Polymer Substituted Amido-Amine Mannich Base Lubricant Dispersant Additives

This invention relates to improved oil soluble dispersant additives useful oleaginous compositions, including fuel and lubricating oil compositions, and to concentrates containing said additives.

U.S. Pat. No. 3,442,808 relates to lubricating oil additives prepared by reacting alkenyl succinic anhydride with the Mannich condensation product prepared by condensing alkyl substituted phenol, formaldehyde and polyalkylene polyamine.

U.S. Pat. No. 3,458,495 relates to oxidation inhibitors and dispersant-detergent oil additives comprising the reaction product of ore equivalent of a phosphosulfurized hydrocarbon and about 0.5 to 4 equivalents of an alkylene amino phenol. The phosphosulfurized hydrocarbons are prepared by reacting a terpene, a petroleum fraction or a 500 to 200,000 molecular weight C.sub.2 to C.sub.6 olefin polymer (including polymers of ethylene, propylene, butylene, isobutylene or isoamylene) and from 5 to 40 wt % of a sulfide of phosphorous. The alkylene amino phenol is prepared by a Mannich Base condensation of aldehyde, alkylene polyamine and alkyl phenol.

U.S. Pat. No. 4,354,950 discloses a method of preparing Mannich base derivative of hydroxyaryl succinimides of the formula: ##STR1## wherein R is hydrocarbyl of 25 to 200 carbon atoms, R' is H, alkyl or halogen, "n" is 2 or 3, "m" has a value of 1 to 5, Y is H or a methylene hydroxyaryl succinimide radical, "x" has a value of 1 to 2 when Y is H and a value of 1 when Y is a methylene hydroxyaryl succinimide radical. The above succinimides are formed in a stepwise reaction, e.g., by reacting a polyalkenyl succinic anhydride with an aminophenol, to produce an intermediate N-(hydroxyaryl) hydrocarbyl succinimide, which is then reacted with an alkylene diamine and an aldehyde (e.g., formaldehyde) in a Mannich base reaction to produce the described succinimides. The described succinimides may be added to a base oil of lubricating viscosity to form lubricant concentrates and lubricating oil formulations.

In accordance with one aspect of the present invention, an oil-soluble fuel and lubricating oil additive is provided which comprises a Mannich Base condensate of an alkyl substituted hydroxyromatic compound with formaldehyde and an amido-amine or thioamido-amine, wherein the alkyl-moiety of the aromatic compounds is derived from at least one polymer of 300 to 10,000 number average molecular weight, and wherein the amido-amine and thioamido-amine comprises the reaction product of at least one polyamine and an alpha, beta-ethylenically unsaturated compound. The alpha, beta-ethylenically unsaturated compound can comprise at least one compound of the formula (I): ##STR2## wherein X is sulfur or oxygen, Y is --OR.sup.4, --SR.sup.4, or --NR.sup.4 (R.sup.5) , and R.sup.1, R.sup.2, R.sup.3, R.sup.4 and R.sup.5 are the same or different and are hydrogen or substituted or unsubstituted hydrocarbyl.

The process of this invention permits the preparation of novel oil-soluble Mannich Base condensate lubricating oil additives as substantially halogen free materials, thereby reducing the corrositivity processing difficulties and environmental concerns which are associated with halogen-containing lubricating oil additives.

The materials of the invention are different from the prior art Mannich Base materials because of their effectiveness and their ability, to provide enhanced lubricating oil dispersancy, as exhibited by their enhanced sludge and varnish control properties.

The hydroxy aromatic compounds useful in the preparation of the alkylated materials of this invention include those compounds having the formula (II):

wherein Ar represents ##STR3## wherein a is 1 or 2, R' is a halogen radical such as the bromide or chloride radical, b is an integer from 0 to 2, and c in an integer from 1 to 2.

Illustrative of such Ar groups are phenylene, biphenylene, naphthylene and the like.

The selected polymer and hydroxy aromatic compound are contacted in the presence of a catalytically effective amount of at least one acidic alkylation catalyst under conditions effective to alkylate the aromatic group of the hydroxy aromatic compound. The alkyation catalyst is conventional and can comprise inorganic acids such as H.sub.3 PO.sub.4, H.sub.2 SO.sub.4, HF, BF.sub.3, HF--BF.sub.3 and the like. The acid catalyst can also comprise an acidic ion exchange resin having acidic groups adsorbed or absorbed thereon, such as Amberlyst 15 resin (Rohm & Haas Co.), and the like. Also useful as catalysts are preformed complexes (or complexes formed in situ) of the foregoing with C.sub.2 to C.sub.10 ethers, C.sub.1 to C.sub.10 alcohols, C.sub.2 to C.sub.10 ketones, phenols and the like, such as BF.sub.3 complexed with dimethyl ether, diethyl ether, phenol, and the like.

The hydroxy aromatic compound and polymer will be generally contacted in a ratio of form about 0.1 to 10, preferably from about 1 to 7, more preferably from about 2 to 5, moles of the aromatic compound per mole of the polymer. The selected acid catalyst can be employed in widely varying concentrations. Generally, when the acid catalyst comprises an inorganic catalyst the acid catalyst will be charged to provide at least about 0.001, preferably from about 0.01 to 0.5, more preferably from about 0.1 to 0.3, moles of catalyst per mole of hydroxy aromatic compound charged to the alkylation reaction zone. Use of greater than 1 mole of the inorganic catalyst per mole of hydroxy aromatic compound is not generally required. When the acid catalyst comprises a supported catalyst, such as an acidic ion exchange resin, the reactants can be contacted with the ion exchange resin employing any conventional solid-liquid contacting techniques, such as by passing the reactants through the resin (e.g., in a catalyst bed or through a membrane impregnated or otherwise containing the resin catalyst) and the upper limit on the moles of catalyst employed per mole of hydroxy aromatic compound is not critical.

The temperature for alkylation can also vary widely, and will usually range from about 20.degree.to 250.degree. C., preferably from about 30.degree.to 150.degree. C., more preferably from about 50.degree.to 80.degree. C.

The alkylation reaction time can vary and will generally be from about 1 to 5 hours, although longer or shorter times can also the employed. The alkylation process can be practiced in a batchwise, continuous or semicontinuous manner. Preferably, the acid catalyst is neutralized and/or removed prior to contacting the alkylation product mixture with the nucleophilic reagent (e.g., polyamine) and aldelyde reactant. The neutralization can be accomplished by contacting the crude alkylation product with gaseous ammonia or other basically reacting compound (e.g., aqueous NaOH, KOH, and the like), followed by filtration to remove any precipitated neutralized catalyst solids.

Alkylation processes of the above types are known and are described, for examples in U.S. Pat. Nos. 3,539,633 and 3,649,229, the disclosures of which are hereby incorporated by reference.

