Mesomorphic Compound, Ferroelectric Liquid Crystal Composition Containing Same and Ferroelectric Liquid Crystal Device

The present invention relates to a mesomorphic compound having an oxidiazole or thiadiazole ring, a ferroelectric liquid crystal composition containing the mesomorphic compound and a ferroelectric liquid crystal device using the composition.

Clark and Lagerwall proposed a ferroelectric liquid crystal display system, called an SSFLC (Surface Stabilized Ferroelectric Liquid Crystal) System in 1980. The SSFLC system is principally characterized in release of a helical structure (having a pitch of 1 .sub.0) owned by a ferroelectric liquid crystal (hereinafter sometimes abbreviated as "FLC") by utilizing the boundary effect of a pair of substrate surfaces, more specifically through the following features.

(1) The spacing (cell gap) between the pair of substrates is set to a sufficiently small value to release the above-mentioned helical structure.

(2) The liquid crystal molecules are set to align in parallel with the boundaries with the substrates, whereby the smectic layers of FLC are disposed perpendicularly to the substrates.

(3) Further, the direction of the alignment of liquid crystal molecules in contact with at least one of the substrates is regulated, whereby the direction of the smectic layers is uniformized over the entire cell area.

When the alignment state formed through such stepwise molecular control is viewed macroscopically, stable longer-axis directions (director n) of ferroelectric liquid crystal molecules are restricted to two directions. In an FLC display, the fact that the two directions (average directions of n) are discriminatable by means of a polarizer is utilized for display.

The basic mechanism of switching between the above-mentioned two stable directions is based on the utilization of a ferroelectricity which FLC shows in its smectic C* phase. FLC has a molecular dipole moment (u) in a plane parallel to the smectic layer and is present between the cell substrates in such a form that it is disposed continuously while changing the direction of the dipole moment (u) to some extent to provide an average spontaneous polarization (Ps) in a direction from the lower substrate to the upper substrate or in the reverse direction. Each of the directions (upward and downward) of the spontaneous polarization (Ps) corresponds to either one of the above-mentioned molecular longer axes (n), so that switching by electric fields becomes possible.

More specifically, when an electric field is applied to the FLC layer from outside, the dipole moments (n) in the layer are all uniformly oriented (U1) in the direction of the electric field, and when the electric field is removed, the dipole moments are settled at a state (S1) after some relaxation time (on the order of 1 .mu.s-2 ms varying depending on an FLC used). U1 is a uniform state having a higher degree of order and optically a better uniaxial characteristic than S1, and S2 is a twisted state where the dipoles of FLC are somewhat twisted to provide a lower uniaxial characteristic than U1 but the directions of the spontaneous polarizations are uniform. Similarly, when the polarity of the external electric field is reversed, there are formed states U2 and S2. As a result, it is possible to select U1 or U2 (and thus S1 or S2) by the polarity of the electric field applied. This is referred to as bistability.

In addition to the above-described characteristic of showing bistability, the ferroelectric liquid crystal has an excellent property, i.e., a high-speed responsiveness. This is because the spontaneous polarization of the ferroelectric liquid crystal and an applied electric field directly interact with each other to induce transition of orientation states. The resultant response speed is faster than the response speed due to the interaction between dielectric anisotropy and an electric field by 3 to 4 digits.

Thus, a ferroelectric liquid crystal potentially has very excellent characteristics, and by making use of these properties, it is possible to provide essential improvements to many of the above-mentioned problems with the conventional TN-type devices. Particularly, the application to a high-speed optical shutter and a display of a high density and a large picture is expected. For this reason, there has been made extensive research with respect to liquid crystal materials showing ferroelectricity. However, ferroelectric liquid crystal materials developed heretofore cannot be said to satisfy sufficient characteristics required for a liquid crystal device including low-temperature operation characteristic, high-speed responsiveness, etc.

