Method for Producing Silver Coated Superconducting Ceramic Powder

This invention relates to metal/ceramic composites and more particularly to silver metal-coated superconducting ceramic powders.

Since the advent of the new generation high Tc (.about.77.degree. K.) ceramic superconducting materials, prodigious efforts have been expended to fabricate same into usable wire form.

The relative metallurgical intractability of these ceramic compounds has been described as follows:

It would be desirable to provide a process by which intimate bonding of the superconductive ceramic particles with a suitable workable metal of good electrical conductivity is achieved while maintaining the superconductive properties of the ceramic.

Accordingly, an object of this invention is to provide a new method of incorporating superconducting ceramics into a workable metal matrix without loss of the superconductive properties.

Another object of this invention is to produce a new superconductive composite powder capable of being worked by techniques such as forging, swaging, drawing, etc.

A further object of this invention is to provide a composite powder in which the superconducting ceramic particles are protected against chemical degradation.

These and other objects of this invention are achieved by providing a process for silver coating superconducting ceramic powders comprising:

(1) coating superconducting ceramic powder particles with AgNO.sub.3 ;

(2) melting the AgNO.sub.3 so that it wets and forms a uniform coating over the surfaces of the particles; and

(3) decomposing the AgNO.sub.3 to form a thin, uniform coating of silver metal on the surfaces of the particles.

The product is a loose powder of superconducting ceramic particles which are uniformly coated with silver metal. The powder can be cold worked (e.g., swaged, forged, etc.) to form superconducting structures such as rods or wires.

A more complete understanding of the invention and many of the attendant advantages thereto will be readily appreciated as the same becomes better understood by reference to the following detailed description when consider in connection with the accompanying figures wherein:

FIGS. 1A, 1B, and 1C show powder X-ray spectra for silver metal coated YBa.sub.2 Cu.sub.3 O.sub.7-x powder composites containing (A) 14.6, (B) 7.9, and (C) 2.09 weight percent silver and is discussed in example 1;

FIGS. 2A and 2B present SEM photographs (5000X) of uncoated (FIG. 2A) and silver metal coated (FIG. 2B) particles of YBa.sub.2 Cu.sub.3 O.sub.7-x high temperature superconducting ceramic powder and are discussed in example 2; and

FIG. 3 is an optical micrograph at 400X magnification of a consolidated composite wire cross section morphology wherein the wire was form according to the process of example 3 from the silver coated ceramic particles (FIG. 2B) of example 2.

The process of this invention quickly and inexpensively produces uniform, thin coatings of silver metal on particles of ceramic superconductors. The process operates at temperatures well below the melting points of the ceramic materials and leaves their superconducting properties undisturbed. These silver metal coated particles have good cold working properties and may be swaged, drawn, pressed, etc., to form wires, rods, or other useful forms. In contrast to the brittle ceramics, the silver matrix or coating produces a flexible, malleable material. The uniform silver metal coating also provides some protection for the superconductor material against the environment.

The key to the present process is the special properties of AgNO.sub.3. At 212.degree. C. silver nitrate melts and forms a clear, low viscosity liquid with excellent wetting properties. The molten AgNO.sub.3 quickly spreads out to form a uniform coating on the surfaces of the ceramic particles. Moreover, the silver nitrate decomposes at 444.degree. C. leaving a thin, uniform coating of silver metal. Note that this decomposition temperature of silver nitrate is more than 500.degree. C. below the melting point of YBa.sub.2 Cu.sub.3 O.sub.7-x. Similarly, it is well below the melting point of the other superconducting ceramics.

Reagent (ACS) grade AgNO.sub.3 is preferred for this process. Less pure AgNO.sub.3 may introduce undesirable impurities.

This process is designed for use on ceramic superconductors. For example, it can be used to coat yttrium (Y) based ceramic superconductors such as YBa.sub.2 Cu.sub.3 O.sub.7-x, bismuth (Bi) based ceramic superconductors such as Bi.sub..7 Pb.sub..3 SrCaCu.sub.1.8 Ox, and thallium (Tl) based superconductors such as Tl.sub.2 Ba.sub.2 Ca.sub.2 Cu.sub.3 O.sub.7-x. Molten AgNO.sub.3 does not chemically attack or adversely affect these ceramic superconductors. In fact, because AgNO.sub.3 is an oxidizer, it helps to maintain the oxygen content in these ceramics.

