US 5,239,524 AGrant
Over Write Capable Magnetooptical Recording Method, and Magnetooptical Recording Apparatus and Medium Used Therefor
Issue Date:1993-08-24
•26 Claims
•22 Drawing Sheets
Abstract
A magnetooptical recording method for recording data using a bit having upward-magnetization and a bit having downward-magnetization on a recording layer of a magnetooptical recording medium comprises the steps of using, as the medium, a multilayered magnetic recording medium consisting of a first layer having a perpendicular magnetic anisotropy acting as a recording layer, and a second layer having a perpendicular magnetic anisotropy acting as a reference layer; moving the medium; applying an initial field so that, before recording, the direction of magnetization of the recording layer is left unchanged, and that of the reference layer is aligned either upward or downward; radiating a laser beam onto the medium; pulse modulating an intensity of the laser beam in accordance with binary data to be recorded; when the laser beam is radiated, applying a bias field to the irradiated portion; and when the intensity of the pulse-modulated laser beam is at high level, forming one of the bit having upward-magnetization and that having downward-magnetization, and when the intensity of the pulse-modulated laser beam is at low level, forming the other bit.
Metadata
Assignee
- Nikon Corporation
Inventors
- Masatoshi Sato
- Jun Saito
- Hideki Akasaka
Application Information
Application Number:US 4532554
Filing Date:1989-12-20
Priority Date:1985-06-11
Art Unit:233
Classifications
IPC:
G11B 1304G11B 1112G11B 1110
Field of Search:
3693603651359;114122;10;27
Patent Drawings (22 sheets)
Description
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a magnetooptical recording method and a magnetooptical recording apparatus and a medium used therefor and, more particularly, to an over write capable magnetooptical recording method, an over write capable magnetooptical recording apparatus and an over write capable medium.
2. Related Background Art
In recent years, many efforts have been made to develop an optical recording/reproduction method, an optical recording apparatus and a medium used therefor, which can satisfy various requirements including high density, large capacity, high speed access, and high recording/reproduction speed.
Of various optical recording/reproduction methods, the magnetooptical recording/reproduction method is most attractive due to its unique advantages that information can be erased after use and new information can be written thereon.
A recording medium used in a magnetooptical recording/reproduction method has a perpendicular magnetic layer or layers as a recording layer. The magnetic layer comprises, for example, amorphous GdFe, GdCo, GdFeCo, TbFe, TbCo, TbFeCo, and the like. Concentric or spiral tracks are formed on the recording layer, and data is recorded on the tracks. Note that in this specification, one of the "upward" and "downward" directions of magnetization with respect to a film surface is defined as an "A direction" and the other one is defined as a "non-A direction". Data to be recorded is binarized in advance, and is recorded by a bit (B.sub.1) having "A-directed" magnetization and a bit (B.sub.0) having "non-A-directed" magnetization. These bits B.sub.1 and B.sub.0 correspond to "1" and "0" levels of a digital signal, respectively. However, in general, the direction of magnetization of the recording tracks can be aligned in the "non-A direction" by applying a strong bias field before recording. This processing is called "initialization". Thereafter, the bit (B.sub.1) having "A-directed" magnetization is formed on the tracks. Data is recorded in accordance with the presence/absence and/or a bit length of the bit (B.sub.1).
Principle of Bit Formation
In the bit formation, a characteristic feature of a laser, i.e., excellent coherence in space and time, is effectively used to focus a beam into a spot as small as the diffraction limit determined by the wavelength of the laser light. The focused light is radiated onto the track surface to write data by producing bits less than 1 .mu.m in diameter on the recording layer. In the optical recording, a recording density up to 10.sup.8 bit/cm.sup.2 can be theoretically attained, since a laser beam can be concentrated into a spot with a size as small as its wavelength.
As shown in FIG. 1, in the magnetooptical recording, a laser beam L is focused onto a recording layer 1 to heat it, while a bias field (Hb) is externally applied to the heated portion in the direction opposite the initialized direction. A coersivity Hc of the locally heated portion is decreased below the bias field (Hb). As a result, the direction of magnetization of that portion is aligned in the direction of the bias field (Hb). In this way, reversely magnetized bits are formed.
Ferromagnetic and ferrimagnetic materials differ in the temperature dependencies of the magnetization and Hc. Ferromagnetic materials have Hc which decreases around the Curie temperature and allow data recording based on this phenomenon. Thus, data recording in ferromagnetic materials is referred to as Tc recording (Curie temperature recording).
On the other hand, ferrimagnetic materials have a compensation temperature, below the Curie temperature, at which magnetization (M) becomes zero. The Hc abruptly increases around this temperature and hence abruptly decreases outside this temperature. The decreased Hc is cancelled by a relatively weak bias field (Hb). Namely, recording is enabled. This process is called Tcomp. recording (compensation point recording).
In this case, however, there is no need to adhere to the Curie point or temperatures therearound, and the compensation temperature. In other words, if a bias field (Hb) capable of cancelling a decreased Hc is applied to a magnetic material having the decreased Hc at a predetermined temperature higher than a room temperature, recording is enabled.
Principle of Reading.
FIG. 2 illustrates the principle of data reading based on the magnetooptical effect. Light is an electromagnetic wave with an electromagnetic-field vector normally emanating in all directions in a plane perpendicular to the light path. When light is converted to linearly polarized beams (Lp) and radiated onto a recording layer (1), it is reflected by or passes through the recording layer (1). At this time, the plane of polarization rotates according to the direction of magnetization (M). This phenomenon is called the magnetic Kerr effect or magnetic Faraday effect.
For example, if the plane of polarization of the reflected light rotates through .theta..sub.k degrees for "A-directed" magnetization, it rotates through -.theta..sub.k degrees for the "non-A-directed" magnetization. Therefore, when the axis of an optical analyzer (polarizer) is set perpendicular to the plane inclined at -.theta..sub.k, the light reflected by "non-A-direction" magnetized bit (B.sub.0) cannot pass through the analyzer. However, a product (X sin2.theta..sub.k).sup.2 of the light reflected by a bit (B.sub.1) magnetized along the "A direction" passes through the analyzer and becomes incident on a detector (photoelectric conversion means). As a result, the bit (B.sub.1) magnetized along the "A direction" looks brighter than the bit (B.sub.0) magnetized along the "non-A direction", and the detector produces a stronger electrical signal for the bit (B.sub.1). The electrical signal from the detector is modulated in accordance with the recorded data, thus reading the data.
SUMMARY OF THE INVENTION
In order to re-use a recorded medium, (i) the medium must be re-initialized by an initializing device, (ii) an erasing head as well as a recording head must be added to a recording apparatus, or (iii) recorded data must be erased using a recording apparatus or an erasing apparatus as preliminary processing.
Therefore, in the conventional magnetooptical recording method, an over-write operation, which allows new data recording regardless of the presence/absence of the recorded data, is impossible.
If the direction of a bias field (Hb) can be freely changed between the "A direction" and "non-A direction", an over-write operation is possible. However, the direction of the bias field (Hb) cannot be changed at high speed. For example, when a bias field (Hb) applying means is a permanent magnet, the direction of the magnet must be mechanically reversed. In this case, it is impossible to rotate the direction of the magnet at high speed. Similarly, when the bias field (Hb) applying means is an electromagnet, the direction of such a large current cannot be reversed at high speed.
It is, therefore, a first object of the present invention to provide a magnetooptical recording method capable of over writing by modulating light without changing the direction of the bias field (Hb).
It is a second object of the present invention to provide a magnetooptical recording apparatus capable of over writing.
It is a third object of the present invention to provide a magnetooptical recording medium capable of over writing.
According to the present invention, there is provided a magnetooptical recording method, in which data is recorded on a recording layer of a magnetooptical recording medium using a bit having upward-magnetization and a bit having downward-magnetization, the method comprising the steps of:
(a) using, as the medium, a multilayered magnetic recording medium consisting of a first layer having a perpendicular magnetic anisotropy acting as a recording layer, and a second layer having a perpendicular magnetic anisotropy acting as a reference layer;
(b) moving said medium;
(c) applying an initial field so that, before recording, the direction of magnetization of the recording layer is left unchanged, and that of the reference layer is aligned either upward or downward;
(d) radiating a laser beam onto the medium;
(e) pulse modulating an intensity of the laser beam in accordance with binary data to be recorded;
(f) when the laser beam is radiated, applying a bias field to the irradiated portion; and
(g) when the intensity of the pulse-modulated laser beam is at high level, forming one of the bit having upward-magnetization and that having downward-magnetization, and when the intensity of the pulse-modulated laser beam is at low level, forming the other bit.
With the method of the present invention, the laser beam is pulse modulated based on data to be recorded. However, this procedure itself has been performed in the conventional magnetooptical recording method, and a means for pulse modulating the beam intensity based on two-valued or binary data to be recorded is a known means. For example, see "THE BELL SYSTEM TECHNICAL JOURNAL, Vol. 62(1983) pp. 1923-1936.
A characteristic feature of the present invention lies in high and low levels of the beam intensity. More specifically, when the beam intensity is at high level, "A-directed" magnetization of the reference layer is reversed to the "non-A direction" by means of a bias field (Hb), and a bit having the "non-A-directed" (or "A-directed) magnetization is thus formed in the recording layer by means of the "non-A-directed" magnetization of the reference layer. When the beam intensity is at low level, a bit having the "A-directed" (or "non-A-directed) magnetization is formed in the recording layer by means of the "A-directed" magnetization of the reference layer. If required high and low levels are given, it is easy for a person skilled in the art to modulate the beam intensity according to the present invention only by partially modifying the modulating means.
In this specification, if expressions ooo (or xxx) appear, ooo outside the parentheses in the first expression corresponds to ooo in the subsequent expressions ooo (or xxx), and vice versa.
As is well known, even if recording is not performed, a laser beam is often turned on at very low level* in order to, for example, access a predetermined recording position on the medium. When the laser beam is also used for reading, the laser beam is often turned on at an intensity of the very low level*. In this invention, the intensity of the laser beam may be set at this very low level. However, low level for forming a bit is higher than the very low level*. Therefore, the output waveform of the laser beam of the present invention is as shown in FIG. 5.
According to the present invention, there is provided a magnetooptical recording apparatus capable of over writing, comprising:
(a) means for moving a magnetooptical recording medium;
(b) initial field applying means;
(c) a laser beam source;
(d) means for pulse modulating a beam intensity in accordance with binary data to be recorded to obtain (1) high level that provides, to the medium, a temperature suitable for forming one of a bit having upward-magnetization and a bit having downward-magnetization, and to obtain (2) low level that provides, to the medium, a temperature suitable for forming the other bit; and
(e) bias field applying means, which can be commonly used as the initial field applying means.
The modulating means is available by partially modifying a conventional beam modulating means if high and low levels of the beam intensity are provided. Such a modification would be easy for those skilled in the art.
In addition, according to the present invention, there is provided an over-write capable multilayered magnetooptical recording medium consisting of a first layer having a perpendicular magnetic anisotropy as a recording layer, and a second layer having a perpendicular magnetic anisotropy as a reference layer.
The present invention is divided into first and second aspects. In both the aspects, the recording medium has a multilayered structure, which is divided into two layers, as shown in FIG. 7A.
The first layer is the recording layer, which exhibits high coersivity at room temperature and has low reversing temperature. The second layer is the reference layer, which exhibits low-coersivity at room temperature and has a higher reversing temperature than the first layer. Both the layers comprise perpendicular magnetic layers. Note that each of the first and second layers can comprise a multilayered structure. If necessary, another layer can be interposed between the first and second layers. In addition, a clear boundary between the first and second layers need not be formed, and one layer can be gradually converted into the other layer.
Furthermore, as shown in FIG. 40, a third layer (transcription layer) may be arranged on the side of the first layer (recording layer) to be in direct contact therewith or through another layer.
The third layer is adapted to transcribed data recorded in the first layer, and is a transcription layer having a higher magnetooptical effect and a smaller coersivity at a room temperature than those of the first layer. The third layer comprises a perpendicular magnetization film.
Therefore, when data recorded in the first layer is reproduced, a reproduction beam is radiated on the third layer, and data is reproduced from a beam reflected by the third layer. Thus, a C/N ratio can be improved as compared to a case wherein data is reproduced from the first layer.
In the first aspect, the coersivity of a recording layer 1 is represented by H.sub.C1 ; that of a reference layer 2, H.sub.C2 ; the Curie temperature of the recording layer 1, T.sub.C1 ; that of the reference layer 2, TC.sub.2 ; the room temperature, T.sub.R ; the temperature of the recording medium when a low level laser beam is radiated, T.sub.L ; that when a high level laser beam is radiated, T.sub.H ; a coupling field applied to the recording layer 1, H.sub.D1 ; and a coupling field applied to the reference layer 2, H.sub.D2. In this case, the recording medium satisfies the following Formula 1, and satisfies Formulas 2 to 5 at the room temperature.
In the above formula, symbol ".apprxeq." means "equal to" or "substantially equal to". In addition, of double signs .+-. and .-+., the upper sign corresponds to an A (antiparallel) type medium, and the lower sign corresponds to a P (parallel) type medium (these media will be described later). Note that the P type medium includes a ferromagnetic material.
The relationship between the coersivity and the temperature is as shown in the graph of FIG. 6. Referring to FIG. 6, the thin curve represents the characteristics of the recording layer 1 and the bold curve represents those of the reference layer 2.
Therefore, when an initial field (Hini.) is applied to the recording medium at room temperature, the direction of magnetization of the reference layer 2 is reversed without reversing that of the recording layer 1, according to Formula 5. When the initial field (Hini.) is applied to the recording layer before recording, the reference layer 2 can be magnetized in the "A direction" (in the drawings, the "A direction" is indicated by an upward arrow " ", and the "non-A direction" is indicated by a downward arrow " "). If the initial field (Hini.) is decreased to zero, the direction of magnetization of the reference layer 2 can be left unchanged without being re-reversed, according to Formula 4.
FIG. 7B schematically shows a state wherein only the reference layer 2 is magnetized in the "A direction" immediately before recording.
Referring to FIG. 7B, the direction of magnetization in the recording layer 1 represents previously recorded data. Since the direction of magnetization in the recording layer 1 does not change the basic operation mechanism, it is indicated by X in the following description. The table in FIG. 7B is modified as shown in Condition 1 in FIG. 8 for the sake of simplicity.
In Condition 1, the high-level laser beam is radiated onto the recording medium to increase the medium temperature to T.sub.H. Since T.sub.H is higher than the Curie temperature T.sub.C1, magnetization of the recording layer 1 disappears. In addition, since T.sub.H is near the Curie temperature T.sub.C2, magnetization of the reference layer 2 also disappears completely or almost completely. The bias field (Hb) in the "A direction" or "non-A direction" is applied to the medium in accordance with the type thereof. The bias field (Hb) can be a stray field from the medium itself. For the sake of simplicity, assume that the bias field (Hb) in the "non-A direction" is applied to the medium. Since the medium is moving, a given irradiated portion is immediately separated from the laser beam and is cooled by air. When the temperature of the medium is decreased under the presence of the field Hb, the direction of magnetization of the reference layer 2 is reversed to the "non-A direction" based on the field Hb (Condition 2.sub.H in FIG. 8).
When the medium is further cooled and the medium temperature is decreased below T.sub.C1, magnetization of the recording layer 1 appears again. In this case, the direction of magnetization of the recording layer 1 is influenced by that of the reference layer 2 due to a magnetic coupling (exchange coupling) force. As a result, magnetization (the P type medium) or (the A type medium) is formed in accordance with the type of the medium, as shown in Condition 3.sub.H in FIG. 8.
A change in conditions due to high-level laser beam irradiation is called a high-temperature cycle herein.
Next, in Condition 1 in FIG. 9, the low-level laser beam is radiated onto the medium to increase the medium temperature to T.sub.L. Since T.sub.L is near the Curie temperature T.sub.C1, magnetization of the recording layer 1 disappears completely or almost completely. However, since T.sub.L is below the Curie temperature T.sub.C2, magnetization of the reference layer 2 does not disappear (Condition 2.sub.L in FIG. 9). In Condition 2.sub.L, although the bias field (Hb) is unnecessary, it cannot be turned on or off at high speed. Therefore, the bias field (Hb) is left applied inevitably.