Among a response time .tau., the magnitude of spontaneous polarization Ps and viscosity .eta., the following relationship exists: .tau.=.eta./(Ps.E), where E is an applied voltage. Accordingly, a large response speed can be obtained by (a) increasing the spontaneous polarization, (b) lowering the viscosity .tau., or (c) increasing the applied voltage. However, the driving voltage has a certain upper limit in view of driving with IC, etc., and should desirably be as low as possible. Accordingly, it is actually necessary to lower the viscosity or increase the spontaneous polarization.

A ferroelectric chiral smectic liquid crystal having a large spontaneous polarization generally provides a large internal electric field in a cell given by the spontaneous polarization and is liable to pose many constraints on the device construction giving bistability. Further, an excessively large spontaneous polarization is liable to accompany an increase in viscosity, so that a remarkable increase in response speed may not be attained as a result.

Further, if it is assumed that the operation temperature of an actual display device is 5-40.degree. C., the response speed changes by a factor of about 20, so that it actually exceeds the range controllable by driving voltage and frequency.

As described hereinabove, commercialization of a ferroelectric liquid crystal device requires a ferroelectric chiral smectic liquid crystal composition having a low viscosity, a high-speed responsiveness and a small temperature-dependence of response speed.

In a representative FLC cell structure, a pair of substrates are disposed, each substrate of e.g. glass being provided with an electrode pattern of e.g. ITO, further thereon with a layer of e.g. SiO.sub.2 (about 1000 .ANG.) for preventing short circuit between the pair of substrates and further thereon with a film of e.g. polyimide (PI; such as SP-510, 710, . . . available from Toray K.K.) of about 500 .ANG. in thickness, which is then treated for alignment control by rubbing with e.g. an acetate fiber-planted cloth. Such a pair of substrates are disposed opposite to each other so that their alignment control directions are symmetrical and the spacing between the substrates is held at 1-3 microns.

On the other hand, it is known that the FLC molecules aligned under such conditions are disposed in succession so that their directors n are twisted between the substrates and do not show a uniaxial alignment or orientation (S1, S2 mentioned above). A problem in this case is a low transmittance through the liquid crystal layer.

The optical selection between the two stable states is effected by disposing a pair of polarizers in cross nicols between which the above cell is interposed, and when the absorption axis of the polarizers is disposed in alignment with the average molecular axis of either one of S1 and S2, e.g. S1, the resultant transmittance becomes extremely low to display "black". Then, when the molecular position is switched to the S2 state, the molecular position is deviated from the absorption axis of the polarizers by 2.theta.a which is an angle between S1 and S2, so that transmission of light is caused to display "white".

The transmitted light intensity I is given by the following equation with respect to the incident light intensity I.sub.0 under cross nicols when the uniaxial alignment of the molecules is assumed:

wherein .DELTA.n denotes the refractive index anisotropy of the FLC; d, the cell thickness; and .lambda., the wavelength of the incident light.

When the above-mentioned cell is used, it has been experimentally known that .theta.a is 5-8 degrees under a twisted alignment condition and is little affected by a liquid crystal material used.

The control of physical properties affecting the term .DELTA.nd.pi./.lambda. cannot be easily performed, so that it is desired to increase .theta.a to increase Ia. However, this has not been successfully accomplished by only a static alignment technique.

With respect to such a problem, it has been proposed to utilize a torque relating to a dielectric anisotropy .DELTA..epsilon. of an FLC (1983 SID report from AT & T; Japanese Laid-Open Patent Appln. Nos. 245142/1986, 246722/1986, 246723/1986, 246724/1986, 249024/1986 and 249025/1986). More specifically, an effective value of AC electric field is applied in a period other than switching so that the molecular stable states are shifted from S1 and S2 under the electric field due to the generation of a dielectric polarization (AC stabilization effect). A torque .GAMMA.Ps acting on FLC molecules involved in switching of states and a torque .GAMMA..DELTA..epsilon. acting on FLC molecules relating to the AC stabilization effect are respectively proportional to physical properties as shown in the following formulas:

The above formula (3) apparently shows that the sign and absolute value of .DELTA..epsilon. of the FLC play an important role.

