In-Line Aminosilane Coated Polyester Film for Glazing Products

The present invention relates to oriented polyester film coated in-line on one or both sides with a primer coating composition comprising a hydrolyzed aminofunctional silane which renders the film more receptive to lamination with other polymeric film materials such as polyvinylbutyral, polyolefins, polyurethanes, and other polymers, useful in glazing products.

Oriented polyester film, particularly biaxially oriented film composed of polyethylene terephthalate (PET), has been widely used as a packaging material or as a base for microfilm, reprographic films, proofing films and the like. It has good optical clarity and toughness which renders it extremely suitable for such applications.

Polyester films have recently found expanded applications as transparent and translucent layers applied to solid substrates and particularly to transparent substrates. Thus, such films may be applied to windows and viewing or lighting media to control the transparency thereof. Another more recent application for polyester film involved its use as an antilacerative layer in the construction of automotive glazing products such as windshields, rear windows, sun roof panels and the like, and in architectural safety and solar glass. One of the simpler automotive glazing products may comprise a flexible interlayer of polyvinylbutyral sandwiched between glass on one side and a high modulus film, for example polyester film, on the opposite side.

Polyvinylbutyral layers are used in sandwich automotive glass construction to prevent breaking of the glass in the case of impact (so called safety glass), whereas the role of the polyester film positioned on the interior glazing surfaces is to prevent skin lacerations caused by hard impact of the head or body with automotive glass causing the glass to shatter, as a consequence of an automobile accident. Constructions of this type and techniques for applying the polyester film to automotive glass surfaces are disclosed in U.S. copending application Ser. No. 07/299,583, filed Jan. 23, 1989, now U.S. Pat. No. 4,973,364, which is a divisional of application Ser. No. 148,818, filed Jan. 27, 1988 (commonly assigned), now abandoned, the disclosure of which is incorporated herein by reference.

The above referenced copending application teaches the use of a layer of plasticized polyvinylbutyral (PVB) as an adhesive layer to facilitate adhesion of the polyester film to the glass. While PVB adheres very well to glass, the adhesion between it and polyester film is not as great, particularly at subfreezing temperatures. Corona discharge treatment and flame treatment have been used to improve adhesion between PVB sheet and polyester film as disclosed in U.S. Pat. No. 3,900,673. Coatings of gelatin and PVDC and acrylic latex coatings have also improved adhesion between polyester film and PVB. However, none of these methods of imparting adhesion improve adhesion at the subfreezing temperatures to which windows in automobiles and buildings are commonly subjected. It is believed that any improvement of the adhesion of the polyester film to the PVB improves the function of the polyester film as an antilacerative shield.

Numerous primer coatings are known in the prior art for the application to the surface of polyester film to improve the adhesion of the film to various materials. Examples of such coatings include compositions based on vinylidene chloride polymers (U.S. Pat. No. 2,698,240), thermosetting acrylic or methacrylic polymers (U.S. Pat. No. 3,819,773) and like materials. Certain water dispersible copolyesters have also been disclosed as adhesives for laminating sheets of polyester film to one another or to sheets of nylon film, as taught in U.S. Pat. Nos. 3,563,942 and No. 3,779,993. Solvent based polyurethane adhesives have also been used to promote adhesion, but with attendant problems of solvent emissions and safety.

The use of silane coupling agents to improve the bonding properties of polyethylene sheets and polyester sheets is known. For example, polyester sheets and polyethylene sheets primed with either vinyltrimethoxy silane or chloropropyltrimethoxy silane have been successfully laminated using a hot melt adhesive such as an ethylene/vinyl acetate terpolymer or an elastomeric polyester as disclosed by E. Plueddemann, "Bonding Through Coupling Agents", Plenum Press, New York, 1985. In addition, the use of N-2-aminoethyl-3-aminopropyltrimethoxy silane (sold under the trademark Z-6020 by Dow Corning) as a primer coating to enhance the adhesion of an ionomer resin (salt of a copolymer of ethylene and methacrylic acid) to glass and to polycarbonate sheets is disclosed in U.S. Pat. No. 4,663,228. Related silanes such as N-3-aminopropyltrialkoxy silanes are known to enhance the adhesion between polyurethane films and glass substrates, as disclosed in published European Patent Application 171,917.