However, since the coersivity H.sub.C2 is maintained high, the direction of magnetization of the reference layer 2 will not be reversed due to the field Hb. Since the medium is moving, a given irradiated portion is immediately separated from the laser beam and is cooled by air. As cooling progresses, magnetization of the recording layer 1 appears. The direction of magnetization is influenced by that of the reference layer 2 due to the magnetic coupling force. As a result, magnetization (the P type medium) or (the A type medium) appears in accordance with the type of the medium. This magnetization is not changed even at the room temperature (Condition 3.sub.L in FIG. 9).
A change in conditions due to low-level laser beam irradiation is called a low-temperature cycle herein.
FIG. 10 summarizes the above descriptions. Referring to FIG. 10, bits, having either magnetization or , which are opposite to each other, are formed in the high- and low-temperature cycles regardless of the direction of magnetization in the recording layer 1. More specifically, an over-write operation is enabled by pulse modulating the laser beam between high level (high-temperature cycle) and low level (low-temperature cycle) in accordance with data to be recorded.
Note that the recording medium normally has a disk shape, and is rotated during recording. For this reason, a recorded portion (bit) is again influenced by the initial field (Hini.) during a single rotation. As a result, the direction of magnetization of the reference layer 2 is aligned along the original "A direction" . However, at the room temperature, magnetization of the reference layer can no longer influence that of the recording layer 1, and the recorded data can be held.
If linearly polarized light is radiated onto the recording layer 1, since light reflected thereby includes data, data can be reproduced as in the conventional magnetooptical recording medium.
However, a presently available material of the second layer has a larger magnetooptical effect than that of the first layer. Therefore, if data is left in the second layer like in a state immediately after recording, data can be reproduced from light reflected by the second layer to have a high C/N ratio.
When the disk-shaped medium after recording is influenced by the initial field Hini. and the second layer is magnetized in the A direction or the non-A direction , the direction of some bits recorded on the first layer is unnatural with respect to that of the second layer. More specifically, in the P type medium the direction of some bits of the first layer is antiparallel to the direction of magnetization of the second layer. In the A type medium, the direction of some bits of the first layer is parallel to the direction of magnetization of the second layer. In this case, a magnetic wall is formed between the first and second layers, and a rather unstable state is set.
Therefore, when a reproduction field H.sub.R in a direction opposite to that of the field Hini. is applied to the medium in this state, the magnetization of the portion of the second layer where the magnetic wall is formed is reversed upon influence of the bits of the first layer. As a result, the magnetic wall is extinguished, and a stable state can be established. This state is the same as that immediately after recording. Therefore, since recorded data also appears in the second layer, data can be reproduced from the second layer.
Therefore, the present invention also provides the following reproduction method.
More specifically, a reproduction method for over write capable magnetooptical recording is characterized in that in a disk-shaped multilayered magnetooptical recording medium capable of over writing comprising a first layer, serving as a recording layer, in which data is recorded in the form of a bit having upward magnetization and a bit having downward magnetization and which has a perpendicular magnetic anisotropy, and a second layer, serving as a reference layer, which has a perpendicular magnetic anisotropy having magnetization aligned in an upward or downward direction, data recorded in the first layer is transcribed to the second layer upon application of a reproduction magnetic field before reproduction, and the transcribed data is reproduced.
The present invention provides the following reproduction apparatus.
A reproduction apparatus for magnetooptical recording, is characterized by comprising:
(a) means for rotating a disk-shaped multilayered magnetooptical recording medium capable of over writing comprising a first layer, serving as a recording layer, in which data is recorded in the form of a bit having upward magnetization and a bit having downward magnetization and which has a perpendicular magnetic anisotropy, and a second layer, serving as a reference layer, which has a perpendicular magnetic anisotropy having magnetization aligned in an upward or downward direction;
(b) reproduction magnetic field applying means for transcribed data recorded in the first layer to the second layer;
(c) a linearly polarized light source; and
(d) reproduction means for receiving reflection light of the linearly polarized light radiated on the second layer and reproducing data included in the reflection light in the form of an electrical signal.
The intensity of a reproduction field H.sub.R preferably satisfies the following condition:
where
H.sub.C 2: coersivity of second layer
M.sub.S 2: saturation magnetic moment of second layer
t.sub.2 : film thickness of second layer
.sigma..sub.w : interface magnetic wall energy
H.sub.R : reproduction field
A perpendicular magnetic film constituting the recording layer 1 and the reference layer 2 is selected from the group consisting of (1) crystalline or amorphous ferromagnetic or ferrimagnetic materials having the Curie temperature and no compensation temperature, and (2) crystalline or amorphous ferrimagnetic materials having both the compensation temperature and the Curie temperature.
The first aspect utilizing the Curie temperature has been described. In contrast to this, the second aspect of the present invention utilizes decreased coersivity HC at a predetermined temperature exceeding the room temperature. The second aspect uses a temperature T.sub.S1 at which the recording layer 1 is magnetically coupled to the reference layer 2, in place of the temperature T.sub.C1 in the first aspect. In addition, instead of the temperature T.sub.C2, a temperature T.sub.S2 at which the reference layer 2 is reversed under the influence of the field Hb is used. Thereby, the second aspect can provide the same effect as in the first aspect.
In the second aspect, the coersivity of the recording layer 1 is represented by H.sub.C1 ; that of the reference layer 2, H.sub.C2 ; a temperature at which the recording layer 1 is magnetically coupled to the reference layer 2, T.sub.S1 ; a temperature at which the direction of magnetization of the reference layer 2 is reversed upon influence of the field Hb, T.sub.S2 ; room temperature, T.sub.R ; a temperature of the medium when a low-level laser beam is applied thereto, T.sub.L ; a temperature of the medium when a high-level laser beam is applied thereto, T.sub.H ; a coupling field applied to the recording layer 1, H.sub.D1 ; and a coupling field applied to the reference layer 2, H.sub.D2. In this case, the recording medium satisfies the following Formula 6, and satisfies Formulas 7 to 10 at the room temperature.
In the above formulas, upper signs of double signs .+-. and .-+. correspond to an A (antiparallel) type medium, and lower signs correspond to a P (parallel) medium (these media will be described later).
In the first and second aspects, the recording medium is constituted by the recording layer 1 and the reference layer 2, each of which preferably comprises an amorphous ferrimagnetic material selected from transition metal (e.g., Fe, Co) - heavy rare earth metal (e.g., Gd, Tb, Dy, and the like) alloy compositions.
When the recording layer 1 and the reference layer 2 are both selected from the transition metal - heavy rare earth metal alloy compositions, the direction and level of magnetization appearing outside the alloy are determined by the relationship between the direction and level of spin (magnetic moment) of transition metal atoms (to be referred to as TM hereinafter) and those of heavy rare earth metal atoms (to be referred to as RE hereinafter) inside the alloy. For example, the direction and level of TM spin are represented by a vector .uparw., those of RE spin are also indicated by a vector .dwnarw., and the direction and level of magnetization of the alloy as a whole are represented by a double-solid vector . In this case, the vector is represented by a sum of vectors .uparw. and .dwnarw.. However, in the alloy, the vectors .uparw. and .dwnarw. are directed in the opposite directions due to the mutual effect of the TM spin and the RE spin. Therefore, when these vectors are equal to each other, the sum of TM and RE vectors .dwnarw. and .uparw. is zero (i.e., the level of magnetization appearing outside the alloy is zero . The alloy composition making the sum of vectors zero is called a compensation composition. When the alloy has another composition, it has a strength equal to a difference between the strengths of both the spins, and has a vector ( or ) having a direction equal to that of the larger of the TM and RE vector. Magnetization of this vectors appears outside the alloy.
When one of the strengths of the vectors of the RE spin and TM spin is larger than the other, the alloy composition is referred to as "oo rich" named after the larger spin name (e.g., RE rich).
The recording layer 1 and the reference layer 2 can be classified into TM rich and RE rich compositions. Therefore, if the composition of the recording layer 1 is plotted along the ordinate and that of the reference layer 2 is plotted along the abscissa, the types of the recording media according to the present invention can be classified into four quadrants, as shown in FIG. 11. The P type medium described previously belongs to Quadrant I and III, and the A type medium belongs to Quadrant II and IV. Referring to FIG. 11, the intersection (origin) of the abscissa and the ordinate represents the compensation composition of both the layers.
In view of a change in coersivity against a change in temperatures, a certain alloy composition has characteristics wherein the coersivity temporarily increases infinitely and then abruptly decreases before a temperature reaches the Curie temperature (at which the coersivity is zero). The temperature corresponding to the infinite coersivity is called a compensation temperature (Tcomp.). No compensation temperature is present between the room temperature and the Curie temperature in the TM rich alloy composition. The compensation temperature below the room temperature is nonsense in the magnetooptical recording, and hence, it is assumed in this specification that the compensation temperature is present between the room temperature and the Curie temperature.
If the first and second layers are classified in view of the presence/absence of the compensation temperature, the recording medium can be classified into four types. The recording medium in Quadrant I includes all the four types of media. The graphs of FIGS. 12A to 12D respectively show the relationship between the coersivity and the temperature of the four types of media. Note that thin curves represent characteristics of the recording layer 1 and bold curves represent those of reference layer 2.
When the recording layer 1 and the reference layer 2 are classified in view of their RE or TM rich characteristics and in view of the presence/absence of the compensation temperature, they can be classified into 9 classes.
The principle of the method of the present invention will be described in detail using a specific medium No. 1 belonging to Class 1 (P type, Quadrant I, Type 1) shown in Table 1.
The medium No. 1 satisfies Formula 11:
The graph of FIG. 13 shows this relation. Note that thin curves indicate the first layer, and bold curves indicate the second layer. Those identifications are the same in the following graphs.
A condition that reverses the direction of magnetization of the reference layer 2 without reversing that of the recording layer 1 by the initial field (Hini.) at the room temperature T.sub.R is represented by Formula 12. The medium No. 1 satisfies Formula 12 at the T.sub.R.
where
H.sub.C1 : coersivity of recording layer 1
H.sub.C2 : coersivity of reference layer 2
M.sub.S1 : saturation magnetization of layer 1
M.sub.S2 : saturation magnetization of layer 2
t.sub.1 : film thickness of layer 1
t.sub.2 : film thickness of layer 2
.sigma..sub.w : interface wall energy
At this time, a condition for the Hini. is represented by Formula 15. If the Hini. disappears, reversed magnetization of the reference layer 2 is influenced by magnetization of the recording layer 1 due to an exchange coupling force. The condition that can hold the direction of magnetization of the layer 2 is represented by Formulas 13 and 14. The medium No. 1 satisfies Formulas 13 and 14.
The layer 2's magnetization of the recording medium which can satisfy Formulas 12 to 14 at the T.sub.R is aligned along the "A direction" (.uparw..dwnarw.) by the Hini. which satisfies Formula 15. At this time, the recording layer 1 is maintained in the recorded state (Condition 1 in FIGS. 14 and 15).
Condition 1 is held to a point immediately before the recording. In this case, the bias field (Hb) is applied in the direction of .uparw..
The high-temperature cycle will now be described with reference to FIG. 14.
HIGH-TEMPERATURE CYCLE
In Condition 1, when the medium temperature is increased to T.sub.L upon irradiation of the high-level laser beam, since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears (Condition 2.sub.H).
When the laser-beam radiation further continues, the temperature of the medium increases accordingly. When the temperature of the medium slightly exceeds the temperature Tcomp.2 of the reference layer 2, the relationship between the strengths of the RE and TM vectors is reversed (.uparw..dwnarw..fwdarw..uparw..dwnarw.) although the directions of the RE and TM spins remain the same. For this reason, the direction of magnetization of the layer 2 is reversed to be along the "non-A direction" (Condition 3.sub.H).
However, since the coersivity H.sub.C2 is still high at this temperature, the direction of magnetization of the layer 2 will not be reversed by the field Hb (.uparw.). When the temperature further increases and reaches the temperature T.sub.H, the temperature of the layer 2 substantially corresponds to the Curie temperature T.sub.C2, and magnetization of the layer 2 also disappears (Condition 4.sub.H).
In Condition 4.sub.H, when an irradiated portion is separated from the laser beam spot, the temperature of the medium begins to decrease. When the temperature of the medium decreases slightly below the temperature T.sub.C2, magnetization appears in the layer 2. In this case, magnetization (.dwnarw..uparw.) is generated by .uparw.Hb (Condition 5.sub.H). However, since the temperature is yet higher than the temperature T.sub.C1, no magnetization appears in the layer 1.
When the temperature of the medium further decreases below the temperature Tcomp.2, the relationship between the strengths of the RE and TM vectors is reversed (.dwnarw..uparw..fwdarw..dwnarw..uparw.) although the directions of the RE and TM spins remain the same. As a result, the direction of magnetization of the alloy as a whole is reversed from to the "non-A direction" (Condition 6.sub.H).
In Condition 6.sub.H, since the temperature of the medium is higher than the temperature T.sub.C1, magnetization of the layer 1 has not yet appeared. In addition, since the coersivity H.sub.C2 at this temperature is high, the direction of magnetization of the layer 2 cannot be reversed by the field .uparw.Hb.
When the temperature of the medium decreases and is slightly below the temperature T.sub.C1, magnetization appears in the layer 1. At this time, the exchange coupling force from the layer 2 acts to align each of the RE and TM spins (.dwnarw. and .uparw.) of the layers 1 and 2. Since the temperature of the layer 1 is higher than the temperature Tcomp.1, the TM spin is larger than the RE spin, and hence, magnetization of .dwnarw..uparw., i.e. appears in the layer 1. This state is Condition 7.sub.H.
When the temperature of the medium is decreased from the temperature in Condition 7.sub.H and is below the temperature Tcomp.1, the relationships between the strengths of the RE and TM spins of the layer 1 is reversed (.dwnarw..uparw..fwdarw..dwnarw..uparw.). As a result, magnetization of appears (Condition 8.sub.H).
Then, the temperature of the medium decreases from the temperature in Condition 8.sub.H to the room temperature. Since the coersivity H.sub.C1 at the room temperature is sufficiently high, Condition 8.sub.H is maintained without reversing the direction of magnetization of the layer 1 by the field .uparw.Hb. In this way, bit formation in the "non-A direction" is completed.
Next, the low-temperature cycle will be described with reference to FIG. 15.
LOW-TEMPERATURE CYCLE
In Condition 1 immediately before recording, the medium temperature is increased to T.sub.L upon irradiation of the low-level laser beam. Since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears (Condition 2.sub.L).
In Condition 2.sub.L, when an irradiated portion is separated from the laser beam spot, the medium temperature begins to fall. When the medium temperature is slightly below the temperature T.sub.C1, the recording layer 1 is influenced by the RE and TM spins (.uparw..dwnarw.) of the reference layer 2 due to the exchange coupling force. In other words, the exchange coupling force acts to align each of the RE and TM spins (.uparw.and .dwnarw.) of the layers 1 and 2. As a result, magnetization of .uparw..dwnarw., i.e., , without regard to the bias field .uparw.Hb, appears in the layer 1 (Condition 3.sub.L). Since the temperature in Condition 3.sub.L is higher than the temperature Tcomp.1, the TM spin is larger than the RE spin.
When the medium temperature is decreased below the temperature Tcomp.1, the relationship between the RE and TM spins of the first layer is reversed (.uparw..dwnarw..fwdarw..uparw..dwnarw.) in the same manner as in the high-temperature cycle. As a result, the magnetization of the layer 1 is (Condition 4.sub.L).
Condition 4.sub.L is maintained even if the medium temperature is decreased to the room temperature. In this way, bit formation in the "A direction" is completed.
The principle of the method of the present invention will be described in detail using a specific medium No. 2 belonging to Class 2 (P type, Quadrant I, Type 2) shown in Table 1.