The sole figure attached hereto shows the change of .theta.a versus Vrms experimentally measured for for 4 FLC's having different values of .DELTA..epsilon.. The measurement was conducted under application of AC rectangular pulses of 60 KHz so as to remove the influence of Ps. The curves (I)-(IV) correspond to the results obtained by using FLCs showing the following .DELTA..epsilon. values. ##STR5## Qualitatively, the order of .DELTA..epsilon. was (I)<(II)<(III)<(IV).

As is clear from the graph in the figure, a larger negative value of .DELTA..epsilon. provides a large .theta.a at a lower voltage and thus contributes to provision of an increased I.

The transmittances obtained by using the liquid crystals (I) and (III) were 15 % for (I) and 6 % for (III), thus showing a clear difference.

As is known from the above examples, the display characteristics of an SSFLC can be remarkably changed by controlling the properties relating to .DELTA..epsilon. and Ps (.eta.).

However, most of ferroelectric liquid crystal compositions used heretofore have a .DELTA..epsilon. of nearly 0, so that an improvement in display characteristics through the above-mentioned AC stabilization effect can hardly be expected.

An object in general of the present invention is to solve the above-mentioned problems to provide a practical ferroelectric liquid crystal device.

A specific object of the present invention is to provide a liquid crystal composition and a liquid crystal device using the composition showing excellent response characteristics through utilization of a novel mesomorphic compound.

Another specific object of the present invention is to provide a liquid crystal composition and a liquid crystal device using the composition having remarkably improved display characteristics through utilization of a novel mesomorphic compound providing an AC stabilization effect.

According to the present invention, there is provided a mesomorphic compound represented by the following formula (I): ##STR6## wherein A.sub.1 denotes a single bond, ##STR7## denotes ##STR8## X denotes hydrogen, a halogen or cyano group; Y denotes oxygen or sulfur; R.sub.1 and R.sub.2 respectively denotes a linear or branched alkyl, alkoxy, alkylcarbonyloxy, alkoxycarbonyl or alkoxycarbonyloxy group each having 1-18 carbon atoms and each capable of having a substituted of chloro, bromo, cyano, alkoxy or alkoxycarbonyl group; and B denotes ##STR9##

The present invention further provides a ferroelectric liquid crystal composition comprising at least two mesomorphic compounds, at least one of which is represented by the above formula (I), and a ferroelectric liquid crystal device comprising such a ferroelectric liquid crystal composition disposed between a pair of substrates.

The mesomorphic compound of the above formula (I) is characterized by having a unique .pi.-electron-structure having hetero-atoms in its cyclic skeleton and an increased dielectric anisotropy in the direction of its shorter axis. According to our study, it has been found that a ferroelectic liquid crystal composition obtained by mixing such a mesomorphic compound with at least one other mesomorphic compound, particularly ferroelectric mesomorphic compound, or a ferroelectric liquid crystal device using such a ferroelectric liquid crystal composition, shows excellent response characteristics and also an AC stabilization effect to be provided with good display characteristics.

The sole figure in the drawing shows changes in tilt angle .theta.a versus effective voltage Vrms with respect to several ferroelectric liquid crystals having different values of dielectric anisotropy .DELTA..epsilon..

(A) Among the mesomorphic compounds represented by the above general formula (I), those corresponding to the case of B being ##STR10## may be synthesized through the following reaction steps; Formula (I) ##STR11##

Alternatively, the following reaction steps may be applicable. ##STR12##

(B) The mesomorphic compounds corresponding to the case of B being ##STR13## may be synthesized through the following reaction steps. ##STR14##

(C) The mesomorphic compounds corresponding to the case of B being --CH.sub.2 O may be synthesized through the following reaction steps. ##STR15##

Specific examples of the mesomorphic compounds represented by the formula (I) are shown below. ##STR16##

The liquid crystal composition of the present invention comprises at least two mesomorphic compound, at least one of which is represented by the formula (I) as described above. More specifically, the liquid crystal composition according to the present invention comprises, in addition to the mesomorphic compound represented by the above formula (I), another compound, particularly mesomorphic compound, selected from the classes of compounds as described below in order to control various properties of the composition, such as spontaneous polarization, helical pitch, phase transition series and related phase temperature ranges, response characteristics, tilt angle, and dielectric anisotropy.