The polymers which can be charged to the alkylation reaction zone include polyalkenes derived alkenes having from 1 to 20 carbon atom: (butene, pentene, octene, decene, dodecene, tetradodecene and the like) and homopolymers of C.sub.3 to C.sub.10, e.g., C.sub.2 to C.sub.5, monoolefins, and copolymers of C.sub.2 to C.sub.10, e.g., C.sub.2 to C.sub.5, monoolefins, said additional polymer having a number average molecular weight of at least about 500, and a molecular weight distribution of less than about 4.0, preferably less than about 3.0 (e.g, from 1.2 to 2.8). Preferred such additional olefin polymers comprise a major molar amount of C.sub.2 to C.sub.10, e.g. C.sub.2 to C.sub.5 monoolefin. Such olefins include ethylene, propylene, butylene, isobutylene, pentene, octene-1, styrene, etc. Exemplary of the additionally charged homopolymers is polypropylene, polyisobutylene, and poly-n-butene the like as well as interpolymers of two or more of such olefins such as copolymers of ethylene and propylene, prepared by conventional methods, which are substantially saturated, wherein less than about 10 wt% of the polymer chains contain ethylenic unsaturation; butylene and isobutylene; propylene and isobutylene; etc. Other copolymers include those in which a minor molar amount of the copolymer monomers, e.g., 1 to 10 mole %, is a C.sub.4 to C.sub.18 non-conjugated diolefin, e.g., a copolymer of isobutylene and butadiene or a copolymer of ethylene, propylene and 1,-hexadiene; etc. Such olefin polymers charged to the alkylation reaction will usually have number average molecular weights of at least about 900 (e.g., from about 700 to about 5,000) more generally within the range of about 1200 and about 5,000, more usually between about 1500 and about 4000. Particularly useful such olefin polymers have number average molecular weights within the range of about 1500 and about 3000 with approximately one double bond per chin. An especially useful polymer is polyisobutylene.

The number average molecular weight for such polymers can be determined by several known techniques. A convenient method for such determination is by gel permeation chromatography (GPC) which additionally provides molecular weight distribution information, see W. W. Yau, J. J. Kirkland and D. D. Bly, "Modern Size Exclusion Liquid Chromatography", John Wiley and Sons, N.Y., 1979.

The aldehyde reactants will generally comprise formaldehyde or parafomaldehyde, although it will be understood that other aldehyde-group containing compounds, such as C.sub.2 to C.sub.10 hydrocarbyl aledehydes (e.g., butyraldehyde, acetaldehyde, propionaldehyde, and he liike) can also be employed. A preferred group of aldehyde materials are compounds o the formula: R"CHO, wherein R" is H or aliphatic hydrocarbon radical having from 1 to 4 carbon atoms.

Amido-amine and thioamido-amine compounds useful herein comprise reaction products of alpha, beta-unsaturated compounds and at least one polyamine. Any polyamine, whether aliphatic, cycloaliphatic, aromatic, heterocyclic, etc., can be employed provided it is capable of adding across the acrylic double bond and amidifying with for example the carbonyl group (--C(O)--) of the acrylate-type compound of formula I, or with the thiocarbonyl group (--C(S)--) of the thioacrylate-type compound of formula I. Amione compounds useful for reaction with the selected alpha, beta unsaturated compound include polyamines of about 2 to 60, preferably 2 to 40 (e.g. 3 to 20), total carbon atoms and about 2 to 12, preferably 3 to 12, and most preferably 3 to 9 nitrogen atoms int eh molecule. These amines may be hydrocarbyl amines or may be hydrocarbyl amines including other groups, e.g., hydroxy groups, alikoxy groups, amide groups, nitriles, imidazoline groups, and the like. Hydroxy amines with 1 to 6 hydroxy groups, preferably 1 to 3 hydroxy groups are particularly useful. Preferred amines are aliphatic saturated amines, including those o the general formulas: ##STR4## wherein R, R', R'' and R''' are independently selected from the group consisting of hydrogen; C.sub.1 to C.sub.25 straight or branched chain alkyl radicals; C.sub.1 to C.sub.12 alkoxy C.sub.2 to C.sub.6 alkylene radicals; C.sub.2 to C.sub.12 hydroxy amino alkylene radicals; and C.sub.1 to C.sub.12 alkylamino C.sub.2 to C.sub.6 alkylene radicals; and wherein R"' can additionally comprise a moiety of the formula: ##STR5## wherein R' is as defined above, and wherein r and r' can be the same or a different number of from 2 to 6, preferably 2 to 4; and t and t' can be the same or different and are numbers of from 0 to 10, preferably 2 to 7, and most preferably about 3 to 7, with the proviso that the sum of t and t' is not greater than 15. To assure a facile reaction, it is preferred that R, R', R'', R''', r, r', t and t'be selected in a manner sufficient to provide the compounds of Formulas II and III with typically at least one primary or secondary amine group, preferably at least two primary or secondary amine groups. This can be achieved by selecting at least one of said R, R', R'', or R''' groups to be hydrogen or by letting t in Formula III be at least on a when R"' is H or when the IV moiety possesses a secondary amino group. The most preferred amine of the above formulas are represented by Formula III and contain at least two primary amine groups and at least one, and preferably at least three, secondary amine groups.

Non-limiting examples of suitable amine compounds include: 1,2-diaminoethane; 1,3-diaminopropane; 1,4-diaminobutane; 1,6-diaminohexane; polyethylene amines such as diethylene triamine; trietylene tetramine; tetraethylene pentamine; polypropylere amines such as 1,2-propylene diamine; di-(1,2-prcpylene)triamine; di -(1,3-propylene) triamine; N,N-dimethyl-1,3-diaxinopropane; N,N-di-(2-aminoethyl) ethylene diamine; N, N-di (2-hydroxyethyl) -1,3-propylene diamine; 3-dodecyloxypropylamine; N-dodecyl-1,3-propane diamine; this hydroxymethylaminomethane (THAM); diisopropanol amine; diethanol amine; triethanol amine; mono-, di-, and tri-tallow amines; amino morpholines such as N-(3-aminopropyl)morpholine; and mixtures thereof.

Other useful amine compounds include alicyclic diamines such as 1,4-di(aminomethyl) cyclohexane, and heterocyclic nitrogen compounds such as imidazolines, and N-aminoalkyl piperazines of the general formula (V): ##STR6## wherein p.sub.1 and p.sub.2 are the same or different and are each integers of from to 4, and n.sub.1, n.sub.2 and n.sub.3 are the same or different and are each integers of from 1 to 3. Non-limiting examples of such amines include 2-pentadecyl imidazoline; N-(2-aminoethy) piperazine; etc.

Commercial mixtures of amine compounds may advantageously be used. For example, one process for preparing alkylene amines involves the reaction of an alkylene dihalide (such as ethylene dichloride or propylene dichloride) with ammonia, which results in a complex mixture of alkylene amines wherein pairs of nitrogens are joined by alkylene groups, forming such compounds as diethylene triamine, triethylenetetramine, tetraethylene pentamine and isomeric piperazines. Low cost poly(ethyleneamines) compounds averaging about 5 to 7 nitrogen atoms per molecule are available commercially under trade names such as "Polyamine H", "Polyamine 400", "Dow Polyamine E-100", etc.