The medium No. 2 satisfies Formula 16:
The graph of FIG. 16 shows this relation.
A condition that reverses the direction of magnetization of the reference layer 2 without reversing that of the recording layer 1 by the initial field (Hini.) at the room temperature T.sub.R is represented by Formula 17. The medium No. 2 satisfies Formula 17 at the T.sub.R :
where
H.sub.C1 : coersivity of recording layer 1
H.sub.C2 : coersivity of reference layer 2
M.sub.S1 : saturation magnetization of layer 1
M.sub.S2 : saturation magnetization of layer 2
t.sub.1 : film thickness of layer 1
t.sub.2 : film thickness of layer 2
.sigma..sub.w : interface wall energy
At this time, a condition for the Hini. is represented by Formula 20. If the Hini. disappears, reversed magnetization of the reference layer 2 is influenced by magnetization of the recording layer 1 due to an exchange coupling force. The condition that can hold the direction of magnetization of the layer 2 is represented by Formulas 18 and 19. The medium No. 2 satisfies Formulas 18 and 19.
The layer 2's magnetization of the recording medium which can satisfy Formulas 17 to 19 at the T.sub.R is aligned along the "A direction" (.uparw..dwnarw.) by the Hini. which satisfies Formula 20. At this time, the recording layer 1 is maintained in the recorded state (Condition 1 in FIGS. 17 and 18).
Condition 1 is held to a point immediately before the recording. In this case, the bias field (Hb) is applied in the direction of .uparw..
The high-temperature cycle will now be described with reference to FIG. 17. HIGH-TEMPERATURE CYCLE
In Condition 1, when the medium temperature is increased to T.sub.L upon irradiation of the high-level laser beam, since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears (Condition 2.sub.H)
When the laser-beam radiation further continues, the temperature of the medium increases accordingly. When the temperature of the medium slightly exceeds the temperature Tcomp.2 of the reference layer 2, the relationship between the strengths of the RE and TM vectors is reversed (.uparw..dwnarw..fwdarw..uparw..dwnarw.) although the directions of the RE and TM spins remain the same. For this reason, the direction of magnetization of the layer 2 is reversed to the "non-A direction" (Condition 3.sub.H).
However, since the coersivity H.sub.C2 is still high at this temperature, the direction of magnetization of the layer 2 will not be reversed by the field Hb(.uparw.). When the temperature further increases and reaches the temperature T.sub.H, the temperature of the layer 2 substantially corresponds to the Curie temperature T.sub.C2, and magnetization of the layer 2 also disappears (Condition 4.sub.H).
In Condition 4.sub.H, when an irradiated portion is separated from the laser beam spot, the temperature of the medium begins to decrease. When the temperature of the medium decreases slightly below the temperature T.sub.C2, magnetization appears in the layer 2. In this case, magnetization (.dwnarw..uparw.) is generated by .uparw.Hb (Condition 5.sub.H). However, since the temperature is yet higher than the temperature T.sub.C1, no magnetization appears in the layer 1.
When the temperature of the medium further decreases below the temperature Tcomp.2, the relationship between the strengths of the RE and TM vectors is reversed (.dwnarw..uparw..fwdarw..dwnarw..uparw.) although the directions of the RE and TM spins remain the same. As a result, the direction of magnetization of the alloy as a whole is reversed from to the "non-A direction" (Condition 6.sub.H).
In Condition 6.sub.H, since the temperature of the medium is higher than the temperature T.sub.C1, magnetization of the layer 1 has not yet appeared. In addition, since the coersivity H.sub.C2 at this temperature is high, the direction of magnetization of the layer 2 cannot be reversed by the field .uparw.Hb.
When the temperature of the medium decreases and is slightly below the temperature T.sub.C1, magnetization appears in the layer 1. At this time, the exchange coupling force from the layer 2 acts to align each of the RE and TM spins (.dwnarw. and .uparw.) of the layers 1 and 2. Thus, magnetization of .dwnarw..uparw., i.e., appears in the layer 1. This state is Condition 7.sub.H.
Then, the temperature of the medium decreases from the temperature in Condition 7.sub.H to the room temperature. Since the coersivity H.sub.C1 at the room temperature is sufficiently high, Condition 7.sub.H is maintained without reversing the direction of magnetization of the layer 1 by the field .uparw.Hb. In this way, bit formation in the "non-A direction" is completed.
Next, the low-temperature cycle will be described with reference to FIG. 18.
LOW-TEMPERATURE CYCLE
In Condition 1 immediately before recording, the medium temperature is increased to T.sub.L upon irradiation of the low-level laser beam. Since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears (Condition 2.sub.L).
In Condition 2.sub.L, when an irradiated portion is separated from the laser beam spot, the medium temperature begins to fall. When the medium temperature is slightly below the temperature T.sub.C1, the recording layer 1 is influenced by the RE and TM spins (.uparw..dwnarw.) of the reference layer 2 due to the exchange coupling force. In other words, the exchange coupling force acts to align each of the RE and TM spins (.uparw. and .dwnarw.) of the layers 1 and 2. As a result, magnetization of .uparw..dwnarw., i.e., , appears in the layer 1 (Condition 3.sub.L).
Condition 3.sub.L is maintained even if the medium temperature is decreased to the room temperature. As a result, a bit in the "A direction" is formed in the recording layer 1.
The principle of the method of the present invention will be described in detail using a specific medium No. 3 belonging to Class 3 (P type, Quadrant I, Type 3) shown in Table 1.
The medium No. 3 satisfies Formula 21:
The graph of FIG. 19 shows this relation.
A condition that reverses the direction of magnetization of the reference layer 2 without reversing that of the recording layer 1 by the initial field (Hini.) at the room temperature T.sub.R is represented by Formula 22. The medium No. 3 satisfies Formula 22 at the T.sub.R :
where
H.sub.C1 : coersivity of recording layer 1
H.sub.C2 : coersivity of reference layer 2
M.sub.S1 : saturation magnetization of layer 1
M.sub.S2 : saturation magnetization of layer 2
t.sub.1 : film thickness of layer 1
t.sub.2 : film thickness of layer 2
.sigma..sub.w : interface wall energy
At this time, a condition for the Hini. is represented by Formula 25. If the Hini. disappears, reversed magnetization of the reference layer 2 is influenced by magnetization of the recording layer 1 due to an exchange coupling force. The condition that can hold the direction of magnetization of the layer 2 is represented by Formulas 23 and 24. The medium No. 3 satisfies Formulas 23 and 24.
The layer 2's magnetization of the recording medium which can satisfy Formulas 22 to 24 at the T.sub.R is aligned along the "A direction" (.uparw..dwnarw.) by the Hini. which satisfies Formula 25. At this time, the recording layer 1 is maintained in the recorded state (Condition 1 in FIGS. 20 and 21).
Condition 1 is held to a point immediately before the recording. In this case, the bias field (Hb) is applied in the direction of .dwnarw..
The high-temperature cycle will now be described with reference to FIG. 20.
HIGH-TEMPERATURE CYCLE
In Condition 1, when the medium temperature is increased to T.sub.L upon irradiation of the high-level laser beam, since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears (Condition 2.sub.H).
When the laser-beam radiation further continues, since the temperature T.sub.H of the medium is substantially equal to the temperature T.sub.C2, magnetization of the layer 2 also disappears (Condition 3.sub.H).
In Condition 3.sub.H, when an irradiated portion is separated from the laser beam spot, the temperature of the medium begins to decrease. When the temperature of the medium decreases slightly below the temperature T.sub.C2, magnetization appears in the layer 2. In this case, magnetization (.dwnarw..uparw.) is generated by .dwnarw.Hb. However, since the temperature is yet higher than the temperature T.sub.C1, no magnetization appears in the layer 1. This state is Condition 4.sub.H.
When the temperature of the medium decreases and is slightly below the temperature T.sub.C1, magnetization appears in the layer 1. At this time, the exchange coupling force from the layer 2 acts to align each of the RE and TM spins (.dwnarw. and .uparw.) of the layers 1 and 2. Since the temperature of the medium is higher than the temperature Tcomp.1, the TM spin is larger than the RE spin (.dwnarw..uparw.). As a result, magnetization of appears in the layer 1 (Condition 5.sub.H).
When the medium temperature further decreases from the temperature in Condition 5.sub.H and is below the temperature Tcomp.1, the relationship between the strengths of the TM and RE spins of the layer 1 is reversed (.dwnarw..uparw..fwdarw..dwnarw..uparw.). For this reason, the direction of magnetization of the layer 1 is reversed to the "non-A direction" (Condition 6.sub.H).
Then, the temperature of the medium decreases from the temperature in Condition 6.sub.H to the room temperature. Since the coersivity H.sub.C1 at the room temperature is sufficiently high, magnetization of the layer 1 is stably maintained. In this way, bit formation in the "non-A direction" is completed.
Next, the low-temperature cycle will be described with reference to FIG. 21.
LOW-TEMPERATURE CYCLE
In Condition 1 immediately before recording, the medium temperature is increased to T.sub.L upon irradiation of the low-level laser beam. Since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears. However, at this temperature, since the coersivity H.sub.C2 of the layer 2 is sufficiently high, magnetization of the layer 2 will not be reversed by the bias field .dwnarw.Hb (Condition 2.sub.L).
In Condition 2.sub.L, when an irradiated portion is separated from the laser beam spot, the medium temperature begins to fall. When the medium temperature is slightly below the temperature T.sub.C1, the respective spins of the recording layer 1 are influenced by the RE and TM spins (.uparw..dwnarw.) of the reference layer 2 due to the exchange coupling force. In other words, the exchange coupling force acts to align each of the RE and TM spins (.uparw. and .dwnarw.) of the layers 1 and 2. As a result, magnetization of .uparw..dwnarw., i.e., , appears in the layer 1. In this case, since the medium temperature is higher than the temperature Tcomp.1, the TM spin is larger than the RE spin (Condition 3.sub.L).
When the medium temperature is further decreased below the temperature Tcomp.1, the relationship between the strengths of the RE and TM spins of the layer 1 is reversed in the same manner as in the high-temperature cycle (.uparw..dwnarw..fwdarw..uparw..dwnarw.). As a result, magnetization of , without regard to the bias field .dwnarw.Hb, appears in the layer 1 (Condition 4.sub.L).
Condition 4.sub.L is maintained even if the medium temperature is decreased to the room temperature. In this way, bit formation in the "A direction" is completed.
The principle of the method of the present invention will be described in detail using a specific medium No. 4 belonging to Class 4 (P type, Quadrant I, Type 4) shown in Table 1.
The medium No. 4 satisfies Formula 26:
The graph of FIG. 22 shows this relation.
A condition that reverses the direction of magnetization of the reference layer 2 without reversing that of the recording layer 1 by the initial field (Hini.) at the room temperature T.sub.R is represented by Formula 27. The medium No. 4 satisfies Formula 27 at the T.sub.R :
where
H.sub.C1 : coersivity of recording layer 1
H.sub.C2 : coersivity of reference layer 2
M.sub.S1 : saturation magnetization of layer 1
M.sub.S2 : saturation magnetization of layer 2
t.sub.1 : film thickness of layer 1
t.sub.2 : film thickness of layer 2
.sigma..sub.w : interface wall energy
At this time, a condition for the Hini. is represented by Formula 30. If the Hini. disappears, reversed magnetization of the reference layer 2 is influenced by magnetization of the recording layer 1 due to an exchange coupling force. The condition that can hold the direction of magnetization of the layer 2 is represented by Formulas 28 and 29. The medium No. 4 satisfies Formulas 28 and 29.
The layer 2's magnetization of the recording medium which can satisfy Formulas 27 to 29 at the T.sub.R is aligned along the "A direction" (.uparw..dwnarw.) by the Hini. which satisfies Formula 30. At this time, the recording layer 1 is maintained in the recorded state (Condition 1 in FIGS. 23 and 24).
Condition 1 is held to a point immediately before the recording. In this case, the bias field (Hb) is applied in the direction of .dwnarw..
The high-temperature cycle will now be described with reference to FIG. 23.
HIGH-TEMPERATURE CYCLE
When the medium temperature is increased to T.sub.L upon irradiation of the high-level laser beam, since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears (Condition 2.sub.H).
When the laser-beam radiation further continues and the medium temperature is equal to the temperature T.sub.H, since the temperature T.sub.H of the layer 2 is substantially equal to the Curie temperature T.sub.C2, magnetization of the layer 2 also disappears. This state is Condition 3.sub.H.
In Condition 3.sub.H, when an irradiated portion is separated from the laser beam spot, the temperature of the medium begins to decrease. When the temperature of the medium decreases slightly below the temperature T.sub.C2, magnetization of the layer 2 appears. In this case, magnetization (.dwnarw..uparw.) is generated by .dwnarw.Hb. However, since the temperature is yet higher than the temperature T.sub.C1, no magnetization appears in the layer 1. This state is Condition 4.sub.H.
When the temperature of the medium decreases and is slightly below the temperature T.sub.C1, magnetization appears in the layer 1. At this time, the exchange coupling force from the layer 2 acts to align each of the RE and TM spins (.dwnarw. and .uparw.) of the layers 1 and 2. As a result, magnetization of .dwnarw..uparw., i.e., appears in the layer 1. This state is Condition 5.sub.H.
Then, the temperature of the medium decreases from the temperature in Condition 5.sub.H to the room temperature. Since the coersivity H.sub.C1 at the room temperature is sufficiently high, magnetization of the layer 1 is stably maintained. In this way, bit formation in the "non-A direction" is completed.
Next, the low-temperature cycle will be described with reference to FIG. 24.
LOW-TEMPERATURE CYCLE
In Condition 1 immediately before recording, the medium temperature is increased to T.sub.L upon irradiation of the low-level laser beam. Since the temperature T.sub.L exceeds the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears. However, at this temperature, since the coersivity H.sub.C2 of the layer 2 is sufficiently high, magnetization of the layer 2 will not be reversed by the bias field .dwnarw.Hb. This state is Condition 2.sub.L
In Condition 2.sub.L, when an irradiated portion is separated from the laser beam spot, the medium temperature begins to fall. When the medium temperature is slightly below the temperature T.sub.C1, the respective spins of the recording layer 1 are influenced by the RE and TM spins (.uparw..dwnarw.) of the reference layer 2 due to the exchange coupling force. In other words, the exchange coupling force acts to align each of the RE and TM spins (.uparw. and .dwnarw.) of the layers 1 and 2. As a result, magnetization of .uparw..dwnarw., i.e., , without regard to the bias field .dwnarw.Hb, appears in the layer 1. This state is Condition 3.sub.L.
Condition 3.sub.L is maintained even if the medium temperature is decreased to the room temperature. In this way, bit formation in the "A direction" is completed.
The principle of the method of the present invention will be described in detail using a specific medium No. 5 belonging to Class 5 (A type, Quadrant II, type 3) shown in Table 1.
The medium No. 5 satisfies Formula 31:
The graph of FIG. 25 shows this relation.
A condition that reverses the direction of magnetization of the reference layer 2 without reversing that of the recording layer 1 by the initial field (Hini.) at the room temperature T.sub.R is represented by Formula 32. The medium No. 5 satisfies Formula 32 at the T.sub.R :
where
H.sub.C1 : coersivity of recording layer 1
H.sub.C2 : coersivity of reference layer 2
M.sub.S1 : saturation magnetization of layer 1
M.sub.S2 : saturation magnetization of layer 2
t.sub.1 : film thickness of layer 1
t.sub.2 : film thickness of layer 2
.sigma..sub.w : interface wall energy
At this time, a condition for the Hini. is represented by Formula 35. If the Hini. disappears, reversed magnetization of the reference layer 2 is influenced by magnetization of the recording layer 1 due to an exchange coupling force. The condition that can hold the direction of magnetization of the layer 2 is represented by Formulas 33 and 34. The medium No. 5 satisfies Formulas 33 and 34.
The layer 2's magnetization of the recording medium which can satisfy Formulas 32 to 34 at the T.sub.R is aligned along the "A direction" (.dwnarw..uparw.) by the Hini. which satisfies Formula 35. At this time, the recording layer 1 is maintained in the recorded state (Condition 1 in FIGS. 26 and 27).