None of these prior art disclosures, however, addresses the problem of the maintenance of good adhesion between polyester film and polyvinylbutyral or other polymer films at subfreezing temperatures where many primer materials fail.

Accordingly, it is an object of this invention to provide an oriented, self supporting film material having enhanced adhesion when laminated with other polymer films.

A further object is to provide a primer coating for polyester film which enhances adhesion between polyester and polyvinylbutyral films and imparts resistance to delamination even at subfreezing temperatures.

These and other objects of the invention may now be achieved by the provision of an oriented polyester film which has been in-line primer-coated with a hydrolyzed aminofunctional silane.

The aminofunctional silanes useful as a primer layer for the purposes of this invention are diamino or triamino silanes responding in their unhydrolyzed state to the general formula:

wherein X is a radical selected from the group consisting of H.sub.2 NR.sup.1 HNR.sup.1 --and H.sub.2 NR.sup.1 HNR.sup.1 HNR.sup.1 --; the R.sup.1 's are the same or different groups selected from the group consisting of C.sub.1 to C.sub.8 alkyl or phenyl; R.sub.2 is a hydrolyzeable group selected from the group consisting of C.sub.1 to C.sub.8 alkoxy, an acetoxy group or a halide; R.sub.3 is a nonreactive, nonhydrolyzeable group selected from the group consisting of C.sub.1 to C.sub.3 alkyl or phenyl; (a) is an integer ranging from 1 to 3; (b) is an integer ranging from 0 to 2, with the sum of (a) and (b) being 3.

Examples of suitable silanes include N-(2-aminoethyl)-3-aminopropylmethyldimethoxysilane, N-(2-aminoethyl-3-aminopropyl) trimethoxysilane, N-2-aminoethyl-3-aminopropyltris(2-ethylhexoxy) silane, 6-(aminohexylaminopropyl)trimethoxysilane, (aminoethylaminomethyl) phenethyltrimethoxysilane and N-2-aminoethyl-2-aminoethyl-3-aminopropyltrimethoxysilane.

The more preferred silanes for the purposes of this invention are diamono primary amines having the following formula:

wherein the R.sup.1 's are the same or different alkyl radicals having from 1 to 3 carbon atoms, R.sup.2 is a C.sub.1 to C.sup.3 alkoxy group, (a) is 3 and (b) is 0.

The most preferred are silanes of the above formula wherein R.sup.1 and R.sup.2 are C.sub.1 to C.sub.3 alkyl radicals, R.sup.3 is a C.sub.1 to C.sub.3 alkoxy group, (a) is 3 and (b) is 0. The most preferred silane is N-2(aminoethyl-3-aminopropyl) trimethoxy silane having the formula:

The hydrolyzed aminosilane is applied to the film, in-line, as an aqueous solution at any suitable stage during manufacture of the film prior to heat setting the film, i.e., before, during, or after the stretching operation, so long as it is done prior to heat setting the film. The resultant primed polyester film is found to exhibit excellent adhesion to other polymeric materials and can be readily laminated to other polymeric films. Adhesive qualities are maintained even at subfreezing temperatures. Less than excellent adhesion is achieved between the polyester and PVB when the hydrolyzed aminosilane primer coating is applied after heat setting the film, e.g., applied off-line by a convertor.

The primer formulation of this invention is prepared by mixing the aminosilane with water at a level within the range of about 0.2 to about 6 percent by weight. Optionally, a weak acid such as acetic acid may be added to facilitate hydrolysis. At least one of the hydrolyzeable groups of the silane is hydrolyzed into a silanol group (SiOH).

Although the preferred exemplified film which is primer coated in accordance with the present invention is polyester film, the invention is equally applicable to other high modulus films including polyamide film and polycarbonate film. The base film used normally has a higher modulus or stiffness than the polymer or sheet to be laminated to it, and a higher melting or softening point.