Useful amines also include polyoxyalkylene polyamines such as those of the formula (V/I): ##STR7## where m has a value of about 3 to 70 and preferably 10 to 35; and the formula (VII):

where n"' has a value of about 1 to 40 with the provision that the sum of all the n"' values is from about 3 to about 70 and preferably from about 6 to about 35, and R.sup.4 is a polyvalent saturated hydrocarbon radical of up to ten carbon atoms wherein the number of substituents on the R.sup.8 group is represented by the value of "a", which is a number of from 3 to 6. The alkylene groups in either formula (VI) or (VII) may be straight or branched chains containing about 2 to 7, and preferably about 2 to 4 carbon atoms.

The polyoxyalkylene polyamines of formulas (VI) or (VII) above, preferably polyoxyalkyene diamines and polyoxyalkylene triamines, may have average molecular weights ranging from about 200 to about 4000 and preferably from about 400 to about 2000. The preferred polyoxyalkelene polyoxyalkylene polyamines include the polyoxyethylene and polyoxypropylene diaminer and the polyoxypoopylene triamines having average molecular weights ranging from about 200 to 2000. The polyoxyalkylene polyamines are commercially available and may be obtained, for example, from the Jefferson Chemical Company, Inc. under the trade name "Jeffamines D-230, D-400, D-1000, D-2000, T-403", etc.

As indicated above, the amido-amine and thioamide-amine compounds are formed by reaction of at least one polyamine with at least one alpha, beta unsaturated compound of the formula: ##STR8## wherein X is sulfur or oxygen, Y is --OR.sup.8, --SR.sup.8, or --NR.sup.8 (R.sup.9), and R.sup.5, R.sup.6, R.sup.7, R.sup.8 and R.sup.9 re the same or different and are hydrogen or substituted or unsubstituted hydrocarbyl.

When R.sup.5, /R.sup.6, R.sup.7, R.sup.8 or R.sup.9 in Formula I are hydrocarbyl, these groups can comprise alkyl, cycloalkyl, aryl, alkaryl, aralkyl or heterocyclic, which can be substituted with groups which are substantially inert to any component of the reaction mixture under conditions selected for preparation of the amido-amine. Such substituent groups include hydroxy, halide (e.g., Cl, Fl, I, Br), --SH and alkylthio. When one or more of R.sup.5 through R.sup.9 are alkyl, such alkyl groups can be straight or branched chain, and will generally contain from 1 to 20, more usually from 1 to 10, and preferably from 1 to 4, carbon atoms. Illustrative of such alkyl groups are methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonly, decyl, dodceyl, tridecyl, hexadecyl, octadecyl and the like. When one or more of R.sup.5 through R.sup.9 are aryl, the aryl group will generally contain from 6 to 10 carbon atoms (e.g., phenyl, naphthyl).

When one or more of R.sup.5 through R.sup.9 are alkaryl, the alkaryl group will generally contain from about 7 to 20 carbon atoms, and preferably from 7 to 12 carbon atoms. Illustrative of such alkaryl groups are tolyl, m-ethylphenyl, o-ethyltolyl, and m-hexytolyl. When one or more of R.sup.5 through R.sup.9 are aralkyl, the aryl component generally consists of phenyl or (C.sub.1 to c.sub.6) alkyl-substituted phenol and he alkyl component generally contains from 1 to 12 carbon atoms, and preferably from 1 to 6 carbon atoms. Example of such aralkyl groups are benzyl, o-ethylbenzyl, and 4-isobutylbenzyl. When one or more of R.sup.5 and R.sup.9 are cycloalkyl, the cycloalkyl group will generally contain from 3 to 12 carbon atoms, and preferably from 3 to 6 carbon atoms. Illustrative of such cycloalkyl groups are cyclopropyl, cyclobutyl, cyclohexyl, cyclobutyl, and cyclododecyl. When one or more of r.sup.5 through R.sup.9 are heterocyclic, the heterocyclic group generally consists of a compound having at least one ring of 6 to 12 members in which on or more ring carbon atoms is replaced by oxygen or nitrogen. Examples of such heterocyclic groups are furyl, pyranyl, pyridyl, piperidyl, dioxanyl, tetrahydrofuryl, pyrazinyl and 1,4-oxyazinyl.

The alpha, beta ethylenically unsaturated caboxylate compounds employed herein have the following formula: ##STR9## wherein R.sup.5, R.sup.6, R.sup.7, and R.sup.8 are the same or different and are hydrogen or substituted or unsubstituted hydrocarbyl as defined above. Example for such alpha, beta-ethylenically unsaturated carboxylate compounds of formula VIII are acrylic acid, methacrylic acid, the methyl, ethyl, isopropyl, n-butyl, and isobutyl esters of acrylic and methacrylic acids, 2-butenoic acid, 2-hexenoic acid, 2-decenoic acid, 3-methyl-2-heptenoic acid, 3-methyl-2-butenoic acid, 3-phenyl-2-propenoic acid, 3-cyclohexyl-2-butenoic acid, 2-methyl-2-butenoic acid, 2-propyl-2-propenoic acid, 2-isopropyl-2-hexenoic acid, 2, 3-dimethyl-2-butenoic acid, 3-cyclohexyl-2-methyl-2-pentenoic acid, 2-propenoic acid, methyl 2-propenoate, methyl 2-methyl 2-propenoate, methyl 2-butenoate, ethyl 2-hexenoate, isopropyl 2-decenoate, phenyl 2-pentenoate, tertiary butyl 2-prepenoate, octadecyl 2-propenoate, dodecyl 2-decenoate, cyclopropyl 2,3-dimethyl-2-butenoate, methyl 3-phenyl-2-propenoate, and the like.

The alpha, beta ethylenically unsaturated carboxylate trimester compounds employed herein have the following formula: ##STR10## wherein R.sup.5, R.sup.6, R.sup.7, and R.sup.8 are the same or different and are hydrogen or substituted or unsubstituted hydrocarbyl as defined above. Examples of such alpha, beta-ethylenically unsaturated carboxylate thioesters of formula IX are methylmercapto 2-butencate, ethylmercapto 2-hexenoate, isopropylmercapto 2-decenoate, phenylmercapto 2-pentenoate, tertiary butylmercapto 2-propenoate, octadecylmercapto 2-propenoate, dodecylmercapto 2-decenoate, cyclopropylmercapto 2,3-dimethyl-2-butenoate, methylmercapto 3-phenyl-2-propenoate, methylmercapto 2-propenoate, methylmercapto 2-methyl-2-propenoate, and the like.