Condition 1 is held to a point immediately before the recording. In this case, the bias field (Hb) is applied in the direction of .dwnarw..
The high-temperature cycle will now be described with reference to FIG. 26.
HIGH-TEMPERATURE CYCLE
When the medium temperature is increased to T.sub.L upon irradiation of the high-level laser beam, since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears (Condition 2.sub.H).
When the laser-beam radiation further continues and the medium temperature is equal to the temperature T.sub.H, since the temperature T.sub.H of the layer 2 is substantially equal to the Curie temperature T.sub.C2, magnetization of the layer 2 also disappears (Condition 3.sub.H).
In Condition 3.sub.H, when an irradiated portion is separated from the laser beam spot, the temperature of the medium begins to decrease. When the temperature of the medium decreases slightly below the temperature T.sub.C2, magnetization of the layer 2 appears. In this case, magnetization (.uparw..dwnarw.) is generated by .dwnarw.Hb. However, since the temperature is yet higher than the temperature T.sub.C1, no magnetization appears in the layer 1. This state is Condition 4.sub.H.
When the temperature of the medium is further decreased slightly below the temperature T.sub.C1, magnetization appears in the layer 1. At this time, the exchange coupling force from the layer 2 acts to align each of the RE and TM spins (.uparw. and .dwnarw.) of the layers 1 and 2. In this case, since the medium temperature is yet higher than the temperature Tcomp.1, the TM spin is larger than the RE spin (.uparw..dwnarw.). As a result, magnetization of appears in the layer 2 (Condition 5.sub.H).
When the medium temperature is decreased below the temperature Tcomp.1 from the temperature in Condition 5.sub.H, the relationship between the strengths of the TM and RE spins of the layer 1 is reversed (.uparw..dwnarw..fwdarw..uparw..dwnarw.). For this reason, magnetization of the layer 1 is reversed to the "A-direction" (Condition 6.sub.H).
Then, the temperature of the medium decreases from the temperature in Condition 6.sub.H to the room temperature. Since the coersivity H.sub.C1 at the room temperature is sufficiently high, magnetization of the layer 1 is stably maintained. In this way, bit formation in the "A direction" is completed.
Next, the low-temperature cycle will be described with reference to FIG. 27.
LOW-TEMPERATURE CYCLE
In Condition 1 immediately before recording, the medium temperature is increased to T.sub.L upon irradiation of the low-level laser beam. Since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears. However, at this temperature, since the coersivity H.sub.C2 of the layer 2 is sufficiently high, magnetization of the layer 2 will not be reversed by the bias field .dwnarw.Hb (Condition 2.sub.L).
When the beam radiation is completed in Condition 2.sub.L, the medium temperature begins to fall. When the medium temperature is slightly below the temperature T.sub.C1, the respective spins of the recording layer 1 are influenced by the RE and TM spins (.dwnarw..uparw.) of the reference layer 2 due to the exchange coupling force. In other words, the exchange coupling force acts to align each of the RE and TM spins and (.dwnarw. and .uparw.) of the layers 1 and 2. As a result, magnetization of .dwnarw..uparw., i.e., , without regard to bias field .dwnarw.Hb, appears in the layer 1. In this case, since the medium temperature is higher than the temperature Tcomp.1, the TM spin is larger than the RE spin (Condition 3.sub.L).
When the medium temperature is decreased below the temperature Tcomp.1, the relationship between the strengths of the RE and TM spins of the layer 1 is reversed as well as the high-temperature cycle (.dwnarw..uparw..fwdarw..dwnarw..uparw.) As a result, the magnetization of the layer 1 is (Condition 4.sub.L).
Condition 4.sub.L is maintained even if the medium temperature is decreased to the room temperature. In this way, bit formation in the "non-A direction" is completed.
The principle of the method of the present invention will be described in detail using a specific medium No. 6 belonging to Class 6 (A type, Quadrant II, Type 4) shown in Table 1.
The medium No. 6 satisfies Formula 36
The graph of FIG. 28 shows this relation.
A condition that reverses the direction of magnetization of the reference layer 2 without reversing that of the recording layer 1 by the initial field (Hini.) at the room temperature T.sub.R is represented by Formula 37. The medium No. 6 satisfies Formula 37 at the T.sub.R :
where
H.sub.C1 : coersivity of recording layer 1
H.sub.C2 : coersivity of reference layer 2
M.sub.S1 : saturation magnetization of layer 1
M.sub.S2 : saturation magnetization of layer 2
t.sub.1 : film thickness of layer 1
t.sub.2 : film thickness of layer 2
.sigma..sub.w : interface wall energy
At this time, a condition for the Hini. is represented by Formula 40. If the Hini. disappears, reversed magnetization of the reference layer 2 is influenced by magnetization of the recording layer 1 due to an exchange coupling force. The condition that can hold the direction of magnetization of the layer 2 is represented by Formulas 38 and 39. The medium No. 6 satisfies Formulas 38 and 39.
The layer 2's magnetization of the recording medium which can satisfy Formulas 37 to 39 at the T.sub.R is aligned along the "A direction" (.dwnarw..uparw.) by the Hini. which satisfies Formula 40. At this time, the recording layer 1 is maintained in the recorded state (Condition 1 in FIGS. 29 and 30).
Condition 1 is held to a point immediately before the recording. In this case, the bias field (Hb) is applied in the direction of .dwnarw..
The high-temperature cycle will now be described with reference to FIG. 29.
HIGH-TEMPERATURE CYCLE
In Condition 1 when the medium temperature is increased to T.sub.L upon irradiation of the high-level laser beam, since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears (Condition 2.sub.H).
When the laser-beam radiation further continues and the medium temperature is equal to the temperature T.sub.H, since the temperature T.sub.H of the layer 2 is substantially equal to the Curie temperature T.sub.C2, magnetization of the layer 2 also disappears. This state is Condition 3.sub.H.
In Condition 3.sub.H, when an irradiated portion is separated from the laser beam spot, the temperature of the medium begins to decrease. When the temperature of the medium decreases slightly below the temperature T.sub.C2, magnetization of the layer 2 appears. In this case, magnetization (.uparw..dwnarw.) is generated by .dwnarw.Hb. However, since the temperature is yet higher than the temperature T.sub.C1, no magnetization appears in the layer 1. This state is Condition 4.sub.H.
When the temperature of the medium is further decreased slightly below the temperature T.sub.C1, magnetization appears in the layer 1. At this time, the exchange coupling force from the layer 2 acts to align each of the RE and TM spins (.uparw. and .dwnarw.) of the layers 1 and 2. For this reason, magnetization .uparw..dwnarw., i.e., , without regard to the bias field .dwnarw.Hb, appears in the layer 1. This state is Condition 5.sub.H.
Then, the temperature of the medium decreases from the temperature in Condition 5.sub.H to the room temperature. Since the coersivity H.sub.C1 at the room temperature is sufficiently high, magnetization of the layer 1 is stably maintained. In this way, bit formation in the "A direction" is completed.
Next, the low-temperature cycle will be described with reference to FIG. 30.
LOW-TEMPERATURE CYCLE
In Condition 1 immediately before recording, the medium temperature is increased to T.sub.L upon irradiation of the low-level laser beam. Since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears. In this state, however, since the coersivity H.sub.C2 of the layer 2 is sufficiently high, magnetization of the layer 2 will not be reversed by the bias field .dwnarw.Hb. This state is Condition 2.sub.L.
In Condition 2.sub.L, when an irradiated portion is separated from the laser beam spot, the medium temperature begins to fall. When the medium temperature is slightly below the temperature T.sub.C1, the respective spins of the recording layer 1 are influenced by the RE and TM spins (.dwnarw..uparw.) of the reference layer 2 due to the exchange coupling force. In other words, the exchange coupling force acts to align each of the RE and TM spins (.dwnarw. and .uparw.) of the layers 1 and 2. As a result, magnetization of .dwnarw..uparw., i.e., , appears in the layer 1. This state is Condition 3.sub.L.
Condition 3.sub.L is maintained even if the medium temperature is decreased to the room temperature. In this way, bit formation in the "non-A direction" is completed.
The principle of the method of the present invention will be described in detail using a specific medium No. 7 belonging to Class 7 (P type, Quadrant III, Type 4) shown in Table 1.
The medium No. 7 satisfies Formula 41:
The graph of FIG. 31 shows this relation.
A condition that reverses the direction of magnetization of the reference layer 2 without reversing that of the recording layer 1 by the initial field (Hini.) at the room temperature T.sub.R is represented by Formula 42. The medium No. 7 satisfies Formula 42 at the T.sub.R :
where
H.sub.C1 : coersivity of recording layer 1
H.sub.C2 : coersivity of reference layer 2
M.sub.S1 : saturation magnetization of layer 1
M.sub.S2 : saturation magnetization of layer 2
t.sub.1 : film thickness of layer 1
t.sub.2 : film thickness of layer 2
.sigma..sub.w : interface wall energy
At this time, a condition for the Hini. is represented by Formula 45. If the Hini. disappears, reversed magnetization of the reference layer 2 is influenced by magnetization of the recording layer 1 due to an exchange coupling force. The condition that can hold the direction of magnetization of the layer 2 is represented by Formulas 43 and 44. The medium No. 7 satisfies Formulas 43 and 44.
The layer 2's magnetization of the recording medium which can satisfy Formulas 42 to 44 at the T.sub.R is aligned along the "A direction" (.dwnarw..uparw.) by the Hini. which satisfies Formula 45. At this time, the recording layer 1 is maintained in the recorded state (Condition 1 in FIGS. 32 and 33). Condition 1 is held to a point immediately before the recording. In this case, the base field (Hb) is applied in the direction of .dwnarw..
The high-temperature cycle will now be described with reference to FIG. 32.
HIGH-TEMPERATURE CYCLE
In Condition 1 when the medium temperature is increased to T.sub.L upon irradiation of the high level laser beam, since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears (Condition 2.sub.H).
When the laser-beam radiation continues and the medium temperature is equal to the temperature T.sub.H, since the temperature T.sub.H of the layer 2 is substantially equal to the Curie temperature T.sub.C2, magnetization of the layer 2 also disappears. This state is Condition 3.sub.H.
In Condition 3.sub.H, when an irradiated portion is separated from the laser beam spot, the temperature of the medium begins to decrease. When the temperature of the medium decreases slightly below the temperature T.sub.C2, magnetization of the layer 2 appears. In this case, magnetization (.uparw..dwnarw.) is generated by .dwnarw.Hb. However, since the temperature is yet higher than the temperature T.sub.C1, no magnetization appears in the layer 1. This state is Condition 4.sub.H. When the temperature of the medium is further decreased slightly below the temperature T.sub.C1, magnetization appears in the layer 1. At this time, the exchange coupling force from the layer 2 (.uparw..dwnarw.) acts to align each of the RE and TM spins (.uparw. and .dwnarw.) of the layers 1 and 2. For this reason, magnetization .uparw..dwnarw., i.e., appears in the layer 1. This state is Condition 5.sub.H.
Then, the temperature of the medium decreases from the temperature in Condition 5.sub.H to the room temperature. Since the coersivity H.sub.C1 at the room temperature is sufficiently high, magnetization of the layer 1 is stably maintained. In this way, bit formation in the "non-A direction" is completed.
Next, the low-temperature cycle will be described with reference to FIG. 33.
LOW-TEMPERATURE CYCLE
In Condition 1 immediately before recording, the medium temperature is increased to T.sub.L upon irradiation of the low-level laser beam. Since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears. In this state, however, since the coersivity H.sub.C2 of the layer 2 is sufficiently high, magnetization of the layer 2 will not be reversed by the bias field .dwnarw.Hb. This state is Condition 2.sub.L.
In Condition 2.sub.L, when an irradiated portion is separated from the laser beam spot, the medium temperature begins to fall. When the medium temperature is slightly below the temperature T.sub.C1, the respective spins of the recording layer 1 are influenced by the RE and TM spins (.uparw..dwnarw.) of the reference layer 2 due to the exchange coupling force. In other words, the exchange coupling force acts to align each of the RE and TM spins (.dwnarw. and .uparw.) of the layers 1 and 2. As a result, magnetization of .dwnarw..uparw., i.e., , without regard to the bias field Hb, appears in the layer 1. This state is Condition 3.sub.L.
Condition 3.sub.L is maintained even if the medium temperature is decreased to the room temperature. In this way, bit formation in the "A direction" is completed.
The principle of the method of the present invention will be described in detail using a specific medium No. 8 belonging to Class 8 (A type, Quadrant IV, Type 2) shown in Table 1.
The medium No. 8 satisfies Formula 46:
T.sub.R <T.sub.C1 .apprxeq.T.sub.L .apprxeq.Tcomp.2 <T.sub.C2 .apprxeq.T.sub.H
The graph of FIG. 34 shows this relation.
A condition that reverses the direction of magnetization of the reference layer 2 without reversing that of the recording layer 1 by the initial field (Hini.) at the room temperature T.sub.R is represented by Formula 47. The medium No. 8 satisfies Formula 47 at the T.sub.R :
where
H.sub.C1 : coersivity of recording layer 1
H.sub.C2 : coersivity of reference layer 2
M.sub.S1 : saturation magnetization of layer 1
M.sub.S2 : saturation magnetization of layer 2
t.sub.1 : film thickness of layer 1
t.sub.2 : film thickness of layer 2
.sigma..sub.w : interface wall energy
At this time, a condition for the Hini. is represented by Formula 50. If the Hini. disappears, reversed magnetization of the reference layer 2 is influenced by magnetization of the recording layer 1 due to an exchange coupling force. The condition that can hold the direction of magnetization of the layer 2 is represented by Formulas 48 and 49. The medium No. 8 satisfies Formulas 48 and 49.
The layer 2's magnetization of the recording medium which can satisfy Formulas 47 to 49 at the T.sub.R is aligned along the "A direction" (.uparw..dwnarw.) by the Hini. Which satisfies Formula 50. At this time the recording layer 1 is maintained in the recorded state (Condition 1 in FIGS. 35 and 36).
Condition 1 is held to a point immediately before the recording. In this case, the bias field (Hb) is applied in the direction of .uparw..
The high-temperature cycle will now be described with reference to FIG. 35.
HIGH-TEMPERATURE CYCLE
In Condition 1 when the medium temperature is increased to T.sub.L upon irradiation of the high-level laser beam, since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears (Condition 2.sub.H).
When the laser-beam radiation continues and the medium temperature is slightly higher than the temperature Tcomp.2, the relationship between the strengths of the RE and TM spins is reversed (.uparw..dwnarw..fwdarw..uparw..dwnarw.) although the directions thereof (.uparw. and .dwnarw.) remain the same. As a result, the direction of the magnetization of the layer 2 is reversed to "non-A direction" . This state is Condition 3.sub.H.
At this temperature, however, since the coersivity H.sub.C2 is yet high, magnetization of the layer 2 will not be reversed by the bias field .uparw.Hb. Assume that the laser-beam radiation further continues and the medium temperature is increased to T.sub.H. Since the temperature T.sub.H is substantially equal to the temperature T.sub.C2, magnetization of the layer 2 also disappears (Condition 4.sub.H).
In Condition 4.sub.H, when an irradiated portion is separated from the laser beam spot, the temperature of the medium begins to decrease. When the temperature of the medium decreases slightly below the temperature T.sub.C2, magnetization of the layer 2 appears. In this case, magnetization (.dwnarw..uparw.) is generated by .uparw.Hb. However, since the temperature is yet higher than the temperature T.sub.C1, no magnetization appears in the layer 1. This state is Condition 5.sub.H.
When the temperature of the medium is further decreased slightly below the temperature Tcomp. 1, the relationship between the strengths of the RE and TM spins is reversed (.dwnarw..uparw..fwdarw..dwnarw..uparw.) without reversing the directions thereof (.dwnarw. and .uparw.). As a result, the direction of magnetization of the layer 2 is reversed to "non-A direction" . In this state, since the coersivity H.sub.C2 is already sufficiently high, magnetization of the layer 2 will not be reversed by the bias field .uparw.Hb. In this case, since the medium temperature is yet higher than the temperature T.sub.C1, no magnetization appears in the layer 1. This state is Condition 6.sub.H.
