Method for Printing

The invention will now be further described with reference to the following examples:

A white screen printing ink was formulated by passing through a triple roll mill a mixture of an enamel and a medium in a weight of 3.1:1. The enamel was a 1:1 mixture (w/w) of two enamels sold by Blythe Colours Ltd, UK under Nos. 43T40 and 43T47 whereas the UV-curable medium is available from Blythe Colours B.V., the Netherlands under the reference number 267/63. The resulting ink had a viscosity of 3000 mPa.s at 21.degree. C. and was applied automatically by screen printing on a "Kammann" 6 color machine (nylon or polyester, mesh size 90T) at a thickness of 20 to 40 .mu.m to articles of glass holloware. The articles were printed at a rate of 40 per minute and then passed under medium pressure mercury vapor lamps giving a power of 80 Watts.cm.sup.-1.

A direct screening "wet" liquid gold was formulated as a thick paste according to procedures known in the art and comprised gold- and silverorgano-sulphur compounds, elements all known in the art as being desirable for brightness and adhesion of the fired precious metal film such as vanadium, rhodium and silicon in organic form (e.g. as resinates), binders and resinous materials, such as modified rosins and natural occurring hydrocarbons, essential oils and solvents. This gel formulation is available from Blythe Colors B.V., the Netherlands under the reference number GBV 9337. The liquid gold printing ink was screen printed onto the articles using the same Kammann 6-color machine (nylon or polyester mesh size 110T) at a thickness of 15 to 30 .mu.m and at the same speed of 40 articles per minute. The articles were then fired at a peak temperature of 580.degree. C. and with a cycle time of 120 minutes. The resulting white layer had a gold layer deposited thereon which was of good quality and free of defects.

Glass articles that had been printed with a film of cured radiation-polymerizable ink as in Example I were overprinted on the film with a direct screening thermoplastic liquid gold printing ink. The gold preparation was basically prepared with the same organometallic compounds as referred to in Example I, according to the procedures known in the art. However solvents and some of the resins were replaced by waxy materials of both natural and synthetic origin, as known in the art, thus giving the preparation the appropriate thermoplastic characteristics. This gel ink is available from Blythe Colours B.V., the Netherlands, under the reference number GBV 358T. The direct screening printing ink was printed at about 55.degree.-60 .degree. C. using the Kammann 6-color machine (metal mesh size 110T) at a speed of 40 articles per minute to give a coating thickness of 20-40 .mu.m. During printing the thermoplastic ink had the consistency of a thick paste and hardened rapidly after printing so that it could, if desired, itself be over-printed at subsequent stations of the printing machine. After printing the articles were fired as in Example I.

The procedure of Example I or II was followed except that the bright gold preparation employed was the non-gel wax liquid gold available from Blythe Colours B.V., the Netherlands, under reference number GBV 137.

The fired article had a blistered film and the gold had diffused into the underlying layer producing a mauve rather than a gold color.