US 5,019,198 AGrant
Method for the Decorative Surface Coating of Flat Substrates
Issue Date:1991-05-28
•13 Claims
Abstract
A method is disclsed for surface improving sheet-like substrates to impart them with a marbleized effect. A transfer sheet is pressed on the substrate at elevated temperatures. The transfer sheet is comprised of superimposed layers of synthetic resin. The resin layer closest to the backing of the transfer sheet is devoid of pigments, while the resin layer adjacent the pigment free layer comprises 2 to 40% by weight, calculated on the amount of resin, of a flake-like pigment. The pressing of the transfer sheet against the substrate is carried out with a press tool devoid of surface pattern and having a generally flat press surface.
Metadata
Assignee
- Th. Goldschmidt AG
Inventors
- Werner Schafer
- Manfred Scheiba
Application Information
Application Number:US 490785&
Filing Date:1990-03-08
Priority Date:1988-09-08
Art Unit:134
Classifications
IPC:
B44C 100
Field of Search:
156428106230;24040;195415
Patent Drawings
This patent does not have any drawings.
Description
Example 1
As support sheet or backing, a paper with a weight of 120 g/m.sup.2 and with an adhesive surface is used.
The composition of the resin is as follows:
Transparent coating resin:
310 g free-flowing, unsaturated polyester resin
40 g diallyl phthalate prepolymer
35 g partially etherified melamine-formaldehyde resin
284 g dichloromethane
3 g p-toluenesulfonic acid
13 g internal release agent
2 g benzoyl peroxide paste
17 g peroxide mixture
Pigmented coating resin: as above, however with the addition of 50 g of Iriodin.RTM. pigment Rotbraun 502, with a particle size of 10 to 60 .mu.m.
The transparent coating resin is applied with a doctor blade at the rate of 40 g/m.sup.2 on the adhesive side of the paper sheet. The solvent is evaporated off in a drying duct at 40.degree. to 80.degree. C. The residual solvent content is 8 to 9%. The pigmented coating resin is then applied with a second metering device in the same amount and dried in the same manner.
To prepare a surface-improved, molded laminated material, the following construction is introduced into a hot press;
forming pad
pressing plate
transfer sheet, coated pursuant to the invention
melamine resin-impregnated black decor paper: weight of paper =80 g/m.sup.2 ; resin content: 80 g/m.sup.2 solid resin
10 phenolic resin-impregnated core films: weight of paper=150 g/m.sup.2 ; resin content: 70 g/m.sup.2 solid resin
release paper
pressing plate
forming pad
The pressing is carried out in a platen press at a pressure of 10 N/mm.sup.2, a temperature of 145.degree. C. and a pressing time of 20 minutes. The pressed material is cooled under pressure and removed from the press. The backing on the upper side of the molded laminated article is pulled off.
A molded, laminated material with a copper-color, marmorated surface is obtained. The black melamine resin film partially shines through as background.
Example 2
As support sheet or backing is used a 10 .mu.m thick aluminum foil, which has been coated with a release lacquer and which is reinforced on the back with 60 g/m.sup.2 paper.
Used as coating resins are:
transparent coating resin:
100 g melamine-formaldehyde resin, etherified with butanol, as a 55 to 60% by weight solution in a butanol-xylene mixture
1 g p-toluenesulfonic acid, as a 50% by weight solution in methanol
Pigmented coating resin: as above, however with 3 g of Iriodin.RTM. pigment Glitzerbronce 530, with a particle size of 10 to 100 .mu.m.
The transparent coating resin is applied on the backing at the rate of 40 g/m.sup.2. The solvent is evaporated off in a drying duct at 60.degree. to 110.degree. C. In a second application, the pigmented resin is applied in the same manner and the product obtained is dried.
For the preparation of the surface-improved molded laminated material, the following construction is introduced into the hot press:
forming pad
pressing plate
backing, coated pursuant to the invention (transfer sheet)
melamine resin-impregnated dark-brown decor paper: weight of paper: 80 g/m.sup.2 ; resin content: 80 g/m.sup.2 solid resin;
50 phenolic resin-impregnated core films: weight of paper: 150 g/m.sup.2 resin content: 70 g/m.sup.2 solid resin
melamine resin-impregnated dark-brown decor paper: weight of paper: 80 g/m.sup.2 ; resin content: 80 g/m.sup.2 solid resin
transfer sheet coated pursuant to the invention
pressing plate
forming pad
The pressing is carried out in a platen press at a pressure of 10 N/mm.sup.2, a temperature of 145.degree. C. and a pressing time of 45 minutes. The pressed material is cooled under pressure and removed from the press. The adhesive backing sheets on the top and bottom sides of the molded laminated article are pulled off.
A panel is obtained with decorative marmoration on both sides. The surface is lustrous with a silky appearance.
Example 3
As backing is used a polypropylene film reinforced with paper. The thickness of the polypropylene film is 30 .mu.m and the weight of the paper on the reverse side is 100 g/.sup.2.
The coating resins used are:
Transparent coating resin:
100 g diallyl phthalate prepolymer
100 g dichloromethane
3 g internal release agent
0.5 g benzoyl peroxide paste
4 g peroxide paste
Pigmented coating resin: as above, however with 10 g Iriodin.RTM. pigment Goldperl 300 with a particle size of 10 to 60 .mu.m.