The alpha, beta ethylentially unsaturated carboxyamide compounds employed herein have the following formula: ##STR11## wherein R.sup.5, R.sup.6, an R.sup.7, R.sup.8 and R.sup.9 are the same or different and are hydrogen or substituted or unsubstituted hydrocarbyl as defined above. Examples of alpha, beta-ethylenically unsaturated carboxyamides of formula X are 2-butenamide, 2-hexenamide, 2-decenamide, 3-methyl-2-heptenamide, 3-methyl-2-butenamide, 3-phenyl-2-propenamide, 3-cycloyexyl-2-butenamide, 2-methyl-2-butenamide, 2-prypyl-2-propenamide, 2-isopropyl-2-hexenamide, 2,3-dimethyl-2-butenamide, 3-cyclohexyl-2-methyl-2-pentenamide, N-methyl 2-butenamide, N,N-diethyl 2-hexenamide, N-isopropyl 2-decenamide, N-phenyl 2-pentenamide, N-tertiary butyl 2-propenamide, N-octadecyl 2-propenamide, N-N-didodetyl 2-decenamide, N-cyclopropyl 2,3-dimethyl-2-butenamide, N-methyl 3-phenyl-2-propenamide, 2-propenamide, 2-methyl-2-propenamide, 2-ethyl-2-propenamide and the like.

The alpha, beta ethylenizally unsaturated thiocarboxylate compounds employed wherein have the following formula: ##STR12## wherein R.sup.5, R.sup.6, R.sup.7, R.sup.8 and R.sup.9 are the same or different and are hydrogen or substituted or unsubstituted hydrocarbyl as defined above. Examples of alpha, beta-ethylenically unsaturated thiocarboxylate compounds of formula XI are 2-butenthioic acid, 2-hexenthioic acid, 2-decenthioic acid, 3-methyl-2-heptenthioic acid, 3-methyl-2-butenthioic acid, 3-phenyl-2-propenthioic acid, 3-cyclohexyl-2-butenthioic acid, 2-methyl-2-butenthioic acid, 2-propyl-2-propenthioic acid, 2-isopropyl-2-hexenthioic acid, 2,3-dimethyl-2-butenthioc acid, 3-cyclo-hexyl-2-methyl-2-pententhioic acid, 2-propenthioic acid, methyl 2-propenthioate, methyl 2-methyl 2-propenthioate, methyl 2-butenthioate, ethyl 2-hexenthioate, isopropyl 2-decenthioate, phenyl 2-pententhioate, tertiary butyl 2-propenthioate, octadecyl 2-propenhioate, dodecyl 2-decenthioate, cyclopropyl 2,3-dimethyl-2-butenthioate, methyl 3-phenyl-2-propenthioate, and the like.

The alpha, beta ethylenically unsaturated dithioic acid and acid ester compounds employed herein have the following formula: ##STR13## wherein R.sup.5, R.sup.6, R.sup.7, and R.sup.8 are the same or different and are hydrogen or substituted or unsubstituted hydrocarbyl as defined above. Examples of alpha, beta-ethylenically unsaturated dithioil acids and acid esters of formula XII are 2-butendithioic acid, 2-hexendithioic acid, 2-decendithioic acid, 3-methyl-2-heptendithioic acid, 3-methyl-2-butendithioic acid, 3-phenyl-2-propendithioic acid, 3-gyclohexyl-2-butendithioic acid, 2-methyl-2-butengithioic acid, 2-propyl-2-propendithioic acid, 2-isopropyl-2-hexendithioic acid, 2,3-dimethyl-2-butendithioic acid, 3-cyclo-hexyl-2-methyl-2-pentendithioic acid, 2-propendithioic acid, methyl 2-propendithioate, methy. 2-methyl 2-propendithioate, methyl 2-butendithioate, ethyl 2-hexendithioate, isopropyl 2-decendiphioate, phenyl 2-pentendithioate, tertiary butyl 2-propendithioate, octadecyl 2-propendithioate, dodecyl 2-decendithioate, cyclopropyl 2,3-dimethyl-2-butendithioate, methyl 3-phenyl-2-propendithioate, and the like.

The alpha, beta ethylenically unsaturated thiocarboxyamide compounds employed herein have the following formula: ##STR14## wherein R.sup.6, R.sup.7, R.sup.8 and R.sup.9 are the same or different and are hydrogen or substituted or unsubstituted hydrocarbyl as defined above. Examples of alpha, beta-ethylenically unsaturated thiocarbonyamides of formula XIIl are 2-butenthioamide, 2-hexenthioamide, 2-iecenthioamide, 3-methy1-2-heptenthioamide, 3-methyl-2-butenthioamide, 3-pheny1-2-propenthioamide, 3-cyclohexyl-2-butenthioamide, 2-methyl-2-butenthioamide, 2-propyl-2-propenthioamide, 2-isopropyl-2-hexenthioamide, 2,3-dimethyl-2-butenthioamide, 3-zyclohexyl-2-methyl-2-pententhioamide, N-methyl 2-butenthioamide, N,N-diethyl 2-hexenthioamide, N-isopropyl 2-mecenthioamide, N-phenyl 2-pententhiamide, N-tertiary butyl 2-propenthioamide, N-octadecyl 2-propenthioamide, N-N-didodecyl 2-decenthioamide, N-cyclopropyl 2,3-dimethyl-2-butenthioamide, N-methyl 3-phenyl-2-propenthioamide, 2-propenthioamide, 2-aethyl-2-propenthioamide, 2-ethyl-2-propenthioamide and the like.

Preferred compounds for reduction with the polyamines in accordance with this invention are lower alkyl esters of acrylic and (lower alkyl) substituted acrylic acid. Illustrative of such preferred compounds are compounds of the formula: ##STR15## where R.sup.7 is hydrogen or a C.sub.1 to C.sub.4 alkyl group, such as methyl, and R.sup.8 is hydrogen or a C.sub.1 to C.sub.4 alkyl group, capable of being removed so as to form an amido group, for example, methyl, ethyl, propyl, isopropyl, butyl, sec-butyl, tert-butyl, aryl, hexyl, etc. In the preferred embodiments these compounds are acrylic and methacrylic esters such as methyl or ethyl acrylate, methyl or ethyl methacrylate. When the selected alpha, beta-unsaturated compound comprises a compound of formula I wherein X is oxygen, the resulting reaction product with the polyamine contains at least one amide linkage (--C(O)N<) and such materials are herein termed "amido-amines." Similarly, when the selected alpha, beta unsaturated compound of formula I comprises a compound wherein X is sulfur, the resulting reaction product with the polyamine contains thioamide linkage (--C(S)N<) and these materials are herein termed "thioamido-amines." Fer convenience, the following discussion is directed to the Preparation and use of amido-amines, although it will be understood that such discussion is also applicable to the thiomido-amines.

