US 5,075,358 AGrant
Multiple Purpose Patching Composition
Issue Date:1991-12-24
•3 Claims
Abstract
A latex modified mortar or concrete material in which a polymeric or latex binding material is combined with a low shrinkage (gypsum) cement and fine fillers. Use of the low shrinkage cement and a higher than previously considered functional ratio of latex binding material to low shrinkage cement permits the resulting patching composition to obtain unexpectedly good adhesion, reduced cracking tendencies, dimensional stability, and flexibility required while maintaining enhanced strength properties. The polymeric binding material may be either an elastomeric or a thermoplastic latex.
Metadata
Inventors
- Victor Riley
- Krishnamurthy Muralidharan
Application Information
Application Number:US 4646266
Filing Date:1990-01-03
Priority Date:1988-03-14
Art Unit:118
Classifications
IPC:
C08L 908C08L 1302
Field of Search:
10652490;689;778;8022;4;5;6;7;8
Patent Drawings
This patent does not have any drawings.
Description
Detailed Description of a Preferred Embodiment
In accordance with the present invention the elastomeric latexes are natural rubber, styrene butadiene, polyacrylonitrile butadiene, and polychloroprene. The preferred thermoplastic latexes are polyvinyl acetate, polystyrene, polyvinylchloride, polyacrylates, or their copolymers. The preferred expansive cement is gypsum.
A typical conventional latex modified mortar, which is representative of those known and used previously would include the ingredients set forth in the Table A below in the indicated parts by weight ratios:
In the Table A above DOW 460 Latex is a styrene butadiene latex and is available from Dow Chemical Company of Midland, MI. Antifoam B is an anti-foam agent available from Dow Corning Corporation. The weight of the latex comprises less than 40% of the weight of the cement.
In the following Table B, column A represents a preferred improved latex modified mortar, column B represents an alternative improved latex modified mortar, and column C represents a patching composition primarily formulated for wood or metal articles.
Duracal cement is a gypsum cement available from United State Gypsum Corporation of Chicago, IL. Duramite is a calcium carbonate filler available from White Pigment Corporation of Florence, VT. Veroc #1 is a calcium limestone filler, also produced by White Pigment Corporation of Florence, VT. E-330 Latex is an acrylic latex available from Rohm and Haas Chemical Company of Philadelphia, PA. Surfanol 104H is a surfactant available from Air Product and Chemical, Inc. of Allentown, PA.
In the patching compounds of Table B, the conventional Portland cement has been replaced by low shrinkage cement (gypsum). As a result the compositions exhibit improved workability in the fresh (wet) state, quicker sets, faster drying, and less shrinkage upon drying which would normally lead to cracks. In addition, the compositions of Table B will exhibit superior properties such as greater flexibility, higher impact resistance, greater resistance to chemical attack, and greater bond with other materials. If some or all of the sand is left out (column C) and the proportion of fine filler in the composition of Table B is increased a putty will result which can be used to fill holes, or as a putty for glazing in windows.
In its broader aspects the proposed mortar composition of the present invention combines the following ingredients in the indicated ranges:
While preferred embodiments have been described in detail hereinabove, it is apparent that various changes and modifications might be made without departing from the scope of the invention which is set forth in the accompanying claims.
Claims
What is claimed is:
1. A patching composition comprising: up to about 65 wt % sand having an average particle size substantially greater in diameter than 0.05 mm; about 16 to about 46 wt % inorganic fine fillers having an average particle size substantially less in diameter than 0.15 mm, wherein the combined weight of said sand and said inorganic fine fillers is greater than 50 wt % of the total weight of said patching composition; about 5 to about 15 wt % low shrinkage cement selected from the group consisting of gypsum cements and magnesium sulfate cements; about 14 to about 39 wt % latex binder selected from the group consisting of polyvinyl acetate, polystyrene, polyvinylchloride, polyacrylates, and copolymers thereof; and up to about 2 wt % additives, selected from the group consisting of anti-foaming agents, surfactants, and retarders.
2. The patching composition, according to claim 1, wherein said low shrinkage cement is a gypsum cement.
3. The patching composition, according to claim 1, wherein said latex binder contains about 50 wt. % solids and the balance is water.