Fire Protectants

In the following, the subject of the invention is illustrated by examples. The parts and percentages given relate to weight, unless stated otherwise.

100 parts of an ethylene/vinyl acetate copolymer having a vinyl acetate content of 45% (Lewapren.RTM.450Bayer AG) were mixed with 170 parts of aluminium hydroxide (Apyral.RTM.B2 from Bayer AG, particle size range 15 to 25 .mu.m) and separately with 170 parts each of the following minerals on an unheated roller: calcium carbonate, dolomite, gypsum, sawdust, barite, carbon black, kaolin, ground shale, marl, iron oxide, talc, fly ash, wolastonite, zinc oxide, borocalcite and colemanite.

A 5 mm thick sheet was produced in each case. Strips of size 10.times.1 cm were cut from this sheet. These were placed in a muffle furnace and heated there from room temperature to 950.degree. C. with the admission of air and left at 950.degree. C. for 30 minutes. The sheets were then cooled.

After cooling, only the strips containing borocalcite and colemanite had formed a ceramic-like ignition residue approximately true to the shape and solidified by sintering processes. The other strips which contained calcium carbonate, dolomite, gypsum, sawdust, barite, carbon black, kaolin, ground shale, marl, iron oxide, talc, fly ash, wolastonite and zinc oxide were decomposed or had yielded a mechanically instable, pulverulent ignition residue.

This means that in the case of joint-sealing or cable-coating by means of a composition corresponding to one of these strips only the calcium borate/aluminium hydroxide combination shows sufficient protection against attack by flames.

A copolymer of ethylene and 35% ethyl acrylate was mixed with a 1.5-fold amount of diphenyl cresyl phosphate. 400 parts of a mixture of 40 parts of pandermite and 60 parts of aluminium hydroxide produced by joint grinding in a ball mill were worked into 100 parts of this mixture in a kneading apparatus. A viscous mastic material was obtained. A strand of 1 cm width and height and 10 cm length produced from this mastic material was heated at 1,000.degree. C. for 1 hour in a muffle furnace. A ceramic, porous, mechanically stable likeness of the original strand remained.

100 parts of an ethylene/vinyl acetate copolymer having an ester content of 35% was kneaded with 150 parts of trioctyl phosphate and 900 parts of a mixture of 60% hydroboracite, 40% aluminium hydroxide and 3 parts of pyrogenic silicic acid. A mastic material marketable in a cartridge was obtained. A strand of this mastic material suitable for joint connection was heated at 950.degree. C. in a muffle oven for 30 minutes with admission of air. After cooling, the formerly flexible strand was present as a solid sintered substance.

1,000 parts of a type of polyisobutylene having a viscosity at 75.degree. C. of 9,500 cP were kneaded with 20 parts of pyrogenic silicic acid and 1,500 parts each of aluminium hydroxide and colemanite. A strand was formed from the mastic obtained and this was heated to 1,000.degree. C. for 30 minutes with admission of air. A sintered substance in the form of the original strand remained.

In the following examples, a type of colemanite was used which contains 9% calcium carbonate as an impurity.

100 parts of a 50% strength latex of an ethylene/vinyl acetate copolymer having 50% vinyl acetate content were kneaded with one part of carboxymethylcellulose, 10 parts of trioctyl phosphate, 20 parts of hollow aluminosilicate beads (mean particle size 250 .mu.m), 120 parts of aluminium hydroxide, 150 parts of colemanite, one part of pyrogenic silicic acid and one part of calcium silicate whiskers. The joint connection paste thus produced was marketable in a cartridge. A strand of this paste gave a solid sintered substance after drying and tempering at 1,000.degree. C. This paste or its dilutions with water are well suited for coating or impregnating foamed plastics against the effects of fire.