The type of amido-amine formed varies with reaction conditions. For example, a more linear amido-amine is formed where substantially) equimolar amounts of the unsaturated carboxylate and polyamine are reacted. The presence of excesses of the ethyletically unsaturated reactant of formula I tends to yield and amido-amine which is more cross-linked than that obtained where substantially equimolar amounts of reactants are employed. Where for economic or other reasons a cross-linked amido-amine using excess amine is desired, generally a polar excess of the ethylenically unsaturated reactant of about at least 10%, such as 10-300%, or greater, for example, 25-200%, is employed. For more efficient cross-linking an excess of carboxylated material should preferably) be used since a cleaner reaction ensues. For example, a molar excess of about 10-100% or greater such as 10-50%, but preferably an excess of 30-50%, of the carboxylatee material. Larger excess can be employed if desired.

In summary, without considering other factors, equimolar amounts of reactants tend to produce a more linear amido-amine whereas excess of the formula I reactant tends to yield a more cross-linked amide-amine. It should be noted that the higher the polyamine (i.e., in greater the number of amino groups on the molecule) the greater the statistical probability of cross-linking since, for example, a tetraalkylenepentaline, such as tetraethylene petamine ##STR16## has more labile hydrogens than ethylene d;.amine.

These amido-amine adducts so formed are characterized by both amido and amino groups. In their simplest embodiments they may be represented by units of the following idealized formula (XIV): ##STR17## wherein the R.sup.10, s, which may be the same or different, are hydrogen or a substituted group, such as a hydrocarbon group, for example, alkyl, alkenyl, alkynyl, aryl, etc., and A is a moiety of the polyamine which, for example, may be aryl, cycloalkyl, alkyl, etc., and n.sub.4 is an integer such as 1-10 or greater.

The above simplified formula represents a linear amido-amine polymer. However, cross-linked polymers may also be formed by employing certain conditions since the polymer has labile hydrogens which can further react with either the unsaturated moiety by adding across the double bond or by amidifying with a carboxylate group.

Preferably, however, the amido-amines employed in this invention are not cross-linked to any substantial degree, and more preferably are substantially linear.

Preferably, the polyamine reactant contains at least one primary amine (and more preferably from 2 to 4 primary amines) group per molecule, and the polyamine and the unsaturated reactant of formula I are contacted in an amount of from about 1 to 10, more preferably from about 2 to 6, and most preferably from about 3 to 5, equivalents of primary amine in the polyamine reactant per mole of the unsaturated reactant of formula I.

The reaction between the selected polyamine and acrylate-type compound is carried out at any suitable temperature. Temperatures up to the decomposition points of reactants and products can be employed. In practice, one generally carries out the reaction by heating the reactants below 100.degree. C., such as 80.degree.-90.degree. C., for a suitable period of time, such as a few hours. Where an acrylic-type ester is employed, the progress of the reaction can be judged by the removal of the alcohol in forming the amide. During the early part of the reaction alcohol is removed quite readily below 100.degree. C. in the case of low boiling alcohols such as methanol or ethanol As the reaction slows, the temperature is raised to push the polymerization to completion and the temperature may be raised to 150.degree. C. toward the end of the reaction. Removal of alcohol is a convenient method of judging the progress and completion of tha reaction which is generally continued until no more alcohol is evolved. Based on removal of alcohol, the yields are generally stoichiometric. In more difficult reactions, yield of at least 95 % are generally obtained.

Similarly, it will be understood that the reaction of an ethylenically unsaturated carbocxylate trimester of formula XII liberates the corresponding HSR.sup.8 compound (e.g., H.sub.2 S when R.sup.8 is hydrogen) as a by-product, and the reaction of an ethylenicailly unsaturated carboxyamide of formula XIII liberates the corresponding HNR.sup.8 pound (e.g., ammonia when R.sup.8 and R.sup.9 are each hydrogen) as by-product.

The reaction time to form an amido-amine material vary widely depending on a wide variety of factors. For example, there is a relationship between time and temperature. In general, lower temperature demands longer times. Usually, reaction times of from about 2 to 30 hours, such as 5 to 25 hours, and preferably 3 to 10 hours be employed. Although one can employ a solvent, the reaction can be run without the use cf any solvent. In fact, where a high degree of cross-linking is desired, it is preferably to avoid the use of solvent and most particularly to avoid a polar solvent such as water. However, taking into consideration the effect of solvent on the reaction, where desired, any suitable solvent can be employed, whether organic or inorganic, pearl or non-polar.

As an example of the amido-amine adducts, the reaction of tetraethylene pentamine TEPA) with methyl methacrylate can be illustrated as follows: ##STR18##

The Mannich Base condensate dispersants of this invention are prepared by condensing at least one of the above described alkylated hydroxyaromative compounds with an amine in the presence of an aldehyde. The reactants are contacted for a time and under conditions sufficient to form the desired dispersant product.

The process employed in the condensation reaction can be any of those disclosed in U.S. Pat. Nos. 3,634,515; 3,649,229; 3,442,808; 3,798,165; 3,798,247; and 3,539,633, the disclosures of which are hereby incorporated by reference in their entirety.

The amount of the reactants employed is not critical and can vary over a wide range. It is, however, preferred to react the alkylated hydroxy aromatic compound, adehyde reactant and amine compound in the respective molar ratios of about 1:1-4:0.1-10. An excess of aldehyde reactant may be used. The reactions are exothermic, but it is desirable to heat the reaction to a temperature of above about 150.degree. C., preferably in the range of form about 150.degree.200.degree. C. This additional heating drives the reaction to completion and removes water from the resultant condensation reaction product.

The condensation reaction can be illustrated by the following reactions employing an amido-amine and formaldehyde: ##STR19## wherein "a" is an integer of 1 or 2, "Link" is the moiety --(C.sub.2 H.sub.5 NH).sub.z C(O)C.sub.2 H.sub.5 (NHC.sub.2 H.sub.5).sub.z --, "z" is an integer of from 1 to 10, and "Poly" is a polymer as described above, and ##STR20## wherein "z", "Link" and "Poly" are as defined above.

A preferred group of Mannich Bate ashless dispersants are those formed by condensing polyisobutylene-substituted phenol with formaldehyde and an amido-amine formed by reaction of a lower alkyl ester of acrylic or methacrylic acid with polyethelene amines, e.g., tetraethylene pentamine, pentaethelene hexamine, polyoxyethylene and polyoxypropylene amines, e.g., polyoxypropylene diamine, and combinations thereof. One particularly preferred dispersant comprises a condensation of (A) polyisobutylene-substituted phenol, (B) formaldehyde, an amido-amine formed by reaction of a lower alkyl ester of acrylic or methacrylic acid with (C) a polyoxyalkylene polyamine, e.g., polyoxypropylene diamine, and (D) a polyalkylene polyamine, e.g. polyethylene diamine and tetraethylene pentamine, using about 2 to about 8 moles each of (B) and about 1 to about 4 mole of (C) or (D) per mole of (A).

