the fibers.
EXAMPLE IV
As yet another example, prepared in accordance with Example I, but without the thermobonding step, the binder may be 200 grams of a 50% solution of polyethyleneimine (molecular weight=50,000-100,000; supplied by ICN Biomedicals, Inc. of Costa Mesa, Calif.), or polyvinyl pyridine per 321 grams (dry weight) wood pulp. Then 435 grams of starch graft polyacrylate hydrogel fines (IM 1000F; supplied by Hoechst-Celanese of Portsmouth, Va.) is added per 321 grams (dry weight) fibers and mixed. The resulting product is dried and fed into a hammermill with a three-eighths inch round hole screen and shunted to an airlay line to produce a web containing 40% SAP attached to the fibers.
The classes of polymeric binders that encompass those described in Examples I-IV are especially preferred over other multiple hydrogen bonding functionality polymers for a number of reasons. One important reason is that their functionalities produce very strong, effective hydrogen bonding. Other important reasons include their relative lack of reactivity (as compared with polyaldehydes or polyisocyanates) and their low toxicity (again, as compared with polyaldehydes or polyisocyanates).
EXAMPLE V
As previously described, repetition of a hydrogen bonding group on each repeating unit of a polymer has been found to produce a binder that provides superior binding of particles to fibers, as compared to polymeric binders in which the hydrogen bonding functionality is not present on all the repeating units. This example shows the difference in binding efficiency between a 20% carboxylated polymer and a 100% carboxylated polymer. Bound samples have been prepared by air entraining 321 grams of southern bleached kraft fluff in a blender-like mixing device with the binder being sprayed onto the entrained fluff, using a 20% carboxylated ethylene acrylic acid copolymer and a 100% carboxylated PAA. 435 grams of IM 1000F superabsorbent particles were added to the binder treated fibers while the binder was wet and mixed. The samples were removed and dried overnight in a fume hood. The resulting samples were fed respectively to a Fitz hammermill with a three-eights inch round hole screen and shunted to a small M & J airlay line to produce webs having 40% SAP attached to the fibers. A sample containing each binder was subjected to the same mechanical agitation (to simulate machine processing required to make a web), screened through a descending series of sieves to remove unattached SAP, and subjected to an absorbent capacity test (less attached SAP would result in a lower absorbent capacity). The result of the test was measured by weighing the unabsorbed liquid (0.9% saline) from a standardized insult, hence a lower number indicates more liquid absorbed or higher absorbent capacity.
In testing wood pulp fiber webs made in this manner with binder applied to dried fibers at a location remote from a pulp sheet manufacturing line, a sample of the 20% carboxylated polymer (15% of the total mix) gave a beaker test result of 19.5 grams. A similar sample of polypropylene glycol gave a result of about 20.0 grams. However, the hydrogen bonding functionality of PPG is not as efficient as the carboxyl functionality of PAA. A similar sample of polyacrylic acid (100% carboxyl functionality of PAA) gave a result of 11.3 grams. A comparison of the 20% and 100% carboxylated polymers shows a substantial increase in SAP binding efficiency, as measured by an increase in absorbency of the product. These same results are expected when the binders are applied on a pulp sheet manufacturing line with particles added at a remote location from the line.
Non-Polymeric Binding Examples
Several examples are given below to illustrate the use of several non-polymeric organic binders of the present invention to attach superabsorbent particles to southern bleached kraft pulp.
EXAMPLE VI
A mat of southern bleached kraft fluff on a pulp manufacturing line may be dried and sprayed with glycerin at location 56 (FIG. 1) (96%, USP; supplied by Dow Chemical Co. of Midland, Mich.) to provide a pulp sheet with 30% binder to the weight of binder and fibers. Then starch graft polyacrylate hydrogel fines (IM 1000F; supplied by Hoechst-Celanese of Portsmouth, VA) may be added to a fiberizer at a remote location (FIG. 2) and mixed with the fluff containing the binder. Although variable, the particles may be added in an amount to comprise 50% by weight particles to the total weight of the particles, fibers and binder. The fiberizer mechanically activates the binder to cause the adherence of the particles to the fibers. The material may then be fed into a Danweb airlay machine to form a web containing bound 50% IM 1000F that would be substantially immobile in the web because the particles are bound to the fibers instead of mechanically entrapped by the matrix.
EXAMPLE VII
A southern bleached kraft fluff pulp sheet on a pulp manufacturing line may be sprayed with a 50% solution of glycine at location 54 in FIG. 1, in this case midway through the drying stage 30, (supplied as a dry powder by Aldrich of Milwaukee, Wis.) and dried on the line. The binder containing sheet may be shipped to a remote location and moisture added to provide, for example, a 17-21% moisture content. This sheet may then be fed into a hammermill. Starch graft polyacrylate hydrogel fines (IM 1000F; supplied by Hoechst-Celanese of Portsmouth, Va.) may simultaneously be added to the mill by a screw feed device, mixed with the fluff, shunted to an airlay forming machine and airlaid to form a web. The resulting web would contain 20% SAP attached to the fibers substantially uniformly throughout the web without being confined to the surface of the web.
EXAMPLE VIII
A southern bleached kraft fluff pulp sheet on a pulp manufacturing line may be sprinkled with solid particulate pentaerythritol (supplied by Aldrich of Milwaukee, Wis.) at location 52 (FIG. 1). The sheet may be moistened to a moisture content of, for example, 17-21% and may be fed into a hammermill. The sheet is dried online and shipped to a remote location. Starch graft polyacrylate hydrogel fines (IM 1000F; supplied by Hoechst-Celanese of Portsmouth, Va.) may simultaneously be added to the mill by a screw feed device and mixed with the fluff. The resulting fibers with adhered particulate may be shunted to an airlay forming machine and airlaid to form a web. The resulting web would contain 20% SAP attached to the fibers.
EXAMPLE IX
A southern bleached kraft fluff pulp sheet on a pulp manufacturing line may be sprayed with a 50% solution of lactose at location 54 and dried. The binder treated sheet may then be fed into a hammermill at a remote location. The sheet may be defiberized and the resulting fibers shunted to an airlay line, and airlaid into a web. As the web emerges, target zones of the web may then be misted with water to raise the moisture content to 17-21%. Five gram aliquots of starch graft polyacrylate hydrogel fines (IM 1000F; supplied by Hoechst-Celanese of Portsmouth, Va.) may then be sifted onto the target zones. The resulting web would have target zones with 5 grams of SAP attached to the fibers of each target zone. Portions of the web that were not targeted for application of the reactivating liquid (water) would not adhere the particles well. This is an example of activating the binder in a target zone at a remote location from the pulp sheet manufacturing line so that SAP primarily adheres to the target areas where the binder is activated. Target zone application of SAP can be advantageous because it reduces the cost of the product to provide SAP only in areas of a product where the SAP is needed, for example, the crotch area of a diaper. Placement of SAP in the area where a liquid insult is expected also decreases the necessity for wicking liquid to a SAP impregnated region. This is an advantage because the requirement for wicking can increase liquid leakage in an absorbent product such as a diaper.
EXAMPLE X
A southern bleached kraft sheet on a pulp manufacturing line may be sprayed with glycerin (96%, USP; supplied by Dow of Midland, Mich.) at location 56 (FIG. 1). Abscents (an odor absorbing zeolite supplied by UOP of Tarrytown, N.Y.) may be added to the sheet and mixed in a fiberizing device at a remote location (see FIG. 2) to provide a homogenous mixture. The material may then be airlaid into a web which would be of fibers with adhered Abscents. The particulate retention would compare favorably to particulate retention with latex binders under similar conditions.