The preferred oriented polyester film base for the purposes of this invention is made from polyethylene terephthalate, although the invention is equally applicable to film based on a crystallizable polyester resulting from the polycondensation of a glycol such as ethylene glycol or butane diol and mixtures thereof with terephthalic acid or mixtures of terephthalic acid and other dicarboxylic acids such as isophthalic acid, diphenic acid and sebacic acid, or their polyester forming equivalents, which polyesters are made by methods well known in the art. The film may be produced by techniques also well known in the art using well known apparatus.

For example, the polyester is melted and extruded as an amorphous sheet onto a polished revolving casting drum to form a cast sheet of the polymer. Thereafter, the film is axially stretched in one direction, either in the direction of extrusion (longitudinal), or perpendicular to the direction of extrusion (transverse) in the case of monoaxially oriented film, and in two directions in the case of biaxially oriented film, that is, the film is stretched in both the longitudinal and transverse directions. The first stretching, to impart strength and toughness to the film, can range from about 3.0 to about 5.0 times.

The hydrolyzed aminosilane primer coating of this invention in the form of an aqueous solution may be applied in-line at one of three stages during the film manufacture; the pre-draw stage at the point between the casting of the armophous sheet and the first stretch such as disclosed, for example, in British Patent No. 1,411,564; the inter-draw stage subsequent to the uniaxial drawing but prior to biaxial drawing such as disclosed, for example, in the U.S. Pat. No. 4,214,035; or the post draw stage subsequent to biaxial stretching, but prior to heat-setting the film. The primer is dried by any conventional system, such as for example, a hot air dryer, an infrared dryer, or a combination of these.

It has been discovered that application of the aqueous based aminosilane primer coating to the polyester film after manufacturing the film, or to be more precise, after the polyester film has been heat set such that the majority of the film exists in a crystalline state, does not result in a primer coated polyester film having superior adhesion characteristics suitable for adhesion with other polymers. Therefore, the aqueous based aminosilane coatings of the present invention must be applied before the polyester film has been heat set, i.e., applied in-line.

In the preferred embodiment, the primer coating is applied after the film is uniaxially stretched, that is, after the film is stretched in one direction, but before the film is stretched in the orthogonal direction. In the preferred embodiment, the polyester film is first stretched in the longitudinal direction prior to coating. In the preferred embodiment, after longitudinal stretching, the film is coated by any of the well known techniques employed in the art. For example, coating may be effected by roller coating, spray coating, slot coating or immersion coating. In the preferred embodiment, the polyester film is coated by means of a gravure cylinder. Also the uniaxially drawn film is preferably subjected to a corona discharge by a corona discharge apparatus prior to primer coating as is known in the art. The discharge treatment decreases the hydrophobic character of the polyester film surface, which permits the water based coating to more easily wet the surface and thus improve the adhesion of the primer coating to the surface of the polyester film.

The hydrolyzed aminosilane of the present invention is applied in-line to the base film as an aqueous solution at a concentration of from about 0.2 to about 6 percent by weight of the hydrolyzed aminosilane. A weak acid such as acetic, phosphoric or the like is then added at a level of from about 0.1 to about 0.5 percent by weight to facilitate hydrolysis. The preferred level of addition of the acid is about 0.2 percent by weight. The preferred concentration of the hydrolyzed aminosilane is within the range of about 0.5 to about 2.5 percent by weight. The preferred concentration is such to yield a final dry primer coating weight of from about 1.0.times.10.sup.-3 to about 4.0.times.10.sup.-2 grams per square meter of film. Preferably the range is from about 2.0.times.10.sup.-3 to about 2.0.times.10.sup.-2 grams per square meter, with about 1.0.times.10.sup.-2 grams per square meter being the target weight for coatings applied in-line.

The coating of this invention may be applied to one or both sides of the film, or it may be applied to one side and a different coating such as a thermosetting acrylic or methacrylic polymer applied to the opposite side, such as taught in U.S. Pat. No. 4,214,035. The coating may also in some cases be applied over a different primer coating to which it will adhere and which is already present on the surface of the film, such as a thermosetting acrylic coating as described in U.S. Pat. No. 3,819,773.