When the medium temperature further decreases slightly below the temperature T.sub.C1, magnetization also appears in the layer 1. At this time, magnetization (.dwnarw..uparw.) of the layer 1 influences the layer 1 due to the exchange coupling force to align each of the RE and TM spins (.dwnarw. and .uparw.) of the layers 1 and 2. For this reason, magnetization .dwnarw..uparw., i.e., appears in the layer 1 (Condition 7.sub.H).
Then, the temperature of the medium decreases from the temperature in Condition 7.sub.H to the room temperature. Since the coersivity H.sub.C1 at the room temperature is sufficiently high, magnetization of the layer 1 is stably maintained. In this way, bit formation in the "A direction" is completed.
Next, the low-temperature cycle will be described with reference to FIG. 36.
LOW-TEMPERATURE CYCLE
In Condition 1 immediately before recording, the medium temperature is increased to T.sub.L upon irradiation of the low-level laser beam. Since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears. In this state, however, since the coersivity H.sub.C2 of the layer 2 is sufficiently high, magnetization of the layer 2 will not be reversed by the bias field .uparw.Hb (Condition 2L).
In Condition 2.sub.L, when an irradiated portion is separated from the laser beam spot, the medium temperature begins to fall. When the medium temperature begins to fall. When the medium temperature is slightly below the temperature T.sub.C1, the respective spins of the recording layer 1 are influenced by the RE and TM spins (.uparw..dwnarw.) of the reference layer 2 due to the exchange coupling force. In other words, the exchange coupling force acts to align each of the RE and TM spins (.uparw. and .dwnarw.) of the layers 1 and 2. As a result, magnetization of .uparw..dwnarw., i.e., , without regard to the bias field .dwnarw.Hb, appears in the layer 1. This state is Condition 3.sub.L.
Condition 3.sub.L is maintained even if the medium temperature is decreased to the room temperature. In this way, bit formation in the "non-A direction" is completed.
The principle of the method of the present invention will be descirbed in detail using a specific medium No. 9 belonging to Class 9 (A type, Quadrant IV, Type 4) shown in Table 1.
The medium No. 9 satisfies Formula 51:
The graph of FIG. 37 shows this relation.
A condition that reverses the direction of magnetization of the reference layer 2 without reversing that of the recording layer 1 by the initial field (Hini.) at the room temperature T.sub.R is represented by Formula 52. The medium No. 9 satisfies Formula 52 at the T.sub.R :
where
H.sub.C1 : coersivity of recording layer 1
H.sub.C2 : coersivity of reference layer 2
M.sub.S1 : saturation magnetization of layer 1
M.sub.S2 : saturation magnetization of layer 2
t.sub.1 : film thickness of layer 1
t.sub.2 : film thickness of layer 2
.sigma..sub.w : interface wall energy
At this time, a condition for the Hini. is represented by Formula 50. If the Hini. disappears, reversed magnetization of the reference layer 2 is influenced by magnetization of the recording layer 1 due to an exchange coupling force. The condition that can hold the direction of magnetization of the layer 2 is represented by Formulas 53 and 54. The medium No. 9 satisfies Formulas 53 and 54.
The layer 2's magnetization of the recording medium which can satisfy Formulas 52 to 54 at the T.sub.R is aligned along the "A direction" (.uparw..dwnarw.) by the Hini. which satisfies Formula 55. At this time, the recording layer 1 is maintained in the recorded state (Condition 1 in FIGS. 38 and 39).
Condition 1 is held to a point immediately before the recording. In this case, the bias field (Hb) is applied in the direction of .dwnarw..
The high-temperature cycle will now be described with reference to FIG. 38.
HIGH-TEMPERATURE CYCLE
In Condition 1 when the medium increased to T.sub.L upon irradiation of the high-level laser beam, since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears (Condition 2.sub.H).
When the laser-beam radiation continues and the medium temperature is equal to the temperature T.sub.H, the temperature T.sub.H is substantially equal to the temperature T.sub.C2, magnetization of the layer 2 also disappears. This state is Condition 3.sub.H.
In Condition 3.sub.H, when an irradiated portion is separated from the laser beam spot, the temperature of the medium begins to decrease. When the temperature of the medium decreases slightly below the temperature T.sub.C2, magnetization of the layer 2 appears. In this case, magnetization (.dwnarw..uparw.) is generated by .dwnarw.Hb. However, since the temperature is yet higher than the temperature T.sub.C1, no magnetization appears in the layer 1. This state is Condition 4.sub.H.
When the temperature of the medium is further decreased slightly below the temperature T.sub.C1, magnetization appears in the layer 1. At this time, the exchange coupling force from the layer 2 (.dwnarw..uparw.) acts to align each of the RE and TM spins and of the layers 1 and 2. For this reason, magnetization .dwnarw..uparw., i.e., , without regard to the bias field .dwnarw.Hb, appears in the layer 1. This state is Condition 5.sub.H.
Then, the temperature of the medium decreases from the temperature in Condition 5.sub.H to the room temperature. Since the coersivity H.sub.C1 at the room temperature is sufficiently high, magnetization of the layer 1 is stably maintained. In this way, bit formation in the "A direction" is completed.
Next, the low-temperature cycle will be described with reference to FIG. 39.
LOW-TEMPERATURE CYCLE
In Condition 1 immediately before recording, the medium temperature is increased to T.sub.L upon irradiation of the low-level laser beam. Since the temperature T.sub.L is substantially equal to the Curie temperature T.sub.C1 of the recording layer 1, magnetization of the layer 1 disappears. In this state, however, since the coersivity H.sub.C2 of the layer 2 is sufficiently high, magnetization of the layer 2 will not be reversed by the bias field .dwnarw.Hb. This state is Condition 2.sub.L.
In Condition 2.sub.L, when an irradiated portion is separated from the laser beam spot, the medium temperature begins to fall. When the medium temperature is slightly below the temperature T.sub.C1, the recording layer 1 is influenced by the RE and TM spins (.uparw..dwnarw.) of the reference layer 2 due to the exchange coupling force. In other words, the exchange coupling force acts to align each of the RE and TM spins (.uparw. and .dwnarw.) of the layers 1 and 2. As a result, magnetization of .uparw..dwnarw., i.e., , appears in the layer 1. This state is Condition 3.sub.L.
Condition 3.sub.L is maintained even if the medium temperature is decreased to the room temperature. In this way, bit formation in the "non-A direction" is completed.
According to the present invention as described above, for the first time, an over-write operation is allowed without turning on or off the bias field Hb or without changing the direction of the bias field Hb.
BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is an illustration for explaining a recording principle of a magnetooptical recording method;
FIG. 2 is an illustration for explaining a reading principle of the magnetooptical recording method;
FIG. 3 is a diagram showing the overall arrangement of a magnetooptical recording apparatus according to Example 10 of the present invention;
FIG. 4 is a diagram showing the overall arrangement of a magnetooptical recording apparatus according to Examples 11 and 12 of the present invention;
FIG. 5 is a chart showing an output waveform according to an embodiment of the present invention;
FIG. 6 is a graph showing the relationship between coersivity and temperature;
FIG. 7A is a diagram of a multilayered structure of a recording medium according to the embodiment of the present invention;
FIG. 7B is a diagram showing the direction of magnetization of a recording layer and a reference layer;
FIG. 8 illustrate changes in the direction of magnetization at high level;
FIG. 9 illustrates changes in the direction of magnetization at low level;
FIG. 10 illustrates flows of the changes in the direction of magnetization shown in FIGS. 8 and 9 for respective P- and A-type media;
FIG. 11 is a map wherein the types of media of the present invention as classified into four quadrants;
FIGS. 12A to 12D are graphs showing the relationship between the coersivity and the temperature respectively for media of Types I to IV;
FIG. 13 is a graph showing the relationship between the coersivity and the temperature for a medium No. 1;
FIGS. 14 and 15 are diagrams showing changes in the direction of magnetization in high- and low-temperature cycles of a medium No. 1;
FIG. 16 is a graph showing the relationship between the coersivity and the temperature for the medium No. 2;
FIGS. 17 and 18 are diagrams showing the changes in the direction of magnetization in high- and low-temperature cycles of a medium No. 2;
FIG. 19 is a graph showing the relationship between the coersivity and the temperature for a medium No. 3;
FIGS. 20 and 21 are diagrams showing the changes in the direction of magnetization in high- and low-temperature cycles of the medium No. 3;
FIG. 22 is a graph showing the relationship between the coersivity and the temperature for a medium No. 4;
FIGS. 23 and 24 are diagrams showing the changes in the direction of magnetization in high- and low-temperature cycles of the medium No. 4;
FIG. 25 is a graph showing the relationship between the coersivity and the temperature for a medium No. 5;
FIGS. 26 and 27 are diagrams showing the changes in the direction of magnetization in high- and low-temperature cycles of the medium No. 5;
FIG. 28 is a graph showing the relationship between the coersivity and the temperature for a medium No. 6;
FIGS. 29 and 30 are diagrams showing the changes in the direction of magnetization in high- and low-temperature cycles of the medium No. 6;
FIG. 31 is a graph showing the relationship between the coersivity and the temperature for a medium No. 7;
FIGS. 32 and 33 are diagrams showing the changes in the direction of magnetization in high- and low-temperature cycles of the medium No. 7;
FIG. 34 is a graph showing the relationship between the coersivity and the temperature for a medium No. 8;
FIGS. 35 and 36 are diagrams showing the changes in the direction of magnetization in high- and low-temperature cycles of the medium No. 8;
FIG. 37 is a graph showing the relationship between the coersivity and the temperature for a medium No. 9;
FIGS. 38 and 39 are diagrams showing the changes in the direction of magnetization in high- and low-temperature cycles of the medium No. 9;
FIG. 40 is a schematic view showing a vertical section of a recording medium with a third layer (transcription layer); and
FIG. 41 is a diagram showing the overall arrangement of a reproduction apparatus according to Example 40 of the present invention.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
The present invention will now be described by way of examples. However, the present invention is not limited to the following examples.
EXAMPLE 1
One of Media No. 1
A vacuum vapor deposition apparatus was used in this example. It included two crucibles as evaporation sources shown in Table 2 and two units for heating the respective sources with an electron beam.
A 1.2-mm thick, 200-mm diameter glass substrate was placed inside a chamber of the apparatus. The chamber of the apparatus was temporarily evacuated to a vacuum of 1.times.10.sup.-6 Torr. or less. Thereafter, deposition was performed at a deposition rate of about 3 .ANG./sec while maintaining the chamber at a vacuum of 1 to 2.times.10.sup.-6 Torr. Then, a 1,000-.ANG. first layer (recording layer) of Gd.sub.14 Gy.sub.12 Fe.sub.74 (note: appendixes, atom.%) was formed on the substrate. Subsequently, the evaporation sources were exchanged while maintaining the vacuum state. Then, deposition was performed again to form a 2,000-.ANG. thick second layer (reference layer) of Gd.sub.24 Tb.sub.3 Fe.sub.73.
The first and second layers were perpendicular magnetic layers.
In this way, a double-layered recording medium No. 1 belonging to Class 1 (i.e., P-type, Quadrant I, and Type 1) was manufactured.
Table 2 below shows the manufacturing conditions and characteristics of the medium No. 1.
If T.sub.L =170.degree. C. and T.sub.H =230.degree. C. (see Example 13), this medium satisfies:
In Formula 15, since
if an initial field Hini.) is 600 Oe, the medium No. 1 can satisfy Formula 15. Thus, the direction of magnetization of the reference layer 2 is reversed at the room temperature due to the initial field (Hini.) without reversing that of the recording layer 1.
In addition, since the medium No. 1 satisfies:
if the initial field (Hini.) is removed, magnetization of the layers 1 and 2 can be maintained.
Therefore, when the initial field (Hini.)=600 Oe is applied in the "A direction" (.uparw.) and the bias field Hb=600 Oe is applied in the "A direction" (.uparw.), an over-write operation is enabled. Note that since the levels and the directions of the fields Hb and Hini. are equal to each other, the recording apparatus which uses a single applying means for applying both the fields Hb and Hini. can be used.
EXAMPLE 2
One of Media No. 2
A 500-.ANG. thick first layer (recording layer) of Tb.sub.27 Fe.sub.73 and a 2,000-.ANG. thick second layer (reference layer) of Gd.sub.24 Tb.sub.3 Fe.sub.73 were sequentially formed on a substrate in the same manner as in Example 1. Then, a medium No. 2 belonging to Class 2 (i.e., P type, Quadrant I, and Type 2) was manufactured.
Table 3 below shows the manufacturing conditions and characteristics of the medium No. 2.
If T.sub.L =150.degree. C. and T.sub.H =230.degree. C. (see Example 14), this medium satisfies:
In Formula 20, since
if an initial field (Hini.) is 600 Oe, the medium No. 2 can satisfy Formula 20. Thus, the direction of magnetization of the reference layer 2 is reversed at the room temperature due to the initial field (Hini.) without reversing that of the recording layer 1.
In addition, since the medium No. 2 satisfies:
if the initial field (Hini.) is removed, magnetization of the layers 1 and 2 can be maintained.
Therefore, when the initial field (Hini.)=600 Oe is applied in the "A direction" (.uparw.) and the bias field Hb=600 Oe is applied in the "A direction" (.uparw.), an over-write operation is enabled. Note that since the levels and the directions of the fields Hb and Hini. are equal to each other, the recording apparatus which uses a single applying means for applying both the fields Hb and Hini. can be used.
EXAMPLE 3
One of Media No. 3
A 500-.ANG. thick first layer (recording layer) of Gd.sub.23 Tb.sub.3 Fe.sub.74 and a 1,000-.ANG. thick second layer (reference layer) of Tb.sub.28 Fe.sub.65 Co.sub.7 were sequentially formed on a substrate in the same manner as in Example 1. Then, a medium No. 3 belonging to Class 3 (i.e., P type, Quadrant I, and Type 3) was manufactured.
Table 4 below shows the manufacturing conditions and characteristics of the medium No. 3.
If T.sub.L =170.degree. C. and T.sub.H =220.degree. C. (see Example 15), this medium satisfies:
In Formula 25, since
if an initial field (Hini.) is 4,000 Oe, the medium No. 3 can satisfy Formula 25. Thus, the direction of magnetization of the reference layer 2 is reversed at the room temperature due to the initial field (Hini.) without reversing that of the recording layer 1.
In addition, since the medium No. 3 satisfies:
if the initial field (Hini.) is removed, magnetization of the layers 1 and 2 can be maintained.
Therefore, when the initial field (Hini.)=4,000 Oe is applied in the "A direction" (.uparw.) and the bias field Hb 300 Oe is applied in the "non-A direction" (.dwnarw.), an over-write operation is enabled.
EXAMPLE 4
One of Media No. 4
A 1,000-.ANG. thick first layer (recording layer) of Tb.sub.13 Dy.sub.13 Fe.sub.74 and a 1,000-.ANG. thick second layer (reference layer) of Gd.sub.14 Dy.sub.14 Fe.sub.72 were sequentially formed on a substrate in the same manner as in Example 1. Then, a medium No. 4 belonging to Class 4 (i.e., P type, Quadrant I, and Type 4) was manufactured.
Table 5 below shows the manufacturing conditions and characteristics of the medium No. 4.
If T.sub.L =120.degree. C. and T.sub.H =160.degree. C. (see Example 16), this medium satisfies:
In Formula 30, since
if an initial field (Hini.) is 4,000 Oe, the medium No. 4 can satisfy Formula 30. Thus, the direction of magnetization of the reference layer 2 is reversed at the room temperature due to the initial field (Hini.) without reversing that of the recording layer 1.
if the initial field (Hini.) is removed, magnetization of the layers 1 and 2 can be maintained.