In this instance, it is desirable that the mesomorphic compound represented by the formula (I) is used to constitute 0.5-60 wt. %, preferably 5-40 wt. %, of the resultant liquid crystal composition.

Class A: Optically active compounds yielding a helix when added to a non-chiral nematic phase. ##STR17##

Class B: Mesomorphic compounds having non-chiral smectic phase and (or) nematic phase. ##STR18##

Hereinbelow the present invention will be explained in further detail based on Examples which should however be not construed to restrict the scope of the present invention.

In the following examples, the values of .DELTA..epsilon. (dielectric anisotropy) were obtained in the following measurement.

A 5 micron-thick homogeneous alignment cell having an electrode of 0.7 m.sup.2 in area and a homogeneous alignment layer (rubbed polyimide) on both substrates, and a 5 micron-thick homeotropic alignment cell having an electrode of 0.7 cm.sup.2 in area and a homeotropic alignment layer (aligning agent: "ODS-E" available from Chisso K.K.) on both substrates, were provided. The respective cells were filled with a sample liquid crystal material (compound or composition) to prepare liquid crystal devices. The capacitances of the liquid crystal layers were measured by applying a sine wave with a frequency of 100 kHz and amplitudes of .+-.0.5 V to the respective devices at a prescribed temperature set for the liquid crystal material, and the dielectric constants .epsilon..parallel. and .epsilon..perp. were obtained from the measured capacitance values of the respective devices, whereby the dielectric anisotropy .DELTA..epsilon. was calculated by the equation of .DELTA..epsilon.=.epsilon..parallel.-.epsilon..perp..

Synthesis of 2-n-decyl-5-[4-(trans-4'-n-pentylcyclohexylcarbonyloxy)phenyl]-1,3,4-oxadi azole (Example compound A-3).

Into a mixture solution of 1.5 g (4.97.times.10.sup.-3 mol) of 2-n-decyl-5-[4-hydroxyphenyl]-1,3,4-oxadiazole, 2.5 ml of dry pyridine and 2.5 ml of dry toluene, a solution of 1.08 g (4.97.times.10.sup.-3 mol) of trans-4-n-pentylcyclohexanecarbonyl chloride in 2.5 ml of dry toluene was added dropwise below 5.degree. C. in 20 minutes, followed by stirring for 27 hours at room temperature. After the reaction, the reaction liquid was poured into 50 ml of iced water and acidified to pH 1 with 6N-HCl, followed by extraction with benzene, washing with water, dehydration and distilling-off of the solvent (benzene) to obtain a crude product. The crude product was purified by silica gel column chromatography with the use of an n-hexane/ethyl acetate=5/1 mixture solvent and recrystallized from ethanol to obtain 1.92 g of 2-n-decyl-5-[4-(trans-4'-n-pentylcyclohexylcarbonyloxy)-phenyl]-1,3,4-oxad iazole. (Yield: 80.1 %)

Cryst.: crystal

S: smectic

Iso.: isotropic phase

.DELTA..epsilon.:-2.8 (at 110.degree. C., 100 kHz)

Three dielectric mesomorphic compounds represented by the formula [I]were synthesized in the same manner as in Example 1 except that the 2-n-decyl-5-[4-hydroxyphenyl]-1,3,4-oxadiazole used in Example 1 was reacted with different acid chlorides as follows.

Acid chloride: trans-4-n-propylcyclohexanecarbonyl chloride.

Product: 2-n-decyl-5-[4-(trans-4'-n-propylcyclohexylcarbonyloxy)-phenyl]-1,3,4-oxad iazole (Example compound A-2).

S.sub.1, S.sub.2 smectic phase (un-identified)

N: nematic phase.

Acid chloride: p-n-decylbenzoic acid chloride.

Product: 2-n-decyl-5-[4-(4'-n-decylbenzoyloxy)phenyl]-1,3,4-oxadiazole. (Example compound A-12).

Acid chloride: 3-fluoro-4-n-octyloxybenzoic acid chloride.

Product: 2-n-decyl-5-[4-(3-fluoro-4'-n-octyloxybenzoyloxy)-phenyl]-1,3,4-oxadiazole (Example compound A-15).