Product Characteristics
The following examples illustrate how SAP retention, pad integrity, wettability, bulk and liquid retention are affected by applying the glycerin binder in accordance with the present invention. In each of the following Examples XI-XVIII, the binder was applied to dried fibers in a test lab separate from a pulp sheet manufacturing line. However, the results are expected to be the same if the binder were applied on the pulp sheet manufacturing line with the particles being added at another location.
EXAMPLE XI
Superabsorbent particles were bound to cellulose fibers with a glycerin binder. More specifically, 321 grams of dried NB 416 fluff from Weyerhaeuser Company was air entrained in a blender like mixing device and sprayed with 100 grams of the glycerin in 100 ml of deionized water. Then 435 grams of superabsorbent particles were mixed with the fibers and binder and allowed to air dry overnight in a fume hood. For purposes of comparison, superabsorbent particles were bound to a separate sample of cellulose fibers using a polyvinyl acetate (PVAc) binder that was about 3% carboxylated, that is only about 3% of the PVA monomers were carboxylated. Binding was performed as above in this Example XI, but PVAc was substituted for glycerin. A 100 gram sample of the glycerin and PVAc treated fluff with attached SAP was fed into a fan that was connected by a hose to a small cyclone mounted on top of a material containment box. This was done in an effort to simulate forces of mechanical agitation the fluff would encounter during the airlay process. After collection in the material containment device, fiber with attached SAP was removed and weighed. A five gram sample of the fiber with attached SAP was then placed in a column of sieves with decreasing mesh sizes and subjected to a shaking and thumping action for ten minutes in order to further dislodge any poorly attached SAP. Unattached or poorly attached SAP sifted through screens having a range of 5-60 mesh, while the fiber with well attached SAP remained on the 5 mesh screen.
A 2.00 gram sample of the fibers that remained near the top of the sieve column was then placed in a 75 ml sample of 0.9% saline for exactly one minute. After that minute, the liquid that was not absorbed was poured off into a separate, tared beaker and weighed. The relative amounts of liquid absorbed is indicative of the amounts of SAP bound to the fiber. Fiber retaining higher amounts of SAP tend to absorb more water and give a smaller amount of liquid not absorbed.
These results are shown in Table I:
Table I illustrates that the glycerin binder provides a product that has an absorbency increase of 400% compared to the PVAc binder. A substantial portion of this improvement is believed to be due to better adhesion between the fibers and SAP, such that the particles are not dislodged from the fibers.
EXAMPLE XII
Pad integrity was compared in fibrous products that used no binder and a glycerin binder at 7% and 11% by weight. Each of these binders was used to bind SAP to fibers as in Example XI, and properties of the pad were measured and are shown in Table II:
The glycerin binder in this example produced a product that had a higher tensile index than an untreated product. The increased tensile strength was especially enhanced in the densified product.
EXAMPLE XIII
The effect of binders on the wettability and bulk of fibers was tested using the following fibers: NB-316 (a standard southern bleached kraft pulp with no binder); GNB 25% (a standard southern bleached kraft pulp with 25% glycerin (entrained and sprayed); HBA (a high bulk intrafiber crosslinked fiber available from the Weyerhaeuser Company that contains intrafiber covalent crosslinks); and GHBA (HBA fibers treated with a glycerin binder) in amounts of 12.5% and 25% by weight. Results are given in Tables III and IV.
FAQ time was determined by airlaying a specific quantity (4.00 grams) of the fluff to be tested into a clear plastic tube that was fitted with a screen at one end. The fluff and tube were then placed into a well in the test device and a metal plunger was lowered onto the fluff and the pad's bulk calculated. Water then flowed from underneath the pad, passed through the screen and wicked up through the pad. Absorbency time was measured from when the liquid makes contact with the bottom screen until the water completes an electrical circuit by contacting the foot of the plunger resting on top of the pad. Lower absorbency times indicate better absorbency. Since the absorption of the liquid by the pad was accompanied with some collapse of the pad's structure, the bulk of the wet pad was ten recalculated. The amount of liquid absorbed was then measured and a gram per gram capacity for the material was calculated.
Table III gives FAQ time as a measure of wettability. A lower FAQ time indicates a product that is more absorbent and wicks faster. Table IV gives wet bulk of fibers and the adjusted bulk of the fibers. The adjusted bulk is a calculated number obtained by dividing the bulk by the actual percent of pulp in the sample.
The low FAQ times (Table III) in the glycerin treated fibers (GNB, GHBA) show that wettability is as good as the untreated fiber (NB-316). The GHBA 25% had significantly better wettability than untreated HBA. Bulk of glycerin treated fibers (Table IV) was not significantly decreased or changed at all levels of glycerin binder on a fiber to fiber comparison basis.
EXAMPLE XIV
Liquid retention of bound fibers was determined and compared to fibers in which no binder was added. NB-316 is a pulp sheet available from Weyerhaeuser Company in which no binder is used. HBA is described in Example X. HBA/Gly SAP was an HBA fiber that was bound with glycerin (12% binder, 48% fiber) and which contained 40% SAP particles. NB-316/Gly SAP is NB-316 fibers to which glycerin and SAP fibers were added.
The procedure for determining liquid retention was to weigh triplicate small portions (near 0.2 grams) of samples to the nearest 0.0001 gram and then heat seal the small portions inside an envelope of a heat sealable nonwoven tea bag. The samples were then immersed in an excess of 0.9% saline for thirty minutes, then drained by suspending them from a clip for fifteen minutes. The samples were weighed to determine the amount of liquid absorbed. The grams of liquid absorbed per gram of sample was calculated and the samples were spun in a centrifuge for one minute. The samples were then reweighed and a percent liquid retention was calculated.
Results are shown in the following Table V:
The results in Table V illustrate that fibers that have SAP bound to them retain liquid well, while fibers without SAP retain liquid poorly. The glycerin binders provided excellent adherence of SAP to the fibers.
EXAMPLE XV
Auxiliary Binder
As previously described, an auxiliary binder can be used in addition to the non-polymeric binders of the present invention. A 321 gram amount of a southern bleached kraft fiber (NB-416, supplied by Weyerhaeuser) was air entrained in a blenderlike mixing device and sprayed with 212.8 grams of a polyvinylacetate latex (PN-3666H, supplied by H B Fuller of Minneapolis, Minn.). While still mixing, 438 grams of a water swellable polyacrylate hydrogel (Favorsab 800, supplied by Stockhausen of Greensboro, N.C.) was added and the resulting mixture was then sprayed with 100 grams of a 50% solution of glycerin (supplied by Dow of Midland, Mich.). The blender was then stopped and the mixture was vacuumed from the blender and placed in a fume hood to air dry overnight. The dried product was then airlaid into a 6" diameter pad in a laboratory padformer, pressed to a density of approximately 0.077 g/cc, and thermobonded at 140.degree. C. for thirty seconds. The resulting pads had 40% bound SAP and improved tensile strength as compared to untreated fluff with SAP and as also compared to binder treated fluff with SAP without the auxiliary binder.
Tensile strength was highest with polyvinylacetate alone, followed by a combination of polyvinylacetate and glycerin, then glycerin alone. Lowest tensile strength was seen with no binder at all.
EXAMPLE XVI
Binders of the present invention may be used to bind particles to pulp fibers that contain synthetic thermobonding fibers. In this example, KittyHawk pulp (available from Weyerhaeuser Company) is a mixture of NB316 southern bleached kraft and 22% polyethylene thermoplastic binder fibers. The KittyHawk pulp may be used to produce a pulp web, to which binder is added with SAP then being bound to the kraft fibers as described in Example III. Webs with these fibers with adhered SAP may then be passed through a thermobonder to soften the polyethylene fibers and fuse the fibers of the web to each other to increase web strength.
EXAMPLE XVII
Solid sample .sup.13 C NMR spectra were obtained on cellulose fibers treated with ascorbic acid to bind SAP to the fibers. An NMR spectra was also obtained on L-ascorbic acid. In both cases, separate spectra were acquired using recovery delays of 1 sec and 5 sec between acquisitions.