An especially significant application in the glass field is the utilization of polyester film coated on one side with the primer coating of this invention and on the opposite side with an abrasion resistant coating such as a radiation curable hydrolyzed vinyl-functional silane composition also containing a multifunctional crosslinking agent and an optional photoinitiator, such as disclosed in U.S. Pat. No. 4,822,828, the disclosure of which application is incorporated herein by reference. Such materials have shown to improve the abrasion resistance of the surfaces of a variety of plastic films, including polyester film making the films more useful in applications where the surface is likely to be subjected to abrasion. Examples of suitable vinyl-functional silanes disclosed in the referenced application include vinyl alkoxy silanes such as vinyltriethoxysilane, or a mixture of vinyltrimethoxysilane and vinyltris (2-methoxyethoxy) silane. Preferred crosslinkers are multi functional acrylate or methacrylate monomers such as ethoxylated trimethylolpropane triacrylate.

Other suitable abrasion resistant coatings may also be used such as are disclosed for example in U.S. Pat. Nos. 4,177,315, 4,239,798, 4,310,600 and 4,348,462.

The coating composition may also contain other ingredients so long as such ingredients do not detract from the adhesion promoting action of the hydrolyzed aminosilane. Such would include minor amounts of colloidal silica, dyes, pH regulating agents, wetting agents and the like. The primer coating is present on the film surface as a continuous coating, which term is also intended to include cases where the primer may form a plurality of islands or segregated regions of coating.

Scrap film made during production that is coated with the primer coatings of the invention can be ground and mixed with fresh polyester, re-melted and re-extruded to produce oriented film. Such film produced containing significant quantities of primed scrap reclaim, exhibits very little degradation of physical properties due to the presence of the coating impurity and color generation is also low. Thus, the primed film of this invention offers commercial advantage to the film manufacturer over many other primed films, such as films primed with vinylidene chloride containing polymers as disclosed in U.S. Pat. Nos. 2,627,088 and 2,698,240, which tend to degrade and discolor when reclaimed as set forth above.

As indicated above, the in-line primer coated film of this invention forms excellent adhesive bonds with other plastic films to which it is laminated. Examples of such films include polyvinylbutyral, polycarbonate, polyurethane, polyolefins such as polyethylene or polypropylene, polystyrene and similar films. Laminates may be made by forming a sandwich of the films and heating the structure to a temperature below the melting point of the polyester film but above the melting point of the other film, preferably while simultaneously applying moderate pressure to the sandwich structures. Preferred heating temperatures generally range from about 125.degree. C. to 225.degree. C. The other plastic films used to form the laminates may themselves be primer coated if desired.

An especially significant application in the glass field is the utilization of polyester film coated on one side with the primer coating of this invention. The primed side of the polyester film is laminated to a sheet of polyvinylbutyral that is also laminated to a sheet of glass. For this application the preferred aminosilane is N-2-(aminoethyl)-3-aminopropyltrimethoxysilane (AE-APTMS). Polyester film primed with AE-APTMS has high adhesion to polyvinylbutyral at normal temperatures and also has good adhesion to polyvinylbutyral at subfreezing temperatures where adhesion fails with other primers and treatments.

The polyester film of this invention can be sandwiched between two layers of PVB and two layers of glass with at least one side of the film primed with aminosilane and the other side either being primed with aminosilane or having a metal or metal oxide coating for solar control and IR reflection. In another configuration the polyester film is laminated to the interior or inboard surface of the glass as an anti-lacerative layer with a layer of PVB between the film and the glass; the side of the film primed with aminosilane is laminated to the glass and the other side of the film is protected by an abrasion resistant coating.

The thickness of polyester film suitable for use in this invention may generally range from about 0.25 to about 10 mils or more. In multilayer automotive windshield applications the preferred thickness is on the order of 2 to 7 mils.

The following examples are illustrative of the invention.