Another aspect of this invention involves the post treatment of the nitrogen containing dispersant materials. The process for post-treating said nitrogen containing dispersant materials is analogous to the post-treating processes used with respect to derivatives of conventional ethylene copolymers of the prior art Accordingly, the same reaction conditions, ratio of reactants and the like can be used.

The nitrogen-containing dispersant materials of the instant invention as described above are post-treated by contacting said nitrogen-containing dispersant materials with one or more post-treating reagent selected from the group consisting of boron oxide, boron oxide hydrate, boron halides, boron acids, esters of boron acids, carbon disulfide, sulfur, sulfur chlorides, alkenyl cyanides, aldehydes, ketones, urea, thio-urea, guanidine, dicyanodiamide, hydrocarbyl phosphates, hydrocarbyl phosphites, hydrocarbyl thiophosphates, hydrocarbyl thiophosphites, phosphorus sulfides, phosphorus oxides, phosphoric acid, hydrocarbyl thiocyalates, hydrocarbyl isocyanates, hydrocarbyl isothiocyntes, epoxides, episulfides, formaldehyde or formaldehyde-producing compounds plus phenols, and sulfur plus phenols, and C.sub.1 to C.sub.30 hydrocarbyl substituted succinic acids and anhydrides (e.g., succinic anhydride, dodecyl succinic anhydride and the like), fumaric acid, itaconic acid, maleic acid, maleic anhydride, chloromaleic acid, chloromaleic anhydride, acrylic acid, methacrylic acid, crotonic acid, cinnamic acid, and lower alkyl (e.g., C.sub.1 to C.sub.4 alkyl) acid esters of the foregoing, e.g., methyl maleate, ethyl fumarate, methyl fumarate, and the like.

For example, the nitrogen containing dispersants can be treated with a boron compound selected from the class consisting of boron oxide, boron halides, boron acids and esters of boron acids in an amount to provide from about 0.1 atomic proportion of boron for each mole of said nitrogen composition to about 20 atomic proportions of boron for each atomic proportion of nitrogen of said nitrogen composition. Usefully the borned dispersants of the invention contain from about 0.05 to 2.0 wt. %, e.g. 0.05 to 0.7 wt. % boron based on the total weight of said borated nitrogen-containing dispersant compound. The boron, which appears to be in the product as dehydrated boric acid polymers (primarily (HBO.sub.2).sub.3), is believed to attach to the dispersant as amine salts, e.g., the metaborate salt of said amine dispersants.

Treating is readily carried but by adding from about 0.05 to 4, e.g. 1 to 3 wt. % (based on the weight of said nitrogen compound) of said boron compound, preferably boric acid which is most usually added is a slurry to said nitrogen compound and heating with stirring at from about 135.degree. C. to 190.degree. e.g. 140.degree.-170.degree. C., for from 1 to 5 hours followed by nitrogen stripping at said temperature ranges.

Since post-treating processes involving the use of these post-treating reagents is known insofar as application to high molecular weight nitrogen containing dispersants of the prior art, further descriptions of these processes herein is unnecessary. In order to apply the prior art processes to the compositions of this invention, all that is necessary is that reaction conditions, ratio of reactants, and the like as described in the prior art, be applied to the novel compositions of this invention. The following U.S. patents are expressly incorporated herein by reference for their disclosure of post-treating processes and post-treating reagents applicable to the compositions of this invention: U.S. Pat. Nos. 3,087,936; 3,200,107; 3,254,025; 3,256,185; 3,278,550; 3,211,428; 3,282,955; 3,284,410; 3,338,832, 3,344,069; 3,356,569; 3,373,111; 3,367,943; 3,403,102; 3,428,561; 3,502,677; 3,513,093; 3,533,945; 3,541,012; 3,639,242; 3,708,522; 3,859,318; 3,865,813; 3,470,098; 3,369,021; 3,184,411; 3,185,645; 3,245,908; 3,245,909; 3,245,910; 3,573,205; 3,692,681; 3,749,695; 3,865,740; 3,954,639; 3,458,530; 3,390,086; 3,367,943; 3,185,704, 3,551,466; 3,415,750; 3,312,619; 3,280,034; 3,718,663; 3,652,616; UK Pat. No. 1,085,903; UK Pat. No. 1,162,436; U.S. Pat. No. 3,558,743.

The nitrogen containing dispersant materials of this invention can also be treated with polymerizable lactones (such as epsilon-caprolactone) to form dispersant adducts having the moiety --[C(O)(CH.sub.2).sub.z O].sub.m H, wherein z is a number of from 4 to 8 (e.g., 5 to 7) and m has an average value of from about 0 to 100 (e.g., 0.2 to 20). The dispersants of this invention can be post-treated with a C.sub.5 to C.sub.9 (e.g., C.sub.5 to C.sub.9) lactone, e.g., epsilon-caprolactone, by heating a mixture of the dispersant material and lactone in a reaction vessel in the absence of a solvent at a temperature of about 50.degree. C. to about 200.degree. C., more preferably from about 75.degree. C. to about 7180.degree. C., and most preferably from about 90.degree. C. to about 160.degree. C., for a sufficient period of time to effect reaction. Optionally, a solvent for the lactone, dispersant material and/or the resulting adduct may be employed to control viscosity and/or the reaction rates.

In one preferred embodiment, the C.sub.5 to C.sub.9 lactone, e.g., epsilon-caprolactone, is reacted with a dispersant material in a 1:1 mole ratio of lactone to dispersant material. In practice, the ratio of lactone to dispersant material may vary considerably as a means of controlling the length of the sequence of the lactone units in the adduct. For example, the mole ratio of the lactone to the dispersant material may vary from about 10:1 to about 0.1:1, more preferably from about 5:1 to about 0.2:1, and most preferably from about 2:1 to about 0.4:1. It is preferable to maintain the average degree of polymerization of the lactone monomer below about 10), with a degree of polymerization on the order of from about 0.2 to about 50 being preferred, and from about 0.2 to about 20 being more preferred. For optimum dispersant performance, sequences of from about 1 to about 5 lactone units in a row are preferred.

Catalysts useful in the promotion of the lactone-dispersant material reactions are selected from the group consisting of stannous octanoate, stannous hexanoate, tetrabutyl titanate, a variety of organic based acid catalysts and amine catalysts, as described on page 266, and forward, in a book chapter authorad by R. D. Lundberg and E. F. Cox, entitled "Kinetics and Mechanisms of Polymerization: Ring Opening Polymerization", edited by Frisch and Reegen, published by Marcel Dekker in 1969, wherein stannous octanoate is an especially preferred catalyst. The catalyst is added to the reaction mixture at a concentration level of about 50 to about 10,000 parts per weight of catalyst per one million parts of the total reaction mixture.