The peaks in the treated fiber spectrum were assigned readily to the components: SAP polyacrylate carboxyl (185 ppm) and backbone (50-30 ppm) carbons; cellulose (106, 90, 84, 76, 73 and 66 ppm); and ascorbic acid ring carbons C-1, C-2 and C-3 (175, 119 and 156/153 ppm, respectively); the other ascorbic acid carbons are in the cellulose region, two of them being resolved at 69 and 61 ppm. The ascorbic acid carbon chemical shifts in this ternary mixture were essentially identical (.+-.0.2 ppm) to their values in pure ascorbic acid. This indicated that the ascorbic acid in the treated fibers had undergone no gross structural changes, such as total neutralization, oxidation or ring opening.
The signal-accumulation rates observed at the two different recovery delay times showed that the proton spins in pure ascorbic acid relaxed after excitation much more slowly than they did in the ternary mixture. As shown in the following table, slow relaxation yields higher signal strength at the long recovery delay relative to the short one. The fast proton spin-lattice relaxation in the coated fibers indicated that the ascorbic acid in this system is held more tightly in place (i.e., is less mobile) than in the bulk acid. The ascorbic acid is apparently held tightly by one or both of the other two components, cellulose and SAP, and not by other ascorbic acid molecules.
If the bonding were purely ionic, involving ascorbate ion and an acrylic acid unit in the SAP, then the NMR of the treated fibers would show the ascorbic acid in the salt form. NMR reference spectra were found of the acid and its salt in aqueous solution, and C-3 is seen to shift dramatically on ionization of its OH group: 156 ppm in the acid to 176 ppm in the salt. Thus, since the NMR spectrum of the ternary mixture contains the peaks at around 156 ppm, the ascorbic acid in this system is not ionized.
The infrared spectra, however, point to substantial disruption in the structure of the ring OH groups, comparing pure ascorbic acid with the treated fibers, with the ascorbic acid in the mixture resembling ascorbate salts in having some of the OH stretching bands missing.
Looking at acidities, ascorbic and polyacrylic acids have nearly identical pK.sub.a values (4.2 vs 5, respectively). They are both typical strong organic acids with weak conjugate bases. Thus, there is no compelling reason for one of these acids to be neutralized (ionized) by the conjugate base of the other acid. Rather, there should be a strong tendency for an ascorbic acid and an acrylate ion to share a hydrogen ion between them, resulting in a long hydrogen bond between partially ionic ascorbic and acrylic acid units. This sharing of hydrogen ions would certainly be reflected in the IR spectrum, yet satisfies the NMR data by not invoking full ionization of ascorbic acid. The spectroscopic data are fully consistent with a hydrogen bonding mechanism between ascorbic acid and an acrylate unit in the superabsorber.
EXAMPLE XVIII
Fibers With Superabsorber And Ascorbic Acid
Infrared Analysis
Infrared transmission spectra of the untreated NB316 pulp, the treated NB316 pulp, ascorbic acid, and the IM 100F superabsorber were prepared. Then, a subtraction spectrum representing the treated pulp minus the untreated control was obtained.
Examination of that subtraction spectrum indicated several infrared bands that were obviously associated with the ascorbic acid. They were evident at 1755, .about.1690 (shifted slightly from 1660-1670), 868, 821, and 756 wavenumbers (cm.sup.-1). However, several other bands that were prominent in the ascorbic acid spectrum were absent in that subtraction spectrum. They included the following: 3525, 3410, 3318, 1319, 1119, and 1026 cm.sup.-1.
The higher frequency bands (3300-3600 cm.sup.-1) in ascorbic acid are indicative of bonded OH groups. The infrared bands at 1319, 1119, and 1026 cm.sup.-1 may also be associated with OH vibrations. Consequently, the IR suggested that the subtraction spectrum reflected primarily a loss of the OH groups that were attached directly to the ring. A likely possibility is that the OH groups were replaced by sodium. The only other major band in the subtraction spectrum was located at 1589 cm.sup.-1. This was probably due to the superabsorber C.dbd.O which had shifted to a slightly higher frequency (from 1562 cm.sup.-1).
EXAMPLE XIX
Activation
The binders of the present invention have the advantage of being activatable by addition of liquid or by heating. "Activation" includes activating a previously inactive binder (e.g., by adding liquid to a solid) or reactivating a previously active binder (e.g., by adding liquid to a dried liquid binder) on the fibers. Hence, a liquid binder can be applied to a cellulose mat on the pulp sheet manufacturing line, in the absence of the particles to be bound. The binder is then dried or allowed to dry, for example until the binder and fiber reach an equilibrium moisture content with ambient air. Alternatively, the binder can be applied as a solid, for example, particles sprinkled onto a fiber mat on the pulp line. In this case, preferably the pulp sheet still contains sufficient moisture to adhere the particles of binder to the fibers. Also, the pulp sheet may have sufficient heat to adhere thermoplastic binder particles to the fibers. At a later stage of processing, the binder is activated, e.g. by using a liquid such as water. The particulates may then be added, and the binder secures the particulates to the fibers. This subsequent processing of the fibers to attach the particles can occur, for example, at a separate location from the location where the binder was applied to the fibers. Therefore, manufacturers of products can add particulates of interest (e.g., superabsorbent particles or fibers; antimicrobial particles, etc.) at the place of manufacture of the end products that incorporate the treated fibers. Also, more than one type of particulate material may be added, if desired.
It has also been found that some of the binders of the present invention can be reactivated by mechanical agitation. For example, glycerin binder may be applied to fibrous cellulose. The glycerin binder may be allowed to dry overnight, and the fibers then mechanically agitated in the presence of superabsorbent particles to reactivate the glycerin binder and bind the particles to the fibers. Mechanical agitation may take place, for example, in a defiberizer where a sheet or mat of glycerin treated cellulose fibers are defiberized while being intimately mixed with SAP that is bound to the fibers by the mechanical agitation.
Binder Activation Examples
Binder reactivation in the present invention allows binder to be added to fibers either before or after particles are added to the fibers. The binder is subsequently activated by addition of liquid, heat, or agitation, and particles are bound to the fibers. The particles may be added to the fibers either before binder activation, after binder activation, or simultaneous with activation. If SAP is to be added to cellulose fibers, for example, the binder may be applied to a pulp sheet during its manufacture with the pulp sheet being subsequently fiberized, for example at a user's plant. A liquid such as water may be added to the pulp before or after fiberization, and SAP may be added before or after water addition, or simultaneously with the water. If SAP is added after water addition, the SAP should be applied to the fibers prior to complete evaporation of the added water from the fibers.
Activation can be of all the fibers, or only portions of the fibers, such as target zones or portions of the mat where particulate binding is desired. The particles may then be added to the mat and adhered to the target zones of the mat which have been activated. In some embodiments, the binder is applied as a solid and heated during a later processing stage to activate the binder by softening it such that it binds the particles to the fibers. The particles may be added in a pattern corresponding to a desired distribution of particles in the fibrous material. Most commonly, however, activation is accomplished by moistening a targeted area of the product into which an inactive (dry or dried) binder has already been introduced.
In yet other embodiments, the binder is applied to the fiber mat and then activated by subsequently applying kinetic energy to the fibers. Neat polypropylene glycol (MW 2000) binder, for example, may be sprayed on the fiber mat and allowed to air dry. Desired particles may then be added to the fibers (e.g. at a user's plant) as the fibers are mechanically agitated in a blender or defiberizer to kinetically activate the binder and bind the particles to the fibers. For kinetic activation, the binder may be added as a liquid or a solid to the fibers. In the case of liquid addition, the liquid is allowed to air dry, and then reactivated by mechanically agitating the fibers and binder. In the case of solid binder addition, the binder is applied as a solid, and then moistened (for example, to a total fiber moisture content of about 7%) and then mechanically agitated.