N-2-(aminoethyl)-3-aminopropyltrimethoxysilane (AE-APTMS) was dispersed in ordinary tap water to form a concentration of 1.0 percent by weight AE-APTMS. Acetic acid was then added at a concentration of 0.2 percent by weight to facilitate hydrolysis.

Polyethylene terephthalate polymer was melted and extruded through a slot die onto a casting drum maintained at a temperature of about 20.degree. C. The melt froze to form a cast sheet. The cast sheet was longitudinally stretched at a draw ratio of approximately 3.5 to 1 while maintained at a temperature of about 80.degree. C. The longitudinally drawn film was corona treated by a corona discharge apparatus and thereafter coated in-line by reverse gravure with the solution of hydrolyzed aminosilane prepared above. The corona treated, longitudinally drawn, coated film was dried at a temperature of about 100.degree. C. Thereafter, the film was stretched in the transverse direction at a draw ratio of 3.9 to 1 to produce biaxially drawn film. The biaxially drawn film was then heat set at a maximum temperature of 230.degree. C. The dry weight of the coating was about 0.50.times.10.sup.-6 pounds per square foot of film. The thickness of the base film was about 3 mils. The result is set forth in Table 1.

In-line primer coated films were prepared exactly as set forth in Example 1 above except that the concentration of AE-APTMS in the coating solution was 1.5 percent by weight in Example 2, 2.0 percent by weight in Example 3 and 2.5 percent by weight in Example 4. The results are set forth in Table 1.

In order to perform comparative tests, solutions of N-3-aminopropyltrimethoxysilane (APTMS) having the formula H.sub.2 N(CH.sub.2).sub.3 Si(OCH.sub.3).sub.3 were prepared by the same method as in Example 1. In-line primer coated films were prepared exactly as set forth in Example 1. The concentration of APTMS in the coating solution was 1.0 percent by weight in Example 5, 1.5 percent by weight in Example 6, 2.0 percent by weight in Example 7 and 2.5 percent by weight in Example 8. The results are set forth in Table 1.

In-line primer coated films were prepared by the same method as set forth in Example 1. For Example 9, the primer coating was an acrylic latex applied from an aqueous dispersion at a concentration of 4 percent by weight. (The acrylic coating is a copolymeric latex as described in U.S. Pat. No. 4,571,363.) For Example 10, the primer coating was an aqueous dispersion of a water dispersible copolyester applied at a concentration of 4 percent by weight. (The water dispersible copolyester coating is described in U.S. Pat. No. 4,493,872.) The result is set forth in Table 1.

Adhesion of each of the films prepared above to polyvinylbutyral was evaluated by laminating the film to a polyvinylbutyral sheet and then testing the peel strength of a one inch wide strip by doing a 180.degree. peel test in an Instron tester. A 6.times.8 inch sheet of the coated film was laminated to "Saflex TG" (sold by Monsanto Chemical Company), a PVB sheet used in automotive safety glass, and to glass by placing the side coated with aminosilane in contact with the PVB and placing the PVB in contact with the glass. A one inch wide strip of plain PET film (0.5 mil thick) was placed between the coated film and the PVB in order to provide a nonadhered leader for doing the peel test. A sheet of "Kapton" (a DuPont trademark) was placed on top of the polyester to serve as a release liner and another piece of glass was placed on top of the Kapton. This construction was sandwiched between two pieces of cardboard, which serves to distribute pressure evenly, and the assembly was placed in a hydraulic press that had been preheated to 150.degree. C. The platens of the press were closed sufficiently for contact to be made top and bottom between the platens and the cardboard and the construction was allowed to preheat for five minutes. Pressure was then increased to 150 psi, and maintained for 30 minutes. With the pressure maintained at 150 psi the platens were cooled to room temperature with circulating water. Once the platens had cooled to room temperature the laminate was removed. One inch wide strips were cut in the PET film using a scalpel.