2-n-octyl-5-[4-hydroxyphenyl]-1,3,4-oxadiazole and trans-4-n-propylcyclohexanecarbonyl chloride were reacted in a similar manner as in Example 1 to obtain 2-n-octyl-5-[4-(trans-4'-n-propylcyclohexylcarbonyloxy)-phenyl]-1,3,4-oxad iazole. (Yield: 85 %)

Synthesis of 2-n-decyl-5-[4-(trans-4'-n-propylcyclohexylmethyleneoxy)-phenyl]-1,3,4-oxa diazole (Example compound No. A-22).

1.5 g (4.97.times.10.sup.-3 mol) of 2-n-decyl-5-[4- hydroxyphenyl]-1,3,4-oxadiazole was dissolved in 20 ml of dimethylformamide, followed by addition of 0.75 g of 85% potassium hydroxide and 1 hour of stirring at 100.degree. C. To the reaction mixture was added 1.54 g 4.97.times.10.sup.-3 mol) of trans-4-n-propylcyclohexylmethyl-p-toluenesulfonate, and the mixture was further stirred for 4 hours at 100.degree. C. After the reaction, the reaction mixture was poured into 200 ml of iced water, followed by extraction with benzene, washing with water, dehydration and distilling off of the solvent to obtain a crude product, which was purified by silica gel column chromatography and recrystallized from ethanol to obtain 0.94 g of 2-n-decyl-5-[4-(trans-4'-n-propylcyclohexylmethyleneoxy)-phenyl]-1,3,4-oxa diazole. (Yield: 43.2 %).

A liquid crystal composition A was prepared by mixing a ferroelectric mesomorphic compound example (9) selected from the above-mentioned Class A and a mesomorphic compound example A-2 represented by the formula (I) in a weight ratio of 4:1. The above ferroelectric mesomorphic compound (9) and the liquid crystal composition A were respectively sandwiched between a pair of electrode plates each having a rubbing-treated polyimide coating film and disposed with a gap of 2 microns from each other to prepare two liquid crystal devices. These liquid crystal devices were respectively subjected to measurement of a response time by detecting an optical response under right angle cross nicols when subjected application of an electric field with a peak-to-peak voltage of 20 V. The results are shown below:

The above results show that the addition of a mesomorphic compound according to the invention [Example A-2] to a ferroelectric mesomorphic compound [Example (9)] provided an improved responsiveness.

A liquid crystal composition B was prepared by mixing ferroelectric mesomorphic compound examples (1) and (38) selected from the class A in a ratio of 4:1.

Then, the liquid crystal composition B and a mesomorphic compound example A-23 represented by the formula (I) were mixed in a ratio of 9:1 to prepare a liquid crystal composition C.

The liquid crystal compositions B and C were used in the same manner as in Example 7 to prepare liquid crystal devices, which were then subjected to measurement of a response time in the same manner as in Example 7 except that the application voltage was changed to 30 V. The results are shown below.

The above results show that the addition of the mesomorphic compound example A-23 according to the invention to the liquid crystal composition B provided an improved responsiveness.

A liquid crystal composition D was prepared by mixing the liquid crystal composition B used in Example 7, a non-chiral smectic mesomorphic compound example 10 selected from the class B, and mesomorphic compound examples A-3 and A-12 represented by the formula (I) in ratios of B: 10:A-3:A-12=14:4:1:1.

A liquid crystal device was prepared by using the above liquid crystal composition D otherwise in quite the same manner as in Example 7 and subjected to measurement of a response time under the same conditions as in Example 7. The results are shown below together with those obtained by using the liquid crystal composition B.

The above results show that the combined addition of the mesomorphic compound examples A-3 and A-12 according to the invention and the non-chiral smectic mesomorphic compound 10 to the liquid crystal composition B provided a further improved responsiveness.

A commercially available ferroelectric liquid crystal ("CS-1014" available from Chisso K.K.) having a .DELTA..epsilon. of nearly 0 (.DELTA..epsilon..noteq.-0.4 (sin wave, 100 kHz)) and a mesomorphic compound example A-22 represented by the formula (I) of the invention were mixed in a ratio of 92:8 to prepare a liquid crystal composition E.