Activation of the binder may be performed prior to adding the particles, subsequent to adding the partices, or simultaneously with addition of the particles. Once the binder is activated, it adheres a substantial portion of the particles to the fibers, wherein "a substantial portion" refers to about half of the particles present in the fibers, at least where the particles are not added in excess.
In embodiments in which the binder is applied to the fibers as a solid, the activating step can comprise applying a liquid to the fibers after the binder has been applied to the fibers.
The activating step is preferably performed after the curing step is complete, if a curing step is to be performed.
The following example will illustrate several specific applications of the activation process, and are not intended to limit the invention to the disclosed methods.
EXAMPLE XX
The method of Example I above could be modified such that the SAP is not added until after the web is heated to 140.degree. C. A solid polyethylene glycol/polypropylene glycol copolymer could be substituted for the PRG of Example I, and it would melt well below 140.degree. C., and in its liquid form bind the SAP to the fibers. The SAP could be applied randomly across the heated product, or applied specifically to a targeted zone of the product where enhanced absorbency is specifically desired.
EXAMPLE XXI
A southern kraft pulp sheet could be immersed or sprayed on the pulp sheet manufacturing line with a 65% solution of polyacrylic acid diluted with deionized water. The sheet may then be misted with water at a remote location to raise its moisture content to, for example, 17-20% as it is fed into a hammermill. Polyacrylate hydrogel particles of FAVOR 800 supplied by Stockhausen may simultaneously be added to the mill by a screw feed device, mixed with the fluff, shunted to an M & J airlay forming machine and airlaid to form a web containing bound SAP throughout the web, i.e., without being confined to a surface of the web. Mixing SAP throughout the fluff helps produce a product in which SAP is homogeneously or randomly distributed, which diminishes problems of gel blocking.
EXAMPLE XXII
A KittyHawk pulp sheet (from the Weyerhaeuser Co., containing 22% synthetic fiber) on a pulp sheet manufacturing line may be immersed into or sprayed with a 10% by weight solution of polyglycine. The sheet may then be fed into a hammermill at a remote location defiberized, shunted to an airlay line, and airlaid into a web. As the web emerges, circular target zones of the web may be misted with water from a spray bottle to raise the moisture content to 17-21% in the target zone. Five gram aliquots of starch graft polyacrylate hydrogel fines (IM 1000F; supplied by Hoechst-Celanese of Portsmouth, Va.) may be subsequently sifted onto the target zones to yield a web with SAP bound in target zones. The SAP does not form a confluent layer, but is instead present in particulate form on and below the surface of the web.
EXAMPLE XXIII
A southern bleached kraft fluff pulp sheet may be sprayed with a 50% solution of polyglycine and dried. The sheet may be fed to a hammermill with liquid added to bring the moisture content to 17-21%. Starch graft polyacrylate hydrogel fines (IM 10000F; supplied by Hoechst-Celanese of Portsmouth, Va.) may simultaneously be added to the mill by a screw feed device as the sheet is fed into the hammermill, mixed with the fluff, shunted to an airlay forming machine and airlaid to form a web. The fines would be intimately mixed with the fluff in the fibermill and bound to the fibers by the polyglycine binder to produce a web with particles distributed throughout its width, and not restricted to a superficial surface.
EXAMPLE XXIV
A southern bleached kraft pulp sheet on a pulp manufacturing line may be immersed into or sprayed with a 2% by mass solution of ascorbic acid (supplied as a dry powder by Aldrich Chemical Co. of Milwaukee, Wis.). The sheet may be dried and sufficient ascorbic acid may be added to provide 7% by weight ascorbic acid. The sheet may be misted with water at a remote location from the line to raise its moisture content to 17-20% as it is fed into a hammermill. Misting with water reactivates the binder prior to addition of superabsorbent particles (SAP). Starch graft polyacrylate hydrogel fines (IM 1000F supplied by Hoechst-Celanese of Portsmouth, Va.) may then be added as SAP to the hammermill by a screw feed device, mixed with the fluff, shunted to an airlay forming machine and airlaid to form a web. The resulting web would contain 20% SAP attached to the fibers by the binder.
EXAMPLE XXV
A KittyHawk pulp sheet on a pulp sheet manufacturing line may be immersed into or sprayed with a 10% by weight solution of urea (supplied by Aldrich of Milwaukee, Wis.). The sheet may be dried. Sufficient urea may be added to provide 30% by weight urea. The sheet may be fed (see FIG. 2) into a hammermill, defiberized, shunted to an airlay line, and airlaid into a web. As the web emerges, the binder in the dried web may be reactivated by misting target zones of the web with deionized water in a circular pattern from a sprayer to raise the moisture content of the web at the target zones to 17-21%. Five gram aliquots of polyacrylate hydrogel (FAVOR 800 supplied by Stockhausen of Greensboro, N.C.) may subsequently be sifted onto each reactivated target zone. The web that results would contain target zones with 5 grams of SAP attached to the fibers in each target zone. Alternative spray patterns could be provided by selecting spray heads or different control devices that mist different patterns.
Thermoplastic Binders
An auxiliary binder may also be used to help bind fibers to each other above the melting point of the auxiliary binder. The auxiliary binder may be a solid thermoplastic material that is applied to the fibers and softened by elevating the temperature during the binding step to above the softening temperature of the auxiliary binder. The auxiliary binder is thereby temporarily softened, rendered more fluid (which for purposes of convenience may be referred to as auxiliary binder melting) and subsequently resolidified as the temperature cools, which thermoplastically binds the fibers to each other, and the particles to the fibers. The auxiliary binder may also contain a hydrogen bonding functionality that hydrogen bonds the particles to the fiber. Examples of auxiliary binders that are thermoplastic and also contain hydrogen bonding groups include ethylene vinyl alcohol, polyvinyl acetate, acrylates, polycarbonates, polyesters and polyamides. Further information about the use of such auxiliary binders can be found in U.S. Pat. No. 5,057,166.
The auxiliary or second binder can be added to the fibers, either before or after a first binder, to help bind the fibers to each other and provide additional binding between the fibers and particles. A suitable second binder would be a thermoplastic or thermosetting binder. In the case of thermoplastic polymers, the polymers may be a material which remains permanently thermoplastic. Alternatively, such polymers may be a material which is partially or fully crosslinkable, with or without an external catalyst, into a thermosetting type polymer. As a few specific examples, suitable thermoplastic binders can be made of the following materials:
ethylene vinyl alcohol
polyvinyl acetate
acrylic
polyvinyl acetate acrylate
acrylates
polyvinyl dichloride
ethylene vinyl acetate
ethylene vinyl chloride
polyvinyl chloride
styrene
styrene acrylate
styrene/butadiene
styrene/acrylonitrile
butadiene/acrylonitrile
acrylonitrile/butadiene/styrene
ethylene acrylic acid
polyethylene
urethanes
polycarbonate
polyphenylene oxide
polypropylene
polyesters
polyimides
In addition, a few specific examples of thermoset binders include those made of the following materials:
epoxy
phenolic
bismaleimide
polyimide
melamine/formaldehyde
polyester
urethanes
urea
urea/formaldehyde
More than one of these materials may be used to treat the fibers. For example, a first coating or sheath of a thermoset material may be used followed by a second coating of a thermoplastic material. The superabsorbent particles or other particles are then typically adhered to the outer binder material. During subsequent use of the fibers to make products, the thermoplastic material may be heated to its softening or tack temperature without raising the thermoset material to its curing temperature. The remaining thermoset material permits subsequent heating of the fibers to cure the thermoset material during further processing. Alternatively, the thermoset material may be cured at the same time the thermoplastic material is heated by heating the fibers to the curing temperature of the thermoset with the thermoplastic material also being heated to its tack temperature.