Therefore, when the initial field (Hini.)=4,000 Oe is applied in the "A direction" (.uparw.) and the bias field Hb=300 Oe is applied in the "non-A direction" (.dwnarw.), an over-write operation is enabled.
EXAMPLE 5
One of Media No. 5
A 500-.ANG. thick first layer (recording layer) of Gd.sub.13 Dy.sub.13 Fe.sub.74 and a 600-.ANG. thick second layer (reference layer) of Tb.sub.18 Fe.sub.74 Co.sub.8 were sequentially formed on a substrate in the same manner as in Example 1. Then, a medium No. 5 belonging to Class 5 (i.e., A type, Quadrant II, and Type 3) was manufactured.
Table 6 below shows the manufacturing conditions and characteristics of the medium No. 5.
If T.sub.L =165.degree. C. and T.sub.H =210.degree. C. (see Example 17), this medium satisfies:
In Formula 35, since
if an initial field (Hini.) is 4,000 Oe, the medium No. 5 can satisfy Formula 35. Thus, the direction of magnetization of the reference layer 2 is reversed at the room temperature due to the initial field (Hini.) without reversing that of the recording layer 1.
In addition, since the medium No. 5 satisfies:
if the initial field (Hini.) is removed, magnetization of layers 1 and 2 can be maintained.
Therefore, when the initial field (Hini.) =4,000 Oe is applied in the "A direction" (.uparw.) and the bias field Hb=300 Oe is applied in the "non-A direction" (.dwnarw.), an over-write operation is enabled.
EXAMPLE 6
One of Media No. 6
A 3-element RF magnetron sputtering apparatus was used and included three targets Tb, Fe, and FeCo alloy shown in Table 7. Targets Tb and Fe were first used, and Tb and FeCo alloy were then used. A 1.2-mm thick, 200-mm diameter glass substrate was placed inside a chamber of the apparatus.
The chamber of the apparatus was temporarily evacuated to a vacuum of 7.times.10.sup.-7 Torr. or less, and 5 .times.10.sup.-3 Torr. of Ar gas was introduced therein. Then, sputtering was performed at a deposition rate of about 2 .ANG.sec. Thereby, a 500-.ANG. thick first layer (recording layer) of Tb.sub.27 Fe.sub.73 was formed on the substrate. Subsequently, the targets were replaced while maintaining the vacuum state. Thereafter, sputtering was performed again to form a 1,000-.ANG. thick second layer of Tb.sub.18 Fe.sub.74 Co.sub.8 on the first layer. Note that the first and second layers were perpendicular magnetic films. In this way, a double-layered magnetooptical recording medium No. 6 belonging to Class 6 (i.e., A type, Quadrant II, and Type 4) was manufactured.
Table 7 shows the manufacturing conditions and characteristics of the medium No. 6.
If T.sub.L =155.degree. C. and T.sub.H =220.degree. C. (see Example 18), this medium satisfies:
In Formula 40, since
if an initial field (Hini.) is 4,000 Oe, the medium No. 6 can satisfy Formula 40. Thus, the direction of magnetization of the reference layer 2 is reversed at the room temperature due to the initial field (Hini.) without reversing that of the recording layer 1.
In addition, since the medium No. 6 satisfies:
if the initial field (Hini.) is removed, magnetization of the layers 1 and 2 can be maintained.
Therefore, when the initial field (Hini.)=4,000 Oe is applied in the "A direction" (.uparw.) and the bias field Hb=300 Oe is applied in the "non-A direction" (.dwnarw.), an over-write operation is enabled.
EXAMPLE 7
One of Media No. 7
A 1,000-.ANG. thick first layer (recording layer) of Tb.sub.21 Fe.sub.79 and a 1,000-.ANG. thick second layer (reference layer) of Tb.sub.18 Fe.sub.74 Co.sub.8 were sequentially formed on a substrate in the same manner as in Example 6. Then, a medium No. 7 belonging to Class 7 (i.e., P type, Quadrant III, and Type 4) was manufactured.
Table 8 shows the manufacturing conditions and characteristics of the medium No. 7.
If T.sub.L =155.degree. C. and T.sub.H =220.degree. C. (see Example 19), this medium satisfies:
In Formula 45, since
i if an initial field (Hini.) is 4,000 Oe, the medium No. 7 can satisfy Formula 45. Thus, the direction of magnetization of the reference layer 2 is reversed at the room temperature due to the initial field (Hini.) without reversing that of the recording layer 1.
In addition, since the medium No. 7 satisfies:
if the initial field (Hini.) is removed, magnetization of the layers 1 and 2 can be maintained.
Therefore, when the initial field (Hini.)=4,000 Oe is applied in the "A direction" (.uparw.) and the bias field Hb=300 Oe is applied in the "non-A direction" (.dwnarw.), an over-write operation is enabled.
EXAMPLE 8
One of Media 8
A 500-.ANG. thick first layer (recording layer) of Tb.sub.21 Fe.sub.79 and a 2,000-.ANG. thick second layer (reference layer) of Gd.sub.24 Tb.sub.3 Fe.sub.73 were sequentially formed on a substrate in the same manner as in Example 6. Then, a medium No. 8 belonging to Class 8 (i.e., A type, Quadrant IV, and Type 2) was manufactured.
Table 9 shows the manufacturing conditions and characteristics of the medium No. 8.
If T.sub.L =155.degree. C. and T.sub.H =230.degree. C. (see Example 20), this medium satisfies:
T.sub.R <T.sub.C1 .apprxeq.T.sub.L .apprxeq.Tcomp. 2<T.sub.C2 .apprxeq.T.sub.H Formula 46
In Formula 50, since
if an initial field (Hini. is 800 Oe, the medium No. 8 can satisfy Formula 50. Thus, the direction of magnetization of the reference layer 2 is reversed at the room temperature due to the initial field (Hini.) without reversing that of the recording layer 1.
In addition, since the medium No. 8 satisfies:
if the initial field (Hini.) is removed, magnetization of the layers 1 and 2 can be maintained. Therefore, when the initial field (Hini.)=800 Oe is applied in the "A direction" (.uparw.) and the bias field Hb=800 Oe is applied in the "A direction" (.uparw.), an over-write operation is enabled. Note that since the levels and the directions of the fields Hb and Hini. are equal to each other, the recording apparatus which uses a single applying means for applying both the fields Hb and Hini. can be used.
EXAMPLE 9
One of Media 9
A 1,000-A thick first layer (recording layer) of Gd.sub.4 Tb.sub.19 Fe.sub.77 and a 500-.ANG. thick second layer (reference layer) of Tb.sub.29 Fe.sub.61 Co.sub.10 were sequentially formed on a substrate in the same manner as in Example 1. Then, a medium No. 9 belonging to Class 9 (i.e., A type, Quadrant IV, and Type 4) was manufactured.
Table 10 shows the manufacturing conditions and characteristics of the medium No. 9.
If T.sub.L =170.degree. C. and T.sub.H =220.degree. C. (see Example 21), this medium satisfies:
In Formula 55, since
if an initial field (Hini.) is 4,000 Oe, the medium No. 9 can satisfy Formula 55. Thus, the direction of magnetization of the reference layer 2 is reversed at the room temperature due to the initial field (Hini.) without reversing that of the recording layer 1.
In addition, since the medium No. 9 satisfies:
and
if the initial field (Hini. is removed, magnetization of the layers 1 and 2 can be maintained.
Therefore, when the initial field (Hini.)=4,000 Oe is applied in the "A direction" (.uparw.) and the bias field Hb=300 Oe is applied in the "non-A direction" (.dwnarw.), an over-write operation is enabled.
EXAMPLE 10
Magnetooptical Recording Apparatus
This apparatus is for recording only, and FIG. 3 shows the overall arrangement thereof.
The apparatus basically comprises:
(a) a rotating means 21 as a means for moving a recording medium 20;
(b) an initial field (Hini.) applying means 22;
(c) a laser beam light source 23;
(d) a means 24 for pulse modulating, in accordance with binary data to be recorded, a beam intensity (1) to obtain high level which provides a medium temperature T.sub.H suitable for forming one of a bit having upward-magnetization and a bit having downward-magnetization and (2) to obtain low level which provides a medium temperature T.sub.L suitable for forming the other bit; and
(e) a bias field (Hb) applying means 25.
The bias field (Hb) applying means 25 normally comprises an electromagnet or, preferably, a permanent magnet. Alternatively, a stray field from a portion other than recording tracks of the recording medium can be used as the bias field Hb. In this case, the applying means 25 indicates a region of perpendicular magnetic films (first and second layers) of the recording medium 20, which produces the stray field.
In this example, a permanent magnet which produced a bias field Hb=300 Oe and had a direction of magnetization along the "non-A direction" (.dwnarw.) was used as the applying means 25. The permanent magnet 25 had a rod-like shape having a length corresponding to the radius of the disk-shaped medium 20 and was fixed in the apparatus. The permanent magnet 25 was not moved together with a recording head (pickup) including the light source 23. This made the pickup light, and allowed high-speed access.
An electromagnet or, preferably, a permanent magnet was used as the initial field (Hini.) applying means 22. In this example, a permanent magnet which produced an initial field (Hini.)=4,000 Oe and had a direction of magnetization along the "A direction" (.uparw.) was used. The permanent magnet 22 had a rod-like shape having a length corresponding to the radius of the disk-shaped medium 20 and was fixed in the apparatus.
Note that a reproduction apparatus can be added to the recording apparatus of this example as a recording/reproduction apparatus.
EXAMPLE 11
Magnetooptical Recording Apparatus
This apparatus is for recording only, and FIG. 4 shows the overall arrangement thereof.
The apparatus basically comprises:
(a) a rotating means 21 as a means for moving a recording medium 20;
(c) a laser beam light source 23;
(d) a means 24 for pulse modulating, in accordance with binary data to be recorded, a beam intensity (1) to obtain high level which provides a medium temperature T.sub.H suitable for forming one of a bit having upward-magnetization and a bit having downward-magnetization and (2) to obtain low level which provides a medium temperature T.sub.L suitable for forming the other bit; and
(b, e) a bias field (Hb) applying means 25, which also serves as an initial field (Hini.) applying means 22.
When the directions of the bias field (Hb) and the initial field (Hini.) coincide with each other, the applying means 25 can also be used as the applying means 22. More specifically, if the applying means 25 is arranged at a recording position (a spot region irradiated with a beam) at which a magnetic field is to be concentrated, it is impossible to concentrate the magnetic field at a point. In other words, a leaking magnetic field is inevitably applied around the recording point. Therefore, if the leaking magnetic field is utilized, the initial field (Hini.) can be applied before recording. For this reason, in the apparatus of this example, the means 25 served as the means 22.
The means 25 and 22 normally comprise electromagnets or, preferably, permanent magnets. In this example, permanent magnets which produced a bias field Hb (Hini.)=600 Oe and had a direction of magnetization along the "A direction" (.uparw.) were used as means 22 and 25. The permanent magnets 22 and 25 had a rod-like shape having a length corresponding to the radius of the disk-shaped recording medium 20. The magnets 22 and 25 were fixed to the apparatus of this example, and were not moved together with a pickup including the light source 23. This made the pickup light, and allowed high-speed access.
EXAMPLE 12
Magnetooptical Recording Apparatus
This apparatus is for recording only, and FIG. 4 shows the overall arrangement thereof.
The apparatus basically comprises:
(a) a rotating means 21 as a means for moving a recording medium 20;
(c) a laser beam light source 23;
(d) a means 24 for pulse modulating, in accordance with binary data to be recorded, a beam intensity (1) to obtain high level which provides a medium temperature T.sub.H suitable for forming one of a bit having upward-magnetization and a bit having downward-magnetization and (2) to obtain low level which provides a medium temperature T.sub.L suitable for forming the other bit; and
(b, e) a bias field (Hb) applying means 25, which also serves as an initial field (Hini.) applying means 22.
In this example, permanent magnets which produced a bias field Hb (Hini.=600 Oe and had a direction of magnetization along the "A direction" (.uparw.) were used as means 22 and 25. The permanent magnets 22 and 25 had a rod-like shape having a length corresponding to the radius of the disk-shaped recording medium 20. The magnets 22 and 25 were fixed to the apparatus of this example, and were not moved together with a pickup including the light source 23.
EXAMPLE 13
Magnetooptical Recording
A magnetooptical recording operation was performed using the recording apparatus of Example 11 (see FIG. 4). First, the recording medium 20 of Example 1 was rotated at a constant speed of 8.5 m/sec by the rotating means 21. A laser beam was radiated onto the medium 20. The laser beam was adjusted by the means 24 to obtain an output of 9.3 mW (on disk) at high level and to obtain an output of 6.6 mW (on disk) at low level. The laser beam was pulse modulated by the means 24 in accordance with data to be recorded. In this example, the data to be recorded was a signal having a frequency of 1 MHz. Therefore, the laser beam was radiated onto the medium 20 while being modulated at the frequency of 1 MHz. As a result, a 1-MHz signal was recorded. When this signal was reproduced by another magnetooptical reproduction apparatus, a C/N ratio was 51 dB and it was confirmed therefrom that the signal was actually recorded.
A signal of a frequency of 5 MHz was newly recorded on an already recorded region of the medium 20.
When the signal was similarly reproduced, it could be reproduced at a C/N ratio of 48 dB. In this case, a bit error rate was 10.sup.-5 to 10.sup.-6. In addition, the 1-MHz signal (preceding data) was not reproduced at all.
As a result, it was found that an over-write operation was enabled.
Note that under these conditions, the temperature of the medium reached T.sub.H =230.degree. C. at high level and T.sub.L =170.degree. C. at low level.
EXAMPLE 14
Magnetooptical Recording
A magnetooptical recording operation was performed using the recording apparatus of Example 11 (see FIG. 4). First, the recording medium 20 of Example 2 was rotated at a constant speed of 8.5 m/sec by the rotating means 21. A laser beam was radiated onto the medium 20. The laser beam was adjusted by the means 24 to obtain an output of 9.3 mW (on disk) at high level and to obtain an output of 5.7 mW (on disk) at low level. The laser beam was pulse modulated by the means 24 in accordance with data to be recorded. In this example, the data to be recorded was a signal having a frequency of 1 MHz. Therefore, the laser beam was radiated onto the medium 20 while being modulated at the frequency of 1 MHz. As a result, a 1-MHz signal was recorded. When this signal was reproduced by another magnetooptical reproduction apparatus, a C/N ratio was 52 dB and it was confirmed therefrom that the signal was actually recorded.
A signal of a frequency of 5 MHz was newly recorded on an already recorded region of the medium 20.
When the signal was similarly reproduced, it could be reproduced at a C/N ratio of 49 dB. In this case, a bit error rate was 10.sup.-5 to 10.sup.-6. In addition, the 1-MHz signal (preceding data) was not reproduced at all.
As a result, it was found that an over-write operation was enabled.
Note that under these conditions, the temperature of the medium reached T.sub.H =230.degree. C. at high level and T.sub.L =150.degree. C. at low level.
EXAMPLE 15
Magnetooptical Recording
A magnetooptical recording operation was performed using the recording apparatus of Example 10 (see FIG. 3). First, the recording medium 20 of Example 3 was rotated at a constant speed of 8.5 m/sec by the rotating means 21. A laser beam was radiated onto the medium 20. The laser beam was adjusted by the means 24 to obtain an output of 8.9 mW (on disk) at high level and to obtain an output of 6.6 mW (on disk) at low level. The laser beam was pulse modulated by the means 24 in accordance with data to be recorded. In this example, the data to be recorded was a signal having a frequency of 5 MHz. Therefore, the laser beam was radiated onto the medium 20 while being modulated at the frequency of 5 MHz. As a result, a 5-MHz signal was recorded. When this signal was reproduced by another magnetooptical reproduction apparatus, a C/N ratio was 51 dB and it was confirmed therefrom that the signal was actually recorded.
A signal of a frequency of 2 MHz was newly recorded on an already recorded region of the medium 20.