The products of the process are loose powders made up of ceramic particles which are uniformly coated with silver metal. This powder composite product is composed of from about 1 to about 25, and preferably from 1 to 15, and more preferably from 10 to 15 weight percent of silver metal with the ceramic superconducting material being the remainder of the composite.

The amounts of AgNO.sub.3 and superconducting ceramic powder in the starting mixture are calculated as follows. The amount of silver metal needed is calculated from the amount of superconducting ceramic powder to be coated and the desired silver metal/ceramic composition. The weight of AgNO.sub.3 to be used in the starting mixture is then calculated by multiplying the weight of silver metal needed by 1.5748 (mol. wt. AgNO.sub.3 divided by at. wt. Ag).

The first step of the process is to coat the superconducting ceramic particles with the AgNO.sub.3 If the silver metal/ceramic composite is to contain 10 to 25 weight percent of silver, the AgNO.sub.3 may be melted and the ceramic particles mixed in until they are wetted. Or the AgNO.sub.3 powder and the superconducting particles may be mixed together before the AgNO.sub.3 is melted. However, if the silver metal content is to be less than 10 weight percent, it will be difficult if not impossible to wet all the ceramic particles in the amount of molten AgNO.sub.3 available.

A procedure that will work for the entire range of from about 1 to about 25 weight percent silver is to dissolve the AgNO.sub.3 in a suitable solvent. Just enough of the solvent is used to make a paste that assures the wetting of all ceramic particle surfaces with the AgNO.sub.3 solution. The solvent is then removed, leaving the AgNO.sub.3 deposited as small crystals over the surfaces of the particles. Note that a suitable solvent is one that (1) dissolves AgNO.sub.3, (2) can be evaporated at relatively low temperatures without leaving a residue, and (3) will not react with or damage the superconducting ceramic. Distilled water (AgNO.sub.3 solubility about 120 g/100 ml at 0.degree. C.) will work well for bismuth or thallium based superconducting ceramics. However, water damages YBa.sub.2 Cu.sub.3 O.sub.7-x. Ethylene glycol, HOCH.sub.2 CH.sub.2 OH, (AgNO.sub.3 solubility about 75 g/100 ml) is the solvent of choice. It is safe for superconducting ceramics (including YBa2Cu.sub.3 O.sub. 7-x). However, care must be taken in removing the ethylene glycol. The temperature should be kept below 75.degree. C. and preferably should be in the range of from 50.degree. C. to 65.degree. C. At high temperatures the ethylene glycol acts as fuel and may catch fire.

In the second step of the process, the AgNO.sub.3 is heated at a temperature above its melting point (212.degree. C.) and below its decomposition temperature (444.degree. C.) until it melts and wets the superconducting ceramic particle surfaces. As a practical matter, this occurs automatically while the AgNO.sub.3 coated particles are being heated up to the AgNO.sub.3 decomposition temperature. When the small AgNO.sub.3 crystals melt on a particle, the molten AgNO.sub.3 seeks to cover as wide an area as possible. As a result, the AgNO.sub.3 wets the particle surface forming a uniform coating.

In the third and final step of the process, the AgNO.sub.3 is decomposed to form a thin, uniform coating of silver metal over the surfaces of the superconducting ceramic particles. The reaction sequence is:

The decomposition step may be run at a temperature of from the decomposition temperature of AgNO.sub.3 (444.degree. C.) up to 50.degree. C. less than the melting point of the superconducting ceramic. As a practical matter there is no need to use very high temperatures. A preferred temperature range from the decomposition step is from 450.degree. C. to 550.degree. C., with from 450.degree. C. to 500.degree. C. being more preferred. After the decomposition is complete, the coated particles are cooled to room temperature.

The silver metal-coated superconducting particles produced are in the form of a loose powder. In contrast to silver coating produced from mixtures of fine silver powder and the superconducting ceramic powder, the coating produced by this process are smooth and uniform. Agglomeration of the silver coated ceramic particles may occur when the silver metal content of the composite is near 25 weight percent. This can be correcting by ball milling to break the particles apart. This creates jagged uneven spots in the silver metal coating. However, because silver metal is soft, the ball milling process smooths and reforms the silver coatings.