Certain types of binders enhance the fire resistance of the treated fibers, and thereby products made from these fibers. For example, polyvinyl chloride, polyvinyl dichloride, ethylene vinyl chloride and phenolic are fire retardant.
Surfactants may also be included in the liquid binder as desired. Other materials may also be mixed with the liquid binder to impart desired characteristics to the treated fibers. For example, particulate material, such as pigments, may also be included in the binder for application to the fibers.
EXAMPLE XXVI
As previously described, an auxiliary binder can be used in addition to the polymeric binders of the present invention. A 3210 gram amount of southern bleached kraft binder (NB-416, supplied by Weyerhaeuser Company) is air entrained in a blenderlike mixing device and sprayed with 2128 grams of a polyvinyl acetate latex (PN-3666H, supplied by H.B. Fuller of Minneapolis, Minn.). This binder may also be applied to the kraft fluff in mat form on a pulp sheet manufacturing line. While still mixing, 4073 grams of a water swellable polyacrylate hydrogel (IM 1000-60, supplied by Hoechst-Celanese of Portsmouth, Va.) is added and the resulting mixture is then sprayed with 1160 grams of a 50% solution of polypropylene glycol (supplied by Union Carbide of Danbury, Conn.). The blender is then stopped and the mixture was shunted into a flash tube dryer. The dried product is then airlaid as a 16 inch wide web on a Danweb airlay machine, pressed to a density of approximately 0.15 g/cc, and thermobonded at 140.degree. C. for thirty seconds. The resulting web would have 40% bound SAP and improved tensile strength (as compared to untreated fluff With SAP).
Application of Binder
The binders of the present invention can be added to the fibers in any convenient manner. One such procedure is to spray the binder or binders on a web of the fibers that is conveyed past a sprayer on the pulp sheet manufacturing line. Another procedure is to roll coat the web with the binder. Relatively high viscosity binders, such as glycerin, are easier to roll coat than to spray. The binder would be added downstream in the process from the headbox because binder would be wasted if added to the slurry in the headbox, or for that matter, prior to the initial dewatering zone of the process at the wire. For solid binders, blending of the fiber and binder may also be accomplished by sprinkling onto or otherwise comingling the binders with the fibers. The fibers may also be sprayed or immersed in the binder, or binder particles may be applied thereto. These fibers can, while still wet in the case of a liquid binder or following reactivation of a liquid or solid, be combined with the particles. The fibers can also be allowed to dry for later reactivation with a reactivation liquid and combined with the particles at that time. Particles may be added from conventional volumetric feeders in a hammermill or from injectors on a pulp sheet manufacturing line such as a paper making line.
Composite Absorbent Product
In accordance with the present invention, absorbent structures may be made from the fibers, with the bound particulates, in accordance with the present invention. These articles may be composite structures (e.g., made of plural materials). For example, the articles may have a core of plural types of fibers, or fiber layers, with or without covering materials. These products are capable of absorbing significant quantities of water and other fluids, such as urine and body fluids. Such products include, but are not limited to, disposable diapers, sanitary napkins, incontinent pads, towels and the like.
As best shown in FIGS. 3 and 4, an absorbent towel 200 may have a core 216 with a cover sheet 232 and a backing sheet 234. The core 216 may be comprised of fibers with the binders of the present invention and particulate materials, such as superabsorbent particles secured to the fibers by the binder. The fibers that contain the binder may be blended with other fibers as well in the core. Cover sheet 232 is made of any suitable material, including liquid permeable, nonwoven materials, which will readily permit the passage of liquid through the cover sheet to the absorbent pad 216. The following list of liquid permeable materials is provided by way of example only: nonwoven sheets of polypropylene, rayon, nylon fibers, polyester fibers, and blends thereof. A specifically preferred cover sheet material for wipes is a 70% rayon/30% polyester blend having a basis weight of 21.5 grams/m.sup.2, available from the Scott Paper Company.
The backing sheet 234 may be, but is not necessarily, made of a liquid impermeable material, including but not limited to, films of polyethylene, polypropylene and polyester and blends thereof along with nylon and polyvinyl chloride films, A specifically preferred backing sheet material is a polyethylene film from Dow Chemical Company.
FIGS. 3-4 illustrate an absorbent pad structure which may be formed from fibers of the present invention, whether or not they are blended with other fibers. FIGS. 1 and 2 represent an absorbent pad having a heat embossed screen pattern. Pads having no pattern may also be used. A pad having a cover sheet and a backing sheet may be formed, for example, by placing a square fiber piece cut from the sheet onto a corresponding precut backing sheet. A corresponding precut cover sheet is placed over the top of the fiber on the backing sheet. This assembly may then be adhesively bonded.
With reference to FIGS. 5-8, absorbent structures in the form of bandages or dressings are shown. In FIGS. 5 and 6, a bandage 410 for application to a wound to absorb blood and other bodily fluids is shown. An absorbent pad 216 (FIG. 6) is securely mounted to an exterior or pad mounting surface 414 of a backing strip 416. Any suitable mounting or securing means may be used to affix pad 216 to the surface 414 of the strip 416. However, it is preferable for surface 414 to be coated with an adhesive so that the pad 216 may be adhesively mounted in place. An exemplary adhesive is ethylene vinyl acetate adhesive. It is also desirable for the overall surface 418 of backing strip 416 to be coated with a conventional adhesive. Surface 418 is the surface which is affixed to the area of the skin surrounding the wound. Conventional "peel-back" tabs may be used to protect the adhesive coating and pad 216 until the bandage is to be applied. This type of backing strip is well known in the art.
The backing strip 416 may be of any known flexible material suitable for application to the skin. It is preferable for the strip 416 to be of a material which is impermeable to the passage of liquid so that fluid from a wound is contained by the bandage. However, the strip 416 may be apertured or otherwise breathable to permit air to reach the wound to promote the healing process. A specific example of a suitable backing strip 416 is a polyethylene film.
As in the other structures described, a variety of combinations of antimicrobials and other particles may be used in such a bandage. Again, however, the particles are adhered securely in place when the particles have a hydrogen bonding or a coordinate covalent bonding functionality, the fibers to which these particles are bound have a hydrogen bonding functionality, and wherein the binder is selected from the group consisting of a polypropylene glycol, a polypropylene glycol/polyethylene glycol copolymer, polyacrylic acid, a polyamide, or a polyamine and the polymeric binder has a hydrogen bonding or a coordinate covalent bond forming functionality on each repeating unit of the binder. Two different particles, such as antimicrobials in particulate form, may be adhered to the same fiber. In the alternative, each different type of antimicrobial particle or other particle may be adhered separately to different fibers. Also, blends of fibers may be included in absorbent structures such as pad 216. For example, these blends may include fibers with adhered antimicrobial (one or more antimicrobials) particles and adhered superabsorbent particles; fibers with one or more antimicrobial particles without superabsorbent particles blended with fibers having adhered superabsorbent particles with or without antimicrobial particles; and combinations of such fibers with untreated fibers and/or binder coated fibers without superabsorbent particles or antimicrobial particles. In addition, other particles, such as anticoagulants or hemostatics may be attached to the fibers.
The absorbent pad 216 of bandage 410 may also include a cover sheet 420. Cover sheet 420 is typically made of any suitable material which will readily permit the passage of liquid through the cover sheet to the absorbent pad 216, such as nonwoven fiber webs of fibers such as, for example, rayon, nylon, polyester, propylene and blends thereof. One specifically preferred cover sheet material is a 70 percent rayon/30 percent polyester blend having a basis weight of 18 g/m.sup.2 from Scott Paper Company.