To test the peel strength, the laminated sample, PET/PVB/glass, was placed in an Instron tester with the glass/PVB clamped in the lower jaws of the Instron and the nonadhered leader hanging free and pointing down toward the jaws A length of #610 "Scotch" tape (a 3M trademark) was doubled over and attached to the nonadhered leader. The length of Scotch tape was then clamped in the upper jaws of the Instron. The angle between the leader and PVB/glass was 180.degree.. The peel was done at a rate of 1 inch/min for a length of one inch. The peak force needed to peel the PET from the PVB was read from the strip chart. Three laminated samples were made for each example. For each 6.times.8 laminated sample three pulls were done at room temperature 23.degree. C.) and three pulls were done at -10.degree. C. Results are shown in Table 1.

As can be seen from the table, film samples primed using the AE-APTMS aminosilane of this invention exhibit a marked improvement in peel resistance in both the room temperature test and also when tested after conditioning at -10.degree. C. for 24 hours when compared with samples primed with a standard water dispersible copolyester or an acrylic latex. Film samples primed with APTMS showed adhesion at room temperature, but essentially no adhesion after the 24 hour conditioning at -10.degree. C. As shown by Examples 1-4, the diamine AE-APTMS has superior peel strengths at -10.degree. C. compared to the mono-amine APTMS.

N-2-(aminoethyl)-3-aminopropyltrimethoxysilane was coated off-line (meaning on a coating line separate from the film production line) onto finished, crystallized, biaxially oriented PET film and nip laminated to PVB. The coating was 1.5 percent Z-6020 (sold by Dow Corning) with 0.2 percent acetic acid added to promote hydrolysis. The film, running at 100 fpm, was corona treated and then coated using reverse gravure. The coating weight was 14.times.10.sup.-6 lbs/ft.sup.2. The coated film was then nip laminated to 30 mil sheet of polyvinylbutyral using a nip roll at 220.degree. F. and 400 lb/linear inch pressure. The PET/PVB laminate was laminated to glass and tested as described for Examples 1-10 with the exception that the steady state peel force was used rather than the peak force. At 23.degree. C. the peel adhesion was 12.5 lbs/inch. At -10.degree. C. the peel adhesion was 1.4 lbs/inch. This example indicates in-line primer coating produces superior results to off-line coating.

A polyester film in-line coated on one side with AE-APTMS for adhesion to polyvinylbutyral may be coated on the opposite side with a suitable anti-abrasion coating as follows:

48.0 grams of vinyltiimethoxysilane are added dropwise at room temperature to 72 grams of Nalco 1034A, a commercially available acidic colloidal silica, with gentle stirring using a magnetic stirrer. The mixture was stirred for 4 hours at room temperature in a closed container and was then heated to 60.degree. C. in a closed container and was then heated to 60.degree. C. in a water bath for 30 minutes while still being stirred.

4.8 grams of SARTOMER C-9035, a water-soluble, highly ethoxylated trimethylolpropane triacrylate commercially available from ARCO Specialty Chemicals, was mixed with 4.0 grams of isopropanol, 0.9 grams of IRGACURE 500, a photoinitiator commercially available from Ciba-Geigy, and 0.2 grams of a fluorinated surfactant commercially available from 3M under the trademark Fluorad. The resulting mixture was added to 12 grams of the silica/vinyltrimethoxysilane condensate to form the radiation curable coating composition.

The coating composition is applied, using a #18 Meyer rod, to a 4 mil thick, acrylic-primed side of polyester film, which was primed on the other side with AE-APTMS aminosilane in accordance with Example 1 of this invention. The coating is first dried in an oven maintained at 75.degree. C. for one minute and then crosslinked by UV irradiation by passing the coated polyester film four times through a RPC Equipment Co. Model QC 1202 processor at 25 feet/minute using two 200 watt/inch lamps. The above coating was found to significantly improve the abrasion resistance of the coated side of the film surface rendering the film more useful in automotive windshield applications.

PET film was prepared and coated in-line with 1.5 percent AE-APTMS hydrolyzed in deionized water as described in Example 1 with the exception that the film was 3 mils thick. The dry coating weight was 0.0065 g/m.sup.2.