Liquid crystal devices were prepared in the same manner as in Example 7 except that the above liquid crystal CS1014 and the liquid crystal composition E were used respectively and the liquid crystal layer thicknesses were changed to 1.5 microns.

The above liquid crystal devices were subjected to measurement of a tilt angle under right angle cross nicols at 25.degree. C. to provide 7 degrees for CS1014 and 7.2 degrees for the liquid crystal composition E. Then, the devices were subjected to application of a .+-.8 V rectangular waveform at a frequency of 60 kHz, and the tilt angles were measured under the voltage application and microscopic observation to provide 8.8 degrees for CS1014 and 11.4 degrees for the liquid crystal composition E. Under these conditions, the transmittances were measured to be 7.8% for CS1014 and 11 % for the composition E. Further, the contrast ratios were measured to be 8:1 for CS1014 and 30:1 for the composition E.

The above results show the addition of the mesomorphic compound example A-22 represented by the formula (I) of the present invention to a liquid crystal CS1014 having a of nearly 0 provided a liquid crystal device showing improved display characteristics.

Synthesis of 2-n-decyl-5-[4-(trans-4'-n-propylcyclohexylcarbonyloxy)phenyl]-1,3,4-thiad iazole (Example compound B-20).

Into a mixture solution of 1.2 g (3.77.times.10.sup.-3 mol) of 2-n-decyl-5-[4-hydroxyphenyl]-1,3,4-thiadiazole, 2.5 ml of dry pyridine and 2.5 ml of dry toluene, a solution of 0.71 g (3.77.times.10.sup.-3 mol) of trans-4-n-propylcyclohexanecarbonyl chloride in 2.5 ml of dry toluene was added dropwise below 5.degree. C. in 15 minutes, followed by stirring for 19 hours at room temperature. After the reaction, the reaction liquid was poured into 50 ml of iced water and acidified to pH 1 with 6N-HCl, followed by extraction with benzene, washing with water dehydration and distilling-off of the solvent (benzene) to obtain a crude product. The crude product was purified by silica gel column chromatography with the use of an n-hexane/ethyl acetate=3/1 mixture solvent and recrystallized from ethanol to obtain 1.15 g of 2-n-decyl-5-[4-(trans-4'-n-propylcyclohexylcarbonyloxy)-phenyl]-1,3,4-thia diazole. (Yield: 64.9%)

S.sub.1 -S.sub.4 : smectic phase (un-identified)

S.sub.A : smectic A phase, S.sub.C : smectic C phase.

IR (cm.sup.-1)

2925, 2850, 1740, 1600, 1510, 1470, 1450,

1205, 1165, 1130, 980, 862

.DELTA..epsilon.: -3.3 (at 100.degree. C., 100 kHz).

2-n-decyl-5-[4-(trans-4'-n-pentylcyclohexylcarbonyloxy)-phenyl]-1,3,4-thiad iazole (Example compound B-34) was prepared in the same manner as in Example 11 except that trans-4-n-pentylcyclohexanecarbonyl chloride was used instead of trans-4-n-propylcyclohexanecarbonyl chloride. Yield: 60.2 % .

IR (cm.sup.-1)

2860, 2825, 1750, 1600, 1508, 1470, 1450,

1205, 1162, 1135, 980, 860

Synthesis of 2-n-decyl-5-[4-(trans-4'-n-propylcyclohexylmethyleneoxy)-phenyl]-1,3,4-thi adiazole (Example compound N. B-3).