Exemplary of adducts formed by reaction of dispersant materials if this invention and epsilon caprolactone are those adducts illustrated by the following equation: ##STR21## wherein m, "Poly" and "Link" are as defined above. The reactions of such lactones with dispersant materials containing nitrogen or ester groups is more completely described in copending applications Ser. Nos. 916,108; 916,217; 916,218; 916,287; 916,303; 916,113; and 916,114, all filed on Oct. 7, 1986; and co-pending Ser. No. 178,099 filed on Apr. 6, 1988; the disclosure of each of which is hereby incorporated by reference in its entirety.

Further aspects of the present invention reside in the formation of metal complexes of the novel dispersant additives prepared in accordance with this invention. Suitable metal complexes may be formed in accordance with known techniques of employing a reactive metal ion species during or after the formation of the present dispersant materials. Complex forming metal reactants include the metal nitrates, thiocyanates, halides, carboxylates, phosphates, thio-phosphates, sulfates, and borates of transition metals such as iron, cobalt, nickel, copper, chromium, manganese, molybdenum, tungsten, ruthenium, palladium, platinum, cadmium, lead, silver, mercury, antimony and the like. Prior art disclosures of these complexing reactions may be also found in U.S. Pat. Nos. 3,306,908 and Re. 26,433, the disclosures of which are hereby incorporated by reference in their entirety.

The processes of these incorporated patents, as applied to the compositions of this invention, and the post-treated compositions thus produced constitute a further aspect of this invention.

The dispersants of the present invention can be incorporated into a lubricating oil in any convenient way. Thus, these mixtures can be added directly to the oil by dispersing or dissolving the same in the oil at the desired level of concentrations of the dispersant and detergent, respectively. Such blending into the additional lube oil can occur at room temperature or elevated temperatures. Alternatively, the dispersants can be blended with a suitable oil-soluble solvent and base boil to form a concentrate, and then blending the concentrative with a lubricating oil basestock to obtain the final formulation. Such dispersant concentrates will typically contain (on an active ingredient (A.I.) basis) from about 20 to about 60 wt. %, and preferably from about 40 to about 50 wt. %, dispersant additive, and typically from about 40 to 80 wt. %, preferably from about 40 to 60 wt. %, base oil, based on the contrite weight. The lubricating oil basestock for the dispersant typically is adapted to perform a selected function by the incorporation of additional additives therein to form lubricating oil compositions (i.e., formulations).

The lubricating oil basestock for the dispersant typically is adapted to perform a selected function by the incorporation of additional additives therein to form lubricating oil compositions (i.e., formulations).

The additive mixtures of the present invention possess very good dispersant properties as measured herein in a wide variety of environments. Accordingly, the additive mixtures are used by incorporation and dissolution into an oleaginous material such as fuels and lubricating oils. When the additive mixtures of this invention are used in normally liquid petroleum fuels such as middle distillates boiling from about 65.degree. to 430.degree. C., including kerosene, diesel fuels, home heating fuel oil, jet fuels, etc., a concentration of the additives in the fuel in the range of typically from about 0.001 to about 0.5, and preferably 0.005 to about 0.15 weight percent, based on the total weight of the composition, will usually be employed. The properties of such fuels are well known as illustrated, for example, by ASTM Specifications D #396-73 (Fuel Oils) and D #439-73 (Gasolines) available from the American Society for Testing Materials ("ASTM"), 1916 Race Street, Philadelphia, PA 19103.

The additive mixtures of the present invention find their primary utility in lubricating oil compositions which employ a base oil in which the additives re dissolved or dispersed. Such base oils may be natural or synthetic. Base oils suitable for use in preparing the lubricating oil compositions of the present invention include those conventionally employed as crankcase lubricating oils for spark-ignited and compression-ignited internal combustion engines, such as automobile and truck engines, marine and mixtures of the present invention in base oils conventionally employed in and/or adapted for use as power transmitting fluids, universal tractor fluids and hydraulic fluids, heavy duty hydraulic fluids, polar steering fluids and the like. Gear lubricants, industrial oils, pump oils and other lubricating oil compositions can also benefit from the incorporation therein of the additive mixtures of the present invention.

These lubricating oil formulations conventionally contain several different types of additives that will supply the characteristics that are required in the formulations. Among these types of additives are included viscosity index improvers, antioxiiants, corrosion inhibitors, detergents, dispersalts, pour point depressants, antiwear agents, friction modifiers, etc. as described in U.S. Pat. No. 4,797,219, the disclosure of which is hereby incorporated by reference in its entirety. Some of these numerous additives can provide a multiplicity of effects, e.g. a dispersant-oxidation inhibitor. This approach is well known and need not be further elaborated herein.

In the preparation of lubricating oil formulations it is common practice to introduce the additives in the form of 10 to 80 wt. %, e.g., 20 to 80 wt. % active ingredient concentrates in hydrocarbon oil, e.g. mineral lubricating oil, or other suitable solvant. Usually these concentrates may be diluted with 3 to 100, e.g., 5 to 40 parts by weight of lubricating oil, per part by weight of the additive package, in forming finished lubricants, e.g. crankcase motor oils. The purpose of concentrates, of course, is to make the handling of the various materials less difficult and awkward as well as to facilitate solution or dispersion in the final blend. Thus, a dispersant would be usually employed in the form of a 40 to 50 wt. % concentrate, for example, in a lubricating oil fraction.

The ashless dispersants of the present invention will be generally used in admixture with a lube oil basestock, comprising an oil of lubricating viscosity, including natural and synthetic lubricating oils and mixtures thereof.

Natural oils include animal oils and vegetable oils (e.g., castor, lard oil) liquid petroleum oils and hydrorefined, solvent-treated or acid-treated mineral lubricating oils of the paraffinic, naphthenic and mixed paraffinic-naphthenic types. Oils of lubricating viscosity derived from coal or shale are also useful base oils.

Alkylene oxide polymers and interpolymers and derivatives thereof where the terminal hydroxy groups have been modified by esterification, etherification, etc., constitute another class of known syrthetic lubricating oils. These are exemplified by polyooyalkylene polymers prepared by polymerization of ethylene oxide or propylene oxide, the alkyl and aryl ethers of these polyoxyalkylene polymers (e.g., methyl-poly isopropylene glycol ether having an average molecular weight of 1000, diphenyl ether of poly-ethylene glycol having a molecular weight of 500-1000, diethyl ether of polypropylere glycol having a molecular weight of 1000-1500) ; and mono- and polycarboxylic esters thereof, for example, the acetic acid esters, mixed C.sub.3 -C.sub.8 fatty acid esters and C.sub.13 Oxo acid diester of tetraethylene glycol.