When the signal was similarly reproduced, it could be reproduced at a C/N ratio of 54 dB. In this case, a bit error rate was 10.sup.-5 to 10.sup.-6. In addition, the 5-MHz signal (preceding data) was not reproduced at all.
As a result, it was found that an over-write operation was enabled.
Note that under these conditions, the temperature of the medium reached T.sub.H =220.degree. C. at high level and T.sub.L =170.degree. C. at low level.
EXAMPLE 16
Magnetooptical Recording
A magnetooptical recording operation was performed using the recording apparatus of Example 10 (see FIG. 3). First, the recording medium 20 of Example 4 was rotated at a constant speed of 8.5 m/sec by the rotating means 21. A laser beam was radiated onto the medium 20. The laser beam was adjusted by the means 24 to obtain an output of 6.1 mW (on disk) at high level and to obtain an output of 4.3 mW (on disk) at low level. The laser beam was pulse modulated by the means 24 in accordance with data to be recorded. In this example, the data to be recorded was a signal having a frequency of 5 MHz. Therefore, the laser beam was radiated onto the medium 20 while being modulated at the frequency of 5 MHz. As a result, a 5-MHz signal was recorded. When this signal was reproduced by another magnetooptical reproduction apparatus, a C/N ratio was 47 dB and it was confirmed therefrom that the signal was actually recorded.
A signal of a frequency of 2 MHz was newly recorded on an already recorded region of the medium 20.
When the signal was similarly reproduced, it could be reproduced at a C/N ratio of 50 dB. In this case, a bit error rate was 10.sup.-5 to 10.sup.-6. In addition, the 5-MHz signal (preceding data) was not reproduced at all.
As a result, it was found that an over-write operation was enabled.
Note that under these conditions, the temperature of the medium reached T.sub.H =160.degree. C. at high level and T.sub.L = 120.degree. at low level.
EXAMPLE 17
Magnetooptical Recording
A magnetooptical recording operation was performed using the recording apparatus of Example 10 (see FIG. 3). First, the recording medium 20 of Example 5 was rotated at a constant speed of 8.5 m/sec by the rotating means 21. A laser beam was radiated onto the medium 20. The laser beam was adjusted by the means 24 to obtain an output of 8.4 mW (on disk) at high level and to obtain an output of 6.4 mW (on disk) at low level. The laser beam was pulse modulated by the means 24 in accordance with data to be recorded. In this example, the data to be recorded was a signal having a frequency of 5 MHz. Therefore, the laser beam was radiated onto the medium 20 while being modulated at the frequency of 5 MHz. As a result, a 5-MHz signal was recorded. When this signal was reproduced by another magnetooptical reproduction apparatus, a C/N ratio was 48 dB and it was confirmed therefrom that the signal was actually recorded.
A signal of a frequency of 4 MHz was newly recorded on an already recorded region of the medium 20.
When the signal was similarly reproduced, it could be reproduced at a C/N ratio of 49 dB. In this case, a bit error rate was 10.sup.-5 to 10.sup.-6. In addition, the 5-MHz signal (preceding data) was not reproduced at all.
As a result, it was found that an over-write operation was enabled.
Note that under these conditions, the temperature of the medium reached T.sub.H =210.degree. C. at high level and T.sub.L =165.degree. C. at low level.
EXAMPLE 18
Magnetooptical Recording
A magnetooptical recording operation was performed using the recording apparatus of Example 10 (see FIG. 3). First, the recording medium 20 of Example 6 was rotated at a constant speed of 8.5 m/sec by the rotating means 21. A laser beam was radiated onto the medium 20. The laser beam was adjusted by the means 24 to obtain an output of 8.1 mW (on disk) at high level and to obtain an output of 5.9 mW (on disk) at low level. The laser beam was pulse modulated by the means 24 in accordance with data to be recorded. In this example, the data to be recorded was a signal having a frequency of 5 MHz. Therefore, the laser beam was radiated onto the medium 20 while being modulated at the frequency of 5 MHz. As a result, a 5-MHz signal was recorded. When this signal was reproduced by another magnetooptical reproduction apparatus, a C/N ratio was 49 dB and it was confirmed therefrom that the signal was actually recorded.
A signal of a frequency of 3 MHz was newly recorded on an already recorded region of the medium 20.
When the signal was similarly reproduced, it could be reproduced at a C/N ratio of 51 dB. In this case, a bit error rate was 10.sup.-5 to 10.sup.-6. In addition, the 5-MHz signal (preceding data) was not reproduced at all.
As a result, it was found that an over-write operation was enabled.
Note that under these conditions, the temperature of the medium reached T.sub.H =220.degree. C. at high level and T.sub.L =155.degree. C. at low level.
EXAMPLE 19
Magnetooptical Recording
A magnetooptical recording operation was performed using the recording apparatus of Example 10 (see FIG. 3). First, the recording medium 20 of Example 7 was rotated at a constant speed of 8.5 m/sec by the rotating means 21. A laser beam was radiated onto the medium 20. The laser beam was adjusted by the means 24 to obtain an output of 8.9 mW (on disk) at high level and to obtain an output of 5.9 mW (on disk) at low level. The laser beam was pulse modulated by the means 24 in accordance with data to be recorded. In this example, the data to be recorded was a signal having a frequency of 5 MHz. Therefore, the laser beam was radiated onto the medium 20 while being modulated at the frequency of 5 MHz. As a result, a 5-MHz signal was recorded. When this signal was reproduced by another magnetooptical reproduction apparatus, a C/N ratio was 49 dB and it was confirmed therefrom that the signal was actually recorded.
A signal of a frequency of 2 MHz was newly recorded on an already recorded region of the medium 20.
When the signal was similarly reproduced, it could be reproduced at a C/N ratio of 52 dB. In this case, a bit error rate was 10.sup.-5 to 10.sup.-6. In addition, the 5-MHz signal (preceding data) was not reproduced at all.
As a result, it was found that an over-write operation was enabled.
Note that under these conditions, the temperature of the medium reached T.sub.H =220.degree. C. at high level and T.sub.L =155.degree. C. at low level.
EXAMPLE 20
Magnetooptical Recording
A magnetooptical recording operation was performed using the recording apparatus of Example 12 (see FIG. 4). First, the recording medium 20 of Example 8 was rotated at a constant speed of 8.5 m/sec by the rotating means 21. A laser beam was radiated onto the medium 20. The laser beam was adjusted by the means 24 to obtain an output of 9.3 mW (on disk) at high level and to obtain an output of 5.9 mW (on disk) at low level. The laser beam was pulse modulated by the means 24 in accordance with data to be recorded. In this example, the data to be recorded was a signal having a frequency of 1 MHz. Therefore, the laser beam was radiated onto the medium 20 while being modulated at the frequency of 1 MHz. As a result, a 1-MHz signal was recorded. When this signal was reproduced by another magnetooptical reproduction apparatus, a C/N ratio was 52 dB and it was confirmed therefrom that the signal was actually recorded.
A signal of a frequency of 2 MHz was newly recorded on an already recorded region of the medium 20.
When the signal was similarly reproduced, it could be reproduced at a C/N ratio of 51 dB. In this case, a bit error rate was 10.sup.-5 to 10.sup.-6. In addition, the 1-MHz signal (preceding data) was not reproduced at all.
As a result, it was found that an over-write operation was enabled.
Note that under these conditions, the temperature of the medium reached T.sub.H =230.degree. C. at high level and T.sub.L =155.degree. C. at low level.
EXAMPLE 21
Magnetooptical Recording
A magnetooptical recording operation was performed using the recording apparatus of Example 10 (see FIG. 3). First, the recording medium 20 of Example 9 was rotated at a constant speed of 8.5 m/sec by the rotating means 21. A laser beam was radiated onto the medium 20. The laser beam was adjusted by the means 24 to obtain an output of 8.9 mW (on disk) at high level and to obtain an output of 6.6 mW (on disk) at low level. The laser beam was pulse modulated by the means 24 in accordance with data to be recorded. In this example, the data to be recorded was a signal having a frequency of 5 MHz. Therefore, the laser beam was radiated onto the medium 20 while being modulated at the frequency of 5 MHz. As a result, a 5-MHz signal was recorded. When this signal was reproduced by another magnetooptical reproduction apparatus, a C/N ratio was 51 dB and it was confirmed therefrom that the signal was actually recorded.
A signal of a frequency of 6 MHz was newly recorded on an already recorded region of the medium 20.
When the signal was similarly reproduced, it could be reproduced at a C/N ratio of 49 dB. In this case, a bit error rate was 10.sup.-5 to 10.sup.-6. In addition, the 5-MHz signal (preceding data) was not reproduced at all.
As a result, it was found that an over-write operation was enabled.
Note that under these conditions, the temperature of the medium reached T.sub.H =220.degree. C. at high level and T.sub.L =170.degree. C. at low level.
EXAMPLE 22
Recording Medium No. 11
In Example 1, a third layer (transcription layer) was formed before formation of the first layer under the same conditions. The third layer was a perpendicular magnetic film of a 500-.ANG. thick Gd.sub.26 Fe.sub.52 Co.sub.22.
A recording medium No. 11 was manufactured following the same procedures as in Example 1 except that the third layer was formed. Table 11 shows the manufacturing conditions and characteristics of the medium No. 11.
EXAMPLE 23
Recording Medium No. 12
In Example 2, a third layer (transcription layer) was formed before formation of the first layer under the same conditions. The third layer was a perpendicular magnetic film of a 500.ANG. thick Gd.sub.26 Fe.sub.52 Co.sub.22.
A recording medium No. 12 was manufactured following the same procedures as in Example 2 except that the third layer was formed. Table 12 shows the manufacturing conditions and characteristics of the medium No. 12.
EXAMPLE 24
Recording Medium No. 13
In Example 3, a third layer (transcription layer) was formed before formation of the first layer under the same conditions. The third layer was a perpendicular magnetic film of a 500-.ANG. thick Gd.sub.22 Fe.sub.55 Co.sub.23.
A recording medium No. 13 was manufactured following the same procedures as in Example 3 except that the third layer was formed. Table 13 shows the manufacturing conditions and characteristics of the medium No. 13.
EXAMPLE 25
Recording Medium No. 14
In Example 4, a third layer (transcription layer) was formed before formation of the first layer under the same conditions. The third layer was a perpendicular magnetic film of a 400-.ANG. thick Gd.sub.22 Fe.sub.55 Co.sub.23.
A recording medium No. 14 was manufactured following the same procedures as in Example 4 except that the third layer was formed. Table 14 shows the manufacturing conditions and characteristics of the medium No. 14.
EXAMPLE 26
Recording Medium No. 15
In Example 5, a third layer (transcription layer) was formed before formation of the first layer under the same conditions. The third layer was a perpendicular magnetic film of a 500.ANG. thick Gd.sub.22 Fe.sub.55 Co.sub.23.
A recording medium No. 15 was manufactured following the same procedures as in Example 5 except that the third layer was formed. Table 15 shows the manufacturing conditions and characteristics of the medium No. 15.
EXAMPLE 27
Recording Medium No. 16
In Example 6, a third layer (transcription layer) was formed before formation of the first layer under the same conditions. The third layer was a perpendicular magnetic film of a 300-.ANG. thick Gd.sub.22 Fe.sub.55 Co.sub.23.
A recording medium No. 16 was manufactured following the same procedures as in Example 6 except that the third layer was formed. Table 16 shows the manufacturing conditions and characteristics of the medium No. 16.
EXAMPLE 28
Recording Medium No. 17
In Example 7, a third layer (transcription layer) was formed before formation of the first layer under the same conditions. The third layer was a perpendicular magnetic film of a 500-.ANG. thick Gd.sub.22 Fe.sub.55 Co.sub.23.
A recording medium No. 17 was manufactured following the same procedure as in Example 7 except that the third layer was formed. Table 17 shows the manufacturing conditions and characteristics of the medium No. 17.
EXAMPLE 29
Recording Medium No. 18
In Example 8, a third layer (transcription layer) was formed before formation of the first layer under the same conditions. The third layer was a perpendicular magnetic film of a 500-.ANG. thick Gd.sub.26 Fe.sub.52 Co.sub.22.
A recording medium No. 18 was manufactured following the same procedures as in Example 8 except that the third layer was formed. Table 18 shows the manufacturing conditions and characteristics of the medium No. 18.
EXAMPLE 30
Recording Medium No. 19
In Example 9, a third layer (transcription layer) was formed before formation of the first layer under the same conditions. The third layer was a perpendicular magnetic film of a 400-.ANG. thick Gd.sub.22 Fe.sub.55 Co.sub.23.
A recording medium No. 19 was manufactured following the same procedures as in Example 9 except that the third layer was formed. Table 19 shows the manufacturing conditions and characteristics of the medium No. 19.
EXAMPLE 31
Magnetooptical Recording
A 1-MHz signal was recorded following the same procedures as in Example 13 except that the medium of Example 22 was used in place of that of Example 1.
A reproduction beam was radiated onto the third layer (transcription layer), and a beam reflected by the third layer was processed by a known method, thereby reproducing data. In this case, a C/N ratio was 59 dB.
Next, a 5-MHz signal was over written. Data was reproduced from the third layer at a C/N ratio of 55 dB. The C/N ratio was improved by 7 dB as compared to Example 13.
EXAMPLE 32
Magnetooptical Recording
A 1-MHz signal was recorded following the same procedures as in Example 14 except that the medium of Example 23 was used in place of that of Example 2.
A reproduction beam was radiated onto the third layer (transcription layer), and a beam reflected by the third layer was processed by a known method, thereby reproducing data. In this case, a C/N ratio was 59 dB.
Next, a 5-MHz signal was over written. Data was reproduced from the third layer at a C/N ratio of 55 dB. The C/N ratio was improved by 6 dB as compared to Example 14.
EXAMPLE 33
Magnetooptical Recording
A 5-MHz signal was recorded following the same procedures as in Example 15 except that the medium of Example 24 was used in place of that of Example 3.
A reproduction beam was radiated onto the third layer (transcription layer), and a beam reflected by the third layer was processed by a known method, thereby reproducing data. In this case, a C/N ratio was 56 dB.
Next, a 2-MHz signal was over written. Data was reproduced from the third layer at a C/N ratio of 59.5 dB. The C/N ratio was improved by 5.5 dB as compared to Example 15.
EXAMPLE 34
Magnetooptical Recording
A 5-MHz signal was recorded following the same procedures as in Example 16 except that the medium of Example 25 was used in place of that of Example 4.
A reproduction beam was radiated onto the third layer (transcription layer), and a beam reflected by the third layer was processed by a known method, thereby reproducing data. In this case, a C/N ratio was 56 dB.
Next, a 2-MHz signal was over written. Data was reproduced from the third layer at a C/N ratio of 59.5 dB. The C/N ratio was improved by 9.5 dB as compared to Example 16.
EXAMPLE 35
Magnetooptical Recording
A 5-MHz signal was recorded following the same procedures as in Example 17 except that the medium of Example 26 was used in place of that of Example 5.
A reproduction beam was radiated onto the third layer (transcription layer), and a beam reflected by the third layer was processed by a known method, thereby reproducing data. In this case, a C/N ratio was 55 dB.
Next, a 4-MHz signal was over written. Data was reproduced from the third layer at a C/N ratio of 56 dB. The C/N ratio was improved by 7 dB as compared to Example 17.
EXAMPLE 36
Magnetooptical Recording
A 5-MHz signal was recorded following the same procedures as in Example 18 except that the medium of Example 27 was used in place of that of Example 6.
A reproduction beam was radiated onto the third layer (transcription layer), and a beam reflected by the third layer was processed by a known method, thereby reproducing data. In this case, a C/N ratio was 56 dB.
Next, a 3-MHz signal was over written. Data was reproduced from the third layer at a C/N ratio of 59 dB. The C/N ratio was improved by 8 dB as compared to Example 18.
EXAMPLE 37
Magnetooptical Recording
A 5-MHz signal was recorded following the same procedures as in Example 19 except that the medium of Example 28 was used in place of that of Example 7.
A reproduction beam was radiated onto the third layer (transcription layer), and a beam reflected by the third layer was processed by a known method, thereby reproducing data. In this case, a C/N ratio was 56 dB.