A 6-inch.times.6-inch sheet of coated PET film was laminated to 30 mil polyvinylbutyral sheet, Saflex TG, and to glass with the AE-APTMS in contact with the PVB sheet. The film, sheet, and glass sandwich was deaired using a nip roll and then the structure was laminated together in an air autoclave at 150 psi and 150.degree. C.

The peel adhesion between the PVB and PET was tested on an Instron. The PET film layer was cut into one inch wide strips. A strip of Scotch tape was attached to a nonadhered leader and the Scotch tape was then clamped in the upper jaws of the Instron. The glass plate with the PVB layer was clamped in the lower jaw of the Instron such that there was a 180.degree. angle between the glass plate and the nonadhered leader held by the upper jaws of the Instron. The test sample was cooled to 0.degree. F. and held at that temperature in a controlled temperature test chamber during the test. The peel was done at one inch/min for a length of one inch and the steady state force needed to peel the PET from the PVB was read from the strip chart. The results are shown in Table 2.

PET film was prepared in Example 1 with exception that 3.0 percent AE-APTMS hydrolyzed in deionized water was used instead of 1.5 percent. The dry coating weight was 0.013 g/m.sup.2. The film was laminated to PVB and the PET/PVB adhesion tested as described in Example 13. The results are shown in Table 2.

PET film was prepared as in Example 1 with exception that the dry coating weight was 0.0086 g/m.sup.2 using a 1.5 percent AE-APTMS aqueous solution. The film was laminated to PVB and the PET/PVB adhesion tested as described in Example 13. The results are shown in Table 2.

PET film was prepared as in Example 1 with exception that the dry coating weight was 0.017 g/m.sup.2 using 3.0 percent AE-APTMS. The film was laminated to PVB and the PET/PVB adhesion tested as described in Example 13. The results are shown in Table 2.

PET film was prepared as described in Example 1 except it was coated off-line in a separate process step on the ER-WE-PA coater/laminator. The film thickness was 4 mils, the line speed was 20 fpm, the dryer temperature was set at 290.degree. F. and the corona treater at 3 kW. The gravure cylinder was 150 quad. Film samples were laminated to PVB and the PET/PVB adhesion tested as described in Example 13. The results are shown in Table 2.

PET film was prepared, coated, laminated, and tested as described in Example 17 with the exception that the concentration of AE-APTMS was 0.5 percent. The results are shown in Table 2.

PET film was prepared, coated, laminated, and tested as described in Example 17 with the exception that the concentration of AE-APTMS was 2.0 percent. The results are shown in Table 2.

PET film was prepared, coated, laminated, and tested as described in Example 17 with the exception that the concentration of AE-APTMS was 5.0 percent. The results are shown in Table 2.

Clearly there is superior low temperature adhesion to polyvinylbutyral for PET coated in-line with an aminosilane hydrolyzed in water versus coating the PET off-line with the hydrolyzed aminosilane.

Previously, only a diamine was tested as the aminofunctional silane for primer coating. In this example a triamine was tested.

PET film was prepared and primer coated in-line as in Example 13, with the exception that the aminosilane employed was N-2-aminoethyl-2-aminoethyl-3-aminopropyltrimethoxysilane (AE-AE-APTMS). The concentration of the triamine in deionized water was 1.5 percent and 3.0 percent by weight with a dry coating weight of 0.0058 g/m.sup.2 and 0.010 g/m.sup.2 respectively. Samples of the film were laminated to glass and PVB and the adhesion was measured as set forth in Example 13. The results are set forth in Table 3.

These results demonstrate that triamines produce similar superior results as diamines.

Thus, it is apparent that there has been provided, in accordance with the invention, a film and laminate structure that fully satisfies the objects, aims, and advantages set forth above. While the invention has been described in conjunction with specific embodiments thereof, it is evident that many alternatives, modifications, and variations will be apparent to those skilled in the art in light of the foregoing description. Accordingly, it is intended to embrace all such alternatives, modifications, and variations as fall within the spirit and broad scope of it.