The coated transfer sheet is prepared as described in Example 1.
For the preparation of a surface-improved chipboard panel, the following construction is pressed:
forming pad
pressing plate
transfer sheet, coated pursuant to the invention
melamine resin-impregnated green decor paper: weight of paper: 80 g/m.sup.2 ; resin content: 80 g/m.sup.2 solid resin
melamine resin-impregnated barrier film: weight of paper: 120 g/m.sup.2 ; resin content: 150 g/m.sup.2 solid resin
chipboard
melamine resin-impregnated barrier film as above
melamine resin impregnated green decor paper as above
transfer sheet, coated pursuant to the invention
pressing plate
forming pad
The pressing is carried out in a platen press at a pressure of 2 N/mm.sup.2, a temperature of 145.degree. C. and a pressing time of 12 minutes. The pressed material is taken from the press without first being cooled. The adhesive backing sheets on the top and bottom sides are pulled off. The panel obtained, which is finished or surface-improved on both sides, exhibits decorative marmoration and is especially suitable, for example, for indoor installations (furniture, self-erecting screens, exhibition constructions).
Example 4
The method of Example 1 is repeated. However, 4 g of the solvent-soluble dye, Zaponblau, are added to the transparent coating resin. A surface coloration results with marmoration corresponding to the varying blue coloration.
Example 5
A backing sheet, as described in Example 1, is coated. The coating resins used are:
Pigmented coating resin:
120 g diallyl phthalate prepolymer
80 g dichloromethane
2.5 g internal release agent
4 g dicumyl peroxide
4 g aluminum paste
0.4 g carbon black paste
Transparent coating resin: as above, however unpigmented.
The coated backing sheet is prepared as in Example 1 and a surface-finished chipboard as in Example 3. A surface improved panel is obtained, which has a silver metallic marmoration and is especially suitable for the manufacture of decorative surfaces.
Claims
What is claimed is:
1. In a method of surface improving a generally flat substrate by providing it with a surface coating, wherein a transfer sheet having a backing and being coated with synthetic resin is pressed with a pressing tool at elevated temperature onto the substrate, so that the resin of the transfer sheet is transferred to the substrate, whereafter the backing is pulled off, the improvement which comprises providing a transfer sheet having a first pigment free layer of a transparent thermoplastic or duroplastic synthetic resin which is capable of flowing when pressed at elevated temperatures, said first layer being adjacent said backing, a second layer of thermoplastic or duroplastic synthetic resin which is capable of flowing when pressed at elevated temperatures, said second layer being superimposed on said first layer, said second layer having incorporated therein 2 to 40% by weight, calculated on the amount of synthetic resin, of a flake-shaped lamellar pigment and pressing said transfer sheet onto the substrate by means of a press tool which is devoid of surface pattern or profile at a temperature and pressure effective to cause the first and second layers to flow and the pigment particles to orient themselves in the direction of flow, whereby a surface coating with a marbleized appearance is obtained.
2. The improvement as claimed in claim 1, wherein the particle size of said pigment in respect to its planar extension is about between 5 to 100 .mu.m.
3. The improvement as claimed in claim 1 or 2, wherein said pigment is present in said second layer in an amount of between about 5 to 20% by weight, calculated on synthetic resin.
4. The improvement as claimed in claim 1, wherein said pigment is mica.
5. The improvement as claimed in claim 4, wherein said mica has a metal oxide surface.
6. The improvement as claimed in claim 5, wherein said metal oxide surface is titanium dioxide or iron oxide.
7. The improvement as claimed in claim 1, wherein said pigment comprises metals or metal alloys.
8. The improvement as claimed in claim 1, wherein said pigment is an aluminum pigment coated with iron oxide.
9. The improvement as claimed in claim 1, wherein the backing of said transfer sheet is of a material that does not melt under the pressing conditions and has adhesive characteristics in respect to said synthetic resin layers.
10. The improvement of claim 1, wherein at least one of said first and second synthetic resin layers is dyed with a dye which is soluble in the synthetic resin.
11. The improvement of claim 1, wherein said first and second synthetic resin layers are dyed with a dye which is soluble in the synthetic resin, the dye for dying said first layer having a different color than the dye for dying said second layer.
12. The improvement of claim 1, wherein a pattern-forming shaped sheet fragment is placed between the transfer sheet and the substrate before pressing the transfer sheet onto the substrate.
13. A method of surface improving a generally flat substrate of molded or laminated wood products or the like which comprises (a) pressing on said substrate at elevated temperature a transfer sheet having an adhesive backing and being coated with a first pigment free layer of a transparent thermoplastic or duroplastic synthetic resin which is capable of flowing when pressed at elevated temperatures, said first layer being adjacent said backing, a second layer of a thermoplastic or duroplastic synthetic resin which is capable of flowing when pressed at elevated temperatures, said second layer being superimposed on said first layer, said second layer having incorporated therein 2 to 40% by weight, calculated on the amount of synthetic resin, of a flake-shaped lamellar pigment, said pressing of said transfer sheet onto the substrate being carried out with a press tool which is devoid of surface pattern or profile, and under pressure and temperature conditions such that the first and second resin layers flow and the pigment particles orient themselves in the direction of flow, whereby a coating with marbleized appearance is formed, and (b) removing the backing.