US 4,959,285 AGrant
Flexographic Relief Printing Plate
Issue Date:1990-09-25
•4 Claims
Abstract
Mixtures which can be cross-linked by photopolymerization and are based on soluble elastomeric block copolymers, photopolymerizable monomers which are compatible with these, photoinitiators and plasticizers contain, as the plasticizer, a chlorolakane of 8 to 40 carbon atoms which has a chlorine content of from 30 to 73% by weight.
Metadata
Assignee
- BASF Aktiengesellschaft
Inventor
- Gerhard Hoffmann
Application Information
Application Number:US 4767802
Filing Date:1990-02-08
Priority Date:1985-10-17
Art Unit:157
Classifications
IPC:
G03C 300
Field of Search:
10143052239511;14;18;270;271;281;300;306;325;327;396;397;312714
Patent Drawings
This patent does not have any drawings.
Description
In the Examples below, the Shore A hardness according to DIN 53,505, the resilience in percent according to DIN 53,512 and the swelling of the samples, in % by weight, after treatment for 24 hours with a solvent mixture consisting of 7 parts by weight of ethanol and 3 parts by weight of ethyl acetate, were determined. The tendency to crack was determined in an ozone chamber at an ozone concentration of 50 ppm and at 25.degree.C. on 10 cm long samples which had been subjected to 10% elongation; the criterion here was the period after which the first cracks appeared.
Example 1
88,00 g of a styrene/isoprene/styrene three-block copolymer according to Example IV of British Pat. No. 1,366,769, having a number average molecular weight of 130,000,
3.55 g of hexanediol diacrylate,
1.75 g of hexanediol dimethacrylate,
1.25 g of benzil dimethyl acetal,
5.30 g of a chloroalkane having a chlorine content of 49% and a density of 1.24 gcm.sup.-3,
5.30 g of an oligomer of 70 parts of vinyltoluene and 30 parts of .alpha.-methylstyrene,
0.53 g of 2,6-di-tert-butyl-p-cresol and 0.006 g of Solvent Black 3 (C.I. 26150)
were dissolved in 114.4 g of toluene at 90.degree.C. The solution was applied, by means of a knife coater, onto the coated side of a biaxially oriented polyethylene terephthalate film coated with a commercial nylon copolymer (Macromelt from Henkel) so that, after the layer had been dried at 80.degree.C. for 1 hour, a 0.7 mm thick film remained. The multilayer element obtained in this manner was exposed uniformly for 30 minutes in a commercial flat-plate exposure unit (40 watt, UV fluorescent lamps). The resulting photopolymerized layer of the exposed multilayer element was a film which had no imagewise information content, possessed a Shore A hardness of 39 and a resilience of 52% and exhibited 7.7% by weight swelling. Cracks occurred after 35 minutes.
Comparative Experiment 1
The procedure described in Example 1 was followed, except that the content of the chloroalkane according to the invention was replaced by the same amount of white oil S 5000, a liquid paraffin usually employed as a plasticizer. The photopolymerized layer of this exposed multilayer element was a film which had no imagewise information content, possessed a Shore A hardness of 41 and a resilience of 56% and exhibited 13.7% by weight swelling. The first cracks appeared after only 12 minutes.
Comparative Experiment 2
The procedure described in Comparatve Experiment 1 was followed, except that 1 g of commercial antiozone wax (Antilux 550 from Rhein-Chemie, Rheinau GmbH) was also added to the material. The Shore A hardness, resilience and swelling of the resulting photopolymerized film without any imagewise information content were similar to the values for Comparative Experiment 1. The first cracks appeared after 25 minutes. This corresponded roughly to a 50% improvement in the tensile strength compared with that of Comparative Experiment 1; the tensile strength of the film according to Example 1 was not reached.
Example 2
In the preparation of the novel mixture, the procedure described in Example 1 was followed, except that the amount of chloroalkane was doubled from 5.3 to 10.6 g, and the amount of block copolymer was reduced from 88.00 g to 82.70 g. This mixture according to the invention was used to produce a multilayer element according to German Laid-Open Application DOS No. 2,444,118, which had a total thickness of 2 mm and possessed, on the upper side, a 0.7 mm thick layer of the novel mixture. The multilayer element was exposed uniformly as described in Example 1. The photopolymerized layer (film) of the multilayer element had a Shore A hardness of 40 and a resilience of 42% and exhibited only 1.9% by weight swelling. Cracks only appeared after 345 minutes; this corresponded to an improvement of more than 1000% over Comparative Experiment 2.
Example 3
The novel mixture according to Example 2 was used to produce a multilayer element as described in Example 1, the relief-forming layer (RL) of this element being 1.7 mm thick, compared with 0.7 mm in Example 1.