1.0 g (3.28.times.10.sup.-3 mol) of 2-n-decyl-5-[4-hydroxyphenyl]-1,3,4-thiadiazole was dissolved in 20 ml of dimethylformamide, followed by addition of 0.5 g of 85 % potassium hydroxide and 1 hour of stirring at 100.degree. C. To the reaction mixture was added 1.02 g (3.28.times.10.sup.-3 mol) of trans-4-n-propylcyclohexylmethyl-p-toluenesulfonate, and the mixture was further stirred for 4 hours at 100.degree. C. After the reaction, the reaction mixture was poured into 200 ml of iced water, followed by extraction with benzene, washing with water, dehydration and distilling off of the solvent to obtain a crude product, which was purified by silica gel column chromatography and recrystallized from ethanol to obtain 0.8 g of 2-n-decyl-5-[4-(trans-4'-n-propylcyclohexylmethyleneoxy)-phenyl]-1,3,4-thi adiazole. (Yield: 53.3 %).

2945, 2860, 1608, 1580, 1520, 1480, 1460,

1320, 1260, 1180, 1125, 1040, 985, 858

Synthesis of 2-(1-methylpropyl)-5-[4-(trans-4- n-pentylcyclohexylcarbonyloxy)phenyl]-1,3,4-thiadiazole (Example compound B-51).

Into a mixture of 0.3 g (1.28.times.10.sup.-3 mol) of 1-methylpropyl-5-[4-hydroxyphenyl]-1,3,4-thiadiazole, 0.26 g (1.31.times.10.sup.-3 mol) of trans-4-n-pentylcyclohexanecarboxylic acid, 0.27 g (1.31.times.10.sup.-3 mol) of dicyclohexylcarbodiimide and 0.03 g of 4-(1-pyrrolidinyl)pyrimidine, 15 ml of methylene chloride was added, followed by 20 hours of stirring at room temperature. After the reaction, the reaction was filtered and the solid was washed with methylene chloride. The filtrate and the washing liquid were dehydrated, and the solvent was distilled off therefrom to obtain a crude product, which was then recrystallized twice to obtain 0.24 g of 2-(1-methylpropyl)-5-[4-(trans-4-n-pentylcyclohexylcarbonyloxy)-phenyl]-1, 3,4-thiadiazole. (Yield: 45.2%).

A liquid crystal composition F was prepared by mixing a ferroelectric mesomorphic compound example (9) selected from the above-mentioned Class A and a mesomorphic compound example B-7 represented by the formula (I) in a ratio of 4:1. The above ferroelectric mesomorphic compound (9) and the liquid crystal composition F were respectively sandwiched between a pair of electrode plates each having a rubbing-treated polyimide coating film and disposed with a gap of 2 microns from each other to prepare two liquid crystal devices in the same manner as in Example 7. These liquid crystal devices were respectively subjected to measurement of a response time by detecting an optical response under right angle cross nicols when subjected application of an electric field with a peak-to-peak voltage of 20 V. The results are shown below:

The above results show that the addition of a mesomorphic compound according to the invention [Example B-7] to a ferroelectric mesomorphic compound [Example (9)] provided an improved responsiveness.

A liquid crystal composition B was prepared by mixing ferroelectric mesomorphic compound examples (1) and (38) selected from the class A in a ratio of 4:1.

Then, the liquid crystal composition B and a mesomorphic compound example B-2 represented by the formula (I) were mixed in a ratio of 9:1 to prepare a liquid crystal composition G.

The liquid crystal compositions B and G were used in the same manner as in Example 15 to prepare liquid crystal devices, which were then subjected to measurement of a response time in the same manner as in Example 15 except that the application voltage was changed to 30 V. The results are shown below.

The above results show that the addition of the mesomorphic compound example B-2 according to the invention to the liquid crystal composition B provided an improved responsiveness.

A liquid crystal composition H was prepared by mixing the liquid crystal composition B used in Example 16, a non-chiral smectic mesomorphic compound example 10 selected from the class B, and mesomorphic compound examples B-3 and B-34 represented by the formula (I) in ratios of B: 10:B-3:B-34 =14:4:1:1.

A liquid crystal device was prepared by using the above liquid crystal composition H otherwise in quite the same manner as in Example 15 and subjected to measurement of a response time under the same conditions as in Example 15. The results are shown below together with those obtained by using the liquid crystal composition B.

The above results show that the combined addition of the mesomorphic compound examples B-3 and B-34 according to the invention and the non-chiral smectic mesomorphic compound 10 to the liquid crystal composition B provided a further improved responsiveness.