Another suitable class of syrthetic lubricating oils comprises the esters of dicarboxylic acids (e.g., phthalic acid, succinic acid, alkyl succinic acids and alkenyl succinic acids, maleic acid, azelaic acid, suberic acid, sebasic acid, fumaric acid, adicic acid, linoleic acid dimer, malonic acid, alkylmalonic acids, alkenyl malonic acids) with a variety of alcohols (e.g., butyl alcohol, hexyl alcohol, dodeoyl alcohol, 2-ethylhexyl alcohol, ethylene glycol, diethylene glycol monoether, propylene glycol). Specific examples of these esters include dibutyl adipate, d.i(2-ethyehexyl)sebacate, di-n-hexyl fumarate, dioctyl sebacate, diisooctyl azelate, diisodecyl azelate, dioctyl pythalate, iidecyl phthalate, dieicosyl sebacate, the 2-ethylhexyl diester of linoleic acLd dimer, and the complex ester formed by reacting one mole of sebacic acid with two moles of tytraethylene glycol and two moles of 2-ethylhexanoic acid.

Esters useful as synthetic oils also include those made from C.sub.5 to C.sub.12 monocarboxylic acids and polyols and polyol ethers such as neopentyl glycol, trimethylolpropane, pentaerythritol, dipentaerythritol and tripentaerythritol.

Silicon-based oils such as the polyalkyl-, polyaryl-, polyalkoxy-, or polyaryloxysiloxane oils and silicate oils comprise another useful class of synthetic lubricants; they include the traethyl silicate, tetraisopropyl silicate, tetra-(2-ethylhexyl)silicate, tetra-(4-methyl-2-ethylhexyl)silicata, tetra-(p-tertbutylphenyl)silicate, hexa-(4-methyl-2-pentoxy)disiloxane, poly(methyl)siloxanes and poly(methy]phenyl)siloxanes. Other synthetic lubricating oils include liquid esters of phosphorus-containing acids (e.g., tricresyl phosphate, trioctyl phosphate, diethyl ester of deeylphosphonic acid) and polymeric tetrahydrofurans.

Unrefined, refined and rerefined oils can be used in the lubricants of the present invention. Unrefined oils are those obtained directly from a natural or synthetic source without further purification treatment. For example, a shale oil obtained directly from retorting operations, a petroleum oil obtained directly from distillation or ester oil obtained directly from an esterification process and used without further treatment would be an unrefined oil. Refined oils are similar to the unrefined oils except they have been further treated in one or more purification steps to improve one or more properties. Many such purification techniques, such as distillation, solvent extraction, acid or base extraction, filtration and percolation are known to those skilled in the art. Rerefined oils are obtained by processes similar to those used to obtain refined oils applied to refined oils which have been already used in service. Such rerefined oils are also known as reclaimed or reprocessed oils and often are additionally processess by techniques for removal of spent additives and oil breaked in products.

Compositions when containing these conventional additives are typically blended into the base oil in amounts effective to provide their normal attendant function. Representative effective amounts of such additives (as the respective active ingredients) in the fully formulated oil are illustrated as follows:

When other additives are employed, it may be desirable, although not necessary, to prepare additive concentrates comprising concentrated solutions or dispersions of the novel dispersants of this invention (in concentrate amounts hereinabove described), together with one or more of said other additives (said concentrate when constituting an additive mixture being referred to herein as an additive-package) whereby several additives can be added simultaneously to the base oil to form the lubricating oil composition. Dissolution of the additive concentrate into the lubricating oil may be facilitated by solvents and by mixing accompanied with mild heating, but this is not essential. The concentrate or additive-package will typically be formulated to contain the additives in proper amounts to provide the desired concentration in the final formulation when the additive-package is combined with a predetermined amount of base lubricant. Thus, the dispersants of the present invention can be added to small amounts of base oil or other compatible solvents along with other desirable additives to form additive-packages containing active ingredients in collective amounts of typically from about 2.5 to about 90%, and preferably from about 15 to about 75%, and most preferably from about 25 to about 60% by weight additives in the appropriate proportions with the remainder being base oil.

The final formulations may employ typically about 10 wt. % of the additive-package with the remainder being base oil.

All of said weight percents expressed herein (unless otherwise indicated) are based on active ingredient (A.I.) content of the additive, and/or upon the total weight of any additive-package, or formulation which will be the sum of the A.I. weight of each additive plus the weight of total oil or diluent.

This invention will be further understood by reference to the following examples, wherein all parts are parts by weight, unless otherwise noted and which include preferred embodiments of the invention.

A series of amido-.amines are prepared as follows: Amido-amine I is prepared by reacting TEPA with methyl acrylate at a 2:1 TEAP:methyl methacrylate molar ratio, to form a product mixture having 30.1 wt.% total N, 8.2 wt.% primary N, and containing about 50 wt.% unreacted TEFA. Amido-amine II is prepared similarly, except that a 1.5:1 TEPA:methyl acrylate molar ratio is employed, to form a product mixture containing 28.3 wt.% total N, 6.1 wt.% primary N, and about 25 wt.% unreacted THPA.

About 50 g. of polyisobutylene (2225 M.sub.n ; M.sub.w /M.sub.n =2.5) is dissolved in 100 ml of chlorobenzene and added to a solution containing 10.45 g. of phenol in 300 ml of chlorcbenzene. While stirring at room temperature under a nitrogen blanket, 0.5 g. of BF.sub.3 gas was bubbled into the charged solution and the reaction mixture was stirred while the temperature was increased to 50.degree. C. for about hour. The reaction mixture is then nautralized with gaseous ammonia until a neutral pH was obtained. The solution is filtered and the filtrate is heated to 150.degree. C. to distill of the solvent and excess phenol. Analytical results showed 70% conversion to the desired polyisobutylene-substituted phenol.

25 Grams of the alkylated phenol prepared as in Example 2 is dissolved in 25 g. of S15(N lubricating oil. To the solution is added 0.61 g. of amieo-amine I and 0.35 g. of formaldehyde at 30.degree. C. under N.sub.2. The mixture is heated to 115.degree. C. and kept at that temperature for 1 hour in a four necked round bottomed 500 mol flask. Then, the reaction mixture's temperature is raised to 130.degree. C. while the reaction vessel was swept with dry, N.sub.2 gas for 45 minutes. The stripped reaction mixture has then cooled to room temperature, diluted with 100 ml. of heptane, and filtered. The filtrate was then stripped at 130.degree. C. with dry N.sub.2 gas to remove heptane.

The procedure of Example 2 is repeated except the amido amine I is replaced with 0.61 g. of amido-amine II. The mixture of amido amide II, formaldehyde and polyisobutylene-substituted phenol is heated to 115.degree. C. and ket at that temperature for 1 hour in a four necked round bottomed 500mol flask. Then, the reaction mixture's temperature was raised to 130.degree. C. while the reaction vessel was swept with dry N.sub.2 gas for 45 minutes. The stripped reaction mixture was then cooled to room temperature, diluted with 100 ml. of heptane, and filtered. The filtrate was then stripped at 130.degree. C. with dry N.sub.2 gas to remove heptane.

The principles, preferred embodiments, and modes of operation of the present invention have been described in the foregoing specification. The invention which is intended to be protected herein, however, is not to be construed as limited to the particular forms disclosed, since these are to be regarded as illustrative rather than restrictive. Variations and changes may, be made by those skilled in the art without departing from the spirit of the invention.