To produce a flexographic printing plate from this multilayer element, a 75 .mu.m thick polyethylene terephthalate film coated with a mixture of adhesive-forming components was first applied, by roller-coating, onto the free surface of the relief-forming layer (RL). A mixture of an isocyanate-cured phenoxy resin and a polycarbonate according to German Laid-Open Application DOS No. 3,100,175 was used as the mixture of adhesive-forming components. Thereafter, the polyester cover sheet was removed, the nylon copolymer layer remaining as a protective layer on the surface of the relief-forming layer (RL).
A photographic image-bearing negative was then placed as a transparency on that side of the relief-forming layer (RL) which was covered with the nylon copolymer, and pressed on with a film using a vacuum frame. Thereafter, imagewise exposure was carried out through the photographic negative for 12 minutes using a commercial flat-plate exposure unit (40 watt, UV fluorescent tubes). Simultaneously with the photopolymerization taking place during this process, the dye present in the relief-forming layer (RL) was bleached, thus permitting a direct assessment of the quality of the result of exposure.
The partially photopolymerized relief-forming layer (RL) of the multilayer element was developed in a commercial spray washer for 4.5 minutes at room temperature using a solvent mixture consisting of 9 parts by volume of tetrachloroethylene and 1 part by volume of n-butanol, dried in a through-circulation dryer at 80.degree.C. for one hour, aftertreated for 3 minutes with a 0.4% strength by weight aqueous bromine solution, washed and dried again.
The resulting relief layer (RL) of the flexographic printing plate was postexposed uniformly for 10 minutes and clamped on a printing cylinder which in turn was coated with a 1 mm thick coating of natural rubber having a Shore A hardness of 30.
The nontacky surface of the flexographic printing plate accepted conventional flexographic printing inks in an outstanding manner. The abrasion resistance, swelling and resilience of the printing plate were similar to those of conventional rubber blocks. The print results obtained showed exact reproduction of the original, with crisp details. For its part, the printing plate showed absolutely no damage or cracks even after a print run of 200,000.
Claims
We claim:
1. A flexographic relief printing plate comprising a dimensionally stable base and a photopolymerized relief layer which is obtained by imagewise exposing to actinic radiation a photopolymerizable elastomeric relief forming layer of a photopolymerizable element, said relief forming layer consisting essentially of (a) from 58% to 92% by weight, based on the sum of all the components of the photopolymerizable elastomeric relief-forming layer, of a solvent soluble elastomeric diene block copolymer containing at least one vinylaromatic and at least one diene polymer block, (b) from 2% to 16% by weight, based on the sum of all the components of the photopolymerizable elastomeric relief-forming layer, of one or more photopolymerizable, ethylenically unsaturated monomers being compatible with the elastomeric diene block copolymer (a), (c) from 0.4% to 6% by weight, based on the sum of all the components of the photopolymerizable elastomeric relief-forming layer, of one or more photoinitiators, and (d) from 3% to 22% by weight, based on the sum of the photopolymerizable elastomeric relief-forming layer, of a chloralkane of 8 to 40 carbons which has a chlorine content of about 49% by weight and then developing the unexposed and unpolymerized areas by liquid solvent washout to obtain said flexographic relief printing plate.
2. The printing plate of claim 1, wherein the chloralkane has a density of 1.24 g/cm.sup.3.
3. The printing plate of claim 2, wherein the chloralkane is an oil.
4. The printing plate of claim 1, wherein said photopolymerizable elastomeric relief forming layer contains 68-82% by weight of (a), from 5% to 12% by weight of (b), from 1.2 to 2.5% by weight of (c) and from 8% to 18% by weight of (d).
Patent Citations (12)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3897255 | 1975-07-01 | Erickson | |
| US4001174 | 1975-10-01 | Yagi et al. | |
| US4045231 | 1977-08-01 | Toda et al. | |
| US4201642 | 1980-05-01 | Nowak | |
| US4339527 | 1982-07-01 | Hill | |
| US4369246 | 1983-01-01 | Chen et al. | |
| US4400460 | 1983-08-01 | Fickes et al. | |
| US4452879 | 1984-06-01 | Fickes et al. | |
| US4636453 | 1987-01-01 | Keys et al. | |
| EPX217324 | 1987-04-01 | ||
| GBX1095518 | 1968-12-01 | ||
| GBX1366769 | 1974-09-01 |
Non-Patent Literature (2)
- Ullmanns Enzyklopaide der Technischen Chemie, vol. 9, No. 4, Aug. 4, 1975, pp. 480-481.
- Kirk-Othmer, Encyclopedia of Chemical Technology, vol. 5, No. 3 1979, pp. 786,790.