A commercially available ferroelectric liquid crystal ("CS-1014" available from Chisso K.K.) having a .DELTA..epsilon. of nearly 0 (.DELTA..epsilon..perspectiveto.-0.4 (sine wave, 100 kHz)) and a mesomorphic compound example B-20 represented by the formula (I) of the invention were mixed in a ratio of 9:1 to prepare a liquid crystal composition I.

Liquid crystal devices were prepared in the same manner as in Example 15 except that the above liquid crystal CS1014 and the liquid crystal composition I were used respectively and the liquid crystal layer thicknesses were changed to 1.5 microns.

The above liquid crystal devices were subjected to measurement of a tilt angle under right angle cross nicols at 25.degree. C. to provide 7 degrees for CS1014 and 8.2 degrees for the liquid crystal composition I. Then, the devices were subjected application of a .+-.8 V rectangular waveform at a frequency of 60 kHz, and the tilt angles were measured under the voltage application and microscopic observation to provide 8.8 degrees for CS1014 and 14.2 degrees for the liquid crystal composition I. Under these conditions, the transmittances were measured to be 7.8 % for CS1014 and 13 % for the composition E. Further, the contrast ratios were measured to be 8:1 for CS1014 and 40:1 for the composition E.

The above results show the addition of the mesomorphic compound example B-20 represented by the formula (I) of the present invention to a liquid crystal CS 1014 having a .DELTA..epsilon. of nearly 0 provided a liquid crystal device showing improved display characteristics.

A liquid crystal composition J was prepared by mixing optically active compound examples (8), (13), (17), (18), (20), (33), (34), (36) and (38) selected from the above-mentioned Class A, and non-chiral smectic or nematic mesomorphic compound examples 1, 5, 6, 7 and 9 selected from the above-mentioned Class B in ratio of (8):(13):(17):(18):(20):(33):(34): (36):(38):1:5:6:E,crc/7/ :9:=10:9:10:10:5:6:3:5:5: 5:6:6:12:8.

Then, a liquid crystal composition K was prepared by mixing the above-prepared composition J and mesomorphic compound examples A-2, A-6, A-17, A-23, A-26, B-3, B-21 and B-33 represented by the formula (I) of the present invention in ratios of the composition J:A-2:A-6:A-17:A-23:A-26:B-3:B-21:B-33 80:3:2:3:3:2: 2:2:3.

The liquid crystal compositions J and K were used in the same manner as in Example 7 to prepare liquid crystal devices, which were then subjected to measurement of a response time in the same manner as in Example 7 except that the application voltage was changed to 30 V (peak-to-peak). The results are shown below.

Then, the above liquid crystal devices were subjected to measurement of tilt angles in the same manner as in Example 10 (under application of rectangular AC waveform of .+-.8 V and 60 kHz) to provide tilt angles of 8.3 degrees for the composition J and 13.8 degrees for the composition K.

The above results show that the addition of mesomorphic compounds according to the present invention to the liquid crystal composition J provided improvements in temperature-dependence of response speed as well as in display characteristics due to AC stabilization effect.

A liquid crystal composition L was prepared by mixing the composition J used in Example 19 and mesomorphic compound examples A-10, A-20, A-25, A-31, A-32, B-2, B-17, B-34, B-41 and B-43 represented by the formula (I) of the invention in ratios of the composition J:A-10:A-20:A-25:A-31:A-32:B-2:B-17:B-34: B-41:B-43 =80:2:2:2:1:1:3:2:5:1:1.

A liquid crystal device was prepared by using the above composition L otherwise in quite the same manner as in Example 19 and subjected to measurement of response time and tilt angle under the same conditions as in Example 19, whereby the following results were obtained.

Title angle: 14.3 degrees

The above results again show that the addition of mesomorphic compounds according to the present invention provides improvements in temperature-dependence of response speed and display characteristics due to AC stabilization effect.

As is understood from the results of the above examples, the liquid crystal composition and the liquid crystal device according to the present invention using the mesomorphic compound represented by the formula (I) show good responsiveness and remarkably improved display characteristic when applied to a display method utilizing the AC stabilization effect.