Silver metal-coated particles produced by this process have been used to produce superconducting pellets by pressing. They also have been used to produce rods and wires by packing in copper or silver tubes and swaging. Explosive compaction and extrusion have been attempted.

The silver metal-coated superconducting particles produced by this process are characterized by uniform coatings which are preferably from about 0.02 to about 10 microns thick, and more preferably from 0.05 to 1 micron thick.

Chemical vapor deposited coatings on such powders, if available, should look similar. However the penetration of silver into the small cavities of individual particles (see FIGS. 2A and 2B might not be as complete. This is simply speculation because such powders are unavailable and if tried would be very expensive to manufacture.

The general nature of the invention having been set forth, the following examples are presented as specific illustrations thereof. It will be understood that the invention is not limited to these specific examples but is susceptible to various modifications that will be recognized by one of ordinary skill in the art.

The described method was used to produce Ag Coated YBa.sub.2 Cu.sub.3 O.sub.7-x (123) high temperature superconducting (HTS) powder in various weight percentages of silver. The steps in accomplishing this are given as follows:

(a) 7.5 grams of AgNO.sub.3 were dissolved into 10 grams of ethylene glycol.

(b) A 4 gram portion of this solution was thoroughly mixed into 10 grams of 123 HTS powder to form a paste. The glycol carrier was carefully evaporated leaving the 123/AgNO.sub.3 mixture. This mixture was heated to 450.degree. C. in air in an oven for 20 minutes to decompose the AgNO.sub.3. The total sample weight after decomposition, 11.714 grams, indicated a weight fraction of silver of 1.714/11.714=14.6%.

(c) The remainder of the original AgNO.sub.3 glycol solution was diluted 2:1 with additional glycol. Following the same procedure as in (b) produced a measured weight of 10.857 grams. The fraction of silver was 0.857/10.857=7.9%.

(d) Further dilution following the same procedure produced silver fractions of 4.1% and 2.09%, respectively. Visual inspection and X-ray spectroscopy indicated a quite uniform distribution of the silver. Powder X-ray spectra of the 14.6%, 7 9% and 2.09% samples are shown in FIGS. 1A, 1B, and 1C, respectively. The progressive growth of the Ag peaks are indicated.

A quantity of YBa.sub.2 Cu.sub.3 O.sub.7-x (123) high temperature superconducting (HTS) powder was coated with 15 weight % silver by applying the method as follows:

(a) 20 grams of 123 HTS powder was weighed. The proportion 0.15=X/(20+X) was used to compute the amount of Ag necessary in the sample. This was 3.53 grams. The corresponding amount of AgNO.sub.3 required for this weight of Ag after decomposition is obtained from the fraction of molecular weight 108/170=3.53/X. X=5.55 grams AgNO.sub.3.

(b) The mixture was heated to about 250.degree. C. on a hot plate while stirring to wet thoroughly the entire body of powder with the liquid AgNO.sub.3. The sample was placed subsequently in a furnace in air at .about.460.degree. C. for 20 minutes to decompose the AgNO.sub.3.

(c) The final product appeared uniform in Ag coating by microscopic observation. FIG. 2A shows a scanning electron microscope (SEM) photograph of the uncoated, as received particles of 123 HTS powder (MAG:5000X) and FIG. 2B shows a SEM photograph of the Ag metal coated particles of 123 HTS powder (MAG:5000X). A notable feature is the filling of micropores observable in the uncoated particles (FIG. 2A) by a smooth layer of silver metal (FIG. 2B).

Approximately 10 grams of 15% 123/Ag powder (example 2) was packed into a 1/2" outside diameter (OD) 0.030" wall silver tube and swaged down to 0.155 inch. The silver tube was removed from a portion of the tube by grinding.

The removed portion of HTS 123/Ag rod was annealed in O.sub.2 atmosphere overnight at 925.degree. C. and subsequently tested for superconducting properties. It was found to have a superconducting transition temperature Tc .apprxeq.93.degree. C. and a superconducting current density capability (Tc) of 125 amps/cm.sup.2.

The optical micrograph (FIG. 3) at 400X magnification shows the consolidated composite wire cross section morphology under these conditons of processing.

Obviously, numerous modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims the invention may be practiced otherwise than as specifically described herein.