100 parts of aluminium hydroxide, 140 parts of colemanite and 1.4 parts of pyrogenic silicic acid were jointly ground for 24 hours in a ball mill. This mixture was stirred with a mixture of equal parts of 15% strength silica sol and 10% strength sodium silicate to give a spreadable dispersion. Using this dispersion, a mineral wool sheet (bulk density 350 kg/m.sup.3, thickness 4 cm) was coated with a 5 mm thick layer on both sides. After drying, a piece of this sheet, standing on the cut surface so that the coated surface remained free, was heated in a muffle furnace at 1,000.degree. C. After 25 minutes, the sheet was taken out and cooled.

A sealed, solid sintered layer had formed on both sides of the sheet.

In a fire resistance test (small fire chamber) according to DIN 4102, a fire resistance time of more than 120 minutes was measured with such sheets. The same sheet having an equally thick coating of cement only achieved a fire resistance time of less than 100 minutes.

A mixture of 50 parts of aluminium hydroxide and 50 parts of colemanite were ground for 14 hours in a ball mill, subsequently mixed with 20 parts of a commercial aromatic polyisocyanate (Desmodur.RTM.44 V 10 from Bayer AG) and 1 ml of water and then compressed to a 6 mm thick sheet for 15 minutes at 300 bar and 130.degree. C. in a sheet press. After cooling under pressure, a stable sheet was obtained which can be employed for flame-protectant purposes. A strip cut from this sheet was heated for 30 minutes in a muffle furnace at 1,000.degree. C., by means of which a solid, ceramic-like sintered substance was formed.

The procedure of Example 7 was used, but the ground material was well mixed with 50 parts of glass fibre cuttings (mean length 9 mm) before compressing. The plate formed on tempering had properties as described in Example 7.

The procedure of Example 7 was used, but 30 parts of ammonium polyphosphate were added during grinding. After tempering, the sheet had properties as described in Example 7.

1,000 parts of a cold-hardening epoxide resin mixture (Lekuthern.RTM.X 20 and hardener T 6 from Bayer AG) were admixed at 15.degree. C. immediately after the preparation of 3,000 parts of a mixture of equal parts of aluminium hydroxide and colemanite. A solid tube having an internal diameter of 3 cm and a wall thickness of 7 mm was produced from the mixture by compressing in a mould and hardening at 20.degree.-25.degree. C. This tube was heated from room temperature to 980.degree. C. in a muffle furnace with admission of air and tempered for one hour at 980.degree. C. After cooling, a solid sintered substance was obtained from the material while maintaining the shape of the tube. These types of tube can then be used for the fire protection of cables.

The procedure of Example 10 was used, but the reaction mixture from a polyurethane pouring material (Baygal.RTM. and Baymidur.RTM. from Bayer AG) was employed instead of the epoxide resin mixture. The protected tube obtained gave a comparably stable sintered substance on tempering according to Example 10.

100 parts of the copolymer as used in Example 1 were kneaded with 350 parts of a mixture of 55% colemanite and 45% aluminium hydroxide. A 3 mm thick sheet was produced from this material on a roller mill. This sheet was provided on both sides with an adhesive paper width by rolling out at 80.degree. C. 10 cm wide and 2 m long strips were cut from the paper-lined material and wrapped as binding on an electric cable. On flaming of the cable thus protected using a natural gas burner achieving a temperature of about 1,100.degree. C., a certain expansion of the material of the protective binding began with concomitant carbonizing and subsequent ceramicization after burning off the external paper layer. The cable was effectively protected against attack by flames. With two-layered bindings, no short-circuit was established after 120 minutes of flaming.

The contents of a commercial cartridge containing moisture-hardening silicone mastic were mixed with 10 times its volume of dried methylene chloride and filtered clear through a pressure filter. The methylene chloride was removed by distillation from the solution obtained. 100 parts of the remaining silicone resin material were kneaded with 130 parts of aluminium hydroxide, 170 parts of colemanite and 2.5 parts of pyrogenic silicic acid (all dried at 110.degree. C.) to again give a paste marketable in a cartridge having good surface adhesion.