The dressing 216 shown in FIGS. 7 and 8 illustrates fibers 421 placed within an enclosure 422. Enclosure 422 has at least one liquid permeable surface through which fluid or liquid may pass to be absorbed by the fibers. The enclosure containing the loose fibers may be secured to the skin using adhesive tape, for example. Again, the fibers 421 preferably include antimicrobial particles attached to at least some of the fibers.
FIGS. 9 and 10 illustrate fibers of the present invention incorporated into a feminine hygiene appliance such as a feminine pad or tampon. In this case, the feminine pad 510 is illustrated as having a cover sheet 512. The loose fibers having adhered antimicrobial particles, which may alternatively be in the form of a pad, are included within the interior of the feminine appliance as indicated at 216 in FIG. 4. The cover 512 is preferably liquid permeable so that bodily fluids may reach the interior of the pad for purposes of absorption. The cover 512 may be wrapped around the core 216 (as indicated by edges 514, 515). A backing sheet 516, preferably of a liquid impermeable material, may be adhered to the edges 514, 515 at the underside of the core. An adhesive containing strip, such as indicated at 520, which may have a peelable or removable cover, may be mounted to the backing sheet 516 for use in adhering the pad, for example to a user's undergarment, during use.
FIGS. 11 and 12 illustrate a conventional disposable diaper 550 with a core 552 which is comprised of fibers of the present invention with adhered superabsorbent particulate materials. These particulate materials may be confined to a target zone (for example, the front portion of a diaper indicated at 556) or of a heavier concentration in the target zone. This can be accomplished by airlaying fibers of the present invention in such a zone. Also, the core may be reactivated by melting the binder or moistening the target zone with water. The superabsorbent particles may be sprinkled on or otherwise applied to this wetted zone. As the zone dries, the particles are adhered in place.
Densification
The products such as described above, as well as webs of the fibers of the present invention, can also be densified by external application of pressure to the web. The web of Example II, for instance, could be densified by passing it through a set of calendar rolls set at 60 and 90 pli (pounds per linear inch, as in a calendar press) respectively to yield sheets with increased densities. Densification may alternatively be provided by compaction rolls or presses. The present inventors have found that densification is facilitated in the products treated with the polymeric organic binders of the present invention. Products that are treated with the binders of the present invention require less heat and pressure than untreated fibers to densify to a given density. Densification is preferably performed to produce a product that has a density of about 0.1 to 0.7 g/cc, more preferably 0.1 to 0.3 g/cc.
An example of densification using some of the binders of the present invention is given below:
EXAMPLE XXVII
Any of the products of the present invention can be formed into 550 gram/square meter sheets, six inches in diameter, in a laboratory padformer. Those pads are then passed through a set of calendar rolls set at 60 and 90 pli, respectively to yield sheets with densities of 0.3 and 0.5 g/cc.
EXAMPLE XXVIII
CCF pulp (Weyerhaeuser Company), containing 40% SAP by weight, was coated with 12.5% glycerin, air laid, and densified to 0.3 g/cc. Densification to this product density required 60 psi for the glycerin coated fibers. In comparison, NB-316 fibers that were not coated with glycerin required densification at 200 psi to reach a 0.3 g/cc density. Absorbent capacity was higher for the coated fibers. This comparison indicates that the fibers with glycerin bound SAP were more easily densified than the fibers that were not coated with the binder.
EXAMPLE XXIX
A 50 gram amount of polypropylene glycol is diluted with 50 grams deionized water. The resulting solution is sprayed on 321 grams of an intrafiber crosslinked cellulose fluff (HBA from Weyerhaeuser Company of Tacoma, Wash.) that was air entrained in a blender like mixing device. While the HBA fiber is still damp, 438 grams of IM 1000F (supplied by Hoechst-Celanese, of Portsmouth, Va.) is added to the mixture. The resultant mixture is then vacuumed from the blender and spread on a counter to dry overnight. Then 550 gram/square meter handsheets, six inches in diameter, are made in a laboratory padformer. Those pads are then pressed at 2000 and 3000 psi (or 60 and 90 pli in a calendar roll), respectively, to yield sheets with densities of 0.3 and 0.5 g/cc. Alternatively, pads of untreated HBA blended with 45% IM 1000F would require heating to 100.degree. C. and pressures between 8,000 and 11,000 psi to produce pads of similar densities. The same results are expected if the binder is applied to HBA fiber while making this fiber into a sheet on a pulp sheet manufacturing line.
Particulate Binding
FIG. 13 shows an isolated, enlarged cellulose fiber 600 with SAP particles 602 bound to it by a binder of the present invention. This drawing illustrates an example of the SAP retaining its discrete particulate form following binding to the fibers. Some particle to particle fusion may occur in accordance with this invention, but maintenance of a discrete particulate form excludes formation of a completely confluent film in which the particles lose their particulate identity. Such a confluent film produces gel blocking that interferes with efficient liquid absorption into the fibers.
The shown fiber 600 is elongated, and has an aspect ratio (ratio of length to width) of about 10:1.
FIG. 14 shows the particles 602 distributed substantially uniformly throughout the depth 604 of a pad 606. The particles are also shown adhering to all the surfaces of the pad. Particles may be distributed in any desired pattern throughout the pad in accordance with this invention, and need not necessarily adhere to all surfaces or be distributed throughout the volume of the mat, or distributed uniformly.
Electron Photomicrographs
An electron photomicrograph of superabsorbent particles (SAP) bound to cellulose fibers with an ascorbic acid binder is shown in FIG. 15. The SAP is at the left margin of the photograph, and is fused to the fiber which occupies the central portion of the photomicrograph. The particle is seen to be fused to the fiber, and the fiber has undergone some shear damage that resulted in a fracture of the fiber. It is significant that the fiber has experienced shear damage while the particle has remained fused to the fiber, because this indicates that the particle-fiber bond formed by the ascorbic acid is very strong and resilient, resisting mechanical disruption.
FIG. 16A-D shows several electron photomicrographs that illustrate individual particles bound to fibers with a lactose binder. FIG. 16C, for example, shows that SAP retains its individual particulate form when adhered to the fiber with a lactose binder. The particles do not form a fused confluent mass without particulate identity.
Fiber Mixtures
The fibers of the present invention, such as fiber 600, can be mixed with other types of fibers, such as that disclosed in U.S. Pat. No. 5,057,166 which is incorporated herein by reference in its entirety. The latex coated fibers of that patent can be mixed with the fibers of the present invention to produce an absorbent product that has characteristics of both types of fibers.
Having illustrated and described the principles of the invention in many preferred embodiments, it should be apparent to those skilled in the art that the invention can be modified in arrangement and detail without departing from such principles. We claim all modifications coming within the spirit and scope of the following claims.
Claims
We claim:
1. A method of producing fibers with adhered particles comprising: providing fibers that have hydrogen bonding functional sites in a wet laid fiber sheet or web manufacturing line in which the fibers are formed into a web; applying a binder to the fibers while the fibers are on the wet laid sheet manufacturing line, the binder having a volatility less than water, the binder also having a functional group that forms a hydrogen bond with the fibers and that is capable of forming a hydrogen bond or a coordinate covalent bond with particles; adding particles having a hydrogen bonding or a coordinate covalent bonding functionality to the fibers; and activating the binder from an inactive state by mechanical agitation, heat, or addition of an activating liquid, to bond the particles to the fibers.
2. A method according to claim 1 in which the fibers include wood pulp fibers.
3. A method according to claim 1 in which the particles are added to the fibers at a location remote from the pulp sheet manufacturing line.
4. A method according to claim 3 in which the web is dried and thereafter fiberized and in which the particles are added to the fibers contemporaneously with the fiberizing of the web.
5. A method according to claim 1 in which the particles are added to the fibers at a location remote from the wet laid sheet manufacturing line.
6. A method according to claim 1 wherein the binder is applied to the fiber web following the drying of the web at least partially on the wet laid sheet manufacturing line.