Next, a 2-MHz signal was over written. Data was 0 reproduced from the third layer at a C/N ratio of 59.5 dB. The C/N ratio was improved by 7.5 dB as compared to Example 19.
EXAMPLE 38
Magnetooptical Recording
A 1-MHz signal was recorded following the same procedures as in Example 20 except that the medium of Example 29 was used in place of that of Example 8.
A reproduction beam was radiated onto the third layer (transcription layer), and a beam reflected by the third layer was processed by a known method, thereby reproducing data. In this case, a C/N ratio was 59 dB.
Next, a 2-MHz signal was over written. Data was reproduced from the third layer at a C/N ratio of 58.5 dB. The C/N ratio was improved by 7.5 dB as compared to Example 20.
EXAMPLE 39
Magnetooptical Recording
A 5-MHz signal was recorded following the same procedures as in Example 21 except that the medium of Example 30 was used in place of that of Example 9.
A reproduction beam was radiated onto the third layer (transcription layer), and a beam reflected by the third layer was processed by a known method, thereby reproducing data. In this case, a C/N ratio was 56 dB.
Next, a 6-MHz signal was over written. Data was reproduced from the third layer at a C/N ratio of 54 dB. The C/N ratio was improved by 5 dB as compared to Example 21.
EXAMPLE 40
Reproduction Apparatus for Magnets optical Recording
This apparatus is for only reproduction, and FIG. 41 shows the overall arrangement thereof.
The apparatus basically comprises:
(a) a rotation means 21 for rotating a disk-shaped multilayered magnetooptical recording medium 20 capable of over writing;
(b) a reproduction field applying means 28 for causing data recording in the first layer to be transcribed to the second layer before reproduction;
(c) a laser beam light source 23 as a linearly polarized light source;
(d) an optical analyzer 30 and a detector 31 constituting a reproduction means for receiving reflection light of linearly polarized light radiated on the second layer and reproducing data included in the reflection light in the form of an electrical signal. Note that the arrangement shown in FIG. 41 also includes a collimator lens 26, an objective lens 27, and a beam splitter 29.
As the reproduction field applying means 28, a permanent magnet of H.sub.R =300 Oe and having a direction of magnetic field corresponding to the "non-A direction" is used. The permanent magnet 28 is a rod-like member having a length corresponding to the radial length of the disk-shaped recording medium 20, and is arranged on the left side of a laser beam irradiation position (position of a pickup including the light source 23) in the rotation direction. As a result, before reproduction, data recorded in the first layer by the means 28 can be transcribed to the second layer. The transcribed data can be reproduced, resulting in a high C/N ratio.
EXAMPLE 41
Magnetooptical Recording/reproduction
A magnetooptical recording operation was performed using the recording apparatus of Example 11 (see FIG. 4). First, the recording medium 20 of Example 1 was rotated at a constant linear speed of 8.5 m/sec by the rotating means 21.
A laser beam is radiated onto the medium 20 from the second layer side. The laser beam was adjusted by means 24 to obtain an output of 9.3 mW (on disk) at high level and to obtain an output of 6.6 mW (on disk) at low level. The laser beam was pulse-modulated by the means 24 in accordance with data to be recorded. In this case, the data to be recorded was a signal having a frequency of 1 MHz. Therefore, the laser beam was radiated onto the medium 20 while being modulated at the frequency of 1 MHz. As a result, a 1-MHz signal was recorded.
When the data was reproduced upon irradiation of the laser beam from the second layer by the magnetooptical reproduction apparatus of Example 40 (FIG. 41), a C/N ratio was 54 dB and it was confirmed therefrom that the signal was actually recorded. The C/N ratio of 54 dB was higher by 3 dB than a case wherein data was reproduced from the first layer without performing application processing of the reproduction field H.sub.R (see Example 13). This will be expressed hereinafter as (+3 dB) after 54 dB.
A signal having a frequency of 5 MHz was newly recorded on an already recorded region of the medium 20 by the apparatus of Example 11. When the data was similarly reproduced, the newly recorded data was reproduced at C/N ratio of 51 dB (+3 dB). A bit error rate was 10.sup.-5 to 10.sup.-6. In addition, the 1-MHz signal (preceding data) was not reproduced at all. As a result, it was found that an over-write operation was enabled.
Note that under these conditions, the temperature of the medium reached T.sub.H =230.degree. C. at high level and T.sub.L =170.degree. C. at low level.
Claims
What is claimed is:
1. A method of thermomagnetic over write recording on a multilayered recording medium having first and second magnetic layers that are magnetically coupled, comprising: a) orienting the direction of magnetization of the second layer at at least one part of the medium in a predetermined direction without changing the direction of magnetization of the first layer at said one part; b) temporarily applying high energy to said one part of the medium so that said one part is heated to a first, high temperature level in accordance with a first kind of data to be recorded on said medium, and is then cooled, the direction of magnetization of said second layer at said one part being determined by the heating of said one part to said first temperature level, and the direction of magnetization of said first layer at said one part being determined in a first direction by said second layer at said one part, due to the magnetic coupling of said layers; c) orienting the direction of magnetization of the second layer at at least another part of the medium in said predetermined direction without changing the direction magnetization of the first layer at said another part; and d) temporarily applying low energy to said another part of the medium so that said another part is heated to a second, low temperature level in accordance with a second kind of data to be recorded on said medium, and is then cooled, the direction of magnetization of said first layer at said another part being determined in a second direction different from said first direction by said second layer at said another part, due to the magnetic coupling of said layers.
2. A method according to claim 1, wherein the method is performed so as to record a plurality of bits of data at a plurality of parts of said medium, respectively.
3. A method according to claim 2, wherein the method is repeated with respect to at least some parts of said plurality of parts of said medium to over write data recorded at said at least some parts with new data.
4. A method according to claim 2, wherein the applying of high and low energy to said medium comprises radiating a laser beam onto said medium and varying the intensity of said laser beam.
5. A method according to claim 4, wherein the method is performed while the medium is moved relative to the laser beam.
6. A method according to claim 1, wherein the method is performed on a recording medium in which the first and second layers are exchange-coupled layers of perpendicular magnetic anisotropy.
7. A method according to claim 1, wherein said orienting of the direction of magnetization of the second layer comprises applying to said medium a magnetic field that is sufficient to reverse the direction of magnetization of the second layer but is insufficient to reverse the direction of magnetization of the first layer.
8. A method according to claim 1, wherein the heating of said another part of the medium to said second, low temperature level is sufficient for reversal of the direction of magnetization of the first layer at said another part but is insufficient for reversal of the direction of magnetization of the second layer at said another part.
9. A method according to claim 1, wherein the heating of said one part of the medium to said first, high temperature level is sufficient for reversal of the direction of magnetization of said second layer at said one part, and wherein, the direction of magnetization of the second layer at said one part is reversed under the influence of a magnetic field.
10. A method according to claim 1, wherein the method is performed on a recording medium in which the first and second layers comprise rare earth (RE) and transition metal (TM) materials and wherein the medium is selected from one of nine classes and four types categorized in accordance with whether the first and second layers are RE rich or TM rich and whether the first and second layers have a compensation temperature (Tcomp.) that is between ambient temperature and the Curie temperature of the layer, as set forth in the following table: First Layer: Second Layer: Class RE rich RE rich Type ______________________________________ 1 Tcomp. Tcomp. 1 2 No Tcomp. Tcomp. 2 3 Tcomp. No Tcomp. 3 4 No Tcomp. No Tcomp. 4 ______________________________________ First Layer: Second Layer: Class RE rich TM rich Type ______________________________________ 5 Tcomp. No Tcomp. 3 6 No Tcomp. No Tcomp. 4 ______________________________________ First Layer: Second Layer: Class TM rich TM rich Type ______________________________________ 7 No Tcomp. No Tcomp. 4 ______________________________________ First Layer: Second Layer: Class TM rich RE rich Type ______________________________________ 8 No Tcomp. Tcomp. 2 9 No Tcomp. No Tcomp. 4 ______________________________________
11. A method according to claim 1, wherein the method is performed on a recording medium that is intrinsically capable of maintaining, at ambient temperature, two different magnetic states, in the first of which the magnetization directions are the same for the first and second layers and in the second of which the magnetization directions of the first and second layers are opposite to each other.
12. A method according to claim 1, further comprising temporarily raising the temperature of said parts of the medium to a temperature level that is lower than said first and second levels and reproducing data from said parts.
13. A method according to claim 1, further comprising reproducing data from said parts magnetooptically.
14. A method according to claim 1, wherein the method is performed on a recording medium in which, at ambient temperature, the coercivity of the first layer is higher than the coercivity of the second layer.
15. A method according to claim 14, wherein the recording medium on which the method is performed has the following characteristics in order of increasing temperature from ambient temperature: compensation temperature of the first layer, Curie temperature of the first layer, compensation temperature of the second layer, and Curie temperature of the second layer, and wherein the low temperature level is a temperature near the Curie temperature of the first layer, and the high temperature level is a temperature near the Curie temperature of the second layer and above the compensation temperature of the second layer.
16. A method according to claim 14, wherein the recording medium on which the method is performed has the following characteristics in order of increasing temperature from ambient temperature: Curie temperature of the first layer, compensation temperature of the second layer, and Curie temperature of the second layer, there being no compensation temperature of the first layer between ambient temperature and the Curie temperature of the first layer, and wherein the low temperature level is near the Curie temperature of the first layer, and the high temperature level is near the Curie temperature of the second layer and above the compensation temperature of the second layer.
17. A method according to claim 14, wherein the recording medium on which the method is performed has the following characteristics in order of increasing temperature from ambient temperature: compensation temperature of the first layer, Curie temperature of the first layer, and Curie temperature of the second layer, there being no compensation temperature of the second layer between ambient temperature and the Curie temperature of the second layer, and wherein the low temperature level is near the Curie temperature of the first layer, and the high temperature level is near the Curie temperature of the second layer and above the Curie temperature of the first layer.
18. A method according to claim 14, wherein the recording medium on which the method is performed has the following characteristics in order of increasing temperature from ambient temperature: Curie temperature of the first layer and Curie temperature of the second layer, neither the first layer nor the second layer having a compensation temperature between ambient temperature and its Curie temperature, and wherein the low temperature level is near the Curie temperature of the first layer and is below the Curie temperature of the second layer, and the high temperature level is near the Curie temperature of the second layer and is above the Curie temperature of the first layer.
19. A method according to claim 14, wherein the recording medium on which the method is performed has the following characteristics in order of increasing temperature from ambient temperature: Curie temperature of the first layer and Curie temperature of the second layer, wherein the low temperature level is a temperature near the Curie temperature of the first layer, and the high temperature level is a temperature near the Curie temperature of the second layer.
20. A method of thermomagnetic recording on a multilayered recording medium having first and second magnetic layers that are magnetically coupled, comprising: a) orienting the direction of magnetization of the second layer at at least a part of the medium in a predetermined direction without changing the direction of magnetization of the first layer at said part; and b) temporarily applying energy to said part of the medium so that said part is heated to a temperature level sufficient for reversal of the direction of magnetization of the first layer at said part but insufficient for reversal of the direction of magnetization of the second layer at said part, and is then cooled, the direction of magnetization of the first layer at said part being determined by the direction of magnetization of the second layer at said part, due to the magnetic coupling of said layers.
21. A method of thermomagnetic recording on a multilayered magnetic recording medium having first and second magnetic layers that are magnetically coupled, comprising: a) orienting the direction of magnetization of the second layer at at least a part of the medium in a predetermined direction without changing the direction of magnetization of the first layer at said part; and b) temporarily applying energy to said part of the medium so that said part is heated to a temperature level sufficient for reversal of the direction of magnetization of said second layer at said part, and is then cooled, the direction of magnetization of the second layer at said part being oriented in a direction opposite to said predetermined direction and the direction of magnetization of the first layer at said part being determined by the direction of magnetization of the second layer at said part, due to the magnetic coupling of said layers.
22. A method of thermomagnetic over write recording on a multilayered recording medium having first and second magnetic layers that are magnetically coupled, comprising: a) orienting the direction of magnetization of the second layer at at least one part of the medium in a predetermined direction without changing the direction of magnetization of the first layer at said one part; b) temporarily applying high energy to said one part of the medium so that said one part is heated to a first, high temperature level in accordance with a first kind of data to be recorded on said medium, and is then cooled, the heating of said one part of the medium to said first, high temperature level being sufficient for reversal of the direction of magnetization of said second layer at said one part, so that the direction of magnetization of said second layer at said one part is determined by the heating of said one part to said first temperature level, and the direction of magnetization of said first layer at said one part being determined in a first direction by said second layer at said one part, due to the magnetic coupling of said layers; c) orienting the direction of magnetization of the second layer at at least another part of the medium in said predetermined direction without changing the direction of magnetization of the first layer at said another part; and d) temporarily applying low energy to said another part of the medium so that said another part is heated to a second, low temperature level in accordance with a second kind of data to be recorded on said medium, and is then cooled, the heating of said another part of the medium to said second, low temperature level being sufficient for the reversal of the direction of magnetization of the first layer at said another part but insufficient for reversal of the direction of magnetization of the second layer at said another part, the direction of magnetization of said first layer at said another part being determined in a second direction different from said first direction by said second layer at said another part, due to the magnetic coupling of said layers; p1 wherein the method is performed so as to record each of said first and second kinds of data at pluralities of parts of said medium.
23. A thermomagnetic over write recording method comprising the steps of: a) providing a thermomagnetic recording medium having a magnetic recording layer formed of first and second magnetic thin films magnetically coupled with each other, each of said first and second magnetic thin films being an alloy of transition metal (TM) and rare earth metal, said second magnetic thin film having TM spin in an initial direction; b) heating said magnetic recording layer to a first temperature which is near a Curie temperature of said first magnetic thin film and which is insufficient to cause invention of said initial direction of TM spin in said second magnetic thin film; c) cooling said magnetic recording layer from said first temperature, said TM spin in said first magnetic thin film then being in the same direction as said initial direction of TM spin in said second magnetic thin film; d) heating said magnetic recording layer to a second temperature which is near a Curie temperature of said second magnetic thin film and is sufficient to cause inversion of said initial direction of TM spin in said second magnetic thin film; and e) cooling said magnetic recording layer from said second temperature, TM spin in said first magnetic thin film then being in the same direction as the inverted direction of TM spin in said second magnetic thin film; wherein said heating is modulated so as to raise the temperature of said magnetic recording layer to one of said first temperature and said second temperature according to a signal to be recorded.
24. A method according to any one of claim 1, 20, 21, and 22, wherein said first layer is a thin magnetic film having a high coercivity at room temperature and said second layer is a thin magnetic film having a lower coercivity at room temperature.
25. A method according to any one of claim 1, 20, 21, and 22, wherein said first layer is a thin magnetic film having a low Curie temperature, and wherein said second layer is a thin magnetic film having a Curie temperature higher than that of said first layer.
26. A method of thermomagnetic over write recording comprising: a) preparing a multilayered recording medium having first and second magnetic layers that are magnetically coupled, in which the direction of magnetization of the second layer can be oriented in a predetermined direction without reversing the direction of magnetization of the first layer and the direction of magnetization of the second layer at at least one part of said medium has been oriented in said predetermined direction; b) moving said medium; c) radiating a laser beam onto said part of said moving medium; and d) pulse modulating an intensity of said laser beam between a high level and a low level in accordance with binary data to be recorded, to from one of two bits having upward-magnetization and downward-magnetization, respectively, on said first layer at said part when the intensity of the pulse-modulated laser beam is at the high level, and to form the other bit on said first layer at said part when the intensity of the pulse-modulated laser beam is at the low level.
Patent Citations (10)
Non-Patent Literature (2)
- Nippon Kogaku K.K., "Overwrite System of Magneto Optical disk system" International Symposium on Magneto-optics, Apr. 1987 (pp. 1-7).
- R. G. Swartz and B. A. Wooley, "The Bell System Technical Journal", 1983, vol. 62, pp. 1925-1937.