A strip of 1 cm diameter was squeezed out from this paste and allowed to stand in the atmosphere, by means of which the hardening customary for silicone pastes of this type occurred. After 30 days, a 10 cm long piece of this hardened elastic strand was heated from room temperature to 1,000.degree. C. in a muffle furnace and tempered for 30 minutes at 1,000.degree. C. A mechanically hard, corresponding sintered piece was obtained.

By repeating the treatment in the muffle furnace, but this time with the original silicone mastic material, a mechanically non-loadable, crumbly material was obtained as an ignition residue.

100 parts of the polymer also used in Example 1 were kneaded in each case with 300 parts of calcium carbonate, 300 parts of gypsum, 300 parts of barite, 300 parts of aluminium hydroxide and a mixture of 150 parts of aluminium hydroxide and 150 parts of colemanite. 0.5 cm thick sheets were drawn from the kneaded mixtures, using an unheated roller mill as when mixing the solid constituents into the polymer.

1 cm wide test strips were cut from the sheets. These were placed on a 1.5 mm thick iron sheet in such a way that the strips projected 1 cm over the edge of the sheet. A Bunsen burner was then brought under the sheet at the site where the test strips overhung the sheet, and sheet and test strips were equally subjected to the blue inner cone of the Bunsen flame (about 1,100.degree. C.).

After 1 minute of flaming, the Bunsen burner was removed. It showed that all test strips were again burnt, except for those which contained aluminium hydroxide and the aluminium hydroxide/colemanite mixture. These two last-mentioned strips were extinguished. Of these two strips, however, only the one to which aluminium hydroxide and colemanite had been added yielded a solid sintered substance.

100 parts of the polymer as used in Example 1, 30 parts of the polyester as used in Example 16 and 500 parts of a mixture of 55% colemanite and 45% aluminium hydroxide were mixed on an unheated roller and the mixture was granulated. The granules were added to an extruder working at 80.degree. C. and discharged through

(a) a round nozzle heated to 110.degree. C. as a strand of 0.5 cm diameter and

(b) a flat profile nozzle heated to 110.degree. C. as a band of 5 mm thickness and 5 cm width.

The round profile and the flat profile were used for wrapping tubes and cables to be protected against flaming. They can also be used for the connection of joints.

Additionally, the granules produced as described above were processed at 110.degree. C. by a spiral injection moulding machine for the production of closure stoppers in the form of commercial rubber stoppers. After moulding, the conical stoppers, whose ratio of greatest diameter to height was 1:1, were used for the fireproof closure of cable openings in cable partitions. In testing the fire resistance time according to DIN 4102, such stoppers gave fire resistance times of over 120 minutes in gas concrete walls. Pierced stoppers of this type can be used as gas tight and moisture-tight cable lead-ins.

100 parts of a polymer as used in Example 1, 100 parts of a polyester of adipic acid and ethylene glycol, pentaerythritol and glycerol (OH No. 157, viscosity at 74.degree. C., 4,500 mPas) and also 600 parts of a mixture of 35% aluminium hydroxide, 10% magnesium hydroxide and 55% colemanite were mixed on an unheated roller. An elastic mastic material resulted. This mastic material was rolled out as a coating on a glass fibre fabric which was used for covering cables and cable conduits against the effects of fire. A 0.5 cm wide strip of this mastic ceramicized on flaming with slight expansion without burning after removal of the flame. Only small amounts of smoke were observed, and no carbon black was formed.

10 parts of the polymer used in Example 1 and 10 parts of the polyester used in Example 16 were mixed at room temperature in a kneader with 60 parts of a mixture of equal parts of colemanite and aluminium hydroxide. A cotton fabric was ined with this mixture in a thickness of 2.5 mm on the unheated roller. After running through a heated space operated at a temperature of 120.degree. C. with a retention time of 15 seconds and subsequent cooling, the lined cotton fabric was wound up. It did not stick together. This type of finished fabric can be used for the protection of cables, pipes and openings against penetration by flames, as can be seen from the following test:

A sample having 3 cm diameter and 5 mm thickness was cut from the mixture used for the coating, heated in a muffle furnace at 940.degree. C. and taken out of the muffle furnace after 30 minutes. A ceramicized, porous piece of material was obtained, which showed about a doubled volume compared to the state before heating. This means that slits and openings sealed with material of this type even in case of fire safely assure sealing off of space without loss of volume.