7. A method according to claim 6 in which the particles are added to the fibers at a location remote from the wet laid sheet manufacturing line.
8. A method according to claim 1 in which the binder is selected from the group consisting of (a) a polymeric binder with repeating units and with each repeating unit having a functional group capable of forming a hydrogen bond or a coordinate covalent bond with the particles, or a hydrogen bond with the fibers; and (b) a non-polymeric organic binder with a functional group capable of forming a hydrogen bond or a coordinate covalent bond with the particles, and a functional group capable of forming a hydrogen bond with the fibers.
9. A method according to claim 8 wherein the particles comprise superabsorbent particles.
10. A method according to claim 8 wherein the binder is a polymeric binder selected from the group consisting of polyethylene glycol, polypropylene glycol, polyacrylic acid, polyamides, polyamines, poly(caprolactone) diol and combinations thereof.
11. A method according to claim 8 wherein the binder is selected from the group consisting of polyacrylic acid, polyamides and polyamines.
12. A method according to claim 8 wherein the binder is selected from the group consisting of a polyamide and a polyamine.
13. A method according to claim 8 wherein the binder is a non-polymeric organic binder selected from the group consisting of a carboxylic acid, an alcohol, an amino acid, an amide, an amine, a carboxyl and combinations thereof.
14. A method according to claim 13 wherein the binder is a carboxylic acid.
15. A method according to claim 13 wherein the binder is selected from the group consisting of an amino acid, an amide, and an amine.
16. A method according to claim 13 wherein the binder is selected from the group consisting of a polycarboxylic acid, a hydroxy acid, an amino acid or a carboxyamide.
17. A method according to claim 13 wherein the binder is an alcohol selected from the group consisting of a polyol and an amino alcohol.
18. A method according to claim 13 wherein the binder is a polyamine.
19. A method according to claim 13 wherein the binder is selected from the group consisting of a hydroxyamide and a polyamide.
20. A method according to claim 13 wherein the binder is selected from the group consisting of glycerin, ascorbic acid, urea, glycine, pentaerythritol, a monosaccharide, a disaccharide, and combinations thereof.
21. A method according to claim 1 wherein the particles are selected from the group consisting of superabsorbent particles, zeolites, and antimicrobials.
22. A method according to claim 1 in which the step of providing fibers comprises the step of providing a blend of fibers having hydrogen bonding functional sites and fibers which lack hydrogen bonding functional sites.
23. The method according to claim 1 in which the step of activating the binder is performed prior to the step of adding the particles.
24. A method according to claim 1 in which the step of activating the binder is performed following the step of adding the particles.
25. A method according to claim 1 in which the step of activating the binder is performed simultaneously with the step of adding the particles.
26. The method of claim 1 wherein the step of activating the binder comprises mechanically agitating the fibers to which the binder has been applied.
27. The method of claim 1 wherein the step of activating the binder comprises adding an activating liquid to the fibers.
28. The method according to claim 27 wherein the activating liquid is water.
29. The method of claim 1 including the step of applying plural binders.
30. The method of claim 1 including the step of applying an auxiliary binder.
31. A method of producing fibers with adhered particles, comprising the steps of: providing cellulose fibers in a wet laid fiber sheet or web manufacturing line in which the fibers are formed into a web; applying at least one binder to the fibers while the fibers are on the wet laid sheet manufacturing line, the binder having a volatility less than water, wherein the binder is selected from the group consisting of (a) a polymeric binder consisting of repeating units selected from the group consisting of polyethylene glycol, polypropylene glycol, polyacrylic acid, a polyamide, a polyamine, and poly(caprolactone) diol; and (b) a non-polymeric organic binder containing at least two functional groups selected from the group consisting of a carboxylic acid, an alcohol, an amino acid, an amide, an amine, an aldehyde, and a polyaldehyde, wherein the two functional groups are the same or different; allowing the binder to become dry and inactivated wherein the binder is not capable of binding particles to the fibers prior to activating the binder; adding particles that are capable of being bound to the fibers by the binder; and activating the binder from an inactive state by mechanical agitation, heat, or addition of a reactivating liquid to bond the particles to the fibers.
32. The method of claim 31 wherein the step of applying the binder comprises applying a binder comprising glycerin.
33. The method of claim 31 wherein the step of applying the binder comprises applying a binder comprising ascorbic acid.
34. The method of claim 31 wherein the step of applying the binder comprises applying a binder comprising urea.
35. The method of claim 31 wherein the step of applying the binder comprises applying a binder comprising glycine.
36. The method of claim 31 wherein the step of applying the binder comprises applying a binder comprising pentaerythritol.
37. The method of claim 31 wherein the step of applying the binder comprises applying a binder comprising monosaccharide.
38. The method of claim 31 wherein the step of applying the binder comprises applying a binder comprising disaccharide.
40. The method according to claim 31 wherein the step of activating the binder comprises adding a reactivating liquid.
41. The method according to claim 40 wherein the reactivating liquid is water.
42. A method of producing fibers with adhered particles, comprising the steps of: providing cellulose fibers in a wet laid fiber sheet or web manufacturing line in which the fibers are formed into a web; applying a binder to the fibers, the binder having a volatility less than water, wherein the binder has a first functional group that is capable of forming a hydrogen bond with the fibers and a second functional group that is capable of forming a hydrogen bond or a coordinate covalent bond with particles, and the binder is capable of being reactivated from an inactive dry state in which the binder is not capable of binding particles to the fibers, to an active state in which the binder is capable of binding the particles to the fibers by the hydrogen bonds, or hydrogen bonds and coordinate covalent bonds; after applying the binder, allowing the binder to become dry and inactivated wherein the binder is not capable of binding particles to the fibers prior to activating the binder, and shipping the fibers to a remote location with the binder dry and inactivated; adding particles having a hydrogen bonding or a coordinate covalent bonding functionality to the fibers; and at the remote location, activating the binder from an inactive state by mechanical agitation or addition of a reactivating liquid, to bind the particles to the fibers by the binder.
43. The method of claim 42 further comprising the step of incorporating the fibers into a product, and the activating step comprises activating the binder in a target area on the product, wherein the target area is less than an entire area of the product.
44. The method of claim 43 wherein the product is selected from the group consisting of an absorbent pad, a bandage, a feminine hygiene appliance, and a diaper.
45. The method of claim 43 wherein the product is a diaper, the target area is the crotch of a diaper, and the particles are selected from the group consisting of superabsorber particles, antimicrobials, and odor absorbers.