A mastic was produced from 30 parts of the polyester also used in Example 16 and 80 parts of the filler mixture used in Example 15 by kneading at room temperature, after which 3% of pyrogenic silicic acid was mixed with the filler. This mastic had sufficient adhesive power to adhere well to a vertically standing steel sheet as a strand squeezed out of a mastic gun. On heating the back side of the steel sheet, the strand did not melt off the steel sheet or slide away, but it remained adhered to the sheet and expanded slightly. On flaming with a natural gas burner, no after-burning of the mastic occurred, and ceramicization occurred at about 900.degree. C.

In a commercial, halogen-free mixture for the production of cable sheaths based on ethylene/vinyl acetate copolymer (Levap.RTM. 450 from Bayer AG), in which 190 parts of aluminium hydroxide were contained per 100 parts of polymer in addition to extenders and vulcanization auxiliaries, 100 parts of the aluminium hydroxide contained were replaced by pandermite, which had been ground to a particle size from 1 to 2 .mu.m. This mixture for the production of a cable sheath was mixed and vulcanized according to the prior art, after it had been compressed to bonded sheets of 0.5.times.25.times.25 cm. These bonded sheets were used for covering cable lead-ins, and the cables were led through after perforation.

In the flaming test, in which 1,000.degree. C. was achieved after 60 minutes, the sheet material sintered after expanding by 160% by volume to a mechanically solid sintered substance having a ceramic ring. On subjecting to a flame and flaming for 2 minutes, the material did not burn after removal of the burner flame.

A cable route having a U-shaped cross-section manufactured from a steel sheet was led through a small fire chamber in such a way that the burner flame impinged on the middle of one side of the route. The cable route was covered over its total width of 10 cm with an aluminium hydroxide/colemanite mixture 2 cm high in a ratio of 1:1. 3 telephone cables and 3 commercial heavy current cables were then placed on the filling and the route was then covered up to 1 cm under its full height with further aluminium hydroxide/colemanite mixture. The covering towards the top was performed with a calcium silicate sheet of 6 mm thickness. The heavy current cables (NYM-I 4.times.6) and the telephone cables were connected in such a way that a short circuit or a break in the line made itself noticeable by the extinguishing of a lamp.

The fire chamber was then fired for 120 minutes in accordance with the standard temperature curve according to DIN 4102 (STC) based on DIN 4102.

No short-circuit and no break in the line occurred in this time. The filling of the route was externally sintered together to give a solid sintered block, and in the interior the pulverulent filling remained preserved. The cables were attacked, however, but the cable sheaths essentially remained intact.

65 parts of colemanite, 65 parts of Al-hydroxide (Apyral B 2, Bayer AG), 50 parts of a commercial polyol of the idealized formula (C.sub.2 H.sub.5 O).sub.2 PHCH.sub.2 N(C.sub.2 H.sub.4 OH).sub.2, water content about 0.25%, 55 parts of commercial polyisocyanate obtained by phosgenation of aniline/formaldehyde condensates and having an NCO content of about 30% (Desmodur.RTM. 44 V 40 Bayer AG) are stirred to homogeneity at room temperature within 20 seconds and introduced into a beaker mould. The reaction mixture begins to foam up in the mould. After about 300 seconds, the foamed plastic moulding can be removed from the mould previously treated with a parting compound based on paraffin.

The foamed plastic moulding has a bulk density of about 250 kg/m.sup.3. This burns weakly on flaming with a Bunsen burner flame, with little generation of smoke, and on removing the flame spontaneous extinguishing occurs within 10 seconds. On tempering in a muffle furnace between 900.degree. and 950.degree. C., a mechanically stable sintered substance is obtained.

Isolating bonded sheets for fire-resistant cable lead-ins can be produced from the foamed plastic material and also cladding for instruments and valves to be protected against the effects of fire.