Patent Citations (100)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US2601597 | 1952-06-01 | Daniel, Jr. et al. | |
| US2953187 | 1960-09-01 | Francis, Jr. | |
| US3010161 | 1961-11-01 | Duvall | |
| US3021242 | 1962-12-01 | Touey | |
| US3059313 | 1962-10-01 | Harmon | |
| US3070095 | 1962-12-01 | Torr | |
| US3087833 | 1963-04-01 | Drelich | |
| US3327708 | 1967-06-01 | Sokolowski | |
| US3344789 | 1967-10-01 | Arnold et al. | |
| US3377302 | 1968-04-01 | Gugliemelli et al. | |
| US3395201 | 1968-07-01 | Kalwaites | |
| US3425971 | 1969-02-01 | Gugliemelli et al. | |
| US3494992 | 1970-02-01 | Wiegand | |
| US3521638 | 1970-07-01 | Parrish | |
| US3554788 | 1970-10-01 | Fechillas | |
| US3661154 | 1972-05-01 | Torr | |
| US3661632 | 1972-05-01 | Gagliardi et al. | |
| US3669103 | 1972-06-01 | Harper et al. | |
| US3670731 | 1972-06-01 | Harmon | |
| US3672945 | 1972-06-01 | Taylor | |
| US3692622 | 1972-09-01 | Dunning | |
| US3766922 | 1973-10-01 | Krusko | |
| US3777758 | 1973-12-01 | Mesek et al. | |
| US3788936 | 1974-01-01 | Brock et al. | |
| US3804092 | 1974-04-01 | Tunc | |
| US3808088 | 1974-04-01 | Knechtges et al. | |
| US3886941 | 1975-06-01 | Duane et al. | |
| US3888256 | 1975-06-01 | Studinger | |
| US3888257 | 1975-06-01 | Cook et al. | |
| US3901236 | 1975-09-01 | Assarsson et al. | |
| US3903889 | 1975-09-01 | Torr, deceased | |
| US3908659 | 1975-09-01 | Wehrmeyer et al. | |
| US3923592 | 1975-12-01 | George et al. | |
| US3949035 | 1976-04-01 | Dunning et al. | |
| US3978257 | 1976-08-01 | Ring | |
| US3991237 | 1976-11-01 | Topfl et al. | |
| US4007083 | 1977-02-01 | Ring et al. | |
| US4009313 | 1977-02-01 | Crawford et al. | |
| US4035217 | 1977-07-01 | Kennette et al. | |
| US4055180 | 1977-10-01 | Karami | |
| US4062451 | 1977-12-01 | Gander | |
| US4071636 | 1978-01-01 | Nishino et al. | |
| US4102340 | 1978-07-01 | Mesek et al. | |
| US4103062 | 1978-07-01 | Aberson et al. | |
| US4160059 | 1979-07-01 | Samejima | |
| US4232674 | 1980-11-01 | Melican | |
| US4250660 | 1981-02-01 | Kitamura et al. | |
| US4282121 | 1981-08-01 | Goodrich | |
| US4289513 | 1981-09-01 | Brownhill et al. | |
| US4364992 | 1982-12-01 | Ito et al. | |
| US4379194 | 1983-04-01 | Clarke et al. | |
| US4394172 | 1983-07-01 | Scheuble et al. | |
| US4404250 | 1983-09-01 | Clarke | |
| US4410571 | 1983-10-01 | Korpman | |
| US4412036 | 1983-10-01 | Pederson et al. | |
| US4424247 | 1984-01-01 | Erickson | |
| US4457978 | 1984-07-01 | Wawzonek | |
| US4467012 | 1984-08-01 | Pederson et al. | |
| US4486501 | 1984-12-01 | Holbek | |
| US4492729 | 1985-01-01 | Bannerman et al. | |
| US4558091 | 1985-12-01 | Hubbard | |
| US4597930 | 1986-07-01 | Szal | |
| US4673402 | 1987-06-01 | Weisman et al. | |
| US4676784 | 1987-06-01 | Erdman et al. | |
| US4758466 | 1988-07-01 | Dabi et al. | |
| US4772492 | 1988-09-01 | Bouchette | |
| US4788080 | 1988-11-01 | Hojo et al. | |
| US4818599 | 1989-04-01 | Marcus | |
| US4826880 | 1989-05-01 | Lesniak et al. | |
| US4833011 | 1989-05-01 | Horimoto | |
| US4842593 | 1989-07-01 | Jorden et al. | |
| US4874811 | 1989-10-01 | Borchers et al. | |
| US4886697 | 1989-12-01 | Perdelwitz, Jr. et al. | |
| US4892769 | 1990-01-01 | Perdelwitz, Jr. et al. | |
| US5002814 | 1991-03-01 | Knack et al. | |
| US5057166 | 1991-10-01 | Young et al. | |
| US5128082 | 1992-07-01 | Makoui | |
| US5161686 | 1992-11-01 | Weber et al. | |
| CAX729513 | 1962-06-01 | ||
| CAX806352 | 1964-04-01 | ||
| CAX813616 | 1965-12-01 | ||
| CAX841940 | 1965-12-01 | ||
| CAX953890 | 1974-09-01 | ||
| CAX1052156 | 1976-12-01 | ||
| EPX122042 | 1984-10-01 | ||
| EPX427316A2 | 1989-07-01 | ||
| EPX427317A2 | 1989-07-01 | ||
| EPX429112A2 | 1989-07-01 | ||
| EPX440472A1 | 1990-01-01 | ||
| EPX442185A1 | 1991-08-01 | ||
| DEX489308 | 1930-01-01 | ||
| DEX1079796 | 1962-06-01 | ||
| DEX2048721 | 1971-06-01 | ||
| FRX1382716 | 1964-02-01 | ||
| JPX61-28422 | 1986-01-01 | ||
| WOXWO88/01316 | 1988-02-01 | ||
| WOXWO90/09236 | 1990-08-01 | ||
| WOXWO90/11181 | 1990-10-01 | ||
| GBX1217452 | 1969-12-01 | ||
| GBX2189127 | 1987-10-01 |
Non-Patent Literature (16)
- S. Lammie, "Use of Glycerine as a Softener for Paper Products," The World's Paper Trade Review, Dec. 13, 1962, p. 2050.
- Gugliemelli et al., "Base-Hydrolyzed Starch-Polyacrylonitrile (S-PAN) Graft Copolymer. S-PAN-1:1, PAN M.W. 794,000*," J. of Applied Copolymer Science, 13:2007-2017 (1969).
- Weaver et al., "Hydrolyzed Starch-Polyacrylonitrile Graft Copolymers: Effect of Structure on Properties*," J. of Applied Polymer Science, 15:3015-3024 (1971).
- Weaver et al., "Highly Absorbent Starch-Based Polymer," Northern Regional Research Laboratory, Agricultural Research Service, U.S. Dept. of Agriculture, Peoria, Ill., pp. 169-177.
- "Super slurpers: Time for change?," Chemical Week, pp. 21-22 (Jul. 24, 1974).
- Lindsay, "Absorbent Starch Based Co-polymers--Their Characteristics and Applications," Formed Fabrics Industry, pp. 20, 24 and 26 (May 1977).
- Burkholder, "Absorbent Polymers--A New Concept in Fluid Absorption," The Dow Chemical Company Designed Products Laboratory, Midland, Mich., pp. 73-79 (1973).
- Lysogorskaya et al., "Effect of Moisture Content on the Development of Interfiber Bonds in Air-Laid Paper," Leningrad Technological Institute of the Pulp and Paper Industry, Zh. Prikl. Khim., 63:(8) 1869-1872 (1990).
- Ogurtsov et al., "Effect of the modulus of elasticity of the binder on the properties of dry-process paper," Sb. Tr. Tsentr. Nauch.-Issled. Inst. Bumagi, 9:123-127 (1974).
- Amosov, et al., "Aluminum hydroxy compounds--binders for dry-process paper," Izv. VUZ, Lesnoi Zh., 6:72-76 (1986).
- Gorbushin et al., "Investigation of the effect of the nature and concentration of binders on the properties of dry-process paper," Sb. Tr. Tsentr. Nauch.-Issled. Inst. Bumagi, 9:117-123 (1974).
- Hoque et al., "Granulation and Tabletting of Iron Oxide-Chromic Oxide Catalyst Mass with the Aid of Binding Ingredients Part II-Cellulosic Derivatives and Polyethylene Glycol as Binding Ingredients," Fertilizer Technology, 20:30-35 (1983).
- Lysogorskaya et al., "Effect of Moisture Content on Development of Interfiber Bonding in the Structure of Air-Dried Paper," Plenum Publ. Corp., pp. 1730-1733 (1991).
- Sliwiok and Kowalska, "Investigation of Self-Association of the Selected Glycols on Cellulose Sorbents," Microchemical Journal, 26:68-74 (1981).
- Blanchard and Reinhart, "Dyeing of Crosslinked Cotton Containing Glycol Additives," U.S. Dept. of Agriculture, New Orleans, 24:13-17 (Jan. 1992).
- Byrd, "How bonds develop during web consolidation," PTI, pp. 240-243 (Oct. 1986).